JP2015063560A - Method for producing aromatic hydrocarbon - Google Patents

Method for producing aromatic hydrocarbon Download PDF

Info

Publication number
JP2015063560A
JP2015063560A JP2014262765A JP2014262765A JP2015063560A JP 2015063560 A JP2015063560 A JP 2015063560A JP 2014262765 A JP2014262765 A JP 2014262765A JP 2014262765 A JP2014262765 A JP 2014262765A JP 2015063560 A JP2015063560 A JP 2015063560A
Authority
JP
Japan
Prior art keywords
catalyst
reaction
aromatic compound
methane
gas
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2014262765A
Other languages
Japanese (ja)
Inventor
洪涛 馬
Koto Ba
洪涛 馬
陽 山本
Hiromi Yamamoto
陽 山本
小川　裕治
Yuji Ogawa
裕治 小川
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Meidensha Corp
Meidensha Electric Manufacturing Co Ltd
Original Assignee
Meidensha Corp
Meidensha Electric Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Meidensha Corp, Meidensha Electric Manufacturing Co Ltd filed Critical Meidensha Corp
Priority to JP2014262765A priority Critical patent/JP2015063560A/en
Publication of JP2015063560A publication Critical patent/JP2015063560A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To stably produce an aromatic hydrocarbon for a long time while maintaining a high aromatic hydrocarbon production yield when producing an aromatic hydrocarbon by catalytically reacting a lower hydrocarbon with a catalyst.SOLUTION: There is provided a method for producing an aromatic hydrocarbon which comprises: a step of catalytically reacting a lower hydrocarbon with a catalyst to obtain an aromatic hydrocarbon and hydrogen; and a step of bringing the catalyst used in the reaction step with hydrogen to regenerate catalytic activity and repeats the reaction step and the regeneration step. In the reaction step, the reaction temperature is set at a temperature higher than 800°C by adding carbon monoxide to the lower hydrocarbon.

Description

本発明は、メタンを主成分とする天然ガス、バイオガス、メタンハイドレートの高度利用に関するものである。特に、メタンからプラスチック類などの化学製品原料であるベンゼン及びナフタレン類を主成分とする芳香族化合物と高純度の水素ガスを製造するための触媒化学変換技術に関するものである。   The present invention relates to advanced utilization of natural gas, biogas, and methane hydrate mainly composed of methane. In particular, the present invention relates to a catalytic chemical conversion technique for producing aromatic compounds mainly composed of benzene and naphthalenes, which are raw materials for chemical products such as plastics, and high-purity hydrogen gas from methane.

天然ガス、バイオガス、メタンハイドレートは、地球温暖化対策として最も効果的なエネルギー資源と考えられ、その利用技術に関心が高まっている。メタン資源は、そのクリーン性を活かして、次世代の新しい有機資源、燃料電池用の水素資源として注目されている。   Natural gas, biogas, and methane hydrate are considered to be the most effective energy resources as a countermeasure against global warming, and there is an increasing interest in their utilization technologies. Taking advantage of its cleanliness, methane resources are attracting attention as new next-generation organic resources and hydrogen resources for fuel cells.

メタンからベンゼン等の芳香族化合物と水素を製造する方法としては、例えば非特許文献１のように、触媒の存在下でメタンを反応させる方法が知られている。この際の触媒としては、ＺＳＭ−５に担持されたモリブデンが有効とされている。   As a method for producing an aromatic compound such as benzene and hydrogen from methane, a method of reacting methane in the presence of a catalyst as in Non-Patent Document 1, for example, is known. As a catalyst in this case, molybdenum supported on ZSM-5 is effective.

しかしながら、これらの触媒を使用した場合でも、炭素析出が多いことやメタンの転化率が低いという問題がある。特に、炭素析出は触媒の劣化現象に直結する問題である。   However, even when these catalysts are used, there are problems that carbon deposition is large and methane conversion is low. In particular, carbon deposition is a problem directly related to the deterioration phenomenon of the catalyst.

これらの問題を解決するために、特許文献１では、触媒反応温度３００℃〜８００℃の条件で、メタンにＣＯ2又はＣＯを添加した混合ガスを触媒反応に供している。ＣＯ2又はＣＯを添加することにより炭素の析出が抑制され、触媒劣化を防ぎ、安定して芳香族を生成することを可能としている。 In order to solve these problems, in Patent Document 1, a mixed gas obtained by adding CO 2 or CO to methane is used for the catalytic reaction under the conditions of a catalytic reaction temperature of 300 ° C. to 800 ° C. By adding CO 2 or CO, carbon deposition is suppressed, catalyst deterioration is prevented, and aromatics can be generated stably.

また、特許文献２、３では、芳香族製造反応とその製造反応に用いた触媒を再生する反応を交互に切り替えて、触媒の経時劣化を抑え、触媒反応を持続させている。つまり、反応原料である低級炭化水素と触媒の維持又は再生のための水素含有ガス（又は水素ガス）を周期的に切り替えて触媒と接触させている。   In Patent Documents 2 and 3, the aromatic production reaction and the reaction for regenerating the catalyst used in the production reaction are alternately switched to suppress the deterioration of the catalyst over time and to maintain the catalytic reaction. That is, the lower hydrocarbon which is the reaction raw material and the hydrogen-containing gas (or hydrogen gas) for maintaining or regenerating the catalyst are periodically switched and brought into contact with the catalyst.

特開平１１−０６０５１４号公報Japanese Patent Laid-Open No. 11-060514 特開２００３−０２６６１３号公報JP 2003-026613 A 特開２００８−２６６２４４号公報JP 2008-266244 A

ＪＯＵＲＮＡＬ ＯＦ ＣＡＴＡＬＹＳＩＳ、１９９７、Ｖｏｌｕｍｅ１６５、ｐ．１５０−１６１JOURNAL OF CATALYSIS, 1997, Volume 165, p. 150-161

上記従来技術で述べた課題のうち、非特許文献１に例示される触媒の炭素析出による劣化は、特に固定床方式の反応系で長時間安定的に芳香族炭化水素等を製造するために、その解決が極めて重要である。   Among the problems described in the above prior art, deterioration due to carbon deposition of the catalyst exemplified in Non-Patent Document 1 is particularly necessary for producing aromatic hydrocarbons and the like stably for a long time in a reaction system of a fixed bed system. The solution is extremely important.

そこで、特許文献１では、反応温度が３００〜８００℃の条件で、原料ガスにＣＯ2又はＣＯを添加して触媒と接触反応させることにより、炭素の析出を抑制し、触媒劣化を防ぐ方法が提案されている。この方法によれば、大幅に触媒の安定性が向上するものの、最大ベンゼン収率が低下する傾向がある。 Therefore, in Patent Document 1, there is a method of suppressing carbon deposition and preventing catalyst degradation by adding CO 2 or CO to a raw material gas and causing a catalytic reaction with the catalyst under a reaction temperature of 300 to 800 ° C. Proposed. According to this method, although the stability of the catalyst is greatly improved, the maximum benzene yield tends to decrease.

一方、特許文献２では、反応ガスと水素ガスまたは水素含有ガスとを一定周期で切り替えることにより、難除去性コークの析出を防止し、長時間安定的に芳香族化合物を得る方法が提案されている。この方法は、析出炭素が蓄積する前に再生処理を行うもので、触媒の活性を示す指標であるベンゼン収率を長時間維持することができる。なお、このベンゼン収率は、反応初期におけるベンゼン収率に依存する。   On the other hand, Patent Document 2 proposes a method for preventing precipitation of difficult-to-removable coke and stably obtaining an aromatic compound for a long period of time by switching the reaction gas and hydrogen gas or hydrogen-containing gas at regular intervals. Yes. In this method, the regeneration treatment is performed before the deposited carbon accumulates, and the benzene yield, which is an index indicating the activity of the catalyst, can be maintained for a long time. This benzene yield depends on the benzene yield at the beginning of the reaction.

反応初期の段階では、炭素析出量が少ないため触媒作用によってメタンから転換された炭化水素が高い確率でベンゼンに変換される。そして、反応温度を８００℃以上にするなどしてメタン転化率をあげることで、この反応初期においてより高いベンゼン収率を得ることができる。しかし、反応温度を高温にすることによりメタン転化率を向上させた場合、炭素析出がより顕著となり炭素の蓄積による触媒劣化がはやくなるという問題がある。   In the initial stage of the reaction, since the amount of carbon deposition is small, hydrocarbons converted from methane by the catalytic action are converted to benzene with a high probability. A higher benzene yield can be obtained at the initial stage of the reaction by increasing the methane conversion rate by increasing the reaction temperature to 800 ° C. or higher. However, when the methane conversion rate is improved by increasing the reaction temperature, there is a problem that carbon deposition becomes more prominent and catalyst deterioration due to carbon accumulation is accelerated.

したがって、高温においても析出炭素の除去に対して有効に作用し、かつ最大ベンゼン収率を低下させないプロセスが強く求められている。   Therefore, there is a strong demand for a process that effectively acts on the removal of precipitated carbon even at high temperatures and does not reduce the maximum benzene yield.

上記課題を解決する本発明の芳香族炭化水素製造方法は、低級炭化水素を触媒に接触反応させ、芳香族炭化水素を主成分とする芳香族化合物及び水素を製造する方法であって、前記低級炭化水素に一酸化炭素を添加し、反応温度を８００℃より高くする、ことを特徴としている。   The aromatic hydrocarbon production method of the present invention that solves the above-mentioned problems is a method for producing an aromatic compound mainly composed of an aromatic hydrocarbon and hydrogen by causing a lower hydrocarbon to contact with a catalyst to produce the lower compound. It is characterized in that carbon monoxide is added to the hydrocarbon so that the reaction temperature is higher than 800 ° C.

また、上記芳香族炭化水素製造方法において、前記一酸化炭素濃度を反応ガスに対して０．７５％〜２０％とするとよい。また、上記芳香族炭化水素製造方法において、前記反応温度を８２０℃以上とするとよい。   In the above aromatic hydrocarbon production method, the carbon monoxide concentration may be 0.75% to 20% with respect to the reaction gas. Moreover, in the said aromatic hydrocarbon manufacturing method, it is good to set the said reaction temperature to 820 degreeC or more.

また、上記芳香族炭化水素製造方法において、前記低級炭化水素を前記触媒と接触反応させる反応工程と、前記反応工程で使用された触媒を再生する再生工程を繰り返して芳香族炭化水素を製造するとよい。   In the above aromatic hydrocarbon production method, the aromatic hydrocarbon may be produced by repeating a reaction step in which the lower hydrocarbon is brought into contact with the catalyst and a regeneration step in which the catalyst used in the reaction step is regenerated. .

以上の発明によれば、低級炭化水素を触媒と接触反応させて芳香族化合物を製造する際、触媒の劣化を抑制すること及び芳香族化合物収率を向上させることに貢献することができる。   According to the above invention, when producing an aromatic compound by contact-reacting a lower hydrocarbon with a catalyst, it can contribute to suppressing deterioration of the catalyst and improving the yield of the aromatic compound.

Ｍｏ−ＨＺＳＭ５触媒の存在下で触媒反応を連続して行った場合のベンゼン収率の時間変化を示す図。The figure which shows the time change of the benzene yield at the time of performing a catalytic reaction continuously in presence of Mo-HZSM5 catalyst. Ｍｏ−ＨＺＳＭ５触媒の存在下（ＣＯを添加して）で触媒反応を連続して行った場合のベンゼン収率の時間変化を示す図。The figure which shows the time change of the benzene yield at the time of performing a catalytic reaction continuously in presence of Mo-HZSM5 catalyst (adding CO). （ａ）触媒反応工程と触媒再生工程を繰り返した場合のベンゼン収率の時間変化を示す図、（ｂ）触媒反応工程と触媒再生工程を繰り返した場合のベンゼン生成速度の時間変化を示す図、（ｂ）触媒反応工程と触媒再生工程を繰り返した場合のメタン転化率の時間変化を示す図。(A) The figure which shows the time change of the benzene yield at the time of repeating a catalyst reaction process and a catalyst regeneration process, (b) The figure which shows the time change of the benzene production rate at the time of repeating a catalyst reaction process and a catalyst regeneration process, (B) The figure which shows the time change of the methane conversion rate at the time of repeating a catalyst reaction process and a catalyst reproduction | regeneration process. 一酸化炭素を添加した場合における反応後のガス１００μｌ中のベンゼン量の時間変化を示す図。The figure which shows the time change of the amount of benzene in 100 microliters of gas after reaction in the case of adding carbon monoxide. 一酸化炭素を添加しない場合における反応後のガス１００μｌ中のベンゼン量の時間変化を示す図。The figure which shows the time change of the amount of benzene in 100 microliters of gas after reaction in the case of not adding carbon monoxide.

本発明は、低級炭化水素の芳香族化合物化触媒（以下、「触媒」と省略する）に低級炭化水素を接触反応させてベンゼン及びナフタレン類を主成分とする芳香族化合物と高純度の水素ガスを製造する方法に関する発明である。そして、接触反応に供される反応ガスに一酸化炭素を添加し、反応温度を８００℃より高くして接触反応を行うことを特徴としている。   The present invention relates to an aromatic compound mainly composed of benzene and naphthalene and a high-purity hydrogen gas obtained by catalytically reacting a lower hydrocarbon with a lower hydrocarbon aromatic compound catalyst (hereinafter abbreviated as “catalyst”). It is invention regarding the method to manufacture. Then, carbon monoxide is added to the reaction gas used for the contact reaction, and the reaction temperature is set higher than 800 ° C. to perform the contact reaction.

本発明に係る芳香族化合物の製造方法によれば、反応に供される触媒の触媒活性の劣化を抑制するだけでなく、メタンのみを触媒に接触反応させた時よりも最大ベンゼン収率を向上させることができる。   According to the method for producing an aromatic compound according to the present invention, not only the degradation of the catalytic activity of the catalyst to be subjected to the reaction is suppressed, but also the maximum benzene yield is improved as compared with the case where only the catalyst is contacted with methane. Can be made.

また、触媒反応工程と前記触媒を再生する工程を交互に行うことで、難除去性コークが蓄積することなく、高収率を維持したまま長時間反応を行わせることができる。   Further, by alternately performing the catalyst reaction step and the step of regenerating the catalyst, it is possible to carry out the reaction for a long time while maintaining a high yield without accumulating difficult-to-removable coke.

本発明の実施形態に係る芳香族化合物製造方法に用いられる触媒は、例えば、メタロシリケートに触媒金属が担持された形態が挙げられる。   Examples of the catalyst used in the method for producing an aromatic compound according to the embodiment of the present invention include a form in which a catalytic metal is supported on a metallosilicate.

触媒金属が担持されるメタロシリケートとしては、例えばアルミノシリケートの場合、シリカ及びアルミナから成り多孔質体であるモレキュラーシーブ５Ａ、フォジャサイト（ＮａＹ及びＮａＸ）、ＺＳＭ−５、ＭＣＭ−２２が挙げられる。また、リン酸を主成分とする多孔質体でＡＬＰＯ−５、ＶＰＩ−５等の６〜１３オングストロームのミクロ細孔やチャンネルからなることを特徴とするゼオライト担体や、シリカを主成分とし一部アルミナを成分として含むメゾ細孔（１０〜１０００オングストローム）の筒状細孔（チャンネル）で特徴付けられるＦＳＭ−１６やＭＣＭ−４１等のメゾ細孔多孔質担体などが例示できる。さらに、前記アルミナシリケートの他に、シリカ及びチタニアからなるメタロシリケート等も触媒として用いることができる。   Examples of the metallosilicate on which the catalyst metal is supported include, in the case of aluminosilicate, molecular sieve 5A, focasite (NaY and NaX), ZSM-5, and MCM-22, which are made of silica and alumina and are porous. . Moreover, it is a porous body mainly composed of phosphoric acid and is composed of 6-13 angstrom micropores and channels such as ALPO-5, VPI-5, etc., and partly composed mainly of silica. Examples thereof include mesoporous porous carriers such as FSM-16 and MCM-41 characterized by cylindrical pores (channels) having mesopores (10 to 1000 angstroms) containing alumina as a component. Furthermore, in addition to the alumina silicate, a metallosilicate composed of silica and titania can also be used as a catalyst.

また、本発明で使用するメタロシリケートは、表面積が２００〜１０００ｍ2／ｇであり、そのミクロ及びメゾ細孔は５〜１００オングストロームの範囲内のものが望ましい。また、メタロシリケートが例えばアルミノシリケートである場合、そのシリカとアルミナの含有比（シリカ／アルミナ）が通常入手し得る多孔質体と同様にシリカ／アルミナ＝１〜８０００のものを用いることができるが、本発明の低級炭化水素の芳香族化反応を、実用的な低級炭化水素の転化率及び芳香族化合物への選択率で実施するためには、シリカ／アルミナ＝１０〜１００の範囲内とすることがより好ましい。 The metallosilicate used in the present invention preferably has a surface area of 200 to 1000 m 2 / g, and its micro and mesopores are in the range of 5 to 100 Å. Further, when the metallosilicate is, for example, aluminosilicate, a silica / alumina content ratio (silica / alumina) of silica / alumina = 1 to 8000 can be used in the same manner as a porous body that can be usually obtained. In order to carry out the aromatization reaction of the lower hydrocarbon of the present invention at a practical conversion rate of the lower hydrocarbon and selectivity to the aromatic compound, the silica / alumina is within the range of 10 to 100. It is more preferable.

メタロシリケートは、通常プロトン交換型（Ｈ型）のものが用いられる。また、プロトンの一部がＮａ、Ｋ、Ｌｉ等のアルカリ金属、Ｍｇ、Ｃａ、Ｓｒ等のアルカリ土類元素、Ｆｅ、Ｃｏ、Ｎｉ、Ｚｎ、Ｒｕ、Ｐｄ、Ｐｔ、Ｚｒ、Ｔｉ等の遷移金属元素から選ばれた少なくとも一種のカチオンで交換されていてもよい。また、メタロシリケートが、Ｔｉ、Ｚｒ、Ｈｆ、Ｃｒ、Ｍｏ、Ｗ、Ｔｈ、Ｃｕ、Ａｇ等を適量含有していてもよい。   As the metallosilicate, a proton exchange type (H type) is usually used. Some protons are alkali metals such as Na, K and Li, alkaline earth elements such as Mg, Ca and Sr, transition metals such as Fe, Co, Ni, Zn, Ru, Pd, Pt, Zr and Ti It may be exchanged with at least one cation selected from elements. The metallosilicate may contain an appropriate amount of Ti, Zr, Hf, Cr, Mo, W, Th, Cu, Ag, and the like.

そして、本発明に係る触媒金属としてはモリブデンを用いることが好ましいが、レニウム、タングステン、鉄、コバルトを用いても良い。これらの触媒金属を組み合わせてメタロシリケートに担持してもよい。さらに、これらの触媒金属に、Ｍｇ等のアルカリ土類元素又はＮｉ、Ｚｎ、Ｒｕ、Ｐｄ、Ｐｔ、Ｚｒ、Ｔｉ等の遷移金属元素から選ばれた少なくとも一種の元素をメタロシリケートに共担持してもよい。   As the catalyst metal according to the present invention, molybdenum is preferably used, but rhenium, tungsten, iron, and cobalt may be used. A combination of these catalytic metals may be supported on the metallosilicate. Furthermore, at least one element selected from alkaline earth elements such as Mg or transition metal elements such as Ni, Zn, Ru, Pd, Pt, Zr and Ti is co-supported on the metallosilicate on these catalytic metals. Also good.

前記触媒金属（を含む前駆体）をメタロシリケートに担持させる場合、触媒金属と担体との重量比は０．００１〜５０％、好ましくは０．０１〜４０％の範囲で行う。また、メタロシリケートへ担持させる方法としては、触媒金属の前駆体の水溶液、あるいはアルコール等の有機溶媒の溶液からメタロシリケート担体に含浸担持あるいはイオン交換方法により担持させた後、不活性ガスあるいは酸素ガス雰囲気下で加熱処理する方法がある。例えば、触媒金属の１つであるモリブデンを含む前駆体の例としては、パラモリブデン酸アンモニウム、リンモリブデン酸アンモニウム、１２系モリブデン酸の他に、塩化物、臭化物等のハロゲン化物、硝酸塩、硫酸塩、リン酸塩等の鉱酸塩、炭酸塩、酢酸塩、蓚酸塩等のカルボン酸塩等を挙げることができる。   When the catalyst metal (including the precursor) is supported on the metallosilicate, the weight ratio of the catalyst metal to the support is 0.001 to 50%, preferably 0.01 to 40%. In addition, as a method for supporting the metallosilicate, an inert gas or oxygen gas is used after impregnation or ion exchange on a metallosilicate support from an aqueous solution of a catalyst metal precursor or an organic solvent such as alcohol. There is a method of heat treatment in an atmosphere. For example, examples of a precursor containing molybdenum which is one of the catalytic metals include ammonium paramolybdate, ammonium phosphomolybdate, 12-type molybdic acid, halides such as chloride and bromide, nitrates and sulfates. And mineral salts such as phosphates, carboxylates such as carbonates, acetates and oxalates.

ここでメタロシリケートに触媒金属を担持する方法を触媒金属としてモリブデンを用いた場合を例示して説明する。まず、メタロシリケート担体にモリブデン酸アンモニウム塩の水溶液を含浸担持させ、その担持体を減圧乾燥して溶媒を除いた後、窒素含有酸素気流中又は純酸素気流中にて温度２５０〜８００℃（好ましくは３５０〜６００℃）で加熱処理して、モリブデンを担持したメタロシリケート触媒を製造することができる。   Here, the method of supporting the catalyst metal on the metallosilicate will be described by exemplifying the case where molybdenum is used as the catalyst metal. First, an aqueous solution of ammonium molybdate is impregnated and supported on a metallosilicate carrier, the support is dried under reduced pressure to remove the solvent, and then a temperature of 250 to 800 ° C. in a nitrogen-containing oxygen stream or a pure oxygen stream (preferably 350 to 600 ° C.) to produce a metallosilicate catalyst carrying molybdenum.

触媒金属を担持したメタロシリケート触媒の形態に格別の制約はなく、粉末状、顆粒状等任意の形状のものを用いればよい。また、触媒金属を担持したメタロシリケート触媒に、シリカ、アルミナ、粘土等のバインダーを添加して、ペレット状若しくは押出品に成型して使用してもよい。   There is no particular restriction on the form of the metallosilicate catalyst supporting the catalytic metal, and any shape such as powder or granules may be used. Further, a binder such as silica, alumina, clay, etc. may be added to a metallosilicate catalyst supporting a catalytic metal, and the resultant may be molded into a pellet or extruded product.

なお、本発明において、低級炭化水素とはメタンや炭素数が２〜６の飽和及び不飽和炭化水素を意味する。これら炭素数が２〜６の飽和及び不飽和炭化水素としては、エタン、エチレン、プロパン、プロピレン、ｎ−ブタン、イソブタン、ｎ−ブテン及びイソブテン等が例示できる。   In the present invention, the lower hydrocarbon means methane or a saturated or unsaturated hydrocarbon having 2 to 6 carbon atoms. Examples of these saturated and unsaturated hydrocarbons having 2 to 6 carbon atoms include ethane, ethylene, propane, propylene, n-butane, isobutane, n-butene, and isobutene.

本発明の実施形態に係る芳香族化合物製造方法で使用する反応器は、例えば、固定床反応器あるいは流動床反応器などを用いればよい。以下、本発明の実施例に係る芳香族化合物製造方法を示してより詳細に説明する。   The reactor used in the aromatic compound production method according to the embodiment of the present invention may be, for example, a fixed bed reactor or a fluidized bed reactor. Hereafter, the aromatic compound manufacturing method which concerns on the Example of this invention is shown and demonstrated in detail.

（１）一酸化炭素を添加することによる触媒活性の変化
（参考例１）
本発明の参考例１に係る芳香族化合物製造法は、触媒にメタンを接触反応させて芳香族化合物と水素ガスを製造する方法において、反応ガスに対して０．７５％の一酸化炭素を添加し、７８０℃で触媒反応を行った。 (1) Change in catalytic activity by adding carbon monoxide (Reference Example 1)
An aromatic compound production method according to Reference Example 1 of the present invention is a method in which methane is contacted with a catalyst to produce an aromatic compound and hydrogen gas, and 0.75% of carbon monoxide is added to the reaction gas. The catalytic reaction was carried out at 780 ° C.

本発明の参考例１に係るメタロシリケート担体としてＨ型ＺＳＭ５ゼオライト（ＳｉＯ2／Ａｌ2Ｏ3＝４０）を用い、以下の調製方法により触媒を作成した。 Using H-type ZSM5 zeolite (SiO 2 / Al 2 O 3 = 40) as the metallosilicate support according to Reference Example 1 of the present invention, a catalyst was prepared by the following preparation method.

イオン交換水２０００ｍｌにモリブデン酸アンモニウム４５６．５ｇを溶解させた水溶液に、ＨＺＳＭ５を４００ｇ加え、室温にて３時間攪拌し、ＨＺＳＭ５にモリブデンを含浸担持した。   400 g of HZSM5 was added to an aqueous solution in which 456.5 g of ammonium molybdate was dissolved in 2000 ml of ion-exchanged water, and the mixture was stirred at room temperature for 3 hours, so that HZSM5 was impregnated with molybdenum.

得られたモリブデン担持ＨＺＳＭ５（Ｍｏ−ＨＺＳＭ５）を乾燥後、前記の担持体を大気条件下にて温度５５０℃で８時間焼成することにより、モリブデンが担持された触媒粉末（Ｍｏの重量比が触媒全体に対して６．８ｗｔ％の触媒）を得た。さらに、この触媒粉末に無機結合剤を加えてペレット状に押し出し成型、焼成を行い触媒とした。   After drying the obtained molybdenum-supported HZSM5 (Mo-HZSM5), the support was calcined at a temperature of 550 ° C. for 8 hours under atmospheric conditions, whereby catalyst powder supporting molybdenum (the weight ratio of Mo was a catalyst). 6.8 wt% catalyst) was obtained. Furthermore, an inorganic binder was added to the catalyst powder, extruded into pellets, and fired to obtain a catalyst.

上記の方法で作製した触媒を、固定床流通式反応装置のインコネル８００Ｈ接ガス部カロライジング処理製反応管（内径１８ｍｍ）内に充填した。この反応管内の反応温度を７８０℃、圧力を０．３ＭＰａに設定し、反応ガスに対して０．７５％の一酸化炭素を添加したメタンを空間速度（ＳＶ：Space Velocity）３０００ｍｌ／ｈｒ／ｇ−ＭＦＩの流量で供給し、メタンの芳香族化反応を行った。そして、メタンの芳香族化反応によるベンゼン及び水素ガスの生成反応の触媒活性を評価した。   The catalyst produced by the above method was packed in a reaction tube (inner diameter: 18 mm) made of Inconel 800H gas contact part calorizing treatment of a fixed bed flow type reactor. The reaction temperature in this reaction tube was set to 780 ° C., the pressure was set to 0.3 MPa, and methane added with 0.75% carbon monoxide with respect to the reaction gas was used as space velocity (SV) 3000 ml / hr / g. -MFI aromatization reaction was carried out at a flow rate of MFI. Then, the catalytic activity of benzene and hydrogen gas production reaction by methane aromatization reaction was evaluated.

触媒活性は、「ベンゼン収率」、「メタン転化率」、「ベンゼン生成速度」に基づいて評価した。なお、本実施例における「ベンゼン収率」、「メタン転化率」、「ベンゼン生成速度」を以下に示すように定義した。
・「ベンゼン収率（％）」＝〔「生成したベンゼン量（ｍｏｌ）」／「メタン改質反応に供されたメタン量（ｍｏｌ）」〕×１００
・「メタン転化率（％）」＝〔「原料メタン流速」−「未反応のメタン流速」）／「原料メタン流速」〕×１００
・「ベンゼン生成速度（ｎｍｏｌ／ｇ／ｓ）」＝「触媒１ｇあたり、１秒間に生成したベンゼンのｎｍｏｌ数」
前記反応ガスを供給する前の触媒の前処理は、触媒を空気気流下５５０℃まで昇温し、２時間維持した後、メタン２０％：水素８０％の前処理ガスに切り替えて、７００℃まで昇温し、３時間維持した。その後、反応ガスに切り替えて所定の温度（７８０℃）まで昇温し触媒の評価を行った。 The catalytic activity was evaluated based on “benzene yield”, “methane conversion rate”, and “benzene production rate”. In this example, “benzene yield”, “methane conversion”, and “benzene production rate” were defined as shown below.
“Benzene yield (%)” = [“Amount of benzene produced (mol)” / “Amount of methane subjected to methane reforming reaction (mol)”] × 100
・ “Methane conversion rate (%)” = [“Raw material methane flow rate” − “Unreacted methane flow rate”) / “Raw material methane flow rate”] × 100
“Benzene production rate (nmol / g / s)” = “nmol number of benzene produced per second per gram of catalyst”
The pretreatment of the catalyst before supplying the reaction gas is performed by heating the catalyst to 550 ° C. under an air stream and maintaining it for 2 hours, and then switching to a pretreatment gas of 20% methane: 80% hydrogen to 700 ° C. The temperature was raised and maintained for 3 hours. Thereafter, the reaction gas was changed to a predetermined temperature (780 ° C.) to evaluate the catalyst.

水素、アルゴン、メタンの分析はＴＣＤ−ＧＣで分析し、ベンゼン、トルエン、キシレン、ナフタレン等の芳香族炭化水素の分析はＦＩＤ−ＧＣで分析した。   Hydrogen, argon and methane were analyzed by TCD-GC, and aromatic hydrocarbons such as benzene, toluene, xylene and naphthalene were analyzed by FID-GC.

（参考例２）
本発明の参考例２に係る芳香族化合物製造法は、触媒にメタンを接触反応させて芳香族化合物と水素ガスを製造する方法において、反応ガスに対して６．４％の一酸化炭素を添加し、７８０℃で触媒反応を行った。 (Reference Example 2)
An aromatic compound production method according to Reference Example 2 of the present invention is a method of producing an aromatic compound and hydrogen gas by catalytic reaction of methane with a catalyst, and adding 6.4% carbon monoxide to the reaction gas. The catalytic reaction was carried out at 780 ° C.

本発明の参考例２に係る芳香族化合物製造方法で用いられた触媒は、参考例１で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法も参考例１と同様であるため、詳細な説明は省略する。なお、添加ガス以外の反応条件についても参考例１と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound production method according to Reference Example 2 of the present invention is the same as the catalyst (Mo-HZSM5) used in Reference Example 1, detailed description of the catalyst production method is omitted. Further, the pretreatment of the catalyst and the analysis method of each substance are the same as those in Reference Example 1, and thus detailed description thereof is omitted. In addition, since it is the same as that of the reference example 1 also about reaction conditions other than additive gas, detailed description is abbreviate | omitted.

（比較例１）
本発明の比較例１に係る芳香族化合物製造法では、触媒にメタンのみを接触反応させ、７８０℃で触媒反応を行い芳香族化合物と水素ガスを製造した。 (Comparative Example 1)
In the method for producing an aromatic compound according to Comparative Example 1 of the present invention, only methane was brought into contact with the catalyst and subjected to catalytic reaction at 780 ° C. to produce an aromatic compound and hydrogen gas.

本発明の比較例１に係る芳香族化合物製造方法で用いられた触媒は、参考例１で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法も参考例１と同様であるため、詳細な説明は省略する。なお、反応に供されるガス以外の反応条件についても参考例１と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound manufacturing method according to Comparative Example 1 of the present invention is the same as the catalyst (Mo-HZSM5) used in Reference Example 1, detailed description of the catalyst manufacturing method is omitted. Further, the pretreatment of the catalyst and the analysis method of each substance are the same as those in Reference Example 1, and thus detailed description thereof is omitted. Since the reaction conditions other than the gas used for the reaction are the same as in Reference Example 1, detailed description thereof is omitted.

（比較例２）
本発明の比較例２に係る芳香族化合物製造法は、触媒にメタンを接触反応させて芳香族化合物と水素ガスを製造する方法において、反応ガスに対して１．２％の二酸化炭素を添加し、７８０℃で触媒反応を行った。 (Comparative Example 2)
The method for producing an aromatic compound according to Comparative Example 2 of the present invention is a method in which methane is contacted with a catalyst to produce an aromatic compound and hydrogen gas, and 1.2% carbon dioxide is added to the reaction gas. The catalytic reaction was performed at 780 ° C.

本発明の比較例２に係る芳香族化合物製造方法で用いられた触媒は、参考例１で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法も参考例１と同様であるため、詳細な説明は省略する。なお、添加ガス以外の反応条件についても参考例１と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound production method according to Comparative Example 2 of the present invention is the same as the catalyst (Mo-HZSM5) used in Reference Example 1, detailed description of the catalyst production method is omitted. Further, the pretreatment of the catalyst and the analysis method of each substance are the same as those in Reference Example 1, and thus detailed description thereof is omitted. In addition, since it is the same as that of the reference example 1 also about reaction conditions other than additive gas, detailed description is abbreviate | omitted.

（比較例３）
本発明の比較例３に係る芳香族化合物製造法は、触媒にメタンを接触反応させて芳香族化合物と水素ガスを製造する方法において、反応ガスに対して３．０％の二酸化炭素を添加し、７８０℃で触媒反応を行った。 (Comparative Example 3)
The method for producing an aromatic compound according to Comparative Example 3 of the present invention is a method in which methane is contacted with a catalyst to produce an aromatic compound and hydrogen gas, and 3.0% of carbon dioxide is added to the reaction gas. The catalytic reaction was performed at 780 ° C.

本発明の比較例３に係る芳香族化合物製造方法で用いられた触媒は、参考例１で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法も参考例１と同様であるため、詳細な説明は省略する。なお、添加ガス以外の反応条件についても参考例１と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound production method according to Comparative Example 3 of the present invention is the same as the catalyst (Mo-HZSM5) used in Reference Example 1, detailed description of the catalyst production method is omitted. Further, the pretreatment of the catalyst and the analysis method of each substance are the same as those in Reference Example 1, and thus detailed description thereof is omitted. In addition, since it is the same as that of the reference example 1 also about reaction conditions other than additive gas, detailed description is abbreviate | omitted.

図１は、Ｍｏ−ＨＺＳＭ５触媒存在下で、上記参考例１、２及び比較例１〜３に示した反応条件で触媒反応を連続して行った場合のベンゼン収率の時間変化を示す図である。   FIG. 1 is a graph showing a change in benzene yield over time when a catalytic reaction is continuously performed under the reaction conditions shown in Reference Examples 1 and 2 and Comparative Examples 1 to 3 in the presence of a Mo-HZSM5 catalyst. is there.

メタンのみを接触反応させた場合（比較例１）は、反応時間が７時間たつと触媒活性を失っているのに対して、二酸化炭素を添加したメタンを接触反応させた場合（比較例２、３）は、触媒活性の低下が抑制されていることがわかる。特に、３．０％の二酸化炭素を添加すると（比較例３）反応時間が１５時間経過しても初期の最大ベンゼン収率を維持している。   When only methane is catalytically reacted (Comparative Example 1), the catalytic activity is lost after 7 hours of reaction, whereas when methane added with carbon dioxide is catalytically reacted (Comparative Example 2, As for 3), it turns out that the fall of a catalyst activity is suppressed. In particular, when 3.0% carbon dioxide is added (Comparative Example 3), the initial maximum benzene yield is maintained even when the reaction time is 15 hours.

しかし、メタンのみを接触反応させた場合（比較例１）の最大ベンゼン収率が８．０％以上であるのに対して、二酸化炭素を添加した場合（例えば、比較例３）は、７．０％と、最大ベンゼン収率が減少する。比較例２と比較例３との比較により、二酸化炭素の添加量が増加すると、最大ベンゼン収率は低下することがわかる。   However, the maximum benzene yield in the case where only methane is catalytically reacted (Comparative Example 1) is 8.0% or more, whereas the case where carbon dioxide is added (for example, Comparative Example 3) is 7. At 0%, the maximum benzene yield decreases. A comparison between Comparative Example 2 and Comparative Example 3 shows that the maximum benzene yield decreases as the amount of carbon dioxide added increases.

つまり、反応温度が同じ場合、反応ガスに二酸化炭素を加えることにより、触媒が活性を維持する時間は長くなるが、最大ベンゼン収率が減少してしまう。   That is, when the reaction temperature is the same, adding carbon dioxide to the reaction gas increases the time for which the catalyst remains active, but reduces the maximum benzene yield.

一方、一酸化炭素を添加したメタンを接触反応させた場合（参考例１）、メタンのみを接触反応させた場合（比較例１）と比較して最大ベンゼン収率が向上している。特に、参考例１と参考例２の比較より、反応ガスに対して一酸化炭素の添加量が増加すると、触媒活性の安定性が向上するとともに、最大ベンゼン収率が向上していることがわかる。   On the other hand, the maximum benzene yield is improved when the methane to which carbon monoxide is added is contact-reacted (Reference Example 1) and when only methane is contact-reacted (Comparative Example 1). In particular, from the comparison between Reference Example 1 and Reference Example 2, it can be seen that when the amount of carbon monoxide added to the reaction gas increases, the stability of the catalytic activity is improved and the maximum benzene yield is improved. .

（２）一酸化炭素の添加量の違いによる触媒活性の変化
（参考例３）
本発明の参考例３に係る芳香族化合物製造法は、触媒にメタンを接触反応させて芳香族化合物と水素ガスを製造する方法において、反応ガスに対して１．５％の一酸化炭素を添加し、７８０℃で触媒反応を行った。 (2) Changes in catalytic activity due to differences in the amount of carbon monoxide added (Reference Example 3)
An aromatic compound production method according to Reference Example 3 of the present invention is a method of producing an aromatic compound and hydrogen gas by catalytic reaction of methane with a catalyst, and adding 1.5% carbon monoxide to the reaction gas The catalytic reaction was carried out at 780 ° C.

本発明の参考例３に係る芳香族化合物製造方法で用いられた触媒は、参考例１で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法も参考例１と同様であるため、詳細な説明は省略する。なお、添加ガス以外の反応条件についても参考例１と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound production method according to Reference Example 3 of the present invention is the same as the catalyst (Mo-HZSM5) used in Reference Example 1, detailed description of the catalyst production method is omitted. Further, the pretreatment of the catalyst and the analysis method of each substance are the same as those in Reference Example 1, and thus detailed description thereof is omitted. In addition, since it is the same as that of the reference example 1 also about reaction conditions other than additive gas, detailed description is abbreviate | omitted.

（参考例４）
本発明の参考例４に係る芳香族化合物製造法は、触媒にメタンを接触反応させて芳香族化合物と水素ガスを製造する方法において、反応ガスに対して３．０％の一酸化炭素を添加し、７８０℃で触媒反応を行った。 (Reference Example 4)
An aromatic compound production method according to Reference Example 4 of the present invention is a method of producing an aromatic compound and hydrogen gas by catalytic reaction of methane with a catalyst, and adding 3.0% carbon monoxide to the reaction gas. The catalytic reaction was carried out at 780 ° C.

本発明の参考例４に係る芳香族化合物製造方法で用いられた触媒は、参考例１で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法も参考例１と同様であるため、詳細な説明は省略する。なお、添加ガス以外の反応条件についても参考例１と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound production method according to Reference Example 4 of the present invention is the same as the catalyst (Mo-HZSM5) used in Reference Example 1, detailed description of the catalyst production method is omitted. Further, the pretreatment of the catalyst and the analysis method of each substance are the same as those in Reference Example 1, and thus detailed description thereof is omitted. In addition, since it is the same as that of the reference example 1 also about reaction conditions other than additive gas, detailed description is abbreviate | omitted.

（参考例５）
本発明の参考例５に係る芳香族化合物製造法は、触媒にメタンを接触反応させて芳香族化合物と水素ガスを製造する方法において、反応ガスに対して１１．９％の一酸化炭素を添加し、７８０℃で触媒反応を行った。 (Reference Example 5)
An aromatic compound production method according to Reference Example 5 of the present invention is a method in which methane is contacted with a catalyst to produce an aromatic compound and hydrogen gas, and 11.9% of carbon monoxide is added to the reaction gas. The catalytic reaction was carried out at 780 ° C.

本発明の参考例５に係る芳香族化合物製造方法で用いられた触媒は、参考例１で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法も参考例１と同様であるため、詳細な説明は省略する。なお、添加ガス以外の反応条件についても参考例１と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound production method according to Reference Example 5 of the present invention is the same as the catalyst (Mo-HZSM5) used in Reference Example 1, detailed description of the catalyst production method is omitted. Further, the pretreatment of the catalyst and the analysis method of each substance are the same as those in Reference Example 1, and thus detailed description thereof is omitted. In addition, since it is the same as that of the reference example 1 also about reaction conditions other than additive gas, detailed description is abbreviate | omitted.

（参考例６）
本発明の参考例６に係る芳香族化合物製造法は、触媒にメタンを接触反応させて芳香族化合物と水素ガスを製造する方法において、反応ガスに対して２０％の一酸化炭素を添加し、７８０℃で触媒反応を行った。 (Reference Example 6)
An aromatic compound production method according to Reference Example 6 of the present invention is a method of producing an aromatic compound and hydrogen gas by catalytic reaction of methane with a catalyst, adding 20% carbon monoxide to the reaction gas, The catalytic reaction was performed at 780 ° C.

本発明の参考例６に係る芳香族化合物製造方法で用いられた触媒は、参考例１で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法も参考例１と同様であるため、詳細な説明は省略する。なお、添加ガス以外の反応条件についても参考例１と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound manufacturing method according to Reference Example 6 of the present invention is the same as the catalyst (Mo-HZSM5) used in Reference Example 1, detailed description of the catalyst manufacturing method is omitted. Further, the pretreatment of the catalyst and the analysis method of each substance are the same as those in Reference Example 1, and thus detailed description thereof is omitted. In addition, since it is the same as that of the reference example 1 also about reaction conditions other than additive gas, detailed description is abbreviate | omitted.

図２は、Ｍｏ−ＨＺＳＭ５触媒存在下で、上記参考例１〜６及び比較例１に示した反応条件で触媒反応を連続して行った場合のベンゼン収率の時間変化を示す図である。   FIG. 2 is a graph showing a change in benzene yield over time when the catalytic reaction is continuously performed under the reaction conditions shown in Reference Examples 1 to 6 and Comparative Example 1 in the presence of the Mo-HZSM5 catalyst.

一酸化炭素を添加したメタンを接触反応させた場合（参考例１〜６）、添加する一酸化炭素の量にかかわらず、メタンのみを接触反応させた場合（比較例１）と比較して触媒活性の低下が抑制されるとともに、最大ベンゼン収率が向上している。一酸化炭素の量が増加することで、触媒の低下抑制効果が向上することがわかる。また、一酸化炭素の添加量が２０％であっても、最大ベンゼン収率はほとんど損なわれることがなく、一酸化炭素の添加量が６．４％の場合（参考例２）には、最大ベンゼン収率が９％を超えている。   When methane added with carbon monoxide is subjected to a catalytic reaction (Reference Examples 1 to 6), regardless of the amount of carbon monoxide to be added, the catalyst is compared with a case where only methane is subjected to a catalytic reaction (Comparative Example 1). The decrease in activity is suppressed and the maximum benzene yield is improved. It can be seen that an increase in the amount of carbon monoxide improves the effect of suppressing the decrease in the catalyst. Further, even when the amount of carbon monoxide added is 20%, the maximum benzene yield is hardly impaired, and when the amount of carbon monoxide added is 6.4% (Reference Example 2), the maximum The benzene yield is over 9%.

（３）触媒反応工程と触媒再生工程を繰り返した場合の、一酸化炭素の添加量の違いによる触媒活性の変化
（実施例１）
本発明の実施例１に係る芳香族化合物製造法は、触媒にメタンを接触反応させて芳香族化合物と水素ガスを製造する方法において、反応ガスに対して３．０％の一酸化炭素を添加し、８２０℃で触媒反応を行った。さらに、１時間の触媒反応（反応工程）と３時間の触媒再生反応（再生工程）を交互に行った。 (3) Changes in catalytic activity due to differences in the amount of carbon monoxide added when the catalytic reaction step and the catalyst regeneration step are repeated (Example 1)
The method for producing an aromatic compound according to Example 1 of the present invention is a method in which methane is contacted with a catalyst to produce an aromatic compound and hydrogen gas, and 3.0% carbon monoxide is added to the reaction gas. Then, a catalytic reaction was performed at 820 ° C. Further, a 1-hour catalytic reaction (reaction process) and a 3-hour catalyst regeneration reaction (regeneration process) were alternately performed.

本発明の実施例１に係る芳香族化合物製造方法で用いられた触媒は、参考例１で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法も参考例１と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound production method according to Example 1 of the present invention is the same as the catalyst (Mo-HZSM5) used in Reference Example 1, detailed description of the catalyst production method is omitted. Further, the pretreatment of the catalyst and the analysis method of each substance are the same as those in Reference Example 1, and thus detailed description thereof is omitted.

ＨＺＳＭ５にモリブデンを担持した触媒を、固定床流通式反応装置のインコネル８００Ｈ接ガス部カロライジング処理製反応管内に充填した。この反応管内の反応温度を８２０℃、圧力を０．１５ＭＰａに設定し、反応ガスに対して３．０％の一酸化炭素を添加したメタンを空間速度３０００ｍｌ／ｈｒ／ｇ−ＭＦＩの流量で供給し、メタンの芳香族化反応（反応工程）を行った。反応工程は、１時間行った。反応工程後、前記反応管内の温度を８２０℃、圧力を０．１５ＭＰａに設定し、再生ガスとして水素ガスを空間速度３０００ｍｌ／ｈｒ／ｇ−ＭＦＩの流量で供給し、触媒の再生反応（再生工程）を行った。再生工程は、３時間行った。そして、メタンの芳香族化反応によるベンゼン及び水素ガスの生成反応の触媒活性を評価した。   A catalyst in which molybdenum was supported on HZSM5 was packed into a reaction tube made by calorizing treatment of an Inconel 800H gas contact part of a fixed bed flow type reactor. The reaction temperature in this reaction tube is set to 820 ° C., the pressure is set to 0.15 MPa, and methane with 3.0% carbon monoxide added to the reaction gas is supplied at a space velocity of 3000 ml / hr / g-MFI. Then, methane aromatization reaction (reaction process) was performed. The reaction process was performed for 1 hour. After the reaction step, the temperature in the reaction tube is set to 820 ° C., the pressure is set to 0.15 MPa, hydrogen gas is supplied as a regeneration gas at a space velocity of 3000 ml / hr / g-MFI, and a catalyst regeneration reaction (regeneration step). ) The regeneration process was performed for 3 hours. Then, the catalytic activity of benzene and hydrogen gas production reaction by methane aromatization reaction was evaluated.

（比較例４）
本発明の比較例４に係る芳香族化合物製造法は、触媒にメタンのみを接触反応させ、８２０℃で触媒反応を行い芳香族化合物と水素ガスを製造した。１時間の触媒反応（反応工程）と３時間の触媒再生反応（再生工程）を交互に行った。 (Comparative Example 4)
In the method for producing an aromatic compound according to Comparative Example 4 of the present invention, only methane was contact-reacted with the catalyst, and a catalytic reaction was performed at 820 ° C. to produce an aromatic compound and hydrogen gas. 1-hour catalytic reaction (reaction process) and 3-hour catalyst regeneration reaction (regeneration process) were alternately performed.

本発明の比較例４に係る芳香族化合物製造方法で用いられた触媒は、参考例１で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法も参考例１と同様であるため、詳細な説明は省略する。なお、反応ガス以外の反応条件については、実施例１と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound production method according to Comparative Example 4 of the present invention is the same as the catalyst (Mo-HZSM5) used in Reference Example 1, detailed description of the catalyst production method is omitted. Further, the pretreatment of the catalyst and the analysis method of each substance are the same as those in Reference Example 1, and thus detailed description thereof is omitted. Since the reaction conditions other than the reaction gas are the same as those in Example 1, detailed description thereof is omitted.

（比較例５）
本発明の比較例５に係る芳香族化合物製造法は、触媒にメタンを接触反応させて芳香族化合物と水素ガスを製造する方法において、反応ガスに対して１．５％の二酸化炭素を添加し、８２０℃で触媒反応を行った。さらに、１時間の触媒反応（反応工程）と３時間の触媒再生反応（再生工程）を交互に行った。 (Comparative Example 5)
The method for producing an aromatic compound according to Comparative Example 5 of the present invention is a method for producing an aromatic compound and hydrogen gas by catalytically reacting methane with a catalyst, and adding 1.5% carbon dioxide to the reaction gas. The catalytic reaction was performed at 820 ° C. Further, a 1-hour catalytic reaction (reaction process) and a 3-hour catalyst regeneration reaction (regeneration process) were alternately performed.

本発明の比較例５に係る芳香族化合物製造方法で用いられた触媒は、参考例１で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法も参考例１と同様であるため、詳細な説明は省略する。なお、添加ガス以外の反応条件については、実施例１と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound production method according to Comparative Example 5 of the present invention is the same as the catalyst (Mo-HZSM5) used in Reference Example 1, detailed description of the catalyst production method is omitted. Further, the pretreatment of the catalyst and the analysis method of each substance are the same as those in Reference Example 1, and thus detailed description thereof is omitted. Since the reaction conditions other than the additive gas are the same as those in Example 1, detailed description is omitted.

図３は、Ｍｏ−ＨＺＳＭ５触媒存在下で、上記実施例１及び比較例４、５に示した反応条件で触媒反応と触媒再生反応を交互に行った場合のベンゼン収率の時間変化を示す図である。   FIG. 3 is a graph showing the change in benzene yield over time when the catalytic reaction and the catalyst regeneration reaction are alternately performed under the reaction conditions shown in Example 1 and Comparative Examples 4 and 5 in the presence of the Mo-HZSM5 catalyst. It is.

一酸化炭素を添加したメタンを接触反応させた場合（実施例１）、メタンのみを接触反応させた場合（比較例４）と比較して触媒活性の低下が抑制されるとともに、最大ベンゼン収率が向上している。二酸化炭素を添加したメタンを接触反応させた場合（比較例５）もメタンのみを接触反応させた場合（比較例４）と比較して触媒活性の低下が抑制されているが、図３（ａ）に示すように、最大ベンゼン収率がメタンのみを接触反応させた場合（比較例４）における最大ベンゼン収率を上回ることがない。図３（ｃ）に示すように、一酸化炭素を添加したメタンを接触反応させた場合（実施例１）は、比較例４、５と比較してメタン転化率が向上し、その結果ベンゼン収率が向上している。   When methane added with carbon monoxide is subjected to a catalytic reaction (Example 1), a decrease in catalytic activity is suppressed as compared with a case where only methane is catalytically reacted (Comparative Example 4), and the maximum benzene yield is obtained. Has improved. When the methane to which carbon dioxide is added is contact-reacted (Comparative Example 5), the decrease in catalytic activity is suppressed as compared with the case where only methane is contact-reacted (Comparative Example 4). ), The maximum benzene yield does not exceed the maximum benzene yield in the case of contact reaction of methane alone (Comparative Example 4). As shown in FIG. 3 (c), when methane added with carbon monoxide was subjected to a catalytic reaction (Example 1), the methane conversion was improved as compared with Comparative Examples 4 and 5, and as a result, the benzene yield was increased. The rate has improved.

（４）一酸化炭素を添加した場合の反応温度の違いによる触媒活性の変化
（実施例２）
本発明の実施例２に係る芳香族化合物製造法は、触媒にメタンを接触反応させて芳香族化合物と水素ガスを製造する方法において、反応ガスに対して３．０％の一酸化炭素を添加し、８９０℃で触媒反応を行った。 (4) Change in catalyst activity due to difference in reaction temperature when carbon monoxide is added (Example 2)
The method for producing an aromatic compound according to Example 2 of the present invention is a method for producing an aromatic compound and hydrogen gas by catalytic reaction of methane with a catalyst, and adding 3.0% of carbon monoxide to the reaction gas. Then, a catalytic reaction was performed at 890 ° C.

本発明の実施例２に係る芳香族化合物製造方法で用いられた触媒は、微細粉末状の触媒を用いたこと以外は参考例１で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。すなわち、実施例２で用いられた触媒は、モリブデンをＨＺＳＭ５に含浸担持した後、この担持体を乾燥し、得られた触媒粉末を焼成した微細粉末状の触媒を用いた。また、触媒の前処理、及び各物質の分析方法も参考例１と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound production method according to Example 2 of the present invention is the same as the catalyst (Mo-HZSM5) used in Reference Example 1 except that a fine powder catalyst was used, Detailed description of the catalyst production method is omitted. That is, the catalyst used in Example 2 was a fine powder catalyst obtained by impregnating and supporting molybdenum in HZSM5, drying the support, and calcining the obtained catalyst powder. Further, the pretreatment of the catalyst and the analysis method of each substance are the same as those in Reference Example 1, and thus detailed description thereof is omitted.

ＨＺＳＭ５にモリブデンを担持した触媒（０．４ｇ）を、固定床流通式反応装置のガラス製反応管内に充填した。この反応管内の反応温度を８９０℃、圧力を０．１５ＭＰａに設定し、反応ガスとして３．０％の一酸化炭素を添加したメタンを空間速度１００００ｍｌ／ｈｒ／ｇ−ＭＦＩの流量で供給し、メタンの芳香族化反応を行った。そして、メタンの芳香族化反応によるベンゼン及び水素ガスの生成反応の触媒活性を評価した。   A catalyst (0.4 g) supporting molybdenum on HZSM5 was charged into a glass reaction tube of a fixed bed flow type reactor. The reaction temperature in the reaction tube was set to 890 ° C., the pressure was set to 0.15 MPa, and methane added with 3.0% carbon monoxide as a reaction gas was supplied at a space velocity of 10,000 ml / hr / g-MFI. Methane aromatization reaction was carried out. Then, the catalytic activity of benzene and hydrogen gas production reaction by methane aromatization reaction was evaluated.

（実施例３）
本発明の実施例３に係る芳香族化合物製造法は、触媒にメタンを接触反応させて芳香族化合物と水素ガスを製造する方法において、反応ガスに対して３．０％の一酸化炭素を添加し、８７０℃で触媒反応を行った。 (Example 3)
The method for producing an aromatic compound according to Example 3 of the present invention is a method in which methane is contacted with a catalyst to produce an aromatic compound and hydrogen gas, and 3.0% carbon monoxide is added to the reaction gas. Then, a catalytic reaction was performed at 870 ° C.

本発明の実施例３に係る芳香族化合物製造方法で用いられた触媒は、実施例２で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法は、参考例１と同様であるため詳細な説明は省略する。なお、温度以外の反応条件については実施例２と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound production method according to Example 3 of the present invention is the same as the catalyst (Mo-HZSM5) used in Example 2, detailed description of the catalyst production method is omitted. Further, the catalyst pretreatment and the analysis method of each substance are the same as those in Reference Example 1, and therefore detailed description thereof is omitted. The reaction conditions other than temperature are the same as in Example 2, and thus detailed description thereof is omitted.

（実施例４）
本発明の実施例４に係る芳香族化合物製造法は、触媒にメタンを接触反応させて芳香族化合物と水素ガスを製造する方法において、反応ガスに対して３．０％の一酸化炭素を添加し、８５０℃で触媒反応を行った。 Example 4
An aromatic compound production method according to Example 4 of the present invention is a method of producing an aromatic compound and hydrogen gas by catalytic reaction of methane with a catalyst, and adding 3.0% of carbon monoxide to the reaction gas. Then, a catalytic reaction was performed at 850 ° C.

本発明の実施例４に係る芳香族化合物製造方法で用いられた触媒は、実施例２で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法は、参考例１と同様であるため詳細な説明は省略する。なお、温度以外の反応条件については実施例２と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound production method according to Example 4 of the present invention is the same as the catalyst (Mo-HZSM5) used in Example 2, detailed description of the catalyst production method is omitted. Further, the catalyst pretreatment and the analysis method of each substance are the same as those in Reference Example 1, and therefore detailed description thereof is omitted. The reaction conditions other than temperature are the same as in Example 2, and thus detailed description thereof is omitted.

（比較例６）
本発明の比較例６に係る芳香族化合物製造法では、触媒にメタンのみを接触反応させ、８９０℃で触媒反応を行い芳香族化合物と水素ガスを製造した。 (Comparative Example 6)
In the aromatic compound production method according to Comparative Example 6 of the present invention, only methane was contact-reacted with the catalyst, and a catalytic reaction was performed at 890 ° C. to produce an aromatic compound and hydrogen gas.

本発明の比較例６に係る芳香族化合物製造方法で用いられた触媒は、実施例２で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法は、参考例１と同様であるため詳細な説明は省略する。なお、反応ガス以外の反応条件については実施例２と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound manufacturing method according to Comparative Example 6 of the present invention is the same as the catalyst (Mo-HZSM5) used in Example 2, detailed description of the catalyst manufacturing method is omitted. Further, the catalyst pretreatment and the analysis method of each substance are the same as those in Reference Example 1, and therefore detailed description thereof is omitted. Since the reaction conditions other than the reaction gas are the same as those in Example 2, detailed description thereof is omitted.

（比較例７）
本発明の比較例７に係る芳香族化合物製造法では、触媒にメタンのみを接触反応させ、８７０℃で触媒反応を行い芳香族化合物と水素ガスを製造した。 (Comparative Example 7)
In the aromatic compound manufacturing method according to Comparative Example 7 of the present invention, only methane was contact-reacted with the catalyst, and a catalytic reaction was performed at 870 ° C. to manufacture an aromatic compound and hydrogen gas.

本発明の比較例７に係る芳香族化合物製造方法で用いられた触媒は、実施例２で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法は、参考例１と同様であるため詳細な説明は省略する。なお、反応ガス以外の反応条件については実施例３と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound production method according to Comparative Example 7 of the present invention is the same as the catalyst (Mo-HZSM5) used in Example 2, detailed description of the catalyst production method is omitted. Further, the catalyst pretreatment and the analysis method of each substance are the same as those in Reference Example 1, and therefore detailed description thereof is omitted. Since the reaction conditions other than the reaction gas are the same as those in Example 3, detailed description thereof is omitted.

（比較例８）
本発明の比較例８に係る芳香族化合物製造法では、触媒にメタンのみを接触反応させ、８５０℃で触媒反応を行い芳香族化合物と水素ガスを製造した。 (Comparative Example 8)
In the method for producing an aromatic compound according to Comparative Example 8 of the present invention, only methane was brought into contact with the catalyst and subjected to catalytic reaction at 850 ° C. to produce an aromatic compound and hydrogen gas.

本発明の比較例８に係る芳香族化合物製造方法で用いられた触媒は、実施例２で用いられた触媒（Ｍｏ−ＨＺＳＭ５）と同様であるため、触媒製造方法の詳細な説明は省略する。また、触媒の前処理、及び各物質の分析方法は、参考例１と同様であるため詳細な説明は省略する。なお、反応ガス以外の反応条件については実施例４と同様であるため、詳細な説明は省略する。   Since the catalyst used in the aromatic compound manufacturing method according to Comparative Example 8 of the present invention is the same as the catalyst (Mo-HZSM5) used in Example 2, detailed description of the catalyst manufacturing method is omitted. Further, the catalyst pretreatment and the analysis method of each substance are the same as those in Reference Example 1, and therefore detailed description thereof is omitted. Since the reaction conditions other than the reaction gas are the same as those in Example 4, detailed description is omitted.

図４は、Ｍｏ−ＨＺＳＭ５触媒存在下で、上記実施例２〜４に示した反応条件で触媒反応を連続して行った場合の反応後のガス中におけるベンゼン量の時間変化を示す図である。また、図５は、Ｍｏ−ＨＺＳＭ５触媒存在下で、上記比較例６〜８に示した反応条件で触媒反応を連続して行った場合の反応後のガス中におけるベンゼン量の時間変化を示す図である。   FIG. 4 is a diagram showing the time change of the amount of benzene in the gas after the reaction when the catalytic reaction is continuously performed under the reaction conditions shown in Examples 2 to 4 in the presence of the Mo-HZSM5 catalyst. . FIG. 5 is a graph showing the time change of the amount of benzene in the gas after the reaction when the catalytic reaction is continuously performed under the reaction conditions shown in Comparative Examples 6 to 8 in the presence of the Mo-HZSM5 catalyst. It is.

図４に示すように、一酸化炭素を添加したメタンを触媒に接触反応させた場合、反応温度の上昇に伴い、反応後のガス中における最大ベンゼン量が増加することがわかる。   As shown in FIG. 4, when the methane added with carbon monoxide is contacted with the catalyst, the maximum amount of benzene in the gas after the reaction increases as the reaction temperature rises.

一方、図５に示すように、メタンのみを触媒に接触反応させた場合、反応後のガス中における最大ベンゼン量はほとんど変化していない。   On the other hand, as shown in FIG. 5, when only methane is brought into contact with the catalyst, the maximum amount of benzene in the gas after the reaction hardly changes.

以上、実施例を挙げて示したように、触媒に低級炭化水素を接触反応させて芳香族化合物と水素ガスを製造する際に、接触反応に供される反応ガスに一酸化炭素を添加し、反応温度を８００℃より高くして接触反応を行うことで、触媒活性の低下を抑制するだけでなく、最大ベンゼン収率を向上させることができる。   As described above, as shown in the examples, when producing an aromatic compound and hydrogen gas by catalytically reacting a lower hydrocarbon with a catalyst, carbon monoxide is added to the reaction gas used for the catalytic reaction, By carrying out the contact reaction at a reaction temperature higher than 800 ° C., not only the decrease in catalyst activity can be suppressed, but also the maximum benzene yield can be improved.

一酸化炭素を反応ガスに添加することにより、反応温度の上昇に伴い最大ベンゼン収率が向上するので、流動層反応器での反応のように瞬時に活性の高い反応が求められる反応形態において特に有効である。   By adding carbon monoxide to the reaction gas, the maximum benzene yield increases as the reaction temperature rises. Therefore, especially in reaction modes that require a highly active reaction instantaneously, such as in a fluidized bed reactor. It is valid.

なお、最大ベンゼン収率が向上する効果は、高ＳＶ（空間速度が速い条件）で顕著であり、ＳＶが３０００ｍｌ／ｈｒ／ｇ−ＭＦＩ以上、特にＳＶが５０００ｍｌ／ｈｒ／ｇ−ＭＦＩ以上で接触反応を行うとよい。   The effect of improving the maximum benzene yield is remarkable at high SV (conditions where the space velocity is high), and SV is 3000 ml / hr / g-MFI or higher, especially when SV is 5000 ml / hr / g-MFI or higher. It is better to carry out the reaction.

触媒反応に供されるガスに一酸化炭素を添加した場合と二酸化炭素を添加した場合の芳香族化合物の生成反応の違いについて説明する。   The difference in the formation reaction of the aromatic compound between the case where carbon monoxide is added to the gas used for the catalytic reaction and the case where carbon dioxide is added will be described.

メタン（ＣＨ4）からベンゼン（Ｃ6Ｈ6）と水素（Ｈ2）を生成する反応は（１）式であらわされる。 The reaction for producing benzene (C 6 H 6 ) and hydrogen (H 2 ) from methane (CH 4 ) is represented by the formula (1).

６ＣＨ4 → Ｃ6Ｈ6 ＋ ９Ｈ2 …（１）
また、コーク（Ｃ）が生成する反応は（２）式による反応であると考えられる。 6CH 4 → C 6 H 6 + 9H 2 (1)
Moreover, it is thought that reaction which coke (C) produces | generates is reaction by (2) Formula.

ＣＨ4 → Ｃ ＋ ２Ｈ2 …（２）
また、（１）式と逆の反応によりメタンを生成する反応も生じる（（３）式に示す）。 CH 4 → C + 2H 2 (2)
Moreover, the reaction which produces | generates methane by reaction opposite to (1) Formula also arises (it shows to (3) Formula).

Ｃ6Ｈ6 ＋ ９Ｈ2 → ６ＣＨ4 …（３）
反応ガスに二酸化炭素（ＣＯ2）を添加した場合、（４）式に示すようにコーク除去反応が起こると考えられる。 C 6 H 6 + 9H 2 → 6CH 4 (3)
When carbon dioxide (CO 2 ) is added to the reaction gas, it is considered that a coke removal reaction occurs as shown in equation (4).

ＣＯ2 ＋ Ｃ → ２ＣＯ …（４）
また、（５）式に示すように、二酸化炭素は、メタンと反応して水素を生成すると考えられる。 CO 2 + C → 2CO (4)
Moreover, as shown in the formula (5), carbon dioxide is considered to react with methane to generate hydrogen.

ＣＯ2 ＋ ＣＨ4 → ２ＣＯ ＋ ２Ｈ2 …（５）
したがって、反応ガスに二酸化炭素を添加した場合、（５）式に示した反応により、水素が発生する。（１）式で示したベンゼン生成反応は平衡反応であり、発生した水素により平衡が移動しベンゼンの生成が抑制されてしまうものと考えられる。 CO 2 + CH 4 → 2CO + 2H 2 (5)
Therefore, when carbon dioxide is added to the reaction gas, hydrogen is generated by the reaction shown in the equation (5). The benzene production reaction represented by the formula (1) is an equilibrium reaction, and it is considered that the equilibrium is shifted by the generated hydrogen and the production of benzene is suppressed.

また、二酸化炭素は、（６）式で示すように、モリブデンカーバイド（ＭｏＣ）と反応して、活性種であるモリブデンカーバイドを減少させる場合がある。この反応は、流量が多い場合（例えば、空間速度１００００ｍｌ／ｈｒ／ｇ−ＭＦＩの場合）に起こりやすいものであると考えられている。   Carbon dioxide may react with molybdenum carbide (MoC) to reduce molybdenum carbide, which is an active species, as shown by equation (6). This reaction is considered to occur easily when the flow rate is large (for example, when the space velocity is 10,000 ml / hr / g-MFI).

４ＣＯ2 ＋ ＭｏＣ → ＭｏＯ3 ＋ ５ＣＯ …（６）
一方、一酸化炭素（ＣＯ）を添加することにより、上記（５）式の逆反応が起こり、二酸化炭素が生成する。この二酸化炭素により（４）式で示したコーク除去反応が起こることで、触媒活性の低下を抑制することができるものと考えられる。そして、（５）式の逆反応により水素が消費されることにより、（１）式において平衡が移動し、ベンゼンの生成が促進されるものと考えられる。 4CO 2 + MoC → MoO 3 + 5CO (6)
On the other hand, by adding carbon monoxide (CO), the reverse reaction of the above formula (5) occurs, and carbon dioxide is generated. It is considered that a decrease in catalyst activity can be suppressed by the coke removal reaction represented by the formula (4) caused by this carbon dioxide. Then, it is considered that hydrogen is consumed by the reverse reaction of the formula (5), whereby the equilibrium is shifted in the formula (1) and the generation of benzene is promoted.

また、一酸化炭素は、（７）式で示される反応をするものと考えられている。この反応も平衡反応である。   Carbon monoxide is considered to react by the formula (7). This reaction is also an equilibrium reaction.

ＣＯ → Ｃ ＋ Ｏ …（７）
（７）式で生成した酸素原子（Ｏ）により、反応器中の水素が消費されることにより、（１）式において平衡が移動しベンゼンの生成が促進されるものと考えられる。 CO → C + O (7)
It is considered that the hydrogen in the reactor is consumed by the oxygen atom (O) generated by the equation (7), whereby the equilibrium moves in the equation (1) and the generation of benzene is promoted.

以上のように、本発明に係る低級炭化水素芳香族化触媒を用いた芳香族炭化水素及び水素製造方法によれば、高収率でベンゼン等の芳香族炭化水素を生成することができる。すなわち、反応温度を８００℃より高くし、一酸化炭素を添加することにより、触媒活性を長期にわたって維持できるだけでなく、実用上十分な収率を得ることができる。   As described above, according to the aromatic hydrocarbon and hydrogen production method using the lower hydrocarbon aromatization catalyst according to the present invention, aromatic hydrocarbons such as benzene can be produced in high yield. That is, by making the reaction temperature higher than 800 ° C. and adding carbon monoxide, not only the catalytic activity can be maintained for a long time, but also a practically sufficient yield can be obtained.

すなわち、一酸化炭素を添加することで、難除去性コークの蓄積を抑えることができるだけでなく、触媒反応温度を上昇させることで、メタンのみを添加させた際の最大ベンゼン収率以上の最大ベンゼン収率を得ることができる。一方、ＣＯ2は、芳香族化反応の抑制効果があるので、メタンのみを添加させた際の最大ベンゼン収率以上のベンゼン収率（触媒活性）を得ることができない。 That is, by adding carbon monoxide, it is possible not only to suppress the accumulation of difficult-to-removable coke, but also by increasing the catalytic reaction temperature, the maximum benzene yield that exceeds the maximum benzene yield when only methane is added Yields can be obtained. On the other hand, since CO 2 has an effect of suppressing the aromatization reaction, a benzene yield (catalytic activity) higher than the maximum benzene yield when only methane is added cannot be obtained.

特に、触媒反応工程と触媒再生工程を繰り返すプロセスでは、初期の反応収率が重要となる。本発明の芳香族炭化水素製造方法によれば、高いベンゼン収率を得るとともに、再生除去が難しい析出炭素の生成を抑えることができるので、触媒反応と再生反応を繰り返しても長期にわたり高い触媒活性を維持することができる。   In particular, in the process of repeating the catalyst reaction step and the catalyst regeneration step, the initial reaction yield is important. According to the aromatic hydrocarbon production method of the present invention, it is possible to obtain a high benzene yield and to suppress the formation of precipitated carbon that is difficult to regenerate and remove. Can be maintained.

以上、本発明において、記載された具体例に対してのみ詳細に説明したが、本発明の技術思想の範囲で多彩な変形及び修正が可能であることは、当業者にとって明白なことであり、このような変形及び修正が特許請求の範囲に属することは当然のことである。   Although the present invention has been described in detail only for the specific examples described above, it is obvious to those skilled in the art that various changes and modifications can be made within the scope of the technical idea of the present invention. Such variations and modifications are naturally within the scope of the claims.

本願発明は、低級炭化水素からなる反応ガスに一酸化炭素を添加することでコークの除去を促進し、さらにベンゼン生成率を向上させることを特徴とするものである。したがって、低級炭化水素芳香族化触媒は、メタロシリケートに担持されたモリブデンに限定されるものではなく、既に低級炭化水素の芳香族化合物化触媒としての効果が確認され、文献（例えば、『表面』ｖｏｌ．３７Ｎｏ．１２（１９９９）７１頁〜８１頁「メタンの触媒化学的変換−鋳型ゼオライト触媒を用いるベンゼン直接合成」）等で紹介されている各種触媒金属のうち、レニウム、タングステン、鉄、コバルト、ならびにそれら（モリブデンを含む）の化合物を単独又は組み合わせて用いた場合においても、同様の作用効果が得られることは明らかである。   The present invention is characterized in that coke removal is promoted by adding carbon monoxide to a reaction gas composed of lower hydrocarbons, and the benzene production rate is further improved. Therefore, the lower hydrocarbon aromatization catalyst is not limited to molybdenum supported on a metallosilicate, and has already been confirmed to be effective as an aromatic compound conversion catalyst for lower hydrocarbons (for example, “surface”). vol. 37 No. 12 (1999), pages 71-81 “Catalytic chemical conversion of methane—direct synthesis of benzene using a template zeolite catalyst”), among other various catalytic metals, rhenium, tungsten, iron, cobalt It is clear that similar effects can be obtained even when these compounds (including molybdenum) are used alone or in combination.

また、反応工程と再生工程を繰り返す場合において、反応時間及び再生時間は実施例に限定されるものではなく、適宜触媒活性の変化に基づいて触媒活性が低下する前に反応工程から再生工程に切り替える等、難除去性コークが析出しない時間を設定すればよい。例えば、触媒反応工程において触媒の温度を測定し、温度変化に基づいて触媒反応工程と再生工程を切り替えてもよい。触媒反応工程では、低級炭化水素の芳香族化反応が吸熱反応であるため、反応時に触媒の温度が低下する。そして、触媒の劣化とともに低級炭化水素の芳香族化反応活性も低下するため、触媒の温度変化を測定することにより触媒の劣化度合いを検出することができる。そこで、触媒の温度が上昇し始めた後に反応工程から再生工程に切り替えることで、より効率的に芳香族炭化水素を製造できるとともに触媒の劣化を防止することもできる。触媒の温度が上昇してから再生工程に切り替えることで、再生工程で触媒温度を反応に必要な設定温度まで上昇させるためのエネルギーを節約することもできる。   In addition, when the reaction step and the regeneration step are repeated, the reaction time and the regeneration time are not limited to those in the examples, and are appropriately switched from the reaction step to the regeneration step before the catalyst activity decreases based on the change in the catalyst activity. For example, a time during which hard-to-removable coke does not precipitate may be set. For example, the temperature of the catalyst may be measured in the catalytic reaction step, and the catalytic reaction step and the regeneration step may be switched based on the temperature change. In the catalytic reaction step, since the lower hydrocarbon aromatization reaction is an endothermic reaction, the temperature of the catalyst decreases during the reaction. And since the aromatization reaction activity of a lower hydrocarbon also falls with catalyst deterioration, the deterioration degree of a catalyst is detectable by measuring the temperature change of a catalyst. Therefore, by switching from the reaction step to the regeneration step after the temperature of the catalyst starts to rise, it is possible to produce aromatic hydrocarbons more efficiently and to prevent deterioration of the catalyst. By switching to the regeneration process after the temperature of the catalyst has risen, it is possible to save energy for increasing the catalyst temperature to the set temperature required for the reaction in the regeneration process.

さらに、反応工程と再生工程を繰り返す場合において、再生工程で使用される再生ガスは、水素に限定されるものではなく、一酸化炭素等の還元性ガスを含んでいれば適宜用いることができる。   Furthermore, when the reaction step and the regeneration step are repeated, the regeneration gas used in the regeneration step is not limited to hydrogen, and can be appropriately used as long as it contains a reducing gas such as carbon monoxide.

Claims (4)

メタロシリケートにモリブデンを担持した触媒と低級炭化水素とを接触反応させ、芳香族炭化水素を主成分とする芳香族化合物及び水素を製造する方法であって、
前記低級炭化水素に前記触媒の活性低下を抑制するガスとして一酸化炭素のみを添加し、反応温度を８００℃より高くして、５０００ｍｌ／ｈｒ／ｇ−ＭＦＩ以上の空間速度で前記触媒に接触反応させる
ことを特徴とする芳香族化合物製造方法。 A method for producing an aromatic compound and hydrogen containing an aromatic hydrocarbon as a main component by catalytically reacting a catalyst supporting molybdenum on a metallosilicate with a lower hydrocarbon,
Only carbon monoxide is added to the lower hydrocarbon as a gas that suppresses the decrease in the activity of the catalyst, the reaction temperature is raised above 800 ° C., and the catalyst is contacted with the catalyst at a space velocity of 5000 ml / hr / g-MFI or higher. A process for producing an aromatic compound, comprising: 前記一酸化炭素濃度は、反応ガスに対して０．７５％〜２０％である
ことを特徴とする請求項１に記載の芳香族化合物製造方法。 2. The method for producing an aromatic compound according to claim 1, wherein the carbon monoxide concentration is 0.75% to 20% with respect to the reaction gas. 前記反応温度は、８２０℃以上である
ことを特徴とする請求項１または請求項２に記載の芳香族化合物製造方法。 The said reaction temperature is 820 degreeC or more, The aromatic compound manufacturing method of Claim 1 or Claim 2 characterized by the above-mentioned. 前記低級炭化水素を前記触媒と接触反応させる反応工程と、前記反応工程で使用された触媒を再生する再生工程を繰り返すことにより前記芳香族化合物を製造する
ことを特徴とする請求項１から請求項３のいずれか１項に記載の芳香族化合物製造方法。 2. The aromatic compound is produced by repeating a reaction step in which the lower hydrocarbon is brought into contact with the catalyst and a regeneration step in which the catalyst used in the reaction step is regenerated. 4. The method for producing an aromatic compound according to any one of 3 above.
JP2014262765A 2014-12-25 2014-12-25 Method for producing aromatic hydrocarbon Pending JP2015063560A (en)