JP2014237763A - Adhesive composition, self-adhesive film using the same, and surface protective film using the same - Google Patents

Adhesive composition, self-adhesive film using the same, and surface protective film using the same Download PDF

Info

Publication number
JP2014237763A
JP2014237763A JP2013121074A JP2013121074A JP2014237763A JP 2014237763 A JP2014237763 A JP 2014237763A JP 2013121074 A JP2013121074 A JP 2013121074A JP 2013121074 A JP2013121074 A JP 2013121074A JP 2014237763 A JP2014237763 A JP 2014237763A
Authority
JP
Japan
Prior art keywords
film
pressure
sensitive adhesive
group
composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2013121074A
Other languages
Japanese (ja)
Other versions
JP6630933B2 (en
Inventor
毅 長倉
Takeshi Nagakura
毅 長倉
龍介 島口
Ryusuke Shimaguchi
龍介 島口
良 長谷川
Makoto Hasegawa
良 長谷川
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujimori Kogyo Co Ltd
Original Assignee
Fujimori Kogyo Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujimori Kogyo Co Ltd filed Critical Fujimori Kogyo Co Ltd
Priority to JP2013121074A priority Critical patent/JP6630933B2/en
Priority to KR1020140060076A priority patent/KR101631826B1/en
Priority to CN201410232710.7A priority patent/CN104231982B/en
Priority to TW103119257A priority patent/TWI548720B/en
Publication of JP2014237763A publication Critical patent/JP2014237763A/en
Application granted granted Critical
Publication of JP6630933B2 publication Critical patent/JP6630933B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide an adhesive composition which has excellent antistatic performance, and is excellent in compatibility to an adhesive mass so that faults in rework ability such as bleed out and contamination generated on an adherend when a self-adhesive film is peeled therefrom are improved, a self-adhesive film, and a surface protective film.SOLUTION: The adhesive composition has antistatic performance. As an antistatic agent, a hydrophobic quaternary onium salt whose melting point is 30-50°C is included. The self-adhesive film and the surface protective film are characterized in that the adhesive agent layer is laminated respectively by using the adhesive composition.

Description

本発明は、帯電防止性能を有する粘着剤組成物、粘着フィルム及び表面保護フィルムに関する。さらに詳細には、帯電防止剤として、疎水性の4級オニウム塩を含有する粘着剤組成物に関し、粘着性能を損なわずに帯電防止性に優れた粘着剤組成物、それを用いた粘着フィルム及び表面保護フィルムを提供することに関するものである。   The present invention relates to an adhesive composition, an adhesive film and a surface protective film having antistatic performance. More specifically, the present invention relates to a pressure-sensitive adhesive composition containing a hydrophobic quaternary onium salt as an antistatic agent, a pressure-sensitive adhesive composition having excellent antistatic properties without impairing the pressure-sensitive adhesive performance, a pressure-sensitive adhesive film using the same The present invention relates to providing a surface protective film.

従来から、液晶ディスプレイを構成する部材である偏光板、位相差板、反射防止フィルムなどの光学部材の製造工程においては、光学部材の表面を一時的に保護するための表面保護フィルムが貼着される。このような表面保護フィルムは、光学部材を製造する工程のみに使用され、光学部材を液晶ディスプレイに組み込む時点で、光学部材から剥離して除去される。このような光学部材の表面を保護するための表面保護フィルムは、製造工程においてのみに使用されるため、一般には、工程フィルムと呼ばれることもある。   Conventionally, in the production process of optical members such as polarizing plates, retardation plates, and antireflection films, which are members constituting a liquid crystal display, a surface protective film for temporarily protecting the surface of the optical member has been attached. The Such a surface protective film is used only in the process of manufacturing the optical member, and is peeled off from the optical member when the optical member is incorporated into the liquid crystal display. Since such a surface protective film for protecting the surface of the optical member is used only in the production process, it may be generally called a process film.

このように、光学部材を製造する工程において使用される表面保護フィルムは、光学的に透明性を有するポリエチレンテレフタレート(PET)樹脂フィルムの片面に粘着剤層が形成されているが、光学部材に貼り合わせるまで、その粘着剤層を保護するための剥離処理された剥離フィルムが、粘着剤層の上に貼り合わされている。
また、偏光板、位相差板、反射防止フィルムなどの光学部材は、表面保護フィルムを貼り合わされた状態で、液晶表示板の表示能力、色相、コントラスト、異物混入などの光学的評価を伴う製品検査を行うため、表面保護フィルムに対する要求性能としては、粘着剤層に気泡や異物が付着していないことが求められている。
また、近年では、偏光板、位相差板、反射防止フィルムなどの光学部材から表面保護フィルムを剥がすときに、粘着剤層を被着体が剥がす時に発生する静電気に伴って生じる剥離帯電が、液晶ディスプレイの電気制御回路の故障に影響することが懸念され、粘着剤層に対して優れた帯電防止性能が求められている。
また、偏光板、位相差板、反射防止フィルムなどの光学部材に表面保護フィルムを貼り合わせるときには、各種の理由により、一旦、表面保護フィルムを剥がして、再度、表面保護フィルムを貼り直すことがあり、そのときに被着体の光学部材から剥がし易いこと(リワーク性)が求められている。また、このとき、被着体を汚染しないこと、いわゆる糊残りが起こらないことが求められている。
また、最終的に偏光板、位相差、反射防止フィルム板などの光学部材から表面保護フィルムを剥がすときには、速やかに剥離できることが求められている。いわゆる、高速度での剥離によっても、速やかに剥離できるように、粘着力が剥離速度によっても変化が少ないことが求められている。
As described above, the surface protective film used in the process of manufacturing the optical member has a pressure-sensitive adhesive layer formed on one side of an optically transparent polyethylene terephthalate (PET) resin film. Until it puts together, the peeling film by which the peeling process for protecting the adhesive layer was bonded on the adhesive layer.
In addition, optical members such as polarizing plates, retardation plates, and antireflection films are inspected for products with optical evaluations such as display performance, hue, contrast, and foreign matter contamination of the liquid crystal display panel with the surface protective film attached. Therefore, as the required performance for the surface protective film, it is required that no bubbles or foreign substances adhere to the pressure-sensitive adhesive layer.
Further, in recent years, when the surface protective film is peeled off from an optical member such as a polarizing plate, a phase difference plate, or an antireflection film, the peeling charge generated along with the static electricity generated when the adherend peels off the adhesive layer is liquid crystal. There is a concern that it may affect the failure of the electric control circuit of the display, and excellent antistatic performance is required for the adhesive layer.
In addition, when a surface protective film is bonded to an optical member such as a polarizing plate, a retardation plate, or an antireflection film, the surface protective film may be peeled off and then reattached for various reasons. At that time, it is required to be easily peeled off from the optical member of the adherend (reworkability). At this time, it is required that the adherend is not contaminated, that is, so-called adhesive residue does not occur.
Moreover, when peeling a surface protection film from optical members, such as a polarizing plate, a phase difference, and an antireflection film board finally, being able to peel rapidly is calculated | required. It is required that the adhesive force change little depending on the peeling speed so that it can be peeled quickly even by so-called high-speed peeling.

例えば、優れた帯電防止性能については、表面保護フィルムに帯電防止性を付与させるための方法として、基材フィルムに帯電防止剤を練り込む方法などが示されている。
帯電防止剤としては、例えば、(a)第4級アンモニウム塩、ピリジニウム塩、第1〜3級アミノ基などのカチオン性基を有する各種のカチオン性帯電防止剤、(b)スルホン酸塩基、硫酸エステル塩基、リン酸エステル塩基、ホスホン酸塩基などのアニオン性基を有するアニオン性帯電防止剤、(c)アミノ酸系、アミノ硫酸エステル系などの両性帯電防止剤、(d)アミノアルコール系、グリセリン系、ポリエチレングリコール系などのノニオン性帯電防止剤、(e)上記の様な帯電防止剤を高分子量化した高分子型帯電防止剤、などが開示されている(特許文献1)。
また、近年では、このような帯電防止剤を基材フィルムに含有させたり、あるいは基材フィルムの表面に塗布するのではなく、直接に粘着剤層に含有させたりすることが提案されている。
For example, with regard to excellent antistatic performance, a method of kneading an antistatic agent into the base film is shown as a method for imparting antistatic properties to the surface protective film.
Examples of the antistatic agent include (a) various cationic antistatic agents having a cationic group such as a quaternary ammonium salt, a pyridinium salt, and a primary to tertiary amino group, and (b) a sulfonate group, sulfuric acid. Anionic antistatic agents having anionic groups such as ester bases, phosphate ester bases, phosphonic acid bases, (c) amphoteric antistatic agents such as amino acid series and aminosulfate ester series, (d) amino alcohol series, glycerin series Nonionic antistatic agents such as polyethylene glycols, and (e) polymeric antistatic agents obtained by increasing the molecular weight of the antistatic agents as described above are disclosed (Patent Document 1).
Further, in recent years, it has been proposed that such an antistatic agent is contained in the base film or directly in the pressure-sensitive adhesive layer rather than being applied to the surface of the base film.

また、リワーク性能については、例えば、アクリル樹脂中に、イソシアネート系化合物の硬化剤と、特定のシリケートオリゴマーをアクリル系樹脂100重量部に対して0.0001〜10重量部で配合した粘着剤組成物が提案されている(特許文献2)。
特許文献2では、アルキル基の炭素数が2〜12程度のアクリル酸アルキルエステルやアルキル基の炭素数が4〜12程度のメタクリル酸アルキルエステル等を主モノマー成分とし、例えば、カルボキシル基含有モノマーなどの他の官能基含有モノマー成分を含むことができるとしている。一般的には、上記主モノマーを50重量%以上含有させることが好ましい、又、官能基含有モノマー成分の含有量は0.001〜50重量%であって、好ましくは0.001〜25重量%、更に好ましくは0.01〜25重量%であることが望まれる、としている。このような特許文献2に記載の粘着剤組成物は、高温下又は高温高湿下でも凝集力及び接着力の経時変化が小さく、かつ、曲面に対する接着力にも優れた効果を示すことから、リワーク性を有するとしている。
一般に、粘着剤層を柔らかい性状のものにすると、糊残りが発生し易くなり、リワーク性が低下し易い。すなわち、誤って貼合したときに剥離し難く、貼り直しが困難となり易い。このことから、カルボキシル基などの官能基を有するモノマーを主剤に架橋させて、粘着剤層を一定の硬さにすることが、リワーク性を持たせるためには必要と考えられる。
As for the rework performance, for example, an adhesive composition in which an isocyanate compound curing agent and a specific silicate oligomer are mixed in an acrylic resin in an amount of 0.0001 to 10 parts by weight with respect to 100 parts by weight of the acrylic resin. Has been proposed (Patent Document 2).
In Patent Document 2, an acrylic acid alkyl ester having an alkyl group having about 2 to 12 carbon atoms, an alkyl group having about 4 to 12 carbon atoms and an alkyl group having about 4 to 12 carbon atoms as a main monomer component, for example, a carboxyl group-containing monomer, etc. Other functional group-containing monomer components can be included. Generally, the main monomer is preferably contained in an amount of 50% by weight or more, and the content of the functional group-containing monomer component is 0.001 to 50% by weight, preferably 0.001 to 25% by weight. More preferably, it is desired to be 0.01 to 25% by weight. Since the pressure-sensitive adhesive composition described in Patent Document 2 has a small change over time in cohesive force and adhesive force even at high temperature or high temperature and high humidity, and exhibits an excellent effect on adhesive force to a curved surface, It has reworkability.
In general, when the pressure-sensitive adhesive layer has a soft property, adhesive residue is likely to be generated, and reworkability is likely to be reduced. That is, it is difficult to peel off when it is mistakenly bonded, and it is difficult to reattach. From this, it is considered necessary to make the pressure-sensitive adhesive layer have a certain hardness by crosslinking a monomer having a functional group such as a carboxyl group to the main agent in order to have reworkability.

特開平11−070629号公報Japanese Patent Laid-Open No. 11-070629 特開平8−199130号公報JP-A-8-199130

上述したように、粘着フィルムとして帯電防止機能を求められることが多く、色々な種類の帯電防止剤が試みられてきた。しかし、特に光学フィルムの用途においては、帯電防止機能は持たせることができるが、透明性が悪いなどの欠点があり、さらには帯電防止剤の粘着剤への相溶性不足などから帯電防止剤のブリードアウトや粘着フィルムを剥がした際に、被着体に汚染が生じてしまうなどのリワーク性が悪い等の欠点が多かった。これら、性能を満足できても、コストが高くなってしまうなどの問題もあり、低コストでこれら欠点を克服出来る帯電防止剤を含んだ粘着剤が必要とされて来た。   As described above, an antistatic function is often required as an adhesive film, and various types of antistatic agents have been tried. However, particularly in the use of an optical film, it can be provided with an antistatic function, but there are drawbacks such as poor transparency, and further, the antistatic agent is not compatible due to lack of compatibility of the antistatic agent with the adhesive. There were many drawbacks such as poor reworkability, such as contamination of the adherend when the bleed out or adhesive film was peeled off. Even if these performances can be satisfied, there is a problem that the cost becomes high, and an adhesive containing an antistatic agent that can overcome these drawbacks at low cost has been required.

本発明は、上記の事情に鑑みてなされたものであり、優れた帯電防止性能を備え、粘着剤との相溶性に優れるためブリードアウトや粘着フィルムを剥がした際に、被着体に汚染が生じてしまうなどのリワーク性の欠点を改善した、粘着剤組成物、粘着フィルム、及び表面保護フィルムを提供することを課題とする。   The present invention has been made in view of the above circumstances, and has excellent antistatic performance and is excellent in compatibility with the pressure-sensitive adhesive, so that the adherend is contaminated when the bleed-out or pressure-sensitive adhesive film is peeled off. It is an object of the present invention to provide a pressure-sensitive adhesive composition, a pressure-sensitive adhesive film, and a surface protective film, which have improved reworkability defects such as occurrence.

前記課題を解決するため、本発明は、帯電防止性能を有する粘着剤組成物であって、帯電防止剤として、融点30〜50℃の疎水性の4級オニウム塩を含有することを特徴とする粘着剤組成物を提供する。   In order to solve the above-mentioned problems, the present invention is a pressure-sensitive adhesive composition having antistatic performance, characterized by containing a hydrophobic quaternary onium salt having a melting point of 30 to 50 ° C. as an antistatic agent. An adhesive composition is provided.

前記4級オニウム塩が、25℃の水100gに対する溶解度が5g以下であることが好ましい。   The quaternary onium salt preferably has a solubility in 100 g of water at 25 ° C. of 5 g or less.

粘着剤成分が、(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーの少なくとも1種と、(B)水酸基および/またはカルボキシル基を含有する共重合性ビニルモノマーの少なくとも1種と、からなる共重合組成物であり、前記共重合組成物の100重量部に対して、(C)前記4級オニウム塩を0.1〜10重量部、を必須成分として含有することが好ましい。   The pressure-sensitive adhesive component is a copolymerizable vinyl monomer containing (A) at least one (meth) acrylic acid alkyl ester monomer having a C1-C14 alkyl group and (B) a hydroxyl group and / or a carboxyl group. And a copolymer composition comprising at least one kind, and (C) 0.1 to 10 parts by weight of the quaternary onium salt as an essential component with respect to 100 parts by weight of the copolymer composition. It is preferable.

粘着剤成分が、(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーの少なくとも1種と、ビニル基を有する共重合性ビニルモノマーの少なくとも1種と、からなる共重合組成物であり、前記共重合組成物の100重量部に対して、(C)前記4級オニウム塩を0.1〜10重量部、を必須成分として含有することが好ましい。   The adhesive component comprises (A) at least one alkyl (meth) acrylic acid alkyl ester monomer having a C1-C14 alkyl group and at least one copolymerizable vinyl monomer having a vinyl group. It is a polymerization composition, and preferably contains (C) 0.1 to 10 parts by weight of the quaternary onium salt as an essential component with respect to 100 parts by weight of the copolymer composition.

粘着剤成分が、(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーの少なくとも2種以上からなる共重合組成物であり、前記共重合組成物の100重量部に対して、(C)前記4級オニウム塩を0.1〜10重量部、を必須成分として含有することが好ましい。   The pressure-sensitive adhesive component is a copolymer composition composed of (A) at least two kinds of (meth) acrylic acid alkyl ester monomers having C1-C14 carbon atoms in the alkyl group, and 100 parts by weight of the copolymer composition On the other hand, it is preferable to contain (C) 0.1 to 10 parts by weight of the quaternary onium salt as an essential component.

粘着剤成分が、(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーの少なくとも1種と、芳香族系モノマーの少なくとも1種と、からなる共重合組成物であり、前記共重合組成物の100重量部に対して、(C)前記4級オニウム塩を0.1〜10重量部、を必須成分として含有することが好ましい。   The pressure-sensitive adhesive component is a copolymer composition comprising (A) at least one of (meth) acrylic acid alkyl ester monomers having C1-C14 carbon atoms and at least one aromatic monomer. It is preferable to contain 0.1 to 10 parts by weight of (C) the quaternary onium salt as an essential component with respect to 100 parts by weight of the copolymer composition.

基材の片面上に、前記粘着剤組成物を積層して形成された粘着剤層において、前記粘着剤層の表面抵抗率が1.0×10+12Ω/□以下であることが好ましい。 In the pressure-sensitive adhesive layer formed by laminating the pressure-sensitive adhesive composition on one side of the substrate, the surface resistivity of the pressure-sensitive adhesive layer is preferably 1.0 × 10 +12 Ω / □ or less.

また、本発明は、基材の片面上に、前記粘着剤組成物を用いて粘着剤層が積層されたことを特徴とする粘着フィルムを提供する。   Moreover, this invention provides the adhesive film characterized by the adhesive layer having been laminated | stacked on the single side | surface of the base material using the said adhesive composition.

また、本発明は、前記粘着剤組成物を用いて粘着剤層が積層されたことを特徴とする粘着フィルムを提供する。   Moreover, this invention provides the adhesive film characterized by the adhesive layer being laminated | stacked using the said adhesive composition.

また、本発明は、前記粘着フィルムが用いられた、表面保護フィルムを提供する。   Moreover, this invention provides the surface protection film using the said adhesive film.

また、本発明は、前記粘着フィルムが用いられた、偏光板用の表面保護フィルムを提供する。   Moreover, this invention provides the surface protection film for polarizing plates in which the said adhesive film was used.

また、本発明は、前記粘着フィルムが用いられた、光学用の表面保護フィルムを提供する。   Moreover, this invention provides the surface protection film for optics using the said adhesive film.

また、本発明は、前記粘着フィルムが用いられた偏光板とディスプレイパネルの貼り合わせ用フィルムを提供する。   Moreover, this invention provides the film for bonding of the polarizing plate using the said adhesive film, and a display panel.

また、本発明は、前記粘着フィルムが用いられた偏光板を構成する材料の貼り合わせ用フィルムを提供する。   Moreover, this invention provides the film for bonding of the material which comprises the polarizing plate in which the said adhesive film was used.

また、本発明は、前記粘着フィルムが用いられたタッチパネル用フィルムを提供する。   Moreover, this invention provides the film for touchscreens in which the said adhesive film was used.

また、本発明は、前記粘着フィルムが用いられた電子ペーパー用フィルムを提供する。   Moreover, this invention provides the film for electronic papers in which the said adhesive film was used.

本発明によれば、融点30〜50℃の疎水性の4級オニウム塩を帯電防止成分として粘着剤に併用することで、粘着剤との相溶性に優れるためブリードアウトや粘着フィルムを剥がした際に、被着体に汚染が生じてしまうなどのリワーク性の欠点である課題を改善することが可能となる。   According to the present invention, when a hydrophobic quaternary onium salt having a melting point of 30 to 50 ° C. is used together with an adhesive as an antistatic component, it has excellent compatibility with the adhesive, and therefore when the bleedout or adhesive film is peeled off In addition, it is possible to improve the problems that are disadvantages of reworkability such as contamination of the adherend.

以下、好適な実施の形態に基づいて本発明を説明する。
本発明の粘着剤組成物は、帯電防止性能を有する粘着剤組成物であって、帯電防止剤として、融点30〜50℃の疎水性の4級オニウム塩を含有することを特徴とする。
Hereinafter, the present invention will be described based on preferred embodiments.
The pressure-sensitive adhesive composition of the present invention is a pressure-sensitive adhesive composition having antistatic properties, and contains a hydrophobic quaternary onium salt having a melting point of 30 to 50 ° C. as an antistatic agent.

本発明の粘着剤組成物に用いる粘着剤成分としては、アクリル系共重合体などの共重合組成物が好ましい。特に、(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーの少なくとも1種を主成分とする共重合体が好ましい。
(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーとしては、メチル(メタ)アクリレート、エチル(メタ)アクリレート、プロピル(メタ)アクリレート、ブチル(メタ)アクリレート、イソブチル(メタ)アクリレート、ペンチル(メタ)アクリレート、ヘキシル(メタ)アクリレート、ヘプチル(メタ)アクリレート、オクチル(メタ)アクリレート、イソオクチル(メタ)アクリレート、2−エチルヘキシル(メタ)アクリレート、ノニル(メタ)アクリレート、イソノニル(メタ)アクリレート、デシル(メタ)アクリレート、シクロペンチル(メタ)アクリレート、シクロヘキシル(メタ)アクリレート等のアルキル(メタ)アクリレートモノマーが挙げられる。アルキル(メタ)アクリレートモノマーのアルキル基は、直鎖、分枝状、環状のいずれでもよい。
As the pressure-sensitive adhesive component used in the pressure-sensitive adhesive composition of the present invention, a copolymer composition such as an acrylic copolymer is preferable. In particular, (A) a copolymer mainly containing at least one (meth) acrylic acid alkyl ester monomer having C1-C14 carbon atoms in the alkyl group is preferred.
(A) Alkyl group C1-C14 (meth) acrylic acid alkyl ester monomers include methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, butyl (meth) acrylate, isobutyl ( (Meth) acrylate, pentyl (meth) acrylate, hexyl (meth) acrylate, heptyl (meth) acrylate, octyl (meth) acrylate, isooctyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, nonyl (meth) acrylate, isononyl ( Examples include alkyl (meth) acrylate monomers such as (meth) acrylate, decyl (meth) acrylate, cyclopentyl (meth) acrylate, and cyclohexyl (meth) acrylate. The alkyl group of the alkyl (meth) acrylate monomer may be linear, branched or cyclic.

本発明に用いる粘着剤成分の共重合組成物として、(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーの少なくとも1種と、他の共重合性モノマーの少なくとも1種とからなる共重合組成物を採用することもできる。この場合、他の共重合性モノマーとしては、ビニル基を有する共重合性ビニルモノマーや、(B)水酸基および/またはカルボキシル基を含有する共重合性ビニルモノマー、芳香族系モノマーが挙げられる。   As a copolymer composition of the pressure-sensitive adhesive component used in the present invention, at least one of (A) (meth) acrylic acid alkyl ester monomers having a C1-C14 alkyl group and at least one other copolymerizable monomer is used. A copolymer composition comprising seeds can also be employed. In this case, examples of the other copolymerizable monomer include a copolymerizable vinyl monomer having a vinyl group, (B) a copolymerizable vinyl monomer containing a hydroxyl group and / or a carboxyl group, and an aromatic monomer.

水酸基を含有する共重合性ビニルモノマーとしては、2−ヒドロキシエチル(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、3−ヒドロキシプロピル(メタ)アクリレート、4−ヒドロキシブチル(メタ)アクリレート、6−ヒドロキシヘキシル(メタ)アクリレート、8−ヒドロキシオクチル(メタ)アクリレート等の水酸基含有(メタ)アクリル酸エステル類や、N−ヒドロキシ(メタ)アクリルアミド、N−ヒドロキシメチル(メタ)アクリルアミド、N−ヒドロキシエチル(メタ)アクリルアミド等の水酸基含有(メタ)アクリルアミド類などが挙げられ、これらの化合物群の中から選択された、少なくとも1種以上であることが好ましい。
カルボキシル基を含有する共重合性ビニルモノマーとしては、(メタ)アクリル酸、イタコン酸、クロトン酸、マレイン酸、フマル酸、カルボキシエチル(メタ)アクリレート、カルボキシペンチル(メタ)アクリレートからなどが挙げられ、これらの化合物群の中から選択された、少なくとも1種以上であることが好ましい。
芳香族系モノマーとしては、ベンジル(メタ)アクリレート、フェノキシエチル(メタ)アクリレート等の芳香族基含有(メタ)アクリル酸エステル類のほか、スチレン等が挙げられる。
上記以外の共重合性ビニルモノマーとしては、アクリルアミド、アクリロニトリル、メチルビニルエーテル、エチルビニルエーテル、酢酸ビニル、塩化ビニルなどの各種ビニルモノマーが挙げられる。
Examples of the copolymerizable vinyl monomer containing a hydroxyl group include 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 3-hydroxypropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, 6- Hydroxyl-containing (meth) acrylic esters such as hydroxyhexyl (meth) acrylate and 8-hydroxyoctyl (meth) acrylate, N-hydroxy (meth) acrylamide, N-hydroxymethyl (meth) acrylamide, N-hydroxyethyl ( Examples include hydroxyl group-containing (meth) acrylamides such as (meth) acrylamide, and at least one selected from these compound groups is preferable.
Examples of the copolymerizable vinyl monomer containing a carboxyl group include (meth) acrylic acid, itaconic acid, crotonic acid, maleic acid, fumaric acid, carboxyethyl (meth) acrylate, carboxypentyl (meth) acrylate, and the like. Preferably, at least one selected from these compound groups is used.
Examples of the aromatic monomer include styrene and the like in addition to aromatic group-containing (meth) acrylic esters such as benzyl (meth) acrylate and phenoxyethyl (meth) acrylate.
Examples of copolymerizable vinyl monomers other than the above include various vinyl monomers such as acrylamide, acrylonitrile, methyl vinyl ether, ethyl vinyl ether, vinyl acetate, and vinyl chloride.

また、本発明に用いる粘着剤成分の共重合組成物として、
(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーの少なくとも1種と、(B)水酸基および/またはカルボキシル基を含有する共重合性ビニルモノマーの少なくとも1種と、からなる共重合組成物、
(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーの少なくとも1種と、ビニル基を有する共重合性ビニルモノマーの少なくとも1種と、からなる共重合組成物
(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーの少なくとも1種と、芳香族系モノマーの少なくとも1種と、からなる共重合組成物、
(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーの少なくとも1種と、(B)水酸基および/またはカルボキシル基を含有する共重合性ビニルモノマーの少なくとも1種と、芳香族系モノマーの少なくとも1種と、からなる共重合組成物、等が挙げられる。
また、(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーの少なくとも2種以上からなる共重合組成物を採用することもできる。この場合、(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマー以外の共重合性ビニルモノマーを用いなくても共重合組成物とすることができる。
Moreover, as a copolymer composition of the pressure-sensitive adhesive component used in the present invention,
(A) at least one of (meth) acrylic acid alkyl ester monomers having C1-C14 carbon atoms in the alkyl group, and (B) at least one copolymerizable vinyl monomer containing a hydroxyl group and / or a carboxyl group, A copolymer composition comprising:
(A) Copolymer composition comprising at least one (meth) acrylic acid alkyl ester monomer having a C1-C14 alkyl group and at least one copolymerizable vinyl monomer having a vinyl group (A) ) A copolymer composition comprising at least one (meth) acrylic acid alkyl ester monomer having a C1-C14 alkyl group and at least one aromatic monomer;
(A) at least one of (meth) acrylic acid alkyl ester monomers having C1-C14 carbon atoms in the alkyl group, and (B) at least one copolymerizable vinyl monomer containing a hydroxyl group and / or a carboxyl group, And a copolymer composition comprising at least one aromatic monomer.
Moreover, the copolymer composition which consists of (A) at least 2 or more types of the (meth) acrylic-acid alkylester monomer whose carbon number of an alkyl group is C1-C14 is also employable. In this case, the copolymer composition can be obtained without using a copolymerizable vinyl monomer other than the (meth) acrylic acid alkyl ester monomer having (A) an alkyl group having C1 to C14 carbon atoms.

アクリル系共重合体等の共重合組成物の重合方法は、特に限定されるものではなく、溶液重合法、乳化重合法等、適宜、公知の重合方法が使用可能である。アクリル系共重合体の重量平均分子量は、20万〜200万であることが好ましい。   The polymerization method of the copolymer composition such as an acrylic copolymer is not particularly limited, and a known polymerization method such as a solution polymerization method or an emulsion polymerization method can be used as appropriate. The weight average molecular weight of the acrylic copolymer is preferably 200,000 to 2,000,000.

本発明の粘着剤組成物は、粘着剤層を形成する際に前記共重合組成物を架橋することが好ましい。架橋をするため、粘着剤組成物が既知の架橋剤を含んでも良く、紫外線(UV)など光架橋で架橋しても良い。架橋剤としては、2官能以上のイソシアネート系架橋剤、2官能以上のエポキシ系架橋剤、アルミニウムキレート系架橋剤からなる化合物群のうちから選択される1種以上の架橋剤が好ましい。架橋剤を用いる場合は、前記共重合組成物の100重量部に対して、0.1〜5重量部含有することが好ましい。   The pressure-sensitive adhesive composition of the present invention preferably crosslinks the copolymer composition when forming the pressure-sensitive adhesive layer. In order to perform crosslinking, the pressure-sensitive adhesive composition may contain a known crosslinking agent, or may be crosslinked by photocrosslinking such as ultraviolet (UV). As the crosslinking agent, one or more kinds of crosslinking agents selected from the group consisting of a bifunctional or higher functional isocyanate crosslinking agent, a bifunctional or higher epoxy crosslinking agent, and an aluminum chelate crosslinking agent are preferable. When using a crosslinking agent, it is preferable to contain 0.1-5 weight part with respect to 100 weight part of the said copolymer composition.

本発明の粘着剤組成物は、帯電防止性能を付与するため、帯電防止剤を含有する。帯電防止剤は、常温(例えば30℃)で固体であることが好ましく、より具体的には、帯電防止剤の融点が、30〜50℃のイオン化合物である。本発明は、帯電防止剤として、融点30〜50℃の疎水性の4級オニウム塩を含有することを特徴とする。
これらの帯電防止剤は、融点が低いため、また、長鎖のアルキル基を有するため、アクリル系ポリマーとの親和性は高いと推測される。
The pressure-sensitive adhesive composition of the present invention contains an antistatic agent in order to impart antistatic performance. The antistatic agent is preferably solid at room temperature (for example, 30 ° C.), and more specifically, is an ionic compound having a melting point of 30 to 50 ° C. The present invention is characterized by containing a hydrophobic quaternary onium salt having a melting point of 30 to 50 ° C. as an antistatic agent.
Since these antistatic agents have a low melting point and have long-chain alkyl groups, it is presumed that they have a high affinity with acrylic polymers.

融点30〜50℃の疎水性の4級オニウム塩である帯電防止剤としては、例えば、炭素数8〜18のアルキル基を有するアルキルジメチルベンジルアンモニウム塩、炭素数8〜18のアルキル基を有するジアルキルメチルベンジルアンモニウム塩、炭素数8〜18のアルキル基を有するトリアルキルベンジルアンモニウム塩、炭素数8〜18のアルキル基を有するテトラアルキルアンモニウム塩、炭素数8〜18のアルキル基を有するアルキルジメチルベンジルホスホニウム塩、炭素数8〜18のアルキル基を有するジアルキルメチルベンジルホスホニウム塩、炭素数8〜18のアルキル基を有するトリアルキルベンジルホスホニウム塩、炭素数8〜18のアルキル基を有するテトラアルキルホスホニウム塩、炭素数14〜20のアルキル基を有するアルキルトリメチルアンモニウム塩、炭素数14〜20のアルキル基を有するアルキルジメチルエチルアンモニウム塩などの、水に難溶性の4級オニウム塩の中から、融点30〜50℃のものを選択して用いることができる。これらのアルキル基は、不飽和結合を有するアルケニル基であってもよい。   Examples of the antistatic agent that is a hydrophobic quaternary onium salt having a melting point of 30 to 50 ° C. include, for example, an alkyldimethylbenzylammonium salt having an alkyl group having 8 to 18 carbon atoms, and a dialkyl having an alkyl group having 8 to 18 carbon atoms. Methylbenzylammonium salt, trialkylbenzylammonium salt having an alkyl group having 8 to 18 carbon atoms, tetraalkylammonium salt having an alkyl group having 8 to 18 carbon atoms, alkyldimethylbenzylphosphonium having an alkyl group having 8 to 18 carbon atoms Salt, dialkylmethylbenzylphosphonium salt having an alkyl group having 8 to 18 carbon atoms, trialkylbenzylphosphonium salt having an alkyl group having 8 to 18 carbon atoms, tetraalkylphosphonium salt having an alkyl group having 8 to 18 carbon atoms, carbon 14 to 20 alkyl groups Select one having a melting point of 30 to 50 ° C. from quaternary onium salts that are hardly soluble in water, such as alkyltrimethylammonium salt having alkyl group and alkyldimethylethylammonium salt having alkyl group having 14 to 20 carbon atoms. Can do. These alkyl groups may be alkenyl groups having an unsaturated bond.

炭素数8〜18のアルキル基としては、オクチル基、ノニル基、デシル基、ドデシル基、トリデシル基、テトラデシル基、ペンタデシル基、ヘキサデシル基、ヘプタデシル基、オクタデシル基などが挙げられる。天然油脂に由来する混合アルキル基であってもよい。炭素数8〜18のアルケニル基としては、オクテニル基、ノネニル基、デセニル基、ドデセニル基、トリデセニル基、テトラデセニル基、ペンタデセニル基、ヘキサデセニル基、ヘプタデセニル基、オクタデセニル基、オレイル基、リノレイル基などが挙げられる。
炭素数14〜20のアルキル基としては、テトラデシル基、ペンタデシル基、ヘキサデシル基、ヘプタデシル基、オクタデシル基、ノナデシル基、イコシル基などが挙げられる。天然油脂に由来する混合アルキル基であってもよい。炭素数14〜20のアルケニル基としては、テトラデセニル基、ペンタデセニル基、ヘキサデセニル基、ヘプタデセニル基、オクタデセニル基、オレイル基、リノレイル基、ノナデセニル基、イコセニル基などが挙げられる。
Examples of the alkyl group having 8 to 18 carbon atoms include octyl group, nonyl group, decyl group, dodecyl group, tridecyl group, tetradecyl group, pentadecyl group, hexadecyl group, heptadecyl group, and octadecyl group. It may be a mixed alkyl group derived from natural fats and oils. Examples of the alkenyl group having 8 to 18 carbon atoms include octenyl group, nonenyl group, decenyl group, dodecenyl group, tridecenyl group, tetradecenyl group, pentadecenyl group, hexadecenyl group, heptadecenyl group, octadecenyl group, oleyl group, and linoleyl group. .
Examples of the alkyl group having 14 to 20 carbon atoms include a tetradecyl group, a pentadecyl group, a hexadecyl group, a heptadecyl group, an octadecyl group, a nonadecyl group, and an icosyl group. It may be a mixed alkyl group derived from natural fats and oils. Examples of the alkenyl group having 14 to 20 carbon atoms include a tetradecenyl group, a pentadecenyl group, a hexadecenyl group, a heptadecenyl group, an octadecenyl group, an oleyl group, a linoleyl group, a nonadecenyl group, and an icocenyl group.

4級オニウム塩のカウンターアニオンとしては、クロリド(Cl)、ブロミド(Br)、メチルサルフェート(CHOSO )、エチルサルフェート(COSO )、パラトルエンスルホネート(p−CHSO )等が挙げられる。 The counter anion of the quaternary onium salt includes chloride (Cl ), bromide (Br ), methyl sulfate (CH 3 OSO 3 ), ethyl sulfate (C 2 H 5 OSO 3 ), paratoluene sulfonate (p- CH 3 C 6 H 4 SO 3 ) and the like.

4級オニウム塩の具体例としては、ドデシルジメチルベンジルアンモニウムクロリド、ドデシルジメチルベンジルアンモニウムブロミド、テトラデシルジメチルベンジルアンモニウムクロリド、テトラデシルジメチルベンジルアンモニウムブロミド、ヘキサデシルジメチルベンジルアンモニウムクロリド、ヘキサデシルジメチルベンジルアンモニウムブロミド、オクタデシルジメチルベンジルアンモニウムクロリド、オクタデシルジメチルベンジルアンモニウムブロミド、トリオクチルベンジルアンモニウムクロリド、トリオクチルベンジルアンモニウムブロミド、トリオクチルベンジルホスホニウムクロリド、トリオクチルベンジルホスホニウムブロミド、トリス(デシル)ベンジルアンモニウムクロリド、トリス(デシル)ベンジルアンモニウムブロミド、トリス(デシル)ベンジルホスホニウムクロリド、トリス(デシル)ベンジルホスホニウムブロミド、テトラオクチルアンモニウムクロリド、テトラオクチルアンモニウムブロミド、テトラオクチルホスホニウムクロリド、テトラオクチルホスホニウムブロミド、テトラノニルアンモニウムクロリド、テトラノニルアンモニウムブロミド、テトラノニルホスホニウムクロリド、テトラノニルホスホニウムブロミド、テトラキス(デシル)アンモニウムクロリド、テトラキス(デシル)アンモニウムブロミド、テトラキス(デシル)ホスホニウムクロリド、テトラキス(デシル)ホスホニウムブロミド、等が挙げられる。
なお、「トリス(デシル)」、「テトラキス(デシル)」は、炭素数10のアルキル基であるデシル基を3個又は4個有することを意味し、炭素数13のアルキル基であるトリデシル基や、炭素数14のアルキル基であるテトラデシル基とは区別される。
Specific examples of the quaternary onium salt include dodecyldimethylbenzylammonium chloride, dodecyldimethylbenzylammonium bromide, tetradecyldimethylbenzylammonium chloride, tetradecyldimethylbenzylammonium bromide, hexadecyldimethylbenzylammonium chloride, hexadecyldimethylbenzylammonium bromide, Octadecyldimethylbenzylammonium chloride, octadecyldimethylbenzylammonium bromide, trioctylbenzylammonium chloride, trioctylbenzylammonium bromide, trioctylbenzylphosphonium chloride, trioctylbenzylphosphonium bromide, tris (decyl) benzylammonium chloride, tris (decyl) benzylan Nitrobromide, Tris (decyl) benzylphosphonium chloride, Tris (decyl) benzylphosphonium bromide, Tetraoctylammonium chloride, Tetraoctylammonium bromide, Tetraoctylphosphonium chloride, Tetraoctylphosphonium bromide, Tetranonylammonium chloride, Tetranonylammonium bromide, Tetra Nonylphosphonium chloride, tetranonylphosphonium bromide, tetrakis (decyl) ammonium chloride, tetrakis (decyl) ammonium bromide, tetrakis (decyl) phosphonium chloride, tetrakis (decyl) phosphonium bromide, and the like.
Note that “tris (decyl)” and “tetrakis (decyl)” mean having 3 or 4 decyl groups, which are alkyl groups having 10 carbon atoms, such as tridecyl groups, which are alkyl groups having 13 carbon atoms, And a tetradecyl group which is an alkyl group having 14 carbon atoms.

前記4級オニウム塩が、25℃の水100gに対する溶解度が5g以下であることが好ましい。前記4級オニウム塩は、共重合組成物の100重量部に対して、(C)前記4級オニウム塩を0.1〜10重量部、を必須成分として含有することが好ましい。   The quaternary onium salt preferably has a solubility in 100 g of water at 25 ° C. of 5 g or less. The quaternary onium salt preferably contains (C) 0.1 to 10 parts by weight of the quaternary onium salt as an essential component with respect to 100 parts by weight of the copolymer composition.

粘着剤組成物に帯電防止剤を添加して帯電防止性能を持たせる場合、前記粘着剤組成物を積層して形成された粘着剤層において、前記粘着剤層の表面抵抗率が1.0×10+12Ω/□以下であることが好ましい。表面抵抗率が大きいと、剥離時に帯電で発生した静電気を逃がす性能に劣る。そのため、表面抵抗率を十分に小さくすることにより、粘着剤層を被着体が剥がす時に発生する、静電気に伴って生じる剥離帯電圧が低減され、被着体の制御用電子回路等に影響することを抑制することができる。 When an antistatic agent is added to the pressure-sensitive adhesive composition to provide antistatic performance, the pressure-sensitive adhesive layer formed by laminating the pressure-sensitive adhesive composition has a surface resistivity of 1.0 ×. It is preferably 10 +12 Ω / □ or less. When the surface resistivity is large, the performance of releasing static electricity generated by electrification at the time of peeling is inferior. Therefore, by making the surface resistivity sufficiently small, the stripping voltage generated due to static electricity that occurs when the adherend peels off the adhesive layer is reduced, affecting the electronic circuit for controlling the adherend, etc. This can be suppressed.

本発明の粘着剤組成物は、粘着剤層を形成する際に共重合組成物を架橋させることが好ましい。粘着剤層の共重合組成物を架橋させるために、粘着剤組成物が既知の架橋剤を含んでいることが好ましい。本発明で使用される架橋剤は、2官能以上のイソシアネート系架橋剤、2官能以上のエポキシ系架橋剤、アルミニウムキレート系架橋剤からなる化合物群のうちから選択される1種以上の架橋剤であることが好ましい。架橋剤は、1種類を単独で使用してもよいし、2種類以上を組み合わせて併用してもよい。   The pressure-sensitive adhesive composition of the present invention preferably crosslinks the copolymer composition when forming the pressure-sensitive adhesive layer. In order to crosslink the copolymer composition of the pressure-sensitive adhesive layer, the pressure-sensitive adhesive composition preferably contains a known crosslinking agent. The crosslinking agent used in the present invention is one or more kinds of crosslinking agents selected from the group consisting of a bifunctional or higher isocyanate crosslinking agent, a bifunctional or higher epoxy crosslinking agent, and an aluminum chelate crosslinking agent. Preferably there is. A crosslinking agent may be used individually by 1 type, and may be used together in combination of 2 or more types.

2官能以上のイソシアネート系化合物としては、1分子中に少なくとも2個以上のイソシアネート(NCO)基を有するポリイソシアネート化合物であればよく、ヘキサメチレンジイソシアネート、イソホロンジイソシアネート、ジフェニルメタンジイソシアネート、トリレンジイソシアネート、キシリレンジイソシアネート等のジイソシアネート類(1分子中に2個のNCO基を有する化合物)のビュレット変性体やイソシアヌレート変性体、トリメチロールプロパンやグリセリン等の3価以上のポリオール(1分子中に少なくとも3個以上のOH基を有する化合物)とのアダクト体(ポリオール変性体)などが挙げられる。
また、3官能以上のイソシアネート化合物が、1分子中に少なくとも3個以上のイソシアネート(NCO)基を有するポリイソシアネート化合物であり、特にヘキサメチレンジイソシアネート化合物のイソシアヌレート体、イソホロンジイソシアネート化合物のイソシアヌレート体、ヘキサメチレンジイソシアネート化合物のアダクト体、イソホロンジイソシアネート化合物のアダクト体、ヘキサメチレンジイソシアネート化合物のビュレット体、イソホロンジイソシアネート化合物のビュレット体からなる化合物群の中から選択された、少なくとも一種以上であることが好ましい。
2官能以上のイソシアネート系架橋剤は、アクリル系共重合体の100重量部に対して、0.01〜5.0重量部含まれることが好ましく、さらに好ましくは0.02〜3.0重量部含まれるのがよい。
The bifunctional or higher isocyanate compound may be a polyisocyanate compound having at least two isocyanate (NCO) groups in one molecule, such as hexamethylene diisocyanate, isophorone diisocyanate, diphenylmethane diisocyanate, tolylene diisocyanate, xylylene diene. A modified burette or isocyanurate of a diisocyanate such as isocyanate (compound having two NCO groups in one molecule) or a trivalent or higher polyol such as trimethylolpropane or glycerin (at least three or more in one molecule) And adduct bodies (polyol-modified bodies) with OH group compounds).
Further, the trifunctional or higher functional isocyanate compound is a polyisocyanate compound having at least three isocyanate (NCO) groups in one molecule, in particular, an isocyanurate body of a hexamethylene diisocyanate compound, an isocyanurate body of an isophorone diisocyanate compound, At least one selected from the group consisting of adducts of hexamethylene diisocyanate compounds, adducts of isophorone diisocyanate compounds, burettes of hexamethylene diisocyanate compounds, and burettes of isophorone diisocyanate compounds is preferred.
The bifunctional or higher isocyanate crosslinking agent is preferably contained in an amount of 0.01 to 5.0 parts by weight, more preferably 0.02 to 3.0 parts by weight, based on 100 parts by weight of the acrylic copolymer. Should be included.

2官能以上のエポキシ系化合物としては、例えば、ビスフェノールA型エポキシ樹脂、ビスフェノールF型エポキシ樹脂等のビスフェノール型エポキシ樹脂、フェノールノボラック型エポキシ樹脂、クレゾールノボラック型エポキシ樹脂、グリシジルエーテル型エポキシ樹脂、グリシジルアミン型エポキシ樹脂等のなどのエポキシ樹脂が挙げられる。これらの中でも、2官能のビスフェノールA型およびビスフェノールF型等のビスフェノール型エポキシ樹脂が、低粘度の液状であり取り扱い易いことからより好ましい。
また、2官能以上のエポキシ系化合物は、具体的には、グリセリンポリ(例えばジ、トリ)グリシジルエーテル、ソルビトールポリグリシジルエーテル、ペンタエリスリトールポリ(例えばジ、トリ、テトラ)グリシジルエーテル、トリメチロールプロパンポリグリシジルエーテル等が挙げられる。
2官能以上のエポキシ系化合物は、アクリル系共重合体の100重量部に対して、0.01〜5.0重量部含まれることが好ましく、さらに好ましくは0.02〜3.0重量部含まれるのが良い。
Examples of the bifunctional or higher functional epoxy compound include bisphenol type epoxy resins such as bisphenol A type epoxy resin and bisphenol F type epoxy resin, phenol novolac type epoxy resins, cresol novolac type epoxy resins, glycidyl ether type epoxy resins, and glycidyl amines. And epoxy resins such as type epoxy resins. Among these, bisphenol type epoxy resins such as bifunctional bisphenol A type and bisphenol F type are more preferable because they are liquids with low viscosity and are easy to handle.
In addition, the bifunctional or higher functional epoxy compounds are specifically glycerin poly (eg, di, tri) glycidyl ether, sorbitol polyglycidyl ether, pentaerythritol poly (eg, di, tri, tetra) glycidyl ether, trimethylolpropane poly. A glycidyl ether etc. are mentioned.
The bifunctional or higher functional epoxy compound is preferably contained in an amount of 0.01 to 5.0 parts by weight, more preferably 0.02 to 3.0 parts by weight, based on 100 parts by weight of the acrylic copolymer. It is good to be.

共重合組成物がカルボキシル基または水酸基を有している場合には、これらの官能基とアルミニウムキレート系化合物との架橋を生じる。このため、アルミニウムキレート系化合物を架橋剤として使用することができる。
本発明で使用できるアルミニウムキレート系化合物としては、アセチルアセトンアルミニウム塩、アセト酢酸エチルアルミニウム塩などのケトエノール互変異性体アルミニウム塩が好ましく、ケトエノール互変異性体アルミニウム塩の中でもアセチルアセトンアルミニウム塩は、架橋剤としての機能に優れるものとして好適に用いられる。
ケトエノール互変異性体アルミニウム塩に用いられる、ケトエノール互変異性体としては、アセチルアセトン等のβ−ジケトンや、アセト酢酸エチル、アセト酢酸メチル、アセト酢酸オレイル、アセト酢酸アルキル等のβ−ケトカルボン酸エステル等が挙げられる。
ケトエノール互変異性体アルミニウム塩としては、具体的には、アルミニウムトリス(アセチルアセトネート)、アルミニウムトリス(エチルアセトアセテート)、アルミニウムモノアセチルアセトネートビス(エチルアセトアセテート)、アルミニウムモノアセチルアセトネートビスオレイルアセトアセテート、エチルアセトアセテートアルミニウムジイソプロピレート、アルキルアセトアセテートアルミニウムジイソプロピレート等が挙げられる。
When the copolymer composition has a carboxyl group or a hydroxyl group, cross-linking between these functional groups and the aluminum chelate compound occurs. For this reason, an aluminum chelate type compound can be used as a crosslinking agent.
As the aluminum chelate compound that can be used in the present invention, ketoenol tautomeric aluminum salts such as acetylacetone aluminum salt and ethylaluminum acetoacetate are preferable, and among ketoenol tautomeric aluminum salts, acetylacetone aluminum salt is used as a crosslinking agent. It is preferably used as one having excellent functions.
Ketoenol tautomers used in aluminum salts include keto enol tautomers such as β-diketones such as acetylacetone, β-ketocarboxylates such as ethyl acetoacetate, methyl acetoacetate, oleyl acetoacetate, alkyl acetoacetate, etc. Is mentioned.
Specific examples of ketoenol tautomeric aluminum salts include aluminum tris (acetylacetonate), aluminum tris (ethylacetoacetate), aluminum monoacetylacetonate bis (ethylacetoacetate), and aluminum monoacetylacetonate bisoleyl. Examples include acetoacetate, ethyl acetoacetate aluminum diisopropylate, alkyl acetoacetate aluminum diisopropylate, and the like.

さらに、その他の成分として、シランカップリング剤、酸化防止剤、界面活性剤、硬化促進剤、可塑剤、充填剤、硬化遅延剤、加工助剤、老化防止剤などの公知の添加剤を適宜に配合することができる。これらは、単独でもしくは2種以上併せて用いることができる。   Furthermore, as other components, known additives such as silane coupling agents, antioxidants, surfactants, curing accelerators, plasticizers, fillers, curing retarders, processing aids, anti-aging agents are appropriately used. Can be blended. These may be used alone or in combination of two or more.

本発明の粘着フィルムは、本発明の粘着剤組成物からなる粘着剤層を、基材又は離型フィルムの片面上に形成することで製造することができる。また、本発明の粘着フィルムは、本発明の粘着剤組成物からなる粘着剤層を、基材の両面に形成することもできる。
粘着剤層の形成に用いる基材フィルムや、粘着面を保護する離型フィルム(セパレーター)としては、ポリエステルフィルムなどの樹脂フィルム等を用いることができる。
基材フィルムには、樹脂フィルムの粘着剤層が形成された側とは反対面に、シリコーン系、フッ素系の離型剤やコート剤、シリカ微粒子等による防汚処理、帯電防止剤の塗布や練り込み等による帯電防止処理を施すことができる。
剥離フィルムには、粘着剤層の粘着面と合わされる側の面に、シリコーン系、フッ素系の離型剤などにより離型処理が施される。
偏光板や位相差フィルムなどの各種光学フィルムを、液晶セルなどの光学部品及び他の光学フィルムに貼り合せる、粘着フィルムの粘着剤層は、十分な透明性を有することが好ましい。また、偏光板用の表面保護フィルムなどの光学用の表面保護フィルムの場合は、基材フィルム及び粘着剤層は、十分な透明性を有することが好ましい。
The adhesive film of this invention can be manufactured by forming the adhesive layer which consists of an adhesive composition of this invention on the single side | surface of a base material or a release film. Moreover, the adhesive film of this invention can also form the adhesive layer which consists of an adhesive composition of this invention on both surfaces of a base material.
As the base film used for forming the pressure-sensitive adhesive layer and the release film (separator) for protecting the pressure-sensitive adhesive surface, a resin film such as a polyester film can be used.
On the base film, on the side opposite to the side where the adhesive layer of the resin film is formed, antifouling treatment with silicone-based, fluorine-based release agent or coating agent, silica fine particles, etc., application of antistatic agent, An antistatic treatment such as kneading can be performed.
The release film is subjected to a release treatment with a silicone-based or fluorine-based release agent or the like on the surface of the pressure-sensitive adhesive layer that is to be combined with the pressure-sensitive adhesive surface.
It is preferable that the pressure-sensitive adhesive layer of the pressure-sensitive adhesive film for bonding various optical films such as a polarizing plate and a retardation film to an optical component such as a liquid crystal cell and other optical films has sufficient transparency. In the case of an optical surface protective film such as a polarizing plate surface protective film, the base film and the pressure-sensitive adhesive layer preferably have sufficient transparency.

粘着フィルムが基材フィルムを有する場合、本発明の粘着フィルムは、例えば、表面保護フィルム、偏光板用の表面保護フィルム、光学用の表面保護フィルム、粘着剤付き光学フィルム、粘着剤付き偏光板などに好適に用いることができる。   When the adhesive film has a base film, the adhesive film of the present invention is, for example, a surface protective film, a surface protective film for a polarizing plate, an optical surface protective film, an optical film with an adhesive, a polarizing plate with an adhesive, etc. Can be suitably used.

粘着フィルムが基材フィルムを有しない場合、1つの粘着剤層の両面に、それぞれ離型フィルムの離型処理が施された面を合わせることで、「離型フィルム/粘着剤層/離型フィルム」の構成とすることもできる。この場合、両側の離型フィルムを、順次、あるいは同時に剥離して粘着面を露出することにより、光学フィルム等の光学部材と貼合可能になる。光学フィルムとしては、偏光フィルム、位相差フィルム、反射防止フィルム、防眩(アンチグレア)フィルム、紫外線吸収フィルム、赤外線吸収フィルム、光学補償フィルム、輝度向上フィルム等が挙げられる。
この場合、本発明の粘着フィルムは、偏光板とディスプレイパネルの貼り合わせに用いることができる。ディスプレイパネルとしては液晶表示装置や有機EL等が挙げられるが、これらに限定されるものではない。
また、本発明の粘着フィルムは、偏光板を構成する材料の貼り合わせ用粘着フィルム、偏光板を主とする液晶表示装置の周辺部材用の各種光学フィルム、タッチパネル用フィルム、電子ペーパー用フィルム、有機EL用フィルム等に用いることができる。
When the pressure-sensitive adhesive film does not have a base film, the surfaces of the pressure-sensitive adhesive layer that have been subjected to the release treatment of the release film are combined with each other to obtain “release film / pressure-sensitive adhesive layer / release film”. It is also possible to adopt a configuration of “ In this case, the release films on both sides are peeled sequentially or simultaneously to expose the adhesive surface, so that it can be bonded to an optical member such as an optical film. Examples of the optical film include a polarizing film, a retardation film, an antireflection film, an antiglare (antiglare) film, an ultraviolet absorption film, an infrared absorption film, an optical compensation film, and a brightness enhancement film.
In this case, the adhesive film of this invention can be used for bonding of a polarizing plate and a display panel. Examples of the display panel include a liquid crystal display device and an organic EL, but are not limited thereto.
The pressure-sensitive adhesive film of the present invention includes a pressure-sensitive adhesive film for bonding materials constituting the polarizing plate, various optical films for peripheral members of liquid crystal display devices mainly comprising a polarizing plate, a film for touch panel, a film for electronic paper, and an organic film. It can be used for EL films and the like.

また、これらの光学フィルムの少なくとも一方の面に、前記粘着剤層が積層されてなる粘着剤層付き光学フィルムとすることができる。具体的には、「光学フィルム/粘着剤層/光学フィルム」、「光学フィルム/粘着剤層/離型フィルム」、「光学フィルム/粘着剤層」、「光学フィルム/粘着剤層/光学フィルム/粘着剤層/光学フィルム」、「光学フィルム/粘着剤層/光学フィルム/粘着剤層/離型フィルム」、「離型フィルム/粘着剤層/光学フィルム/粘着剤層/離型フィルム」等の構成が挙げられる。
例えば、「光学フィルム/粘着剤層/離型フィルム」のように、離型フィルムで保護された粘着剤層を有する場合、離型フィルムを剥がして、「光学フィルム/粘着剤層」のように粘着剤層を露出させ、他の光学フィルムと貼合することにより、粘着剤層が層間の貼合に用いられた「光学フィルム/粘着剤層/光学フィルム」のような構成が得られる。
Moreover, it can be set as the optical film with an adhesive layer formed by laminating | stacking the said adhesive layer on the at least one surface of these optical films. Specifically, “optical film / pressure-sensitive adhesive layer / optical film”, “optical film / pressure-sensitive adhesive layer / release film”, “optical film / pressure-sensitive adhesive layer”, “optical film / pressure-sensitive adhesive layer / optical film / “Adhesive layer / optical film”, “optical film / adhesive layer / optical film / adhesive layer / release film”, “release film / adhesive layer / optical film / adhesive layer / release film”, etc. A configuration is mentioned.
For example, when having a pressure-sensitive adhesive layer protected by a release film such as “optical film / pressure-sensitive adhesive layer / release film”, the release film is peeled off, and “optical film / pressure-sensitive adhesive layer” By exposing the pressure-sensitive adhesive layer and pasting with another optical film, a configuration such as “optical film / pressure-sensitive adhesive layer / optical film” in which the pressure-sensitive adhesive layer is used for bonding between layers is obtained.

以下、実施例をもって、本発明を具体的に説明する。   Hereinafter, the present invention will be specifically described with reference to examples.

<アクリル系共重合体の製造>
[実施例1]
撹拌機、温度計、還流冷却器及び窒素導入管を備えた反応装置に、窒素ガスを導入して、反応装置内の空気を窒素ガスで置換した。その後、反応装置に2−エチルヘキシルアクリレート100重量部、6−ヒドロキシヘキシルアクリレート1.5重量部とともに溶剤(酢酸エチル)を100部加えた。その後、重合開始剤としてアゾビスイソブチロニトリル0.1重量部を2時間かけて滴下させ、65℃で8時間反応させ、重量平均分子量50万の、実施例1のアクリル系共重合体溶液1を得た。
[実施例2〜6及び比較例1〜3]
単量体の組成を各々、表1の(A)、(A′)、及び(B)の記載のようにする以外は、上記の実施例1に用いるアクリル系共重合体溶液1と同様にして、実施例2〜6及び比較例1〜3に用いるアクリル系共重合体溶液を得た。
<Manufacture of acrylic copolymer>
[Example 1]
Nitrogen gas was introduced into a reactor equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen inlet tube, and the air in the reactor was replaced with nitrogen gas. Thereafter, 100 parts of a solvent (ethyl acetate) was added to the reaction apparatus together with 100 parts by weight of 2-ethylhexyl acrylate and 1.5 parts by weight of 6-hydroxyhexyl acrylate. Thereafter, 0.1 part by weight of azobisisobutyronitrile as a polymerization initiator was added dropwise over 2 hours, reacted at 65 ° C. for 8 hours, and the acrylic copolymer solution of Example 1 having a weight average molecular weight of 500,000 was obtained. 1 was obtained.
[Examples 2-6 and Comparative Examples 1-3]
The monomer composition is the same as that of the acrylic copolymer solution 1 used in Example 1 except that the composition of each monomer is as described in (A), (A ′) and (B) of Table 1. Thus, acrylic copolymer solutions used in Examples 2 to 6 and Comparative Examples 1 to 3 were obtained.

<粘着剤組成物及び粘着フィルムの製造>
[実施例1]
上記のとおり製造したアクリル系共重合体溶液1(そのうちアクリル系共重合体が100重量部)に対して、コロネートHX 1.5重量部と、トリオクチルホスホニウムベンジルクロリド2.0重量部を加えて撹拌混合して実施例1の粘着剤組成物を得た。この粘着剤組成物をシリコーン樹脂コートされたポリエチレンテレフタレート(PET)フィルムからなる剥離フィルムの上に塗布後、90℃で乾燥することによって溶剤を除去し、粘着剤層の厚さが25μmである粘着フィルムを得た。
その後、一方の面に帯電防止及び防汚処理されたポリエチレンテレフタレート(PET)フィルムの帯電防止及び防汚処理された面とは反対の面に粘着フィルムを転写させ、「帯電防止及び防汚処理されたPETフィルム/粘着剤層/剥離フィルム(シリコーン樹脂コートされたPETフィルム)」の積層構成を有する実施例1の粘着フィルムを得た。
[実施例2〜6及び比較例1〜3]
添加剤の組成を各々、表1の「架橋剤」及び(C)の記載のようにする以外は、上記の実施例1の粘着フィルムと同様にして、実施例2〜6及び比較例1〜3の粘着フィルムを得た。
<Production of pressure-sensitive adhesive composition and pressure-sensitive adhesive film>
[Example 1]
1.5 parts by weight of coronate HX and 2.0 parts by weight of trioctylphosphonium benzyl chloride are added to the acrylic copolymer solution 1 produced as described above (of which 100 parts by weight of the acrylic copolymer). The pressure-sensitive adhesive composition of Example 1 was obtained by stirring and mixing. After applying this adhesive composition on a release film made of a polyethylene terephthalate (PET) film coated with a silicone resin, the solvent is removed by drying at 90 ° C., and the adhesive layer has a thickness of 25 μm A film was obtained.
Then, the adhesive film was transferred to the opposite side of the antistatic and antifouling surface of the polyethylene terephthalate (PET) film that had been antistatic and antifouling treated on one side. The pressure-sensitive adhesive film of Example 1 having a laminated structure of “PET film / pressure-sensitive adhesive layer / release film (PET film coated with silicone resin)” was obtained.
[Examples 2-6 and Comparative Examples 1-3]
Examples 2-6 and Comparative Examples 1 to 6 were the same as the adhesive film of Example 1 except that the composition of the additive was as described in “Crosslinking agent” and (C) in Table 1, respectively. 3 adhesive films were obtained.

表1において、各成分の配合比は、(A)と(A′)との合計量を100重量部として求めた重量部の数値を括弧で囲んで示す。また、表1に用いた各成分の略記号の化合物名を、表2に示す。また、表2(C)群には、帯電防止剤の25℃における水100gへの溶解度(g)、及び融点(℃)を合わせて示した。
なお、コロネート(登録商標)HX、同HLは日本ポリウレタン工業株式会社の商品名であり、TETRAD(登録商標)−Xは三菱ガス化学株式会社の商品名であり、デュラネート(登録商標)24A−100は旭化成ケミカルズ株式会社の商品名である。
In Table 1, the compounding ratio of each component is indicated by enclosing the numerical value of parts by weight enclosed in parentheses with the total amount of (A) and (A ′) as 100 parts by weight. In addition, Table 2 shows the names of the abbreviations of each component used in Table 1. In Table 2 (C), the solubility (g) of the antistatic agent in 100 g of water at 25 ° C. and the melting point (° C.) are also shown.
Coronate (registered trademark) HX and HL are trade names of Nippon Polyurethane Industry Co., Ltd., TETRAD (registered trademark) -X is a trade name of Mitsubishi Gas Chemical Company, Inc., and Duranate (registered trademark) 24A-100. Is a trade name of Asahi Kasei Chemicals Corporation.

Figure 2014237763
Figure 2014237763

Figure 2014237763
Figure 2014237763

<試験方法及び評価>
実施例1〜6及び比較例1〜3における粘着フィルムを23℃、50%RHの雰囲気下で7日間エージングした後、剥離フィルム(シリコーン樹脂コートされたPETフィルム)を剥がして、粘着剤層を露出させた粘着フィルムを、表面抵抗率の測定試料とした。
さらに、この粘着剤層を露出させた粘着フィルムを、粘着剤層を介して液晶セルに貼られた偏光板の表面に貼り合わせ、1日放置した後、50℃、5気圧、20分間オートクレーブ処理し、室温でさらに12時間放置したものを、粘着力の測定試料とした。
<Test method and evaluation>
The adhesive films in Examples 1 to 6 and Comparative Examples 1 to 3 were aged for 7 days in an atmosphere of 23 ° C. and 50% RH, and then the release film (silicone resin-coated PET film) was peeled off to form an adhesive layer. The exposed adhesive film was used as a sample for measuring surface resistivity.
Further, the pressure-sensitive adhesive film with the pressure-sensitive adhesive layer exposed is bonded to the surface of the polarizing plate attached to the liquid crystal cell via the pressure-sensitive adhesive layer, and left for 1 day, and then autoclaved at 50 ° C., 5 atm for 20 minutes. Then, the sample that was allowed to stand at room temperature for another 12 hours was used as a sample for measuring the adhesive strength.

<粘着剤層の表面抵抗率>
エージングした後、偏光板に貼り合わせる前に、剥離フィルム(シリコーン樹脂コートされたPETフィルム)を剥がして粘着剤層を露出させ、抵抗率計ハイレスタUP−HT450(三菱化学アナリテック製)を用いて粘着剤層の表面抵抗率(Ω/□)を測定した。
<Surface resistivity of adhesive layer>
After aging, before bonding to the polarizing plate, peel off the release film (silicone resin-coated PET film) to expose the adhesive layer, and use a resistivity meter Hiresta UP-HT450 (manufactured by Mitsubishi Chemical Analytech) The surface resistivity (Ω / □) of the pressure-sensitive adhesive layer was measured.

<粘着力>
上記で得られた粘着剤層を露出させた粘着フィルムを、25mm幅の粘着フィルムに裁断し、偏光板の表面に貼り合わせた後、180°方向に引張試験機を用いて30m/minの剥離速度において剥がして測定した剥離強度を粘着力(N/25mm)とした。
<Adhesive strength>
The pressure-sensitive adhesive film obtained by exposing the pressure-sensitive adhesive layer obtained above is cut into a 25 mm-wide pressure-sensitive adhesive film and bonded to the surface of the polarizing plate, and then peeled off at 30 ° using a tensile tester in the 180 ° direction. The peel strength measured by peeling off at a speed was defined as the adhesive strength (N / 25 mm).

<耐汚染性>
上記で得られた粘着剤層を露出させた粘着フィルムを、偏光板に貼り合せた後、60℃90%RHの雰囲気下に250時間放置後、室温に取り出し、さらに12時間放置した後、試料を30m/minの引張速度で180°剥離した際に偏光板表面に汚染移行の無いことを確認した。評価目標基準は、偏光板に汚染移行の無い場合を「○」、少なくとも一部汚染移行が確認された場合を「△」、全面に汚染移行が確認された場合を「×」と評価した。
<Contamination resistance>
The pressure-sensitive adhesive film with the pressure-sensitive adhesive layer exposed above was bonded to a polarizing plate, left in an atmosphere of 60 ° C. and 90% RH for 250 hours, taken out to room temperature, and further left for 12 hours. Was peeled 180 ° at a tensile speed of 30 m / min, it was confirmed that there was no contamination transfer on the polarizing plate surface. The evaluation target criteria were evaluated as “◯” when there was no contamination transfer on the polarizing plate, “△” when at least partial contamination transfer was confirmed, and “×” when contamination transfer was confirmed on the entire surface.

表3に、評価結果を示す。なお、粘着剤層の表面抵抗率は、「m×10+n」を「mE+n」とする方式(ただし、mは任意の実数値、nは正の整数)により表記した。 Table 3 shows the evaluation results. The surface resistivity of the pressure-sensitive adhesive layer was expressed by a method in which “m × 10 + n ” is “mE + n” (where m is an arbitrary real value and n is a positive integer).

Figure 2014237763
Figure 2014237763

実施例1〜6の粘着剤組成物及び粘着フィルムは、粘着剤組成物の中に帯電防止剤として融点30〜50℃の疎水性の4級オニウム塩を含有するため、表面抵抗率が十分に低く、耐汚染性が良好であった。帯電防止性については、表3に示すとおり、表面抵抗率がいずれも、1.0×10+12Ω/□以下となっており、剥離帯電圧の低減効果を有している。
また、比較例1の粘着剤組成物及び粘着フィルムは、粘着剤組成物の中に帯電防止剤を含まないため、表面抵抗率が高く、しかも、耐汚染性に問題があった。
比較例2、3の粘着剤組成物及び粘着フィルムは、粘着剤組成物の中の帯電防止剤として、融点が50℃を越える親水性の4級オニウム塩を含有するため、表面抵抗率が高く、しかも、耐汚染性に問題があった。
Since the adhesive composition and adhesive film of Examples 1 to 6 contain a hydrophobic quaternary onium salt having a melting point of 30 to 50 ° C. as an antistatic agent in the adhesive composition, the surface resistivity is sufficiently high. Low and good contamination resistance. As shown in Table 3, the antistatic property has a surface resistivity of 1.0 × 10 +12 Ω / □ or less, and has an effect of reducing the peeling band voltage.
Moreover, since the adhesive composition and adhesive film of Comparative Example 1 did not contain an antistatic agent in the adhesive composition, the surface resistivity was high and there was a problem in contamination resistance.
The pressure-sensitive adhesive composition and the pressure-sensitive adhesive film of Comparative Examples 2 and 3 have a high surface resistivity because they contain a hydrophilic quaternary onium salt having a melting point exceeding 50 ° C. as an antistatic agent in the pressure-sensitive adhesive composition. In addition, there was a problem with stain resistance.

本発明の粘着剤組成物は、疎水性の4級オニウム塩を帯電防止成分として粘着剤に併用することで、粘着剤との相溶性に優れるためブリードアウトや粘着フィルムを剥がした際に、被着体に汚染が生じてしまうなどのリワーク性の欠点である課題を改善することができ、産業上の利用価値が大である。   The pressure-sensitive adhesive composition of the present invention has excellent compatibility with a pressure-sensitive adhesive by using a hydrophobic quaternary onium salt as an antistatic component in combination with the pressure-sensitive adhesive. The problem which is a defect of reworkability, such as contamination of the kimono, can be improved, and the industrial utility value is great.

Claims (16)

帯電防止性能を有する粘着剤組成物であって、帯電防止剤として、融点30〜50℃の疎水性の4級オニウム塩を含有することを特徴とする粘着剤組成物。   A pressure-sensitive adhesive composition having antistatic properties, comprising a hydrophobic quaternary onium salt having a melting point of 30 to 50 ° C. as an antistatic agent. 前記4級オニウム塩が、25℃の水100gに対する溶解度が5g以下であることを特徴とする請求項1に記載の粘着剤組成物。   The pressure-sensitive adhesive composition according to claim 1, wherein the quaternary onium salt has a solubility in 100 g of water at 25 ° C. of 5 g or less. 粘着剤成分が、(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーの少なくとも1種と、(B)水酸基および/またはカルボキシル基を含有する共重合性ビニルモノマーの少なくとも1種と、からなる共重合組成物であり、前記共重合組成物の100重量部に対して、(C)前記4級オニウム塩を0.1〜10重量部、を必須成分として含有することを特徴とする請求項1または2に記載の粘着剤組成物。   The pressure-sensitive adhesive component is a copolymerizable vinyl monomer containing (A) at least one (meth) acrylic acid alkyl ester monomer having a C1-C14 alkyl group and (B) a hydroxyl group and / or a carboxyl group. And a copolymer composition comprising at least one kind, and (C) 0.1 to 10 parts by weight of the quaternary onium salt as an essential component with respect to 100 parts by weight of the copolymer composition. The pressure-sensitive adhesive composition according to claim 1 or 2. 粘着剤成分が、(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーの少なくとも1種と、ビニル基を有する共重合性ビニルモノマーの少なくとも1種と、からなる共重合組成物であり、前記共重合組成物の100重量部に対して、(C)前記4級オニウム塩を0.1〜10重量部、を必須成分として含有することを特徴とする請求項1または2に記載の粘着剤組成物。   The adhesive component comprises (A) at least one alkyl (meth) acrylic acid alkyl ester monomer having a C1-C14 alkyl group and at least one copolymerizable vinyl monomer having a vinyl group. It is a polymerization composition and contains 0.1 to 10 parts by weight of the quaternary onium salt as an essential component with respect to 100 parts by weight of the copolymer composition. Or the adhesive composition of 2. 粘着剤成分が、(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーの少なくとも2種以上からなる共重合組成物であり、前記共重合組成物の100重量部に対して、(C)前記4級オニウム塩を0.1〜10重量部、を必須成分として含有することを特徴とする請求項1または2に記載の粘着剤組成物。   The pressure-sensitive adhesive component is a copolymer composition composed of (A) at least two kinds of (meth) acrylic acid alkyl ester monomers having C1-C14 carbon atoms in the alkyl group, and 100 parts by weight of the copolymer composition On the other hand, (C) 0.1-10 weight part of said quaternary onium salt is contained as an essential component, The adhesive composition of Claim 1 or 2 characterized by the above-mentioned. 粘着剤成分が、(A)アルキル基の炭素数がC1〜C14の(メタ)アクリル酸アルキルエステルモノマーの少なくとも1種と、芳香族系モノマーの少なくとも1種と、からなる共重合組成物であり、前記共重合組成物の100重量部に対して、(C)前記4級オニウム塩を0.1〜10重量部、を必須成分として含有することを特徴とする請求項1または2に記載の粘着剤組成物。   The pressure-sensitive adhesive component is a copolymer composition comprising (A) at least one of (meth) acrylic acid alkyl ester monomers having C1-C14 carbon atoms and at least one aromatic monomer. The content of (C) 0.1 to 10 parts by weight of the quaternary onium salt is contained as an essential component with respect to 100 parts by weight of the copolymer composition. Adhesive composition. 基材の片面上に、前記粘着剤組成物を積層して形成された粘着剤層において、前記粘着剤層の表面抵抗率が1.0×10+12Ω/□以下であることを特徴とする請求項1〜6のいずれかに記載の粘着剤組成物。 In the pressure-sensitive adhesive layer formed by laminating the pressure-sensitive adhesive composition on one surface of the base material, the pressure-sensitive adhesive layer has a surface resistivity of 1.0 × 10 +12 Ω / □ or less. The pressure-sensitive adhesive composition according to any one of claims 1 to 6. 基材の片面上に、請求項1〜7のいずれかに記載の粘着剤組成物を用いて粘着剤層が積層されたことを特徴とする粘着フィルム。   A pressure-sensitive adhesive film comprising a pressure-sensitive adhesive layer laminated on one side of a substrate using the pressure-sensitive adhesive composition according to claim 1. 請求項1〜7のいずれかに記載の粘着剤組成物を用いて粘着剤層が積層されたことを特徴とする粘着フィルム。   A pressure-sensitive adhesive film in which a pressure-sensitive adhesive layer is laminated using the pressure-sensitive adhesive composition according to claim 1. 請求項8に記載の粘着フィルムが用いられた、表面保護フィルム。   A surface protective film using the pressure-sensitive adhesive film according to claim 8. 請求項8に記載の粘着フィルムが用いられた、偏光板用の表面保護フィルム。   The surface protection film for polarizing plates in which the adhesive film of Claim 8 was used. 請求項8に記載の粘着フィルムが用いられた、光学用の表面保護フィルム。   An optical surface protective film using the pressure-sensitive adhesive film according to claim 8. 請求項8に記載の粘着フィルムが用いられた偏光板とディスプレイパネルの貼り合わせ用フィルム。   The film for bonding of the polarizing plate and display panel in which the adhesive film of Claim 8 was used. 請求項8に記載の粘着フィルムが用いられた偏光板を構成する材料の貼り合わせ用フィルム。   The film for bonding the material which comprises the polarizing plate in which the adhesive film of Claim 8 was used. 請求項8に記載の粘着フィルムが用いられたタッチパネル用フィルム。   The film for touchscreens in which the adhesive film of Claim 8 was used. 請求項8に記載の粘着フィルムが用いられた電子ペーパー用フィルム。   The film for electronic papers using the adhesive film of Claim 8.
JP2013121074A 2013-06-07 2013-06-07 Pressure-sensitive adhesive composition, pressure-sensitive adhesive film and surface protective film using the same Active JP6630933B2 (en)