JP2014198411A - 粘着シート - Google Patents
粘着シート Download PDFInfo
- Publication number
- JP2014198411A JP2014198411A JP2013074664A JP2013074664A JP2014198411A JP 2014198411 A JP2014198411 A JP 2014198411A JP 2013074664 A JP2013074664 A JP 2013074664A JP 2013074664 A JP2013074664 A JP 2013074664A JP 2014198411 A JP2014198411 A JP 2014198411A
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- sensitive adhesive
- release
- adhesive layer
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】基材2Aと、基材2Aの片面または両面に積層された粘着剤層3と、粘着剤層3における基材2Aと反対側の面に積層された剥離シート4とを有する粘着シート1Aであって、粘着剤層3の厚さが、1〜16μmであり、基材2Aの厚さが、1〜16μmであり、剥離シート4を除く粘着シート1Aの厚さが、2〜20μmであり、基材2Aにおける粘着剤層3と接触する側の面の表面粗さ(Ra)が、0.15μm以下である粘着シート1A。
【選択図】図1
Description
〔第1の実施形態〕
本発明の第1の実施形態に係る粘着シート1Aは、図1に示すように、剥離シート4と、剥離シート4の剥離面上に積層された粘着剤層3と、粘着剤層3の剥離シート4側とは反対側(図1では上側)に積層された基材2Aとから構成されており、いわゆる片面粘着シートである。なお、本明細書における剥離シートの剥離面とは、剥離シートにおいて剥離性を有する面をいい、剥離処理を施した面および剥離処理を施さなくても剥離性を示す面のいずれをも含むものである。
シリコーン量(%)={Si/(Si+C+O)}×100
すなわち、粘着剤層3の粘着面においてXPSにより検出される原子は、ケイ素、炭素および酸素で略100%となるため、それらの原子中におけるケイ素の割合を上記のとおりシリコーン量とする。なお、粘着剤層そのものは、XPSによりケイ素が検出されない水準であることが大半であるため、当該シリコーン量を剥離剤層の剥離剤(シリコーン系化合物)の転移量の評価基準として利用することができる。
本発明の第2の実施形態に係る粘着シート1Bは、図2に示すように、基材2Bと、基材2Bの一方の面(図2では上側の面)に積層された第1の粘着剤層31と、第1の粘着剤層31における基材2Bとは反対側(図2では上側)に積層された第1の剥離シート41と、基材2Bの他方の面(図2では下側の面)に積層された第2の粘着剤層32と、第2の粘着剤層32における基材2Bとは反対側(図2では下側)に積層された第2の剥離シート42とから構成される。なお、第1の剥離シート41および第2の剥離シート42は、それらの剥離面が粘着剤層に接するように、第1の粘着剤層31および第2の粘着剤層32に積層されている。本実施形態における粘着シート1Bは、いわゆる両面粘着シートであり、基材2Bは、第1の粘着剤層31および第2の粘着剤層32を支持する支持基材である。
1.(メタ)アクリル酸エステル重合体の調製
攪拌機、温度計、還流冷却器、滴下装置および窒素導入管を備えた反応容器に、アクリル酸n−ブチル90質量部、アクリル酸10質量部、酢酸エチル200質量部、および2,2'−アゾビスイソブチロニトリル0.15質量部を仕込み、上記反応容器内の空気を窒素ガスで置換した。この窒素雰囲気下中で攪拌しながら、反応溶液を60℃に昇温し、16時間反応させた後、室温まで冷却した。ここで、得られた溶液の一部を後述する方法で分子量を測定し、重量平均分子量(Mw)60万の(メタ)アクリル酸エステル重合体の生成を確認した。
上記工程(1)で得られた(メタ)アクリル酸エステル重合体(A)100質量部(固形分換算値;以下同じ)と、架橋剤(イソシアネート系架橋剤)としてのトリメチロールプロパン変性トリレンジイソシアネート(日本ポリウレタン社製,コロネートL)0.15質量部とを混合し、十分に撹拌して、メチルエチルケトンで希釈することにより、不揮発分濃度15質量%の粘着性組成物の塗布溶液を得た。
得られた粘着性組成物の塗布溶液を、ポリエチレンテレフタレートフィルムの片面をシリコーン系剥離剤で剥離処理した剥離シート(リンテック社製,RL−1,厚さ:38μm)の剥離処理面に、乾燥後の厚さが2μmになるようにナイフコーターで塗布したのち、90℃で1分間加熱処理して塗布層を形成した。
剥離シートとして、ポリエチレンテレフタレートフィルムの片面をシリコーン系剥離剤で剥離処理した剥離シート(リンテック社製,RL−2,厚さ:38μm)を使用する以外、実施例1と同様にして粘着シートを作製した。
剥離シートとして、ポリエチレンテレフタレートフィルムの片面をシリコーン系剥離剤で剥離処理した別の剥離シート(リンテック社製,RL−3,厚さ:38μm)を使用する以外、実施例1と同様にして粘着シートを作製した。
粘着剤層の厚さを4μmとし、基材として別のポリエチレンテレフタレートフィルム(ユニチカ社製,エンブレットPET,厚さ:12μm)を使用する以外、実施例1と同様にして粘着シートを作製した。
粘着性組成物における架橋剤の配合量を0.03質量部に変更する以外、実施例1と同様にして粘着シートを作製した。
剥離シートとして、ポリエチレンテレフタレートフィルムの片面をシリコーン系剥離剤で剥離処理した別の剥離シート(リンテック社製,RL−6,厚さ:38μm)を使用する以外、実施例1と同様にして粘着シートを作製した。
剥離シートとして、ポリエチレンテレフタレートフィルムの片面をシリコーン系剥離剤で剥離処理した別の剥離シート(リンテック社製,RL−7,厚さ:38μm)を使用する以外、実施例1と同様にして粘着シートを作製した。
基材として別のポリエチレンテレフタレートフィルム(三菱樹脂社製,K880−4.5W,厚さ:4.5μm)を使用し、剥離シートとして、ポリエチレンテレフタレートフィルムの片面をシリコーン系剥離剤で剥離処理した別の剥離シート(リンテック社製,RL−6,厚さ:38μm)を使用する以外、実施例1と同様にして粘着シートを作製した。
基材として別のポリエチレンテレフタレートフィルム(三菱樹脂社製,K880−4.5W,厚さ:4.5μm)を使用し、剥離シートとして、ポリエチレンテレフタレートフィルムの片面をシリコーン系剥離剤で剥離処理した別の剥離シート(リンテック社製,RL−7,厚さ:38μm)を使用する以外、実施例1と同様にして粘着シートを作製した。
基材として別のポリエチレンテレフタレートフィルム(三菱樹脂社製,K880−4.5W,厚さ:4.5μm)を使用する以外、実施例1と同様にして粘着シートを作製した。
<測定条件>
・GPC測定装置:東ソー社製,HLC−8020
・GPCカラム(以下の順に通過):東ソー社製
TSK guard column HXL−H
TSK gel GMHXL(×2)
TSK gel G2000HXL
・測定溶媒:テトラヒドロフラン
・測定温度:40℃
実施例および比較例で使用した基材における粘着剤層と接触する側の面の表面粗さ(Ra)を、JIS B0601:2001に準拠し、表面粗さ計(ミツトヨ社製,SURFTEST SV−3000)を使用して測定した。測定条件は、カットオフ値λc=0.8mm、評価長さln=10mmとした。結果を表1に示す。
実施例または比較例で得られた粘着シートを裁断し、10mm幅、10mm長のサンプルを作製した。このサンプルから剥離シートを剥がし、粘着剤層の露出面(粘着面)におけるシリコーン量(%)を、X線光電子分析法(XPS)によって測定・算出した。測定装置としては、アルバックファイ社製のQuantera SXMを使用し、測定条件は以下の通りとした。
X線:AlKα(1486.6eV)
取り出し角度:45°
測定元素:ケイ素原子(Si),炭素原子(C),酸素原子(O)
シリコーン量(%)={Si/(Si+C+O)}×100
実施例または比較例にて使用した基材に替えて、ポリエチレンテレフタレートフィルムの片面をシリコーン系剥離剤で剥離処理した剥離シート(リンテック社製,RL−5,厚さ:38μm)を使用し、粘着シートを作製した。具体的には、実施例または比較例の製造過程で得られた剥離シート/粘着剤層(厚さ:2μm)からなる構成体の露出している粘着剤層上に、上記剥離シートを剥離処理面側が接するように積層した。これにより、剥離シート/粘着剤層/剥離シートの構成からなる粘着シートを作製した。
実施例または比較例で得られた粘着シートを裁断し、25mm幅、250mm長のサンプルを作製した。このサンプルから剥離シートを剥がし、2kgのゴムローラを使用して、当該サンプルを無アルカリガラス(コーニング社製,イーグルXG)に貼付した。その後、23℃、50%RHの条件下で24時間放置してから、引張試験機(オリエンテック社製,テンシロン)を用い、JIS Z0237:2009に準じて、剥離速度300mm/min、剥離角度180°の条件で粘着力(N/25mm)を測定した。結果を表1に示す。
実施例または比較例で得られた粘着シートを裁断し、50mm幅、50mm長のサンプルを作製した。このサンプルから剥離シートを剥がし、2kgのゴムローラを使用して、当該サンプルを無アルカリガラス(コーニング社製,イーグルXG)に貼付した。
○:浮きや発泡が確認されなかった。
×:浮きや発泡が確認された。
2A,2B…基材
3…粘着剤層
31…第1の粘着剤層
32…第2の粘着剤層
4…剥離シート
41…第1の剥離シート
42…第2の剥離シート
Claims (10)
- 基材と、前記基材の片面または両面に積層された粘着剤層と、前記粘着剤層における前記基材と反対側の面に積層された剥離シートとを有する粘着シートであって、
前記粘着剤層の厚さは、1〜16μmであり、
前記基材の厚さは、1〜16μmであり、
前記剥離シートを除く前記粘着シートの厚さは、2〜20μmであり、
前記基材における前記粘着剤層と接触する側の面の表面粗さ(Ra)は、0.15μm以下である
ことを特徴とする粘着シート。 - 前記基材は、プラスチックフィルムから構成されることを特徴とする請求項1に記載の粘着シート。
- 前記基材を構成する前記プラスチックフィルムは、ポリエチレンテレフタレートフィルムであることを特徴とする請求項2に記載の粘着シート。
- 前記剥離シートは、剥離基材と、前記剥離基材の片面または両面に形成された剥離剤層とから構成され、
前記剥離剤層は、シリコーン系化合物を含有しており、
前記粘着剤層における前記剥離シート側の面のシリコーン量が、2.5%以下である
ことを特徴とする請求項1〜3のいずれか一項に記載の粘着シート。 - 前記剥離基材の厚さは、12〜75μmであることを特徴とする請求項4に記載の粘着シート。
- 前記剥離基材は、プラスチックフィルムから構成されることを特徴とする請求項4または5に記載の粘着シート。
- 前記剥離基材を構成する前記プラスチックフィルムは、ポリエチレンテレフタレートフィルムであることを特徴とする請求項6に記載の粘着シート。
- 前記粘着剤層を構成する粘着剤のゲル分率は、20〜100%であることを特徴とする請求項1〜7のいずれか一項に記載の粘着シート。
- 前記粘着剤層は、アクリル系粘着剤から構成されることを特徴とする請求項1〜8のいずれか一項に記載の粘着シート。
- 前記アクリル系粘着剤は、(メタ)アクリル酸エステル重合体と架橋剤とを含有する粘着性組成物を架橋したものである請求項9に記載の粘着シート。