JP2013256084A - Decoration synthetic resin molding and decorating method thereof - Google Patents

Decoration synthetic resin molding and decorating method thereof Download PDF

Info

Publication number
JP2013256084A
JP2013256084A JP2012134374A JP2012134374A JP2013256084A JP 2013256084 A JP2013256084 A JP 2013256084A JP 2012134374 A JP2012134374 A JP 2012134374A JP 2012134374 A JP2012134374 A JP 2012134374A JP 2013256084 A JP2013256084 A JP 2013256084A
Authority
JP
Japan
Prior art keywords
layer
synthetic resin
decorative
resin molded
base
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2012134374A
Other languages
Japanese (ja)
Inventor
Atsuhiro Inoue
厚弘 井上
Yoshihiro Yamada
恵寛 山田
Original Assignee
Sanyo Kagaku Kogyo Kk
三洋化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sanyo Kagaku Kogyo Kk, 三洋化学工業株式会社 filed Critical Sanyo Kagaku Kogyo Kk
Priority to JP2012134374A priority Critical patent/JP2013256084A/en
Publication of JP2013256084A publication Critical patent/JP2013256084A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide a decoration synthetic resin molding visually appearing overflow feeling of three-dimensional, clear, and luxury pattern by the insert molding of which the insert material is the decorative film, and to provide a decorating method of the decoration synthetic resin molding.SOLUTION: In a decoration synthetic resin molding: a decorative film F includes, a thickly raised ink layer A disposed contacting a cavity surface 2, and a solid appearance layer R provided at an opposing side of the cavity surface 2 and accumulating at least a base material layer B and an adhesive layer G; the thickly raised ink layer A is formed with the ink that is transparent or has translucency; the solid appearance layer R is extruded along a shape of a space 4 formed between the thickly raised ink layer I and the cavity surface 2 by injecting the molten resin from the solid appearance layer R side by insert molding; and the surface of the molding becomes nearly a flush surface by only the thickly raised ink layer A, or the thickly raised ink layer A and the solid appearance layer R.

Description

本発明は、金型を直接加工することなく立体的な加飾を施した加飾合成樹脂成形品及びその加飾方法に関する。   The present invention relates to a decorative synthetic resin molded product that is three-dimensionally decorated without directly processing a mold, and a method for decorating the same.

従来より、金型のキャビティー面に凹凸状の模様を刻設することなく、立体的な視覚効果を有する加飾合成樹脂成形品が公知である。例えば、加飾フィルムをインサート材としたインサート成形により表面を加飾した合成樹脂成形品において、成形品は透明性を有するものとし、加飾フィルムは基材フィルムの表面に厚盛印刷層による凸部を形成したものとし、インサート成形により成形品の加飾フィルムが貼着する面側に、凸部が嵌入した状態で凹部が形成される加飾合成樹脂成形品が公知である(特許文献1参照)。   Conventionally, a decorative synthetic resin molded product having a three-dimensional visual effect without engraving an uneven pattern on the cavity surface of a mold is known. For example, in a synthetic resin molded product in which the surface is decorated by insert molding using a decorative film as an insert material, the molded product has transparency, and the decorative film is projected on the surface of the base film by a thick print layer. A decorative synthetic resin molded product in which a concave portion is formed in a state in which a convex portion is fitted on a surface side to which a decorative film of a molded product is attached by insert molding is known (Patent Document 1). reference).

これにより、透明性を有する成形品の裏側面に凹凸模様を形成することで、表側面から壁厚を透して凹凸模様を現出させることが可能であるとされる。   Thereby, it is said that by forming a concavo-convex pattern on the back side surface of the molded product having transparency, it is possible to make the concavo-convex pattern appear through the wall thickness from the front side surface.

特開2012−11614号公報JP2012-11614A

しかしながら、上記特許文献1の加飾合成樹脂成形品を成形するために使用される加飾フィルムの基本的な第1の層構成は、接着層、基材フィルム層、厚盛印刷層の順に構成されたものであり、その加飾フィルムをインサート材として、厚盛印刷層側を金型のキャビティー面に配設し、インサート成形することで、透明性を有する成形品の裏側面に、厚盛印刷層の凸部が嵌入した凹部が形成されることで凹凸模様を現出させている。   However, the basic first layer configuration of the decorative film used for molding the decorative synthetic resin molded article of Patent Document 1 is an adhesive layer, a base film layer, and a thick print layer in this order. The decorative film is used as an insert material, the thick print layer side is disposed on the cavity surface of the mold, and insert molding is performed, so that the thickness of the back side of the molded product having transparency is increased. The concave / convex pattern appears by forming the concave portion into which the convex portion of the prime printing layer is inserted.

つまり、上記特許文献1によれば、層厚が僅か0.05mm程度の厚さである、厚盛印刷層の凸部が、基材フィルムを介して成形品裏側面の凹部を形成している。   That is, according to the above-mentioned Patent Document 1, the convex portion of the thick print layer having a layer thickness of only about 0.05 mm forms a concave portion on the back side of the molded product via the base film. .

そのため、上記第1の層構成を使用した加飾合成樹脂成形品においては、凹凸模様の輪郭がくっきりしないため、シャープな凹凸模様にはならず、ぼやけた印象の凹凸模様が観察されることとなる。   Therefore, in the decorative synthetic resin molded product using the first layer configuration, the contour of the concavo-convex pattern is not clear, so that the concavo-convex pattern with a blurred impression is observed instead of a sharp concavo-convex pattern. Become.

また、このように成形された成形品の凹凸模様を観察する際、基材フィルムを介してこの厚盛印刷による凹凸模様を観察することとなるので、さらに、凹凸模様がぼやけた印象として観察されることとなる。   In addition, when observing the concavo-convex pattern of the molded product formed in this way, the concavo-convex pattern by the thick printing is observed through the base film, and further, the concavo-convex pattern is observed as a blurred impression. The Rukoto.

さらに、上記特許文献1の加飾合成樹脂成形品を成形するために使用される加飾フィルムの基本的な第2の層構成は、接着層、厚盛印刷層、基材フィルム層の順に構成されたものであり、その加飾フィルムをインサート材として、厚盛印刷層の凸部側を溶融樹脂が充填される金型のキャビティー面にして、他方の金型の平端なキャビティー面に基材フィルム層を配設し、インサート成形することで、厚盛印刷層の形成付近と非成形付近により形成される凹凸に沿って溶融樹脂が充填し、透明性を有する成形品の裏側面に厚盛印刷層の凸部が嵌入した凹部が形成されることで凹凸模様を現出させている。   Furthermore, the basic second layer configuration of the decorative film used for forming the decorative synthetic resin molded article of Patent Document 1 is an adhesive layer, a thick print layer, and a base film layer in this order. With the decorative film as an insert material, the convex side of the thick print layer is the cavity surface of the mold filled with molten resin, and the other mold has a flat cavity surface. By placing the base film layer and insert molding, the molten resin fills along the irregularities formed by the formation of the thick print layer and the vicinity of the non-molding, and on the back side of the molded product having transparency The concave / convex pattern appears by forming the concave portion into which the convex portion of the thick print layer is inserted.

この場合、第1の層構成を使用して成形した場合とは異なり、基材フィルムを介して成形品裏側面の凹部を形成していないものの、単に着色した厚盛印刷層を観察できるにとどまるものであり、立体的な視覚効果が十分に得られるものではなかった。   In this case, unlike the case of molding using the first layer configuration, the concave portion on the back side of the molded product is not formed through the base film, but only a colored thick print layer can be observed. However, a three-dimensional visual effect was not sufficiently obtained.

加飾合成樹脂成形品のなかでも、例えば、化粧品等が充填される加飾合成樹脂成形品においては、その合成樹脂成形品に施された加飾によって、商品イメージを大きく左右し得るものであり、さらには購買意欲にも影響を及ぼすものであることから、完成度の高い立体的な模様を現出させることにより、高級感のある高度な加飾を施した合成樹脂成形品の開発が望まれている。   Among decorative synthetic resin molded products, for example, in decorative synthetic resin molded products filled with cosmetics etc., the product image can be greatly influenced by the decoration applied to the synthetic resin molded products. Furthermore, since it also affects the willingness to purchase, it is hoped to develop a synthetic resin molded product with a high-class and sophisticated decoration by revealing a highly complete three-dimensional pattern. It is rare.

そこで、本発明は直接金型のキャビティー面に凹凸状の模様を刻設することなく、加飾フィルムをインサート材としたインサート成形により、視覚的に高級感あふれる立体的かつ鮮明な模様が現出される加飾合成樹脂成形品及びその加飾方法を提供することを課題とする。   Therefore, the present invention does not engrave the uneven pattern directly on the cavity surface of the mold, and insert molding using a decorative film as an insert material provides a three-dimensional and clear pattern that is visually luxurious. It is an object of the present invention to provide a decorated synthetic resin molded article and a decoration method thereof.

上記課題を解決すべく、本発明では下記手段を講じている。   In order to solve the above problems, the present invention takes the following measures.

本発明の加飾合成樹脂成形品は、インサート材として加飾フィルムを成形金型のキャビティー面に配設した状態でインサート成形され、前記加飾フィルムによって表面が加飾された加飾合成樹脂成形品であって、前記加飾フィルムは、前記キャビティー面に接触して配設される厚盛りインク層と、前記キャビティー面の反対側に設けられ、少なくとも基材層と接着層とを積層した立体現出層とを備え、前記厚盛インク層は透明又は透光性を有するインクによって形成されており、前記インサート成形により、前記立体現出層側から溶融樹脂を注入することで、前記厚盛インク層と前記キャビティー面との間に形成された空間の形状に沿うように、立体現出層を押出して、成形品の表面が前記厚盛インク層のみ、または、前記厚盛インク層と前記立体現出層とによって、略面一になっているものである。   The decorative synthetic resin molded product of the present invention is a decorative synthetic resin that is insert-molded in a state in which a decorative film is disposed as an insert material on the cavity surface of a molding die, and the surface is decorated with the decorative film. The decorative film is a thick ink layer disposed in contact with the cavity surface, provided on the opposite side of the cavity surface, and at least a base material layer and an adhesive layer. And the thick ink layer is formed of a transparent or translucent ink, and by insert molding, by injecting molten resin from the three-dimensional appearance layer side, The solid appearance layer is extruded so as to conform to the shape of the space formed between the thick ink layer and the cavity surface, and the surface of the molded product is only the thick ink layer or the thick film. Ink layer and front By the steric revealing layer, in which it is substantially flush.

また、前記基材層は、樹脂からなる透明のフィルムとすることができる。   Moreover, the said base material layer can be used as the transparent film which consists of resin.

また、前記加飾フィルムは、前記基材層の一方の片面側に、凸部を有する厚盛りインク層を設けると共に、基材層の他方の片面側に、インク層と接着層の順に積層したものとすることができる。   In addition, the decorative film is provided with a thick ink layer having a convex portion on one side of the base material layer, and the ink layer and the adhesive layer are sequentially laminated on the other side of the base material layer. Can be.

また、前記基材層に少なくともメタリック調のインクを塗布することによりインク層を構成することができる。   Moreover, an ink layer can be comprised by apply | coating at least metallic ink to the said base material layer.

また、前記加飾フィルムが、基材層の一方の片側面に、メタリック調の光沢を現出させるための蒸着箔層と、適宜の模様を印刷したインク層と、凸部を有する厚盛インク層の順に積層すると共に、基材層の他方の片側面に、樹脂の成形品に貼着するための接着層を積層したものとすることができる。   Further, the decorative film is a thick ink having a convex portion, a vapor deposition foil layer for displaying a metallic gloss on one side surface of the base material layer, an ink layer printed with an appropriate pattern, and the like. While laminating in the order of the layers, an adhesive layer for adhering to a resin molded product may be laminated on the other side surface of the base material layer.

さらに、上記の加飾合成樹脂成形品の表面側に、透明又は透光性を有する外側樹脂部を設けることとすることができる。   Furthermore, the outer side resin part which has transparency or translucency can be provided in the surface side of said decorative synthetic resin molded product.

本発明の加飾方法は、インサート材として加飾フィルムを成形金型のキャビティー面に配設した状態でインサート成形され、前記加飾フィルムによって表面が加飾される加飾合成樹脂成形品の加飾方法であって、透明又は透光性を有するインクによって形成された厚盛りインク層と、少なくとも基材層と接着層とを積層した立体現出層とを備える前記加飾フィルムの厚盛りインク層と前記キャビティー面が接触し、立体現出層が前記キャビティー面の反対側に位置するように配設する工程、前記立体現出層側から溶融樹脂を注入してインサート成形工程、前記インサート成形工程により、前記厚盛インク層と前記キャビティー面との間に形成された空間の形状に沿うように、立体現出層を押出して、成形品の表面が前記厚盛インク層のみ、または、前記厚盛インク層と前記立体現出層とによって、略面一にするものである。   The decorative method of the present invention is a decorative synthetic resin molded product that is insert-molded in a state where a decorative film is disposed as an insert material on the cavity surface of a molding die, and the surface is decorated by the decorative film. A decorative method, comprising: a thick ink layer formed of a transparent or translucent ink; and a three-dimensional appearance layer obtained by laminating at least a base material layer and an adhesive layer. An ink layer and the cavity surface are in contact with each other, a step of disposing the three-dimensionally exposed layer on the opposite side of the cavity surface, an injection molding step by injecting a molten resin from the three-dimensionally exposed layer side, By the insert molding step, the three-dimensional revealing layer is extruded so as to follow the shape of the space formed between the thick ink layer and the cavity surface, and the surface of the molded product is only the thick ink layer. , Ma Includes the AtsuSakari ink layer by said stereoscopic revealing layer is for substantially flush.

本発明の加飾合成樹脂成形品では、上述した構成及び方法となっているため、直接金型のキャビティー面に凹凸状の模様を刻設することなく、加飾フィルムをインサート材としたインサート成形により、視覚的に高級感あふれる立体的かつ鮮明な模様が現出されることにより、高度な加飾効果を有する加飾合成樹脂成形品とすることができる。   Since the decorative synthetic resin molded product of the present invention has the above-described configuration and method, an insert using a decorative film as an insert material without engraving an uneven pattern directly on the cavity surface of the mold By forming a three-dimensional and clear pattern that is visually luxurious, a decorative synthetic resin molded product having a high degree of decoration effect can be obtained.

本発明の第1実施形態における加飾合成樹脂成形品の斜視図である。It is a perspective view of the decorative synthetic resin molded product in 1st Embodiment of this invention. 図1のA−A線断面図である。It is the sectional view on the AA line of FIG. 本発明の第1実施形態における加飾合成樹脂成形品のインサート成形に使用する加飾フィルムの層構成の説明図及び製造工程図である。It is explanatory drawing and manufacturing process figure of the layer structure of the decorating film used for insert molding of the decorative synthetic resin molded product in 1st Embodiment of this invention. 本発明の第2実施形態における加飾合成樹脂成形品の斜視図である。It is a perspective view of the decorative synthetic resin molded product in 2nd Embodiment of this invention. 本発明の第2実施形態における加飾合成樹脂成形品のインサート成形に使用する加飾フィルムの層構成の説明図及び製造工程図である。It is explanatory drawing and manufacturing process figure of the layer structure of the decoration film used for insert molding of the decorative synthetic resin molded product in 2nd Embodiment of this invention. 本発明の第3実施形態における加飾合成樹脂成形品のインサート成形に使用する加飾フィルムの層構成の説明図である。It is explanatory drawing of the laminated constitution of the decorating film used for insert molding of the decorative synthetic resin molded product in 3rd Embodiment of this invention. 本発明の第4実施形態における加飾合成樹脂成形品の斜視図である。It is a perspective view of the decorative synthetic resin molded product in 4th Embodiment of this invention. 図7のC−C線断面図である。It is CC sectional view taken on the line of FIG. 第2実施形態の加飾合成樹脂成形品の斜視図(図4)及び図4のB−B線断面図を用いて立体的に観察できるメカニズムを説明した説明図である。It is explanatory drawing explaining the mechanism which can be observed three-dimensionally using the perspective view (FIG. 4) of the decorative synthetic resin molded product of 2nd Embodiment, and the BB sectional drawing of FIG.

以下、本発明の実施形態における加飾合成樹脂成形品Kについて図面に基づいて説明する。   Hereinafter, a decorative synthetic resin molded product K according to an embodiment of the present invention will be described with reference to the drawings.

本発明に係る加飾合成樹脂成形品Kは、直接金型1のキャビティー面2に凹凸状の模様を刻設することなく、加飾フィルムFをインサート材としたインサート成形により、合成樹脂成形品の表面側に図1、図4、図7に示すように、視覚的に立体的な模様が現出されるものである。   The decorative synthetic resin molded product K according to the present invention is formed by synthetic resin molding by insert molding using the decorative film F as an insert material without engraving a concave-convex pattern directly on the cavity surface 2 of the mold 1. As shown in FIGS. 1, 4, and 7, a visually three-dimensional pattern appears on the surface side of the product.

〔第1実施形態〕
図1は本発明の加飾合成樹脂成形品Kの第1実施形態の外観を示す斜視図であり、成形品の表面側から「1」、「2」、「3」の数字及び四角形状の図形、三角形状の図形が、手前に突出したように視覚的に観察できる。図2は、図1の加飾合成樹脂成形品Kの「四角」部分(A−A線部分)の断面図(A−A線断面図)である。
[First Embodiment]
FIG. 1 is a perspective view showing the external appearance of a first embodiment of a decorative synthetic resin molded product K of the present invention. The numbers “1”, “2”, and “3” and square shapes are formed from the surface side of the molded product. A figure and a triangular figure can be visually observed as if they protruded toward you. FIG. 2 is a cross-sectional view (A-A line cross-sectional view) of a “square” portion (A-A line portion) of the decorative synthetic resin molded product K of FIG. 1.

図1及び図2に示すような、成形品の表面側から視覚的に立体的に見える適宜の凹凸模様を現出させるために使用する加飾フィルムFと加飾方法について、図3を参照しながら詳細に説明する。   Refer to FIG. 3 for the decorative film F and the decorative method used to reveal an appropriate uneven pattern that visually appears three-dimensionally from the surface side of the molded product as shown in FIG. 1 and FIG. However, it explains in detail.

図3(a)は、第1実施形態の加飾合成樹脂成形品Kをインサート成形する際、インサート材として使用される加飾フィルムFの層構成を示す一部断面図である。   Fig.3 (a) is a partial cross section figure which shows the layer structure of the decorating film F used as an insert material, when insert-molding the decorative synthetic resin molded product K of 1st Embodiment.


この加飾フィルムFは、基材層Bの一方の片側面に、凸部A2を有する厚盛インク層Aを設けると共に、基材層Bの他方の片側面に、インク層Iと接着層Gをこの順に積層したものである。

The decorative film F is provided with a thick ink layer A having a convex portion A2 on one side surface of the base material layer B, and an ink layer I and an adhesive layer G on the other side surface of the base material layer B. Are stacked in this order.

基材層Bは、ポリエチレンテレフタラート(PET)、ポリプロピレン(PP)、ポリカーボネート等の樹脂からなる透明なフィルムであって、成形時に延伸変形性を有するものが好ましい。   The base material layer B is a transparent film made of a resin such as polyethylene terephthalate (PET), polypropylene (PP), or polycarbonate, and preferably has stretch deformability at the time of molding.

インク層Iは、加飾合成樹脂成形品Kのデザインに応じて適宜の色又は模様を基材層Bにインクを塗布又は印刷等することにより形成する。基材層Bに適宜のメタリックを塗布すれば、透明な基材層Bを透して金属調の光沢感を現出させることが可能となり、より高級感のある加飾合成樹脂成形品Kとすることができる。   The ink layer I is formed by applying or printing ink on the base material layer B with an appropriate color or pattern according to the design of the decorative synthetic resin molded product K. If an appropriate metallic material is applied to the base material layer B, it becomes possible to show a metallic luster through the transparent base material layer B, and a higher-quality decorative synthetic resin molded product K and can do.

厚盛インク層Aは、加飾合成樹脂成形品Kの表面側から観察したとき、表面側に立体的に突出するように現出させたい模様、絵柄、文字、記号等の部分はインクを盛らず凹部A1に形成し、突出させたくない部分はインクを盛って凸部A2に形成する。   When the thick ink layer A is observed from the surface side of the decorative synthetic resin molded product K, portions such as patterns, patterns, characters, symbols, etc., which are desired to appear so as to protrude three-dimensionally on the surface side, are filled with ink. The portion which is formed in the recess A1 and is not desired to protrude is formed in the protrusion A2 by depositing ink.

具体的には、図1の側壁部分の「1」、「2」、「3」の数字及び四角形状の図形、三角形状の図形以外の部分、つまり背景部分となる高さ位置をベース位置とし、「1」、「2」、「3」の数字及び四角形状の図形、三角形状の図形部分を表面側に突出するように立体的に現出させたい場合、厚盛インク層Aのベース位置となる部分は、インクを厚く盛って凸部A2(厚盛ベース凸部A3)として形成し、ベース位置よりも表面側に突出するように立体的に現出させたい模様(絵柄、文字、図形、記号等のことをいう。)の部分は、インクを盛らずに凹部A1とする。   Specifically, the numbers “1”, “2”, and “3” on the side wall portion in FIG. 1 and the shape other than the square shape and the triangle shape, that is, the height position that becomes the background portion are set as the base position. , “1”, “2”, “3” numbers, quadrilateral figures, and triangular figure parts to be projected three-dimensionally so as to protrude to the surface side, the base position of the thick ink layer A The portion to be formed is formed as a convex portion A2 (thick base base convex portion A3) by thickly depositing ink, and a pattern (pattern, character, figure) that is desired to appear three-dimensionally so as to protrude to the surface side from the base position. , A symbol or the like) is a recess A1 without depositing ink.

つまり、立体感を現出させたい模様等に相当する凹部A1を厚盛印刷層に形成する。   That is, the recess A1 corresponding to a pattern or the like for which a three-dimensional effect is desired to appear is formed in the thick print layer.

厚盛インク層Aは、インクジェット方式の印刷で多数回の重ね印刷をして形成すれば、微細かつ精巧であって、凸部A2の高さも自在に調節可能であり特に好ましいが、スクリーン印刷等の他の印刷方法により厚盛印刷層を形成することもできる。   The thick ink layer A is particularly preferable because it is fine and fine if it is formed by overprinting many times by ink jet printing, and the height of the convex portion A2 can be freely adjusted. The thick print layer can also be formed by other printing methods.

インク層Iに模様が印刷等されている場合、その模様に合わせた立体感を現出させるために、インク層Iの模様に合わせながら厚盛インク層Aを凹凸にすることもできる。   When a pattern is printed on the ink layer I, the thick ink layer A can be made uneven while matching the pattern of the ink layer I in order to reveal a three-dimensional effect that matches the pattern.

厚盛インク層Aに使用するインクは、無色透明なインクを使用することが特に好ましい。有色透明とすることも可能である。また、透光性を有するインクとすることもできる。   The ink used for the thick ink layer A is particularly preferably a colorless and transparent ink. It can also be colored and transparent. Moreover, it can also be set as the ink which has translucency.

本実施形態における厚盛インク層Aは、インクを厚く盛る部分とインクを盛らない部分とによって凹凸を形成しているが、インクを盛らない部分を設けずに、インクを盛る厚さを異ならせることによって凹凸を形成することとしても良い。   The thick ink layer A in the present embodiment forms irregularities by a portion where the ink is thick and a portion where the ink is not thick, but the thickness where the ink is thick is made different without providing a portion where the ink is not thick. It is good also as forming an unevenness | corrugation by.

接着層Gとしては成形品に貼着可能な公知の手段が用いられる。   As the adhesive layer G, a known means that can be attached to a molded product is used.

また、厚盛インク層Aの表面側にはニス等を塗布した適宜の保護層を設けることもできる。   An appropriate protective layer coated with varnish or the like can be provided on the surface side of the thick ink layer A.

なお、加飾フィルムFはデザインによっては、インク層Iを設けない層構成にすることもできる。この場合、厚盛インク層Aのインクの色が、透明又は透光性を有するインクからなる場合、加飾合成樹脂成形品Kの樹脂自体の色が表面側から観察されることとなるので、樹脂自体の色を加飾目的に応じた適宜の色にする必要がある。   In addition, the decorative film F can also be made into the layer structure which does not provide the ink layer I depending on a design. In this case, when the ink color of the thick ink layer A is made of transparent or translucent ink, the color of the resin of the decorative synthetic resin molded product K is observed from the surface side. It is necessary to change the color of the resin itself to an appropriate color according to the decoration purpose.

ここで、第1実施形態の加飾合成樹脂成形品Kの加飾方法を説明する。   Here, the decoration method of the decorative synthetic resin molded product K of 1st Embodiment is demonstrated.

まず、図3(b)に示すように、前述したインサート材である加飾フィルムFを、厚盛インク層Aの凸部A2側が射出成形の金型1の平坦なキャビティー面2に接触するように配設する。このとき、厚盛インク層Aは、インクを厚く盛った凸部A2とインクを盛っていない凹部A1とで構成されているため、凹部A1と平坦なキャビティー面2との間に凹部A1状の空間4ができる。   First, as shown in FIG. 3 (b), the decorative film F which is the insert material described above is such that the convex portion A2 side of the thick ink layer A contacts the flat cavity surface 2 of the injection mold 1. It arrange | positions as follows. At this time, the thick ink layer A is composed of a convex portion A2 thickly filled with ink and a concave portion A1 where ink is not thickened, so that a concave A1 shape is formed between the concave portion A1 and the flat cavity surface 2. Space 4 is created.

その後、金型1内に溶融樹脂を射出充填していくと、溶融樹脂の流動あるいは溶融樹脂の充填圧力により、溶融樹脂が凹部A1状の空間4に向かって、キャビティー面2の平坦な面と略面一になるように押出され、凸状に嵌入していく。   Thereafter, when the molten resin is injected and filled into the mold 1, the flat surface of the cavity surface 2 is directed toward the space 4 having the recess A1 due to the flow of the molten resin or the filling pressure of the molten resin. It is extruded so that it is substantially flush with it, and is inserted into a convex shape.

そのため、図3(c)の概略断面図に示すように、厚盛インク層Aの凹部A1付近では溶融樹脂がその凹部A1付近(凹部A1状の空間4)に向けて押出されることで嵌入すると共に、加飾フィルムFはその嵌入した樹脂に沿ってキャビティー面2に押し付けられるように変形する。   Therefore, as shown in the schematic cross-sectional view of FIG. 3C, the molten resin is inserted in the vicinity of the concave portion A1 of the thick ink layer A by being extruded toward the concave portion A1 (space 4 in the concave portion A1). At the same time, the decorative film F is deformed so as to be pressed against the cavity surface 2 along the inserted resin.

その結果、加飾合成樹脂成形品Kの表面が略面一となると共に、凸部A2付近の基材層B、インク層I及び接着層G(以下、これらをまとめて立体現出層Rという。)の高さ位置はほとんど変化せずベース部R0を成形し、凹部A1付近の立体現出層Rの断面が凸状に変形し隆起部R1を形成する。   As a result, the surface of the decorative synthetic resin molded product K becomes substantially flush, and the base material layer B, the ink layer I, and the adhesive layer G (hereinafter collectively referred to as the three-dimensional appearance layer R) near the convex portion A2. .) Is hardly changed, the base portion R0 is formed, and the cross section of the three-dimensional appearance layer R in the vicinity of the recess A1 is deformed into a convex shape to form a raised portion R1.

つまり、凹状空間4に樹脂部3が凸状に嵌入することで、凹凸部を形成した樹脂部3の表面に沿って立体現出層Rが融着している。   That is, when the resin part 3 is fitted into the concave space 4 in a convex shape, the three-dimensional appearance layer R is fused along the surface of the resin part 3 on which the uneven part is formed.

また、上述した工程により、インサート成形された加飾合成樹脂成形品Kの実際の表面は、面一にはなっておらず、図2及び図3(c)に示すように、成形前にキャビティー面2に接触していた凸部A2と、成形後に凹部A1に嵌入された立体現出層Rの隆起部R1との境界の、加飾合成樹脂成形品Kの表面近傍には、僅かな溝5が形成される。   Further, the actual surface of the decorative synthetic resin molded product K that has been insert-molded by the above-described process is not flush, and as shown in FIG. 2 and FIG. In the vicinity of the surface of the decorative synthetic resin molded product K at the boundary between the convex portion A2 that has been in contact with the tee surface 2 and the raised portion R1 of the three-dimensional appearance layer R that is inserted into the concave portion A1 after molding, there is a slight amount. A groove 5 is formed.

図1に示す第1実施形態の加飾合成樹脂成形品Kの「四角」部分は、四辺が表面側に突出し、その四辺に囲まれた内部が凹んだように立体的に観察される。「四角」部分をこのように立体的に現出させるための加飾フィルムFの厚盛インク層Aの構成を図1のA−A線部分を例にして具体的に説明する。   The “square” portion of the decorative synthetic resin molded product K of the first embodiment shown in FIG. 1 is three-dimensionally observed such that the four sides protrude to the surface side and the interior surrounded by the four sides is recessed. The configuration of the thick ink layer A of the decorative film F for causing the “square” portion to appear three-dimensionally in this way will be specifically described taking the AA line portion of FIG. 1 as an example.

図2は、図1のA−A線の断面の状態を示す図であり、成形品の表面から突出するように観察される「四角」の上辺と下辺部分は、立体現出層Rの隆起部R1であることが分かる。   FIG. 2 is a diagram illustrating a cross-sectional state taken along line AA in FIG. 1. The upper side and the lower side of the “square” observed so as to protrude from the surface of the molded product are raised portions of the three-dimensional appearance layer R. It turns out that it is part R1.

よって、加飾合成樹脂成形品Kの表面側に突出するように立体的に現出させたい部分の厚盛インク層Aを凹部A1とし、ベース部R0分の厚盛インク層Aを凸部A2とした加飾フィルムFをインサート材として、上述したような方法でインサート成形すれば、視覚的に立体的な模様が現出されることとなる。   Accordingly, the thick ink layer A that is to be three-dimensionally projected so as to protrude to the surface side of the decorative synthetic resin molded product K is defined as the concave portion A1, and the thick ink layer A corresponding to the base portion R0 is defined as the convex portion A2. If the decorative film F is used as an insert material and insert-molded by the method described above, a visually three-dimensional pattern will appear.

このようにインサート成形された加飾合成樹脂成形品Kの表面側から立体的に観察できるメカニズムについては後述する。   The mechanism that can be observed three-dimensionally from the surface side of the decorative synthetic resin molded product K thus insert-molded will be described later.

〔第2実施形態〕
図4は本発明の加飾合成樹脂成形品Kの第2実施形態の外観を示す斜視図であり、成形品の表面側から「1」、「2」、「3」の数字及び上下に並んだ上側の四角形状の図形、三角形状の図形が、手前に突出したように視覚的に観察できると共に、上下に並んだ下側の四角形状の図形が奥側に凹んだように視覚的に観察できる。
[Second Embodiment]
FIG. 4 is a perspective view showing the external appearance of the second embodiment of the decorative synthetic resin molded product K of the present invention. The numbers “1”, “2” and “3” are arranged in the vertical direction from the surface side of the molded product. The upper quadrilateral figure and the triangular figure can be visually observed as if they protruded toward you, and the lower quadrilateral figure that is lined up and down is visually observed as if they were recessed. it can.

このように文字、図形などの模様が、手前に突出したように立体的に観察できる部分と、奥側に凹んだように立体的に観察できる部分とからなる凹凸模様を現出させるために使用する加飾フィルムFと加飾方法について、図5を参照しながら説明する。   In this way, the pattern of characters, figures, etc. is used to reveal a concavo-convex pattern consisting of a part that can be observed stereoscopically as if it protruded toward the front and a part that can be observed stereoscopically as if it was recessed toward the back. The decorating film F and the decorating method will be described with reference to FIG.

図5(a)は第2実施形態の加飾合成樹脂成形品Kをインサート成形する際、インサート材として使用される加飾フィルムFの層構成を示す一部断面図である。   Fig.5 (a) is a partial cross section figure which shows the laminated constitution of the decoration film F used as an insert material, when insert-molding the decorative synthetic resin molded product K of 2nd Embodiment.

基本的な層構成は第1実施形態の加飾フィルムFと同様であるが、厚盛インク層Aの構成が異なる。上述した奥側に凹んだように立体的に観察させたい部分について、厚盛インク層Aの凸部A2(ベース凸部A3)からさらに厚くインクを重ねた凸部A2(重ね凸部A4)を設ける(図5(a))。   The basic layer configuration is the same as that of the decorative film F of the first embodiment, but the configuration of the thick ink layer A is different. Convex portion A2 (overlapping convex portion A4) in which the ink is further thickened from the convex portion A2 (base convex portion A3) of the thick ink layer A with respect to the portion that is desired to be stereoscopically observed as recessed toward the back side described above. Provided (FIG. 5A).

この第2実施形態の加飾合成樹脂成形品Kの加飾方法は、図5(b)、(c)に示す、第1実施形態の加飾方法と同様に、厚盛インク層Aの凸部A2側が射出成形の金型1の平坦なキャビティー面2に接触するように配設する。   The decorative method of the decorative synthetic resin molded product K of the second embodiment is similar to the decorative method of the first embodiment shown in FIGS. It arrange | positions so that the part A2 side may contact the flat cavity surface 2 of the metal mold | die 1 of injection molding.

このとき、本実施形態の場合第1実施形態と異なり、厚盛インク層Aの構成が、凸部A2(ベース凸部A3)よりもさらに突出した凸部A2(重ね凸部A4)を有するため、ベース凸部A3とキャビティー面2との間、及び、凹部A1とキャビティー面2との間に凹状の空間4ができる。   At this time, unlike the first embodiment, the configuration of the thick ink layer A has a convex portion A2 (overlapping convex portion A4) that protrudes further than the convex portion A2 (base convex portion A3). A concave space 4 is formed between the base convex portion A 3 and the cavity surface 2 and between the concave portion A 1 and the cavity surface 2.

その後、金型1内に溶融樹脂を射出充填していくと、溶融樹脂の流動あるいは溶融樹脂の充填圧力により、充填した溶融樹脂が上記凹状の空間4に向かって押出され、凸状に嵌入していく。   Thereafter, when the molten resin is injected and filled into the mold 1, the filled molten resin is extruded toward the concave space 4 due to the flow of the molten resin or the filling pressure of the molten resin, and is inserted into a convex shape. To go.

その結果、図5(c)の概略断面図に示すように、加飾合成樹脂成形品Kの表面が略面一になると共に、加飾フィルムFの立体現出層Rが断面凹凸形状に変形する。   As a result, as shown in the schematic cross-sectional view of FIG. 5C, the surface of the decorative synthetic resin molded product K becomes substantially flush, and the three-dimensional appearance layer R of the decorative film F is deformed into a concave-convex shape. To do.

具体的には、ベース凸部A3付近の立体現出層Rはベース凸部A3とキャビティー面2との空間4分の距離を移動してベース部R0を形成する。そして、凹部A1付近の立体現出層Rは凸状に変形した隆起部R1を形成し、重ね凸部A4付近の立体現出層Rは凹状に変形した沈下部R2を形成する。   Specifically, the three-dimensional appearance layer R in the vicinity of the base convex portion A3 moves the distance of the space 4 between the base convex portion A3 and the cavity surface 2 to form the base portion R0. The solid appearance layer R in the vicinity of the concave portion A1 forms a raised portion R1 that is deformed into a convex shape, and the solid appearance layer R in the vicinity of the overlapping convex portion A4 forms a depressed portion R2 that is deformed in a concave shape.

つまり、凹状空間4に樹脂部3が凸状に嵌入することで、凹凸部を形成した樹脂部3の表面に沿って立体現出層Rが融着している。   That is, when the resin part 3 is fitted into the concave space 4 in a convex shape, the three-dimensional appearance layer R is fused along the surface of the resin part 3 on which the uneven part is formed.

また、キャビティー面2に接触していた重ね凸部A4と、成形後にキャビティー面2に接触したベース凸部A3との境界の、加飾合成樹脂成形品の表面近傍、及び、凹部A1に嵌入された立体現出層Rの隆起部R1との境界の、加飾合成樹脂成形品の表面近傍には、それぞれ僅かな溝5が形成される。   In addition, in the vicinity of the surface of the decorative synthetic resin molded product at the boundary between the overlapping convex portion A4 that has been in contact with the cavity surface 2 and the base convex portion A3 that has been in contact with the cavity surface 2 after molding, and in the concave portion A1 A few grooves 5 are formed in the vicinity of the surface of the decorative synthetic resin molded product at the boundary with the raised portion R1 of the inserted solid appearance layer R.

〔第3実施形態〕
図6は、本発明の加飾合成樹脂成形品Kの第3実施形態に使用する加飾フィルムFの層構成を示す一部断面図である。
[Third Embodiment]
FIG. 6 is a partial cross-sectional view showing a layer configuration of a decorative film F used in the third embodiment of the decorative synthetic resin molded product K of the present invention.

この加飾フィルムFは、基材層Bの一方の片側面に、メタリック調の光沢を現出させるための蒸着箔層Jと、適宜の模様を印刷したインク層Iと、凸部A2を有する厚盛インク層Aの順に積層すると共に、基材層Bの他方の片側面に、樹脂の成形品に貼着するための接着層Gを積層したものである。   This decorative film F has, on one side surface of the base material layer B, a vapor-deposited foil layer J for revealing metallic gloss, an ink layer I printed with an appropriate pattern, and a convex portion A2. The thick ink layer A is laminated in this order, and an adhesive layer G for adhering to a resin molded product is laminated on the other side surface of the base material layer B.

つまり、厚盛インク層Aの構成は第1実施形態及び第2実施形態で使用される加飾フィルムFと略同様の構成であるが、厚盛インク層A以外の層構成が異なる。第1実施形態及び第2実施形態で使用される加飾フィルムFの場合、メタリック調の光沢を現出させるためには、基材層Bにメタリック調のインクを塗布したインク層Iを設けることにより光沢を現出させることが可能であるが、本実施形態においては、基材層Bに蒸着箔層Jの裏面側を貼り合せることによって同様の効果を現出させることができる層構成となっている。   That is, the configuration of the thick ink layer A is substantially the same as the decorative film F used in the first and second embodiments, but the layer configuration other than the thick ink layer A is different. In the case of the decorative film F used in the first embodiment and the second embodiment, in order to reveal metallic gloss, an ink layer I obtained by applying metallic ink to the base material layer B is provided. However, in the present embodiment, the layer configuration is such that the same effect can be obtained by bonding the back surface side of the vapor deposition foil layer J to the base material layer B. ing.

第3実施形態における加飾フィルムFの立体現出層Rは、インク層I、蒸着箔層J、基材層B、及び接着層Gで構成されている。   The three-dimensional appearance layer R of the decorative film F in the third embodiment includes an ink layer I, a vapor deposition foil layer J, a base material layer B, and an adhesive layer G.

この加飾フィルムFをインサート材として使用して、第1実施形態及び第2実施形態と同様の加飾方法によって成形されたものは、第1実施形態及び第2実施形態の加飾合成樹脂成形品Kの外観と同様の仕上がりとなる。   Using this decorative film F as an insert material, what is molded by the same decorative method as in the first and second embodiments is the decorative synthetic resin molding of the first and second embodiments. The finish is the same as the appearance of the product K.

なお、第3実施形態の加飾フィルムFは、第1実施形態及び第2実施形態の加飾フィルムF同様、インク層Iを有さない層形成とすることもできる。また、蒸着箔層Jの形成範囲は加飾目的に合わせて、全面に設けることもできるし、一部分に設けることもできる。   In addition, the decorative film F of 3rd Embodiment can also be set as the layer formation which does not have the ink layer I like the decorative film F of 1st Embodiment and 2nd Embodiment. Moreover, the formation range of the vapor deposition foil layer J can also be provided in the whole surface according to the decoration objective, and can also be provided in a part.

〔第4実施形態〕
第4実施形態の加飾合成樹脂成形品Kは、第1、2、3実施形態の加飾合成樹脂成形品Kの表面側に、外側樹脂部6を設けた加飾合成樹脂成形品である(図7、図8参照)。
[Fourth Embodiment]
The decorative synthetic resin molded product K of the fourth embodiment is a decorative synthetic resin molded product in which the outer resin portion 6 is provided on the surface side of the decorative synthetic resin molded product K of the first, second, and third embodiments. (See FIGS. 7 and 8).

外部樹脂部6は、加飾合成樹脂成形品の表面側に加飾された模様等を視認可能な、透明または透光性を有する樹脂材料により構成されるが、透明な樹脂材料により構成することが好ましい。   The external resin portion 6 is made of a transparent or translucent resin material that can visually recognize a pattern or the like decorated on the surface side of the decorative synthetic resin molded product, but is made of a transparent resin material. Is preferred.

本実施形態の外部樹脂部6を設けた加飾合成樹脂成形品の製造方法は、加飾された内側に位置する樹脂成形品と外部樹脂とが一体化したものを提供することができる方法であれば特に限定されない。   The manufacturing method of the decorative synthetic resin molded product provided with the external resin portion 6 according to the present embodiment is a method capable of providing an integrated resin molded product positioned on the decorated inner side and the external resin. If there is no particular limitation.

好ましい製造方法としては、まず、加飾フィルムFをインサート材として、内側に位置する樹脂成形品を射出成形により成形し、加飾面を内包するように外側樹脂部6を射出成形により形成する方法である。   As a preferable manufacturing method, first, the decorative film F is used as an insert material, a resin molded product positioned inside is molded by injection molding, and the outer resin portion 6 is formed by injection molding so as to enclose the decorative surface. It is.

本実施形態のように成形品が容器形状の場合、使用する金型1は内側に位置する容器形状の加工品の外側に閉じてできる形状であることが好ましい。   When the molded product has a container shape as in the present embodiment, it is preferable that the mold 1 to be used has a shape that can be closed outside the container-shaped processed product located inside.

上述した方法により、内側に位置する加飾された加工品と外側樹脂部6が一体化された場合、図8に示すように、加飾された加工品の表面側に形成される溝5に外側樹脂部6が入り込んだ状態で一体化されることとなる。   When the decorated product positioned on the inner side and the outer resin portion 6 are integrated by the above-described method, as shown in FIG. 8, the groove 5 formed on the surface side of the decorated workpiece is formed. It will be integrated in the state where the outer side resin part 6 entered.

本実施形態において、「一体化」とは、複数の部材の各接面に浮や空気溜りがない状態で密接接合していることをいう。   In the present embodiment, “integrated” means that the contact surfaces of a plurality of members are intimately joined without any floating or air accumulation.

また、外側樹脂部6の表面を加工して梨地、または、エンボス加工を施しても良い。   Further, the surface of the outer resin portion 6 may be processed and subjected to a satin finish or an embossing process.

(立体的に見えるメカニズムについて)
上述した加飾フィルムFをインサート材として使用して成形された加飾合成樹脂成形品が立体的に観察できるメカニズムについて、第2実施形態の加飾合成樹脂成形品を例にして説明する(図9参照)。
(About the mechanism that looks three-dimensional)
The mechanism by which the decorative synthetic resin molded product molded using the decorative film F described above as an insert material can be observed in three dimensions will be described using the decorative synthetic resin molded product of the second embodiment as an example (FIG. 9).

第2実施形態の加飾合成樹脂成形品Kを表面側から観察した場合、上下に並んだ上側の四角形状の図形は手前に突出したように視覚的に観察できると共に、上下に並んだ下側の四角形状の図形は奥側に凹んだように視覚的に観察できる(図9(a))。   When the decorative synthetic resin molded product K of the second embodiment is observed from the surface side, the upper and lower quadrangular figures arranged vertically can be visually observed as if they protruded toward the front, and the lower side arranged vertically. The rectangular figure can be visually observed as if it was recessed in the back side (FIG. 9A).

この部分(図9(a)のB−B線)の断面図(図9(b)のB−B線断面図)からも分かる通り、インサート成形によって、凹凸部を形成した樹脂部3の表面に沿って立体現出層Rが融着することにより、ベース部R0、隆起部R1、及び沈下部R2が形成されることで、成形品の表面側から立体的に観察することができる。   As can be seen from a cross-sectional view (cross-sectional view taken along line B-B in FIG. 9B) of this part (line B-B in FIG. 9A), the surface of the resin part 3 on which the uneven part is formed by insert molding. As a result, the base portion R0, the raised portion R1, and the sinking portion R2 are formed, so that the three-dimensional appearance layer R can be observed three-dimensionally from the surface side of the molded product.

厚盛インク層Aの凸部A2が透明又は透光性を有するインクによって形成されているので、上述した立体現出層Rを立体的に観察することが可能となっている。   Since the convex part A2 of the thick ink layer A is formed of a transparent or translucent ink, the above-described three-dimensional appearance layer R can be observed three-dimensionally.

また、従来の加飾合成樹脂成形品は、基材フィルムを介して成形品裏側面の凹部A1を形成しているため、シャープな凹凸模様にはならないうえに、成形品の凹凸模様を観察する際、基材フィルムを介してこの厚盛印刷による凹凸模様を観察しなければならなかったので、さらに、凹凸模様がぼやけた印象として観察されていたが、本発明によればこの問題も解消され、シャープかつ高度な凹凸模様を現出できる。   Moreover, since the conventional decorative synthetic resin molded product forms the concave portion A1 on the back side surface of the molded product through the base film, it does not become a sharp concavo-convex pattern and observes the concavo-convex pattern of the molded product. At this time, since the uneven pattern by the thick printing had to be observed through the base film, the uneven pattern was observed as a blurred impression, but according to the present invention, this problem was also solved. A sharp and sophisticated uneven pattern can be revealed.

また、キャビティー面2に接触していた重ね凸部A4と、成形後にキャビティー面2に接触したベース凸部A3との境界の、加飾合成樹脂成形品の表面近傍、及び、凹部A1に嵌入された立体現出層Rの隆起部R1との境界の、加飾合成樹脂成形品の表面近傍には、それぞれ僅かな溝5が形成されていることで、立体的な模様等をさらに際立たせることができる。   In addition, in the vicinity of the surface of the decorative synthetic resin molded product at the boundary between the overlapping convex portion A4 that has been in contact with the cavity surface 2 and the base convex portion A3 that has been in contact with the cavity surface 2 after molding, and in the concave portion A1 In the vicinity of the surface of the decorative synthetic resin molded product at the boundary with the raised portion R1 of the inserted three-dimensional appearance layer R, a slight groove 5 is formed, so that a three-dimensional pattern or the like further stands out. Can be made.

加飾フィルムFの厚盛印刷層の層厚を変化させることにより、突出高を変化させることができる。何種類かの層厚を組み合わせれば、突出高の異なる立体感を現出させることもできる。   By changing the layer thickness of the thick print layer of the decorative film F, the protruding height can be changed. By combining several types of layer thicknesses, it is possible to produce a three-dimensional effect with different protruding heights.

また、基材層Bにメタリック調のインクを塗布したインク層Iを設けたり、基材層Bに蒸着箔層Jを貼り合せることによって高級感あふれるメタリック調の光沢を現出させることができる。   Further, by providing the base layer B with the ink layer I in which metallic ink is applied, or by attaching the vapor deposition foil layer J to the base layer B, it is possible to reveal a metallic gloss full of luxury.

また、第4実施形態の場合、加飾面が透明又は透過性を有する樹脂材料によって成形された外側樹脂部6によって内包されているため、外側樹脂部6の光沢等が装飾面に反映してより高級感を高めることができる。   Moreover, in the case of 4th Embodiment, since the decorating surface is included by the outer side resin part 6 shape | molded by the resin material which has transparency or permeability | transmittance, the glossiness etc. of the outer side resin part 6 reflect on a decoration surface. A sense of quality can be enhanced.

内側に位置する加飾成形品と外側樹脂部6が一体化された場合、図8に示すように、加飾された加工品の表面側に形成される溝5に外側樹脂部6が入り込んだ状態で一体化されることとなる。その為、その溝5に入り込んだ外側樹脂部6は光の反射やレンズ効果を奏することとなり、さらに立体的に観察することができる。   When the decorative molded product located on the inner side and the outer resin portion 6 are integrated, as shown in FIG. 8, the outer resin portion 6 enters the groove 5 formed on the surface side of the decorated processed product. It will be integrated in the state. Therefore, the outer resin portion 6 that has entered the groove 5 exhibits light reflection and a lens effect, and can be further observed in three dimensions.

外側樹脂部6の表面を加工して梨地とすれば、ぼかしの表現を意図的に付与することができる。また、エンボス加工をすることで、その凹凸がレンズとして作用する為、立体的に加飾された加飾合成樹脂成形品をさらに立体的に観察することができる。   If the surface of the outer resin portion 6 is processed into a satin finish, the expression of blur can be intentionally given. Moreover, since the unevenness | corrugation acts as a lens by embossing, the decorative synthetic resin molded product decorated in three dimensions can be further observed in three dimensions.

以上、説明した本発明に係る加飾合成樹脂成形品Kによれば、直接金型1のキャビティー面2に凹凸状の模様を刻設することなく、加飾フィルムFをインサート材としたインサート成形により、視覚的に高級感あふれる立体的かつ鮮明な模様が現出されることにより、高度な加飾効果を有する加飾合成樹脂成形品Kとすることができる。   As described above, according to the decorative synthetic resin molded product K according to the present invention described above, the insert using the decorative film F as the insert material without directly engraving the cavity surface 2 of the mold 1. By forming a three-dimensional and clear pattern that is visually luxurious, a decorative synthetic resin molded product K having an advanced decoration effect can be obtained.

当該発明は、上述の実施形態の構成に限定させるものではなく、厚盛インク層A及びインク層Iの印刷方法等を適宜変更したり、加飾目的に合わせて加飾フィルムFの層構成を変更して実施することが可能である。また、一部構成を省略することができるし、一部抽出した構成とすることも出来る。   The said invention is not limited to the structure of the above-mentioned embodiment, The printing method etc. of the thick ink layer A and the ink layer I are changed suitably, or the layer structure of the decoration film F according to the decoration objective It is possible to change and implement. In addition, a part of the configuration can be omitted, or a part of the configuration can be extracted.

また、上記実施例では成形品を射出成形により成形するとしたが、インサート成形が適用可能なブロー成形、熱成形によって成形することもでき、使用する樹脂も何ら限定されるものでもない。   In the above embodiment, the molded product is molded by injection molding. However, it can be molded by blow molding or thermoforming to which insert molding can be applied, and the resin to be used is not limited at all.

厚盛印刷層の凸部A2の形状も、加飾フィルムFが延伸変形できる範囲でさまざまな形状とすることができる。   The shape of the convex portion A2 of the thick print layer can also be various shapes as long as the decorative film F can be stretched and deformed.

本実施形態においては、背景部分の高さ位置をベース位置として、その位置を基準にして表側に突出又は凹んだように立体的に観察できる加飾合成樹脂成形品Kについて例示したが、背景部分という概念のない立体模様も当然に含むものであり、厚盛インク層Aの凸部A2、凹部A1の突出高さを異ならせることで、様々な立体模様を現出できる。   In the present embodiment, the decorative synthetic resin molded product K that can be observed three-dimensionally as if it is projected or recessed to the front side with respect to the height position of the background portion as a base position has been exemplified. Naturally, a three-dimensional pattern having no concept is also included, and various three-dimensional patterns can appear by changing the protruding heights of the convex portion A2 and the concave portion A1 of the thick ink layer A.

また、本実施形態の加飾合成樹脂成形品Kは、適宜の内容物を収容することが可能な上方が開口した有底円筒状形状をした収納容器の樹脂成形品を例示して説明したが、本発明の加飾合成樹脂成形品Kは上述した形状の収納容器に限らず、種々の形状の収納容器とすることができるし、インサート成形によって成形可能な樹脂成形品であれば使用目的に合わせて様々な成形品とすることができることは勿論である。   Moreover, although the decorative synthetic resin molded product K of this embodiment illustrated and illustrated the resin molded product of the container with the bottomed cylindrical shape which the upper part opened which can accommodate an appropriate content, it demonstrated. The decorative synthetic resin molded product K of the present invention is not limited to the storage container having the shape described above, and can be a storage container having various shapes, or any resin molded product that can be molded by insert molding. Of course, various molded products can be obtained.

K 加飾合成樹脂成形品
F 加飾フィルム
A 厚盛りインク層
A2 凸部
B 基材層
I インク層
G 接着層
J 蒸着薄層
R 立体現出層
1 金型
2 キャビティー面
3 樹脂部
4 空間
6 外側樹脂部
K decorative synthetic resin molded product F decorative film A thick ink layer A2 convex part B base material layer I ink layer G adhesive layer J vapor deposition thin layer R solid appearance layer 1 mold 2 cavity surface 3 resin part 4 space 6 Outer resin part

Claims (7)

インサート材として加飾フィルムを成形金型のキャビティー面に配設した状態でインサート成形され、前記加飾フィルムによって表面が加飾された加飾合成樹脂成形品であって、
前記加飾フィルムは、前記キャビティー面に接触して配設される厚盛りインク層と、前記キャビティー面の反対側に設けられ、少なくとも基材層と接着層とを積層した立体現出層とを備え、
前記厚盛インク層は透明又は透光性を有するインクによって形成されており、
前記インサート成形により、前記立体現出層側から溶融樹脂を注入することで、前記厚盛インク層と前記キャビティー面との間に形成された空間の形状に沿うように、立体現出層を押出して、成形品の表面が前記厚盛インク層のみ、または、前記厚盛インク層と前記立体現出層とによって、略面一になっていることを特徴とする加飾合成樹脂成形品。
It is a decorative synthetic resin molded product that is insert-molded in a state where a decorative film is disposed on the cavity surface of the molding die as an insert material, and the surface is decorated by the decorative film,
The decorative film includes a thick ink layer disposed in contact with the cavity surface, and a three-dimensional manifestation layer provided on the opposite side of the cavity surface, wherein at least a base material layer and an adhesive layer are laminated. And
The thick ink layer is formed of a transparent or translucent ink,
By inserting the molten resin from the three-dimensional appearance layer side by the insert molding, the three-dimensional appearance layer is formed so as to conform to the shape of the space formed between the thick ink layer and the cavity surface. A decorative synthetic resin molded product, wherein the surface of the molded product is substantially flush with only the thick ink layer or with the thick ink layer and the three-dimensional appearance layer.
前記基材層は、樹脂からなる透明のフィルムであることを特徴とする請求項1に記載の加飾合成樹脂成形品。   The decorative synthetic resin molded product according to claim 1, wherein the base material layer is a transparent film made of a resin. 前記加飾フィルムは、前記基材層の一方の片面側に、凸部を有する厚盛りインク層を設けると共に、基材層の他方の片面側に、インク層と接着層の順に積層したものであることを特徴とする請求項1または請求項2に記載の加飾合成樹脂成形品。   The decorative film is formed by providing a thick ink layer having a convex portion on one side of the base material layer and laminating an ink layer and an adhesive layer in this order on the other side of the base material layer. The decorative synthetic resin molded article according to claim 1 or 2, wherein the decorative synthetic resin molded article is provided. 前記加飾フィルムが、基材層の一方の片側面に、メタリック調の光沢を現出させるための蒸着箔層と、適宜の模様を印刷したインク層と、凸部を有する厚盛インク層の順に積層すると共に、基材層の他方の片側面に、樹脂の成形品に貼着するための接着層を積層したものであることを特徴とする請求項1または請求項2に記載の加飾合成樹脂成形品。   The decorative film is a vapor-deposited foil layer for revealing metallic gloss on one side surface of the base material layer, an ink layer printed with an appropriate pattern, and a thick ink layer having a convex portion. The decoration according to claim 1 or 2, wherein the decorative layer is laminated in order, and an adhesive layer for adhering to a resin molded product is laminated on the other side surface of the base material layer. Synthetic resin molded product. 前記基材層に少なくともメタリック調のインクを塗布することによりインク層を構成していることを特徴とする請求項3に記載の加飾合成樹脂成形品。   The decorative synthetic resin molded article according to claim 3, wherein an ink layer is formed by applying at least metallic ink to the base material layer. 請求項1乃至請求項5に記載の加飾合成樹脂成形品の表面側に、透明又は透光性を有する外側樹脂部を設けたことを特徴とする加飾合成樹脂成形品。   A decorative synthetic resin molded product, comprising an outer resin portion having transparency or translucency on the surface side of the decorative synthetic resin molded product according to claim 1. インサート材として加飾フィルムを成形金型のキャビティー面に配設した状態でインサート成形され、前記加飾フィルムによって表面が加飾される加飾合成樹脂成形品の加飾方法であって、
透明又は透光性を有するインクによって形成された厚盛りインク層と、少なくとも基材層と接着層とを積層した立体現出層とを備える前記加飾フィルムの厚盛りインク層と前記キャビティー面が接触し、立体現出層が前記キャビティー面の反対側に位置するように配設する工程、
前記立体現出層側から溶融樹脂を注入してインサート成形工程、
前記インサート成形工程により、前記厚盛インク層と前記キャビティー面との間に形成された空間の形状に沿うように、立体現出層を押出して、成形品の表面が前記厚盛インク層のみ、または、前記厚盛インク層と前記立体現出層とによって、略面一にする、加飾合成樹脂成形品の加飾方法。
It is a decorative synthetic resin molded product that is insert-molded in a state where a decorative film is disposed on the cavity surface of a molding die as an insert material, and the surface is decorated by the decorative film,
A thick ink layer and the cavity surface of the decorative film, comprising: a thick ink layer formed of a transparent or translucent ink; and a three-dimensional appearance layer obtained by laminating at least a base material layer and an adhesive layer. Is disposed so that the three-dimensional manifestation layer is located on the opposite side of the cavity surface,
Insert molding process by injecting molten resin from the three-dimensional appearance layer side,
By the insert molding step, the three-dimensional revealing layer is extruded so as to follow the shape of the space formed between the thick ink layer and the cavity surface, and the surface of the molded product is only the thick ink layer. Or the decoration method of the decorative synthetic resin molded product which makes it substantially flush with the said thick ink layer and the said three-dimensional appearance layer.
JP2012134374A 2012-06-14 2012-06-14 Decoration synthetic resin molding and decorating method thereof Pending JP2013256084A (en)