JP2013095906A - シール用ゴム組成物の製造方法、シール用ゴム組成物およびシール - Google Patents
シール用ゴム組成物の製造方法、シール用ゴム組成物およびシール Download PDFInfo
- Publication number
- JP2013095906A JP2013095906A JP2011242687A JP2011242687A JP2013095906A JP 2013095906 A JP2013095906 A JP 2013095906A JP 2011242687 A JP2011242687 A JP 2011242687A JP 2011242687 A JP2011242687 A JP 2011242687A JP 2013095906 A JP2013095906 A JP 2013095906A
- Authority
- JP
- Japan
- Prior art keywords
- seal
- rubber composition
- kneading
- mass
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】未架橋ゴムおよび架橋剤を含むシール用ゴム組成物の製造方法であって、未架橋ゴムを含む未架橋ゴム組成物を70〜110℃の温度で混練する混練工程を有することを特徴とするシール用ゴム組成物の製造方法。
【選択図】なし
Description
[2] さらに、前記混練工程の後に、前記混練工程の混練の温度よりも低い温度で未架橋ゴム組成物を混練する混練工程を有することを特徴とする上記[1]に記載の製造方法。
[3] 未架橋ゴム100質量部に対して1〜15質量部の金属酸化物を使用する上記[1]または[2]に記載の製造方法。
[4] 未架橋ゴム100質量部に対して20〜200質量部の補強剤を使用する上記[1]〜[3]のいずれか一つに記載の製造方法。
[5] 70〜110℃の温度での混練時間が、3〜20分である上記[1]〜[4]のいずれか一つに記載の製造方法。
[6] 未架橋ゴムが、エチレン−プロピレン−ジエン三元共重合体(EPDM)を含む上記[1]〜[5]のいずれか一つに記載の製造方法。
[7] 車載エアコン用コンプレッサーのシールに使用されるシール用ゴム組成物を製造する上記[1]〜[6]のいずれか一つに記載の製造方法。
[8] 前記車載エアコン用コンプレッサーが、HFO−1234yfを使用するものである上記[7]に記載の製造方法。
[9] 上記[1]〜[8]のいずれか一つに記載の製造方法によって得られたシール用ゴム組成物。
[10] 上記[9]に記載のシール用ゴム組成物を架橋することによって得られたシール。
実施例で使用した原料を以下に記載する。
・JSR社製「EP27」(ML1+4(125℃):105、第三成分:ENB、第三成分含有量:15質量%、エチレン含有量:57質量%)
・三井化学社製「EPT3045」(ML1+4(125℃):25、第三成分:ENB、第三成分含有量:4.5質量%、エチレン含有量:56質量%)
・三井化学社製「EPT3070」(ML1+4(125℃):47、第三成分:ENB、第三成分含有量:4.5質量%、エチレン含有量:58質量%)
・三井化学社製「EPT1070」(ML1+4(125℃):48、第三成分:DCPD、第三成分含有量:4.0質量%、エチレン含有量:57質量%)
・ダウ・ケミカル社製「ノーデルIP4640」(ML1+4(125℃):40、第三成分:ENB、第三成分含有量:4.9質量%、エチレン含有量:55質量%)
・アルケマ吉富社製「ルペロックス101XL」(炭酸カルシウム:シリカ=50質量%:50質量%の混合物に、2,5−ジメチル−2,5−ジ(t−ブチルパーオキシ)ヘキサンを45質量%の量で含浸させた粉体、ルペロックス101XLの配合量の45質量%が架橋剤の配合量に相等する):架橋剤担持体
(i)老化防止剤
・大内新興化学工業社製「ノクラック224S」(2,2,4−トリメチル−1,2−ジヒドロキノリン重合体)
(ii)補強剤
・東海カーボン社製「シーストG−S」(SRFカーボンブラック)
・東海カーボン社製「シーストG−SO」(FEFカーボンブラック)
(iii)金属酸化物:酸化亜鉛
(iv)加工助剤:ステアリン酸
下記表1に示す量で原料を配合して未架橋ゴム組成物を調製し、オープンロールを用いてこれを下記表2および3に示す温度および時間で混練することによって、シール用ゴム組成物の製造を調製した。
得られたシール用ゴム組成物を、プレス圧型機を用いて170℃および表2および3に示す時間でプレス架橋することによって、シール物性測定用シートを調製した。
得られたシール物性測定用シートの物性を、以下のようにして測定した。結果を下記表2および3に示す。
得られたシール物性測定用シートから直径25mmで厚さ6mmの円柱状試験片を作製し、JIS K 6253:1997におけるデュロメーター硬さ(タイプA)試験により測定した。
(2)100%モジュラス
得られたシール物性測定用シートから、JIS K 6251:2010におけるダンベル状3号形の試験片を作製し、JIS K 6251:2010における所定伸び引張応力試験により、伸び100%時の引張応力を測定した。
(3)引張強さ
得られたシール物性測定用シートから、JIS K 6251:2010におけるダンベル状3号形の試験片を作製し、JIS K 6251:2010における引張強さ試験により、引張強さを測定した。
(4)伸び
得られたシール物性測定用シートから、JIS K 6251:2010におけるダンベル状3号形の試験片を作製し、JIS K 6251:2010における切断時伸び試験により、伸びを測定した。
(5)比重
得られたシール物性測定用シートから、50×50mm角で厚さ2mmの試験片を作製し、ASTM D297−93(2006)により、比重を測定した。
(6)圧縮永久ひずみ
得られたシール物性測定用シートからJIS K 6262:2006における大型試験片を用いて、JIS K 6262:2006における圧縮永久ひずみ試験により、圧縮永久ひずみを測定した。圧縮条件を150℃×70時間とし、圧縮率を25%とした。
(7)耐ブリスタ性
得られたシール物性測定用シートからシート状試験片(長さ:50mm、幅:20mm、厚さ:2mm)を作製した。この試験片を、HFC−134aまたはHFO−1234yfに40℃で24時間浸漬した後、取り出して、オーブン中で、150℃で1時間熱処理した。熱処理後の試験片の表面に発生したブリスタの個数を目視で計数した。この試験を3回行った。3回の試験中、ブリスタの個数の最大値が3個以下のものを耐ブリスタ性に優れると評価した。
Claims (10)
- 未架橋ゴムおよび架橋剤を含むシール用ゴム組成物の製造方法であって、未架橋ゴムを含む未架橋ゴム組成物を70〜110℃の温度で混練する混練工程を有することを特徴とするシール用ゴム組成物の製造方法。
- さらに、前記混練工程の後に、前記混練工程の混練の温度よりも低い温度で未架橋ゴム組成物を混練する混練工程を有することを特徴とする請求項1に記載の製造方法。
- 未架橋ゴム100質量部に対して1〜15質量部の金属酸化物を使用する請求項1または2に記載の製造方法。
- 未架橋ゴム100質量部に対して20〜200質量部の補強剤を使用する請求項1〜3のいずれか一項に記載の製造方法。
- 70〜110℃の温度での混練時間が、3〜20分である請求項1〜4のいずれか一項に記載の製造方法。
- 未架橋ゴムが、エチレン−プロピレン−ジエン三元共重合体(EPDM)を含む請求項1〜5のいずれか一項に記載の製造方法。
- 車載エアコン用コンプレッサーのシールに使用されるシール用ゴム組成物を製造する請求項1〜6のいずれか一項に記載の製造方法。
- 前記車載エアコン用コンプレッサーが、HFO−1234yfを使用するものである請求項7に記載の製造方法。
- 請求項1〜8のいずれか一項に記載の製造方法によって得られたシール用ゴム組成物。
- 請求項9に記載のシール用ゴム組成物を架橋することによって得られたシール。