JP2012512806A - Cmas緩和組成、cmas緩和組成を備える環境バリアコーティング、およびcmas緩和組成を備えるセラミック構成部品 - Google Patents
Cmas緩和組成、cmas緩和組成を備える環境バリアコーティング、およびcmas緩和組成を備えるセラミック構成部品 Download PDFInfo
- Publication number
- JP2012512806A JP2012512806A JP2011542209A JP2011542209A JP2012512806A JP 2012512806 A JP2012512806 A JP 2012512806A JP 2011542209 A JP2011542209 A JP 2011542209A JP 2011542209 A JP2011542209 A JP 2011542209A JP 2012512806 A JP2012512806 A JP 2012512806A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- cmas
- rare earth
- component
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【選択図】図1
Description
12 EBC
14 ケイ素接合コーティング層
15 シリカ層
16 移行層
18 外層
20 CMAS緩和層
22 磨耗性の層
120 一体化したCMAS緩和層
Claims (22)
- 亜鉛アルミネートスピネル、アルカリ土類ジルコネート、アルカリ土類ハフネート、希土類没食子酸塩、緑柱石、およびそれらの組合せからなる群から選択されるカルシウムマグネシウムアルミノシリケート(CMAS)緩和組成であって、
前記CMAS緩和組成が高温基板構成部品用の環境バリアコーティング内に別個のCMAS緩和層として含まれる、CMAS緩和組成。 - 亜鉛アルミネートスピネル、アルカリ土類ジルコネート、アルカリ土類ハフネート、ハフニウムシリケート、ジルコニウムシリケート、希土類没食子酸塩、希土類ホスフェート、酸化タンタル、緑柱石、アルカリ土類アルミネート、希土類アルミネート、およびそれらの組合せからなる群から選択されるCMAS緩和組成であって、
前記CMAS緩和組成が高温基板構成部品用の環境バリアコーティング内に一体化したCMAS緩和層として含まれる、CMAS緩和組成。 - 接合コーティング層と、
任意選択のシリカ層と、
少なくとも1つの移行層と、
任意選択の外層と、
亜鉛アルミネートスピネル、アルカリ土類ジルコネート、アルカリ土類ハフネート、希土類没食子酸塩、緑柱石、およびそれらの組合せからなる群から選択されるCMAS緩和組成を備える別個のCMAS緩和層とを備える、CMAS緩和能力を有する環境バリアコーティング(EBC)。 - 前記接合コーティング層がケイ素を含み、前記移行層がムライト、バリウムストロンチウムアルミノシリケート(BSAS)、希土類ジシリケート、およびそれらの組合せからなる群から選択される組成を含み、前記外層がBSAS、希土類モノシリケート、希土類ジシリケート、およびそれらの組合せからなる群から選択される外層材料を含む、請求項3記載のEBC。
- 前記別個のCMAS緩和層に付着された磨耗性の層をさらに備える、請求項4記載のEBC。
- 請求項3記載の前記EBCを備える、燃焼器構成部品、タービンブレード、シュラウド、ノズル、熱シールドおよびベーンからなる群から選択されるタービンエンジン構成部品。
- 接合コーティング層と、
任意選択のシリカ層と、
少なくとも1つの移行層と、
任意選択の外層と、
一体化したCMAS緩和層であって、
BSAS、希土類モノシリケート、希土類ジシリケート、およびそれらの組合せからなる群から選択される少なくとも1つの外層材料と、
亜鉛アルミネートスピネル、アルカリ土類ジルコネート、アルカリ土類ハフネート、ハフニウムシリケート、ジルコニウムシリケート、希土類没食子酸塩、希土類ホスフェート、酸化タンタル、緑柱石、アルカリ土類アルミネート、希土類アルミネート、およびそれらの組合せからなる群から選択されるCMAS緩和組成とを備える、一体化したCMAS緩和層とを備える、CMAS緩和能力を有するEBC。 - 前記一体化したCMAS緩和層が、前記外層材料内の粒界相として、または前記外層材料内の分散した難溶性粒子としての前記CMAS緩和組成を含む、請求項7記載のEBC。
- 前記接合コーティング層がケイ素を含み、前記移行層がムライト、BSAS、希土類ジシリケート、およびそれらの組合せからなる群から選択される組成を含み、前記外層が前記外層材料のうちの少なくとも1つを含む、請求項8記載のEBC。
- 前記別個のCMAS緩和層に付着された磨耗性の層をさらに備える、請求項9記載のEBC。
- 請求項8記載の前記EBCを備える、燃焼器構成部品、タービンブレード、シュラウド、ノズル、熱シールドおよびベーンからなる群から選択されるタービンエンジン構成部品。
- 接合コーティング層と、
任意選択のシリカ層と、
少なくとも1つの移行層と、
任意選択の外層と、
亜鉛アルミネートスピネル、アルカリ土類ジルコネート、アルカリ土類ハフネート、希土類没食子酸塩、緑柱石、およびそれらの組合せからなる群から選択されるCMAS緩和組成を含む別個のCMAS緩和層とを含む、
環境バリアコーティングを備える、CMAS緩和能力を有する高温構成部品。 - 前記接合コーティング層がケイ素を含み、前記移行層がムライト、BSAS、希土類ジシリケート、およびそれらの組合せからなる群から選択される組成を含み、前記外層がBSAS、希土類モノシリケート、希土類ジシリケート、およびそれらの組合せからなる群から選択される外層材料を含む、請求項12記載の構成部品。
- セラミック母組織複合材料またはモノリシックセラミックを備える、請求項13記載の構成部品。
- 燃焼器構成部品、タービンブレード、シュラウド、ノズル、熱シールドおよびベーンからなる群から選択されるタービンエンジン構成部品を含む、請求項14記載の構成部品。
- 前記別個のCMAS緩和層に付着された磨耗性の層をさらに備える、請求項15記載の構成部品。
- 接合コーティング層と、
任意選択のシリカ層と、
少なくとも1つの移行層と、
任意選択の外層と、
一体化したCMAS緩和層であって、
BSAS、希土類モノシリケート、希土類ジシリケート、およびそれらの組合せからなる群から選択される少なくとも1つの外層材料と、
亜鉛アルミネートスピネル、アルカリ土類ジルコネート、アルカリ土類ハフネート、ハフニウムシリケート、ジルコニウムシリケート、希土類没食子酸塩、希土類ホスフェート、酸化タンタル、緑柱石、アルカリ土類アルミネート、希土類アルミネート、およびそれらの組合せからなる群から選択されるCMAS緩和組成を含む一体化したCMAS緩和層とを含む、環境バリアコーティングを備える、CMAS緩和能力を有する高温構成部品。 - 前記接合コーティング層がケイ素を含み、前記移行層がムライト、BSAS、希土類ジシリケート、およびそれらの組合せからなる群から選択される組成を含み、前記外層が前記外層材料のうちの少なくとも1つを含む、請求項17記載の構成部品。
- 前記一体化したCMAS緩和層が、前記外層材料内の粒界相として、または前記外層材料内の分散した難溶性粒子としての前記CMAS緩和組成を含む、請求項18記載の構成部品。
- 前記基板構成部品がセラミック母組織複合材料またはモノリシックセラミックである、請求項19記載の構成部品。
- 燃焼器構成部品、タービンブレード、シュラウド、ノズル、熱シールドおよびベーンからなる群から選択されるタービンエンジン構成部品を含む、請求項20記載の構成部品。
- 前記別個のCMAS緩和層に付着された磨耗性の層をさらに備える、請求項21記載の構成部品。