JP2012002763A - コンクリート硬化体の乾燥収縮推定方法 - Google Patents
コンクリート硬化体の乾燥収縮推定方法 Download PDFInfo
- Publication number
- JP2012002763A JP2012002763A JP2010140011A JP2010140011A JP2012002763A JP 2012002763 A JP2012002763 A JP 2012002763A JP 2010140011 A JP2010140011 A JP 2010140011A JP 2010140011 A JP2010140011 A JP 2010140011A JP 2012002763 A JP2012002763 A JP 2012002763A
- Authority
- JP
- Japan
- Prior art keywords
- drying
- concrete
- material age
- shrinkage strain
- dry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】コンクリート硬化体の乾燥収縮ひずみを推定する方法は、コンクリート硬化体と同一のコンクリート材料を用いて作製したコンクリート供試体の乾燥収縮ひずみを第1の乾燥材齢及び第2の乾燥材齢において測定し、コンクリート供試体の乾燥収縮ひずみの測定値に基づいて、コンクリート硬化体の所定の乾燥材齢における乾燥収縮ひずみを推定する。
【選択図】なし
Description
本実施形態に係るコンクリート硬化体の乾燥収縮ひずみ推定方法においては、まず、当該コンクリート硬化体と同一の材料(セメント、骨材、混和材、混和剤等)を用い、同一の配合に基づいてコンクリート供試体を作製する。
北海道から中国地方までに存在する任意の生コンクリート工場において製造されたコンクリートのうちランダムに選択した96種のコンクリート試料(使用セメント:普通ポルトランドセメント(太平洋セメント社製)80種,高炉セメント(太平洋セメント社製)13種,中庸熱ポルトランドセメント(太平洋セメント社製)3種)の乾燥収縮ひずみ(乾燥材齢:3日、7日、9日、11日、14日、17日、19日、21日、24日、26日、28日、30日、32日、35日、42日、56日、91日及び182日)をJIS−A1129に準拠して測定した。なお、上記コンクリート試料96種における水セメント比は、33.5〜56.0%であった。また、供試体サイズは、100×100×400mmとした。
試験例1において得られた測定データ(乾燥材齢:7日、9日、11日、14日、28日、35日、56日及び91日)を用い、上記式(1)及び(2);式(3)に基づいて乾燥材齢182日における乾燥収縮ひずみ推定値を算出した。算出した乾燥収縮ひずみ推定値(乾燥材齢182日)と乾燥収縮ひずみ実測値(乾燥材齢182日)との関係を示すグラフを図3及び4に示す。なお、図3は、式(1)及び(2)に基づいて算出した乾燥収縮ひずみ推定値と乾燥収縮ひずみ実測値との関係を示すグラフであり、図4は、式(3)に基づいて算出した乾燥収縮ひずみ推定値と実測値との関係を示すグラフである。
[1]コンクリート供試体の作製
セメントC(普通ポルトランドセメント(試料1〜28)、高炉セメント(試料29〜33)又は中庸熱ポルトランドセメント(試料34〜38);いずれも太平洋セメント社製)と、細骨材S及び粗骨材Gとを20秒間混練した。その後、水W、並びに膨張材EX(製品名:ハイパーエクスパン,太平洋マテリアル社製)及び/又は収縮低減剤SRA(製品名:テトラガードAS21,太平洋マテリアル社製)を投入して60秒間混練し、掻落し後にさらに60秒間混練して、型枠に打設してコンクリート供試体(試料1〜38)を作製した。各コンクリート供試体の配合、並びに使用した粗骨材及び細骨材の種類を表1に示す。
上述のようにして得られたコンクリート供試体(試料1〜38)を標準水中養生し、JIS−A1129に準拠して、乾燥材齢7日、28日及び182日における乾燥収縮ひずみを測定した。
上述のようにして得られたコンクリート供試体(試料1〜38)について、上記乾燥収縮ひずみの実測値(乾燥材齢7日、28日)を用いて、上記式(1)及び(2);式(3)に基づいて乾燥材齢182日における乾燥収縮ひずみ推定値を算出した。上記乾燥収縮ひずみ推定値と上記乾燥収縮ひずみ実測値(乾燥材齢182日)との関係を図5に示す。
Claims (4)
- コンクリート硬化体の乾燥収縮を推定する方法であって、
前記コンクリート硬化体と同一のコンクリート材料を用いて作製したコンクリート供試体の乾燥収縮ひずみを少なくとも第1の乾燥材齢及び第2の乾燥材齢のそれぞれにおいて測定し、前記コンクリート供試体の第1の乾燥材齢及び第2の乾燥材齢のそれぞれにおける乾燥収縮ひずみ測定値に基づいて、前記コンクリート硬化体の所定の乾燥材齢における乾燥収縮ひずみを推定することを特徴とするコンクリート硬化体の乾燥収縮推定方法 - 前記第2の乾燥材齢が、10〜35日であることを特徴とする請求項1に記載のコンクリート硬化体の乾燥収縮推定方法。
- 前記第1の乾燥材齢から前記第2の乾燥材齢までの期間が、3〜30日間であることを特徴とする請求項1又は2に記載のコンクリート硬化体の乾燥収縮推定方法。
- 前記コンクリート供試体の第1の乾燥材齢及び第2の乾燥材齢における乾燥収縮ひずみ測定値から下記式(1)及び(2)に基づいて、前記コンクリート硬化体の所定の乾燥材齢における乾燥収縮ひずみ推定値を算出することを特徴とする請求項1〜3のいずれかに記載のコンクリート硬化体の乾燥収縮推定方法。
式(1)中、εtnは「所定の乾燥材齢(tn)におけるコンクリート硬化体の乾燥収縮ひずみの推定値(×10−6)」を表し、εt1は「第1の乾燥材齢(t1)におけるコンクリート供試体の乾燥収縮ひずみの測定値(×10−6)」を表し、εt2は「第2の乾燥材齢(t2)におけるコンクリート供試体の乾燥収縮ひずみの測定値(×10−6)」を表し、Vは「コンクリート供試体の体積(mm3)」を表し、Sは「コンクリート供試体の外気に接する表面積(mm2)」を表し、Aは「第1の乾燥材齢(t1)及び第2の乾燥材齢(t2)に応じて定まる係数」を表す。
式(2)中、t1は「第1の乾燥材齢」を表し、t2は「第2の乾燥材齢」を表す。