JP2009285874A - Decorative sheet and its manufacturing method - Google Patents

Decorative sheet and its manufacturing method Download PDF

Info

Publication number
JP2009285874A
JP2009285874A JP2008137957A JP2008137957A JP2009285874A JP 2009285874 A JP2009285874 A JP 2009285874A JP 2008137957 A JP2008137957 A JP 2008137957A JP 2008137957 A JP2008137957 A JP 2008137957A JP 2009285874 A JP2009285874 A JP 2009285874A
Authority
JP
Japan
Prior art keywords
sheet
decorative
layer
printing
vapor deposition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2008137957A
Other languages
Japanese (ja)
Other versions
JP4906783B2 (en
Inventor
Hiroyuki Negishi
宏幸 根岸
Original Assignee
Peg:Kk
株式会社ピーイージー
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Peg:Kk, 株式会社ピーイージー filed Critical Peg:Kk
Priority to JP2008137957A priority Critical patent/JP4906783B2/en
Publication of JP2009285874A publication Critical patent/JP2009285874A/en
Application granted granted Critical
Publication of JP4906783B2 publication Critical patent/JP4906783B2/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

<P>PROBLEM TO BE SOLVED: To provide a decorative sheet having a mirror which forms a mirror surface as viewed from the substrate sheet and allows the see-through of a pattern on the protective layer through the mirror when illuminated from the side of the protective layer and its manufacturing method. <P>SOLUTION: The decorative sheet 1 has at least a vapor-deposited layer 4, the protective layer 5 and the first decorative portion in order on the upper surface of a transparent substrate sheet 2. The vapor-deposited layer 4 forms a mirror surface as viewed from the substrate sheet 2 and has such a film thickness that allows the see-through of a pattern of the first decorative portion on the protective layer 5 through the vapor-deposited layer 4 when illuminated from the side of the protective layer 5. A colored layer 3 may be formed between the substrate sheet 2 and the vapor-deposited layer. Resist printed portions are formed by applying resist-printing to a part to be printed of the protective layer 5. After the layer laminated in a part other than the resist-printed part is removed by etching, the first decorative portion may be formed on the resist-printed part. <P>COPYRIGHT: (C)2010,JPO&INPIT

Description

本発明は、加飾シートおよびその製造方法に関し、詳しくは、鏡面部分を有し、この鏡面部分が、基材シートからみたとき鏡面を形成し、保護層側から照明を当てた際、保護層上の図柄を透視することができる視覚的多様性を実現した加飾シートおよびその製造方法に関する。   The present invention relates to a decorative sheet and a method for producing the same, and in particular, has a mirror surface portion, and this mirror surface portion forms a mirror surface when viewed from the base material sheet, and when the illumination is applied from the protective layer side, the protective layer The present invention relates to a decorative sheet that realizes visual diversity through which the above pattern can be seen and a method for manufacturing the decorative sheet.

透明なシート基材に透明カラーの着色層、例えば、透明黄色の着色層を施し、かかるシート基材に金属蒸着層を積層することで、全体が鏡面状の金色のシートを形成することができる。また、透明なシート基材に直接金属蒸着層を積層することにより、鏡面状の銀色のシートを形成することができる。さらに、このようにして形成されたシートに必要な部分を残して着色層および蒸着層をエッチングにより除去し、除去した部分に加飾を施すことにより、部分的に鏡面部を有する加飾シートを形成することができる。   By applying a transparent colored layer, for example, a transparent yellow colored layer to a transparent sheet base material, and laminating a metal vapor deposition layer on the sheet base material, a mirror-like gold sheet can be formed as a whole. . Moreover, a mirror-like silver sheet can be formed by directly laminating a metal vapor deposition layer on a transparent sheet substrate. Furthermore, the coloring layer and the vapor deposition layer are removed by etching, leaving necessary portions on the sheet formed in this way, and a decorative sheet partially having a mirror surface is obtained by decorating the removed portion. Can be formed.

これら部分的に鏡面を有する加飾シートは、外観的な優雅さを醸し出すと共に、人の目を引きやすいため、電化製品、インテリア、照明器具、携帯電話等の装飾や広告として幅広く使用されている。   These decorative sheets that have a partially mirrored surface bring out the elegance of the appearance and are easy to catch people's eyes, so they are widely used as decorations and advertisements for appliances, interiors, lighting fixtures, mobile phones, etc. .

その他、スロットマシンやパチンコ等の遊技機のホイルシートやパネルにおいても、赤や青等の複数の色彩を有する図柄が施された加飾シートが使用されている。特に、大当たりや中当たりの図柄には、遊戯者に視覚的刺激を与えるために、図柄の一部に光沢を有する金色や銀色の鏡面を施すことは広く行われている。 In addition, decorative sheets with a plurality of colors such as red and blue are used in foil sheets and panels of gaming machines such as slot machines and pachinko machines. In particular, in order to give a visual stimulus to the player on the jackpot or middle hit symbol, it is widely practiced to give a glossy gold or silver mirror surface to a part of the symbol.

例えば、特許文献1には、上述の図柄や色彩を有する加飾シートにおいて、絵柄層の形成を部分金属蒸着層の形成と同時に行い、両者を正確に同調させ、特に部分金属蒸着層の端部と同調させることで、絵柄層端部も鮮明でシャープに形成することができる化粧シートの製造方法が提案されている。   For example, in Patent Document 1, in the decorative sheet having the above-described design and color, the pattern layer is formed simultaneously with the formation of the partial metal vapor deposition layer, and the both are accurately synchronized. A method for manufacturing a decorative sheet has been proposed in which the edge of the pattern layer can be formed clearly and sharply by synchronizing with the above.

かかる化粧シートの製造方法では、耐熱性基材の片面に耐熱性樹脂層を設け、該樹脂層上の全面に金属蒸着層を設けた後、該金属蒸着層上の蒸着必要箇所に耐酸又は耐アルカリ性を有し且つ金属蒸着層と密着性の良いインキにて透明レジスト層を形成し、次いで、少なくとも該レジスト層上に金属蒸着層と密着性の弱い印刷用インキにて絵柄層を形成し、しかる後、酸又はアルカリ溶液に浸漬して上記レジスト層の非形成部分の金属蒸着層を溶解除去して部分金属蒸着層を形成する。   In such a method for producing a decorative sheet, a heat-resistant resin layer is provided on one surface of a heat-resistant substrate, a metal vapor deposition layer is provided on the entire surface of the resin layer, and then an acid-proof or A transparent resist layer is formed with an ink having alkalinity and good adhesion to the metal vapor deposition layer, and then a pattern layer is formed at least on the resist layer with a printing ink having low adhesion to the metal vapor deposition layer, Thereafter, it is immersed in an acid or alkali solution to dissolve and remove the metal deposition layer on the non-formed portion of the resist layer, thereby forming a partial metal deposition layer.

また、特許文献2には、エッチングにより容易に複雑な図形等を加工でき、その上に加飾印刷をすることができるエッチングホイルシート及びその製造方法が提案されている。かかるエッチングホイルシートは、合成樹脂製の可撓性のある透明な基材シート上に透明な着色層が形成され、その上に金属蒸着層が形成され、その上に前記蒸着層の保護層が形成されると共に、前記着色層、前記蒸着層及び前記保護層はアルカリ可溶性を有する。   Further, Patent Document 2 proposes an etching foil sheet and a method for manufacturing the same, which can easily process a complicated figure or the like by etching and can perform decorative printing thereon. In such an etching foil sheet, a transparent colored layer is formed on a flexible transparent base sheet made of synthetic resin, a metal vapor deposition layer is formed thereon, and a protective layer for the vapor deposition layer is formed thereon. While being formed, the colored layer, the vapor deposition layer, and the protective layer have alkali solubility.

さらに、特許文献3には、優れた外観、優れた美観、各種耐久性等に優れた部分蒸着化粧シートを容易に提供することを目的とした部分蒸着化粧シートの製造方法が提案されている。かかる蒸着化粧シートの製造方法は、エッチングレジストが、形成される塗膜の表面に微細な凹凸を形成し得る実質上無色の粒子を含有している。
特開昭64−47847号公報(特許請求の範囲等) 特許第2812354号公報(特許請求の範囲等) 特許第3313741号公報(特許請求の範囲等)
Furthermore, Patent Document 3 proposes a method for producing a partially vapor-deposited decorative sheet for the purpose of easily providing a partial vapor-deposited decorative sheet having excellent appearance, excellent aesthetics, various durability, and the like. In such a method for producing a vapor-deposited decorative sheet, the etching resist contains substantially colorless particles that can form fine irregularities on the surface of the coating film to be formed.
JP-A 64-47847 (Claims etc.) Japanese Patent No. 2812354 (Claims etc.) Japanese Patent No. 3313741 (Claims etc.)

しかしながら、特許文献1記載の製造方法により製造される化粧シートは、耐熱性基材側からみた場合、レジスト層を施した箇所は金属蒸着層の銀色が直接視認されるため、鏡面部の彩を向上させることはできなかった。また、鏡面部に金色を表現するには、真鍮等の金色を有する素材を塗布または蒸着させる必要があり、コスト高になるという欠点もあった。   However, the decorative sheet manufactured by the manufacturing method described in Patent Document 1, when viewed from the heat-resistant substrate side, the silver color of the metal vapor deposition layer is directly visible at the location where the resist layer is applied, so It could not be improved. In addition, in order to express gold on the mirror surface portion, it is necessary to apply or vapor-deposit a material having a gold color such as brass, which has a disadvantage of increasing the cost.

また、特許文献2記載のエッチングホイルシートにおいては、単なる鏡面部と加飾部との組み合わせに過ぎず、鏡面部分での更なる高い視覚的刺激や意外性を演出するには必ずしも十分とはいえなかった。   Moreover, in the etching foil sheet | seat of patent document 2, it is only a combination of a mere mirror surface part and a decoration part, and it may be said that it is not enough to produce the further high visual irritation | stimulation and unexpectedness in a mirror surface part. There wasn't.

また、特許文献3記載の蒸着化粧シートの製造方法においては、基材シートから視た際、レジスト部分における色彩は銀鏡面に限定される。また、銀鏡面以外の鏡面色を施すには、エッチングレジスト後に印刷模様を印刷するため、蒸着部分と着色部分の繊細な合わせに難があり、複雑なイラストの表現はできない。さらに、製造工程が多くなりコスト高になるという問題もあった。   Moreover, in the manufacturing method of the vapor deposition decorative sheet of patent document 3, when it sees from a base material sheet, the color in a resist part is limited to a silver mirror surface. Further, in order to apply a mirror color other than the silver mirror surface, a printed pattern is printed after the etching resist, so that it is difficult to delicately match the vapor deposition part and the colored part, and a complicated illustration cannot be expressed. Furthermore, there is a problem that the manufacturing process is increased and the cost is increased.

そこで、本発明の目的は、上記の課題を解決するために、シートに施された鏡面部分の多様性を実現することで、より高い視覚的刺激や意外性を演出することができる加飾シートとその製造方法を提供することにある。   Accordingly, an object of the present invention is to provide a decorative sheet that can produce higher visual stimulation and unexpectedness by realizing a variety of mirror surface portions applied to the sheet in order to solve the above-described problems. And providing a manufacturing method thereof.

上記課題を解決するために、本発明の加飾シートは、透明な基材シート上面に、順次、少なくとも蒸着層と保護層と第1加飾部とが形成されてなる加飾シートであって、前記蒸着層が、基材シートからみたとき鏡面を形成し、かつ、保護層側から照明を当てた際、保護層上の前記第1加飾部の図柄を透視することができる膜厚であることを特徴とするものである。   In order to solve the above problems, the decorative sheet of the present invention is a decorative sheet in which at least a vapor deposition layer, a protective layer, and a first decorative portion are sequentially formed on the transparent base sheet upper surface. When the vapor deposition layer forms a mirror surface when viewed from the base material sheet and is illuminated from the protective layer side, the film thickness allows the first decorative part on the protective layer to be seen through. It is characterized by being.

本発明の加飾シートにおいては、前記蒸着層の膜厚が0.015〜0.035μmであることが好ましく、また、前記基材シートと蒸着層との間に着色層が形成されていてもよい。   In the decorative sheet of the present invention, the thickness of the vapor deposition layer is preferably 0.015 to 0.035 μm, and even if a colored layer is formed between the base material sheet and the vapor deposition layer. Good.

また、本発明の加飾シートにおいては、前記保護層上の必要な部分にレジスト印刷によりレジスト印刷部が形成され、該レジスト印刷部以外の部分に積層された層がエッチングにより除去された後、前記レジスト印刷部上に前記第1加飾部が施されていてもよく、さらに、前記エッチングにより除去されたエッチング除去部に加飾印刷が施され、第2加飾部が形成されていることが好ましい。さらにまた、前記レジスト印刷部および前記エッチング除去部に加飾印刷が施され、第1加飾部および第2加飾部が形成されていてもよい。   Further, in the decorative sheet of the present invention, a resist printing portion is formed by resist printing on a necessary portion on the protective layer, and a layer laminated on a portion other than the resist printing portion is removed by etching, The first decorative portion may be provided on the resist printing portion, and further, decorative printing is performed on the etching removal portion removed by the etching, so that a second decorative portion is formed. Is preferred. Furthermore, decorative printing may be performed on the resist printing part and the etching removal part, and a first decorative part and a second decorative part may be formed.

本発明の加飾シートは、好適には遊技機のエッチングホイルシートである。   The decorative sheet of the present invention is preferably an etching foil sheet of a gaming machine.

また、本発明の加飾シートの製造方法は、透明なロール状の基材シート上面に、順次、少なくとも蒸着層および保護層を積層し、次いでロール状のまま、又は枚葉に断裁した状態で前記保護層上の必要な部分にレジスト印刷によりレジスト印刷部を形成した後、エッチングにより該レジスト印刷部以外の部分に積層された層を除去してエッチング除去部を形成し、前記レジスト印刷部に第1加飾部を施すことを特徴とするものである。   In addition, the method for producing a decorative sheet according to the present invention is such that at least a vapor deposition layer and a protective layer are sequentially laminated on the upper surface of a transparent roll-shaped base sheet, and then in a roll shape or in a state of being cut into sheets. After forming a resist printing part by resist printing on a necessary part on the protective layer, an etching removal part is formed by removing a layer laminated on a part other than the resist printing part by etching, and the resist printing part The first decoration portion is applied.

本発明の製造方法においては、前記基材シートと蒸着層との間に着色層を形成してもよく、また、前記エッチング除去部を形成した後、前記レジスト印刷部に第1加飾部を施すと共に、前記エッチング除去部に加飾印刷を施し、第2加飾部を形成することができる。   In the manufacturing method of the present invention, a colored layer may be formed between the base sheet and the vapor deposition layer, and after forming the etching removal portion, a first decoration portion is formed on the resist printing portion. At the same time, decorative printing can be applied to the etching removal portion to form a second decoration portion.

本発明の加飾シートによれば、保護層側から照明を当てた際、鏡面が消え保護層上に加飾した図柄を蒸着層を介して透視することができるので、鏡面部から加飾した図柄が浮き出てくる。このように1枚のシートの同一箇所で反射と透過及び、鏡面と加飾部の色彩を変化させることができることから、シートに施された鏡面部分の多様性をこれまで以上に実現でき、視覚的刺激や意外性を演出することも可能になる。   According to the decorative sheet of the present invention, when the illumination is applied from the protective layer side, the mirror surface disappears and the design decorated on the protective layer can be seen through the vapor deposition layer, so the decorative surface is decorated from the mirror surface portion. The pattern comes out. In this way, reflection and transmission at the same location of one sheet and the color of the mirror surface and the decorative part can be changed, so that the diversity of the mirror surface part applied to the sheet can be realized more than ever, and visual It is also possible to produce sexual stimulation and unexpectedness.

以下に、図面を参照して本発明の実施の形態について説明する。
図1に示す本発明の好適例の加飾シート1は、透明な基材シート2の上面に、順次、着色層3、蒸着層4、保護層5が形成されている。また保護層5を形成した後、基材シート2の下面に粘着層10と剥離シート11が積層されているが、粘着層10および剥離シート11は必要に応じ適宜設ければよい。
Embodiments of the present invention will be described below with reference to the drawings.
In the decorative sheet 1 of the preferred embodiment of the present invention shown in FIG. 1, a colored layer 3, a vapor deposition layer 4, and a protective layer 5 are sequentially formed on the upper surface of a transparent base sheet 2. In addition, after the protective layer 5 is formed, the adhesive layer 10 and the release sheet 11 are laminated on the lower surface of the base material sheet 2, but the adhesive layer 10 and the release sheet 11 may be provided as appropriate.

本発明で使用し得る基材シート2は、透明な合成樹脂製フィルムであり、例えば、PENやPETなどのポリエステル、ポリエチレン、ポリプロピレン、ポリ塩化ビニル、ポリスチレン、ポリカーボネート、ポリイミド、ポリオレフィン等のプラスチックフィルムから適宜選定することができるが、印刷適性の観点からポリカーボネート、ポリエステル、ポリプロピレンが特に好ましい。また、基材シート2の厚さは、好ましくは12〜600μmである。   The base material sheet 2 that can be used in the present invention is a transparent synthetic resin film, for example, a polyester film such as PEN and PET, a plastic film such as polyethylene, polypropylene, polyvinyl chloride, polystyrene, polycarbonate, polyimide, and polyolefin. Although it can select suitably, a polycarbonate, polyester, and a polypropylene are especially preferable from a printable viewpoint. Moreover, the thickness of the base material sheet 2 becomes like this. Preferably it is 12-600 micrometers.

着色層3はアルカリ可溶性インキからなり、透明な基材シート2上面にグラビア、オフセット、ロールツーロール、フレキソ等の印刷をすることにより好適に形成される。例えば、鏡面状の金色の色彩を映し出す部分には着色層3として透明度のある黄色のインキで印刷すればよい。また、銀色の色彩を映し出す部分には、透明のインキで印刷するか、または着色層3を印刷しなければよい。さらに、着色層3に透明度のある茶色のインキで印刷すると鏡面状の銅色が映し出される。このように着色層3に印刷されるインキの色を調節することで、さまざまな鏡面状の色彩を施すことができる。   The colored layer 3 is made of an alkali-soluble ink, and is preferably formed by printing gravure, offset, roll-to-roll, flexo or the like on the upper surface of the transparent substrate sheet 2. For example, the colored layer 3 may be printed with a transparent yellow ink on a portion that reflects a mirror-like gold color. In addition, it is only necessary to print with a transparent ink or not to print the colored layer 3 on the portion where the silver color is projected. Further, when the colored layer 3 is printed with a transparent brown ink, a mirror-like copper color is projected. By adjusting the color of the ink printed on the colored layer 3 in this way, various specular colors can be applied.

また、着色層3の形成に際し、グラビア、オフセット、ロールツーロール、フレキソ等の印刷を用いることで、鏡面状の金色と銀色の入り乱れた繊細な画像を形成することができる。なお、着色層3の厚さも通常の印刷で形成される厚さでよく、例えば、0.5〜2μmが好適範囲である。   In addition, when the colored layer 3 is formed, a delicate image in which mirror-like gold and silver are mixed can be formed by using printing such as gravure, offset, roll-to-roll, flexo and the like. In addition, the thickness of the colored layer 3 may be a thickness formed by normal printing, and for example, 0.5 to 2 μm is a suitable range.

着色層3の上面には蒸着層4が形成されている。なお、図示はしないが、着色層3を形成しないときは基材シート2の上面に蒸着層4が形成される。この蒸着層4は、アルミニウムを加熱して蒸着させ、かかる蒸気を着色層3の表面に付着させるもので、蒸着層4を形成する手法としては、ルツボ方式、エレクトロビーム等の真空蒸着、またはイオンプレティーング、スパッタリングターゲットが使用される。   A vapor deposition layer 4 is formed on the upper surface of the colored layer 3. Although not shown, when the colored layer 3 is not formed, the vapor deposition layer 4 is formed on the upper surface of the base sheet 2. The vapor deposition layer 4 is a layer in which aluminum is heated and vapor-deposited, and the vapor is deposited on the surface of the colored layer 3. The vapor deposition layer 4 can be formed by a crucible method, vacuum vapor deposition such as electrobeam, or ion A plating or sputtering target is used.

蒸着層4の上面に形成された保護層5は、蒸着層4の表面が酸化したり、傷が発生したりするのを防ぐために、蒸着層4の上面に形成されるものである。この保護層5は、アルカリ可溶性の無色透明インキからなる。   The protective layer 5 formed on the upper surface of the vapor deposition layer 4 is formed on the upper surface of the vapor deposition layer 4 in order to prevent the surface of the vapor deposition layer 4 from being oxidized or scratched. The protective layer 5 is made of an alkali-soluble colorless transparent ink.

本発明の好適例の加飾シート1は、図2に示すように、保護層5の上面にレジスト印刷によりレジスト印刷部6が形成されている。かかるレジスト印刷部6は、耐アルカリ性の無色透明、または遮蔽性のインキからなる。またレジスト印刷部6は、加飾シート1において鏡面を施したい部分に施される。なお、レジスト印刷部6に遮光性のあるインキを用いることで、蒸着層4の反射のみを映し出すこともできる。   As shown in FIG. 2, the decorative sheet 1 of a preferred example of the present invention has a resist printing portion 6 formed on the upper surface of the protective layer 5 by resist printing. The resist printing portion 6 is made of an alkali-resistant colorless and transparent or shielding ink. Moreover, the resist printing part 6 is given to the part which wants to give a mirror surface in the decorating sheet 1. FIG. In addition, only the reflection of the vapor deposition layer 4 can be projected by using the ink which has light-shielding property for the resist printing part 6. FIG.

保護層5の上面にレジスト印刷部6を部分的に施すことにより、アルカリエッチングを施した際、図3に示すように、着色層3、蒸着層4、保護層5が除去され、エッチング除去部8が形成される。レジスト印刷部6は、オフセット印刷、スクリーン印刷、ロールツーロール、グラビア印刷、パッド印刷、フレキソ印刷等の方法により印刷される。なお、着色層3、蒸着層4、保護層5まではロール対応の印刷機であるロールツーロール、グラビア印刷、オフセット印刷、フレキソ印刷等の方法により印刷される。   When alkali etching is performed by partially applying a resist printing portion 6 on the upper surface of the protective layer 5, the colored layer 3, the vapor deposition layer 4, and the protective layer 5 are removed as shown in FIG. 8 is formed. The resist printing unit 6 is printed by a method such as offset printing, screen printing, roll-to-roll, gravure printing, pad printing, or flexographic printing. In addition, the coloring layer 3, the vapor deposition layer 4, and the protective layer 5 are printed by methods such as roll-to-roll, gravure printing, offset printing, and flexographic printing, which are roll-compatible printing machines.

次に、図4に示すように、レジスト印刷部6の上面には、第1加飾部7が形成されている。かかる第一加飾部7は、アルカリエッチング洗浄後に、適宜色彩のデザインを施すことにより形成される。この第1加飾部7は、保護層5側から照明Aを照射させた際、蒸着層4から透過され鏡面部aから映し出される(図6)。かかる第1加飾部7は、オフセット印刷、スクリーン印刷、ロールツーロール、グラビア印刷、パッド印刷、フレキソ印刷等の印刷により形成される。なお、レジスト印刷部6、第1加飾部7はロール形状対応または枚葉対応のロールツーロール、グラビア印刷、オフセット印刷、フレキソ印刷、スクリーン印刷、パッド印刷等の方法により印刷される。   Next, as shown in FIG. 4, a first decorating part 7 is formed on the upper surface of the resist printing part 6. The first decorative portion 7 is formed by appropriately designing the color after the alkali etching cleaning. When the illumination A is irradiated from the protective layer 5 side, the first decorative portion 7 is transmitted from the vapor deposition layer 4 and projected from the mirror surface portion a (FIG. 6). The first decorating unit 7 is formed by printing such as offset printing, screen printing, roll-to-roll, gravure printing, pad printing, flexographic printing, and the like. Note that the resist printing unit 6 and the first decorating unit 7 are printed by methods such as roll-to-roll, gravure printing, offset printing, flexographic printing, screen printing, pad printing, etc.

また、本発明の好適例の加飾シート1には、図5に示すように、エッチングにより除去されているエッチング除去部8に加飾印刷により第2加飾部9が形成されている。かかる第2加飾部9は、基材シート2側からみた際、赤や青等の通常の色彩が映し出される。なお、前記第2加飾部9には、透過性および遮光性のいずれのインキも使用することができる。   Moreover, as shown in FIG. 5, the decoration sheet 1 of the suitable example of this invention has the 2nd decoration part 9 formed by the decoration printing in the etching removal part 8 removed by the etching. When viewed from the base material sheet 2 side, the second decorating unit 9 projects normal colors such as red and blue. In addition, in the said 2nd decorating part 9, both a permeable and light-shielding ink can be used.

本発明においては、上述のように、蒸着層4を、保護層5側(内側)から照明を当てた際、レジスト印刷部6の第1加飾部7を透視することができる膜厚とすることが肝要である。かかる膜厚を施す方法としては、前記のスパッタリングターゲットにおけるアルミ材料の量の調節、またはルツボ方式における熱量および蒸着スピードの調節により行うことができ、これにより全光線透過率を管理することができる。   In this invention, as above-mentioned, when the vapor deposition layer 4 is illuminated from the protective layer 5 side (inner side), it is set as the film thickness which can see through the 1st decoration part 7 of the resist printing part 6. FIG. It is important. The film thickness can be adjusted by adjusting the amount of the aluminum material in the sputtering target, or by adjusting the amount of heat and vapor deposition speed in the crucible method, whereby the total light transmittance can be managed.

蒸着層4を、レジスト印刷部6の第1加飾部7を透視することができる膜厚とすることで、通常は図6に示すように、加飾シート1を基材シート2側(外側)から見た場合、蒸着層4にて反射し鏡面を形成する一方、図7に示すように、保護層5側(内側)から照明Aを当てると、鏡面部分が消え、レジスト印刷部6に施された第1加飾部7の図柄が蒸着層4を通して鏡面部aから浮き出てくる。このように、本発明では、鏡面部aにおける反射と透過及び、鏡面と加飾部の色彩を変化させることができる。   By making the vapor deposition layer 4 into the film thickness which can see through the 1st decorating part 7 of the resist printing part 6, normally, as shown in FIG. 6, the decorating sheet 1 is the base material sheet 2 side (outside) ), When reflected from the vapor deposition layer 4 to form a mirror surface, as shown in FIG. 7, when the illumination A is applied from the protective layer 5 side (inside), the mirror surface portion disappears and the resist printing unit 6 The applied design of the first decoration portion 7 comes out of the mirror surface portion a through the vapor deposition layer 4. Thus, in this invention, the reflection and permeation | transmission in the mirror surface part a and the color of a mirror surface and a decorating part can be changed.

かかる蒸着層4の膜厚は、好ましくは0.015〜0.035μmである。この膜厚が0.015μm未満であると、蒸着層に膜厚のムラが生じると共に、鏡面部aにおける反射効率が低下する。一方、0.035μmを超えると光透過性が得られなくなる。   The film thickness of the vapor deposition layer 4 is preferably 0.015 to 0.035 μm. If the film thickness is less than 0.015 μm, unevenness of the film thickness occurs in the vapor deposition layer, and the reflection efficiency at the mirror surface portion a decreases. On the other hand, if it exceeds 0.035 μm, light transmittance cannot be obtained.

本発明の他の好適例を図8乃至図10に示す。基材シート2、着色層3、蒸着層4、保護層5からなる加飾シート1において、保護層5の必要な部分上面にレジスト印刷部6を形成し、レジスト印刷部6が形成されている領域を残して着色層3、蒸着層4、保護層5をアルカリエッチングにより除去し、レジスト印刷部6およびエッチング除去部8に加飾印刷により同時に第2加飾部9が形成されている。この場合、前記第2加飾部9が透過性のインキであれば、鏡面部a部分において第2加飾部9が透けるが、第2加飾部9が遮光性のインキであれば、鏡面部a部分は反射となる。   Another preferred embodiment of the present invention is shown in FIGS. In the decorative sheet 1 composed of the base material sheet 2, the colored layer 3, the vapor deposition layer 4, and the protective layer 5, the resist printing part 6 is formed on the upper surface of the necessary part of the protective layer 5, and the resist printing part 6 is formed. The colored layer 3, the vapor deposition layer 4, and the protective layer 5 are removed by alkali etching while leaving a region, and the second decorative portion 9 is simultaneously formed on the resist printing portion 6 and the etching removal portion 8 by decorative printing. In this case, if the second decorative portion 9 is transmissive ink, the second decorative portion 9 is transparent in the mirror surface portion a, but if the second decorative portion 9 is light-shielding ink, the mirror surface is used. The part a is reflected.

本発明の加飾シートは、電化製品、インテリア、照明器具、装飾ケース、化粧ケース、携帯電話、また遊技機のエッチングホイルシートに使用されるもので、特に、加飾シートに施された鏡面部分の多様性を実現することができる。   The decorative sheet of the present invention is used for electrical appliances, interiors, lighting fixtures, decorative cases, decorative cases, mobile phones, and etching foil sheets of gaming machines, and in particular, a mirror surface portion applied to the decorative sheet Can be realized.

本発明の加飾シートの断面図である。It is sectional drawing of the decorating sheet of this invention. 保護層上にレジスト印刷部を形成した状態の断面図である。It is sectional drawing of the state which formed the resist printing part on the protective layer. エッチングを施した状態の断面図である。It is sectional drawing of the state which gave the etching. レジスト印刷部に加飾部を施した状態の断面図である。It is sectional drawing of the state which gave the decoration part to the resist printing part. エッチング除去部に加飾印刷を施した状態の断面図である。It is sectional drawing of the state which gave decorative printing to the etching removal part. 基材シート側から見た鏡面部の反射状態を示す断面図である。It is sectional drawing which shows the reflective state of the mirror surface part seen from the base material sheet side. 保護層側から照射した際の鏡面部の状態を示す断面図である。It is sectional drawing which shows the state of the mirror surface part at the time of irradiating from the protective layer side. 他の好適例、保護層上にレジスト印刷部を形成した状態の断面図である。It is sectional drawing of the state which formed the resist printing part on another suitable example and a protective layer. 前記加飾シートにエッチングを施した状態の断面図である。It is sectional drawing of the state which etched the said decorating sheet. 前記加飾シートに加飾印刷を施した状態の断面図である。It is sectional drawing of the state which gave decorative printing to the said decorating sheet.

符号の説明Explanation of symbols

1 加飾シート
2 基材シート
3 着色層
4 蒸着層
5 保護層
6 レジスト印刷部
7 第1加飾部
8 エッチング除去部
9 第2加飾部
10 粘着層
11 剥離シート
A 照明
a 鏡面部
DESCRIPTION OF SYMBOLS 1 Decorating sheet 2 Base material sheet 3 Colored layer 4 Deposition layer 5 Protective layer 6 Resist printing part 7 1st decorating part 8 Etching removal part 9 2nd decorating part 10 Adhesive layer 11 Release sheet
A Lighting a Mirror surface

Claims (10)

透明な基材シート上面に、順次、少なくとも蒸着層と保護層と第1加飾部とが形成されてなる加飾シートであって、
前記蒸着層が、基材シートからみたとき鏡面を形成し、かつ、保護層側から照明を当てた際、保護層上の前記第1加飾部の図柄を透視することができる膜厚であることを特徴とする加飾シート。
A decorative sheet in which at least a vapor deposition layer, a protective layer, and a first decorative part are sequentially formed on the upper surface of the transparent base sheet,
When the vapor deposition layer is viewed from the substrate sheet, it forms a mirror surface, and when illuminated from the protective layer side, it is a film thickness that allows the design of the first decorative portion on the protective layer to be seen through. A decorative sheet characterized by that.
前記蒸着層の膜厚が0.015〜0.035μmである請求項1記載の加飾シート。   The decorative sheet according to claim 1, wherein the vapor deposition layer has a thickness of 0.015 to 0.035 μm. 前記基材シートと蒸着層との間に着色層が形成されている請求項1または2記載の加飾シート。   The decorative sheet according to claim 1, wherein a colored layer is formed between the base sheet and the vapor deposition layer. 前記保護層上の必要な部分にレジスト印刷によりレジスト印刷部が形成され、該レジスト印刷部以外の部分に積層された層がエッチングにより除去された後、前記レジスト印刷部上に前記第1加飾部が施されている請求項1乃至3のうちいずれか1項記載の加飾シート。   A resist printing part is formed by resist printing on a necessary part on the protective layer, and a layer laminated on a part other than the resist printing part is removed by etching, and then the first decoration is formed on the resist printing part. The decorative sheet according to any one of claims 1 to 3, wherein a portion is provided. 前記エッチングにより除去されたエッチング除去部に加飾印刷が施され、第2加飾部が形成されている請求項4記載の加飾シート。   The decorative sheet according to claim 4, wherein decorative printing is performed on the etching removed portion removed by the etching, and a second decorative portion is formed. 前記レジスト印刷部および前記エッチング除去部に加飾印刷が施され、第1加飾部および第2加飾部が形成されている請求項5記載の加飾シート。   The decorative sheet according to claim 5, wherein decorative printing is performed on the resist printing portion and the etching removal portion, and a first decorative portion and a second decorative portion are formed. 遊技機のエッチングホイルシートである請求項1乃至6のうちいずれか1項記載の加飾シート。   The decorative sheet according to any one of claims 1 to 6, which is an etching foil sheet for a gaming machine. 透明なロール状の基材シート上面に、順次、少なくとも蒸着層および保護層を積層し、次いでロール状のまま、又は枚葉に断裁した状態で前記保護層上の必要な部分にレジスト印刷によりレジスト印刷部を形成した後、エッチングにより該レジスト印刷部以外の部分に積層された層を除去してエッチング除去部を形成し、前記レジスト印刷部に第1加飾部を施すことを特徴とする加飾シートの製造方法。   At least a vapor deposition layer and a protective layer are sequentially laminated on the upper surface of the transparent roll-shaped base sheet, and then a resist is printed by resist printing on a necessary portion on the protective layer in a roll-like state or cut into a sheet. After forming the printing portion, etching is performed to remove a layer laminated on a portion other than the resist printing portion to form an etching removal portion, and a first decoration portion is applied to the resist printing portion. A method for producing a decorative sheet. 前記基材シートと蒸着層との間に着色層を形成する請求項8記載の加飾シートの製造方法。   The manufacturing method of the decorating sheet of Claim 8 which forms a colored layer between the said base material sheet and a vapor deposition layer. 前記エッチング除去部を形成した後、前記レジスト印刷部に第1加飾部を施すと共に、前記エッチング除去部に加飾印刷を施し、第2加飾部を形成する請求項8または9記載の加飾シートの製造方法。   10. The process according to claim 8, wherein after the etching removal portion is formed, a first decoration portion is applied to the resist printing portion, and a decoration printing is applied to the etching removal portion to form a second decoration portion. A method for producing a decorative sheet.
JP2008137957A 2008-05-27 2008-05-27 Decorative sheet and manufacturing method thereof Expired - Fee Related JP4906783B2 (en)