JP2007282720A - Fabric for mask having moisture retentivity, and hygienic mask using it - Google Patents

Fabric for mask having moisture retentivity, and hygienic mask using it Download PDF

Info

Publication number
JP2007282720A
JP2007282720A JP2006111086A JP2006111086A JP2007282720A JP 2007282720 A JP2007282720 A JP 2007282720A JP 2006111086 A JP2006111086 A JP 2006111086A JP 2006111086 A JP2006111086 A JP 2006111086A JP 2007282720 A JP2007282720 A JP 2007282720A
Authority
JP
Japan
Prior art keywords
mask
woven
fabric
cloth
woven fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2006111086A
Other languages
Japanese (ja)
Inventor
Ei Sawa
映 佐波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nitto Denko Corp
Original Assignee
Nitto Denko Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nitto Denko Corp filed Critical Nitto Denko Corp
Priority to JP2006111086A priority Critical patent/JP2007282720A/en
Publication of JP2007282720A publication Critical patent/JP2007282720A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a fabric for a mask having a high moisture retentivity in the fabric for mask using a polytetrafluoroethylene porous film. <P>SOLUTION: This fabric for a mask has a laminated structure, and has the polytetrafluoroethylene porous film, and a woven or non-woven fabric having moisture retentivity. As the woven or non-woven fabric having moisture retentivity, a woven or non-woven fabric being formed of a natural fiber is preferably used. The fabric for mask preferably has a supporting layer as well. Also, the fabric for mask preferably has air permeability expressed by the number of flagyls of 150 cm/second or higher. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

本発明は、ポリテトラフルオロエチレン(以下、PTFEともいう)多孔質膜を用いたマスク用布および当該マスク用布を用いた衛生マスクに関し、より具体的には、保湿性が付加された、PTFE多孔質膜を用いたマスク用布および当該マスク用布を用いた衛生マスクに関する。   The present invention relates to a mask cloth using a polytetrafluoroethylene (hereinafter also referred to as PTFE) porous membrane and a sanitary mask using the mask cloth, and more specifically, PTFE to which moisture retention is added. The present invention relates to a mask cloth using a porous membrane and a sanitary mask using the mask cloth.

近年、インフルエンザ、SARSを始めとする新種の空気感染性伝染病の世界的な蔓延に伴い、衛生マスクに対する要求が高まっている。衛生マスク用布には、通常、ガーゼ等の織布、またはスパンボンド、スパンレース、サーマルボンド、メルトブローン等の不織布が用いられている。しかし、これらの織布、不織布の網目は、感染性を有するウイルスの付着した飛沫粒子よりも大きいことが多く、当該粒子の捕集効率に問題があった。   In recent years, demand for sanitary masks has increased with the global spread of new species of airborne infectious diseases such as influenza and SARS. As the sanitary mask fabric, a woven fabric such as gauze or a non-woven fabric such as spunbond, spunlace, thermal bond, or meltblown is usually used. However, the meshes of these woven fabrics and nonwoven fabrics are often larger than the droplet particles to which infectious viruses are attached, and there is a problem in the collection efficiency of the particles.

新しいマスク用布として、近年、PTFE多孔質膜を用いたものが注目を集めている(例えば、特許文献1〜3参照)。PTFE多孔質膜は、微細なPTFE繊維からなる極めて多数の細孔を有する膜であり、低い圧力損失と高い捕集効率を併せ持つ。このため、PTFE多孔質膜は、ウイルスの付着した飛沫粒子を高い効率でろ過除去することができ、一般にマスクに用いられるガーゼ等の織布、不織布よりもウイルス感染を防ぐことができるものである。   In recent years, a new mask cloth using a PTFE porous membrane has attracted attention (see, for example, Patent Documents 1 to 3). The PTFE porous membrane is a membrane having an extremely large number of pores made of fine PTFE fibers, and has both a low pressure loss and a high collection efficiency. For this reason, the porous PTFE membrane is capable of filtering and removing virus-attached droplet particles with high efficiency, and can prevent virus infection more than woven or non-woven fabric such as gauze generally used for masks. .

その一方、多くの病原性ウイルスにとって好適な環境は、乾燥状態であり、織布または不織布を用いたマスクは、呼気中の水分によって湿潤な状態となることにより、ウイルスの感染性を低下させている。ところが、PTFE多孔質膜は極めて薄く(<20μm)、気孔率の大きい(>80%)膜であるために、それ自体は水分の保持性がほとんどない。PTFE多孔質膜を用いたマスクは、捕集効率が高いものの、水分保持量が低いため、わずかに透過したインフルエンザウイルスの感染性を十分に低下させることができない。   On the other hand, the preferred environment for many pathogenic viruses is the dry state, and masks using woven or non-woven fabrics are moistened by moisture in exhaled air, thereby reducing the infectivity of the virus. Yes. However, since the PTFE porous membrane is a very thin membrane (<20 μm) and a high porosity (> 80%), it itself has little water retention. Although the mask using the PTFE porous membrane has a high collection efficiency, it has a low water retention amount, and therefore cannot sufficiently reduce the infectivity of the slightly permeated influenza virus.

また、PTFE多孔質膜は、撥水性であるために、呼気中に含まれる水分が膜中に保持されず、膜表面で凝結して水滴となり、着用者の口の周辺に付着して不快感を与える他、水滴が垂れてくると不快感のみならず美観をも損なうという問題もある。
実開昭57−134047号公報 実公平3−30129号公報 特開平11−267234号公報
In addition, since the PTFE porous membrane is water-repellent, moisture contained in the exhaled breath is not retained in the membrane, but condenses on the surface of the membrane to form water droplets and adheres to the periphery of the wearer's mouth. In addition to giving water, there is also a problem that drops of water damage not only discomfort but also beauty.
Japanese Utility Model Publication No. 57-134047 No. 3-30129 Japanese Patent Laid-Open No. 11-267234

上記事情に鑑み、本発明は、ポリテトラフルオロエチレン多孔質膜を用いたマスク用布において、水分保持能の高いマスク用布を提供することを課題とする。   In view of the above circumstances, an object of the present invention is to provide a mask cloth having a high moisture retention ability in a mask cloth using a polytetrafluoroethylene porous membrane.

上記目的を達成するために、本発明は、積層構造を有するマスク用布であって、ポリテトラフルオロエチレン多孔質膜、および保湿性を有する織布または不織布を有することを特徴とする。前記保湿性を有する織布または不織布は、好ましくは天然繊維より形成される。   In order to achieve the above object, the present invention is a mask fabric having a laminated structure, and is characterized by having a polytetrafluoroethylene porous membrane and a woven or non-woven fabric having moisture retention. The woven or non-woven fabric having moisturizing properties is preferably formed from natural fibers.

本発明の積層構造を有するマスク用布は、さらに支持層を有することが好ましい。この場合、マスク用布は、前記支持層が前記ポリテトラフルオロエチレン多孔質膜の両表面上に積層されており、前記支持層の少なくとも一面に保湿性を有する織布または不織布が積層されている構造を有することが最も好ましい。前記支持層としては、熱可塑性樹脂の繊維より形成される不織布が好ましく、前記保湿性を有する織布または不織布が木綿であることが特に好ましい。また、本発明のマスク用布は、フラジール数で表される通気度が150cm/秒以上であることが好ましい。   The mask cloth having the laminated structure of the present invention preferably further has a support layer. In this case, in the mask cloth, the support layer is laminated on both surfaces of the polytetrafluoroethylene porous membrane, and a woven or non-woven fabric having moisture retention is laminated on at least one surface of the support layer. Most preferably, it has a structure. The support layer is preferably a non-woven fabric formed of thermoplastic resin fibers, and the moisturizing woven fabric or non-woven fabric is particularly preferably cotton. In addition, the mask cloth of the present invention preferably has an air permeability expressed by Frazier number of 150 cm / second or more.

本発明のマスク用布を用いた衛生マスクもまた、本発明に包含され、前記マスク用布の前記保湿性を有する織布または不織布が、咽頭側に配置されていることが好ましい。   The sanitary mask using the mask cloth of the present invention is also included in the present invention, and it is preferable that the woven or non-woven fabric having the moisture retention property of the mask cloth is disposed on the pharynx side.

本発明のマスク用布によれば、ウイルスの付着した飛沫粒子の捕集効率が高く、かつ保湿性が高い衛生マスクを作成することができる。本発明の衛生マスクを着用した場合、呼気に自然に含まれる水分が、保湿性を有する織布または不織布に吸収されるが、マスク用布のPTFE多孔質膜により水分の蒸発が抑制されるため、通常の織布または不織布を用いたマスクよりも多い水分量が保持される。従って、PTFE多孔質膜を病原性ウイルスが通過した場合でも、マスク内部の湿潤な環境において不活性化されるので、感染の確率が極めて低減する。また、保湿性を有する織布または不織布が、呼気中の水分を吸収するために、凝結した水分が着用者の口の周辺に付着するということもない。従って、着用者は不快感を感じることがなく、また、美観上でも問題となる水滴が垂れるということもない。   According to the mask cloth of the present invention, it is possible to create a sanitary mask that has a high collection efficiency of droplet particles to which viruses are attached and that has high moisture retention. When the sanitary mask of the present invention is worn, moisture naturally contained in exhaled breath is absorbed by the woven or non-woven fabric having moisture retention, but evaporation of moisture is suppressed by the PTFE porous membrane of the mask fabric. More water content is retained than a mask using a normal woven fabric or non-woven fabric. Therefore, even when a pathogenic virus passes through the porous PTFE membrane, it is inactivated in a moist environment inside the mask, so that the probability of infection is greatly reduced. Further, since the woven or non-woven fabric having moisture retention absorbs moisture in the breath, the condensed moisture does not adhere to the periphery of the wearer's mouth. Therefore, the wearer does not feel uncomfortable, and water drops that pose a problem in terms of beauty are not dripped.

本発明のマスク用布は、PTFE多孔質膜、および保湿性を有する織布または不織布を有する。PTFE多孔質膜は、PTFEシートを延伸多孔化および焼成することによって得られるものであり、高い通気性と粒子捕集効率を併せ持つものである。本発明においては、マスク用布に従来用いられているPTFE多孔質膜およびそれと同等の特性を有するPTFE多孔質膜を用いることができ、PTFE多孔質膜は、最大孔径が30〜150μm、膜厚が0.002〜0.03mm、気孔率が85〜99%であることが好ましい。PTFE多孔質膜の通気度については、マスク用布全体で後述のフラジール数で表される通気度となるような通気度を選択することが好ましく、PTFE多孔質膜の通気度としてより好ましくは、後述のフラジール数で表される通気度で150cm/秒以上であり、さらに好ましくは300cm/秒以上である   The mask fabric of the present invention has a PTFE porous membrane and a woven or non-woven fabric having moisture retention. The PTFE porous membrane is obtained by stretching and firing a PTFE sheet, and has both high air permeability and particle collection efficiency. In the present invention, it is possible to use a PTFE porous membrane conventionally used for a mask cloth and a PTFE porous membrane having the same characteristics as the PTFE porous membrane, and the PTFE porous membrane has a maximum pore diameter of 30 to 150 μm and a film thickness. Is 0.002 to 0.03 mm, and the porosity is preferably 85 to 99%. As for the air permeability of the PTFE porous membrane, it is preferable to select an air permeability such that the air permeability represented by the number of fragiles described later is used for the entire mask cloth, and more preferably, the air permeability of the PTFE porous membrane is: The air permeability represented by the number of fragile described later is 150 cm / second or more, more preferably 300 cm / second or more.

保湿性を有する織布または不織布(以下、保湿層ともいう)は、呼気に含まれる水分を保持して、ウイルスを不活性化させる層として機能する。本発明において、織布または不織布が「保湿性を有する」とは、織布または不織布が「人間の呼気中の水分を吸着または吸収して保持することができる程度に親水性を有する」ことをいう。   A woven or non-woven fabric having moisture retention (hereinafter also referred to as a moisture retention layer) functions as a layer that retains moisture contained in exhaled air and inactivates viruses. In the present invention, the woven or non-woven fabric has “moisturizing” means that the woven or non-woven fabric is “hydrophilic enough to absorb or absorb moisture in human breath”. Say.

織布または不織布の素材および形態には、保湿性を有する限り特に制限はないが、保湿性を有する素材により形成される織布または不織布を使用するのがよい。保湿性を有する素材としては、−OH、−NH、−COOH等の極性基を繰り返し単位中に有する高分子化合物を主成分として含む素材等が挙げられる。当該素材の例としては、木綿、羊毛等の天然繊維、レーヨン等の再生繊維、ナイロン等の合成繊維が挙げられる。保湿層としては、天然繊維より形成される織布または不織布が好ましく、中でも木綿より形成される織布または不織布が好ましく、木綿から造られた医療ガーゼが最も好ましい。   The material and form of the woven or non-woven fabric are not particularly limited as long as it has moisture retention, but it is preferable to use a woven or nonwoven fabric formed of a material having moisture retention. Examples of the material having moisturizing properties include materials containing, as a main component, a polymer compound having a polar group such as —OH, —NH, and —COOH in the repeating unit. Examples of the material include natural fibers such as cotton and wool, regenerated fibers such as rayon, and synthetic fibers such as nylon. The moisturizing layer is preferably a woven fabric or non-woven fabric formed from natural fibers, more preferably a woven fabric or non-woven fabric formed from cotton, and most preferably a medical gauze made from cotton.

保湿層の目付量としては、100g/m2以上であることが好ましく、200〜350g/m2であることがより好ましい。 The basis weight of the moisturizing layer, is preferably 100 g / m 2 or more, and more preferably 200~350g / m 2.

また、保湿層は通気性が必要であり、マスク用布全体で後述のフラジール数で表される通気度となるような通気度のものを選択することが好ましい。   Further, the moisture retaining layer needs to be breathable, and it is preferable to select a layer having an air permeability such that the entire mask cloth has an air permeability represented by the number of fragile described later.

保湿層の厚みに関しては、十分な保湿性が得られる限り特に制限はないが、保湿効果の観点から厚手であることが好ましく、例えば、0.3〜3.0mmであり、より好ましくは0.5〜1.0mmである。   The thickness of the moisturizing layer is not particularly limited as long as sufficient moisturizing properties can be obtained, but it is preferably thick from the viewpoint of the moisturizing effect, for example, 0.3 to 3.0 mm, more preferably 0.00. 5 to 1.0 mm.

本発明のマスク用布は、強度を高めるために、支持層を有することが好ましい。PTFE多孔質膜は厚みが小さく気孔率が高いので、単体では強度不足となり得る場合があるためであり、また、保湿層を支持層と兼ねることも可能であるが、上記のように保湿層として好ましいものには強度の弱い素材が多く、強度不足となり得る場合があるためである。当該支持層は、衛生マスク作成時や衛生マスク使用時のダメージからPTFE多孔質膜を防護する保護材として機能する。   The mask cloth of the present invention preferably has a support layer in order to increase the strength. This is because the PTFE porous membrane has a small thickness and a high porosity, so that the strength alone may be insufficient, and the moisturizing layer can also serve as the support layer. This is because preferred materials include many materials having low strength, and the strength may be insufficient. The said support layer functions as a protective material which protects a PTFE porous membrane from the damage at the time of sanitary mask preparation or use of a sanitary mask.

支持層には、PTFE多孔質膜および保湿層より強度に優れた材料であり、通気性を有する材料を使用する。支持層は、積層構造のマスク用布の製造の利便性の観点から、熱溶着が可能である熱可塑性樹脂の繊維より形成されていることが好ましい。熱可塑性樹脂の例としては、ポリオレフィン(例、ポリエチレン、ポリプロピレン等)、ポリエステル、ポリアミド、芳香族ポリアミド、およびこれらの複合材が挙げられる。支持層の形態の例としては、フェルト、織布、不織布、メッシュ(網目状シート)等が挙げられる。支持層が不織布である場合は、これを構成する一部または全部の繊維が芯鞘構造の複合繊維であってもよく、この場合は、芯成分の融点が鞘成分の融点より高いものがよい。支持層としては、熱可塑性樹脂の繊維より形成される不織布が好ましく、当該熱可塑性樹脂の繊維が芯鞘構造を有する複合繊維であることがより好ましい。   For the support layer, a material that is stronger than the PTFE porous membrane and the moisture retention layer and has air permeability is used. The support layer is preferably formed from fibers of thermoplastic resin that can be heat-welded from the viewpoint of convenience in manufacturing a mask fabric having a laminated structure. Examples of the thermoplastic resin include polyolefin (eg, polyethylene, polypropylene, etc.), polyester, polyamide, aromatic polyamide, and composite materials thereof. Examples of the form of the support layer include felt, woven fabric, non-woven fabric, mesh (mesh sheet) and the like. When the support layer is a non-woven fabric, some or all of the fibers constituting the support layer may be a composite fiber having a core-sheath structure. In this case, the core component preferably has a higher melting point than the sheath component. . The support layer is preferably a nonwoven fabric formed from fibers of thermoplastic resin, and more preferably, the fibers of the thermoplastic resin are composite fibers having a core-sheath structure.

支持層は、マスク用布全体で後述のフラジール数で表される通気度となるような通気度のものを選択することが好ましい。   It is preferable to select a support layer having an air permeability such that the entire mask cloth has an air permeability represented by the number of fragile described later.

支持層の厚みは、十分な強度が得られる限り制限はなく、保湿層よりも厚みが小さいことが好ましく、例えば0.3mm以下であり、より好ましくは0.2mm以下である。   The thickness of the support layer is not limited as long as sufficient strength can be obtained, and is preferably smaller than the moisture retention layer, for example, 0.3 mm or less, and more preferably 0.2 mm or less.

支持層の目付量としては、12〜100g/m2が好ましく、15〜70g/m2がより好ましい。 The basis weight of the support layer, preferably 12~100g / m 2, 15~70g / m 2 is more preferable.

これらのPTFE多孔質膜、保湿性を有する織布または不織布(保湿層)、および場合により支持層を積層することにより、本発明のマスク用布が形成される。   The mask fabric of the present invention is formed by laminating these PTFE porous membranes, a woven or non-woven fabric having moisture retention (moisture retention layer), and optionally a support layer.

各層の積層は、例えば、単純な端部の折込による接合、縫製、接着剤による接着などにより行うことができる。この際、マスク用布が十分な通気性を有するような積層構造とすることが重要である。例えば、接着剤により接着する場合には、接着剤を点状、繊維状等に塗布し、十分な通気面積を確保する。また、支持層が熱可塑性樹脂製の不織布であった場合は、支持層を加熱して熱溶着して積層することも可能であるが、このとき、通気性が維持されるように熱溶着することが重要である。   Lamination of each layer can be performed by, for example, joining by simple folding of end portions, sewing, adhesion by an adhesive, or the like. At this time, it is important to have a laminated structure in which the mask cloth has sufficient air permeability. For example, when bonding with an adhesive, the adhesive is applied in the form of dots, fibers, or the like to ensure a sufficient ventilation area. If the support layer is a nonwoven fabric made of a thermoplastic resin, the support layer can be heated and welded to be laminated, but at this time, it is heat welded so that air permeability is maintained. This is very important.

積層されるPTFE膜、保湿層および支持層の数には制限が無く、各種の層は複数設けられていてもよい。さらに、活性炭を含む吸着層等その他の機能層が設けられていてもよい。   There are no limitations on the number of PTFE membranes, moisture retention layers, and support layers to be laminated, and a plurality of various layers may be provided. Furthermore, other functional layers such as an adsorption layer containing activated carbon may be provided.

本発明のマスク用布の積層構造の例を図1〜3に示す。図1および2に示すように、支持層3は、PTFE多孔質膜1に対し、保湿層2が積層される側、積層されない側のいずれに配置されてもよい。図3に示すように、支持層3がPTFE多孔質膜1の両表面上に積層されており、支持層3の一つにさらに保湿層2が積層されている構造とすることもできる。当該マスク用布の積層構造としては、強度面およびPTFE多孔質膜面へのダメージに対する保護の観点から、図3に示される構造が好ましい。   Examples of the laminated structure of the mask cloth of the present invention are shown in FIGS. As shown in FIGS. 1 and 2, the support layer 3 may be disposed on the PTFE porous membrane 1 on either the side where the moisture retention layer 2 is laminated or the side where it is not laminated. As shown in FIG. 3, the support layer 3 may be laminated on both surfaces of the PTFE porous membrane 1, and the moisture retaining layer 2 may be further laminated on one of the support layers 3. The laminated structure of the mask cloth is preferably the structure shown in FIG. 3 from the viewpoint of protection against damage to the strength surface and the PTFE porous membrane surface.

各層には、抗菌処理、消臭処理を行うことも可能であり、当該処理は、保湿層に行うことが好ましい。   Each layer can be subjected to antibacterial treatment and deodorization treatment, and the treatment is preferably performed on the moisture retaining layer.

本発明のマスク用布は、マスクとしての実用面から通気性が要求されるが、その通気度としては、フラジール数で表される通気度が150cm/秒以上であることが好ましく、200〜2000cm/秒であることがより好ましい。当該通気度は、例えば、JIS L 1096(フラジールテスター法)に記載の方法に準拠して求められる値である。   The mask fabric of the present invention is required to have air permeability from the practical aspect as a mask, and the air permeability is preferably 150 cm / second or more, represented by the Frazier number, 200 to 2000 cm. / Second is more preferable. The said air permeability is a value calculated | required based on the method as described in JISL1096 (fragile tester method), for example.

本発明のマスク用布を用い、常法に従って衛生マスクを製造することができる。このとき、マスク用布の前記保湿性を有する織布または不織布が、咽頭側に配置されることが好ましい。   Using the mask cloth of the present invention, a sanitary mask can be produced according to a conventional method. At this time, it is preferable that the woven fabric or non-woven fabric having the moisturizing property of the mask fabric is disposed on the pharynx side.

ここで、衛生マスクとは、インフルエンザ、SARS等の空気感染性伝染病のウイルスが付着した粒子等をろ過除去することを目的として使用されるマスクをいう。   Here, the sanitary mask refers to a mask used for the purpose of filtering and removing particles and the like to which viruses of air-borne infectious diseases such as influenza and SARS are attached.

咽頭側とは、大気側とは逆の側であり、マスク着用者の顔面と接触することになる側のことをいう。   The pharyngeal side is the side opposite to the atmosphere side and refers to the side that comes into contact with the face of the mask wearer.

衛生マスクは平板状としてもよいが、好ましくは、装着時の違和感を軽減するため、顔の形状に沿って伸縮できるように加工する。また、装着時に鼻部に接するマスクの端部は、軟鋼薄片等の容易に変形可能な部材が内装される等、鼻等の形状に即してマスク端部を変形させて顔とマスクとの間に生じる隙間を低減できるよう加工されていることが好ましい。衛生マスクにはマスクを口および鼻部に固定するための掛け紐が取付けられるが、掛け紐は、耳に掛けられるようなループ状であってよく、後頭部で結べるような形状であってもよい。   The sanitary mask may have a flat plate shape, but preferably, the sanitary mask is processed so that it can expand and contract along the shape of the face in order to reduce discomfort during wearing. Also, the end of the mask that touches the nose when worn is equipped with an easily deformable member such as a thin piece of mild steel, etc. so that the mask end is deformed according to the shape of the nose, etc. It is preferable that it is processed so that a gap generated between them can be reduced. The sanitary mask is attached with a hanging strap for fixing the mask to the mouth and nose, but the hanging strap may be looped so as to be hung on the ear or may be shaped to be tied at the back of the head. .

本発明の衛生マスクは、PTFE膜を使用しているため、優れたウイルスの捕集効率を有する。また、本発明の衛生マスクを着用した場合、呼気に自然に含まれる水分が、保湿性を有する織布または不織布に吸収されることにより保湿されるが、PTFE多孔質膜により水分の蒸発が抑制されているため、通常の織布または不織布を用いたマスクよりも高く保湿がなされる。従って、従来のマスクに比べ、ウイルス感染の確率を低減することができる。さらに、保湿性を有する織布または不織布が、呼気中の水分を吸収するために、凝結した水分が着用者の口の周辺に付着するということがない。よって、着用者が不快感を感じることもなく、また美観上でも問題となる水滴が垂れることもない。   Since the sanitary mask of the present invention uses a PTFE membrane, it has excellent virus collection efficiency. In addition, when the sanitary mask of the present invention is worn, moisture naturally contained in exhaled breath is absorbed by the moisturizing woven or non-woven fabric, but moisture evaporation is suppressed by the PTFE porous membrane. Therefore, the moisture retention is higher than that of a mask using a normal woven fabric or non-woven fabric. Therefore, the probability of virus infection can be reduced as compared with the conventional mask. Further, since the woven or non-woven fabric having moisture retention absorbs moisture in the breath, the condensed moisture does not adhere to the periphery of the wearer's mouth. Therefore, the wearer does not feel uncomfortable, and water drops that are problematic in terms of aesthetics do not drip.

以下、実施例により本発明をさらに具体的に説明するが、本発明は、これら実施例により何ら限定されるものではない。   EXAMPLES Hereinafter, the present invention will be described more specifically with reference to examples, but the present invention is not limited to these examples.

PTFE多孔質膜の合成
PTFEファインパウダー(旭アイシーアイフロロポリマーズ社製フルオンCD−123)100質量部に対して液状潤滑剤(ナフサ)20質量部を均一に混合し、この混合物を20kg/cm2の条件で予備成形し、次いでこれをロッド状にペースト押出成形し、さらにこのロッド状成形体を1対の金属圧延ロール間に通し、厚さ250μmの長尺シートを得た。このシートを290℃の延伸温度でシート長手方向に35倍延伸し、さらにテンター法により80℃の延伸温度でシート幅方向に40倍延伸し、未焼成PTFE多孔質膜を得た。この未焼成PTFE多孔質膜を、熱風発生炉を用いて400℃で3秒間焼成し、焼成PTFE多孔質膜を得た。得られた焼成PTFE多孔質膜の通気度(フラジール数)は、230cm/秒であった。なお、ここでいう通気度とは、JIS L 1096(フラジールテスター法)に記載の方法により測定される値である。
Synthesis of PTFE Porous Membrane 20 parts by mass of a liquid lubricant (naphtha) was uniformly mixed with 100 parts by mass of PTFE fine powder (Fluon CD-123 manufactured by Asahi IC Fluoropolymers Co., Ltd.), and this mixture was 20 kg / cm 2. Then, this was preformed in a rod shape, and this rod-shaped compact was passed between a pair of metal rolling rolls to obtain a long sheet having a thickness of 250 μm. This sheet was stretched 35 times in the longitudinal direction of the sheet at a stretching temperature of 290 ° C., and further stretched 40 times in the sheet width direction at a stretching temperature of 80 ° C. by a tenter method to obtain a non-fired PTFE porous membrane. This unsintered PTFE porous membrane was fired at 400 ° C. for 3 seconds using a hot air generator to obtain a fired PTFE porous membrane. The air permeability (fragile number) of the obtained fired PTFE porous membrane was 230 cm / second. Here, the air permeability is a value measured by the method described in JIS L 1096 (Fragile tester method).

PTFE多孔質膜の捕集効率を以下の方式で測定した。サンプルを、有効面積100cm2の円形ホルダーにセットし、入口側と出口側に圧力差を与え、このサンプルを通過する空気の流速を流速計で5.3cm/秒に調節した。上流側に多分散ジオクチルフタレート(DOP)を、粒子径0.1〜0.2μmの粒子が4×108個/リットル、粒子径0.2〜0.3μmの粒子が6×107個/リットルとなるように供給し、上流側の粒子濃度とサンプルを透過してきた下流側の粒子濃度とをパーティクルカウンター(リオン社製KC−18)で測定した。粒子径0.3〜0.5μmの粒子について、以下の式で捕集効率を求めた。
捕集効率(%)=(1−下流側粒子濃度/上流側粒子濃度)×100
The collection efficiency of the PTFE porous membrane was measured by the following method. The sample was set in a circular holder having an effective area of 100 cm 2 , a pressure difference was applied between the inlet side and the outlet side, and the flow rate of air passing through the sample was adjusted to 5.3 cm / sec with a flowmeter. On the upstream side, polydisperse dioctyl phthalate (DOP) is used, 4 × 10 8 particles / liter of particles having a particle size of 0.1 to 0.2 μm, and 6 × 10 7 particles / particle of 0.2 to 0.3 μm in particle size. Then, the concentration of particles on the upstream side and the concentration of particles on the downstream side that had passed through the sample were measured with a particle counter (KC-18 manufactured by Rion Co., Ltd.). For particles having a particle size of 0.3 to 0.5 μm, the collection efficiency was determined by the following equation.
Collection efficiency (%) = (1−downstream particle concentration / upstream particle concentration) × 100

実施例1
上記で得られたPTFE多孔質膜を、支持層として芯ポリエチレンテレフタレート(PET)/鞘ポリエチレン(PE)複合スパンボンド不織布(ユニチカ社製エルベスTO153WDO(商品名)、目付量15g/m2、繊維径25μm)2枚に挟んで積層し、150℃に加熱した熱ロールで連続的に熱ラミネートすることにより接着した(これをマスク用布Cとする)。このマスク用布Cの通気度は、220cm/秒、目付けは30g/m2であった。
Example 1
The PTFE porous membrane obtained above is a core polyethylene terephthalate (PET) / sheathed polyethylene (PE) composite spunbonded nonwoven fabric (Elves TO153WDO (trade name) manufactured by Unitika Ltd., basis weight 15 g / m 2 , fiber diameter) 25 μm) Laminated between two sheets and bonded by continuous thermal lamination with a hot roll heated to 150 ° C. (this is referred to as mask cloth C). The air permeability of this mask cloth C was 220 cm / second, and the basis weight was 30 g / m 2 .

マスク用布Cと医療ガーゼ(日本薬局方準拠の医療ガーゼタイプI、織布、綿素材、目付量34g/m2)を組み合わせた。医療ガーゼを4枚重ねとし、マスク用布Cと組み合わせ端を折り込む事によって固定した(これをマスク用布Aとする)。マスク用布Aの通気度は200cm/秒、目付量は170g/m2であった。 The mask cloth C and medical gauze (medical gauze type I conforming to the Japanese Pharmacopoeia, woven fabric, cotton material, basis weight 34 g / m 2 ) were combined. Four sheets of medical gauze were stacked and fixed by folding the combination end with the mask cloth C (this is referred to as mask cloth A). The air permeability of the mask cloth A was 200 cm / second, and the basis weight was 170 g / m 2 .

実施例2
マスク用布Cと、医療ガーゼを組み合わせた。医療ガーゼを8枚重ねとし、マスク用布Cと組み合わせ端を折り込むことによって固定した(これをマスク用布Bとする)。マスク用布Bの通気度は160cm/秒、目付量は300g/m2であった。
Example 2
The mask cloth C and medical gauze were combined. 8 sheets of medical gauze were stacked and fixed by folding the combination end with the mask cloth C (this is referred to as mask cloth B). The air permeability of the mask cloth B was 160 cm / second, and the basis weight was 300 g / m 2 .

比較例1
比較例として、マスク用布Cをそのまま使用した。
Comparative Example 1
As a comparative example, the mask cloth C was used as it was.

マスク用布A、BおよびCの構成を表2に示す。   Table 2 shows the configurations of the mask fabrics A, B, and C.

マスク用布の保湿性能を以下の方法で測定した。スイスLyssy社製の全自動水蒸気透過度試験機L80−4000型を用い、水蒸気透過試験を行った。この装置は、JIS Z 0208に準拠し、温度40℃で片側の相対湿度を90%RHに保つことができる。本装置にマスク用布を装着した。高湿度の咽頭側を模すために、湿度90%の高湿度側を咽頭側とし、マスク用布A、Bにおいては保湿層を高湿度側に向けて装着した。水蒸気透過度試験機に各マスク用布を100cm2装着した。装置を作動し、定常状態に達するまで1時間連続運転を行った。 The moisture retention performance of the mask cloth was measured by the following method. A water vapor transmission test was conducted using a fully automatic water vapor transmission rate tester L80-4000 manufactured by Swiss Lyssy. This apparatus is based on JIS Z 0208, and can maintain the relative humidity on one side at 90% RH at a temperature of 40 ° C. A mask cloth was attached to the apparatus. In order to simulate the pharynx side with high humidity, the high humidity side with a humidity of 90% was set as the pharyngeal side, and the mask cloth A and B were mounted with the moisture retention layer facing the high humidity side. Each mask cloth was attached to a water vapor permeability tester at 100 cm 2 . The apparatus was operated and operated continuously for 1 hour until a steady state was reached.

保湿試験後、直ぐにマスク用布の重量を測定し、目付量に換算した。また通気度も測定した。試験結果を表3に示す。   Immediately after the moisture retention test, the weight of the mask cloth was measured and converted to a basis weight. Air permeability was also measured. The test results are shown in Table 3.

上記のように、保湿層を設けたマスク用布では、高い水分保持能が得られることが明らかとなった。   As described above, it has been clarified that a mask cloth provided with a moisturizing layer can obtain a high water retention ability.

本発明のマスク用布の一例の断面図である。It is sectional drawing of an example of the cloth for masks of this invention. 本発明のマスク用布の別の例の断面図である。It is sectional drawing of another example of the cloth for masks of this invention. 本発明のマスク用布のさらに別の例の断面図である。It is sectional drawing of another example of the cloth for masks of the present invention.

符号の説明Explanation of symbols

1 PTFE多孔質膜
2 保湿層
3 支持層
1 PTFE porous membrane 2 Moisturizing layer 3 Support layer

Claims (8)

積層構造を有するマスク用布であって、ポリテトラフルオロエチレン多孔質膜、および保湿性を有する織布または不織布を有することを特徴とするマスク用布。   A mask cloth having a laminated structure, comprising a polytetrafluoroethylene porous film and a woven or non-woven cloth having moisture retention. 前記保湿性を有する織布または不織布が、天然繊維より形成される織布または不織布である請求項1に記載のマスク用布。   The mask cloth according to claim 1, wherein the woven or non-woven fabric having moisture retention is a woven or non-woven cloth formed from natural fibers. さらに支持層を有する請求項1または2に記載のマスク用布。   Furthermore, the mask cloth of Claim 1 or 2 which has a support layer. 前記支持層が前記ポリテトラフルオロエチレン多孔質膜の両表面上に積層されており、前記支持層の少なくとも一面に保湿性を有する織布または不織布が積層されている構造を有する請求項3に記載のマスク用布。   The said support layer is laminated | stacked on both surfaces of the said polytetrafluoroethylene porous membrane, It has a structure where the woven fabric or nonwoven fabric which has moisture retention is laminated | stacked on the at least one surface of the said support layer. Mask cloth. 前記支持層が、熱可塑性樹脂の繊維より形成される不織布であり、前記保湿性を有する織布または不織布が、木綿より形成される織布または不織布である請求項3または4に記載のマスク用布。   The mask layer according to claim 3 or 4, wherein the support layer is a nonwoven fabric formed from fibers of a thermoplastic resin, and the woven fabric or nonwoven fabric having moisture retention is a woven fabric or nonwoven fabric formed from cotton. cloth. フラジール数で表される通気度が150cm/秒以上である請求項1〜5のいずれか1項に記載のマスク用布。   6. The mask cloth according to any one of claims 1 to 5, wherein an air permeability represented by a fragile number is 150 cm / second or more. 請求項1〜6のいずれか1項に記載のマスク用布を用いた衛生マスク。   A sanitary mask using the mask cloth according to any one of claims 1 to 6. 前記マスク用布の前記保湿性を有する織布または不織布が、咽頭側に配置されている請求項7に記載の衛生マスク。
The sanitary mask according to claim 7, wherein the woven fabric or non-woven fabric having the moisture retention property of the mask fabric is disposed on the pharynx side.
JP2006111086A 2006-04-13 2006-04-13 Fabric for mask having moisture retentivity, and hygienic mask using it Pending JP2007282720A (en)