JP2006282697A - 共重合ポリエステル - Google Patents
共重合ポリエステル Download PDFInfo
- Publication number
- JP2006282697A JP2006282697A JP2005100801A JP2005100801A JP2006282697A JP 2006282697 A JP2006282697 A JP 2006282697A JP 2005100801 A JP2005100801 A JP 2005100801A JP 2005100801 A JP2005100801 A JP 2005100801A JP 2006282697 A JP2006282697 A JP 2006282697A
- Authority
- JP
- Japan
- Prior art keywords
- phase polycondensation
- polyester
- cyclic ester
- polycondensation
- intrinsic viscosity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】
ジカルボン酸成分としてテレフタル酸単位、ジオール成分としてモノエチレングリコールならびにジエチレングリコール単位を含み、液相重縮合の後に固相重縮合を行って得られる共重合ポリエステルであって、固相重縮合前後の固有粘度の増加量ΔIVが式 ΔIV≧0.18 dl/gを満たし、(a)ジオール成分中のジエチレングリコール単位が1.0〜5.0モル%、(b)固有粘度が0.6〜1.5dl/g、(c)末端カルボキシル基濃度が19当量/トン以下、(d)環状エステル体の含有量が0.39重量%以下であって、(e)リン化合物及び/またはその金属塩を含む共重合ポリエステル。
【選択図】 なし
Description
D.R.Cooper et al.,Polymer, 14, 185(1973).
ΔIV≧0.18 dl/g
(ただしΔIVは固相重縮合前のIVLと固相重縮合後のIVSの差: ΔIV=IVS−IVL)
かつ、a)ジオール成分中のジエチレングリコール単位が1.0〜5.0モル%、b)固有粘度が0.6〜1.5dl/g、c)末端カルボキシル基濃度が19当量/トン以下、d)環状エステル体の含有量が0.39重量%以下であって、e)下記一般式1および一般式2から選ばれる少なくとも一種のリン化合物及び/またはその金属塩を含むことを特徴とする共重合ポリエステル。
テレフタル酸が前記含有量を満たす範囲で、ジカルボン酸としてはテレフタル酸のほかに、フタル酸、イソフタル酸、2,6−ナフタレンジカルボン酸、ジフェニル−4,4−ジカルボン酸、ジフェノキシエタンジカルボン酸等の芳香族ジカルボン酸を共に用いることができる。
モノエチレングリコールが前記含有量を満たす範囲で、ジオールとしてはモノエチレングリコールのほか、トリメチレングリコール、プロピレングリコール、テトラメチレングリコール、ネオペンチルグリコール、ヘキサンメチレングリコール、ドデカメチレングリコールなどの脂肪族グリコールを用いることができる。
1.0モル%以上であると、共重合ポリエステルを製造する際の固相重縮合工程の環状エステル体低減化速度が高く、成形時に金型に付着する環状エステル体を低減できるので好ましい。5.0モル%以下であると、成形体の耐熱性が低下することなく、また延伸成形体をヒートセットした場合の耐熱性の向上効果も大きいため好ましい。
これらDEGの生成を抑制及びまたは促進させる化合物の添加量としては、原料酸性分に対して、0.001モル%乃至1モル%の範囲で加えられることが好ましい。
上記のようなエステル化工程で得られた低次縮合物は、次いで重縮合(液相重縮合)工程に供給される。
重縮合反応は、1段階で行ってもよく、複数段階に分けて行ってもよい。例えば、重縮合反応が複数段階で行われる場合には、第1段目の重縮合反応は、反応温度が250乃至290℃、好ましくは260乃至280℃、圧力が66乃至2.7kPa、好ましくは27乃至4kPaの条件下で行われ、最終段の重縮合反応は、反応温度が265乃至300℃、好ましくは270乃至295℃、圧力が1.3乃至0.013kPa、好ましくは0.67乃至0.067kPaの条件下で行われる。
また上述金属塩の金属としては、L i 、B e 、N a 、M g、K 、Ca、M n 、N i、C u 、Z n、S r 、B aから選択されたものを用いることが好ましい。
更に後述の固相重縮合反応において、不活性ガス中の脂肪族ジオール成分濃度によっても制御することが出来る。脂肪族ジオール成分濃度が高いと末端カルボキシル基濃度を低減することが出来る。
本実施例で用いた種々の測定法を以下に示す。
試料をモノエタノールアミンで加水分解し、過剰のモノエタノールアミンを中和後、ガスクロマトグラフィーを使用して内部標準法により定量した。
(固有粘度、以下IVと略称することもある)
試料をフェノール/1,1,2,2−テトラクロロエタン混合溶媒(50/50重量比)を用いて溶解した。0.5g/dlの試料溶液を調製し、25℃で測定した溶液粘度から固有粘度(IV)を算出した。
(末端カルボキシル基濃度、以下COOH基濃度と略称することもある)
試料をo−クレゾールに加熱溶解し、クロロホルムを加え電位差滴定装置を用いてNaOH水溶液を標準溶液としてて規定した。
試料をメタパラクレゾールで加熱溶解、さらにテトラヒドロフランを加えてポリマーを析出させた。その後濾過した濾液を液体クロマトグラフィーを用いて内部標準法により定量した。
(成形体)
ポリエチレンテレフタレートチップを真空乾燥機、170℃、4時間乾燥した。乾燥したポリエチレンテレフタレートを射出成形機M−70B(商品名、(株)名機製作所)にて、290℃で成形し、段付き角板状成形体を得た。段付き角板状成形体は図1に示す様な形状を有しており、A部の厚さは約6.5mmであり、B部の厚さは約5mmであり、C部の厚さは約4mmである。
高純度テレフタル酸 13000部、モノエチレングリコール 5000部、テトラエチルアンモニウムヒドロキシド20%水溶液 6.88部をオートクレーブに仕込み、圧力 0.17MPaG、260℃の窒素雰囲気下6時間攪拌しながら反応させた。この反応により生成した水は常時系外に留去した。次に重縮合触媒として、二酸化ゲルマニウム 3.3部、メチルアシッドフォスフェート(以下MAPと称す) 2.2部を加えた。1時間かけて280℃まで昇温し、系内を0.27kPaまで減圧し、更に50分反応させ、エチレングリコールを系外に留去した。反応終了後反応物をチップ状に裁断した。以上の液相重縮合によって得られたポリエチレンテレフタレートの固有粘度(IVL)は0.58dl/gであった。
このようにして得られたポリエチレンテレフタレートの固有粘度(IVS)は0.77dl/gであり、DEG濃度は2.3モル%、COOH基濃度15当量/トン、環状エステル体濃度(CES)は0.33重量%であった。
得られたポリエチレンテレフタレートを前記した方法に従い射出成形機で成形した段付き角板状成形体の環状エステル体は0.35重量%であった。この環状エステル体濃度をW0とする。
液相重縮合の固有粘度(IVL)を表1に示すように低くした以外は実施例1と同様に行った。すなわち固相重縮合でのIV上昇幅(ΔIV)を大きく取った。固相重縮合の終点はIV=0.77dl/gに到達するまでとした。
液相重縮合の安定剤(リン化合物)の種類をMAPから化3で表す化合物に変更した以外は同様に行った。
高純度テレフタル酸 13000部、モノエチレングリコール 4930部、テトラエチルアンモニウムヒドロキシド20%水溶液 6.88部をオートクレーブに仕込み、圧力 0.17MPaG、260℃の窒素雰囲気下6時間攪拌しながら反応させた。この反応により生成した水は常時系外に留去した。次に重縮合触媒として、二酸化ゲルマニウム 3.3部、リン酸 1.4部を加えた。1時間かけて290℃まで昇温し、系内を0.27kPaまで減圧し、更に50分反応させ、エチレングリコールを系外に留去した。反応終了後反応物をチップ状に裁断した。以上の液相重縮合によって得られたポリエチレンテレフタレートの固有粘度(IVL)は0.62dl/gであった。
得られたポリエチレンテレフタレートを前記した方法に従い射出成形機で成形した段付き角板状成形体の環状エステル体は0.60重量%であった。この環状エステル体濃度をW0とする。
高純度テレフタル酸 13000部、モノエチレングリコール 4930部、テトラエチルアンモニウムヒドロキシド20%水溶液 51.8部、イソプロピルチタネート 1.6部をオートクレーブに仕込み、圧力 0.17MPaG、240℃の窒素雰囲気下6時間攪拌しながら反応させた。この反応により生成した水は常時系外に留去した。次に重縮合触媒として、二酸化ゲルマニウム 3.3部、リン酸 1.4部を加えた。1時間かけて290℃まで昇温し、系内を0.27kPaまで減圧し、更に50分反応させ、エチレングリコールを系外に留去した。反応終了後反応物をチップ状に裁断した。以上の液相重縮合によって得られたポリエチレンテレフタレートの固有粘度は0.55dl/gであった。
得られたポリエチレンテレフタレートを前記した方法に従い射出成形機で成形した段付き角板状成形体の環状エステル体は0.55重量%であった。この環状エステル体濃度をW0とする。
Claims (3)
- ジカルボン酸成分としてテレフタル酸単位を含み、ジオール成分としてモノエチレングリコールならびにジエチレングリコール単位を含み、液相重縮合の後に固相重縮合を行って得られる共重合ポリエステルであって、固相重縮合前と固相重縮合後の固有粘度の増加量が下記式を満たし、
ΔIV≧0.18 dl/g
(ただしΔIVは固相重縮合前のIVLと固相重縮合後のIVSの差: ΔIV=IVS−IVL)
かつ、a)ジオール成分中のジエチレングリコール単位が1.0〜5.0モル%、b)固有粘度が0.6〜1.5dl/g、c)末端カルボキシル基濃度が19当量/トン以下、d)環状エステル体の含有量が0.39重量%以下であって、e)下記一般式1および一般式2から選ばれる少なくとも一種のリン化合物及び/またはその金属塩を含むことを特徴とする共重合ポリエステル。
(ただし化1において、R1、R2、R3、R4はそれぞれ独立に水素あるいは炭素数1乃至4のアルキル基である)
(ただし化2においてR5は炭素数1乃至8個のアルキル化合物及びまたはフェニル基であり、aは0乃至2の正数であり、R5は複数ある時それぞれ異なっていても、同一でも良い。) - 請求項1に記載の共重合ポリエステルであって、該ポリエステルを290℃の成形温度で射出成形して得られた成形品の環状エステル体の含有量をW0重量%とし、一方該ポリエステルを温度95℃の熱水で8時間浸積した後に乾燥し、ついで上記のようにして射出成形して得られた成形品の環状エステル体の含有量をW1重量%とした場合に、W0−W1が0乃至0.10重量%であることを特徴とするポリエステル。
- 請求項1乃至2に記載のポリエステルの製造方法であって、固相重縮合行程を、ポリエステル構成成分の脂肪族ジオール蒸気を0.1乃至1重量%含む不活性ガス雰囲気で処理することを特徴とする方法。