JP2006159028A - 分散液およびコーティング液 - Google Patents
分散液およびコーティング液 Download PDFInfo
- Publication number
- JP2006159028A JP2006159028A JP2004351663A JP2004351663A JP2006159028A JP 2006159028 A JP2006159028 A JP 2006159028A JP 2004351663 A JP2004351663 A JP 2004351663A JP 2004351663 A JP2004351663 A JP 2004351663A JP 2006159028 A JP2006159028 A JP 2006159028A
- Authority
- JP
- Japan
- Prior art keywords
- dispersion
- titanium oxide
- coating liquid
- titanium
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】光触媒性を有する酸化チタンを、水溶性金属キレート化合物を含有する水性媒体中に分散してなることを特徴とする分散液。
【選択図】なし
Description
(分散液J1の調製)
イオン交換水83部に可視光型酸化チタン(住友化学工業(株)製、TP−S201、一次粒子径15nm)15部を配合して公知の方法で懸濁し、該懸濁液にジヒドロキシビス(アンモニウムラクテート)チタニウム2部を添加し、メディアを使用して分散を行い、分散液中の酸化チタンの平均粒径がメジアン径で40nmである分散液J1を得た。なお、上記のメジアン径は、MOUNTECH社製、Microtrac UPAで測定した値である。
(分散液J2の調製)
実施例1における分散液J1の調製において、イオン交換水を84部に、ジヒドロキシビス(アンモニウムラクテート)チタニウムを1部に置き換える以外は分散液J1の調製と同様にして、分散液中の酸化チタンの平均粒径がメジアン径で80nmである分散液J2を得た。
(分散液K1の調製)
実施例1における分散液J1の調製において、ジヒドロキシビス(アンモニウムラクテート)チタニウムを有機物分散剤A(ビックケミー・ジャパン(株)製、BYK−154)に置き換える以外は分散液J1の調製と同様にして分散を行い、分散液中の酸化チタンの平均粒径がメジアン径で100nmである比較例の分散液K1を得た。
(分散液K2の調製)
実施例1における分散液J1の調製において、ジヒドロキシビス(アンモニウムラクテート)チタニウムを有機物分散剤B(エアープロダクツ・ジャパン(株)製、サーフィノールCT−136)に置き換える以外は分散液J1の調製と同様にして分散を行い、分散液中の酸化チタンの平均粒径がメジアン径で140nmである比較例の分散液K2を得た。
(分散液K3の調製)
実施例1における分散液J1の調製において、ジヒドロキシビス(アンモニウムラクテート)チタニウムを有機物分散剤C(ビックケミー・ジャパン(株)製、BYK−187)に置き換える以外は分散液J1の調製と同様にして分散を行い、分散液中の酸化チタンの平均粒径がメジアン径で240nmである比較例の分散液K3を得た。
(コーティング液L1の調製)
実施例1の分散液J1 33.3部に、シリカゾル41.7部およびイオン交換水25.0部を添加し、公知の方法で均一に混合撹拌し本発明のコーティング液L1を得た。
(コーティング液L2の調製)
実施例3におけるコーティング液L1の調製において分散液J1を分散液J2に置き換える以外はコーティング液L1の調製と同様にして本発明のコーティング液L2を得た。
(コーティング液L3の調製)
実施例1の分散液J1 33.3部に、スチレン−アクリルエマルジョン(星光ポリマー(株)製、ハイロスX X−2008L)20部、およびイオン交換水46.7部を添加し、公知の方法で均一に混合撹拌し本発明のコーティング液L3を得た。
(コーティング液M1〜M3の調製)
比較例の分散液K1〜K3の各々33.3部にスチレン−アクリルエマルジョン(星光ポリマー(株)製、ハイロスX X−2008L)50部、およびイオン交換水16.7部を添加し、公知の方法で均一に混合撹拌し比較例のコーティング液M1〜M3を得た。
(分散安定性)
上記の各々の分散液を水で希釈して可視光型酸化チタンの固形分を1.5%にする。これら溶液を30mlのラボランスクリュー管瓶に20ml入れ、室温で放置し、1週間後の可視光型酸化チタンの沈降度合いを目視にて確認し、下記の判定基準により評価した。
◎:酸化チタンの沈降が、認められない。
○:酸化チタンの沈降が、僅かに認められるが分散液層(下部)と水層(上部)との分離がない。
△:酸化チタンの沈降が、僅かに認められ、液層の分離がある。
×:酸化チタンが完全に沈降している。
上記の各々のコーティング液を10cm×20cmPETフィルム全体に塗布(乾燥厚み2.0g/m2)して乾燥させる。次に、これを5Lテドラーバックに詰めたのち、2.9Lの空気を注入する。空気注入後、6,000ppmのアセトアルデヒドを0.1L注入し、30分間放置して酸化チタンにアセトアルデヒドを十分に吸着させる。このときのアセトアルデヒド濃度を初期濃度とし、これを室温で2,500ルクス(lx)の蛍光灯に当て、経時のアセトアルデヒド濃度を測定し、下記の判定基準によりアセトアルデヒドの分解性により光触媒性能を評価した。なお、測定にはガステック社製のガステック検知管を使用した。
◎:48時間以内にアセトアルデヒドが、ほぼ100%分解している。
○:48時間以内にアセトアルデヒドが、70%分解している。
△:48時間以内にアセトアルデヒドが、50%分解している。
×:48時間以内ではアセトアルデヒドが、分解していない。
Claims (11)
- 光触媒性を有する酸化チタンを、水溶性金属キレート化合物を含有する水性媒体中に分散してなることを特徴とする分散液。
- 水溶性金属キレート化合物が、チタンキレート化合物である請求項1に記載の分散液。
- チタンキレート化合物が、ジヒドロキシビス(アンモニウムラクテート)チタニウムである請求項2に記載の分散液。
- 分散液中に分散している酸化チタンの平均粒径S(nm)が、1nm≦S≦500nmである請求項1に記載の分散液。
- 前記の酸化チタン(a)に対する水溶性金属キレート化合物(b)の配合割合が、b/a=1〜50/100(質量比)である請求項1または2に記載の分散液。
- 請求項1〜5のいずれか1項に記載の分散液中に、さらに無機系および/または有機系のバインダーを配合してなることを特徴とするコーティング液。
- 無機系バインダーが、珪素化合物および珪酸塩から選ばれる少なくとも1種である請求項6に記載のコーティング液。
- 珪素化合物が、シリカおよび/またはコロイダルシリカである請求項7に記載のコーティング液。
- 珪酸塩が、珪酸リチウムおよび/または珪酸カリウムである請求項7に記載のコーティング液。
- 有機系バインダーが、アクリルエマルジョン、スチレン−アクリルエマルジョンおよびアクリル樹脂から選ばれる少なくとも1種である請求項6に記載のコーティング液。
- 請求項6〜10のいずれか1項に記載のコーティング液から形成された塗膜を有することを特徴とする光触媒塗工物。