JP2005205064A - Shoe upper material quickly dried and shoe using the same - Google Patents
Shoe upper material quickly dried and shoe using the same Download PDFInfo
- Publication number
- JP2005205064A JP2005205064A JP2004016864A JP2004016864A JP2005205064A JP 2005205064 A JP2005205064 A JP 2005205064A JP 2004016864 A JP2004016864 A JP 2004016864A JP 2004016864 A JP2004016864 A JP 2004016864A JP 2005205064 A JP2005205064 A JP 2005205064A
- Authority
- JP
- Japan
- Prior art keywords
- foam
- shoe
- shoe upper
- water
- upper material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、水に濡れた場合や洗濯後において、水分を保持せず乾きの速い靴甲被材及びそれを用いた乾きの速い靴に関する。 The present invention relates to a shoe upper material that does not retain moisture and quickly dries when wet or after washing, and a shoe that quickly dries using the same.
現在市販されている靴は、軽量感及びフィット感を得るため、更に、価格が安いといった理由により甲被の裏材に軟質ウレタンフォームを使用している。また、靴内に水が浸入しにくくするために甲被の表材には合成皮革や人工皮革を多く使用している。
乾燥性に優れた靴として、登録実用新案第3027760号には、ダイビングシューズの甲被材にネオプレンスポンジを主な素材として、該ネオプレンスポンジの両面或いは片面にジャージ等が貼り合わせされた靴甲被が記載されている。
Registered utility model No. 3027760 is a shoe with excellent drying characteristics. The shoe upper cover is made of neoprene sponge as a main material for the upper cover material of diving shoes, and jersey etc. are bonded to both sides or one side of the neoprene sponge. Is described.
前記軟質ウレタンフォームは、連続気泡タイプのものである為、水分を吸収しやすく、通気性に乏しい合成皮革や人工皮革などを表材として組み合わせた場合、一旦吸水すると水分が逃げにくいといった欠点があるので、履用中に甲被が濡れたり、洗濯をした場合、乾燥するまでにかなり時間がかかる。特にベロの部分や履き口部分はウレタンフォームの厚さが厚かったり、また先部を合成皮革や人工皮革等で覆われた構造は最も乾きにくい部分である。
前記ネオプレンスポンジのように、水に濡れても水が沁み込まず、乾燥が速いという長所は持ち合わせているが、材料コストが高いという欠点がある。
軟質ウレタンフォームに代わる安価でクッション性に優れた靴甲被材が求められている。
Since the flexible urethane foam is of the open cell type, when it is combined with a surface material such as synthetic leather or artificial leather that is easy to absorb moisture and has poor air permeability, there is a drawback that it is difficult for moisture to escape once water is absorbed. Therefore, if the upper is wet or is washed while wearing, it will take a long time to dry. In particular, the velo part and the mouth part have the thickest urethane foam, and the structure in which the tip part is covered with synthetic leather or artificial leather is the most difficult part to dry.
Like the neoprene sponge, even if it gets wet, it does not squeeze in water and has the advantages of fast drying, but has the disadvantage of high material costs.
There is a demand for a shoe upper material that is inexpensive and excellent in cushioning properties, replacing soft urethane foam.
本発明の履き口部や舌部に使用する靴甲被材は、表材と裏材の間に発泡体が挿入されている靴甲被材や履き口部材や舌部材に用いられる厚手の甲被材であり、前記発泡体は、芯材となる発泡体の両面に薄手の被覆材となる発泡体が積層されており、芯材となる発泡体は、比重が0.05〜0.20の非保水性の発泡体であることを特徴とする。 The shoe upper material used for the mouth part and tongue part of the present invention is a shoe upper material in which a foam is inserted between the front material and the back material, and the thick upper material used for the mouth material and tongue member. The foam is formed by laminating a foam as a thin coating material on both sides of a foam as a core, and the foam as a core has a specific gravity of 0.05 to 0.20. It is a non-water-retaining foam.
前記芯材となる非保水性の発泡体は、水に濡れた時、水分を保持しないものであり、独立気泡を有する発泡体や撥水性を付与した発泡体を使用することが好ましい。具体的には、芯材の具体的な例として、EVAスポンジ、ポリエチレンフォーム、ポリプロピレンフォーム、ゴムスポンジがあげられるが、撥水化した軟質ウレタンフォームを使用することもできる。又、芯材としての機能を有するために、クッション性がよく、比重が0.05〜0.20の軽量な発泡体であることが好ましい。 The non-water-retaining foam used as the core material does not retain moisture when wet, and it is preferable to use a foam having closed cells or a foam imparted with water repellency. Specifically, examples of the core material include EVA sponge, polyethylene foam, polypropylene foam, and rubber sponge, but water-repellent flexible urethane foam can also be used. Moreover, since it has a function as a core material, it is preferably a lightweight foam having good cushioning properties and a specific gravity of 0.05 to 0.20.
前記靴甲被材において、薄手の被覆材となる発泡体は、洗濯後の乾燥を速める為に、非保水性の発泡体であることが好ましい。
又、甲被材の表材や裏材と貼り合わせされるので、接着性の良いものが好ましい。
In the shoe upper material, the foam serving as a thin covering material is preferably a non-water-retaining foam in order to speed up drying after washing.
Moreover, since it is bonded together with the front material and the back material of the upper material, those having good adhesiveness are preferable.
前記靴甲被材において、表材及び裏材は、保水性のものが水分を保持しないものが適し、ポリエステルやナイロン等合成繊維製の織物やメッシュ生地,人工皮革,合成皮革を使用することが好ましい。 In the above-mentioned shoe upper material, the surface material and the back material are preferably water-retaining materials that do not retain moisture, and fabrics and mesh fabrics made of synthetic fibers such as polyester and nylon, artificial leather, and synthetic leather may be used. preferable.
本発明の靴は、水に濡れた後の乾燥を速める為に、前項で説明した本発明の靴甲被材を履き口部や舌部に配置し、その他の甲被材を非保水性の靴甲被材で構成することを特徴とする。
その他の甲被材に用いる非保水性の靴甲被材は、水に濡れた場合、水分を保持しない素材であり、具体的な例として、通常の連続気泡タイプの軟質ウレタンフォームや保水性の良い綿布は適さず、合成繊維製の織物やメッシュ生地、合成皮革、人工皮革等を使用することができる。
本発明の靴は、中底と外底を踏まず部から踵部の間で繰り抜き、プラスチック製のメッシュを配置して靴内の水分が靴底より放出されるような構造にすると、通水性が良くなり、水に濡れた後、さらに乾きの速い靴が得られる。
The shoe of the present invention has the shoe upper material of the present invention described in the previous section placed on the mouth and tongue to accelerate drying after getting wet with water, and the other upper material is non-water-retaining. It is characterized by comprising a shoe upper material.
Non-water-retaining shoe upper materials used for other upper materials are materials that do not retain moisture when wet, such as ordinary open cell type flexible urethane foam or water-retaining properties. Good cotton cloth is not suitable, and synthetic fabrics and mesh fabrics, synthetic leather, artificial leather and the like can be used.
If the shoe of the present invention is constructed so that the inside of the shoe and the outside of the shoe are not stepped on between the heel and the heel, and a plastic mesh is arranged to release the moisture in the shoe from the shoe sole. After the water becomes better and gets wet, shoes that dries faster can be obtained.
本発明の靴甲被材を履き口部や舌部など厚手の素材に使用すると、水に濡れた後、乾燥しやすい靴を提供することができる。例えば、夕方、靴を洗って干しておいても、乾きが速いので、次の朝には履くことができるので、手軽に靴を洗うことができる。
又、本発明の靴甲被材は、表材と裏材の間に挿入している発泡体は、比重が0.05〜0.2の芯材となる発泡体の両面に薄手の発泡体が被覆されているので、コストや機能に対応して、芯材や被覆材を適宜選定することができる。
When the shoe upper material of the present invention is used for a thick material such as a mouth portion and a tongue portion, it is possible to provide a shoe that is easy to dry after getting wet. For example, even if you wash your shoes and dry them in the evening, they dry quickly and can be worn the next morning, so you can easily wash your shoes.
Further, the shoe upper material of the present invention is such that the foam inserted between the front material and the back material is a thin foam on both sides of the foam which becomes a core material having a specific gravity of 0.05 to 0.2. Therefore, the core material and the covering material can be appropriately selected according to the cost and function.
本発明の靴甲被材として履き口材を選定した。実施例の履き口材を実施例1、実施例2として設定した。
又、比較例の履き口材を比較例1、比較例2として設定した。そしてこれらの各履き口材を水浸後、乾燥性評価を行った。
又、本発明の靴には、実施例1の履き口材を使用した靴の実施例の靴として設定し、比較例1の履き口材を使用した靴を比較例の靴として設定し、靴の洗濯後の乾燥性評価を行った。
A footwear material was selected as the shoe upper material of the present invention. The footwear material of the example was set as Example 1 and Example 2.
Moreover, the footwear material of the comparative example was set as the comparative example 1 and the comparative example 2. Each of these footwear was immersed in water and then evaluated for dryness.
In addition, the shoe of the present invention is set as a shoe of the shoe example using the footwear material of Example 1, and the shoe using the footwear material of Comparative Example 1 is set as a shoe of the comparative example. The drying property after washing was evaluated.
1.履き口材の構成
履き口材の構成は、表材がポリエステルメッシュ素材、裏材がポリエステル系ニット素材であり、この表材と裏材の間に発泡体シートが挿入されており、発泡体シートはその両面において、表材及び裏材と接着剤等により貼り合わせされており、また、芯材と被覆材とは接着剤により貼り合わせされている。
1. Composition of the footwear material The composition of the footwear material is that the front material is a polyester mesh material and the back material is a polyester knit material, and a foam sheet is inserted between the front material and the back material. Is bonded to the front and back materials with an adhesive or the like on both sides thereof, and the core material and the covering material are bonded to each other with an adhesive.
実施例及び比較例に使用する発泡体シートの比重及び硬度を表1に示す。
表1において、軟質ウレタンフォームは連続気泡タイプ、EVAスポンジは独立気泡タイプのものである。
Table 1 shows the specific gravity and hardness of the foam sheets used in Examples and Comparative Examples.
In Table 1, the flexible urethane foam is of the open cell type, and the EVA sponge is of the closed cell type.
以下、実施例1、実施例2、比較例1、比較例2の履き口材の構成を示す。
<実施例1 履き口材a>
実施例1の履き口材aは、下記のような構成であり、表材のポリエステルメッシュ素材は、発泡体シートの軟質ウレタンフォーム4.0mmと接着剤により貼り合わせされており、又、裏材のポリエステル系ニット素材は、EVAスポンジ1.5mmと接着剤により貼り合わせされている。
又、芯材のEVAスポンジ5.0mmと被覆材のEVAスポンジ1.5mm、軟質ウレタンフォーム4.0mmとは接着剤によりそれぞれ貼り合わせされている。
履き口材aの構成
表材:ポリエステルメッシュ素材
発泡体シート:軟質ウレタンフォーム4.0mm/EVAスポンジ5.0mm/EVAス ポンジ1.5mm
裏材:ポリエステル系ニット素材
Hereinafter, the configurations of the footwear materials of Example 1, Example 2, Comparative Example 1, and Comparative Example 2 are shown.
<Example 1 Footwear a>
The footwear material a of Example 1 has the following configuration, and the polyester mesh material of the front material is bonded to the foamed sheet of urethane foam 4.0 mm with an adhesive, and the backing material. The polyester knit material is bonded to EVA sponge 1.5 mm with an adhesive.
Further, the EVA sponge 5.0 mm as the core material, the EVA sponge 1.5 mm as the covering material, and the flexible urethane foam 4.0 mm are bonded together by an adhesive.
Composition table of the mouth material a: Polyester mesh material Foam sheet: Soft urethane foam 4.0 mm / EVA sponge 5.0 mm / EVA sponge 1.5 mm
Backing: Polyester knit material
<実施例2 履き口材b>
実施例2の履き口材bは、下記の構成であり、表材のポリエステルメッシュ素材は、発泡体シートのEVAスポンジ1.5mmと接着剤により貼り合わせされており、又、裏材のポリエステル系ニット素材は、EVAスポンジ1.5mmと接着剤により貼り合わせされている。又、芯材のEVAスポンジ5.0mmと被覆材のEVAスポンジ1.5mmとは接着剤によりそれぞれ貼り合わせされている。
履き口材bの構成
表材:ポリエステルメッシュ素材
発泡体シート:EVAスポンジ1.5mm/EVAスポンジ5.0mm/EVAスポンジ 1.5mm
裏材:ポリエステル系ニット素材
<Example 2 Footwear b>
The footwear b of Example 2 has the following constitution, and the polyester mesh material of the front material is bonded to the foamed EVA sponge 1.5 mm with an adhesive, and the polyester material of the backing material The knit material is bonded to EVA sponge 1.5 mm with an adhesive. The core EVA foam 5.0 mm and the covering EVA sponge 1.5 mm are bonded together with an adhesive.
Construction material of the mouthpiece material b: Polyester mesh material Foam sheet: EVA sponge 1.5 mm / EVA sponge 5.0 mm / EVA sponge 1.5 mm
Backing: Polyester knit material
<比較例1 履き口材c>
比較例1の履き口材cは、下記の構成であり、表材のポリエステルメッシュ素材は、発泡体シートの軟質ウレタンフォーム4.0mmと接着剤により貼り合わせされており、又、裏材のポリエステル系ニット素材は、軟質ウレタンフォーム15.0mmと接着剤により貼り合わせされている。又、軟質ウレタンフォーム15.0mmと軟質ウレタンフォーム4.0mmとは接着剤によりそれぞれ貼り合わせされている。
履き口材cの構成
表材:ポリエステルメッシュ素材
発泡体シート:軟質ウレタンフォーム4.0mm/軟質ウレタンフォーム15.0mm
裏材:ポリエステル系ニット素材
<Comparative Example 1 Footwear c>
The mouthpiece c of Comparative Example 1 has the following configuration, and the polyester mesh material of the front material is bonded to the foamed sheet of urethane foam 4.0 mm by an adhesive, and the polyester of the backing material. The system knit material is bonded to flexible urethane foam 15.0 mm with an adhesive. The flexible urethane foam 15.0 mm and the flexible urethane foam 4.0 mm are bonded to each other with an adhesive.
Composition of the cuff material c: Polyester mesh material Foam sheet: Soft urethane foam 4.0 mm / Soft urethane foam 15.0 mm
Backing: Polyester knit material
<比較例2 履き口材d>
比較例1の履き口材dは、下記の構成であり、表材のポリエステルメッシュ素材は、発泡体シートのEVAスポンジ3.0mmと接着剤により貼り合わせされており、又、裏材のポリエステル系ニット素材は、軟質ウレタンフォーム15.0mmと接着剤により貼り合わせされている。又、軟質ウレタンフォーム15.0mmとEVAスポンジ3.0mmとは接着剤によりそれぞれ貼り合わせされている。
履き口材dの構成
表材:ポリエステルメッシュ素材
発泡体シート:EVAスポンジ3.0mm/軟質ウレタンフォーム15.0mm
裏材:ポリエステル系ニット素材
<Comparative Example 2 Footwear d>
The footwear d of Comparative Example 1 has the following configuration, and the polyester mesh material of the front material is bonded to the foamed EVA sponge 3.0 mm with an adhesive, and the polyester material of the backing material The knit material is bonded to the flexible urethane foam 15.0 mm with an adhesive. Moreover, 15.0 mm of flexible urethane foam and 3.0 mm of EVA sponge are each bonded together with the adhesive agent.
Composition material of the mouthpiece material d: Polyester mesh material Foam sheet: EVA sponge 3.0 mm / soft urethane foam 15.0 mm
Backing: Polyester knit material
2.履き口材の水浸後の乾燥性評価
実施例1(履き口材a)、実施例2(履き口材b)、比較例1(履き口材c)、比較例2(履き口材d)の水浸後の乾燥度合いを、各試料に含まれる水分量変化を測定した。
試験方法は、各試料の大きさを7cm×9cmのサイズとし、予め乾燥状態での重量を測定した。
次に各試料に水を十分吸わせ、手で10回振って水切りをし、その直後の重量を測定後1時間毎に重量を測定した。そして、水浸後の試料の重量から乾燥状態での資料の重量を差し引いて求め、表2のごとくグラフに示す。
2. Example 1 (Foot mouth material a), Example 2 (Foot mouth material b), Comparative example 1 (Foot mouth material c), Comparative example 2 (Foot mouth material d) The degree of drying after water immersion was measured for the change in the amount of water contained in each sample.
In the test method, the size of each sample was 7 cm × 9 cm, and the weight in a dry state was measured in advance.
Next, each sample was sufficiently sucked with water, shaken by hand 10 times to drain water, and immediately after measuring the weight, the weight was measured every hour. And it subtracts the weight of the material in a dry state from the weight of the sample after water immersion, and shows it as a graph like Table 2.
<結果の考察>
実施例1及び実施例2の履き口材は、比較例1及び比較例2の履き口材に比べて、クッション性も良く、水浸後の吸水量が非常に少ないために速く乾燥することができた。
<Consideration of results>
The footwear materials of Example 1 and Example 2 have better cushioning properties than the footwear materials of Comparative Example 1 and Comparative Example 2, and can dry quickly because the amount of water absorption after water immersion is very small. did it.
3.靴での実施例
実施例の靴と比較例の靴の構成を表3に示す。
3. Example with shoes
Table 3 shows configurations of the shoe of the example and the shoe of the comparative example.
以下、実施例の靴と比較例の靴の詳細について述べる。
(実施例の靴)
実施例の靴の甲被は、履き口部および、舌の一部に前項で説明した<実施例1の履き口材a>を使用し、飾り材には合成皮革を使用し、その他の部分には、ナイロン製のダブルラッセルを用いた。この靴甲被を表3の中底材と共に吊り込みし、表3の底材を接着剤にて底付けし実施例の靴を得た。
実施例1の履き口材aの構成は下記の通りである。
<実施例1の履き口材a>
表材:ポリエステル系メッシュ
発泡体シート:軟質ウレタンフォーム4.0mm/EVAスポンジ5.0mm/EVAス ポンジ1.5mm
裏材:ポリエステル系ニット
Details of the shoes of the examples and the shoes of the comparative examples will be described below.
(Example shoes)
The upper part of the shoe of the example uses <the mouth material of Example 1> described in the previous section for the mouth part and part of the tongue, synthetic leather is used for the decoration material, and other parts A double raschel made of nylon was used. This shoe upper was hung together with the mid-sole material of Table 3, and the bottom material of Table 3 was attached with an adhesive to obtain the shoe of the example.
The configuration of the mouthpiece material a of Example 1 is as follows.
<Footwear material a of Example 1>
Surface: Polyester mesh foam sheet: Soft urethane foam 4.0 mm / EVA sponge 5.0 mm / EVA sponge 1.5 mm
Backing: Polyester knit
(比較例の靴)
比較例の靴の甲被は、履き口部及び舌部に前項で説明した比較例1の履き口材cを使用し、飾り材には合成皮革を使用し、その他の部分には、ナイロン製のダブルラッセルを用いた。この靴甲被を実施例の靴と同じ中底材と共に吊り込みし、実施例の靴と同じ底材を接着剤にて底付けし比較例の靴を得た。
比較例1の履き口材cの構成は下記の通りである。
<比較例1の履き口材c>
表材:ポリエステル系織物
発泡体シート:軟質ウレタンフォーム4.0mm/軟質ウレタンフォーム15.0mm/ EVAスポンジ1.5mm
裏材:ポリエステル系ニット
(Comparative shoes)
The shoe upper of the comparative example uses the cuff material c of the comparative example 1 described in the previous section for the mouth part and the tongue part, synthetic leather is used for the decoration material, and the other parts are made of nylon. Double raschel was used. This shoe upper was hung together with the same insole material as the shoe of the example, and the same bottom material as the shoe of the example was attached with an adhesive to obtain a shoe of a comparative example.
The structure of the footwear c of Comparative Example 1 is as follows.
<Footwear c of Comparative Example 1>
Surface material: polyester-based woven foam sheet: soft urethane foam 4.0 mm / soft urethane foam 15.0 mm / EVA sponge 1.5 mm
Backing: Polyester knit
4.靴での水浸後の乾燥性評価
上記実施例の靴と比較例の靴を洗濯し、乾燥度合いを比較した。
試験方法として、予め乾燥状態での各靴の重量を測定した。
次に各靴をドラム式洗濯機で10分間水洗いし水を十分含んだ状態にし、手で10回振って水切りを行った。その直後の靴の重量を測定し、以後1時間毎に重量を測定した。
靴に含まれる水分量を靴の重量から乾燥状態での靴の重量を差し引き求めた。
各靴に含まれる水分量変化を表4のごとくグラフに表した。
4). Dryability evaluation after water immersion in shoes The shoes of the above examples and the shoes of the comparative example were washed and the degree of drying was compared.
As a test method, the weight of each shoe in a dry state was measured in advance.
Next, each shoe was washed with a drum-type washing machine for 10 minutes so that it sufficiently contained water, and drained by shaking 10 times by hand. Immediately thereafter, the weight of the shoe was measured, and thereafter the weight was measured every hour.
The amount of water contained in the shoe was determined by subtracting the weight of the shoe in the dry state from the weight of the shoe.
Changes in the amount of water contained in each shoe are shown in a graph as shown in Table 4.
<結果の考察>
本発明の実施例の靴は、比較例の靴に比べて、水浸時の保水量が非常に少ないために速く乾燥することができた。
<Consideration of results>
The shoes of the examples of the present invention could be dried quickly because the amount of water retained during water immersion was very small compared to the shoes of the comparative examples.
1.表材
2.裏材
3.被覆材1
4.芯材
5.被覆材2
6.本発明の発泡体
7.従来品の発泡体
8.接着剤
1. Surface material 2. Backing 3. Covering material 1
4). 4. Core material Covering material 2
6). 6. Foam of the present invention 7. Conventional foam adhesive
Claims (5)
前記発泡体は、芯材となる発泡体の両面に薄手の被覆材となる発泡体が積層されており、芯材となる発泡体は、比重0.05〜0.20の非保水性の発泡体であることを特徴とする甲被材。 It is a thick shoe upper material used for the upper material, the mouthpiece member, the tongue member, etc. in which the foam is inserted between the front material and the back material,
In the foam, a foam as a thin coating material is laminated on both sides of a foam as a core material, and the foam as a core material is a non-water-retaining foam having a specific gravity of 0.05 to 0.20. Upper material characterized by the body.