JP2005179849A - Woven fabrics and uniforms with excellent heat retention - Google Patents
Woven fabrics and uniforms with excellent heat retention Download PDFInfo
- Publication number
- JP2005179849A JP2005179849A JP2003424617A JP2003424617A JP2005179849A JP 2005179849 A JP2005179849 A JP 2005179849A JP 2003424617 A JP2003424617 A JP 2003424617A JP 2003424617 A JP2003424617 A JP 2003424617A JP 2005179849 A JP2005179849 A JP 2005179849A
- Authority
- JP
- Japan
- Prior art keywords
- fabric
- polyphenylene sulfide
- fiber
- yarn
- woven fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【課題】低熱伝導性を有するポリフェニレンサルファイド繊維を用いて接触温感及び保温性を向上させると共に、織物表面への露出を極少に留め、織物品位及び物性の経時変化、劣化を防ぐと共にポリフェニレンサルファイド繊維の使用量を少なく留めることによって製品価格の向上を抑制した織物と前記織物を用いたユニフォームを提供すること。
【解決手段】 ポリフェニレンサルファイド繊維を少なくとも一部に使用した織物であって、ポリフェニレンサルファイド繊維を含む糸条の裏面浮き数最大値が２〜５本であり、前記糸条を構成するポリフェニレンサルファイド繊維以外の構成繊維がポリエステル系、ポリアミド系、ポリアクリロニトリル系、ポリオレフィン系、綿、羊毛、山羊毛、レーヨン、ポリノジックから選択される少なくとも一種類である保温性に優れた織物。及び前記織物を少なくとも一部に用いてなるユニフォーム。
【選択図】なし
[PROBLEMS] To improve contact thermal sensation and heat retention by using polyphenylene sulfide fiber having low thermal conductivity, minimize exposure to the surface of the fabric, prevent aging and deterioration of the fabric quality and physical properties, and polyphenylene sulfide fiber. The present invention provides a woven fabric that suppresses an improvement in product price by keeping the amount of use of the material small, and a uniform using the woven fabric.
SOLUTION: A woven fabric using polyphenylene sulfide fiber at least in part, wherein the maximum number of floats on the back side of the yarn containing polyphenylene sulfide fiber is 2 to 5, and other than polyphenylene sulfide fiber constituting the yarn A woven fabric excellent in heat retention, wherein the constituent fiber is at least one selected from polyester, polyamide, polyacrylonitrile, polyolefin, cotton, wool, goat wool, rayon and polynosic. And a uniform comprising at least a part of the fabric.
[Selection figure] None
Description
本発明は各種製造業、熱・ガス・電力供給業、鉄道など各種輸送業、飲食業など各種サービス業、病院など各種医療機関、上・下水道など各種公共機関等で着用されるユニフォーム用途に好適な織物及び該織物よりなるユニフォームに関するものであり、更に詳しくには接触温感に優れ冬季や寒冷地等の着用にても適度の保温性を有する織物及び該織物よりなるユニフォームに関するものである。 The present invention is suitable for uniforms worn in various manufacturing industries, heat / gas / power supply industries, various transport industries such as railways, various service industries such as restaurants, various medical institutions such as hospitals, various public institutions such as water and sewage systems, etc. The present invention relates to a woven fabric and a uniform made of the woven fabric. More specifically, the present invention relates to a woven fabric having excellent contact temperature feeling and suitable heat retention even when worn in winter or cold regions, and a uniform made of the woven fabric.
従来より、綿や羊毛などの天然繊維、レーヨンやポリノジックなどの再生繊維、ポリエステルやポリアミドなどの合成繊維がユニフォーム素材として広く使用されている。取り分け綿混素材やウール混素材は官公庁、学校を始め広く普及している。これら天然繊維素材の有する吸湿性能や保温性能は非常に良好であるが洗濯耐久性、Ｗ＆Ｗ性、その他取扱性に関して或る程度消費者の知識が必要になる他、耐薬品性や耐熱性が要求される分野においては支障を来す場合も多い。 Conventionally, natural fibers such as cotton and wool, recycled fibers such as rayon and polynosic, and synthetic fibers such as polyester and polyamide have been widely used as uniform materials. In particular, cotton blends and wool blends are widely used in government agencies and schools. These natural fiber materials have very good moisture absorption and heat retention performance, but require some consumer knowledge on washing durability, W & W performance, and other handling characteristics, as well as chemical resistance and heat resistance. In many cases, it will cause trouble.
ポリエステルやポリアミド等の合成繊維も物性面や価格面、取扱性の点で広く一般に使用されているが、汎用合成繊維からなる生地は保温性に乏しく冬季や寒冷地、或いは保冷倉庫など環境温度が低い条件での作業には支障を来たすものであった。係る問題を解決する為に最近、ポリフェニレンサルファイド繊維が注目されてきている。ポリフェニレンサルファイド繊維は耐熱性、耐薬品性、耐燃焼性に優れると共に低熱伝導性を有する素材として知られているが価格が汎用繊維対比で高価であること、染色性に乏しいこと、紫外線照射により変色すること（耐光堅牢性に乏しい）等が欠点となっている。該欠点を解決する為にポリフェニレンサルファイドの染色処方を検討し染色性、耐光堅牢度を向上させる方法が開示されている（例えば、特許文献１、２参照。）。
これらの染色処方によるとポリフェニレンサルファイド繊維も分散染料によって染色することが可能であるが高温高圧条件にて長時間染色が必須となり他繊維の劣化を引き起こす恐れがある他、分散剤や紫外線吸収剤、キャリアー剤等の薬剤が必須となり薬液コストも大きくなる。また紫外線吸収剤の効果によってある程度の耐光堅牢度向上が期待出来るが織編物の表面に多く露出する形態となれば経時変化による変色むらも懸念され、外衣やその他屋外作業ユニフォーム用途などには適したものにはならない。 According to these dyeing prescriptions, polyphenylene sulfide fibers can also be dyed with disperse dyes, but dyeing for a long period of time under high temperature and high pressure conditions may cause deterioration of other fibers, dispersants and ultraviolet absorbers, A drug such as a carrier agent is essential, and the cost of the chemical solution increases. In addition, it can be expected to improve light fastness to some extent by the effect of the UV absorber, but if it is exposed to a large amount on the surface of the woven or knitted fabric, there is a risk of discoloration unevenness due to aging, and it is suitable for outerwear and other outdoor work uniform applications. It will not be a thing.
本発明はかかる従来技術の課題を背景になされたものであって、低熱伝導性を有するポリフェニレンサルファイド繊維を用いて接触温感及び保温性を向上させると共に、織物表面への露出を極少に留め、織物品位及び物性の経時変化、劣化を防ぐと共にポリフェニレンサルファイド繊維の使用量を少なく留めることによって製品価格の向上を抑制した織物と前記織物を用いたユニフォームを提供することを課題とするものである。 The present invention has been made against the background of the problems of the prior art, and uses polyphenylene sulfide fibers having low thermal conductivity to improve the contact temperature feeling and heat retention, while keeping the exposure to the fabric surface to a minimum. It is an object of the present invention to provide a woven fabric and a uniform using the woven fabric in which improvement in product price is suppressed by preventing a change in fabric quality and physical properties with time and deterioration, and suppressing the amount of polyphenylene sulfide fiber used.
本発明者らは上記課題を解決する為に鋭意検討を重ねた結果、本発明を完成するに至ったもので、本発明は熱伝導性に乏しいポリフェニレンサルファイド繊維を肌側主体に配して接触温感、保温性を向上させると共に、該ポリフェニレンサルファイド繊維特有の低染色性、低耐光堅牢度という欠点を織組織の改良によって、織物表面への露出を抑え、外観品位低下や各種物性低下を防止することに着目し、本発明を完成した。即ち、本発明は以下の構成よりなる。
１．ポリフェニレンサルファイド繊維を少なくとも一部に使用した織物であって、ポリフェニレンサルファイド繊維を含む糸条の裏面浮き数最大値が２〜５本であり、前記糸条を構成するポリフェニレンサルファイド繊維以外の構成繊維がポリエステル系、ポリアミド系、ポリアクリロニトリル系、ポリオレフィン系、綿、羊毛、山羊毛、レーヨン、ポリノジックから選択される少なくとも一種類であることを特徴とする保温性に優れた織物。
２．生地熱伝導率が５．０×１０-2Ｗ／（ｍ・Ｋ）以下、最大熱流速度が０．０８Ｊ／（ｃｍ2・秒）以下であることを特徴とする上記第１に記載の保温性に優れた織物。
３．嵩高度が０．２０〜０．３５ｇ／ｃｍ3であることを特徴とする上記第１又は第２に記載の保温性に優れた織物。
４．導電性合成繊維フィラメントが織物の経糸及び／又は緯糸の少なくとも一部に使用され、二重織又は多重織の織組織の裏面側又は中間層に配されてなることを特徴とする上記第１〜第３のいずれかに記載の保温性に優れた織物。
５．ポリフェニレンサルファイド繊維の生地重量に占める含有率が２〜３０重量％であることを特徴とする上記第１〜第４のいずれかに記載の保温性に優れた織物。
６．上記第１〜第５のいずれかに記載の織物を少なくとも一部に用いてなることを特徴とするユニフォーム。
As a result of intensive studies to solve the above-mentioned problems, the present inventors have completed the present invention, and the present invention is arranged by contacting polyphenylene sulfide fibers having poor thermal conductivity on the skin side main body. Improves warmth and heat retention, as well as the low dyeability and low light fastness characteristic of polyphenylene sulfide fibers, improving the weaving structure suppresses exposure to the surface of the fabric and prevents deterioration in appearance quality and various physical properties. The present invention has been completed by paying attention to the above. That is, the present invention has the following configuration.
1. It is a woven fabric using polyphenylene sulfide fiber at least in part, and the maximum number of floats on the back surface of the yarn containing polyphenylene sulfide fiber is 2 to 5, and the constituent fibers other than polyphenylene sulfide fiber constituting the yarn are A woven fabric excellent in heat retention, characterized in that it is at least one selected from polyester, polyamide, polyacrylonitrile, polyolefin, cotton, wool, goat wool, rayon and polynosic.
2. The heat retention according to the first aspect, wherein the thermal conductivity of the dough is 5.0 × 10 −2 W / (m · K) or less and the maximum heat flow rate is 0.08 J / (cm 2 · sec) or less. Fabric with excellent properties.
3. The woven fabric excellent in heat retention according to the above first or second, wherein the bulk height is 0.20 to 0.35 g / cm 3 .
4). The conductive synthetic fiber filament is used for at least a part of the warp and / or weft of the woven fabric, and is arranged on the back side or the intermediate layer of the double woven or multi-woven woven structure. The fabric excellent in heat retention in any one of 3rd.
5). The woven fabric excellent in heat retention according to any one of the first to fourth aspects, wherein the content of the polyphenylene sulfide fiber in the fabric weight is 2 to 30% by weight.
6). A uniform comprising at least part of the woven fabric according to any one of the first to fifth aspects.
本発明によると、ポリフェニレンサルファイド繊維の特徴である低熱伝導性効果によって着用時の接触冷感が伴わず、冬季や保冷倉庫といった環境温度の低い状態でも快適に作業することが可能となる。またポリフェニレンサルファイド繊維を織物裏面又は中間層に配置することによって該ポリフェニレンサルファイド繊維特有の変色、堅牢度等の欠点を解決することが出来る他、該繊維使用量を少なく留め製品価格の向上を抑制することが出来る。 According to the present invention, due to the low thermal conductivity effect that is characteristic of polyphenylene sulfide fibers, there is no feeling of contact cooling at the time of wearing, and it becomes possible to work comfortably even in a low environmental temperature state such as winter or cold storage. In addition, by disposing polyphenylene sulfide fibers on the back or intermediate layer of the fabric, it is possible to solve the disadvantages such as discoloration and fastness that are specific to the polyphenylene sulfide fibers, and to reduce the amount of the fibers used to suppress an increase in product price. I can do it.
以下、本発明を更に詳細に説明する。
ポリフェニレンサルファイド繊維を含む糸条を構成するポリフェニレンサルファイド繊維以外の構成繊維はポリ（エチレンテレフタレート）、ポリ（トリメチレンテレフタレート）、ポリ（ブチレンテレフタレート）等の芳香族ポリエステル、ポリ（Ｌ−乳酸）、ポリ（βーヒドロキシブチレート）、ポリ（ωーカプロラクトン）、ポリ（ブチレンサクシネート）など脂肪族ポリエステル及びこれらの共重合物、ポリ（ε−カプロラクタム）やポリ（ヘキサメチレンアジパミド）などのポリアミド及びこれらの共重合物、ポリエチレンやポリプロピレンなどのポリオレフィン及びこれらの共重合物、ポリアクリロニトリル及びこれらの共重合物、エジプト綿やインド綿などの綿、ウールやアルパカ、モヘア等の羊毛及び山羊毛、銅アンモニアレーヨンやビスコースレーヨンなどのレーヨン及びポリノジックから用途に応じて適宜選択して使用されるものであり、一種類のみでなく複数種組み合わせて使用することも出来る。また上記の合成繊維、再生繊維は必要に応じて二酸化チタン、硫酸バリウムなどの艶消剤やその他改質剤を含有していてもよいし、断面形状も公知のものを採用することが出来る。
Hereinafter, the present invention will be described in more detail.
Constituent fibers other than polyphenylene sulfide fibers constituting the yarn containing polyphenylene sulfide fibers are aromatic polyesters such as poly (ethylene terephthalate), poly (trimethylene terephthalate), poly (butylene terephthalate), poly (L-lactic acid), poly Aliphatic polyesters such as (β-hydroxybutyrate), poly (ω-caprolactone), poly (butylene succinate) and their copolymers, polyamides such as poly (ε-caprolactam) and poly (hexamethylene adipamide) And copolymers thereof, polyolefins such as polyethylene and polypropylene, and copolymers thereof, polyacrylonitrile and copolymers thereof, cotton such as Egyptian cotton and Indian cotton, wool and goat wool such as wool, alpaca and mohair, Copper ammonia Are those that are suitably selected depending on the application of rayon and polynosic such Yung and viscose rayon, it may also be used in combinations of two or more thereof not only one type. Further, the above synthetic fibers and regenerated fibers may contain matting agents such as titanium dioxide and barium sulfate and other modifiers if necessary, and those having a known cross-sectional shape may be employed.
ポリフェニレンサルファイド繊維を含む糸条とはポリフェニレンサルファイドマルチフィラメント、及びその他のマルチフィラメント糸との混繊交絡糸、合撚糸、交撚糸等の長繊維束、ポリフェニレンサルファイドステープルファイバーを用いてなる紡績糸、及びその他の短繊維を混紡してなる紡績糸などを指す。長繊維束は必要に応じて撚糸して使用しても良いし、仮撚加工や流体攪乱処理その他公知の糸加工処理を施してもよい。また紡績糸についてもリング精紡の他、サイロスパン法やエアジェット法その他公知の紡績技術を用いて製造することが出来る。また長繊維と短繊維を複合させた長短複合紡績糸も取扱性や品位、物性面から好ましい形態である。 The yarn containing polyphenylene sulfide fiber is a polyphenylene sulfide multifilament, a mixed fiber entangled yarn with other multifilament yarn, a twisted yarn, a long fiber bundle such as a twisted yarn, a spun yarn using polyphenylene sulfide staple fiber, and This refers to spun yarn made by blending other short fibers. The long fiber bundle may be used after being twisted as necessary, or may be subjected to false twisting, fluid disturbance processing, or other known yarn processing. Also, the spun yarn can be produced using ring spinning, silo span method, air jet method, or other known spinning techniques. Long and short composite spun yarns in which long fibers and short fibers are combined are also preferable from the viewpoints of handleability, quality, and physical properties.
またポリフェニレンサルファイド繊維を含む糸条の裏面浮き数最大値を２〜５本とすることが耐スナッグ、耐ピリング性能を向上させるためにも好ましい。該最大値が２本未満の場合、即ち浮き数が１本の場合は織物裏面への露出が小さく留まる為に接触温感効果が小さく留まるばかりか織物表面への繊維露出が多くなり織物品位を損ねてしまう。また該最大値が５本を超過する範囲ではピリングやスナッグが抑制されず繰返し着用や洗濯操作による品位低下が著しくなり好ましくない。 In addition, it is preferable that the maximum value of the number of floats on the back surface of the yarn containing polyphenylene sulfide fiber is 2 to 5 in order to improve snag resistance and pilling resistance. When the maximum value is less than two, that is, when the number of floats is one, the exposure to the back of the fabric remains small, so the contact temperature effect is not only small, but also the fiber exposure to the fabric surface increases and the fabric quality is improved. It will be damaged. In addition, in the range where the maximum value exceeds 5, no pilling or snuggling is suppressed, and the deterioration in quality due to repeated wearing or washing operations becomes remarkable, which is not preferable.
本発明織物の熱伝導率はポリフェニレンサルファイド繊維の低熱伝導性の効果から低く留めることが可能である。生地の熱伝導率は５．０×１０-2Ｗ／（ｍ・Ｋ）以下、より好ましくは４．５×１０-2Ｗ／（ｍ・Ｋ）以下の範囲である。該熱伝導率が５．０×１０-2Ｗ／（ｍ・Ｋ）を超過する範囲では肌面から生地への熱移動が生じやすくなる為に着用時の接触冷感を伴うものとなってしまう。また生地の最大熱流速度は０．０８Ｊ／（ｃｍ2・秒）以下、より好ましくは０．０６Ｊ／（ｃｍ2・秒）以下の範囲が望ましい。最大熱流速度についても０．０８Ｊ／（ｃｍ2・秒）を超過する範囲となれば肌面から瞬時に生地への熱移動が生じてしまうために着用時の接触冷感を伴うものとなってしまい、保温性や着用快適性に優れたものにはならない。 The thermal conductivity of the woven fabric of the present invention can be kept low due to the low thermal conductivity effect of the polyphenylene sulfide fiber. The thermal conductivity of the dough is 5.0 × 10 −2 W / (m · K) or less, more preferably 4.5 × 10 −2 W / (m · K) or less. In the range where the thermal conductivity exceeds 5.0 × 10 −2 W / (m · K), heat transfer from the skin surface to the fabric is likely to occur, so that it is accompanied by a feeling of cold contact when worn. End up. The maximum heat flow rate of the dough is desirably 0.08 J / (cm 2 · sec) or less, more preferably 0.06 J / (cm 2 · sec) or less. If the maximum heat flow rate also exceeds 0.08 J / (cm 2 · sec), heat transfer from the skin surface to the fabric will occur instantaneously, which causes a feeling of cold contact when worn. Therefore, it does not become excellent in heat retention and wearing comfort.
また本発明織物の嵩高度は０．２０〜０．３５ｇ／ｃｍ3、より好ましくは０．２０〜０．３０ｇ／ｃｍ3の範囲であることが保温性や作業性等の面で好適である。嵩高度が小さい、即ち嵩密度が小さくなると生地に含まれる空気量が多くなる為に保温効果に優れたものとなる。嵩高度が０．２０ｇ／ｃｍ3未満の範囲では軽くて保温性に優れた生地とすることが可能であるが引裂強度や引張強度など生地物性面でユニフォームに供するには満足し得ないものとなる。逆に０．３５ｇ／ｃｍ2を超過する範囲では生地強度がユニフォーム用途に供するには十分なものとなるが保温性に乏しくなる他、生地目付が重くなる効果で作業性が悪くなる。 The bulk height of the woven fabric of the present invention is preferably in the range of 0.20 to 0.35 g / cm 3 , more preferably 0.20 to 0.30 g / cm 3 in terms of heat retention and workability. . When the bulk height is small, that is, when the bulk density is small, the amount of air contained in the dough increases, so that the heat retention effect is excellent. When the bulk height is less than 0.20 g / cm 3, it is possible to make a fabric that is light and excellent in heat retention, but is unsatisfactory for use as a uniform in terms of fabric properties such as tear strength and tensile strength. Become. On the other hand, in the range exceeding 0.35 g / cm 2 , the fabric strength is sufficient for use in uniforms, but the heat retention is poor, and workability is deteriorated due to the effect of increasing the fabric weight.
また本発明織物は導電性合成繊維フィラメントを織物の経糸及び／又は緯糸の少なくとも一部に使用し、二重織又は多重織の織組織の裏面側又は中間層に配したものであることがより好ましい。綿など親水性繊維の混率が大きくなれば導電性合成繊維フィラメントの混率を少なくすることが可能であるが、ポリフェニレンサルファイド繊維やポリエステル繊維など疎水性繊維の混率が高くなれば帯電し易く、特に冬季など低湿度環境下では着用快適性に支障を来すものになる他、静電気が原因で可燃物等に引火し思わぬ事故を誘発することもある。該導電性合成繊維フィラメントは等間隔に配置することが望ましく、経糸にストライプ状に配置したり経緯糸双方に使用しチェック状に配置することが出来る。配置する間隔は特に限定を加えるものでなく使用環境に応じて適宜選定すれば良い。 In the woven fabric of the present invention, the conductive synthetic fiber filament is used for at least a part of the warp and / or weft of the woven fabric and is arranged on the back side or the intermediate layer of the double woven or multi-woven woven structure. preferable. If the blending ratio of hydrophilic fibers such as cotton increases, the blending ratio of conductive synthetic fiber filaments can be reduced. However, if the blending ratio of hydrophobic fibers such as polyphenylene sulfide fibers and polyester fibers increases, charging tends to occur. In a low-humidity environment, wearing comfort may be disturbed, and flammable materials may be ignited by static electricity, causing unexpected accidents. The conductive synthetic fiber filaments are desirably arranged at equal intervals, and can be arranged in a stripe shape on the warp yarn or in a check shape using both the warp yarn and the weft yarn. The arrangement interval is not particularly limited and may be appropriately selected according to the use environment.
該導電性合成繊維マルチフィラメントは、二重織又は多重織の織組織の裏面又は中間層に配することが望ましい。表面に多く露出させると作業中の表面擦過により該導電性合成繊維マルチフィラメントが切断され易く制電効果が低下してしまい好ましくない。裏面若しくは中間層に配置することによって表面擦過による該繊維の損傷を防止すると共に、ユニフォームと肌面、ユニフォームとインナーとの摩擦等により発生する静電気を効果的に除去することが出来る。 The conductive synthetic fiber multifilament is preferably disposed on the back surface or intermediate layer of a double-woven or multi-woven texture. Exposing a large amount on the surface is not preferable because the conductive synthetic fiber multifilament is easily cut by surface abrasion during work and the antistatic effect is lowered. By disposing on the back surface or the intermediate layer, damage to the fibers due to surface abrasion can be prevented, and static electricity generated by friction between the uniform and the skin surface, the uniform and the inner can be effectively removed.
本発明のユニフォームは上記の織物生地を少なくとも一部に用いて公知の縫製方法によって得られるものである。該織物はエアージェットルーム、レピアルーム、プロジェクタイルルームなど公知の織機を用いて得ることが出来る。二重織若しくは多重織組織により生地製織されるため、経糸が複数種の糸配列の場合は複数のウィ−バースビームを用いて製織することが経糸緩みや経糸吊りなどを防止する上で有効である。 The uniform of the present invention is obtained by a known sewing method using at least a part of the woven fabric. The fabric can be obtained using a known loom such as an air jet loom, a rapier room, or a projector room. Since the fabric is woven in a double woven or multiple woven structure, weaving using multiple weaver beams is effective in preventing warp loosening and warp hanging when multiple types of warp are used. is there.
染色についても糸染め、浸染、捺染など公知の方法を用いて実施することが可能である。本発明ではポリフェニレンサルファイド繊維を生地裏面に多く露出させることによって該ポリフェニレンサルファイド繊維の欠点であった染色性の悪さや低耐光堅牢度、変色などの諸問題を抑制することが可能である。即ち、染色し難いポリフェニレンサルファイド繊維を織物織組織の鋭意検討によって極力、表面に露出させないようにすることにより表面品位の低下を抑制することが可能となった。織物織組織の検討により、染色し難いポリフェニレンサルファイド繊維をキャリアーやその他染色助剤を用いて無理に染色する必要がないので染色工程における高エネルギー負荷や廃液負荷を抑制すると共に、キャリアーや各種助剤等の生地残存による皮膚障害やその他の障害も抑制出来る。 Dyeing can also be carried out using known methods such as yarn dyeing, dip dyeing, and printing. In the present invention, by exposing a large amount of polyphenylene sulfide fiber on the back side of the fabric, it is possible to suppress various problems such as poor dyeability, low light fastness, and discoloration, which were disadvantages of the polyphenylene sulfide fiber. That is, it has become possible to suppress the deterioration of the surface quality by preventing polyphenylene sulfide fibers that are difficult to be dyed from being exposed to the surface as much as possible through intensive studies of the woven fabric structure. By examining the texture of the woven fabric, it is not necessary to forcibly dye polyphenylene sulfide fibers that are difficult to dye with a carrier or other dyeing assistants. It is also possible to suppress skin damage and other problems caused by remaining dough.
また本発明の織物及び該織物からなるユニフォームはその任意の製造工程において吸汗・吸水加工剤、抗菌・制菌加工剤、消臭加工剤、撥水加工剤、難燃加工剤、制電加工剤、紫外線吸収剤、蛍光増白剤などの機能加工剤をパッドスチーム法、パッドドライ法、吸尽法、スプレー法等の公知の方法で付与することが出来る。より好ましくは生地の状態でのパッドスチーム法、パッドドライ法、吸尽法が好適であり、更に好ましくは生地の状態での吸尽法が各種機能加工の耐久性からも有効である。 Further, the woven fabric of the present invention and the uniform made of the woven fabric are perspiration / water absorption processing agent, antibacterial / antibacterial processing agent, deodorant processing agent, water repellent processing agent, flame retardant processing agent, antistatic processing agent in any manufacturing process. Functional processing agents such as ultraviolet absorbers and fluorescent brighteners can be applied by known methods such as pad steam method, pad dry method, exhaust method, and spray method. More preferably, the pad steam method, pad dry method, and exhaust method in the fabric state are suitable, and still more preferably, the exhaust method in the fabric state is effective in terms of durability of various functional processes.
ポリフェニレンサルファイド繊維の生地重量に占める含有率は２〜３０重量％、より好ましくは２〜２０重量％の範囲である。該含有率が２重量％未満では接触温感を感じ得るものには仕上がらず、逆に該含有率が３０重量％を超過する範囲では接触温感を十分に感じ得るものとなるが織物表面への露出が多くなる為に、表面染め品位が悪くなるばかりでなく紫外線による変色も起こりやすく消費性能的にも好ましいものにはならない。 The content of the polyphenylene sulfide fiber in the fabric weight is in the range of 2 to 30% by weight, more preferably 2 to 20% by weight. If the content is less than 2% by weight, it will not be finished so that a feeling of contact temperature can be felt. Conversely, if the content exceeds 30% by weight, the feeling of contact temperature can be sufficiently felt, but the surface of the fabric will be felt. Therefore, not only the surface dyeing quality is deteriorated but also discoloration due to ultraviolet rays is likely to occur, which is not preferable in terms of consumption performance.
使用するポリフェニレンサルファイド繊維の単糸繊度については特に限定を加えるものでないが大略０．５〜３．０デシテックス、好ましくは０．７〜２．５デシテックスの範囲で用途、目的に応じて適宜選定すればよい。断面形状についても特に限定されるものでなく中実丸断面、中空丸断面、三角断面、偏平断面、多葉断面その他公知の断面形状で用途、目的に応じて選定することが出来る。また必要に応じて酸化チタンや硫酸バリウムなどの艶消剤や酸化防止剤や紫外線吸収剤、その他改質剤を添加物として予め繊維に含有させておくことも好ましい。 Although there is no particular limitation on the single yarn fineness of the polyphenylene sulfide fiber to be used, it is appropriately selected depending on the application and purpose within the range of about 0.5 to 3.0 dtex, preferably 0.7 to 2.5 dtex. That's fine. The cross-sectional shape is not particularly limited, and a solid round cross-section, a hollow round cross-section, a triangular cross-section, a flat cross-section, a multi-leaf cross-section, and other known cross-sectional shapes can be selected according to applications and purposes. Moreover, it is also preferable to add a matting agent such as titanium oxide or barium sulfate, an antioxidant, an ultraviolet absorber, and other modifiers as additives to the fiber as necessary.
本発明の織物に使用する導電性合成繊維マルチフィラメントは低融点の導電性金属やカーボンブラック等の導電性物質を複合紡糸法によってサイドバイサイド断面やシースコア断面、海島断面として複合させたもの、或いは合成繊維フィラメントや合成樹脂フィルム糸の表面に導電性繊維を蒸着、スパッタリングしたもの等が挙げられ、ポリエステル系やポリアミド系が好適に用いられる。該導電性合成繊維マルチフィラメントは導電性物質の少なくとも一部が表面に露出している形態が除電効果の観点から好ましい。導電性合成繊維マルチフィラメントは力学的強度に乏しい為、他の合成繊維マルチフィラメントや仮撚加工糸、紡績糸などと複合し交撚糸、カバリング糸として用いることが出来る。 The conductive synthetic fiber multifilament used in the woven fabric of the present invention is a composite of a low melting point conductive metal or a conductive material such as carbon black as a side-by-side cross section, seascore cross section or sea island cross section by a composite spinning method. Examples include those obtained by vapor-depositing and sputtering conductive fibers on the surface of fiber filaments or synthetic resin film yarns, and polyesters and polyamides are preferably used. In the conductive synthetic fiber multifilament, a form in which at least a part of the conductive material is exposed on the surface is preferable from the viewpoint of the static elimination effect. Since the conductive synthetic fiber multifilament has poor mechanical strength, it can be combined with other synthetic fiber multifilament, false twisted yarn, spun yarn and the like and used as a twisted yarn and a covering yarn.
以下、実施例に従い本発明を更に詳細に説明する。尚、本発明は以下の実施例に何ら限定されるものではない。また本文中及び実施例中の特性値は下記評価方法に準じて実施するものである。 Hereinafter, the present invention will be described in more detail with reference to examples. The present invention is not limited to the following examples. The characteristic values in the text and in the examples are implemented according to the following evaluation methods.
（生地目付）ＪＩＳ Ｌ−１０９６に記載の方法に準じた方法で１０ｃｍ×１０ｃｍにカットした試料を電子天秤で秤量し１ｍ2あたりに換算して生地目付（ｇ／ｍ2）を算出した。
（生地水分率）ＪＩＳ Ｌ−１０９６に記載の方法に準じた方法で１０ｃｍ×１０ｃｍにカットした試料の生地水分率（％）を評価した。
（生地厚さ）ＪＩＳ Ｌ−１０９６記載の方法に準じた方法で６ｇ／ｃｍ2の荷重下で生地厚さ（ｍｍ）を求めた。
（生地通気度）ＪＩＳ Ｌ−１０９６ Ａ法（フラジール形法）に準じた方法で生地の通気度（ｃｍ3／（ｃｍ2・秒））を求めた。
(Dough weight) A sample cut to 10 cm × 10 cm by a method according to JIS L-1096 was weighed with an electronic balance, and converted to 1 m 2 to calculate the dough weight (g / m 2 ).
(Dough moisture content) The dough moisture content (%) of the sample cut into 10 cm x 10 cm was evaluated by a method according to the method described in JIS L-1096.
(Dough thickness) The cloth thickness (mm) was determined under a load of 6 g / cm 2 by a method according to the method described in JIS L-1096.
(Fabric permeability) The permeability (cm 3 / (cm 2 · sec)) of the cloth was determined by a method according to JIS L-1096 A method (Fragile type method).
（生地の熱伝導率）精密迅速熱物質測定装置（カトウテック社製 サーモラボーII）を用
い熱源板温度３５℃、環境温湿度が２０℃及び６５％ＲＨの条件下で消費電力量（熱損失速度Ｗ）を測定した。また測定時の圧力（６ｇ／ｃｍ2荷重）での厚みを測定し熱伝導率（Ｗ／（ｍ・Ｋ））を求めた。
（保温率）上記熱伝導率測定により求めた消費電力量から保温率（％）を算出した。
（最大熱流速度）上記熱伝導率測定結果から最大熱流速度（Ｊ／（ｃｍ2・秒））を求めた。
（嵩高度）上記生地目付と生地厚さから嵩高度（ｇ／ｃｍ3）を算出した。
(Thermal conductivity of the dough) Power consumption (heat loss rate) under the conditions of a heat source plate temperature of 35 ° C, ambient temperature and humidity of 20 ° C and 65% RH using a precise rapid thermal substance measuring device (Thermabo II manufactured by Kato Tech Co. W) was measured. Further, the thickness at the measurement pressure (6 g / cm 2 load) was measured to obtain the thermal conductivity (W / (m · K)).
(Heat retention rate) The heat retention rate (%) was calculated from the power consumption determined by the above thermal conductivity measurement.
(Maximum heat flow rate) The maximum heat flow rate (J / (cm 2 · sec)) was determined from the thermal conductivity measurement result.
(Bulk height) The bulk height (g / cm 3 ) was calculated from the fabric weight and the fabric thickness.
（ピリング試験）ＪＩＳ Ｌ−１０７６ Ａ法（ＩＣＩ形試験機を用いる方法）記載の方法に準じてピリング試験を実施した。試料は生地表面の経方向、緯方向、及び生地裏面の経方向、緯方向をサンプリングし評価に供し、ピリング判定標準写真を用いて目視判定した。
（スナッグ試験）ＪＩＳ Ｌ−１０５８ Ａ法（ＩＣＩ形メース試験機法）記載の方法に準じてスナッグ試験を実施した。試料は生地表面の経方向、緯方向、及び生地裏面の経方向、緯方向をサンプリングし評価に供し、スナッグ判定標準写真を用いて目視判定した
(Pilling test) A pilling test was carried out according to the method described in JIS L-1076 A method (method using an ICI type testing machine). The sample was sampled for the warp direction and the weft direction of the fabric surface, and the warp direction and the weft direction of the back surface of the fabric for evaluation, and visually judged using a standard pilling judgment photograph.
(Snag test) A snag test was carried out according to the method described in JIS L-1058 A method (ICI type mace tester method). Samples were sampled for the warp direction of the fabric surface, the weft direction, and the warp direction and the weft direction of the back surface of the fabric and used for evaluation, and visually judged using a snug judgment standard photograph.
（実施例１）
ポリエステルセミダル丸断面マルチフィラメント部分配向糸（ＰＯＹ）を使用し公知の方法で仮撚施撚方向がＳ→Ｚの条件で延伸仮撚加工を実施し１６７デシテックス４８フィラメントのポリエステル仮撚加工糸を得た。引き続き、得られた仮撚加工糸をダブルツイスター（村田機械社製ＤＴ−３０８型）を用いてＳ撚方向に３５０回／ｍの追撚を加えた。以下、該撚糸条を繊維Ａと称する。
(Example 1)
Using a polyester semi-dal round cross-section multifilament partially oriented yarn (POY), a false twisting process is performed by a known method under the condition that the false twisting direction is S → Z, and a polyester false twisted yarn of 167 dtex 48 filament is obtained. Obtained. Subsequently, the obtained false twisted yarn was subjected to an additional twist of 350 times / m in the S twist direction using a double twister (DT-308 type manufactured by Murata Machinery Co., Ltd.). Hereinafter, the twisted yarn is referred to as fiber A.
導電性合成繊維フィラメント２８デシテックス２フィラメント（クラレ社製 商品名クラカーボ（Ｒ））とポリエステルセミダルマルチフィラメント仮撚加工糸５６デシテックス３６フィラメントとを同率供給下で合撚機（石川製作所社製ＤＴＦ型）を用いてＺ撚方向に４５０回／ｍの加撚を行った。以下、該合撚糸条を導電繊維Ｂと称する。 Conductive synthetic fiber filament 28 decitex 2 filament (Kuraray Co., Ltd., trade name Kurabobo (R)) and polyester semi-dal multifilament false twisted yarn 56 decitex 36 filament are fed at the same rate, and twisting machine (DTF type manufactured by Ishikawa Seisakusho Co., Ltd.) ) Was used to twist 450 times / m in the Z twist direction. Hereinafter, the twisted yarn is referred to as a conductive fiber B.
繊維Ａと導電繊維Ｂを同一のウィ―バースビームに導電繊維Ｂを同一間隔でストライプ状に配して巻取り経糸ビームを得た。該経糸ビームをレピアルーム（津田駒工業社製Ｒ−２００型）に設置し、図１に記載した織物組織を基本組織として、緯糸にポリフェニレンサルファイド繊維（東洋紡績社製 商品名ＰＲＯＣＯＮ（Ｒ））２．２デシテックス３８ｍｍステープルファイバーとポリエステル繊維（東洋紡績社製 商品名東洋紡エステル（Ｒ））１．７デシテックス３８ｍｍステープルファイバーの混率が重量比換算で７０：３０となるよう混打綿混紡しコーマ精紡糸（英式綿番手２０番相当）とした糸と経糸として用いた繊維Ａを双糸合撚した糸条（３３５デシテックス相当）を１本：１本交互の構成になるように用いた。製織された生機は実質的に上記コーマ糸が織物裏面に多く露出しており、織物表面には殆ど露出しない形態であった。因みに上記コーマ糸の織物裏面浮き数最大値は４本である。 The fiber A and the conductive fiber B were arranged in the same weave beam and the conductive fiber B in a stripe shape at the same interval to obtain a wound warp beam. The warp beam is installed in a rapier room (R-200 type, manufactured by Tsudakoma Kogyo Co., Ltd.), and the weave yarn shown in FIG. 1 is used as a basic structure, and polyphenylene sulfide fiber (trade name PROCON (R)) 2 is used for the weft. .2 decitex 38 mm staple fiber and polyester fiber (trade name Toyobo Ester (R) manufactured by Toyobo Co., Ltd.) 1.7 decitex 38 mm staple fiber blended cotton blended and combed cotton spinning so that the blend ratio is 70:30 in terms of weight ratio A yarn (corresponding to 335 decitex) obtained by twisting and twisting the yarn A (corresponding to English cotton count No. 20) and the fiber A used as the warp yarn was used so as to have an alternate configuration. The woven weaving machine has a form in which the combed yarn is substantially exposed on the back side of the fabric and hardly exposed on the surface of the fabric. Incidentally, the maximum value of the number of floats on the back side of the fabric of the combed yarn is four.
引き続き得られた織物生機を浴温９０℃のオープンソーパーで拡布状態でプレリラックスした後、浴温１２０℃で高圧液流精練を実施した。その後、乾熱雰囲気温度が１９０℃のヒートセッターで中間セットを実施した。その後、高圧液流染色機にて浴温１３０℃条件で分散染料による染色を実施した後、十分な還元洗浄、湯洗を実施し脱水後にウエット条件で帯電防止剤をパッドドライ法により付与し、乾熱雰囲気温度が１６０℃の条件でヒートセッターによる仕上げセットを実施し染生地を得た。染生地重量に対するポリフェニレンサルファイド繊維の重量比率は１５．２重量％であった。 Subsequently, the obtained fabric raw machine was pre-relaxed in an expanded state with an open soaper having a bath temperature of 90 ° C., and then subjected to high-pressure liquid scouring at a bath temperature of 120 ° C. Then, the intermediate set was implemented with the heat setter whose dry-heat atmosphere temperature is 190 degreeC. Then, after dyeing with a disperse dye at a bath temperature of 130 ° C. in a high-pressure liquid dyeing machine, sufficient reduction washing and hot water washing are performed, and after dehydration, an antistatic agent is applied by a pad dry method under wet conditions, Finishing set with a heat setter was performed under the condition of a dry heat atmosphere temperature of 160 ° C. to obtain a dyed fabric. The weight ratio of polyphenylene sulfide fiber to dyed fabric weight was 15.2% by weight.
得られた染生地を身生地に用いて公知の縫製方法によりツーピースの工場作業衣（ブルゾン、パンツ）を得た。着用時の接触温感があり保温性にも優れており、肌表面から熱を奪い難い為、温感が持続し寒冷地や冬季、保冷倉庫などの作業に好適なものとなった。得られた生地の一般物性を表１としてまとめた。 A two-piece factory work clothes (blouson, pants) were obtained by a known sewing method using the dyed fabric obtained as a body fabric. There is a feeling of contact temperature at the time of wearing and excellent heat retention, and it is difficult to take heat away from the skin surface, so the feeling of warmth is maintained and it is suitable for work in cold districts, winter and cold storage warehouses. The general physical properties of the obtained dough are summarized in Table 1.
（実施例２）
繊維Ａを単独で巻き取った経糸ビームとポリフェニレンサルファイド繊維（東洋紡績社製 商品名ＰＲＯＣＯＮ（Ｒ））２．２デシテックス３８ｍｍステープルファイバーとポリエステル繊維（東洋紡績社製 商品名東洋紡エステル（Ｒ））１．７デシテックス３８ｍｍステープルファイバーの混率が重量比換算で７０：３０となるよう混打綿混紡しコーマ精紡糸（英式綿番手２０番相当）とした糸を単独で巻き取った経糸ビームを使用し２本のウィ―バースビームによるダブルビーム方式を採用し図７に記載した織物組織を基本組織として製織した。使用した織機はレピアルーム（津田駒工業社製 Ｒ−２００型）であり緯糸には繊維Ａを双糸合撚した糸条（３３５デシテックス相当）を用いた。製織された生機は実質的に上記コーマ糸が織物裏面に多く露出しており、織物表面には殆ど露出しない形態であった。因みに上記コーマ糸の織物裏面浮き数最大値は２本である。
(Example 2)
Warp beam and polyphenylene sulfide fiber (trade name PROCON (R) manufactured by Toyobo Co., Ltd.) 2.2 decitex 38 mm staple fiber and polyester fiber (trade name Toyobo Ester (R) manufactured by Toyobo Co., Ltd.) 1 .7 Decitex 38mm staple fiber blended cotton blended so that the blend ratio is 70:30 in terms of weight ratio, using a warp beam that has been wound into a single combed yarn (corresponding to British cotton count 20). A double beam method using two weave beams was adopted, and the fabric structure shown in FIG. 7 was used as a basic structure. The loom used was a rapier room (R-200 type, manufactured by Tsudakoma Kogyo Co., Ltd.), and the weft was a yarn (corresponding to 335 decitex) in which the fiber A was twisted and twisted. The woven weaving machine has a form in which the combed yarn is substantially exposed on the back side of the fabric and hardly exposed on the surface of the fabric. Incidentally, the maximum value of the number of floats on the back side of the fabric of the combed yarn is two.
得られた生機を実施例１同様の方法で染色加工を施して染生地を得た。染生地重量に対するポリフェニレンサルファイド繊維の重量比率は１２．６重量％であった。得られた染生地を身生地に用いて公知の縫製方法によりツーピースの工場作業衣（ブルゾン、パンツ）を得た。着用時の接触温感があり保温性にも優れており、肌表面から熱を奪い難い為、温感が持続し寒冷地や冬季、保冷倉庫などの作業に好適なものとなった。得られた生地の一般物性を表１としてまとめた。 The obtained raw machine was dyed in the same manner as in Example 1 to obtain a dyed fabric. The weight ratio of polyphenylene sulfide fiber to dyed fabric weight was 12.6% by weight. A two-piece factory work clothes (blouson, pants) were obtained by a known sewing method using the dyed fabric obtained as a body fabric. There is a feeling of contact temperature at the time of wearing and excellent heat retention, and it is difficult to take heat away from the skin surface, so the feeling of warmth is maintained and it is suitable for work in cold districts, winter and cold storage warehouses. The general physical properties of the obtained dough are summarized in Table 1.
（比較例１）
実施例１で用いた繊維Ａ、導電繊維Ｂを配列したウィ―バースビームを用いて緯糸としてポリエステル繊維（東洋紡績社製 商品名東洋紡エステル（Ｒ））１．７デシテックス３８ｍｍステープルファイバーを１００％使用したコーマ精紡糸（英式綿番手２０番相当）と経糸として用いた繊維Ａを双糸合撚した糸条（３３５デシテックス相当）とを１本：１本交互の構成になるように用いた他は実施例１と同様にして染生地を得た。ポリフェニレンサルファイド繊維を含む繊維は不使用であるため該繊維の生地重量に対する重量比率は０重量％、該繊維の織物裏面浮き数の最大値は０本である。
(Comparative Example 1)
Polyester fiber (trade name Toyobo Ester (R) manufactured by Toyobo Co., Ltd.) 1.7 decitex 38 mm staple fiber is used as a weft using the weaver beam in which the fibers A and conductive fibers B used in Example 1 are arranged. Combed yarn (corresponding to British cotton count No. 20) and yarn (twisted with 335 dtex) twisted from fiber A used as the warp yarn are used in an alternate configuration. Obtained a dyed fabric in the same manner as in Example 1. Since fibers containing polyphenylene sulfide fibers are not used, the weight ratio of the fibers to the fabric weight is 0% by weight, and the maximum number of floats on the back side of the fabric is 0.
得られた染生地を身生地に用いて公知の縫製方法によりツーピースの工場作業衣（ブルゾン、パンツ）を得た。着用時には適度の保温性を有するものであったが、接触冷感を示すものとなり肌表面から熱を奪い易く、寒冷地や冬季、保冷倉庫などの作業には適したものにならなかった。得られた生地の一般物性を表１としてまとめた。 A two-piece factory work clothes (blouson, pants) were obtained by a known sewing method using the dyed fabric obtained as a body fabric. Although it had moderate heat retaining properties when worn, it showed a feeling of contact cooling and easily took heat from the skin surface, and was not suitable for work in cold regions, winter, cold storage warehouses and the like. The general physical properties of the obtained dough are summarized in Table 1.
（比較例２）
織物組織を図９に変更した（ポリフェニレンサルファイド繊維を含む糸条の織物裏面浮き数の最大値が１本）他は実施例２同様の方法で染生地を得た。染生地重量に対するポリフェニレンサルファイド繊維の重量比率は１２．６重量％であった。得られた染生地を身生地に用いて公知の縫製方法によりツーピースの工場作業衣（ブルゾン、パンツ）を得た。ポリフェニレンサルファイド繊維を含むコーマ精紡糸の織物裏面浮き数の最大値が２本と少なく裏面の耐ピリング性能、耐スナッグ性能その他物理的性能は良好なものであったが、織物表面への露出が多く、染色し難く耐光堅牢性の悪いポリフェニレンサルファイド繊維による表面のイラツキや変色が生じ、商品として好ましいものにはならなかった。得られた生地の一般物性を表１としてまとめた。
(Comparative Example 2)
A dyed fabric was obtained in the same manner as in Example 2 except that the fabric structure was changed to that shown in FIG. 9 (the maximum value of the number of floats on the back side of the fabric including the polyphenylene sulfide fiber was 1). The weight ratio of polyphenylene sulfide fiber to dyed fabric weight was 12.6% by weight. A two-piece factory work clothes (blouson, pants) were obtained by a known sewing method using the dyed fabric obtained as a body fabric. Comb spinning with polyphenylene sulfide fibers has a maximum number of floats on the back of the fabric of 2 and the back surface has good pilling resistance, snag resistance, and other physical performance, but there are many exposures to the fabric surface. However, it was difficult to dye, and surface irregularity and discoloration were caused by polyphenylene sulfide fibers having poor light fastness, which was not preferable as a product. The general physical properties of the obtained dough are summarized in Table 1.
（比較例３）
織物組織を図１０に変更した（ポリフェニレンサルファイド繊維を含む糸条の織物裏面浮き数の最大値が８本）他は実施例２同様の方法で染生地を得た。染生地重量に対するポリフェニレンサルファイド繊維の重量比率は１２．６重量％であった。得られた染生地を身生地に用いて公知の縫製方法によりツーピースの工場作業衣（ブルゾン、パンツ）を得た。ポリフェニレンサルファイド繊維を含むコーマ精紡糸の織物裏面浮き数の最大値は８本と多く、織物表面へのポリフェニレンサルファイド繊維の露出が少なく留まるために表面品位は良好であったが、裏面の耐ピリング性能、耐スナッグ性能が低く留まってしまい
消費性能的に好ましいものにはならなかった。得られた生地の一般物性を表１としてまとめた。
(Comparative Example 3)
A dyed fabric was obtained in the same manner as in Example 2 except that the fabric structure was changed to that shown in FIG. 10 (the maximum value of the number of floats on the back side of the fabric containing polyphenylene sulfide fibers was 8). The weight ratio of polyphenylene sulfide fiber to dyed fabric weight was 12.6% by weight. A two-piece factory work clothes (blouson, pants) were obtained by a known sewing method using the dyed fabric obtained as a body fabric. The maximum number of floats on the back side of the fabric of comb spinning spinning containing polyphenylene sulfide fibers is as high as 8 and the surface quality is good because the exposure of the polyphenylene sulfide fibers to the fabric surface remains low, but the back surface is resistant to pilling. The snag resistance performance remained low, and the consumption performance was not favorable. The general physical properties of the obtained dough are summarized in Table 1.
本発明の保温性に優れた織物及び該織物を用いてなるユニフォームは適度な保温性を有し、着用時の接触冷感を伴うことがないので冬季や低温環境下においても作業性を損なうことなく快適な作業を実施することが可能となる。またＷ＆Ｗ性や力学的物性も良好であり取扱性に優れた織物及びユニフォームを得ることが出来る。 The woven fabric excellent in heat retention of the present invention and the uniform formed using the woven fabric have moderate heat retention, and do not have a feeling of contact cooling when worn, so that workability is impaired even in winter or in a low temperature environment. It is possible to carry out comfortable work without any problems. In addition, it is possible to obtain a woven fabric and a uniform having excellent W & W properties and mechanical properties and excellent handleability.
（Ａ）ポリフェニレンサルファイド繊維を含む糸条（緯糸）
（Ｂ）ポリフェニレンサルファイド繊維を含まない糸条（緯糸）
（Ｃ）ポリフェニレンサルファイド繊維を含む糸条（経糸）
（Ｄ）ポリフェニレンサルファイド繊維を含まない糸条（経糸）
（Ｅ）導電性合成繊維糸条（経糸）
(A) Yarn (weft) containing polyphenylene sulfide fiber
(B) Yarn not containing polyphenylene sulfide fiber (weft)
(C) Yarn (warp) containing polyphenylene sulfide fiber
(D) Yarn not containing polyphenylene sulfide fiber (warp)
(E) Conductive synthetic fiber yarn (warp)
Claims (6)
A uniform comprising at least a part of the woven fabric according to any one of claims 1 to 5.