JP2005048367A

JP2005048367A - Frp concrete anti-corrosive panel and its manufacturing method

Info

Publication number: JP2005048367A
Application number: JP2003203276A
Authority: JP
Inventors: Masaru Uehara; 大上原; Shoji Yanada; 昭二簗田
Original assignee: Nitto Boseki Co Ltd
Current assignee: Nitto Boseki Co Ltd
Priority date: 2003-07-29
Filing date: 2003-07-29
Publication date: 2005-02-24
Anticipated expiration: 2023-07-29
Also published as: JP3972874B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide a lightweight FRP concrete anti-corrosive panel firmly adhesive to concrete, having rigidity usable as a permanent form, and having superior anti-corrosiveness and waterproofness. <P>SOLUTION: This anti-corrosive panel 1 of a laminated structure is constituted by joining a polymer cement layer 3 to one surface of a sheet-like base material 2, and an FRP layer 4 to an opposite side surface. Since the polymer cement layer 3 has superior affinity to the concrete, adhesive strength to the concrete can be enhanced. Since the FRP layer 4 has superior anti-corrosiveness and waterproofness and has large rigidity while being lightweight, the anti-corrosive panel can be used as the permanent form, and a superior anti-corrosive covering can be formed in a state of being installed on a concrete surface. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

【０００１】
【発明の属する技術分野】
本発明は、コンクリート製の躯体や建築物の補修、再生、防水、または防食用パネル等の用途に適した、永久型枠タイプ又は被覆防食タイプの繊維強化熱可塑性樹脂（ＦＲＰと略称する）製のコンクリート防食パネル（ＦＲＰコンクリート防食パネルという）及びその製造方法に関する。
【０００２】
【従来の技術】
【特許文献１】実開平６−３２０２８号公報
【特許文献２】特開平１１−３２４１０９号公報
【特許文献３】特開平７−２７６５３９号公報
従来より、コンクリート躯体の浸水・侵食防止のために、防水、防食用の防水パネルをコンクリート表面にコンクリートと一体化させて取り付けることが知られており、また、その防食パネルを永久型枠として用いることも知られている。この種の防水パネルには、軽量で薄いにも係わらず高い剛性を有し、且つコンクリートに対する接着性に優れ、しかも安価に製造できるという特性が要求されており、これらの特性を得るための種々な提案がされている。例えば、実開平６−３２０２８号公報（特許文献１）には、繊維強化熱可塑性樹脂（ＦＲＰ）上に立体編物を載せて一体化成形し、立体編物によりコンクリートに対するアンカー効果を持たせたコンクリート用防食板が提案されている。また、特開平１１−３２４１０９号公報（特許文献２）には、軽量化のためにプラスチックスバルーンや炭酸カルシウムを充填したタイプのＦＲＰを使った表面被覆型枠が提案されている。更に、特開平７−２７６５３９号公報（特許文献３）には、ＦＲＰの上にコアマット（商品名、オランダのランター社製）と言われる樹脂含浸不織布マット等とマイクロバルーンを含むハニカム構造の樹脂液不浸透性不織布マットからなるものを付着させたコンクリート用の仮設パネルが提案されている。
【０００３】
【発明が解決しようとする課題】
しかしながら、これらにはいずれも問題点があった。すなわち、特許文献１に示す防食板は、コンクリート打込み時に立体編物が潰れ易く、また、コンクリート配合によっては立体編物に当たって詰まり、コンクリートの進入を妨げて、そこに空隙を生じてしまうといった欠点があった。また、特許文献２に示す表面被覆型枠は、使用する資材が高価であるのみならず、コンクリートの一体性に問題を生ずる場合があり、又、パッチ式でパネルを製造するためコスト高になるという欠点があった。また、特許文献３に示す仮設パネルは、仮設パネルとしては有効であるが剛性に欠け、永久型枠としては使えない。
【０００４】
本発明はかかる問題点に鑑みてなされたもので、コンクリートに対して強固に接着することができ、且つ永久型枠としても使用可能な剛性を備え、軽量で且つ薄く、安価に製造可能なＦＲＰコンクリート防食パネル並びにその製造方法を提供することを課題とする。
【０００５】
【課題を解決するための手段】
請求項１に係る本発明のＦＲＰコンクリート防食パネルは、上記課題を解決するため、シート状の基材と、その基材の一方の面に接合されたポリマーセメント層と、前記基材の他方の面に接合された繊維強化熱可塑性樹脂層（ＦＲＰ層）を備えるという構成としたものである。このように基材の両面にポリマーセメント層とＦＲＰ層を積層する構成としたことで、ポリマーセメント層とＦＲＰ層が基材を介して強固に一体化した防食パネルを形成でき、ＦＲＰ層は、防食パネルに優れた防水性、防食性を付与すると共に、軽量で現場作業性を向上させ得るにも係わらず大きい剛性（強度特性）を付与することができ、ポリマーセメント層は、対セメント親和性により防食パネルにコンクリートに対する優れた一体化特性を付与する。かくして本発明の防食パネルは、コンクリートに対して良好に一体化することができ、長期間に渡って優れた防水、防食効果を発揮することができ、また、永久型枠として使用することにより、コンクリート打設作業の簡略化にも貢献できる。
【０００６】
ここで、前記したシート状の基材は、シート状材料に繊維をニードルパンチして前記シート状材料の両面に繊維が立体的な形態で存在するように取り付けたものとすることが好ましい。この構成とすると、繊維がポリマーセメント層やＦＲＰ層に対するアンカー効果を発揮し、ポリマーセメント層とＦＲＰ層の基材を介した接合強度をきわめて大きくできる利点が得られる。
【０００７】
請求項３に係る本発明のＦＲＰコンクリート防食パネルの製造方法は、シート状の基材の一方の面にポリマーセメントを塗布し硬化させてポリマーセメント層を形成し、次いで、前記基材の他方の面に接着剤を介してＦＲＰ板を重ね合わせ、全体をプレス機によって加圧し、基材とＦＲＰ板を接着することを特徴とし、この方法によりバッチ式で、上記した本発明に係るＦＲＰコンクリート防食パネルを製造できる。
【０００８】
請求項４に係る本発明のＦＲＰコンクリート防食パネルの製造方法は、予め、長尺のシート状の基材の一方の面にポリマーセメントを塗布し硬化させてポリマーセメント層を形成した長尺の前段積層材を用意しておき、走行中の第一のキャリアフィルム上に、熱硬化性樹脂液と強化繊維を供給し、その強化繊維に熱硬化性樹脂液を含浸させて強化繊維混合熱硬化性樹脂液層を形成し、その上に前記した前段積層材を、基材側を向けて載置し、その上に第二のキャリアフィルムを供給して挟み、その後、前記熱硬化性樹脂液を加熱硬化させて一体成形することを特徴とする、この方法により連続式で、上記した本発明に係るＦＲＰコンクリート防食パネルを製造できる。
【０００９】
上記した連続式での製造方法において、前記前段積層材を、前記第一のキャリアフィルム上の強化繊維混合熱硬化性樹脂液層の上に載置する前に、前記前段積層材の、前記基材側の表面に低収縮性樹脂を塗布することが好ましい。この構成とすると、熱硬化性樹脂液が基材中に含浸され過ぎることを防止すると共に加熱硬化時の収縮を抑制して反りの発生を抑制できる利点が得られる。
【００１０】
【発明の実施の形態】
以下に添付図面を参照して本発明のＦＲＰコンクリート防食パネル及びその製造方法の実施の形態を詳細に説明する。
【００１１】
図１は、本発明の基本的な実施形態に係るＦＲＰコンクリート防食パネル１の断面を拡大して概略的に示すものである。防食パネル１は、シート状の基材２と、その基材２の一方の面に接合されたポリマーセメント層３と、前記基材２の他方の面に接合された繊維強化熱可塑性樹脂層（ＦＲＰ層）４を備えた積層構造のものである。以下、各層を詳細に説明する。
【００１２】
基材２：基材２はポリマーセメント層３を担持してＦＲＰ層４に接合させるために使用されるものであり、ポリマーセメント層３を担持するのに必要な強度を備えると共にポリマーセメント層３及びＦＲＰ層４と良好に一体化することのできる特性を備えたものが使用される。基材２にはその片面に液状のポリマーセメントを塗布してポリマーセメント層３を形成し、その後に反対側の面にＦＲＰ層４を形成するが、片面に液状のポリマーセメントを塗布した際にそのポリマーセメントが基材の反対側の表面にまで浸透してしまうと、ＦＲＰ層の接合強度が低下する恐れがある。そこで、基材２はその片面に液状のポリマーセメントを塗布した際にそのポリマーセメントが基材の反対側の表面にまで染み出すことがほとんどなく、厚み方向のほぼ中央程度で浸透が止まるような特性のものとすることが好ましい。基材２としては、不織布、スパンボンド、織布、紙、シート、フィルム等を例示でき、特に、ポリマーセメントやＦＲＰ（接着剤を介してＦＲＰを接合する場合にはその接着剤）が入り込んで機械的な結合が得られるよう多くの微小な空隙を備えた構造のものが好ましい。また、これらの不織布、スパンボンド、織布、紙、シート、フィルム等は単体で用いる場合に限らず、適宜組み合わせて積層した形態で基材２として用いても良い。更には、基材２として、図２に示すように、不織布、スパンボンド、織布、紙、シート、フィルム等からなるシート状材料６に、繊維７（短繊維或いは長繊維のいずれでもよい）をニードルパンチしてそのシート状材料６の両面に繊維７が存在するように取り付けた不織布状の基材２Ａを用いることもできる。この構成の基材２Ａを用いると、シート状材料６の両面に繊維７が立体的な形態（多くの微小な空隙を備えた形態）で存在するため、図３に示すようにこの基材２Ａを用いて防食パネル１を作成した場合、ポリマーセメント層３及びＦＲＰ層４に対する接合強度を大きくできる。すなわち、基材２Ａの一方の面にポリマーセメントを塗布して一体化した際に、ポリマーセメントが繊維７間の空隙に進入し、換言すれば繊維７がポリマーセメント層３の中に入り込んだ状態となってアンカー効果を発揮することとなり、ポリマーセメント層に対する接合強度を大きくできる。また、その基材２Ａの他方の面にＦＲＰ層４を形成するには後述するように、基材２ＡにＦＲＰ板を接着剤を用いて接合する方法、或いは、基材２Ａを強化繊維混合熱硬化性樹脂液層に積層し、その熱硬化性樹脂液を加熱硬化させて一体化成形する方法を採るが、接着剤を用いてＦＲＰ板を接合した場合には接着剤層内に繊維７が存在することで接着剤層の基材２Ａに対する接着強度が大きくなり、結果的にＦＲＰ層に対する接合強度が大きくなり、また、一体化成形する場合においては繊維７に熱硬化性樹脂液が含浸して一体化するため、ＦＲＰ層内に繊維７が存在してアンカー効果を発揮し、ＦＲＰ層に対する接合強度が大きくなる。しかも、シート状材料６の両側に存在する繊維７はシート状材料６を貫通しているものが多いので、同じ繊維７にポリマーセメント層３とＦＲＰ層４が固定された形態となり、このため、繊維７がシート状材料６から剥がれるということがなく、この点からもポリマーセメント層３とＦＲＰ層４の基材２Ａを介した接合強度を大きくできる。
【００１３】
基材２、２Ａに用いる不織布、スパンボンド、織布等の材料としては、ポリエステル繊維、ポリアミド繊維、ポリエチレン繊維、アクリル繊維、ビニールエステル繊維などの耐アルカリ性を備えた材料を例示でき、なかでも、ポリアミド繊維、ポリエステル繊維が、ポリマーセメント層やＦＲＰ層に対する親和性、強度、耐久性、コスト等の面から好適である。また、基材２、２Ａに用いるシート、フィルム等の材料としても、ポリエステル、ポリアミド、ポリエチレン、アクリルなどの耐アルカリ性を備えた樹脂を例示できる。基材２Ａに用いる繊維７の材料としては、ポリエステル繊維、ポリアミド繊維、ポリエチレン繊維、アクリル繊維、ビニールエステル繊維などの耐アルカリ性を備えた材料を例示でき、特にビニールエステル繊維が好ましい。繊維７の長さ及び太さはニードルパンチ加工によりシート状材料６に取り付けることができると共にその両面に適度な剛性をもって立体的な形態を採りうるように定めれば良く、具体的には、長さは３０ｍｍ程度以上であれば、長繊維、短繊維のいずれでもよく、また、太さは１０〜３００デニール程度とすることが好ましい。基材２、２Ａの目付け量は、必要な強度及びポリマーセメント層及びＦＲＰ層に対する必要な接合強度が確保できるように定めるものであり、例えば、基材２を不織布単体で形成する場合は、８０〜２００ｇ／ｍ^２程度が好ましく、スパンボンド単体で形成する場合は、２０〜５０ｇ／ｍ^２程度が好ましい。また、基材２Ａにおいて、シート状材料６をスパンボンドで形成する場合、その目付け量は２０〜５０ｇ／ｍ^２程度が好ましく、それにニードルパンチして取り付ける繊維７の目付け量は５０〜２００ｇ／ｍ^２程度が好ましい。
【００１４】
ポリマーセメント層３：このポリマーセメント層３は、コンクリート、セメント、モルタル等に対して良好な接着性を発揮するように設けられるものであり、基材２の片面にポリマーセメントを塗布し乾燥させることにより形成される。ここで、基材に塗布するポリマーセメントは、セメントと耐アルカリ性のポリマー液を混合したものであり、そのポリマー液としては、ポリアクリル酸エステル共重合体エマルジョンを代表的なものとして例示できる。またこの他にも、エチレン酢酸ビニル共重合体エマルジョン、ＳＢＲエマルジョン等を用いても良い。ポリマーセメント層３におけるセメントとポリマーの比は、セメント１に対してポリマー０．２〜０．５程度とすることが好ましく、０．３程度とすることが最も好ましい。セメントの比率をあまり高くすると、塗布する際に流動性が不足して塗布が困難となると共に硬くなりすぎて、基材にポリマーセメンとを塗布して形成したシートの巻取が困難となり、一方、ポリマーの比率を高くするとコスト高となるので、前記のように定めるのが好ましい。ポリマーセメント層３内には必要に応じ、適当な骨材や充填材、例えば、炭酸カルシウム、珪砂、バルーン等を混入しておいてもよい。基材２の片面に塗布するポリマーセメント層３の厚さとしては、０．５〜３．０ｍｍ程度が好ましい。なお、ポリマーセメントを基材２に塗布するに当たっては、ポリマーセメントが基材２の裏側にまで浸透しないように、好ましくは基材の厚み方向のほぼ中央で浸透が止まるように、粘度、温度等の塗布条件を定めておくことが好ましい。図２に示す構成の基材２Ａを用いてその表面にポリマーセメント層を形成する場合、図５（ｂ）に示すように、その基材２Ａの片面に形成したポリマーセメント層３の表面から繊維７が露出するように、ポリマーセメント層３の厚さ及び／又は繊維７の突出高さを定めてもよいし、繊維７がポリマーセメント層３内に完全に埋もれるようにしてもよい。繊維７をポリマーセメント層３の表面に露出させておくと、その繊維がポリマーセメント層３の表面に接合するコンクリートに対してアンカー作用を果たし、接合強度を高めることができる。なお、防食パネル１の製造に当たっては、通常、図５（ａ）、（ｂ）に示すように、基材２、２Ａにポリマーセメント層３を接合した構成の前段積層材２０を作成しておき、その前段積層材２０の基材側表面にＦＲＰ層を形成する。このため前記した前段積層材２０を製造して保管することが多いので、ロール状に巻き取って保管できるようにすることが好ましく、従って、ポリマーセメント層３の厚さやセメントとポリマーの比の選定に当たっては、前段積層材２０が、ロール状に巻き取ることができる程度のやわらかさは備えるように選定することが好ましい。
【００１５】
ＦＲＰ層４：このＦＲＰ層４は防食パネル１に対して必要な剛性、強度、防水性、防食性等を付与するためのものである。ＦＲＰ層４に用いる熱硬化性樹脂は、基材２との密着性や、硬化した時の樹脂の剛性、靱性、成形性、及びコスト等の諸条件を考慮して選定するが、安価な点で最も良く使われるものとして、不飽和ポリエステル樹脂、フェノール（又はフェノールフォルマリン）樹脂、尿素ホルマリン樹脂がある。他の素材としては、エポキシ樹脂、ビニルエステル樹脂、及びウレタン樹脂、アクリルウレタン樹脂、アクリル系樹脂等を挙げることができる。必要に応じて樹脂中に適当なフィラーや着色剤を混入させてもよい。また、樹脂中に軽量性の機能を付与するために、中空バルーン等の軽量化材を、場合によっては、不燃性を付与するために水酸化アルミニウム等の難燃化剤を混入することも可能である。ＦＲＰ層４に用いる強化繊維としては、ガラス繊維、炭素繊維、水酸化アルミニウム繊維等の無機繊維、ビニロン繊維、ポリエステル繊維またはアラミド繊維等の有機繊維を用いることができるが、特にガラス繊維は強度が大きいので好まれる。これらの繊維の形態としては、織布、不織布、マット又は組布等を挙げることができる。不織布やマットを構成する繊維の長さも、短繊維、長繊維のいずれでもよい。形態は、通常はチョップドストランド（長さは自由）が用いられるが、これに限定されるものではない。ＦＲＰ層４における強化繊維の含有率は、必要な強度、生産性等を考慮して適宜定めれば良く、通常２５〜６０重量％程度に定められる。また、ＦＲＰ層４の厚さは、防食パネルに要求される強度、防食性等に応じて定めれば良く、例えば、防食パネルを、コンクリート管内面などの、あまり過酷でない条件下で使用する場合には、２〜３ｍｍ程度に、護岸のように過酷な条件下で使用する場合には、防食パネルに大きい剛性が必要とされるので、硬くて曲がり難くするために３〜１０ｍｍ程度に選定することが好ましい。
【００１６】
ＦＲＰ層４の形成には二つの方法を採りえる。一つは、基材２、２ＡにＦＲＰ板を接着剤を用いて接合する方法であり、他の一つは、基材２、２Ａを強化繊維混合熱硬化性樹脂液層に積層し、その熱硬化性樹脂液を加熱硬化させて一体化成形する方法である。このうち、後者の方法では基材２、２Ａに熱硬化性樹脂液が含浸して一体化するため、より大きい接合強度が得られる。
【００１７】
防食パネル１の形状は、通常は平坦であるが、使用場所に応じて、適宜湾曲させた形状としても良い。例えば、コンクリート管内面に取り付ける場合には、そのコンクリート管内面の湾曲に一致した形状としておけばよい。
【００１８】
次に、上記構成の防食パネル１の使用方法を説明する。この防食パネル１を永久型枠として使用する場合には、この防食パネル１をコンクリートを打設するための型枠として、ポリマーセメント層３がコンクリート側となるよにう設置し、その型枠内にコンクリートを流し込み、固化させる。これにより、図４に示すように、形成されたコンクリート躯体９の表面に防食パネル１が接合するので、防食パネル１をそのままコンクリート躯対９の表面に残し、防食被覆とする。ここで、ポリマーセメント層３はコンクリートに対する親和性に優れているので、防食パネル１はコンクリート躯体９に対してきわめて強固に接合しており、このため長期間に渡って剥がれることがない。また、表面側には剛性、防水性、防食性に優れたＦＲＰ層４があるため、長期間に渡って、剛性、防水性、防食性に優れた防食被覆として使用できる。
【００１９】
また、この防食パネル１は永久型枠として使用する場合に限らず、単にコンクリート表面の防食被覆として使用することもできる。その場合には、コンクリート打設用の型枠を設置し、その型枠内に防食パネル１をセットし、その後コンクリートを流し込んで固化させ、その後、型枠のみを外せばよい。これによってもコンクリート躯体の表面に防食パネル１を強固に接合させ、防食被覆を形成できる。なお、防食パネル１を永久型枠として使用せず、単にコンクリート表面の防食被覆として使用する場合にも、防食パネル１の形状を形成しようとするコンクリートの表面に対応した形状としておけばよいが、その防食パネル１の厚さが薄く、容易に変形させることができる場合には、必ずしもコンクリート表面形状に合わせる必要はなく、単に平坦な形状としておけばよい。この平坦な形状の防食パネル１をコンクリート管内面のような湾曲面に取り付けるに当たって、型枠の湾曲した内面に沿うように、防食パネルを湾曲させてセットし、その上にコンクリートを流し込むことによって、コンクリートの湾曲した面に防食パネル１を取り付けることができる。
【００２０】
次に、上記構成のＦＲＰコンクリート防食パネル１の製造方法を説明する。本願において提供する製造方法には、大別して二つの方法、すなわち、加圧接着法（製法Ａ）と連続成形法（製法Ｂ）の二つがある。以下それぞれを説明する。
【００２１】
（製法Ａ）加圧接着法
この方法は、あらかじめ作成したＦＲＰ板を基材に対して接着剤を用いて加圧接着することでＦＲＰ層４を形成する方法である。
この方法の実施に当たっては、まず、シート状の基材２を用意し、その基材２の一方の面にポリマーセメントを塗布し硬化させてポリマーセメント層４を形成し、図５（ａ）に示すように、基材２とポリマーセメント層４を一体構造とした前段積層材２０を作成する。なお、基材２として図２に示す基材２Ａを用いる場合には、図５（ｂ）に示すようにその基材２Ａにポリマーセメント層３を一体化した前段積層材２０を作成する。前段積層材２０は、製造しようとする防食パネル１にほぼ等しい大きさのものでもよいが、それよりもはるかに長尺のものを作成し、所望の長さに切断して使用する方法を採ることが作業効率が良いので好ましい。長尺の前段積層材２０を作成した場合には、ロール状に巻き取っておくことが取り扱いやすいので好ましい。また、前段積層材２０の作成と並行して、形成しようとするＦＲＰ層４の厚さに等しい厚さのＦＲＰ板を準備する。ＦＲＰ板の大きさは製造しようとする防食パネル１の大きさにほぼ等しく設定しておくものであり、例えば、幅１０００ｍｍ、長さ１８００〜２０００ｍｍ程度としておく。
【００２２】
次に、ＦＲＰ板の表面及び／又は前段積層材２０の基材２側の表面に、ＦＲＰ板と基材２の接着のための接着剤を塗布する。この塗布には任意の方法を採りうるが、一つの方法として図６（ａ）に示すロールコータ２１を用いてＦＲＰ板２５に塗布する方法を例示できる。このロールコータ２１は、上２個、下２個のそれぞれ反対向きに回転するローラ２３、２４を備えており、ＦＲＰ板２５の厚さに応じて上下のローラ間を適当なクリアランスを設定できるようになっている。このロールコータ２１では、上部の２個のローラ２３の間に接着剤２６をセットしておくことで、ローラ２３の回転で接着剤をローラ表面に付着させ、上下のローラ２３、２４の間を、ローラの回転によって送られるＦＲＰ板２５の上部ローラ２３側と接触する面にのみ接着剤２６を塗布することができる。この際、上側のローラ２３間のクリアランスを調整することで、ＦＲＰ板２５表面に対する接着剤の塗布量を所望の値に設定することができ、ＦＲＰ板２５の表面に所望量の接着剤を均等に塗布できる。なお、ロールコータ２１に通すＦＲＰ板２５の表面は、アセトン等で、ほこりやごみ等を予め落としておくことが好ましい。また、図５（ｂ）に示す形態の前段積層材２０を用いる場合で且つ基材２Ａの表面の繊維７が嵩張りすぎている場合には、前段積層材２０の基材２Ａ側の表面をプレス或いは加圧ローラ等で加圧加工処理して繊維７の膨らみを抑えておいてもよい。この加圧加工処理を施しておくと、繊維７間の空隙が小さくなって、接着剤の基材２Ａ表面への含浸速度を早くできる。
【００２３】
ここで用いる接着剤は、基材２とＦＲＰ板２５との間の塗工適正、及び作業性を主眼に選定すればよく、好ましい例を挙げるならば、ウレタン樹脂系、ゴム系、エポキシ樹脂系等であり、溶剤系、エマルジョン系、水系または無溶媒系を問わない。また、塗布量は、特に限定されないが、基材２又はＦＲＰ板２５に対して或いは界面当たり、通常１５０〜４５０ｇ／ｍ^２の塗布量が好ましい。
【００２４】
次いで、図６（ｂ）に示すように、ＦＲＰ板２５の接着剤２６の塗布面に、前段積層材２０を、基材２側の面を向けて重ね合わせて密着させて貼り合わせる。この時、ＦＲＰ板２５と前段積層材２０がずれないように、ゆっくりとどちらかの一端側から重ねてゆくのが望ましい。このようにして図６（ｃ）に示すように、前段積層剤２０とＦＲＰ板２５を積層した積層体２８が形成される。次に、その積層体２８を図６（ｄ）に示すプレス機３０内に積み重ねた状態で配置し、接着剤２６が完全に働くまで、プレス機３０で圧力３１を掛け、積層体２８全体を十分な時間圧縮し、ＦＲＰ板２５と前段積層剤２０の基材２とを確実に接着させる。これにより、図１に示す防食パネル１が形成される。この時のプレス機３０の圧力は、０．５〜３．０ｋｇｆ／ｃｍ^２程度が望ましいが、適宜変えても良い。プレス時間は８〜２４時間が適当である。プレス時間は季節などの環境的要因にもよるため、この限りではない。１回のプレスで一度に圧縮できるパネルの枚数は、生産性や、接着剤が働きはじめるまでに準備しうる積層体２８の枚数等を考慮して定めればよく、２０〜４０枚程度が好ましい。圧縮終了後、プレス機３０より積層体２８を取り出し、十分に接着しているかどうかを確認する。以上により、基材２に対してＦＲＰ板２５が強固に接着して一体化し、防食パネル１のＦＲＰ層４（図１参照）が形成され、図６（ｅ）に示すように、本発明に係る防食パネル１が得られる。その後、必要に応じ、該防食パネル１の端部４辺をカット機（図示せず）で予め設定されたサイズ、通常は９００ｍｍ×１８００ｍｍに精寸カットすることによって最終製品のサイズに加工する場合もある。また、成形する防食パネル１のサイズが、９００ｍｍ×１８００ｍｍ程度であれば、別に設置したターンバックルにパネルを移して圧縮させておき、プレス加工回数を向上させることも可能である。なお、図面の実施形態では平坦な防食パネル１を製造しているが、プレス機の積層体２８を支持する面を湾曲させた形としておくことにより、湾曲した形状の防食パネルを製造することができる。
【００２５】
（製法Ｂ）連続成形法
この方法は、基材に強化繊維混合熱硬化性樹脂液層を重ね合わせ、その熱硬化性樹脂を連続的に硬化させて一体化成形する方法である。
この方法においても、あらかじめ基材２にポリマーセメント層３を一体化した構造の長尺の前段積層材２０（図５参照）を作成し、ロール状に巻いて前段積層材ロールとしておく。なお、以下の実施の形態では、基材２として図２に示す形態の基材２Ａを用い、従って、図５（ｂ）に示す構造の前段積層材２０を用いている。
【００２６】
図７に示すように、キャリアフィルムロール３４Ａから第一のキャリアフィルム３４を引き出し、所定の走行経路に沿って走行させておく。このキャリアフィルム３４並びに後述する第二のキャリアフィルム３５には、通常、ＰＥＴ、ナイロン及びＰＶＡ等の長尺フィルムが良く使われるが、これらに限定されるものではない。走行中の第一のキャリアフィルム３４の上に、樹脂タンク３８から液状の未硬化の熱硬化性樹脂３９を一定量連続供給し、ドクターナイフ４０でキャリアフィルム３４上の樹脂３９の厚さを一定に調整する。次いで、キャリアフィルム３４上の樹脂３９の上に強化繊維４２をコンベア４３により連続的に供給してゆく。ここで用いる強化繊維４２の形態としては、織布、不織布、マット、組布等を挙げることができる。また、不織布、マット等を用いる場合、それを構成する繊維の長さは短繊維、長繊維のいずれでもよい。マットを用いる場合には、ロービング等の連続した強化繊維を所定の長さに切断して短繊維形態（チョップドストランド）の強化繊維とし、そのチョップドストランドを一定速度で走行しているコンベア等の上に一定厚さとなるように供給することで、一定厚さのチョップドストランドマットを形成し、そのチョップドストランドマットを強化繊維４２としてキャリアフィルム３４上に供給すればよい。このようにして、強化繊維４２をキャリアフィルム３４上の未硬化の熱硬化性樹脂３９の上に連続的に供給することで、その強化繊維４２に熱硬化性樹脂３９が含浸し、キャリアフィルム３４上に未硬化の強化繊維混合熱硬化性樹脂液層３９Ａが形成される。なお、必要に応じ、前記強化繊維混合熱硬化性樹脂液層３９Ａ内の強化繊維に対する樹脂液の含浸を確実にするため適当な含浸ローラを設けるとか、熱硬化性樹脂液を新たに供給する等の変更を加えても良い。
【００２７】
一方、あらかじめ準備していた前段積層材ロール（図示せず）から前段積層材２０を、基材２（図５参照）側を下側にして引き出し、その前段積層材２０の基材表面に、低収縮性樹脂液（詳細は後述する）を樹脂液塗布ローラ４５で塗布した後、その前段積層材２０をキャリアフィルム３４上の強化繊維混合熱硬化性樹脂液層３９Ａ上に、基材側を向けた状態で載置してゆき、含浸ローラ４６で押し付けて行く。次いで、キャリアフィルムロール３５Ａから引き出した第二のキャリアフィルム３５を、強化繊維混合熱硬化性樹脂液層３９Ａ上に載置された前段積層材２０上にかぶせ、上下のキャリアフィルム３４、３５及びそれに挟まれた強化繊維混合熱硬化性樹脂液層３９Ａと前段積層材２０を上下のスクイズローラ４８の間に送り込んで加圧し、未硬化の強化繊維混合熱硬化性樹脂液層を脱泡させると共に全体の厚さを所望の値に（例えば、用途によっても異なるが、通常２〜１０ｍｍ程度）に調整する。次いで、その強化繊維混合熱硬化性樹脂液層３９Ａと前段積層材２０との積層体を、通常、８０〜１５０°Ｃに昇温させた硬化炉５０に送り込み、硬化に要するに十分な時間通過させ、熱硬化性樹脂を硬化させる。これにより、強化繊維混合熱硬化性樹脂液層３９Ａが硬化してＦＲＰ層４（図１参照）となると共に前段積層材２０に接合し、完全に一体化した積層体が連続的に成形されてゆく。その後、その積層体からその両面に付着している第一及び第二のキャリアフィルム３４、３５を剥がしてロール３４Ｂ、３５Ｂに巻き取り、次いで前記積層体をカッター５２で任意の寸法にカットする。これにより、ＦＲＰコンクリート防食パネル１が形成される。以上の成形工程におけるラインスピードは特に限定されないが、０．１〜１０ｍ／分、好ましくは０．８〜５ｍ／分である。以上のようにして、所望長さのＦＲＰコンクリート防食パネル１を連続成形方法によって低コストで製造できる。
【００２８】
以上に説明した連続成形方法においては、前段積層材２０の基材表面に低収縮性樹脂液を塗布している。これは次の理由による。すなわち、この実施の形態では、前段積層材２０に用いている基材２Ａが、ニードルパンチ加工によって取り付けられた多量の繊維７を有するきわめて空隙の多い不織布状となっているので、この基材２Ａを未硬化の強化繊維混合熱硬化性樹脂液層３９Ａの上に載置した時、熱硬化性樹脂液を含浸しすぎてしまうことがあり、また、加熱硬化の際に熱収縮して反りを生じてしまうことがある。そこでこれを防止するため、前段積層材２０の基材表面に低収縮性樹脂液を塗布しておき、熱硬化性樹脂液の含浸を抑制し、また、熱収縮を抑制して反りの発生を防止している。ここで使用する低収縮性樹脂としては、例えば、日立化成工業株式会社製のＷＰＣ−４０２Ａ、ＷＰＣ−４０２Ｂ等を挙げることができる。
【００２９】
また、上記した連続成形方法の実施に当たって、前段積層材２０の基材表面に低収縮性樹脂液を塗布する樹脂液塗布ローラ４５の上流において、前段積層材２０の基材表面を加圧ローラ等で加圧加工処理して繊維７［図５（ｂ）参照］のふくらみ量を抑制することも推奨される。この加圧加工処理を施しておくと、繊維７間の空隙が小さくなって、熱硬化性樹脂液の基材２Ａへの含浸速度が早くなり、該樹脂液の吸着率が早く飽和点に達する利点が得られる。
【００３０】
上記の連続成形方法によって製造した防食パネル１では、強化繊維混合熱硬化性樹脂液が基材２Ａ内に浸透・拡散し、基材２Ａを共有した形態で硬化するため、基材２ＡとＦＲＰ層４が強固に一体化しており、高い剛性を持った防食パネルを得ることができる。
【００３１】
【実施例】
実施例１
（１）前段積層材２０の作成
ポリエステル繊維製のスパンボンド（目付け量３０ｇ／ｍ^２）にビニロン繊維（太さ１００デニール、目付け量２００ｇ／ｍ^２）をニードルパンチ加工して取り付け、図２に示す形態の基材２Ａを作成した。次いで、その基材２Ａの片面に、セメントとポリアクリル酸エステル共重合体エマルジョンの混合体（固形分の混合比１：０．５）を約１ｍｍの厚さに塗布し、乾燥、硬化させて、図５（ｂ）に示す形態の前段積層材２０を作成した。
（２）ＦＲＰ板
ＦＲＰ板として、厚さ２ｍｍのガラス繊維強化ポリエステル樹脂板（日東紡績株式会社製）を準備した。
（３）加圧接着操作
ＦＲＰ板の表面に接着剤（ＫＵ−８５０、コニシ株式会社製）を、図６（ａ）に示すロールコータ２１によって塗布量３００ｇ／ｃｍ^２となるように塗布し、その上に前段積層材２０を重ね合わせて積層体２８とした。次に、この積層体２８をプレス機にセットし、１．０ｋｇｆ／ｃｍ^２の圧力を加えた状態で１６時間保持した。その後、プレス機から取り出して防食パネル１を得た。
（４）結果
得られた防食パネル１では、基材２Ａの両面にポリマーセメント層３とＦＲＰ層４が確実に接着した状態となっており且つ反りのない平坦なものであった。この防食パネル１のポリマーセメント層側にコンクリートを打設したところ、防食パネル１はコンクリート表面に確実に接着していた。また、対コンクリート剥離強度を測定したところ、２０ｋｇｆ／ｃｍ^２もあり、きわめて大きい値であった。
【００３２】
実施例２
（１）前段積層材２０の作成
ポリエステル繊維製のスパンボンド（目付け量３０ｇ／ｍ^２）にビニロン繊維（太さ１００デニール、目付け量２００ｇ／ｍ^２）をニードルパンチ加工して取り付け、図２に示す形態の基材２Ａを作成した。次いで、その基材２Ａの片面に、セメントとポリアクリル酸エステル共重合体エマルジョンの混合体（固形分の混合比１：０．５）を約１ｍｍの厚さに塗布し、乾燥、硬化させて図５（ｂ）に示す形態の前段積層材２０を作成した。
（２）連続成形操作
図７に示す連続成形ラインにおいて、ライン速度０．８５ｍ／ｍｉｎで走行するポリエチレンテレフタレート製の第一のキャリアフィルム３４（ユニチカ株式会社製、厚さ２５μｍ）上に未硬化の不飽和ポリエステル樹脂液（大日本インキ工業株式会社製）及びガラス繊維（日東紡績株式会社製、平均直径０．０２ｍｍ、平均長さ５０ｍｍのガラス繊維のマット）を供給し、ガラス繊維混合不飽和ポリエステル樹脂液層３９Ａ（厚さ２〜３ｍｍ程度）を形成した。次に、前段積層材２０の基材側表面に樹脂液塗布ローラ４５によって低収縮性樹脂液（ＷＰＣ−４０２ＡとＷＰＣ−４０２Ｂの混合液、日立化成工業株式会社製）を塗布した後、その前段積層材２０を第一のキャリアフィルム３４上のガラス繊維混合不飽和ポリエステル樹脂液層３９Ａ上に重ね合わせ、更にその上に第二のキャリアフィルム３５（ユニチカ株式会社製、厚さ２５μｍ）をかぶせた後、上下のスクイズローラ４８の間に送って挟み込み、密着させると共にガラス繊維混合不飽和ポリエステル樹脂液層３９Ａを脱泡させ、厚さを約５ｍｍに調整した後、１５０°Ｃに設定している硬化炉５０内に送り込み、炉内を３０分間走行させることで、不飽和ポリエステル樹脂液３９Ａを加熱、硬化させ、一体化した積層体とした。走行して硬化炉５０から出てきた積層体から第一及び第二のキャリアフィルム３４、３５を剥がして巻き取り、積層体をカッターによって約１．８ｍの長さにカットし、幅９００ｍｍ×長さ１８００ｍｍの防食パネル１を得た。
（３）結果
得られた防食パネル１は、全体の厚さが約５ｍｍ、ＦＲＰ層４の厚さが約２ｍｍであった。また、基材２Ａの両面にポリマーセメント層３とＦＲＰ層４が確実に接着した状態となっており且つ反りのない平坦なものであった。この防食パネル１のポリマーセメント層側にコンクリートを打設したところ、防食パネル１はコンクリート表面に確実に接着していた。また、対コンクリート剥離強度を測定したところ、２１ｋｇｆ／ｃｍ^２もあり、きわめて大きい値であった。
【００３３】
【発明の効果】
以上に説明したように、本発明のＦＲＰコンクリート防食パネルは、ポリマーセメント層とＦＲＰ層をシート状の基材を介して一体化した積層構造のものであるので、ポリマーセメント層による、コンクリート（セメント、モルタル等を含む）に対する優れた親和性を備え、且つＦＲＰ層による、軽量性、大きい剛性、優れた防水、防食性等を備えており、コンクリート表面に大きい接合力で取り付けることができると共に、長期間に渡って優れた防水、防食効果を発揮することができ、また、軽量であるので作業性が良く、しかも剛性が大きいので永久型枠として使用することもできるといった種々な効果を有している。また、本発明の防食パネルの製造に使用する資材は、特に高価なものはないので、低コストで製造できるといった効果も有している。
【００３４】
また、本発明の第一の製造方法は、シート状の基材を用意し、その基材の一方の面にポリマーセメントを塗布し硬化させてポリマーセメント層を形成し、次いで、前記基材の他方の面に接着剤を介してＦＲＰ板を重ね合わせ、全体を加圧して接着する構成としているので、バッチ式で、上記した本発明のＦＲＰコンクリート防食パネルを製造でき、また、プレスの加圧面の形状を所望の形状となるように湾曲させておくことで、湾曲した形状の防食パネルを製造することもできるという効果を有している。
【００３５】
本発明の第二の製造方法は、予め、長尺のシート状の基材の一方の面にポリマーセメントを塗布し硬化させてポリマーセメント層を形成した長尺の前段積層材を用意しておき、走行中の第一のキャリアフィルム上に、強化繊維と熱硬化性樹脂液を供給して強化繊維混合熱硬化性樹脂液層を形成し、その上に前記した前段積層材を、基材側を向けて載置し、その上に第二のキャリアフィルムを供給して挟み、その後前記熱硬化性樹脂液を加熱硬化させて一体成形する構成としているので、連続式で生産性良く、且つ低コストで上記した本発明のＦＲＰコンクリート防食パネルを製造できるという効果を有している。
【図面の簡単な説明】
【図１】本発明の一実施形態に係るＦＲＰコンクリート防食パネルの概略断面図
【図２】図１の防食パネルに用いる基材の１例を示す概略断面図
【図３】図２の基材を用いて形成した防食パネルの概略断面図
【図４】図１の防食パネルをコンクリート表面に接合した状態を示す概略断面図
【図５】（ａ）基材とポリマーセメント層の積層体である前段積層材の概略断面図
（ｂ）図２に示す基材を用いて形成した前段積層材の概略断面図
【図６】（ａ）、（ｂ）、（ｃ）、（ｄ）、（ｅ）は、加圧接着法によって防食パネルを製造する工程を説明する模式図
【図７】連続成形法によって防食パネルを製造する工程を示す模式図
【符号の説明】
１ＦＲＰコンクリート防食パネル
２、２Ａ基材
３ポリマーセメント層
４ＦＲＰ層
６シート状材料
７繊維
９コンクリート躯体
２０前段積層材
２１ロールコータ
２３、２４ローラ
２５ＦＲＰ板
２６接着剤
３０プレス機
３４第一のキャリアフィルム
３５第二のキャリアフィルム
３９熱硬化性樹脂液
３９Ａ強化繊維混合熱硬化性樹脂液層
４２強化繊維
４５樹脂液塗布ローラ
４６含浸ローラ
４８スクイズローラ
５０硬化炉
５２カッター[0001]
BACKGROUND OF THE INVENTION
The present invention is a permanent frame type or coated anticorrosion type fiber reinforced thermoplastic resin (abbreviated as FRP) suitable for applications such as repairing, recycling, waterproofing, and anticorrosion panels for concrete frames and buildings. The present invention relates to a concrete anticorrosion panel (referred to as FRP concrete anticorrosion panel) and a method for producing the same.
[0002]
[Prior art]
[Patent Document 1] Japanese Utility Model Publication No. 6-32028
[Patent Document 2] JP-A-11-324109
[Patent Document 3] JP-A-7-276539
Conventionally, it has been known that a waterproof and anticorrosion waterproof panel is attached to a concrete surface in an integrated manner with concrete to prevent water intrusion and erosion of the concrete frame, and the anticorrosion panel is used as a permanent formwork. It is also known. This type of waterproof panel is required to have characteristics that it is lightweight and thin but has high rigidity, excellent adhesion to concrete, and can be manufactured at low cost. Proposals have been made. For example, in Japanese Utility Model Publication No. 6-32028 (Patent Document 1), a solid knitted fabric is placed on a fiber reinforced thermoplastic resin (FRP) and integrally molded, and the solid knitted fabric has an anchor effect on the concrete. Anticorrosion plates have been proposed. Japanese Patent Application Laid-Open No. 11-324109 (Patent Document 2) proposes a surface-covered formwork using a plastic balloon or FRP filled with calcium carbonate for weight reduction. Further, JP-A-7-276539 (Patent Document 3) discloses a resin liquid having a honeycomb structure including a resin-impregnated nonwoven mat called a core mat (trade name, manufactured by Lanter, the Netherlands) on the FRP, and a microballoon. There has been proposed a temporary panel for concrete to which is attached an impermeable nonwoven mat.
[0003]
[Problems to be solved by the invention]
However, both of these have problems. That is, the anticorrosion plate shown in Patent Document 1 has a drawback in that the solid knitted fabric is easily crushed when the concrete is placed, and depending on the concrete composition, the solid knitted fabric hits and clogs, impedes the entry of the concrete and creates a void there. . In addition, the surface-covered form shown in Patent Document 2 is not only expensive, but may cause problems in the integrity of the concrete, and the cost increases because the panel is manufactured in a patch type. There was a drawback. The temporary panel shown in Patent Document 3 is effective as a temporary panel, but lacks rigidity, and cannot be used as a permanent mold.
[0004]
The present invention has been made in view of such a problem, and is an FRP that can be firmly bonded to concrete, has rigidity that can be used as a permanent mold, is lightweight and thin, and can be manufactured at low cost. It aims at providing a concrete anticorrosion panel and its manufacturing method.
[0005]
[Means for Solving the Problems]
In order to solve the above problems, the FRP concrete anticorrosion panel of the present invention according to claim 1 is a sheet-like base material, a polymer cement layer bonded to one surface of the base material, and the other base material of the base material. The fiber reinforced thermoplastic resin layer (FRP layer) joined to the surface is provided. As described above, the construction in which the polymer cement layer and the FRP layer are laminated on both surfaces of the base material can form a corrosion prevention panel in which the polymer cement layer and the FRP layer are firmly integrated via the base material. In addition to providing excellent anti-corrosion and anti-corrosion properties to the anti-corrosion panel, it can provide high rigidity (strength characteristics) despite being lightweight and capable of improving on-site workability, and the polymer cement layer is compatible with cement This gives the anticorrosion panel excellent integration characteristics for concrete. Thus, the anticorrosion panel of the present invention can be satisfactorily integrated with concrete, can exhibit excellent waterproofing and anticorrosion effects over a long period of time, and can also be used as a permanent formwork. It can also contribute to simplification of concrete placement work.
[0006]
Here, it is preferable that the above-described sheet-like base material is attached so that fibers are needle punched into the sheet-like material and the fibers are present in a three-dimensional form on both surfaces of the sheet-like material. With this configuration, the fiber exhibits an anchor effect on the polymer cement layer and the FRP layer, and an advantage that the bonding strength of the polymer cement layer and the FRP layer through the base material can be extremely increased is obtained.
[0007]
In the method for producing an FRP concrete anticorrosion panel of the present invention according to claim 3, a polymer cement is applied to one surface of a sheet-like base material and cured to form a polymer cement layer, and then the other side of the base material is formed. FRP plate is superimposed on the surface via an adhesive, the whole is pressed by a press machine, and the base material and the FRP plate are bonded to each other. By this method, the FRP concrete anticorrosion according to the present invention described above is batch-type. Panels can be manufactured.
[0008]
The manufacturing method of the FRP concrete anticorrosion panel of this invention which concerns on Claim 4 applies the polymer cement to one surface of the elongate sheet-like base material beforehand, and was made to harden | cure and formed the polymer cement layer previously. Prepare a laminated material, supply thermosetting resin liquid and reinforcing fiber on the first carrier film while running, impregnate the reinforcing fiber with thermosetting resin liquid, and mix the reinforcing fiber with thermosetting A resin liquid layer is formed, and the above-mentioned previous laminated material is placed on the base material side, and a second carrier film is supplied and sandwiched thereon, and then the thermosetting resin liquid is added. The FRP concrete anticorrosion panel according to the present invention described above can be manufactured continuously by this method, which is characterized by being integrally formed by heat curing.
[0009]
In the above-described continuous production method, before placing the preceding laminated material on the reinforcing fiber mixed thermosetting resin liquid layer on the first carrier film, It is preferable to apply a low shrinkage resin to the surface on the material side. With this configuration, there is an advantage that the thermosetting resin liquid can be prevented from being excessively impregnated in the base material, and shrinkage at the time of heat curing can be suppressed to suppress warpage.
[0010]
DETAILED DESCRIPTION OF THE INVENTION
Embodiments of an FRP concrete anticorrosion panel and a method for manufacturing the same according to the present invention will be described below in detail with reference to the accompanying drawings.
[0011]
FIG. 1 schematically shows an enlarged cross section of an FRP concrete anticorrosion panel 1 according to a basic embodiment of the present invention. The anticorrosion panel 1 includes a sheet-like substrate 2, a polymer cement layer 3 bonded to one surface of the substrate 2, and a fiber reinforced thermoplastic resin layer bonded to the other surface of the substrate 2 ( FRP layer) 4 is a laminated structure. Hereinafter, each layer will be described in detail.
[0012]
Base material 2: The base material 2 is used for supporting the polymer cement layer 3 and bonding it to the FRP layer 4. The base material 2 has a strength necessary for supporting the polymer cement layer 3 and is provided with the polymer cement layer 3 And the thing with the characteristic which can be favorably integrated with the FRP layer 4 is used. The substrate 2 is coated with a liquid polymer cement on one side to form a polymer cement layer 3 and then an FRP layer 4 is formed on the opposite side. When the liquid polymer cement is coated on one side, If the polymer cement penetrates to the surface on the opposite side of the substrate, the bonding strength of the FRP layer may be reduced. Therefore, when the liquid polymer cement is applied to one side of the base material 2, the polymer cement hardly oozes out to the surface on the opposite side of the base material, and the penetration stops at about the center in the thickness direction. It is preferable to have a characteristic. Examples of the substrate 2 include non-woven fabric, spunbond, woven fabric, paper, sheet, film and the like, and in particular, polymer cement and FRP (adhesive when FRP is bonded via an adhesive) enter. A structure having a large number of minute voids is preferable so that a mechanical bond can be obtained. Moreover, these nonwoven fabrics, spunbonds, woven fabrics, papers, sheets, films, and the like are not limited to being used alone, and may be used as the base material 2 in a suitably laminated form. Furthermore, as shown in FIG. 2, the base material 2 is made of a sheet-like material 6 made of nonwoven fabric, spunbond, woven fabric, paper, sheet, film, or the like, and fibers 7 (which may be either short fibers or long fibers). It is also possible to use a non-woven substrate 2A attached by needle punching so that the fibers 7 are present on both sides of the sheet-like material 6. When the base material 2A having this configuration is used, the fibers 7 are present in a three-dimensional form (a form having many minute voids) on both surfaces of the sheet-like material 6, and as shown in FIG. In the case where the anticorrosion panel 1 is prepared using the above, the bonding strength to the polymer cement layer 3 and the FRP layer 4 can be increased. That is, when polymer cement is applied and integrated on one surface of the substrate 2A, the polymer cement enters the space between the fibers 7, in other words, the fiber 7 enters the polymer cement layer 3. Thus, the anchor effect is exhibited and the bonding strength to the polymer cement layer can be increased. In order to form the FRP layer 4 on the other surface of the base material 2A, as will be described later, a method of joining an FRP plate to the base material 2A using an adhesive, or the base material 2A is mixed with reinforced fibers. It is laminated on the curable resin liquid layer, and the thermosetting resin liquid is heated and cured and integrated molding is performed. However, when the FRP plate is bonded using an adhesive, the fibers 7 are present in the adhesive layer. The presence of the adhesive layer increases the adhesive strength of the adhesive layer to the base material 2A, resulting in an increase in the bonding strength of the FRP layer. In the case of integral molding, the fiber 7 is impregnated with the thermosetting resin liquid. Therefore, the fibers 7 are present in the FRP layer, exhibit an anchor effect, and increase the bonding strength to the FRP layer. Moreover, since the fibers 7 present on both sides of the sheet-like material 6 often penetrate the sheet-like material 6, the polymer cement layer 3 and the FRP layer 4 are fixed to the same fiber 7. The fiber 7 is not peeled off from the sheet-like material 6, and the bonding strength of the polymer cement layer 3 and the FRP layer 4 through the base material 2A can be increased also from this point.
[0013]
Examples of materials such as nonwoven fabric, spunbond, and woven fabric used for the base materials 2 and 2A include materials having alkali resistance such as polyester fiber, polyamide fiber, polyethylene fiber, acrylic fiber, and vinyl ester fiber. Polyamide fibers and polyester fibers are preferable from the viewpoints of affinity, strength, durability, cost, and the like for the polymer cement layer and the FRP layer. Also, as materials for the sheet, film, etc. used for the substrates 2 and 2A, resins having alkali resistance such as polyester, polyamide, polyethylene, and acrylic can be exemplified. Examples of the material of the fiber 7 used for the base material 2A include materials having alkali resistance such as polyester fiber, polyamide fiber, polyethylene fiber, acrylic fiber, and vinyl ester fiber, and vinyl ester fiber is particularly preferable. The length and thickness of the fiber 7 may be determined so that it can be attached to the sheet-like material 6 by needle punching and can take a three-dimensional form with appropriate rigidity on both sides. As long as the thickness is about 30 mm or more, either a long fiber or a short fiber may be used, and the thickness is preferably about 10 to 300 denier. The basis weight of the base materials 2 and 2A is determined so as to ensure the required strength and the required bonding strength to the polymer cement layer and the FRP layer. For example, when the base material 2 is formed of a single nonwoven fabric, 80 ~ 200g / m ² The degree is preferable, and when formed with spunbond alone, 20 to 50 g / m ² The degree is preferred. Moreover, in the base material 2A, when the sheet-like material 6 is formed by spunbonding, the basis weight is 20 to 50 g / m. ² The weight of the fiber 7 attached by needle punching is 50 to 200 g / m. ² The degree is preferred.
[0014]
Polymer cement layer 3: This polymer cement layer 3 is provided so as to exhibit good adhesion to concrete, cement, mortar, etc., and is coated with polymer cement on one side of the substrate 2 and dried. It is formed by. Here, the polymer cement applied to the substrate is a mixture of cement and an alkali-resistant polymer solution, and a typical example of the polymer solution is a polyacrylate copolymer emulsion. In addition, an ethylene vinyl acetate copolymer emulsion, an SBR emulsion, or the like may be used. The ratio of cement to polymer in the polymer cement layer 3 is preferably about 0.2 to 0.5 polymer, and most preferably about 0.3, with respect to the cement 1. If the ratio of the cement is too high, it will be difficult to apply due to insufficient fluidity during application, and it will become too hard, making it difficult to wind up the sheet formed by applying polymer cement to the base material. Since the cost increases when the ratio of the polymer is increased, it is preferably determined as described above. In the polymer cement layer 3, an appropriate aggregate or filler, for example, calcium carbonate, silica sand, balloon or the like may be mixed as required. As thickness of the polymer cement layer 3 apply | coated to the single side | surface of the base material 2, about 0.5-3.0 mm is preferable. In applying the polymer cement to the base material 2, viscosity, temperature, etc., so that the polymer cement does not permeate to the back side of the base material 2, and preferably the permeation stops at approximately the center in the thickness direction of the base material. It is preferable to determine the coating conditions. When a polymer cement layer is formed on the surface of the base material 2A having the structure shown in FIG. 2, fibers are formed from the surface of the polymer cement layer 3 formed on one side of the base material 2A as shown in FIG. 5 (b). The thickness of the polymer cement layer 3 and / or the protruding height of the fibers 7 may be determined such that the fibers 7 are exposed, or the fibers 7 may be completely embedded in the polymer cement layer 3. If the fiber 7 is exposed on the surface of the polymer cement layer 3, the fiber can act as an anchor on the concrete bonded to the surface of the polymer cement layer 3, thereby increasing the bonding strength. In manufacturing the anticorrosion panel 1, normally, as shown in FIGS. 5 (a) and 5 (b), a pre-stage laminated material 20 having a structure in which the polymer cement layer 3 is joined to the base materials 2 and 2A is prepared. Then, an FRP layer is formed on the base material side surface of the former laminated material 20. For this reason, it is often possible to manufacture and store the preceding laminated material 20 described above, so that it is preferable to be able to be wound and stored in a roll shape. Therefore, the thickness of the polymer cement layer 3 and the ratio of cement to polymer are selected. In this case, it is preferable that the pre-stage laminated material 20 is selected so as to be soft enough to be wound up in a roll shape.
[0015]
FRP layer 4: This FRP layer 4 is for providing the anticorrosion panel 1 with necessary rigidity, strength, waterproofness, anticorrosion and the like. The thermosetting resin used for the FRP layer 4 is selected in consideration of various conditions such as adhesion to the substrate 2 and rigidity, toughness, moldability, and cost of the resin when cured, but it is inexpensive. Among them, there are unsaturated polyester resin, phenol (or phenol formalin) resin, and urea formalin resin. Examples of other materials include epoxy resins, vinyl ester resins, urethane resins, acrylic urethane resins, and acrylic resins. If necessary, an appropriate filler or colorant may be mixed in the resin. It is also possible to mix a weight-reducing material such as a hollow balloon in order to impart a light weight function to the resin, and in some cases, a flame retardant such as aluminum hydroxide to impart incombustibility. It is. As the reinforcing fibers used for the FRP layer 4, inorganic fibers such as glass fibers, carbon fibers, and aluminum hydroxide fibers, and organic fibers such as vinylon fibers, polyester fibers, and aramid fibers can be used. Large is preferred. Examples of the form of these fibers include woven fabric, non-woven fabric, mat, and braided fabric. The length of the fibers constituting the nonwoven fabric or mat may be either short fibers or long fibers. The form is usually chopped strands (free length), but is not limited thereto. The content of the reinforcing fiber in the FRP layer 4 may be appropriately determined in consideration of necessary strength, productivity, and the like, and is usually determined to be about 25 to 60% by weight. In addition, the thickness of the FRP layer 4 may be determined according to the strength, corrosion resistance, etc. required for the anticorrosion panel. For example, when the anticorrosion panel is used under less severe conditions such as the inner surface of a concrete pipe. When using under severe conditions such as revetment, about 2 to 3 mm, the anti-corrosion panel requires high rigidity, so it is selected to be about 3 to 10 mm to make it hard and difficult to bend. It is preferable.
[0016]
There are two methods for forming the FRP layer 4. One is a method of bonding the FRP plate to the base materials 2 and 2A using an adhesive, and the other is a method of laminating the base materials 2 and 2A on the reinforced fiber mixed thermosetting resin liquid layer, In this method, the thermosetting resin liquid is cured by heating and integrally molded. Among these, in the latter method, since the thermosetting resin liquid is impregnated and integrated into the base materials 2 and 2A, higher bonding strength can be obtained.
[0017]
The shape of the anticorrosion panel 1 is usually flat, but may be appropriately curved according to the place of use. For example, when it is attached to the inner surface of a concrete pipe, it may have a shape that matches the curvature of the inner surface of the concrete pipe.
[0018]
Next, the usage method of the anticorrosion panel 1 of the said structure is demonstrated. When this anticorrosion panel 1 is used as a permanent formwork, the anticorrosion panel 1 is installed as a formwork for placing concrete so that the polymer cement layer 3 is on the concrete side. Pour concrete into and solidify it. Thereby, as shown in FIG. 4, since the anticorrosion panel 1 is joined to the surface of the formed concrete casing 9, the anticorrosion panel 1 is left as it is on the surface of the concrete fence pair 9, and is used as an anticorrosion coating. Here, since the polymer cement layer 3 is excellent in affinity to concrete, the anticorrosion panel 1 is very strongly bonded to the concrete housing 9, and therefore does not peel off over a long period of time. Moreover, since the FRP layer 4 excellent in rigidity, waterproofness, and corrosion resistance is provided on the surface side, it can be used as an anticorrosion coating excellent in rigidity, waterproofness, and corrosion resistance over a long period of time.
[0019]
The anticorrosion panel 1 is not limited to being used as a permanent mold, but can also be used simply as an anticorrosion coating on the concrete surface. In that case, it is only necessary to install a formwork for casting concrete, set the anticorrosion panel 1 in the formwork, and then pour and solidify the concrete, and then remove only the formwork. Also by this, the anticorrosion panel 1 can be firmly joined to the surface of the concrete frame, and the anticorrosion coating can be formed. In addition, when using the anticorrosion panel 1 as a permanent mold, and merely using it as an anticorrosion coating on the concrete surface, the shape of the anticorrosion panel 1 may be a shape corresponding to the surface of the concrete to be formed. When the thickness of the anticorrosion panel 1 is thin and can be easily deformed, it is not always necessary to match the shape of the concrete surface, and it may be simply a flat shape. In attaching this flat anticorrosion panel 1 to a curved surface such as an inner surface of a concrete pipe, by setting the anticorrosion panel to be curved along the curved inner surface of the formwork, and pouring the concrete onto it, The anticorrosion panel 1 can be attached to the curved surface of concrete.
[0020]
Next, the manufacturing method of the FRP concrete anticorrosion panel 1 of the said structure is demonstrated. The manufacturing methods provided in the present application are roughly divided into two methods, namely, a pressure bonding method (production method A) and a continuous molding method (production method B). Each will be described below.
[0021]
(Production method A) Pressure bonding method
This method is a method of forming the FRP layer 4 by pressure-bonding a pre-made FRP plate to a base material using an adhesive.
In carrying out this method, first, a sheet-like base material 2 is prepared, and polymer cement is applied to one surface of the base material 2 and cured to form a polymer cement layer 4, as shown in FIG. As shown, a pre-layered material 20 in which the base material 2 and the polymer cement layer 4 are integrated is created. In addition, when using the base material 2A shown in FIG. 2 as the base material 2, as shown in FIG.5 (b), the front | former layer laminated material 20 which integrated the polymer cement layer 3 with the base material 2A is created. The pre-layered material 20 may have a size substantially equal to the anticorrosion panel 1 to be manufactured, but a method of making a material much longer than that and cutting it to a desired length is used. It is preferable because the working efficiency is good. When the long front laminated material 20 is prepared, it is preferable to wind it in a roll shape because it is easy to handle. In parallel with the preparation of the pre-stage laminated material 20, an FRP plate having a thickness equal to the thickness of the FRP layer 4 to be formed is prepared. The size of the FRP plate is set to be approximately equal to the size of the anticorrosion panel 1 to be manufactured. For example, the width is about 1000 mm and the length is about 1800 to 2000 mm.
[0022]
Next, an adhesive for adhering the FRP plate and the base material 2 is applied to the surface of the FRP plate and / or the surface of the upstream laminate 20 on the base material 2 side. Although any method can be adopted for this application, a method of applying to the FRP plate 25 using the roll coater 21 shown in FIG. The roll coater 21 includes two upper and two lower rollers 23 and 24 that rotate in opposite directions, so that an appropriate clearance can be set between the upper and lower rollers according to the thickness of the FRP plate 25. It has become. In this roll coater 21, an adhesive 26 is set between the two upper rollers 23, so that the adhesive is adhered to the roller surface by the rotation of the roller 23, and the gap between the upper and lower rollers 23, 24 is set. The adhesive 26 can be applied only to the surface of the FRP plate 25 that is fed by the rotation of the roller and that contacts the upper roller 23 side. At this time, the amount of adhesive applied to the surface of the FRP plate 25 can be set to a desired value by adjusting the clearance between the upper rollers 23, and the desired amount of adhesive is evenly applied to the surface of the FRP plate 25. Can be applied. The surface of the FRP plate 25 that passes through the roll coater 21 is preferably preliminarily dusted with acetone or the like. In addition, when the front-stage laminated material 20 having the form shown in FIG. 5B is used and the fibers 7 on the surface of the base material 2A are too bulky, the surface on the base material 2A side of the front-stage laminated material 20 is used. The bulging of the fibers 7 may be suppressed by pressure processing using a press or a pressure roller. If this pressurization processing is performed, the space | gap between the fibers 7 will become small and the impregnation speed | rate to the base-material 2A surface of an adhesive agent can be made quick.
[0023]
The adhesive used here may be selected based on the appropriateness of coating between the base material 2 and the FRP plate 25 and the workability, and preferable examples include urethane resin, rubber, and epoxy resin. It does not ask | require solvent type, emulsion type, aqueous type, or solventless type. The coating amount is not particularly limited, but is usually 150 to 450 g / m with respect to the substrate 2 or the FRP plate 25 or per interface. ² The coating amount of is preferable.
[0024]
Next, as shown in FIG. 6 (b), the pre-layer laminate 20 is laminated and adhered to the application surface of the adhesive 26 of the FRP plate 25 with the surface on the base material 2 side facing. At this time, it is desirable that the FRP plate 25 and the previous laminated material 20 are slowly stacked from either one end side so as not to shift. In this way, as shown in FIG. 6C, a laminated body 28 in which the pre-stage laminating agent 20 and the FRP plate 25 are laminated is formed. Next, the laminated body 28 is arranged in a state of being stacked in the press machine 30 shown in FIG. 6D, and a pressure 31 is applied by the press machine 30 until the adhesive 26 works completely, and the whole laminated body 28 is It compresses for sufficient time, and adhere | attaches the FRP board 25 and the base material 2 of the front | former layer lamination agent 20 reliably. Thereby, the anticorrosion panel 1 shown in FIG. 1 is formed. The pressure of the press machine 30 at this time is 0.5 to 3.0 kgf / cm. ² The degree is desirable, but may be changed as appropriate. The pressing time is suitably 8 to 24 hours. The press time is not limited as it depends on environmental factors such as the season. The number of panels that can be compressed at one time by one press may be determined in consideration of productivity, the number of laminates 28 that can be prepared before the adhesive starts to work, and is preferably about 20 to 40. . After completion of the compression, the laminated body 28 is taken out from the press machine 30 and it is confirmed whether or not it is sufficiently adhered. As described above, the FRP plate 25 is firmly bonded and integrated with the base material 2, and the FRP layer 4 (see FIG. 1) of the anticorrosion panel 1 is formed. As shown in FIG. Such an anticorrosion panel 1 is obtained. Thereafter, if necessary, the end four sides of the anticorrosion panel 1 are processed into the final product size by cutting precisely to a preset size, usually 900 mm × 1800 mm, with a cutting machine (not shown). There is also. Moreover, if the size of the anticorrosion panel 1 to be molded is about 900 mm × 1800 mm, the panel can be transferred to a separately installed turnbuckle and compressed to improve the number of press processes. In addition, although the flat anticorrosion panel 1 is manufactured in embodiment of drawing, the anticorrosion panel of a curved shape can be manufactured by making the surface which supports the laminated body 28 of a press machine into the curved shape. it can.
[0025]
(Production method B) Continuous molding method
This method is a method in which a reinforcing fiber mixed thermosetting resin liquid layer is superimposed on a base material, and the thermosetting resin is continuously cured to perform integral molding.
Also in this method, a long front laminated material 20 (see FIG. 5) having a structure in which the polymer cement layer 3 is integrated with the base material 2 is prepared in advance, and wound into a roll shape to form a front laminated material roll. In the following embodiment, the base material 2A having the form shown in FIG. 2 is used as the base material 2, and therefore, the pre-layered material 20 having the structure shown in FIG. 5B is used.
[0026]
As shown in FIG. 7, the first carrier film 34 is pulled out from the carrier film roll 34 </ b> A and travels along a predetermined travel route. For the carrier film 34 and the second carrier film 35 described later, long films such as PET, nylon and PVA are usually used, but are not limited thereto. A constant amount of liquid uncured thermosetting resin 39 is continuously supplied from the resin tank 38 onto the traveling first carrier film 34, and the thickness of the resin 39 on the carrier film 34 is fixed with a doctor knife 40. Adjust to. Next, the reinforcing fiber 42 is continuously supplied onto the resin 39 on the carrier film 34 by the conveyor 43. Examples of the form of the reinforcing fiber 42 used here include a woven fabric, a nonwoven fabric, a mat, and a braided fabric. Moreover, when using a nonwoven fabric, a mat | matte, etc., the length of the fiber which comprises it may be either a short fiber or a long fiber. When using a mat, continuous reinforcing fibers such as rovings are cut into a predetermined length to form reinforcing fibers in the form of short fibers (chopped strands), and the chopped strands on a conveyor or the like running at a constant speed The chopped strand mat having a constant thickness may be formed by supplying the chopped strand mat to the carrier film 34 as the reinforcing fibers 42. In this way, by continuously supplying the reinforcing fibers 42 onto the uncured thermosetting resin 39 on the carrier film 34, the reinforcing fibers 42 are impregnated with the thermosetting resin 39, and the carrier film 34. An uncured reinforcing fiber mixed thermosetting resin liquid layer 39A is formed thereon. If necessary, an appropriate impregnation roller is provided to ensure that the reinforcing fibers in the reinforcing fiber mixed thermosetting resin liquid layer 39A are impregnated with the resin liquid, or a thermosetting resin liquid is newly supplied. You may make changes.
[0027]
On the other hand, the pre-stage laminate material 20 is drawn out from the pre-stage laminate material roll (not shown) prepared in advance with the base material 2 (see FIG. 5) side down, and on the base material surface of the pre-stage laminate material 20, After applying a low-shrinkage resin liquid (details will be described later) with a resin liquid application roller 45, the pre-layer laminate 20 is placed on the reinforcing fiber-mixed thermosetting resin liquid layer 39A on the carrier film 34, and the substrate side is It is placed in a state of being directed and pressed by the impregnation roller 46. Next, the second carrier film 35 pulled out from the carrier film roll 35A is placed on the former laminated material 20 placed on the reinforcing fiber mixed thermosetting resin liquid layer 39A, and the upper and lower carrier films 34, 35 and The sandwiched reinforcing fiber mixed thermosetting resin liquid layer 39A and the pre-layered laminate 20 are fed between the upper and lower squeeze rollers 48 and pressed to defoam the uncured reinforcing fiber mixed thermosetting resin liquid layer. Is adjusted to a desired value (for example, usually 2 to 10 mm, although depending on the application). Next, the laminated body of the reinforcing fiber mixed thermosetting resin liquid layer 39A and the pre-stage laminated material 20 is usually fed into a curing furnace 50 heated to 80 to 150 ° C. and allowed to pass for a sufficient time for curing. The thermosetting resin is cured. As a result, the reinforced fiber mixed thermosetting resin liquid layer 39A is cured to become the FRP layer 4 (see FIG. 1), and is joined to the pre-stage laminated material 20, and a completely integrated laminated body is continuously formed. go. Thereafter, the first and second carrier films 34 and 35 adhering to both surfaces of the laminate are peeled off and wound on rolls 34B and 35B, and then the laminate is cut into arbitrary dimensions by a cutter 52. Thereby, the FRP concrete anticorrosion panel 1 is formed. The line speed in the above molding process is not particularly limited, but is 0.1 to 10 m / min, preferably 0.8 to 5 m / min. As described above, the FRP concrete anticorrosion panel 1 having a desired length can be manufactured at a low cost by the continuous molding method.
[0028]
In the continuous molding method described above, a low-shrinkage resin liquid is applied to the surface of the base material of the former laminated material 20. This is due to the following reason. That is, in this embodiment, the base material 2A used for the pre-stage laminated material 20 is a non-woven fabric with a lot of voids having a large amount of fibers 7 attached by needle punching. Is placed on the uncured reinforcing fiber mixed thermosetting resin liquid layer 39A, the thermosetting resin liquid may be excessively impregnated. May occur. Therefore, in order to prevent this, a low shrinkage resin liquid is applied to the surface of the base material of the previous laminated material 20 to suppress impregnation of the thermosetting resin liquid, and to suppress the occurrence of warpage by suppressing heat shrinkage. It is preventing. Examples of the low shrinkage resin used here include WPC-402A and WPC-402B manufactured by Hitachi Chemical Co., Ltd.
[0029]
Further, in carrying out the above-described continuous forming method, the base material surface of the front-stage laminated material 20 is applied to the surface of the base material of the front-stage laminated material 20 upstream of the resin liquid application roller 45 that applies a low-shrinkage resin liquid to the surface of the base material of the front-stage laminated material 20. It is also recommended to reduce the amount of swelling of the fiber 7 [see FIG. When this pressure processing is performed, the gap between the fibers 7 is reduced, the impregnation rate of the thermosetting resin liquid into the base material 2A is increased, and the adsorption rate of the resin liquid quickly reaches the saturation point. Benefits are gained.
[0030]
In the anticorrosion panel 1 manufactured by the above continuous molding method, the reinforcing fiber mixed thermosetting resin liquid permeates and diffuses into the base material 2A and cures in a form in which the base material 2A is shared. Since 4 is firmly integrated, a corrosion-resistant panel having high rigidity can be obtained.
[0031]
【Example】
Example 1
(1) Preparation of the former laminated material 20
Spunbond made of polyester fiber (weight per unit area 30g / m ² ) Vinylon fiber (thickness 100 denier, basis weight 200g / m) ² ) Was attached by needle punching to prepare a base material 2A having the form shown in FIG. Next, a mixture of cement and polyacrylate copolymer emulsion (solid content ratio 1: 0.5) was applied to one side of the substrate 2A to a thickness of about 1 mm, dried and cured. A pre-stage laminated material 20 having the form shown in FIG.
(2) FRP board
A glass fiber reinforced polyester resin plate (manufactured by Nitto Boseki Co., Ltd.) having a thickness of 2 mm was prepared as the FRP plate.
(3) Pressure bonding operation
An adhesive (KU-850, manufactured by Konishi Co., Ltd.) is applied to the surface of the FRP plate by a roll coater 21 shown in FIG. ² The laminated body 28 was formed by superimposing the previous laminated material 20 thereon. Next, this laminate 28 is set in a press machine, and 1.0 kgf / cm. ² The pressure was maintained for 16 hours. Then, it took out from the press machine and obtained the anticorrosion panel 1.
(4) Results
In the obtained anticorrosion panel 1, the polymer cement layer 3 and the FRP layer 4 were securely bonded to both surfaces of the base material 2A and were flat without warping. When concrete was placed on the polymer cement layer side of the anticorrosion panel 1, the anticorrosion panel 1 was securely bonded to the concrete surface. Further, when the peel strength against concrete was measured, it was 20 kgf / cm. ² There was also a very large value.
[0032]
Example 2
(1) Preparation of the former laminated material 20
Spunbond made of polyester fiber (weight per unit area 30g / m ² ) Vinylon fiber (thickness 100 denier, basis weight 200g / m) ² ) Was attached by needle punching to prepare a base material 2A having the form shown in FIG. Next, a mixture of cement and polyacrylate copolymer emulsion (solid content ratio 1: 0.5) was applied to one side of the substrate 2A to a thickness of about 1 mm, dried and cured. The former laminated material 20 of the form shown in FIG.5 (b) was created.
(2) Continuous molding operation
In the continuous molding line shown in FIG. 7, an uncured unsaturated polyester resin liquid (on a first carrier film 34 made of polyethylene terephthalate running at a line speed of 0.85 m / min (Unitika Ltd., thickness 25 μm)) ( Dainippon Ink Industries Co., Ltd.) and glass fiber (manufactured by Nitto Boseki Co., Ltd., glass fiber mat with an average diameter of 0.02 mm and an average length of 50 mm) are supplied, and a glass fiber mixed unsaturated polyester resin liquid layer 39A (thickness) About 2 to 3 mm). Next, after the low-shrinkage resin liquid (mixed liquid of WPC-402A and WPC-402B, manufactured by Hitachi Chemical Co., Ltd.) is applied to the substrate side surface of the pre-layered laminate 20 by the resin liquid application roller 45, the pre-stage The laminated material 20 was overlaid on the glass fiber mixed unsaturated polyester resin liquid layer 39A on the first carrier film 34, and a second carrier film 35 (manufactured by Unitika Ltd., thickness 25 μm) was further placed thereon. Thereafter, the glass fiber mixed unsaturated polyester resin liquid layer 39A is degassed by adjusting the thickness to about 5 mm and then set to 150 ° C. The unsaturated polyester resin liquid 39A was heated and cured by feeding into the curing furnace 50 and running in the furnace for 30 minutes to obtain an integrated laminate. The first and second carrier films 34 and 35 are peeled off from the laminate that has traveled and emerged from the curing furnace 50 and wound, and the laminate is cut into a length of about 1.8 m by a cutter. A 1800 mm anti-corrosion panel 1 was obtained.
(3) Results
The obtained anticorrosion panel 1 had an overall thickness of about 5 mm, and the FRP layer 4 had a thickness of about 2 mm. In addition, the polymer cement layer 3 and the FRP layer 4 were securely bonded to both surfaces of the base material 2A and were flat without warping. When concrete was placed on the polymer cement layer side of the anticorrosion panel 1, the anticorrosion panel 1 was securely bonded to the concrete surface. Moreover, when the peel strength against concrete was measured, 21 kgf / cm ² There was also a very large value.
[0033]
【The invention's effect】
As described above, the FRP concrete anticorrosion panel of the present invention has a laminated structure in which a polymer cement layer and an FRP layer are integrated via a sheet-like base material. In addition, the FRP layer has light weight, large rigidity, excellent waterproofing, corrosion resistance, etc., and can be attached to the concrete surface with a large bonding force. It can exhibit excellent waterproofing and anticorrosion effects over a long period of time, and it has various effects such as light weight, good workability, and high rigidity that can be used as a permanent mold. ing. Moreover, since the material used for manufacture of the anticorrosion panel of the present invention is not particularly expensive, it has an effect that it can be manufactured at low cost.
[0034]
In the first production method of the present invention, a sheet-like base material is prepared, and polymer cement is applied to one surface of the base material and cured to form a polymer cement layer. Since the FRP plate is superposed on the other surface via an adhesive and the whole is pressed and bonded, the batch-type FRP concrete anticorrosion panel of the present invention can be manufactured, and the pressing surface of the press It has the effect that the anticorrosion panel of a curved shape can also be manufactured by curving so that the shape of may become a desired shape.
[0035]
In the second production method of the present invention, a long pre-layer laminate material in which a polymer cement layer is formed by applying polymer cement on one surface of a long sheet-like base material and curing it is prepared in advance. The reinforcing fiber and the thermosetting resin liquid are supplied on the first traveling carrier film to form a reinforcing fiber mixed thermosetting resin liquid layer, and the above-mentioned laminated material is disposed on the substrate side. , And the second carrier film is supplied and sandwiched between them, and the thermosetting resin liquid is then heat-cured and integrally molded. It has the effect that the FRP concrete anticorrosion panel of this invention mentioned above can be manufactured at cost.
[Brief description of the drawings]
FIG. 1 is a schematic cross-sectional view of an FRP concrete anticorrosion panel according to an embodiment of the present invention.
FIG. 2 is a schematic cross-sectional view showing an example of a base material used in the anticorrosion panel of FIG.
3 is a schematic cross-sectional view of an anticorrosion panel formed using the base material of FIG.
4 is a schematic cross-sectional view showing a state in which the anticorrosion panel of FIG. 1 is joined to a concrete surface.
FIG. 5A is a schematic cross-sectional view of a previous-stage laminated material that is a laminate of a base material and a polymer cement layer.
(B) Schematic cross-sectional view of the former laminated material formed using the base material shown in FIG.
FIGS. 6 (a), (b), (c), (d), and (e) are schematic views for explaining a process for manufacturing a corrosion-proof panel by a pressure bonding method.
FIG. 7 is a schematic diagram showing a process for producing a corrosion-proof panel by a continuous molding method.
[Explanation of symbols]
1 FRP concrete anticorrosion panel
2, 2A base material
3 Polymer cement layer
4 FRP layer
6 Sheet material
7 Fiber
9 Concrete frame
20 Pre-laminated material
21 Roll coater
23, 24 Roller
25 FRP board
26 Adhesive
30 Press machine
34 First carrier film
35 Second carrier film
39 Thermosetting resin liquid
39A Reinforced fiber mixed thermosetting resin liquid layer
42 Reinforcing fiber
45 Resin liquid application roller
46 Impregnation roller
48 Squeeze Roller
50 Curing furnace
52 cutter

Claims

An FRP concrete anticorrosion panel comprising a sheet-like substrate, a polymer cement layer bonded to one surface of the substrate, and an FRP layer bonded to the other surface of the substrate.

2. The FRP concrete anticorrosion panel according to claim 1, wherein the base material is a non-woven fabric attached by needle punching a fiber into a sheet-like material so as to be present on both sides of the sheet-like material.

A polymer cement is applied to one side of a sheet-like base material and cured to form a polymer cement layer, and then an FRP plate is superimposed on the other side of the base material via an adhesive, and the whole is pressed. A method for producing an FRP concrete anticorrosion panel, characterized in that the substrate and the FRP plate are bonded together under pressure.

Prepare a long pre-layered material that has been coated with polymer cement on one side of a long sheet-like base material and cured to form a polymer cement layer. In addition, the thermosetting resin liquid and the reinforcing fiber are supplied, and the reinforcing fiber is impregnated with the thermosetting resin liquid to form a reinforcing fiber mixed thermosetting resin liquid layer, and the above-mentioned previous-stage laminated material is formed thereon, FRP concrete anticorrosion panel, which is placed with the base material side facing, and a second carrier film is supplied and sandwiched thereon, and then the thermosetting resin liquid is heat-cured and integrally molded. Manufacturing method.

Before placing the pre-stage laminate on the reinforcing fiber-containing thermosetting resin liquid layer on the first carrier film, apply a low-shrinkage resin to the substrate-side surface of the pre-stage laminate. The manufacturing method of the FRP concrete anticorrosion panel of Claim 4 characterized by the above-mentioned.