JP2004315426A - Additive for cosmetic - Google Patents

Additive for cosmetic Download PDF

Info

Publication number
JP2004315426A
JP2004315426A JP2003111196A JP2003111196A JP2004315426A JP 2004315426 A JP2004315426 A JP 2004315426A JP 2003111196 A JP2003111196 A JP 2003111196A JP 2003111196 A JP2003111196 A JP 2003111196A JP 2004315426 A JP2004315426 A JP 2004315426A
Authority
JP
Japan
Prior art keywords
skin
additive
color
cosmetic
titanium oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2003111196A
Other languages
Japanese (ja)
Other versions
JP4438310B2 (en
Inventor
Tatsuya Goto
Toshiyuki Kani
俊之 可児
後藤  達也
Original Assignee
L'oreal Sa
ロレアルLoreal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by L'oreal Sa, ロレアルLoreal filed Critical L'oreal Sa
Priority to JP2003111196A priority Critical patent/JP4438310B2/en
Publication of JP2004315426A publication Critical patent/JP2004315426A/en
Application granted granted Critical
Publication of JP4438310B2 publication Critical patent/JP4438310B2/en
Application status is Expired - Fee Related legal-status Critical
Anticipated expiration legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To prepare a cosmetic enabling healthy natural skin originally possessed by everyone and having no dullness to be taken back, i.e. enabling the beautiful skin having own color to be taken back.
SOLUTION: An additive for the cosmetic for forming skin into the beautiful skin having the own color is obtained by covering the surface of a titanium oxide-covered mica with a red organic coloring matter. The additive exhibits a spectral reflection factor curve in the same shape as that of the undamaged original skin. A cosmetic composition containing the additive and a makeup method using the cosmetic composition are also provided.
COPYRIGHT: (C)2005,JPO&NCIPI

Description

【0001】 [0001]
【発明の属する技術分野】 BACKGROUND OF THE INVENTION
本発明は化粧品用添加剤、特にファンデーション等のメークアップ化粧品に配合することにより各人が本来有していた、くすみのない自然で健康的な肌色(「自分色のきれい肌」)を取り戻すことのできる化粧品用添加剤に関する。 The present invention is to regain cosmetic additives, had each person originally by blending in particular make-up cosmetics such as foundation, a natural and healthy skin color without dullness ( "my color of beautiful skin") on cosmetic additives that can. また本発明は、当該添加剤を含有する化粧品組成物及びそれを用いた化粧方法にも関する。 The invention also relates to a cosmetic process for cosmetic compositions and using the same containing the additive.
【0002】 [0002]
【従来の技術】 BACKGROUND OF THE INVENTION
従来のメークアップ化粧品、特にファンデーション類は、シミ、ソバカス等の欠点をカバーして、素肌の上に素肌とは別の理想の肌色を創出することを目的としていた。 Traditional make-up cosmetics, especially foundation class is, stains, cover the shortcomings such as freckles, the skin on top of the skin had been intended to create the skin color of another ideal. そこで、従来のファンデーション類は、欠点のカバー力(隠蔽力)を向上させるため、例えば酸化チタンや酸化鉄等の着色顔料といった隠蔽力の大きな成分が配合されていた。 Therefore, conventional foundations such, in order to improve covering power deficiencies (the hiding power), for example, a large component of hiding power such coloring pigments such as titanium oxide or iron oxide has been incorporated. しかしながら、これら従来のファンデーション類を塗布することにより肌のくすみ等の欠点を隠蔽することはできるが、全体に白く粉っぽい不自然な感じとなる場合が多かった。 However, although it is possible to hide the shortcomings of such dullness of the skin by applying these conventional foundations such, in many cases to be a white chalky unnatural feeling to the whole.
【0003】 [0003]
人間の皮膚は、本来の無垢な状態では透明感のある自然で健康的な肌色をしており、その分光反射率を測定すると、約450〜550nmの波長領域(領域I)に上に凸のブロードなピーク、約500〜620nmの波長領域(領域II)に下に凸のピークを有し、約600〜700nmの波長領域(領域III)において漸増する基本的に右上がりの曲線を示すことが知られている(図1(A)参照)。 Human skin is a natural and healthy skin color in the original solid state a sense of transparency, when measuring the spectral reflectance of the upper convexly wavelength region of about 450 to 550 nm (region I) broad peak, has a convex peak below into a wavelength region of about 500~620Nm (region II), to exhibit essentially upward sloping curve gradually increasing in the wavelength region of about 600 to 700 nm (region III) known (see FIG. 1 (A)). ところが、紫外線等を含む様々なダメージを受けることによりくすんだ肌となると、その肌の分光反射率は全体的に低下するとともに前記波長領域の凹凸が縮小して平坦になる傾向があることも知られている(図1(B)参照)。 Knowledge, however, when it comes to the skin dull by receiving various damage including ultraviolet rays, also unevenness of the wavelength region that tends to be flattened by reducing with spectral reflectance of the skin entirely decreased are (see FIG. 1 (B)).
【0004】 [0004]
特許文献1には、前記領域IIにおける分光反射曲線の窪みの変化に着目し、赤色色材と黄色色材とを特定割合で配合することにより曲線の窪みを復活させ、自然で健康的な化粧肌を得るファンデーションが記載されている。 Patent Document 1 focuses on changes in the recess in the spectral reflection curve in the region II, revived depressions curve by blending a red colorant and yellow colorant in a specific ratio, a natural healthy cosmetic foundation to obtain the skin have been described. このファンデーションは、前記波長領域に曲線の窪みを形成させることには成功しているが、複数の着色顔料の組合せによる減法混色に基づく色相補正であるため、透明感や明るさ或いは自然な仕上がりといった点で本来の素肌には及ばない。 This foundation, said although it to form a depression of the curve in the wavelength region have been successful, because it is the hue correction based on subtractive color mixing by multiple combinations of colored pigment, such as transparency or brightness, or natural finish It falls short of the original skin at the point.
【0005】 [0005]
同様に分光反射曲線に着目した他の技術として、特許文献2には、酸化チタン、微粒子酸化チタン、顔料粉末、酸化チタン類及び顔料以外の球状粉末を特定量含有せしめたファンデーションが記載されており、それを塗布することにより、400〜700nmの波長領域全体における反射率が塗布しない場合より向上したとされている。 As well as the spectral reflection curve was another focus techniques, Patent Document 2, titanium oxide, fine particles of titanium oxide, pigment powder, describes a foundation was allowed specific amount of spherical powder other than titanium oxides and pigments , by applying it, reflectance in the entire wavelength region of 400~700nm is to have improved compared with the case of not applying.
しかしながら、特許文献2の図1及び図2に記載されているように、そのファンデーションを塗布していない素肌の分光反射曲線においても約500〜600nmの波長領域に窪みが形成されていることから、下地となる素肌がダメージを受けていないものと推測される。 However, since the depression in the wavelength region of about 500~600nm are formed also in the spectral reflectance curve of the skin, as described, not applied in the foundation 1 and 2 of Patent Document 2, skin to be a base is assumed that not damaged. 即ち、このファンデーションは、配合する酸化チタンや酸化鉄等の着色顔料の配合量を制限することによって下地となる素肌の反射率を活かして可視光領域での反射率全体を向上させただけであり、分光反射率曲線の窪みを喪失したダメージ肌を改善するには至っていない。 In other words, the foundation is only improved the overall reflectance in the visible light region by utilizing the reflectance of the skin to be a base by limiting the amount of coloring pigments such as titanium oxide or iron oxide to be blended , it has yet to improve the damage skin that has lost a recess of the spectral reflectance curve.
【0006】 [0006]
一方、特許文献3には、シミ、ソバカス等の皮膚トラブルによって生じた肌の濃色部分を目立たなくするため、当該部分の肌の色に対して補色(近傍)の色域を透過光として有する干渉光物質(雲母チタン)を配合した肌色調整用組成物が記載されている。 On the other hand, Patent Document 3 has, stains, for inconspicuous dark portion of the skin caused by skin troubles such as freckles, the color gamut of the complementary (near) as transmitted light to the color of the skin of the partial skin color adjustment compositions containing interference light material (mica titanium) is described. この組成物によれば、肌をくすませることなく皮膚の色調トラブルを改善することが可能であると記載されている。 According to this composition is described that it is possible to improve the color tone skin problems without saddened skin.
【0007】 [0007]
しかしながら、雲母チタンの透過光の色域は、雲母を被覆する酸化チタンの膜厚で決まり、赤色濃色部分の調製用組成物には黄〜赤色透過性(青〜緑色干渉色)の雲母チタンを配合し、青色濃色部分の調製用組成物には青〜緑色透過性(黄〜赤干渉色)の雲母チタンを配合する必要がある。 However, the color gamut of the light transmitted through the mica titanium is determined by the thickness of the titanium oxide coating mica, mica titanium red in preparing compositions of the dark portion yellow to red transparent (blue to green interference color) blended, the composition for preparing a blue dark portion has to be blended mica titanium blue to green permeability (yellow-red interference color). 即ち、赤色及び青色の濃色部分が混在する皮膚トラブルを改善するためには少なくとも2種類の組成物を別々に適用することが必要である。 That is, in order to improve skin troubles red and dark portion of the blue mixed, it is necessary to apply separately at least two compositions. ところが、後述の比較例4に示すように、異なる干渉色を有する複数の干渉光物質(雲母チタン)を混合した場合、加法混色に従って分光反射曲線が全波長領域に渡って平坦となり、全体の色調は白色に近づいてしまうため、特許文献3の教示に基づいて分光反射率曲線に凹凸を持った本来の自然な肌色を得ることは不可能である(図6参照)。 However, as shown in Comparative Example 4 described later, a plurality of different interference light material having an interference color when mixed with (mica titanium), a spectral reflection curve according additive mixture becomes flat over the entire wavelength region, the whole color tone since become close to white, it is impossible to obtain the original natural skin color having an uneven spectral reflectance curve based on the teachings of patent document 3 (see FIG. 6).
【0008】 [0008]
特許文献4にも、透明性の高い自然な仕上がりが得られるファンデーションとして干渉光物質を含有したものが記載されている。 In Patent Document 4 has described a containing the interference light material as foundation high natural finish transparency is obtained. 特許文献4で使用される干渉光物質は、雲母又は雲母の表面を少なくとも酸化チタン及び又は酸化鉄で被覆した粉体である。 Interference light materials used in Patent Document 4 is a powder coated with at least titanium oxide and or iron oxide the surface of mica or mica. 特許文献4では、これらの干渉光物質に起因するぎらつき感を抑制すると同時に肌表面の凹凸トラブルを解消するために、鉄含有酸化チタンと球状樹脂粉末とを含有することを必須としている。 In Patent Document 4, in order to eliminate the irregularities trouble when suppressing glare due to these interference light material simultaneously skin surface, it is essential and that it contains the iron-containing titanium oxide and spherical resin powder. その結果、赤色及び/又は黄色干渉系の雲母チタンを配合した場合に肌色補正効果に優れたファンデーションが得られたと記載されている。 As a result, the foundation having an excellent skin color correction effect when incorporated mica titanium in the red and / or yellow interference system is described as obtained.
しかしながら、特許文献4における「肌色補正効果」は、特許文献3に記載された「肌色調整」と同様に、色むら、シミ等の色調トラブルをカバーする効果であり(段落0056参照)、所定波長領域に凹凸を持った分光反射率曲線を示す化粧肌を得ることとは根本的に相違している。 However, "skin color correction effect" in Patent Document 4, as the "skin color adjustment" described in Patent Document 3 is effective to cover irregular color, the color tone troubles such as stain (see paragraph 0056), the predetermined wavelength It is different fundamentally from obtaining a cosmetic skin showing the spectral reflectance curve having an uneven area.
【0009】 [0009]
肌の色は本来各人様々であり、同一人においても部位によって色が異なるのが自然である。 The color of the skin is inherently each person different, it is different from the natural color by the site is also in the same person. 近年の個性志向及びナチュラル志向の風潮と相俟って、自然で個性的な肌、言い換えれば各自が本来有していたダメージを受けていない肌を取り戻すことのできる化粧品が求められている。 What climate coupled with the recent years of the personality-oriented and natural-oriented, are natural and unique skin, cosmetics that each person can regain the skin that is not damaged, which had originally in other words sought. 本発明者等は、このようなダメージを受けていない肌を「自分色のきれい肌(personal beautiful skin)」と命名した。 The present inventors have, was named the skin that have not undergone such damage as "their own color of beautiful skin (personal beautiful skin)". 「自分色のきれい肌」とは、下記で定義するように、図1(A)に示す分光反射率を示す肌であり、このような肌を得ることのできる化粧品は未だ得られていない。 The "my color clean peel", as defined below, a skin showing the spectral reflectance shown in FIG. 1 (A), cosmetics have not been obtained yet capable of obtaining such a skin.
【0010】 [0010]
【特許文献1】特開平10−17437号公報【特許文献2】特開平10−7525号公報【特許文献3】特開平8−81334号公報【特許文献4】特開2002−241212号公報【0011】 [Patent Document 1] JP-A-10-17437 [Patent Document 2] JP-A-10-7525 [Patent Document 3] JP-A-8-81334 [Patent Document 4] JP 2002-241212 JP [0011 ]
【発明が解決しようとする課題】 [Problems that the Invention is to Solve
よって本発明における課題は、「自分色のきれい肌」、即ち、各自が本来有していたダメージを受けていない美しい肌を取り戻すことのできる化粧品を提供することにある。 Therefore, problems in the present invention, "his color of beautiful skin", that is, it is to provide a cosmetic that can regain the beautiful skin that is not damaged that each had originally.
【0012】 [0012]
【課題を解決するための手段】 In order to solve the problems]
本発明者らは、図1(A)及び(B)に示すような肌の分光反射率曲線の変化に着目して鋭意研究を続けた結果、酸化チタン被覆雲母(雲母チタン)に赤色有機色素を被覆した物質が、図1(A)と極めて類似する分光反射率曲線の波形を示すことを見出し、本発明をなすに至った。 The present inventors have, FIGS. 1 (A) and 1 results continued extensive studies by paying attention to the change of the spectral reflectance curves of the skin, such as (B), the red organic pigment titanium oxide-coated mica (mica titanium) materials coated with is found to exhibit a waveform of the spectral reflectance curve very similar to FIG. 1 (a), the the present invention has been accomplished.
即ち、上記の課題は、酸化チタン被覆雲母を赤色有機色素でさらに被覆してなることを特徴とする化粧品用添加剤を使用することによって解決することができる。 That is, the above problem can be solved by using a cosmetic additive characterized by comprising further coating the titanium oxide-coated mica with a red organic dye.
【0013】 [0013]
図1(B)に示すように凹凸を無くした平坦な分光反射率曲線を示すダメージ肌に本発明の添加剤を含有する化粧料を塗布することにより、その分光反射曲線を、図1(A)における領域I、II及びIIIにおいて特徴的な凹凸を有する形状とするとともに曲線全体を上昇させ、本来の素肌が示す分光反射率曲線に近づけることができる。 By applying a cosmetic composition comprising the additive of the present invention to damage skin showing a flat spectral reflectance curve eliminating uneven as shown in FIG. 1 (B), the spectral reflectance curve, FIG. 1 (A region I in) to raise the entire curve with a shape having characteristic irregularities in the II and III, can be brought close to the spectral reflectance curve shown is the original skin. その結果、得られた化粧肌は、透明感を有し、くすみがなく、しかも明るく自然な仕上がりとなる。 As a result, the resulting cosmetic skin, has a sense of transparency, there is no dull, yet the bright natural finish.
さらに、前記のような化粧効果を、複数の着色剤等を混合するのではなく、本発明に係る一つの添加剤のみで達成することができることは驚くべきことである。 Furthermore, the cosmetic effect as described above, instead of mixing a plurality of coloring agent, it is surprising that can be achieved with only one additive of the present invention.
【0014】 [0014]
【発明の実施の形態】 DETAILED DESCRIPTION OF THE INVENTION
本発明における「自分色のきれい肌」とは、紫外線等によるダメージを受けていない無垢な肌、即ち、図1(A)に示すような分光反射率を有する肌の色を意味する。 The "own color beautiful skin" in the present invention, solid skin that is not damaged by ultraviolet rays or the like, ie, a skin color having spectral reflectance as shown in FIG. 1 (A).
図1(A)に見られるように、「自分色のきれい肌」の分光反射率曲線は、約450〜550nmの波長領域(領域I)に上に凸のブロードなピーク、約500〜620nmの波長領域(領域II)に下に凸のピークを有し、約600〜700nmの波長領域(領域III)において漸増する基本的に右上がりの形状を有している。 As seen in FIG. 1 (A), the spectral reflectance curve of the "own color beautiful skin" is about on the convex broad peak in the wavelength region (region I) of 450 to 550 nm, about 500~620nm has a peak downward convex in a wavelength region (region II), it has an essentially upward sloping shape gradually increasing in the wavelength region of about 600 to 700 nm (region III). これに対してダメージを受けてくすんだ色の肌は、図1(B)に示される分光反射率を有し、(A)に比較して前記の凹凸が縮小して平坦化するとともに反射率が全体的に低下している。 The skin color dull damaged hand, has a spectral reflectance as shown in FIG. 1 (B), the reflectance as to flatten shrinking said irregularities compared to (A) There has been an overall decline.
よって、本発明において「自分色のきれい肌とする」とは、ダメージ等を受けて図1(B)に示すような平坦な分光反射率を有するに至ったダメージ肌又はそれに類似する肌を、前記の「自分色のきれい肌」とすることを意味する。 Thus, the term "the own color of beautiful skin" in the present invention, damage the skin or skin similar to that leading to having a flat spectral reflectance as shown in FIG. 1 (B) are damaged or the like, means that as "their own color of beautiful skin" of the.
【0015】 [0015]
本発明に係る化粧品用添加剤は、酸化チタン被覆雲母を赤色有機色素でさらに被覆してなり、これをファンデーション等の化粧品に配合することにより、当該化粧品を塗布した皮膚は、図1(A)に示すような分光反射率を有する「自分色のきれい肌」となる。 Cosmetic additive of the present invention is made by further coating the titanium oxide-coated mica with a red organic pigment, by incorporating this into cosmetic foundation or the like, the skin coated the cosmetics, FIG 1 (A) It becomes "his own color of beautiful skin", which has the spectral reflectance, such as shown in FIG.
【0016】 [0016]
本発明の添加剤を構成する赤色有機色素は、一般に赤色に分類される有機合成色素及び天然色素を含むが、赤酸化鉄(ベンガラ)等の無機顔料は含まない。 Red organic dye constituting the additive of the present invention generally includes an organic synthetic dyes and natural dyes are classified into red, it does not include inorganic pigments such as red iron oxide (red iron oxide). 有機合成色素としては、例えば、赤色505号等のアゾ系染料、赤色230号、赤色233号等のキサンテン系染料を含む染料、赤色202号等のレーキ、及び赤色228号等の有機顔料が挙げられる。 The organic synthetic dyes include for example, azo dyes such as Red No. 505, 230 Red No., dyes containing xanthene dyes such as Red No. 233, lakes such as Red No. 202, and organic pigments Red No. 228, etc. It is. 天然色素としては、例えば、カルサミン等のカロチノイド系色素、アントシアニジン系やカルコン系を含むフラボノイド系色素、アントラキノン系及びナフトキノン系を含むキノン系色素、ベタニン等のベタシアニジン系色素が挙げられる。 The natural pigment, for example, carotenoid-based pigments such as carthamin, flavonoid pigment containing anthocyanidin system and chalcone, quinone dyes, including anthraquinone and naphthoquinone, include Betashianijin based dyes such as betanin.
【0017】 [0017]
これらの赤色有機色素の中では、天然色素、特にアントラキノン系色素を使用するのが好ましく、中でも、カルミン酸(コチニール)又はそのアルミニウムレーキを使用するのが好ましい。 Among these red organic pigment, it is preferable to use natural pigments, in particular anthraquinone dyes, among others, preferably used carminic acid (cochineal) or aluminum lakes.
【0018】 [0018]
一方、本発明の添加剤を構成する酸化チタン被覆雲母(雲母チタン)は、雲母片の表面に酸化チタンを被覆したものである。 On the other hand, titanium oxide-coated mica constituting the additive of the present invention (mica titanium) is obtained by coating titanium oxide on the surface of mica flakes. この酸化チタン被覆雲母としては、好ましくは平均粒径が約15〜30μm、より好ましくは約20〜28μmのものであるが、約15μm未満の平均粒径を持つものであってもよい。 As the titanium oxide-coated mica, preferably having an average particle size of about 15 to 30 [mu] m, and more preferably is of about 20~28Myuemu, it may be one having an average particle size of less than about 15 [mu] m. また、酸化チタン被覆雲母の形状は、球状、板状、薄片状のものであってよい。 The shape of the titanium oxide-coated mica, spherical, plate-like, may be those flaky.
雲母表面の酸化チタン層の膜厚は、干渉色が得られれば特に限定されるものではなく、約140〜450nmの範囲で適宜選択される。 The film thickness of the titanium oxide layer of the mica surface is not limited in particular as long resulting interference color is properly selected within a range of from about 140~450Nm. 例えば、約140〜300nmの膜厚を有する黄色〜橙色干渉色のもの、あるいは約300〜450nmの膜厚を有する青〜紫干渉色のもの等が使用できる。 For example, such can be used as about 140~300nm those yellow to orange interference color having a thickness of, or blue-purple interference color having a thickness of about 300 to 450 nm.
【0019】 [0019]
本発明で使用される酸化チタン被覆雲母は種々の公知の方法で製造することができる。 Titanium oxide-coated mica used in the present invention can be produced by various known methods. 例えば、特公昭43−25644号公報には、硫酸チタニル、四塩化チタン等のチタン無機酸塩を雲母の存在下で分解し、含水酸化チタン又は二酸化チタンを析出させた後、大気中約500〜1000℃の温度で焼成する方法が記載されている。 For example, in JP-B-43-25644, titanyl sulfate, four titanium inorganic acid salt such as titanium chloride decomposes in the presence of mica, After precipitation of the hydrous titanium oxide or titanium dioxide, about atmospheric 500 It describes a method of firing at a temperature of 1000 ° C.. あるいは、酸化チタン被覆雲母として市販の製品をそのまま使用してもよい。 Alternatively, it may be a commercially available product as titanium oxide-coated mica. 上記の膜厚の酸化チタン層を有する製品として、エンゲルハード社製のフラメンコレッド、フラメンコゴールド、フラメンコサテンゴールド等、メルク社製のティミロンスーパーゴールド等が挙げられる。 As a product having a titanium oxide layer having a thickness of above, manufactured by Engelhard Corporation Flamenco Red, Flamenco Gold, Flamenco Satin Gold etc., Merck tee Milon Super Gold and the like.
【0020】 [0020]
本発明の添加剤は、これらの酸化チタン被覆雲母を上記の赤色有機色素で更に被覆してなる。 Additives of the present invention, these titanium oxide coated mica is obtained by further coating the above red organic dye. 赤色有機色素での被覆は、上記の赤色有機色素を水あるいは有機媒体などの適当な媒体に溶解又は分散させ、その溶液又は分散液に上記酸化チタン被覆雲母を浸漬して乾燥させることにより実施できる。 Coating a red organic dye, the red organic dye are dissolved or dispersed in a suitable medium such as water or an organic medium can be carried out by drying the immersing the titanium oxide-coated mica to the solution or dispersion .
このようにして製造される本発明の添加剤は、約1〜5重量%の赤色有機色素を含有しているのが好ましい。 Such additive of the present invention is manufactured is preferably contains about 1 to 5% by weight of a red organic dye. また、本発明の添加剤は、本発明の効果を妨げない程度の含有量で酸化鉄、フェリシアン化鉄等の他の成分を含んでいてもよい。 Further, the additives of the present invention, the iron oxide at a content of a degree that does not interfere with the effect of the present invention may contain other components such as ferricyanide iron.
【0021】 [0021]
本発明の添加剤としては、上記のようにして製造したもの以外に、市販されている製品をそのまま使用することもできる。 The additives of the present invention, in addition to those produced in the manner described above, can be used as it is the product sold. 例えば、エンゲルハード社製のデュオクロムRY(DUOCROME RY)、デュオクロムRB、デュオクロムRG、デュオクロムRV、クロイゾン・レッド(CLOISONNE RED)、ジェムトーン・サンストーン(Gemtone Sunstone) 、ジェムトーン・ガーネット(Gemtone Garnet) 、ジェムトーン・ルビー(Gemtone Ruby)あるいはタン・オパール(Tan Opal)等を挙げることができる。 For example, Engelhard Corporation of duo chrome RY (DUOCROME RY), duo chrome RB, duo chrome RG, duo chrome RV, Kuroizon Red (CLOISONNE RED), Gem tone Sunstone (Gemtone Sunstone), Gem tone garnet ( Gemtone Garnet), Gem tone ruby ​​(Gemtone ruby) or Tan opal (Tan opal), and the like can be given. これらは、いずれも赤色有機色素としてカルミンを用いたものであり、中でもデュオクロムRYは、カルミン/酸化チタン/雲母の重量比が1.5〜3%/31〜37%/61〜67%の薄片状であり、その薄片の幅が6〜50μmであるものが95%を占め(平均粒径22μm)、本発明において特に好適に使用される。 These are those both with carmine as a red organic pigment, among others duo chromium RY, the weight ratio of carmine / titanium oxide / mica 1.5 to 3% / 31-37% / 61-67% a flaky, in width of the flakes is 6~50μm accounted for 95% (average particle size 22 .mu.m), are particularly preferably used in the present invention. さらに、メルク社製のコロロナ・カーマインレッド(Colorona Carmine Red)、コロロナ・マジェンダ(Colorona Magenda)、コロロナ・インペリアルレッド(Colorona Imperial Red)、ディクロナRY(Dichrona RY)、ディクロナRB(Dichrona RB)、及びディクロナRG(Dichrona RG)、エンゲルハード社製のチェリーニカラーズ・コーラル(Cellini Coloes Coral)及びチェリーニカラーズ・レッド(Cellini Coloes Red)を好適な例として挙げることができる。 In addition, Merck & Co., Inc. of Kororona-carmine red (Colorona Carmine Red), Kororona, magenta (Colorona Magenda), Kororona Imperial Red (Colorona Imperial Red), Dikurona RY (Dichrona RY), Dikurona RB (Dichrona RB), and Dikurona RG (Dichrona RG), mention may be made of Engelhard Corp. Cellini Colors Coral a (Cellini Coloes Coral) and Cellini Colors Red (Cellini Coloes Red) preferred examples.
【0022】 [0022]
本発明の添加剤は、さらに表面処理を施したものであってもよい。 Additives of the present invention, may further subjected to surface treatment. 表面処理としては、化粧品用添加剤等に従来から施されている処理が挙げられる。 As the surface treatment, and treatment has been applied conventionally cosmetic additives. 例えば、酸化アルミニウム、酸化マグネシウム、酸化カルシウム等の無機金属酸化物や水酸化アルミニウム、水酸化マグネシウム、水酸化カルシウム等の無機金属水酸化物による処理(特開平9−20609号公報及び特開平9−30917号公報参照);珪酸、二酸化珪素、又は無機金属珪酸塩による処理(特公平5−74564号公報参照);シリカゲル、酸化チタン、酸化亜鉛、酸化マグネシウム、酸化鉄、又は雲母等の球状粒子による処理(特公平7−103324号公報、特開平9−132514号公報及び特許第278461号公報参照)、キトサン(誘導体)やシリコーンポリマーを含む天然又は合成ポリマー、あるいはNε−ラウロイル−L−リジン等のアミノ酸類による処理(G. Uzunian, et al., Cos For example, aluminum oxide, magnesium oxide, inorganic metal oxides and aluminum hydroxide, such as calcium oxide, magnesium hydroxide, treatment with an inorganic metal hydroxide such as calcium hydroxide (Japanese Patent Laid-Open 9-20609 and JP Hei 9- Referring 30917 JP); silicates, silicon dioxide or treatment with an inorganic metal silicate (see JP Kokoku 5-74564): silica gel, titanium oxide, zinc oxide, magnesium oxide, according to the spherical particles such as iron oxide, or mica processing (Kokoku 7-103324 and JP see Japanese and Japanese Patent No. 278461 Patent Laid-Open No. 9-132514), chitosan (derivatives) or a silicone polymer, natural or synthetic polymers including, or Nε- such lauroyl -L- lysine treatment with amino acids (G. Uzunian, et al., Cos etic and Toiletries, Vol.108, No.2, p93−98 (1993)参照)などが挙げられる。 etic and Toiletries, Vol.108, No.2, see p93-98 (1993)) and the like.
これらの表面処理を施すことにより、光沢の抑制、分散性(非凝集性)、潤滑性又はしまり性(compressibility)の向上、肌への付着性や保湿性の向上、あるいは感触の改善及び撥水性の付与といった効果が得られる。 By performing these surface treatments, the suppression of gloss, dispersibility (non-aggregated), improvement in lubricity or interference properties (Compressibility), improvement of adhesion and moisture to the skin, or feel improved and water repellency effect can be obtained, such as the grant.
【0023】 [0023]
本発明に係る添加剤は、本発明における「自分色のきれい肌」と同様に、図1(A)に示すような分光反射率曲線の波形を示すとともに、可視光波長領域(約400〜700nm)全体に渡って、実際に測定したダメージを受けていない人間の本来の肌よりも高い反射率を示す。 Additives according to the present invention, like the "own color beautiful skin" in the present invention, along with showing the waveform of the spectral reflectance curve as shown in FIG. 1 (A), the visible light wavelength region (approximately 400~700nm ) throughout the show actually a higher reflectance than the original skin of human beings who have not received the measured damage. よって、ダメージを受けてくすんだ色となった皮膚に適用し、透明感があって健康的で明るい「自分色のきれい肌」を取り戻すための化粧品の添加剤として特に適している。 Thus, it applied to the skin, which became the color of dull damaged, is particularly suitable as a cosmetic additives to regain a bright and healthy when there is a clear sense of "their own color of beautiful skin."
【0024】 [0024]
また本発明は、上記の添加剤を含有する化粧品組成物にも関する。 The invention also relates to cosmetic compositions containing said additives. この化粧品組成物は、「自分色のきれい肌」とするためのものである。 The cosmetic composition is intended to be as "their own color of beautiful skin."
この組成物中の添加剤の含有量は特に限られないが、一般的には組成物全重量に対して約1〜25重量%、より好ましくは約3〜20重量%、さらに好ましくは約4〜15重量%である。 This not the content of the additive in the composition is limited in particular, generally from about 1 to 25% by weight relative to the total weight of the composition, more preferably from about 3 to 20 wt%, more preferably about 4 it is a 15% by weight.
【0025】 [0025]
本発明の化粧品組成物は、皮膚に適用されるメークアップ化粧品とするのが好ましく、皮膚用のメークアップ化粧品、中でもファンデーション類であるのが好ましい。 The cosmetic composition of the present invention may preferably be make-up cosmetics applied to the skin, make-up cosmetics for skin, it is preferably Among them, foundations such. しかしながら、例えば「自分色のきれい肌」の風合いを付加した口紅、ほほ紅、アイシャドウ、アイブロウ、マスカラ、ベースメイク、コントロールカラー等の化粧品であってもよい。 However, for example lipstick obtained by adding the texture of "their own color of beautiful skin", blusher, eye shadow, eyebrow, mascara, base makeup, it may be a cosmetic, such as a control color. これらの化粧品組成物は、粉末状、固形粉末状、水中油型乳化状、油中水型乳化状、油性状、油性固型状、多層状、ゲル状等の形態であってよい。 These cosmetic compositions, powder, solid powder, an oil-in-water emulsified, water-in-oil emulsified, oil-like, oil-based solid shape, multi-layered, and may be in the form of gel or the like.
【0026】 [0026]
本発明の化粧品組成物は、特にメークアップ化粧品に通常使用されている他の成分を含有していてもよい。 The cosmetic composition of the present invention may also contain other ingredients usually used particularly in makeup cosmetics. 例えば、粉体、油性成分、水性成分、界面活性剤、酸化防止剤、香料、防腐剤、増粘剤、化粧品用活性成分、ポリマー類等が挙げられる。 For example, powders, oil components, aqueous components, surfactants, antioxidants, fragrances, preservatives, thickeners, cosmetic active components include polymers and the like. 当業者であれば、考慮される添加により、本発明の組成物の有利な特性が、全く又は実質的に悪影響を受けないように留意して、添加可能な他の成分及びその量を選択することができる。 Those skilled in the art, by the addition to be considered, advantageous properties of the compositions of the present invention, and taken not undergo no or substantially adversely, select other ingredients and amounts that can be added be able to.
【0027】 [0027]
粉体は、化粧品用として通常使用されている顔料、真珠光沢剤、及びフィラーを含む。 Powder includes pigments which are usually used for cosmetics, pearlescent agents, and fillers.
顔料は、無機又は有機の白色又は有色顔料を含む。 Pigments, including white or colored pigments of an inorganic or organic. 無機顔料としては、表面が処理されていてもよい二酸化チタン、酸化ジルコニウム又は酸化セリウム、並びに、酸化鉄又は酸化クロム、マンガンバイオレット、ウルトラマリンブルー、クロム水和物及びフェリックブルーを挙げることができる。 The inorganic pigments may titanium dioxide even surface being treated, zirconium oxide or cerium oxide, as well, may be mentioned iron oxide or chromium oxide, manganese violet, ultramarine blue, chromium hydrate and ferric blue. 有機顔料としては、カーボンブラック、D&C型の顔料、アルミニウム、カルシウム、ストロンチウム、バリウム又はコチニールカルミンをベースとしたレーキ類を挙げることができる。 As the organic pigments include carbon black, D & C type pigments, aluminum, calcium, strontium, and the lakes based barium or cochineal carmine.
【0028】 [0028]
真珠光沢剤は、本願請求項1に係る添加剤以外の干渉性物質を意味し、白色の真珠光沢顔料、例えば、酸化チタン又はオキシ塩化ビスマスで被覆されたマイカ、有色の真珠光沢顔料、例えば、酸化鉄を有する酸化チタン被覆雲母、特に、フェリックブルー又は酸化クロムを有する酸化チタン被覆雲母、上述した種類の有機顔料を有する酸化チタン被覆雲母、及びオキシ塩化ビスマスをベースとした真珠光沢顔料から選択することができる。 Pearlescent agents, means interfering substances other than additive of the present claim 1, white nacreous pigments such as mica covered with titanium oxide or with bismuth oxychloride, colored nacreous pigments such as titanium oxide-coated mica with iron oxides, in particular, be chosen from ferric blue or titanium oxide-coated mica with chromium oxide, titanium oxide-coated mica having organic pigment of the abovementioned type, and pearlescent pigments based on bismuth oxychloride be able to.
【0029】 [0029]
フィラーは、無機又は有機で、ラメラ状又は球状のものとすることができる。 Fillers, inorganic or organic, can be of lamellar or spherical. このようなフィラーとしては、タルク、マイカ、シリカ、カオリン、ナイロン[アトケム(Atochem)社のオルガソール(Orgasol)]、ポリ−β−アラニン及びポリエチレンパウダー、ポリテトラフルオロエチレン、ラウロイルリシン、デンプン、窒化ホウ素、テトラフルオロエチレンポリマーのパウダー、中空のミクロスフェア、例えば、エクスパンセル(ノーベルインダストリー社)、ポリトラップ(polytrap)(ダウコーニング社)及びシリコーン樹脂のマイクロビーズ[例えば、東芝のトスパール(Tospearls)]、炭酸カルシウム、炭酸マグネシウム及び水酸化マグネシウム、ヒドロキシアパタイト、中空のシリカのミクロスフェア[マプレコス(Maprecos)社のシリカビーズ]、ガラス Such fillers, talc, mica, silica, kaolin, Nylon [Atochem (Atochem) Co. Olga sole (Orgasol)], poly -β- alanine and polyethylene powders, polytetrafluoroethylene, lauroyl lysine, starch, nitride boron, powders of tetrafluoroethylene polymers, hollow microspheres, for example, Expancel (Nobel Industrie), poly trap (Polytrap®) (Dow Corning) microbeads example of and silicone resins, Toshiba Tospearl (Tospearls) ], calcium carbonate, magnesium and magnesium hydroxide carbonate, hydroxyapatite, hollow silica microspheres [Mapurekosu (Maprecos) Company silica beads, glass はセラミックのマイクロカプセル;8〜22の炭素原子、好ましくは12〜18の炭素原子を含有する有機カルボン酸から誘導される金属石鹸、例えば、ステアリン酸亜鉛、マグネシウム又はリチウム、ラウリン酸亜鉛又はミリスチン酸マグネシウムを挙げることができる。 Ceramic microcapsules; 8 to 22 carbon atoms, preferably a metal soaps derived from organic carboxylic acids containing 12 to 18 carbon atoms, for example, zinc stearate, magnesium or lithium, zinc laurate or myristate mention may be made of magnesium.
【0030】 [0030]
脂溶性着色料は、例えば、スーダンレッド、DCレッド17、DCグリーン6、β−カロテン、大豆油、スーダンブラウン、DCイエロー11、DCバイオレット2、DCオレンジ5又はキノリンイエロー等である。 Fat-soluble colorants, for example, Sudan Red, DC Red 17, DC Green 6, beta-carotene, soybean oil, Sudan brown, DC Yellow 11, DC Violet 2, DC Orange 5, or quinoline yellow, and the like. 水溶性着色料は、例えばビート根汁又はメチレンブルー等である。 Water-soluble colorants are, for example, beetroot juice or methylene blue and the like. 前記の顔料及び/又は着色料を配合することにより、組成物全体の色調を調整することができる。 By blending the pigments and / or colorants can adjust the color tone of the entire composition.
化粧品用活性成分としては、保湿剤、ビタミン類、必須脂肪酸、スフィンゴ脂質又はサンスクリーン剤を挙げることができる。 The active ingredient for cosmetics, mention may be made of moisturizers, vitamins, essential fatty acids, sphingolipids or sunscreen agents.
【0031】 [0031]
本発明の組成物は、考慮される用途の種類に応じて、植物、動物、鉱物又は合成由来、又はシリコーン由来のロウ、油、ガム及び/又はペースト状脂肪物質、及びそれらの混合物から選択される脂肪相を含有してもよい。 The compositions of the present invention is selected according to the type of application envisaged, plant, animal, mineral or synthetic origin, or silicone origin, waxes, oils, gums and / or pasty fatty substances, and mixtures thereof that may contain a fat phase.
室温で固体状のロウとしては、炭化水素含有ロウ、例えば、ミツロウ、カルナウバロウ、キャンデリラロウ、オーリクリーロウ(ouricury wax)、モクロウ、コルク繊維ロウ、又はサトウキビロウ、パラフィン又は褐炭ロウ、マイクロクリスタリンワックス、ラノリンロウ、モンタンロウ、オゾケライト、ポリエチレンロウ、フィッシャー−トロプシュの合成により得られるロウ、水素添加油、25℃で固体のグリセリド及び脂肪エステルを挙げることができる。 The solid wax at room temperature, a hydrocarbon-containing wax, for example, beeswax, carnauba wax, candelilla wax, Fiori Cree wax (ouricury wax), Japan wax, cork fiber wax or sugarcane wax, paraffin or lignite waxes, microcrystalline waxes , lanolin wax, montan wax, ozokerite, polyethylene waxes, Fischer - may waxes obtained by synthesis Tropsch, hydrogenated oils, and the like solid glycerides and fatty esters 25 ° C.. また、シリコーンロウを使用することもでき、このようなものとしては、ポリメチルシロキサンのアルキル、アルコキシ及び/又はエステルを挙げることができる。 It is also possible to use silicone waxes, These include, alkyl polymethylsiloxane, and alkoxy and / or esters. ロウは、コロイド状のロウ粒子の安定した分散物の形態で提供することができ、公知の方法、例えば、アカデミックプレス社から出版されている、エル・エム・プリンス(L.M. Prince)の「マイクロエマルションの理論と実際」(1977)の21−32頁に記載されている方法により調製することができる。 Wax may be provided in the form of a stable dispersion of colloidal wax particles, a known method, for example, published by Academic Press, El M. Prince (L. M. Prince) can be prepared by the methods described on pages 21-32 of "the theory and practice of microemulsions" (1977). 室温で液状のロウとしては、ホホバ油等を挙げることができる。 The liquid wax at room temperature, mention may be made of jojoba oil.
【0032】 [0032]
実際に、後述の実施例及び比較例に示すように、本発明の添加剤を含有していない化粧品組成物(ファンデーション)の分光反射曲線の各波長における反射率をA、添加剤を含有する組成物の分光反射曲線の各波長における反射率をBとしたとき、図1における領域IではA>B、領域IIではA<B、そして領域IIIではA>Bとなる。 Indeed, as shown in the Examples and Comparative Examples described later, the reflectance at each wavelength of the spectral reflectance curves of a cosmetic composition not containing the additive of the present invention (foundation) A, containing the additive composition when the reflectance at each wavelength of the spectral reflectance curve of the object and B, a> B in the region I in FIG. 1, in the region II a <B, and a region III in a> B. 即ち、本発明の化粧品組成物を適用した化粧肌は、約450〜550nmの波長領域(領域I)に上に凸のブロードなピーク、約500〜620nmの波長領域(領域II)に下に凸のピークを有し、約600〜700nmの波長領域(領域III)において漸増する基本的に右上がりとなる分光反射率曲線の波形を有し、これはダメージを受けていない「自分色のきれい肌」の波形と同じである。 That is, the decorative skin of applying a cosmetic composition of the present invention, on the convex broad peak in the wavelength region (region I) of about 450 to 550 nm, a downward convex in a wavelength region of about 500~620Nm (region II) has a peak, it has a waveform of the spectral reflectance curve to be essentially upward sloping gradually increasing in the wavelength region of about 600 to 700 nm (region III), which is not damaged "clean skin their color "is the same as that of the waveform.
【0033】 [0033]
最後に本発明は、本発明に係る添加剤を配合した化粧料を皮膚に塗布することからなる、くすんだダメージ肌(分光反射率曲線が凹凸を失って平坦化した肌)を「自分色のきれい肌」とする化粧方法にも関する。 Finally, the present invention is that the cosmetics containing the additive according to the present invention consists in applying to the skin, dull damaged skin (skin spectral reflectance curve has flattened losing irregularities) "own color also it relates to a cosmetic process to clean skin ".
この化粧方法は、本発明に係る化粧品組成物を皮膚に直接塗布する態様のみならず、例えば下地化粧料などを塗布した上に本発明の組成物を重ねて塗布する態様も包含する。 The cosmetic method, the cosmetic composition according to the present invention not only embodiment is applied directly to the skin, for example, also encompasses embodiments that applied over the composition of the present invention on which the base cosmetics, etc. is applied.
【0034】 [0034]
【実施例】 【Example】
以下に、具体例を挙げて本発明を更に詳細に説明する。 Hereinafter, more detailed description of the present invention with specific examples.
(実施例1) (Example 1)
一般募集したモニター103人について、紫外線等の外的刺激の影響を受けていると思われる前腕部外側の肌(「ダメージ肌」モデル)と、比較的刺激を受けていないと思われる上腕部内側の肌(「自分色のきれい肌」モデル)の分光反射率を測定した。 The public offering was monitored 103 people, and external stimulation of the affected and that the forearm outside of the skin that are considered, such as ultraviolet ( "damage skin" model), upper arm inside that would not have received relatively stimulus the spectral reflectance of the skin ( "my color of beautiful skin" model) of was measured.
各モニターの「ダメージ肌」モデル及び「自分色のきれい肌」モデルの部分の反射率を、カラーメーター(ミノルタ社製)を用いて測定した。 The reflectance of the "damage skin" model and the model of the part, "clean skin of his color" of each monitor, was measured using a color meter (made by Minolta Co., Ltd.). 分光測色計は、ワンプッシュで3回フラッシュした平均値を算出する設定とし、各モデルについて3カ所の測定を行い、3カ所の平均値を当該モデルの測定値とした。 Spectral colorimeter is a set for calculating the average value was flushed 3 times with one push, was measured in three places for each model, the average value of the three locations was a measure of the model. 得られた測定値を色彩解析ソフトウエア(コアサイエンス社)に入力して分光反射率曲線とした。 The resulting measured value is input to the color analysis software (core Science) was the spectral reflectance curve.
【0035】 [0035]
測定した103人のモニターの約90%に該当する人々についての分光反射率曲線は図1(A)及び(B)に示す波形を有していた。 The spectral reflectance curve for those corresponding to about 90% of the 103 people monitor measured had the waveform shown in FIG. 1 (A) and (B). 図1の曲線(A)が上腕部内側(「自分色のきれい肌」モデル)、(B)が前腕部外側(「ダメージ肌」モデル)の分光反射率曲線である。 Of the curve (A) is the upper arm inside Figure 1 ( "beautiful skin of his color" model), a spectral reflectance curve of (B) is the forearm outside ( "damage skin" model). ダメージを受けていない「自分色のきれい肌」モデルでは、約450〜550nmの波長領域(領域I)に上に凸のブロードなピーク、約500〜620nmの波長領域(領域II)に下に凸のピークを有し、約600〜700nmの波長領域(領域III)において漸増する基本的に右上がりの波形であった。 Not damaged in the model "clean skin of his color" is, above the convex of the broad peak in the wavelength region (I) of about 450~550nm, convex downward in the wavelength region of about 500~620nm (region II) has a peak was essentially upward-sloping waveform gradually increasing in the wavelength region of about 600 to 700 nm (region III). 一方、「ダメージ肌」モデルでは、領域I及びIIにおける曲線の凹凸が縮小し、なおかつ反射率が全波長領域に渡って低下していることがわかる。 On the other hand, the "damage skin" model, shrinking unevenness of the curve in regions I and II, it can be seen that yet reflectance is lowered over the entire wavelength range.
【0036】 [0036]
また、モニターの残り約10%の人々については、図2に示すような分光反射率曲線が得られた。 Further, for the remaining approximately 10% of people monitor, the spectral reflectance curve as shown in FIG. 2 was obtained. 図2中の(A)及び(B)は図1と同じ意味である。 2 in (A) and (B) has the same meaning as Figure 1. 図2では、「自分色のきれい肌」モデル(A)の領域I及びIIにおける凹凸が図1(A)より目立たなくなっており、全波長領域に渡って反射率が低下している。 In Figure 2, unevenness in the region I and II of "clean skin their color" model (A) has become less noticeable than FIG. 1 (A), the reflectance over the entire wavelength range is reduced. 即ち、これらのモニターでは、「自分色のきれい肌」モデルとして選択した上腕部内側の肌が、何らかの原因により若干のダメージを受けていたものと推量される。 That is, in these monitors, "his color of beautiful skin" selected upper arm inside of the skin as a model, be inferred that the had received some damage from any cause.
但し、図1に示した波形を示すモニターが全体の約90%を占める有意な結果であることは明らかである。 However, it is clear that a significant result of monitoring showing the waveform shown in FIG. 1 occupy approximately 90% of the total. よって、本発明においては、図1(A)及び(B)に示される波形の分光反射率を有する肌を、各々「自分色のきれい肌」及び「ダメージ肌」として定義した。 Therefore, in the present invention, the skin having a spectral reflectance of the waveform shown in FIG. 1 (A) and (B), and defined respectively as "my color clean peel" and "damage skin".
【0037】 [0037]
(実施例2) (Example 2)
本発明の化粧品用添加剤として、エンゲルハード社から市販されているデュオクロムRYを採用した。 As cosmetic additives of the present invention, employing a duo chromium RY commercially available from Engelhard Corporation. この添加剤は、カルミン/酸化チタン/雲母の構造を有し、その重量比が1.5〜3%/31〜37%/61〜67%の薄片状であり、その薄片の幅が6〜50μmであるものが95%を占める。 The additive, carmine / structure of the titanium oxide / mica has a weight ratio is from 1.5 to 3% / 31-37% / 61-67% of flaky, the width of the flakes 6 what is 50μm occupies 95%.
白色紙に、3x3cm の面積の透明(両面)粘着テープ(株式会社共和、パイロンらくはるテープ)を貼り付け、その粘着面に本発明の添加剤0.03gをファンデーション用パフを用いて塗布した。 White paper, transparent (double-sided) pressure-sensitive adhesive tape (Kyowa Limited, pylon RakuHaru tape) area of 3X3cm 2 paste, using foundation puff additives 0.03g of the present invention to its adhesive surface coating did.
このサンプルの反射率を、カラーメーター(ミノルタ社製)を用いて測定した。 The reflectance of the sample was measured using a color meter (manufactured by Minolta Co.). 分光測色計は、ワンプッシュで3回フラッシュした平均値を算出する設定とし、1サンプルについて3カ所の測定を行い、3カ所の平均値を当該サンプルの測定値とした。 Spectral colorimeter is a set for calculating the average value was flushed 3 times with one push, the one sample was measured for three locations, the average value of the three locations was a measure of the sample.
得られた測定値を、色彩解析ソフトウエア(コアサイエンス社)に入力して分光反射率曲線とした。 The resulting measured value was a spectral reflectance curve by entering the color analysis software (core Science). その曲線を図3(A)に示し、実施例1で測定した「自分色のきれい肌」モデルの分光反射曲線を(B)として示した。 The curve a shown in FIG. 3 (A), showed a spectral reflection curve model "clean skin their color" measured in Example 1 as (B).
【0038】 [0038]
(比較例1) (Comparative Example 1)
添加剤として、エンゲルハード社から市販されているデュオクロムYRを使用し、同様の測定を実施した。 As an additive, by using the duo chrome YR commercially available from Engelhard Corporation, it was carried out similar measurements. この添加剤は、赤酸化鉄/酸化チタン/雲母の構造を有し、その重量比が3〜5%/36〜42%/56〜61%の薄片状であり、その薄片の幅が6〜50μmであるものが95%を占める。 This additive has the structure of red iron oxide / titanium oxide / mica, the weight ratio is 3-5% / 36-42% / 56-61% of flaky, the width of the flakes 6 what is 50μm occupies 95%. この添加剤の分光反射率曲線を(C)として図3に示した。 The spectral reflectance curve of the additive as (C) shown in FIG.
【0039】 [0039]
図3から明らかなように、本発明の添加剤(A)は「自分色のきれい肌」モデル(B)と同様の波形を有する分光反射率を示し、その値は「自分色のきれい肌」モデルよりも高い。 As apparent from FIG. 3, the additives of the present invention (A) shows the spectral reflectance having the same waveform as "clean skin their color" model (B), the value is "my color clean peel" higher than the model. 一方、比較例1の添加剤では、領域Iにおけるブロードなピークも領域IIにおける窪みも見られず、「自分色のきれい肌」モデルとは全く異なる波形を示す。 On the other hand, in the additive of Comparative Example 1, broad peaks in the region I nor not observed depressions in the region II, shows a completely different waveform from the "own color beautiful skin" model.
【0040】 [0040]
(実施例3及び比較例2及び3) (Example 3 and Comparative Examples 2 and 3)
下記の表1に示す組成のファンデーションを調製した(表1に示す数値は重量%である)。 The foundation of the composition shown in Table 1 below was prepared (numerical values ​​shown in Table 1 are in weight percent).
【表1】 [Table 1]
【0041】 [0041]
個体差による影響を排除するため、市販の人工皮膚に3x3cm の領域を3カ所(A、B及びC)とり、当該領域A、B及びCに下地化粧料0.05gを塗布した。 To eliminate the influence of individual differences, commercially available 3 places the region of 3X3cm 2 in artificial skin (A, B and C) take and the area A, B and C the underlying cosmetic 0.05g applied. その上に、領域Aには上記実施例3、領域Bには比較例2、そして領域Cには比較例3のファンデーションを各々0.06gずつ塗布した。 Thereon, in the area A above Example 3, Comparative Examples in the region B 2, and the region C were each applied by 0.06g foundation of Comparative Example 3.
領域A、B及びCの各々の分光反射率を実施例1と同様にして測定した。 Region A, the spectral reflectance of each of B and C were measured in the same manner as in Example 1.
【0042】 [0042]
領域A及びBで得られた曲線を図4に示した。 The resulting curves in the region A and B shown in FIG. 本発明の添加剤(デュオクロムRY)を配合したファンデーション(実施例3)を塗布した肌(領域A)は、それを配合しないファンデーション(比較例2)を塗布した肌(領域B)に比較して、波長450nm近傍の上側ピーク及び波長500nm近傍の下側ピークが増大し、600nmより長波長の領域では反射率が向上している。 Additives of the present invention the skin coated with (duo chrome RY) foundation formulated with Example 3 (region A) compares it to the foundations not blended (Comparative Example 2) the coated skin (area B) Te, and increases the lower the peak of the upper peak and the wavelength 500nm vicinity of a wavelength near 450nm has improved reflectivity in the wavelength region longer than 600 nm. 即ち、本発明の添加剤を配合したファンデーションを塗布することにより、「自分色のきれい肌」に近い反射率を示す化粧肌が得られた。 That is, by applying a foundation formulated with additives of the present invention, the cosmetic skin showing reflectance close to "own color beautiful skin" is obtained.
【0043】 [0043]
次に、領域A、B及びCで得られた曲線を図5に示す。 Next, the region A, the curve obtained with B and C in FIG. 5. 参考のため、「自分色のきれい肌」モデルの曲線も示した。 For reference, also showed curve of the model "clean skin of his color". 赤酸化鉄被覆された酸化チタン被覆雲母添加剤を含有するファンデーション(比較例3)を塗布した領域Cでは、500nmより長波長の領域において、添加剤を含有しない比較例2よりも高い反射率を示したが、その波形は凹凸が無く平坦であった。 In red iron oxide coated regions coated with foundation containing titanium oxide coated mica additive (Comparative Example 3) C, in the region of wavelengths longer than 500 nm, a reflectance higher than that of Comparative Example 2 containing no additive It indicated, but the waveform irregularities was not flat. 即ち、赤色有機色素(カルミン)ではなく赤色無機顔料(赤酸化鉄)で被覆した表面を持つ添加剤では、本発明が意図する「自分色のきれい肌」は得られない。 That is, in the additive having the surfaces coated with the red organic pigment (carmine) rather than red inorganic pigments (red iron oxide), "their colors beautiful skin" of the present invention is intended can not be obtained.
【0044】 [0044]
(実施例4) (Example 4)
実施例3のファンデーションにおいて、デュオクロムRYの添加量を4.5重量%とし、タルクの含有量を35.0重量%としたファンデーション(実施例4)を調製した。 In foundation of Example 3, the amount of duo chrome RY to 4.5 wt%, the content of talc to prepare a 35.0 wt% and the foundation (Example 4).
年齢18〜45歳の女性パネリスト35人に、日頃使用しているパウダーファンデーションに換えて実施例4及び比較例2のファンデーションを3週間使用してもらい、その結果を1週間毎に聞き取り調査を実施した。 To 35 women panelists of age 18 to 45-year-old, asked to use three weeks the foundation of Example 4 and Comparative Example 2 in place of the powder foundation that you are using daily, conducted a survey interviews the results every week did.
【0045】 [0045]
その結果、下記の表2に示す意見が聴取された。 As a result, an opinion that shown in Table 2 below were listening.
【表2】 [Table 2]
【0046】 [0046]
3週間経過後、各パネリストの評価結果をまとめると以下のようになった。 After three weeks passed, it became be summarized as follows results of the evaluation of each panelist.
(1)塗布後の肌のくすみ: (1) dullness of the skin after application:
比較例2のファンデーションについては86%が「くすみがある」と評価したのに対し、実施例4については56%が「くすみがない」と評価した。 To 86% for the foundation of Comparative Example 2 was evaluated as "dullness is", 56% for Example 4 was evaluated as "not dull".
(2)全体的な満足度: (2) overall satisfaction:
実施例4のファンデーションについて、77%以上がその広がり易さを含めて「満足である」と評価した。 The foundation of Example 4, more than 77% was evaluated to be "satisfied" including the spread ease.
(3)購入意欲: (3) purchase motivation:
実施例4のファンデーションについて、71%以上が「購入したい」と評価した。 The foundation of Example 4, more than 71% was evaluated as "want to buy".
【0047】 [0047]
(比較例4) (Comparative Example 4)
(A)橙色干渉色の酸化チタン被覆雲母(エンゲルハード社、フラメンコオレンジ); (A) orange interference color of titanium oxide coated mica (Engelhard, Flamenco Orange);
(B)緑色干渉色の酸化チタン被覆雲母(エンゲルハード社、フラメンコグリーン); (B) a green interference color of titanium oxide coated mica (Engelhard, Flamenco Green);
(C)(A)と(B)の1:1混合物を用意し、各々について実施例2と同様の反射率測定を実施した。 1 (C) (A) and (B): 1 mixture was prepared, each was carried out reflectometry as in Example 2 for. 得られた分光反射率曲線を図6に示す。 The resulting spectral reflectance curve shown in FIG.
【0048】 [0048]
図6に示されるように、異なる干渉色を有する雲母チタン(A)及び(B)を混合した場合、その混合物の分光反射率曲線は、加法混色に従って互いのピークが打ち消しあい、可視光の全波長領域(400〜700nm)に渡って平坦となることが確認された。 As shown in FIG. 6, when mixing the mica titanium having a different interference color (A) and (B), the spectral reflectance curve of the mixture, cancel each other's peak according additive color mixing, the entire visible light it was confirmed that the flat over the wavelength region (400 to 700 nm).
【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS
【図1】「自分色のきれい肌」モデル(A)及び「ダメージ肌」モデル(B)の分光反射率曲線の典型的な波形を示す図である。 FIG. 1 is a diagram illustrating a typical waveform of the spectral reflectance curve of the "beautiful skin of his color" model (A) and "damage skin" model (B). 実施例1で測定した103名のモニターのうち、約90%の分光反射率曲線が図1に示した波形パターンに該当した。 Of Monitor 103 persons measured in Example 1, the spectral reflectance curve of about 90% was applicable to the waveform pattern shown in FIG.
【図2】「自分色のきれい肌」モデル(A)及び「ダメージ肌」モデル(B)の少数の例で得られた分光反射率曲線の波形を示す図である。 2 is a diagram showing the waveform of the spectral reflectance curves obtained with a small number of examples of "clean skin their color" model (A) and "damage skin" model (B). 実施例1で測定した103名のモニターのうち、約10%の分光反射率曲線が図2に示した波形パターンに該当した。 Of Monitor 103 persons measured in Example 1, the spectral reflectance curve of about 10% was applicable to the waveform pattern shown in FIG.
【図3】本発明の添加剤(A)、「自分色のきれい肌」モデル(B)及び赤酸化鉄で被覆した酸化チタン被覆雲母雲母(C)の分光反射曲線を示すグラフである。 [3] The additives of the present invention (A), is a graph showing the spectral reflectance curves of the "own color beautiful skin" model (B) and the titanium oxide-coated mica mica coated with red iron oxide (C).
【図4】実施例3(●)及び比較例2(◆)のファンデーションを塗布した肌の分光反射率曲線を示すグラフである。 4 is a graph showing the spectral reflectance curve of skin coated with foundation of Example 3 (●) and Comparative Example 2 (◆).
【図5】実施例3(●)、比較例2(△)及び比較例3(▲)のファンデーションを塗布した肌の分光反射率曲線を示すグラフである。 [5] Example 3 (●), is a graph showing the spectral reflectance curve of Comparative Example 2 (△) and Comparative Example 3 (▲) skin foundation was applied for. 参考のため、「自分色のきれい肌」モデルの分光反射曲線も併せて示す(◆)。 For reference, also shows the spectral reflectance curves of the model "clean skin of his color" (◆).
【図6】異なる干渉色を持つ酸化チタン被覆雲母の混合による加法混色を示すグラフである。 6 is a graph showing the additive color mixing due to mixing of the titanium oxide-coated mica having a different interference colors. 橙色干渉色の酸化チタン被覆雲母を(A)、緑色干渉色の酸化チタン被覆雲母を(B)、そして(A)と(B)の1:1混合物を(C)で示す。 Titanium oxide coated mica orange interference color (A), titanium oxide coated mica green interference color (B), and (A) and 1 (B): indicated by a mixture (C).

Claims (12)

  1. 酸化チタン被覆雲母を赤色有機色素でさらに被覆してなることを特徴とする、自分色のきれい肌とするための化粧品用添加剤。 Characterized by comprising further coating the titanium oxide-coated mica with a red organic dye, cosmetic additive for a clean skin their color.
  2. ピークが消失又は縮小した平坦な形状の分光反射率曲線を示すダメージ肌を、約450〜550nmの波長領域に上に凸のブロードなピーク、約500〜620nmの波長領域に下に凸のピークを有し、約600〜700nmの波長領域において漸増する基本的に右上がりの形状を有する分光反射率曲線を示す自分色のきれい肌とするための、請求項1に記載の添加剤。 Damage skin showing the spectral reflectance curve of the flat shape of the peak is lost or reduced, on the convex broad peak in the wavelength region of about 450 to 550 nm, the peak of the convex downward in the wavelength region of about 500~620nm has, for the clean skin their color showing the spectral reflectance curves having essentially upward sloping shape gradually increasing in the wavelength region of about 600 to 700 nm, the additive of claim 1.
  3. 有機色素がアントラキノン系色素である、請求項1に記載の添加剤。 Organic dye is an anthraquinone dye, additive according to claim 1.
  4. 有機色素がカルミンである、請求項1に記載の添加剤。 Organic dyes are carmine, additive according to claim 1.
  5. 酸化チタン被覆雲母の酸化チタン膜厚が140〜450nmである、請求項1に記載の添加剤。 Titanium oxide film thickness of the titanium oxide coated mica is 140~450Nm, additive according to claim 1.
  6. 平均粒径が15〜30μmである、請求項1に記載の添加剤。 Average particle diameter of 15 to 30 [mu] m, the additive of claim 1.
  7. 赤色有機色素の含有量が1〜5%である、請求項1に記載の添加剤。 The content of the red organic dye is 1-5%, the additive of claim 1.
  8. 表面処理を施したものである、請求項1に記載の添加剤。 It was subjected to surface treatment, the additive of claim 1.
  9. 請求項1から8のいずれか一項に記載の添加剤を含有してなることを特徴とする、自分色のきれい肌とする化粧品組成物。 Characterized by containing an additive according to any one of claims 1 to 8, the cosmetic composition to clean skin their color.
  10. ファンデーションの形態である、請求項9に記載の化粧品組成物。 In the form of a foundation, the cosmetic composition according to claim 9.
  11. 添加剤の含有量が組成物全重量に対して1〜25重量%である、請求項9に記載の化粧品組成物。 The content of the additive is 1 to 25% by weight relative to the total weight of the composition, cosmetic composition according to claim 9.
  12. 請求項9から11のいずれか一項に記載の化粧品組成物を皮膚に塗布することからなる、自分色のきれい肌とする化粧方法。 It consists of applying to the skin the cosmetic composition according to any one of claims 9 11, cosmetic process to clean skin their color.
JP2003111196A 2003-04-16 2003-04-16 Cosmetic additives Expired - Fee Related JP4438310B2 (en)