JP2004115766A - Pressure-sensitive adhesive sheet - Google Patents

Pressure-sensitive adhesive sheet Download PDF

Info

Publication number
JP2004115766A
JP2004115766A JP2002285235A JP2002285235A JP2004115766A JP 2004115766 A JP2004115766 A JP 2004115766A JP 2002285235 A JP2002285235 A JP 2002285235A JP 2002285235 A JP2002285235 A JP 2002285235A JP 2004115766 A JP2004115766 A JP 2004115766A
Authority
JP
Japan
Prior art keywords
adhesive layer
sheet
surface
pressure
sensitive adhesive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2002285235A
Other languages
Japanese (ja)
Inventor
Ichiro Kawabata
Haruo Ono
Kazuhiro Takahashi
Kenichi Yamaguchi
大野 晴男
山口 健一
川幡 一郎
高橋 一弘
Original Assignee
Dainippon Printing Co Ltd
大日本印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dainippon Printing Co Ltd, 大日本印刷株式会社 filed Critical Dainippon Printing Co Ltd
Priority to JP2002285235A priority Critical patent/JP2004115766A/en
Publication of JP2004115766A publication Critical patent/JP2004115766A/en
Application status is Pending legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide an adhesive sheet securing "easy air letting out" on pasting through unevenness on the surface of the adhesive layer, capable of pasting temporarily and performing strong actual adhesion afterwards.
SOLUTION: This adhesive sheet 10 installed with many projecting bodies 2a on the surface of an adhesive layer 2 on a substrate sheet 1 is provided by presenting many projecting bodies having different heights h as mixed. By the surface unevenness of the adhesive layer caused by the projecting bodies, the easy air letting out is secured and also by pushing it with a light pressure, the adhesive layer makes a contact with a material to be adhered mainly with the top parts of the projecting bodies for setting the position by a temporary adhesion. By further pushing forcefully, the projecting bodies having lower height can make a contact with the substrate to obtain more contacting parts to get a sufficiently strong actual adhesion. Further, on the surface of the adhesive layer, it is better to laminate a releasing sheet 3 having a releasing surface having a reverse unevenness shape to the unevenness shape of the adhesive layer.
COPYRIGHT: (C)2004,JPO

Description

【0001】 [0001]
【発明の属する技術分野】 BACKGROUND OF THE INVENTION
本発明は、粘着剤層表面に凹凸を設けた粘着シートに関する。 The present invention relates to a pressure-sensitive adhesive sheet having irregularities on the surface of the adhesive layer. 特に、被着体に貼り付け時に空気を抱き込み難い「空気抜け容易性」を有すると共に、仮貼り及び、強固な本接着ができる粘着シートに関する。 In particular, and it has a "air escape ease" hardly embrace the air when stuck to an adherend, temporary attachment and to a pressure-sensitive adhesive sheet can firm the adhesive.
【0002】 [0002]
【従来の技術】 BACKGROUND OF THE INVENTION
一般的に粘着シートの粘着剤層表面は平坦面であり、その為に、被着体に粘着シートを貼り付けるときは、注意して貼らないと空気を抱き込み易い。 Generally the pressure-sensitive adhesive layer surface of the adhesive sheet is a flat surface, in order that, when joining the adhesive sheet to the adherend, when not stick note embrace the air easily. この様な場合、粘着剤層表面を凹凸面とした粘着シートを使用すれば、粘着剤層表面の凸部と凸部との間に空気の逃げ道ができるので、空気の抱き込みは改善する。 In such cases, the use of pressure-sensitive adhesive sheet was uneven surface an adhesive layer surface, since it is an escape route for air between the protruding portions of the adhesive layer surface, embrace the air improves. この様に粘着剤層表面が凹凸を有し空気を抱き込み難い性質(本明細書では、これを「空気抜け容易性」と称することにする。)を備えている粘着シートとしては、例えば、特許文献1、特許文献2等に開示の粘着シートが挙げられる。 The embrace difficult nature (herein, this. To be referred to as "air escape ease") air has is such a pressure-sensitive adhesive layer surface irregularities as an adhesive sheet provided with a, for example, Patent Document 1, include pressure-sensitive adhesive sheet disclosed in Patent Document 2 or the like. 例えば、特許文献2で開示する粘着シートでは、図2の斜視図で例示する粘着シート30の如く、基材シート31上の粘着剤層32の表面の凹凸形状として、下端部の外径が0.3mmで、表面からの高さ(高低差)が20μmの凸状体32aを、縦横に間隔1mmで散在する様に配列した形状等を開示している。 For example, in the pressure-sensitive adhesive sheet disclosed in Patent Document 2, as the pressure-sensitive adhesive sheet 30 illustrated in the perspective view of FIG. 2, as the uneven shape of the surface of the adhesive layer 32 on the substrate sheet 31, the outer diameter of the lower portion 0 in .3Mm, discloses a convex body 32a height (height difference) is 20μm in from the surface, sequence shape so as to interspersed intervals 1mm vertically and horizontally, and the like.
【0003】 [0003]
【特許文献1】 [Patent Document 1]
特許第2994411号公報【特許文献2】 Japanese Patent No. 2994411 [Patent Document 2]
実用新案登録第2503717号公報【0004】 JP Utility Model Registration No. 2503717 [0004]
【発明が解決しようとする課題】 [Problems that the Invention is to Solve
しかしながら、図2の様に、全ての凸状体32aの高さが同じであると、凸状体の頂上部周辺のみ被着体に接触する様に軽い圧力で押し付けて、仮接着して位置決めした後、強く押し付けて本接着させても、被着体に接触している接着剤層の部分が十分に得られず、十分に強固な接着力が得られないことがあった。 However, as in FIG. 2, when the height of all the convex member 32a is the same, only the top portion surrounding the convex-shaped body is pressed against a light pressure so as to contact with the adherend, temporarily adhered to the positioning after, also be present bonded firmly pressed, there is the portion of the adhesive layer in contact with the adherend can not be sufficiently obtained, not sufficiently strong adhesion force can not be obtained.
【0005】 [0005]
すなわち、本発明の課題は、貼着時の「空気抜け容易性」を粘着剤層表面の凹凸により確保すると共に、仮貼りができ、しかもその後に、強固な本接着ができる様にすることである。 That is, an object of the present invention, while securing the unevenness of the "air escape ease" pressure-sensitive adhesive layer surface during sticking, temporary attachment can, moreover that thereafter, to such can firm the adhesion is there.
【0006】 [0006]
【課題を解決するための手段】 In order to solve the problems]
そこで、上記課題を解決すべく、本発明の粘着シートでは、基材シート上に粘着剤層が設けられた粘着シートにおいて、該粘着剤層はその表面から外方に突出する多数の凸状体を有し、且つ高さの異なる多数の凸状体が混在している構成とした。 To solve the above problems, the pressure-sensitive adhesive sheet of the present invention, the pressure-sensitive adhesive sheet where the pressure-sensitive adhesive layer is provided on a substrate sheet, the pressure-sensitive adhesive layer a large number of convex body which projects outwardly from the surface thereof the a, and a number of different convex body height has a configuration in which a mix.
【0007】 [0007]
この様な構成とすることで、凸状体によって形成される粘着剤層表面の凹凸によって、空気抜け容易性が確保される上、軽い圧力で押し付ければ高さの高い凸状体の頂上部を主体に被着体に接触して仮接着による位置決めができ、更に強く押し付ければ、高さの低い凸状体も被着体に接触して、高さの低い凸状体も含めて被着体との十分な接触部分が得られるので、十分に強固な本接着ができる。 By virtue of the above configuration, the irregularity of the adhesive layer surface formed by the convex-shaped body, on deflation ease is secured, the top of the high convex body height if Oshitsukere with light pressure the contact with the adherend and be positioned by the temporary adhesive mainly, if Oshitsukere stronger, low convex body height also in contact with the adherend, the, including low convex body height because sufficient contact portion with the adherend is obtained, it is sufficiently strong the bond.
【0008】 [0008]
また、本発明の粘着シートは、上記構成に於いて更に、粘着剤層の表面に、該表面の凹凸形状とは逆凹凸形状の離型面を有する離型シートが積層されて成る構成とした。 Further, the pressure-sensitive adhesive sheet of the present invention, further above-mentioned configuration, the surface of the pressure-sensitive adhesive layer, the irregularities of the surface has a configuration in which a release sheet having a release surface opposite irregularities formed by laminating .
この様な構成とすることにより、粘着剤層への凸状体の形成が容易となる上、更には、粘着シート保存時、流通時、使用時等に於いて、凸状体による表面凹凸の形状維持が容易となる。 By virtue of the above configuration, on formation of the convex body to the pressure-sensitive adhesive layer is facilitated, and further, when the pressure-sensitive adhesive sheet storage, during distribution, in the use or the like, the surface irregularities due to projecting member shape retention is facilitated.
【0009】 [0009]
【発明の実施の形態】 DETAILED DESCRIPTION OF THE INVENTION
以下、図面を参照しながら本発明の実施の形態を説明する。 Hereinafter, with reference to the drawings illustrating the embodiments of the present invention.
【0010】 [0010]
〔凸状体による粘着剤層表面の凹凸〕 [Irregularities of the adhesive layer surface with a convex body]
本発明の粘着シート10は、その一形態を図1の断面図で概念的に示す如く、基材シート1上に粘着剤層2が設けらており、該粘着剤層2は、その表面から外方(図面上方)に突出する多数の凸状体2aによって、表面に凹凸形状を有する。 The adhesive sheet 10 of the present invention, the one form as conceptually shown in a cross-sectional view of FIG. 1, the pressure-sensitive adhesive layer 2 on the substrate sheet 1 has et provided, the pressure-sensitive adhesive layer 2 from its surface by a large number of convex bodies 2a projecting outwardly (drawing above), having an irregular shape on the surface. しかも、凸状体2aは、高さhが異なる多数の凸状体が混在している構成である。 Moreover, the convex body 2a has a configuration in which a large number of convex body height h are different are mixed. なお、更に好ましくは、図1に例示の如く、粘着剤層2の表面上には、粘着剤層表面の凹凸形状とは逆凹凸形状の離型面を有する離型シート3を積層した構成とする。 Incidentally, more preferably, as illustrated in FIG. 1, on the surface of the adhesive layer 2, an uneven shape of the surface of the adhesive layer is a structure obtained by laminating a release sheet 3 having a release surface opposite irregularities to.
【0011】 [0011]
本発明で言うところの凸状体2aの高さhとは、粘着剤層2の下側境界(図面で基材シート1と粘着剤層2との境界)を基準とした凸状体の頂上部の高さである。 The height h of the convex body 2a as referred in the present invention, the top of the convex body and the lower boundary of the pressure-sensitive adhesive layer 2 (the boundary between the substrate sheet 1 and the adhesive layer 2 in the drawing) as a reference it is the height of the part. つまり、凸状体の頂上部に於ける粘着剤層の部分の厚みである。 In other words, the thickness of the portion of the in the pressure-sensitive adhesive layer on the top of the convex body. 本発明でいうところの凸状体の高さとは、隣接する凸状体間の谷部2bの谷底を基準とした凸状体の頂上部の高さ(高低差)ではない。 The height of the convex body referred to in the present invention, not the height of the top portion of the convex body relative to the trough bottom of the valley portion 2b between the adjacent convex body (height difference). それは、隣接する凸状体間の谷部2bの谷底の高さ(粘着剤層2の下側境界を基準とした高低差)は、図面で例示の如く本発明では一定である必要は無いからである。 It (height difference relative to the lower boundary of the pressure-sensitive adhesive layer 2) the height of the root of the valley portion 2b between the adjacent convex body, because need not be constant in the present invention as illustrated in the drawings it is. 例えば、異なる高さの谷底を基準にした高さが異なる凸状体同士では、それの本発明定義による凸状体の高さhが同じこともあり得るからである。 For example, in the height relative to the root of different heights are different convex bodies, because the height h of the convex body may also same by it of the present invention defined. なお、粘着剤層2の下側境界(基材シートとの境界)は平面であるが、もしも特殊なケースとして、平面ではなく凹凸面である場合は、任意の水平部分(境界面の凹凸の平均位置等)を基準面として、この基準面からの高低差を凸状体の高さhとしても良い。 Incidentally, the lower boundary of the pressure-sensitive adhesive layer 2 (the boundary between the base sheet) is a plan, if as a special case, if an uneven surface instead of a plane, any of the horizontal portion (the boundary surface irregularities of as a reference surface a mean position, etc.), the height difference from the reference plane may be the height h of the convex body.
【0012】 [0012]
上記の如く、高さの異なる多数の凸状体を混在させることで、軽い圧力で押し付けた時は、高さが比較的高い多数の凸状体は圧力で若干押し潰される様に変形しつつ、その頂上部周辺が主体となって、被着体と接触するので、貼り付け位置の修正が必要な場合でも、軽い力で容易に剥がせ、仮接着による仮貼りが出来る。 As described above, by mixing the different number of the convex body height, when pressed with light pressure is relatively high number of convex body height while deformed so as to be crushed slightly pressure , so that the top portion around mainly because contact with the adherend, even when the correction of the bonding position necessary, easily Hegase a small force, temporary attachment can be by temporary adhesion. そして、正しい位置に仮貼りできているとなれば、今度は強い圧力で押し付ける。 And, if that can be temporarily attached to the correct position, now it presses under strong pressure. すると、既に頂上部が接触している比較的高さが高い凸状体は、更に押し潰される様に変形しつつ、その山腹部分まで被着体との接触部分が広がると共に、今まで被着体に接触していなかった比較的高さが低い多数の凸状体も、被着体に接触して圧力で押し潰される様に変形しつつ、その頂上部周辺、さらにはその山腹部分、或いは更に一部の谷部の谷底部分までも被着体に接触する様になるので、強固な本接着が可能となるのである。 Then, already top portion in contact with and relatively high high convex body, while deformed so as to be crushed further, with the contact portion of the adherend until the flank portion expands, deposited until now relatively low height many convex body which has not been in contact with the body and while deformed so as to be crushed by pressure in contact with the adherend, the top portion surrounding, more hillsides portion thereof, or also becomes a way to contact the adherend further to valley bottom portion of the valley portion, it become possible to firm the adhesive.
【0013】 [0013]
しかし、もしも、全ての凸状体の高さが同一であれば、仮接着は全ての凸状体の頂上部付近が関与した被着体との接触でなされ、その後、本接着の為に強い圧力を加えたときの接着では、既に頂上部が接触している全ての凸状体において、それらの山腹部分に接触部分を広げる様になる。 However, if, as long as the same height of all the convex body, the provisional adhesion is near the top of all the convex body made in contact with the adherend involved, then strong for the adhesive the adhesion when a pressure is applied, already in all convex body whose top portion is in contact, becomes as spread the contact portion thereof mountainside portions. このとき、圧力の増大とともに、被着体との接触部分は増大するが、凸状体が変形して初めてその山腹部分も接触可能となる為に、圧力増分に対する接触部分の増分の度合いは少ない。 In this case, with increasing pressure, but the contact portion between the adherend is increased, for convex bodies is possible also contacts the first time that flank portion is deformed, the small degree of increment of the contact portion with respect to the pressure increment . これが、全ての凸状体の高さが同一の場合、強い圧力で押し付けても、強固な接着力を得難い理由であった。 If this is the height of all the convex body of the same, even if pressed by strong pressure, was the reason that it is difficult to obtain a strong adhesion.
【0014】 [0014]
なお、凸状体の山腹の斜面をなだらかにすれば、圧力増分に対する接触部分の増分の度合いを大きくできるので、この点では凸状体の変形がより少ない状態で、被着体との接触面積を増やせる。 Incidentally, if the slope of the hillside convex body gently, it is possible to increase the degree of increment of the contact portion against the pressure increment, in a state deformed less of convex bodies In this regard, the contact area between the adherend the Fuyaseru. しかし、この様ななだらかな凸状体とすると、粘着剤層の表面凹凸のうねりが大きくなり過ぎて、被着体に貼り付けた後に表面凹凸模様となって見え易くなってしまうので、それも限界がある。 However, when such a smooth convex body, too large undulation of the surface unevenness of the pressure-sensitive adhesive layer, so it becomes easier to look become a surface unevenness pattern after stuck to the adherend, even it There is a limit. しかし、凸状体として異なる高さを有する多数の凸状体を混在させれば、この様な表面凹凸模様が生じないか生じたとしても目立たず、仮接着と強固な本接着が可能となるのである。 However, if a mix of multiple convex bodies having different heights as a convex body is not conspicuous even such surface unevenness pattern has occurred or not occurred, it is possible to temporarily adhered and firm the adhesion than is.
【0015】 [0015]
凸状体2aの高さhは、少なくとも2レベルの高さ、より好ましくは3レベル以上の多数の高さを有するものが良い。 The height of the convex body 2a h at least two levels of height, more preferably those having a large number of height of three or more levels. それは、押し付け圧力の増大と共に、より滑らかに被着体との接触部分の増大が得られるからである。 It, along with the increase in pressing pressure, because more smoothly increase in the contact portion between the adherend is obtained. そして、これらの異なる高さレベルを有する凸状体を多数、混在させる。 Then, a large number of convex bodies having these different height levels, mix. 混在はそれが最終的に目立たなければ、高さの異なる凸状体を(少なくとも隣接する凸状体の全てが同じ高さhとはならない様に、同一高さの凸状体を他の凸状体に対して)規則的に配置しも良いが、より目立ち難くさせるには、同じ高さの凸状体が集中しない様になるべくランダムに混在させるのが良い。 If mixed unless it eventually inconspicuous, different convex body height (As all of at least the adjacent convex body is not the same height h, flush convex body other convex ) good servants regularly arranged against Jo body, but is hardly more noticeable, is good to mix as much as possible random as convex body does not concentrate at the same height.
【0016】 [0016]
この他、凸状体の形状としては特に制限は無い。 In addition, no particular restriction on the shape of the convex body. 例えば、凸状体の(垂直断面形状は)、頂上部、側面、谷部等の形状は曲線、直線、これら組み合わせ等任意である。 For example, the convex body (vertical cross-sectional shape), the top portion, the side surface, the shape of the valley, such as curves, straight lines, a combination such as any. 但し、谷部は少なくとも貼着時は空気抜け層として、空気を逃がす道を作る必要がある事から、散発的に点在していたのでは、用を成さない。 However, at least stuck when the valley is as an air escape layer, from the fact that there is a need to create a way to escape the air, than had been sporadically dotted with, not make use. この為、谷部は、空気の逃げ道が出来る様に水平面内で連続している、つまり「溝状」を成すのが好ましい。 For this reason, the valley is continuous in the horizontal plane as can escape of air, preferably in other words to form a "groove-like". 谷部の連続性は、最低限、貼着時に空気が逃げ得る程度の距離(少なくとも5mm以上、より好ましくは10mm以上)は連続しているのが好ましいが、連続部分の終端での空気の抱き込みを回避する点で、より好ましくは、粘着シートの全水平面に亘って端から端まで連続しているのが良い。 Continuity of the valley, the minimum distance to the extent that air can escape when stuck (at least 5mm, more preferably at least 10 mm) is preferably continuous, embracing of the air at the end of the continuous portion in terms avoiding Inclusive, more preferably, it is good are continuous from the edge over the entire horizontal surface of the adhesive sheet to the end.
【0017】 [0017]
次に、凸状体2aの水平面での水平断面形状は、例えば、三角形、四角形、五角形、六角形等の正多角形を含む多角形、円形、楕円形、或いは有限幅で無限長又は有限長の線形状(直線や曲線)等であり、(垂直面での)垂直断面形状は、台形、半円形、半楕円形、三角形等である。 Next, the horizontal sectional shape of a horizontal plane of the convex body 2a is, for example, triangular, square, pentagonal, polygonal including regular polygon such as a hexagon, a circle, an ellipse, or an infinite length or of finite length in a finite width a line shape (straight line or curve) or the like, the vertical cross-section (in the vertical plane), trapezoidal, semi-circular, semi-elliptical, a triangular, or the like. また、各凸状体の水平面での水平断面形状は、不揃いであっても良い。 The horizontal sectional shape of a horizontal plane of the convex body may be irregular.
また、凸状体の水平面内での配置は、格子状等と規則的に配列しても良いし、不規則に配置しても良い。 The arrangement in the horizontal plane of the convex body may be lattice-like shape and regularly arranged, may be irregularly arranged.
一方、谷部の形状は、凸状体の形状及びその配置に応じた形状となる。 On the other hand, the shape of the valley has a shape corresponding to the shape and arrangement of the convex body.
【0018】 [0018]
ところで、個々の凸状体2aの具体的な大きさは、用途によるが、通常、谷部谷底との高低差は3〜100μm、より好ましくは10〜100μmである。 Incidentally, the specific size of the individual convex body 2a, depending on the application, typically, the height difference between the valley valley is 3 to 100 m, more preferably 10 to 100 [mu] m. 該高低差が10μm未満、特に3μm未満であると十分な空気抜け容易性を確保できず、逆に100μm超過であると、たとえ、深さが深い谷部を設けたとしても、粘着剤層面の凹凸が貼着後も残り美観を損ない易い。 Less than the elevation difference is 10 [mu] m, especially not reserve enough air escape ease is less than 3 [mu] m, when is 100μm excess Conversely, even if the depth is provided a deep valley portion, the adhesive layer surface after the irregularities are adhered also likely to impair the remaining aesthetic.
【0019】 [0019]
なお、粘着剤層2が有する多数の凸状体2aは、図1の断面図で例示する如く、隣接する凸状体2a間の谷部2bが、その谷底部分の基材シート1側にも、粘着剤層2を成す構成の他、図示は省略するが、谷底部分の基材シート1側は、粘着剤層2が無い構成でも良い。 Incidentally, a large number of convex body 2a having the adhesive layer 2, as illustrated in the sectional view of FIG. 1, a valley portion 2b between the adjacent convex body 2a is, in the substrate sheet 1 side of the trough bottom other configurations constituting the pressure-sensitive adhesive layer 2, although not shown, the substrate sheet 1 side of the trough bottom may be a pressure-sensitive adhesive layer 2 is not configured. 但し、後者の場合は、多くの谷部でそうなると、隣接する凸状体同士が連続した粘着剤層で連結していないので、貼着後、粘着シートが不要になり粘着シートを剥離する際に、粘着剤層(凸状体)の一部が、粘着シートから脱落して被着体側に残って綺麗に剥がし難いという問題が起こることもある。 However, in the latter case, the so made in a number of valleys, so not connected with a convex-shaped body with adjacent continuous adhesive layer, after sticking, when the adhesive sheet is peeled off the adhesive sheet becomes unnecessary , a part of the pressure-sensitive adhesive layer (convex form), sometimes problems arise that fall off from the adhesive sheet cleanly peeled hardly remain in the deposition side. この点で、図1の如き前者の方が好ましい。 In this regard, preferably the former, such as FIG.
【0020】 [0020]
また、隣接する凸状体2a同士が連続した粘着剤層2で連結した図1の様な場合、粘着剤層2の凸状体2a部分のみを他の粘着剤層部分とは区別して形成しても良いが、区別せずに、凸状体2a部分も含めて全ての粘着剤層2部分を、同一粘着剤で一体的な連続層として形成するのが製造が容易な点で好ましい。 Moreover, if convex body 2a with adjacent in such Figure 1 coupled with a continuous pressure-sensitive adhesive layer 2, only the convex body 2a portion of the pressure-sensitive adhesive layer 2 is formed separately from the other pressure-sensitive adhesive layer portion and may, but without distinction, all of the pressure-sensitive adhesive layer 2 parts, including convex body 2a portion, preferably the point production is easy to form as an integral continuous layer of the same adhesive. その為には、後述する如き、粘着剤層の所望の表面凹凸形状とは逆凹凸形状の離型シートを用意し、これに粘着剤を塗工して粘着剤層を形成後、基材シートを積層すれば良い。 For this purpose, such as will be described later, after a release sheet prepared by coating a pressure-sensitive adhesive to the adhesive layer of the opposite concave-convex shape from the desired surface irregularities of the adhesive layer, a base sheet the may be laminated.
【0021】 [0021]
なお、粘着剤層(全体)の厚さ(凸状体の高さhとなる)は、用途に応じたものとすれば良く、10μm〜200μm程度である。 Incidentally, (a height h of the convex body) thickness of the pressure-sensitive adhesive layer (the whole) may be assumed depending on the application, is about 10 m to 200 m. 厚さが10μm未満であると、接着力(粘着力)が不十分となり、逆に200μm超過ではコスト高となる。 When the thickness is less than 10 [mu] m, the adhesive force (adhesive strength) becomes insufficient, and the cost becomes high at 200μm excess reversed.
【0022】 [0022]
〔粘着剤層の材料及び形成法〕 [Materials and method for forming the pressure-sensitive adhesive layer]
粘着剤層2は、その表面に上述した如き表面凹凸形状を有するものであるが、この様な粘着剤層の形成に用いる粘着剤としては、従来公知のものを用途に応じて適宜使用すれば良い。 Pressure-sensitive adhesive layer 2 are those having the above-mentioned such surface irregularities on the surface, as the adhesive used in formation of such a pressure-sensitive adhesive layer, be suitably used in accordance with the conventionally known applications good. 例えば、ゴム系粘着剤、アクリル系粘着剤、シリコーン系粘着剤等の粘着剤である。 For example, rubber-based adhesives, acrylic adhesives, a pressure-sensitive adhesive such as silicone adhesive.
【0023】 [0023]
また、上述所望の凹凸形状を表面に有する粘着剤層を形成する方法としては、特に限定されるものではないが、該凹凸形状とは逆凹凸形状の離型面を有する離型シートを用意して、該離型シート上に粘着剤層を、ロールコート等の公知の塗工法等によって形成するのが、該凹凸形状を容易に形成できる点で好ましい一方法である。 Further, as a method of forming an adhesive layer having on the surface of the above desired uneven shape is not particularly limited, prepared release sheet having a release surface opposite unevenness and concavo-convex shape Te, a pressure-sensitive adhesive layer on said release sheet, to form by a known coating method such as roll coat, a preferred method in that the concave-convex shape can be easily formed. 基材シートは、離型シート上に粘着剤層を形成して積層シートとした後、この積層シートの粘着剤層面に対して基材シートを貼り付けて積層することで、所望の粘着シートが得られる。 The base sheet, after forming an adhesive layer to form a laminated sheet on the release sheet, by laminating paste the substrate sheet against the adhesive layer surface of the laminated sheet, a desired pressure-sensitive adhesive sheet can get.
【0024】 [0024]
〔離型シート〕 [Release sheet]
次に、離型シート3としては、その離型面が平坦面の離型シートでも、使用することはできる(粘着剤層表面に所望の凹凸形状を形成した後で、離型シートを積層する場合で、粘着剤層の谷部と離型シート間には空気が存在する)。 Next, the release sheet 3, also with a release sheet for the release surface is a flat surface, after forming a desired uneven shape that can be used (pressure-sensitive adhesive layer surface, laminating a release sheet in case, there is air between the trough release sheet of the adhesive layer). しかし、離型シートとしては、粘着剤層表面の凹凸形状に対応した(該凹凸形状とは逆)凹凸形状を離型面に有する離型シートを用いるのが、好ましい。 However, as the release sheet, to use a release sheet having corresponding to the concavo-convex shape of the pressure-sensitive adhesive layer surface irregularities (contrary to the irregular shape) on the release surface, preferably. これによって、前記した如く、離型シート上に粘着剤層を塗工法等で形成することで、該粘着剤層表面に所望の凸状体による表面凹凸形状を容易に形成できる。 Thus, as mentioned above, the pressure-sensitive adhesive layer on the release sheet by forming in a coating method or the like can be easily formed a surface irregularity with the desired convex body pressure-sensitive adhesive layer surface. また、凸状体部分も含めて粘着剤層全体を一体的な連続層として形成できる。 Further, the total adhesive layer, including convex body portions can be formed as an integral continuous layer. しかも、粘着シートの保存時、或いは流通時や使用時等に於いて、凸状体による粘着剤層の表面凹凸が潰れず、その形状維持も容易となる。 Moreover, during storage of the adhesive sheet, or at the distribution time and use time, etc., is not crushed surface roughness of the pressure-sensitive adhesive layer formed by the convex body, the easier its shape maintained.
【0025】 [0025]
この様な離型面に所望の凹凸形状を設けた離型シートとしては、離型シートとして従来公知のシートに、エンボス加工等の従来公知の賦形手段を適用することで得られる。 Examples of the release sheet provided the desired uneven shape such release surface, the conventional sheet as the release sheet, obtained by applying the conventional shaping means such as embossing.
【0026】 [0026]
例えば、離型シートの材料としては、例えばポリエチレンテレフタレート等の樹脂シートや紙等のシートに、シリコーン樹脂、メラミン樹脂、ポリオレフィン系樹脂、或いは、ワックス等の離型剤を添加した樹脂等で離型層を積層したもの、或いは、ポリオレフィン系樹脂等のそれ自体が離型性を有する樹脂シート等である。 For example, as the material of the release sheet, for example, a sheet of the resin sheet or paper such as polyethylene terephthalate, silicone resins, melamine resins, polyolefin resins, or releasing agent releasing a resin or the like added with such wax a laminate of a layer, or per se such as polyolefin-based resin is a resin sheet having releasability.
なお、離型シートの厚みは、用途に応じたものとすれば良く、例えば20〜300μm程度である。 The thickness of the release sheet may be assumed depending on the application, for example, about 20 to 300 [mu] m.
【0027】 [0027]
離型シートの離型面を、所望の凹凸形状とするには、従来公知のエンボス加工を適用すれば良いが、エンボス加工としては、例えば、加熱されたシートにエンボス版としてエンボスローラを押圧して賦形する方法が代表的である。 The release surface of the release sheet, to a desired concave-convex shape may be applied to conventional embossing. The preferred embossing, for example, the embossing roller presses the embossing plate to the heated sheet how to shaping Te is typical. この他、樹脂シートや紙上への樹脂層の溶融塗工法による成膜時に、その冷却ローラの表面をエンボス面としたエンボスローラを用いる成膜同時賦形法等でも良い。 In addition, during the film formation by melt coating method of the resin layer of the resin sheet or paper, it may be deposited simultaneously shaping method using an embossing roller in which the surface of the cooling roller and the embossed surface. 或いは、樹脂層を溶融塗工法に代えて、紫外線や電子線等で硬化する電離放射線硬化性樹脂を用いてその塗工・硬化と同時に、硬化物としての樹脂層に賦形する方法でも良い。 Alternatively, instead of the resin layer to melt coating method, simultaneously with the coating and cured with an ionizing radiation-curable resin cured by ultraviolet rays or electron beams, or a method of shaping the resin layer as a cured product. また、スクリーン印刷等の公知の印刷法を利用した盛上げ印刷等によって、離型面に所望の凹凸形状を賦形しても良い。 Also, the thermographic printing using a known printing method such as screen printing, may be shaped to a desired uneven shape on the release surface.
なお、エンボス版に所望の凹凸形状を設ける方法は、カーボンティッシュ等を利用した多段エッチング法(特開平8−1770号公報等参照)、機械的な切削法、レーザ加工法等の公知の形成方法によれば良い。 A method of providing a desired uneven shape on the embossing plate is (see Japanese Patent Laid-Open No. 8-1770, etc.) carbon multistage etching using such tissue, mechanical cutting method, known forming method such as laser processing may According to the.
【0028】 [0028]
〔基材シート〕 [Substrate sheet]
基材シート1としては、従来公知のものを用途に応じて適宜採用すれば良い。 The substrate sheet 1 may be adopted appropriately in accordance with the conventionally known applications. 例えば、樹脂シート、金属箔、或いは、紙、不織布、織布、突板等の繊維質シート等、或いは、これら2種以上の積層シートや、樹脂含浸不織布等の様な複合シート等からなるシートである。 For example, a resin sheet, a metal foil, or paper, non-woven, woven, fibrous sheets such as veneer, or two or more of these or a laminated sheet, a sheet made of such a composite sheet such as a resin-impregnated nonwoven fabric is there. なお、樹脂シートは、透明(無着色、着色)、不透明、半透明等のシートを用いる。 The resin sheet is transparent (uncolored, colored) opaque, using a sheet of translucent or the like. なお、基材シートの厚みは、用途に応じたものとすれば良く、例えば、5〜500μm程度、通常は20〜300μm程度である。 The thickness of the base sheet may be one corresponding to the application, for example, about 5 to 500 [mu] m, is usually about 20 to 300 [mu] m.
【0029】 [0029]
〔その他〕 [Other]
なお、粘着シートには、必要に応じて適宜、絵柄や凹凸等による模様、印字、コード、記号、画像等による可視或いは不可視情報を、公知の印刷・塗工手段等により施した構成としても良い。 Incidentally, the pressure-sensitive adhesive sheet, as necessary, pattern due to the pattern or unevenness, etc., printing the code, symbols, visible or invisible information by the image or the like, may be configured subjected by such known printing-coating means . 通常、これらは基材シートの片面(表面或いは裏面)、或いは両面に対して施される。 Usually, these are one side of the substrate sheet (surface or back surface), or is performed on both sides. 絵柄等の模様を施したものは、建材用途にて化粧シートとして使用され得る。 Which was subjected to pattern such as pattern, it can be used as the decorative sheet in building materials. なお、模様とする絵柄には、全面着色等の全面ベタ模様もある。 Note that the picture to be patterned, is also entirely solid patterns such as entire surface coloration. また、不可視情報とは、例えば、蛍光インキや赤外線吸収インキの印刷等による紫外線や赤外線照射にて判読可能な模様や文字等の情報等である。 Further, the invisible information, for example, information such as patterns or characters legible ultraviolet ray or by infrared irradiation by printing fluorescent ink or IR absorbing ink.
【0030】 [0030]
また、粘着シートには、必要に応じて、各種機能性を付与した構成としても良い。 Further, the pressure-sensitive adhesive sheet, if necessary, may be configured to impart various functionalities. 機能性としては、例えば、耐摩耗性、耐擦傷性、耐汚染性、防曇性、反射防止性、帯電防止性、断熱性、抗菌性、電磁波シールド性等である。 The functionality, for example, abrasion resistance, scratch resistance, stain resistance, anti-fogging, anti-reflection properties, antistatic properties, heat insulation, antibacterial, an electromagnetic wave shielding property and the like. これらは、その機能に応じて、樹脂シート等の基材シート中に、それに必要な物質を添加するか、基材シート上に該物質或いは該物質を添加したインキや塗液等の層を形成する等して実現する。 These are formed according to the function, the base material in the sheet of the resin sheet, etc., it should be added the necessary material, a layer of ink and the coating liquid or the like with the addition of the substance or substance on a substrate sheet the like to be realized. 例えば、耐摩耗性や耐擦傷性等は、シリカ等の耐摩剤を、樹脂シート中に添加するか、該耐摩剤を含む塗液で基材シート表面に塗工形成するる。 For example, abrasion resistance and scratch resistance, etc., the abrasion agent such as silica, either added to the resin sheet, Ruru to form coating on the surface of the substrate sheet with a coating liquid containing a resistant friction agent.
【0031】 [0031]
【実施例】 【Example】
以下、実施例及び比較例により本発明を更に詳述する。 Hereinafter, further details of the invention are illustrated by the examples and comparative examples.
【0032】 [0032]
〔実施例1〕 Example 1
図1の如き粘着シート10を次の様にして作製した。 Was prepared such pressure-sensitive adhesive sheet 10 of FIG. 1 in the following manner.
先ず、離型シートとして、厚み150μmのポリプロピレン系樹脂シートの離型面とする面に対して、エンボスローラを用いて、所望の粘着剤層表面凹凸形状と逆凹凸形状の凹凸を形成して、離型シート3を得た。 First, as the release sheet, against the surface to release surface of the polypropylene resin sheet having a thickness of 150 [mu] m, using an embossing roller, to form irregularities of a desired pressure-sensitive adhesive layer surface irregularity reverse uneven shape, thereby obtaining a release sheet 3.
【0033】 [0033]
次に、上記離型シート3の凹凸が形成された離型面に対してアクリル系粘着剤を、離型面の凹部を完全に充填し更にその上にも粘着剤層が覆う様に塗布し、加熱乾燥して粘着剤層2を形成して、離型シートと粘着剤層とが積層された積層シートを得た。 Next, an acrylic pressure-sensitive adhesive against a release surface irregularities of the release sheet 3 is formed, and completely fills the recess of the release surface be coated so as to cover the pressure-sensitive adhesive layer thereon further and heat dried to form an adhesive layer 2, to obtain a laminated sheet with the release sheet and the adhesive layer is laminated.
【0034】 [0034]
そして、上記積層シートの粘着剤層2の面に、基材シート1として厚さ50μmのポリエチレンテレフタレートシートをラミネータを用いて貼り合わせて、図1の断面図の如き、粘着剤層2表面に高さの異なる多数の凸状体2aを有する、所望の粘着シート10を得た。 Then, the surface of the adhesive layer 2 of the laminated sheet, a polyethylene terephthalate sheet having a thickness of 50μm as the substrate sheet 1 by bonding with a laminator, such as the cross-sectional view of FIG. 1, a high pressure-sensitive adhesive layer 2 surface has a number of convex body 2a having different is, to give the desired pressure-sensitive adhesive sheet 10.
【0035】 [0035]
この粘着シートの粘着剤層2は、高さhが35μmと50μm(各々谷部谷底との高低差15μmと30μm)との異なる高さを有する多数の水平断面形状が底面部分で縦横2mmの四角錐台類似の角が丸まった凸状体2aが、隣接する凸状体同士間の谷部谷底に基材シートが露出せず全ての凸状体同士が粘着剤層で連続した表面凹凸を有するものであった。 Pressure-sensitive adhesive layer 2 of the adhesive sheet, the height h is 35μm and 50μm Aspect 2mm in a number of horizontal cross-sectional shape base part having a different height (and 30μm height difference 15μm and each valley valley) and four convex body 2a having rounded corners truncated pyramid similar, having all convex bodies not exposed substrate sheet valley valley between adjacent convex body to each other continuous surface irregularities in the adhesive layer It was those.
【0036】 [0036]
〔比較例1〕 Comparative Example 1
実施例1に於いて、エンボス時の離型シートの離型面の凹凸形状を変更して、全ての凸状体の高さhを同一(h=45μm、谷底との高低差25μm)とした他は、実施例1と同様して、粘着シートを作製した。 In Example 1, by changing the unevenness of the release surface of the release sheet during the embossing was the height h of all the convex body and the same (h = 45 [mu] m, height difference 25μm and valley) others, in the same manner as in example 1, to prepare a pressure-sensitive adhesive sheet.
【0037】 [0037]
〔性能評価〕 (Performance Evaluation)
上記実施例及び比較例の粘着シートを、それぞれ、透明ガラス板にゴム製スキージで軽くしごいて空気を抜きながら仮貼りした後、強く押し付けて本接着してみた。 The pressure-sensitive adhesive sheet of Examples and Comparative Examples, respectively, after squeezes lightly with a rubber squeegee was temporarily attached while deflated a transparent glass plate, tried to present bonded strongly pressed. その結果、実施例及び比較例共に空気残り無く空気抜け容易性は良好であった。 As a result, it was good air remaining without air escape ease in Examples and Comparative Examples both. しかし、比較例1は本接着で強固な接着が得られなかった。 However, Comparative Example 1 did not firm adhesion is obtained in this adhesion. これに対して、実施例1は本接着で強固な接着が得られ、また表面(凹凸)状態も良好であった。 In contrast, Example 1 strong adhesion is obtained in this adhesive, and the surface (uneven) state was also good.
【0038】 [0038]
【発明の効果】 【Effect of the invention】
(1)本発明の粘着シートによれば、空気抜け容易性が確保される上、しかも、軽い圧力で仮接着による位置決めができ、更に強い圧力で十分に強固な本接着ができる。 (1) According to the pressure-sensitive adhesive sheet of the present invention, on the air escape easily is ensured, moreover, can be positioned by the temporary adhesive at light pressure, it is sufficiently strong the adhesive further under strong pressure.
(2)更に、粘着剤層の表面に、該表面の凹凸形状とは逆凹凸形状の離型面を有する離型シートが積層されて成る構成とすれば、粘着剤層への凸状体の形成が容易となる上、更には、粘着シート保存時、流通時、使用時等に於いて、凸状体による表面凹凸の形状維持が容易となる。 (2) Further, the surface of the pressure-sensitive adhesive layer, the irregular shape of the surface with the configuration of release sheet having a release surface opposite irregularities are laminated, the convex body to the pressure-sensitive adhesive layer upper forming is facilitated, further, when the pressure-sensitive adhesive sheet storage, during distribution, in the use or the like, the shape maintenance of the surface irregularities due to the convex body is facilitated.
【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS
【図1】本発明による粘着シートを概念的に説明する断面図。 Sectional view conceptually illustrating the pressure-sensitive adhesive sheet according to the invention; FIG.
【図2】従来の粘着シートの一例を示す斜視図。 Figure 2 is a perspective view showing an example of a conventional adhesive sheet.
【符号の説明】 DESCRIPTION OF SYMBOLS
1 基材シート2 粘着剤層2a 凸状体2b 谷部3 離型シート10 粘着シート30 粘着シート31 基材シート32 粘着剤層32a 凸状体h 凸状体の高さ The height of the first substrate sheet 2 pressure-sensitive adhesive layer 2a convex member 2b valley 3 release sheet 10 adhesive sheet 30 adhesive sheet 31 base material sheet 32 ​​adhesive layer 32a convex body h convex body

Claims (2)

  1. 基材シート上に粘着剤層が設けられた粘着シートにおいて、 The adhesive sheet where the pressure-sensitive adhesive layer is provided on a substrate sheet,
    該粘着剤層はその表面から外方に突出する多数の凸状体を有し、且つ高さの異なる多数の凸状体が混在している、粘着シート。 Adhesive layer has a number of convex body which projects outwardly from the surface, and a number of different convex body height are mixed, the adhesive sheet.
  2. 粘着剤層の表面に、該表面の凹凸形状とは逆凹凸形状の離型面を有する離型シートが積層されて成る、請求項1記載の粘着シート。 The surface of the pressure-sensitive adhesive layer, composed of a release sheet having a release surface opposite irregularities are laminated with irregularities of the surface, the pressure-sensitive adhesive sheet according to claim 1, wherein.
JP2002285235A 2002-09-30 2002-09-30 Pressure-sensitive adhesive sheet Pending JP2004115766A (en)