JP2003280049A - Functional fiber and textile using the same - Google Patents

Functional fiber and textile using the same

Info

Publication number
JP2003280049A
JP2003280049A JP2002086726A JP2002086726A JP2003280049A JP 2003280049 A JP2003280049 A JP 2003280049A JP 2002086726 A JP2002086726 A JP 2002086726A JP 2002086726 A JP2002086726 A JP 2002086726A JP 2003280049 A JP2003280049 A JP 2003280049A
Authority
JP
Japan
Prior art keywords
functional
woven
fibers
fiber
knitted fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
JP2002086726A
Other languages
Japanese (ja)
Inventor
Osamu Shinoura
Noriyuki Yasuda
徳行 安田
治 篠浦
Original Assignee
Tdk Corp
Tdk株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tdk Corp, Tdk株式会社 filed Critical Tdk Corp
Priority to JP2002086726A priority Critical patent/JP2003280049A/en
Publication of JP2003280049A publication Critical patent/JP2003280049A/en
Application status is Withdrawn legal-status Critical

Abstract

<P>PROBLEM TO BE SOLVED: To provide a functional fiber whose external appearance such as the color and pattern can be changed at any time as a user desires and to provide a textile which uses the functional fiber. <P>SOLUTION: A dispersion system obtained by dispersing migrating particles 4 in a dispersant solvent 3 is charged in a transparent hollow yarn 2. The distribution state of the migrating particles 4 is changed by applying a voltage and a magnetic field to change the outward appearance as needed. Function fibers or a functional fiber and a nonfunctional fiber are woven to obtain the textile having a display function. <P>COPYRIGHT: (C)2004,JPO

Description

【発明の詳細な説明】 【0001】 【産業上の利用分野】本発明は、色や模様等の外観を随時変化させることが可能な機能性ファイバー及び機能性ファイバーを用いた織編物に関する。 BACKGROUND OF THE INVENTION [0001] BACKGROUND OF THE INVENTION This invention relates to woven or knitted fabric with functional fibers and functional fibers capable of changing the appearance of such colors and patterns from time to time. 特に電圧作用により可逆的に瞬時に、その色を変化させることが可能な機能性ファイバー及び機能性ファイバーを用いた織編物である。 Instantaneously especially reversibly by voltage effect and is woven or knitted fabric with functional fibers and functional fibers capable of changing its color. 本発明の織編物は、衣料素材、壁紙素材等として広く利用可能なだけでなく、局所的に電圧を印加することで、所望のパターン、文字等も表示可能な表示装置としても使用可能な高機能織編物である。 Woven or knitted fabric of the present invention, clothing materials, not only widely available as wallpaper material or the like, by applying the locally voltage, a desired pattern, such as characters even higher that can also be used as a viewable display unit it is a functional woven or knitted fabric. 【0002】 【従来の技術】衣料素材、壁紙素材等として広く利用可能な織編物の高機能化が進んでいるが、その模様、色彩を変化させることは困難であった。 [0002] clothing material, but is progressing sophistication of widely available woven or knitted fabric as wallpaper material, etc., the pattern, it has been difficult to change the color. 【0003】登録実用新案公報第3020011号には、明るい場所では普通に着用出来、暗い場所でブラックライトからの光を受けて明るい所では見られなかった模様・記号・文字等を鮮やかな発光状態で浮き出させることが出来、着替えの必要をなくし、暗い場所での演出効果を高める変化性を持った衣服が開示されている。 [0003] The registered utility model in the Publication No. 3020011, bright normally be worn in places, bright light-emitting state pattern, symbols, characters or the like was not seen at the bright receives light from a black light in a dark place in embossed so it is possible to eliminate the need for change of clothes, discloses garments having a variability to increase the stage effects in a dark place. 【0004】特開平11−43864号公報には、 [0004] in Japanese Unexamined Patent Publication No. 11-43864,
(イ)特定の電子供与性近赤外吸収性有機化合物、 (B) specific electron donating near infrared absorbing organic compound,
(ロ)前記有機化合物に対して電子受容性である化合物、(ハ)前記(イ)、(ロ)成分による電子授受反応を特定温度域において可逆的に生起させる反応媒体である化合物を内包させた微小カプセルを合成樹脂に分散して形成した可逆熱変色層を設けた可逆熱変色性吸熱性布開示されている。 Compounds which are electron accepting property with respect to (ii) the organic compound with encapsulating (c) the (i), the compound is a reaction medium which reversibly occurs in a specific temperature range the electron transfer reaction with component (ii) the microcapsules are reversible thermochromic endothermic fabric disclosed is provided a reversible thermochromic layer formed by dispersing a synthetic resin. 【0005】一方、特許2551783号公報には、図7に示すように、対向する基板31、32のそれぞれの表面に形成された電極33、34間に有機溶媒からなる分散溶媒35と電気泳動粒子36とが封入されたマイクロカプセル37を有する構造の電気泳動表示装置が開示されている。 On the other hand, Japanese Patent 2551783 discloses, as shown in FIG. 7, the dispersion solvent 35 and electrophoretic particles consisting of organic solvents between each electrode formed on the surface 33, 34 of the opposing substrate 31 36 and the electrophoretic display device having the structure having microcapsules 37 that is sealed is disclosed. この電気泳動表示装置では、少なくとも一方が透明な一組の対向電極33、34間に電気泳動粒子36を含む分散溶媒35を封入し、該電極33、34間に印加した表示制御用電圧の作用下に分散系内の電気泳動粒子36の分布状態を変えることによって光学的反射特性に変化を与えて所要の表示動作を行わせる電気泳動表示装置であり、着色した分散溶媒35中に分散溶媒3 In the electrophoretic display device, at least one of the dispersion solvent 35 containing electrophoretic particles 36 enclosed between the transparent one pair of opposing electrodes 33 and 34, the action of the display control voltage applied between the electrodes 33 and 34 an electrophoretic display device to perform the required display operation giving a change in optical reflection properties by varying the distribution state of the electrophoretic particles 36 in the dispersion below, dispersed in the colored dispersion solvent 35 solvent 3
5と光学的特性の異なる少なくとも一種類の電気泳動粒子36を分散させた分散系を封入した多数のマイクロカプセル37を形成し、これらのマイクロカプセル37を上記電極33、34間に配装するように構成したものである。 5 a plurality of microcapsules 37 dispersed system was encapsulated with different dispersed at least one kind of the electrophoretic particles 36 having optical characteristics is formed, these microcapsules 37 to HaiSo between the electrodes 33 and 34 it is those that you have configured. 【0006】 【発明が解決しようとする課題】しかし、例えば登録実用新案公報第3020011号や特開平11−4386 [0006] The present invention is to provide, however, for example, Registered Utility Model No. 3020011 and JP-A-11-4386
4号公報に記載のような従来の色彩や模様が変化する織編物等は、外部からの光照射や温度等により変化するものであり、使用者が任意に変えられるものではなかった。 4 No. woven or knitted fabric or the like conventional color or pattern is changed as described in Japanese is to change by light irradiation, temperature, etc. from the outside, the user was not be arbitrarily changed. 【0007】これに対して、特許2551783号公報に記載され、かつ図7に示すように、マイクロカプセル37に分散系を封入した電気泳動表示装置は、もちろん任意に表示を変えることが可能であるが、2枚の基板3 [0007] In contrast, as described in Japanese Patent No. 2551783, and as shown in FIG. 7, the electrophoretic display device encapsulating dispersion in microcapsule 37 is capable of changing the course arbitrarily displayed There, the two substrates 3
1、32間にマイクロカプセル37を挟み込むために厚さが厚くなり、柔軟性を保つことが困難であり、かつ高価なものであり衣料素材、壁紙素材等として広く使用できるものではなかった。 The thickness becomes thicker in order to sandwich the microcapsules 37 between 1.32, it is difficult to maintain the flexibility and is intended expensive clothing materials, were not widely be used as wallpaper material or the like. 【0008】本発明の目的は、使用者が希望に応じて随時、色、模様の外観を変化させることが可能な機能性ファイバー及びこの機能性ファイバーを用いた織編物を提供することである。 An object of the present invention is that the user provides a woven or knitted fabric with at any time, color, functional fibers capable of changing the appearance of the pattern and the functional fibers as desired. 【0009】また、本発明の目的は、衣料素材、壁紙素材等として広く利用可能なだけでなく、局所的に電圧等を印加することで、所望のパターン、文字、画像、動画等も表示可能な表示装置としても使用可能な柔軟性のある高機能織編物を提供することである。 Another object of the present invention, clothing materials, not only widely available as wallpaper material or the like, by applying the locally voltage, etc., the desired pattern, text, image, and video, etc. can be displayed to provide a high performance textile fabric also a usable flexibility as Do display device. 【0010】 【課題を解決するための手段】本発明の機能性ファイバーは、透明な中空糸の内部に、分散溶媒中に泳動粒子を分散させた分散系を充填し、前記泳動粒子の分布状態を変化させることにより所要の外観変化を行わせることが可能であることを特徴とする。 [0010] Functional fiber SUMMARY OF to the present invention, the interior of the transparent hollow fibers, filled with a dispersion prepared by dispersing electrophoretic particles in a dispersion solvent, the distribution state of the electrophoretic particles characterized in that it is possible to perform the necessary changes in appearance by changing the. 【0011】本発明の機能性ファイバーにおいて、前記分布状態変化は電圧により発生することを特徴とする。 [0011] In the functional fibers of the present invention, the distribution state change is characterized by generating by a voltage. 【0012】本発明の機能性ファイバーを用いた織編物は、透明な外壁を有する中空糸の内部に、分散溶媒中に泳動粒子を分散させた分散系を充填し、前記泳動粒子の分布状態を変化させることにより所要の表示動作を行わせることが可能な機能性ファイバーを編み上げた構造を有することを特徴とする。 [0012] Functional woven using fiber knitted of the present invention, the inside of the hollow fiber having a transparent outer wall, filled with a dispersion prepared by dispersing electrophoretic particles in a dispersion solvent, the distribution of the electrophoretic particles It characterized by having a structure braided functional fibers capable of causing the required display operation by changing. 【0013】また、本発明の機能性ファイバーを用いた織編物は、透明な中空糸の内部に、分散溶媒中に泳動粒子を分散させた分散系を充填し、前記泳動粒子の分布状態を変化させることにより所要の表示動作を行わせることが可能な機能性ファイバーを横糸および/または縦糸として編み上げた構造を有することを特徴とする。 Furthermore, the functional woven using fiber knitted of the present invention is transparent in the interior of the hollow fibers, filled with a dispersion prepared by dispersing electrophoretic particles in a dispersion solvent, changing the distribution state of the electrophoretic particles It characterized by having a braided structure the functional fibers capable of causing the required display operation by the weft and / or warp. 【0014】また、本発明の機能性ファイバーを用いた織編物は、前記分布状態変化は電圧(電界、電場)により発生することを特徴とする。 [0014] woven or knitted fabric with functional fibers of the present invention, the distribution state change is characterized by generating by a voltage (electric field, electric field). 【0015】また、本発明の機能性ファイバーを用いた織編物は、前記機能性ファイバーを編み上げた構造の少なくとも片面に電圧印加のための電極を設けたことを特徴とする。 Further, woven or knitted fabric with functional fibers of the present invention is characterized by comprising an electrode for voltage application on at least one surface of the structure braided said functional fibers. 【0016】また、本発明の機能性ファイバーを用いた織編物は、前記機能性ファイバーを編み上げた織編物の隙間に充填材を充填し、該充填材を充填した織編物の両面を平滑化し、該平滑化した面に電極を設けたことを特徴とする。 Further, woven or knitted fabric with functional fibers of the present invention, by filling the filler into the gap woven or knitted fabric of braided said functional fibers, smooth on both sides of the filled textile fabric the filler, characterized by providing an electrode on the smoothed surface. 【0017】 【発明の実施の形態】以下、本発明について、さらに詳細に説明する。 DETAILED DESCRIPTION OF THE INVENTION Hereinafter, the present invention will be described in detail. 図1は、本発明の機能性ファイバー1の概略斜視図である。 Figure 1 is a schematic perspective view of a functional fiber 1 of the present invention. 該機能性ファイバー1は、透明材料からなる中空糸2の内部に分散溶媒3と泳動粒子4が内包されている長尺のファイバーである。 The functional fibers 1 is a fiber elongated dispersion solvent in the interior of the hollow fiber 2 made of a transparent material 3 and electrophoretic particles 4 are included. なお、ファイバーとは単繊維を意味し、繊維を束ねたものが糸で、糸を織り上げたものを織編物と定義されることもあるが、本発明においては編み上げる前段階の状態の糸をファイバーとする。 Note that the fiber means single fiber, a bundle of fibers in the yarn, it is sometimes defined as knitted woven those woven yarn, fiber yarn pre-stage of the conditions in which knit in the present invention to. 【0018】前記中空糸2の断面は円に限らず楕円、四角形あるいは、織物用の糸として公知がその他の形状とすることが出来る。 The cross section of the hollow fiber 2 is elliptical not limited to circles, squares or known can be other shapes as yarns for textile use. また可撓性のある材料を中空糸材料として用いることで作成後に変形することも可能である。 It is also possible to deform after creating by using a flexible material as the hollow fiber material. 【0019】本発明に用いるファイバーは直径が1〜1 The fibers used in the present invention is a diameter 1 to 1
000μm、ファイバー外壁の厚さが0.01〜300 000Myuemu, the thickness of the fiber outer wall 0.01 to 300
μmで、ファイバー直径と外壁厚さの比が100:1〜 In [mu] m, the ratio of fiber diameter and the outer wall thickness is 100: 1
3:1であることが好ましい。 3: 1. いすれも前記範囲未満ではファイバー強度が不足し、前記範囲を超えると表示特性が劣化する。 Isure be insufficient fiber strength is less than the above range, the display characteristic over that range is deteriorated. 【0020】予め、中空糸2の材料を着色しておくことや、中空糸2の表面に、さらに有色透明材料層を形成して着色することも可能である。 [0020] previously, it and to keep coloring the hollow fiber 2 material, on the surface of the hollow fiber 2, can be further colored by forming a colored transparent material layer. 【0021】該機能性ファイバー1を得るには、最初に中空糸2を作成し、その後に分散溶媒3に泳動粒子4を含ませた分散系をファイバー中空部に充填する中空糸使用でも良いが、ファイバーの壁厚が厚くなり、かつ工程が増加し、コスト高という欠点を有する。 [0021] To obtain the functional fibers 1 first creates a hollow fiber 2, but the subsequent dispersion moistened with electrophoretic particles 4 in the dispersion solvent 3 may be hollow fibers used to fill the fiber hollow portion , the wall thickness of the fiber becomes thicker, and steps increases, with the disadvantage of high cost. このため本発明の機能性ファイバーは分散系を細孔から押し出しながら、その外周部に樹脂を形成する一体押出形成(共押し出し法)により作成された機能性ファイバーが特に好ましい。 While extruding the functional fiber dispersion of the for the present invention from the pores, functional fibers created by integrally extrusion forming (co-extrusion) of forming a resin on the outer periphery thereof are particularly preferred. さらに可塑性のある壁材料を用い、分散系を圧力を印加しながら充填することで、より壁厚を薄くすることが可能である。 Further using a wall material that is plastic, a dispersion by filling while applying a pressure, it is possible to reduce the more the wall thickness. その際に作成された直後のファイバー自体も長手方向に張力を印加し引き延ばしながら行うと壁厚を薄くすることに上でより効果的である。 It is more effective on the thinning the wall thickness is performed while stretching to apply a fiber itself tension in the longitudinal direction immediately after being created at that time. 可塑性のある壁材料とは常温においての可塑性だけでなく、充填の際の適度の加熱により可塑性を有するようになる熱可塑性樹脂を好ましく用いることが出来る。 The wall material with plasticity as well plasticity at room temperature, can be preferably used a thermoplastic resin so as to have a plasticity by moderate heating during filling. 【0022】中空糸を用いる場合に、中空糸は公知の各種の方法により作成可能である。 [0022] When using a hollow fiber, the hollow fiber can be produced by various known methods. 代表的な方法が共押出法である。 Representative methods are coextrusion. これは適当な溶媒または溶媒系に溶解された重合体と不活性であり得るかまたは凝固液体あるいは沈殿流体であり得る流体との共押出する。 This co-extrusion of the fluid which may be possible or coagulation liquid or precipitation fluid in dissolved polymer and inert in a suitable solvent or solvent system. すなわち、重合体溶液は、円形オリフィスを通して押出される。 That is, the polymer solution is extruded through a circular orifice. 不活性流体または凝固流体または沈殿流体は円形スリットの中心の穴から押出される。 Inert fluid or solidified fluids or precipitated fluid is extruded through the hole in the center of the circular slit. この流体は、中心流体または中心媒質と呼ばれる。 This fluid is referred to as a central fluid or central medium. 共押出物を、数分の1秒〜数秒の範囲の短時間大気中を走行させることが普通の慣例であり、しかも得られた中空繊維膜の性質はこの空気間隔の長さによって影響される。 The coextrudate is a common practice that for running short in the air in the range of a fraction of a second to several seconds, yet the properties of the hollow fiber membrane obtained is affected by the length of the air gap . 続けて、共押出物を中心流体と同一または異なる若干の流体を通して延伸するのが普通である。 Subsequently, it is common to draw through coextrudate the center fluid and the same or slightly different fluids. 中心流体としては、水や窒素ガスが一般的に広く使用されている。 The center fluid, water and nitrogen gas is commonly and widely used. また、射出成形法等による作成も可能である。 Further, it is also possible to create by injection molding or the like. 【0023】一体押出形成の場合には上記共押出法において中心流体として、後述の分散系を用いれば良い。 [0023] As center fluid in the co-extrusion method when integrated extrusion forming, may be used dispersion described below. そして、もちろん中空糸の完成と同時に分散系の充填が完了した機能性ファイバーが得られる。 And, of course functional fibers completed simultaneously with the filling of the dispersion of the hollow fiber is completed is obtained. 【0024】なお、中空糸2の内壁に、さらに表面コーティング層を形成することも可能である。 [0024] Incidentally, the inner wall of the hollow fiber 2, it is also possible to further form a surface coating layer. このコーティング層にフッ素系樹脂等を用いることで、泳動粒子4の内壁への付着を効果的に防止することが出来る。 By using a fluorine-based resin or the like to the coating layer, it can be prevented from adhering to the inner wall of the electrophoretic particles 4 effectively. 【0025】「溶媒」本発明に用いる分散溶媒3は、芳香族炭化水素類、脂肪族炭化水素類、ハロゲン化炭化水素類や、シリコンオイルなどの油脂類などを単独または適宜混合したものや合成樹脂、合成ワックスなどの合成物や、天然ワックス、シリコーンオイル、フッ素オイル等の公知の溶液化合物などを用いることができる。 The dispersion solvent 3 for use in the present invention, "solvent", aromatic hydrocarbons, aliphatic hydrocarbons, halogenated hydrocarbons and, which like fats and oils such as silicone oil mixed alone or as appropriate and synthetics resin, composite or the like synthetic waxes, natural waxes, silicone oils, such known solutions compounds such as fluorine oil can be used. 上記したうちでは、好ましくは直鎖アルキルベンゼン構造を有する液体分散溶媒、たとえばn−アミルベンゼン、n Among the above-mentioned, preferably a liquid dispersion solvent having a linear alkyl benzene structures, for example, n- amyl benzene, n
−ヘキシルベンゼン、n−ヘプチルベンゼンおよびn− - hexyl benzene, n- heptyl benzene and n-
オクチルベンゼン等あるいはフッ素オイルを用いることができる。 It can be used octyl benzene or fluorine oil. 【0026】分散溶媒は、染料を添加し着色することも可能で、染料としては、アントラキノン類やアゾ化合物類等の油溶性染料などの染料等を用いることができる。 The dispersion solvent, it is also possible to added dye coloring, as the dye, a dye can be used, such as such as oil-soluble dyes such as anthraquinone and azo compounds. 【0027】「泳動粒子」泳動粒子4は、酸化チタン、 [0027] "electrophoretic particles" electrophoretic particles 4, titanium oxide,
カーボンブラック、紺青又はフタロシアニングリーンや周知のコロイド粒子のほか、種々の有機および無機顔料、染料、金属粉、ガラスあるいは樹脂等の微粉末などを使用できる。 Carbon black, in addition to the iron blue or phthalocyanine green and well-known colloidal particles, various organic and inorganic pigments, dyes, metal powders, and the like fine powders such as glass or resin. これらの内の1種類のみを用いることも可能であり、2種類以上、特に白粒子、黒粒子を用いること、赤、青、緑の3色を用いること、さらには白、 It is also possible to use only one kind of these or two or more, in particular the use white particles, black particles, red, blue, using the green three colors, more white,
黒、赤、青、緑の5色の粒子を用いることも可能である。 Black, red, blue, it is also possible to use the green of the five colors of the particles. 例えば、白黒2粒子を用いた場合に、その帯電を正負と逆に設定することで、外部電圧により白粒子は引きつけられ、黒粒子は反発して遠ざかる、あるいは、その逆の状態となることで白黒の色変化が可能となる。 For example, in the case of using the black and white particles, by setting the charged polarity opposite, the white particles are attracted by an external voltage, the black particles away repelled, or by the state of the opposite the color change of the black-and-white becomes possible. 図4 Figure 4
は、帯電を正負にした黒粒子4a、白粒子4bを用いた場合を示している。 The black particles 4a in which the charged positive and negative, shows the case of using the white particles 4b. 【0028】また、電気泳動粒子4の粒径は、0.01 [0028] In addition, the particle size of the electrophoretic particles 4, 0.01
〜10μmが好ましい。 ~10μm is preferable. 粒径をこのような範囲とすることで好適に分散させることができ、移動速度も実用上問題のない速度とすることが出来る。 Particle size to be able to such a range that it is suitably dispersed, moving speed may be no practical problem speed. 【0029】また、泳動粒子4の表面電荷量の制御や分散性を高める目的で、ステアリン酸、オレイン酸、リノール酸、ジオクチルスルホコハク酸ナトリウム、ポリエチレンオキシド、ポリメチルメタクリレート、シランカップリング剤、チタンカップリング剤、シランカップリング剤等を添加してもよい。 Further, for the purpose of enhancing control and dispersibility of the surface charge of the electrophoretic particles 4, stearic acid, oleic acid, linoleic acid, sodium dioctyl sulfosuccinate, polyethylene oxide, polymethyl methacrylate, a silane coupling agent, titanium coupling coupling agent, a silane coupling agent or the like may be added. 【0030】「中空糸」中空糸2を構成する合成樹脂としては連続生産での安定品質と経済的に量産し得ることにおいて熱可塑性合成樹脂が好ましく、例えば、エチレン、プロピレン、1−ブテン、4−メチル−ペンテンなどのα−オレフィンの単独重合体もしくは相互共重合体またはこれらのα−オレフィンと他のモノマ−の共重合体からなるポリオレフィン系合成樹脂のほか、ナイロン等のポリアミド系合成樹脂、ポリエチレンテレフタレ− The thermoplastic synthetic resin is preferable in that it can stabilize quality and economical mass production in continuous production as the synthetic resin that constitutes the "hollow fiber" hollow fiber 2, for example, ethylene, propylene, 1-butene, 4 - methyl - homopolymer or mutual copolymer or these α- olefin and other monomers of the α- olefin such as pentene - copolymers other polyolefin synthetic resin made of polyamide-based synthetic resin such as nylon, polyethylene terephthalate -
ト等のポリエステル系合成樹脂、ポリ塩化ビニル系合成樹脂、ポリ塩化ビニリデン−ビニル共重合体系合成樹脂等が挙げられ、これら2種類以上をブレンドしたものであっても良い。 Polyester synthetic resin bets such as polyvinyl chloride-based synthetic resin, polyvinylidene chloride - vinyl copolymer synthetic resin and the like, or may be a blend of two kinds or more. またオンラインで重合可能な紫外線硬化樹脂等も好ましく用いることができる。 Also it is possible to use an ultraviolet curable resin or the like is also preferably can be polymerized online. 【0031】また、樹脂組成物には、可塑剤、滑剤、紫外線吸収剤、帯電防止剤、難燃剤、着色剤、充填剤等の添加剤を所定量添加配合することは任意である。 Further, the resin composition, plasticizers, lubricants, ultraviolet absorbers, antistatic agents, flame retardants, colorants, it is optional to predetermined amounts added compounding additives such as fillers. 【0032】「織り方」本発明の機能性ファイバーを別途準備した基体上に平面上に密に一列に並べることも可能であるが、細いファイバーを規則正しく並べることは工業上、極めて困難であり、かつ基体の存在により薄型化、可撓性が損なわれる。 [0032] "weave," but it is also possible to densely arranged in a row in the separately prepared on a plane on the substrate the functionality of fibers of the present invention, by arranging the thin fibers regularly is industrial, is very difficult, and thin, flexible is impaired by the presence of the substrate. このため本発明においては、 Therefore, in the present invention,
基体を用いないでファイバーを編み上げた構造が特に好ましい。 Structure braided fiber without using the substrate is particularly preferred. 【0033】本発明の機能性ファイバーを用いた織編物は、前述の機能性ファイバーを編み上げたものをいう。 The woven or knitted fabric with functional fibers of the present invention refers to those braided functional fiber described above.
織り方としては、機能性ファイバーを縦糸および横糸に用いて編み上げたものが一般的である。 The weave, which functional fiber braided with the warp and weft are common. 【0034】ここで、織編物とは狭義の織物ことでは無く、広い意味の、糸(ファイバー)が組み合わされた、 [0034] Here, the woven or knitted fabric is not is that narrow sense of the fabric, of a broad sense, the thread (fiber) are combined,
平面状の構造体をいう。 It refers to the planar structure. 例えば、縦糸と横糸は必ずしも直角に交差するとは限定されず、両者が傾斜し交差している場合等も含まれる。 For example, warp and weft are not limited necessarily intersect at right angles, includes a case or the like where both are crossed inclined. また、「編む」と「織る」は異なる概念とする定義もあるが、本発明においてはファイバーを組み上げて平面構造を作成する手段として同じ意味として用いる。 Further, "weave" and "weaving" is also defined to be different concepts, in the present invention is used as the same meaning as a means of creating a planar structure assembled fibers. 【0035】よって織り方に、特に限定はなく平織り、 [0035] Therefore, to weave, plain weave is not particularly limited,
綾織、朱子織の3つの代表的な織り方はもちろん、各種の変化や応用、組み合わせによって出来上がる平面構造を使用することが出来る。 Twill, three representative weave satin weave, of course, various changes and applications can be used a planar structure be ready by the combination. 図2(A)は前記機能性ファイバー1を縦糸、横糸を平織りによりくみ上げた織編物の一例を示す。 FIG. 2 (A) shows an example of a woven or knitted fabric which pumped by warp the functional fibers 1, the weft plain weave. 【0036】なお、本発明の機能性ファイバーを用いた織編物は、本発明のファイバーのみで織り上げることはもちろん、本発明の機能性ファイバーと本発明の機能性ファイバー以外のファイバー(以下非機能性ファイバーと称す)を組み合わせて構成することも可能である。 It should be noted, woven or knitted fabric with functional fibers of the present invention, the weave only fibers of the present invention of course, the functional fibers and fiber (hereinafter nonfunctional non functional fibers of the present invention of the present invention it is also possible to constitute in combination referred to as fiber). 図2(B)は縦糸(または横糸)に機能性ファイバー1を用い、横糸(または縦糸)に機能性ファイバー以外のファイバーを用いた例を示す。 FIG. 2 (B) using the functional fibers 1 in the warp (or weft), an example of using a fiber other than the functional fibers weft (or warp). 【0037】図3は織り方を機能性ファイバーの軸心方向に見た織り方の種々の例を示しており、図3(A)の例は図2(A)のように、機能性ファイバー1を縦糸、 [0037] Figure 3 shows various examples of weave viewed weave in the axial direction of the functional fibers, the example of FIG. 3 (A) as shown in FIG. 2 (A), the functional fibers 1 warp,
横糸に用いるか、あるいは一方は機能性ファイバー、他方は非機能性ファイバー5を用いて平織りした例である。 Or used in the weft, or one of the functional fibers, the other is an example of plain weave with a non-functional fibers 5. 図3(B)の例は、縦糸(または横糸)に機能性ファイバー1を用い、横糸(または縦糸)に非機能性ファイバー5を用い、かつ交差状に織り込んだものである。 Example of FIG. 3 (B), using the functional fibers 1 in the warp (or weft), a non-functional fibers 5 used in the weft (or warp), and those woven in cross shape.
図3(C)の例は、縦糸(または横糸)に機能性ファイバー1を用い、横糸(または縦糸)に非機能性ファイバー5を用い、かつ非機能性ファイバー5は各機能性ファイバー1に対して1周まわして織り込んだものである。 Example of FIG. 3 (C), using the functional fibers 1 in the warp (or weft), a non-functional fibers 5 used in the weft (or warp), and non-functional fibers 5 to each functional fiber 1 Te are those woven by turning one lap.
図3(D)の例は、縦糸(または横糸)に機能性ファイバー1を用い、横糸(または縦糸)に機能性ファイバー1または非機能性ファイバー5を用い、かつ横糸(または縦糸)に対し、さらに非機能性ファイバー5を織り込んだものである。 Examples of FIG. 3 (D) relative to the warp (or weft) to using the functional fibers 1, weft (or warp) with functional fibers 1 or nonfunctional fibers 5 and weft (or warp), it is further intended to incorporating a non-functional fiber 5. 【0038】以上は、横糸1本と縦糸1本を交互に編み上げる基本例を示しているが、例えば横糸3本をまとめて、縦糸1本で織り上げる等の編み方も適用可能である。 The above is show basic examples knit into one and one warp weft alternately, for example, collectively weft three, weave, such as weaving a single warp can also be applied. また例えば横糸として、織り上げる織物の幅に比して遙かに長い1本の機能性ファイバーを用い、織物の左右端で折り曲げて使用することも好ましい。 As another example weft, using a long one functional fiber far than the width of the weave fabrics, it is also preferable to use folded at left and right ends of the fabric. さらには、 Moreover,
1本の機能性ファイバーを折返して、縦糸構造を作成した後に、さらに折返し横糸として用いることで、1本で織り上げることも可能である。 By folding one functional fibers, after creating a warp structure, further by using as a folded weft, it is also possible to weave a single. もちろん、いわゆる編み物として1本の機能性ファイバーで編み上げることも可能である。 Of course, it is also possible to knit into a single functional fiber as a so-called knitting. 【0039】本発明に用いる非機能性ファイバーとしては、上記の合成樹脂に限定されず、天然繊維からなる紡績糸、例えば羊毛紡績糸、綿紡績糸、麻紡績糸やレ−ヨン紡績糸なども使用可能であるが、好ましくは実質的に透明な材料である。 [0039] As non-functional fibers used in the present invention is not limited to the above synthetic resin, yarn made of natural fibers, such as wool yarn, cotton yarn, hemp yarn Yare - even such Yung spun yarn Although available, it is preferably substantially transparent material. 実質的に透明な材料を用いることで、機能性ファイバーの色、模様の変化が明瞭に観察される。 By using a substantially transparent material, the color of the functional fibers, the change pattern is clearly observed. 【0040】「電極」本発明の機能性ファイバーおよび機能性ファイバーを用いた織編物は電圧の印加により、 The woven or knitted fabric with functional fibers and functional fibers of the present invention "electrode" by applying a voltage,
その表面に現われる色を可逆的に変化させることが可能である。 Color appearing on the surface it is possible to reversibly change. 機能性ファイバーおよび機能性ファイバーを用いた織編物への電圧印加は、公知の種々の方法を用いることが可能である。 Voltage application to the functional fibers and woven or knitted material with functional fibers, it is possible to use various known methods. その中で、機能性ファイバーや機能性ファイバーを用いた織編物上に電極を設けることが好ましい。 Among them, it is preferable to provide an electrode on woven or knitted fabric using a functional fiber and a functional fiber. 【0041】図4(A)は織編物を用いて機能性ファイバー1と非機能性ファイバー5とにより組み上げられた織編物の隙間に透明樹脂等でなる充填材8を充填し、この充填材8を充填した織編物の両面に電極6、7を設け、電極6、7の外面は絶縁材でなる保護層9、10によって被覆してシート状に構成したものである。 [0041] FIG. 4 (A) filled with a filler 8 made of a transparent resin or the like into the gap of the woven or knitted fabric which is assembled by a nonfunctional fiber 5 and the functional fibers 1 with woven or knitted fabric, the filler 8 the electrodes 6 and 7 provided on both surfaces of the woven or knitted fabric filled with, the outer surface of the electrode 6, 7 is obtained by constituting the sheet coated with a protective layer 9 made of an insulating material. 図4 Figure 4
(B)はその縦断面図である。 (B) is a longitudinal sectional view thereof. このような充填材8を用いる場合、機能性ファイバー1を結束するための非機能性ファイバー5は必ずしも必要ではない。 When using such a filler 8, non-functional fibers in order to bind the functional fibers 1 5 is not necessarily required. 【0042】電極6、7としては、金属やカーボンブラック、酸化物等の公知の各種導電性材料を用いることができる。 [0042] The electrodes 6 and 7 may be a metal or carbon black, various known conductive material such as an oxide. また、表示面となる透明基板に形成される電極はITO、ZnOなどの透明導電体を用いればよい。 The electrode formed on the transparent substrate as a display surface may be used ITO, a transparent conductor such as ZnO. あるいは、非透明導電体であっても、非常に薄く形成することで、使用上、問題のない透過率を得ることが出来る場合もある。 Alternatively, even non-transparent conductive material, by forming very thin, there is a case that can be obtained using the, no problem transmittance. 電極6、7は、これらの材料を用いて膜状に形成される。 Electrodes 6, 7 is formed into a film shape by using these materials. 電極6、7は、湿式法、蒸着法などの形成方法や塗布法による形成方法により形成すればよい。 Electrodes 6 and 7, wet method, may be formed by forming method by the formation method or a coating method such as an evaporation method.
そして、必要に応じてパターニングされる。 And, it is patterned as needed. パターニングは公知のフォトリソグラフィを用いたエッチング法や、膜形成の際にマスクを用いてパターン塗布することも可能である。 Patterning the etching or using a known photolithography, it is possible to pattern applied using a mask during the film formation. 【0043】本発明の織編物は機能性ファイバーが織り上げられた状態で、それ自体が平面構造物として取り扱うことが可能である。 The woven or knitted fabric of the present invention in a state in which the functional fibers are woven, per se can be handled as a planar structure. すなわち、従来の電気泳動表示装置では構造を維持するための基体があったために、薄型化、柔軟性等に制限があり、かつ少なくとも基体の価格分だけ製品価格が高くなっていた。 That is, in order the conventional electrophoretic display device was a substrate for maintaining the structure and thinner, there is a limit to the flexibility and the like, and price amount corresponding product prices at least substrate was high. これに対して本発明では単に構造を支えるためだけの基体を用いる必要がない。 It is not necessary to use a substrate only for supporting the just structure in the present invention, on the other hand. 本発明において、好ましくは織編物厚に対して、導電性層厚、保護層厚等の機能層の層厚の合計が薄い。 In the present invention, preferably for knitted thick woven, conductive layer thickness, the total thickness of the protective layer thickness and the like functional layer is thin. すなわち、織編物それ自体が主たる構造物であり、導電性層厚、保護層厚等の機能層は、あくまで補助層である。 That is woven or knitted fabric itself primary structure, the conductive layer thickness, the protective layer thickness functional layer such as is merely auxiliary layer.
このように構成することで薄く安価とすることが可能となる。 Thus it is possible to inexpensively thin By configuring. 【0044】本発明による織編物は編み上がった状態で、そのまま使用することも可能である。 [0044] In state woven or knitted fabric according to the present invention, which went up knitting, it is also possible to directly use. この場合には、外部の電圧印加装置を用いて、本発明の機能性ファイバー、織編物に所定の電圧を印加することで、外観変化を起こさせる。 In this case, by using an external voltage application device, functional fibers of the present invention, by applying a predetermined voltage to the woven or knitted fabric, cause a change in appearance. 裏面のみに電極(透明である必要は無い)を設け、外部の電極との間に電圧を印加することも、局所的な電圧発生には有効であり、好ましい。 Only provided with an electrode (not but need transparent) back surface, applying a voltage between the external electrodes also are effective for local voltage generator, preferably. 【0045】本発明において好ましくは図4、図5に示したように、電圧印加のための電極6、7を織編物上に設ける。 [0045] Preferably in the present invention it is 4, as shown in FIG. 5, providing an electrode 6 and 7 for the voltage applied to the woven or knitted fabric. 例えば、織編物をウレタン等の絶縁性樹脂でなる充填材8でその両面をコーティングして貫通孔、すなわち機能性ファイバー1、1間の隙間または機能性ファイバー1と非機能性ファイバー5との間の隙間を封止した後に、少なくとも片面に透明導電膜でなる電極6または7、あるいは、極薄の非透明導電膜を形成する。 For example, during the woven or knitted fabric through by coating both sides with a filler 8 made of an insulating resin such as urethane hole, i.e. a gap or functional fibers 1 between functional fiber 1,1 nonfunctional fibers 5 after sealing the gap, the electrode 6 or 7 made of a transparent conductive film on at least one side, or to form a non-transparent conductive film extremely thin. 特に好ましくは、導電性樹脂または塗布型ITO(インジウムスズ酸化物)膜である。 Particularly preferably, conductive resin or coating-type ITO (indium tin oxide) film. 【0046】また、本発明の表示装置は、基板の対向する表面に形成された電極により泳動粒子に電界を与える電気泳動表示装置ばかりではなく、外部の装置(電圧印加ペン、電圧印加ヘッド、静電イオンフロー装置等々) [0046] In addition, the display device of the present invention is not only an electrophoretic display device for providing an electric field to the electrophoretic particles by the electrode formed on the opposing surfaces of the substrate, an external device (voltage application pen, the voltage application head, static electrostatic ion flow device, etc.)
により粒子に電界、帯電を与え、粒子の分布状態を制御して表示を行う表示装置とすることもできる。 Given electric field to the particles, charged by may be a display device that performs display by controlling the distribution of the particles. さらに、 further,
本発明の機能性ファイバーは電気泳動粒子を含有するものだけでなく、磁気泳動を利用し、外部から磁界を印加して磁気泳動粒子の分布状態を制御して表示を行う磁気泳動による外観変化型とすることもできる。 Functional fibers of the present invention is not only those containing electrophoretic particles, using magnetic migration appearance change by magnetic migration performing display by controlling the distribution of the magnetic electrophoretic particles by applying a magnetic field from the outside It can also be a. また、電圧を制御するための制御回路やメモリー回路等の各種の制御装置を組み合わせても良い。 It is also possible to combine the various control devices such as a control circuit and a memory circuit for controlling the voltage. 【0047】「動作」図5を用いて図4に示した織編物の動作原理を説明する。 [0047] The operation principle of the woven or knitted fabric shown in FIG. 4 will be described with reference to FIG. 5 "Operation". 図5(A)に示すように電極6、7間に電圧を印加すると、帯電している泳動粒子4 5 when voltage is applied between the electrodes 6 and 7 (A), the electrophoretic particles 4 are charged
は、その帯電と逆の電極側へと移動する。 Moves to its charging the opposite electrode side. その結果、表面には泳動粒子の色が観察される。 As a result, the surface color of the electrophoretic particles is observed. これに対して裏面は溶媒3の色が観察されることになる。 Backside contrast will be the color of the solvent 3 is observed. 図5(B)に示すように図5(A)と逆方向の電圧を印加すると、今度は泳動粒子4が裏面側に移動するため、表面からは溶媒3 Figure 5 is applied to FIG. 5 (A) and a reverse voltage (B), the order electrophoretic particles 4 in turn is moved to the back side, the solvent from the surface 3
の色が、裏面は泳動粒子4の色が観察されることになる。 Color of the back surface will be the color of the electrophoretic particles 4 are observed. なお、いったん移動した泳動粒子は長時間にわたり、そのままの場所に留まるために電圧印加をやめてもいったん表示した色は変わらない。 It should be noted that, once moved electrophoretic particles for a long period of time, does not change color to display once even quit the voltage applied in order to stay as it is of location. なお、図5(C)のように泳動粒子4を分散系中に均一に分散すれば溶媒と泳動粒子の色の混合色となる。 Incidentally, the mixed color color uniformly dispersed them if solvent and electrophoretic particle electrophoretic particles 4 in the dispersion system as in FIG. 5 (C). このような分布状態とするには比較的高速(10〜100Hz)の交流電圧を電極間に印加すれば良い。 Such a distribution may be relatively applying an alternating voltage of a high speed (10-100 Hz) between the electrodes. 【0048】「電極形成面の平滑化」電極6、7は平滑な表面に形成することが好ましい。 The "smoothing of the electrode forming surface" electrodes 6 and 7 is preferably formed on the smooth surface. 図6(A)に示すように充填材8を施した凹凸のある織編物の面上に電極6、7を形成した場合には、電圧分布に片寄りが生じるため、所望の電圧を印加することが出来ない。 In the case of forming the electrodes 6 and 7 on the surface of a woven or knitted fabric uneven subjected filler 8 as shown in FIG. 6 (A), since the offset voltage distribution occurs, to apply a desired voltage it can not be. このため充填材8となる絶縁性樹脂コーティングの表面を図6 Thus Figure surface of the insulating resin coating of the filling material 8 6
(B)に示すようにより平滑にするには、充填材8が未乾燥状態でのレベリング作用を活用するだけでなく、積極的に絶縁性樹脂コーティング面を、別途準備した表面が平滑な基板等と密着させて表面が平滑な基板表面形状を転写することも好ましい方法である。 To more smoothing (B), the well filler 8 is to take advantage of leveling action in undried, actively insulating resin coated surface, separately prepared smooth surface substrates such as it is also preferable that the adhesion is not the surface is transferred to smooth substrate surface shape and. 表面が平滑な基板等としては平板に限られず、円筒状(ロール状)基板、特に加熱した2本の円筒状基板の間を通過させることで両面を同時に平滑化することも好ましく用いることが出来る。 Surface is not limited to the flat plate as smooth substrates such as cylindrical (roll form) substrate, both surfaces simultaneously is also preferably used to smooth by in particular to pass between the two cylindrical substrate heated . 平滑性は、表面粗さ計を用い評価することが可能な場合には、短い表面粗さの成分を除去した曲線から求めた、うねり(Wca)が、絶縁性樹脂コーティングの表面間の距離の1/5以下であることが好ましく、 Smoothness, when it is possible to evaluate using a surface roughness meter was determined from the curve obtained by removing the component of the short surface roughness, waviness (Wca) is the distance between the surface of the insulating resin coating is preferably 1/5 or less,
特に好ましくは1/10以下である。 And particularly preferably 1/10 or less. 下限は特に制限はない。 The lower limit is not particularly limited. 前記範囲を越える時には電圧分布に片寄りが生じる。 It is offset to the voltage distribution generated when exceeding the above range. 【0049】なお本発明の織編物は、熱に対して反応し不燃物および/または不燃性ガスを発生、および/または吸熱する自己消火性物質を含有することや、熱に対して反応し発泡成分を含有することで、高い難燃性を得ることが可能であり好ましい。 It should be noted woven or knitted fabric of the present invention, generates a reaction was incombustible and / or non-combustible gas to heat, and / or or contain a self-extinguishing material to endothermic reaction and foaming to heat by containing the component, it is possible to obtain a high flame retardancy preferred. 具体的には、一般的に用いられているUL−94(アンダライターズラボラトリー)規格による垂直燃焼試験に準拠した評価においては、本発明の表示装置は、「V−0」グレード以上の難燃性を有することである。 Specifically, in the evaluation that conforms to the vertical combustion test according to UL-94 (under-Writers Laboratories) standards which are generally used, the display device of the present invention, "V-0" grade or flame retardant it is to have sex. 【0050】 【実施例】以下、実施例をあげて具体的に説明する。 [0050] EXAMPLES The following specifically described by way of examples. 【0051】[実施例1]泳動粒子4としての平均粒径0.8μmの白色酸化チタン12重量部と、分散剤としての2重量部のベータパーフルオロヘプチルエチルトリメトキシシランと、分散溶媒着色用の1重量部の青色染料と、分散溶媒3の主体としての85重量部のフッ素オイル(住友スリーエム社製フロリナート)とを超音波分散により混和したものを調製して分散系とした。 [0051] [Example 1] and the average particle diameter 0.8μm white titanium oxide 12 parts by weight of the electrophoretic particles 4, and beta perfluoroheptyl ethyltrimethoxysilane 2 parts by weight of a dispersing agent, dispersion solvent colored 1 blue dye parts of, and the dispersion to prepare a material obtained by mixing and an ultrasonic dispersing 85 parts by weight of fluorinated oil as an agent for dispersing the solvent 3 (Sumitomo 3M Fluorinert). 次に、 next,
本分散系を心材として、ポリエチレンを壁材、すなわち中空糸2として、共押出法により作成した機能性ファイバーを実施例1とする。 This dispersion as a core, polyethylene wall material, i.e. as a hollow fiber 2, the functional fibers prepared by co-extrusion as in Example 1. なお、押し出し直後にファイバーに張力を加えながら引き延ばすことにより、押し出し直後の直径の約60%とした。 Incidentally, by stretching while applying tension to the fiber immediately after extrusion was about 60% immediately after extrusion diameter. 実施例1は断面が、ほぼ円形であり、平均直径は50μm、壁厚(中空糸2の肉厚)は2μmであった。 Example 1 in cross-section, approximately circular, the average diameter is 50 [mu] m, wall thickness (thickness of the hollow fiber 2) was 2 [mu] m. 【0052】[実施例2]泳動粒子4としての平均粒径0.8μmの白色酸化チタン12重量部と、分散剤および表面電荷調整用の1.5部のオレイン酸および0.5 [0052] [Example 2] electrophoretic particles and white titanium oxide 12 parts by weight of the average particle diameter 0.8μm as 4, dispersant and 1.5 parts of oleic acid and 0.5 for surface charge adjustment
重量部のシランカップリング剤と、分散溶媒着色用の1 And parts by weight of a silane coupling agent, 1 for the dispersion solvent colored
重量部の黒色染料と、分散溶媒3の主体としての85重量部のシリコーンオイルとを超音波分散により混和したものを調製して分散系とした。 And black dye parts by weight was dispersed system and silicone oil 85 parts by weight of a subject of dispersion solvent 3 prepared that mixed by ultrasonic dispersion. 【0053】そして、上記分散系を心材として、紫外線硬化性樹脂を壁材、すなわち中空糸2として、共押出法により押し出しながら、同時に紫外線を照射することで、機能性ファイバーを得た。 [0053] Then, as the core of the above dispersion, an ultraviolet curable resin wall material, i.e. as a hollow fiber 2, while extruded by co-extrusion method, by simultaneously irradiated with ultraviolet rays to obtain a functional fiber. これにより、断面は正方形、1辺の長さの平均30μm、壁厚10μmの機能性ファイバーを得、これを実施例2とした。 Thus, the cross-section square, average 30μm in length of one side, to obtain a functional fiber wall thickness 10 [mu] m, which was used as a second embodiment. 【0054】[実施例3、4、5]実施例2において、 [0054] In Example 3, 4, 5] Example 2,
原料の紫外線硬化性樹脂を染料を用いて、赤、緑、青に着色したものをそれぞれ中空糸2として用いた機能性ファイバー1を実施例3、4、5とする。 The ultraviolet-curable resin raw material with dyes, red, green, and functional fibers 1 Example 3, 4 and 5 was used as the colored blue as the hollow fiber 2, respectively. 【0055】[実施例6]実施例1の機能性ファイバー1と、直径10μmの透明ポリエチレンテレフタレート糸を前記非機能性ファイバー5として平織りに織り上げた後に、充填材8としてのトルエン含有ウレタン樹脂溶液に浸漬塗布、乾燥を3回繰り返した後、表面が平滑な2本の金属ロールを用いて、さらに表面を平滑とした。 [0055] The functional fiber 1 of Example 6 Example 1, after the woven in plain weave transparent polyethylene terephthalate yarn having a diameter of 10μm as the non-functional fibers 5, in toluene containing urethane resin solution as a filler 8 after repeated dip coating, drying three times, the surface with a smooth two metal rolls, a further surface is smooth.
その後、電極6、7としての導電性樹脂、保護層9、1 Thereafter, conductive resin as the electrodes 6 and 7, the protective layer 9,1
0としての樹脂を順に塗布し、実施例6の機能性織編物とした。 The resin as 0 was applied in order to obtain a functional textile fabric of Example 6. 【0056】実施例6の織編物の表と裏の各電極間に3 [0056] 3 between the electrodes of the front and back of the woven or knitted fabric of Example 6
0Vの電圧を印加したところ、表面は分散溶媒3の色である青、裏面は泳動粒子4の色である白に変わった。 When voltage was applied to 0V, surface is the color of the dispersion solvent 3 blue, back surface has changed to white is the color of the electrophoretic particles 4. 次に印加電圧を逆にすると表面は白、裏面は青に変わった。 The surface now the applied voltage in the reverse white, back surface has changed to blue. この変化は可逆的で変化速度は100msであった。 This change reversible change rate was 100 ms. また電圧印加をやめても、その直前の色が保持されていた。 Also quit voltage application, the color of the immediately preceding was retained. 【0057】[実施例7]縦糸として、実施例3の中空糸2が赤色の機能性ファイバーを500本連続し、その横の縦糸とし、実施例4の中空糸2が緑色の機能性ファイバーを500本連続し、さらに、実施例5の中空糸2 [0057] [Example 7] warp, exemplary hollow fiber 2 of Example 3 are continuous 500 red functional fiber, and next to the warp, the hollow fiber 2 of Example 4 green functional fiber 500 continuously, further, the hollow fiber 2 of example 5
が青色の機能性ファイバーを500本連続し、さらに同様に、実施例3の中空糸2が赤色の機能性ファイバー、 There blue functional fibers continuously 500, further Similarly, the hollow fiber 2 in Example 3 a red functional fibers,
実施例4の中空糸2が緑色の機能性ファイバー、実施例5の中空糸2が青色の機能性ファイバーの繰り返しを複数回作成した縦糸に、直径10μmの非機能性ファイバー5としての透明ポリエチレンテレフタレート糸を横糸に用い、平織りした後に、充填材8用のトルエン含有ウレタン樹脂溶液に浸積塗布、乾燥した後、表面が平滑な2本の金属ロールを用いて、表面を平滑とした。 Hollow fiber 2 green functional fibers of Example 4, the warp of the hollow fiber 2 has created multiple repeating blue functional fiber of Example 5, a transparent polyethylene terephthalate as a nonfunctional fiber 5 having a diameter of 10μm using yarn weft, after plain weave, after immersion coating, and dried in toluene containing urethane resin solution for filling material 8, the surface with a smooth two metal rolls, the surface was smooth. その後、片面のみに電極6用のカーボン含有導電性塗料、両面に保護層9、10用の樹脂を順に塗布し、実施例7の機能性織編物とした。 Thereafter, only the carbon-containing conductive coating material for electrode 6 one side, the resin for the protective layer 9, 10 on both sides is applied in order to obtain a functional textile fabric of Example 7. 【0058】実施例7の外部に設けた銅板を実施例7の織編物表面に密着させながら、銅板と織編物導電性層との間に30Vの電圧を印加したところ、全面が黒となり、イニシャライズされた。 [0058] while in close contact with the woven or knitted fabric surface of the copper plate in Example 7 provided outside the Example 7, was applied to 30V voltage between the copper plate and the woven or knitted fabric the conductive layer, and the entire surface is black, initialization It has been. そして、織編物の導電性塗料層からなる電極6と、外部に設けた電圧印加ペンの先端にイニシャライズ時と逆の20Vの電圧を印加しながら、電圧印加ペンを織編物表面に接触させ線を引いたところ、赤、緑、青と3色に変化する1本の線が織編物上に形成された。 Then, woven and electrode 6 made of a conductive coating layer of the knitted fabric, while applying a voltage of initialization when the reverse 20V to the tip of the voltage application pen provided outside, the line contacting the voltage application pen woven or knitted fabric surface was caught, red, green, 1 lines to change to blue and three colors are formed on a woven or knitted fabric. すなわち電圧印加ペンの接触により白色の泳動粒子4が表示面に移動した状態では中空糸2の色である赤、緑あるいは青の色が現れ、泳動粒子4が裏面側にあるときには分散溶媒3の黒色が現れる。 That red in a state in which the white electrophoretic particles 4 by contact of the voltage application pen moves on the display surface is the color of the hollow fiber 2, appear the color of green or blue, electrophoretic particles 4 is dispersed solvent 3 when on the back side black appear. 【0059】再度、消去用に外部に設けた銅板を実施例7の織編物の表面に密着させながら、銅板と織編物の導電性塗料層との間に電圧印加ペンと逆のイニシャライズ電圧を印加したところ、全面が黒となり、再びイニシャライズされたことが確認出来た。 [0059] Again, applying with a copper plate provided outside is adhered to the surface of the woven or knitted fabric in Example 7, the voltage application pen opposite the initialization voltage between the conductive coating layer of the copper plate and the woven or knitted fabric for erasing When the entire surface becomes black, it was confirmed to have been initialized again. 【0060】[実施例8]なお、実施例6において、充填材8用のトルエン含有ウレタン樹脂溶液に浸積塗布、 [0060] [Example 8] In Examples 6, dip coating in toluene containing urethane resin solution for filling material 8,
乾燥した後、金属ロールを用いた表面平滑化処理を行わなかったものを実施例8とした。 After drying, and those not subjected to a surface smoothing treatment using a metal roll as in Example 8. この実施例8においては、ファイバーに直角な方向に約17μmのうねりが生じていた(実施例6では約3μm)。 In this embodiment 8, undulation of about 17μm in a direction perpendicular to the fiber has occurred (Example 6 about 3 [mu] m). なお、絶縁性樹脂コーティングの表面間の距離は70μmであったため、 Since the distance between the surface of the insulating resin coating was 70 [mu] m,
その1/5は、14μm、1/10は7μmである。 Its 1/5, 14μm, 1/10 is 7μm. このうねりの凸部はファイバー部と一致し、凹部はファイバー間と一致していた。 The convex portion of the undulations coincides with the fiber portion, the concave portion was consistent with inter fiber. そして、実施例1と同様の評価を行ったところコントラストの変化は実施例1に比べると約半分であった。 The change in contrast was evaluated in the same manner as in Example 1 was about half as compared to Example 1. 【0061】 【発明の効果】本発明によれば、使用者が希望に応じて随時、色、模様の外観を変化させることが可能な機能性ファイバー及びこの機能性ファイバーを用いた織編物を提供することができる。 [0061] According to the present invention, it provides a woven or knitted fabric the user using it at any time, color, functional fibers capable of changing the appearance of the pattern and the functional fibers as desired can do. また、本発明によれば、衣料素材、壁紙素材等として広く利用可能なだけでなく、局所的に電圧を印加することで、所望のパターン、文字、画像、動画等も表示可能な表示装置としても使用可能な、 Further, according to the present invention, clothing materials, not only widely available as wallpaper material or the like, by applying the locally voltage, a desired pattern, text, image, video, etc. as a display can display device which can also be used,
薄く安価で折り曲げ易い織編物を提供することができる。 Thin, it is possible to provide an inexpensive and bending easy woven or knitted fabric.

【図面の簡単な説明】 【図1】 本発明の機能性ファイバーの一実施の形態の概略斜視図である。 BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a schematic perspective view of one embodiment of the functional fibers of the present invention. 【図2】 (A)、(B)は本発明において採用可能な織編物の織り方の2例を示す平面図である。 Figure 2 (A), (B) is a plan view showing two examples of weave adoptable woven or knitted fabric in the present invention. 【図3】 (A)〜(D)は本発明において採用可能な織編物の織り方の4例を示す横断面図である。 [3] (A) ~ (D) is a cross-sectional view showing a fourth example of the weave of adoptable woven or knitted fabric in the present invention. 【図4】 (A)、(B)はそれぞれ本発明の織編物の一実施の形態を示す透視斜視図および縦断面図である。 [4] (A), (B) is a transparent perspective view and a longitudinal sectional view showing an embodiment of a woven or knitted fabric of the present invention, respectively. 【図5】 (A)〜(C)は図4の織編物の動作説明図である。 [5] (A) ~ (C) are timing charts for explaining the operation of the woven or knitted fabric of FIG. 【図6】 (A)、(B)は電極形成面を平滑化しない織編物と平滑化した織編物をそれぞれ示す図である。 6 (A), (B) is a diagram illustrating smoothing an electrode formation surface and not a woven or knitted fabric and the smoothed woven or knitted fabric, respectively. 【図7】 従来の表示装置の断面図である。 7 is a cross-sectional view of a conventional display device. 【符号の説明】 1:機能性ファイバー、2:中空糸、3:分散溶媒、 [Description of Reference Numerals] 1: Functional fiber, 2: hollow fiber, 3: dispersion solvent,
4:泳動粒子、5:非機能性ファイバー、6、7:電極、8:充填材、9、10:保護層 4: electrophoretic particles, 5: non-functional fibers, 6 and 7: electrode, 8: filler, 9, 10: protective layer

フロントページの続き (51)Int.Cl. 7識別記号 FI テーマコート゛(参考) A41D 31/00 501 A41D 31/00 501Z Fターム(参考) 3B011 AC12 5C094 AA60 BA05 BA09 BA75 CA21 DA05 DA06 EA05 FA04 FB01 FB16 HA10 Of the front page Continued (51) Int.Cl. 7 identification mark FI theme Court Bu (Reference) A41D 31/00 501 A41D 31/00 501Z F-term (reference) 3B011 AC12 5C094 AA60 BA05 BA09 BA75 CA21 DA05 DA06 EA05 FA04 FB01 FB16 HA10

Claims (1)

  1. 【特許請求の範囲】 【請求項1】 透明な中空糸の内部に、分散溶媒中に泳動粒子を分散させた分散系を充填し、前記泳動粒子の分布状態を変化させることにより所要の外観変化を行わせることが可能であることを特徴とする機能性ファイバー。 Inside of the Claims 1 Transparent hollow fibers, filled with a dispersion prepared by dispersing electrophoretic particles in a dispersion solvent, the required appearance change by changing the distribution state of the electrophoretic particles functional fiber, characterized in that it is possible to perform. 【請求項2】 前記分布状態変化は電圧により発生することを特徴とする請求項1に記載の機能性ファイバー。 2. A functional fiber of claim 1 wherein the distribution state change, characterized in that generated by the voltage. 【請求項3】 透明な中空糸の内部に、分散溶媒中に泳動粒子を分散させた分散系を充填し、前記泳動粒子の分布状態を変化させることにより所要の表示動作を行わせることが可能な機能性ファイバーを編み上げた構造を有することを特徴とする機能性ファイバーを用いた織編物。 Inside of 3. A transparent hollow fibers, filled with a dispersion prepared by dispersing electrophoretic particles in a dispersion solvent, it can be made to perform the required display operation by changing the distribution state of the electrophoretic particles woven or knitted fabric with functional fibers and having a Do functional fibers braided structure. 【請求項4】 透明な中空糸の内部に、分散溶媒中に泳動粒子を分散させた分散系を充填し、前記泳動粒子の分布状態を変化させることにより所要の表示動作を行わせることが可能な機能性ファイバーを横糸および/または縦糸として編み上げた構造を有することを特徴とする機能性ファイバーを用いた織編物。 Inside of 4. A transparent hollow fibers, filled with a dispersion prepared by dispersing electrophoretic particles in a dispersion solvent, it can be made to perform the required display operation by changing the distribution state of the electrophoretic particles woven or knitted fabric with functional fibers and having a braided structure Do functional fiber as weft and / or warp. 【請求項5】 前記分布状態変化は電圧により発生することを特徴とする請求項3または4に記載の機能性ファイバーを用いた織編物。 Wherein said distribution state change woven or knitted fabric using a functional fiber of claim 3 or 4, characterized in that generated by the voltage. 【請求項6】 前記機能性ファイバーを編み上げた構造の少なくとも片面に電圧印加のための電極を設けたことを特徴とする請求項5に記載の機能性ファイバーを用いた織編物。 Wherein said functional textile fabric with functional fibers according to claim 5 on at least one surface of the braided structure fibers is characterized by providing an electrode for voltage application. 【請求項7】 前記機能性ファイバーを編み上げた織編物の隙間に充填材を充填し、該充填材を充填した織編物の両面を平滑化し、該平滑化した面に電極を設けたことを特徴とする請求項6に記載の機能性ファイバーを用いた織編物。 7. filled with a filler in a gap of the functional fibers a braided woven or knitted fabric, characterized in that smoothes the both sides of the filled textile fabric the filler, provided the electrode on the smoothed surface woven or knitted fabric with functional fibers according to claim 6,.
JP2002086726A 2002-03-26 2002-03-26 Functional fiber and textile using the same Withdrawn JP2003280049A (en)