JP2003213593A - Diatomaceous earth paper including diatomaceous earth, high-filler paper containing diatomaceous earth and inorganic material and method for producing them - Google Patents

Diatomaceous earth paper including diatomaceous earth, high-filler paper containing diatomaceous earth and inorganic material and method for producing them

Info

Publication number
JP2003213593A
JP2003213593A JP2002003880A JP2002003880A JP2003213593A JP 2003213593 A JP2003213593 A JP 2003213593A JP 2002003880 A JP2002003880 A JP 2002003880A JP 2002003880 A JP2002003880 A JP 2002003880A JP 2003213593 A JP2003213593 A JP 2003213593A
Authority
JP
Japan
Prior art keywords
diatomaceous earth
paper
pulp
inorganic
resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2002003880A
Other languages
Japanese (ja)
Other versions
JP3624377B2 (en
Inventor
Masatoshi Yuasa
正敏 湯浅
Masahiro Hashikawa
雅弘 橋川
Katsuhiko Kitora
且彦 木寅
Original Assignee
Sanzen Seishi Kk
三善製紙株式会社
Toli Corp
東リ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sanzen Seishi Kk, 三善製紙株式会社, Toli Corp, 東リ株式会社 filed Critical Sanzen Seishi Kk
Priority to JP2002003880A priority Critical patent/JP3624377B2/en
Publication of JP2003213593A publication Critical patent/JP2003213593A/en
Application granted granted Critical
Publication of JP3624377B2 publication Critical patent/JP3624377B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

<P>PROBLEM TO BE SOLVED: To provide diatomaceous earth paper and high-filler paper rich in diatomaceous earth and/or inorganic material(s), capable of absorbing toxic gas emanated from construction materials or the like through making the best use of the properties inherent in diatomaceous earth, and enabling indoor humidity to be conditioned, and to provide a method for producing the paper. <P>SOLUTION: The diatomaceous earth paper having paper strength or the like enough to be used as wall paper or the like is produced by the following process: pulp is beaten so as to be 100-200 ml freeness, the resultant pulp slurry is incorporated with diatomaceous earth and additives for increasing the binding strength or the like between the pulp and the diatomaceous earth including a sizing agent, paper strengthening agent and yield improving agent in such proportions that both the diatomaceous earth and additives account for ≥30 wt.% of the whole diatomaceous earth paper to prepare a diatomaceous earth- containing pulp slurry about 1-2 wt.% in inlet concentration, which is then put to papermaking operation. <P>COPYRIGHT: (C)2003,JPO

Description

【発明の詳細な説明】Detailed Description of the Invention
【0001】[0001]
【発明の属する技術分野】本発明は、建材などから発生
する有害ガスを吸収し、さらに室内の湿度を調整可能な
消臭性能や調湿性能に優れる紙およびその製造方法に関
し、特に住宅の壁材等に使用される珪藻土を含む珪藻土
紙あるいは珪藻土と無機質材料とを含む高填料紙および
それらの製造方法に関する。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a paper which absorbs harmful gas generated from building materials and has excellent deodorant performance and humidity control performance capable of controlling indoor humidity, and a method for producing the paper, and particularly to walls of houses. TECHNICAL FIELD The present invention relates to a diatomaceous earth paper containing diatomaceous earth or a highly-filled paper containing diatomaceous earth and an inorganic material, and a method for producing the same, which are used as materials and the like.
【0002】[0002]
【従来の技術】近年、住宅の天井や壁などには様々な種
類の建材が使用されており、またそれらの建材の表面に
は、意匠性を高めるために室内装飾用の化粧シート(例
えば、合成樹脂製、布製、紙製など)を貼り合わせて使
用する場合も多い。
2. Description of the Related Art In recent years, various kinds of building materials have been used for ceilings and walls of houses, and on the surfaces of these building materials, decorative sheets for interior decoration (for example, Synthetic resin, cloth, paper, etc.) are often used by bonding them together.
【0003】これらの建材や化粧シートとして用いられ
る合成樹脂製シート中には、例えば、ホルムアルデヒド
など、いわゆる「シックハウス症候群」を引き起こす有
害ガスを発生する化学物質を含む場合があり、施工当初
に特有の不快な臭気を発することがある。そのため、室
内装飾用の化粧シートとして、耐久性の良い合成樹脂製
シートの代わりに、布製や紙製の壁紙などを使用する場
合も多くなっている。
Synthetic resin sheets used as these building materials and decorative sheets may contain chemical substances such as formaldehyde, which generate harmful gases causing so-called "sick house syndrome", and are peculiar to the beginning of construction. May give an unpleasant odor. Therefore, as a decorative sheet for interior decoration, a cloth or paper wallpaper is often used instead of a synthetic resin sheet having high durability.
【0004】一方、夏場に高温多湿となる我が国の気候
風土において、密閉性が高くなっている最近の住宅で
は、気象条件によっては、室内に結露を生じ、結露した
周辺にカビを発生する場合がある。また、結露に至らな
くても室内が常に湿度の高い状態となりやすい最近の住
宅では、住人の健康に影響を及ぼすことが懸念される。
On the other hand, in the climate climate of Japan, which is hot and humid in the summer, in a recent house with a high degree of airtightness, depending on the weather conditions, dew condensation may occur inside the room, and mold may form around the dew condensation. is there. In addition, there is a concern that the resident's health may be affected in a recent house where the room is always in a high humidity state even if it does not cause dew condensation.
【0005】しかしながら、化粧シートとして紙製の壁
紙を使用する場合には、壁紙はある程度の有害ガスや湿
気を吸収するもののその吸収性能はそれほど大きくない
ため、建材から発生する「シックハウス症候群」を引き
起こす有害ガスや結露を生じる湿気をより多く吸収し、
消臭性や調湿性に優れる壁紙が望まれている。
However, when a paper wallpaper is used as the decorative sheet, the wallpaper absorbs harmful gases and moisture to some extent, but its absorption performance is not so great, which causes "sick house syndrome" generated from building materials. Absorbs more harmful gases and moisture that causes condensation,
A wallpaper with excellent deodorant and humidity control properties is desired.
【0006】ただし、紙製の壁紙に調湿剤を添加する場
合、壁紙の紙厚は薄いことから、「シックハウス症候
群」を引き起こす有害ガスを吸収し、結露の生じにくい
調湿性能に優れる壁紙を製造するためには、壁紙中に可
能な限りの調湿剤を添加する必要がある。
However, when a humidity control agent is added to a paper wallpaper, the thickness of the wallpaper is thin, so that the wallpaper that absorbs harmful gas causing "sick house syndrome" and has excellent humidity control performance in which dew condensation does not easily occur. In order to produce it, it is necessary to add as much humidity control agent to the wallpaper as possible.
【0007】[0007]
【発明が解決しようとする課題】この紙製の壁紙の消臭
性能、調湿性能を改善する試みとしては、例えば、特開
平10−212694号公報に、調湿剤として炭素粉や
珪藻土を含有する建物内装用シートが開示されている。
As an attempt to improve the deodorant performance and humidity control performance of this paper wallpaper, for example, Japanese Patent Application Laid-Open No. H10-212694 contains carbon powder or diatomaceous earth as a humidity control agent. A sheet for building interior is disclosed.
【0008】しかしながら、特開平10−212694
号公報には、壁紙として使用可能な所定強度を有する建
物内装用シートを形成するために建物内装用シート中に
含有可能な調湿剤の添加量およびその製造方法について
は開示されていない。そのため、どの程度の調湿剤をど
のような方法で添加すると所定強度を有する壁紙を形成
することができるかについては不明である。
However, Japanese Unexamined Patent Application Publication No. 10-212694
The publication does not disclose the addition amount of a humidity control agent that can be contained in a building interior sheet to form a building interior sheet that can be used as a wallpaper and has a predetermined strength, and a manufacturing method thereof. Therefore, it is unclear how much humidity control agent is added by what method to form a wallpaper having a predetermined strength.
【0009】一方、特開昭59−100798号公報に
は、珪藻土とパルプをブレンドして形成される珪藻土を
含有する裏打紙およびその製造方法が開示されている
が、開示された製造方法では、パルプ100重量部に対
して珪藻土を20重量部より多く添加すると、裏打紙と
しての強度が低下し、裏打紙として使用できないことが
開示されている。
On the other hand, Japanese Patent Laid-Open No. 59-100798 discloses a backing paper containing diatomaceous earth formed by blending diatomaceous earth and pulp, and a method for producing the same. It is disclosed that when more than 20 parts by weight of diatomaceous earth is added to 100 parts by weight of pulp, the strength of the backing paper is reduced and it cannot be used as a backing paper.
【0010】すなわち、特開平10−212694号公
報および特開昭59−100798号公報によれば、壁
紙中に珪藻土を含有する製造技術は開示されているもの
の壁紙を形成するためには、最大20重量部の珪藻土を
パルプ100重量部に添加するのが限界である。
That is, according to Japanese Unexamined Patent Publication No. 10-212469 and Japanese Unexamined Patent Publication No. 59-100798, a manufacturing technique for containing diatomaceous earth in a wallpaper is disclosed, but a maximum of 20 is required to form a wallpaper. The limit is to add 100 parts by weight of diatomaceous earth to 100 parts by weight of pulp.
【0011】しかしながら、上記説明したように紙厚の
薄い壁紙に消臭性能や調湿性能を有する珪藻土などを添
加する場合には、壁紙中に可能な限りの珪藻土を添加し
て、建材から発生する有害ガスや室内の湿気を吸収し
て、壁紙の消臭性能や調湿性能を向上することが望まれ
る。
However, as described above, when diatomaceous earth or the like having deodorant performance and humidity control performance is added to the thin paper wallpaper, diatomaceous earth is added to the wallpaper as much as possible to generate from the building material. It is desired to improve the deodorizing performance and humidity control performance of the wallpaper by absorbing harmful gases and indoor humidity.
【0012】本発明は上記説明した従来技術の問題点を
解決することを出発点としてなされたものであり、その
目的は、建材などから発生する有害ガスを吸収し、さら
に室内の湿度を調整可能な、消臭性能や調湿性能に優れ
る珪藻土を多く含み壁紙などに適用可能な珪藻土紙およ
びその製造方法を提供することである。
The present invention was made as a starting point to solve the above-mentioned problems of the prior art, and its purpose is to absorb harmful gas generated from building materials and to adjust the indoor humidity. It is another object of the present invention to provide a diatomaceous earth paper which contains a large amount of diatomaceous earth excellent in deodorant performance and humidity controllability and is applicable to wallpaper and the like, and a method for producing the same.
【0013】また本発明の別の目的は、建材などから発
生する有害ガスを吸収し、さらに室内の湿度を調整可能
な、消臭性能や調湿性能に優れる珪藻土や無機質材料を
多く含み、さらに配合により難燃性や不燃性を示し壁紙
などに適用可能な高填料紙およびその製造方法を提供す
ることである。
Another object of the present invention is to contain a large amount of diatomaceous earth and an inorganic material capable of absorbing harmful gas generated from building materials and controlling indoor humidity, and having excellent deodorant performance and humidity control performance. It is an object of the present invention to provide a highly-filled paper which is flame-retardant or non-flammable by blending and can be applied to wallpaper and the like, and a method for producing the same.
【0014】[0014]
【課題を解決するための手段】上記目的を達成するため
の本発明に係る一実施形態の珪藻土紙は、以下の構成を
有する。すなわち、全重量の30〜80重量%の珪藻土
と、所定のフリーネスとなるように叩解されたパルプ
と、前記珪藻土と前記パルプとの間の少なくとも結合強
度を高める添加剤と、を含むことを特徴とする。
[Means for Solving the Problems] A diatomaceous earth paper according to an embodiment of the present invention for achieving the above object has the following constitution. That is, it comprises 30 to 80% by weight of the total weight of diatomaceous earth, pulp beaten to have a predetermined freeness, and an additive that enhances at least the bonding strength between the diatomaceous earth and the pulp. And
【0015】ここで、例えば、前記パルプは、前記フリ
ーネスが100〜200mlとなるように調成されてい
ることが好ましい。
Here, for example, the pulp is preferably prepared so that the freeness is 100 to 200 ml.
【0016】ここで、例えば、前記添加剤は、全重量の
0.2〜1.7重量%含まれることが好ましい。
Here, for example, the additive is preferably contained in an amount of 0.2 to 1.7% by weight based on the total weight.
【0017】ここで、例えば、前記添加剤には、サイズ
剤、紙力増強剤、歩留向上剤が含まれることが好まし
い。
Here, for example, it is preferable that the additives include a sizing agent, a paper strengthening agent, and a retention improving agent.
【0018】ここで、例えば、前記サイズ剤は、パルプ
を疎水化する構造を含む樹脂から選択され、前記紙力増
強剤は、パルプの水酸基と水素結合を形成するあるいは
3次元化した網目構造でパルプを固定して強度を増加さ
せる性能を有する水溶性樹脂から選択され、前記歩留向
上剤は、ワイヤーパートでの歩留まり率を示すワンパス
リテンションを向上させる水溶性樹脂から選択されるこ
とが好ましい。
Here, for example, the sizing agent is selected from resins containing a structure that makes the pulp hydrophobic, and the paper strengthening agent forms a hydrogen bond with the hydroxyl groups of the pulp or has a three-dimensional network structure. It is preferable that the retention improver is selected from water-soluble resins that have the property of fixing pulp and increasing strength, and the retention improver is selected from water-soluble resins that improve one-pass retention, which indicates the retention rate in the wire part.
【0019】ここで、例えば、前記サイズ剤は、オレフ
ィン系樹脂、アルキルケテンダイマー、スチレンアクリ
ル系樹脂およびロジン系のうちの少なくともいずれか1
つを含み、前記紙力増強剤は、ポリアクリルアミド系樹
脂、ポリアミドエピクロロヒドリン樹脂、メラミン樹
脂、尿素樹脂およびポリアミド樹脂のうちの少なくとも
いずれか1つを含み、前記歩留向上剤は、ポリアクリル
アミド系樹脂、スチレン系樹脂、ポリアミド縮合物およ
び多価フェノール系樹脂のうちの少なくともいずれか1
つを含むことが好ましい。
Here, for example, the sizing agent is at least one of an olefin resin, an alkyl ketene dimer, a styrene acrylic resin, and a rosin resin.
And the paper-strengthening agent includes at least one of a polyacrylamide-based resin, a polyamide epichlorohydrin resin, a melamine resin, a urea resin, and a polyamide resin. At least one of acrylamide resin, styrene resin, polyamide condensate, and polyhydric phenol resin
It is preferable to include one.
【0020】ここで、例えば、前記サイズ剤を全重量の
0.1〜1.0重量%、前記紙力増強剤を全重量の0.
1〜0.5重量%、前記歩留向上剤を全重量の0.05
〜0.2重量%含むことが好ましい。
Here, for example, the sizing agent is 0.1 to 1.0% by weight based on the total weight, and the paper strength agent is 0.1% to total weight.
1 to 0.5% by weight, 0.05% of the total amount of the yield improver
It is preferable that the content is 0.2% by weight.
【0021】上記目的を達成するための本発明に係る一
実施形態の珪藻土と無機質材料とを含有する高填料紙
は、以下の構成を有する。すなわち、所定のフリーネス
となるように叩解されたパルプと、珪藻土と、無機質材
料と、前記パルプ、前記珪藻土および前記無機質材料の
間の少なくとも結合強度を高める添加剤とを含み、前記
珪藻土と前記無機質材料とを合わせた量が全重量の30
〜85重量%となるように調成されていることを特徴と
する。
The highly filled paper containing diatomaceous earth and an inorganic material according to one embodiment of the present invention for achieving the above object has the following constitution. That is, pulp that has been beaten to have a predetermined freeness, diatomaceous earth, an inorganic material, and an additive that enhances at least the bonding strength between the pulp, the diatomaceous earth and the inorganic material, the diatomaceous earth and the inorganic material. The total amount of materials is 30
It is characterized in that it is prepared so as to be 85% by weight.
【0022】ここで、例えば、前記パルプは、フリーネ
スが100〜200mlであることが好ましい。
Here, for example, the freeness of the pulp is preferably 100 to 200 ml.
【0023】ここで、例えば、前記添加剤は、全重量の
0.2〜1.7重量%含まれることが好ましい。
Here, for example, the additive is preferably contained in an amount of 0.2 to 1.7% by weight based on the total weight.
【0024】ここで、例えば、前記無機材料は、水酸化
アルミニウム、クレー、カオリン、焼成カオリン、タル
ク、炭酸カルシウムあるいは二酸化チタン、水酸化チタ
ン等のチタン酸化物又は水酸化物、硫酸バリウム、酸化
亜鉛、硫酸カルシウム、酸化アルミニウム、炭酸マグネ
シウム、酸性白土、珪藻頁岩、ケイ酸塩鉱物およびホワ
イトカーボンから選択された1種または2種以上を複合
して使用することが好ましい。
Here, for example, the inorganic material is aluminum hydroxide, clay, kaolin, calcined kaolin, talc, calcium carbonate or titanium oxide or hydroxide such as titanium dioxide, titanium hydroxide, barium sulfate, zinc oxide. It is preferable to use one or more compounds selected from calcium sulfate, aluminum oxide, magnesium carbonate, acid clay, diatom shale, silicate minerals and white carbon in combination.
【0025】ここで、例えば、前記添加剤は、サイズ
剤、紙力増強剤、歩留向上剤を含むことが好ましい。
Here, for example, it is preferable that the additives include a sizing agent, a paper strengthening agent, and a retention improving agent.
【0026】ここで、例えば、前記サイズ剤は、パルプ
を疎水化する構造を含む樹脂から選択され、前記紙力増
強剤は、パルプの水酸基と水素結合を形成するあるいは
3次元化した網目構造でパルプを固定して強度を増加さ
せる性能を有する水溶性樹脂から選択され、前記歩留向
上剤は、ワイヤーパートでの歩留まり率を示すワンパス
リテンションを向上させる水溶性樹脂から選択されるこ
とが好ましい。
Here, for example, the sizing agent is selected from resins containing a structure which makes the pulp hydrophobic, and the paper strengthening agent forms a hydrogen bond with the hydroxyl groups of the pulp or has a three-dimensional network structure. It is preferable that the retention improver is selected from water-soluble resins that have the property of fixing pulp and increasing strength, and the retention improver is selected from water-soluble resins that improve one-pass retention, which indicates the retention rate in the wire part.
【0027】ここで、例えば、前記サイズ剤は、オレフ
ィン系樹脂、アルキルケテンダイマー、スチレンアクリ
ル系樹脂およびロジン系のうちの少なくともいずれか1
つを含み、前記紙力増強剤は、ポリアクリルアミド系樹
脂、ポリアミドエピクロロヒドリン樹脂、メラミン樹
脂、尿素樹脂およびポリアミド樹脂のうちの少なくとも
いずれか1つを含み、前記歩留向上剤は、ポリアクリル
アミド系樹脂、スチレン系樹脂、ポリアミド縮合物およ
び多価フェノール系樹脂のうちの少なくともいずれか1
つを含むことが好ましい。
Here, for example, the sizing agent is at least one of an olefin resin, an alkyl ketene dimer, a styrene acrylic resin, and a rosin resin.
And the paper-strengthening agent includes at least one of a polyacrylamide-based resin, a polyamide epichlorohydrin resin, a melamine resin, a urea resin, and a polyamide resin. At least one of acrylamide resin, styrene resin, polyamide condensate, and polyhydric phenol resin
It is preferable to include one.
【0028】ここで、例えば、前記サイズ剤を全重量の
0.1〜1.0重量%、前記紙力増強剤を全重量の0.
1〜0.5重量%、前記歩留向上剤を全重量の0.05
〜0.2重量%含むことが好ましい。
Here, for example, the sizing agent is 0.1 to 1.0% by weight based on the total weight, and the paper strength agent is 0.1% to total weight.
1 to 0.5% by weight, 0.05% of the total amount of the yield improver
It is preferable that the content is 0.2% by weight.
【0029】上記目的を達成するための本発明に係る一
実施形態の珪藻土紙の製造方法は、以下の構成を有す
る。すなわち、パルプを所定のフリーネスとなるように
叩解し、前記叩解したパルプを、珪藻土と、さらに前記
パルプと前記珪藻土との間の少なくとも結合強度を高め
る添加剤と混合して珪藻土入りパルプスラリーを調成
し、前記珪藻土入りパルプスラリーを抄造して前記珪藻
土が全量の30〜80重量%となるように調成されてい
る珪藻土紙を製造することを特徴とする。
The method for producing diatomaceous earth paper according to one embodiment of the present invention for achieving the above object has the following constitution. That is, the pulp is beaten so as to have a predetermined freeness, the beaten pulp is mixed with diatomaceous earth, and an additive for increasing at least the bonding strength between the pulp and the diatomaceous earth to prepare a diatomaceous earth-containing pulp slurry. The present invention is characterized in that the diatomaceous earth paper is prepared, and the pulp slurry containing the diatomaceous earth is made into a paper to prepare a diatomaceous earth paper in which the diatomaceous earth is adjusted to 30 to 80 wt% of the total amount.
【0030】上記目的を達成するための本発明に係る一
実施形態の高填料紙の製造方法は、以下の構成を有す
る。すなわち、パルプを所定のフリーネスとなるように
叩解し、前記叩解したパルプを、珪藻土と、無機質材料
と、さらに前記パルプ、前記珪藻土および前記無機質材
料の間の少なくとも結合強度を高める添加剤と混合して
スラリーを調成し、前記スラリーを抄造し、前記珪藻土
と前記無機質材料とを合わせた量が全重量の30〜85
重量%となるように調成されている珪藻土と無機質材料
を含有する高填料紙を製造することを特徴とする。
The method for producing highly-filled paper according to one embodiment of the present invention for achieving the above object has the following constitution. That is, pulp is beaten to have a predetermined freeness, and the beaten pulp is mixed with diatomaceous earth, an inorganic material, and an additive that enhances at least the bonding strength between the pulp, the diatomaceous earth and the inorganic material. To prepare a slurry, papermaking the slurry, and the total amount of the diatomaceous earth and the inorganic material is 30 to 85 of the total weight.
It is characterized by producing a highly-filled paper containing diatomaceous earth and an inorganic material, which is adjusted to have a weight percentage.
【0031】[0031]
【発明の実施形態】以下に図面を参照して、本発明に係
る好適な実施形態である「珪藻土紙」あるいは「高填料
紙」およびそれらの製造方法を例示的に詳しく説明す
る。ただし、この実施形態に記載されている構成要素、
数値などは、特に特定的な記載がない限りは、この発明
をそれらのみに限定する趣旨のものではない。
BEST MODE FOR CARRYING OUT THE INVENTION Preferred embodiments of the present invention, "diatomaceous earth paper" or "high filling paper", and methods for producing them will be described in detail below with reference to the drawings. However, the components described in this embodiment,
Numerical values and the like are not intended to limit the present invention thereto unless otherwise specified.
【0032】[定義]まず本実施形態で用いる「珪藻土
を含む珪藻土紙」、「珪藻土と無機質材料を含む高填料
紙」および「フリーネス(ろ水度)」について以下に定
義する。
[Definition] First, "diatomaceous earth paper containing diatomaceous earth", "high-filler paper containing diatomaceous earth and an inorganic material" and "freeness (freeness)" used in the present embodiment will be defined below.
【0033】「珪藻土を含む珪藻土紙」とは、所定のフ
リーネスを有するように叩解されたパルプ中に所定量の
珪藻土と、結合強度やワンパスリテンションなどの特性
を高める添加剤とを混合してスラリーを調成し、このス
ラリーを抄造して得られる紙と定義する。
The "diatomaceous earth paper containing diatomaceous earth" is a slurry prepared by mixing a predetermined amount of diatomaceous earth with an additive that enhances properties such as binding strength and one-pass retention in pulp that has been beaten to have a predetermined freeness. Is prepared and paper is obtained by making this slurry into paper.
【0034】「珪藻土と無機質材料を含む高填料紙」と
は、所定のフリーネスを有するように叩解されたパルプ
中に所定量の珪藻土と、無機質材料と、結合強度などの
特性を高める添加剤とを混合してスラリーを調成し、こ
のスラリーを抄造して得られる紙と定義する。
"High-filler paper containing diatomaceous earth and an inorganic material" means a predetermined amount of diatomaceous earth in pulp that has been beaten to have a predetermined freeness, an inorganic material, and an additive that enhances properties such as bond strength. Is defined as a paper obtained by preparing a slurry and mixing the slurry to prepare a slurry.
【0035】なお、本実施形態では、「珪藻土を含む珪
藻土紙」を単に「珪藻土紙」と称し、「珪藻土と無機質
材料を含む高填料紙」を単に「高填料紙」と称して区別
する。
In the present embodiment, "diatomaceous earth paper containing diatomaceous earth" is simply referred to as "diatomaceous earth paper", and "high filler paper containing diatomaceous earth and an inorganic material" is simply referred to as "high filler paper".
【0036】[フリーネス(ろ水度)]とは、パルプの
水切れの程度を表す指標(数値)で、繊維の叩解の度合
いを示すものである。パルプのフリーネスの測定方法
は、日本工業規格JIS P8121で、「カナダ標準
ろ水度試験方法」および「ショッパーろ水度試験方法」
に規定されている。本実施形態では、フリーネス(ろ水
度)を「カナダ標準ろ水度試験方法」を用いて測定した
が、「ショッパーろ水度試験方法」を用いて測定しても
よい。
[Freeness (freeness)] is an index (numerical value) indicating the degree of drainage of pulp, and indicates the degree of beating of fibers. The freeness of pulp is measured according to Japanese Industrial Standard JIS P8121, "Canadian Standard Freeness Test Method" and "Shopper Freeness Test Method".
Stipulated in. In the present embodiment, the freeness (freeness) is measured using the “Canadian standard freeness test method”, but it may be measured using the “Shopper freeness test method”.
【0037】[珪藻土、高填料紙の原料]次に、上記説
明した「珪藻土紙」あるいは「高填料紙」を製造するた
めに用いる原料について以下詳しく説明する。
[Raw materials for diatomaceous earth and highly-filled paper] Next, the raw materials used for producing the above-mentioned "diatomaceous earth paper" or "high-filled paper" will be described in detail.
【0038】なお上記定義したように、「高填料紙」の
構成成分は、「珪藻土紙」の構成成分に無機質材料成分
をさらに添加したものであり、「珪藻土紙」と「高填料
紙」の原料の違いは、無機質材料のみである。そこで以
下の説明では、「珪藻土紙」および「高填料紙」の各原
料は重複するものが多いので、それぞれの原料を区別し
て説明することなく一括して説明することとする。
As defined above, the constituents of "high-filler paper" are those obtained by adding inorganic material components to the constituents of "diatomaceous earth paper". The only difference between the raw materials is the inorganic material. Therefore, in the following description, since the respective raw materials of “diatomaceous earth paper” and “highly filled paper” are often duplicated, the respective raw materials will be collectively described without being separately described.
【0039】[パルプ]本実施形態の「珪藻土紙」ある
いは「高填料紙」で使用するパルプとしては、種々のパ
ルプを使用することができる。例えば、針葉樹未晒クラ
フトパルプ(NUKP)、針葉樹晒クラフトパルプ(N
BKP)、広葉樹未晒クラフトパルプ(LUKP)、広
葉樹晒クラフトパルプ(LBKP)、針葉樹晒サルファ
イトパルプ(NBSP)等の木材パルプと、サーモメカ
ニカルパルプ(TMP)や砕木パルプ(GP)等の高収
率パルプのいずれかを単独又は複合して使用することが
できる。
[Pulp] As the pulp used in the "diatomaceous earth paper" or the "highly-filled paper" of this embodiment, various pulps can be used. For example, unbleached softwood kraft pulp (NUKP), bleached softwood kraft pulp (N
BKP), hardwood unbleached kraft pulp (LUKP), hardwood bleached kraft pulp (LBKP), softwood bleached sulphite pulp (NBSP) and other wood pulp, and thermomechanical pulp (TMP) and groundwood pulp (GP) and other high yields. Any of the rate pulps can be used alone or in combination.
【0040】また木材パルプに限らず、麻、こうぞ等の
じん皮繊維、竹、わら、バガス、ケナフ等の非木材パル
プも利用および配合することもできる。さらに用途に応
じて、有機合成繊維、無機質繊維を混合しても良い。
Further, not only wood pulp but also non-wood pulp such as hemp and groove, and non-wood pulp such as bamboo, straw, bagasse and kenaf can be used and blended. Further, organic synthetic fibers and inorganic fibers may be mixed depending on the application.
【0041】[パルプのフリーネス]上記より選択され
たパルプは、「珪藻土紙」あるいは「高填料紙」が壁紙
などとして使用できる程度の強度等を有するようにフリ
ーネス(ろ水度)を調成して用いる。本実施形態のパル
プのフリーネス(ろ水度)は、80〜300mlが好ま
しく、より好ましくは、100〜200mlとなるよう
に叩解して使用する。
[Freeness of Pulp] The pulp selected from the above is adjusted in its freeness (freeness) so that "diatomaceous earth paper" or "highly filled paper" has such strength that it can be used as wallpaper or the like. To use. The freeness (freeness) of the pulp of the present embodiment is preferably 80 to 300 ml, more preferably 100 to 200 ml by beating.
【0042】また上記の範囲のフリーネスに調成された
パルプにおいて、フリーネスが小さい程、「珪藻土紙」
あるいは「高填料紙」の強度などが高くなり、珪藻土や
無機質材料を多く含有することもできる。
Further, in the pulp tuned to the freeness within the above range, the smaller the freeness, the "diatomaceous earth paper".
Alternatively, the strength of the “high-filler paper” is increased, and the diatomaceous earth and inorganic materials can be contained in large amounts.
【0043】なお、「珪藻土紙」あるいは「高填料紙」
を作製する際に、フリーネス(ろ水度)が300ml以
上のパルプを用いると、得られる「珪藻土紙」あるいは
「高填料紙」の強度は、壁紙等で使用できる程度の強度
に達することができず、使用できない。この点につい
て、以下詳しく説明する。
Incidentally, "diatomaceous earth paper" or "high filling paper"
When pulp with a freeness (freeness) of 300 ml or more is used in making, the strength of the obtained "diatomaceous earth paper" or "high filler paper" can reach such strength that it can be used as wallpaper. No, it cannot be used. This point will be described in detail below.
【0044】パルプを100〜200mlとなるように
叩解すると繊維が柔軟になり、さらにフィブリル化が進
んで繊維間の結合面積が増大し、繊維同士の絡みが増え
る。この繊維同士の絡みが多くあるパルプを珪藻土や無
機質材料と混合すると、フィブリル化した繊維の交点部
分に珪藻土や無機質材料が付着し、パルプと珪藻土ある
いは無機質材料との接触面積が増加する。その結果、そ
れらの間で発生する摩擦抵抗が増加し、「珪藻土紙」あ
るいは「高填料紙」を作製するときに得られる紙の強度
を高くすることができる。
When the pulp is beaten to 100 to 200 ml, the fibers become soft, and further fibrillation progresses to increase the bonding area between the fibers and increase the entanglement between the fibers. When the pulp in which the fibers are entangled with each other is mixed with the diatomaceous earth or the inorganic material, the diatomaceous earth or the inorganic material adheres to the intersection of the fibrillated fibers, and the contact area between the pulp and the diatomaceous earth or the inorganic material increases. As a result, the frictional resistance generated between them increases, and the strength of the paper obtained when producing "diatomaceous earth paper" or "highly-filled paper" can be increased.
【0045】一方、フリーネス(ろ水度)が450ml
のパルプは、叩解が進んでいないため、フィブリル化が
少なく、繊維同士の絡みが少ない。そのため、この繊維
同士の絡みが少ないパルプを珪藻土や無機質材料と混合
すると、フィブリル化した繊維の交点部分に珪藻土や無
機質材料が付着しにくいためパルプと珪藻土などとの間
の接触面積はそれほど増加しない。その結果、それらの
間で発生する摩擦抵抗の増加は少ないため、パルプに珪
藻土あるいは無機質材料などを含有させて珪藻土紙や高
填料紙を作製するときに得られる紙の強度を高くするこ
とができない。
On the other hand, the freeness (freeness) is 450 ml.
Since pulp is not beaten, it is less likely to be fibrillated and has less entanglement between fibers. Therefore, if pulp with less entanglement between these fibers is mixed with diatomaceous earth or an inorganic material, the contact area between the pulp and diatomaceous earth does not increase so much because the diatomaceous earth or the inorganic material does not easily adhere to the intersections of the fibrillated fibers. . As a result, since the increase in frictional resistance generated between them is small, it is not possible to increase the strength of the paper obtained when diatomaceous earth or an inorganic material is added to the pulp to produce diatomaceous earth paper or highly filled paper. .
【0046】なお、「珪藻土紙」中にパルプは任意量添
加することができるが、「珪藻土紙」の消臭性能や調湿
性能を高めるために本実施形態では、パルプは「珪藻土
紙」の全重量の70重量部以下となるように添加するの
が望ましい。また同様に、「高填料紙」中にもパルプは
任意量添加することができる。
Although any amount of pulp can be added to the "diatomaceous earth paper", in order to enhance the deodorizing performance and humidity control performance of the "diatomaceous earth paper", the pulp is "diatomaceous earth paper". It is desirable to add it so as to be 70 parts by weight or less of the total weight. Similarly, an arbitrary amount of pulp can be added to the "highly-filled paper".
【0047】[珪藻土]珪藻土は、藻類が珪藻殻となっ
て長い間地層に堆積し化石化したものであり、主成分
は、SiO(シリカ)である。本実施形態の「珪藻土
紙」あるいは「高填料紙」で使用する珪藻土の粒子径
は、5〜100ミクロン、好ましくは10〜50ミクロ
ンに整粒されたものが望ましい。
[Diatomaceous earth] Diatomaceous earth is a material in which algae form diatom shells and have been fossilized by being deposited in the formation for a long time, and the main component is SiO 2 (silica). It is desirable that the diatomaceous earth used in the "diatomaceous earth paper" or the "highly filled paper" of the present embodiment has a particle size adjusted to 5 to 100 microns, preferably 10 to 50 microns.
【0048】そのために天然に存在する珪藻土は使用前
に十分精製・乾燥されたものまたは乾燥品を焼成したも
のを用いる。
For that purpose, as the diatomaceous earth which is naturally present, one which is sufficiently purified and dried before use or one obtained by baking a dried product is used.
【0049】このように調成された珪藻土は、水蒸気の
吸湿・放湿性能および有害ガスの消臭性能に優れている
ことから建材などから放出される有害ガスを吸着しやす
く、また室内の湿度に合わせて水蒸気を吸収したり、放
湿しやすいくなる。珪藻土は、これらの特性を生かし
て、建材の他に、ろ過助剤、吸着・脱臭剤、充填材など
に幅広く利用されている。
The diatomaceous earth thus prepared is excellent in moisture vapor absorbing / releasing performance of water vapor and deodorizing performance of harmful gas, so that it is easy to adsorb harmful gas emitted from building materials and the humidity in the room. It becomes easy to absorb water vapor and release moisture according to. Taking advantage of these characteristics, diatomaceous earth is widely used as a building aid, as well as a filter aid, an adsorbing / deodorizing agent, a filler, and the like.
【0050】なお本実施形態では、「珪藻土紙」中に珪
藻土を好ましくは全重量の30〜80重量%、より好ま
しくは、全重量の50〜80重量%添加することができ
る。また「珪藻土紙」中の珪藻土の割合は、珪藻土紙の
特性に応じて選択することができ、例えば、珪藻土紙の
消臭性能や調湿性能を高めるためには、「珪藻土紙」中
の珪藻土の割合を増やせばよい。
In the present embodiment, the diatomaceous earth may be added to the "diatomaceous earth paper" in an amount of preferably 30 to 80% by weight, and more preferably 50 to 80% by weight of the total weight. The proportion of diatomaceous earth in the "diatomaceous earth paper" can be selected according to the characteristics of the diatomaceous earth paper. For example, in order to enhance the deodorizing performance and humidity control performance of the diatomaceous earth paper, the diatomaceous earth in the "diatomaceous earth paper" can be selected. You can increase the ratio of.
【0051】また同様に、本実施形態では、「高填料
紙」中に珪藻土を好ましくは無機質材料と合わせて全重
量の30〜85重量%、より好ましくは、全重量の50
〜85重量%添加することができる。なお「高填料紙」
中の珪藻土の割合は、特に限定する必要が無く、使用す
る「高填料紙」の特性に応じて選択することができる。
例えば、珪藻土の有する消臭性能や調湿性能より利用し
たい場合には、「高填料紙」中の珪藻土の割合を増やせ
ばよい。
Similarly, in this embodiment, diatomaceous earth is preferably combined with the inorganic material in the "highly-filled paper" in an amount of 30 to 85% by weight, more preferably 50 to 50% by weight.
~ 85 wt% can be added. "Highly-filled paper"
The proportion of diatomaceous earth in the medium is not particularly limited and can be selected according to the characteristics of the "highly-filled paper" used.
For example, if it is desired to utilize the deodorant performance and humidity control performance of diatomaceous earth, the proportion of diatomaceous earth in the "highly-filled paper" may be increased.
【0052】[無機質材料]本実施形態の「高填料紙」
で使用する無機質材料としては、消臭性能、調湿性能を
示し、難燃性の材料であれば天然のものであれ人工のも
のであれどのようなものであっても良い。例えば、水酸
化アルミニウム、クレー、カオリン、焼成カオリン、タ
ルク、炭酸カルシウムあるいは二酸化チタン、水酸化チ
タン等のチタン酸化物又は水酸化物、硫酸バリウム、酸
化亜鉛、硫酸カルシウム、ホワイトカーボン、酸化アル
ミニウム、炭酸マグネシウム、酸性白土、珪藻頁岩、ケ
イ酸塩鉱物等を単独あるいは数種類組み合わせて使用す
ることができる。
[Inorganic Material] “Highly Filled Paper” of the Present Embodiment
As the inorganic material used in, any material may be used whether it is a natural material or an artificial material as long as it exhibits deodorant performance and humidity control performance and is a flame-retardant material. For example, aluminum hydroxide, clay, kaolin, calcined kaolin, talc, calcium carbonate or titanium dioxide or titanium oxide or hydroxide such as titanium hydroxide, barium sulfate, zinc oxide, calcium sulfate, white carbon, aluminum oxide, carbonic acid. Magnesium, acid clay, diatom shale, silicate minerals, etc. can be used alone or in combination of several kinds.
【0053】このような無機質材料は、水蒸気の吸湿・
放湿性能および有害ガスの消臭性能に優れることから建
材などから放出される有害ガスを吸着しやすく、また室
内の湿度に合わせて水蒸気を吸収したり、放湿しやすい
くなる。また難燃性や不燃性の特性を持たせることもで
きる。
Such an inorganic material absorbs water vapor
Due to its excellent moisture-releasing performance and deodorizing performance of harmful gases, it easily absorbs harmful gases emitted from building materials, and also absorbs water vapor according to indoor humidity and easily releases moisture. It can also have flame retardant or non-flammable characteristics.
【0054】本実施形態では、無機質材料を「高填料
紙」中に好ましくは珪藻土と合わせて全重量の30〜8
5重量%、より好ましくは、全重量の50〜85重量%
添加することができる。なお「高填料紙」中の無機質材
料の割合は、特に限定する必要が無く、使用する「高填
料紙」の特性に応じて選択することができる。例えば、
無機質材料の有する消臭性能、調湿性能および難燃性の
特性をより利用したい場合には、「高填料紙」中の無機
質材料の割合を増やせばよく、無機質材料の有する消臭
性能、調湿性能および他の特性を利用したい場合には、
高填料紙中の無機質材料の割合を増やせばよい。またな
お「高填料紙」中の無機質材料の種類は、上記説明した
ものから1種あるいは2種以上を所定量ずつ複合して使
用すれば良く、その種類および量については特に限定す
る必要が無く、使用する「高填料紙」の特性に応じて選
択することができる。
In the present embodiment, the inorganic material is combined in the "high-filler paper", preferably diatomaceous earth, in a total weight of 30-8.
5% by weight, more preferably 50-85% by weight of the total weight
It can be added. The proportion of the inorganic material in the "high-filler paper" does not need to be particularly limited and can be selected according to the characteristics of the "high-filler paper" to be used. For example,
In order to make better use of the deodorant performance, humidity control performance and flame retardant properties of the inorganic material, it is sufficient to increase the proportion of the inorganic material in the “high-filler paper”. If you want to take advantage of wet performance and other properties,
It suffices to increase the proportion of the inorganic material in the highly-filled paper. Further, the type of the inorganic material in the "highly-filled paper" may be one kind or a combination of two or more kinds from the above-described ones in a predetermined amount, and the kind and the amount are not particularly limited. Can be selected according to the characteristics of the "highly-filled paper" used.
【0055】[添加剤:内添用]本実施形態の「珪藻土
紙」あるいは「高填料紙」で使用する内添する添加剤
は、珪藻土とパルプとの間の結合強度等の特性、あるい
は、珪藻土とパルプあるいは無機質材料との間の結合強
度やワンパスリテンション等の特性を高めるために用い
られる。添加剤としては、下記に示するサイズ剤、紙力
増強剤および歩留向上剤を用いることが好ましい。
[Additive: For Internal Addition] The additive to be added internally used in the “diatomaceous earth paper” or the “highly filled paper” of the present embodiment is a characteristic such as the bond strength between diatomaceous earth and pulp, or It is used to enhance properties such as bond strength and one-pass retention between diatomaceous earth and pulp or inorganic material. As the additive, it is preferable to use the following sizing agent, paper strength enhancer and retention improver.
【0056】[サイズ剤]サイズ剤は、パルプ(の主成
分であるセルロース)を疎水化する構造を含む樹脂が好
ましく、例えば、オレフィン系樹脂、アルキルケテンダ
イマー、スチレンアクリル樹脂、ロジンなどを用いるの
が好ましい。
[Sizing agent] The sizing agent is preferably a resin having a structure for making pulp (the main component thereof) hydrophobic, and for example, an olefin resin, an alkyl ketene dimer, a styrene acrylic resin, a rosin or the like is used. Is preferred.
【0057】[紙力増強剤]紙力増強剤は、パルプの水
酸基と水素結合を形成したり、3次元化した網目構造で
パルプを固定して強度等を増加させる性能を有する水溶
性樹脂が好ましく、例えば、ポリアクリルアミド系樹
脂、ポリアミドエピクロロヒドリン樹脂、メラミン樹
脂、尿素樹脂、ポリアミド樹脂などを用いるのが好まし
い。
[Paper Strength Enhancing Agent] The paper strength enhancing agent is a water-soluble resin having the ability to form hydrogen bonds with the hydroxyl groups of the pulp and to fix the pulp with a three-dimensional network structure to increase the strength and the like. Preferably, for example, polyacrylamide resin, polyamide epichlorohydrin resin, melamine resin, urea resin, polyamide resin, etc. are preferably used.
【0058】[歩留向上剤]歩留向上剤は、ワイヤーパ
ートでのワンパスリテンションを向上させる水溶性樹脂
が好ましく、例えば、ポリアクリルアミド系樹脂、スチ
レン系樹脂、ポリアミド縮合物および多価フェノール系
樹脂などを用いるのが好ましい。
[Retention Improver] The retention improver is preferably a water-soluble resin which improves one-pass retention in the wire part, and examples thereof include polyacrylamide resin, styrene resin, polyamide condensate and polyhydric phenol resin. And the like are preferably used.
【0059】なお上記説明した添加剤の「珪藻土紙」あ
るいは「高填料紙」に添加する量は、「珪藻土紙」ある
いは「高填料紙」中の各成分の割合および所望する特性
(強度等)によって変化するが、添加剤(サイズ剤、紙
力増強剤および歩留向上剤)の合計量は、「珪藻土紙」
の場合には、全重量に対して0.2〜1.7重量%であ
ることが好ましく、「高填料紙」の場合には、全重量に
対して0.2〜1.7重量%であることが好ましい。
The amount of the above-described additive added to the "diatomaceous earth paper" or the "high filling paper" is the proportion of each component in the "diatomaceous earth paper" or the "high filling paper" and the desired characteristics (strength, etc.). The total amount of additives (size, paper strengthening agent and retention aid) varies depending on "diatomaceous earth paper".
In the case of, the content is preferably 0.2 to 1.7% by weight based on the total weight, and in the case of "highly-filled paper", the content is 0.2 to 1.7% by weight based on the total weight. Preferably there is.
【0060】また添加剤中のサイズ剤、紙力増強剤およ
び歩留向上剤の各割合もまた、「珪藻土紙」あるいは
「高填料紙」中の各成分の割合および所望する特性(強
度等)によって変化する。例えば、「珪藻土紙」の場合
には、全重量に対してサイズ剤が0.1〜1.0重量
%、紙力増強剤が0.1〜0.5重量%、歩留向上剤が
0.05〜0.2重量%であることが好ましく、「高填
料紙」の場合には、全重量に対してサイズ剤が0.1〜
1.0重量%、紙力増強剤が0.1〜0.5重量%、歩
留向上剤が0.05〜0.2重量%であることが好まし
い。
The proportions of the sizing agent, paper strength enhancer and retention aid in the additives are also the proportions of the respective components in the "diatomaceous earth paper" or the "highly filled paper" and the desired characteristics (strength, etc.). It depends on For example, in the case of "diatomaceous earth paper", the sizing agent is 0.1 to 1.0% by weight, the paper strengthening agent is 0.1 to 0.5% by weight, and the retention aid is 0% to the total weight. It is preferably 0.05 to 0.2% by weight, and in the case of "highly-filled paper", the sizing agent is 0.1 to 0.1% with respect to the total weight.
It is preferable that the content of the paper strength enhancer is 0.1 to 0.5% by weight, and the amount of the retention improver is 0.05 to 0.2% by weight.
【0061】これらの添加剤は、「珪藻土紙」あるいは
「高填料紙」を製造する途中で調成される「珪藻土紙」
用スラリーあるいは「高填料紙」用スラリー中に添加
(内添)され、抄造されることにより、所定の強度等を
有する「珪藻土紙」および「高填料紙」が作製される。
また必要に応じて、上記説明した添加剤に加えて防かび
剤などの添加剤をを更に添加しても良い。
These additives are "diatomaceous earth paper" prepared during the production of "diatomaceous earth paper" or "highly-filled paper".
The "diatomaceous earth paper" and "high-filler paper" having a predetermined strength and the like are produced by adding (internally adding) to the slurry for use or "high-filler paper" and making a paper.
If necessary, in addition to the additives described above, additives such as antifungal agents may be further added.
【0062】また上記のサイズ剤、紙力増強剤および歩
留向上剤は、作製する「珪藻土紙」あるいは「高填料
紙」の特性に応じて、それぞれ最適な種類を選択し、さ
らに各添加量の割合いを「珪藻土紙」あるいは「高填料
紙」に適した量に最適化することにより、更に「珪藻土
紙」および「高填料紙」の強度等を向上することができ
る。
The above-mentioned sizing agent, paper strength enhancer and retention aid are selected according to the characteristics of the "diatomaceous earth paper" or "highly-filled paper" to be produced, and the addition amount of each is selected. By optimizing the ratio of “diatomaceous earth paper” or “high filling paper” to an amount suitable for “diatomaceous earth paper” or “high filling paper”, the strength of “diatomaceous earth paper” and “high filling paper” can be further improved.
【0063】また本実施形態の「珪藻土紙」あるいは
「高填料紙」で使用する添加剤は、上記説明したスラリ
ーに添加(内添)する添加剤の他に、「珪藻土紙」ある
いは「高填料紙」の表面のみに添加(外添)し、「珪藻
土紙」あるいは「高填料紙」の表面性状、例えば、表面
紙力の向上などするために必要に応じて添加される添加
剤を含んでも良い。外添する添加剤とは、例えば、酸化
デンプン等を用いることができる。
The additives used in the “diatomaceous earth paper” or the “highly filled paper” of the present embodiment include the “diatomaceous earth paper” or the “highly filled paper” in addition to the additive added (internally added) to the slurry described above. It may be added (externally added) only to the surface of "paper", and may include additives that are added as needed to improve the surface properties of "diatomaceous earth paper" or "highly-filled paper", for example, surface paper strength. good. As the additive to be added externally, for example, oxidized starch or the like can be used.
【0064】[珪藻土紙あるいは高填料紙の配合:図
1]以上説明した各原料より「珪藻土紙」あるいは「高
填料紙」を製造するための好適な配合およびより好適な
配合をまとめたものを図1に示す。
[Composition of diatomaceous earth paper or high-filler paper: FIG. 1] A suitable composition for producing “diatomaceous earth paper” or “high-filler paper” and a more suitable composition are summarized below. As shown in FIG.
【0065】[珪藻土紙の製造方法:図2]上記説明し
た各原料を用いる本実施形態の「珪藻土紙」あるいは
「高填料紙」の製造方法について以下説明する。まず珪
藻土紙の製造方法について、図2を参照して説明する。
[Method for producing diatomaceous earth paper: FIG. 2] A method for producing "diatomaceous earth paper" or "highly-filled paper" of the present embodiment using the above-mentioned raw materials will be described below. First, a method for manufacturing diatomaceous earth paper will be described with reference to FIG.
【0066】[原料の調成]図2の原料で、パルプ、珪
藻土、内添する添加剤について説明する。所定のフリー
ネスを有するパルプは、上記説明した原料パルプから選
択され、公知技術により調成された原料パルプから所定
濃度、例えば、数%のパルプスラリーを作製し、このパ
ルプスラリーを叩解装置であるDDRで所定のフリーネ
ス(例えば、100〜200ml)となるまで叩解する
ことによって得られる。
[Preparation of Raw Materials] The pulp, diatomaceous earth, and additives internally added to the raw materials shown in FIG. 2 will be described. The pulp having a predetermined freeness is selected from the above-described raw material pulp, and a pulp slurry having a predetermined concentration, for example, several% is prepared from the raw material pulp prepared by a known technique, and the pulp slurry is a beating apparatus DDR. It is obtained by beating at a predetermined freeness (for example, 100 to 200 ml).
【0067】珪藻土は、使用前に十分精製・乾燥された
もの、または乾燥品を焼成したものを用いる。
As the diatomaceous earth, one which has been sufficiently purified and dried before use, or one obtained by baking a dried product is used.
【0068】また内添する添加剤としては、上記説明し
た添加剤の中から選択されたサイズ剤、紙力増強剤、歩
留向上剤を所望の特性(強度等)が得られるように所定
量ずつ配合して得られる。
As the additives to be added internally, a sizing agent selected from the above-mentioned additives, a paper strength enhancer, and a retention improver in predetermined amounts so as to obtain desired characteristics (strength, etc.). It is obtained by blending each.
【0069】[調成工程]次に、図2の調成工程(珪藻
土入りパルプスラリーの調成)について説明する。上記
調成された原料パルプ、珪藻土、内添する添加剤を「珪
藻土紙」中に所定濃度となるように配合してから均一に
混合し、珪藻土入りパルプのインレット濃度、約1〜2
重量%のスラリーを得る。
[Preparation Step] Next, the preparation step in FIG. 2 (preparation of diatomaceous earth-containing pulp slurry) will be described. The above-prepared raw material pulp, diatomaceous earth, and additives to be added internally are blended in "diatomaceous earth paper" so as to have a predetermined concentration and then uniformly mixed, and the inlet concentration of the diatomaceous earth-containing pulp is about 1-2.
A weight% slurry is obtained.
【0070】[抄造工程]次に、図2の抄造工程(「珪
藻土紙」の抄造)について説明する。調成工程で調成さ
れた珪藻土入りパルプスラリーは、長網多筒式抄紙機を
用いて「珪藻土紙」に抄造される。
[Papermaking Step] Next, the papermaking step of FIG. 2 (papermaking of "diatomaceous earth paper") will be described. The pulp slurry containing diatomaceous earth prepared in the preparation step is made into "diatomaceous earth paper" by using a Fourdrinier multi-cylinder paper machine.
【0071】すなわち、所定濃度に調成された珪藻土入
りパルプスラリーをストイックインレットに送り、ワイ
ヤーパートにおいて珪藻土入りパルプスラリーをワイヤ
ー上に流出させて、原料を脱水し紙層を形成させてか
ら、プレスパートでさらに紙層の水分を低下させる。次
のプレドライヤーパートで紙層を乾燥させてから、サイ
ズプレスを用いて「珪藻土紙」の表面に外添する添加剤
を塗工後、再びアフタードライヤーパートにて乾燥させ
る。
That is, the diatomaceous earth-containing pulp slurry adjusted to a predetermined concentration is sent to the stoic inlet, the diatomaceous earth-containing pulp slurry is allowed to flow out onto the wire in the wire part, and the raw material is dehydrated to form a paper layer, followed by pressing. In the part, further reduce the water content of the paper layer. After the paper layer is dried in the next pre-dryer part, an external additive is applied to the surface of the “diatomaceous earth paper” using a size press, and then dried in the after-dryer part.
【0072】[仕上工程]次に、図2の仕上工程(表面
仕上げ)について説明する。乾燥させた「珪藻土紙」を
スーパーキャレンダーに通紙することにより、所定の紙
厚、表面平滑度を有する「珪藻土紙」を得る。
[Finishing Step] Next, the finishing step (surface finishing) of FIG. 2 will be described. By passing the dried "diatomaceous earth paper" through a super calender, "diatomaceous earth paper" having a predetermined paper thickness and surface smoothness is obtained.
【0073】[高填料紙の製造方法:図3]次に、上記
説明した各原料を用いる本実施形態の「高填料紙」の製
造方法について、図3を参照して説明する。
[Manufacturing Method of High-Filling Paper: FIG. 3] Next, a manufacturing method of the “high-filling paper” of the present embodiment using each raw material described above will be described with reference to FIG.
【0074】なお図3の「高填料紙」の製造方法は、図
2の「珪藻土紙」の製造方法と類似する製造方法であ
る。従って、以下に示す「高填料紙」の製造方法では、
「珪藻土紙」と共通する部分の内容の説明は省略し、異
なる点についてのみ説明することとする。
The method for producing the "high-filler paper" in FIG. 3 is similar to the method for producing the "diatomaceous earth paper" in FIG. Therefore, in the method for producing "highly-filled paper" shown below,
The description of the contents in common with “diatomaceous earth paper” is omitted, and only the different points will be explained.
【0075】[原料の調成]まず図3の原料(パルプ、
珪藻土、無機質材料、内添する添加剤)について説明す
る。
[Preparation of Raw Material] First, the raw material (pulp,
The diatomaceous earth, the inorganic material, and the additive added internally will be described.
【0076】パルプ、珪藻土、無機質材料、内添する添
加剤の調成方法は、「珪藻土紙」の場合と同様であるの
で、その説明は重複するので省略する。
The method for preparing the pulp, diatomaceous earth, the inorganic material, and the additives to be added internally is the same as in the case of "diatomaceous earth paper", and the description thereof will be omitted to avoid duplication.
【0077】また無機質材料は、上記説明した無機質材
料から選択された無機質材料を必要に応じて1種あるい
は2種以上複合して用いる。
As the inorganic material, one kind or a combination of two or more kinds of inorganic materials selected from the above-mentioned inorganic materials is used as necessary.
【0078】[調成工程]次に、図3の調成工程(珪藻
土および無機質材料入りパルプスラリーの調成)につい
て説明する。上記調成された原料パルプ、珪藻土、無機
質材料および内添する添加剤を「高填料紙」中に所定濃
度となるように配合してから均一に混合し、珪藻土およ
び無機質材料を含むパルプのインレット濃度約1〜2重
量%のスラリーを得る。
[Preparation Step] Next, the preparation step in FIG. 3 (preparation of diatomaceous earth and pulp slurry containing inorganic material) will be described. The above-prepared raw material pulp, diatomaceous earth, an inorganic material, and an additive to be internally added are blended in a "high-filler paper" to a predetermined concentration and then uniformly mixed, and a pulp inlet containing the diatomaceous earth and the inorganic material is mixed. A slurry with a concentration of about 1-2% by weight is obtained.
【0079】[抄造工程]次に、図3の抄造工程(「高
填料紙」の抄造)について説明する。調成工程で調成さ
れた珪藻土および無機質材料入りパルプスラリーは、長
網多筒式抄紙機を用いて「高填料紙」に抄造される。
[Papermaking Process] Next, the papermaking process of FIG. 3 (papermaking of "highly-filled paper") will be described. The pulp slurry containing the diatomaceous earth and the inorganic material prepared in the preparation step is made into a "high-filler paper" by using a Fourdrinier multi-cylinder paper machine.
【0080】[仕上工程]次に、図3の仕上工程(表面
仕上げ)について説明する。乾燥させた「高填料紙」を
スーパーキャレンダーに通紙することにより、所定の紙
厚、表面平滑度を有する「高填料紙」を得る。
[Finishing Step] Next, the finishing step (surface finishing) of FIG. 3 will be described. The dried "high-filler paper" is passed through a super calender to obtain "high-filler paper" having a predetermined paper thickness and surface smoothness.
【0081】このようにして得られる「珪藻土紙」およ
び「高填料紙」は、紙の強度等が強く、適正な層間強度
等を有しているため加工時の作業性に富んでおりかつ表
面が滑らかで、印刷適正に優れている。
The "diatomaceous earth paper" and "highly-filled paper" thus obtained have strong paper strength and the like, and have suitable interlayer strength, etc. Is smooth and has excellent printability.
【0082】なお上記説明した「珪藻土紙」および「高
填料紙」の抄紙方法は、特に限定されるものではなく、
酸性抄紙、中性抄紙、アルカリ性抄紙のいずれであって
もよく、用いるパルプは、NBKP、LBKPなどの化
学パルプの他、TMPなどの高歩留パルプを含む中質原
紙あるいは回収古紙パルプも使用できる。
The method for making the "diatomaceous earth paper" and the "highly filled paper" described above is not particularly limited,
It may be any of acid papermaking, neutral papermaking, and alkaline papermaking. The pulp to be used can be chemical pulp such as NBKP and LBKP, as well as medium quality raw paper containing high yield pulp such as TMP or recovered wastepaper pulp. .
【0083】また、添加剤としては、上記説明した紙力
増強剤、歩留向上剤、サイズ剤の他に、例えば、顔料、
着色染料、等の抄紙用補助薬品をパルプスラリーに必要
に応じて添加してもよい。
Further, as the additive, in addition to the paper strength enhancer, the retention improver and the sizing agent described above, for example, a pigment,
If necessary, a papermaking auxiliary agent such as a coloring dye may be added to the pulp slurry.
【0084】また、抄造については、長網多筒式抄紙機
に限ることはなく、公知の抄紙機で抄造してもよい。
Further, the papermaking is not limited to the fourdrinier cylinder type paper machine, but may be made by a known paper machine.
【0085】なお本実施形態では、上記のようにして得
られた「珪藻土紙」あるいは「高填料紙」を、抄造した
後、その原紙をスーパーキャレンダーに通紙して仕上げ
処理しているが、キャレンダー圧力、ニップ数について
は特に限定されず、要求される品質に応じて適宜選択し
て使用することができる。またスーパーキャレンダーに
オンライン方式で仕上げ処理する場合も同様である。
In this embodiment, after the "diatomaceous earth paper" or "highly-filled paper" obtained as described above is made into paper, the base paper is passed through a super calender for finishing treatment. The calender pressure and the number of nips are not particularly limited, and can be appropriately selected and used according to the required quality. The same applies to the case where the online calendering is applied to the super calender.
【0086】[実施例:図4、5]上記説明した「珪藻
土紙」および「高填料紙」の製造方法に基づいて、各種
配合の「珪藻土紙」および「高填料紙」をそれぞれ作製
し、それらの製紙強度およびワンパスリテンションを測
定した結果を図4および図5に示す。
[Examples: FIGS. 4 and 5] Based on the above-described method for producing "diatomaceous earth paper" and "high filling paper", various formulations of "diatomaceous earth paper" and "high filling paper" were prepared, The results of measuring the papermaking strength and the one-pass retention are shown in FIGS. 4 and 5.
【0087】また図4および図5には、本実施例の「珪
藻土紙」および「高填料紙」と比較するために比較例1
および比較例2の配合で作製した紙の製紙強度およびワ
イヤー上の歩留まり率を示すワンパスリテンションを評
価した結果をあわせて示す。
4 and 5 show Comparative Example 1 for comparison with the "diatomaceous earth paper" and the "high filler paper" of this Example.
The results of evaluation of one-pass retention indicating the paper-making strength and the yield rate on the wire of the paper prepared with the composition of Comparative Example 2 are also shown.
【0088】図4の「珪藻土紙1」〜「珪藻土紙4」
は、フリーネスが100mlまたは200mlのパルプ
(針葉樹晒クラフトパルプ(NBKP))に珪藻土を全
重量に対して30重量%または80重量%、添加剤とし
て全重量の1.0重量%含有させたものである。また添
加剤としては、サイズ剤、紙力増強剤および歩留向上剤
を用いた。
"Diatomaceous earth paper 1" to "diatomaceous earth paper 4" in FIG.
Is a pulp (freewood bleached kraft pulp (NBKP)) having a freeness of 100 ml or 200 ml and containing diatomaceous earth in an amount of 30% by weight or 80% by weight, and 1.0% by weight of the total weight as an additive. is there. As the additives, a sizing agent, a paper strengthening agent and a retention improving agent were used.
【0089】また「比較例1−1」および「比較例1−
2」は、「珪藻土紙1」および「珪藻土紙2」と同じ配
合で、針葉樹晒クラフトパルプ(NBKP)のフリーネ
スを450mlとしたものである。
Also, "Comparative Example 1-1" and "Comparative Example 1-"
"2" has the same composition as "diatomaceous earth paper 1" and "diatomaceous earth paper 2", and the freeness of softwood bleached kraft pulp (NBKP) is 450 ml.
【0090】「珪藻土紙1」〜「珪藻土紙4」は、図4
に示すように「珪藻土紙」としての製紙強度を有するこ
とが示されたが、「比較例1−1」および「比較例1−
2」は、「珪藻土紙」としての製紙強度を有さないこと
が示された。また「珪藻土紙1」〜「珪藻土紙4」のワ
イヤー上の歩留まり率を示すワンパスリテンション(8
2〜93%)は、「比較例1−1」および「比較例1−
2」のワンパスリテンション(59〜60%)に比べて
高いことも示された。
"Diatomaceous earth paper 1" to "diatomaceous earth paper 4" are shown in FIG.
It was shown that it has a papermaking strength as "diatomaceous earth paper" as shown in Table 1. However, "Comparative Example 1-1" and "Comparative Example 1-"
It was shown that "2" does not have papermaking strength as "diatomaceous earth paper". In addition, the one-pass retention (8) indicating the yield rate on the wire of "diatomaceous earth paper 1" to "diatomaceous earth paper 4"
2 to 93%), "Comparative Example 1-1" and "Comparative Example 1-"
It was also shown to be higher than the one-pass retention of 2 ”(59 to 60%).
【0091】上記の結果から、珪藻土を全重量の30〜
80重量%含む「珪藻土紙」が壁紙としての特性(強
度、ワンパスリテンションなど)を示すには、フリーネ
スが100〜200mlのパルプと所定量の添加剤(サ
イズ剤、紙力増強剤および歩留向上剤)を含む必要があ
ることが示された。
From the above results, the total weight of diatomaceous earth is 30 to 30%.
In order to show the properties (strength, one-pass retention, etc.) as wallpaper of "diatomaceous earth paper" containing 80% by weight, pulp with a freeness of 100 to 200 ml and a predetermined amount of additives (size agent, paper strengthening agent and yield improvement). It has been shown that it is necessary to include an agent).
【0092】図5の「高填料紙1」〜「高填料紙6」
は、フリーネスが100mlまたは200mlのパルプ
(針葉樹晒クラフトパルプ(NBKP))に珪藻土と無
機質材料を全重量に対して30、50重量%または85
重量%、添加剤として全重量の1.0重量%含有させた
ものである。また添加剤としては、サイズ剤、紙力増強
剤および歩留向上剤を用いた。
"Highly Filled Paper 1" to "Highly Filled Paper 6" in FIG.
Is a pulp (freewood bleached kraft pulp (NBKP)) with a freeness of 100 ml or 200 ml, and diatomaceous earth and an inorganic material with respect to the total weight of 30, 50% by weight or 85%.
%, And 1.0% by weight of the total weight as an additive. As the additives, a sizing agent, a paper strengthening agent and a retention improving agent were used.
【0093】また「比較例2−1」および「比較例2−
2」は、「高填料紙1」および「高填料紙3」と同じ配
合で、針葉樹晒クラフトパルプ(NBKP)のフリーネ
スを450mlとしたものである。
[Comparative Example 2-1] and [Comparative Example 2-
"2" has the same composition as "highly filled paper 1" and "highly filled paper 3", and the freeness of softwood bleached kraft pulp (NBKP) is 450 ml.
【0094】「高填料紙1」〜「高填料紙6」は、図5
に示すように「高填料紙」としての製紙強度を有するこ
とが示されたが、「比較例2−1」および「比較例2−
2」は、「高填料紙」としての製紙強度を有さないこと
が示された。また「高填料紙1」〜「高填料紙6」のワ
イヤー上の歩留まり率を示すワンパスリテンション(8
0〜90%)は、「比較例2−1」および「比較例2−
2」のワンパスリテンション(56〜57%)に比べて
高いことも示された。
"Highly-filled paper 1" to "highly-filled paper 6" are shown in FIG.
It was shown that it has a paper-making strength as "highly-filled paper" as shown in No. 2, but "Comparative Example 2-1" and "Comparative Example 2-
It was shown that "2" does not have papermaking strength as "highly-filled paper". In addition, the one-pass retention (8) indicating the yield rate on the wire of "high filling paper 1" to "high filling paper 6"
0 to 90%) is “Comparative Example 2-1” and “Comparative Example 2-
It was also shown to be higher than the one-pass retention of 2 ”(56 to 57%).
【0095】上記の結果から、珪藻土と無機質材料を全
重量の30〜85重量%含む「高填料紙」が壁紙として
の特性(強度、ワンパスリテンションなど)を示すに
は、フリーネスが100〜200mlのパルプと所定量
の添加剤(サイズ剤、紙力増強剤および歩留向上剤)を
含む必要があることが示された。
From the above results, in order to show the characteristics (strength, one-pass retention, etc.) as wallpaper, "high filler paper" containing diatomaceous earth and inorganic material in an amount of 30 to 85% by weight based on the total weight, the freeness is 100 to 200 ml. It has been shown that it is necessary to include pulp and a certain amount of additives (sizes, strength agents and retention aids).
【0096】[0096]
【発明の効果】以上説明したように、本発明によれば、
建材などから発生する有害ガスを吸収し、さらに室内の
湿度を調整可能な、消臭性能や調湿性能に優れる珪藻土
を多く含む壁紙およびその製造方法を提供できる。
As described above, according to the present invention,
It is possible to provide a wallpaper containing a large amount of diatomaceous earth capable of absorbing harmful gas generated from building materials and adjusting indoor humidity and having excellent deodorant performance and humidity control performance, and a method for producing the same.
【0097】またさらに、建材などから発生する有害ガ
スを吸収し、さらに室内の湿度を調整可能な、消臭性能
や調湿性能に優れる珪藻土や無機質材料を多く含み、さ
らに配合により難燃性や不燃性を示す高填料紙およびそ
の製造方法を提供できる。
Furthermore, it contains a large amount of diatomaceous earth and an inorganic material capable of absorbing harmful gas generated from building materials and adjusting the indoor humidity and excellent in deodorant performance and humidity control performance. A highly-filled paper exhibiting nonflammability and a method for producing the same can be provided.
【0098】また壁紙の表紙や裏打ち紙だけでなく、珪
藻土の特性を生かして、他の用途にも利用できる。
Further, it can be used not only for the front cover and backing paper of wallpaper, but also for other purposes by utilizing the characteristics of diatomaceous earth.
【図面の簡単な説明】[Brief description of drawings]
【図1】本発明に係る一実施形態の珪藻土紙および高填
料紙の組成を示す図である。
FIG. 1 is a diagram showing the composition of diatomaceous earth paper and highly-filled paper according to one embodiment of the present invention.
【図2】本発明に係る一実施形態の珪藻土紙の製造方法
を説明する図である。
FIG. 2 is a diagram illustrating a method for manufacturing diatomaceous earth paper according to an embodiment of the present invention.
【図3】本発明に係る一実施形態の高填料紙の製造方法
を説明する図である。
FIG. 3 is a diagram illustrating a method for manufacturing highly filled paper according to an embodiment of the present invention.
【図4】本発明に係る一実施形態の珪藻土紙の配合と製
紙強度などの関係を説明する図である。
FIG. 4 is a diagram for explaining the relationship between the formulation of diatomaceous earth paper and the strength of papermaking according to an embodiment of the present invention.
【図5】本発明に係る一実施形態の高填料紙の配合と製
紙強度などの関係を説明する図である。
FIG. 5 is a diagram illustrating the relationship between the composition of the high-filler paper and the papermaking strength according to the embodiment of the present invention.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 橋川 雅弘 石川県金沢市金石北3丁目1番1号 三善 製紙株式会社内 (72)発明者 木寅 且彦 兵庫県伊丹市東有岡5丁目125番地 東リ 株式会社内 Fターム(参考) 4L055 AA02 AC06 AG25 AG40 AG50 AG72 AG80 AG99 AH01 AH11 AH16 AH18 AH50 EA05 EA32 FA30 GA23 GA27 GA38    ─────────────────────────────────────────────────── ─── Continued front page    (72) Inventor Masahiro Hashikawa             3-1-1, Kanaishikita, Kanazawa, Ishikawa Prefecture             Paper Manufacturing Co., Ltd. (72) Inventor Katsuhiko Kita             5-125 Higashiarioka, Itami-shi, Hyogo Tori             Within the corporation F-term (reference) 4L055 AA02 AC06 AG25 AG40 AG50                       AG72 AG80 AG99 AH01 AH11                       AH16 AH18 AH50 EA05 EA32                       FA30 GA23 GA27 GA38

Claims (17)

    【特許請求の範囲】[Claims]
  1. 【請求項1】 全重量の30〜80重量%の珪藻土と、 所定のフリーネスとなるように叩解されたパルプと、 前記珪藻土と前記パルプとの間の少なくとも結合強度を
    高める添加剤と、を含むことを特徴とする珪藻土を含む
    珪藻土紙。
    1. A diatomaceous earth in an amount of 30 to 80% by weight based on the total weight, a pulp beaten to have a predetermined freeness, and an additive which enhances at least a bond strength between the diatomaceous earth and the pulp. A diatomaceous earth paper containing diatomaceous earth characterized by the above.
  2. 【請求項2】 前記パルプは、前記フリーネスが100
    〜200mlとなるように調成されていることを特徴と
    する請求項1に記載の珪藻土を含む珪藻土紙。
    2. The pulp has a freeness of 100.
    The diatomaceous earth paper containing diatomaceous earth according to claim 1, wherein the diatomaceous earth paper is prepared so as to have a volume of up to 200 ml.
  3. 【請求項3】 前記添加剤は、全重量の0.2〜1.7
    重量%含まれることを特徴とする請求項1または請求項
    2に記載の珪藻土を含む珪藻土紙。
    3. The additive has a total weight of 0.2 to 1.7.
    The diatomaceous earth paper containing the diatomaceous earth according to claim 1 or 2, wherein the diatomaceous earth paper is contained in a weight percentage.
  4. 【請求項4】 前記添加剤には、サイズ剤、紙力増強
    剤、歩留向上剤が含まれることを特徴とする請求項1乃
    至請求項3のいずれか1項に記載の珪藻土を含む珪藻土
    紙。
    4. The diatomaceous earth containing the diatomaceous earth according to claim 1, wherein the additive includes a sizing agent, a paper strengthening agent, and a retention improving agent. paper.
  5. 【請求項5】 前記サイズ剤は、パルプを疎水化する構
    造を含む樹脂から選択され、前記紙力増強剤は、パルプ
    の水酸基と水素結合を形成するあるいは3次元化した網
    目構造でパルプを固定して強度を増加させる性能を有す
    る水溶性樹脂から選択され、前記歩留向上剤は、ワイヤ
    ーパートでの歩留まり率を示すワンパスリテンションを
    向上させる水溶性樹脂から選択されることを特徴とする
    請求項4に記載の珪藻土を含む珪藻土紙。
    5. The sizing agent is selected from resins containing a structure that hydrophobizes the pulp, and the paper strength agent forms a hydrogen bond with a hydroxyl group of the pulp or fixes the pulp in a three-dimensional network structure. Selected from water-soluble resins having the ability to increase strength, wherein the retention aid is selected from water-soluble resins that improve one-pass retention, which indicates the yield rate in the wire part. A diatomaceous earth paper containing the diatomaceous earth according to 4.
  6. 【請求項6】 前記サイズ剤は、オレフィン系樹脂、ア
    ルキルケテンダイマー、スチレンアクリル系樹脂および
    ロジン系のうちの少なくともいずれか1つを含み、前記
    紙力増強剤は、ポリアクリルアミド系樹脂、ポリアミド
    エピクロロヒドリン樹脂、メラミン樹脂、尿素樹脂およ
    びポリアミド樹脂のうちの少なくともいずれか1つを含
    み、前記歩留向上剤は、ポリアクリルアミド系樹脂、ス
    チレン系樹脂、ポリアミド縮合物および多価フェノール
    系樹脂のうちの少なくともいずれか1つを含むことを特
    徴とする請求項5に記載の珪藻土を含む珪藻土紙。
    6. The sizing agent includes at least one of an olefin resin, an alkyl ketene dimer, a styrene acrylic resin, and a rosin resin, and the paper strengthening agent is a polyacrylamide resin or a polyamide epi resin. It contains at least one of chlorohydrin resin, melamine resin, urea resin and polyamide resin, and the retention agent is a polyacrylamide resin, styrene resin, polyamide condensate or polyhydric phenol resin. The diatomaceous earth paper containing the diatomaceous earth according to claim 5, characterized in that at least one of them is contained.
  7. 【請求項7】 前記サイズ剤を全重量の0.1〜1.0
    重量%、前記紙力増強剤を全重量の0.1〜0.5重量
    %、前記歩留向上剤を全重量の0.05〜0.2重量%
    含むことを特徴とする請求項4に記載の珪藻土を含む珪
    藻土紙。
    7. The total weight of the sizing agent is 0.1 to 1.0.
    % By weight, 0.1 to 0.5% by weight of the paper-strength enhancing agent, and 0.05 to 0.2% by weight of the retention aid.
    A diatomaceous earth paper containing the diatomaceous earth according to claim 4, characterized in that it contains.
  8. 【請求項8】 所定のフリーネスとなるように叩解され
    たパルプと、 珪藻土と、 無機質材料と、 前記パルプ、前記珪藻土および前記無機質材料の間の少
    なくとも結合強度を高める添加剤とを含み、 前記珪藻土と前記無機質材料とを合わせた量が全重量の
    30〜85重量%となるように調成されていることを特
    徴とする珪藻土と無機質材料とを含む高填料紙。
    8. A diatomaceous earth comprising: a pulp beaten to a predetermined freeness; a diatomaceous earth; an inorganic material; and an additive that enhances at least the bonding strength between the pulp, the diatomaceous earth and the inorganic material. A high-filler paper containing diatomaceous earth and an inorganic material, which is prepared so that the total amount of the above and the inorganic material is 30 to 85% by weight of the total weight.
  9. 【請求項9】 前記パルプは、フリーネスが100〜2
    00mlであることとを特徴とする請求項8に記載の珪
    藻土と無機質材料とを含む高填料紙。
    9. The freeness of the pulp is 100 to 2
    It is 00 ml, The high filler paper containing the diatomaceous earth and the inorganic material of Claim 8 characterized by the above-mentioned.
  10. 【請求項10】 前記添加剤は、全重量の0.2〜1.
    7重量%含まれることを特徴とする請求項8または請求
    項9に記載の珪藻土と無機質材料とを含む高填料紙。
    10. The additive comprises 0.2-1.
    The high-filler paper containing the diatomaceous earth according to claim 8 or 9, characterized in that the content is 7% by weight.
  11. 【請求項11】 前記無機材料は、水酸化アルミニウ
    ム、クレー、カオリン、焼成カオリン、タルク、炭酸カ
    ルシウムあるいは二酸化チタン、水酸化チタン等のチタ
    ン酸化物又は水酸化物、硫酸バリウム、酸化亜鉛、硫酸
    カルシウム、酸化アルミニウム、炭酸マグネシウム、酸
    性白土、珪藻頁岩、ケイ酸塩鉱物およびホワイトカーボ
    ンから選択された1種または2種以上を複合して使用す
    ることを特徴とする請求項8に記載の珪藻土と無機質材
    料とを含む高填料紙。
    11. The inorganic material is aluminum hydroxide, clay, kaolin, calcined kaolin, talc, calcium carbonate or titanium dioxide or titanium oxide or hydroxide such as titanium hydroxide, barium sulfate, zinc oxide, calcium sulfate. The diatomaceous earth according to claim 8, wherein the diatomaceous earth and the inorganic substance are used in combination with one or more selected from the group consisting of aluminum oxide, magnesium carbonate, acid clay, diatom shale, silicate minerals and white carbon. Highly-filled paper containing materials and.
  12. 【請求項12】 前記添加剤は、サイズ剤、紙力増強
    剤、歩留向上剤を含むことを特徴とする請求項8に記載
    の珪藻土と無機質材料とを含む高填料紙。
    12. The high-filler paper containing diatomaceous earth and an inorganic material according to claim 8, wherein the additive includes a sizing agent, a paper strength enhancer, and a retention improver.
  13. 【請求項13】 前記サイズ剤は、パルプを疎水化する
    構造を含む樹脂から選択され、前記紙力増強剤は、パル
    プの水酸基と水素結合を形成するあるいは3次元化した
    網目構造でパルプを固定して強度を増加させる性能を有
    する水溶性樹脂から選択され、前記歩留向上剤は、ワイ
    ヤーパートでの歩留まり率を示すワンパスリテンション
    を向上させる水溶性樹脂から選択されることを特徴とす
    る請求項12に記載の珪藻土と無機質材料とを含む高填
    料紙。
    13. The sizing agent is selected from resins containing a structure that hydrophobizes pulp, and the paper strength agent forms a hydrogen bond with a hydroxyl group of the pulp or fixes the pulp in a three-dimensional network structure. Selected from water-soluble resins having the ability to increase strength, wherein the retention aid is selected from water-soluble resins that improve one-pass retention, which indicates the yield rate in the wire part. A high-filler paper containing the diatomaceous earth according to 12 and an inorganic material.
  14. 【請求項14】 前記サイズ剤は、オレフィン系樹脂、
    アルキルケテンダイマー、スチレンアクリル系樹脂およ
    びロジン系のうちの少なくともいずれか1つを含み、前
    記紙力増強剤は、ポリアクリルアミド系樹脂、ポリアミ
    ドエピクロロヒドリン樹脂、メラミン樹脂、尿素樹脂お
    よびポリアミド樹脂のうちの少なくともいずれか1つを
    含み、前記歩留向上剤は、ポリアクリルアミド系樹脂、
    スチレン系樹脂、ポリアミド縮合物および多価フェノー
    ル系樹脂のうちの少なくともいずれか1つを含むことを
    特徴とする請求項13に記載の珪藻土と無機質材料とを
    含む高填料紙。
    14. The sizing agent is an olefin resin,
    At least any one of an alkyl ketene dimer, a styrene acrylic resin and a rosin resin is used, and the paper strength agent is a polyacrylamide resin, a polyamide epichlorohydrin resin, a melamine resin, a urea resin or a polyamide resin. At least one of the above, the retention aid is a polyacrylamide resin,
    The high filler paper containing diatomaceous earth and an inorganic material according to claim 13, comprising at least one of a styrene resin, a polyamide condensate and a polyhydric phenol resin.
  15. 【請求項15】 前記サイズ剤を全重量の0.1〜1.
    0重量%、前記紙力増強剤を全重量の0.1〜0.5重
    量%、前記歩留向上剤を全重量の0.05〜0.2重量
    %含むことを特徴とする請求項12に記載の珪藻土と無
    機質材料とを含む高填料紙。
    15. The total size of the sizing agent is 0.1-1.
    13. The composition comprises 0% by weight, 0.1 to 0.5% by weight of the paper-strength enhancing agent, and 0.05 to 0.2% by weight of the retention improving agent. A high-filler paper containing the diatomaceous earth according to 1. and an inorganic material.
  16. 【請求項16】 パルプを所定のフリーネスとなるよう
    に叩解し、 前記叩解したパルプを、珪藻土と、さらに前記パルプと
    前記珪藻土との間の少なくとも結合強度を高める添加剤
    と混合して珪藻土入りパルプスラリーを調成し、 前記珪藻土入りパルプスラリーを抄造して前記珪藻土が
    全量の30〜80重量%となるように調成されている珪
    藻土紙を製造することを特徴とする珪藻土紙の製造方
    法。
    16. A pulp containing diatomaceous earth obtained by beating pulp so as to have a predetermined freeness, and mixing the beaten pulp with diatomaceous earth and an additive which enhances at least a bond strength between the pulp and the diatomaceous earth. A method for producing a diatomaceous earth paper, which comprises preparing a slurry, and making a pulp slurry containing the diatomaceous earth into a paper to prepare a diatomaceous earth paper in which the diatomaceous earth constitutes 30 to 80% by weight of the total amount.
  17. 【請求項17】 パルプを所定のフリーネスとなるよう
    に叩解し、 前記叩解したパルプを、珪藻土と、無機質材料と、さら
    に前記パルプ、前記珪藻土および前記無機質材料の間の
    少なくとも結合強度を高める添加剤と混合してスラリー
    を調成し、 前記スラリーを抄造し、前記珪藻土と前記無機質材料と
    を合わせた量が全重量の30〜85重量%となるように
    調成されている珪藻土と無機質材料を含有する高填料紙
    を製造することを特徴とする高填料紙の製造方法。
    17. An additive that enhances at least a bond strength between a diatomaceous earth, an inorganic material, and the pulp, the diatomaceous earth, and the inorganic material by beating the pulp so that the pulp has a predetermined freeness. And slurries are prepared by mixing the diatomaceous earth and the inorganic material so that the total amount of the diatomaceous earth and the inorganic material is 30 to 85% by weight of the total weight. A method for producing a highly-filled paper, comprising producing a highly-filled paper containing the same.
JP2002003880A 2002-01-10 2002-01-10 Diatomaceous earth containing diatomaceous earth, high-filler paper containing diatomaceous earth and inorganic materials, and methods for producing them Active JP3624377B2 (en)