JP2003090903A - Transmitting visible filter - Google Patents

Transmitting visible filter

Info

Publication number
JP2003090903A
JP2003090903A JP2002152816A JP2002152816A JP2003090903A JP 2003090903 A JP2003090903 A JP 2003090903A JP 2002152816 A JP2002152816 A JP 2002152816A JP 2002152816 A JP2002152816 A JP 2002152816A JP 2003090903 A JP2003090903 A JP 2003090903A
Authority
JP
Japan
Prior art keywords
transparent
line segment
transmission visibility
equilateral
visibility filter
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2002152816A
Other languages
Japanese (ja)
Inventor
Koji Muraoka
貢治 村岡
Original Assignee
Shuho:Kk
株式会社秀峰
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to JP2001-183066 priority Critical
Priority to JP2001183066 priority
Application filed by Shuho:Kk, 株式会社秀峰 filed Critical Shuho:Kk
Priority to JP2002152816A priority patent/JP2003090903A/en
Publication of JP2003090903A publication Critical patent/JP2003090903A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide an inexpensive transmitting visible filter which can effectively shield electromagnetic waves and reflected light. SOLUTION: The transmitting visible filter is produced by directly providing a transparent member or by providing a transparent film sheet member to be laminated on the transparent member with lines made of a conductive metal or containing conductive powder or magnetic powder as the profile lines of continuously formed equilateral polygons. The lines are formed to have 5 to 100 μm line width t, 5 to 100 μm thickness h, 0.01 to 0.50 mm minimum line distance (diameter ϕ of inscribed circles) and 1 to 30 ratio (A) of the inscribed circle diameter ϕ to the line width t.

Description

【発明の詳細な説明】Detailed Description of the Invention
【0001】[0001]
【発明の属する技術分野】本発明は、透過可視性フィル
タに関するものであり、より詳細には、透過可視部材に
おける、外部光線による反射、および電磁波の外部への
漏れを防止するための透過可視性フィルタに関するもの
である。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a transmission visibility filter, and more specifically, to a transmission visibility member for preventing reflection of external light rays and leakage of electromagnetic waves to the outside in a transmission visible member. It is about filters.
【0002】[0002]
【従来の技術】最近のコンピュータによる情報の拡大は
驚異的なものがあり、近年はビル全体が情報化の発信、
送信の集合体として構成されている、いわゆるインテリ
ジェント ビルなども多く建設されている。また、電子
機器類の市場拡大も目覚ましく、特にパソコンや携帯電
話などは、その至便性から普及の速度も著しいものがあ
る。しかしながら、一方これら電子機器類による不具合
も増加してきている。
2. Description of the Related Art The recent expansion of information by computers has been phenomenal, and in recent years, the entire building has become a source of information technology.
Many so-called intelligent buildings, which are configured as a transmission group, are also being constructed. In addition, the market of electronic devices has been remarkably expanding, and in particular, personal computers, mobile phones, and the like are very popular because of their convenience. However, on the other hand, defects due to these electronic devices are also increasing.
【0003】特に、電子機器類から発せられる電磁波に
よる各種の不具合は、電子機器類同士の誤動作発生など
のトラブルの他に、人体への影響は深刻な問題を提起し
ている。このためインテリジェント ビルのシールド方
法には色々な手段が用いられている。しかしながら、イ
ンテリジェント ビルにおける窓部や仕切戸部のごと
く、外側を透過可視可能である要求があるものは、透過
可視の条件とシールド条件とが相反するものであり、な
かなか両者を十分満足するものが得られていないのも事
実である。
In particular, various problems caused by electromagnetic waves emitted from electronic devices pose serious problems in that they affect the human body in addition to troubles such as malfunctions occurring between electronic devices. For this reason, various methods are used for the shielding method of intelligent buildings. However, in the case of windows and partition doors in intelligent buildings, where there is a requirement to be able to see and see through the outside, the conditions for seeing and seeing are in conflict with the shielding conditions, and it is quite easy to obtain the one that satisfies both conditions. It is also true that it has not been done.
【0004】インテリジェント ビルにおける窓部や仕
切戸部のガラスにシールドシートを添付したり、ガラス
そのものに金属線ネットを埋め込んだりして一応の電磁
波シールドの対策がされているが、透過可視の観点では
十分ではない。また、携帯電話のディスプレー部におい
てもケーシング部分のシールド度合いに比較して必ずし
も十分ではない。
Although a shield sheet is attached to the glass of a window or a partition door in an intelligent building, or a metal wire net is embedded in the glass itself, provisional electromagnetic wave shielding measures are taken. is not. Also, in the display part of a mobile phone, it is not always sufficient as compared with the degree of shielding of the casing part.
【0005】一方、外部からの光線による窓ガラス面や
電子画像表示装置のディスプレー画面などによる反射
(いわゆる写り込み)は、直接視覚に対する負荷とな
り、色々な視覚障害の原因となっている。勿論、従来で
も、これに対する対策がなされていないわけではない、
即ち、AGコート(Antiglare Coat)や
ARコート(Anti−Reflection Coa
t)を塗布することにより、この反射光をある程度防止
することができるが、ディスプレーとしての画像情報機
能は十分満足し得ない。
On the other hand, reflection (so-called reflection) by a window glass surface or a display screen of an electronic image display device due to a light beam from the outside directly imposes a load on the visual sense and causes various visual defects. Of course, even in the past, no measures have been taken against this,
That is, an AG coat (Antiglare Coat) and an AR coat (Anti-Reflection Coa)
By applying t), the reflected light can be prevented to some extent, but the image information function as a display cannot be sufficiently satisfied.
【0006】[0006]
【発明が解決しようとする課題】前述のごとく、インテ
リジェント ビルの窓部や仕切戸部におけるガラス面や
パソコン、携帯電話などの電子画像表示装置としてのデ
ィスプレー画面は、前記のごとく写り込みや漏れ電磁波
に対して色々の手段がとられてきてはいるが、これらの
手段では必ずしも十分とは言えない。即ち、インテリジ
ェント ビルの窓部や仕切戸部等におけるガラス面の電
磁波に対するシールドシートの使用や、金属線ネットの
封入は、外部に対する視野を極めて悪くし、居住空間と
しての機能を全く悪化させている。
As described above, the glass surface in the windows and partition doors of intelligent buildings and the display screens as electronic image display devices for personal computers, mobile phones, etc. are subject to reflections and leakage electromagnetic waves as described above. While various measures have been taken, these measures are not always sufficient. That is, the use of a shield sheet against electromagnetic waves on the glass surface and encapsulation of a metal wire net in the windows and partition doors of intelligent buildings make the field of view to the outside extremely bad, and the function as a living space is completely deteriorated.
【0007】また、携帯電話やパソコンなどのディスプ
レー画面にとって、外部からの光による反射光は、画像
情報機能の低下ばかりでなく、使用時間の長期化と相俟
って人体、特に視覚障害に対して重大な影響をもたらし
ている。従って、携帯電話やパソコンなどの電子画像表
示装置としてのディスプレー画面に、十分に透過可視可
能で、且つ電磁波のシールドおよび反射光防止効果のあ
る、しかも安価な透過可視性フィルタが強く要求されて
いる。
For display screens of mobile phones, personal computers, and the like, the reflected light caused by light from the outside not only deteriorates the image information function, but also prolongs the usage time, and Have serious consequences. Therefore, there is a strong demand for an inexpensive transmission visibility filter that is sufficiently transparent and visible on a display screen as an electronic image display device such as a mobile phone or a personal computer, and has an electromagnetic wave shielding and reflected light preventing effect. .
【0008】本発明は、これらに鑑み、電磁波に対する
シールドと反射光の防止とを、透過可視の条件のもとで
安価に得んとするところにその目的がある。
In view of the above, the present invention has an object to obtain a shield against electromagnetic waves and a prevention of reflected light at a low cost under the condition of transmission and visibility.
【0009】[0009]
【課題を解決するための手段】本発明のフィルタは、以
下の構成よりなるものである。 1)透明部材に直接または該透明部材に添付する透明フ
ィルムシート状部材に、連続形成した等辺多角形の輪郭
線分として、導電性金属による、または導電性粉末乃至
磁性粉体を含む、線分を、線幅tを5〜100μm、厚
さhを5〜100μm、最少線間距離(内接円直径φ)
を0.01〜0.50mm、且つ、内接円直径φと線幅
tの比Aを1〜30として設けたものである。
The filter of the present invention has the following configuration. 1) A line segment made of a conductive metal or containing a conductive powder or a magnetic powder as a contour line segment of an equilateral polygon formed continuously on a transparent member or a transparent film sheet member attached to the transparent member. The line width t is 5 to 100 μm, the thickness h is 5 to 100 μm, and the minimum line distance (inscribed circle diameter φ)
Is 0.01 to 0.50 mm, and the ratio A of the inscribed circle diameter φ to the line width t is 1 to 30.
【0010】2)前記等辺多角形を、二等辺三角形、正
三角形、等辺四角形、正方形、等辺六角形または正六角
形のいずれか1より選ばれたものとし、また、3)前記
線分を、粒度が0.1〜70μmの導電性金属粉末乃至
磁性粉体を5〜80wt%含有する艶消しインキを使用
した印刷により設けるものであり、更に、4)前記線分
を、第1ステップとして、拭き取り清浄化可能なインキ
により周辺を前記線幅に囲まれた前記等辺多角形面をマ
スキング面として印刷し、第2ステップとして該マスキ
ング面を印刷された部材の線幅部に、真空蒸着またはコ
ーティングにより前記導電性金属を線分として設け、第
3ステップとして前記マスキング面としてのインキを除
去する各ステップにより設けたものである。
2) The equilateral polygon is selected from any one of an isosceles triangle, an equilateral triangle, an equilateral quadrangle, a square, an equilateral hexagon and a regular hexagon, and 3) the line segment has a granularity. Is provided by printing using a matte ink containing 5 to 80 wt% of a conductive metal powder or magnetic powder of 0.1 to 70 μm, and 4) the line segment is wiped off as a first step. The equilateral polygonal surface surrounded by the line width is printed as a masking surface with a cleanable ink, and as a second step, the masking surface is vacuum-deposited or coated on the line width part of the printed member. The conductive metal is provided as a line segment, and the third step is provided by each step of removing the ink as the masking surface.
【0011】また、本発明は、5)前記艶消しインキ
を、その色相をマンセル色相環5GY〜5R(Bを含む
側)の範囲においては、明度6以下、彩度9以下、また
5BG〜5PB(Bを含む側)の範囲においては、明度
8以下、彩度10以下なる艶消インキとしたものであ
り、6)前記輪郭線分の色相をマンセル色相環の明度を
3以下の黒色または暗色とした場合、前記線幅tを5〜
70μm、内接円直径φと線幅tの比Aを10〜30、
但し、 内接円直径φを700μm以下としたものであ
り、また、7)前記導電性粉末または導電性金属を、少
なくとも、Cu、Ti、Fe、Ni、Mg、Au、A
g、またはそれらの各合金のうちの1種を含むものとし
たものである。
Further, according to the present invention, 5) the matte ink has a hue of 6 or less, a saturation of 9 or less, and 5BG to 5PB within the range of Munsell hue circles 5GY to 5R (the side including B). In the range of (side including B), a matte ink having a lightness of 8 or less and a saturation of 10 or less is used. 6) The hue of the contour line segment is black or dark with a lightness of 3 or less in the Munsell hue circle. And the line width t is 5 to
70 μm, the ratio A of the inscribed circle diameter φ and the line width t is 10 to 30,
However, the inscribed circle diameter φ is 700 μm or less, and 7) the conductive powder or conductive metal is at least Cu, Ti, Fe, Ni, Mg, Au, A
g, or one of those alloys.
【0012】更に、本発明は、8)記導電性粉末を、カ
ーボン繊維粉末とすることにより、更にまた、9)前記
透明部材をガラスまたはプラスチックとすることによ
り、また、10)前記透明部材のプラスチックを、ポリ
カーボネート、メタクリルまたはポリプロピレン樹脂と
することにより、また、11)前記透明部材に添付する
透明フィルムシート状部材を、ポリエチレン、ポリプロ
ピレン、ポリエチレンテレフタレート、ポリ塩化ビニリ
デン、アセテートのいずれかとするものである。
Further, in the present invention, 8) the conductive powder is carbon fiber powder, 9) the transparent member is glass or plastic, and 10) the transparent member. The plastic is polycarbonate, methacryl or polypropylene resin, and 11) the transparent film sheet member attached to the transparent member is any of polyethylene, polypropylene, polyethylene terephthalate, polyvinylidene chloride and acetate. .
【0013】更にまた、本発明は、12)前記マスキン
グ面としての印刷を、半乾燥状態または被印刷部材との
接着力が通常の50%以下である印刷とすることを特徴
とする透過可視性フィルタにより、また、13)前記線
分を、予め機械的または電気化学的に穿削構成された凹
溝を、埋め込むように形成された前記導電性粉末乃至磁
性粉体、または導電性金属による線分とすることによ
り、また、14)前記透明部材を、その全面または一部
を曲面により構成したものである。
Further, according to the present invention, 12) transmission visibility is characterized in that the printing as the masking surface is a semi-dry state or a printing in which an adhesive force with a member to be printed is 50% or less than usual. 13) A line made of the conductive powder or the magnetic powder or a conductive metal formed so as to fill the groove formed by mechanically or electrochemically cutting the line segment with a filter. In addition, 14), the transparent member is configured such that the whole surface or a part thereof is a curved surface.
【0014】[0014]
【発明の実施の形態】図1は、本発明の透過可視性フィ
ルタの1実施例である等辺六角形の線分として印刷した
印刷面を例示する説明図である。1は連続的に等辺六角
形の輪郭線分を印刷された面、2は該等辺六角形の線分
であり線幅tは約20μm、3は該線分に囲まれた等辺
六角形面、4は等辺六角形の内接円で直径は約100μ
m、(実色相は5PB5/10相当)である。図2は、
本発明の透過可視性フィルタの他の実施例である等辺四
角形(菱形)の線分として印刷した印刷面を示す図であ
る。5は連続的に等辺四角形の輪郭線分を印刷した印刷
面、6は該等辺四角形の線分であり線幅tは約20μ
m、7は線分6で囲まれた等辺四角形面、8は該等辺四
角形の内接円で直径は約100μm、(実色相は5PB
5/10相当)である。前記等辺四角形は正方形または
矩形でも良い。
1 is an explanatory view illustrating a printed surface printed as an equilateral hexagonal line segment which is an embodiment of a transmission visibility filter of the present invention. 1 is a surface on which contour lines of an equilateral hexagon are continuously printed, 2 is a line segment of the equilateral hexagon, and a line width t is about 20 μm, 3 is an equilateral hexagon surface surrounded by the line segment, 4 is an equilateral hexagonal inscribed circle with a diameter of approximately 100μ
m, (actual hue is equivalent to 5PB5 / 10). Figure 2
It is a figure which shows the printing surface printed as a line segment of an equilateral quadrangle (diamond) which is another Example of the transmission visibility filter of this invention. 5 is a printed surface on which contour lines of an equilateral quadrangle are continuously printed, 6 is a line segment of the equilateral quadrangle, and a line width t is about 20 μm.
m and 7 are equilateral quadrangular surfaces surrounded by the line segment 6, 8 is an inscribed circle of the equilateral quadrangular, the diameter is about 100 μm, and the actual hue is 5 PB.
Equivalent to 5/10). The equilateral quadrangle may be a square or a rectangle.
【0015】図3は、本発明の透過可視性フィルタの更
に他の実施例である正三角形の線分として印刷した印刷
面を示す図である。9は連続的に正三角形の輪郭線分を
印刷した面、10は前記正三角形の線分であり同じく線
幅は約20μm、11は線分10で囲まれた正三角形
面、12は該正三角形の内接円で、直径は約100μ
m、(実色相は5PB5/10相当)である。この正三
角形は、二等辺三角形であっても良い。図4は、周辺を
線分で囲まれた等辺六角形面をマスキング面として印刷
した状態を示す図である。13は連続的に等辺六角形を
マスキング面として印刷を施された面、14はマスキン
グ面の周辺である線幅約20μmの非印刷線分、15は
等辺六角形をマスキング面として印刷を施された印刷面
である。マスキング厚さは約約5μmである。前記マス
キング面は、等辺六角形面以外の等辺四角形面または二
等辺三角形面でもよい。
FIG. 3 is a diagram showing a printed surface printed as an equilateral triangle line segment which is still another embodiment of the transmission visibility filter of the present invention. Reference numeral 9 is a surface on which contour lines of an equilateral triangle are continuously printed, 10 is a line segment of the equilateral triangle, the line width is also about 20 μm, 11 is an equilateral triangle surface surrounded by the line segment 10, and 12 is the equilateral triangle. Triangular inscribed circle with a diameter of about 100μ
m, (actual hue is equivalent to 5PB5 / 10). This equilateral triangle may be an isosceles triangle. FIG. 4 is a diagram showing a state in which an equilateral hexagonal surface surrounded by line segments is printed as a masking surface. 13 is a surface that is continuously printed with an equilateral hexagon as a masking surface, 14 is a non-printed line segment with a line width of about 20 μm that is the periphery of the masking surface, and 15 is an equilateral hexagon that is used as a masking surface. The printed surface. The masking thickness is about 5 μm. The masking surface may be an equilateral quadrangular surface or an isosceles triangular surface other than the equilateral hexagonal surface.
【0016】図5は、本発明に線分としての印刷に使用
される、印刷インキの色相範囲をマンセル色相環で示し
た図である。色相範囲は、マンセル色相環5GY〜5R
(Bを含む側)の範囲においては、明度6以下、彩度9
以下、また5BG〜5PB(Bを含む側)の範囲におい
ては、明度8以下、彩度10以下であり、インキの性状
はUV乾燥型などの艶消しインキである。
FIG. 5 is a diagram showing the hue range of the printing ink used in the printing as a line segment in the present invention in the Munsell hue circle. Hue range is Munsell hue ring 5GY to 5R
In the range (the side including B), the brightness is 6 or less and the saturation is 9
In the following, in the range of 5BG to 5PB (the side including B), the lightness is 8 or less and the saturation is 10 or less, and the ink is a matte ink such as a UV dry type.
【0017】マスキング面として使用するインキは、線
分を真空蒸着、メッキまたはコーティングによりプリン
ト後、これを拭き取りなどにより容易に取り除けるもの
でなければならないし、また、マスキング面を侵食する
ものであってはならない。本発明においては、UV型イ
ンキなどを通常の乾燥条件に対し、表面のみ乾燥状態と
した半乾燥状態(生乾燥状態ともいう)とするか、また
は、本発明で使用する透明部材(ガラスまたはプラスチ
ック)面、または透明フィルムシート状部材面への印刷
に、通常の枚葉凸版印刷などに使用される紙用インキを
転用することにより、乾燥後において印刷面の接着力を
低下させ、マスキングインキを容易に取り除くことがで
きる。
The ink used as the masking surface must be one that can be easily removed by wiping it after printing the line segment by vacuum vapor deposition, plating or coating, and it also erodes the masking surface. Don't In the present invention, UV type ink or the like is set in a semi-dried state (also referred to as a raw dry state) in which only the surface is in a dried state, or a transparent member (glass or plastic) used in the present invention. ) Surface or the surface of the transparent film sheet-like member, by diversion of the paper ink used in ordinary sheet-fed relief printing, the adhesive strength of the printed surface is reduced after drying and masking ink is removed. It can be easily removed.
【0018】図6は、本発明の透過可視性フィルタの1
実施例における1断面を示す図である。2は線分として
印刷された印刷インキ、3は該線分に囲まれた等辺多角
形面、16は透明部材、17は、表面に前記線分を印刷
され該透明部材に貼付された透明フィルムシート状部材
である。
FIG. 6 shows one of the transmission visibility filters of the present invention.
It is a figure which shows 1 cross section in an Example. 2 is a printing ink printed as a line segment, 3 is an equilateral polygonal surface surrounded by the line segment, 16 is a transparent member, 17 is a transparent film having the line segment printed on the surface and attached to the transparent member It is a sheet-shaped member.
【0019】図7は、本発明の透過可視性フィルタの実
施例における等辺多角形の大きさ、即ち内接円直径dお
よび、線分の線幅tを変化した場合の透過視野の見掛明
度Vを、フィルタ無しのもの(線幅t=0)を100と
して各比率で表した線図である。試料は100mm×1
00mm×5mm(板厚)のポリカーボネート板を用い
た。平均線幅tを10、50、および100μm 、等
辺多角形を、その内接円直径dが約10、50、10
0、200、300および400μmの正六角形とし
て、その輪郭線分をTi微粉末(平均粒度0.20μm
)を 約50wt%含有せしめたUV乾燥型凸版インキ
(実色相は5PB5/10相当)により凸版印刷した。
FIG. 7 shows the apparent brightness of the transmission visual field when the size of the equilateral polygon, that is, the diameter d of the inscribed circle and the line width t of the line segment in the embodiment of the transmission visibility filter of the present invention is changed. FIG. 5 is a diagram showing V as each ratio, where V is a value without a filter (line width t = 0) is 100. Sample is 100 mm x 1
A polycarbonate plate of 00 mm × 5 mm (plate thickness) was used. The average line width t is 10, 50, and 100 μm, and an equilateral polygon has an inscribed circle diameter d of about 10, 50, 10
As regular hexagons of 0, 200, 300 and 400 μm, the contour line segment is Ti fine powder (average grain size 0.20 μm
) Was contained in a UV dry type relief ink (actual hue is equivalent to 5PB5 / 10).
【0020】線幅tの見掛明度への影響が大きく、線幅
が10μmのものでは、内接円直径φが10μm(A=
1)でも見掛明度比が50程度で良好なシールド効果が
認められが、内接円直径φが大きくなると200μm
(A=20)で、既に見掛明度比100となりシールド
効果が認められなくなる。また、線幅tが100μmの
ものでは、内接円直径φが100μm(A=1)以下で
既に暗視野状態に近くなり、更に内接円直径φが400
μm(A=4)を超える領域では見掛明度比100とな
りシールド効果が認められない。
The line width t has a great influence on the apparent brightness, and when the line width is 10 μm, the inscribed circle diameter φ is 10 μm (A =
Even in 1), a good shielding effect is recognized with an apparent brightness ratio of about 50, but it becomes 200 μm when the inscribed circle diameter φ increases.
At (A = 20), the apparent brightness ratio is already 100 and the shielding effect cannot be recognized. Further, when the line width t is 100 μm, the inscribed circle diameter φ is 100 μm (A = 1) or less, and it is already close to the dark field state.
In the region exceeding μm (A = 4), the apparent brightness ratio becomes 100 and the shielding effect cannot be recognized.
【0021】線幅tが50μmのものでは、内接円直径
φが50μm(A=1)で暗視野に近い。また、内接円
直径φが100μm(A=2)と300μm(A=6)
の領域では良好なシールド効果を得ることができる。内
接円直径φが400μmを超える領域ではいずれの線幅
でも見掛明度のシールド効果を期待することはできな
い。色相がダーク側に振れると見掛明度比は低くなる。
When the line width t is 50 μm, the inscribed circle diameter φ is 50 μm (A = 1), which is close to a dark field. In addition, the inscribed circle diameter φ is 100 μm (A = 2) and 300 μm (A = 6)
A good shielding effect can be obtained in the region of. In the region where the inscribed circle diameter φ exceeds 400 μm, the shield effect of apparent brightness cannot be expected with any line width. When the hue shifts to the dark side, the apparent lightness ratio becomes low.
【0022】図8は、図7における試料により透過磁界
強度比を比較測定した結果を示す図である。測定値のバ
ラツキが大きく絶対値による比較は得られなかったが、
アベレージとしてのシールド効果は有意差ありとして推
定できた。しかし、内接円直径700μm以上では、シ
ールド効果はほとんど認められない。線幅tが100μ
mと大きいものでは、内接円直径の減少と共に急激に電
磁的シールド効果は向上する。
FIG. 8 is a diagram showing the results of comparative measurement of the transmitted magnetic field strength ratios of the samples in FIG. Although there was a large variation in the measured values, comparison by absolute value could not be obtained, but
The shield effect as an average could be estimated as having a significant difference. However, when the diameter of the inscribed circle is 700 μm or more, the shield effect is hardly recognized. Line width t is 100μ
If it is as large as m, the electromagnetic shield effect is rapidly improved as the diameter of the inscribed circle is reduced.
【0023】図9は、前記試料により写り込み量を比較
測定した結果を示す図である。天井に100W−2連型
蛍光灯を、2m×2mにつき1個配置せる夜間事務所
(200坪)内において、無差別方向にて反射光(写り
込み)の有無を観察した。内接円直径φが10μm〜2
00μmでは写り込みに対する効果が認められた。しか
し、内接円直径400μm以上では透過可視性フィルタ
の写り込みに対する効果は余り顕著ではない。また、色
相としてはマンセル色相環5GY〜5R(Bを含む側)
で、明度6以上、また5BG〜5PB(Bを含む側)
で、明度8以上となると写り込み防止に対する効果は殆
ど認められなくなる。
FIG. 9 is a diagram showing the results of comparative measurement of the amount of reflection of the sample. In a night office (200 tsubo) in which one 100W-2 continuous fluorescent lamp was placed every 2 m × 2 m on the ceiling, the presence or absence of reflected light (reflection) was observed in an indiscriminate direction. Inscribed circle diameter φ is 10μm ~ 2
At 00 μm, an effect on reflection was recognized. However, when the inscribed circle diameter is 400 μm or more, the effect of the transmission visibility filter on the reflection is not so remarkable. Further, as the hue, the Munsell hue circles 5GY to 5R (the side including B)
And brightness of 6 or more, 5BG to 5PB (B side included)
However, when the brightness is 8 or more, the effect of preventing reflection is hardly recognized.
【0024】図7、8および9の結果から、見掛明度、
透過磁界強度および写り込みに対するシールド効果は、
総合的に内接円直径φと線幅tとの比A(A=φ/t)
は1乃至10、好ましくは2乃至5程度但し、色相環に
おける明度が3以下のインキでは、10〜30とするこ
とにより、良好となることがわかった。なお、線幅t
は、5乃至100μm、好ましくは5乃至70μmが望
ましい。
From the results of FIGS. 7, 8 and 9, the apparent brightness,
The shield effect against the transmitted magnetic field strength and reflection is
Overall, the ratio A of the inscribed circle diameter φ and the line width t (A = φ / t)
However, it has been found that the ink having a lightness of 3 or less in the hue circle has a value of 10 to 30 and is favorable. The line width t
Is 5 to 100 μm, preferably 5 to 70 μm.
【0025】なお、詳細確認試験の結果、色相環におけ
る明度が3以下の黒色または暗色の領域においては、ほ
とんどの色相において線幅tは5〜30μm、内接円直
径φと線幅tの比Aは10〜30程度でないと概ね暗視
野となり透過可視性フィルタとしての目的を達せられな
いという試験結果を得た。但し内接円直径φは700μ
m以下であることが望ましい。内接円直径φが700μ
m以上では写り込みおよび透過磁界強度に対するシール
ド効果が急激に低下する。
As a result of the detailed confirmation test, the line width t is 5 to 30 μm and the ratio of the inscribed circle diameter φ to the line width t in most hues in the black or dark region where the lightness in the hue circle is 3 or less. The test results obtained indicate that unless A is about 10 to 30, the field becomes a dark field and the purpose as a transmission visibility filter cannot be achieved. However, inscribed circle diameter φ is 700μ
It is preferably m or less. Inscribed circle diameter φ is 700μ
When it is more than m, the shielding effect against reflection and transmitted magnetic field strength is sharply reduced.
【0026】本発明は、透明部材の全部または少なくと
も一部が曲面により構成されている場合に極めて効果的
であることを特徴としている。従来の凸版印刷方法では
該曲面に精度良く等辺多角形を印刷することは不可能で
あった。従って、極細の線幅と内接円直径を有する微小
の等辺多角形を、曲面に精度良く印刷することを必須条
件とする本発明にあっては、本出願人による出願になる
特願平01−059697号(登録第2961153
号)「曲面への印刷方法」の併用によってのみ、この実
現が可能となったものである。
The present invention is extremely effective when all or at least a part of the transparent member is formed by a curved surface. It has been impossible to accurately print an equilateral polygon on the curved surface by the conventional letterpress printing method. Therefore, in the present invention in which it is indispensable to print a minute equilateral polygon having an extremely fine line width and an inscribed circle diameter on a curved surface with high precision, it is filed by the applicant of the present application. -059697 (Registration No. 2961153)
No.) "Printing method on curved surface" can be used only in combination.
【0027】また、マスキング面として等辺多角形面を
印刷した印刷インキは、導電性金属を輪郭線分として真
空蒸着、メッキまたはコーティングにより作成したのち
には、これを速やかに除去することが必要である。しか
も真空蒸着、メッキまたはコーティング工程において、
該マスキング面が作業上支障があるものであってはなら
ない。本出願人は、マスキング面としての印刷を、半乾
燥状態(生乾燥状態)または被印刷部材との接着力が通
常の50%以下である印刷とすることにより実現した。
Further, the printing ink in which an equilateral polygonal surface is printed as a masking surface needs to be promptly removed after being formed by vacuum deposition, plating or coating using a conductive metal as a contour line segment. is there. Moreover, in the vacuum deposition, plating or coating process,
The masking surface should not be an obstacle to work. The applicant has realized printing as a masking surface by printing in a semi-dried state (raw dried state) or in which the adhesive force with a member to be printed is 50% or less of a normal level.
【0028】試料として100mm×100mm×5m
m(板厚)のポリカーボネート板を用い、UV乾燥型イ
ンキ(大阪印刷インキ製造(株)製AD型)により内接
円直径50μmの正六角形のマスキング面を印刷し、U
V照射時間を変えて、その乾燥状態を比較観察した。照
射時間2〜3秒の範囲で印刷面の表面が適度の半乾燥状
態(生乾燥状態)が得られることがわかった。このマス
キング面は軟質布地により軽度の拭き取り行程により容
易にこれを取り除くことができる。
100 mm × 100 mm × 5 m as a sample
Using a m (thickness) polycarbonate plate, a regular hexagonal masking surface with an inscribed circle diameter of 50 μm was printed with UV dry type ink (AD type manufactured by Osaka Printing Ink Mfg. Co., Ltd.).
The V irradiation time was changed and the dried state was comparatively observed. It was found that an appropriate semi-dry state (raw dry state) of the printed surface was obtained in the irradiation time range of 2 to 3 seconds. The masking surface can be easily removed with a soft cloth by a mild wiping process.
【0029】また、枚葉凸版印刷に使用する凸版インキ
(大阪印刷インキ製造(株)製紙用インキ)を使用し、
通常の枚葉印刷と同一条件にて前記ポリカーボネート板
に印刷し自然乾燥させた。十分乾燥したマスキング面を
軟質布地により拭き取りを行った。作業性は若干悪いが
マスキング面の除去を完全に実施することができた。こ
れは被印刷面との接触力の低下による効果であり、除去
力の比較から、接着力は、ほぼ枚葉印刷時の50%以下
程度となっており、本発明のマスキング面としての条件
としてこの程度が限界であることがわかった。
Further, using a letterpress ink used for sheet-fed relief printing (ink for papermaking of Osaka Printing Ink Mfg. Co., Ltd.),
The polycarbonate plate was printed under the same conditions as in normal sheet-fed printing and naturally dried. The sufficiently dried masking surface was wiped off with a soft cloth. Although the workability was slightly poor, the masking surface could be completely removed. This is an effect due to the reduction of the contact force with the surface to be printed. From the comparison of the removing force, the adhesive force is about 50% or less of that at the time of sheet-fed printing, which is a condition for the masking surface of the present invention. It turns out that this is the limit.
【0030】また、本発明の実施例の内、等辺多角形の
形状が正六角形の場合は、特に、電子画像表示装置のデ
ィスプレーに設けられたシャドーマスクの直角格子によ
る、モアレ干渉縞の発生防止に対して、極めて効果があ
ることが確認された。
Further, in the embodiment of the present invention, when the shape of the equilateral polygon is a regular hexagon, in particular, the generation of moire interference fringes is prevented by the rectangular grid of the shadow mask provided in the display of the electronic image display device. Was confirmed to be extremely effective.
【0031】なお、磁性粉体により磁気遮蔽効果を期待
する場合は、比較的透磁率μの高い磁性材料を使用する
ことが望ましい。透磁率μの高い材料として、純鉄、S
i、Al、Fe2 4 系、Al・Si系などを使用する
ことができる。
When the magnetic powder is expected to have a magnetic shielding effect, it is desirable to use a magnetic material having a relatively high magnetic permeability μ. Pure iron and S as materials with high permeability μ
i, Al, Fe 2 O 4 type, Al.Si type, etc. can be used.
【0032】[0032]
【発明の効果】本発明は、1)透明部材に直接または該
透明部材に添付する透明フィルムシート状部材に、導電
性金属による、または導電性金属粉末を含む線分を線幅
10〜100μm、厚さ5〜100μm、最少線間距離
(内接円直径)が0.01〜0.50mmの連続形成さ
れた等辺多角形の輪郭線分として設けた透過可視性フィ
ルタにより、透過可視可能で、且つ電磁波のシールドお
よび反射光防止効果のある、透過可視性フィルタを提供
することができる。
Industrial Applicability According to the present invention, 1) a line segment having a conductive metal or a powder containing a conductive metal is formed on a transparent film sheet-shaped member directly or attached to the transparent member in a line width of 10 to 100 μm, With a transmission visibility filter provided as a contour line segment of a continuously formed equilateral polygon having a thickness of 5 to 100 μm and a minimum distance between lines (inscribed circle diameter) of 0.01 to 0.50 mm, transmission visible is possible, Further, it is possible to provide a transmission visibility filter having an electromagnetic wave shield and a reflected light prevention effect.
【0033】また、2)前記等辺多角形を、二等辺三角
形、正三角形、等辺四角形、等辺六角形または正六角形
のいずれか1より選ばれたものとすることにより、更に
3)前記線分を、粒度が0.1〜70μmの導電性金属
粉末を5〜80wt%含有する艶消しインキを使用した
印刷により設けたことにより、透過可視可能で、且つ、
より確実に電磁波のシールドおよび反射光防止効果のあ
る透過可視性フィルタを提供することができる。
Further, 2) the equilateral polygon is selected from any one of an isosceles triangle, an equilateral triangle, an equilateral quadrangle, an equilateral hexagon, and an equilateral hexagon. Since it is provided by printing using a matte ink containing 5 to 80 wt% of a conductive metal powder having a particle size of 0.1 to 70 μm, it is visible and transparent, and
It is possible to more reliably provide a transmission visibility filter having an electromagnetic wave shield and a reflected light prevention effect.
【0034】本発明は、4)第1ステップとして、前記
透明部材または透明フィルムシート状部材に、拭き取
り、清浄化可能なインキにより、前記線分に囲まれた輪
郭を有する等辺多角形面をマスキング面として印刷し、
第2ステップとして、該マスキング面を印刷された部材
の輪郭線分の線幅部に、真空蒸着、メッキまたはコーテ
ィングにより前記導電性金属を線分として設け、第3ス
テップとして、前記マスキング面としてのインキを除去
する、各ステップにより構成された線分を有するの透過
可視性フィルタにより、透過可視可能で、且つ強力な電
磁波シールド効果を得ることができる。
According to the present invention, 4) As a first step, the transparent member or the transparent film sheet member is masked with an ink that can be wiped and cleaned to form an equilateral polygonal surface having an outline surrounded by the line segments. Print as the side,
As a second step, the conductive metal is provided as a line segment by vacuum vapor deposition, plating or coating on the line width portion of the contour line segment of the member on which the masking surface is printed, and as a third step, as the masking surface, A transmission visible filter having a line segment constituted by each step for removing ink can be transmitted and visible, and a strong electromagnetic wave shielding effect can be obtained.
【0035】本発明は、5)前記艶消しインキを、その
色相がマンセル色相環5GY〜5R(Bを含む側)の範
囲においては、明度6以下、彩度9以下、また5BG〜
5PB(Bを含む側)の範囲においては、明度8以下、
彩度10以下なる艶消しインキとすることにより、ま
た、6)前記輪郭線分の色相がマンセル色相環の明度3
以下の黒色または暗色の領域では、前記線幅tを5〜7
0μm、内接円直径φと線幅tの比Aを10〜30、但
し、内接円直径φは700μm以下とすることにより、
さらに、7)前記導電性金属粉末または導電性金属が、
少なくとも、Cu、Ti、Fe、Ni、Mg、Au、A
g、またはそれらの各合金のうちの1種を含むものとす
ることにより、透過可視効果と反射光防止効果に勝れた
電磁波シールド用の透過可視性フィルタを提供すること
ができる。
In the present invention, 5) the matte ink has a lightness of 6 or less, a chroma of 9 or less, and a color of 5BG to 5GY in the Munsell hue ring 5GY to 5R (the side including B).
In the range of 5 PB (the side including B), the brightness is 8 or less,
By using a matte ink having a saturation of 10 or less, 6) the hue of the contour line segment is the lightness of the Munsell hue circle of 3
In the following black or dark areas, the line width t is 5 to 7
0 μm, the ratio A of the inscribed circle diameter φ to the line width t is 10 to 30, provided that the inscribed circle diameter φ is 700 μm or less,
Further, 7) the conductive metal powder or conductive metal is
At least Cu, Ti, Fe, Ni, Mg, Au, A
By including g or one of the alloys thereof, it is possible to provide a transmission visibility filter for an electromagnetic wave shield that excels in the transmission visible effect and the reflected light prevention effect.
【0036】また、8)前記透明部材を、ガラスまたは
プラスチックとすることにより、さらに、9)前記透明
部材のプラスチックを、ポリカーボネート、メタクリル
またはポリプロピレン樹脂のいずれかとすることによ
り、また、10)前記透明部材に添付する透明フィルム
シート状部材を、ポリエチレン、ポリプロピレン、ポリ
エチレンテレフタレート、ポリ塩化ビニリデン、アセテ
ートのいずれかにすることにより、安価で且つ市場性の
ある透過可視可能で、電磁波のシールドおよび反射光防
止効果のある、透過可視性フィルタを提供することがで
きる。
Further, 8) the transparent member is made of glass or plastic, 9) the plastic of the transparent member is made of polycarbonate, methacryl, or polypropylene resin, and 10) the transparent member. The transparent film sheet member attached to the member is made of polyethylene, polypropylene, polyethylene terephthalate, polyvinylidene chloride, or acetate, which is inexpensive and marketable, and allows visible transmission, shielding of electromagnetic waves and prevention of reflected light. It is possible to provide an effective transmission visibility filter.
【0037】本発明は、11)前記マスキング面として
の印刷を、半乾燥状態または被印刷部材との接着力が通
常の50%以下である印刷とすることにより、生産性が
良い透過可視可能で、且つ、強力な電磁波シールド効果
をもつ透過可視性フィルタを得ることができる。
In the present invention, 11) the printing as the masking surface is a semi-dry state or a printing in which the adhesive force with the member to be printed is 50% or less of the normal level, so that it is possible to see and visualize with good productivity. In addition, it is possible to obtain a transmission visibility filter having a strong electromagnetic wave shielding effect.
【0038】また、本発明は、12)前記透明部材を、
その全面または一部が曲面により構成することにより、
居住性や芸術性に勝れた構造物に対する透過可視可能
で、且つ、電磁波のシールドおよび反射光防止効果のあ
る透過可視性フィルタを提供することができる。
The present invention also provides 12) the transparent member,
By constructing the entire surface or part of it with a curved surface,
It is possible to provide a transparent and visible filter which is transparent and visible to structures having excellent habitability and artistry, and which has an electromagnetic wave shielding and reflected light preventing effect.
【図面の簡単な説明】[Brief description of drawings]
【図1】 本発明の透過可視性フィルタの1実施例であ
る等辺六角形の線分として印刷した印刷面を示す図であ
る。
FIG. 1 is a diagram showing a printing surface printed as an equilateral hexagonal line segment that is an embodiment of a transmission visibility filter of the present invention.
【図2】 本発明の透過可視性フィルタの他の実施例で
ある等辺四角形(菱形)の線分として印刷した印刷面を
示す図である。
FIG. 2 is a diagram showing a printing surface printed as line segments of an equilateral quadrangle (diamond) which is another embodiment of the transmission visibility filter of the present invention.
【図3】 本発明の透過可視性フィルタの更に他の実施
例である正三角形の線分として印刷した印刷面を示す図
である。
FIG. 3 is a diagram showing a printing surface printed as a line segment of an equilateral triangle which is still another embodiment of the transmission visibility filter of the present invention.
【図4】 周辺を線分で囲まれた等辺六角形面をマスキ
ング面として印刷した状態を示す図である。
FIG. 4 is a diagram showing a state in which an equilateral hexagonal surface surrounded by line segments is printed as a masking surface.
【図5】 本発明に線分としての印刷に使用される、印
刷インキの色相範囲をマンセル色相環で示した図であ
る。
FIG. 5 is a diagram showing a hue range of printing ink used for printing as a line segment in the present invention with a Munsell hue circle.
【図6】 本発明の透過可視性フィルタの1実施例にお
ける1断面を示す図である。
FIG. 6 is a view showing one section in one embodiment of the transmission visibility filter of the present invention.
【図7】 本発明の透過可視性フィルタの実施例におけ
る内接円直径dおよび、線幅tに対する透過視野の見掛
け明度V比を表した線図である。
FIG. 7 is a diagram showing an apparent brightness V ratio of a transmission visual field with respect to an inscribed circle diameter d and a line width t in an example of the transmission visibility filter of the present invention.
【図8】 図7の試料により透過磁界強度比を比較測定
した結果を示す線図である。
8 is a diagram showing the results of comparative measurement of transmitted magnetic field intensity ratios using the sample of FIG.
【図9】 図7の試料により写り込み量を比較測定した
結果を示す線図である。
9 is a diagram showing the results of comparative measurement of the amount of reflection with the sample of FIG.
【符号の説明】[Explanation of symbols]
1 等辺六角形を印刷された面、2 線分、3 線分に
囲まれた等辺六角形面、4 等辺六角形の内接円、5
等辺四角形を印刷された面、6 線分、7 等辺四角形
面、8 等辺四角形の内接円、9 正三角形を印刷され
た面、10 線分、11 正三角形面、12 正三角形
の内接円、13 等辺六角形をマスキング面として印刷
された面、14 マスキング面の周辺の非印刷線分、1
5 等辺六角形のマスキング印刷面、16 透明部材、
17 透明フィルムシート状部材。
1 A surface on which an equilateral hexagon is printed, 2 lines, an equilateral hexagon surrounded by 3 lines, 4 an inscribed circle of an equilateral hexagon, 5
Faces with equilateral quadrilaterals, 6 line segments, 7 equilateral quadrilateral faces, 8 inscribed circles of equilateral quadrilaterals, 9 faces with equilateral triangles printed, 10 line segments, 11 equilateral triangle faces, 12 inscribed circles of equilateral triangles , 13 Surface printed with equilateral hexagon as masking surface, 14 Non-printed line segment around masking surface, 1
5 equilateral hexagonal masking printing surface, 16 transparent member,
17 Transparent film sheet member.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 FI テーマコート゛(参考) G02F 1/1343 G02B 1/10 Z Fターム(参考) 2H048 AA07 AA09 AA11 AA18 AA22 2H091 FA37X FD12 GA02 LA08 LA16 LA30 2H092 GA64 NA01 NA17 NA30 2K009 AA02 BB11 CC01 CC14 CC21 DD02 EE00 EE03 FF01 4K044 AA12 AA16 AB02 BA02 BA06 BA08 BA11 BB01 BC14 CA04 CA07 CA13 CA16 CA17 CA64─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 7 Identification code FI theme coat (reference) G02F 1/1343 G02B 1/10 Z F term (reference) 2H048 AA07 AA09 AA11 AA18 AA22 2H091 FA37X FD12 GA02 LA08 LA16 LA30 2H092 GA64 NA01 NA17 NA30 2K009 AA02 BB11 CC01 CC14 CC21 DD02 EE00 EE03 FF01 4K044 AA12 AA16 AB02 BA02 BA06 BA08 BA11 BB01 BC14 CA04 CA07 CA13 CA16 CA17 CA64

Claims (14)

    【特許請求の範囲】[Claims]
  1. 【請求項1】 透明部材に直接または該透明部材に添付
    する透明フィルムシート状部材に、連続形成した等辺多
    角形の輪郭線分として、導電性金属による、または導電
    性粉末乃至磁性粉体を含む、線分を、線幅tを5〜10
    0μm、厚さhを5〜100μm、最少線間距離(内接
    円直径φ)を0.01〜0.50mm、且つ、内接円直
    径φと線幅tの比Aを1〜30として設けたことを特徴
    とする透過可視性フィルタ。
    1. A transparent film sheet-shaped member directly attached to or attached to a transparent member, comprising a conductive metal or conductive powder or magnetic powder as a contour line segment of an equilateral polygon formed continuously. , A line segment, and a line width t of 5 to 10
    0 μm, thickness h is 5 to 100 μm, minimum distance between lines (inscribed circle diameter φ) is 0.01 to 0.50 mm, and ratio A of inscribed circle diameter φ to line width t is 1 to 30 A transmission visibility filter characterized by the above.
  2. 【請求項2】 前記等辺多角形が二等辺三角形、正三角
    形、等辺四角形、正方形、等辺六角形または正六角形の
    いずれか1より選ばれたものであることを特徴とする請
    求項1に記載の透過可視性フィルタ。
    2. The equilateral polygon is selected from any one of an isosceles triangle, an equilateral triangle, an equilateral quadrangle, a square, an equilateral hexagon and a regular hexagon. Transmission visibility filter.
  3. 【請求項3】 前記線分が、粒度が0.1〜70μmの
    導電性粉末乃至磁性粉体を5〜80wt%含有する艶消
    しインキを使用した印刷により設けられたことを特徴と
    する請求項1または2に記載の透過可視性フィルタ。
    3. The line segment is provided by printing using a matte ink containing 5 to 80 wt% of conductive powder or magnetic powder having a particle size of 0.1 to 70 μm. The transmission visibility filter according to 1 or 2.
  4. 【請求項4】 第1ステップとして、前記透明部材また
    は透明フィルムシート状部材に、拭き取り、清浄化可能
    なインキにより、前記線分に囲まれた輪郭を有する等辺
    多角形面をマスキング面として印刷し、第2ステップと
    して、該マスキング面を印刷された部材の輪郭線分の線
    幅部に、真空蒸着、メッキまたはコーティングにより前
    記導電性金属を線分として設け、第3ステップとして、
    前記マスキング面としてのインキを除去する、各ステッ
    プにより構成された線分を有することを特徴とする請求
    項1または2に記載の透過可視性フィルタ。
    4. As a first step, the transparent member or the transparent film sheet-like member is printed with an ink that can be wiped and cleaned to print an equilateral polygonal surface having a contour surrounded by the line segment as a masking surface. As the second step, the conductive metal is provided as a line segment by vacuum vapor deposition, plating or coating in the line width portion of the contour line segment of the member having the masking surface printed, and as the third step,
    The transmission visibility filter according to claim 1 or 2, further comprising a line segment configured by each step for removing ink as the masking surface.
  5. 【請求項5】 前記艶消しインキが、その色相がマンセ
    ル色相環5GY〜5R(Bを含む側)の範囲において
    は、明度6以下、彩度9以下、また5BG〜5PB(B
    を含む側)の範囲においては、明度8以下、彩度10以
    下なる艶消しインキであることを特徴とする請求項1乃
    至3のいずれか1項に記載の透過可視性フィルタ。
    5. The matte ink has a lightness of 6 or less, a saturation of 9 or less, and a color of 5BG to 5PB (B) in the Munsell hue circles 5GY to 5R (the side including B).
    4. The transmission visibility filter according to any one of claims 1 to 3, wherein the matte ink has a lightness of 8 or less and a saturation of 10 or less in the range of (including side).
  6. 【請求項6】 前記輪郭線分の色相がマンセル色相環の
    明度3以下の黒色または暗色の領域では、前記線幅tを
    5〜70μm、内接円直径φと線幅tの比Aを10〜3
    0、但し、内接円直径φは700μm以下としたことを
    特徴とする請求項1乃至3、5のいずれか1項に記載の
    透過可視性フィルタ。
    6. In a region where the hue of the contour line segment is black or dark with a lightness of 3 or less in the Munsell hue circle, the line width t is 5 to 70 μm, and the ratio A between the inscribed circle diameter φ and the line width t is 10. ~ 3
    0, where the inscribed circle diameter φ is 700 μm or less. 6. The transmission visibility filter according to claim 1, wherein
  7. 【請求項7】 前記導電性粉末または導電性金属が、少
    なくとも、Cu、Ti、Fe、Ni、Mg、Au、A
    g、またはそれらの各合金のうちの1種を含むものであ
    ることを特徴とする請求項1乃至6のいずれか1項に記
    載の透過可視性フィルタ。
    7. The conductive powder or conductive metal is at least Cu, Ti, Fe, Ni, Mg, Au, A
    The transmission visibility filter according to any one of claims 1 to 6, further comprising g or one of the alloys thereof.
  8. 【請求項8】 記導電性粉末が、カーボン繊維粉末であ
    ることを特徴とする請求項1乃至4、6のいずれか1項
    に記載の透過可視性フィルタ。
    8. The transmission visibility filter according to claim 1, wherein the conductive powder is carbon fiber powder.
  9. 【請求項9】 前記透明部材が、ガラスまたはプラスチ
    ックであることを特徴とする請求項1乃至8のいずれか
    1項に記載の透過可視性フィルタ。
    9. The transmission visibility filter according to claim 1, wherein the transparent member is glass or plastic.
  10. 【請求項10】 前記透明部材のプラスチックが、ポリ
    カーボネート、メタクリルまたはポリプロピレン樹脂の
    いずれかであることを特徴とする請求項1乃至7のいず
    れか1項に記載の透過可視性フィルタ。
    10. The transmission visibility filter according to claim 1, wherein the plastic of the transparent member is any one of polycarbonate, methacryl, and polypropylene resin.
  11. 【請求項11】 前記透明部材に添付する透明フィルム
    シート状部材が、ポリエチレン、ポリプロピレン、ポリ
    エチレンテレフタレート、ポリ塩化ビニリデン、アセテ
    ートのいずれかよりなることを特徴とする請求項1乃至
    10のいずれか1項に記載の透過可視性フィルタ。
    11. The transparent film sheet-like member attached to the transparent member is made of any one of polyethylene, polypropylene, polyethylene terephthalate, polyvinylidene chloride, and acetate. The transmission visibility filter described in.
  12. 【請求項12】 前記マスキング面としての印刷が、半
    乾燥状態または被印刷部材との接着力が通常の50%以
    下である印刷であることを特徴とする請求項5に記載の
    透過可視性フィルタ。
    12. The transmission visibility filter according to claim 5, wherein the printing as the masking surface is a printing in a semi-dried state or an adhesion with a member to be printed is 50% or less of a normal level. .
  13. 【請求項13】 前記線分が、予め機械的または電気化
    学的に穿削構成された凹溝を、埋め込むように形成され
    た前記導電性粉末乃至磁性粉体を含む、または導電性金
    属による線分であることを特徴とする請求項1乃至12
    のいずれか1項に記載の透過可視性フィルタ。
    13. The line segment includes the conductive powder or magnetic powder formed so as to fill a concave groove that has been mechanically or electrochemically drilled in advance, or a line made of a conductive metal. Minutes are minutes.
    The transmission visibility filter according to any one of 1.
  14. 【請求項14】 前記透明部材が、その全面または一部
    が曲面により構成されていることを特徴とする請求項1
    乃至13のいずれか1項に記載の透過可視性フィルタ。
    14. The transparent member, wherein the entire surface or a part thereof is formed by a curved surface.
    The transmission visibility filter according to any one of 1 to 13.
JP2002152816A 2001-06-18 2002-05-27 Transmitting visible filter Pending JP2003090903A (en)