JP2003020263A - Self-levelling plaster - Google Patents

Self-levelling plaster

Info

Publication number
JP2003020263A
JP2003020263A JP2001207282A JP2001207282A JP2003020263A JP 2003020263 A JP2003020263 A JP 2003020263A JP 2001207282 A JP2001207282 A JP 2001207282A JP 2001207282 A JP2001207282 A JP 2001207282A JP 2003020263 A JP2003020263 A JP 2003020263A
Authority
JP
Japan
Prior art keywords
self
parts
weight
leveling material
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2001207282A
Other languages
Japanese (ja)
Inventor
Hideki Takaoka
秀樹 高岡
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toli Corp
Original Assignee
Toli Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toli Corp filed Critical Toli Corp
Priority to JP2001207282A priority Critical patent/JP2003020263A/en
Publication of JP2003020263A publication Critical patent/JP2003020263A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To obtain a self-levelling plaster which can form and maintain a smooth and dense surface, and is particularly suitable for a floor material having an adhesive agent or a tacky adhesive agent. SOLUTION: This self-levelling plaster essentially consists of cement, a filler and a water holding agent. As a synthetic resin, one or a mixture of two or more selected from a vinyl acetate resin, a vinyl vassatate resin, a vinyl acetate- vinyl versatic acid copolymer, an ethylene-vinyl acetate copolymer, an acrylic resin, a vinyl acetate-acrylic acid copolymer, a vinyl acetate-vinyl vassatate- acrylic ester copolymer and SBR(styrene-butadiene-rubber) is contained in 3 to 25 pts.wt. per 100 pts.wt. of the cement.

Description

【発明の詳細な説明】Detailed Description of the Invention

【0001】[0001]

【発明の属する技術分野】接着剤、若しくは粘着剤付き
の床タイル等の床材に適した床下地であって、改修工事
等の際、残存する接着剤等が残りにくく、容易に平滑か
つ鏡面に近い緻密な床下地の表面を形成し維持すること
ができるセルフレベリング材に関する。
TECHNICAL FIELD The present invention relates to a floor base material suitable for floor materials such as floor tiles with adhesives or adhesives, and is less likely to leave residual adhesives during repair work, etc. The present invention relates to a self-leveling material capable of forming and maintaining a surface of a dense floor base close to the above.

【0002】[0002]

【従来の技術】従来、接着剤、若しくは粘着剤付きの床
タイル等の床材(以下、接着剤等付き床材と記す。)を
施工する際、例えば通常のモルタルやコンクリート等の
表面の粗い下地には前記接着剤等付き床材は下地との接
着性等が悪かったため、施工することはできなかった。
そこで、レベリング材を塗布処理することにより、下地
の不陸を解消するとともに当該床面を平滑にし、さら
に、ウレタン系、アクリル系、エポキシ系樹脂等からな
る防塵塗料等で処理することにより、或いは、レベリン
グ材を塗布処理した表面に酢酸ビニル系樹脂等を主成分
とするプライマーで処理することにより、施工後の下地
の仕上りの向上、及び施工床面への接着剤等付き床材の
との接着性の安定化を図ることが一般的に行われてい
た。
2. Description of the Related Art Conventionally, when a floor material such as a floor tile with an adhesive or a pressure sensitive adhesive (hereinafter referred to as a floor material with an adhesive, etc.) is used, for example, a rough surface such as ordinary mortar or concrete is used. The above-mentioned floor material with an adhesive or the like could not be applied to the base because the adhesiveness to the base was poor.
Therefore, by applying a leveling material, the unevenness of the base is eliminated and the floor surface is smoothed, and further, a urethane-based, acrylic-based, or epoxy-based resin or the like is used to treat the dust-proof coating, or the like. By treating the surface coated with the leveling material with a primer whose main component is vinyl acetate resin, etc., the finish of the groundwork after construction is improved, and with the floor material with adhesive etc. on the construction floor surface. It has been common practice to stabilize the adhesiveness.

【0003】また、改修工事等の場合にも前記の下地処
理は古い接着剤等付き床材を剥離、除去した後、床面に
接着剤等が残存することがあり、さらに、当該残存接着
剤等により下地に不陸があるという問題点も生じること
があるため、当該諸問題を解決することを目的としても
上記と同様、レベリング材処理やプライマー塗布の下地
処理が行われていた。
Also, in the case of repair work and the like, the above-mentioned base treatment may leave the adhesive or the like on the floor surface after peeling and removing the floor material with the old adhesive or the like. There is also a problem that the ground is uneven due to such reasons. Therefore, for the purpose of solving the various problems, the leveling material treatment and the primer treatment such as primer coating have been performed similarly to the above.

【0004】[0004]

【発明が解決しようとする課題】しかしながら、上記の
下地処理は特に改修工事等の残存接着剤等による不陸の
解消、及び下地と接着剤等付き床材との接着強度の確保
等の観点から不可欠な処理であるにも拘わらず、時間を
要する上、労力面においても経済面においても負担が大
きいという問題があった。従って、かかる下地処理にお
ける労力面等の負担により、接着剤等付き床材において
は接着剤等の塗布等が不要であるという有用性にもかか
わらず、モルタル下地等比較的粗い表面しか得られない
下地に対しては接着剤等付き床材は敬遠され、表面が平
滑、かつ鏡面に近いスチールやアルミ製の二重床の設置
部材、又は表面に緻密な平滑性、若しくは鏡面を有する
既設床への重ね貼り等に使用されるにすぎなかった。
However, the above-mentioned surface treatment is particularly required from the viewpoint of eliminating unevenness due to residual adhesive and the like during repair work and ensuring the adhesive strength between the base and the floor material with adhesive. Although it is an indispensable process, it has been problematic in that it takes time and is burdensome in terms of labor and economy. Therefore, due to the burden of labor in the surface treatment, a relatively rough surface such as a mortar substrate can be obtained despite the usefulness that the adhesive or the like is not required to be applied to the floor material with the adhesive or the like. Floor materials with adhesives are shunned against the groundwork, and the surface is smooth, and it is a double-floor installation member made of steel or aluminum that is close to the mirror surface, or an existing floor with a dense smooth surface or a mirror surface. It was only used for layering and pasting.

【0005】[0005]

【課題を解決するための手段】本発明は上記問題点を平
滑かつ鏡面に近い緻密な表面を形成し維持することがで
きるセルフレベリング材を提供することにより解決する
ものであり、より詳しくは請求項1に記載する発明はセ
メント、骨材、及び保水剤を主成分とするセルフレベリ
ング材であって、前記セメント100重量部に対し合成
樹脂として酢酸ビニル樹脂、バーサチック酸ビニル樹
脂、酢酸ビニル−バーサチック酸ビニル共重合体、エチ
レン−酢酸ビニル共重合体、アクリル樹脂、酢酸ビニル
−アクリル酸共重合体、酢酸ビニル−バーサチック酸ビ
ニル−アクリル酸エステル共重合体、SBRの中の一、
又は二以上の混合物が3〜25重量部を含有することを
特徴とするセルフレベリング材を提供するものである。
The present invention solves the above problems by providing a self-leveling material capable of forming and maintaining a smooth and dense surface close to a mirror surface. The invention according to Item 1 is a self-leveling material containing cement, an aggregate, and a water retention agent as main components, and vinyl acetate resin, versatic acid vinyl resin, vinyl acetate-versatitic as a synthetic resin with respect to 100 parts by weight of the cement. One of vinyl acetate copolymer, ethylene-vinyl acetate copolymer, acrylic resin, vinyl acetate-acrylic acid copolymer, vinyl acetate-vinyl versatic acid-acrylic acid ester copolymer, SBR,
Alternatively, the self-leveling material is characterized in that the mixture of two or more contains 3 to 25 parts by weight.

【0006】請求項2記載の発明は請求項1の特徴に加
え、前記セメント100重量部に対して、骨材が30〜
300重量部含有することを特徴としたセルフレベリン
グ材を提供するものである。
In addition to the features of claim 1, the invention of claim 2 is characterized in that the aggregate is 30 to 100 parts by weight of the cement.
A self-leveling material containing 300 parts by weight is provided.

【0007】請求項3記載の発明は請求項1又は2の特
徴に加え、前記セメント100重量部に対して、石膏が
1〜50重量部含有することを特徴としたセルフレベリ
ング材を提供するものである。
The invention according to claim 3 provides a self-leveling material characterized by containing 1 to 50 parts by weight of gypsum per 100 parts by weight of cement in addition to the features of claim 1 or 2. Is.

【0008】請求項4記載の発明は請求項1乃至3の特
徴に加え、前記セメント100重量部に対して、減水剤
が0.1〜5重量部を含有することを特徴とするセルフ
レベリング材を提供するものである。
The invention according to claim 4 is, in addition to the features of claims 1 to 3, characterized in that the water reducing agent contains 0.1 to 5 parts by weight with respect to 100 parts by weight of the cement. Is provided.

【0009】請求項5記載の発明は請求項1乃至4の特
徴に加え、前記セメント100重量部に対して、保水剤
が0.02〜5重量部を含有することを特徴とする請求
項1乃至4記載のセルフレベリング材を提供するもので
ある。
In addition to the features of claims 1 to 4, the invention of claim 5 is characterized in that the water retention agent contains 0.02 to 5 parts by weight with respect to 100 parts by weight of the cement. The present invention also provides the self-leveling material according to any one of 1 to 4.

【0010】請求項6記載の発明は請求項1乃至5の特
徴に加え、前記セメント100重量部に対して、消泡剤
が0.05〜3重量部を含有することを特徴とするセル
フレベリング材を提供するものである。
The invention according to claim 6 is, in addition to the features of claims 1 to 5, characterized in that the defoaming agent contains 0.05 to 3 parts by weight with respect to 100 parts by weight of the cement. The material is provided.

【0011】請求項7記載の発明は請求項1乃至6の特
徴に加え、前記合成樹脂の平均粒径が1〜7μmである
ことを特徴とするセルフレベリング材を提供するもので
ある。
According to a seventh aspect of the present invention, in addition to the features of the first to sixth aspects, there is provided a self-leveling material, wherein the synthetic resin has an average particle size of 1 to 7 μm.

【0012】請求項8記載の発明は請求項1乃至7の特
徴に加え、前記骨材の平均粒径が45〜710μmであ
ることを特徴とするセルフレベリング材を提供するもの
である。
In addition to the features of claims 1 to 7, the invention of claim 8 provides a self-leveling material, wherein the average particle diameter of the aggregate is 45 to 710 μm.

【0013】請求項9記載の発明は請求項1乃至8の特
徴に加え、前記石膏の平均粒径が45〜250μmであ
ることを特徴とするセルフレベリング材を提供するもの
である。
In addition to the features of claims 1 to 8, the invention of claim 9 provides a self-leveling material characterized in that the gypsum has an average particle size of 45 to 250 μm.

【0014】[0014]

【発明の実施の形態】本発明のセルフレベリング材にお
いてはセメント、骨材、合成樹脂、保水剤、減水剤、及
び水を原材料とし、必要に応じて消泡剤、遅延剤、早強
剤を添加する。以下、順次上記原材料等について詳述す
る。
BEST MODE FOR CARRYING OUT THE INVENTION In the self-leveling material of the present invention, a cement, an aggregate, a synthetic resin, a water retention agent, a water reducing agent, and water are used as raw materials, and if necessary, an antifoaming agent, a retarder, and an early strengthening agent. Added. Hereinafter, the raw materials and the like will be described in detail in order.

【0015】本発明セルフレベリング材に使用するセメ
ントの具体例としては通常繁用される普通ポルトランド
セメントの他、早強ポルトランドセメント、超早強ポル
トランドセメント、アルミナセメント、シリカセメン
ト、ジェットセメント、フライアッシュセメント等各種
セメントが挙げられ、これらセメントの一種、又は二種
以上を混合して用いても良い。尚、本発明セルフレベリ
ング材に使用するセメントの平均粒径は一般的に用いら
れているセメントの平均粒径であればよく、例えば普通
ポルトランドセメントの場合、比表面積で3000〜3
500cm2/g程度が好適であり、また、アルミナセ
メントの場合は比表面積で2850〜5250cm2/
g程度が好ましい。
Specific examples of the cement used in the self-leveling material of the present invention include normal Portland cement which is usually used frequently, fast early Portland cement, super early early Portland cement, alumina cement, silica cement, jet cement and fly ash. Various cements such as cement may be mentioned, and one kind or a mixture of two or more kinds of these cements may be used. The average particle size of the cement used in the self-leveling material of the present invention may be the average particle size of commonly used cement. For example, in the case of ordinary Portland cement, the specific surface area is 3000 to 3
500 cm2 / g is suitable, and in the case of alumina cement, the specific surface area is 2850-5250 cm2 / g.
About g is preferable.

【0016】また、本発明セルフレベリング材に使用す
る骨材の具体例としては川砂、海砂、山砂、ケイ砂、及
びガラスビーズ等の人工砂、重質炭酸カルシウム等が挙
げられ、これら例示した骨材を一種、又は二種以上混合
して用いても良い。また、当該骨材の配合量としてはセ
メント100重量部に対し、30〜300重量部が好ま
しい。配合量が30重量部未満の場合には施工時に持続
的な流動性が得られず、作業性の低下を起こすことがあ
り、一方、配合量が300重量部を超えると十分な流動
性が得られない上、施工後のセルフレベリング材の物性
強度面で劣るという問題を生じることがあるからであ
る。また、骨材の平均粒径は45〜710μmが好まし
い。当該平均粒径が45μm未満の場合にはセメント等
の他の配合材料と混合する際、十分な流動性が持続して
得られなくなり、合成樹脂粉末が塊状物となって分散不
良を起こすことがある上、混合した材料の硬化後にひび
割れが生じ易くなる等の問題がある。一方、平均粒径が
710μmより大きい場合には、材料分離が起こり易く
なり、混合した材料の均質な硬化体が得られず、施工後
のセルフレベリング材の表面の緻密さが不十分となり、
表面の仕上り点で問題が生ずることがあるからである。
Specific examples of aggregates used in the self-leveling material of the present invention include river sand, sea sand, mountain sand, silica sand, artificial sand such as glass beads, and ground calcium carbonate. The above aggregates may be used alone or in combination of two or more. The amount of the aggregate is preferably 30 to 300 parts by weight with respect to 100 parts by weight of cement. If the blending amount is less than 30 parts by weight, continuous fluidity may not be obtained at the time of construction and workability may be deteriorated. On the other hand, if the blending amount exceeds 300 parts by weight, sufficient fluidity may be obtained. In addition, the self-leveling material after construction may be inferior in physical strength. The average particle size of the aggregate is preferably 45 to 710 μm. When the average particle size is less than 45 μm, when mixed with other compounding materials such as cement, sufficient fluidity cannot be obtained continuously, and the synthetic resin powder may become a lump and cause poor dispersion. In addition, there is a problem that cracks easily occur after the mixed materials are cured. On the other hand, when the average particle size is larger than 710 μm, material separation is likely to occur, a homogeneous cured product of the mixed material cannot be obtained, and the surface level of the self-leveling material after construction becomes insufficient,
This is because problems may occur at the finish point of the surface.

【0017】また、本発明セルフレベリング材に石膏を
施工性、及び物性面から使用する。石膏の配合量として
はセメント100重量部に対し、1〜50重量部が好ま
しい。配合量が1重量部未満の場合には持続的な引張強
度が得られ難く、始発・終結時間に効果が少ないという
問題を生じることがあり、一方、配合量が50重量部を
超えると膨張によるひび割れを起こす可能性がある上、
下地からの膨れの危険性が大きいという問題を生じるこ
とがあるからである。また、本発明セルフレベリング材
に使用する石膏の平均粒径としては45〜250μmが
好ましい。
Further, gypsum is used for the self-leveling material of the present invention in terms of workability and physical properties. The blending amount of gypsum is preferably 1 to 50 parts by weight with respect to 100 parts by weight of cement. If the blending amount is less than 1 part by weight, it may be difficult to obtain a continuous tensile strength and there may be a problem that there is little effect on the starting and closing time, while if the blending amount exceeds 50 parts by weight, it may be caused by expansion. It can crack and
This is because there is a problem that the risk of swelling from the base is great. The average particle size of the gypsum used in the self-leveling material of the present invention is preferably 45 to 250 μm.

【0018】本発明のセルフレベリング材において添加
する合成樹脂として酢酸ビニル樹脂、バーサチック酸ビ
ニル樹脂、酢酸ビニル−バーサチック酸ビニル共重合
体、エチレン−酢酸ビニル共重合体、アクリル樹脂、酢
酸ビニル−アクリル酸共重合体、酢酸ビニル−バーサチ
ック酸ビニル−アクリル酸エステル共重合体、又はSB
Rを含有し、前記セルフレベリング材を施工した場合に
放置、乾燥中に合成樹脂が表面に集合し、その状態で硬
化することにより、優れたセルフレベリング性と表面に
鏡面に近い緻密さが得られる。即ち、本発明セルフレベ
リング材により、合成樹脂様の表面状態を得ることがで
きる。尚、上記合成樹脂は単独で使用してもよいし、ま
た、二種以上を混合して使用しても同様の効果を奏する
ことができる。
As the synthetic resin added to the self-leveling material of the present invention, vinyl acetate resin, vinyl versatate resin, vinyl acetate-vinyl versatate copolymer, ethylene-vinyl acetate copolymer, acrylic resin, vinyl acetate-acrylic acid. Copolymer, vinyl acetate-vinyl versatic acid-acrylic acid ester copolymer, or SB
When R is contained and the above-mentioned self-leveling material is applied, the synthetic resin gathers on the surface during standing and drying, and by curing in that state, excellent self-leveling property and surface-like closeness to a mirror surface are obtained. To be That is, with the self-leveling material of the present invention, a synthetic resin-like surface state can be obtained. The above synthetic resins may be used alone, or two or more kinds thereof may be mixed and used to obtain the same effect.

【0019】本発明のセルフレベリング材を作成する際
の当該合成樹脂の形態としては他の配合材料、即ち、セ
メント、骨材、水等と均一に混合可能であれば限定はさ
れないが、均一混合の容易性という観点から、パウダー
状であることが好ましく、さらに、パウダー状である前
記合成樹脂を予め水等の溶媒に分散させたエマルジョン
の形態であることがより好ましい。前記合成樹脂がパウ
ダー状である場合の粒径については1〜7μmが好まし
い。当該粒径が1μm未満の場合にはセメント等の他の
配合材料と混合する際、合成樹脂粉末が塊状物となって
分散不良を起こすことがあり、一方、粒径が7μmより
大きい場合には、施工後のセルフレベリング材の形成す
る表面の緻密さが不十分となり、仕上りの点で問題が生
ずることがあるからである。
The form of the synthetic resin used in preparing the self-leveling material of the present invention is not limited as long as it can be uniformly mixed with other compounding materials, that is, cement, aggregate, water, etc. From the viewpoint of ease of use, it is preferably in the form of powder, and more preferably in the form of an emulsion in which the powdery synthetic resin is previously dispersed in a solvent such as water. When the synthetic resin is powdery, the particle size is preferably 1 to 7 μm. If the particle size is less than 1 μm, when mixed with other compounding materials such as cement, the synthetic resin powder may form lumps and cause poor dispersion, while if the particle size is greater than 7 μm, The reason is that the surface formed by the self-leveling material after construction becomes insufficiently dense, which may cause a problem in terms of finish.

【0020】また、合成樹脂の配合量についてはセメン
ト100重量部に対し、3〜25重量部であることが好
ましい。合成樹脂の配合量が3重量部未満であると施工
後のセルフレベリング材の表面の緻密さが十分に確保す
ることができない上、セルフレベリング材としての強
度、耐摩耗性、耐候性、防水性、耐衝撃性、弾性、及び
当該セルフレベリング材と下地との接着強度が不足する
ことがあり、一方、25重量部を超えるとセルフレベリ
ング材の凝結遅延が起こり、作業性の低下や空気連行に
よる硬化後の強度不足が起こることがあるからである。
The amount of the synthetic resin compounded is preferably 3 to 25 parts by weight with respect to 100 parts by weight of cement. If the content of the synthetic resin is less than 3 parts by weight, the denseness of the surface of the self-leveling material after construction cannot be sufficiently ensured, and the strength, abrasion resistance, weather resistance and waterproofness as the self-leveling material are not ensured. , Impact resistance, elasticity, and the adhesive strength between the self-leveling material and the base may be insufficient, while if it exceeds 25 parts by weight, the self-leveling material may be delayed in setting, resulting in lower workability and air entrainment. This is because the strength after curing may be insufficient.

【0021】本発明セルフレベリング材が表面に鏡面に
近い緻密さを形成する等の効果を奏するためには、上述
したように前記セルフレベリング材を施工した際に配合
した合成樹脂が表面に集合することが必要であるが、当
該作用を奏するためには添加剤として減水剤、及び保水
剤が重要な役割を果たす。
In order for the self-leveling material of the present invention to exert an effect such as forming a denseness close to a mirror surface on the surface, the synthetic resin compounded when the self-leveling material is applied as described above gathers on the surface. However, the water-reducing agent and the water-retaining agent play an important role as additives in order to exert the effect.

【0022】減水剤はセルフレベリング材の原材料の混
和を促進し、展延した場合に骨材の沈降等を防止する
他、混合された原材料間の流動を円滑にし、各々の原材
料の均一混合を容易にするとともに、施工後の酢酸ビニ
ル樹脂、バーサチック酸ビニル樹脂等の樹脂の表面への
集合をも円滑にする作用がある。本発明セルフレベリン
グ材において使用可能な減水剤としては、メラミンホル
マリン縮合物スルホン酸塩、リグニンスルホン酸塩、ポ
リアルキルアリルスルホン酸塩、β−ナフタレンスルホ
ン酸アルデヒド縮合物、ポリカルボン酸塩、酸性リン酸
モノエステル、酸性リン酸ジエステル、ポリエーテルジ
オール等が例示でき、これら例示した一種、又は二種以
上の物質を適宜選択し、又は混合して使用することもで
きる。また、減水剤の添加量はセメント100重量部に
対し0.1〜5重量部であることが好ましい。減水剤が
0.1重量部未満になると、十分な流動性が得られず、
骨材の沈降等を防止するなどの効果不十分であり、ま
た、セルフレベリング材の初期ひび割れの低減効果が低
下してしまう等の質的な低下が避けられず、一方、減水
剤が5重量部を超えると凝結遅延性が顕著となり、硬化
不良を引き起こすことがある上、混合した原材料の分離
が起こり易くなり、均質な硬化体が得られず、セルフレ
ベリング材自体の圧縮強度等を著しく低下させてしまう
可能性があるからである。
The water-reducing agent promotes mixing of the raw materials of the self-leveling material, prevents sedimentation of aggregates when spread, smooths the flow between the mixed raw materials, and uniformly mixes the raw materials. In addition to facilitating the work, it has an effect of facilitating the assembly of the resin such as vinyl acetate resin and versatic vinyl acid resin on the surface after the construction. Examples of the water reducing agent that can be used in the self-leveling material of the present invention include melamine formalin condensate sulfonate, lignin sulfonate, polyalkylallyl sulfonate, β-naphthalene sulfonate aldehyde condensate, polycarboxylate, and acidic phosphorus. Examples thereof include acid monoesters, acidic phosphoric acid diesters, and polyether diols, and one or more of these exemplified substances can be appropriately selected or mixed and used. The amount of the water reducing agent added is preferably 0.1 to 5 parts by weight with respect to 100 parts by weight of cement. If the water reducing agent is less than 0.1 part by weight, sufficient fluidity cannot be obtained,
Inadequate effects such as preventing sedimentation of aggregates are unavoidable, and qualitative deterioration such as a decrease in the initial cracking reduction effect of self-leveling materials is unavoidable. If the content exceeds the above range, the retardation of setting becomes remarkable, which may cause curing failure, and the mixed raw materials are likely to be separated, a homogeneous cured product cannot be obtained, and the compressive strength of the self-leveling material itself is significantly reduced. This is because there is a possibility of causing it.

【0023】保水剤はセルフレベリング材を展延した場
合に骨材の沈降等を防止する他、混合された原材料間の
流動を円滑にし、各々の原材料の均一混合を容易にする
とともに、施工後の酢酸ビニル樹脂、バーサチック酸ビ
ニル樹脂等の樹脂の表面への集合をも円滑にする作用が
ある。本発明セルフレベリング材において使用可能な保
水剤としてはセルロースエーテル類、例えば、メチルセ
ルロース、エチルセルロース、ヒドロキシエチルセルロ
ース、カクボキシメチル等、又は水溶性高分子、例え
ば、ポリアクリルアミド、ポリエチレンオキシド、ポリ
ビニルアルコール等が挙げられ、これら例示した一種、
又は二種以上の物質を適宜選択し、又は混合して使用す
ることもできる。また、保水剤の添加量はセメント10
0重量部に対し0.02〜5重量部であることが好まし
い。保水剤が0.02重量部未満になると、十分な保水
効果が得られない。一方、保水剤が5重量部を超えると
混合した原材料の分離が顕著となり、セルフレベリング
材自体の強度が著しく低下させてしまう可能性がある。
The water retention agent prevents sedimentation of the aggregate when the self-leveling material is spread, smoothes the flow between the mixed raw materials, facilitates uniform mixing of each raw material, and after the construction. It also has an effect of smoothly assembling the resin such as vinyl acetate resin and vinyl versatate resin on the surface. Examples of the water retention agent that can be used in the self-leveling material of the present invention include cellulose ethers such as methyl cellulose, ethyl cellulose, hydroxyethyl cellulose, caboxoxymethyl and the like, or water-soluble polymers such as polyacrylamide, polyethylene oxide and polyvinyl alcohol. One of these examples
Alternatively, two or more kinds of substances may be appropriately selected or mixed and used. The amount of water retention agent added is 10
It is preferably 0.02 to 5 parts by weight with respect to 0 parts by weight. If the amount of the water retention agent is less than 0.02 part by weight, a sufficient water retention effect cannot be obtained. On the other hand, when the amount of the water retention agent exceeds 5 parts by weight, the separation of the mixed raw materials becomes remarkable, and the strength of the self-leveling material itself may be significantly reduced.

【0024】消泡剤は原材料の攪拌時に巻き込まれた空
気が気泡を形成してしまい、当該気泡が原因でセルフレ
ベリング材の強度を損なうことがあるため、界面活性剤
等の作用により、かかる現象を防止することを目的とし
て添加する。本発明セルフレベリング材に使用可能な消
泡剤としてはアルコール系、脂肪酸エステル系、ポリオ
ール系等のものが例示でき、これら例示した一種、又は
二種以上の物質を適宜選択して使用することもできる。
また、消泡剤の添加量は使用する消泡剤の種類によって
異なるが、セメント100重量部に対し0.05〜3重
量部であることが好ましい。消泡剤が0.05重量部未
満になると、十分な消泡効果は得られず、空気連行によ
る強度不足や表面状態が滑らかにならない等の仕上り不
良が起こることがあり、一方、消泡剤が3重量部を超え
て添加したとしても、更なる消泡効果の向上が期待でき
ないため、経済的観点より適切でない。
In the defoaming agent, the air entrained during the stirring of the raw materials forms bubbles, and the bubbles may impair the strength of the self-leveling material. Is added for the purpose of preventing Examples of the defoaming agent that can be used in the self-leveling material of the present invention include alcohol-based, fatty acid ester-based, and polyol-based defoaming agents, and these exemplified one or two or more substances may be appropriately selected and used. it can.
The amount of the defoaming agent added varies depending on the type of the defoaming agent used, but is preferably 0.05 to 3 parts by weight with respect to 100 parts by weight of cement. If the amount of the defoaming agent is less than 0.05 parts by weight, a sufficient defoaming effect cannot be obtained, and finish defects such as insufficient strength due to air entrainment and a non-smooth surface condition may occur. Is more than 3 parts by weight, further improvement of the defoaming effect cannot be expected, so that it is not appropriate from an economical point of view.

【0025】また、必要に応じて、その他の添加剤、即
ち、遅延剤、又は早強剤を使用してもよい。当該遅延
剤、又は早強剤はセルフレベリング材の硬化速度を適宜
調節するために添加される。本発明セルフレベリング材
に使用可能な遅延剤としてはグルコン酸、グルコヘプト
ン酸、アラボン酸、リンゴ酸、又はクエン酸、及び、こ
れらの、ナトリウム、カリウム、カルシウム、マグネシ
ウム、アンモニウム、トリエタノールアミン等の無機
塩、又は有機塩等のオキシカルボン酸;グルコース、フ
ラクトース、ガラクトース、サッカロース、キシロー
ス、アビトース、リポーズ、異性化糖等の単糖類や、二
糖、三糖などのオリゴ糖、又はデキストリンなどのオリ
ゴ糖、又はデキストラン等の多糖類、これらを含む糖蜜
類等の糖類、又はソルビトール等の糖アルコール、弗化
マグネシウム、リン酸並びにその塩又はホウ酸エステル
類、アミノカルボン酸とその塩、アルカリ可溶タンパク
質、フミン酸、タンニン酸、フェノール、グリセリン等
の多価アルコール、アミノトリ(メチレンホスホン酸)、
1-ヒドロキシエチリデン-1,1-ジホスホ1-ジホスホン
酸、エチレンジアミンテトラ(メチレンホスホン酸)、ジ
エチレントリアミンペンタ(メチレンホスホン酸)、及び
これらのアルカリ金属塩、アルカリ土類金属塩等のホス
ホン酸及びその誘導体等を例示することができる。ま
た、遅延剤の添加量は使用する遅延剤の種類によって異
なるが、セメント100重量部に対し0.01〜2重量
部であることが好ましい。遅延剤が0.01重量部未満
になると、硬化時間が早すぎるため、施工作業上必要な
可使時間が得られず、作業性の観点から好ましくなく、
一方、遅延剤が2重量部を超えて添加されると凝結遅延
による作業性の低下や材料の硬化不良、及び強度不良が
発生することがあり適切でないからである。
If desired, other additives, that is, a retarder or an early strengthening agent may be used. The retarder or early-strengthening agent is added to appropriately adjust the curing rate of the self-leveling material. Examples of the retarder that can be used in the self-leveling material of the present invention include gluconic acid, glucoheptonic acid, arabonic acid, malic acid, or citric acid, and their inorganics such as sodium, potassium, calcium, magnesium, ammonium, and triethanolamine. Oxycarboxylic acids such as salts or organic salts; monosaccharides such as glucose, fructose, galactose, saccharose, xylose, abitose, repose, isomerized sugar, oligosaccharides such as disaccharides and trisaccharides, or oligosaccharides such as dextrin. , Or polysaccharides such as dextran, sugars such as molasses containing these, sugar alcohols such as sorbitol, magnesium fluoride, phosphoric acid and salts thereof or borate esters, aminocarboxylic acids and salts thereof, alkali-soluble proteins , Humic acid, tannic acid, phenol, glycerin Polyhydric alcohols and the like, amino tri (methylene phosphonic acid),
1-Hydroxyethylidene-1,1-diphospho-1-diphosphonic acid, ethylenediaminetetra (methylenephosphonic acid), diethylenetriaminepenta (methylenephosphonic acid), and phosphonic acids such as alkali metal salts and alkaline earth metal salts and derivatives thereof Etc. can be illustrated. The amount of retarder added varies depending on the type of retarder used, but is preferably 0.01 to 2 parts by weight per 100 parts by weight of cement. If the amount of the retarder is less than 0.01 parts by weight, the curing time will be too fast, and the work life required for the construction work will not be obtained, which is not preferable from the viewpoint of workability.
On the other hand, if the retarder is added in an amount of more than 2 parts by weight, workability may be deteriorated due to retardation of setting, poor curing of the material, and poor strength may occur, which is not appropriate.

【0026】一方、本発明セルフレベリングにて使用可
能な早強剤としては塩化カルシウム、亜硝酸カルシウ
ム、硝酸カルシウム、臭化カルシウム、ヨウ化カルシウ
ム等の可溶性カルシウム塩、塩化鉄、塩化マグネシウム
等の塩化物の他、硫酸塩、水酸化カリウム、水酸化ナト
リウム、炭酸塩、チオ硫酸塩、ギ酸及びギ酸カルシウム
等のギ酸塩等が例示できる。また、早強剤の添加量は使
用する早強剤の種類によって異なるが、セメント100
重量部に対し0.05〜3重量部であることが好まし
い。早強剤が0.05重量部未満になると、十分な速硬
性が得られず、初期強度の発現に効果が期待できない。
一方、早強剤が3重量部を超えて添加されると、使用す
るセメントの種類によっては材料の硬化が早く起こりす
ぎるため、作業性の観点から適切でない場合があるから
である。
On the other hand, as an early strengthening agent that can be used in the self-leveling of the present invention, soluble calcium salts such as calcium chloride, calcium nitrite, calcium nitrate, calcium bromide and calcium iodide, and chlorides such as iron chloride and magnesium chloride. In addition to the substances, sulfates, potassium hydroxide, sodium hydroxide, carbonates, thiosulfates, formates such as formic acid and calcium formate, etc. can be exemplified. The amount of the early strengthening agent added varies depending on the type of the early strengthening agent used.
It is preferably 0.05 to 3 parts by weight with respect to parts by weight. If the amount of the early-hardening agent is less than 0.05 parts by weight, sufficient fast-hardening property cannot be obtained, and the effect of developing the initial strength cannot be expected.
On the other hand, if the early-strengthening agent is added in an amount of more than 3 parts by weight, the material may harden too quickly depending on the type of cement used, which may not be appropriate from the viewpoint of workability.

【0027】また、本発明セルフレベリング材を施工す
る際には溶媒として水を添加することが必要となる。添
加する水の量としてはセメント100重量部に対して、
30〜60重量部であることが好適である。前記水の量
が30重量部未満であると十分な流動性が得られず、展
延が困難となり作業性が低下することがあり、一方、6
0重量部を超えるとセルフレベリング材自体の強度面で
問題が生ずることがあるからである。
Further, when applying the self-leveling material of the present invention, it is necessary to add water as a solvent. The amount of water added is 100 parts by weight of cement,
It is preferably 30 to 60 parts by weight. If the amount of water is less than 30 parts by weight, sufficient fluidity may not be obtained, spreading may be difficult and workability may decrease, while 6
This is because if it exceeds 0 parts by weight, problems may occur in the strength of the self-leveling material itself.

【0028】また、本発明セルフレベリング材は従来、
床面に流し込み、展延した後、放置、乾燥、硬化させる
ことにより施工する。本発明が使用可能な床面として、
モルタル、セメント、木質、プラスチック製タイル、若
しくはシート、セラミクス、ステンレス等の金属が例示
できる。また、従来のセルフレベリング材同様、床面に
不陸や改装工事等の際、タイル、又はシート等の床材を
剥離した場合に生ずる床面に残存する接着剤、又は粘着
剤等が多少ならあってもよい。
Further, the self-leveling material of the present invention has hitherto been
After pouring it on the floor and spreading it, leave it, dry it, and cure it. As a floor surface that can be used in the present invention,
Examples of the metal include mortar, cement, wood, plastic tiles, sheets, ceramics, and stainless steel. Also, like conventional self-leveling materials, if there is some residual adhesive or adhesive on the floor surface that occurs when the floor material such as tiles or sheets is peeled off when the floor surface is uneven or renovation work is performed. It may be.

【0029】本発明セルフレベリング材を上記に例示し
た床面に適量流し込む。流し込むセルフレベリング材の
量は床面の状態、即ち、不陸の程度、又は残存接着剤等
が形成する床面の凹凸の度合いによって加減する。具体
的には0.1mm以上の厚さに展延することが好まし
く、より好ましくは0.1〜30mm以下に展延する。
セルフレベリング材の厚みの最も薄い部分が0.1mm
の厚みを下回るとセルフレベリング材としての十分な強
度が得られず、一方、30mmを上回ると表面が平滑か
つ緻密な床面は得られるが、経済的観点からは好ましく
ないためである。
An appropriate amount of the self-leveling material of the present invention is poured onto the floor surface exemplified above. The amount of the self-leveling material to be poured varies depending on the condition of the floor surface, that is, the degree of unevenness or the degree of unevenness of the floor surface formed by the residual adhesive or the like. Specifically, it is preferably spread to a thickness of 0.1 mm or more, more preferably 0.1 to 30 mm or less.
The thinnest part of the self-leveling material is 0.1 mm
If it is less than 30 mm, sufficient strength as a self-leveling material cannot be obtained, and if it exceeds 30 mm, a smooth and dense floor surface can be obtained, but this is not preferable from an economical point of view.

【0030】セルフレベリング材の展延後、当該セルフ
レベリング材が硬化するまで放置することにより、本発
明セルフレベリング材の施工は終了する。
After the self-leveling material is spread, the self-leveling material of the present invention is left to stand until the self-leveling material is cured, whereby the construction of the self-leveling material of the present invention is completed.

【0031】[0031]

【発明の効果】本発明は以上に説明した形態で実施さ
れ、以下に記載される効果を奏する。
The present invention is carried out in the form described above, and has the following effects.

【0032】床材の施工の際、本発明セルフレベリング
材の使用により、従来のセルフレベリング材と比較して
より容易に平滑かつ緻密な表面を形成することができ
る。即ち、従来のセルフレベリング材のようにプライマ
ー処理をしなくとも鏡面に近い極めて緻密な表面と平滑
性を得ることができる。
By using the self-leveling material of the present invention, it is possible to form a smooth and dense surface more easily than the conventional self-leveling material when applying the floor material. That is, it is possible to obtain an extremely dense surface close to a mirror surface and smoothness without a primer treatment unlike the conventional self-leveling material.

【0033】従って、従来、単にセルフレベリング材に
よって処理しただけでは、接着剤付き床材を施工するた
めに十分な表面の緻密さが得られず、施工安定性や接着
力の観点から、プライマー処理をしない限り施工が不可
能であった前記接着剤等付き床材が本発明セルフレベリ
ング材を使用することにより、前記プライマー処理をし
なくとも施工が可能となる。
Therefore, conventionally, simply treating with a self-leveling material cannot provide sufficient surface denseness for constructing a floor material with an adhesive, and from the viewpoint of construction stability and adhesive strength, a primer treatment is applied. By using the self-leveling material of the present invention for the floor material with an adhesive or the like which could not be applied unless the above-mentioned step, it becomes possible to perform the operation without the primer treatment.

【0034】また、改装時等に接着剤付き床材を貼りか
える場合、当該床材を剥離させた時、本発明セルフレベ
リング材によって処理された床面においては、表面平滑
性、かつ鏡面に近い緻密な表面を形成、維持できるた
め、前記床面に接着剤、又は粘着剤が残存することが極
めて少ない。従って、さらにレベリング材、若しくはけ
れん等の接着剤等の除去作業、又はプライマーによる再
度の下地処理は不要となり、当該貼り替え作業において
は作業効率が著しく向上し、作業時間も大幅に短縮され
る。
In addition, when the floor material with the adhesive is re-attached at the time of renovation, etc., when the floor material is peeled off, the floor surface treated with the self-leveling material of the present invention has surface smoothness and close to a mirror surface. Since a dense surface can be formed and maintained, the adhesive or the pressure-sensitive adhesive rarely remains on the floor surface. Therefore, it is not necessary to further remove the leveling material, the adhesive such as convulsions or the like, or to re-prime the surface with a primer, so that the work efficiency in the replacement work is significantly improved and the work time is significantly shortened.

【0035】さらに、本発明セルフレベリング材はモル
タルのみならず、コンクリート、木質、金属等下地の素
材を選ばず用いることができるため、極めて有用であ
る。
Furthermore, the self-leveling material of the present invention can be used not only as mortar but also as a base material such as concrete, wood and metal, and is therefore extremely useful.

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 FI テーマコート゛(参考) C04B 24:26 C04B 24:26 D G Z 14:36 14:36 22:14 B 22:14) 111:60 111:60 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 7 Identification code FI theme code (reference) C04B 24:26 C04B 24:26 DG 14:36 14:36 22:14 B 22:14) 111: 60 111: 60

Claims (9)

【特許請求の範囲】[Claims] 【請求項1】セメント、骨材、石膏、減水剤、保水剤、
及び消泡剤を主成分とするセルフレベリング材であっ
て、前記セメント100重量部に対し合成樹脂として酢
酸ビニル樹脂、バーサチック酸ビニル樹脂、酢酸ビニル
−バーサチック酸ビニル共重合体、エチレン−酢酸ビニ
ル共重合体、アクリル樹脂、酢酸ビニル−アクリル酸共
重合体、酢酸ビニル−バーサチック酸ビニル−アクリル
酸エステル共重合体、SBRの中の一、又は二以上の混
合物が3〜25重量部を含有することを特徴とするセル
フレベリング材。
1. Cement, aggregate, gypsum, water reducing agent, water retention agent,
And a self-leveling material containing a defoaming agent as a main component, wherein vinyl acetate resin, vinyl versatate resin, vinyl acetate-vinyl versatate copolymer, ethylene-vinyl acetate copolymer as a synthetic resin relative to 100 parts by weight of the cement. One, or a mixture of two or more of a polymer, an acrylic resin, a vinyl acetate-acrylic acid copolymer, a vinyl acetate-vinyl versatic acid-acrylic acid ester copolymer, and SBR should contain 3 to 25 parts by weight. Self-leveling material characterized by.
【請求項2】前記セメント100重量部に対して、骨材
が30〜300重量部含有することを特徴とした請求項
1記載のセルフレベリング材。
2. The self-leveling material according to claim 1, wherein the aggregate contains 30 to 300 parts by weight with respect to 100 parts by weight of the cement.
【請求項3】前記セメント100重量部に対して、石膏
が1〜50重量部含有することを特徴とした請求項1乃
至2記載のセルフレベリング材。
3. The self-leveling material according to claim 1, wherein gypsum is contained in an amount of 1 to 50 parts by weight based on 100 parts by weight of the cement.
【請求項4】前記セメント100重量部に対して、減水
剤が0.1〜5重量部を含有することを特徴とする請求
項1乃至3記載のセルフレベリング材。
4. The self-leveling material according to claim 1, wherein the water reducing agent is contained in an amount of 0.1 to 5 parts by weight based on 100 parts by weight of the cement.
【請求項5】前記セメント100重量部に対して、保水
剤が0.02〜5重量部を含有することを特徴とする請
求項1乃至4記載のセルフレベリング材。
5. The self-leveling material according to claim 1, wherein the water retention agent contains 0.02 to 5 parts by weight with respect to 100 parts by weight of the cement.
【請求項6】前記セメント100重量部に対して、消泡
剤が0.05〜3重量部を含有することを特徴とする請
求項1乃至5記載のセルフレベリング材。
6. The self-leveling material according to claim 1, wherein the defoaming agent contains 0.05 to 3 parts by weight with respect to 100 parts by weight of the cement.
【請求項7】前記合成樹脂の平均粒径が1〜7μmであ
ることを特徴とする請求項1乃至6記載のセルフレベリ
ング材。
7. The self-leveling material according to claim 1, wherein the synthetic resin has an average particle diameter of 1 to 7 μm.
【請求項8】前記骨材の平均粒径が45〜710μmで
あることを特徴とする請求項1乃至7記載のセルフレベ
リング材。
8. The self-leveling material according to claim 1, wherein the average particle diameter of the aggregate is 45 to 710 μm.
【請求項9】前記石膏の平均粒径が45〜250μmで
あることを特徴とする請求項1乃至8記載のセルフレベ
リング材。
9. The self-leveling material according to claim 1, wherein the gypsum has an average particle size of 45 to 250 μm.
JP2001207282A 2001-07-09 2001-07-09 Self-levelling plaster Pending JP2003020263A (en)