JP2003017261A - Manufacturing method and device of electroluminescent element - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a manufacturing method and device of an electroluminescent element in which the constituting layer in the emission region that is almost impossible of patterning is formed uniformly and in high quality membrane and the patterning is performed in a wide viscosity range and in wide selections of use of solvent, and which can be implemented in a short time. SOLUTION: In the manufacturing method of an electroluminescent element in which a hole transport layer 4 and an electron transport luminous layer 5 are provided as a layer having a light-emitting region between a transparent picture element electrode 2 and a negative electrode 10, at least the electron transport luminous layer 5 is formed in a prescribed pattern by the transfer of its constituting material by the letterpress reverse-offset method.

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method and an apparatus for manufacturing an electroluminescent element suitable as, for example, a self-luminous thin flat display.

[0002]

2. Description of the Related Art Conventionally, research and development of a lightweight and highly efficient flat panel display have been actively carried out for a screen display of a computer or a television.

One of them is a cathode ray tube (CRT).
Is currently used as the most popular display because of its high brightness and good color reproducibility, but it has a problem that it is relatively heavy, takes up space, and consumes high power.

Therefore, as a lightweight and thin display, a liquid crystal display has been commercialized and is becoming popular nowadays. However, the drawbacks peculiar to the liquid crystal display are that the viewing angle is narrow and that it is sufficient for high-speed pixel signals. There is a problem that response performance cannot be obtained. In particular, there is a problem in that it is difficult to manufacture and the cost is high for increasing the screen size of the display.

As an alternative to this, there is a display using a light emitting diode, but there are still problems that the manufacturing cost is high and it is difficult to form a matrix structure of the light emitting diode on one substrate.

As a flat panel display capable of solving these problems, attention has recently been paid to an organic electroluminescent device (organic EL device) using an organic light emitting material.
L element). That is, the organic electroluminescent device is expected to realize a flat panel display that is self-luminous, has a high response speed, and has no viewing angle dependency by using an organic compound as a light emitting material.

In recent years, reports have been made on electroluminescent devices using organic compounds as constituent materials (Applied Physics
Letters, 51, p. 913 (1987)). In this report, C.I. W. T
ang et al. disclose an electroluminescent device having a structure in which an organic light emitting layer and a charge transport layer are laminated.

An excellent electroluminescent device is obtained by using a tris (8-quinolinol) aluminum complex (hereinafter referred to as Alq ₃ ) having both high luminous efficiency and electron transporting property as a light emitting material. In addition, Coumarin derivative and DCM1 (Eastman) are added to Alq ₃ forming the organic light emitting layer.
(Chemicals Co., Ltd.) was manufactured with a device doped with a fluorescent dye, and it was reported that the emission color was changed by proper selection of the dye, and it was also disclosed that the luminous efficiency was increased as compared with the undoped one. (Journal of Applied Physic
s, 65, p. 3610 (1989)).

Following this research, many researches and developments have been carried out, and as a new functional material, fluorescent chelating metal complexes, electron-transporting organic molecules and hole-transporting organic molecules have been developed and used for colorization. Various studies have been made toward this.

FIG. 8 shows an example of a conventional organic electroluminescent device.

This organic electroluminescence (EL) element 73A is
ITO (Indium Tin Oxid) is placed on the transparent glass substrate 51.
e) The transparent pixel electrode (anode) 52, the hole transport layer 54, the light emitting layer 75, the electron transport layer 55, and the cathode 62 are sequentially formed by, for example, a vacuum vapor deposition method or the like.

Then, the organic electroluminescence (EL) device 7
In 3A, when a DC voltage 74 is applied between the ITO transparent pixel electrode 52 which is an anode and the cathode 62, holes as carriers injected from the ITO transparent pixel electrode 52 pass through the hole transport layer 54. On the other hand, the electrons injected from the cathode 62 move through the electron transport layer 55, respectively, and recombination of these electron-hole pairs occurs in the light emitting layer 75, and light emission 76 of a predetermined wavelength occurs from there. This can be observed from the transparent glass substrate 51 side.

FIG. 9 shows another conventional organic electroluminescent element 73B. In this organic electroluminescent element 73B,
The electron transport layer 55A also serves as a light emitting layer.

Then, this structure is specifically constructed as a laminated structure shown in FIG. That is, a hole transporting layer 54 is formed on a glass substrate 51 provided with an ITO transparent pixel electrode (anode) 52, an electron transporting light emitting layer 55A is formed on the hole transporting layer 54, and calcium which enhances electron injecting property is formed on the hole transporting layer 55A. (C
The a) layer 63 is provided between the a) layer 63 and the aluminum (Al) layer 60.

Such an organic electroluminescence (EL) device 73
In the layer structure of B, the material of the hole transport layer 54 is poly (3,4) -ethylenedioxythiophene (hereinafter, PE).
Abbreviated as DOT. ), Poly (2-methoxy-5- (2′-ethylhexyloxy)) is used for the electron-transporting light-emitting layer 55A.
-1,4-phenylene vinylene) (hereinafter MEH-PP
Abbreviated as V. ) Is used, and a cathode 62 composed of a calcium (Ca) layer 63 and an aluminum (Al) layer 60 for improving the electron injection property is provided thereon.

FIG. 11 shows the organic electroluminescent device 7 of FIG.
The structural example of the flat display using 3B is shown.

As shown in the figure, an organic laminated structure composed of an electron transport layer 55A and a hole transport layer 54 has a cathode 62 and an anode 52.
Are arranged in a predetermined pattern. Cathode 62 and anode 52
Are provided in stripes intersecting with each other, and the luminance signal circuit 84 and the shift register built-in control circuit 85 are respectively provided.
And the signal voltage is applied. This allows
The organic laminated structure emits light at the position (pixel) where the selected cathode 62 and anode 52 intersect.

[0018]

In the conventional fabrication of organic electroluminescent elements, the organic light emitting layer such as the electron transporting light emitting layer and the electrode are mainly formed by the vacuum deposition method.

However, the display using the current organic electroluminescence device is difficult to produce because the size of the display causes vapor spots and the like. Moreover, organic E
It is said that the L material cannot be patterned after the film formation.

As a method of solving this, a device manufacturing method using a polymer EL material has been attracting attention. For example, a method for producing a polymer EL device by an inkjet printing technique described in JP-A-10-153967 is known.

However, in the method for producing a polymer organic EL device by the ink jet printing method, first, since it is possible to handle only a material having a low viscosity and it is a droplet discharge type, an enclosure is provided with a black resist (resin). Without it, the pattern cannot be formed. That is, by removing the low-viscosity ink adhering to the black resist together with the resist, the ink is left in a predetermined pattern on the other portions.

Further, as described in Japanese Patent Application Laid-Open No. 10-153967, the ink material is water-soluble or soluble in alcohol- and glycol-based solvents because of the ink jet head. Because of their desirability, only limited solvents can be used. In addition, since the ink jetting time for a unit screen is fixed in an inkjet, the larger the screen, the longer the time.

The object of the present invention is to form a uniform and high-quality patterned constituent layer of a light-emitting region where patterning is impossible, and to perform the patterning in a wide viscosity range and a wide range of solvents. It is an object of the present invention to provide a method for manufacturing an electroluminescent device and a device for the same, which can be carried out in a short time under selective use.

[0024]

That is, the present invention provides a method for manufacturing an electroluminescent element, wherein a layer having a light emitting region is provided between a first electrode and a second electrode, The present invention relates to a method for manufacturing an electroluminescence device (hereinafter, referred to as a manufacturing method of the present invention), which comprises forming at least one layer into a predetermined pattern by transferring the constituent material by a letterpress inversion offset method.

The present invention is also used for manufacturing an electroluminescent device in which a layer having a light emitting region is provided between a first electrode and a second electrode, and at least one of the layers is The present invention also provides an electroluminescent device manufacturing apparatus (hereinafter, referred to as the manufacturing apparatus of the present invention) including a transfer unit for forming a predetermined pattern by transferring the constituent material by a letterpress inversion offset method.

According to the manufacturing method and the apparatus thereof of the present invention,
Since at least one of the layers having a light emitting region is formed into a predetermined pattern by transfer of the constituent material by the letterpress inversion offset method, even a material that cannot be patterned can be formed into a uniform and high-quality predetermined pattern. It can be formed and arrayed, the constituent materials can be transferred in a wide range of viscosities, the solvent used can be selected and used in a wide range, and the rapid transfer of each pattern enables the time to be shortened. It is possible to provide an electroluminescent device having high light emission efficiency and high light emission intensity which is sufficiently compatible with patterning of materials of a plurality of colors on a screen.

[0027]

BEST MODE FOR CARRYING OUT THE INVENTION In the manufacturing method and the apparatus therefor of the present invention, it is desirable to form the layer having the predetermined pattern by removing the solvent after transferring the ink comprising the solution or dispersion liquid of the constituent materials. .

In this case, after an ink composed of a solution or dispersion of the constituent materials is prepared, it is applied on the ink releasable treated surface, and a relief plate made of glass or the like having a predetermined pattern is pressed against the applied surface, The ink may be transferred and removed on the convex portion of the letterpress, and the ink remaining on the coating surface may be transferred to the predetermined pattern on a substrate such as glass.

Further, an organic light emitting material (for example, MEH-PP) is used.
Polymer light-emitting materials such as V, low-molecular light-emitting materials such as anthracene and phthalocyanine) or precursors thereof are added to water or an organic solvent (for example, cyclohexanone, tetrahydrofuran (TH
F), xylene, dimethylformamide (DMF), dimethylsulfoxide (DMSO), acetonitrile, etc.)
After preparing the ink by dissolving or dispersing it in the above, a light emitting layer may be formed by the transfer.

Further, a polymer light emitting material such as MEH-PPV or a precursor thereof and an organic material such as PEDOT or a precursor thereof are mixed with water or an organic solvent (cyclohexanone, tetrahydrofuran (THF), xylene, dimethylformamide (DMF). After preparing or preparing the ink by dissolving or dispersing it in dimethylsulfoxide (DMSO), acetonitrile or the like), a composite layer (laminated structure) of the polymer light emitting material and the organic material may be formed by the transfer.

Further, after transferring the ink to the predetermined pattern on the hole transport layer, the solvent is removed to form an electron transporting light emitting layer, or after transferring the ink to the predetermined pattern, the solvent is removed. May be removed to form a single-color or multi-color layer.

For example, the layer is formed in the predetermined pattern on an electrode patterned at least for each pixel on a substrate made of glass or at least on an electrode patterned at least for each pixel on a substrate made of glass. Inks of three kinds of luminescent colors of red, green and blue are transferred for each color to form a luminescent layer of each color in the predetermined pattern.

Further, the transfer means for transferring the ink to form the light emitting layer, the composite layer, the electron transporting light emitting layer or the layer is an ink composed of a solution or dispersion of the constituent materials. An ink coating / transferring means having an ink releasable treated surface for coating with, and a relief plate of a predetermined pattern pressed against the ink application surface, and after transferring and removing the ink to the convex portion of the relief plate, It is preferable that the ink remaining on the ink application surface is transferred to a predetermined pattern.

In this case, the ink applying / transferring means may be formed in a roll shape, and by this rotation, the transfer removal of the ink to the relief printing plate and the transfer of the predetermined pattern may be performed.

Next, preferred embodiments of the present invention will be specifically described with reference to the drawings.

First, FIGS. 2 and 3 exemplify a manufacturing process of the organic electroluminescence (EL) device according to the present embodiment.

First, as shown in FIG. 2A, the transparent glass substrate 1 having a hydrophobic surface is ultrasonically cleaned using a cleaning agent manufactured by Fisher in a substrate cleaning process, and then, The washing step of washing several times with ultrapure water is performed twice. Then, after washing with acetone and isopropyl alcohol, it is dried in a clean oven, and further, before and / or before irradiation with ultraviolet-ozone (UV-ozone), the ITO transparent pixel electrode (anode) 2 is subjected to vacuum deposition or the like and patterning. Form.

This ITO transparent pixel electrode 2 is shown in FIG.
As shown in (1), the pixel portion 37 is formed, for example, 70 ×
It may be an island-shaped independent pattern of 200 nm, and each pattern may be insulated and separated by an insulator 14 as shown in FIGS. 7 (2) and 7 (3). Alternatively, the pixel electrode may have a stripe shape.

Next, as shown in FIG. 2 (2), the hole transporting aqueous solution 4a of PEDOT having the molecular structure shown in FIG. 5 is dropped by a microsyringe 3 under controlled atmospheric conditions, for example, 2 sec. , 600 rpm and 58
sec, spin coating is performed at 3000 rpm.

Next, as shown in FIG. 2C, this is placed on a hot plate and baked to form a hole transport (PEDOT) layer 4. In addition, this firing treatment is performed, for example, at 120 ° C. for 10 minutes while controlling the firing temperature or the degree of reduced pressure in a treatment tank in an atmospheric state or a reduced pressure state.

Next, by controlling the conditions in the atmospheric condition, as shown in FIG. 3 (4), ME which is an electron transporting polymer having the molecular structure shown in FIG. 4 (1), (2) or (3).
The ink 5b made of an organic solution of H-PPV, CN-PPV or PPV is transferred onto the hole transport layer 4 in a predetermined pattern by the letterpress inversion offset method.

Next, this is baked at, for example, 70 ° C. for 2 hours to form a film, after which the solvent is removed by evaporation in a vacuum oven at, for example, 70 ° C., and electron-transporting light emission is performed as shown in FIG. 3 (5). Form layer 5.

Here, the ink 5 of PPV or its derivative is used.
The transfer of b is preferably performed by the relief inversion offset method shown in FIG.

That is, as shown in FIG. 1 (1), a wire bar (not shown) is provided for a roll 21 which has been subjected to an ink peeling treatment and which is integrally provided with, for example, a silicone resin 20 on its peripheral surface.
After applying the ink 5a with a predetermined thickness (for example, 100 nm) by the above method, as shown in FIG. 1 (2), the roll 21 is relatively rolled on the relief plate 22 (glass mask) made of glass, The ink in contact with the leading end of the roll is removed as 5c from the surface of the roll 21. This is silicone resin 2
The peeling action by 0 makes it possible to perform easily and with high accuracy. The convex portion of the relief plate 22 is preliminarily processed into a pattern opposite to the electron transporting light emitting layer to be formed.

In this way, after the necessary ink pattern 5b is left on the roll 21, as shown in FIG. 1 (3), the roll 21 is relatively rolled while being in contact with the glass substrate 1 of the organic electroluminescent device. The ink 5b remaining on the roll 21 is transferred onto the substrate 1 in a predetermined pattern, and the above-described baking and drying processes are performed. This transfer is performed by the silicon resin 20 of the roll 21.
Can be easily and highly accurately performed by the peeling action of. The electron-transporting light-emitting layer 5 thus formed is not limited to the monochrome pattern shown in FIG. 6, but the full-color pattern 5 shown in FIG. 7 can be obtained by sequentially performing the relief inversion offset method.
R (for red), 5G (for green), and 5B (for blue) can be formed, respectively.

Next, as shown in FIG. 3 (6), a calcium (Ca) layer 13 having a thickness of 5000 nm, for example, is formed on the electron-transporting light-emitting layer 5 by vacuum evaporation or the like and patterning. An aluminum (Al) layer 10 serving as a main electrode is formed on the layer 13 by, for example, 10,000 n.
Then, an Au—Ge layer 9 for protection and improving the bonding property is formed on the aluminum (Al) layer 10 to a thickness of, for example, 10,000 nm to form a cathode.

Next, as shown in FIG. 3 (7), Au-G
The counter substrate 8 is covered on the e layer 9 and the side portions are further sealed with an epoxy resin or the like to complete the organic electroluminescence device 15.

Organic electroluminescent device 15 according to the present embodiment
According to the manufacturing method and the apparatus thereof, at least one of the layers having a light emitting region, that is, the electron transporting light emitting layer 5 is formed in a predetermined pattern by transfer of the constituent material by the letterpress inversion offset method. Even a material that cannot be processed can be formed and arranged in a predetermined pattern having a uniform and high film quality.

Further, the constituent materials can be transferred in a wide range of viscosities, and a wide range of solvents can be selected and used.

Moreover, since each pattern can be transferred quickly, the time can be shortened, and the electroluminescence of high emission rate and high emission intensity can be achieved even on a large screen and for patterning materials of a plurality of colors. An element can be provided.

In the letterpress inversion offset method described above, in particular, the ink 5a is applied on the silicon resin 20 of the roll 21, and the unnecessary ink 5c is removed by the letterpress 22 made of glass.
Also, since the subsequent transfer of the ink 5b is performed from the silicon resin 20, there is no so-called stringing phenomenon that occurs due to the separation of each ink, unevenness of the transferred ink does not occur, and the target pattern is easily and highly accurately. can get.

In this case, since the relief plate 22 is made of glass, the unnecessary ink 5c can be easily removed, and the necessary ink 5b can be easily transferred onto the organic hole transport layer 4, and the transferred ink has a pattern collapse. It is possible to transfer with good adhesion without using. Even in the case of the element structure in which the hole transport layer 4 is not provided, since the base of the transfer is ITO or the glass substrate, the peeling removal of the unnecessary ink 5c and the peeling transfer of the necessary ink 5b can be performed at the same level, and each peeling is performed. It becomes easier to control the conditions.

Moreover, the use of the relief plate 22 facilitates the removal of the unnecessary ink 5c from the silicone resin 20, and facilitates the peeling transfer of the required ink 5b from the silicone resin 20 to a substantially flat surface, thus eliminating the transfer ink. The surface property is also improved, and a uniform layer having a good film quality can be formed. The relief plate 22 itself can also be processed with high accuracy by etching, and can be processed into a pattern particularly suitable for a pattern having a low projection (that is, a thin ink layer), and thus organic electroluminescence that requires transfer of a thin ink. It is advantageous for devices.

[0054]

EXAMPLES Examples of the present invention will be described below.

<Production of Organic Electroluminescent Device> First, UV-
By irradiating with ozone, the ITO transparent pixel electrode 2 was patterned as shown in FIG. After UV-ozone treatment of this as needed, 600 r of PEDOT was formed on the glass substrate.
Spin coating was performed at pm for 2 seconds, and 3000 rpm for 58 seconds. After completion of this spin coating, it was baked at 120 ° C. for 10 minutes using a hot plate to form a hole transport layer on the entire surface.

Next, after completion of the firing, the electron transporting light emitting material is printed in a predetermined pattern on the hole transporting layer by a relief inversion offset method as shown in FIG. 1 to form the electron transporting light emitting layer in a predetermined pattern. did. The following materials were used as the light emitting material. After completion of printing, a film was formed by baking at 70 ° C. for 2 hours, and then the solvent was removed in a vacuum oven at 70 ° C.

[0057]

[Chemical 1]

Next, calcium (Ca) is made to have a thickness of 500 Å, aluminum (Al) is made to have a thickness of 1000 Å, and Au-G.
e was vacuum-deposited to a thickness of 1000Å in sequence and then patterned to form a cathode. After that, sealing was performed using an epoxy resin to fabricate an organic electroluminescent device as shown in FIG. 3 (7).

<Evaluation of Luminescent Properties> Luminous efficiency (cd / A) and luminous intensity (cd / m ² ) of each color were measured for this organic electroluminescent device, and the results are shown in Tables 1 to 3 below. These tables also show measured values of luminous efficiency and luminous intensity when PPV or a derivative thereof was formed on the entire surface by spin coating for comparison.

[0060]

[Table 1]

After manufacturing this organic electroluminescent device, it was left in a nitrogen atmosphere for one month, but no device deterioration was observed. In addition, when the initial luminance was 100 cd / m ² and a constant current was applied to continuously emit light to forcibly degrade the luminance, it was 1300 hours until the luminance decreased to half.

[0062]

[Table 2]

After manufacturing this organic electroluminescent device, it was left in a nitrogen atmosphere for one month, but no device deterioration was observed. In addition, when the initial luminance was 100 cd / m ² and the current value was constantly energized to continuously emit light and forcibly deteriorated, it was 1210 hours until the luminance decreased to half.

[Table 3]

After manufacturing this organic electroluminescent device, it was left in a nitrogen atmosphere for one month, but no device deterioration was observed. In addition, when the initial luminance was 100 cd / m ² and the current value was constantly energized to continuously emit light and forcibly deteriorated, it was 1450 hours until the luminance decreased to half.

According to the results shown in the above tables, the organic electroluminescent devices of the examples of the present invention are easy to pattern the light emitting layer and have a luminous efficiency comparable to that of the spin coating method. It had a luminescence intensity and showed good luminescence characteristics.
Then, this was advantageous for forming the above-described light emitting layers of the respective colors on the common substrate to manufacture an organic electroluminescent element for full-color display.

The embodiments and examples of the present invention described above can be further modified based on the technical idea of the present invention.

For example, in the above-mentioned organic electroluminescence device, the luminescent material transferred by the relief inversion offset method is PP
Not only V or its derivative, but also other organic or polymer light emitting materials may be used. For example, the hole transport layer made of PEDOT described above may be formed in a predetermined pattern by the same relief inversion offset method.

The shape, structure, operating method, etc. of each member used in the above-mentioned relief inversion offset method may be variously changed.

Further, although the above-mentioned element is for a display element, for example, it may have various other structures.
Further, other than the display element, it may be an element as an optical communication means for receiving the light emitted by electroluminescence as the signal light.

[0070]

According to the manufacturing method and the apparatus thereof of the present invention, at least one of the layers having the light emitting region is formed into a predetermined pattern by transferring the constituent material thereof by the letterpress inversion offset method. It is possible to form and arrange even a material that cannot be processed into a predetermined pattern of uniform and high film quality, transfer the constituent materials in a wide range of viscosity, and use a wide range of solvents to select. It is possible to provide a high luminous efficiency and high luminous intensity electroluminescence device that can be used for a large screen and is sufficiently compatible with patterning of materials of a plurality of colors. .

[Brief description of drawings]

FIG. 1 is a cross-sectional view for explaining a letterpress inversion offset method used for manufacturing an organic electroluminescent device according to the present invention in the order of steps.

FIG. 2 is a cross-sectional view showing the steps of manufacturing the organic electroluminescent device in the same order.

FIG. 3 is a cross-sectional view showing the steps of manufacturing the organic electroluminescent element in the same order.

[FIG. 4] Similarly, MEH which is a light emitting material of an organic electroluminescence device.
It is a molecular structure figure of -PPV, CN-PPV, and PPV.

FIG. 5 is a molecular structure diagram of PEDOT.

FIG. 6 is a pattern diagram of the same electron-transporting light-emitting layer.

FIG. 7 is a plan view (1) of the pixel section and sectional views (2) and (3) taken along the line AA of the same.

FIG. 8 is a schematic cross-sectional view showing an example of an organic electroluminescent element in a conventional example.

FIG. 9 is a schematic cross-sectional view showing another example of the organic electroluminescent element.

FIG. 10 is a cross-sectional view showing a configuration example of the same organic electroluminescent element.

FIG. 11 is a schematic view showing a configuration example of a flat display using the same organic electroluminescent element.

[Explanation of symbols]

1, 8 ... Glass substrate, 2 ... ITO transparent pixel electrode (anode), 3 ... Microsyringe, 4 ... Hole transport layer, 5 ...
Electron-transporting light-emitting layer, 5a ... Ink for organic EL material, 5
b ... Necessary ink, 5c ... Unwanted ink, 7 ... Epoxy resin, 9 ... Au-Ge layer, 10 ... Aluminum (Al)
Layer, 13 ... Calcium (Ca) layer, 14 ... Insulating layer, 15
... organic electroluminescent device, 20 ... Releasable treated surface (silicon resin), 21 ... Roll, 22 ... Letterpress (glass mask), 3
7 ... Pixel part

   ─────────────────────────────────────────────────── ─── Continued front page    F-term (reference) 3K007 AB02 AB03 AB04 AB11 AB18                       BA06 CA01 CB01 DA01 DB03                       EB00 FA01

Claims (14)

[Claims] 1. A method of manufacturing an electroluminescent device comprising a layer having a light emitting region provided between a first electrode and a second electrode, wherein at least one of the layers is a letterpress inversion of its constituent material. A method for manufacturing an electroluminescent device, which comprises forming a predetermined pattern by transfer by an offset method. 2. The method for manufacturing an electroluminescent element according to claim 1, wherein the solvent is removed after the transfer of the ink composed of the solution or dispersion liquid of the constituent materials to form the layer having the predetermined pattern. 3. An ink comprising a solution or dispersion of the constituent materials is prepared and then applied on the ink releasable treated surface,
Pressing a relief plate of a predetermined pattern against the application surface, transferring and removing the ink to the convex portion of the relief plate, and further transferring the ink remaining on the application surface to the predetermined pattern,
The method for manufacturing an electroluminescent device according to claim 2. 4. An organic light emitting material or a precursor thereof is dissolved or dispersed in water or an organic solvent to prepare the ink,
The method for manufacturing an electroluminescent device according to claim 2, wherein a light emitting layer is formed by the transfer. 5. A polymer light emitting material or a precursor thereof and an organic material or a precursor thereof are dissolved or dispersed in water or an organic solvent to prepare the ink, and then by the transfer, the polymer light emitting material and the polymer light emitting material are prepared. Forming a composite layer with the organic material,
The method for manufacturing an electroluminescent device according to claim 2. 6. The method of manufacturing an electroluminescent device according to claim 2, wherein the electron transporting light emitting layer is formed by removing the solvent after transferring the ink to the predetermined pattern on the hole transporting layer. 7. The method for manufacturing an electroluminescent device according to claim 2, wherein after the ink is transferred to the predetermined pattern, the solvent is removed to form a layer for a single color or a plurality of colors. 8. The method for manufacturing an electroluminescence device according to claim 7, wherein the layer is formed in the predetermined pattern on an electrode patterned on at least each pixel on a substrate. 9. Ink of at least three types of emission colors of red, green and blue is transferred for each color onto an electrode patterned on a substrate at least for each pixel, and the emission layer of each color is formed into the predetermined pattern. The method for manufacturing an electroluminescent device according to claim 7, wherein the electroluminescent device is formed according to claim 1. 10. Used in manufacturing an electroluminescent device in which a layer having a light emitting region is provided between a first electrode and a second electrode, and at least one of the layers is made of a constituent material thereof. An apparatus for manufacturing an electroluminescence device, comprising a transfer means for forming a predetermined pattern by transfer by the letterpress inversion offset method. 11. The ink comprising a solution or dispersion of the constituent materials is transferred by the transfer means.
The manufacturing apparatus of the electroluminescent element as described in 0. 12. The transfer means comprises an ink applying / transfer means having an ink releasable treatment surface for applying ink made of a solution or dispersion of the constituent material, and a predetermined pattern pressed against the ink applying surface. 12. The electroluminescence according to claim 11, further comprising a relief plate, which is configured to transfer the ink onto the convex portion of the relief plate and then transfer the ink remaining on the ink application surface to the predetermined pattern. Device manufacturing equipment. 13. The electroluminescent device according to claim 12, wherein the ink applying / transferring unit is formed in a roll shape, and the rotation removes and transfers the ink to the relief plate and transfers the predetermined pattern. Manufacturing equipment. 14. The electroluminescent device according to claim 10, which is used for forming the light emitting layer, the composite layer, the electron transporting light emitting layer, or the layer according to claim 4. Device manufacturing equipment.