JP2002364091A - Outer wall structure - Google Patents

Outer wall structure

Info

Publication number
JP2002364091A
JP2002364091A JP2001172325A JP2001172325A JP2002364091A JP 2002364091 A JP2002364091 A JP 2002364091A JP 2001172325 A JP2001172325 A JP 2001172325A JP 2001172325 A JP2001172325 A JP 2001172325A JP 2002364091 A JP2002364091 A JP 2002364091A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
outer wall
wood
wall structure
receiving material
veneer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2001172325A
Other languages
Japanese (ja)
Inventor
Hideoki Toriyama
秀興 鳥山
Original Assignee
Nippon Paper Industries Co Ltd
Pal Co Ltd
日本製紙株式会社
株式会社パル
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To provide an outer wall structure which sets the vapor release speed in a wall body to a large value to improve condensation preventing effect, is excellent in strength, maintains air-tightness in a room, and is low in production cost. SOLUTION: The outer wall structure is constructed according to a wood frame construction method with a venting construction method applied thereto. According to the outer wall structure, a frame wall 2 is erected, which has a waterproof vapor-permeable sheet 3 stuck to an outside thereof, and a venting corbel 5 of a predetermined size, formed of a woody laminate which is obtained by laminating and bonding woody veneers together, is mounted on vertical frames (studs) 4 of the frame wall 2 from above the waterproof vapor-permeable sheet 3. Then, an outer wall panel 12 is stuck to the venting corbel 5, and a vent passage 14 is defined between the outer wall panel 12 and the waterproof vapor-permeable sheet 3.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001 】 [0001]

【発明の属する技術分野】本発明は、外壁内部に結露が発生することを防止する通気構法を施した枠組壁工法による外壁構造に関し、しかも壁倍率の大きな耐久性のある外壁構造に関する。 The present invention relates to relates to the outer wall structure by wood frame construction subjected to ventilation construction method for preventing condensation inside the outer wall occurs, moreover relates outer wall structure with large durable walls magnification.

【0002 】 [0002]

【従来の技術】外壁内部に結露が発生することを防止する通気構法を施した枠組壁工法(ツーバイフォー工法) BACKGROUND OF THE INVENTION wood frame construction subjected to ventilation construction method for preventing outer wall inside the condensation occurs (two-by-four construction method)
による従来の木造住宅の外壁構造として、図3に示すように、枠組壁51の縦枠(スタッド)52の室外側側面上に、下地板53としてのOSB等のボード類や構造用合板等を張り付け、その上に湿気は通すが水分は通さない防水透湿シート54で覆い、防水透湿シート54の上から、ムク材からなる通気用受材55を取り付け、該通気用受材55の上にサイディング等の外壁パネル56を張り付け、該外壁パネル56と前記防水透湿シート54 By the outer wall structure of a conventional wooden houses, as shown in FIG. 3, the vertical frame (stud) 52 of the outdoor-side upper side of the framework wall 51, the board such as OSB and structural plywood or the like as a base plate 53 It stuck, thereon moisture pass but covered with a waterproof breathable sheet 54 impermeable moisture, from the top of the waterproof breathable sheet 54, attached to vent receiving material 55 made of solid wood, on the vent for receiving material 55 affixed to the outer wall panel 56 of the siding or the like, the the outer wall panel 56 waterproof breathable sheet 54
との間に通気路57を設けた構造が知られている。 The provided structure ventilation passage 57 is known between.

【0003 】しかしながら、このような外壁構造では、ボード類や構造用合板等の下地板53の透湿抵抗が大きいので、壁体内の水蒸気の放出速度が遅く、このため壁体内に結露が発生したり、枠組材などの壁体構造部材が湿気のために腐朽したりするなどの恐れがあるといった問題点があった。 However, in such an outer wall structure, the moisture permeation resistance of the underlying plate 53 such Boards or structural plywood is large, slow rate of release of water vapor wall body, condensation occurs Consequently wall body or, the wall structure member, such as a framework material has a problem such risk is such or decay for moisture.

【0004 】そこで、これを解決するべく、特開平5 [0004] Therefore, in order to solve this problem, JP-A-5
−5331号公報及び特開平5−280110号公報においては、下地構造用合板の適宜箇所に通気孔を設けて、湿気の放出を行い結露の発生を防止することが開示されている。 In -5331 and JP Hei 5-280110 discloses, in a vent provided in appropriate positions of the plywood base structure, preventing the occurrence of condensation performs the release of moisture is disclosed.

【0005 】また、実開平7−13918号公報によれば、枠組壁の垂直部材の室内側にスペーサーを介して壁面下地材が取り付けられ、外壁下地板と枠組壁における水平部材の室内側側面との間に通気用の隙間を形成し、この隙間に対峙する床面構成用の構造用合板の部分に通気用の貫通孔を形成することが開示されている。 Further, according to the actual Hei 7-13918, JP-wall base member via a spacer is attached to the interior side of the vertical members of the frame wall, and the indoor side surface of the horizontal member at the outer wall base plate and framed wall forming a gap for ventilation, to form a through hole for venting the portion of structural plywood for the floor structure that faces in the gap is disclosed in between.

【0006 】 [0006]

【発明が解決しようとする課題】しかしながら、特開平5−5331号公報及び特開平5−280110号公報においては、下地構造用合板を張り付けて且つ通気孔を設けているために、その手間暇とコストがかさむばかりでなく、壁体内の水蒸気放出速度を実用レベルにまでもっていくには、かなりの通気孔面積を必要とし、その通気孔面積が大きすぎると、通気用受材がムク材からなる胴縁材等である場合には、外壁構造体としての強度、すなわち壁倍率が低下してしまうという問題点があった。 [SUMMARY OF THE INVENTION However, in Japanese Laid-5-5331 and JP-A No. 5-280110, JP-to are provided and vents sticking a plywood base structure, and its time and effort costs not only increase, the bring the steam release rate wall body to a practical level, and require substantial vent area, when the vent area is too large, ventilation image receiving material is made of solid wood If a furring strip material or the like, the strength of the outer wall structure, ie walls magnification is disadvantageously lowered.
そして、このように、壁体内の水蒸気放出速度を実用レベルにまで高めて結露を防止し、しかも外壁構造体としての強度すなわち壁倍率を維持することは至難の業であった。 And thus, to increase the vapor release rate wall body to a practical level to prevent condensation, yet maintaining the strength or walls magnification as the outer wall structure was extremely difficult.

【0007 】また、結露防止を重視するあまり、ボード類や構造用合板を省いて前記枠組壁51の縦枠(スタッド)52の上に直接防水透湿シート54を張り付け、 Moreover, too much emphasis on anti-condensation, affixed directly waterproof breathable sheet 54 omitted Boards and structural plywood on top of the vertical frame (stud) 52 of the framework wall 51,
該防水透湿シート54の上から前記枠組壁51の縦枠5 Vertical frame of the framed wall 51 from the top of the waterproof moisture-permeable sheet 54 5
2に、通気用受材55を取り付け、該通気用受材55の上に外壁パネル56を張り付けることも試みられたが、 2, mounting the vent receiving material 55, but also attempted to paste an outer wall panel 56 over the vent for receiving material 55,
通気用受材55がムク材からなる胴縁材等の場合では、 In the case of the barrel edge material such that the ventilation image receiving material 55 is made of solid wood,
上記と同様に外壁構造体としての強度、すなわち壁倍率が低下してしまい、特に地震等で外力が加わった時、通気用受材55が割れたり変形し外壁パネル56の接合部で割れ、脱落等が発生する恐れがあった。 Strength as the same manner as described above the outer wall structure, i.e. causes reduced wall ratio, especially when the external force is applied by an earthquake or the like, cracks at the junction of the outer wall panel 56 is deformed or cracked ventilation receiving material 55, falling etc. there is a risk to occur.

【0008 】一方、実開平7−13918号公報においては、スペーサーを介して床面用の構造用合板に通気用の貫通孔を設けた構造になっているため、床下から室内側へ隙間風が入り易く冷暖房効果も低下し住み心地に問題点があった。 On the other hand, in the real-Open 7-13918 discloses because the device has a structure in which a through hole for ventilation through the spacer structural plywood for floor and draft underfloor toward the cabin easy heating and cooling effect also enters there is a problem in the comfortable to live decreases.

【0009 】本発明は、上述した事情に鑑みてなされるもので、壁体内の水蒸気放出速度を大きくして結露防止効果を向上させ、しかも強度に優れ、室内側の気密性を保持し、更にコストの低減を図った外壁構造を提供することを課題とする。 [0009] The present invention has made in view of the above circumstances, to improve the anti-condensation effect by increasing the steam release rate wall body, moreover excellent in strength, it holds the indoor side of the air-tightness, further and to provide an outer wall structure thereby reducing the cost.

【0010 】 [0010]

【課題を解決するための手段】上記課題を解決するためなされた請求項1記載の本発明は、通気構法を施した枠組壁工法による外壁構造であって、前記枠組壁の外側に防水透湿シートが張り付けられ、該防水透湿シートの上から前記枠組壁の縦枠に、木質単板を積層接着して得られた木質積層材からなる所定の大きさの通気用受材が取り付けられ、該通気用受材の上に外壁パネルが張り付けられて、該外壁パネルと前記防水透湿シートとの間に通気路が設けられてなることを特徴とする。 SUMMARY OF THE INVENTION The present invention of claim 1, wherein has been made for solving the aforementioned problems is a external wall structure according to wood frame construction subjected to aeration construction method, waterproof breathable outside the framework wall sheet affixed to the vertical frame of the framed wall over the waterproof moisture-permeable sheet, a predetermined consisting resulting wood laminated material wood veneer laminated adhesive attached magnitude ducting receiving material, vent and exterior wall panels affixed to the top of the air for receiving material, wherein the vent passage is provided between the outer wall panel and the waterproof breathable sheet.

【0011 】かかる構成から、ボード類や構造用合板などの下地板が省けるので、これによる透湿抵抗がなくなり、壁体内の水蒸気放出速度が大きくなり、壁体内の水蒸気を防水透湿シートを通過させて容易に且つ確実に屋外へ放出することが可能になる。 [0011] From such a configuration, since the base plate such as Boards and structural plywood can be saved, this by eliminating the moisture permeation resistance, water vapor release rate of the wall inside the body increases, passes through a waterproof breathable sheet of water vapor of the wall body It is not it is possible to easily and reliably released to the outdoors. 従って、壁体内の結露防止効果の他、壁体内の乾燥により、枠組材の耐久性と断熱材の断熱性が一段と優れたものになる。 Accordingly, other condensation-preventing effect of the wall body, the drying of the wall body, the one thermal insulation durability and heat insulating material of the framework material is more excellent. また、通気用受材がムク材でなく木質積層材であるので、その木質積層材はムク材に比べ狂いや割れが生じ難く、釘保持力や材の剪断力に優れ、結果として壁倍率の大きな外壁構造を得ることが可能になることから、下地板を省くことによる強度の低下を木質積層材で十分補うことができ、強度に優れた外壁構造を得ることができる。 Further, aeration image receiving material because a wood laminate rather than solid wood, the wood laminates hardly occurs deviation or cracking compared to solid wood, excellent shear nail holding force or wood, as a result the walls magnification since it is possible to obtain a large outer wall structure, it is possible to compensate sufficiently the reduction in strength due omitting the base plate in wood laminate, it is possible to obtain an excellent external wall structure strength. また、 Also,
通気用受材の変形が抑えられるので外壁パネルの接合部に表面仕上げ材の割れ等の発生を有効に防止することができる。 The deformation ducting image receiving material is suppressed can be effectively prevent the occurrence of cracks in the surface finishing material at the junction of the outer wall panel. また、下地板を省くことにより、その分、外壁構造の壁厚を薄くすることが可能となり軽量化が図れる。 Further, by omitting the base plate, correspondingly, lighter it is possible to reduce the wall thickness of the outer wall structure can be achieved. また、部品点数や作業工程が少なくなるので、よりコストの低減が図れる。 Further, since the number of parts and working process are reduced, more cost reduction can be achieved. また、室内側の気密性が保持され、冷暖房効果の低下防止が図れる。 Further, the airtightness of the interior side is held, thereby decrease prevent heating and cooling effects.

【0012 】請求項2記載の本発明は、請求項1に記載の前記木質積層材が前記木質単板の繊維方向を互いに直交させて複数枚積層接着した合板であることを特徴とする。 [0012] According to a second aspect of the invention is characterized in that said plywood wood laminate has said fiber direction of the wood veneer is orthogonal laminating a plurality adhesion according to claim 1.

【0013 】かかる構成から、前記通気用受材となる木質積層材が木質単板の繊維方向を互いに直交させているので、通気用受材の含水率変動に伴うアバレや狂いがより少なく安定したものになり、壁体強度の一層の向上が図れる。 [0013] From such a construction, wood laminated material comprising said venting the image receiving material is because the are perpendicular to the fiber direction of the wood veneer to each other, abarelix and deviations caused by moisture content variations ducting image receiving material is less stable becomes a thing, it attained a further improvement in the wall strength.

【0014 】請求項3記載の本発明は、請求項1に記載の前記木質積層材が前記木質単板の繊維方向を互いに平行させて複数枚積層接着した平行合板で、該平行合板を構成する木質単板のうち、少なくとも一枚が前記木質単板の繊維方向を他の木質単板層と直交させた平行合板であることを特徴とする。 [0014] According to a third aspect of the invention, in the parallel plywood wood laminate has said fiber direction of the wood veneer is parallel laminating a plurality adhesion according to claim 1, constituting the parallel plate of wood veneer, characterized in that it is a parallel plate, at least one has a fiber direction of the wood veneer is orthogonal to the other wood veneer layer.

【0015 】かかる構成から、全ての木質単板層が平行である木質積層材に比べて繊維方向を他の木質単板層と直交させた木質単板層が有るので、通気用受材の含水率変動に伴うアバレや狂いがより少なく安定したものになり、壁体強度の一層の向上が図れる。 [0015] From this configuration, since all of the wood veneer layer is wood veneer layers and the fiber direction is perpendicular to the other wood veneer layers in comparison with wood laminates are parallel there, water ducting receiving material abarelix and deviations due to rate fluctuations become those less stable, thereby to achieve better wall strength.

【0016 】請求項4記載の本発明は、請求項2又は3に記載の前記木質積層材の厚さが7〜30mmであることを特徴とする。 [0016] According to a fourth aspect of the invention, the thickness of the wood laminate according to claim 2 or 3, characterized in that it is 7~30Mm.

【0017 】かかる構成から、木質積層材の厚さを7 [0017] from such a configuration, the thickness of the wood laminate 7
mm以上とすることにより、外壁構造としての強度すなわち壁倍率を維持すための強度を一層確実に得ることができ、そして木質積層材の厚さを30mm以下とすることにより、外壁構造の軽量化を一層効果的に得ることができる。 With more mm, it is possible to obtain the strength to maintain the strength or walls magnification as the outer wall structure more reliably and by a 30mm or less the thickness of the wood laminate, weight of the outer wall structure it can be obtained more effectively.

【0018 】請求項5記載の本発明は、請求項1ないし請求項4いずれか記載の前記枠組壁に所定間隔を開けて設けられている縦枠のなかの一部又は全部の縦枠が複数本並設して構成され、該複数本並設して構成された各縦枠を跨ぐように前記通気用受材が取り付けられ、前記外壁パネルはその接合部が前記通気用受材の幅の範囲内に位置するように張り付けられていることを特徴とする。 [0018] According to a fifth aspect of the invention, some or all of the vertical frame among the vertical frame on the framework wall according to any one of claims 1 to 4 are provided at predetermined intervals a plurality is constituted by Hon'nami set, it attached the ventilation receiving material so as to straddle the respective vertical frame which is constituted by said plurality of Hon'nami set, the outer wall panel has its junction the width of the venting receiving material characterized in that it is affixed to lie within the range.

【0019 】かかる構成から、縦枠のなかの一部又は全部の縦枠が複数本並設して構成されているので強度が向上し、しかも該複数本並設して構成された各縦枠には前記通気用受材が各縦枠を跨ぐように取り付けられているので、各縦枠は一体化され、前記外壁パネルはその接合部が前記通気用受材の幅の範囲内に位置するように張り付けられているので、外壁パネルによっても各縦枠の動きが有効に抑制されることになり、外壁構造としての強度すなわち壁倍率を維持するための強度をより一層確実に得ることができる。 [0019] From this configuration, since a part or the whole of the vertical frame among the vertical frame is constituted by a plurality Hon'nami set to improve strength, yet each vertical frame which is constituted by said plurality of Hon'nami set since the ventilation image receiving material is mounted so as to straddle the respective vertical frame, each vertical frame is integrated, the outer wall panel has its junction located within the width of the venting receiving material since affixed to, can also result in the movement of each vertical frame is effectively suppressed by the outer wall panels to give a strength to maintain the strength or walls magnification as the outer wall structure more reliably . また、各縦枠の動きが有効に抑制されることにより、外壁パネルの接合部の表面仕上げ材の割れ、脱落等の発生を有効に防止することができる。 Further, since the movement of each vertical frame is effectively suppressed, cracking of the facings of the junction of the outer wall panel, it is possible to effectively prevent the occurrence of dropout or the like.

【0020 】 [0020]

【発明の実施の形態】以下本発明に係る外壁構造の実施の形態を図面により詳細に説明する。 Described in more detail DETAILED DESCRIPTION OF THE INVENTION Hereinafter the embodiments of the outer wall structure according to the present invention with reference to the accompanying drawings. 図1は本発明の外壁構造の一実施の形態を示す一部切欠正面図、図2は図1のA−A線断面図である。 Figure 1 is a partially cutaway front view showing one embodiment of the outer wall structure of the present invention, FIG. 2 is a sectional view along line A-A of FIG.

【0021 】本例に示す通気構法を施した枠組壁工法(ツーバイフォー工法)による外壁構造としての外壁構造体1は、枠組壁2の室外側に防水透湿シート3が貼着され、該防水透湿シート3の上から前記枠組壁2の縦枠(スタッド)4に、木質単板を積層接着して得られた木質積層材からなる所定の大きさの通気用受材5が釘6で取り付けられている。 The outer wall structure 1 as the outer wall structure by wood frame construction subjected to aeration Construction (two-by-four construction method) described in the present embodiment, the waterproof moisture permeable sheet 3 is adhered to the outdoor side of the framework wall 2,-proof MizuToru the fountain vertical frame from the top of the wood frame 2 sheets 3 (stud) 4, mounting a predetermined size ventilation receiving material 5 consisting of a resulting wood laminated material wood veneer laminated adhesive nails 6 It is. 更に本例では、枠組壁2の二階部分の端根太7及び一階部分の端根太8と土台9とに通気用受材10が釘11で取り付けられている。 Further in this example, aeration image receiving material 10 is attached with nails 11 to the end joists 8 and base 9 of the end joists 7 and first floor of the second floor portion of the framed wall 2. 符号12は外壁パネルを示しており、釘13によって通気用受材5、10の上に固定され張り付けられている。 Reference numeral 12 denotes an outer wall panel, and affixed fixed on the vent receiving material 5,10 by nails 13. その外壁パネル12と前記防水透湿シート3との間には、通気用受材5、10がスペーサーとなって通気路14が設けられている。 Between the waterproof moisture permeable sheet 3 and an outer wall panel 12, ventilation passage 14 is provided so aeration image receiving material 5, 10 is a spacer. 尚、符号15は上枠、16は下枠、17は頭つなぎ、18は基礎、19は断熱材を示している。 Reference numeral 15 is the upper frame, 16 lower frame, 17 connecting head 18 is basic, 19 denotes a heat insulating material.

【0022 】前記枠組壁2で、所定間隔に設けられている縦枠4にあっては、本例では二本、一本、二本、一本・・・と、交互に設けられている。 [0022] In the framework wall 2, in the vertical frame 4 is disposed in a predetermined interval, two in this example, one, two, and one ..., are provided alternately. 間欠的に二本の縦枠4をその側面を接触させて並設したのは、外壁パネル12の接合部の固定を補強し外壁構造としての強度すなわち壁倍率を維持するための強度をより確実に得るためである。 The juxtaposed by intermittently the two vertical frames 4 are brought into contact with the side surface is more reliably the strength to maintain the strength or walls magnification as the outer wall structure to reinforce the fixing of the junction of the outer wall panel 12 it is to get to. ここで、二本としたのは、枠組壁工法(ツーバイフォー工法)では縦枠4の寸法が基準化されているため、強度保持に必要な太さを得るために二本とするものであって、更に強度が必要な場合は、三本或いはそれ以上であってもよいものとする。 Here, the reason the two, because the dimensions of the wood frame construction (two-by-four construction method) In the vertical frame 4 is scaled, there is to be two in order to obtain the thickness required for strength retention If further strength is required, it is assumed may be three or more. また、必ずしも間欠的である必要はなく、これらについては要求される強度に応じて縦枠4のなかの一部または全部の縦枠4に適宜選択されるものとする。 Moreover, not necessarily is intermittent, it shall be suitably selected part of among the vertical frame 4 or the vertical frame 4 of the whole in accordance with the strength required for these. このように、必要に応じて縦枠4を複数本並設し、該縦枠4の側面から釘等(図示せず)で縦枠4同士を縫い合わせるようにして接合すると、強度的により一層確実になる。 Thus, the vertical frames 4 and a plurality Hon'nami set as required, when joined as stitching vertical frame 4 together with nails or the like from the side of the vertical frame 4 (not shown), more reliably by strength become.

【0023 】前記通気用受材5は、長さ50〜65m In one embodiment of the invention, the ventilation for the image receiving material 5, length 50~65m
mの釘6(釘ピッチを100〜300mmピッチとする。接着剤を併用してもよい)で釘着されている。 Nails 6 m are Kugigi by (the nail pitch is 100~300mm pitch. May also be used in combination adhesive). また、通気用受材5は、枠組壁2の縦枠(スタッド)4に取り付けられているが、前記のように縦枠4のなかの一部の縦枠4が複数本(本例では二本)並設して構成されている場合には、その通気用受材5が複数本並設して構成された各縦枠4を跨ぐように取り付けられている。 Further, receiving material 5 for ventilation, but is attached to the vertical frame (studs) 4 framework wall 2, the two part of the vertical frame 4 is a plurality of (in this example of among the vertical frame 4 as described above when configured in this) juxtaposed, its aeration image receiving material 5 is attached so as to straddle the respective vertical frame 4 which is constituted by a plurality Hon'nami set. さらに、通気用受材5は、その大きさが前記外壁パネル1 Further, receiving material 5 for ventilation, whose magnitude is the outer wall panel 1
2と前記防水透湿シート3との間に設けられる通気路1 Air passage 1 provided between 2 and the waterproof breathable sheet 3
4を形成する間隙に応じて設定されている。 4 depending on the gap to form a has been set.

【0024 】前記通気用受材10は、通気用受材5と同様に長さ50〜65mmの釘11(釘ピッチを100 [0024] The ventilation image receiving material 10, the nail 11 (nail pitch length 50~65mm Like the aeration receiving material 5 100
〜300mmピッチとする。 And ~300mm pitch. 接着剤を併用してもよい) The adhesive may be used in combination)
で釘着されている。 In are Kugigi. また、通気用受材10は、その大きさが前記外壁パネル12と前記防水透湿シート3との間に設けられる通気路14を形成する間隙に応じて設定されている。 Furthermore, ventilation image receiving material 10 is set in accordance with the gap size thereof to form a ventilation channel 14 provided between the waterproof moisture permeable sheet 3 and the outer wall panel 12.

【0025 】かかる通気用受材5及び通気用受材10 [0025] for such ventilation receiving material 5 and the vent for receiving material 10
は、前記の通り所定厚さの木質単板を複数枚接着剤にて積層接着して得られた木質積層材からなっている。 It is made from the lamination adhesive-obtained wood laminate at a plurality glue wood veneer of the street predetermined thickness. その木質積層材としては、単板の木質繊維方向を互いに直交させた、いわゆる合板と、単板の木質繊維方向を互いに平行させた、いわゆる平行合板(LVL)とがあり、合板においては積層用接着剤の耐水性能によって普通合板と構造用合板とがある。 As the wood laminate, a wood fiber direction of the veneer were perpendicular to each other, so-called plywood, a wood fiber direction of the veneer were parallel to each other, there is a so-called parallel plate (LVL), laminated in plywood there is and ordinary plywood and structural plywood by the water resistance of the adhesive. 尚、合板は日本農林規格に定める構造用合板を用いることが最適である。 Incidentally, plywood is best to use a structural plywood specified in Japanese Agricultural Standards. 一方、平行合板においては、繊維方向を全ての単板で平行にしたものであってもよいが、その平行合板の各単板うち少なくとも一枚の単板の繊維方向を他の単板層と直交させた特殊な平行合板であると、割裂強度がよりいっそう高くなって各釘の固定力が増し壁体強度的に最適となる。 On the other hand, in the parallel plywood, the fiber direction may be obtained by parallel in all veneer, but the veneer layer fiber direction of at least another one of the veneer of the veneer of the parallel Plywood If it is a special parallel plywood was orthogonal to, splitting strength is more raised by the wall strength-optimal fixing force is increased for each nail. その一例としては、平行合板の表面から二層目と裏面から二層目の単板を直交させたものが挙げられる。 Examples thereof include those obtained by orthogonal two-layer veneer from the second layer and the rear surface from the surface of the parallel plate. 前記の合板及び平行合板は、単板積層枚数が奇数枚であっても、偶数枚であってもよいものとする。 The plywood and parallel plywood, laminated veneer sheets can be odd number shall be a even number.

【0026 】以上のように、通気用受材5及び通気用受材10が合板又は平行合板等の木質積層材であると、 [0026] As described above, the ventilation receiving material 5 and venting the image receiving material 10 is a wood laminate, such as plywood or parallel plywood,
従来のムク材の通気用受材と比べて、まわりの湿気や水分によって膨潤したり逆に収縮したり、反りが発生したりということが少なくなるという利点がある。 Compared with ventilation receiving material of a conventional solid wood, contracted in the opposite or swelled by moisture or water around or, there is an advantage that warpage is less that or generated. 言い換えれば、含水率変動に伴うアバレや狂いが従来のムク材に比べてより少なくなり安定したものになる。 In other words, the ones Abare and deviations caused by moisture content variations have fewer stable than traditional solid wood. 従って、通気用受材5及び通気用受材10の表面の平滑性が確保され、通気用受材5、10にあっては釘13で外壁パネル12を固着する際に外壁パネル12の安定した平滑性と釘保持力が得られるので面内剪断強度の強い壁体となる。 Thus, smoothness of the surface of the vent receiving material 5 and venting the image receiving material 10 is secured, in the ventilation receiving material 5,10 stable outer wall panel 12 when fixing the outer wall panel 12 with nails 13 since smoothness and nail holding power is obtained a strong wall in-plane shear strength. 前記外壁パネル12は長さ50mm程度の釘又はビス等(ピッチは100〜200mm程度)で固定されている(接着剤と併用してもよい)。 The outer wall panel 12 is length 50mm about nails or screws or the like (pitch about 100 to 200 mm) (may be used in combination with adhesive) that has been fixed in.

【0027 】また、通気用受材5においては、その通気用受材5が、複数本並設して構成された各縦枠4を跨ぐように取り付けられると、壁体にかかる外力による縦枠4の動きを有効に封じることができるという利点がある。 Further, in the aeration image receiving material 5, when the aeration image receiving material 5 is mounted so as to straddle the respective vertical frame 4 which is constituted by a plurality Hon'nami set, vertical frame due to an external force applied to the wall it can be advantageously effectively seal the fourth motion. 従って、その上に張り付けられた外壁パネル12の接合部の動きやズレが抑止され、外壁パネル12の接合部の表面仕上げ材の割れ等の発生を有効に防止することができる。 Therefore, it is possible that movement or displacement of the joints of the outer wall panel 12 attached on top is suppressed, effectively preventing the occurrence of cracks in the surface finishing material of the junction of the outer wall panel 12. また、縦枠4が複数本並設された箇所においては、通常よりも幅広い通気用受材5を用いることができるので、壁体強度的にもいっそう優れたものになる。 Further, in a portion where the vertical frame 4 has a plurality Hon'nami set, it is possible to use a wide range of ventilation receiving material 5 than normal, becomes excellent even in wall strength.
また、外壁パネル12の接合部が通気用受材5の幅方向のほぼ中央にくるようにすると壁体強度的にもいっそう優れたものになる(外壁パネル12の接合部の表面仕上げ材の割れ等の発生が有効に防止される)。 Further, substantially becomes excellent even in when to come to the central wall strength (crack of facings of the junction of the outer wall panel 12 in the width direction of the joint ventilation receiving material 5 of the outer wall panel 12 generation etc. can be prevented effectively).

【0028 】通気用受材5及び通気用受材10の寸法は、木質積層材の厚みを7〜30mm程度にすることが最適である。 The dimensions of the vent receiving material 5 and venting the receiving material 10, it is optimal to the thickness of the wood laminate about 7~30Mm. 木質積層材の厚さを7mm以上にすることにより、外壁構造としての強度すなわち壁倍率を維持すための強度を一層確実に得ることができるようになる。 By the thickness of the wood laminate than 7 mm, it is possible to obtain a strength for to maintain the intensity or walls magnification as the outer wall structure more reliably.
また、木質積層材の厚さを30mm以下にすることにより、外壁構造の軽量化を一層効果的に得ることができるようになる。 Further, by setting the thickness of the wood laminate to 30mm or less, it becomes possible to obtain a lighter of the outer wall structure more effectively. 一方、幅寸法は、縦枠4が一本の箇所である場合には、その縦枠4の幅に見合った寸法としておよそ30〜40mm程度がよいものとする。 On the other hand, the width dimension, when vertical frame 4 is sites of one shall approximately be about 30~40mm as the dimension commensurate with the width of the vertical frame 4. 二本又はそれ以上の複数本の箇所の場合には、それに見合った幅寸法とする。 In the case of two or more of the plurality of locations is a width dimension commensurate therewith. 例えば二本の箇所の場合は45〜80mm程度がよいものとする。 For example, in the case of two locations and good about 45~80Mm. 他方、長さ寸法は、枠組壁工法下地構造体の長さ寸法に見合った長さでよいものとする。 On the other hand, the length is assumed be a length commensurate with the length dimension of the wood frame construction underlying structure. 長さ方向のジョイントはあってもよいが、一本通しの場合の方が壁体強度上、より最適である。 The length direction of the joint may be, but towards the case of threading one is on wall strength, it is more optimum. 尚、ムク材からなる従来の通気用受材55(図3参照)の場合、その厚みが18mmを下回ると従来の通気用受材55(図3参照)が割れたり、反り狂いが生じ易く、釘保持力が低下し、従って壁体強度が低下する。 In the case of the conventional ventilation receiving material 55 (see FIG. 3) made of solid wood, cracked conventional ducting receiving material 55 (see FIG. 3) when the thickness is below 18 mm, easily warped deviation, nail holding force is lowered, thus wall strength decreases. この点本発明の外壁構造にかかる通気用受材5及び通気用受材10は木質積層材からなるので18mmより薄くてもこのようなことがない。 Ventilation receiving material 5 and venting the receiving material 10 of the outer wall structure of this point the present invention is such that there is no thinner than 18mm since a wood laminate.

【0029 】前記枠組壁2を構成する縦枠4、上枠1 The vertical frames 4 which constitute the framework wall 2, the upper frame 1
5、下枠16等は、栂材、ベイツガ材、スプルース材、 5, the like lower frame 16, Toga material, hemlock material, spruce,
スギ材、檜材又はこれらの集成材などの材料が用いられているが、これら以外であってもよい。 Cedar, although materials such as Japanese cypress material or these laminated wood is used, may be other than these. 通気用受材5及び通気用受材10に使用する木質積層材の樹種としては、ラワン、ジョンコン、メランティー、カポール、アビトンなどが用いられるが、これら以外の広葉樹又は針葉樹であってもよい。 The species of the wood laminate for use in ventilation receiving material 5 and venting the receiving material 10, lauan, Jonkon, Melan tea, Kapoor, although such Abiton is used, it may be a hardwood or softwood other than these. 単板の厚みは0.7〜3.0mm The thickness of the veneer is 0.7~3.0mm
程度のものが使われているが、この範囲に限ったものではない。 The extent of what is being used, but is not limited to this range. また、各単板の厚みを変えてもよい。 It is also possible to change the thickness of each single plate.

【0030 】その他、通気用受材5及び通気用受材1 [0030] Other, ventilation for receiving material 5 and ventilation for receiving material 1
0として防虫、防腐、防蟻処理した材料を用いてもよい。 Insect 0, preservatives, may be used anti-termite treated material. この場合、通気用受材5及び通気用受材10の耐久性がよりいっそう向上し、従って、壁体強度的にも最適である。 In this case, to further improve the durability of the vent receiving material 5 and venting the receiving material 10, therefore, it is ideal for wall strength. こうした防虫、防腐、防蟻の処理にあっては、 These insect repellent, antiseptic, in the processing of anti-termite,
木質積層材を構成する木質単板を積層接着する際の接着剤中に防虫、防腐、防蟻薬剤を所定量混入すればよい。 Insect in the adhesive at the time of laminating bond the wood veneer constituting the wood laminate, preservatives, may be mixed a predetermined amount of anti-termite agents.
混入量は接着剤に対して重量比で1〜2%混入すればよく、あまり多く混入し過ぎると接着不良の恐れがあるので注意を要する。 Mixing amount may be mixed 1-2% by weight relative to the adhesive requires attention because there is a risk of adhesive failure too contaminated too much. 例えば防虫薬剤として硼砂、硼酸、弗化ソーダ、ホキシム、フェニトロチオン、その他の薬剤が使用できる。 For example borax as insect agent, boric acid, sodium fluoride, phoxim, fenitrothion, other agents can be used. 単板への薬剤浸透量は硼砂、硼酸の場合、単板の全乾重量に対して0.2%以上であればよい。 Drug penetration amount into the veneer borax, when the boric acid, may be at least 0.2% relative to the total dry weight of the veneer. 弗化ソーダの場合は0.1%以上であればよい。 For sodium fluoride may be at least 0.1%. 積層用接着剤としては、ユリア系樹脂からなる通常の合板用接着剤でもよいが、耐水性能を考慮すればフェノール樹脂系接着剤又はその他の耐水性接着剤を用いることができる。 The laminating adhesive may be a conventional plywood adhesives consisting of urea resin, but can be used a phenolic resin-based adhesive, or other water-resistant adhesives Considering water resistance.

【0031 】枠組壁2は従来からの方法で製作し施工するものとする。 The framework wall 2 shall be made in the manner of a conventional construction. 土台9、基礎18なども従来からのものでよい。 Foundation 9, such as foundation 18 also may be of the past. 防水透湿シート3は、湿気は通すが水分は通さないものであって、ステープル等を用いて貼着されている。 Waterproof breathable sheet 3, moisture passes but be one impervious moisture, is stuck with the staples. その防水透湿シート3としては、例えばデュポン社製の「タイベック」などがよく使われている。 As a waterproof moisture-permeable sheet 3, for example, manufactured by DuPont "Tyvek" is often used.

【0032 】以上本発明に係る外壁構造によれば、ボード類や構造用合板などの従来の下地板が省けるので、 According to the external wall structure according to the present invention described above, since the conventional base plate including Boards and structural plywood can be omitted,
これによる透湿抵抗がなくなり、壁体内の水蒸気放出速度が大きくなる。 This by eliminating the moisture permeation resistance, water vapor release rate of the wall inside the body increases. そして、壁体内の水蒸気を防水透湿シートを通過させて容易に且つ確実に屋外へ放出することができる。 Then, it is possible to easily and reliably released to the outdoors water vapor wall body and passed through a waterproof breathable sheet. 従って、結露防止効果に一段と優れたものにすることができる。 Therefore, it is possible to those more excellent in dew condensation prevention effect. また、通気用受材5及び通気用受材10が従来のようなムク材でなく木質積層材であるので、材に狂いが生じ難く釘保持力や材の剪断力に優れ、 Further, since the ventilation receiving material 5 and venting the image receiving material 10 is wood laminate rather than solid wood, such as in the prior art, excellent shear difficult nail holding force or wood cause deviation in wood,
結果として壁倍率の大きな外壁構造を得ることが可能になる。 As a result it is possible to obtain a large outer wall structure of the wall magnification. 従って、従来の下地板を省くことによる強度の低下を木質積層材で十分補うことができ、強度に優れた外壁構造を得ることができる。 Therefore, a decrease in strength due omitting conventional base plate with wood laminate can compensate sufficiently, it is possible to obtain an excellent external wall structure strength. また、通気用受材5及び通気用受材10の変形が抑えられるので外壁パネル12の接合部の表面仕上げ材の割れ等の発生を有効に防止することができる。 Further, it is possible to effectively prevent the occurrence of cracks in the surface finishing material of the junction of the outer wall panel 12 the deformation ducting receiving material 5 and venting the image receiving material 10 is suppressed. また、従来の下地板を省くことにより、 Further, by eliminating the conventional base plate,
その分外壁構造の壁厚を薄くすることが可能となり軽量化を図ることができる。 It is possible to reduce the weight it is possible to reduce the wall thickness of that amount the outer wall structure. また、部品点数や作業工程が少なくなりコストの低減を図ることができる。 Further, it is possible to reduce the cost of parts and working process are reduced. また、従来のような通気用の貫通孔を設ける構造ではないため室内側の気密性が保持されることから、冷暖房効果の低下防止を図ることができる。 Also, since the airtightness of the interior side for the through-hole is not a structure in which the for conventional such ventilation is maintained, it is possible to prevent deterioration of the cooling and heating effect.

【0033 】 [0033]

【実施例】次に実施例1〜4、比較例1、2にもとづいて壁耐力試験を行い、本発明に係る外壁構造が従来の下地板を省くことによる強度の低下を木質積層材で十分に補い、その結果、強度に優れた外壁構造になっていることを証明する(実施例1〜4の壁倍率結果と比較例1の壁倍率結果とを比較する)。 The following Examples 1-4, performed walls proof test based on Comparative Examples 1 and 2, sufficient reduction in strength due to the external wall structure according to the present invention is omitted conventional base plate with wood laminate supplemented, the result, (comparing the walls magnification results of Comparative example 1 and the wall magnification results of examples 1 to 4) to prove that it is excellent outer wall structure strength. また、通気用受材がムク材でなく木質積層材であることにより、壁倍率の大きな外壁構造になっていることを証明する(実施例1〜4の壁倍率結果と比較例2の壁倍率結果とを比較する)。 Furthermore, by venting the image receiving material is wood laminate rather than solid wood, proves that it is a major outer wall structure of the wall magnification (wall magnification compared to the wall magnification results of Examples 1 to 4 Example 2 to compare the results and). 〔実施例1〕枠組壁工法の外壁構造体を以下のように作製した。 The outer wall structure of Example 1 wood frame construction was prepared as follows. 樹種として米栂材を使用し、上枠、下枠、縦枠(スタッド)からなる高さ2730mm、横幅1820 Using the hemlock material as species, upper frame, lower frame, the vertical frame height 2730mm consisting (stud), width 1820
mm、厚さ90mmの枠組壁工法の外壁構造体を作製した。 mm, to prepare an outer wall structure of wood frame construction with a thickness of 90 mm. スタッドは外壁パネルの接合部がくる箇所は910 Locations stud joint portions of the outer wall panels come 910
mm間隔に二本重ねとし、その中間位置に一本のスタッドを配置した。 And two superimposed mm intervals and arranged one stud in its intermediate position. 上枠、下枠、スタッドの断面寸法は40 Upper frame, lower frame, the cross-sectional dimensions of the studs 40
mm×90mmのツーバイフォー材を使用した。 Using the two-by-four material mm × 90mm. 次に、 next,
その外面側に防水透湿シートを貼着した。 It was stuck a waterproof breathable sheet on its outer surface side. 続いて、木質積層材からなる通気用受材を長さ65mmの釘(CN− Subsequently, length 65mm nail the ventilation receiving material consisting of wood laminate (CN @ -
65)で、上枠、下枠、スタッドの上に釘打ちピッチ2 65), the upper frame, lower frame, nailing pitch over the stud 2
00mmとして釘着し、その上に長さ50mmの釘(C And nails applied as a 300 mm, nail length 50mm thereon (C
N−50)で釘打ちピッチ100mmで外壁パネルを張り付けた。 Pasted outer wall panel nailing pitch 100mm in N-50). 通気用受材の寸法は厚さ7.0mm、幅寸法は、スタッドを二本重ねとした箇所は80mm、スタッド一本の箇所は40mmとした。 Dimensions thickness 7.0 mm, width of ventilation image receiving material has portions where the stud with two overlapped 80 mm, sites of one stud was 40 mm. 長さはそれぞれ273 Each of the length 273
0mmとした。 It was 0mm. 外壁パネルは当社製の軽量モルタル層複合合板「商品名:ラストップ15」を使用した。 Outer wall panel Our made of lightweight mortar layer composite plywood "product name: Las Top 15" was used. サイズは厚さ15mm、縦2730mm、横幅910mmを幅方向に二枚並べて使用した。 Size thickness 15 mm, vertical 2730Mm, were used side by side two lateral width 910mm in the width direction. ラストップの軽量モルタル層は7.0mmで合板層は厚さ7.5mmの構造用合板とした。 Lightweight mortar layer Las top plywood layer at 7.0mm was structural plywood with a thickness of 7.5mm. 通気用受材に使用した木質積層材は、フェノール樹脂接着剤使用の構造用合板を採用した。 Wood laminated material used in the ventilation receiving material adopts the structural plywood phenolic resin adhesive used. 各単板の繊維方向は互いに直交させたものである。 Fiber direction of each single plate is obtained by mutually orthogonal. 単板樹種としてはラワン材を使用し、単板厚さは1.0mmとした。 The veneer species using lauan, veneer thickness was 1.0 mm. 積層プライ数は7プライ等厚とし、仕上がり厚さを7.0 The number of laminate plies is set to such thickness 7-ply, the finished thickness 7.0
mmとした。 It was mm. 日本農林規格の構造用合板規格に適合するものとした。 And it shall conform to the structure for plywood standard of the Japan Agricultural Standards.

【0034 】〔実施例2〕通気用受材に使用する木質積層材として、単板厚さを2.8mmとし、単板厚さ構成を11プライの等厚とし、通気用受材の仕上がり厚さを30mmとしたことの他は実施例1と同様にして実施例2の枠組壁工法の外壁構造体を作製した。 [0034] As Example 2 wood laminate for use in ventilation receiving material, and 2.8mm of the veneer thickness, veneer and the thickness structure of 11 plies equal thickness, finished thickness ducting receiving material other possible was 30mm was prepared an outer wall structure of the wood frame construction example 2 in the same manner as in example 1 of.

【0035 】〔実施例3〕通気用受材に使用する木質積層材として、単板厚さを1.0mmとし、各単板の繊維方向は表面から二層目の単板及び裏面から二層目の単板を直交単板としその他の単板は互いに平行にして7プライ等厚の単板構成で積層接着した仕上がり厚さ7.0 [0035] As Example 3 wood laminate for use in ventilation receiving material, the veneer thickness and 1.0 mm, two layers of veneer and the rear surface of the second layer from the fiber direction surface of each veneer eye veneer orthogonal veneer and to other veneer finished thickness was laminated and adhered in parallel to 7 ply such veneer structure thickness mutually 7.0
mmの特殊な平行合板を用いたことの他は実施例1と同様にして実施例3の枠組壁工法の外壁構造体を作製した。 Another possible using a special parallel plywood mm was prepared an outer wall structure of wood frame construction of Example 3 in the same manner as in Example 1.

【0036 】〔実施例4〕通気用受材に使用する木質積層材として、単板厚さを2.8mmとし、各単板の繊維方向は表面から二層目の単板及び裏面から二層目の単板を直交単板としその他の単板は互いに平行にして11 [0036] As Example 4 wood laminate for use in ventilation receiving material, the veneer thickness and 2.8 mm, two layers of veneer and the rear surface of the second layer from the fiber direction surface of each veneer eyes veneer and perpendicular veneer in the other single plate parallel to each other 11
プライ等厚の単板構成で積層接着した仕上がり厚さ3 Finished thickness was laminated and adhered with a single-plate configuration of the ply, such as thickness 3
0.0mmの特殊な平行合板を用いたことの他は実施例1と同様にして実施例4の枠組壁工法の外壁構造体を作製した。 Another possible using a special parallel plywood 0.0mm was prepared an outer wall structure of wood frame construction of Example 4 in the same manner as in Example 1.

【0037 】〔比較例1〕枠組壁工法の外壁構造体の上枠、下枠、縦枠(スタッド)の上に、5プライ9.0 The upper frame of Comparative Example 1 the outer wall structure of wood frame construction, on the lower frame, the vertical frame (studs), 5 ply 9.0
mm厚さで幅910mm、長さ2730mmの構造用合板を幅方向に二枚並べて張り付けた。 Width mm thickness 910 mm, was stuck side by side two structural plywood length 2730mm in width. その上に防水透湿シートを貼着し、続いてその上に厚さ18mmのムク材からなる通気用受材を取り付けたことの他は実施例1と同様にして比較例1の外壁構造体を作製した。 And adhering a waterproof breathable sheet thereon, followed by an outer wall structure of the other in the same manner as in Example 1 Comparative Example 1 that was equipped with a vent receiving material consisting of solid wood with a thickness of 18mm thereon It was produced.

【0038 】〔比較例2〕通気用受材として、ムク材からなる厚さ18mmの通気用受材を使用したことの他は実施例1と同様にして比較例2の枠組壁工法の外壁構造体を作製した。 [0038] Comparative Example 2 as a ventilation image receiving material, the outer wall structure of wood frame construction other things using ventilation receiving material thickness 18mm made of solid wood Example 1 in the same manner as in Comparative Example 2 to produce a body.

【0039 】〔壁耐力試験〕上記実施例1〜4及び比較例1、2の外壁構造体をホールダウン金物で試験台に固定し、面内剪断試験を実施し壁倍率を比較した。 [0039] The [walls proof test] outer wall structure of the above Examples 1 to 4 and Comparative Examples 1 and 2 was fixed to a test stand with hold-down hardware, were compared walls magnification conducted plane shear test. 試験の方法は無載荷式で、上部の上枠部側面から、正負交番繰り返し加力とし、見かけの剪断変形角1/450、1 The method of testing a non-loading type, the upper frame portion side of the upper, and positive and negative Cyclic Loading, apparent shear angle 1 / 450,1
/300、1/200、1/150、1/100、1/ / 300,1 / 200,1 / 150, / 100, /
75、1/50ラジアンの正負変形時に、同一サイクルで三回繰り返し加力を行った後、単調加力で破壊させ、 75,1 / 50 radians at the time of positive and negative deformation of, after the three times repeated the force in the same cycle, was destroyed in the monotonous the force,
最大荷重に達した後、試験体の変形角が1/30ラジアン以上に達するまで加力した。 After reaching the maximum load, deformation angle of the test body is the force to reach more than 1/30 radians. 試験値より短期許容剪断力の算出を行い、見かけの壁倍率を算出したものである。 It performs calculation of short-term permissible shear force than the test value is obtained by calculating the wall factor apparent.

【0040 】〔試験結果〕試験の結果(壁倍率)を表1に示す。 [0040] [Test Results] test results (wall magnification) shown in Table 1.

【表1】 [Table 1]

【0041 】 [0041]

【発明の効果】以上のように本発明に係る外壁構造によれば、壁体内の水蒸気放出速度を大きくして結露防止効果を向上させ、しかも強度に優れ、室内側の気密性を保持し、更にコストの低減を図った外壁構造を提供することができる。 According to the external wall structure according to the present invention as described above, according to the present invention, to improve the anti-condensation effect by increasing the steam release rate wall body, moreover excellent in strength, it holds the indoor side of the air-tightness, Furthermore it is possible to provide an outer wall structure thereby reducing the cost.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】本発明の外壁構造の一実施の形態を示す一部切欠正面図である。 1 is a partially cutaway front view showing one embodiment of the outer wall structure of the present invention.

【図2】図1のA−A線断面図である。 2 is a sectional view along line A-A of FIG.

【図3】従来例の枠組壁工法における通気構法用外壁構造を示す断面図である。 3 is a cross-sectional view showing an outer wall structure for venting construction method in a conventional example of a wood frame construction.

【符号の説明】 DESCRIPTION OF SYMBOLS

1 外壁構造体 2 枠組壁 3 防水透湿シート 4 縦枠(スタッド) 5、10 通気用受材 6、11、13 釘 7、8 端根太 9 土台 12 外壁パネル 14 通気路 15 上枠 16 下枠 17 頭つなぎ 18 基礎 19 断熱材 51 枠組壁 52 縦枠(スタッド) 53 下地板 54 防水透湿シート 55 通気用受材 56 外壁パネル 57 通気路 1 the outer wall structure 2 framed wall 3 waterproof breathable sheet 4 vertical frame (studs) 5,10 ducting receiving material 6,11,13 nail 7,8 end joists 9 base 12 outer side wall panels 14 ventilation channel 15 upper frame 16 lower frame 17 animals joint 18 basic 19 heat insulating material 51 framed wall 52 vertical frame (stud) 53 base plate 54 for waterproof breathable sheet 55 breathable receiving material 56 the outer wall panel 57 ventilation channel

───────────────────────────────────────────────────── フロントページの続き Fターム(参考) 2E001 DB02 EA08 FA04 GA12 GA24 GA48 GA63 HC02 HF01 NA07 NB05 NC01 ND12 2E002 EA01 EA02 EB12 FA03 FB07 FB16 HB01 JA01 JA02 JB01 MA27 NA04 ────────────────────────────────────────────────── ─── front page of continued F-term (reference) 2E001 DB02 EA08 FA04 GA12 GA24 GA48 GA63 HC02 HF01 NA07 NB05 NC01 ND12 2E002 EA01 EA02 EB12 FA03 FB07 FB16 HB01 JA01 JA02 JB01 MA27 NA04

Claims (5)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 通気構法を施した枠組壁工法による外壁構造であって、 前記枠組壁の外側に防水透湿シートが張り付けられ、該防水透湿シートの上から前記枠組壁の縦枠に、木質単板を積層接着して得られた木質積層材からなる所定の大きさの通気用受材が取り付けられ、該通気用受材の上に外壁パネルが張り付けられて、該外壁パネルと前記防水透湿シートとの間に通気路が設けられてなることを特徴とする外壁構造。 1. A external wall structure according to wood frame construction subjected to aeration construction method, the framework wall outer waterproof breathable sheet is affixed to the, to the vertical frame of the framed wall over the waterproof moisture-permeable sheet, wood ventilation receiving material of veneer lamination adhesive and a predetermined size formed of the obtained wood laminate is attached, and an outer wall panel affixed onto the receiving material for air vent, the waterproof and outer wall panels the outer wall structure, characterized in that the vent passage is provided between the moisture permeable sheet.
  2. 【請求項2】 請求項1に記載の外壁構造において、 前記木質積層材が前記木質単板の繊維方向を互いに直交させて複数枚積層接着した合板であることを特徴とする外壁構造。 2. An external wall structure according to claim 1, wherein the outer wall structure, characterized in that wood laminate is plywood said wood veneer is orthogonal to the fiber direction of laminating a plurality adhesion.
  3. 【請求項3】 請求項1に記載の外壁構造において、 前記木質積層材が前記木質単板の繊維方向を互いに平行させて複数枚積層接着した平行合板で、該平行合板を構成する木質単板のうち、少なくとも一枚が前記木質単板の繊維方向を他の木質単板層と直交させた平行合板であることを特徴とする外壁構造。 3. A external wall structure according to claim 1, wherein the parallel plywood wood laminated material is the wood veneer is parallel to the fiber direction of laminating a plurality adhesive, wood veneer constituting the the parallel plywood of the outer wall structure, characterized in that the parallel plate in which at least one has a fiber direction of the wood veneer is orthogonal to the other wood veneer layer.
  4. 【請求項4】 請求項2又は3に記載の外壁構造において、 前記木質積層材の厚さが7〜30mmであることを特徴とする外壁構造。 4. A external wall structure according to claim 2 or 3, the outer wall structure thickness of the wood laminate is characterized in that it is a 7~30Mm.
  5. 【請求項5】 請求項1ないし請求項4いずれか記載の外壁構造において、 前記枠組壁に所定間隔を開けて設けられている縦枠のなかの一部又は全部の縦枠が複数本並設して構成され、該複数本並設して構成された各縦枠を跨ぐように前記通気用受材が取り付けられ、前記外壁パネルはその接合部が前記通気用受材の幅の範囲内に位置するように張り付けられていることを特徴とする外壁構造。 5. outer wall structure according to any one of claims 1 to 4, the vertical frame a plurality Hon'nami setting of some or all of among the vertical frame which is provided at a predetermined interval in the framework wall and is constituted by, it attached the ventilation receiving material so as to straddle the respective vertical frame which is constituted by said plurality of Hon'nami set, said outer wall panel is in the range that the junction of the width of the venting receiving material the outer wall structure, characterized in that it is affixed so as to be located.
JP2001172325A 2001-06-07 2001-06-07 Outer wall structure Pending JP2002364091A (en)