JP2002338912A - Rolled material of pressure-sensitive adhesive tape - Google Patents

Rolled material of pressure-sensitive adhesive tape

Info

Publication number
JP2002338912A
JP2002338912A JP2001151321A JP2001151321A JP2002338912A JP 2002338912 A JP2002338912 A JP 2002338912A JP 2001151321 A JP2001151321 A JP 2001151321A JP 2001151321 A JP2001151321 A JP 2001151321A JP 2002338912 A JP2002338912 A JP 2002338912A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
pressure
sensitive adhesive
adhesive tape
substrate
material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2001151321A
Other languages
Japanese (ja)
Inventor
Hiroyasu Iizuka
裕保 飯塚
Original Assignee
Sekisui Chem Co Ltd
積水化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To provide a rolled material of a pressure-sensitive adhesive tape, which can be stably produced without the necessity for complicated control in the industrial production and is suitable for applications where air permeability is required. SOLUTION: This rolled material of a pressure-sensitive adhesive tape comprises a material made by laminating a pressure-sensitive adhesive layer on one side of a base material having fine voids and an interlaminar strength of 1.9 N/cm<2> or higher. The material has no permeability in a state before being rolled into a roll, and reveals permeability only when it is unrolled and the pressure-sensitive adhesive layer is peeled for use.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、粘着テープの巻物状体に関し、より詳しくは医療、服飾、食品等の分野において通気性を必要とする用途に用いられる粘着テープの巻物状体に関する。 BACKGROUND OF THE INVENTION The present invention relates to a scroll-like body of the adhesive tape, and more particularly medical, apparel, relates scroll-like body of the adhesive tape used in applications requiring breathability in the field of foods.

【0002】 [0002]

【従来の技術】基材と粘着剤層とからなる通気性粘着テープは、基材が通気性を有し且つ粘着剤層が通気性を有することによって粘着テープ全体の通気性を確保することができる。 Breathable adhesive tape consisting of a Related Art substrate and the pressure-sensitive adhesive layer may be the substrate and the adhesive layer has a permeability to ensure ventilation of the entire adhesive tape by having air permeability it can. 従来、基材の通気性は、例えば、不織布、 Traditionally, breathable substrate, for example, a nonwoven fabric,
布、ガーゼ等の空隙を有する基材を用いることで確保されたが、粘着剤層の通気性を確保するために様々な提案がなされてきた。 Fabric, has been secured by using a substrate having voids gauze, various proposals have been made in order to ensure proper ventilation of the pressure-sensitive adhesive layer.

【0003】例えば、特開昭49−97058号公報には、粘着剤に液泡や気泡を微小分散させて基材に塗布する際に、塗布厚みを制御することにより乾燥後の粘着剤皮膜に亀裂等を生じさせる粘着テープの製造方法が開示されている。 [0003] For example, JP-A-49-97058, when applying a liquid foam and bubbles on the substrate by fine dispersed in the adhesive, a crack in the pressure-sensitive adhesive film after drying by controlling the coating thickness method of producing a pressure-sensitive adhesive tape to produce discloses the like. しかし、上記の方法では通気性は得られるものの、製造時に液泡や気泡を均一に微小分散させることが難しく、制御が極めて難しいという問題があった。 However, in the above method but breathable obtained uniformly it is difficult to minutely dispersed liquid bubbles and air bubbles at the time of manufacture, control is disadvantageously extremely difficult.

【0004】また、水及び親水性物質を粘着剤に強制的に分散して粘着剤層に欠陥を生じさせたり、加熱発泡で通気孔を開ける手法もあるが、粘着剤には、通常、性能向上のためイソシアネート系架橋剤を添加することが一般的であり、この場合イソシアネート系架橋剤が水との反応により消費されてしまうという問題があった。 [0004] or cause defects in the adhesive layer of water and a hydrophilic substance forcibly dispersed in the adhesive, there is a method of opening a vent hole in the heat-foamable, the adhesive, normally, the performance adding the isocyanate crosslinking agent to improve are common, isocyanate crosslinking agents in this case there is a problem that is consumed by reaction with water.

【0005】上記問題を改善する方法として、例えは、 [0005] As a method for improving the above-mentioned problem, for example,
特開平2−296881号公報には、水と疎水性無機微粒子が分散された感圧接着剤と多官能性イソシアネート化合物が含有された有機溶媒系分散液を塗布して加熱乾燥して通気性を得る方法が開示されている。 JP-A-2-296881, water and hydrophobic inorganic fine particles are dispersed the pressure sensitive adhesive with a polyfunctional isocyanate compound an organic solvent-based dispersions containing to take dried by heating by applying a breathable the method of obtaining is disclosed.

【0006】 [0006]

【発明が解決しようとする課題】しかしながら、本発明者の検討によれば、上記の方法においても、工業生産時においては、イソシアネート系架橋剤の添加量と疎水性無機微粒子分散物の配合比率及び均一分散性の制御が難しく、安定した生産が困難という問題があった。 [0007] However, according to the study by the present inventors, even in the above method, during industrial production, mixing ratio of the added amount and the hydrophobic inorganic fine particle dispersion of the isocyanate-based crosslinking agent and it is difficult to control the uniform dispersibility, there is a stable production problem difficult. また、 Also,
従来の考え方は、いずれも製造時において通気性を発現させるものであり、製造時には通気性を有さず、使用時に初めて通気性を発現させるという発想はなかった。 Conventional thinking are both used in order to exhibit air permeability during production, no breathability at the time of manufacture, there was no first idea to express breathability in use.

【0007】上記に鑑み、本発明の目的は、使用時に初めて通気性を発現させるという発想にたち、特に複雑な制御を必要とせずに工業的生産が可能な、通気性用途に適した粘着テープの巻物状体を提供することにある。 [0007] In view of the above, an object of the present invention, stood the first idea to express breathability in use, capable of industrial production without requiring particularly complex control, the pressure-sensitive adhesive tape suitable for ventilation purposes and to provide a scroll-like body.

【0008】 [0008]

【課題を解決するための手段】請求項1記載の粘着テープの巻物状体は、微細な空隙を有し、層間強度が1.9 Scroll-like body of the pressure-sensitive adhesive tape SUMMARY OF THE INVENTION The first aspect has a fine voids, the interlayer strength is 1.9
N/cm 2以上の基材の片面に、粘着層が積層されてなる粘着テープの巻物状体であって、巻き取られて巻物状になされる前の状態では通気性を有さず、巻きほぐして粘着層を基材から剥がして使用する際に初めて通気性を発現するようになされていることを特徴とする。 On one side of N / cm 2 or more substrates, a roll-like body of the pressure-sensitive adhesive tape adhesive layer are laminated, has no breathability in a state before made wound into a roll form, the winding that it has been made to express the first breathable when using peeling the adhesive layer from the substrate to loosen characterized.

【0009】以下、本発明を詳細に説明する。 [0009] In the following, the present invention will be described in detail. 本発明に用いられる基材としては、微細な空隙を有するものが用いられる。 The substrate used in the present invention, is used which has a fine voids. 空隙については特に限定されないが、本発明の効果をより確実にするためには、空隙の孔径は10〜 No particular limitation is imposed on the air gap, in order to secure the effect of the present invention, voids having a pore size of 10 to
50μmのものが好ましい。 It is preferable of 50μm. 上記基材の材料としては、 As the material of the substrate,
特に限定されず、例えば、和紙、不織布、布等の繊維で構成される材料等が挙げられ好ましく用いられるが、これ等に限らず、その他の材料として、穿孔されたフィルム或いは各種網目状の材料等を用いてもよい。 Is not particularly limited, for example, Japanese paper, nonwoven fabric, although fiber composed materials such as cloth are preferably used include, not limited thereto, etc., as other materials, perforated films or various mesh material or the like may be used. 上記基材の層間強度は、巻きほぐして粘着層を基材から剥がして使用する際の通気性を発現させるため、1.9N/cm Since the interlayer strength of the base material, to express permeability when used by peeling from the substrate an adhesive layer and unwinding, 1.9 N / cm
2以上とされる。 It is 2 or more. 尚、層間強度とは、基材の上面と下面を垂直方向(基材の厚み方向)に対して引張り応力をかけ、基材を破壊(層間破壊)させた場合の破壊に到るまでの最大強度とする。 The maximum of the interlayer strength, stressed tensile upper and lower surfaces of the substrate with respect to the vertical direction (thickness direction of the substrate), up to the breakdown of when to break a substrate (substrate failure) and strength.

【0010】上記層間強度が1.9N/cm 2に満たない場合は、巻きほぐして使用する際に基材が垂直方向(基材の厚み方向)に裂けて(層間破壊)しまうことが有る。 [0010] The bond strength is If less than 1.9 N / cm 2, it substrate when used by unwinding is torn in a vertical direction (thickness direction of the substrate) (substrate failure) there. 層間強度の上限は特に認められないが、高すぎる場合はテープの柔軟性が悪化するので注意を要する。 Although not observed in particular upper limit of the interlaminar strength is, if it is too high, take a note that the flexibility of the tape is deteriorated.

【0011】本発明における粘着層を構成する粘着剤としては、特に限定されず、例えば、ゴム系、アクリル系、シリコーン系等の粘着剤が挙げられる。 [0011] As the adhesive constituting the adhesive layer in the present invention is not particularly limited, for example, rubber-based, acrylic, and a pressure-sensitive adhesive silicone or the like. また、これ等の粘着剤の分散形態としては、例えば、溶剤溶解型、 As the dispersed form of the pressure-sensitive adhesive of this such, for example, a solvent soluble type,
エマルジョン型、ホットメルト型等が挙げられる。 Emulsion type, hot melt type, and the like. 上記粘着剤には、性能向上のためイソシアネート系架橋剤が添加されたものであってもよい。 The pressure-sensitive adhesive may be one isocyanate crosslinking agent to improve performance was added.

【0012】上記粘着剤の塗工方法としては、特に限定されず、直塗り、剥離紙を介しての転写塗工等が適宜用いられる。 [0012] As a coating method of the adhesive is not particularly limited, a straight-coating, transfer coating, etc. through the release paper may be appropriately used. また、特殊な塗工設備等は不要であり、通常一般に用いられる、例えば、ロールコーター、マイヤーバー、フラットバー、ホットメルトによるリップコーター、グラビヤ、カレンダー等が必要に応じて選択され用いられる。 Also, special coating facilities is not necessary, commonly used in general, for example, a roll coater, a Mayer bar, flat bar, hot-melt by a lip coater, gravure, used are selected as needed calendar like.

【0013】本発明の巻物状体の製造方法としては、特に限定されず、例えば、層間強度が1.9N/cm 2以上であり微細な空隙を有する基材の片面に、イソシアネート系架橋剤が添加された粘着剤を、剥離紙に塗布、乾燥した後、これを上記基材の片面に貼り合わせ、剥離紙付きの巻物を製造し、次に、上記巻物の剥離紙を剥ぎ取りながら巻き戻しを行い、巻き取られたロール状の巻物を所定の幅に切断することにより粘着テープの巻物状体を得ることができる。 [0013] As a method for producing a scroll-shaped body of the present invention is not particularly limited, for example, interlaminar strength is on one side of the substrate having fine voids is at 1.9 N / cm 2 or more, isocyanate crosslinking agent an added adhesive, coated on release paper, dried, which adhered to one surface of the substrate, to produce a roll with a release paper, then rewound while we strip the release paper of the roll was carried out, it is possible to obtain a roll-shaped body of the pressure-sensitive adhesive tape by cutting the wound roll-shaped scroll to the predetermined width. 上記の方法は、各工程を個別に行うこともできるし、連続的に行うこともできる。 The above method can either be carried out each step separately, it is also carried out continuously. また、 Also,
上記により得られる粘着テープの巻物状体が巻きほぐして使用する際に通気性が発現しやすいように、粘着層の厚みは40μm以下であることが好ましい。 As breathability is easily expressed when used in unwinding roll-shaped body of the pressure-sensitive adhesive tape obtained by above, it is preferable that the thickness of the adhesive layer is 40μm or less. また、剥離紙付きの巻物の状態で50℃以上の加熱養生を行うとより効果的である。 Further, it is more effective to perform heating curing over 50 ° C. while scrolls with release paper.

【0014】(作用)本発明の粘着テープの巻物状体が、巻きほぐして粘着層を基材から剥がして使用する際に、通気性を発現し得る詳細な機構は未だ十分には明らかではないが、次のように考えられる。 [0014] (Operation) scroll-shaped body of the pressure-sensitive adhesive tape of the present invention, when used by peeling from the substrate an adhesive layer and unwinding, detailed mechanisms capable of expressing the air permeability is not clear to yet fully but it is considered as follows. すなわち、層間強度が1.9N/cm 2以上であり微細な空隙を有する基材の片面に、粘着層を積層形成し、巻き取られて製造するので、巻きほぐして使用する際に、基材に浸透していた粘着剤が部分的に粘着層から引き出され、基材の層間強度と引張り応力とのバランスにより、粘着層に極めて微少な孔(通気性発現上良い意味での亀裂欠点)が生じ通気性を発現するものと推定される。 That is, on one side of the substrate bond strength is having a and fine voids 1.9 N / cm 2 or more, the adhesive layer was laminated so prepared wound, when used with unwinding, the substrate adhesive had penetrated is drawn from partially adhesive layer, the balance between the tensile stress and the interlaminar strength of the base material, extremely fine pores in the adhesive layer (crack defect on good sense breathability expression) is occurs is estimated to express breathability.

【0015】 [0015]

【実施例】以下に実施例及び比較例を示すことにより、 EXAMPLE by showing Examples and Comparative Examples below,
本発明を具体的に説明する。 Specifically describe the present invention. 尚、本発明は下記実施例のみに限定されるものではない。 The present invention is not limited to the following examples.

【0016】(実施例1) 1. [0016] (Example 1). 基材 層間強度1.96N/cm 2のパルプを主体とした不織布[空隙率60面積%、坪量38g/m 2 ] 2. Nonwoven fabric mainly composed of pulp substrate interlaminar strength 1.96 N / cm 2 [porosity 60 area%, a basis weight of 38g / m 2] 2. 粘着剤 組成:BA/2EHA/AAc=40/57/3(重量比)の共重合体 (但し、BAはブチルアクリレート、2EHAは2−エチルヘキシルアクリレート、AAcはアクリル酸を示す。) 濃度:固形分40% 3. PSA composition: BA / 2EHA / AAc = 40/57/3 copolymer (weight ratio) (where, BA is butyl acrylate, 2EHA 2-ethylhexyl acrylate, AAc denotes acrylic acid.) Concentration: solids 40% 3. 架橋剤 イソシアネート系架橋剤(日本ポリウレタン社製、商品名「コロネートL28」) 添加量:液重量比で、粘着剤/架橋剤=100/2 Crosslinking agent isocyanate crosslinking agent (manufactured by Nippon Polyurethane Co., Ltd., trade name "Coronate L28") added to the amount of: a liquid weight ratio, the pressure-sensitive adhesive / cross-linking agent = 100/2

【0017】4. [0017] 4. 粘着テープの巻物状体の作製 上記架橋剤を配合した粘着剤を剥離紙に固形分が30g Solids adhesive compounded with produced the crosslinking agent of the scroll-shaped body of adhesive tape release paper 30g
/m 2となるように塗布し、乾燥した。 / M 2 and composed manner was coated and dried. 上記基材と貼り合わせて、剥離紙付きの巻物を作製した。 Bonded with the substrate, to produce a roll with a release paper. ここで得られた巻物について、下記評価のため剥離紙付きのシートサンプルAを切断採取した。 The scroll obtained here was cut taken sheet sample A with release paper for the following evaluation. 次に、上記巻物の剥離紙を剥ぎ取りながら巻き戻しを行った。 Next, we rewind while we strip the release paper of the roll. この時巻き戻しの巻き硬さが均一となるように、巻き戻し時の張力は9.8N As the winding hardness of the time rewinding is uniform, tension during rewinding 9.8N
/cm 2とした。 / Was cm 2. 上記により巻き取られて得られたロールの巻物を切断し、粘着テープの巻物状体(テープ幅2 Cutting the roll of scrolls obtained is wound by the pressure-sensitive adhesive tape of the roll-like body (tape width 2
5mm)を作製した。 To prepare a 5mm). その後架橋反応が安定するまで十分に養生した。 Then the cross-linking reaction is sufficiently cured to stabilize. 得られた粘着テープの巻物状体(テープ幅25mm)を、使用する状態で巻きほぐして粘着層を基材から剥がし通気性を発現させ、以下の評価における通気性粘着テープのサンプルBとした。 Scroll-shaped body of the resulting adhesive tape (tape width 25 mm), and unwound in a state to be used to express a peeling breathable adhesive layer from the substrate, and a sample B of breathable pressure-sensitive adhesive tape in the following evaluation.

【0018】4. [0018] 4. 評価 上記により得られたサンプルについて、以下の評価を行った。 The samples obtained by the evaluation described above were evaluated as follows. (1)通気性(透気度) 上記シートサンプルAから剥離紙を剥ぎ取ったサンプルCと、上記通気性テープBについて、ガーレ式デンソメーターにて、300mlの空気が試料を通過するのに要する時間(秒/cm 2 )を計測した。 (1) and the sample C was peeled release paper from breathable (air permeability) The sheet sample A, for the breathable tape B, necessary for Gurley densometer, to air 300ml is passing through the sample It was measured the amount of time (in seconds / cm 2). (2)テープ展開力 上記粘着テープ(テープ幅25mm)を使用する状態で巻きほぐして粘着層を基材から剥がし(速度30m/ (2) unwound in a state of using tape deployment force the adhesive tape (tape width 25 mm) is peeled off the adhesive layer from the substrate (speed 30 m /
分)、展開するのに要する力を計測した。 Minute), was measured the force required to deploy. (3)層割れ 上記粘着テープ(テープ幅25mm)を使用する状態で巻きほぐす際に、粘着層の層割れの有無を目視により確認した。 (3) when loosening wound in a state that use delamination the adhesive tape (tape width 25 mm), was visually confirmed whether the delamination of the adhesive layer.

【0019】(実施例2)基材として層間強度3.92 [0019] (Example 2) bond strength 3.92 as a base material
N/cm 2のパルプを主体とした不織布[空隙率60面積%、坪量38g/m 2 ]を用いたこと以外は実施例1 N / cm 2 of pulp as a main component nonwoven [porosity 60 area%, a basis weight of 38 g / m 2], except for using Example 1
と全く同様にしてシートサンプル及び通気性粘着テープサンプルを作製し同様の評価を行った。 When conducted prepared the same evaluation Sheet samples and breathable adhesive tape samples in the same manner.

【0020】(比較例1)基材として層間強度1.47 The bond strength (Comparative Example 1) substrate 1.47
N/cm 2のパルプを主体とした不織布[空隙率60面積%、坪量38g/m 2 ]を用いたこと以外は実施例1 N / cm 2 of pulp as a main component nonwoven [porosity 60 area%, a basis weight of 38 g / m 2], except for using Example 1
と全く同様にしてシートサンプル及び通気性粘着テープサンプルを作製し同様の評価を行った。 When conducted prepared the same evaluation Sheet samples and breathable adhesive tape samples in the same manner. 上記の評価結果は表1に示すとおりであった。 The above evaluation results were as shown in Table 1.

【0021】 [0021]

【表1】 [Table 1] 表1から明らかなように、本発明における実施例においては、通気性テープとしての透気度が優れているとともに、耐層割れについても優れていることが判明した。 As evident from Table 1, in Examples of the present invention, together with its excellent air permeability as breathable tape was found to be excellent also 耐層 cracking.

【0022】 [0022]

【発明の効果】本発明の粘着テープの巻物状体は、微細な空隙を有し、特定の層間強度を有する基材の片面に粘着層が積層され巻き取られて巻物状体になされているので、巻きほぐして粘着層を基材から剥がして使用する際に、粘着層に通気性が発現し、粘着テープとしての通気性を発現し得るものである。 Scroll-shaped body of the pressure-sensitive adhesive tape of the present invention according to the present invention has fine voids, the adhesive layer on one surface of a substrate having a specific bond strength have been made in the scroll-like body is wound laminated since, when using peeling the adhesive layer by unwinding from the substrate, in which breathable adhesive layer is expressed and capable of expressing the air permeability as a pressure-sensitive adhesive tape. 上記粘着テープの巻物状体においては、上記従来技術の如き複雑な制御は、必要とせず、工業的生産が可能であり、しかも使用時には優れた通気性を発現するのである。 In scroll-like body of the adhesive tape, the prior art such as complicated control is not required, but may be industrial production, yet it is to express the excellent breathability in use.

Claims (1)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 微細な空隙を有し、層間強度が1.9N 1. A has minute voids, interlaminar strength is 1.9N
    /cm 2以上の基材の片面に、粘着層が積層されてなる粘着テープの巻物状体であって、巻き取られて巻物状になされる前の状態では通気性を有さず、巻きほぐして粘着層を基材から剥がして使用する際に初めて通気性を発現するようになされていることを特徴とする粘着テープの巻物状体。 On one side of the / cm 2 or more substrates, a roll-like body of the pressure-sensitive adhesive tape adhesive layer are laminated, it has no breathability in a state before made wound into a roll shape, unwound scroll-like body of the adhesive tape, characterized in that have been made to express the first breathable when using peeling the adhesive layer from the substrate Te.
JP2001151321A 2001-05-21 2001-05-21 Rolled material of pressure-sensitive adhesive tape Pending JP2002338912A (en)