JP2002307874A - Card, manufacturing method for card, and manufacturing device therefor - Google Patents
Card, manufacturing method for card, and manufacturing device thereforInfo
- Publication number
- JP2002307874A JP2002307874A JP2001111789A JP2001111789A JP2002307874A JP 2002307874 A JP2002307874 A JP 2002307874A JP 2001111789 A JP2001111789 A JP 2001111789A JP 2001111789 A JP2001111789 A JP 2001111789A JP 2002307874 A JP2002307874 A JP 2002307874A
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- card
- over
- receiving layer
- laminated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明はインクジェット方式
により表示部が形成されるカード、カード製造方法及び
カード製造装置に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a card having a display section formed by an ink jet method, a card manufacturing method, and a card manufacturing apparatus.
【0002】[0002]
【従来の技術】従来、量産される磁気カードなどの用途
においては、カード部材であるコアシートにオフセット
印刷などで所定の画像、デザイン、約款、ロゴなどを印
刷し、大量生産に対応してきたが、少量多品種への対応
には不向きであった。近年、社員証、会員証などの識別
カードに見られるように、使用者の顔写真や名前をカー
ド個別に印刷することが要求されるに至って、従来の印
刷方法では、いたずらにロスが増えるばかりで製造原価
が上昇し、殆ど対応不可能となった。現在、これを解決
するために、カードに固有情報を印刷する手法としてカ
ード上に顔写真などを昇華転写方式にてオンデマンド印
刷する手法がとられている。昇華転写方式は諧調再現性
には優れているが、イエロー・マゼンタ・シアン・ブラ
ック・保護層の5色のリボンを順次使用して画像・文字
情報を付与するため、生産性が悪くなり印刷時間が2分
/カードに及ぶ場合もある。また、適正な昇華転写を実
現するためにはカードとリボンを適切に密着させてやる
必要があるため、カード表面に凹凸があると印刷ムラが
発生し易いなどの問題があった。さらに、昇華転写用の
リボンは一般に高価であるため、ランニングコストが嵩
むことも問題視されてきた。2. Description of the Related Art Conventionally, in applications such as magnetic cards to be mass-produced, predetermined images, designs, articles, logos, etc. are printed on a core sheet as a card member by offset printing or the like, so that mass production is supported. However, it was unsuitable for dealing with a small number of varieties. In recent years, as seen on identification cards such as employee ID cards and membership ID cards, it has been required to print a photograph of the user's face and name individually for each card, and the conventional printing method has increased the loss unnecessarily. As a result, the manufacturing cost has risen, making it almost impossible to respond. At present, in order to solve this problem, as a method of printing unique information on a card, a method of on-demand printing of a face photograph or the like on a card by a sublimation transfer method has been adopted. The sublimation transfer method is excellent in gradation reproducibility, but since image and text information is added by sequentially using five color ribbons of yellow, magenta, cyan, black and a protective layer, productivity deteriorates and printing time is reduced. May be as long as 2 minutes / card. In addition, in order to realize proper sublimation transfer, it is necessary to make the card and the ribbon properly adhere to each other, and there is a problem that unevenness on the card surface easily causes printing unevenness. Furthermore, since the ribbon for sublimation transfer is generally expensive, the problem that the running cost is increased has been regarded as a problem.
【0003】一方、インクジェット方式はインクをピエ
ゾ素子や加熱発泡させることで微粒子化して高速で射出
し、紙やフィルムの表面に付着させたり受容層に高速拡
散させて印刷を固定する手法であり、画質の向上に伴っ
て少量部数のポスター製作などにオンデマンド印刷とし
て近年急速に普及してきている。先にあげた昇華転写に
よるカード印刷の課題を解決するためにも、特開平8−
2090号公報、特開2000−118126号公報な
どでインクジェットプリンタを用いたカード印刷方式が
提案されているが、付着したインクが表面に露出してい
たり、インク吸収性の確保から受容層の空隙率を高める
と同時にバインダー組成にも制限があり物理的強度が出
せないインク受容層を最表面に形成しているために、充
分な耐擦性・耐水性を実現できていない。これを解決す
るために一般的には受容層の上に樹脂多孔質層を形成し
ておいて、インクジェット印刷後これを加熱により緻密
化させる手法が採られているが、該多孔質層は柔弱な高
分子ラテックスから形成されており、厚さも1〜2μm
しかないため、充分な耐擦性・耐熱性が得られていると
は言い難かった。On the other hand, the ink-jet method is a method of fixing ink by piezo elements or by heating and foaming the ink to form fine particles and eject the ink at a high speed, to attach the ink to the surface of paper or a film, or to diffuse the ink at a high speed to a receiving layer to fix the print. In recent years, on-demand printing has been rapidly widespread for producing small number of posters and the like with the improvement of image quality. To solve the above-mentioned problem of card printing by sublimation transfer, Japanese Patent Application Laid-Open
JP-A-2090 and JP-A-2000-118126 propose a card printing method using an ink-jet printer. However, the adhering ink is exposed on the surface, or the porosity of the receiving layer is increased due to the ink absorption. At the same time, the ink receiving layer, which cannot provide physical strength due to the limitation of the binder composition, is formed on the outermost surface, so that sufficient rub resistance and water resistance cannot be realized. In order to solve this, a method is generally adopted in which a resin porous layer is formed on the receiving layer, and after ink jet printing, the resin is densified by heating, but the porous layer is soft. It is formed from a high polymer latex and has a thickness of 1-2 μm.
Therefore, it was difficult to say that sufficient abrasion resistance and heat resistance were obtained.
【0004】[0004]
【発明が解決しようとする課題】本発明は、インクジェ
ット方式により、カード毎に異なる使用者の顔写真画像
を付与するなど、少量多品種生産に対する対応を可能と
しながら、従来のインクジェット受容カードの耐擦性、
耐久性、耐水性などを改善されたカードを提供するもの
である。SUMMARY OF THE INVENTION According to the present invention, it is possible to cope with high-mix low-volume production, for example, by giving a different face photograph image of a user to each card by an ink jet method, and to improve the durability of a conventional ink jet receiving card. Abrasion,
An object of the present invention is to provide a card having improved durability and water resistance.
【0005】[0005]
【課題を解決するための手段】本発明(1)は、コアシ
ートおよびオーバーラミネートシートを有するカードに
おいて、オーバーラミネートシートが透明ないし半透明
の基材であり、該基材の片面に3〜50μmのインク受
容層を有し、インク受容層にはインクジェット方式にて
記録が施され、インク受容層面がコアシート側になるよ
うにコアシートとオーバーラミネートシートが積層一体
化され、前記記録がオーバーラミネートシートを透して
視認できることを特徴とするカードである。この発明に
は、コアシートの両面にオーバーラミネートシートを有
し、両方のオーバーラミネートシートが透明ないし半透
明の基材であり、該基材の片面に3〜50μmのインク
受容層を有し、且つ、インク受容層にはインクジェット
方式にて記録が施され、インク受容層面がコアシート側
になるようにコアシートと両方のオーバーラミネートシ
ートが積層一体化され、前記記録がオーバーラミネート
シートを透してそれぞれ視認できることを特徴とするカ
ードを含む。また、両面にインクジェット記録を施した
オーバーラミネートシートを積層する構成は両面に情報
を付与することができるので特に好ましい。The present invention (1) relates to a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent substrate, and one side of the substrate has a thickness of 3 to 50 μm. Recording is performed on the ink receiving layer by an ink jet method, and a core sheet and an over laminate sheet are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording is over laminated. It is a card characterized by being visible through a sheet. In the present invention, the core sheet has over-laminated sheets on both sides, both over-laminated sheets are transparent or translucent base materials, and has an ink receiving layer of 3 to 50 μm on one side of the base material, In addition, recording is performed on the ink receiving layer by an ink jet method, the core sheet and both over laminate sheets are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording passes through the over laminate sheet. And cards that can be visually recognized. A configuration in which an over-laminated sheet on which ink jet recording is performed on both sides is laminated is particularly preferable because information can be added to both sides.
【0006】本発明(2)は、コアシートおよびオーバ
ーラミネートシートを有するカードにおいて、オーバー
ラミネートシートが透明ないし半透明の基材であり、該
基材の片面にインク受容層を有し、インク受容層にはイ
ンクジェット方式にて記録が施され、インク受容層面が
コアシート側になるようにコアシートとオーバーラミネ
ートシートが積層一体化され、前記記録がオーバーラミ
ネートシートを透して視認できるカードであって、コア
シートとオーバーラミネートシートの積層が、熱圧着に
よる積層一体化であることを特徴とするカードである。The present invention (2) relates to a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent substrate, and has an ink receiving layer on one side of the substrate. The recording is performed on the layer by an ink jet method, and a core sheet and an over laminate sheet are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording is visually recognized through the over laminate sheet. Further, the card is characterized in that the lamination of the core sheet and the overlaminate sheet is lamination integration by thermocompression bonding.
【0007】本発明(3)は、コアシートおよびオーバ
ーラミネートシートを有するカードにおいて、オーバー
ラミネートシートが透明ないし半透明の基材であり、該
基材の片面にインク受容層を有し、インク受容層にはイ
ンクジェット方式にて記録が施され、インク受容層面が
コアシート側になるようにコアシートとオーバーラミネ
ートシートが積層一体化され、前記記録がオーバーラミ
ネートシートを透して視認できるカードであって、コア
シートとオーバーラミネートシートの積層一体化が、コ
アシートとオーバーラミネートシートの間に挟みこまれ
た2〜300μmの厚さの接着剤を介しての積層一体化
であることを特徴とするカードである。接着剤としては
シート状接着剤が好ましく、特に、ポリエステル、エチ
レン酢酸ビニル共重合体、ポリアミドおよび熱可塑性ゴ
ムから選ばれる成分を主成分とするシート状接着剤が好
ましい。The present invention (3) relates to a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent substrate, the substrate having an ink receiving layer on one surface, The recording is performed on the layer by an ink jet method, and a core sheet and an over laminate sheet are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording is visually recognized through the over laminate sheet. Wherein the lamination and integration of the core sheet and the overlaminate sheet are lamination and integration via an adhesive having a thickness of 2 to 300 μm sandwiched between the core sheet and the overlaminate sheet. Card. As the adhesive, a sheet adhesive is preferable, and particularly, a sheet adhesive mainly containing a component selected from polyester, ethylene-vinyl acetate copolymer, polyamide and thermoplastic rubber is preferable.
【0008】本発明(4)は、コアシートおよびオーバ
ーラミネートシートを有するカードにおいて、オーバー
ラミネートシートが透明ないし半透明の基材であり、該
基材の片面にインク受容層を有し、インク受容層にはイ
ンクジェット方式にて記録が施され、インク受容層面が
コアシート側になるようにコアシートとオーバーラミネ
ートシートが積層一体化され、前記記録がオーバーラミ
ネートシートを透して視認できるカードであって、コア
シートが塩化ビニルを含有する樹脂フィルム、非結晶性
のポリエステルフィルム、及びABS樹脂フィルムから
選ばれる一種であることを特徴とするカードである。The present invention (4) relates to a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent substrate, and has an ink receiving layer on one side of the substrate, The recording is performed on the layer by an ink jet method, and a core sheet and an over laminate sheet are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording is visually recognized through the over laminate sheet. Wherein the core sheet is a kind selected from a resin film containing vinyl chloride, an amorphous polyester film, and an ABS resin film.
【0009】本発明(5)は、コアシートおよびオーバ
ーラミネートシートを有するカードにおいて、オーバー
ラミネートシートが透明ないし半透明の基材であり、該
基材の片面にインク受容層を有し、インク受容層にはイ
ンクジェット方式にて記録が施され、インク受容層面が
コアシート側になるようにコアシートとオーバーラミネ
ートシートが積層一体化され、前記記録がオーバーラミ
ネートシートを透して視認できるカードであって、オー
バーラミネートシートが塩化ビニルを含有する樹脂フィ
ルム、非結晶性のポリエステルフィルム、ポリカーボネ
ートフィルム、及びABS樹脂フィルムから選ばれる一
種であることを特徴とするカードである。The present invention (5) relates to a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent substrate, and has an ink receiving layer on one side of the substrate. The recording is performed on the layer by an ink jet method, and a core sheet and an over laminate sheet are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording is visually recognized through the over laminate sheet. Wherein the overlaminate sheet is a kind selected from a resin film containing vinyl chloride, an amorphous polyester film, a polycarbonate film, and an ABS resin film.
【0010】本発明(6)は、コアシートおよびオーバ
ーラミネートシートを有するカードにおいて、オーバー
ラミネートシートが透明ないし半透明の基材であり、該
基材の片面にインク受容層を有し、インク受容層にはイ
ンクジェット方式にて記録が施され、インク受容層面が
コアシート側になるようにコアシートとオーバーラミネ
ートシートが積層一体化され、前記記録がオーバーラミ
ネートシートを透して視認できるカードであって、コア
シートとオーバーラミネートシートが同種のフィルムで
あることを特徴とするカードである。[0010] The present invention (6) relates to a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent base material, and has an ink receiving layer on one surface of the base material. The recording is performed on the layer by an ink jet method, and a core sheet and an over laminate sheet are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording is visually recognized through the over laminate sheet. Wherein the core sheet and the overlaminate sheet are the same type of film.
【0011】本発明(7)は、コアシートおよびオーバ
ーラミネートシートを有するカードにおいて、コアシー
トの両面にオーバーラミネートシートが積層されてお
り、両方のオーバーラミネートシートが透明ないし半透
明の基材であり、該基材の片面にインク受容層を有し、
且つ、インク受容層にはインクジェット方式にて記録が
施され、インク受容層面がコアシート側になるようにコ
アシートと両方のオーバーラミネートシートが積層一体
化され、前記記録がオーバーラミネートシートを透して
それぞれ視認できるカードであって、両方のオーバーラ
ミネートシートが実質的に同一の厚みであることを特徴
とするカードである。The present invention (7) provides a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheets are laminated on both sides of the core sheet, and both over-laminated sheets are transparent or translucent base materials. Having an ink receiving layer on one side of the substrate,
In addition, recording is performed on the ink receiving layer by an ink jet method, the core sheet and both over laminate sheets are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording passes through the over laminate sheet. , Wherein both over-laminated sheets have substantially the same thickness.
【0012】本発明(8)は、コアシートおよびオーバ
ーラミネートシートを有するカードにおいて、コアシー
トの両面にオーバーラミネートシートが積層一体化され
ており、両方のオーバーラミネートシートが透明ないし
半透明の基材であり、該基材の片面にインク受容層を有
し、且つ、インク受容層にはインクジェット方式にて記
録が施され、インク受容層面がコアシート側になるよう
にコアシートと両方のオーバーラミネートシートが積層
一体化され、前記記録がオーバーラミネートシートを透
してそれぞれ視認できるカードであって、インク受容層
に形成された記録が片面と他面とで異なることを特徴と
するカードである。The present invention (8) provides a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is laminated and integrated on both sides of the core sheet, and both over-laminated sheets are transparent or translucent base materials. The substrate has an ink-receiving layer on one side, and the ink-receiving layer is subjected to recording by an ink-jet method, and both the core sheet and the oversheet are laminated so that the ink-receiving layer side is on the core sheet side. A card in which sheets are laminated and integrated, and the recording is visible through an over-laminated sheet, wherein the recording formed on the ink receiving layer is different on one side and the other side.
【0013】(1)〜(8)に記載のカードであって、
インク受容層が、非晶質シリカ及び/又はアルミナを有
することが好ましい。また、インク受容層が、ポリビニ
ルアルコールまたはシリル変性ポリビニルアルコールを
有することが好ましい。更に、インク受容層は、オーバ
ーラミネートシートの全域に形成する場合も、一部分の
領域に形成する場合も可能である。一部分の領域にイン
ク受容層を形成する場合は印刷方式で形成することが好
ましい。[0013] The card according to (1) to (8),
Preferably, the ink receiving layer has amorphous silica and / or alumina. Further, the ink receiving layer preferably contains polyvinyl alcohol or silyl-modified polyvinyl alcohol. Further, the ink receiving layer may be formed on the entire area of the overlaminate sheet or on a part of the area. When forming the ink receiving layer in a part of the region, it is preferable to form the ink receiving layer by a printing method.
【0014】(1)〜(8)に記載のカードであって、
オーバーラミネートシートの厚みが1.5〜250μm
であることが好ましい。また、オーバーラミネートシー
トは、コアシートと略同一の形状であってもよいし、コ
アシートよりも小さい面積の形状であってもよい。小さ
い面積の形状の場合、コアシートの一部分にオーナーラ
ミネートシートが積層されることになる。更に、コアシ
トが不透明であることが好ましい。[0014] The card according to (1) to (8),
The thickness of the over-laminated sheet is 1.5 to 250 μm
It is preferable that Further, the over-laminated sheet may have substantially the same shape as the core sheet, or may have a smaller area than the core sheet. In the case of a shape having a small area, the owner laminate sheet is laminated on a part of the core sheet. Further, it is preferable that the core site is opaque.
【0015】本発明(9)は、インクジェット方式がソ
リッドインクを使用したものである(1)〜(8)記載
のカードである。本発明(10)は、カードが非接触式
及び/又は接触式ICカードである(1)〜(9)記載
のカードである。The present invention (9) is the card according to any one of (1) to (8), wherein the ink jet system uses solid ink. The present invention (10) is the card according to any one of (1) to (9), wherein the card is a non-contact type and / or contact type IC card.
【0016】(1)〜(10)記載のカードであって、
インク受容層に形成された記録に、顔写真、氏名などの
個人情報を含むことが好ましい。また、インク受容層に
形成された記録にバーコードを含むことが好ましい。The card according to (1) to (10),
It is preferable that the record formed on the ink receiving layer contains personal information such as a face photograph and a name. Further, it is preferable that the recording formed on the ink receiving layer includes a barcode.
【0017】本発明(11)は、透明ないし半透明の基
材である連続するオーバーラミネートシートの片面に、
インク受容層を塗布乾燥して形成し、これにインクジェ
ット方式で記録を行った後、カードの大きさに切断し、
該記録を行った面とカードの大きさのコアシートが対向
して積層一体化することを特徴とするカードの製造方法
である。The present invention (11) relates to a method for manufacturing a transparent or translucent base material on one side of a continuous over-laminated sheet.
An ink receiving layer is formed by coating and drying, and after performing recording on the ink receiving layer by an ink jet method, cutting into a card size,
A card manufacturing method characterized in that a surface on which the recording is performed and a core sheet having a size of the card are laminated and integrated so as to face each other.
【0018】本発明(12)は、透明ないし半透明の基
材である連続するオーバーラミネートシートの片面に、
インク受容層を塗布乾燥して形成し、これにインクジェ
ット方式で記録を行った後、該記録を行った面と連続す
るコアシートが対向して積層一体化した後、カードの大
きさに切断することを特徴とするカードの製造方法であ
る。The present invention (12) relates to a method for manufacturing a transparent or translucent base material on one side of a continuous over-laminated sheet.
An ink receiving layer is formed by coating and drying, and after recording is performed on the ink receiving layer by an ink jet method, a continuous core sheet is opposed to the recording surface and laminated and integrated, and then cut into a card size. A method for manufacturing a card, characterized in that:
【0019】本発明(13)は、透明ないし半透明の基
材である連続するオーバーラミネートシートの片面に、
インク受容層を塗布乾燥して形成した後、カードの大き
さに切断し、これにインクジェット方式で記録を行った
後、該記録を行った面とカードの大きさのコアシートが
対向して積層一体化することを特徴とするカードの製造
方法である。The present invention (13) relates to a method for producing a transparent or translucent base material on one side of a continuous overlaminated sheet.
After the ink receiving layer is formed by coating and drying, it is cut into the size of a card, and after recording on this by an ink jet method, the recording side and the core sheet of the size of the card are laminated facing each other. A card manufacturing method characterized by being integrated.
【0020】本発明(14)は、インク受容層にインク
ジェット方式で鏡像印刷する(11)〜(13)記載の
カードの製造方法である。本発明(15)は、オーバー
ラミネートシートとコアシートの積層一体化が、熱圧着
することによる(11)〜(14)記載のカードの製造
方法である。本発明(16)は、コアシートとオーバー
ラミネートシートの間に、2〜300μmの厚さのシー
ト状接着剤を介して熱圧着する(11)〜(14)記載
のカードの製造方法である。The present invention (14) is the method for producing a card according to (11) to (13), wherein mirror image printing is performed on the ink receiving layer by an ink jet method. The present invention (15) is the method for producing a card according to any one of (11) to (14), wherein the lamination and integration of the overlaminate sheet and the core sheet are performed by thermocompression bonding. The present invention (16) is the method for producing a card according to any of (11) to (14), wherein the card is thermocompression-bonded between the core sheet and the over-laminated sheet via a sheet adhesive having a thickness of 2 to 300 μm.
【0021】(11)〜(16)記載のカードの製造方
法において、カードが非接触式及び/又は接触式ICカ
ードであることが好ましい。In the method for producing a card according to any one of (11) to (16), the card is preferably a non-contact type and / or contact type IC card.
【0022】本発明(17)は、連続するコアシートを
供給するコアシート供給手段、透明又は半透明の基材
で、その片面にインク受容層を有する連続するオーバー
ラミネートシートを供給するオーバーラミネートシート
供給手段、オーバーラミネートシートのインク受容層に
インクジェット方式により記録を行うインクジェット記
録手段、コアシートとオーバーラミネートシートのイン
ク受容層面を積層一体化する一体化手段、一体化した積
層シートをカードの大きさに切断する切断手段を有する
ことを特徴とするカードの製造装置である。The present invention (17) provides a core sheet supplying means for supplying a continuous core sheet, an over-laminated sheet for supplying a continuous over-laminated sheet having an ink receiving layer on one side of a transparent or translucent substrate. Supply means, ink jet recording means for performing recording on the ink receiving layer of the overlaminated sheet by an ink jet method, integrating means for laminating and integrating the ink receiving layer surface of the core sheet and the overlaminated sheet, and card size of the integrated laminated sheet An apparatus for manufacturing a card, comprising a cutting means for cutting into pieces.
【0023】本発明(18)は、カード状のコアシート
を供給するコアシート供給手段、透明又は半透明の基材
で、その片面にインク受容層を有する連続するオーバー
ラミネートシートを供給するオーバーラミネートシート
供給手段、オーバーラミネートシートのインク受容層に
インクジェット方式により記録を行うインクジェット記
録手段、オーバーラミネートシートをカードの大きさに
切断する切断手段、コアシートとオーバーラミネートシ
ートのインク受容層面を積層一体化する一体化手段を有
することを特徴とするカードの製造装置である。The present invention (18) is a core sheet supply means for supplying a card-shaped core sheet, an overlamination for supplying a continuous overlaminate sheet having an ink receiving layer on one surface of a transparent or translucent substrate. Sheet supply means, ink jet recording means for performing recording on the ink receiving layer of the over-laminated sheet by the ink jet method, cutting means for cutting the over-laminated sheet into a card size, lamination and integration of the core sheet and the ink-receiving layer surface of the over-laminated sheet An apparatus for manufacturing a card, comprising an integrated means for performing the above.
【0024】本発明(19)は、カード状のコアシート
を供給するコアシート供給手段、透明又は半透明の基材
で、その片面にインク受容層を有するカード状のオーバ
ーラミネートシートを供給するオーバーラミネートシー
ト供給手段、オーバーラミネートシートのインク受容層
にインクジェット方式により記録を行うインクジェット
記録手段、コアシートとオーバーラミネートシートのイ
ンク受容層面を積層一体化する一体化手段を有すること
を特徴とするカードの製造装置である。The present invention (19) provides a core sheet supply means for supplying a card-shaped core sheet, and a transparent or translucent base material for supplying a card-shaped over-laminated sheet having an ink receiving layer on one surface thereof. A card having a laminate sheet supply means, an ink jet recording means for performing recording on the ink receiving layer of the over laminate sheet by an ink jet method, and an integrating means for laminating and integrating the ink receiving layer surface of the core sheet and the over laminate sheet. Manufacturing equipment.
【0025】本発明(20)は、オーバーラミネートシ
ート供給手段とインクジェット記録手段を二つずつ有
し、コアシートの両面にオーバーラミネートシートのイ
ンク受容層面を積層一体化する一体化手段を有する(1
7)〜(19)記載のカードの製造装置である。本発明
(21)は、コアシートがその内部あるいは表面にIC
チップおよびアンテナを有する(17)〜(20)記載
のカードの製造装置である。本発明(22)は、ICチ
ップに情報を読み取り或いは書き込む為のリーダ・ライ
タ手段を有する(21)記載のカード製造装置である。The present invention (20) has two means for supplying the overlaminated sheet and two ink jet recording means, and has an integrating means for laminating and integrating the ink receiving layer surface of the overlaminated sheet on both sides of the core sheet (1).
7) A card manufacturing apparatus according to any one of 7) to (19). In the present invention (21), the core sheet has an IC inside or on its surface.
The card manufacturing apparatus according to any one of (17) to (20), further comprising a chip and an antenna. The present invention (22) is the card manufacturing apparatus according to (21), further comprising reader / writer means for reading or writing information on or from an IC chip.
【0026】[0026]
【発明の実施の形態】本発明であるカードの一例を、図
面をもって説明する。図1乃至図4は、説明する為の断
面図である。勿論、これらの図面に本発明を限定するも
のではない。図1は、オーバーラミネートシート3の片
面にインク受容層4を有し、インク受容層にはインクジ
ェット方式による記録5が施され、コアシート2と積層
一体化されたカード1である。図2は、オーバーラミネ
ートシート3の片面にインク受容層4を有し、インク受
容層にはインクジェット方式による記録5が施され、コ
アシート2と接着剤6を介して積層一体化されたカード
1である。図3は、2枚のオーバーラミネートシート
3,3’の片面にそれぞれインク受容層4,4’を有
し、そのインク受容層にはインクジェット方式による記
録5,5’が施され、コアシート2の両面に積層一体化
されたカード1である。図4は、2枚のオーバーラミネ
ートシート3,3’の片面にそれぞれインク受容層4,
4’を有し、そのインク受容層にはインクジェット方式
による記録5,5’が施され、コアシート2の両面に接
着剤層6,6’を介して積層一体化されたカード1であ
る。DESCRIPTION OF THE PREFERRED EMBODIMENTS An example of a card according to the present invention will be described with reference to the drawings. 1 to 4 are cross-sectional views for explanation. Of course, the present invention is not limited to these drawings. FIG. 1 shows a card 1 having an ink receiving layer 4 on one side of an over-laminated sheet 3, recording 5 on the ink receiving layer by an ink jet method, and being laminated and integrated with a core sheet 2. FIG. 2 shows a card 1 having an ink receiving layer 4 on one side of an over-laminated sheet 3, a recording 5 by an ink jet method being applied to the ink receiving layer, and being laminated and integrated with a core sheet 2 and an adhesive 6. It is. FIG. 3 shows two overlaminated sheets 3, 3 'each having an ink receiving layer 4, 4' on one side thereof. Is a card 1 laminated and integrated on both sides of the card 1. FIG. 4 shows the ink receiving layers 4, 4 on one side of the two over-laminated sheets 3, 3 ', respectively.
The card 1 has a 4 ', the recording 5 and 5' of the ink receiving layer is performed by the ink jet method, and the both sides of the core sheet 2 are laminated and integrated via the adhesive layers 6 and 6 '.
【0027】本発明でいうコアシートとは、磁気カード
の原紙シートや、ICカード(スマートカードともい
う)のICチップやアンテナが埋設されたシートなどで
あり、オーバーラミネートシートを積層一体化する前の
中間製品であり、各種カードに切り出す前、あるいは切
り出した後のシートである。The core sheet referred to in the present invention is a base paper sheet of a magnetic card, a sheet of an IC card (also referred to as a smart card) in which an IC chip or an antenna is embedded, and the like. This is an intermediate product before and after cutting into various cards.
【0028】非接触ICカードの場合、一般的には、ポ
リエステル、ポリイミド、ポリプロピレン、ポリエチレ
ンなどの樹脂からなる厚さ20〜100μmの絶縁性シ
ートに、次の各手法でアンテナを形成する。 ・銀や銅等のワイヤーからなるコイルを貼り付ける方法 ・予め銅やアルミニウム等の薄膜を積層しておいて、こ
れをコイル状にエッチングする方法 ・導電性インキ等を用いてコイル状に印刷する方法 このようにして形成したアンテナに、データ記憶及び/
又は演算部する各種ICチップを組み合わせ、ICカー
ドの回路基板となるインレットシートが作成される。こ
のほか、インレットシート上にコンデンサーなどを配置
することも適宜可能である。In the case of a non-contact IC card, an antenna is generally formed on an insulating sheet having a thickness of 20 to 100 μm made of a resin such as polyester, polyimide, polypropylene, or polyethylene by the following methods. -A method of attaching a coil made of a wire such as silver or copper-A method of laminating a thin film of copper or aluminum in advance and etching this into a coil shape-Printing in a coil shape using conductive ink etc. Method The data storage and / or
Alternatively, an inlet sheet serving as a circuit board of an IC card is created by combining various IC chips to be operated. In addition, a condenser or the like can be appropriately disposed on the inlet sheet.
【0029】本発明でいうコアシートは、上記のインレ
ットシートをさらに上下から塩化ビニルを含有する樹脂
フィルムや非結晶性ポリエステルフィルム、ABS樹脂
フィルム等にて挟みこんだシートをいう。インレットシ
ートと上下のフィルムは必要があればシート状接着剤で
接合することも可能である。このインレットフィルムを
上下からフィルムで挟みコアシートを形成する工程は、
本発明でコアシートとオーバーラミネートシートを熱圧
着する工程で同時に実施することが可能である。このと
き、コアシートのオーバーラミネートシート側の接合面
となる部材に予め易接着処理を実施しておくことも可能
である。The core sheet referred to in the present invention is a sheet in which the above-mentioned inlet sheet is further sandwiched from above and below by a resin film containing vinyl chloride, an amorphous polyester film, an ABS resin film and the like. If necessary, the inlet sheet and the upper and lower films can be joined with a sheet adhesive. The step of forming the core sheet by sandwiching the inlet film from above and below the film,
In the present invention, the core sheet and the over-laminated sheet can be simultaneously performed in the step of thermocompression bonding. At this time, it is also possible to previously perform an easy-adhesion treatment on a member to be a bonding surface of the core sheet on the side of the over laminate sheet.
【0030】最近、絶縁性シートに導電性インキ等を用
いてアンテナを印刷し、ICチップと組み合わせた静電
結合方式のものもモトローラ社からBiStatixと
いう商品名で提案されているが、このアンテナとICチ
ップの組み合わせも本発明では適用できる。Recently, an electrostatic coupling type in which an antenna is printed on an insulating sheet using a conductive ink or the like and combined with an IC chip has been proposed by Motorola under the trade name BiStatix. A combination of IC chips can also be applied in the present invention.
【0031】接触型ICカードの場合は、チップなしの
カード形成後、特定の部位にICチップを埋設する窪み
を切削して設定し、ICチップを埋め込んで固定する。
本発明はチップなしのカード形成プロセスに関わるもの
であるため、接触型のICカードにも適用可能である。In the case of a contact type IC card, after forming a card without a chip, a recess for embedding the IC chip is cut and set in a specific portion, and the IC chip is embedded and fixed.
Since the present invention relates to a chipless card forming process, the present invention is also applicable to a contact type IC card.
【0032】本発明でいうオーバーラミネートシートと
は、透明乃至半透明の基材であり、前記コアシートの表
面に積層されるシートである。材質としては、塩化ビニ
ル樹脂、ポリエステル樹脂(例えばPET)、非結晶性
のポリエステル樹脂(例えばPET−G)、ポリカーボ
ネート樹脂(PC)、アクリロニトリル−ブタジエン−
スチレン共重合体樹脂(ABS)、ポリエチレン樹脂
(PE)、ポリプロピレン樹脂(PP)などのフィルム
状物が挙げられるが、特に光透過性を重視する場合には
アクリル樹脂やポリスチレン樹脂のフィルム状物を、運
転免許証など夏場の車内高温化対策として耐熱性を重視
する場合にはポリエチレンナフタレート樹脂(PEN)
などのフィルム状物から選択して使用することができ
る。厚みとしては1.5〜250μm程度である。な
お、オーバーラミネートシートの基材フィルムとインク
受容層の間に易接着層を塗布することが可能である。な
お、透明乃至半透明とはオーバーラミネートシートを透
してインクジェット記録が視認可能な程度であればよい
が、できるだけ透明度の高い方がよい。また、オーバー
ラミネートシートはコアシートと略同一の形状であって
もよいし、コアシートよりも小さい形状であってもよ
い。前者の場合、オーバーラミネートシートがカードの
全面を覆うことになり、後者はカードの一部分をオーバ
ーラミネートシートが覆うことになる。The over-laminated sheet in the present invention is a transparent or translucent substrate, and is a sheet laminated on the surface of the core sheet. Materials include vinyl chloride resin, polyester resin (for example, PET), non-crystalline polyester resin (for example, PET-G), polycarbonate resin (PC), acrylonitrile-butadiene-
Film-like materials such as styrene copolymer resin (ABS), polyethylene resin (PE), and polypropylene resin (PP) can be cited, but when light transmittance is particularly important, acrylic resin or polystyrene resin film-like material is used. In cases where heat resistance is important as a countermeasure against in-car high temperatures in the summer, such as a driver's license, polyethylene naphthalate resin (PEN)
It can be used by selecting from film-like materials such as. The thickness is about 1.5 to 250 μm. In addition, it is possible to apply an easy-adhesion layer between the base film of the over laminate sheet and the ink receiving layer. The term “transparent” or “translucent” means that the inkjet recording can be visually recognized through the over-laminated sheet, but it is preferable that the transparency is as high as possible. Further, the over-laminated sheet may have substantially the same shape as the core sheet, or may have a shape smaller than the core sheet. In the former case, the overlaminate sheet covers the entire surface of the card, and in the latter case, the overlaminate sheet covers a part of the card.
【0033】本発明でいうコアシートとオーバーラミネ
ートシートの一体化する方法としては、コアシートとオ
ーバーラミネートシートの間に接着剤を介して熱圧着す
る方法、コアシートとオーバーラミネートシートの間に
粘着剤を介して圧着する方法、コアシートとオーバーラ
ミネートシートの間に溶融した樹脂を挟み込んで圧着す
る方法、コアシートとオーバーラミネートシートを積層
し、接着剤、粘着剤、樹脂などを介在させないで熱圧着
する方法などが挙げられる。The method of integrating the core sheet and the over-laminated sheet according to the present invention includes a method of thermocompression bonding between the core sheet and the over-laminated sheet via an adhesive, and a method of bonding between the core sheet and the over-laminated sheet. Pressure bonding method, a method in which a molten resin is sandwiched between a core sheet and an over-laminated sheet, and a method in which the core sheet and an over-laminated sheet are laminated, and heat is applied without interposing an adhesive, an adhesive, a resin, etc. Compression bonding method and the like can be mentioned.
【0034】本発明でいうインク受容層とは、インクジ
ェット方式の記録に対して記録適性を有するものであれ
ば特に限定しないが、インクジェット記録がオーバーラ
ミネートシートを透して視認可能なインク受容層である
必要がある。インク受容層としては、水溶性樹脂系受容
層、顔料系受容層などインクジェット記録適性を有する
公知の記録層が適用できる。The ink-receiving layer in the present invention is not particularly limited as long as it has recording suitability for ink-jet recording, but is an ink-receiving layer that can be visually recognized through an over-laminated sheet by ink-jet recording. Need to be. As the ink receiving layer, a known recording layer having inkjet recording suitability such as a water-soluble resin-based receiving layer and a pigment-based receiving layer can be applied.
【0035】水溶性樹脂系受容層は、水やアルコール等
の水性溶媒に可溶な水溶性樹脂を主体としたものであ
り、従来公知の種々のものが用いられる。例えば、ポリ
ビニルアルコールやポリビニルピロリドン、ポリ(メ
タ)アクリル酸、セルロース系樹脂(CMC、HEC、
HPC等)、ポリアクリルアミド、ポリエチレンオキサ
イド、ポリエチレングリコール、ポリビニルアセタール
系樹脂、ポリビニルメチルエーテル、ポリアミン、ポリ
エチレンイミン、カゼイン、ゼラチン、でんぷん等の水
溶性樹脂及び/またはこれらの共重合体、カチオン/ア
ニオン変性物等の少なくとも1種以上が用いられる。The water-soluble resin-based receiving layer is mainly composed of a water-soluble resin soluble in an aqueous solvent such as water or alcohol, and various conventionally known ones are used. For example, polyvinyl alcohol, polyvinylpyrrolidone, poly (meth) acrylic acid, cellulose resin (CMC, HEC,
HPC, etc.), water-soluble resins such as polyacrylamide, polyethylene oxide, polyethylene glycol, polyvinyl acetal resin, polyvinyl methyl ether, polyamine, polyethylene imine, casein, gelatin, starch and / or copolymers thereof, cation / anion-modified At least one or more materials are used.
【0036】顔料系受容層は、各種顔料およびバインダ
ー等からなる。顔料としては、例えば、ゼオライト、軽
質炭酸カルシウム、重質炭酸カルシウム、炭酸マグネシ
ウム、カオリン、タルク、硫酸カルシウム、硫酸バリウ
ム、酸化チタン、酸化亜鉛、硫化亜鉛、炭酸亜鉛、サチ
ンホワイト、ケイ酸アルミニウム、ケイソウ土、焼成ク
レ−、ケイ酸カルシウム、ケイ酸マグネシウム、コロイ
ダルシリカ、非晶質シリカ、水酸化アルミニウム、コロ
イダルアルミナ、アルミナ、アルミナ水和物等の一般塗
工紙のコ−ト剤に使用されている顔料を挙げることがで
きる。インク受容層に使用し得るより好ましい顔料とし
て、コロイダルシリカ、非晶質シリカ、水酸化アルミニ
ウム、アルミナ、アルミナ水和物を挙げることができ
る。これらは単独あるいは2種以上を混合して用いるこ
とができる。The pigment-based receiving layer comprises various pigments and a binder. Examples of the pigment include zeolite, light calcium carbonate, heavy calcium carbonate, magnesium carbonate, kaolin, talc, calcium sulfate, barium sulfate, titanium oxide, zinc oxide, zinc sulfide, zinc carbonate, satin white, aluminum silicate, and diatomaceous Used as a coating agent for general coated paper such as earth, calcined clay, calcium silicate, magnesium silicate, colloidal silica, amorphous silica, aluminum hydroxide, colloidal alumina, alumina, alumina hydrate Pigments. More preferred pigments that can be used in the ink receiving layer include colloidal silica, amorphous silica, aluminum hydroxide, alumina, and alumina hydrate. These can be used alone or in combination of two or more.
【0037】インク受容層に使用し得るバインダーとし
て、例えば酸化澱粉、エーテル化澱粉等の澱粉誘導体、
カルボキシメチルセルロース、ヒドロキシエチルセルロ
ース等のセルロース誘導体、カゼイン、ゼラチン、大豆
タンパク、完全ケン化ポリビニルアルコール、部分ケン
化ポリビニルアルコール、ケイ素変性ポリビニルアルコ
ール、アセトアセチル基変性ポリビニルアルコール、ス
チレン−無水マレイン酸共重合体の塩、スチレン−ブタ
ジエン系ラテックス、アクリル系ラテックス、ポリエス
テルポリウレタン系ラテックス、酢酸ビニル系ラテック
ス等の水性接着剤、或いはポリメチルメタクリレート、
ポリウレタン樹脂、不飽和ポリエステル樹脂、塩化ビニ
ル−酢酸ビニルコポリマー、ポリビニルブチラール、ア
ルキッド樹脂等の有機溶剤可溶性樹脂等が挙げられる。
これらは単独あるいは2種以上を混合して用いられる。As binders that can be used in the ink receiving layer, for example, starch derivatives such as oxidized starch and etherified starch;
Carboxymethyl cellulose, cellulose derivatives such as hydroxyethyl cellulose, casein, gelatin, soy protein, fully saponified polyvinyl alcohol, partially saponified polyvinyl alcohol, silicon-modified polyvinyl alcohol, acetoacetyl group-modified polyvinyl alcohol, styrene-maleic anhydride copolymer Aqueous adhesive such as salt, styrene-butadiene latex, acrylic latex, polyester polyurethane latex, vinyl acetate latex, or polymethyl methacrylate,
Organic solvent-soluble resins such as polyurethane resins, unsaturated polyester resins, vinyl chloride-vinyl acetate copolymers, polyvinyl butyral, and alkyd resins.
These are used alone or in combination of two or more.
【0038】また、インク受容層中には、インク受容層
中にカチオン性樹脂を配合することができる。インク受
容層に使用し得るカチオン性樹脂としては、例えば、ポ
リジアリルアミン塩酸塩、ジアリルアミン塩酸塩・アク
リルアミド共重合物、ポリジアリルジメチルアンモニウ
ムクロライド、ジアリルジメチルアンモニウムクロライ
ド・アクリルアミド共重合物、ジアリルジメチルアンモ
ニウムクロライド・二酸化イオウ共重合物、ポリアリル
アミン塩酸塩、アリルアミン塩酸塩・ジアリルアミン塩
酸塩共重合体、N−ビニルアクリルアミジン塩酸塩・ア
クリルアミド共重合体、エピクロロヒドリン・ジアルキ
ルアミン付加重合物、ポリアミドポリアミンエピクロロ
ヒドリン重合物、ジシアンジアミド・ホルマリン重縮合
物、ジシアンジアミド・ポリエチレンアミン重縮合物、
ポリエチレンイミン塩酸塩、ポリ(メタ)アクリロイル
オキシアルキルトリアルキルアンモニウムクロライド、
ポリ(メタ)アクリロイルオキシアルキルトリアルキル
アンモニウムクロライド・アクリルアミド共重合体、ポ
リ(メタ)アクリルアミドアルキルトリアルキルアンモ
ニウムクロライド、ポリ(メタ)アクリルアミドアルキ
ルトリアルキルアンモニウムクロライド・アクリルアミ
ド共重合体等が挙げられる。これらは単独あるいは2種
以上を混合して用いられる。カチオン樹脂を配合する
と、記録後の積層の際に、例えば熱圧着の際の熱によ
り、インクが移動することを防ぐことができる。In the ink receiving layer, a cationic resin can be blended in the ink receiving layer. Examples of the cationic resin that can be used in the ink receiving layer include, for example, polydiallylamine hydrochloride, diallylamine hydrochloride / acrylamide copolymer, polydiallyldimethylammonium chloride, diallyldimethylammonium chloride / acrylamide copolymer, diallyldimethylammonium chloride. Sulfur dioxide copolymer, polyallylamine hydrochloride, allylamine hydrochloride / diallylamine hydrochloride copolymer, N-vinylacrylamidine hydrochloride / acrylamide copolymer, epichlorohydrin / dialkylamine addition polymer, polyamide polyamine epichloro Hydrin polymer, dicyandiamide / formalin polycondensate, dicyandiamide / polyethyleneamine polycondensate,
Polyethyleneimine hydrochloride, poly (meth) acryloyloxyalkyltrialkylammonium chloride,
Examples thereof include poly (meth) acryloyloxyalkyltrialkylammonium chloride / acrylamide copolymer, poly (meth) acrylamidoalkyltrialkylammonium chloride, and poly (meth) acrylamidoalkyltrialkylammonium chloride / acrylamide copolymer. These are used alone or in combination of two or more. When a cationic resin is blended, it is possible to prevent the ink from moving due to heat during thermocompression bonding during lamination after recording.
【0039】なお、インクジェット記録がオーバーラミ
ネートシートを透して視認可能な範囲であればインク受
容層は、オーバーラミネートシートに単層あるいは2層
以上形成してもよい。オーバーラミネートシート上への
インク受容層形成の方法としては、グラビアコーティン
グ、ナイフコーティング、ダイコーティング等の公知の
塗工方式やスクリーン印刷、フレキソ印刷等の公知の印
刷方式が採用できるほか、カード面の一部に本発明を適
用する場合はスクリーン印刷、フレキソ印刷等の公知の
印刷方式が使用できる。The ink-receiving layer may be formed as a single layer or two or more layers on the over-laminated sheet as long as the ink-jet recording is in a visible range through the over-laminated sheet. As a method of forming the ink receiving layer on the over-laminated sheet, a known coating method such as gravure coating, knife coating, die coating or the like, or a known printing method such as screen printing or flexographic printing can be employed. When the present invention is partially applied, known printing methods such as screen printing and flexographic printing can be used.
【0040】本発明(1)は、コアシートおよびオーバ
ーラミネートシートを有するカードにおいて、オーバー
ラミネートシートが透明ないし半透明の基材であり、該
基材の片面に3〜50μmのインク受容層を有し、イン
ク受容層にはインクジェット方式にて記録が施され、イ
ンク受容層面がコアシート側になるようにコアシートと
オーバーラミネートシートが積層一体化され、前記記録
がオーバーラミネートシートを透して視認できることを
特徴とするカードである。中でも、インク受容層の厚み
を3〜50μmとすることが重要である。因みに厚みが
3μmに満たないと、インクジェット記録した際のイン
クが十分吸収されず、空孔に残留したインクによる滲み
が発生して正確な画像が得られない。一方、50μmを
越えるとインク受容層が弱く(剥離強度が弱く)なり、
カードとした場合インク受容層から剥がれる可能性があ
る。また、インク受容層は顔料を含んでいる為の厚みが
大きくなると、インク受容層上に射出されたインクが裏
面のオーバーラミネートシートの透明基材側へ充分透過
できず、現実性のある画像が得られない。特に厚みは5
〜40μmにすることが好ましい。なお、コアシートお
よびオーバーラミネートシートの積層一体化の方法とし
ては、特に限定するものではなく、接着剤を用いたり、
熱圧着する方法などが採用できる。The present invention (1) relates to a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent base material, and has an ink receiving layer of 3 to 50 μm on one side of the base material. Then, recording is performed on the ink receiving layer by an ink jet method, and the core sheet and the over laminate sheet are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording is visually recognized through the over laminate sheet. A card characterized by being able to. In particular, it is important that the thickness of the ink receiving layer be 3 to 50 μm. If the thickness is less than 3 μm, the ink at the time of ink-jet recording is not sufficiently absorbed, and bleeding occurs due to the ink remaining in the pores, so that an accurate image cannot be obtained. On the other hand, if it exceeds 50 μm, the ink receiving layer becomes weak (peeling strength becomes weak),
When a card is used, there is a possibility that the card is peeled off from the ink receiving layer. In addition, when the ink receiving layer becomes thicker because it contains a pigment, the ink ejected on the ink receiving layer cannot sufficiently penetrate to the transparent substrate side of the over-laminated sheet on the back surface, and a realistic image can be obtained. I can't get it. Especially the thickness is 5
It is preferable to set it to 4040 μm. The method of laminating and integrating the core sheet and the overlaminate sheet is not particularly limited, and an adhesive may be used,
A method such as thermocompression bonding can be adopted.
【0041】また、コアシートの両面にオーバーラミネ
ートシートを有し、両方のオーバーラミネートシートが
透明ないし半透明の基材であり、該基材の片面に3〜5
0μmのインク受容層を有し、且つ、インク受容層には
インクジェット方式にて記録が施され、インク受容層面
がコアシート側になるようにコアシートと両方のオーバ
ーラミネートシートが積層一体化され、前記記録がオー
バーラミネートシートを透してそれぞれ視認できるよう
に構成することも可能である。また、両面にインクジェ
ット記録を施したオーバーラミネートシートを積層する
構成は両面に情報を付与することができるので特に好ま
しい。Further, the core sheet has overlaminated sheets on both sides, and both overlaminated sheets are transparent or translucent substrates, and 3 to 5
It has an ink receiving layer of 0 μm, and recording is performed on the ink receiving layer by an inkjet method, and the core sheet and both over laminate sheets are laminated and integrated so that the ink receiving layer surface is on the core sheet side, It is also possible to configure so that the recordings can be visually recognized through the over-laminated sheet. A configuration in which an over-laminated sheet on which ink jet recording is performed on both sides is laminated is particularly preferable because information can be added to both sides.
【0042】本発明(2)は、コアシートおよびオーバ
ーラミネートシートを有するカードにおいて、オーバー
ラミネートシートが透明ないし半透明の基材であり、該
基材の片面にインク受容層を有し、インク受容層にはイ
ンクジェット方式にて記録が施され、インク受容層面が
コアシート側になるようにコアシートとオーバーラミネ
ートシートが積層一体化され、前記記録がオーバーラミ
ネートシートを透して視認できるカードであって、コア
シートとオーバーラミネートシートの積層が、熱圧着に
よる積層一体化であることを特徴とするカードである。
発明(2)のカードは、積層一体化の際に、接着剤、粘
着剤などを使用せず、コアシートとオーバーラミネート
シートを積層状態で熱圧着(熱および圧を加えること)
により一体化される。コアシートおよびオーバーラミネ
ートシートの少なくとも一方が、熱により表面的に溶融
し、両シートを融着しているものと考えられる。更には
恐らく、熱圧着の際に、インク受容層表面に存在するフ
ィラー粒子がオーバーラミネートシートやコアシート部
材表面に食い込む、或いは、熱圧着により溶融したオー
バーラミネートシートやコアシート部材樹脂がインク受
容層の空隙に侵入、固化する、或いは、インク受容層に
含有させた樹脂粒子あるいはバインダー樹脂がオーバー
ラミネートシートやコアシート部材樹脂との熱融着する
ため、強固な積層状態となると考えられる。The present invention (2) relates to a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent substrate, the substrate having an ink receiving layer on one surface, The recording is performed on the layer by an ink jet method, and a core sheet and an over laminate sheet are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording is visually recognized through the over laminate sheet. Further, the card is characterized in that the lamination of the core sheet and the overlaminate sheet is lamination integration by thermocompression bonding.
In the card of the invention (2), the core sheet and the over-laminated sheet are thermocompression-bonded (by applying heat and pressure) without using an adhesive or a pressure-sensitive adhesive during lamination and integration.
Are integrated. It is considered that at least one of the core sheet and the over-laminated sheet is surface-melted due to heat, and both sheets are fused. Further, probably, at the time of thermocompression bonding, the filler particles existing on the surface of the ink receiving layer bite into the surface of the overlaminated sheet or the core sheet member, or the resin of the overlaminated sheet or the core sheet member melted by the thermocompression bonding becomes the ink receiving layer. It is considered that the resin particles or the binder resin contained in the ink-receiving layer invades and solidifies into the voids, and is thermally fused with the over-laminated sheet or the core sheet member resin, resulting in a strong laminated state.
【0043】オーバーラミネートシートとしては、特
に、塩化ビニルを含有する樹脂フィルム、非結晶性のポ
リエステルフィルムの使用が好ましい。また、オーバー
ラミネートの耐熱性などを改善するために、PET−G
のような非結晶性ポリエステル樹脂に相溶性が良く耐熱
性に優れたポリカーボネート等の樹脂をブレンドして作
成されたフィルムを使用することも有効である。インク
受容層に含有せしめるバインダーや樹脂粒子としては、
塩化ビニル樹脂、PET−G樹脂、ABS樹脂などの熱
可塑性樹脂のほか、ホットメルト接着剤原料に使用され
る公知の各種樹脂などが挙げられる。更に、オーバーラ
ミネートシートとコアシートの両方が同一の塩化ビニル
を含有する樹脂フィルムまたは非結晶性のポリエステル
フィルムまたはABS樹脂で形成されている場合は、受
容層を挟んで部材同士が融着するため、オーバーラミネ
ートシートとコアシートの間に接着剤を挟む必要がな
く、効果的である。同様の効果は公知のヒートシール性
が認められるポリエチレンフィルム、ポリプロピレンフ
ィルムでも得られる。さらに、非結晶性のポリエステル
フィルムとポリカーボネートフィルムのように相溶性の
良い樹脂フィルムの組合せでも実現することができる。
なお、熱圧着の条件は、使用するコアシート、オーバー
ラミネートシートの材種、厚みなど、或いはインク受容
層の成分、厚みによって一概に言えないが、40〜25
0℃で、圧力0.1〜20kg/cm2程度でプレスす
るとよい。この範囲を外れると、熱圧着時に融着不良や
インク色素の退色、カード厚みムラを起こし易い。As the overlaminate sheet, it is particularly preferable to use a resin film containing vinyl chloride and a non-crystalline polyester film. In order to improve the heat resistance of the overlaminate, PET-G
It is also effective to use a film prepared by blending a non-crystalline polyester resin such as polycarbonate with a resin having good compatibility and excellent heat resistance. As a binder or resin particles to be contained in the ink receiving layer,
In addition to thermoplastic resins such as vinyl chloride resin, PET-G resin, and ABS resin, various known resins used as raw materials for hot melt adhesives can be used. Further, when both the over-laminated sheet and the core sheet are formed of the same vinyl chloride-containing resin film or amorphous polyester film or ABS resin, the members are fused together with the receiving layer interposed therebetween. This is effective because there is no need to sandwich an adhesive between the over-laminated sheet and the core sheet. The same effect can be obtained with a known polyethylene film or polypropylene film having a heat sealing property. Further, it can be realized by a combination of a non-crystalline polyester film and a resin film having good compatibility such as a polycarbonate film.
The conditions of the thermocompression bonding cannot be generally described depending on the material type and thickness of the core sheet and the over-laminated sheet to be used, or the components and thickness of the ink receiving layer.
Pressing at 0 ° C. and a pressure of about 0.1 to 20 kg / cm 2 is preferable. Outside this range, poor fusion, discoloration of the ink dye, and uneven card thickness are likely to occur during thermocompression bonding.
【0044】本発明(3)は、コアシートおよびオーバ
ーラミネートシートを有するカードにおいて、オーバー
ラミネートシートが透明ないし半透明の基材であり、該
基材の片面にインク受容層を有し、インク受容層にはイ
ンクジェット方式にて記録が施され、インク受容層面が
コアシート側になるようにコアシートとオーバーラミネ
ートシートが積層一体化され、前記記録がオーバーラミ
ネートシートを透して視認できるカードであって、コア
シートとオーバーラミネートシートの積層一体化が、コ
アシートとオーバーラミネートシートの間に挟みこまれ
た2〜300μmの厚さの接着剤を介しての積層一体化
であることを特徴とするカードである。発明(3)は、
コアシートとオーバーラミネートシートを熱接着、圧接
着、熱圧接着、湿潤接着することのできる接着剤を用い
て積層一体化する。中でも、シート状接着剤を用い、熱
圧接着すると、強固な接着のカードとなるので好まし
い。熱圧接着する為のシート状接着剤としては、ホット
メルト接着剤が好適である。ホットメルト接着剤として
はベースポリマー別にポリエステルまたはエチレン酢酸
ビニル共重合体またはポリアミドまたは熱可塑性ゴムを
主成分とするものなどが挙げられ、これにロジン、ロジ
ン誘導体、ピネン系樹脂等の粘着付与剤とポリエチレン
ワックス、パラフィンワックス等のワックス類と各種可
塑剤、充填剤、熱安定剤などが添加されて調製される。
ポリエステル系は、例えばテレフタル酸、エチレングリ
コール、テトラメチレングリコール、イソフタル酸、セ
バシン酸、ドデカン酸、ポリテトラメチレンエーテルグ
リコール等の中から選ばれる成分の共重合体などであ
り、ポリアミド系はダイマー酸とジアミンの重縮合反応
による生成物、熱可塑性ゴム系はポリスチレン−ポリブ
タジエン−ポリスチレンのブロック共重合体などが挙げ
られる。その他シート状接着剤以外でも、製造工程に応
じたポットライフが確保できれば、熱硬化型、紫外線硬
化型、2液硬化型など公知の接着剤を塗布することなど
で使用することが可能である。The present invention (3) relates to a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent substrate, the substrate having an ink receiving layer on one surface, The recording is performed on the layer by an ink jet method, and a core sheet and an over laminate sheet are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording is visually recognized through the over laminate sheet. Wherein the lamination and integration of the core sheet and the overlaminate sheet are lamination and integration via an adhesive having a thickness of 2 to 300 μm sandwiched between the core sheet and the overlaminate sheet. Card. Invention (3)
The core sheet and the over-laminated sheet are laminated and integrated by using an adhesive capable of heat bonding, pressure bonding, hot pressure bonding, and wet bonding. Among them, it is preferable to use a sheet-like adhesive and bond by heat and pressure, since a strongly bonded card can be obtained. As a sheet adhesive for hot-pressure bonding, a hot melt adhesive is suitable. Examples of the hot melt adhesive include those having polyester or ethylene vinyl acetate copolymer or polyamide or thermoplastic rubber as a main component according to the base polymer, and rosin, rosin derivative, tackifier such as pinene resin and the like. It is prepared by adding waxes such as polyethylene wax and paraffin wax, and various plasticizers, fillers, and heat stabilizers.
The polyester type is, for example, a copolymer of a component selected from terephthalic acid, ethylene glycol, tetramethylene glycol, isophthalic acid, sebacic acid, dodecanoic acid, polytetramethylene ether glycol, etc., and the polyamide type is dimer acid. A product obtained by a polycondensation reaction of a diamine, and a thermoplastic rubber system include a block copolymer of polystyrene-polybutadiene-polystyrene. Other than the sheet adhesive, if a pot life according to the manufacturing process can be ensured, it can be used by applying a known adhesive such as a thermosetting type, an ultraviolet curing type, or a two-part curing type.
【0045】本発明(4)は、コアシートおよびオーバ
ーラミネートシートを有するカードにおいて、オーバー
ラミネートシートが透明ないし半透明の基材であり、該
基材の片面にインク受容層を有し、インク受容層にはイ
ンクジェット方式にて記録が施され、インク受容層面が
コアシート側になるようにコアシートとオーバーラミネ
ートシートが積層一体化され、前記記録がオーバーラミ
ネートシートを透して視認できるカードであって、コア
シートが塩化ビニルを含有する樹脂フィルム、または非
結晶性のポリエステルフィルムまたはABS樹脂フィル
ムであることを特徴とするカードである。コアシートと
して、塩化ビニルを含有する樹脂フィルムや非結晶性の
ポリエステルフィルム、ABS樹脂フィルムを用いる
と、積層一体化の際に接着剤などを用いることなく熱圧
着できるので好ましい。特に、コアシートが、非結晶性
のポリエステルフィルムである、少なくともエチレング
リコール、テレフタル酸および1,4−シクロヘキサン
ジメタノールの3成分を重合した変性ポリエステル樹脂
(例えばPET−G)フィルムの使用が好ましい。The present invention (4) relates to a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent substrate, and has an ink receiving layer on one side of the substrate. The recording is performed on the layer by an ink jet method, and a core sheet and an over laminate sheet are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording is visually recognized through the over laminate sheet. Wherein the core sheet is a resin film containing vinyl chloride, an amorphous polyester film or an ABS resin film. It is preferable to use a resin film containing vinyl chloride, a non-crystalline polyester film, or an ABS resin film as the core sheet because thermocompression bonding can be performed without using an adhesive or the like during lamination and integration. In particular, it is preferable to use a modified polyester resin (for example, PET-G) film in which at least three components of ethylene glycol, terephthalic acid and 1,4-cyclohexanedimethanol are polymerized, wherein the core sheet is a non-crystalline polyester film.
【0046】本発明(5)は、コアシートおよびオーバ
ーラミネートシートを有するカードにおいて、オーバー
ラミネートシートが透明ないし半透明の基材であり、該
基材の片面にインク受容層を有し、インク受容層にはイ
ンクジェット方式にて記録が施され、インク受容層面が
コアシート側になるようにコアシートとオーバーラミネ
ートシートが積層一体化され、前記記録がオーバーラミ
ネートシートを透して視認できるカードであって、オー
バーラミネートシートが塩化ビニルを含有する樹脂フィ
ルム、非結晶性のポリエステルフィルム、ABS樹脂フ
ィルムまたはポリカーボネートフィルムであることを特
徴とするカードである。オーバーラミネートシートとし
て、塩化ビニルを含有する樹脂フィルム、非結晶性のポ
リエステルフィルム、ABS樹脂フィルムを用いると、
積層一体化の際に接着剤などを用いることなく熱圧着で
きるので好ましい。またコアシートとして非結晶性のポ
リエステルフィルムを使用している場合、オーバーラミ
ネートシートとしてポリカーボネートフィルムの使用も
好ましい。特に、オーバーラミネートシートが、非結晶
性のポリエステルフィルムである、少なくともエチレン
グリコール、テレフタル酸および1,4−シクロヘキサ
ンジメタノールの3成分を重合した変性ポリエステル樹
脂(例えばPET−G)フィルムの使用が好ましい。イ
ンクジェット印刷の経時による退色などを防ぐために、
オーバーラミネートシート基材に紫外線吸収剤等を含有
させておくことも可能である。The present invention (5) relates to a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent base material, and has an ink receiving layer on one side of the base material. The recording is performed on the layer by an ink jet method, and a core sheet and an over laminate sheet are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording is visually recognized through the over laminate sheet. Wherein the overlaminate sheet is a resin film containing vinyl chloride, an amorphous polyester film, an ABS resin film or a polycarbonate film. When a resin film containing vinyl chloride, an amorphous polyester film, or an ABS resin film is used as the overlaminate sheet,
This is preferable because thermocompression bonding can be performed without using an adhesive or the like during lamination and integration. When an amorphous polyester film is used as the core sheet, it is also preferable to use a polycarbonate film as the overlaminate sheet. In particular, it is preferable to use a modified polyester resin (for example, PET-G) film in which at least three components of ethylene glycol, terephthalic acid and 1,4-cyclohexanedimethanol are polymerized, in which the overlaminate sheet is an amorphous polyester film. . In order to prevent fading due to the aging of inkjet printing,
It is also possible to make the overlaminate sheet base contain an ultraviolet absorber or the like.
【0047】本発明(6)は、コアシートおよびオーバ
ーラミネートシートを有するカードにおいて、オーバー
ラミネートシートが透明ないし半透明の基材であり、該
基材の片面にインク受容層を有し、インク受容層にはイ
ンクジェット方式にて記録が施され、インク受容層面が
コアシート側になるようにコアシートとオーバーラミネ
ートシートが積層一体化され、前記記録がオーバーラミ
ネートシートを透して視認できるカードであって、コア
シートとオーバーラミネートシートが同種のフィルムで
あることを特徴とするカードである。コアシートとオー
バーラミネートシートが異種である場合、それぞれのフ
ィルム表面の性質(例えば極性など)が異なるので、接
着性が低下する可能性がある。また、それぞれの熱によ
る収縮性がことなるので、カールを生じる可能性があ
る。コアシートとオーバーラミネートシートが同種のフ
ィルムで構成することにより、接着が強固なカードで、
且つ積層一体化の際のカールを生じ難いカードが得られ
る。同種のフィルムとして最も好ましいものは、塩化ビ
ニルを含有する樹脂、非結晶性ポリエステル樹脂、AB
S樹脂が挙げられる。The present invention (6) relates to a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent substrate, and the substrate has an ink receiving layer on one side, The recording is performed on the layer by an ink jet method, and a core sheet and an over laminate sheet are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording is visually recognized through the over laminate sheet. Wherein the core sheet and the overlaminate sheet are the same type of film. When the core sheet and the overlaminate sheet are different, the properties (for example, polarities) of the respective film surfaces are different, so that the adhesiveness may be reduced. In addition, since the shrinkage due to each heat is different, there is a possibility of curling. By forming the core sheet and the over laminate sheet with the same type of film, the card with strong adhesion,
In addition, a card that is unlikely to cause curl during lamination and integration can be obtained. The most preferable films of the same kind are resins containing vinyl chloride, non-crystalline polyester resins, AB
S resin is mentioned.
【0048】本発明(7)は、コアシートおよびオーバ
ーラミネートシートを有するカードにおいて、コアシー
トの両面にオーバーラミネートシートが積層されてお
り、両方のオーバーラミネートシートが透明ないし半透
明の基材であり、該基材の片面にインク受容層を有し、
且つ、インク受容層にはインクジェット方式にて記録が
施され、インク受容層面がコアシート側になるようにコ
アシートと両方のオーバーラミネートシートが積層一体
化され、前記記録がオーバーラミネートシートを透して
それぞれ視認できるカードであって、両方のオーバーラ
ミネートシートが実質的に同一の厚みであることを特徴
とするカードである。両方の面にオーバーラミネートシ
ートがある場合、両方のオーバーラミネートシートが同
じ材質でも、厚みが異なると、熱圧着の際に片側にカー
ルを生じ易い。実質的に同一の厚みにオーバーラミネー
トシートを構成することが好ましい。なお、インク受容
層も、同じ厚みで構成することがより好ましい。The present invention (7) is a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheets are laminated on both sides of the core sheet, and both over-laminated sheets are transparent or translucent base materials. Having an ink receiving layer on one side of the substrate,
In addition, recording is performed on the ink receiving layer by an ink jet method, the core sheet and both over laminate sheets are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording passes through the over laminate sheet. , Wherein both over-laminated sheets have substantially the same thickness. When there are over-laminated sheets on both sides, even if both over-laminated sheets are of the same material, if the thicknesses are different, curling is likely to occur on one side during thermocompression bonding. It is preferable to configure the overlaminate sheet to have substantially the same thickness. It is more preferable that the ink receiving layer also has the same thickness.
【0049】本発明(8)は、コアシートおよびオーバ
ーラミネートシートを有するカードにおいて、コアシー
トの両面にオーバーラミネートシートが積層一体化され
ており、両方のオーバーラミネートシートが透明ないし
半透明の基材であり、該基材の片面にインク受容層を有
し、且つ、インク受容層にはインクジェット方式にて記
録が施され、インク受容層面がコアシート側になるよう
にコアシートと両方のオーバーラミネートシートが積層
一体化され、前記記録がオーバーラミネートシートを透
してそれぞれ視認できるカードであって、インク受容層
に形成された記録が片面と他面とで異なることを特徴と
するカードである。表裏にインクジェット記録方式で記
録されるカードであって、表裏で異なる記録を行うこと
ができ、また好ましい。例えば、表面に図柄、カード
名、有効期限などをインクジェット記録し、裏面に所有
者名、顔写真などをインクジェット記録するとよい。The present invention (8) relates to a card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is laminated and integrated on both sides of the core sheet, and both over-laminated sheets are made of a transparent or translucent substrate. The substrate has an ink-receiving layer on one side, and the ink-receiving layer is subjected to recording by an ink-jet method, and both the core sheet and the oversheet are laminated so that the ink-receiving layer side is on the core sheet side. A card in which sheets are laminated and integrated, and the recording is visible through an over-laminated sheet, wherein the recording formed on the ink receiving layer is different on one side and the other side. This is a card recorded on the front and back by an ink jet recording method, and different recording can be performed on the front and back, which is preferable. For example, a pattern, a card name, an expiration date, and the like may be inkjet-recorded on the front surface, and an owner name, a face photograph, and the like may be inkjet-recorded on the rear surface.
【0050】(1)〜(8)記載のカードであって、イ
ンク受容層が、非晶質シリカ及び/又はアルミナを有す
る事が好ましい。インク受容層に使用する顔料として非
晶質シリカ、アルミナを含むことを規定する。非晶質シ
リカの使用は、インクジェット方式のインクを効率よく
吸収するので、吸収されないで空孔に残留したインクに
よる滲みを防止できる。一方、アルミナは、透明なイン
クジェット受容層を形成できるので、鮮明な画像が形成
できる。In the card according to any one of (1) to (8), the ink receiving layer preferably contains amorphous silica and / or alumina. It specifies that the pigment used in the ink receiving layer contains amorphous silica and alumina. The use of amorphous silica efficiently absorbs ink jet ink, so that bleeding due to the ink not absorbed but remaining in the pores can be prevented. On the other hand, alumina can form a transparent ink jet receiving layer, so that a clear image can be formed.
【0051】発明(1)〜(8)のカードであって、イ
ンク受容層に使用するバインダーとしてポリビニルアル
コール、シリル変性ポリビニルアルコールを含むことが
好ましい。ポリビニルアルコール、シリル変性ポリビニ
ルアルコールは、インクジェット方式の記録に適してい
るだけでなく、比較的強いインク受容層が形成できるた
め、カードに適している。In the cards according to the inventions (1) to (8), it is preferable that the binder used in the ink receiving layer contains polyvinyl alcohol or silyl-modified polyvinyl alcohol. Polyvinyl alcohol and silyl-modified polyvinyl alcohol are suitable for cards because they can form a relatively strong ink-receiving layer in addition to being suitable for ink-jet recording.
【0052】発明(1)〜(8)のカードであって、オ
ーバーラミネートシートの厚みを1.5〜250μmで
あることが好ましい。因みに1.5μmに満たない場
合、インク受容層の形成が困難であり、製品カード表面
の耐擦性が不充分となる。250μmを越えるような場
合、カードの厚みが厚くなり実用的でなくなるばかり
が、半透明フィルムの場合、インクジェット記録像が視
認し難くなる。In the cards of the inventions (1) to (8), the thickness of the overlaminated sheet is preferably 1.5 to 250 μm. If the thickness is less than 1.5 μm, it is difficult to form an ink receiving layer, and the abrasion resistance of the product card surface becomes insufficient. When the thickness exceeds 250 μm, the thickness of the card becomes too large to be practical, but in the case of a translucent film, the ink jet recorded image becomes difficult to visually recognize.
【0053】発明(1)〜(8)のカードであって、コ
アシートが不透明であることが好ましい。コアシートが
不透明であると、インク受容層の記録が鮮明に視認でき
るようになるので好ましい態様である。特に白色が好ま
しい。In the cards of the inventions (1) to (8), the core sheet is preferably opaque. When the core sheet is opaque, the recording of the ink receiving layer can be clearly recognized, which is a preferable embodiment. Particularly, white is preferable.
【0054】本発明(9)は、インクジェット方式がソ
リッドインクを使用したものである(1)〜(8)記載
のカードである。発明(1)〜(8)のカードにおい
て、インクジェット方式がソリッドインクを使用したも
のであることを規定する。ソリッドインクジェットイン
クは常温では固体であり、ノズルから射出する直前に加
熱溶融させて噴射し、被印刷物上で再固化させる方式で
ある。ソリッドインクジェットインクの融点にもよる
が、オーバーラミシートを積層する際の加熱加圧によっ
て流動性が増して印刷画像に滲みなどを発生させる可能
性があるので、この場合にもある程度の空隙率を持った
インク受容層が必要と考えられる。The present invention (9) is the card according to any one of (1) to (8), wherein the ink jet system uses solid ink. In the cards of the inventions (1) to (8), it is specified that the ink jet system uses solid ink. The solid inkjet ink is a solid at normal temperature, and is a system in which it is heated and melted immediately before being ejected from a nozzle, ejected, and re-solidified on a printing material. Depending on the melting point of the solid inkjet ink, the heating and pressurization when laminating the over-laminate sheet may increase the fluidity and cause bleeding in the printed image. It is considered necessary to have an ink receiving layer.
【0055】本発明(10)は、カードが非接触式及び
/又は接触式ICカードである(1)〜(9)記載のカ
ードである。発明(1)〜(9)のカードにおいて、カ
ードが非接触式及び/又は接触式ICカードであること
を規定する。非接触式、接触式、そして非接触式と接触
式の両方式を採用したICカードは、保有できる情報量
が多く、リーダーライタにより読み取り書き込みが行え
るのでカードとして特に好ましい態様である。The present invention (10) is the card according to any one of (1) to (9), wherein the card is a non-contact type and / or contact type IC card. In the cards of the inventions (1) to (9), it is specified that the card is a non-contact type and / or a contact type IC card. An IC card employing a non-contact type, a contact type, or both a non-contact type and a contact type is a particularly preferable embodiment as a card because it can hold a large amount of information and can be read and written by a reader / writer.
【0056】発明(1)〜(10)において、インク受
容層に形成された記録に、顔写真、氏名などの個人情報
を含むことが好ましい。記録がオーバーラミネートシー
トに被われているので、個人情報を改ざんすることがで
きないので、特に好ましい態様である。In the inventions (1) to (10), it is preferable that the record formed on the ink receiving layer contains personal information such as a face photograph and a name. This is a particularly preferable embodiment, since the record is covered by the over-laminated sheet, so that the personal information cannot be falsified.
【0057】発明(1)〜(10)において、インク受
容層に形成された記録にバーコードを含むことが好まし
い。例えば、インクジェット方式によりバーコードで情
報を保持させると、ICチップが何らかの影響で読み取
りできない場合でも、必要最小限の情報がバーコードに
よって読み取ることができる。また、製造工程で、IC
チップへの個人情報の記録と、カードへのインクジェッ
ト方式による個人情報の記録が一致しているか否かを、
バーコードにより管理することも可能となる。バーコー
ドが通常のバーコードのほか、二次元バーコードでもよ
い。In the inventions (1) to (10), it is preferable that the recording formed on the ink receiving layer contains a bar code. For example, when information is held in a barcode by an ink jet method, the minimum necessary information can be read by the barcode even if the IC chip cannot be read due to some influence. Also, in the manufacturing process, IC
Whether the recording of personal information on the chip and the recording of personal information on the card by the inkjet method match,
It can also be managed by a barcode. The barcode may be a normal barcode or a two-dimensional barcode.
【0058】なお、発明(1)〜(10)において、カ
ードにエンボス加工を施したり、コアシートとオーバー
ラミネートシートの間にホログラムやスレッド或いは地
紋診察を設けることもできる。In the inventions (1) to (10), the card may be embossed, or a hologram, thread or tint block may be provided between the core sheet and the over-laminated sheet.
【0059】次に、上記の如きカードの製造方法につい
て説明する。オーバーラミネートシートにインク受容層
の形成方法としては、インク受容層用塗工液をバーコー
ター、ブレードコーター、エアナイフコーター、ロ−ル
コ−タ−、グラビアコーター、ダイコーター、カーテン
コーター等の塗工方式で塗布乾燥して形成される。イン
クジェット方式による記録は、記録するプリンターに応
じてロール状、平判状の形態でオーバーラミネートシー
トを供給するとよい。コアシートもロール状であって
も、平判状であってもよい。Next, a method of manufacturing the above card will be described. As a method for forming the ink receiving layer on the over-laminated sheet, a coating method for the ink receiving layer is applied by a bar coater, a blade coater, an air knife coater, a roll coater, a gravure coater, a die coater, a curtain coater, or the like. And dried. In the recording by the ink jet method, it is preferable to supply the over-laminated sheet in a roll shape or a plain format according to the printer to be recorded. The core sheet may be in the form of a roll or a plain sheet.
【0060】本発明(11)は、透明ないし半透明の基
材である連続するオーバーラミネートシートの片面に、
インク受容層を塗布乾燥して形成し、これにインクジェ
ット方式で記録を行った後、カードの大きさに切断し、
該記録を行った面とカードの大きさのコアシートが対向
して積層一体化することを特徴とするカードの製造方法
である。この方法は、オーバーラミネートシートが連続
したシートとして供給されるので、プリンター内でのシ
ート詰まりが殆どなく、好ましい製造方法である。The present invention (11) relates to a method in which a transparent or translucent substrate, a continuous overlaminate sheet,
An ink receiving layer is formed by coating and drying, and after performing recording on the ink receiving layer by an ink jet method, cutting into a card size,
A card manufacturing method characterized in that a surface on which the recording is performed and a core sheet having a size of the card are laminated and integrated so as to face each other. This method is a preferable manufacturing method since the over-laminated sheet is supplied as a continuous sheet, and there is almost no sheet clogging in the printer.
【0061】本発明(12)は、透明ないし半透明の基
材である連続するオーバーラミネートシートの片面に、
インク受容層を塗布乾燥して形成し、これにインクジェ
ット方式で記録を行った後、該記録を行った面と連続す
るコアシートが対向して積層一体化した後、カードの大
きさに切断することを特徴とするカードの製造方法であ
る。この方法は、連続したコアシートとオーバーラミネ
ートシートを積層一体化後、カードの大きさに切断する
ので、微細な寸歩合わせが必要なく製造できるので、製
造速度を速くすることができる。The present invention (12) relates to a method in which a transparent or translucent base material having a continuous overlaminated sheet is
An ink receiving layer is formed by coating and drying, and after recording is performed on the ink receiving layer by an ink jet method, a continuous core sheet is opposed to the recording surface and laminated and integrated, and then cut into a card size. A method for manufacturing a card, characterized in that: According to this method, a continuous core sheet and an over-laminated sheet are laminated and integrated, and then cut to the size of a card. Thus, the production can be performed without the necessity of fine step-by-step, so that the production speed can be increased.
【0062】本発明(13)は、透明ないし半透明の基
材である連続するオーバーラミネートシートの片面に、
インク受容層を塗布乾燥して形成した後、カードの大き
さに切断し、これにインクジェット方式で記録を行った
後、該記録を行った面とカードの大きさのコアシートが
対向して積層一体化することを特徴とするカードの製造
方法である。この方法は、カード状のオーバーラミネー
トシートにインクジェット方式で記録するので、後から
切断する場合に比べ、位置合わせ等に精密さが要求され
るが、図柄の途中で切断されるようなことが生じないの
で、好ましい。The present invention (13) relates to a method in which one side of a continuous overlaminate sheet as a transparent or translucent substrate is
After the ink receiving layer is formed by coating and drying, it is cut into the size of a card, and after recording on this by an ink jet method, the recording side and the core sheet of the size of the card are laminated facing each other. A card manufacturing method characterized by being integrated. Since this method records on a card-shaped over-laminated sheet using the inkjet method, precision is required for positioning, etc., compared to cutting afterwards, but cuts may occur in the middle of the design. Not preferred.
【0063】本発明(14)は、インク受容層にインク
ジェット方式で鏡像印刷する(11)〜(13)記載の
カードの製造方法である。発明(11)〜(13)のカ
ードの製造方法において、インク受容層にインクジェッ
ト方式で鏡像印刷することを規定する。The present invention (14) is the method for producing a card according to (11) to (13), wherein mirror image printing is performed on the ink receiving layer by an ink jet method. In the method for producing a card according to any one of the inventions (11) to (13), it is specified that mirror printing is performed on the ink receiving layer by an inkjet method.
【0064】本発明(15)は、オーバーラミネートシ
ートとコアシートの積層一体化が、熱圧着することによ
る(11)〜(14)記載のカードの製造方法である。
発明(11)〜(14)のカードの製造方法において、
オーバーラミネートシートとコアシートの積層一体化
が、熱圧着すること規定する。熱圧着による積層一体化
が、オーバーラミネートシート、インク受容層とコアシ
ートの密着性が極めて優れるので好ましい。コアシート
が、塩化ビニルを含有する樹脂フィルム、非結晶性のポ
リエステルフィルムを用いると、積層一体化の際に接着
剤などを用いることなく熱圧着できるので効率よく製造
でき、好ましい。The present invention (15) is the method for producing a card according to any one of (11) to (14), wherein the lamination and integration of the overlaminate sheet and the core sheet are performed by thermocompression bonding.
In the card manufacturing methods of the inventions (11) to (14),
It specifies that the lamination and integration of the over-laminated sheet and the core sheet are thermocompression bonded. Lamination integration by thermocompression bonding is preferred because the adhesion between the overlaminated sheet, the ink receiving layer and the core sheet is extremely excellent. If a resin film containing vinyl chloride or a non-crystalline polyester film is used as the core sheet, thermocompression bonding can be performed without using an adhesive or the like at the time of lamination and integration, so that the core sheet can be efficiently produced and is preferable.
【0065】本発明(16)は、コアシートとオーバー
ラミネートシートの間に、2〜50μmの厚さのシート
状接着剤を介して熱圧着する(11)〜(15)記載の
カードの製造方法である。発明(11)〜(15)のカ
ードの製造方法において、コアシートとオーバーラミネ
ートシートの間に、2〜300μmの厚さのシート状接
着剤を介しての熱圧着することを規定する。コアシート
が塩化ビニルを含有する樹脂フィルム、非結晶性のポリ
エステルフィルム、およびABS樹脂フィルム以外の場
合や、インク受容層の成分により塩化ビニルを含有する
樹脂フィルム、非結晶性のポリエステルフィルム、およ
びABS樹脂フィルムであっても密着性が不十分である
場合、シート状接着剤を用いて熱圧着による積層一体化
が好ましい。The present invention (16) provides a method for producing a card according to (11) to (15), wherein the core sheet and the over-laminated sheet are thermocompression-bonded via a sheet-like adhesive having a thickness of 2 to 50 μm. It is. In the card manufacturing methods of the inventions (11) to (15), it is specified that a thermocompression bonding is performed between a core sheet and an overlaminated sheet via a sheet adhesive having a thickness of 2 to 300 μm. When the core sheet is other than a resin film containing vinyl chloride, a non-crystalline polyester film, and an ABS resin film, or a resin film containing vinyl chloride, a non-crystalline polyester film, and ABS depending on the components of the ink receiving layer. When the adhesion is insufficient even with a resin film, lamination and integration by thermocompression bonding using a sheet adhesive is preferable.
【0066】(11)〜(16)記載のカードの製造方
法であって、カードが非接触式及び/又は接触式ICカ
ードであることが好ましい。非接触式、接触式、そして
非接触式と接触式の両方式を採用したICカードは、保
有できる情報量が多く、リーダーライタにより読み取り
書き込みが行えるのでカードとして特に好ましい態様で
ある。In the method for producing a card according to any one of (11) to (16), the card is preferably a non-contact type and / or contact type IC card. An IC card employing a non-contact type, a contact type, or both a non-contact type and a contact type is a particularly preferable embodiment as a card because it can hold a large amount of information and can be read and written by a reader / writer.
【0067】次に、カードの製造装置について説明す
る。本発明(17)は、連続するコアシートを供給する
コアシート供給手段、透明又は半透明の基材で、その片
面にインク受容層を有する連続するオーバーラミネート
シートを供給するオーバーラミネートシート供給手段、
オーバーラミネートシートのインク受容層にインクジェ
ット方式により記録を行うインクジェット記録手段、コ
アシートとオーバーラミネートシートのインク受容層面
を積層一体化する一体化手段、一体化した積層シートを
カードの大きさに切断する切断手段を有することを特徴
とするカードの製造装置である。図5において、連続す
るコアシート13を供給するコアシート供給手段12、
透明又は半透明の基材で、その片面にインク受容層(図
示せず。図中a面)を有する連続するオーバーラミネー
トシート15を供給するオーバーラミネートシート供給
手段14、オーバーラミネートシートのインク受容層に
インクジェット方式により記録を行うインクジェット記
録手段16、コアシートとオーバーラミネートシートの
インク受容層面を積層一体化する一体化手段17、一体
化した積層シートをカードの大きさに切断する切断手段
18を有することを特徴とするカードの製造装置11で
ある。Next, a card manufacturing apparatus will be described. The present invention (17) provides a core sheet supply means for supplying a continuous core sheet, an over laminate sheet supply means for supplying a continuous over laminate sheet having an ink receiving layer on one surface of a transparent or translucent substrate,
Ink jet recording means for performing recording on the ink receiving layer of the overlaminated sheet by an ink jet method, integrating means for laminating and integrating the ink receiving layer surface of the core sheet and the overlaminated sheet, and cutting the integrated laminated sheet into a card size. An apparatus for manufacturing a card, comprising cutting means. In FIG. 5, a core sheet supply means 12 for supplying a continuous core sheet 13;
Over-laminated sheet supply means 14 for supplying a continuous over-laminated sheet 15 which is a transparent or translucent substrate and has an ink receiving layer (not shown; a side in the figure) on one side, an ink receiving layer of the over laminated sheet Recording means 16 for performing recording by an ink jet method, an integrating means 17 for laminating and integrating the ink receiving layer surfaces of the core sheet and the over-laminated sheet, and a cutting means 18 for cutting the integrated laminated sheet into a card size. A card manufacturing apparatus 11 characterized in that:
【0068】本発明(18)は、カード状のコアシート
を供給するコアシート供給手段、透明又は半透明の基材
で、その片面にインク受容層を有する連続するオーバー
ラミネートシートを供給するオーバーラミネートシート
供給手段、オーバーラミネートシートのインク受容層に
インクジェット方式により記録を行うインクジェット記
録手段、オーバーラミネートシートをカードの大きさに
切断する切断手段、コアシートとオーバーラミネートシ
ートのインク受容層面を積層一体化する一体化手段を有
することを特徴とするカードの製造装置である。図6に
おいて、カード状のコアシート33を供給するコアシー
ト供給手段32、透明又は半透明の基材で、その片面に
インク受容層(図示せず。図中a面)を有する連続する
オーバーラミネートシート35を供給するオーバーラミ
ネートシート供給手段34、オーバーラミネートシート
のインク受容層にインクジェット方式により記録を行う
インクジェット記録手段36、オーバーラミネートシー
トをカードの大きさに切断する切断手段38、コアシー
トとオーバーラミネートシートのインク受容層面を積層
一体化する一体化手段37を有することを特徴とするカ
ードの製造装置31である。The present invention (18) relates to a core sheet supplying means for supplying a card-shaped core sheet, and an overlamination for supplying a continuous overlaminate sheet having an ink receiving layer on one side of a transparent or translucent substrate. Sheet supply means, ink jet recording means for performing recording on the ink receiving layer of the over-laminated sheet by the ink jet method, cutting means for cutting the over-laminated sheet into a card size, lamination and integration of the core sheet and the ink-receiving layer surface of the over-laminated sheet An apparatus for manufacturing a card, comprising an integrated means for performing the above. In FIG. 6, a core sheet supply means 32 for supplying a card-shaped core sheet 33, a continuous overlaminate made of a transparent or translucent base material having an ink receiving layer (not shown; a side in the figure) on one side thereof. Over-laminated sheet supply means 34 for supplying the sheet 35, ink-jet recording means 36 for performing recording on the ink-receiving layer of the over-laminated sheet by an ink-jet method, cutting means 38 for cutting the over-laminated sheet into a card size, core sheet and over-sheet A card manufacturing apparatus 31 having an integrating means 37 for laminating and integrating an ink receiving layer surface of a laminate sheet.
【0069】本発明(19)は、カード状のコアシート
を供給するコアシート供給手段、透明又は半透明の基材
で、その片面にインク受容層を有するカード状のオーバ
ーラミネートシートを供給するオーバーラミネートシー
ト供給手段、オーバーラミネートシートのインク受容層
にインクジェット方式により記録を行うインクジェット
記録手段、コアシートとオーバーラミネートシートのイ
ンク受容層面を積層一体化する一体化手段を有すること
を特徴とするカードの製造装置である。図7において、
カード状のコアシート53を供給するコアシート供給手
段52、透明又は半透明の基材で、その片面にインク受
容層(図示せず。図中a面)を有するカード状のオーバ
ーラミネートシート55を供給するオーバーラミネート
シート供給手段54、オーバーラミネートシートのイン
ク受容層にインクジェット方式により記録を行うインク
ジェット記録手段56、コアシートとオーバーラミネー
トシートのインク受容層面を積層一体化する一体化手段
57を有することを特徴とするカードの製造装置であ
る。The present invention (19) relates to a core sheet supply means for supplying a card-shaped core sheet, a transparent or translucent base material for supplying a card-shaped over-laminated sheet having an ink receiving layer on one side thereof. A card having a laminate sheet supply means, an ink jet recording means for performing recording on the ink receiving layer of the over laminate sheet by an ink jet method, and an integrating means for laminating and integrating the ink receiving layer surface of the core sheet and the over laminate sheet. Manufacturing equipment. In FIG.
A core sheet supply means 52 for supplying a card-shaped core sheet 53, a card-shaped over-laminated sheet 55 made of a transparent or translucent base material and having an ink receiving layer (not shown; a side in the figure) on one side thereof. An over-laminated sheet supply means 54 for supplying, an ink-jet recording means 56 for performing recording on the ink-receiving layer of the over-laminated sheet by an ink-jet method, and an integrating means 57 for laminating and integrating the core sheet and the ink-receiving layer surface of the over-laminated sheet. An apparatus for manufacturing a card, characterized in that:
【0070】本発明(20)は、オーバーラミネートシ
ート供給手段とインクジェット記録手段を二つずつ有
し、コアシートの両面にオーバーラミネートシートのイ
ンク受容層面を積層一体化する一体化手段を有する(1
7)〜(19)記載のカードの製造装置である。発明
(17)〜(20)のカードの製造装置において、オー
バーラミネートシート供給手段とインクジェット記録手
段を二つずつ有し、コアシートの両面にオーバーラミネ
ートシートのインク受容層面を積層一体化すると、両面
にインクジェット方式により形成された記録を有するカ
ードの製造装置となる。The present invention (20) has two means for supplying an over-laminated sheet and two ink-jet recording means, and has an integrating means for laminating and integrating the ink receiving layer surface of the over-laminated sheet on both sides of the core sheet.
7) A card manufacturing apparatus according to any one of 7) to (19). In the card manufacturing apparatus according to any one of the inventions (17) to (20), two over-laminated sheet supply means and two ink jet recording means are provided, and the ink receiving layer surface of the over-laminated sheet is laminated and integrated on both sides of the core sheet. A card manufacturing apparatus having a record formed by an inkjet method.
【0071】本発明(21)は、コアシートがその内部
あるいは表面にICチップおよびアンテナを有する(1
7)〜(20)記載のカードの製造装置である。発明
(17)〜(20)のカードの製造装置において、カー
ドが非接触式及び/又は接触式ICカードであることを
規定する。非接触式、接触式、そして非接触式と接触式
の両方式を採用したICカードは、保有できる情報量が
多く、リーダーライタにより読み取り書き込みが行える
のでカードとして特に好ましい態様である。According to the present invention (21), the core sheet has an IC chip and an antenna inside or on the surface thereof (1).
7) A card manufacturing apparatus according to any one of 7) to (20). In the card manufacturing apparatus of the inventions (17) to (20), it is specified that the card is a non-contact type and / or a contact type IC card. An IC card employing a non-contact type, a contact type, or both a non-contact type and a contact type is a particularly preferable embodiment as a card because it can hold a large amount of information and can be read and written by a reader / writer.
【0072】本発明(22)は、ICチップに情報を読
み取り或いは書き込む為のリーダ・ライタ手段を有する
(21)記載のカード製造装置である。カードの製造装
置内にリーダ・ライタ21,41,61を設けることに
より、効率良くICカードを製造することができる。リ
ーダ・ライタで読み取りし、不良があったICカードを
取り除く手段、カードに刻印手段などを付与することが
好ましい。The present invention (22) is the card manufacturing apparatus according to (21), further comprising reader / writer means for reading or writing information on or from an IC chip. By providing the reader / writers 21, 41, 61 in the card manufacturing apparatus, an IC card can be manufactured efficiently. It is preferable to provide means for reading out a defective IC card by reading with a reader / writer and engraving means for the card.
【0073】更に、発明(17)〜(22)のカード製
造装置において、シート状接着剤をコアシートとオーバ
ーラミネートシートの間に挿入する手段を配置すること
もできる。また、コアシート、オーバーラミネートシー
トを積層一体化する前に、塵などを除去する手段を配置
することが好ましい。例えば、エアーにより塵を除去す
るほか、粘着ロールや粘着テープで塵を取る方法も採用
できる。なお、コアシート、オーバーラミネートシート
には、インクジェット方式の記録の視認を妨げない範囲
で、印刷(例えばオフセット印刷)を施すこともでき
る。Further, in the card manufacturing apparatus of the inventions (17) to (22), means for inserting the sheet-like adhesive between the core sheet and the over-laminated sheet may be arranged. Before laminating and integrating the core sheet and the overlaminate sheet, it is preferable to arrange means for removing dust and the like. For example, besides removing dust with air, a method of removing dust with an adhesive roll or adhesive tape can also be adopted. In addition, printing (for example, offset printing) can be performed on the core sheet and the over-laminated sheet within a range that does not hinder the visual recognition of the ink jet recording.
【0074】[0074]
【実施例】以下に、実施例を示し、本発明をより具体的
に説明するが、もちろんこれらに限定されるものではな
い。また、特に断らない限り例中の部および%はそれぞ
れ重量部および重量%を示す。EXAMPLES The present invention will be described below in more detail with reference to Examples, but it should be understood that the present invention is by no means restricted thereto. Unless otherwise specified, parts and% in the examples are parts by weight and% by weight, respectively.
【0075】実施例1 (1)コアシートの作成 厚さ188μmの不透明PETフィルム(製品名:UP2
W、帝人ディュポン社製)を使用した。このフィルムに
厚さ35μm銅箔アンテナ回路をエッチング法で形成し
た。さらに、高さ20μmの接続用バンプを印刷したI
Cチップ(4mm×4mm、250μm厚さ)を厚さ50
μmの異方導電性フィルム接着剤(製品名:FC161
A、日立化成製)を用いて前記アンテナ回路の端子部に
接続してインレットを得た。このインレットシートの両
側を厚さ200μmのシート状ホットメルト接着剤(製
品名:アロンメルトPES−111EEW、東亞合成
製)で挟み、さらにその外側を300μmの2枚の白色
PET−Gフィルム(製品名:PG−WHI、三菱樹脂
製)で挟み、端部を粘着テープで仮留めし、コアシート
となる短冊を作成した。Example 1 (1) Preparation of a core sheet An opaque PET film having a thickness of 188 μm (product name: UP2)
W, Teijin Dupont). A 35 μm thick copper foil antenna circuit was formed on this film by an etching method. Further, the I bump printed with a connection bump having a height of 20 μm
C chip (4mm × 4mm, 250μm thickness) with thickness 50
μm anisotropic conductive film adhesive (Product name: FC161
A, manufactured by Hitachi Chemical Co., Ltd.) to obtain an inlet. Both sides of this inlet sheet are sandwiched by a 200-μm-thick sheet-like hot-melt adhesive (product name: Aronmelt PES-111EEW, manufactured by Toagosei Co., Ltd.), and the outside thereof is further coated with two 300-μm white PET-G films (product name: (PG-WHI, manufactured by Mitsubishi Plastics), and the ends were temporarily fastened with an adhesive tape to prepare a strip serving as a core sheet.
【0076】(2)オーバーラミネートシートの作成 厚さ100μmの透明PET−Gフィルム(製品名:P
G−CHI、三菱樹脂製)の片面に、アンカー層として
ポリエステル樹脂(ポリメントSK−1000、日本触
媒製)を2g/m2塗工し、下記の組成からなるインク
受容層用塗液を乾燥後の厚みが20μmとなるように塗
布乾燥してインク受容層を形成し、インクジェット方式
のプリンター(BJC−4651、キャノン製)を用い
てカードの地模様と、カード名、日付、バーコードを鏡
像記録したカード裏面用オーバーラミネートシート
(A)と、顔写真および氏名を鏡像記録したカード表面
用オーバーラミネートシート(B)の、2種類のオーバ
ーラミネートシートを得た。 インク受容層用組成 ・非晶質シリカ(ファインシールX−37、トクヤマ製) 100部 ・ポリビニルアルコール(GL−03、JSR製) 20部 ・シリル変性ポリビニルアルコール (PVA R−1130、クラレ製) 15部(2) Preparation of Over Laminated Sheet A transparent PET-G film having a thickness of 100 μm (product name: P
G-CHI, manufactured by Mitsubishi Plastics Co., Ltd.) is coated with a polyester resin (Polyment SK-1000, manufactured by Nippon Shokubai) at 2 g / m 2 as an anchor layer, and dried with a coating liquid for an ink receiving layer having the following composition. Is applied and dried so as to have a thickness of 20 μm to form an ink receiving layer, and the ground pattern of the card and the card name, date, and barcode are mirror-image-recorded using an inkjet printer (BJC-4651, manufactured by Canon Inc.). There were obtained two types of over-laminated sheets, the over-laminated sheet for the back side of the card (A) and the over-laminated sheet for the front side of the card (B) in which the face photograph and the name were mirror-recorded. Composition for ink receiving layer ・ Amorphous silica (Fine Seal X-37, manufactured by Tokuyama) 100 parts ・ Polyvinyl alcohol (GL-03, manufactured by JSR) 20 parts ・ Silyl-modified polyvinyl alcohol (PVAR-1130, manufactured by Kuraray) 15 Department
【0077】(3)カードの製造 得られたオーバーラミネートシート(A)、(B)の間
に、カードの面付け位置を合せてコアシート短冊をはさ
み、積層物とした。この積層物を熱プレス装置を用いて
熱プレスした。圧縮用金属板として圧縮用金属板(厚さ
1mm、SUS304製、川崎製鉄社製)を使用し、1
20℃まで昇温し、圧力300kPaで圧着した。圧着
後、冷却したのち、打抜き機でカードを打抜き、ICカ
ードを得た。(3) Production of Card A core sheet strip was sandwiched between the obtained over-laminated sheets (A) and (B) with the imposition positions of the cards aligned to form a laminate. This laminate was hot-pressed using a hot press. A compression metal plate (thickness: 1 mm, made of SUS304, manufactured by Kawasaki Steel Corporation) was used as the compression metal plate.
The temperature was raised to 20 ° C. and pressure bonding was performed at a pressure of 300 kPa. After the compression, after cooling, the card was punched by a punching machine to obtain an IC card.
【0078】(4)カードの評価 得られたカードは、先に説明した図3に示した断面構造
を有するものとなっている。全体の平面性が良好で、チ
ップ、アンテナ、コンデンサーパターンなどの表面基材
への浮き上がりもなく、優れた外観を備えていた。ま
た、各積層シート間の層間強度は10N/cm以上と強
く、人手では簡単に剥離することが不可能で良好な層間
強度を持ったカードであることが確かめられた。この層
間強度の規定は「識別カード−物理特性」:JIS X 6301
(1998)に定められおり、同規定に記載される、6N/cm
以上の層間はく離強度を十分満足するものである。記録
像は、鮮明であり、充分実用に耐えるものであった。(4) Evaluation of Card The obtained card has the above-described cross-sectional structure shown in FIG. The overall flatness was good, the chip, the antenna, the capacitor pattern, etc., did not float on the surface substrate, and had an excellent appearance. In addition, the interlayer strength between the laminated sheets was as high as 10 N / cm or more, and it was confirmed that the card was not easily peelable by hand and had good interlayer strength. The definition of the interlayer strength is "Identification card-physical characteristics": JIS X 6301
(1998) and described in the same regulations, 6N / cm
The above-mentioned interlayer peeling strength is sufficiently satisfied. The recorded image was clear and sufficiently usable.
【0079】実施例2 (1)コアシートの作成 実施例1と全く同様の手法でコアシートを作成した。 (2)オーバーラミネートシートの作成 厚さ50μmの透明PETフィルム(製品名:帝人テト
ロンフィルムGE、帝人デュポン製)の片面に、アンカ
ー層としてポリエステル樹脂(ポリメントSK−100
0、日本触媒製)を2g/m2塗工し、下記の組成から
なるインク受容層用塗液を乾燥後の厚みが20μmとな
るように塗布乾燥してインク受容層を形成し、インクジ
ェット方式のプリンター(BJC−4651、キャノン
製)を用いてカードの地模様と、カード名、日付、バー
コードを鏡像記録したカード裏面用オーバーラミネート
シート(A)と、顔写真および氏名を鏡像記録したカー
ド表面用オーバーラミネートシート(B)の、2種類の
オーバーラミネートシートを得た。 インク受容層用組成 ・非晶質シリカ(ファインシールX−37、トクヤマ製) 100部 ・ポリビニルアルコール(GL−03、JSR製) 20部 ・シリル変性ポリビニルアルコール (PVA R−1130、クラレ製) 15部Example 2 (1) Preparation of a core sheet A core sheet was prepared in exactly the same manner as in Example 1. (2) Preparation of over-laminated sheet A polyester resin (Polyment SK-100) was used as an anchor layer on one side of a transparent PET film (product name: Teijin Tetron Film GE, manufactured by Teijin Dupont) having a thickness of 50 μm.
0, manufactured by Nippon Shokubai Co., Ltd.) at 2 g / m 2, and a coating liquid for an ink receiving layer having the following composition was applied and dried so as to have a thickness of 20 μm after drying to form an ink receiving layer. Using a printer (BJC-4651, manufactured by Canon Inc.), an over-laminated sheet (A) for the back of the card on which the card name, date, and barcode are mirror-image-recorded, and a card on which the face photograph and the name are mirror-image-recorded Two types of over-laminated sheets, that is, an over-laminated sheet for surface (B) were obtained. Composition for ink receiving layer ・ Amorphous silica (Fine Seal X-37, manufactured by Tokuyama) 100 parts ・ Polyvinyl alcohol (GL-03, manufactured by JSR) 20 parts ・ Silyl-modified polyvinyl alcohol (PVAR-1130, manufactured by Kuraray) 15 Department
【0080】(3)カードの製造 カードの面付け位置を合せて、上からオーバーラミネー
トシート(A)、厚さ200μmのシート状ホットメル
ト接着剤(製品名:アロンメルトPES−111EE
W、東亞合成製)、コアシート、厚さ200μmのシー
ト状ホットメルト接着剤(製品名:アロンメルトPES
−111EEW、東亞合成製)、オーバーラミネートシ
ート(B)順に積層し、積層物とした。この積層物を実
施例1と同条件で熱プレスし、打抜き機でカードを打抜
き、ICカードを得た。 (4)カードの評価 得られたカードは、先に説明した図4に示した断面構造
を有するものとなっている。全体の平面性が良好で、チ
ップ、アンテナ、コンデンサーパターンなどの表面基材
への浮き上がりもなく、優れた外観を備えていた。ま
た、各積層シート間の層間強度は10N/cm以上と強
く、人手では簡単に剥離することが不可能で良好な層間
強度を持ったカードであることが確かめられた。この層
間強度の規定は「識別カード−物理特性」:JIS X 6301
(1998)に定められおり、同規定に記載される、6N/cm
以上の層間はく離強度を十分満足するものである。記録
像は、鮮明であり、充分実用に耐えるものであった。(3) Manufacture of Cards The imposition positions of the cards were aligned, and the overlaminated sheet (A) and a 200 μm thick sheet-like hot melt adhesive (product name: Aronmelt PES-111EE) were placed from above.
W, manufactured by Toagosei Co., Ltd., a core sheet, a 200 μm thick sheet-like hot melt adhesive (product name: Aronmelt PES)
-111EEW, manufactured by Toagosei Co., Ltd.) and an overlaminate sheet (B) in this order to form a laminate. This laminate was hot-pressed under the same conditions as in Example 1, and a card was punched out with a punching machine to obtain an IC card. (4) Evaluation of Card The obtained card has the above-described cross-sectional structure shown in FIG. The overall flatness was good, the chip, the antenna, the capacitor pattern, etc., did not float on the surface substrate, and had an excellent appearance. In addition, the interlayer strength between the laminated sheets was as high as 10 N / cm or more, and it was confirmed that the card was not easily peelable by hand and had good interlayer strength. The definition of the interlayer strength is "Identification card-physical characteristics": JIS X 6301
(1998) and described in the same regulations, 6N / cm
The above-mentioned interlayer peeling strength is sufficiently satisfied. The recorded image was clear and sufficiently usable.
【0081】実施例3 (1)コアシートの作成 実施例1と同様にしてコアシートを得た。 (2)オーバーラミネートシートの作成 インク受容層の厚みが8μmとなるように塗布乾燥した
以外は実施例1と同様にして2種類のオーバーラミネー
トシートを得た。 (3)カードの製造 実施例1と同様にしてICカードを得た。 (4)カードの評価 得られたカードは、先に説明した図3に示した断面構造
を有するものとなっている。全体の平面性が良好で、チ
ップ、アンテナ、コンデンサーパターンなどの表面基材
への浮き上がりもなく、優れた外観を備えていた。ま
た、基材とインレットの層間強度は10N/cm以上と強
く、人手では簡単に剥離することが不可能で良好な層間
強度を持ったカードであることが確かめられた。この層
間強度の規定は「識別カード−物理特性」:JIS X 6301
(1998)に定められおり、同規定に記載される、6N/cm
以上の層間はく離強度を十分満足するものである。記録
像は、鮮明であり、充分実用に耐えるものであった。Example 3 (1) Preparation of Core Sheet A core sheet was obtained in the same manner as in Example 1. (2) Preparation of Overlaminated Sheet Two types of overlaminated sheets were obtained in the same manner as in Example 1 except that the ink receiving layer was applied and dried so that the thickness of the ink receiving layer was 8 μm. (3) Production of Card An IC card was obtained in the same manner as in Example 1. (4) Evaluation of Card The obtained card has the cross-sectional structure shown in FIG. 3 described above. The overall flatness was good, the chip, the antenna, the capacitor pattern, etc., did not float on the surface substrate, and had an excellent appearance. In addition, the interlayer strength between the base material and the inlet was as high as 10 N / cm or more, and it was confirmed that the card had good interlayer strength because it could not be easily peeled off manually. The definition of the interlayer strength is "Identification card-physical characteristics": JIS X 6301
(1998) and described in the same regulations, 6N / cm
The above-mentioned interlayer peeling strength is sufficiently satisfied. The recorded image was clear and sufficiently usable.
【0082】比較例1 (1)コアシートの作成 実施例1と同様にしてコアシートを得た。 (2)オーバーラミネートシートの作成 インク受容層の厚みが2μmとなるように塗布乾燥した
以外は実施例1と同様にして2種類のオーバーラミネー
トシートを得た。 (3)カードの製造 実施例1と同様にしてICカードを得た。 (4)カードの評価 得られたカードは、先に説明した図3に示した断面構造
を有するものとなっている。全体の平面性が良好で、チ
ップ、アンテナ、コンデンサーパターンなどの表面基材
への浮き上がりもなく、優れた外観を備えていた。ま
た、基材とインレットの層間強度は10N/cm以上と強
く、人手では簡単に剥離することが不可能で良好な層間
強度を持ったカードであることが確かめられた。この層
間強度の規定は「識別カード−物理特性」:JIS X 6301
(1998)に定められおり、同規定に記載される、6N/c
m以上の層間はく離強度を十分満足するものである。し
かしながら記録像には、滲みが生じており、画像の判
読、文字の読取が不可能な状態であった。Comparative Example 1 (1) Preparation of Core Sheet A core sheet was obtained in the same manner as in Example 1. (2) Preparation of Overlaminated Sheet Two types of overlaminated sheets were obtained in the same manner as in Example 1 except that the ink receiving layer was applied and dried so as to have a thickness of 2 μm. (3) Production of Card An IC card was obtained in the same manner as in Example 1. (4) Evaluation of Card The obtained card has the cross-sectional structure shown in FIG. 3 described above. The overall flatness was good, the chip, the antenna, the capacitor pattern, etc., did not float on the surface substrate, and had an excellent appearance. In addition, the interlayer strength between the base material and the inlet was as high as 10 N / cm or more, and it was confirmed that the card had good interlayer strength because it could not be easily peeled off manually. The definition of the interlayer strength is "Identification card-physical characteristics": JIS X 6301
6N / c as defined in (1998)
The interlayer peeling strength of m or more is sufficiently satisfied. However, bleeding occurred in the recorded image, making it impossible to read the image and read the characters.
【0083】比較例2 (1)コアシートの作成 実施例1と同様にしてコアシートを得た。 (2)オーバーラミネートシートの作成 インク受容層の厚みが60μmとなるように塗布乾燥
(二度塗り)した以外は実施例1と同様にして2種類の
オーバーラミネートシートを得た。 (3)カードの製造 実施例1と同様にしてICカードを得た。 (4)カードの評価 得られたカードは、先に説明した図3に示した断面構造
を有するものとなっている。全体の平面性が良好で、チ
ップ、アンテナ、コンデンサーパターンなどの表面基材
への浮き上がりもなく、優れた外観を備えていた。層間
剥離試験では受容層内部での破壊が認められ、強度は5N
/cmと弱く、人手ではやや簡単に剥離することができ、
「識別カード−物理特性」:JIS X 6301(1998)に定め
らた6N/cm以上の層間はく離強度を満足することがで
きなかった。また、記録像は不鮮明であり、インクジェ
ットインクがオーバーラミネートシート近傍まで到達し
ていない状態であった。Comparative Example 2 (1) Preparation of Core Sheet A core sheet was obtained in the same manner as in Example 1. (2) Preparation of Overlaminated Sheet Two types of overlaminated sheets were obtained in the same manner as in Example 1 except that the ink receiving layer was applied and dried (twice-coated) so that the thickness of the ink receiving layer became 60 μm. (3) Production of Card An IC card was obtained in the same manner as in Example 1. (4) Evaluation of Card The obtained card has the cross-sectional structure shown in FIG. 3 described above. The overall flatness was good, the chip, the antenna, the capacitor pattern, etc., did not float on the surface substrate, and had an excellent appearance. In the delamination test, destruction inside the receiving layer was observed, and the strength was 5 N
/ Cm, which is weak and can be easily peeled off by hand.
"Identification card-physical properties": The delamination strength of 6 N / cm or more specified in JIS X 6301 (1998) could not be satisfied. Further, the recorded image was unclear, and the ink jet ink did not reach the vicinity of the overlaminated sheet.
【0084】[0084]
【発明の効果】以上に説明したように本発明によれば、
インクジェット印刷によって、夫々に異なる氏名、会員
番号、顔写真、バーコード等の固有情報を付与した磁気
カード、IDカード、クレジットカード、ICカード、
タグなどを容易に作成することが可能となり、個々の識
別を確実に行うことのできる識別媒体、識別媒体の作成
方法、および識別媒体作成装置を提供することができ
る。According to the present invention as described above,
A magnetic card, an ID card, a credit card, an IC card, each of which is provided with unique information such as a name, a member number, a face photograph, a barcode, etc.
A tag or the like can be easily created, and an identification medium, an identification medium creating method, and an identification medium creating apparatus that can reliably perform individual identification can be provided.
【図1】図1は、本発明のカードの一実施態様である。FIG. 1 is an embodiment of a card of the present invention.
【図2】図2は、本発明のカードの別の実施態様であ
る。FIG. 2 is another embodiment of the card of the present invention.
【図3】図3は、本発明のカードの別の実施態様であ
る。FIG. 3 is another embodiment of the card of the present invention.
【図4】図4は、本発明のカードの別の実施態様であ
る。FIG. 4 is another embodiment of the card of the present invention.
【図5】図5は、本発明のカードの製造装置を説明する
概略図である。FIG. 5 is a schematic diagram illustrating a card manufacturing apparatus according to the present invention.
【図6】図6は、本発明のカードの製造装置を説明する
概略図である。FIG. 6 is a schematic diagram illustrating a card manufacturing apparatus of the present invention.
【図7】図7は、本発明のカードの製造装置を説明する
概略図である。FIG. 7 is a schematic diagram illustrating a card manufacturing apparatus according to the present invention.
1:カード 2:コアシート 3,3’:オーバーラミネートシート 4,4’:インク受容層 5,5’:インクジェット記録 6,6’:接着剤 11,31,51:カード製造装置 12,32,52:コアシート供給手段 13,33,53:コアシート 14,34,54:オーバーラミネートシート供給手段 15,35,55:オーバーラミネートシート 16,36,56:インクジェット記録手段 17,37,57:一体化手段 18,38:切断手段 19,39,59:カード 20,40,60:カード受け 21,41,61:リーダライタ 1: Card 2: Core sheet 3, 3 ': Over laminate sheet 4, 4': Ink receiving layer 5, 5 ': Ink jet recording 6, 6': Adhesive 11, 31, 51: Card manufacturing device 12, 32, 52: core sheet supply means 13, 33, 53: core sheet 14, 34, 54: over laminate sheet supply means 15, 35, 55: over laminate sheet 16, 36, 56: inkjet recording means 17, 37, 57: integrated Conversion means 18, 38: cutting means 19, 39, 59: card 20, 40, 60: card receiver 21, 41, 61: reader / writer
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 FI テーマコート゛(参考) B41M 5/00 B41M 5/00 E G06K 19/00 K G06K 19/077 B41J 3/04 101Z 101Y (72)発明者 田井 靖人 東京都中央区銀座4丁目7番5号 王子製 紙株式会社内 Fターム(参考) 2C005 HB01 JA01 JA08 JA15 JB02 JB08 JB19 JB28 KA01 KA37 LA03 LA19 LA27 LA29 MA11 MB01 MB10 NA02 NA09 NA31 PA01 PA18 QC12 RA04 RA09 RA12 SA14 TA21 TA22 2C056 EA13 EC69 FC06 FD02 HA44 2H086 BA19 BA51 5B035 AA00 BA05 BB00 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) B41M 5/00 B41M 5/00 E G06K 19/00 KG06K 19/077 B41J 3/04 101Z 101Y (72) Inventor Yasuhito Tai 4-7-5 Ginza, Chuo-ku, Tokyo F term in Oji Paper Co., Ltd. 2C005 HB01 JA01 JA08 JA15 JB02 JB08 JB19 JB28 KA01 KA37 LA03 LA19 LA27 LA29 MA11 MB01 MB10 NA02 NA09 NA31 PA01 PA18 QC12 RA04 RA09 RA12 SA14 TA21 TA22 2C056 EA13 EC69 FC06 FD02 HA44 2H086 BA19 BA51 5B035 AA00 BA05 BB00
Claims (22)
トを有するカードにおいて、オーバーラミネートシート
が透明ないし半透明の基材であり、該基材の片面に3〜
50μmのインク受容層を有し、インク受容層にはイン
クジェット方式にて記録が施され、インク受容層面がコ
アシート側になるようにコアシートとオーバーラミネー
トシートが積層一体化され、前記記録がオーバーラミネ
ートシートを透して視認できることを特徴とするカー
ド。1. A card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent base material, and three to three sides are provided on one side of the base material.
It has an ink receiving layer of 50 μm, recording is performed on the ink receiving layer by an ink jet method, and a core sheet and an over laminate sheet are laminated and integrated so that the ink receiving layer surface is on the core sheet side, and the recording is over A card characterized by being visible through a laminate sheet.
トを有するカードにおいて、オーバーラミネートシート
が透明ないし半透明の基材であり、該基材の片面にイン
ク受容層を有し、インク受容層にはインクジェット方式
にて記録が施され、インク受容層面がコアシート側にな
るようにコアシートとオーバーラミネートシートが積層
一体化され、前記記録がオーバーラミネートシートを透
して視認できるカードであって、コアシートとオーバー
ラミネートシートの積層が、熱圧着による積層一体化で
あることを特徴とするカード。2. A card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent substrate, the substrate has an ink receiving layer on one side, and the ink receiving layer has an ink jet system. A recording is performed, a core sheet and an over laminate sheet are laminated and integrated such that the ink receiving layer surface is on the core sheet side, and the recording is a card that can be visually recognized through the over laminate sheet, A card wherein the lamination of the overlaminate sheet is lamination and integration by thermocompression bonding.
トを有するカードにおいて、オーバーラミネートシート
が透明ないし半透明の基材であり、該基材の片面にイン
ク受容層を有し、インク受容層にはインクジェット方式
にて記録が施され、インク受容層面がコアシート側にな
るようにコアシートとオーバーラミネートシートが積層
一体化され、前記記録がオーバーラミネートシートを透
して視認できるカードであって、コアシートとオーバー
ラミネートシートの積層一体化が、コアシートとオーバ
ーラミネートシートの間に挟みこまれた2〜300μm
の厚さの接着剤を介しての積層一体化であることを特徴
とするカード。3. A card having a core sheet and an overlaminate sheet, wherein the overlaminate sheet is a transparent or translucent substrate, the substrate has an ink receiving layer on one side, and the ink receiving layer has an ink jet system. A recording is performed, a core sheet and an over laminate sheet are laminated and integrated such that the ink receiving layer surface is on the core sheet side, and the recording is a card that can be visually recognized through the over laminate sheet, 2 to 300 µm sandwiched between the core sheet and the overlaminated sheet
A card integrated by lamination through an adhesive having a thickness of 3 mm.
トを有するカードにおいて、オーバーラミネートシート
が透明ないし半透明の基材であり、該基材の片面にイン
ク受容層を有し、インク受容層にはインクジェット方式
にて記録が施され、インク受容層面がコアシート側にな
るようにコアシートとオーバーラミネートシートが積層
一体化され、前記記録がオーバーラミネートシートを透
して視認できるカードであって、コアシートが塩化ビニ
ルを含有する樹脂フィルム、非結晶性のポリエステルフ
ィルム、及びABS樹脂フィルムから選ばれる一種であ
ることを特徴とするカード。4. A card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent substrate, the substrate has an ink receiving layer on one side, and the ink receiving layer has an ink jet system. The recording is performed in, the core sheet and the over laminate sheet are laminated and integrated such that the ink receiving layer surface is on the core sheet side, and the recording is a card that can be visually recognized through the over laminate sheet, wherein the core sheet is A card characterized by being one kind selected from a resin film containing vinyl chloride, an amorphous polyester film, and an ABS resin film.
トを有するカードにおいて、オーバーラミネートシート
が透明ないし半透明の基材であり、該基材の片面にイン
ク受容層を有し、インク受容層にはインクジェット方式
にて記録が施され、インク受容層面がコアシート側にな
るようにコアシートとオーバーラミネートシートが積層
一体化され、前記記録がオーバーラミネートシートを透
して視認できるカードであって、オーバーラミネートシ
ートが塩化ビニルを含有する樹脂フィルム、非結晶性の
ポリエステルフィルム、ポリカーボネートフィルム、お
よびABS樹脂フィルムから選ばれる一種であることを
特徴とするカード。5. A card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent substrate, the substrate has an ink receiving layer on one surface, and the ink receiving layer has an ink jet system. A core sheet and an over-laminated sheet are laminated and integrated such that the ink receiving layer surface is on the core sheet side, and the recording is visible through the over-laminated sheet. Is a kind selected from a resin film containing vinyl chloride, an amorphous polyester film, a polycarbonate film, and an ABS resin film.
トを有するカードにおいて、オーバーラミネートシート
が透明ないし半透明の基材であり、該基材の片面にイン
ク受容層を有し、インク受容層にはインクジェット方式
にて記録が施され、インク受容層面がコアシート側にな
るようにコアシートとオーバーラミネートシートが積層
一体化され、前記記録がオーバーラミネートシートを透
して視認できるカードであって、コアシートとオーバー
ラミネートシートが同種のフィルムであることを特徴と
するカード。6. A card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is a transparent or translucent substrate, the substrate has an ink receiving layer on one surface, and the ink receiving layer has an ink jet system. A recording is performed, a core sheet and an over laminate sheet are laminated and integrated such that the ink receiving layer surface is on the core sheet side, and the recording is a card that can be visually recognized through the over laminate sheet. A card wherein the overlaminate sheet is the same type of film.
トを有するカードにおいて、コアシートの両面にオーバ
ーラミネートシートが積層されており、両方のオーバー
ラミネートシートが透明ないし半透明の基材であり、該
基材の片面にインク受容層を有し、且つ、インク受容層
にはインクジェット方式にて記録が施され、インク受容
層面がコアシート側になるようにコアシートと両方のオ
ーバーラミネートシートが積層一体化され、前記記録が
オーバーラミネートシートを透してそれぞれ視認できる
カードであって、両方のオーバーラミネートシートが実
質的に同一の厚みであることを特徴とするカード。7. A card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is laminated on both sides of the core sheet, and both over-laminated sheets are transparent or translucent base materials. Having an ink receiving layer on one side, and recording is performed on the ink receiving layer by an ink jet method, and the core sheet and both over laminate sheets are laminated and integrated such that the ink receiving layer surface is on the core sheet side, A card in which the recording is visible through an over-laminated sheet, wherein both over-laminated sheets have substantially the same thickness.
トを有するカードにおいて、コアシートの両面にオーバ
ーラミネートシートが積層一体化されており、両方のオ
ーバーラミネートシートが透明ないし半透明の基材であ
り、該基材の片面にインク受容層を有し、且つ、インク
受容層にはインクジェット方式にて記録が施され、イン
ク受容層面がコアシート側になるようにコアシートと両
方のオーバーラミネートシートが積層一体化され、前記
記録がオーバーラミネートシートを透してそれぞれ視認
できるカードであって、インク受容層に形成された記録
が片面と他面とで異なることを特徴とするカード。8. A card having a core sheet and an over-laminated sheet, wherein the over-laminated sheet is laminated and integrated on both sides of the core sheet, and both over-laminated sheets are transparent or translucent base materials. The material has an ink receiving layer on one side, and the ink receiving layer is recorded by ink jet method, and the core sheet and both over laminate sheets are laminated and integrated so that the ink receiving layer side is on the core sheet side A card wherein the recording is visible through an over-laminated sheet, wherein the recording formed on the ink receiving layer is different on one side from the other.
用したものである請求項1〜8の何れか一項に記載のカ
ード。9. The card according to claim 1, wherein the ink jet system uses solid ink.
カードである請求項1〜9の何れか一項に記載のカー
ド。10. A non-contact type and / or contact type IC card.
The card according to any one of claims 1 to 9, which is a card.
オーバーラミネートシートの片面に、インク受容層を塗
布乾燥して形成し、これにインクジェット方式で記録を
行った後、カードの大きさに切断し、該記録を行った面
とカードの大きさのコアシートが対向して積層一体化す
ることを特徴とするカードの製造方法。11. An ink-receiving layer is formed by applying and drying an ink-receiving layer on one side of a continuous over-laminated sheet which is a transparent or translucent substrate. A method for manufacturing a card, comprising cutting and recording, and stacking and integrating a core sheet having a size of the card and a surface on which the recording is performed.
オーバーラミネートシートの片面に、インク受容層を塗
布乾燥して形成し、これにインクジェット方式で記録を
行った後、該記録を行った面と連続するコアシートが対
向して積層一体化した後、カードの大きさに切断するこ
とを特徴とするカードの製造方法。12. An ink-receiving layer is formed by coating and drying on one side of a continuous overlaminate sheet as a transparent or translucent substrate, and recording is performed on the ink-receiving layer by an ink jet method, and then the recording is performed. A method for manufacturing a card, comprising cutting a card size after stacking and integrating a core sheet continuous with a surface.
オーバーラミネートシートの片面に、インク受容層を塗
布乾燥して形成した後、カードの大きさに切断し、これ
にインクジェット方式で記録を行った後、該記録を行っ
た面とカードの大きさのコアシートが対向して積層一体
化することを特徴とするカードの製造方法。13. An ink receiving layer is formed by applying and drying an ink-receiving layer on one side of a continuous over-laminated sheet which is a transparent or translucent base material, and then cut into a card size. A method of manufacturing a card, wherein after performing the recording, the surface on which the recording has been performed and the core sheet having the size of the card face each other and are laminated and integrated.
像印刷する請求項11〜13の何れか一項に記載のカー
ドの製造方法。14. The method for producing a card according to claim 11, wherein mirror image printing is performed on the ink receiving layer by an ink jet method.
の積層一体化が、熱圧着することによる請求項11〜1
4の何れか一項に記載のカードの製造方法。15. The method according to claim 11, wherein the lamination and integration of the overlaminate sheet and the core sheet are performed by thermocompression bonding.
The method for producing a card according to any one of claims 4 to 10.
の間に、2〜50μmの厚さのシート状接着剤を介して
熱圧着する請求項11〜14の何れか一項に記載のカー
ドの製造方法。16. The method for producing a card according to claim 11, wherein the card is thermocompression-bonded between the core sheet and the over-laminated sheet via a sheet adhesive having a thickness of 2 to 50 μm.
ト供給手段、透明又は半透明の基材で、その片面にイン
ク受容層を有する連続するオーバーラミネートシートを
供給するオーバーラミネートシート供給手段、オーバー
ラミネートシートのインク受容層にインクジェット方式
により記録を行うインクジェット記録手段、コアシート
とオーバーラミネートシートのインク受容層面を積層一
体化する一体化手段、一体化した積層シートをカードの
大きさに切断する切断手段を有することを特徴とするカ
ードの製造装置。17. A core sheet supply means for supplying a continuous core sheet, an over-lamination sheet supply means for supplying a continuous over-laminate sheet having a transparent or translucent substrate and having an ink receiving layer on one surface thereof, an over-lamination Ink jet recording means for performing recording on the ink receiving layer of the sheet by an ink jet method, integrating means for laminating and integrating the ink receiving layer surfaces of the core sheet and the overlaminated sheet, and cutting means for cutting the integrated laminated sheet into a card size An apparatus for manufacturing a card, comprising:
ート供給手段、透明又は半透明の基材で、その片面にイ
ンク受容層を有する連続するオーバーラミネートシート
を供給するオーバーラミネートシート供給手段、オーバ
ーラミネートシートのインク受容層にインクジェット方
式により記録を行うインクジェット記録手段、オーバー
ラミネートシートをカードの大きさに切断する切断手
段、コアシートとオーバーラミネートシートのインク受
容層面を積層一体化する一体化手段を有することを特徴
とするカードの製造装置。18. A core sheet supply means for supplying a card-shaped core sheet, an over laminate sheet supply means for supplying a continuous over laminate sheet having an ink receiving layer on one surface of a transparent or translucent base material, Ink jet recording means for performing recording on the ink receiving layer of the laminate sheet by the ink jet method, cutting means for cutting the overlaminated sheet into a card size, and integrating means for laminating and integrating the core sheet and the ink receiving layer surface of the overlaminated sheet. An apparatus for manufacturing a card, comprising:
ート供給手段、透明又は半透明の基材で、その片面にイ
ンク受容層を有するカード状のオーバーラミネートシー
トを供給するオーバーラミネートシート供給手段、オー
バーラミネートシートのインク受容層にインクジェット
方式により記録を行うインクジェット記録手段、コアシ
ートとオーバーラミネートシートのインク受容層面を積
層一体化する一体化手段を有することを特徴とするカー
ドの製造装置。19. A core sheet supply means for supplying a card-shaped core sheet, an over-laminated sheet supply means for supplying a card-shaped over-laminated sheet having a transparent or translucent substrate and having an ink receiving layer on one surface thereof, A card manufacturing apparatus, comprising: an ink jet recording means for performing recording on an ink receiving layer of an overlaminated sheet by an ink jet method; and an integrating means for laminating and integrating an ink receiving layer surface of a core sheet and an overlaminated sheet.
ンクジェット記録手段を二つずつ有し、コアシートの両
面にオーバーラミネートシートのインク受容層面を積層
一体化する一体化手段を有する請求項17〜19の何れ
か一項に記載のカードの製造装置。20. An apparatus according to claim 17, comprising two overlaminated sheet supply means and two ink jet recording means, and integrated means for laminating and integrating the ink receiving layer surface of the overlaminated sheet on both sides of the core sheet. An apparatus for manufacturing a card according to claim 1.
Cチップおよびアンテナを有する請求項17〜20の何
れか一項に記載のカードの製造装置。21. A core sheet having an I or I inside or on its surface.
The card manufacturing apparatus according to any one of claims 17 to 20, comprising a C chip and an antenna.
込む為のリーダ・ライタ手段を有する請求項21記載の
カード製造装置。22. The card manufacturing apparatus according to claim 21, further comprising a reader / writer means for reading or writing information on the IC chip.