JP2002283720A - Thermal paper - Google Patents

Thermal paper

Info

Publication number
JP2002283720A
JP2002283720A JP2001082564A JP2001082564A JP2002283720A JP 2002283720 A JP2002283720 A JP 2002283720A JP 2001082564 A JP2001082564 A JP 2001082564A JP 2001082564 A JP2001082564 A JP 2001082564A JP 2002283720 A JP2002283720 A JP 2002283720A
Authority
JP
Japan
Prior art keywords
thermal
layer
formed
paper
printing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
JP2001082564A
Other languages
Japanese (ja)
Inventor
Yoshinori Yamaoka
義紀 山岡
Original Assignee
Kobayashi Kirokushi Co Ltd
小林記録紙株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kobayashi Kirokushi Co Ltd, 小林記録紙株式会社 filed Critical Kobayashi Kirokushi Co Ltd
Priority to JP2001082564A priority Critical patent/JP2002283720A/en
Publication of JP2002283720A publication Critical patent/JP2002283720A/en
Application status is Withdrawn legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To simplify operations for cleaning a head of a printer for a handy terminal(H/T). SOLUTION: In thermal paper 10, a thermal layer 11 is formed on a surface of a base paper material 1, and a printing layer 12 using heat-resistant UV ink is formed on a surface of the thermal layer 11. A self-cleaning layer 20 using colorless, transparent overprint(OP) varnish, to which at least one kind of fine particle selected from among the fine particles of silica, magnesium carbonate, calcium carbonate, a metallic oxide, etc., is added, is formed throughout the surfaces of the layers 11 and 12.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、感熱記録用紙に関し、特に、ハンディターミナル用プリンタに用いられるサーマル用紙に関する。 The present invention relates to relates to a heat-sensitive recording paper, in particular, it relates to a thermal paper used in the printer handy terminal.

【0002】 [0002]

【従来の技術】ハンディターミナル(以下、H/Tと略す)用プリンタは、主にガス、水道、電力の検針などの検針業務に用いられ、その印字方式としては、サーマル印字方式が主流となっている。 BACKGROUND ART handy terminal (hereinafter, H / T abbreviated) printer mainly gas, water, used in meter reading tasks such as power meter reading, as its printing method, a thermal printing method is the mainstream ing.

【0003】このサーマル印字方式は、用紙に形成された感熱記録層をサーマルヘッドなどの加熱手段により加熱して所定情報を印字記録する方式であるが、用紙についた紙粉、ゴミ、手垢などの汚れがサーマルヘッドに付着し、このサーマルヘッドを用いて印字処理を行なった場合、消去不良や印字情報のかすれ等の印字不良が発生し易いため、サーマルヘッドに付着した汚れを定期的に除去するヘッドクリーニングを実施する必要が生じる。 [0003] The thermal printing method, although the heat-sensitive recording layer formed on the sheet by heating by a heating means such as a thermal head is a method of printing and recording the predetermined information, with the sheet paper dust, dirt, such as finger marks dirt adheres to the thermal head, when performing printing processing using the thermal head, liable printing defects such as thin spots occurred erase failure and print information, periodically remove stains adhering to the thermal head necessary to carry out head cleaning occurs.

【0004】ところが、上記H/T用プリンタは小型であり、そのサーマルヘッドは小さく、サーマルヘッドをプリンタから取り外して直接クリーニングすることは極めて困難であるため、クリーニングシート等を通してサーマルヘッドをクリーニングしているのが実情であり、 [0004] However, the H / T printer is compact, the thermal head is small, since it is very difficult to clean directly remove the thermal head from the printer, clean the thermal head through the cleaning sheet, etc. is a fact is that there,
ヘッドクリーニングに別途クリーニングシートを必要とするとともに、クリーニングシート等でもなかなかきれいにサーマルヘッドに付着した汚れが除去できず、定期的にヘッドクリーニングを実施する必要があり手間がかかるため、H/T用プリンタのメンテナンス作業は煩わしいものであった。 While requiring a separate cleaning sheet to a head cleaning can not be easily removed cleanly stains adhered to the thermal head in the cleaning sheet or the like, periodically for labor must be carried out head cleaning is applied, the printer H / T maintenance work were cumbersome.

【0005】 [0005]

【発明が解決しようとする課題】本発明は、上記のような問題点に鑑みてなされたものであり、その目的とするところは、H/T用プリンタに用いられるサーマル用紙において、クリーニング機能を備えたサーマル用紙を提供することにある。 SUMMARY OF THE INVENTION It is an object of the present invention has been made in view of the above problems, it is an object of the thermal paper used for H / T printer, the cleaning function and to provide a thermal paper with.

【0006】 [0006]

【課題を解決するための手段】上記目的を達成するために、本発明に係るサーマル用紙は、ベース紙材表面にサーマル層が形成され、サーマル層表面に耐熱性UVインキによる印刷層が形成されてなるサーマル用紙であって、上記サーマル層および印刷層の表面に、研磨材が添加された無色透明OPニスによるセルフクリーニング層が形成されていることを特徴とする。 To achieve the above object, according to the Invention The thermal paper of the present invention, the thermal layer is formed on the base paper material surface, the printing layer due to the heat resistance UV ink is formed on the thermal layer surface a thermal sheet comprising Te, the surface of the thermal layer and printing layer, wherein the self-cleaning layer is formed by a colorless transparent OP varnish abrasive is added.

【0007】また、本発明に係るサーマル用紙は、上記研磨材は、シリカ、炭酸マグネシウム、炭酸カルシウム、金属酸化物微粒子等から選ばれる少なくとも一つの微細粒子であることを特徴とする。 [0007] The thermal paper of the present invention, the abrasive is silica, magnesium carbonate, calcium carbonate, characterized in that at least one of fine particles selected from metal oxide fine particles.

【0008】また、本発明に係るサーマル用紙は、ベース紙材表面にサーマル層が形成されてなるサーマル用紙であって、上記サーマル層表面に、シリカ、炭酸マグネシウム、炭酸カルシウム、金属酸化物微粒子等から選ばれる少なくとも一つの微細粒子が添加された有色インキにより罫線、文字、地紋、または網点等からなる印刷層が形成されていることを特徴とする。 [0008] The thermal paper of the present invention is a thermal paper comprising a thermal layer is formed on the base paper material surface, in the thermal layer surface, silica, magnesium carbonate, calcium carbonate, metal oxide particles or the like that at least one ruled line by colored ink is added fine particles, letter, background pattern or printed layer formed of halftone dots or the like, it is formed selected from and wherein.

【0009】また、本発明に係るサーマル用紙は、上記セルフクリーニング層が上記サーマル層および印刷層からなる印字領域を除いた非印字領域に限定して形成されていることを特徴とする。 [0009] The thermal paper of the present invention is characterized in that the self-cleaning layer is formed as being limited to the non-printing area excluding the printing area consisting of the thermal layer and print layer.

【0010】また、本発明に係るサーマル用紙は、上記サーマル用紙がハンディターミナル用紙であることを特徴とする。 [0010] The thermal paper of the present invention is characterized in that the thermal paper is handy terminal paper.

【0011】 [0011]

【発明の実施の形態】以下、本発明に係るサーマル用紙の実施形態について添付図面を参照しながら詳細に説明する。 DETAILED DESCRIPTION OF THE INVENTION Hereinafter, embodiments of the thermal paper will be described in detail with reference to the accompanying drawings according to the present invention.

【0012】図1および図2は本発明に係るサーマル用紙をガス料金通知書に適用した第1の実施形態を示すもので、図1は上記通知書の表面を示す平面図、図2は上記通知書の構成を示す断面図である。 [0012] Figures 1 and 2 is a thermal sheet according to the present invention show a first embodiment applied to gas rates notice, 1 is a plan view showing the surface of the notice, 2 above it is a sectional view showing a notice configuration.

【0013】本実施形態におけるガス料金通知書10 [0013] The gas rates notice 10 in the present embodiment
は、図1に示すように、所定項目や罫線からなる印刷層12が形成されており、感熱記録層であるサーマル層1 As shown in FIG. 1, the print layer 12 having a predetermined item and lines are formed, a thermal layer 1 is heat-sensitive recording layer
1には検針日、メーター指示数、使用量、使用料金からなる各種情報がH/T用プリンタにより印字処理されて各家庭に通知されるものである。 Meter reading day to 1, meter indication number, the amount, in which various kinds of information consisting of usage charge is notified is print processing by H / T printer to each household.

【0014】なお、本発明において、上記サーマル層1 [0014] In the present invention, the thermal layer 1
1および印刷層12とからなる領域を印字領域A、上記サーマル層11および印刷層12からなる印字領域Aを除いた領域を非印字領域Bとする。 1 and the printing layer 12. area printing area A consisting of the area excluding the printing area A consisting of the thermal layer 11 and the print layer 12 and the non-printing area B.

【0015】上記通知書10の構成について図2に基づき説明すると、ベース紙材1表面にサーマル層11が形成されている。 [0015] will be described with reference to FIG. 2 the structure of the notification 10, the thermal layer 11 is formed on the base sheet material 1 surface. このサーマル層11は、常温では固体、 The thermal layer 11 is at normal temperature solid,
加熱することで溶融状態になって互いに反応し発色する電子供与体と電子受容体の2つの成分が、固体微粒子として樹脂バインダ中に分散されたものである。 Two components Become a molten state by heating to react with each other color electron donor and the electron acceptor is one which is dispersed in a resinous binder as solid particulates.

【0016】また、上記サーマル層11表面には、所定項目や罫線からなる印刷層12が、耐熱性UVインキによって形成されている。 [0016] The aforementioned thermal layer 11 surface, the printing layer 12 composed of a predetermined item and a ruled line is formed by a heat-resistant UV inks.

【0017】さらに、本実施形態においては、上記サーマル層11および印刷層12の表面全面、すなわち、印字領域Aおよび非印字領域B表面の全面に、セルフクリーニング層20が形成されている。 Furthermore, in the present embodiment, the entire surface of the thermal layer 11 and the print layer 12, i.e., the entire surface of the printing area A and a non-printing area B surface, the self-cleaning layer 20 is formed. このセルフクリーニング層20は、無色透明のオーバープリント(OP)ニスの中に、研磨材が添加された印刷インキを用いて、グラビアコーティング法やオフセット印刷法などの従来公知の塗工方法や印刷方法で塗布またはベタ印刷することによって構成されている。 The self-cleaning layer 20 is in a colorless transparent overprint (OP) varnish, using a printing ink which abrasive is added, conventionally known coating methods and printing methods such as a gravure coating method or an offset printing method in is formed by applying or solid printing.

【0018】上記研磨材としては、シリカ、炭酸マグネシウム、炭酸カルシウム、金属酸化物微粒子などの無機物質の微細粒子のうち少なくとも一つを選択して添加すればよく、また、上記無機物質の微細粒子を複数組み合わせて添加することもできる。 [0018] As the abrasive, silica, magnesium carbonate, calcium carbonate, may be added by selecting at least one of fine particles of inorganic substances such as metal oxide particles, also fine particles of the inorganic substance It may be added in multiple combining.

【0019】また、上記微細粒子の粒子径は、0.1μ [0019] The particle diameter of the fine particles, 0.1 [mu]
m乃至5.0μmの範囲内にあることが好ましい。 It is preferably in the range of m to 5.0 .mu.m. これは、上記粒子径が0.1μm未満の場合には微細粒子の粒子径が小さすぎて研磨材として機能せず十分なクリーニング効果が得られないためであり、上記粒子径が5. This is because when the particle size is less than 0.1μm is for a sufficient cleaning effect can not be obtained does not function as an abrasive too small particle size of the fine particles, the particle diameter of 5.
0μm超過の場合には微細粒子の径が大きすぎてクリーニング時にサーマルヘッドを傷つけてしまう可能性があり好ましくないためである。 In the case of 0μm excess is because it has undesirable possibility that damage the thermal head during cleaning diameter is too large for the fine particles.

【0020】なお、上記微細粒子の添加割合は、1重量部乃至20重量部、上記微細粒子の中では、汚れの吸着性に優れたシリカを用いるとよい。 [0020] The addition rate of the fine particles, 1 part by weight to 20 parts by weight, among the fine particles, preferably used high silica adsorptive fouling.

【0021】また、図示はしないが、セルフクリーニング層20の形態として、上記微細粒子が添加された無色透明のOPニスを用いて印字領域Aおよび非印字領域B Further, although not shown, the form of the self-cleaning layer 20, printing using a colorless transparent OP varnish the fine particles are added region A and non-printing area B
の表面全面に、特定の絵柄、地紋、文字、または網点などをパターン印刷することによって構成されていてもよい。 The entire surface of a particular picture, background pattern, character or may be configured by pattern printing and halftone.

【0022】次に、本発明に係るサーマル用紙の第2の実施形態について図3に基づき説明する。 Next, a second embodiment of the thermal sheet according to the present invention based on FIG. 3 will be described.

【0023】図3は本実施形態におけるサーマル用紙をガス料金通知書に適用した場合の構成を示す断面図である。 [0023] FIG. 3 is a sectional view showing the structure of the thermal sheet in this embodiment is applied to the gas rates notice. なお、上記実施形態と同一の構成については同一の符号を付してその詳細な説明を省略する。 Incidentally, detailed explanation thereof will be denoted by the same reference configuration as the above embodiment.

【0024】本実施形態におけるガス料金通知書10a The gas rates notice 10a in this embodiment
は、図3に示すように、検針日、メーター指示数、使用量、使用料金からなる各種情報欄は上記サーマル層11 As shown in FIG. 3, meter reading day, the meter indication number, amount, various types of information fields composed of a usage fee is the thermal layer 11
により構成され、所定項目、罫線、文字、地紋、または網点などからなる印刷層21にセルフクリーニング機能を持たせたことが特徴である。 It is composed of a predetermined item, borders, text, background pattern or characteristic which gave a self-cleaning function to the printing layer 21 made of halftone dots. すなわち、同図に示すように、ベース紙材1表面にサーマル層11が形成され、 That is, as shown in the figure, the thermal layer 11 is formed on the base sheet material 1 surface,
上記サーマル層11の表面に、汎用の有色の紫外線硬化型インキ、例えば、アクリル系、シリコーン系、フッ素系、エポキシ系樹脂材料の中に、研磨材が添加された印刷インキを用いて、所定項目、罫線、文字、地紋、または網点などからなる印刷層が形成されている。 On the surface of the thermal layer 11, an ultraviolet-curable ink generic colored, for example, acrylic, silicone, fluorine, in the epoxy resin material, using a printing ink which abrasive is added, predetermined items , borders, text, background pattern or printing layer made of halftone dots, are formed. 研磨材としては、上記第1実施形態と同様に、シリカ、炭酸マグネシウム、炭酸カルシウム、金属酸化物微粒子などの無機物質の微細粒子のうちから少なくとも一つを選択して添加する。 The abrasive, as in the first embodiment, silica, magnesium carbonate, calcium carbonate, selected and added at least one from among the fine particles of inorganic substances such as metal oxide particles.

【0025】なお、有色の紫外線硬化型インキに添加する微細粒子の粒子径、添加割合は、上記第1実施形態における微細粒子の粒子径、添加割合と同様である。 [0025] The particle size of the fine particles to be added to the ultraviolet curable ink colored, addition rate, the particle size of the fine particles in the first embodiment, is the same as the addition ratio.

【0026】このように、上記第1および第2実施形態におけるサーマル用紙は、セルフクリーニング層20および印刷層21がともに用紙の最表面に位置し、上記セルフクリーニング層20および印刷層21には、研磨材として無機物質の微細粒子が添加されているため、サーマル印字時にはサーマルヘッドが上記クリーニング層2 [0026] Thus, the thermal paper in the first and second embodiment, located on the outermost surface of both sheets is a self-cleaning layer 20 and the printed layer 21, to the self-cleaning layer 20 and the print layer 21, since the fine particles of inorganic substances are added as an abrasive, thermal print thermal head above the cleaning layer during 2
0または印刷層21に接触し、このとき、サーマルヘッドに付着した用紙についた紙粉、ゴミ、手垢などの汚れがセルフクリーニング層に添加された微細粒子の凹凸の凹部内に吸着されて、サーマルヘッドに付着した汚れが除去される。 Contacting the 0 or printed layer 21, this time, paper dust attached to the sheet adhering to the thermal head, dust, are adsorbed to dirt in the recess of the irregularities of the added fine particles in the self-cleaning layer such as finger marks, thermal dirt adhering to the head is removed. 特に、微細粒子としてシリカが添加されている場合には、シリカの吸着性能によって汚れを除去する効果が大きい。 In particular, when the silica is added, the greater the effect of removing the dirt by the adsorption performance of silica as fine particles.

【0027】したがって、上記各実施形態におけるサーマル用紙を使用すれば、用紙についた紙粉、ゴミ、手垢などの汚れがサーマルヘッドに付着しても、サーマルヘッドに付着した汚れはクリーニング機能を有するセルフクリーニング層もしくは印刷層21で吸着して除去することができるため、サーマル用紙をH/T用プリンタに通す度にサーマルヘッドのヘッドクリーニングが行なわれ、従来のようにクリーニングシートを必要とせず、定期的にヘッドクリーニングを実施する必要もないため、 [0027] Thus, the use of thermal paper in the above embodiment, paper powder adhering to the paper, dust, be attached to contaminate the thermal head, such as finger marks, self dirt adhering to the thermal head having a cleaning function it is possible to remove adsorbed by the cleaning layer or printing layer 21, head cleaning of the thermal head is performed every time through a thermal paper printer H / T, without the need for conventional cleaning sheet as a regular since manner there is no need to carry out head cleaning,
煩わしいメンテナンス作業を廃止でき、メンテナンス作業に要するコストや労力を削減できる。 Can eliminate the troublesome maintenance work, it is possible to reduce the cost and effort required for maintenance work.

【0028】次に、本発明に係るサーマル用紙の第3の実施形態について図4に基づき説明する。 [0028] Next, a third embodiment of the thermal sheet according to the present invention based on FIG. 4 will be described.

【0029】図4は本実施形態におけるサーマル用紙をガス料金通知書に適用した場合の構成を示す断面図である。 [0029] FIG. 4 is a sectional view showing the structure of the thermal sheet in this embodiment is applied to the gas rates notice. なお、上記実施形態と同一の構成については同一の符号を付してその詳細な説明を省略する。 Incidentally, detailed explanation thereof will be denoted by the same reference configuration as the above embodiment.

【0030】本実施形態におけるガス料金通知書10b The gas rates notice 10b in this embodiment
は、図4に示すように、検針日、メーター指示数、使用量、使用料金からなる各種情報欄がサーマル層11により形成され、所定項目や罫線からなる印刷層12が形成されており、上記サーマル層11および印刷層12からなる印字領域Aを除いた非印字領域Bに限定して、セルフクリーニング層31が形成されている。 As shown in FIG. 4, meter reading day, the meter indication number, amount, various types of information fields composed of a usage charge is formed by the thermal layer 11, print layer 12 having a predetermined item and lines are formed, the It is limited to non-printing area B, excluding the printing area a consisting of the thermal layer 11 and the print layer 12, the self-cleaning layer 31 is formed. セルフクリーニング層31は、無色透明のOPニスの中に、研磨材として、シリカ、炭酸マグネシウム、炭酸カルシウム、金属酸化物微粒子などの無機物質の微細粒子が添加された印刷インキを用いて、グラビアコーティング法やオフセット印刷法などの従来公知の塗工方法や印刷方法で塗布またはベタ印刷することによって構成されている。 Self-cleaning layer 31, in the OP varnish colorless transparent, using as an abrasive, silica, magnesium carbonate, calcium carbonate, a printing ink in which fine particles of inorganic substances such as metal oxide fine particles are added, gravure coating It is constructed by coating or solid printing by a known coating method or printing method, such as law or an offset printing method.

【0031】なお、無色透明のOPニスに添加する微細粒子の粒子径、添加割合は、上記第1実施形態における微細粒子の粒子径、添加割合と同様である。 [0031] The particle size of the fine particles added to the OP varnish colorless transparent, the addition ratio, the particle size of the fine particles in the first embodiment, is the same as the addition ratio.

【0032】このように、本実施形態におけるサーマル用紙は、上記第1および第2実施形態において説明した効果に加え、非印字領域Bにのみセルフクリーニング層31を形成することとしたため、印字領域A表面にはO [0032] Thus, the thermal sheet in this embodiment, in addition to the effects described in the first and second embodiments, since it was decided to form a non-printing area B Shin'ie self-cleaning layer 31, printing area A O on the surface
Pニスまたは印刷インキは印刷されず、印字領域Aの視認性がよく、また感度低下も起こらない。 P varnish or the printing ink is not printed, the visibility of the printing area A is good, also does not occur even desensitization.

【0033】さらに、非印字領域Bに形成するセルフクリーニング層31の面積を調整することによりサーマル用紙の使用頻度に応じてセルフクリーニング機能の微調整を行なうことができ、サーマル用紙の利便性が向上するとともに、サーマル用紙表面の全面にOPニスまたは印刷インキを印刷する必要がなく、比較的低コストでセルフクリーニング層を形成することができる。 Furthermore, by adjusting the area of ​​the self-cleaning layer 31 that forms the non-printing area B can make fine adjustment of the self-cleaning function according to the frequency of use of the thermal sheet, improving the convenience of the thermal sheet as well as, the entire surface is not necessary to print the OP varnish or printing ink of the thermal paper surface, it is possible to form the self-cleaning layer at a relatively low cost.

【0034】 [0034]

【発明の効果】以上、詳細に説明したように、本発明に係るサーマル用紙によれば、以下のような効果を奏する。 Effect of the Invention] As described above in detail, according to the thermal sheet according to the present invention, the following effects. (1)用紙についた紙粉、ゴミ、手垢などの汚れがサーマルヘッドに付着しても、サーマルヘッドに付着した汚れはクリーニング機能を有するセルフクリーニング層で吸着して除去することができるため、サーマル用紙をH (1) For paper powder adhering to the paper, dust, and stains such as finger marks it may adhere to the thermal head, dirt adhering to the thermal head can be removed by suction in a self-cleaning layer having a cleaning function, thermal the paper H
/T用プリンタに通す度にサーマルヘッドのヘッドクリーニングが行なわれ、従来のようにクリーニングシートを必要とせず、定期的にヘッドクリーニングを実施する必要もないため、煩わしいメンテナンス作業を廃止でき、メンテナンス作業に要するコストや労力を削減できるという効果を奏する。 / The passed time to T for printer head cleaning of the thermal head is performed, without the need for conventional cleaning sheet as, there is no need to conduct regular head cleaning, can eliminate the troublesome maintenance work, maintenance work an effect of reducing the cost and labor required for. (2)非印字領域にのみセルフクリーニング層を形成することとしたため、印字領域表面にはOPニスまたは印刷インキは印刷されず、印字領域の視認性がよく、また感度低下も起こらないという効果を奏する。 (2) Since it was decided to form a self-cleaning layer only in the non-printing area, OP varnish or the printing ink is not printed on the printing area surface, the effect that the visibility of the print area is good, also does not occur even desensitization unlikely to. (3)非印字領域に形成するセルフクリーニング層の面積を調整することによりサーマル用紙の使用頻度に応じてセルフクリーニング機能の微調整を行なうことができ、サーマル用紙の利便性が向上するとともに、サーマル用紙表面の全面にOPニスまたは印刷インキを印刷する必要がなく、比較的低コストでセルフクリーニング層を形成することができるという効果を奏する。 (3) can perform fine adjustment of the self-cleaning function according to the frequency of use of the thermal paper by adjusting the area of ​​the self-cleaning layer formed on the non-printing area, along with the convenience of the thermal sheet is improved, thermal the entire surface is not necessary to print the OP varnish or printing ink sheet surface, an effect that it is possible to form a self-cleaning layer at a relatively low cost.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】本発明に係るサーマル用紙をガス料金通知書に適用した第1の実施形態を示す平面図。 Plan view of the thermal sheet according to [1] The present invention showing a first embodiment applied to gas rates notice.

【図2】図1に示すガス料金通知書の構成を示す断面図。 2 is a cross-sectional view showing the configuration of a gas bill notice shown in FIG.

【図3】本発明に係るサーマル用紙の第2の実施形態の構成を示す断面図。 Sectional view showing a configuration of a second embodiment of the thermal sheet according to the present invention; FIG.

【図4】本発明に係るサーマル用紙の第3の実施形態の構成を示す断面図。 Sectional view showing a configuration of a third embodiment of the thermal sheet according to the present invention; FIG.

【符号の説明】 DESCRIPTION OF SYMBOLS

1 ベース紙材 10,10a,10b サーマル用紙 11 サーマル層 12 印刷層 20,21,31 セルフクリーニング層 A 印字領域 B 非印字領域 1 base paper material 10, 10a, 10b thermal sheet 11 thermal layer 12 printed layer 20,21,31 self-cleaning layer A printing region B non-printing area

Claims (5)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 ベース紙材表面にサーマル層が形成され、サーマル層表面に耐熱性UVインキによる印刷層が形成されてなるサーマル用紙であって、 上記サーマル層および印刷層の表面に、研磨材が添加された無色透明OPニスによるセルフクリーニング層が形成されていることを特徴とするサーマル用紙。 1. A thermal layer is formed on the base paper substrate surface, a thermal paper formed by printed layer by heat resistant UV ink on the thermal layer surface formed on the surface of the thermal layer and printing layer, abrasive thermal paper, characterized in that the self-cleaning layer is formed by a colorless transparent OP varnish but that is added.
  2. 【請求項2】 上記研磨材は、シリカ、炭酸マグネシウム、炭酸カルシウム、金属酸化物微粒子等から選ばれる少なくとも一つの微細粒子であることを特徴とする請求項1に記載のサーマル用紙。 Wherein said abrasive silica, magnesium carbonate, calcium carbonate, thermal sheet according to claim 1, characterized in that at least one of fine particles selected from metal oxide fine particles.
  3. 【請求項3】 ベース紙材表面にサーマル層が形成されてなるサーマル用紙であって、 上記サーマル層表面に、シリカ、炭酸マグネシウム、炭酸カルシウム、金属酸化物微粒子等から選ばれる少なくとも一つの微細粒子が添加された有色インキにより罫線、文字、地紋、または網点等からなる印刷層が形成されていることを特徴とするサーマル用紙。 3. A thermal paper thermal layer formed on the base paper material surface, in the thermal layer surface, silica, magnesium carbonate, calcium carbonate, at least one fine particle selected from a metal oxide fine particles thermal paper characterized but ruled by the added colored inks, characters, that background pattern or printed layer formed of halftone dots or the like, it is formed.
  4. 【請求項4】 上記セルフクリーニング層が上記サーマル層および印刷層からなる印字領域を除いた非印字領域に限定して形成されていることを特徴とする請求項1乃至請求項3に記載のサーマル用紙。 4. A thermal according to claims 1 to 3 said self-cleaning layer is characterized in that it is formed as being limited to the non-printing area excluding the printing area consisting of the thermal layer and printing layer paper.
  5. 【請求項5】 上記サーマル用紙がハンディターミナル用紙であることを特徴とする請求項1乃至請求項4に記載のサーマル用紙。 5. A thermal sheet according to claims 1 to 4, characterized in that the thermal paper is handy terminal paper.
JP2001082564A 2001-03-22 2001-03-22 Thermal paper Withdrawn JP2002283720A (en)