JP2002282762A - Coated porous plate and coater, coating method - Google Patents

Coated porous plate and coater, coating method

Info

Publication number
JP2002282762A
JP2002282762A JP2001089815A JP2001089815A JP2002282762A JP 2002282762 A JP2002282762 A JP 2002282762A JP 2001089815 A JP2001089815 A JP 2001089815A JP 2001089815 A JP2001089815 A JP 2001089815A JP 2002282762 A JP2002282762 A JP 2002282762A
Authority
JP
Japan
Prior art keywords
coating
surface
paint
porous material
air
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2001089815A
Other languages
Japanese (ja)
Other versions
JP3730529B2 (en
Inventor
Toshiki Hamabe
Yoshihiro Koike
Shoichi Komasaka
Naomichi Nagazoe
Takashi Naito
隆 内藤
喜寛 小池
敏樹 濱邊
直道 長副
昇一 駒坂
Original Assignee
Asahi Kasei Corp
Nippon Paint Co Ltd
Toa Kogyo Kk
Tokai Sanki Kk
日本ペイント株式会社
旭化成株式会社
東亜工業株式会社
東海産機株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Asahi Kasei Corp, Nippon Paint Co Ltd, Toa Kogyo Kk, Tokai Sanki Kk, 日本ペイント株式会社, 旭化成株式会社, 東亜工業株式会社, 東海産機株式会社 filed Critical Asahi Kasei Corp
Priority to JP2001089815A priority Critical patent/JP3730529B2/en
Publication of JP2002282762A publication Critical patent/JP2002282762A/en
Application granted granted Critical
Publication of JP3730529B2 publication Critical patent/JP3730529B2/en
Application status is Active legal-status Critical
Anticipated expiration legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a method of applying a waterproofing coating material on a porous base material, by which a uniform and exact coating film is formed without increasing the coating film thickness and generating an uncoated part, and an apparatus for executing the method.
SOLUTION: Air pools in the bubbles under a coating material liquid film burst to release the air by charging the porous base material, on the surface of which the coating material liquid film is formed, to a pressure reduced chamber and after that, the coating material of a part of the coating material liquid film is deposited on the whole surface in the bubbles by blowing air to close the pin holes after the air pools burst and to coat the whole inner circumferential surface of the bubbles. As a result, the uniform coating film free from the bubbles left as they are uncoated is formed more thinly on the surface of the porous base material and the coating material to be used is saved by forming the thin coating film.
COPYRIGHT: (C)2002,JPO

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は表面に凸凹と気泡とがある多孔質素材(例えば軽量気泡コンクリートで、以下単にALC板或はALC製の外壁材ともいう)の表面に塗料を塗着する方法、装置、塗料或はALC板に係り、特にALC板の表面に内在する気泡内に空気が閉じ込められること(空気溜の発生)を防止すると共に該気泡の内周面全面にも塗料を流入させて塗膜を形成する塗装方法、塗装装置、防水性塗料及びそのALC板に関するものである。 TECHNICAL FIELD The present invention relates to (for example, lightweight concrete, simply referred to as ALC plate or ALC made in the outer wall member below) a porous material there is the uneven and bubbles on the surface to coating wear coating on the surface of method, apparatus, relates to paint or ALC plate, in particular flows a coating to the inner circumferential surface entire bubble is prevented that the air is trapped in the bubbles inherent in the surface of the ALC plate (occurrence of air reservoir) it is allowed by coating method for forming a coating film, coating apparatus, and a waterproof coating and ALC plate.

【0002】 [0002]

【従来の技術】従来、建物の外壁としては、土等を塗った土壁等のように、建築現場で施工する外壁が多かったが、最近では、外壁材を工場等で生産し、この外壁材を建物の外壁部分に取り付けた外壁が、速く、均質に、しかも、見栄え良く施工できるので広く普及してきている。 Conventionally, as the outer wall of the building, such as such as soil walls painted the soil, etc., but outer wall construction at the building site there were many, in recent years, to produce the outer wall material in the factory or the like, the outer wall an outer wall attached to timber to the outer wall portion of the building, fast, and homogeneously, moreover, been widespread because good appearance can construction. 工場生産される外壁材としては、ALC(Autoclave The outer wall member to be factory production, ALC (Autoclave
dLight-weight Concrete)製の外壁材、プレキャストコンクリート製の外壁材、硬質木片セメント板製の外壁材等が多い。 dLight-weight Concrete) made of the outer wall material, precast concrete outer wall material, hard wood chip cement board made of the outer wall material or the like in many cases.

【0003】特に、ALC製の外壁材は、外観がプレキャストコンクリート製の外壁材に似ていて、しかも、軽く施工し易いので、多く生産されている。 [0003] In particular, ALC made of the outer wall material, appearance is similar to the outer wall material made of precast concrete, moreover, because it is easy and light construction, it has been produced many. そして、住宅等の建物の外壁材としては、最近彫りの深い凹凸模様を設けたものが、外観が豪華であることから、施工主に好まれている。 And, as the outer wall material of the building such as a house, those who have recently formed a deep uneven pattern of carving, from that appearance is gorgeous, are favored in construction main.

【0004】このような外壁材では、通常、外観を良くしたり水分を吸収しないようにするために、表面に塗料が塗布される。 [0004] In such a siding, usually, in order not to absorb well or moisture appearance, paint is applied to the surface. 従来から、このような外壁材の表面に塗料を塗布する塗装方法としては、刷毛塗り方法、スプレー塗装方法、ロールコーター、フローコーター、ディッピング方法等がある。 Conventionally, as a coating method for applying a coating to the surface of such outer walls, brushing method, spray coating method, a roll coater, flow coater, a dipping method or the like.

【0005】刷毛塗り方法では、塗料を付着させた刷毛で外壁材の表面を撫でて塗布する方法であり、最も原始的な方法である。 [0005] In the brushing method, a method of applying stroking the surface of the outer wall member with a brush adhered with paint, is the most primitive way. この刷毛塗り方法は、刷毛を塗料溜に入れて刷毛に塗料を付着させ、この刷毛を外壁材表面に撫でて塗布するので、少量生産の外壁材や外壁材の塗装面を修理する場合に適しているが、大量生産には適していないため、外壁材の大量生産工程では採用されていない。 The brushing method, putting the brush into the paint reservoir to adhere the paint brush, the coating stroking the brush on the outer wall material surface, suitable for repairing the painted surface of the outer wall member and an outer wall material for small production and that it, because it is not suitable for mass production, the mass production process of the outer wall material has not been adopted.

【0006】これに対して、スプレー塗装方法は、スプレーの先端のノズルから塗料を吹き出させ、この吹き出た塗料を外壁材の表面に吹き付けて塗装する方法であり、エアスプレー方式とエアレススプレー方式とがある。 [0006] In contrast, spray coating method, coating blown from the nozzles of the spray tip, a method of coating by spraying the blown paint on the surface of the outer wall member, an air spray method and airless spray system there is. エアスプレー方式は、スプレーガンの先端のノズルに通ずる圧縮空気の通路と、塗料溜からこの圧縮空気の通路に通ずる通路とから構成されているものであって、 Air spray method, there is configured from a passage of compressed air leading to the nozzle tip of the spray gun, a passage leading to the passage of the compressed air from the paint reservoir,
圧縮空気の通路を介してエアガンの先端のノズルに圧縮空気を通過させると、この圧縮空気の通路が減圧になり、この圧縮空気の通路に通ずる通路を通して塗料溜の塗料が吸い込まれ、この吸い込んだ塗料と空気とが一緒になってノズルから出て塗装する方法である。 When through the passage of the compressed air is passed through the compressed air to the nozzle tip of the air gun, the passage of the compressed air is a vacuum, the paint reservoir of paint is drawn through the passage leading to the passage of the compressed air, but this breathed it is a method of painting out of a nozzle coating and air together.

【0007】かつ、エアレススプレー方式とは、塗料溜からスプレーガンの先端のノズルに通ずる通路が設けられていて、塗料溜の中に圧縮空気を導入すると、この圧縮空気の圧力により塗料溜の塗料が通路に押し出され、 [0007] and, with the airless spray method, it is provided a passage communicating from the paint reservoir to the nozzle tip of the spray gun, the introduction of compressed air into the paint reservoir, paint reservoir by the pressure of the compressed air paint There are pushed out into the passage,
スプレーガンの先端のノズルから塗料が吹き出て塗装する方法である。 Paint from the nozzle tip of the spray gun is a method of painting with blown. このスプレー塗装方法は、塗料を外壁材の表面に吹き付けることができるので、彫りの深い外壁材でも塗装でき、様々な外壁材の塗装に採用されている。 How this spray painting, it is possible to spray paint on the surface of the outer wall member, also coated with a deep outer walls sculpted, are employed for coating a variety of exterior wall materials.

【0008】更に、エアレススプレー塗装した後に、空気噴流をスリット状にだすエアーナイフ等で余分な塗料を削ぎ落とす方法やスプレー塗装後減圧ブースを通した後に加圧ブースで空気噴流をあてる方法等の組み合わせ塗装が採用されている。 Furthermore, after the airless spray coating, a method in which applying air jets a pressurized booth after passing a vacuum booth after methods and spray coating scraped off the excess paint an air knife or the like issues a jet of air to the slit-shaped the combination painting has been adopted.

【0009】 [0009]

【発明が解決しようとする課題】しかしながら、外壁材の表面を塗布する最も効果的な方法と考えられている従来のスプレー塗装方法にあっても、彫りの深いALC製の外壁材を塗装する場合には、多くの問題が生じていた。 [SUMMARY OF THE INVENTION However, even in the most effective way and thought to have a conventional spray coating method of applying the surface of the outer wall member, when painted deep ALC made of exterior wall materials sculpted in had caused many problems. すなわち、溝等の深い彫りがあると、溝部と非溝部とでは、スプレーによって塗布された塗料の塗布量が異なる等の問題があった。 That is, if there is a deep carving of the groove or the like, in the groove and the non-groove portion, the coating amount of paint applied by spraying there was a problem of a different like.

【0010】また、ALC製の外壁材では、製造時、表面に多くの気泡が現れて微細な穴(凹凸)となるので、 Further, in the outer wall material made of ALC, during manufacture, because many bubbles appear on the surface a fine hole (irregularities),
この表面にスプレー方式で塗料を塗布すると、凹凸の内部まで塗布されず、この凹凸の内部に空気溜を含んだ状態になり、この塗膜形成後に空気溜が破け、その部分が、塗装されていない状態または塗膜の薄い状態になる。 When applying the paint spraying on the surface is not coated to the inside of the irregularities, will state containing air reservoir inside the irregularities, the coating film formed after torn air reservoir, part thereof, unpainted It becomes thin the absence state or coating. 又スプレー塗装後のエアーナイフによる塗料削ぎ落としや、減圧ブース+加圧ブースで塗料を均一な薄膜化にする方法では溝部等の塗料溜りは減少するが気泡内部まで塗膜を形成できないという問題がある。 Further and scraped paint by an air knife after spraying, a problem that the paint reservoir of the groove such a way that a uniform thin the paint under reduced booth + pressurization booth decreases can not form a coating film to the inside bubbles is there.

【0011】従来の表面に塗膜が形成されたALC板の一部を図式化して例示すると、例えば図8(a)に示す如く、ALC板1の表面に防水塗装装置を用いて塗装を施して塗膜2を形成した場合には、ALC板1の表面に在る多数の気泡3の内部に空気が塗膜2によって密封された状態で空気溜5が形成されていた。 [0011] subjecting To illustrate diagrammatically a part of the ALC plate coating is formed on the conventional surface, for example, as shown in FIG. 8 (a), a coating with a waterproof coating device on the surface of the ALC plate 1 in the case of forming a coating film 2 Te, air reservoir 5 has been formed in a state where the air inside of a large number of bubbles 3 at the surface of the ALC plate 1 is sealed by a coating film 2.

【0012】しかし、気泡3の孔径が大きい場合には、 [0012] However, if the pore size of the bubble 3 is large,
図8(b)に示す如く、時間が経過しかつ気圧が変化したような場合には、気泡3内の空気溜5が膨張してはじけて塗膜2にピンホール4が生ずる問題があった。 As shown in FIG. 8 (b), when such changes are over time and pressure, air reservoir 5 in the bubble 3 had pinholes 4 problems caused in the coating film 2 bursting expanded .

【0013】図9(a)は、ALC板1の表面の顕微鏡写真であって、前述の図8(b)に示すように、塗膜2 [0013] FIG. 9 (a), a micrograph of the surface of the ALC plate 1, as shown in Figure 8 of the aforementioned (b), the coating film 2
にピンホール4が生じた状態を示している。 Pinholes 4 shows a state that occurred. 図9(b) Figure 9 (b)
はALC板1の縦断面の顕微鏡写真であって、ALC板1の表面側に在る気泡3の内部に塗料が押込まれずに、 Is a photomicrograph of a longitudinal section of the ALC plate 1, the paint inside the bubble 3 located on the surface side of the ALC plate 1 is pushed Marezu,
塗膜2が形成されてない状態を示している。 It shows a state where the coating film 2 is not formed.

【0014】かかる問題点を解決するためのひとつの方策として、塗膜を厚く塗布する方策が考えられるが、このようにすると、多量の塗料(被覆組成物)が必要となり、解決策としては未だ不十分である等の問題があった。 [0014] One way to solve such problems, although measures to thickly applied coating film is considered, in this case, a large amount of coating material (coating composition) is required, yet is as a solution there was a problem and the like is insufficient. 図10はALC板1の表面に極めて肉厚の塗膜2を形成した状態を図式化したものである。 10 is obtained by graphically a state in which a coating film 2 of the very thick on the surface of the ALC plate 1.

【0015】本発明に係る塗装方法等は前述の多くの問題点に鑑み開発された全く新しい発明であって、特に多孔質素材の表面に塗料を加圧吹付けしてその表面に設けられた気泡内に塗料を押し込め、この多孔質素材の塗料液膜表面を減圧することによって気泡内に閉じ込められた空気溜を膨張破裂させて塗膜を形成させるようにした全く新しい塗装方法及び塗膜装置等の発明を提供するものである。 The coating method and the like according to the present invention is an entirely new invention was developed in view of the many problems described above, provided on the surface thereof with pressure 圧吹 paint, especially the surface of the porous material pushed the paint inside the bubbles, the porous material completely new coating method and coating apparatus so as to form a coating film is expanded ruptured air reservoir trapped in the bubble by the coating liquid film surface under vacuum of there is provided a present invention and the like.

【0016】 [0016]

【課題を解決するための手段】本発明に係る塗装方法は、前述の多くの問題点を根本的に改善した発明であって、その塗装方法の第1発明の要旨は、多数の気泡が内在する多孔質素材の表面に防水性塗膜を形成する塗装方法に於て、前記多孔質素材の表面に塗料を加圧吹付けして前記多孔質素材の気泡内に塗料を押し込めて、所定厚の塗料液膜を形成し、該多孔質素材の該塗料液膜表面を減圧することによって塗料液膜の形成により閉じ込められた気泡内の空気溜を膨張破裂させ、塗膜を形成させることを特徴とした多孔質素材の塗装方法である。 Means for Solving the Problems] coating method according to the present invention is an invention which fundamentally improve the many problems described above, the gist of the first invention of the coating method, a large number of bubbles inherent to the surface of the porous material at a coating method for forming a waterproof coating film, said paint on the surface of the porous material to put pressure 圧吹 pushed the paint inside the bubbles of the porous material, a predetermined thickness features of the coating liquid film is formed, the air reservoir in the bubbles trapped by the formation of the coating liquid film is expanded ruptured by reducing the pressure of the paint liquid film surface of the porous material, that to form a coating film is a porous material way of painting was.

【0017】前述の第1発明の塗装方法に於ては、多孔質素材の表面に塗料を加圧吹付けするので、多孔質素材の表面に内在する気泡内にも塗料を押し込めて塗着して多孔質素材の表面全面に所定厚の塗料液膜を形成することが出来る。 [0017] At a coating method of the first invention described above, since with pressure 圧吹 paint to the surface of the porous material, the coating and wear tucked paint in the air bubbles inherent in the surface of the porous material it can be formed a predetermined thickness of the coating liquid film on the entire surface of the porous material Te.

【0018】また、この第1発明の塗装方法に於ては、 [0018] Te is at the coating method of the first aspect of the invention,
多孔質素材の表面に所定厚の塗料液膜が形成された後で多孔質素材の塗料液膜表面を減圧するので、この該塗料液膜の形成によって閉じ込められていた気泡内の空気溜を膨張破裂させ、後になってピンホールの発生の大きな原因となる気泡内の空気を事前に放出して除去することが出来る。 Since depressurizing the coating liquid film surface of the porous material after the coating liquid film having a predetermined thickness on the surface of the porous material is formed, expanded air reservoir in the bubbles that were trapped by the formation of the coating composition liquid film ruptured, air in the bubbles become a major cause of the occurrence of pinholes at a later can be removed by releasing beforehand.

【0019】本発明に係る塗装方法の第2発明の要旨は、前記多孔質素材の表面に塗料を加圧吹付けして前記多孔質素材の気泡内に塗料を押し込めた後で、該多孔質素材の表面の過剰分の塗料を除去手段で除去することを特徴とした第1発明の多孔質素材の塗装方法である。 [0019] Summary of the second aspect of the coating method according to the present invention, after tucked paint to the porous foam material to put pressure 圧吹 paint to the surface of the porous material, the porous a porous material coating method of the first invention which is characterized in that removal removal means excess coating material on the surface.

【0020】前述の第2発明の塗装方法に於ては、前記多孔質素材の表面に塗料を加圧吹付けしてその表面に塗料を塗着した後で、表面に付着した過剰分の塗料を除去手段(例えば空気吹付け)で除去するので、多孔質素材の表面に形成される塗料の肉厚を一定に保つことが出来、しかも除去した塗料は再利用することが出来るので、極めて経済的である。 [0020] Te is at the coating method of the second invention described above, the paint on the surface of the porous material after Nurigi paint to pressurized 圧吹 attached to its surface, excess paint adhered to the surface since removed by removal means (for example only air blowing), it is possible to maintain the thickness of the coating formed on the surface of the porous material constant, and since the removed paint can be reused, extremely economical is a basis.

【0021】本発明に係る塗装方法の第3発明の要旨は、前記多孔質素材の該塗料液膜表面の減圧によって塗料液膜の形成により閉じ込められた気泡内の空気溜を膨張破裂させた後で、塗料液膜表面に空気を吹付けることによって、前記気泡内全面に塗料液を流入させて塗膜を形成させることを特徴とした第1発明或は第2発明の多孔質素材の塗装方法である。 [0021] SUMMARY OF third aspect of the coating method according to the present invention, after the air reservoir in the trapped air bubbles by forming a coating liquid film is expanded ruptured by vacuum of the porous material paint-film surface in, by blowing air into the coating liquid film surface, the first invention or the porous material coating method of the second invention which is characterized in that by introducing the coating liquid to form a coating film on the bubble in the entire it is.

【0022】前述の第3発明の塗装方法に於ては、前記多孔質素材の塗料液膜表面の減圧によって塗料液膜の形成により閉じ込められた気泡内の空気溜を膨張破裂させた後で、塗料液膜の表面に空気を吹付けるので、塗料液膜を形成するまだ流動性を持った塗料液を気泡内全面に流入させて塗膜を形成し、気泡内に未塗装部分が設けられることを防止出来る。 [0022] After Te is at the coating method of the third invention described above, the air reservoir in the trapped air bubbles by forming a coating liquid film is expanded ruptured by vacuum of the porous material of the coating liquid film surface, since blowing air to the surface of the coating liquid film, yet paint liquid having flowability to form a coating liquid film to flow into the bubble within the entire surface to form a coating film, the unpainted portion is provided inside the bubbles a it can be prevented.

【0023】本発明に係る塗装方法の第4発明の要旨は、前記多孔質素材の表面に塗料を加圧吹付けする以前に該多孔質素材を加熱して所定の温度にすることを特徴とした第1発明乃至第3発明の多孔質素材の塗装方法である。 [0023] SUMMARY OF fourth aspect of the coating method according to the present invention, the wherein the coating material to the porous material surface prior to attaching pressurized 圧吹 by heating the porous material to a predetermined temperature a first invention to the porous material coating method of the third invention has been.

【0024】前述の第4発明の塗装方法に於ては、前記多孔質素材の表面に塗料を加圧吹付けする以前に該多孔質素材を加熱して所定の温度にしたので、加圧吹付けされた塗料が加温されて凹凸及び気泡が介在する多孔質素材の表面全面に均一に塗着されると共に、塗料によって塗膜を早く形成することが出来る。 [0024] Te is at the coating method of the fourth aspect of the present invention described above, since said porous material coating on the surface of heating the previously porous material to give pressurized 圧吹 to a predetermined temperature, pressure 圧吹together with paint that is warmed by irregularities and air bubbles are uniformly coated on the entire surface of the porous material interposed, it is possible to quickly form a coating film by coating.

【0025】本発明に係る塗装装置の第1発明の要旨は、多数の気泡が内在する多孔質素材の表面に防水性塗膜を形成する塗装装置に於て、前記多孔質素材の表面に塗料を加圧吹付けて前記多数の気泡内に塗料を押し込める加圧吹付装置と、過剰分の塗料を除去する(例えば空気吹付)除去装置と、減圧することによって前記多数の気泡内に塗料液膜の形成によって閉じ込められた空気溜を膨張破裂させる減圧装置と、空気を塗料液膜表面に吹付けることによって塗料液を前記気泡内に流入させる空気吹付装置との組合せより構成されることを特徴とした多孔質素材の塗装装置である。 [0025] SUMMARY OF first aspect of the coating apparatus according to the present invention, At a coating apparatus for forming a waterproof coating film on the surface of the porous material many bubbles inherent, paint on the surface of the porous material a pressurized 圧吹 with apparatus of sticking the paint pressurized 圧吹 put it in the number of bubbles, the removal of excess paint and (for example, air spray) removing apparatus, paint liquid layer in the number of bubbles by vacuum a decompressor for inflating rupture the air reservoir trapped by the formation of, and characterized in that it is composed of a combination of an air spray apparatus for flowing coating liquid in the bubble by blowing air into the coating liquid film surface It was a coating apparatus of a porous material.

【0026】前述の塗装装置の第1発明は、塗料を該多孔質素材の表面に強く吹付けることが出来る加圧吹付装置を設けたので、この装置によって多孔質素材の表面に内在する気泡内に塗料を押し込めることが出来る。 [0026] The first invention of the aforementioned coating apparatus, is provided with the coating the porous pressurized 圧吹 with device strongly capable sprayed on the surface of the material, inside the bubbles inherent in the surface of the porous material by the device You can of sticking the paint. かつ、除去装置によって多孔質素材の表面に塗着された過剰な塗料を除去することが出来る。 And removing device makes it possible to remove excess coating material is coated on the surface of the porous material.

【0027】また、前記塗装装置の第1発明には、減圧装置が設けられているので、この装置によって多孔質素材の塗料液膜表面を減圧させることによって、多数の気泡内に塗料液膜の形成により閉じ込められていた空気溜を膨張破裂させて気泡内から除去することが出来る。 Further, the first aspect of the coating apparatus, the pressure reducing device is provided, by vacuum paint liquid film surface of the porous material by the device, the coating liquid film in a number of bubbles the air reservoir which has been trapped by the forming inflated rupture can be removed from inside the bubbles.

【0028】さらに、前記第1発明には、前述の装置とは別に空気吹付装置が設けられているので、この装置で多孔質素材の表面に塗着された塗料液膜に空気を強く吹付けることによって、塗料液を前記多孔質素材の表面に内在する多数の気泡内に流入させて気泡内に塗膜を形成することが出来る。 Furthermore, wherein the first invention, since separate air blowing device is provided with the aforementioned device, applying a strong blow air into Nurigi paint liquid film on the surface of the porous material in this device it makes it possible to form a coating film of the coating material was allowed to flow into the number of bubbles inherent in the surface of the porous material into the bubble.

【0029】本発明に係る塗装装置の第2発明の要旨は、前記除去装置の作動によって除去された過剰分の塗料を回収する回収槽と、回収槽に回収された過剰塗料を濾過して再利用する濾過装置とを具備したことを特徴とした第1発明の多孔質素材の塗装装置である。 [0029] Summary of the second aspect of the coating apparatus according to the present invention, re a recovery tank for collecting the excess coating removed by the operation of the removing device, the excess paint collected in the collection tank by filtration a coating apparatus of the porous material of the first invention which is characterized by comprising a filtering device for use.

【0030】前述の第2発明の塗装装置に於ては、前記除去装置の作動によって除去された過剰塗料を回収する回収槽と、過剰分の塗料を濾過して再利用する濾過装置とが設けられているので、これ等の回収槽と濾過装置とを利用することによって、過剰塗料を有効にかつ経済的に再利用することが出来る。 [0030] Te is at the coating apparatus of the second invention described above, a recovery tank for collecting the excess coating removed by the operation of the removing device, a filtration device to be reused by filtration the excess paint is provided since being, by utilizing the a collecting tank for this such as filtration apparatus, excess paint effectively and economically can be reused.

【0031】本発明に係る防水性塗料の要旨は、前記多孔質素材の塗装方法或は多孔質素材の塗装装置に用いられる防水性塗料に於て、水溶性、水分散型および/またはエマルジョン型の水性樹脂であって、アクリル樹脂、 [0031] Summary of the waterproof coating material according to the present invention, the the porous material coating method or a waterproof coating for use in coating device of porous material Te at a water-soluble, water-dispersible and / or emulsion type a water-based resin, an acrylic resin,
変性アクリル樹脂等の1種または2種以上の混合物及びヒドラジド、グリシジルメタアクリレート、シラノール、オキサゾリン、酸化金属等の架橋剤の1種または2 One or more thereof and hydrazides such as modified acrylic resin, glycidyl methacrylate, silanol, oxazoline, one cross-linking agent such as a metal oxide or 2
種以上を主成分として構成されたことを特徴とした多孔質素材の塗装用の防水性塗料である。 A waterproof paint for painting a porous material which is characterized in that it is constituted of the above species as a main component.

【0032】前述のような構成を有する防水性塗料は、 The waterproof coatings with as described above arrangement,
多孔質素材の表面に加圧吹付けによって塗着された際に、多孔質素材の表面に内在する気泡内に容易に流入して塗料液膜を形成することが出来、かつ多孔質素材を減圧した際には気泡内の空気を簡単に膨張破裂させることも出来、さらに空気吹付装置で空気を強く吹き付けられた際には、塗料液膜の一部の塗料液が気泡内にスムーズに流入して気泡内全面を塗装することが出来る特性を有している。 When it is coated applied by pressurization 圧吹 with the surface of the porous material, and readily flows into the bubbles inherent in the surface of the porous material can form a coating liquid film, and vacuum the porous material It was also able to easily inflated burst of air in the bubbles when, upon further blown strongly air with air blowing device, a portion of the coating liquid of the coating liquid film flows smoothly into the bubble has a can property be painted bubbles within the entire surface of Te.

【0033】本発明に係る多孔質素材の要旨は、表面と連通する気泡を多数有する多孔質素材に於て、該多数の気泡内に空気溜が存在せず、かつこれ等の気泡の内周面全面に所定厚さの塗料膜が被覆されて形成されていることを特徴とした多孔質素材である。 The porous material according to the present invention gist, the bubbles which communicates with the surface At a porous material having a large number, there is no air reservoir in the bubbles said multiple, and which like the inner periphery of the bubbles it is a porous material that was characterized by a predetermined thickness of the coating film is formed is coated on whole surface.

【0034】前述の多孔質素材は、多数の気泡内に空気溜が存在しないので、後から気泡内の空気溜が膨張破裂して、気泡の入口に被覆されていた防水塗料膜の一部にピンホールが生ずる恐れがない。 The aforementioned porous material, since there is no air reservoir in the number of bubbles, the air reservoir in the bubbles expands ruptured later, a part of the waterproof coating film was coated on the inlet of the bubble there is no risk of causing pinhole. また、多数の気泡の内周面全面には所定厚の塗料膜が被覆されているので、気泡の内周壁面より雨水が多孔質素材内に浸み込む心配もない。 Further, since numerous inner circumferential surface entire predetermined thickness of the paint film to the bubble are covered, there is no fear of rainwater from the inner peripheral wall surface of the bubble can Komu penetrates into the porous material.

【0035】 [0035]

【発明の実施の形態】図により本発明に係る塗装方法、 Coating method according to the present invention by showing PREFERRED EMBODIMENTS,
塗装装置、防水性塗料及びALC板(多孔質素材)の一実施例を具体的に説明すると、図1は本発明の塗装方法を実施するための装置の簡略説明図、図2は図1の装置に取付けられるフィルタの断面図、図3は本発明の方法を示すフローチャート図、図4(a)、(b)、 Coating apparatus, concretely describing one embodiment of a waterproof coating and ALC plate (porous material), simplified illustration of an apparatus for Figure 1 for implementing the coating method of the present invention, FIG. 2 in FIG. 1 sectional view of a filter attached to the device, FIG. 3 is a flowchart illustrating a method of the present invention, FIG. 4 (a), (b),
(c)、(d)は夫々ALC板の表面の気泡内に塗膜が形成される工程を示す断面説明図である。 (C), (d) is a sectional view showing a step of coating is formed in the bubble surface of each ALC plate.

【0036】図5は本発明のALC板の要部の断面拡大説明図、図6(a)は本発明のALC板の平面の顕微鏡写真図、図6(b)は同図の要部の縦断面の顕微鏡写真図、図7(a)、(b)も夫々図6(a)の要部の縦断面の顕微鏡写真図である。 [0036] Figure 5 is a cross-sectional enlarged view of a main part of the ALC plate of the present invention, FIG. 6 (a) micrograph of a plane of the ALC plate of the present invention, FIG. 6 (b) of the main part of FIG. micrograph of a longitudinal section, FIG. 7 (a), the a micrograph of a longitudinal section of an essential part of (b) also respectively FIG 6 (a).

【0037】図1により本発明に係る方法及び装置について説明すると、次の通りである。 [0037] The Figure 1 Referring to the method and apparatus according to the present invention is as follows. 図中10は本発明に係る塗装装置全体を示しており、装置対象とするALC Figure 10 shows the entire coating apparatus according to the present invention, ALC to device object
板11に対して、ALC板11を予熱するプレヒート部25と、ALC板11の表面に塗料を塗着する塗装部3 With respect to the plate 11, the preheating unit 25 for preheating the ALC plate 11, coating station 3 for coating wear coating on the surface of the ALC plate 11
0とを有している。 Has a 0 and.

【0038】前述のALC板11は予めプレヒート部2 The ALC plate 11 described above in advance preheating unit 2
5で例えば40〜50℃に熱せられる。 5, for example, is heated to 40 to 50 ° C.. 次に搬送ローラ72及び73に載せられたALC板11は、搬送ローラ72および73の回転によって図中矢印a方向に送られ、これにより塗装部30による各処理がALC板11 ALC plate 11 placed on the conveyance rollers 72 and 73 then are in the drawing is sent in the direction of arrow a by the rotation of the conveying rollers 72 and 73, thereby the processing by the coating unit 30 ALC plate 11
に対して順次施されるようになされている。 It is adapted to be sequentially subjected to.

【0039】この塗装装置10には制御部22が設けられており、制御部22は入力されたコマンドに従って塗装装置10の各部を制御する。 [0039] has been the control unit 22 to the coating apparatus 10 is provided, the control unit 22 controls each unit of the coating system 10 in accordance with the input command.

【0040】前述のようにプレヒート部25において所定温度に加熱されたALC板11は、塗装部30に送られる。 The ALC plate 11 heated to a predetermined temperature in the preheating section 25 as described above is sent to the coating unit 30. 塗装部30のALC板11の搬入口近傍には、A The entrance near the ALC plate 11 of the coating unit 30, A
LC板11の有無を検出するためのセンサ26が設けられている。 Sensor 26 for detecting the presence or absence of LC plate 11 is provided. このセンサ26は、レーザ光をALC板11 The sensor 26 is, ALC plate 11 with a laser beam
の搬入経路に照射してその反射光の強度に基づいてAL AL based on the intensity of the reflected light is irradiated to the conveyance path of the
C板11の有無を検出するもの等を用いることが可能である。 It is possible to use a for detecting the presence or absence of C plate 11.

【0041】制御部22はセンサ26の検出結果を常時監視しており、ALC板11が搬入されたことを検出すると、塗装部30の各部を動作させることにより、当該搬入されたALC板11に対する塗装処理を塗装部30 The control unit 22 always monitors the detection result of the sensor 26 detects that the ALC plate 11 is carried by operating each part of the coating unit 30, for ALC plate 11 which is the carrying coating the coating processing unit 30
に実行させるようになされている。 It has been made so as to execute.

【0042】塗装部30は、筐体31によってその内部の塗装処理空間が外部空間から遮蔽されている。 The coating unit 30, paint processing space therein is shielded from the external space by the housing 31. この塗装処理空間は隔壁42、43及び44によって4つの処理空間に分けられている。 The painting space is divided into four treatment space by partitions 42, 43 and 44. これら4つの処理空間のうち、ALC板11の搬入口側に設けられている第1の処理空間は、塗料を加圧吹付けする加圧吹付室であって、 Of these four processing space, the first processing space provided entrance side of the ALC plate 11 is a - added 圧吹 chamber for attaching a paint additive 圧吹,
ALC板11の表面に対して塗料(被覆組成物)12を高圧で叩き付けるための噴射塗装部32があり、ポンプ52から配管51を介して塗料12が噴射ノズル54に供給される。 Yes paint (coating composition) 12 is injection coated part 32 to slap at high pressure to the surface of the ALC plate 11, coating 12 is supplied to the injection nozzle 54 from the pump 52 via the pipe 51.

【0043】このとき塗料12は、液圧計53によってその圧力が制御されながら、ALC板11の表面に対する塗装打力が2g/cm2以上(好ましくは10 g/cm2以上) [0043] In this case coating 12, while the pressure is controlled by the liquid pressure gauge 53, painted batting power to the surface of the ALC plate 11 2 g / cm @ 2 or more (preferably 10 g / cm @ 2 or more)
となるような圧力でALC板11の表面に吹き付けられる。 It is blown to the surface of the ALC plate 11 to become such pressures. この結果、ALC板11の表面の微細な穴に塗料がほとんど押し込まれることとなる。 As a result, an paint is almost pressed into fine pores of the surface of the ALC plate 11. 因みに、この噴射塗装部32を構成する第1の処理空間内には、ALC板1 Incidentally, in the first treatment space constituting the injection coating unit 32, ALC plates 1
1の搬入口から塗料12が外部に漏れ出さないようにするためのシャッタ41が設けられている。 Shutter 41 so that the paint 12 does not leak to the outside from the first inlet port.

【0044】噴射塗装部32においてその表面に塗料1 The paint 1 to the surface in the injection coating unit 32
2の塊が高圧噴射によって吹き付けられたALC板11 ALC plate 11 2 of mass was sprayed by high-pressure injection
は、搬送ローラ72、73の回転によって第2の処理空間に送り込まれる。 It is fed into the second process space by the rotation of the conveying rollers 72 and 73. この第2の処理空間は、過剰分の塗料を空気吹付けによって除去する空気吹付室であって、 The second process space, the excess paint an air spray chamber be removed by air blowing,
ALC板11の表面に盛られた状態の塗料12にエアーを吹き付けることによって、ALC板11の表面から余分な塗料を削ぎ取るためのエアーブロー部33が設けられている。 By blowing air into the coating 12 in a state of being piled on the surface of the ALC plate 11, an air blowing portion 33 for taking stripped excess paint from the surface of the ALC plate 11 is provided. このエアーブロー部33に設けられたエアーカッタ65に対して、ブロアー部61からエアー分配室62を介してエアーが供給されるようになされており、 Against air cutter 65 provided in the air blowing unit 33, it has been made as air is supplied from the blower unit 61 through the air distribution chamber 62,
当該供給されたエアーは、エアーカッタ65の一対のエアーブロー板65A及び65Bに供給され、それらの先端部からALC板11の塗料に対して高圧のエアーが吹き付けられる。 The supplied air is supplied to the pair of air blow plates 65A and 65B of the air cutter 65, high-pressure air is blown against those from the tip of the ALC plate 11 paint.

【0045】このようにして、ALC板はエアーカッタ65によってエアーが吹き付けられながら搬送ローラ7 [0045] In this manner, ALC plate conveyed while air is blown by an air cutter 65 rollers 7
2、73の回転によって矢印a方向に送られることにより、その表面に盛られている塗料のうち、過剰な塗料が除去される。 By being sent in the direction of the arrow a by the rotation of 2,73, of paints that are piled on the surface, excess paint is removed. 除去された塗料は、ALC板11の両側部から回収タンク46に流れ落ちる。 The removed paint flows down into the collection tank 46 from both sides of the ALC plate 11. 回収タンク46に溜まった塗料12は、ポンプ74によって配管75に送られ、当該配管75の先に設けられているフィルターに供給される。 Coating 12 collected in the recovery tank 46 is sent to the pipe 75 by the pump 74, it is supplied to a filter provided ahead of the pipe 75.

【0046】図2は配管75(図1)の先に設けられているフィルタ90を示す断面図である。 [0046] FIG. 2 is a sectional view showing a filter 90 provided in the tip of the pipe 75 (FIG. 1). この図2に示されるように、フィルタ90は回収タンク46(図1)から排出された塗料12から不純物(ALC粉等)を除去するためのものであり、筐体91内に、回収塗料を通過させて濾過するための金網92が設けられている。 As shown in FIG. 2, the filter 90 is for removing impurities (ALC powder, etc.) from the coating 12 discharged from the collection tank 46 (FIG. 1), in the housing 91, the recovered paint wire mesh 92 for filtrated through is provided. 金網92を通った回収塗料は不純物が除去されてタンク96 Recovered paint passing through the wire mesh 92 is removed impurities tank 96
に溜められる。 It is accumulated to. タンク96に溜められた濾過済みの塗料は、ポンプ97によって再び塗装装置10(図1)に戻され、図1について上述した場合と同様にして、噴射塗装部32においてALC板11に噴射塗装される。 Filtered paint accumulated in the tank 96 is returned again to the coating apparatus 10 by the pump 97 (FIG. 1), as in the case described above with reference to FIG. 1, is injected painted ALC plate 11 in the injection coating station 32 that.

【0047】また、フィルタ90(図2)において回収塗料から除去されたALC粉等の不純物は、廃棄槽95 [0047] The filter 90 impurities ALC dust removed from the recovered paint in (FIG. 2) is, disposal tank 95
に溜められる。 It is accumulated to. このように、塗装装置10においては、 In this manner, the coating apparatus 10,
エアーカッタ65で削ぎ落とされる等した余分な塗料が回収タンク46に回収された後、フィルタ90を介して再利用されることにより、塗料の使用効率が高くなるようになされている。 After excess paint or the like is scraped off by the air cutter 65 is collected in the collection tank 46, by being recycled through the filter 90 are adapted to use the efficiency of the coating material is increased.

【0048】図1に示される塗装装置10のエアーブロー部33において過剰な塗料が除去されたALC板11 The ALC plate 11 excess paint is removed in the air blow portion 33 of the coating apparatus 10 shown in FIG. 1
は、搬送ローラ72、73の回転によって第3の処理空間に送り込まれる。 It is fed into the third processing space by the rotation of the conveying rollers 72 and 73. この第3の処理空間は、ALC板1 The third processing space, ALC plates 1
1の表面に塗着された塗料液膜表面を減圧させる処理空間であって、ALC板11の表面において塗料12が確実に入りきっていない気泡、つまり塗料液膜の形成によって、残留する気泡内に閉じ込められた空気のある状態の空気溜を膨張破裂させるための減圧室34である。 A The Nurigi paint liquid film surface on one surface a processing space to be vacuum bubbles coating 12 on the surface of the ALC plate 11 is not completely enter ensured, i.e. the formation of the coating liquid film, the bubbles remaining a decompression chamber 34 for inflating bursting air reservoir of states of air trapped. ブロアー部61によってエアーを引き出すことにより、減圧室34の内部が大気圧よりも1.5KPa以上低い気圧を保つことにより、気泡内の空気溜の空気が膨張するようになされている。 By drawing air by blower unit 61, the interior of the vacuum chamber 34 by keeping the pressure lower than 1.5KPa than the atmospheric pressure, the air reservoir of the air inside the bubbles have been made to expand. この時、エアーブロー部における過剰塗料の除去が少ないと気泡入口上の塗料液膜が厚くなり気泡内の空気の膨張によりはじけることができなくなり塗り残しが発生することとなる。 In this case, so that the remaining coating will not be able to pop the expansion of air in the coating liquid film is thicker becomes the bubble on the bubble inlet removal of excess paint in the air blow portion is small it occurs.

【0049】減圧室34において塗装部分の気泡内の空気溜がはじけたALC板11は、搬送ローラ72、73 The ALC plate 11 air reservoir is bursting in the air bubbles paintwork in a vacuum chamber 34, conveying rollers 72 and 73
の回転によって続く第4の処理空間に送られる。 It is sent to the fourth processing space followed by rotation of the. この第4の処理空間は、ALC11の表面に塗着された塗料液膜に空気を吹き付ける加圧室であって、気泡内の空気溜がはじけ入口の開いた気泡内部に塗料を、加圧されたエアーの流れによって流し込むための加圧室35が設けられている。 The fourth processing space is a pressure chamber for blowing air into the coating liquid film which is coated on the surface of the ALC11, paint inside bubbles air reservoir is open inlet bursting in bubbles, pressurized pressurizing chamber 35 for pouring by the air flow are provided with. この加圧室35には、ブロアー部61からエアー分配室62を介して加圧エアーが供給されるようになされている。 This pressurizing chamber 35, pressurized air from the blower unit 61 through the air distribution chamber 62 is adapted to be supplied. このような加圧室35から隣接する減圧室34には図中矢印bで示すようなエアーの流れが発生しており、かかるエアーの流れの中をALC板11が送られることにより、その表面の塗装部分が滑らかに伸ばされるとともに気泡内部へも塗料が流れ込むこととなる。 By such a vacuum chamber 34 adjacent the pressure chamber 35 is generated an air flow as indicated by the arrow b, the inside of such air flow ALC plate 11 is sent, and the surface paintwork is that paint flows also to the bubble interior with the smooth extended.

【0050】かくして、ALC板11の表面には、気泡内部まで塗装され、塗装されない箇所のないように塗料液膜20が形成されることとなる。 [0050] Thus, the surface of the ALC plate 11, is coated to the inside bubbles, so as not places that are not coated so that the coating liquid film 20 is formed.

【0051】因みに、図3は図1について上述した塗装装置10の塗装処理手順を示すフローチャートである。 [0051] Incidentally, FIG. 3 is a flowchart showing a painting procedure of coating apparatus 10 described above with reference to FIG.
この図2に示されるように、塗装装置10がステップA As shown in FIG. 2, the coating apparatus 10 Step A
1から当該処理手順に入ると、塗装対象であるALC板11は、ステップA2に移る。 Once from 1 to the processing procedure, ALC plate 11 is coated object, the process proceeds to step A2.

【0052】ステップA2において、塗装装置10は、 [0052] In step A2, the coating apparatus 10,
プレヒート部25によってALC板11を加熱した後、 After heating the ALC plate 11 by preheating section 25,
ステップA3に移る。 It proceeds to step A3. ステップA3からは塗装部30における塗装工程に入り、当該ステップA3において塗装装置10は、噴射塗装部32によってALC板11の表面に塗料の塊を高圧噴射する。 From step A3 enters the painting process in the coating unit 30, coating apparatus 10 in the step A3, the high-pressure injection chunks of paint on the surface of the ALC plate 11 by injection coating unit 32. そしてステップA4に移って、エアーブロー部33においてエアカッタ65による余分な塗料の削ぎ取り処理を行い、塗料液膜20を形成する。 Then the process shifts to a step A4, it performs stripped up processing of surplus color by Eakatta 65 in an air blowing unit 33, to form a coating liquid film 20. さらにステップA5に移って、減圧室34によって、ALC板11の表面の塗料が確実に入りきっていない気泡つまり、塗料液膜20の形成によって残留する気泡内に閉じ込められた空気のある状態の、気泡内の空気溜を膨張させることによってはじけさせ、ステップA Furthermore proceeds to step A5, by vacuum chamber 34, it bubbles paint surfaces of ALC plate 11 is not completely enter the certainty that is, the states of air trapped inside the bubbles remaining by the formation of the coating liquid film 20, popped by inflating the air reservoir in the bubble, step a
6に移る。 Turning to 6.

【0053】ステップA6において、塗装装置10は気泡内で空気溜がはじけてピンホールが形成された状態のALC板11を加圧室35に送ることにより、ALC板11の表面に形成された塗料液膜20に空気を吹き付けて塗料液膜20の表面の塗料を気泡内に流し込み前記ピンホールを閉鎖し、かつ塗料液膜20を滑らかに伸ばす。 [0053] In step A6, the coating apparatus 10 by sending an ALC plate 11 of the pin hole is formed by bursting of the air reservoir in the bubbles into the pressurizing chamber 35, formed on the surface of the ALC plate 11 coating by blowing air paint surface of the coating liquid film 20 closes the pinhole poured into bubbles liquid film 20, and smoothly stretch the coating liquid film 20. かくして塗装装置10はステップA7において塗料液膜の乾燥及び冷却をしALC11に対する塗装工程を終了する。 Thus the coating apparatus 10 finishes the painting process for ALC11 dried and cooling of the coating liquid film in the step A7.

【0054】次に、図4(a)、(b)、(c)、 Next, FIG. 4 (a), (b), (c),
(d)及び図5に於て、ALC板1の表面に設けられた気泡内に塗膜が形成される状態を工程順に説明する。 (D) and At a 5, illustrating a state in which the coating is formed inside the bubbles formed on the surface of the ALC plate 1 in order of steps. 即ち、ALC板11の表面には、図4(a)の加圧吹付室に於て、多量の塗料12が高圧吹付けによって肉厚に装着される(前記ステップA3)。 That is, the surface of the ALC plate 11, At a - added 圧吹 chamber of FIG. 4 (a), a large amount of paint 12 is attached to the wall thickness by a high 圧吹 with (step A3). その際に、塗料12はALC板11の表面に内在する気泡3内に、その入口より押し込められてその気泡3の奥に空気を閉じ込めて空気溜5を形成する。 At that time, the coating 12 is in the bubble 3 inherent in the surface of the ALC plate 11, is pushed from its inlet to form an air reservoir 5 confine the air to the back of the bubbles 3. 同図(b)の空気吹付室に於て、ノズルより高圧空気が噴出されて、ALC板11の表面に装着された塗料12の内の余分なものが除去されてAL At a air spray booth of FIG. (B), high pressure air from the nozzle is jetted, extra ones of the coating 12, which is attached on the surface of the ALC plate 11 is removed AL
C板11の表面には塗料液膜20が形成される(前記ステップA4)。 The surface of the C plate 11 coating liquid film 20 is formed (step A4).

【0055】続いて、図4(c)の減圧室に於て、AL [0055] Then, At a vacuum chamber of FIG. 4 (c), AL
C板11に塗着された塗料液膜20の表面が減圧されるので、前述のように気泡3内に閉じ込められていた空気溜5の空気は膨張して、気泡3内の入口に押し込められていた塗料よりなる塗料液膜20を破裂させて外方に放出される。 Since the surface of the C plate 11 coating liquid film 20 is coated on is reduced, air in the air reservoir 5 which has been trapped inside bubbles 3 as described above is expanded, pushed into the inlet of the bubble 3 is released to the outside paint liquid film 20 made of, it had paint ruptured. その空気が放出された塗料液膜20の所定の部分にはピンホール4が形成される(前記ステップA Pinhole 4 is formed in a predetermined portion of the coating liquid film 20 to which the air has been released (step A
5)。 5).

【0056】さらに図4(d)の加圧室に於て、ノズルより高圧空気をALC板11の表面の塗料液膜20に吹き付けることによって、前述のように気泡3内に閉じ込められていた空気が放出された後のピンホール4の周りの塗料液膜20の塗料の一部が、ピンホール4内に流入してピンホール4を閉鎖し、この部分に塗料による塗料液膜20を形成する。 [0056] Te further at the pressure chamber in FIG. 4 (d), by blowing high pressure air to the coating liquid film 20 on the surface of the ALC plate 11 from the nozzle, the air which has been trapped inside bubbles 3 as described above There is a part of the paint in the paint liquid film 20 around the pinhole 4 after being released, the pin hole 4 closes to flow into the pin hole 4, to form a coating liquid film 20 by coating this part . 同時にこの空気の吹付けによって塗料液膜20の表面を滑らかに伸ばすことが出来る(前記ステップA6)。 Simultaneously with spraying air paint liquid film 20 surface smoothly extending it possible for (step A6). 従って、本発明の方法を実施することによって、図4(d)及び図5に示す如く、気泡3の内部の奥部全面にも塗装されない個所のないように塗料液膜20を形成することが出来る。 Thus, by practicing the process of the present invention, to form a FIG 4 (d) and as shown in FIG. 5, the coating liquid film 20 so as not places that are not coated in the interior of the inner part entirely of the bubble 3 can.

【0057】前述のように本発明の方法を実施して製造したALC板の表面を顕微鏡写真で撮影した状態が、図6(a)に示すものである。 [0057] state that the surface of the ALC plate method was prepared by carrying out the present invention taken with a microscope photograph as described above, showing in Figure 6 (a). この写真でも明らかな如く、ALC板の表面に内在する多数の気泡内全面に塗料が充填されると共に、その気泡の内周壁に続く内壁にも塗料が深く浸透されていることが明らかである。 The As is apparent in photographs, along with a number of air bubbles in the entire surface coating inherent in the surface of the ALC plate is filled, it is clear that the paint also on an inner wall that follows the inner peripheral wall of the bubble is deeply rooted.

【0058】図6(b)及び図7(a)、(b)は、それぞれALC板を縦方向に切断したものを撮影した顕微鏡写真であるが、この写真によってALC板の表面にある気泡の内周壁面全面に塗膜が形成されていることが明らかである。 [0058] FIG. 6 (b) and FIG. 7 (a), (b) is a microscopic photograph of the obtained by cutting the ALC plate in the longitudinal direction, respectively, of the air bubbles on the surface of the ALC plate by the photo it is evident that the coating film on the inner peripheral wall surface entirely is formed. 特に、ALC板の表面より離れた、即ちA In particular, apart from the surface of the ALC plate, i.e. A
LC板の内部に存在する内側気泡に於ても、この内側気泡が表面側の気泡に連通している場合には、この内側気泡の内部全面にも塗料が侵入して塗膜が形成されていることが明らかである。 Even at the inner air bubbles present inside the LC panel, when the inner air bubble is communicated with the bubble surface side, coating penetrates paint also inside the whole surface of the inner bubbles formed it is clear that you are.

【0059】前述の本発明に係る装置方法を実施するために使用される塗料について説明すると次の通りである。 [0059] is as follows when described coating used to implement the apparatus method according to the present invention described above. 即ち、本実施の形態に用いる下塗り被覆組成物である水性塗料は、樹脂/顔料=1/10〜6/10(固形分重量比)であり、塗装時における不揮発分が50%以上、#4フォードカップによる粘度が10〜50秒/2 That is, water-based paint is a subbing coating composition used in this embodiment is a resin / pigment = 1 / 10-6 / 10 (solid weight ratio), a nonvolatile content during coating is 50% or more, # 4 viscosity by Ford Cup from 10 to 50 seconds / 2
5で、ラメラ長が3mm以下である下塗り被覆組成物である。 5, a subbing coating composition a lamellar length is 3mm or less. そのためには(A)樹脂、(B)顔料及び(C) To achieve this (A) resin, (B) a pigment and (C)
溶媒に分散するものであり、樹脂としてアクリルエマルション樹脂が好ましいものとして構成される。 Is intended to disperse in a solvent, and as the acrylic emulsion resin is preferably a resin.

【0060】樹脂塗膜を形成する樹脂としては、例えばアクリル樹脂、シリコン変性アクリル樹脂等の水溶性、 [0060] As the resin for forming the resin coating film, for example, acrylic resins, water-soluble, such as silicone-modified acrylic resin,
水分散(エマルション)型の水性樹脂が挙げられ、特に、アクリル樹脂又はシリコン変性アクリル樹脂のエマルション樹脂が好ましく用いられる。 Aqueous dispersion (emulsion) type of aqueous resin. Particularly, emulsion resin of an acrylic resin or a silicone-modified acrylic resin is preferably used. ヒドラジド、グリシジルメタアクリレート、シラノール、オキサゾリン、 Hydrazide, glycidyl methacrylate, silanol, oxazoline,
酸化金属等の架橋材と混合して使用することも出来る。 It can also be used in admixture with the crosslinking material such as a metal oxide.
また、これらの樹脂は、1種に限らず2種以上を組み合わせて使用することが出来る。 These resins may be used in combination of two or more it is not limited to one type.

【0061】本実施の形態の下塗り被覆組成物は、ラメラ長が3mm以下であることが好ましい。 [0061] subbing coating composition of the present embodiment is preferably lamellar length is less than 3mm. ラメラ長とは、塗料等の液状膜における液切れの程度を示すもので、測定値が小さいほど塗料の液膜が切れやすく、空気吹付けによる過剰塗料の除去がしやすい。 The lamellar length, indicates the degree of liquid exhaustion at the liquid film of the paint or the like, the more prone to breakage coating liquid film is measured is small, easier to remove excess paint by air spraying. ラメラ長が3 Lamellar length is 3
mmを超えると、塗料の液膜の液切れが良くなく、空気吹付けによる過剰塗料の除去が困難となる傾向がある。 Beyond mm, no good solution break the coating liquid film tends to remove excess paint by air spraying becomes difficult.
より好ましくは、0.1〜2mmである。 More preferably, a 0.1~2mm.

【0062】因みに、防水用塗料組成物としてアクリルエマルション系のシーラー(オーデータイト155、日本ペイント社製)を用いて塗布量と透水量の対比を行った。 [0062] Incidentally, it was compared with a coating weight of the water permeation amount by using the acrylic emulsion sealer (O data byte 155, manufactured by Nippon Paint Co., Ltd.) as a waterproof coating composition. 本発明の方法により加圧吹付けシャワーとエアーナイフとを使用した場合(2回処理)、シーラーの塗布量が750〜850g/m 2で透水量が2cc/24時間以下であった。 When using a pressurized圧吹shower and air knife according to the method of the present invention (2 times processing), the coating amount of the sealer water permeation amount 750~850g / m 2 was less than 2 cc / 24 hr. 一方、従来法である一般的なスプレーの2 On the other hand, the general spray a conventional method 2
度塗りでは、シーラーの塗布量を2100g/m 2にしても透水量が4cc/24時間以下になる程度であった。 The degree coating, even if the coating amount of sealer to 2100 g / m 2 water permeability was much reduced below 4 cc / 24 hr.
なお、透水量を測定する方法として、ロートを逆さにしてALC表面に立て、ロート円周部をシーラーで止め水を注入する方法を用いた。 As a method of measuring the water permeability, standing on ALC surface is a funnel turned upside down, the funnel circumference using the method of injecting the water stop with sealer.

【0063】さらに本発明の塗装方法の動作について説明すると、次の通りである。 [0063] To further illustrate the operation of the coating method of the present invention is as follows. 即ち、上述のような機能、 In other words, the function as described above,
構成を有する本発明に係る塗装装置10においては、その塗装部30において、ALC板11の表面に高圧で叩き付けられた塗料のうち、余分な塗料をエアーカッタ6 In the coating apparatus 10 according to the present invention having the structure, in its coating unit 30, among the coatings which are slammed at high pressure to the surface of the ALC plate 11, air cutter excess paint 6
5によって削ぎ落とす。 5 by scraped off. ここにおいては、ALC板11 In this case, ALC plate 11
の表面には塗料(被覆組成物)が本来有する防水性等の特性を発揮するために必要十分な厚みの塗料液膜20が確保される。 The surface of the paint (coating composition) of the coating liquid film 20 necessary and sufficient thickness to exhibit the characteristics of the waterproof and the like inherent is ensured. これは、従来のように、塗装乾燥後に塗料液膜下にある気泡が破けて膜厚が薄くなったり、塗り残しが発生することに対応して余分な厚みを確保する場合に比べて、一段と薄い膜厚となっている。 This, as is traditional, as compared with the case of securing or film thickness bubbles torn under the coating liquid film becomes thinner after coating drying, the excess thickness in response to the unpainted occurs, further and it has a thin film thickness.

【0064】このような厚みで形成された塗料液膜は、 [0064] coating liquid film formed in such a thickness,
その下に多孔質素材表面の気泡の内に塗料が完全に入っていない気泡が生じている状態となっているが、塗装装置10は、当該気泡が生じている塗料液膜を形成してなるALC板11を減圧室34に入れることにより、気泡3の内部の気圧が減圧室34の気圧よりも高くなって、 While in a state of bubbles paint is not in the completely within the bubble of the porous material surface under it occurs, coating apparatus 10 is obtained by forming a coating liquid film in which the bubble is generated by placing the ALC plate 11 to vacuum chamber 34, the internal air pressure of the bubble 3 is higher than the pressure of the decompression chamber 34,
気泡3内に閉じ込められている空気溜5の空気が膨張してはじけることとなる。 Air in the air reservoir 5 so that the popping and expansion have been trapped inside the bubbles 3.

【0065】このように空気溜5がはじけた塗料液膜2 [0065] Coating Solution film 2 is air reservoir 5 bursting in this way
0の表面は、はじけた部分においてピンホール4等の凹凸を有する状態となっているが、かかる塗膜は未だ硬化していない状態であり、このような状態において続く加圧室35に入ることにより、空気を吹き付けることによって加圧エアーの流れによって塗料液膜20の表面がならされ、気泡内に塗料が流れ込み、塗り残しのない塗料液膜20となる。 Surface of the 0 is in a state having unevenness such as pinholes 4 in burst portion, such coating is in a state that is not cured yet, to enter the pressurizing chamber 35 continues in this state by being not the surface of the coating liquid film 20 by the flow of pressurized air by blowing air, paint flows into the bubble, the coating liquid film 20 without unpainted. かくして、ALC板11の表面にはその凹凸(微細な穴)に十分に行き渡った塗り残した気泡3がなくかつ必要十分な厚みの塗膜が形成されることとなる。 Thus, the surface of the ALC plate 11 so that the coating of the unevenness (fine holes) without air bubbles 3 unpainted to sufficiently distributed throughout the necessary and sufficient thickness is formed.

【0066】なお上述の実施形態においては、減圧室3 [0066] In the above embodiment, the vacuum chamber 3
4によって気泡3の空気溜5がはじけた状態で、当該塗料液膜20が形成されたALC板11を加圧室35に入れ、加圧室35から減圧室34に流れる空気によって塗料液膜20を伸ばすようにしたが、本発明はこれに限らず、例えば噴射ノズルを用いて塗料液膜20の表面に空気を吹き付けるようにしてもよく、要は、塗料液膜20 In a state where the air reservoir 5 of the bubble 3 was burst by 4, the coating liquid film 20 by the air flowing through the ALC plate 11 to which the coating liquid film 20 is formed taking into pressurizing chamber 35, the vacuum chamber 34 from the pressurizing chamber 35 was to extend the present invention is not limited to this, it may also be blow air for example by using an injection nozzle to the surface of the coating liquid film 20, short, paint-film 20
の表面を空気の流れにさらすようにすればよい。 The surface of it is sufficient to expose the flow of air.

【0067】また上述の実施形態においては、図2に示した構成のフィルタ90を用いて回収塗料を濾過する場合について述べたが、本発明はこれに限らず、回収塗料を攪拌しながら濾過するフィルタや、濾過前に回収塗料に加水を行い濾過をしやすくするフィルタ等、他の種々の構成のフィルタを用いるようにしてもよい。 [0067] In the embodiment described above has dealt with the case of filtering the recovered paint with a filter 90 having the structure shown in FIG. 2, the present invention is not limited thereto, and filtered while stirring recovered paint filter or filter or the like to facilitate the filtration performed hydro to recover the paint prior to filtration may be used other filters of various configurations.

【0068】また上述の実施形態においては、加圧室3 [0068] In the embodiment described above, the pressurizing chamber 3
5から減圧室34にエアーの流れを生じさせて、塗料液膜20の表面を均一に伸ばすようにしたが、本発明はこれに限らず、加圧室35を設けることなく、減圧室34 5 causes the air flow to the vacuum chamber 34 from, has been to extend uniformly the surface of the coating liquid film 20, the present invention is not limited to this, without providing the pressurizing chamber 35, vacuum chamber 34
に対して外部空間からエアーが流れ込むようにすることによって、当該流れ込むエアーによって塗料の表面を伸ばすようにしてもよい。 Respect by ensuring that air flows from the outer space, it may be extended to the surface of the paint by the air to the flow.

【0069】 [0069]

【発明の効果】本発明の塗装方法に於ては、多孔質素材の表面に塗料を加圧吹付けするので、多孔質素材の表面に内在する気泡内にも塗料を押し込めて塗着して多孔質素材の表面全面に所定厚の塗料液膜を形成することが出来る効果を有している。 Te is at the coating method of the present invention, since the coating on the surface of the porous material to give pressurized 圧吹, and coating wear tucked paint in the air bubbles inherent in the surface of the porous material It has the effect that can be formed on the entire surface of the porous material having a predetermined thickness of the coating liquid film. また、多孔質素材の表面に所定厚の塗料液膜が形成された後で多孔質素材の塗料液膜表面を減圧するので、この該塗料液膜の形成によって閉じ込められていた気泡内の空気溜を膨張破裂させ、後になってピンホールの発生の大きな原因となる気泡内の空気を事前に放出して除去することが出来る効果を有している。 Further, since the reduced pressure paint liquid film surface of the porous material after the coating liquid film having a predetermined thickness on the surface of the porous material is formed, the air reservoir in the bubbles that were trapped by the formation of the coating composition liquid film the has the effect of air can be removed by releasing beforehand in bubble inflated rupture, a major cause of the occurrence of pinholes at a later.

【0070】前記多孔質素材の表面に塗料を加圧吹付けしてその表面に塗料を塗着した後で、表面に付着した過剰分の塗料を除去手段によって除去した場合には、多孔質素材の表面に形成される塗料の肉厚を一定に保つことが出来、しかも除去した塗料は再利用することが出来るので、極めて経済的である等の効果を有している。 [0070] After Nurigi paint to the surface to put pressure 圧吹 paint to the surface of the porous material, when removed by excess paint removal means attached to the surface, the porous material since the thickness of the coating formed on the surface of the can be kept constant, moreover removed paint can be reused, has an effect equal is very economical. かつ、前記多孔質素材の塗料液膜表面の減圧によって塗料液膜の形成により閉じ込められた気泡内の空気溜を膨張破裂させた後で、塗料液膜の表面に空気を吹付けた場合には、塗料液膜を形成するまだ流動性を持った塗料液を気泡内全面に流入させて塗膜を形成し、気泡内に未塗装部分が設けられることを防止出来る効果を有している。 And, the air reservoir in the trapped air bubbles by forming a coating liquid film by vacuum of the paint liquid film surface of the porous material after inflated rupture, when blowing air to the surface of the coating liquid film , still paint liquid having flowability to form a coating liquid film to flow into the bubble within the entire surface to form a coating film, unpainted portion has the effect that can prevent provided inside the bubbles.

【0071】本発明に係る塗装装置に於ては、塗料を該多孔質素材の表面に強く吹付けることが出来る加圧吹付装置を設けたので、この装置によって多孔質素材の表面に内在する気泡内に塗料を押し込めることが出来る。 [0071] Te is at the coating apparatus according to the present invention, is provided with the coating the porous pressurized 圧吹 with device strongly capable sprayed on the surface of the material, air bubbles inherent in the surface of the porous material by the device You can of sticking the paint within. かつ、除去装置によって多孔質素材の表面に塗着された過剰な塗料を除去することが出来る効果を有している。 And has the effect capable of removing the excess coating material is coated on the surface of the porous material by the removal device. また、減圧装置が設けられているので、この装置によって多孔質素材の塗料液膜表面を減圧させることによって、 Further, since the decompression device is provided, by vacuum paint liquid film surface of the porous material by the device,
多数の気泡内に塗料液膜の形成により閉じ込められていた空気溜を膨張破裂させて気泡内から除去することが出来る効果も有している。 Several advantages that can be removed from the air reservoir which has been trapped by the formation of the coating liquid film is expanded ruptured inside the bubbles within bubbles have.

【0072】さらに、前述の装置とは別に空気吹付装置が設けられているので、この装置で多孔質素材の表面に塗着された塗料液膜に空気を強く吹付けることによって、塗料液を前記多孔質素材の表面に内在する多数の気泡内に流入させて気泡内に塗膜を形成することが出来る効果も有している。 [0072] Further, since the separate air blowing device and the aforementioned devices are provided, by attaching a strong blow air into the coating liquid film which is coated on the surface of the porous material in this device, the paint liquid several advantages that can which is flowed into the bubble to form a coating film on the bubbles inherent in the surface of the porous material also has.

【0073】本発明に係る防水性塗料は、多孔質素材の表面に加圧吹付けによって塗着された際に、多孔質素材の表面に内在する気泡内に容易に流入して塗料液膜を形成することが出来、かつ多孔質素材を減圧した際には気泡内の空気溜を簡単に膨張破裂させることも出来、さらに空気吹付装置で空気を強く吹き付けられた際には、塗料液膜の一部の塗料液が気泡内にスムーズに流入して気泡内全面を塗装することが出来る特性を有している。 [0073] waterproof coating according to the present invention, when it is coated applied by pressurization 圧吹 with the surface of the porous material, the coating liquid film is easily flows into the bubbles inherent in the surface of the porous material It can be formed, and when the porous material and pressure reduction can also be easily expanded burst of air reservoir in the bubbles, when further blown strongly air with air blowing device, the coating liquid film and a can characteristic that some of the paint liquid is coated bubbles in the entire surface and flows smoothly into the bubble.

【0074】本発明に係る多孔質素材は、多数の気泡内に空気溜が存在しないので、後から気泡内の空気溜が膨張破裂して、気泡の入口に被覆されていた防水塗料膜の一部にピンホールが生ずる恐れがない。 [0074] The porous material according to the present invention, since there is no air reservoir in the number of bubbles, the air reservoir in bubbles later expands ruptured, waterproof paint film which has been coated on the inlet of the bubble one there is no risk of causing pinhole in part. また、多数の気泡の内周面全面には所定厚の塗料膜が被覆されているので、気泡の内周壁面より雨水が多孔質素材内に浸み込む心配もない等の多大な効果を有している。 Further, since numerous inner circumferential surface entire predetermined thickness of the paint film to the bubble are covered, significant effects such as rainwater from the inner peripheral wall surface of the air bubbles no fear Komu penetrates into the porous material Yes doing.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】 本発明の塗装方法を実施するための装置の簡略説明図である。 1 is a simplified illustration of an apparatus for carrying out the coating method of the present invention.

【図2】 図1の装置に取付けられるフィルタの断面図である。 2 is a cross-sectional view of a filter attached to the apparatus of FIG.

【図3】 本発明の方法を示すフローチャート図である。 3 is a flowchart showing a method of the present invention.

【図4】 図4(a)、(b)、(c)、(d)は夫々ALC板の表面の気泡内に塗膜が形成される工程を示す断面説明図である。 [4] FIG. 4 (a), a cross-sectional view showing a (b), (c), (d) the step of coating is formed in the bubble surface of each ALC plate.

【図5】 本発明のALC板の要部の断面拡大説明図である。 5 is a cross-sectional enlarged view of a main part of the ALC plate of the present invention.

【図6】 図6(a)は本発明のALC板の平面の顕微鏡写真図、図6(b)は同図の要部の縦断面の顕微鏡写真図である。 [6] FIG. 6 (a) micrograph of a plane of the ALC plate of the present invention, FIG. 6 (b) is a micrograph of a longitudinal section of a main part of FIG.

【図7】 図7(a)、(b)は夫々図6(a)の要部の縦断面の顕微鏡写真図である。 [7] FIG. 7 (a), the a micrograph of a longitudinal section of an essential part of (b) are each FIG 6 (a).

【図8】 従来例の塗装されたALC板の表面の縦断面拡大図である。 8 is a vertical sectional enlarged view of a painted ALC plate surface of the conventional example.

【図9】 図9(a)は従来例の塗装されたALC板の表面の顕微鏡写真である。 [9] FIG. 9 (a) is a photomicrograph of a painted ALC plate surface of the conventional example. 図9(b)は従来例の塗装されたALC板の表面側の縦断面の顕微鏡写真である。 9 (b) is a photomicrograph of a longitudinal section of the surface side of the conventional example of painted ALC plate.

【図10】 従来例の塗装されたALC板であって、表面に多量の塗料が塗着された状態の縦断面拡大説明図である。 [Figure 10] A ALC plate painted in the conventional example, is a vertical sectional enlarged view of a state where a large amount of coating material on the surface is coated wear.

【符号の説明】 DESCRIPTION OF SYMBOLS

1 …ALC板 2 …塗膜 3 …気泡 4 …ピンホール 5 …空気溜 10 …塗装装置 11 …ALC板 12 …塗料 20 …塗料液膜 22 …制御部 25 …プレヒート部 26 …センサ 30 …塗装部 32 …噴射塗装部 33 …エアーブロー部 34 …減圧室 35 …加圧室 41 …シャッタ 42 …隔壁 43 …隔壁 44 …隔壁 46 …回収タンク 51 …配管 52 …ポンプ 53 …液圧計 54 …噴射ノズル 61 …ブロアー部 62 …エアー分配室 65 …エアーカッタ 72 …搬送ローラ 73 …搬送ローラ 90 …フィルタ 91 …筐体 92 …金網 95 …廃棄槽 96 …タンク 1 ... ALC plate 2 ... coating 3 ... bubble 4 ... pinhole 5 ... air reservoir 10 ... coating apparatus 11 ... ALC plate 12 ... coating 20 ... coating liquid film 22 ... controller 25 ... preheat section 26 ... sensor 30 ... coating unit 32 ... injection painting section 33 ... air blow section 34 ... decompression chamber 35 ... pressure chamber 41 ... shutter 42 ... partition wall 43 ... partition wall 44 ... partition wall 46 ... recovery tank 51 ... pipe 52 ... pump 53 ... liquid gauge 54 ... injection nozzle 61 ... blower unit 62 ... air distribution chamber 65 ... air cutter 72 ... conveying rollers 73 ... conveying rollers 90 ... filter 91 ... housing 92 ... wire mesh 95 ... disposal tank 96 ... tank

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl. 7識別記号 FI テーマコート゛(参考) B05D 1/02 B05D 1/02 Z 4J038 3/02 3/02 B 7/00 7/00 C C09D 5/02 C09D 5/02 133/00 133/00 // C04B 41/63 C04B 41/63 (71)出願人 591006612 東海産機株式会社 愛知県名古屋市南区城下町1丁目1番地 (72)発明者 濱邊 敏樹 東京都千代田区有楽町1丁目1番2号 旭 化成株式会社内 (72)発明者 駒坂 昇一 東京都千代田区有楽町1丁目1番2号 旭 化成株式会社内 (72)発明者 小池 喜寛 東京都品川区南品川4丁目1番15号 日本 ペイント株式会社内 (72)発明者 長副 直道 茨城県つくば市片田字浦割東492丁目1番 東亜工業株式会社内 (72)発明者 内藤 隆 愛知 ────────────────────────────────────────────────── ─── front page continued (51) Int.Cl. 7 identifications FI theme coat Bu (reference) B05D 1/02 B05D 1/02 Z 4J038 3/02 3/02 B 7/00 7/00 C C09D 5 / 02 C09D 5/02 133/00 133/00 // C04B 41/63 C04B 41/63 (71) the applicant 591,006,612 Tokai Industrial equipment Co., Ltd., Nagoya, Aichi, Minami-ku, castle town 1-chome address 1 (72) inventor Hama邊 Toshiki Chiyoda-ku, Tokyo Yurakucho 1-chome No. 1 No. 2 Asahi Kasei Co., Ltd. in the (72) inventor frame Shoichi Saka, Chiyoda-ku, Tokyo Yurakucho 1-chome No. 1 No. 2 Asahi Kasei Co., Ltd. in the (72) inventor Koike KiHiroshi Tokyo Shinagawa Subdivision Minamishinagawa 4 chome No. 15 Nippon paint Co., Ltd. in the (72) inventor length Vice Naomichi Tsukuba, Ibaraki Prefecture Katada shaped Ura Warihigashi 492 chome Toa industry Co., Ltd. in the (72) inventor Takashi Naito Aichi 県名古屋市南区城下町1丁目1番 東 海産機株式会社内 Fターム(参考) 4D073 AA01 BB06 DC02 DC22 4D075 AC01 AC60 AC84 AC95 BB23X BB57Y BB57Z BB93X BB93Y BB93Z CA38 DA06 DB12 DC02 EA05 EA06 EA10 EA13 EB22 EB45 EB52 EC02 EC37 4F041 AA02 AA08 AB01 BA10 BA51 BA54 BA59 4F042 AA02 AA17 BA07 CB02 CB03 CB10 CC02 CC09 CC22 CC30 DA09 DD07 DD31 DD34 ED05 4G028 CA01 CB04 CB08 CC01 CD03 4J038 CG141 DL131 KA03 MA08 MA10 NA01 NA04 PA15 PB05 PC04 Prefecture Nagoya Minami-ku castle town chome east marine machine Co., Ltd. in the F-term (reference) 4D073 AA01 BB06 DC02 DC22 4D075 AC01 AC60 AC84 AC95 BB23X BB57Y BB57Z BB93X BB93Y BB93Z CA38 DA06 DB12 DC02 EA05 EA06 EA10 EA13 EB22 EB45 EB52 EC02 EC37 4F041 AA02 AA08 AB01 BA10 BA51 BA54 BA59 4F042 AA02 AA17 BA07 CB02 CB03 CB10 CC02 CC09 CC22 CC30 DA09 DD07 DD31 DD34 ED05 4G028 CA01 CB04 CB08 CC01 CD03 4J038 CG141 DL131 KA03 MA08 MA10 NA01 NA04 PA15 PB05 PC04

Claims (8)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 多数の気泡が内在する多孔質素材の表面に防水性塗膜を形成する塗装方法に於て、前記多孔質素材の表面に塗料を加圧吹付けして前記多孔質素材の気泡内に塗料を押し込めて所定厚の塗料液膜を形成し、該多孔質素材の該塗料液膜表面を減圧することによって塗料液膜の形成により閉じ込められた気泡内の空気溜を膨張破裂させて塗膜を形成させることを特徴とした多孔質素材の塗装方法。 1. A At a coating method a large number of bubbles to form a waterproof coating film on the surface of the porous material underlying the porous material to put pressure 圧吹 paint to the surface of the porous material tucked paint to form a coating liquid film having a predetermined thickness in the air bubbles, the air reservoir in the bubbles trapped by the formation of the coating liquid film is expanded ruptured by reducing the pressure of the paint liquid film surface of the porous material the porous material the method of coating which is characterized in that to form a coating film Te.
  2. 【請求項2】 前記多孔質素材の表面に塗料を加圧吹付けして前記多孔質素材の気泡内に塗料を押し込めた後で、該多孔質素材の表面の過剰分の塗料を除去手段で除去することを特徴とした請求項1の多孔質素材の塗装方法。 Wherein after tucked paint to the porous the porous foam material paint on the surface of the material to put pressure 圧吹, the excess coating material on the surface of the porous material removal means the porous material the method of coating of claim 1 which is characterized in that removal.
  3. 【請求項3】 前記塗料液膜の形成により閉じ込められた気泡内の空気溜を、前記多孔質素材の該塗料液膜表面の減圧によって膨張破裂させた後で、塗料液膜表面に空気を吹付けることによって前記気泡内全面に塗料液を流入させて塗膜を形成させることを特徴とした請求項1或は請求項2の多孔質素材の塗装方法。 The wherein the air reservoir in the trapped air bubbles by forming the coating liquid film, after inflating ruptured by vacuum of the porous material paint liquid film surface, blowing air into the coating liquid film surface claim 1 or porous material method of coating according to claim 2 characterized in that to form a coating film allowed to flow into the paint liquid to the bubble in the entire surface by attaching.
  4. 【請求項4】 前記多孔質素材の表面に塗料を加圧吹付けする以前に該多孔質素材を加熱して所定の温度にすることを特徴とした請求項1乃至請求項3の多孔質素材の塗装方法。 4. The porous material of the porous claim previously by heating the porous material is characterized in that a predetermined temperature of the coating material on the surface of the material to put pressure 圧吹 1 to claim 3 method of painting.
  5. 【請求項5】 多数の気泡が内在する多孔質素材の表面に防水性塗膜を形成する塗装装置に於て、前記多孔質素材の表面に塗料を加圧吹付けて前記多数の気泡内に塗料を押し込める加圧吹付装置と、過剰分の塗料を除去する除去装置と、多孔質素材の塗料液膜表面を減圧することによって前記多数の気泡内に塗料液膜の形成によって閉じ込められた空気溜を膨張破裂させる減圧装置と、空気を塗料液膜表面に吹付けることによって塗料液を前記気泡内に流入させる空気吹付装置との組合せより構成されることを特徴とした多孔質素材の塗装装置。 At a wherein a number of coating apparatus for forming a waterproof coating film on the surface of the porous material bubbles inherent in the porous the number of the bubbles paint on the surface of the material put pressure 圧吹a pressing 圧吹 with apparatus of sticking paint, a removal device for removing excess paint, the air reservoir trapped by the formation of the coating liquid layer in the number of bubbles by reducing the pressure of the coating liquid film surface of the porous material a decompressor for inflating rupture the porous material of the coating apparatus the coating liquid was characterized in that it is composed of a combination of an air spray apparatus for flowing into the bubble by blowing air into the coating liquid film surface.
  6. 【請求項6】 前記除去装置の作動によって除去された過剰分の塗料を回収する回収槽と、回収槽に回収された過剰塗料を濾過して再利用する濾過装置とを具備したことを特徴とした請求項5の多孔質素材の塗装装置。 6. A collecting tank for collecting the excess coating removed by the operation of the removing device, and characterized in that the excess paint collected in the collection vessel was and a filtration device to be reused by filtration the porous material of the coating apparatus of claims 5.
  7. 【請求項7】 前記多孔質素材の塗装方法或は多孔質素材の塗装装置に用いられる防水性塗料に於て、水溶性、 7. At a waterproof paint used in painting equipment coating method or a porous material of the porous material, a water-soluble,
    水分散型および/またはエマルジョン型の水性樹脂であって、アクリル樹脂、変性アクリル樹脂等の1種または2種以上の混合物及びヒドラジド、グリシジルメタアクリレート、シラノール、オキサゾリン、酸化金属等の架橋剤の1種または2種以上を主成分として構成されたことを特徴とした多孔質素材の塗装用の防水性塗料。 A water-dispersible and / or emulsion type of aqueous resin, the first acrylic resin, one or a mixture of two or more such modified acrylic resin and a hydrazide, glycidyl methacrylate, silanol, oxazoline, such metal oxide cross-linking agent waterproof paint for painting a porous material which is characterized in that it is configured or more species or two or as a main component.
  8. 【請求項8】 表面と連通する気泡を多数有する多孔質素材に於て、該多数の気泡内に空気溜が存在せず、かつこれ等の気泡の内周面全面に所定厚さの塗料膜が被覆されて形成されていることを特徴とした多孔質素材。 At a 8. porous material having a large number of air bubbles in communication with the surface, there is no air reservoir in the bubbles said multiple, and which like a predetermined thickness of the coating film on the inner peripheral surface entire bubbles porous material which is characterized in that There are formed is coated.
JP2001089815A 2001-03-27 2001-03-27 Coating method and apparatus of the porous material Active JP3730529B2 (en)