JP2002267815A - Reflection preventive molded part and method for manufacturing the same - Google Patents

Reflection preventive molded part and method for manufacturing the same

Info

Publication number
JP2002267815A
JP2002267815A JP2001064668A JP2001064668A JP2002267815A JP 2002267815 A JP2002267815 A JP 2002267815A JP 2001064668 A JP2001064668 A JP 2001064668A JP 2001064668 A JP2001064668 A JP 2001064668A JP 2002267815 A JP2002267815 A JP 2002267815A
Authority
JP
Japan
Prior art keywords
molded article
mold
light
resin
anti
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2001064668A
Other languages
Japanese (ja)
Inventor
Fumihiro Arakawa
Hiroko Suzuki
文裕 荒川
裕子 鈴木
Original Assignee
Dainippon Printing Co Ltd
大日本印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dainippon Printing Co Ltd, 大日本印刷株式会社 filed Critical Dainippon Printing Co Ltd
Priority to JP2001064668A priority Critical patent/JP2002267815A/en
Publication of JP2002267815A publication Critical patent/JP2002267815A/en
Application status is Pending legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To eliminate defects of a reflection preventing measure which is conventionally used for a display or the like, i.e., such unsatisfactory aspects as a production efficiency, a coloring which happens depending on a viewing angle, the reproducibility of a projected and recessed mold in production.
SOLUTION: The reflection preventive molded part is composed of a reflection preventive structure 3 on at least one surface or both surfaces of a molded part 2. The structure 3 comprises innumerable ruggedness with a pitch equal to or smaller than a wavelength of light and has a refractive index varying in the thickness direction. The reflection prevention structure 3 may be continuously made with the raw material of the molded work on the surface of the molded work 2 or placed on a surface layer 4 which is a different layer.
COPYRIGHT: (C)2002,JPO

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、各種ディスプレイ装置の観察側に配置され、室内照明や屋外の太陽光等がディスプレイの観察側の表面で反射し、まぶしく感じれられることを抑制したり、透明素材からなる場合に、光が入射する際、反射を起こし、入射効率が低下することを抑制するための反射防止性成形品、およびその製造方法に関するものである。 BACKGROUND OF THE INVENTION The present invention is disposed on the observation side of various display devices, interior lighting and outdoor sunlight is reflected by the surface of the viewing side of the display, or to prevent the used is felt bright, transparent If made of material, when light is incident, cause reflection, antireflective molded article for incident efficiency to suppress a decrease, and a manufacturing method thereof.

【0002】 [0002]

【従来の技術】ディスプレイ装置としては、種々のものが知られているが、いずれの種類のディスプレイを使用する際にも、そのディスプレイが置かれた空間の照明(人工照明、天然照明を問わない。)が問題となる。 2. Description of the Related Art As a display apparatus, various ones are known, even when using any type of display, illumination of the space that the display is placed (artificial illumination, regardless of natural lighting .) is a problem. 例えば、家庭でテレビ放送を視聴する際に、テレビの置かれた部屋の照明が、映像の見易さに影響を与えることは日常経験することである。 For example, when you watch live TV at home, the lighting of the room, placed the TV, can affect the visibility of the video is to everyday experience. また、視聴する者の位置によっては、画面に照明が写って映像が見えないことすらある。 Also, depending on the position of the person view, even some that video is not visible reflected illumination on the screen. 車載用のテレビであれば、朝日や夕日が車窓から差し込んで、画面で反射し、見づらいことも少なからずある。 If the television mounted on a vehicle, the rising sun and the setting sun is inserted from the car window, I reflected on the screen, hard to see it there not a little.

【0003】勿論、従来から、そのような問題点への対処は色々な方法で行なわれており、その一つに、互いに屈折率の異なる光学薄膜どうしを多層に重ねた透明板を使用して、反射防止を図ることが行なわれていた。 [0003] Of course, conventionally, such a addressing any issues are carried out in a variety of ways, on the one, by using the transparent plate superimposed on the multilayer different optical thin films each other refractive indices , it has been made to achieve antireflection. しかし、この方式によるときは、スパッタ等の真空での薄膜形成の速度が充分でなく、生産効率が悪いこと、また、 However, when by this method, the speed of film formation in a vacuum such as sputtering is insufficient, it is poor production efficiency, also,
見る角度によっては、各薄膜内での光の行路長が変化することから、赤みを帯びたり、青みを帯びる欠点もある。 Depending on the viewing angle, since the path length of light in each thin film is changed, there or reddish, also disadvantages bluish. あるいは、透明板の表面を梨地状態とし、反射防止を図ることも行なわれているが、効果が十分とはいえないものであった。 Alternatively, the surface of the transparent plate and matte finish, but is also made possible to prevent reflection, the effect was achieved not sufficient.

【0004】また、出願人は、特願2000−7434 [0004] In addition, the applicant, Japanese Patent Application No. 2000-7434
7号において、光の波長以下のピッチの無数の微細凹凸が形成された凹凸部を有している反射防止フィルムを提案したが、この反射防止フィルムは、一旦作製した上で、対象物に貼り付けるか、もしくは固定する等の、適用のための手段を別個に要するものであり、形状によっては適用がむずかしい場合もあった。 In No. 7, it has been proposed an anti-reflection film having a myriad of fine irregularities of the pitch of the following wavelengths of light are formed uneven portion, the anti-reflection film, once on prepared, adhered to the object etc. or, or for fixing attached, which requires a separate means for the application, depending on the shape was also applied difficult.

【0005】 [0005]

【発明が解決しようとする課題】本発明においては、従来、ディスプレイ等で用いられてきた反射防止手段の欠点、即ち、生産効率、見る角度によって生じる着色、製造時の凹凸型の再現性等の項目において、不満足であった点を解消することを課題とするものである。 In THE INVENTION It is an object of the present invention, conventional, disadvantages antireflection means has been used in a display or the like, i.e., productivity, see coloration caused by the angle, at the time of manufacture of the irregularities type reproducibility of in item, we are an object of the invention is to eliminate the point was unsatisfactory.

【0006】 [0006]

【課題を解決する手段】本発明と同じ出願人は、特願2 The same applicant as the present invention means to solve the above-mentioned object, No. 2
000−74347号において、光の波長以下のピッチの微細凹凸が形成された凹凸部を有する反射防止フィルムを既に提案しており、この反射防止フィルムを種々のディスプレイ装置に適用するには、貼付け等の手段を要していたのを、ディスプレイ装置に取り付ける板状体に直接、そのような微細凹凸を形成しておくことにより、 In No. 000-74347, an antireflection film having an uneven portion which fine unevenness of the pitch of the following wavelength of light is formed has already proposed to apply the antireflection film in a variety of display devices, pasting, etc. the G-banding method, requires means, directly to the plate-like member attached to the display device, by forming such a fine unevenness,
課題を解決することができた。 We were able to solve the problem.

【0007】第1の発明は、透明性成形品の少なくとも片面に、透明性素材で形成され、光の波長以下のピッチの無数の微細凹凸からなり、厚み方向に光の屈折率が変化する反射防止構造を有することを特徴とする反射防止性成形品に関するものである。 A first invention, on at least one surface of the transparent molded article, formed of a transparent material, made innumerable fine irregularities smaller than the wavelength of the pitch of the light, the refractive index of light varies in the thickness direction of reflection it relates antireflective molded article characterized by having a preventing structure. 第2の発明は、透明性成形品の片面に、透明性素材で形成され、光の波長以下のピッチの無数の微細凹凸からなり、厚み方向に光の屈折率が変化する反射防止構造を有することを特徴とする反射防止性成形品に関するものである。 The second invention, on one surface of the transparent molded article, formed of a transparent material, made innumerable fine irregularities of the following pitch wave of light, having an antireflection structure in which the refractive index changes in the optical thickness direction it relates to antireflective molded article characterized by. 第3の発明は、透明性成形品の両面に、透明性素材で形成され、光の波長以下のピッチの無数の微細凹凸からなり、厚み方向に光の屈折率が変化する反射防止構造を有することを特徴とする反射防止性成形品に関するものである。 A third invention is to both surfaces of the transparent molded article, formed of a transparent material, made innumerable fine irregularities of the following pitch wave of light, having an antireflection structure in which the refractive index changes in the optical thickness direction it relates to antireflective molded article characterized by. 第4の発明は、第1〜第3いずれかの発明において、透明性を有する基板層と前記反射防止構造を有する表面層とが積層されており、各々が一つの射出成形機に接続された異なる樹脂射出装置または複数の樹脂材料を射出する一つの樹脂射出装置から射出された素材からなることを特徴とする反射防止性成形品に関するものである。 The fourth invention is the first to third one of the invention, and a surface layer having the anti-reflection structure and the substrate layer having transparency is laminated, each connected to one of the injection molding machine it relates different resin injection device or antireflective molded article characterized by comprising an injection has been the material from one of the resin injection device in which a plurality of the resin material is injected. 第5の発明は、第1〜第4いずれかの発明において、表面層の一部、表面層の全部、もしくは表面層および基板層を含む全体が電離放射線硬化性樹脂組成物の硬化物からなることを特徴とする反射防止性成形品に関するものである。 According to a fifth invention, in any one of the invention first to fourth, part of the surface layer, the whole comprising all of the surface layer or the surface layer and the substrate layer is made of a cured product of an ionizing radiation curable resin composition it relates to antireflective molded article characterized by.
第6の発明は、内面の少なくとも片面に、光の波長以下のピッチの無数の微細凹凸が形成された金型を準備する準備工程、前記金型の内部に透明性を有する成形用樹脂を射出して充填する充填工程、冷却工程、金型を開いて成形品を取り出す脱型工程とを逐次行なうことからなる反射防止性成形品の製造方法に関するものである。 Sixth invention, at least in one side of the inner surface, a preparation step of preparing a mold having innumerable fine unevenness of the wavelength or less of the pitch of the light is formed, injecting a molding resin having transparency in the interior of the mold filling step of filling in, but the cooling step, a method of manufacturing anti-reflective molded article comprising to perform a demolding step sequential to the mold is opened removing the molded article. 第7 Seventh
の発明は、内面の片面に、光の波長以下のピッチの無数の微細凹凸が形成された金型を準備する準備工程、前記金型の内部に透明性を有する成形用樹脂を射出して充填する充填工程、冷却工程、金型を開いて成形品を取り出す脱型工程とを逐次行なうことからなる反射防止性成形品の製造方法に関するものである。 The invention is on one side of the inner surface, a preparation step of preparing a mold having innumerable fine unevenness of the wavelength or less of the pitch of the light is formed, filled by injection of the molding resin having transparency in the interior of the mold filling step of, those cooling process, a method of manufacturing anti-reflective molded article comprising to perform a demolding step sequential to the mold is opened removing the molded article. 第8の発明は、内面の相対する二面に、光の波長以下のピッチの無数の微細凹凸が形成された金型を準備する準備工程、前記金型の内部に透明性を有する成形用樹脂を射出して充填する充填工程、冷却工程、および金型を開いて成形品を取り出す脱型工程とを逐次行なうことからなる反射防止性成形品の製造方法に関するものである。 An eighth aspect of the present invention, the two opposite sides of the inner surface, a preparation step of preparing a mold having innumerable fine unevenness of the wavelength or less of the pitch of the light is formed, molding resins having transparency in the interior of the mold filling step of filling by injection a, but the cooling step, and a method for producing anti-reflective molded article comprising the mold opening is performed and a demolding step of removing the molded article sequentially. 第9の発明は、第6 A ninth aspect of the invention, a sixth
〜第8いずれかの発明において、前記充填工程を、一つの射出成形機に接続された二以上の樹脂射出装置または複数の樹脂材料を射出する一つの樹脂射出装置を用いて行なうことを特徴とする反射防止性成形品の製造方法に関するものである。 In any of the invention to eighth, and characterized by performing the filling step, using one of the resin injection device for injecting a connected two or more resin injection device or a plurality of resin materials in a single injection molding machine to a method of manufacturing anti-reflective molded article. 第10の発明は、第5〜第9いずれかの発明において、前記充填工程に先立って、金型の内部を排気して真空状態とする排気工程を行なうことを特徴とする反射防止性成形品の製造方法に関するものである。 Tenth invention, in any one of the invention the fifth to ninth, the prior to the filling process, antireflective molded article and performing an exhaust process of the vacuum state by evacuating the interior of the mold the method of manufacturing the present invention relates. 第11の発明は、第10の発明において、前記充填工程中も排気工程を続けることを特徴とする反射防止性成形品の製造方法に関するものである。 An eleventh invention, in the tenth aspect, even during the filling process a process for producing the antireflection molded article, characterized in that continued evacuation process.

【0008】 [0008]

【発明の実施の形態】図1(a)に示すように、本発明の反射防止性成形品1は、例えば、成形品2の片面に、 DESCRIPTION OF THE PREFERRED EMBODIMENTS As shown in FIG. 1 (a), antireflective molded article 1 of the present invention, for example, on one surface of the molded article 2,
光の波長以下のピッチの無数の微細凹凸からなり、厚み方向に光の屈折率が変化する反射防止構造3を有するものであり、成形品2および反射防止構造3のいずれも透明性素材からなっている。 Consists innumerable fine irregularities smaller than the wavelength of the pitch of the light, which has an anti-reflection structure 3 in which the refractive index of the light is changed in the thickness direction, both of the molded article 2 and the anti-reflection structure 3 made of a transparent material ing. 図1(a)に示すように、本発明の反射防止性成形品1の反射防止構造3を有する部分は、成形品2と連続した透明性素材からなっているか、図1(b)に示すように、反射防止構造3を有する透明性素材からなる表面層4が、透明性素材からなる基板層である成形品2上に積層した積層構造からなっていてもよい。 As shown in FIG. 1 (a), the portion having the anti-reflection structure 3 of antireflective molded article 1 of the present invention are either made from continuous transparency material and the molded article 2, shown in FIG. 1 (b) as such, the surface layer 4 made of a transparent material having an antireflection structure 3 may be made of laminated structure formed by laminating on the molded article 2 is a substrate layer made of a transparent material.

【0009】図1(c)に示すように、本発明の反射防止性成形品1は、成形品2の両面に、光の波長以下のピッチの無数の微細凹凸からなり、厚み方向に光の屈折率が変化する反射防止構造3および3'を有していてもよく、この場合、反射防止構造3および3'は、成形品2 [0009] As shown in FIG. 1 (c), antireflective molded article 1 of the present invention, on both sides of the molded article 2, consists innumerable fine irregularities smaller than the wavelength of the pitch of the light, the thickness direction of the light 'may have, in this case, anti-reflection structure 3 and 3' anti-reflection structure 3 and third refractive index is changed, the molded article 2
と連続した透明性素材からなっていてもよいが、いずれか一方もしくは両方が、反射防止構造を有する表面層4 Continuous may comprise a transparent material but with, either or both of the surface layer 4 having an anti-reflection structure
および/または4'として、基板層である成形品2上に積層した積層構造を構成していてもよい。 As and / or 4 'may constitute a laminated structure obtained by laminating on the molded article 2 is the substrate layer.

【0010】表面層4および/または4'と基板層である成形品2とが積層構造を構成する場合、成形品2と、 [0010] When the surface layer 4 and / or 4 'and the molded article 2 is a substrate layer constituting the laminate structure, the molded article 2,
表面層4および/または4'とは、同種の透明性素材からなっていてもよいし、別種の透明性素材からなっていてもよい。 The surface layer 4 and / or 4 ', may be made of a transparent material of the same type, may consist another kind of transparent material. また、表面層4および4'とが、異種の透明性素材からなっていてもよく、この場合、いずれかの表面層が成形品2と同種の透明性素材からなっていてもよい。 Further, the surface layer 4 and 4 ', but may be made of a transparent material different in this case, any of the surface layer may be made of a transparent material of the molded article 2 and the like.

【0011】図1(b)および図1(c)を引用して説明したような積層構造を有する反射防止性成形品1の場合、表面層と基板層とは、一つの射出成形機に接続された異なる樹脂射出装置から射出された素材からなっていてもよく、あるいは、複数の樹脂材料を一度に射出する一つの樹脂射出装置から射出された素材からなっていてもよい。 [0011] In FIG. 1 (b) and 1 anti-reflective molded article 1 having a laminated structure as described with reference to (c), and the surface layer and the substrate layer, connected to one of the injection molding machine it may be made of a material emitted from been different resin injection device, or may be made a plurality of resin material from the material emitted from one of resin injection device for injecting at a time. なお、本発明の反射防止性成形品1は、反射防止という観点のみからすれば、表面の反射防止構造を除き、成形品の内部が不透明であることも有り得るが、後に述べる、種々の用途において、成形品自体、その内部および表面を含めて透明であるものとして扱っており、 Incidentally, antireflective molded article 1 of the present invention, if only from the viewpoint of antireflection, except anti-reflection structure of the surface, also possible that the interior of the molded article is opaque, but described later, in a variety of applications the molded article itself, and treated as being transparent, including its internal and surface,
そのような場合に効果が大きいことから、この明細書中の成形品、基板層、表面層、および反射防止構造は、特に断らない限り、いずれも透明なものであるとする。 Since a large effect in such a case, the molded article in this specification, a substrate layer, a surface layer, and the anti-reflection structure, unless otherwise specified, it is assumed both transparent. また、透明とは無色透明に限らず、有色透明も含むものとする。 Further, the transparent not limited to colorless, the category includes colored.

【0012】本発明の反射防止性成形品1は、熱可塑性樹脂で構成してもよいが、熱硬化性樹脂(製品の状態では硬化済みである。)で構成してもよく、後者に概念的に含まれる、電離放射線硬化性樹脂(製品の状態では、 [0012] antireflective molded article 1 of the present invention may be composed of a thermoplastic resin, but (a product of the state is already cured.) Thermosetting resin may be composed of a concept to the latter included, in the state of the ionizing radiation curable resin (product basis,
やはり硬化済みである。 Again it is already cured. )で構成してもよい。 ) May be configured by. これらのタイプの異なる樹脂を併用することもあり得る。 It may also be used in combination of these different types of resins. 併用する場合、少なくとも、表面層4および/または4'のいずれか、もしくは両方を熱硬化性樹脂や電離放射線硬化性樹脂で構成すると、表面の物理的および化学的性状が優れた反射防止性成形品1とすることができる。 When used in combination, at least, one of the surface layer 4 and / or 4 ', or when both comprise a thermosetting resin or an ionizing radiation curable resin, the physical and chemical properties are excellent antireflection molded surface it can be a goods 1.

【0013】透明性素材として熱可塑性樹脂を用いる場合には、ポリスチレン、ABS樹脂、ACS樹脂、AE [0013] In the case of using a thermoplastic resin as a transparent material, polystyrene, ABS resins, ACS resins, AE
S樹脂、セルロース樹脂、ポリアリレート、ポリブタジエン、ポリブチレン、アイオノマー、ポリエチレン、ポリプロピレン、ポリメチルペンテン、ポリメタクリル酸メチルやポリメタクリル酸エチル等のメタクリル樹脂、 S resins, cellulose resins, polyarylate, polybutadiene, polybutylene, ionomer, polyethylene, polypropylene, polymethylpentene, polymethyl methacrylate, methacrylic resins polyethyl methacrylate,
ポリアクリル酸ブチル等のアクリル樹脂、メタクリル/ Acrylic resins such as polybutyl acrylate, methacrylic /
スチレン共重合体、ニトリル樹脂、ポリアセタール、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリエチレンテレフタレート・イソフタレート共重合体等のポリエステル系樹脂、ポリブチレンテレフタレート、ポリカーボネート、ポリフッ化塩化ビニル、ポリフッ化ビニリデン、ポリ4フッ化エチレン、エチレン・ Styrene copolymers, nitrile resins, polyacetal, polyethylene terephthalate, polyethylene naphthalate, polyethylene terephthalate isophthalate copolymer, polyester resin, polybutylene terephthalate, polycarbonate, polyvinyl fluoride chloride, polyvinylidene fluoride, tetrafluoromethane ethylene, ethylene
4フッ化エチレン共重合体等のポリフッ化エチレン系樹脂、ナイロン6、ナイロン66等のポリアミド樹脂、ポリイミド樹脂、ポリ塩化ビニル、塩化ビニル/酢酸ビニル共重合体、エチレン・ビニルアルコール共重合体等のビニル系樹脂、三酢酸セルロース、セロファン等のセルロース系樹脂等を、単独もしくは混合、あるいはこれらの共重合体として使用することができる。 4 polyfluoroethylene resins such as fluorinated ethylene copolymer, nylon 6, polyamide resins such as nylon 66, polyimide resins, polyvinyl chloride, vinyl chloride / vinyl acetate copolymer, and ethylene-vinyl alcohol copolymer vinyl resins, cellulose triacetate, a cellulose resin such as cellophane or the like, can be used individually or in combination, or copolymers thereof.

【0014】透明性素材として熱硬化性樹脂を用いる場合、ポリアミド樹脂、不飽和ポリエステル樹脂、もしくはエポキシ樹脂等を使用することができる。 [0014] When a thermosetting resin is used as the transparent material, it is possible to use polyamide resin, unsaturated polyester resin, or epoxy resin.

【0015】透明性素材としての電離放射線硬化性樹脂組成物は、分子中に重合性不飽和結合または、エポキシ基を有するプレポリマー、オリゴマー、及び/又はモノマーを適宜に混合したものである。 The ionizing radiation-curable resin composition as transparency materials, polymerizable in a molecule an unsaturated bond or a prepolymer having an epoxy group is obtained by mixing appropriate oligomers, and / or monomers. 電離放射線とは、電磁波又は荷電粒子線のうち分子を重合又は架橋し得るエネルギー量子を有するものを指し、通常、紫外線、もしくは電子線を用いる。 The ionizing radiation refers to those having an energy quantum which molecules capable of polymerization or crosslinking of the electromagnetic waves or charged particle beams, typically, ultraviolet light, or an electron beam is used.

【0016】電離放射線硬化性樹脂組成物中のプレポリマー、オリゴマーの例としては、不飽和ジカルボン酸と多価アルコールの縮合物等の不飽和ポリエステル類、ポリエステルメタクリレート、ポリエーテルメタクリレート、ポリオールメタクリレート、メラミンメタクリレート等のメタクリレート類、ポリエステルアクリレート、 The prepolymers of the ionizing radiation curable resin composition, examples of oligomers, unsaturated polyesters condensates of polyhydric alcohol and unsaturated dicarboxylic acids, polyester methacrylate, polyether methacrylate, polyol methacrylate, melamine methacrylates such as methacrylate, polyester acrylate,
エポキシアクリレート、ウレタンアクリレート、ポリエーテルアクリレート、ポリオールアクリレート、メラミンアクリレート等のアクリレート類、もしくはカチオン重合型エポキシ化合物が挙げられる。 Epoxy acrylates, urethane acrylates, polyether acrylates, polyol acrylates, acrylates such as melamine acrylate, or include cationically polymerizable epoxy compound.

【0017】電離放射線硬化性樹脂組成物中のモノマーの例としては、スチレン、α−メチルスチレン等のスチレン系モノマー、アクリル酸メチル、アクリル酸−2− [0017] Examples of monomers of ionizing radiation curable resin composition, styrene, styrenic monomers such as α- methyl styrene, methyl acrylate, 2-
エチルヘキシル、アクリル酸メトキシエチル、アクリル酸ブトキシエチル、アクリル酸ブチル、アクリル酸メトキシブチル、アクリル酸フェニル等のアクリル酸エステル類、メタクリル酸メチル、メタクリル酸エチル、メタクリル酸プロピル、メタクリル酸メトキシエチル、メタクリル酸エトキシメチル、メタクリル酸フェニル、メタクリル酸ラウリル等のメタクリル酸エステル類、アクリル酸−2−(N,N−ジエチルアミノ)エチル、アクリル酸−2−(N,N−ジメチルアミノ)エチル、アクリル酸−2−(N,N−ジベンジルアミノ)メチル、アクリル酸−2−(N,N−ジエチルアミノ)プロピル等の不飽和置換の置換アミノアルコールエステル類、アクリルアミド、メタクリルアミド等の不飽和カルボン酸アミド、エチレングリ Ethylhexyl, methoxyethyl acrylate, butoxyethyl acrylate, butyl acrylate, methoxy butyl acrylate, acrylic acid esters of phenyl acrylate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, methoxyethyl methacrylate, ethoxymethyl, phenyl methacrylate, methacrylic acid esters of lauryl methacrylate, acrylic acid-2 (N, N-diethylamino) ethyl, 2- acrylate (N, N- dimethylamino) ethyl, acrylate -2 - (N, N-dibenzylamino) methyl, acrylate-2-(N, N-diethylamino) substituted amino alcohol esters of unsaturated substituent such as propyl, acrylamide, unsaturated carboxylic acid amides such as methacrylamide, ethylene Gris ールジアクリレート、プロピレングリコールジアクリレート、ネオペンチルグリコールジアクリレート、1,6−ヘキサンジオールジアクリレート、トリエチレングリコールジアクリレート等の化合物、ジプロピレングリコールジアクリレート、エチレングリコールジアクリレート、プロピレングリコールジメタクリレート、ジエチレングリコールジメタクリレート等の多官能性化合物、及び/又は分子中に2個以上のチオール基を有するポリチオール化合物、例えばトリメチロールプロパントリチオグリコレート、トリメチロールプロパントリチオプロピレート、ペンタエリスリトールテトラチオグリコレート等が挙げられる。 Over diacrylate, propylene glycol diacrylate, neopentyl glycol diacrylate, 1,6-hexanediol diacrylate, compounds such as triethylene glycol diacrylate, dipropylene glycol diacrylate, ethylene glycol diacrylate, propylene glycol dimethacrylate, diethylene glycol polyfunctional compounds such as dimethacrylate, and / or a polythiol compound having two or more thiol groups in the molecule, such as trimethylolpropane trithioglycolate, trimethylolpropane tri thio propylate, pentaerythritol tetrathioglycolate, etc. and the like.

【0018】通常、電離放射線硬化性樹脂組成物中のモノマーとしては、以上の化合物を必要に応じて、1種若しくは2種以上を混合して用いるが、電離放射線硬化性組成物に通常の塗布適性を与えるために、前記のプレポリマー又はオリゴマーを5重量%以上、前記モノマー及び/又はポリチオール化合物を95重量%以下とするのが好ましい。 [0018] Normally, the monomer of the ionizing radiation curable resin composition, if desired the above compounds, used as a mixture of at least one or two, but usually the coating to ionizing radiation-curable composition to provide suitability, the prepolymer or oligomer 5 wt% or more, the monomer and / or polythiol compound preferably 95 wt% or less.

【0019】電離放射線硬化性樹脂組成物を硬化させたときのフレキシビリティーが要求されるときは、モノマー量を減らすか、官能基の数が1又は2のアクリレートモノマーを使用するとよい。 [0019] When the flexibility when curing the ionizing radiation-curable resin composition is required, reduce the monomer content, the number of functional groups may be used one or two acrylate monomers. 電離放射線硬化性樹脂組成物を硬化させたときの耐摩耗性、耐熱性、耐溶剤性が要求されるときは、官能基の数が3つ以上のアクリレートモノマーを使う等、電離放射線硬化性樹脂組成物の設計が可能である。 Wear resistance upon curing the ionizing radiation-curable resin composition, heat resistance, when the solvent resistance is required, such as the number of functional groups to use three or more acrylate monomers, ionizing radiation-curable resin design of the composition is possible. ここで、官能基が1のものとして、2− Here, as the functional group is 1, 2
ヒドロキシアクリレート、2−ヘキシルアクリレート、 Hydroxy acrylate, 2-hexyl acrylate,
フェノキシエチルアクリレートが挙げられる。 Phenoxyethyl acrylate. 官能基が2のものとして、エチレングリコールジアクリレート、 As the functional group is 2, ethylene glycol diacrylate,
1,6−ヘキサンジオールジアクリレートが挙げられる。 1,6-hexanediol diacrylate. 官能基が3以上のものとして、トリメチロールプロパントリアクリレート、ペンタエリスリトールトリアクリレート、ペンタエリスリトールテトラアクリレート、 As the functional group is at least 3, trimethylolpropane triacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate,
ジペンタエリスリトールヘキサアクレリート等が挙げられる。 Dipentaerythritol hexa Acre REIT, and the like.

【0020】電離放射線硬化性樹脂組成物を硬化させたときのフレキシビリティーや表面硬度等の物性を調整するため、電離放射線硬化性樹脂組成物に、電離放射線照射では硬化しない樹脂を添加することもできる。 [0020] To adjust the physical properties such as flexibility and surface hardness upon curing the ionizing radiation-curable resin composition, the ionizing radiation curable resin composition, adding a resin which is not cured by ionizing radiation It can also be. 具体的な樹脂の例としては次のものがある。 It is those of the Examples of specific resins. ポリウレタン樹脂、セルロース樹脂、ポリビニルブチラール樹脂、ポリエステル樹脂、アクリル樹脂、ポリ塩化ビニル樹脂、ポリ酢酸ビニル等の熱可塑性樹脂である。 Polyurethane resins, cellulose resins, polyvinyl butyral resins, polyester resins, acrylic resins, polyvinyl chloride resins, thermoplastic resins and polyvinyl acetate. 中でも、ポリウレタン樹脂、セルロース樹脂、ポリビニルブチラール樹脂等の添加がフレキシビリティーの向上の点で好ましい。 Among them, polyurethane resins, cellulose resins, additives such as polyvinyl butyral resin is preferred in terms of improvement in flexibility.

【0021】電離放射線硬化性樹脂組成物の硬化が紫外線照射により行われるときは、光重合開始剤や光重合促進剤を添加する。 [0021] When the curing of the ionizing radiation curable resin composition is carried out by ultraviolet irradiation, a photopolymerization initiator is added or a photopolymerization accelerator. 光重合開始剤としては、ラジカル重合性不飽和基を有する樹脂系の場合は、アセトフェノン類、ベンゾフェノン類、チオキサントン類、ベンゾイン、ベンゾインメチルエーテル等を単独又は混合して用いる。 As the photopolymerization initiator, the case of a resin system having a radical polymerizable unsaturated group, acetophenones, benzophenones, thioxanthones, benzoin, used alone or as a mixture of benzoin methyl ether. また、カチオン重合性官能基を有する樹脂系の場合は、光重合開始剤として、芳香族ジアゾニウム塩、芳香族スルホニウム塩、芳香族ヨードニウム塩、メタセロン化合物、ベンゾインスルホン酸エステル等を単独又は混合物として用いる。 In the case of a resin system having a cation polymerizable functional group, it is used as a photopolymerization initiator, an aromatic diazonium salts, aromatic sulfonium salts, aromatic iodonium salts, metallocene compounds, benzoin sulfonic esters and the like alone or as a mixture . 光重合開始剤の添加量は、電離放射線硬化性樹脂組成物100重量部に対し、0.1〜1 The amount of the photopolymerization initiator added is, relative to the ionizing radiation curable resin composition 100 parts by weight, 0.1 to 1
0重量部である。 0 parts by weight.

【0022】電離放射線硬化性樹脂組成物には、次のような有機反応性ケイ素化合物を併用してもよい。 [0022] The ionizing radiation curable resin composition may be used in combination with organic reactive silicon compound such as the following.

【0023】有機ケイ素化合物の1は、一般式R m Si The first organosilicon compound has the general formula R m Si
(OR') nで表せるもので、RおよびR'は炭素数1 'Those expressed by n, R and R (OR)' is 1 carbon atoms
〜10のアルキル基を表し、Rの添え字mとR'の添え字nとは、各々が、m+n=4の関係を満たす整数である。 Represents an 10 alkyl group, the subscript n of R subscript m and R ', each is an integer satisfying the relationship of m + n = 4.

【0024】具体的には、テトラメトキシシラン、テトラエトキシシラン、テトラ−iso−プロポキシシラン、テトラ−n−プロポキシシラン、テトラ−n−ブトキシシラン、テトラ−sec−ブトキシシラン、テトラ−tert−ブトキシシラン、テトラペンタエトキシシラン、テトラペンタ−iso−プロポキシシラン、テトラペンタ−n−プロポキシシラン、テトラペンタ−n− [0024] More specifically, tetramethoxysilane, tetraethoxysilane, tetra -iso- propoxysilane, tetra -n- propoxysilane, tetra -n- butoxysilane, tetra -sec- butoxysilane, tetra -tert- butoxysilane , tetra-penta-ethoxy silane, Tetorapenta -iso- propoxysilane, Tetorapenta -n- propoxysilane, Tetorapenta -n-
ブトキシシラン、テトラペンタ−sec−ブトキシシラン、テトラペンタ−tert−ブトキシシラン、メチルトリエトキシシラン、メチルトリプロポキシシラン、メチルトリブトキシシラン、ジメチルジメトキシシラン、 Butoxysilane, Tetorapenta -sec- butoxysilane, Tetorapenta -tert- butoxysilane, methyltriethoxysilane, methyl tripropoxysilane, methyl tributoxysilane silane, dimethyldimethoxysilane,
ジメチルジエトキシシラン、ジメチルエトキシシラン、 Dimethyl diethoxy silane, dimethyl silane,
ジメチルメトキシシラン、ジメチルプロポキシシラン、 Dimethyl silane, dimethyl propoxysilane,
ジメチルブトキシシラン、メチルジメトキシシラン、メチルジエトキシシラン、ヘキシルトリメトキシシラン等が挙げられる。 Dimethyl butoxysilane, methyl dimethoxy silane, methyl diethoxy silane, hexyl trimethoxy silane and the like.

【0025】電離放射線硬化性樹脂組成物に併用し得る有機ケイ素化合物の2は、シランカップリング剤である。 [0025] 2 of the organosilicon compounds may be used in combination to ionizing radiation curable resin composition is a silane coupling agent.

【0026】具体的には、γ−(2−アミノエチル)アミノプロピルトリメトキシシラン、γ−(2−アミノエチル)アミノプロピルメチルジメトキシシラン、β− [0026] Specifically, .gamma. (2-aminoethyl) aminopropyl trimethoxysilane, .gamma. (2-aminoethyl) aminopropyl methyl dimethoxy silane, beta-
(3,4−エポキシシクロヘキシル)エチルトリメトキシシラン、γ−アミノプロピルトリエトキシシラン、γ (3,4-epoxycyclohexyl) ethyltrimethoxysilane, .gamma.-aminopropyltriethoxysilane, gamma
−メタクリロキシプロピルメトキシシラン、N−β− - methacryloxypropyl methoxy silane, N-beta-
(N−ビニルベンジルアミノエチル)−γ−アミノプロピルメトキシシラン・塩酸塩、γ−グリシドキシプロピルトリメトキシシラン、アミノシラン、メチルメトキシシラン、ビニルトリアセトキシシラン、γ−メルカプトプロピルトリメトキシシラン、γ−クロロプロピルトリメトキシシラン、ヘキサメチルジシラザン、ビニルトリス(β−メトキシエトキシ)シラン、オクタデシルジメチル[3−(トリメトキシシリル)プロピル]アンモニウムクロライド、メチルトリクロロシラン、ジメチルジクロロシラン等が挙げられる。 (N- vinylbenzylaminoethyl)-.gamma.-aminopropyl trimethoxysilane hydrochloride, .gamma.-glycidoxypropyltrimethoxysilane, aminosilane, methyl methoxy silane, vinyl triacetoxy silane, .gamma.-mercaptopropyltrimethoxysilane, .gamma. chloropropyltrimethoxysilane, hexamethyldisilazane, tris (beta-methoxyethoxy) silane, octadecyl dimethyl [3- (trimethoxysilyl) propyl] ammonium chloride, methyl trichlorosilane, dimethyl dichlorosilane, and the like.

【0027】電離放射線硬化性樹脂組成物に併用し得る有機ケイ素化合物の3は、電離放射線硬化性ケイ素化合物である。 [0027] 3 of the organosilicon compounds may be used in combination to ionizing radiation curable resin composition is ionizing radiation-curable silicon compound. 具体的には、電離放射線の照射によって反応し架橋する複数の官能基、例えば、重合性二重結合基を有する分子量5,000以下の有機ケイ素化合物が挙げられ、より具体的には、片末端ビニル官能性ポリシラン、両末端ビニル官能性ポリシラン、片末端ビニル官能ポリシロキサン、両末端ビニル官能ポリシロキサン、又はこれらの化合物を反応させたビニル官能性ポリシラン、もしくはビニル官能性ポリシロキサン等が挙げられる。 Specifically, a plurality of functional groups reactive to crosslinking by irradiation of ionizing radiation, for example, it includes molecular weight of 5,000 or less of an organic silicon compound having a polymerizable double bond group, and more specifically, one end vinyl functional polysilane, both terminal vinyl functional polysilane, one terminal vinyl functional polysiloxane, both terminal vinyl functional polysiloxane, or these vinyl functional polysilane compound was reacted, or vinyl-functional polysiloxane and the like.

【0028】より具体的には、次のような化合物である。 [0028] More specifically, compounds as follows.

【0029】 [0029]

【化1】 [Formula 1]

【0030】その他、電離放射線硬化性樹脂組成物に併用し得る有機ケイ素化合物としては、3−(メタ)アクリロキシプロピルトリメトキシシラン、3−(メタ)アクリロキシプロピルメチルジメトキシシラン等の(メタ)アクリロキシシラン化合物等が挙げられる。 [0030] Other examples of the organic silicon compound may be used in combination to ionizing radiation curable resin composition, 3- (meth) acryloxy propyl trimethoxy silane, 3- (meth) acryloxy propyl and methyl dimethoxy silane (meth) acryloxy silane compounds, and the like. 電離放射線硬化性樹脂としては、硬化後の硬度が、JIS K As the ionizing radiation curable resin, the hardness after curing, JIS K
5400で示す鉛筆硬度試験で「H」以上の硬度を示すものがより好ましい。 In the pencil hardness test shown in 5400 indicates the "H" or higher hardness is more preferable.

【0031】なお、いずれのタイプの樹脂も、反射防止性能を発揮するためには屈折率が低い方が好ましいが、 It should be noted, both types of resins, but preferably it is a low refractive index in order to exhibit the antireflection performance,
反射防止性成形品として長期間使用するには、表面の耐久性、特に耐擦傷性が必要であり、硬度を高くした方が有利になるため、密度を上げて硬度を高くする必要がある。 The long-term use as an anti-reflective molded article, durability of the surface is particularly necessary scratch resistance, to become advantageous to increase the hardness, it is necessary to increase the hardness by increasing the density. 反射防止構造の屈折率としては、1.4〜1.7、 The refractive index of the antireflection structure, 1.4 to 1.7,
より好ましくは、1.6以下である。 More preferably 1.6 or less.

【0032】反射防止構造3を構成する、光の波長以下のピッチの微細凹凸の形状としては、図2(a)に例示するような、断面の上縁の形状が正弦曲線のもの、断面の頂部3aが円弧状で、立ち上がり部分3bが直線状であり、上へ行くほどすぼまった形状のもの(図2 [0032] constituting the anti-reflection structure 3, the shape of the following pitch of the fine irregularities wavelength of light, as illustrated in FIG. 2 (a), the shape of the upper cross section edge those sinusoids, the cross-section top 3a is arcuate, the rising portion 3b is straight, a shape which narrowed as it goes upward (FIG. 2
(b))、上側が尖った三角波状のもの(図2 (B)), and the upper side is pointed triangular (FIG. 2
(c))、断面が上すぼまりの台形状のもの(図2 (C)), those trapezoidal in Subomari upper cross-section (FIG. 2
(d))等の種々のバリエーションがあり得る。 (D)) may have various variations and the like.

【0033】微細凹凸の形状としては上記の図2 [0033] Figure 2 above as shape of the fine uneven
(a)、図2(b)、図2(c)、および図2(d)に示すような断面形状のものが好ましく、このような断面形状のものを使用すると、反射防止構造3を有する部分(図2では成形品2の表面近傍である。)の厚み方向の位置により、光の屈折率が連続的に変化する性質が付与される。 (A), FIG. 2 (b), the a is preferably a cross-sectional shape as shown in FIG. 2 (c), and FIG. 2 (d), the when using those such cross-sectional shape, the anti-reflection structure 3 part (a vicinity of the surface of FIG. 2 in the molded article 2.) the position in the thickness direction of the nature that the refractive index of light continuously changes is given.

【0034】特に図2(a)、図2(b)、および図2 [0034] In particular FIG. 2 (a), the FIG. 2 (b), the and 2
(c)に示すような形状のものが空気中に存在する場合、透明層3の最上部では、成形品2の存在する割合が限りなく0%に近いので、この部分での屈折率は、周囲を取り巻く物質(通常の生活空間では空気であり、透明層の屈折率より明らかに低く、その屈折率はほぼ1.0 If a shape as shown in (c) is present in the air, the top of the transparent layer 3, the proportion of the presence of the molded article 2 is close to 0% as possible, the refractive index in this part, It is a substance (usually a living space the surrounding air, clearly lower than the refractive index of the transparent layer, the refractive index is approximately 1.0
である。 It is. )の屈折率と等しく、凹凸の最も下部では、透明層の存在する割合が限りなく100%に近いので、成形品2を構成する素材の屈折率と等しく、中間部では、 Equal to the refractive index of), in the most lower part of the irregularities, so close to 100% without rate is limited to the presence of the transparent layer is equal to the refractive index of the material constituting the molded article 2, the middle portion,
その高さにおける成形品2の面積率(即ち、そのスライスレベルにおける透明層3の断面積が全体に占める割合)に比例した屈折率を有し、従って、成形品2の微細凹凸からなる反射防止構造3は、その厚み方向に、空気の屈折率から透明層の屈折率の間で連続的に屈折率が変化する性質を持った反射防止層としての機能を有する。 Area ratio of the molded article 2 in its height (i.e., percentage of total cross-sectional area of ​​the transparent layer 3 in the slice level) has a refractive index which is proportional to, thus, prevent reflections consisting of fine irregularities shaped article 2 structure 3 has, in its thickness direction, and has a function as an antireflective layer having a property of continuous refractive index between the refractive index of the transparent layer from the refractive index of the air is changed.

【0035】なお、図2(a)、図2(b)、図2 [0035] Incidentally, FIG. 2 (a), the FIG. 2 (b), the 2
(c)、および図2(d)に示す反射防止構造の場合、 (C), and if the anti-reflection structure shown in FIG. 2 (d),
凹凸の底部よりも下の部分では、屈折率は、成形品2の屈折率そのもので、一定である。 The portion below the bottom of the unevenness, the refractive index, the refractive index itself of the molded article 2, is constant.

【0036】以上の説明からも明らかなように、逆に、 [0036] As is apparent from the above description, on the contrary,
厚み方向の位置と屈折率との要望される関係が与えられれば、反射防止構造の断面形状を設計することが可能である。 Given the relationship is desired between the position in the thickness direction and the refractive index, it is possible to design the cross-sectional shape of the anti-reflection structure. 断面形状によって、屈折率の変化が連続的なものも、不連続的なものも、いずれも形成可能であるが、屈折率が不連続なものは、屈折率の異なる層を重ねて積層することによっても実現でき、むしろ、本発明においては、反射防止構造の部分では、屈折率が連続的に変化するものとして製作してあるものの方が好ましく、かつ、 The cross-sectional shape, also the change in refractive index is continuous ones, discontinuous ones also, although both can also be formed, a refractive index is discontinuous, laminating superimposed layers of different refractive index also be achieved by, but rather, in the present invention, in the portion of the anti-reflection structure, preferably towards those are manufactured as refractive index changes continuously, and,
屈折率が空気の屈折率から成形品2の屈折率まで連続的に変化するものがより好ましい。 Which the refractive index changes continuously from the refractive index of air to the refractive index of the molded article 2 is more preferable. 表面層4を有している場合は、屈折率が空気の屈折率から表面層4の素材の持つ屈折率まで連続的に変化するものがより好ましい。 If it has a surface layer 4, which refractive index is continuously varied from the refractive index with the material of the surface layer 4 from the refractive index of the air is more preferable.

【0037】これらの断面形状を持つ反射防止構造3 The anti-reflection structure 3 with these cross-sectional shape
を、凹凸のある側から観察するとき、微細凹凸の配列としては、図3(a)(斜視図である。)中に示す凹部5 The, when observing from the uneven side, as the array of fine irregularities, recesses 5 shown in FIG. 3 (a) (a perspective view.)
が平行に配列したものや、図3(b)もしくは図3 And which is arranged in parallel, and FIG. 3 (b) or FIG. 3
(c)に上方から見た図(同心円は等高線を示す。)で示すように、平面的に並べて配列して形成したものとが有り得る。 View from above (c) (concentric circles shows the contour lines.) As shown in, there can be as formed by arranging side by side in a plane. いずれのタイプのものも、反射防止性を有するが、図3(a)に示すような溝状のタイプのものは方向性を有するために、入射光の方向によって反射率が変わる。 Others of any type, but having an antireflection property, in order to have the direction of that of the groove-shaped type as shown in FIG. 3 (a), the reflectance changes depending on the direction of the incident light. これに対し、図3(b)もしくは図3(c)に示すような凹凸を二次元に配列した二次元配列の微細凹凸を有するものは、方向性が事実上無く、好ましい。 In contrast, those having a fine uneven shown in FIG. 3 (b) or uneven dimensional array arranged in a two-dimensional as shown in FIG. 3 (c), the directional without over fact, preferred. 勿論、図3(b)もしくは図3(c)に示すような、凹凸を二次元に配列したものの凸部の形状を、(この図のものは凸部が円形であるが、)楕円形にして方向性を持たせることもできる。 Of course, as shown in FIG. 3 (b) or 3 (c), the shape of the convex portion but an array of irregularities in two dimensions, (although protrusions that of the figure is circular) and an ellipse it is also possible to have directionality Te.

【0038】反射防止構造3の形状自体には種々のものがあり得るが、断面形状に表れる凹凸の波のピッチ(= [0038] Although the shape itself of the anti-reflection structure 3 may have various things, wave irregularities appearing in cross section pitch (=
周期)は、光の波長以下の微細なものである必要があり、ピッチとしては、300nm以下が好ましい。 Period), it is desired to have a less than or equal to the wavelength of light of the fine, the pitch is preferably equal to or less than 300 nm. 型の精度や、製品における型の再現性を考慮すると、ピッチとしては、100nm以上であることが好ましいが、下限は特になく、もっと細かくてもよい。 Type and accuracy, considering the type of reproducibility in the product, as the pitch, it is preferably 100nm or more, the lower limit is not particularly may be more closely.

【0039】反射防止構造3は凹凸の高低差が大きい方が、反射率が低くなり、反射防止効果があるため、高低差が50nm以上であることが好ましい。 [0039] Write antireflection structure 3 has a large height difference of the unevenness is, the reflectance is lowered, since it is anti-reflection effect, it is preferred height difference is 50nm or more. 上限は特に無いが、通常のピッチである100nm〜300nmを想定すると、ピッチの値の50%〜200%程度であることが好ましく、50nm〜600nm程度である。 The upper limit is no particular, assuming a normal pitch 100 nm to 300 nm, preferably about 50% to 200% of the value of the pitch is about 50 nm~600 nm. 勿論、これらの範囲を外れるものもあり得る。 Of course, there may be a departure of these ranges.

【0040】本発明の反射防止性成形品1は、図4、もしくは図5に示すように射出成形装置11を用いて製造することが好ましい。 The antireflective molded article 1 of the present invention, FIG. 4, or it is preferable to produce by using an injection molding apparatus 11 as shown in FIG.

【0041】図4は射出成形装置11の主要部分を示す図であって、左右に可動側取付板12および固定側取付板13を有しており、可動側取付板12には可動側型板12aが、また、固定側取付板13には固定側型板13 FIG. 4 is a diagram showing a main portion of an injection molding apparatus 11, the left and right has a movable side mounting plate 12 and the fixed-side mounting plate 13, the movable side mold plate on the movable side mounting plate 12 12a is also fixed die plate to the fixed-side mounting plate 13 13
aがそれぞれ取り付けられている。 a are respectively attached. 可動側型板12aと固定側型板13aからなる一対の金型の間には、キャビティ14が形成されており、キャビティ14内の可動側型板12a側および/または固定側型板13aの内面に、微細凹凸を形成するための型形状が設けられている。 Between the pair of molds composed of a movable side mold plate 12a and the fixed-side mold plate 13a, a cavity 14 is formed, the inner surface of the movable side mold plate 12a side and / or the fixed-side mold plate 13a of the cavity 14 in is provided the shape of the mold for forming the fine irregularities.

【0042】固定側取付板13には、樹脂射出装置のノズル16が設置されており、溶融した樹脂材料が固定側取付板13、および固定側型板13aを経由してキャビティに供給されるように構成されている。 [0042] the fixed side mounting plate 13 is installed a nozzle 16 of the resin injection device, so that the molten resin material is supplied to the cavity via the fixed-side mounting plate 13, and the fixed-side mold plate 13a It is configured. また、固定側型板13aには、排気孔15が型板13aの周囲に向かって開けられている。 Further, the stationary side mold plate 13a is an exhaust hole 15 is opened toward the periphery of the template 13a.

【0043】このように構成された射出成形装置11のキャビティ14内に、溶融した樹脂材料を射出して充填し、樹脂材料が行き渡らせ、その後、冷却し、冷却の後、金型を開放して、成形品を取り出すことにより、本発明の反射防止性成形品1を得ることができる。 [0043] The thus-configured cavity 14 of the injection molding apparatus 11, the molten resin material is filled by injection, resin material is spread, then cooled, after cooling, opening the mold Te, by taking out the molded article, it is possible to obtain an antireflection molded article 1 of the present invention.

【0044】上記の一連の工程において、キャビティ1 [0044] In the series of steps described above, the cavity 1
4は排気を行なって真空状態としておくことが好ましく、排気は、キャビティ14内への樹脂材料の充填より前に行なって、予め、キャビティ14内を真空状態としておくことが好ましい。 4 is preferably to keep a vacuum state by performing evacuation, evacuation is performed prior to the filling of the resin material into the cavity 14, pre, it is preferable to a vacuum in the cavity 14. 排気は排気孔15を通じ、真空ポンプを用いて行なう。 Exhaust through the exhaust hole 15 is performed using a vacuum pump. なお、樹脂材料を充填することにより、樹脂材料の分解や反応等によりガスが発生することがあるので、排気は、充填工程中も続けて行なうことが好ましい。 Incidentally, by filling the resin material, since there is a gas is generated by decomposition or reaction of the resin material, evacuation is preferably carried out continuously also during the filling process. この真空状態は、遅くとも、金型の開放直前に開放すればよい。 The vacuum at the latest, can be opened to open just before the die.

【0045】真空状態とするためには、上記のように、 [0045] in order to make the vacuum state is, as described above,
排気孔を設けて行なう以外に、金型の隙間から行なうこともできる。 Besides performing provided an exhaust hole may be carried out from a gap of the mold. 図5は、金型の隙間から排気を行なえるよう構成した射出成形機11の主要部分を示す図であって、可動側型板12aの固定側型板(A)と対する面の周縁よりも内側に、キャビティ14の全周を囲む円形状等の溝18を形成しておき、溝19内にOリングを埋めたものである。 Figure 5 is a diagram showing a main portion of an injection molding machine 11 configured so performed exhaust from the gap of the die, from an edge surface of the fixed side mold plate of the movable-side mold plate 12a (A) and against inwardly, previously formed grooves 18 of circular shape that surrounds the entire periphery of the cavity 14, in which buried O-ring in the groove 19. なお、この図5に示す射出成形機11では、さらに固定側型板(A)13aと固定側取付板13 In the injection molding machine 11 shown in FIG. 5, further fixed die plate and (A) 13a fixed side mounting plate 13
との間に固定側型板(B)13bを介在させて、ランナ17を形成し、かつ、固定側型板(A)13aの固定側取付板13側にも、ランナ17を囲む円形状等の溝18 And the fixed-side mold plate (B) 13b is interposed between, forms a runner 17, and, in the fixed-side mounting plate 13 side of the fixed-side mold plate (A) 13a, a circular shape surrounding the runner 17 of the groove 18
を形成しておき、Oリングを埋めてある。 To form the advance, it is buried the O-ring.

【0046】この射出成形機11においては、一旦型を閉じ(隙間19が無くなる状態とする。)、その後、圧力を開放すると、Oリングの弾性回復力(必要であれば、さらにバネを組み込んでおくことにより、そのバネの弾性回復力とも合わせた力としてもよい。)により、 [0046] In the injection molding machine 11, once the mold closed (a state where the clearance 19 is eliminated.) Thereafter, when releasing the pressure, if the elastic resilience of the O-ring (necessary, further incorporate a spring by placing, by may also be.) as a force fit also the elastic recovery force of the spring,
可動側型板12aと固定側型板(A)13aとの間、および固定側型板13(A)と固定側型板(B)13bとの間に隙間を生じるので、これらの隙間を利用して排気を行なうことができ、排気を行なうタイミングは、図4 Between the movable side mold plate 12a and the fixed-side mold plate (A) 13a, and therefore results in a gap between the stationary side mold plate 13 (A) and the fixed side mold plate and (B) 13b, utilize these gaps to be able to perform the exhaust, timing of exhaust, 4
を引用して説明したときと同様である。 The same as is when has been described with reference to.

【0047】図4および図5においては、溶融した樹脂材料を供給するノズルは一つであるとして描き、一種類の樹脂材料を充填することを念頭において説明したが、 [0047] In FIGS. 4 and 5, nozzle for supplying a molten resin material is drawn as it is one, has been described in mind filling one type of resin material,
いずれの成形機においても、充填工程を、一つの射出成形機に接続された二以上の樹脂射出装置を使用するか、 In any of the molding machine, a filling step, use the connected two or more resin injection device into one of the injection molding machine,
もしくは複数の樹脂材料を射出する一つの樹脂射出装置を使用して、行なうことができる。 Or a plurality of resin material using a resin injection device for injecting can be carried out.

【0048】二以上の樹脂を使用する場合、一旦、いずれか一の樹脂を使用して、その樹脂で形成すべき部分を成形して半製品としておき、その半製品を金型内にセットして、他の樹脂を供給して成形するような二色成形法を利用することもできる。 [0048] When using two or more resins, once using any of the resin, leave by molding the portion to be formed in the resin semi-products, sets its semi-finished product in the mold Te, it can be used a two-color molding method such as molding by supplying the other resin.

【0049】上記の射出成形装置11を用いての本発明の反射防止性成形品1の製造の際に用いる金型において、反射防止構造3を形成するための型の形成は次のように行なう。 [0049] In a mold used in the preparation of anti-reflective molded article 1 of the present invention using an injection molding apparatus 11 described above, formation of the mold for forming the anti-reflection structure 3 is carried out as follows . まず、適当な基材に感光性樹脂を積層したものを準備し、これにレーザー光干渉法により露光を行なう。 First, prepare the that the photosensitive resin is laminated to a suitable substrate, to which performs exposure by a laser beam interference method. 感光性樹脂としては、一般的なものに加え、レリーフホログラム製造用として市販されているフィルム付きの感光材を利用することができ、手法自体もホログラムの製造方法として、よく行なわれていて、安定な手法である。 As the photosensitive resin, common ones in addition, it is possible to use a film with a photosensitive material, which is commercially available for relief hologram production, as a production method of approach itself holograms, have been well performed, stable it is an approach. 露光は、レーザー光を2ないしそれ以上に分割して干渉させることによって行ない、ピッチが光の波長以下の硬化部と未硬化部とを得る。 Exposure performed by interference by dividing a laser beam into two or more, the pitch to obtain a wavelength less hardened part of the light and the uncured portion. 露光後、感光性樹脂の種類に応じた現像法、通常は特定の溶剤による未硬化部分の除去により、現像を行なって、ピッチが光の波長以下の無数の微細凹凸が形成された凹凸型面を有する原型を得る。 After exposure, development method in accordance with the type of the photosensitive resin, the normal removal of the uncured portion by a specific solvent, by developing, uneven die surface pitch countless fine unevenness equal to or less than the wavelength of light is formed obtain a prototype with. レーザー光干渉法以外の手法としては、サンドブラスト法や、フォトマスク製作における電子ビーム露光を利用する方法によってもよい。 As a method other than the laser light interferometry, sandblasting and may by a method of using an electron beam exposure in photomask fabrication.

【0050】得られた原型は、レーザー光の干渉露光法の場合、凹凸を形成しやすくするために、比較的分子量の小さい高分子からなっているため、溶剤に対する耐久性も不十分であり、また、もろいため、この原型を何度も使用して複製を行なうことは、必ずしも好ましくない等、そのまま、大量生産に適用することは必ずしも好ましくない。 The resulting prototype, if the interference exposure method of the laser light, in order to easily form irregularities, since that is a small polymer having relatively low molecular weight, and durability is insufficient to solvents, Further, since brittle, to perform replicated using this prototype many times, not necessarily preferable or the like, it is, not necessarily preferred be applied to mass production. そこで、原型にニッケル等の金属でめっきを行なって、第1の金属製の型を形成し、この第1の金属製の型を使用するか、または第1の金属製の型にめっきを行なって、第2の金属製の型を幾つか形成し、得られた第2の金属製の型を使用して複製を行なう事が好ましい。 Therefore, by performing plating with a metal such as nickel prototype, forming a first metallic mold, either by using the first metal mold, or a plating on the first metallic mold made Te, a second metallic mold was some form, it is preferable that using a second metallic mold obtained performing replication.

【0051】なお、型面の形状を複製する際に、原型と第2の金属製の型とは同形状であり、原型と第1の金属製の型とは互いに逆型形状の関係となる。 [0051] At the time of duplicating the shape of the mold surface, the prototype and the second metal mold have the same shape, a reverse shape of each other is a prototype and the first metallic mold . また反射防止性成形品の微細凹凸の形状と、それを製造するための型上の型面の微細凹凸の形状とは逆型形状となる。 Also the shape of the fine irregularities of the anti-reflection moldings, the inverse shape to the mold on the mold surface of the fine irregularities for making the same. 従って、反射防止性成形品として欲しい形状が得られるよう、必要なら更に、めっきによる金属型の形成を加えて、微細凹凸の形状を逆転させるとよい。 Therefore, to want shape is obtained as an anti-reflective molded article, further if necessary, in addition to the formation of the metal mold by plating, it may reverse the shape of the fine irregularities. ただし、微細凹凸の断面形状が正弦曲線のように、元の型形状と逆型形状との間で違いがない場合もある。 However, there as the cross-sectional shape is a sine curve of fine unevenness, even if there is no difference between the original type shape reverse shape. この明細書中では、成形の際の金型内部の型面の微細凹凸形状としては、上記のような例外を除き、反射防止性成形品に、得たい微細凹凸形状が得られるよう、逆型形状に形成されているものを指すものとする。 In this specification, the fine uneven shape of the mold surface of the inner mold during molding, with the exceptions as described above, the antireflective molded article, so that fine irregularities to be obtained is obtained, the inverse-type It is intended to refer to what is formed in the shape.

【0052】本発明の反射防止性成形品1は、微細凹凸からなる反射防止構造3が表面に露出したままでも、充分効果を発揮するが、不用意な接触による傷付きや汚染を防止する意味で、反射防止構造の部分よりも光の屈折率が低い樹脂組成物からなる低屈折率層をその微細凹凸上に積層しておくことが好ましい。 [0052] antireflective molded article 1 of the present invention, even while the anti-reflection structure 3 consisting of fine irregularities is exposed on the surface, but exhibits sufficient effect to prevent scratching or contamination due to inadvertent contact means in, it is preferable to a low refractive index layer in which the refractive index is a low resin composition of light was laminated on the fine irregularities than the portion of the anti-reflection structure.

【0053】低屈折率層をフッ素系樹脂もしくはシリコーン系樹脂の素材で形成すると、いずれも光の屈折率が1.3〜1.4であるため、電離放射線硬化性樹脂組成物の硬化物からなる透明層3の一般的な屈折率(アクリレート系の樹脂組成物の硬化物であり、光の屈折率は1.5以上である。)よりも低いので好ましく、なお、 [0053] When forming the low refractive index layer of a material of fluorine resin or silicone resin, for both refractive index of the light is 1.3 to 1.4, a cured product of an ionizing radiation curable resin composition (a cured product of acrylate-based resin composition, the refractive index of the light is 1.5 or more.) transparent layer common refractive index of 3 made is lower than preferably still,
これら素材の水との接触角が100度以上あるため、防汚性も有していて好ましい。 The contact angle with water of these materials is more than 100 degrees, preferably have also antifouling property. 上記のフッ素系樹脂もしくはシリコーン系樹脂等の使用によって、低屈折率層に特別の機能を持たせる必要性が低いときは、反射防止構造3との接着を考慮して選択したフッ素系樹脂・シリコーン系樹脂以外の熱可塑性樹脂を用いて低屈折率層を構成してもよい。 The use of such above fluorine-based resin or a silicone resin, when the need to have a special function in the low refractive index layer is low, fluorine resin, silicone selected in consideration of the adhesion between the anti-reflection structure 3 the thermoplastic resin other than the system resin may constitute the low-refractive index layer used.

【0054】これらの素材は、蒸着等の乾式工程、もしくは通常のコーティングのような湿式工程のいずれによって形成してもよい。 [0054] These materials may be formed by either a wet process such as a dry process or a conventional coating, such as vapor deposition. あるいは、反射防止構造3に微細凹凸を与えるための型面に予め塗付しておき、その上から電離放射線硬化性樹脂組成物を適用することにより、 Alternatively, previously subjected beforehand coated on the mold surface to provide fine irregularities on the anti-reflection structure 3, by applying an ionizing radiation-curable resin composition thereon,
積層する方法も採れる。 Method of stacking is also mined. または、上記のフッ素系樹脂もしくはシリコーン系樹脂を、成形品2もしくは表面層4 Or, the above-mentioned fluorine-based resin or a silicone resin, molded articles 2 or the surface layer 4
を形成するための電離放射線硬化性樹脂組成物と混合して、反射防止構造3を形成した後に、これらフッ素系樹脂もしくはシリコーン系樹脂をブリードアウトさせることによってよい。 Mixed to ionizing radiation curable resin composition for forming the, after forming the anti-reflection structure 3 may by bleed out these fluorine-based resin or a silicone resin.

【0055】本発明の反射防止成形品1には、上記の構成に加えて、使用時の塵埃の付着を防止するための帯電防止処理や、種々の用途に適用する際の便を考慮して、 [0055] The antireflective molded article 1 of the present invention, in addition to the above, the adhesion of dust antistatic treatment and for preventing use, taking into account the flights when applied to various applications ,
反射防止構造3を有するのとは反対側に粘着加工を施す等を行なってもよい。 It may be performed such as applying adhesive layer on the opposite side as having an anti-reflection structure 3.

【0056】帯電防止処理は、具体的には帯電防止剤や導電性微粒子を適用することにより行なえ、成形品2や表面層4を形成する際に樹脂材料中に配合するか、もしくは反射防止構造3上に塗付することによって行なう。 [0056] The antistatic treatment is performed by specifically applying the antistatic agent and conductive fine particles, or incorporated into the resin material in forming the molded article 2 and the surface layer 4, or the anti-reflection structure 3 carried out by with paint on.
あるいは金属酸化物薄膜を形成することにより、帯電防止処理を行なってもよい。 Or by forming a metal oxide thin film may be subjected to antistatic treatment.

【0057】粘着加工は、ポリアクリル酸エステルやゴム系の粘着剤を直接塗付してもよいが、通常は、離型紙に粘着剤を塗付したものをラミネートすることによって適用し、離型紙は、粘着剤が露出して不用意に接着したり、塵埃が付着するのを防止する意味で、使用するまでの間、貼ったままにしておくとよい。 [0057] adhesive processing, polyacrylate or rubber based adhesive to be directly coated subjected, but usually applies by laminating those given coating an adhesive to the release paper, release paper is or inadvertently adhered adhesive is exposed, in the sense to prevent the dust from adhering until use, or if left stuck. 粘着剤層の厚みとしては、20〜40μm程度が好ましい。 The thickness of the adhesive layer, about 20~40μm are preferred.

【0058】本発明の反射防止性成形品1は、当った光の反射を抑制して眩しさを減らすことができるが、逆に、当った光を反対側に有効に出射する用途において使用することもできる。 [0058] antireflective molded article 1 of the present invention can reduce glare by suppressing reflection of hit light is, on the contrary, be used in applications that effectively emits light hit the opposite side it is also possible. 反射を抑制して眩しさを減らす目的では、本来的な機能との兼ね合いもあるが、自動車、 For the purpose of reducing to glare suppressing reflection, there is a trade-off between intrinsic function, an automobile,
鉄道車両、船舶、航空機等の交通機関の窓、展望用窓、 Railway vehicles, ships, window of transportation such as aircraft, outlook for the window,
ドア等、あるいは、建造物の窓、天窓、ドア、はめ殺しの窓、明かり採り窓等(総称して窓等と言う。)がある。 Door or the like, or, window of a building, skylights, doors, windows fit killing, lights picking window or the like (referred to collectively, the window or the like with.) There is. これら窓等は、太陽光や夜間の自動車のヘッドライト等を反射して、予期しない場合に、眩しさをもたらすことが有り得るので、これらの窓等の外側に、もしくはこららに置き換えて本発明の反射防止性成形品1を適用し得る。 These window or the like reflects the sunlight and nighttime automobile headlights, if unexpected, since it is likely to result in glare, outside of such these windows, the present invention replaces the Moshikuwakorara It may apply antireflective molded article 1. これらにおいては反射防止構造が屋外側、もしくは外側になるようにする。 In these so that the anti-reflection structure is an outdoor side, or on the outside.

【0059】勿論、これら窓等においては、交通機関内部、もしくは建造物内部に設置された照明が内部で反射するために、屋外を眺めるときに支障をもたらすこともあるので、そのような場合には、本発明の反射防止性成形品1を反射防止構造を内側に向けて、窓等に適用することも有り得る。 [0059] Of course, in these windows and the like, in order to transport inside or lighting installed inside buildings reflected internally, since also result in trouble when overlooking the outdoors in such a case is the antireflective molded article 1 of the present invention toward the anti-reflection structure on the inside, also likely be applied to windows or the like. 従って、場合によっては、窓等の外側と内側に反射防止構造を必要とすることがあり、別々の反射防止性成形品1を窓等の外側と内側とに適用してもよいが、図1を引用して説明したような両面に反射防止構造を有する反射防止性成形品1を用いてもよい。 Therefore, in some cases, it may require anti-reflection structure on the outside and the inside of the window or the like, but a separate antireflective molded article 1 may be applied to the outer and inner window or the like, FIG. 1 sided anti-reflection structure as described with reference to be used antireflective molded article 1 having a.

【0060】上記のような交通機関においては、運転席、操縦席やその他の場所に備えられた計器類やディスプレイの表面に、本発明の反射防止性成形品1を反射防止構造を観察側に向けて、適用することが出来る。 [0060] In the transportation as described above, the driver's seat, the cockpit and other a provided instruments and surface of the display location, on the observation side of the anti-reflection structure antireflective molded article 1 of the present invention directed, it can be applied. 眩しさを減らして、計器やディスプレイの視認性を向上させ得る。 Reduce the glare may improve the visibility of the instruments and displays.

【0061】また、一般的な電気器具、音響機器、時計、もしくはカメラ等の機器類が有する種々の表示部分にも、本発明の反射防止性成形品1を適用することが出来る。 [0061] Further, general electric appliances, audio equipment, also various display portions equipment has such as a watch or a camera, can be applied antireflective molded article 1 of the present invention. 例を挙げると、電卓、パソコンのディスプレイ(CRT、液晶ディスプレイ、PDP等がある。)や携帯可能な端末機器のディスプレイ、携帯電話、IC録音機、CDプレーヤー、DVDプレーヤー、MDプレーヤー、ビデオテープレコーダー、各種オーディオ機器、ビデオカメラ、デジタルカメラの表示機構を有する機器類である。 By way of example, a calculator, a computer display (CRT, a liquid crystal display, there is a PDP and the like.) And portable terminal equipment of the display, mobile phones, IC recorders, CD players, DVD players, MD players, video tape recorder a equipment with various audio equipment, video cameras, a display mechanism of a digital camera. 外光の反射防止の目的で、本発明の反射防止性成形品1を反射防止構造を外側にして適用する。 Outside of preventing reflection of light objects, the antireflective molded article 1 of the present invention to apply the anti-reflection structure on the outside. これらに適用する際には、基板が偏光板であったり、帯電防止性であってもよいし、また、基板がタッチパネルであってもよい。 When applying to these, or a substrate is a polarizing plate may be a antistatic, The substrate may be a touch panel.

【0062】これら計器やディスプレイは、自己発光型のものも有り得るが、通常は、バックライト、もしくはフロントライトにより、照明して視認性を付与していることが多いので、窓等の例で述べたのと同様に、両面に反射防止構造を有する反射防止性成形品1を用いてもよい。 [0062] These instruments and displays, but also likely that the self-luminous type, usually, the backlight, or by the front light, because it is often to impart visibility and lighting, described in example window or the like in the same way as may be used antireflective molded article 1 having an anti-reflection structure on both sides. 一つの例として、フロントライト型の液晶ディスプレイにおける、導光板の液晶側に反射防止構造を適用して反射防止性成形品とすることが好ましい。 As one example, in the front light type liquid crystal display, it is preferable that the antireflective molded article by applying an anti-reflection structure on the liquid crystal side of the light guide plate. 観察側は、 Observation side,
通常、傾斜を持っているか、もしくは稜線が平行になるよう廃止されたプリズムアレイを形成したものであるが、必要によっては、観察側にも、反射防止構造を適用するとよい。 Normally, either have an inclination, or it ridge is made by forming obsolete prism array so as to be parallel, the need is also the observation side, it is preferable to apply an anti-reflection structure.

【0063】 [0063]

【発明の効果】請求項1の発明によれば、射出成形によるため、高圧で型内に樹脂材料を充填するために型形状の再現性がよく、効率的な生産が可能であり、干渉膜を有するものではないので、見る角度によって着色して見える欠点がない反射防止性成形品を提供することができる。 According to the invention of claim 1 according to the present invention, since by injection molding, good reproducibility of the mold shape to fill the resin material into the mold at high pressure, it is possible to perform efficient production, interference film because it does not have a can provide without drawbacks which appears colored by the angle antireflective molded article View. 請求項2の発明によれば、種々の用途に適用したときに、一方向からの光の反射を防止して反射させない性質、もしくは一方向からの光を反射を防止して有効に反対側に導くことが可能な性質を有する反射防止性成形品を提供することができる。 According to the invention of claim 2, when applied to various uses, not reflected by preventing the reflection of light from one direction properties, or the light from one direction to prevent reflected effectively on the opposite side it can provide antireflective molded article having a capable property be derived. 請求項3の発明によれば、一方向からの光を光を、反射を防止して、有効に他方向に導くと共に、他方向から眺めた際に、外光の反射が防止されるので、一方向からの光の視認性を高くすることが可能な反射防止性成形品を提供することができる。 According to the invention of claim 3, the light from one direction, to prevent reflection, effectively guides the other direction, when viewed from the other direction, the reflection of external light is prevented, it is possible to provide an antireflection molded article capable of increasing the visibility of the light from one direction. 請求項4の発明によれば、請求項1〜請求項3いずれかの発明の効果に加え、基板層と表面層とを構成する樹脂材料を各々選択して使用し、しかも成形により両層の積層までが完成した反射防止性成形品を提供することができる。 According to the invention of claim 4, claims 1 to 3 in addition to the effects of the invention of any one, using the resin material constituting the substrate layer and the surface layer each selected and, moreover by molding both layers until lamination may provide a finished antireflective molded article. 請求項5の発明によれば、請求項1〜請求項4いずれかの発明の効果に加え、少なくとも電離放射線硬化性樹脂組成物の硬化物から構成された部分の物理的もしくは化学的性状の優れた反射防止性成形品を提供することができる。 According to the invention of claim 5, in addition to the claims 1 to 4 the effect of any of the invention, excellent physical or chemical properties of the constructed portions of a cured product of at least an ionizing radiation curable resin composition the anti-reflective molded article can be provided. 請求項6の発明によれば、型の内面に光の波長以下のピッチの無数の微細凹凸が形成されたものを使用して、射出成形を行なうので、型形状がよく再現された反射防止性成形品を効率よく製造することが可能な、 According to the invention of claim 6, using what innumerable fine irregularities inner surface of a pitch equal to or less than the wavelength of the light type is formed, because the injection molding, antireflective the mold shape is reproducibly capable of producing a molded article efficiently,
反射防止性成形品の製造方法を提供することができる。 Method of manufacturing anti-reflection moldings can be provided.
請求項7の発明によれば、片面に反射防止構造を有する反射防止性成形品を製造する以外、請求項6の発明と同じ効果を生じ得る、反射防止性成形品の製造方法を提供することができる。 According to the invention of claim 7, except that the production of anti-reflective molded article having an anti-reflection structure on one side, can produce the same effect as the invention of claim 6, to provide a method for producing anti-reflective molded article can. 請求項8の発明によれば、相対する二面に反射防止構造を有する反射防止性成形品を製造する以外、請求項6の発明と同じ効果を生じ得る、反射防止性成形品の製造方法を提供することができる。 According to the invention of claim 8, except that the production of anti-reflective molded article having an anti-reflection structure on opposite two surfaces, may produce the same effect as the invention of claim 6, the method for manufacturing the anti-reflection moldings it is possible to provide. 請求項9の発明によれば、請求項6〜請求項8いずれかの発明の効果に加え、二以上の樹脂材料を用いた積層体としての反射防止性成形品を製造し得る反射防止性成形品の製造方法を提供することができる。 According to the invention of claim 9, claim 6 in addition to claim 8 effect of the invention of any one, antireflective molded capable of producing an antireflective molded article of a laminated body using two or more resin materials it is possible to provide a manufacturing method of the goods. 請求項10の発明によれば、請求項5〜請求項9いずれかの発明の効果に加え、予め金型の内部を真空状態とする排気工程を行なうので、樹脂材料の充填がスムーズに行なえ、歪みが少ない反射防止性成形品を製造し得る反射防止性成形品の製造方法を提供することができる。 According to the invention of claim 10, in addition to the effect of the invention of any one claims 5 to 9, in advance since the interior of the mold perform the exhausting process of the vacuum state, easy and convenient to fill the resin material, method for producing anti-reflective molded article that can produce less distortion antireflective molded article can be provided. 請求項11の発明によれば、請求項10の発明の効果に加え、充填工程中も排気工程を続けるので、樹脂材料が分解する等して発生するガスを除去できるので、歪みがごく少ない反射防止性成形品を製造し得る反射防止性成形品の製造方法を提供することができる。 According to the invention of claim 11, the effect of the invention according to claim 10, since during the filling process continued evacuation process, since the gas resin material is generated in such degrading can be removed, the strain with few reflecting method for producing anti-reflective molded article capable of producing anti-molded article can be provided.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】反射防止性成形品の断面構造を示す図である。 1 is a diagram showing a sectional structure of the antireflective article.

【図2】反射防止性成形品の微細凹凸の断面形状を示す図である。 2 is a diagram showing a sectional shape of the fine irregularities of the anti-reflective molded article.

【図3】反射防止性成形品の微細凹凸の配列を示す図である。 3 is a diagram showing an arrangement of fine irregularities of the anti-reflective molded article.

【図4】反射防止性成形品の製造に用いる成形機の一例を示す図である。 4 is a diagram showing an example of a molding machine used for the production of anti-reflective molded article.

【図5】反射防止性成形品の製造に用いる成形機の他の例を示す図である。 5 is a diagram showing another example of a molding machine used for the production of anti-reflective molded article.

【符号の説明】 1 反射防止性成形品 2 成形品 3 反射防止構造 4 表面層 11 射出成形機 12 可動側取付板(12a;可動側型板) 13 固定側取付板(13a;固定側型板) 14 キャビティ 15 排気孔 16 ノズル 17 ランナ 18 溝(Oリング) 19 隙間 [EXPLANATION OF SYMBOLS] 1 antireflective molded article 2 molded article 3 anti-reflection structure 4 surface layer 11 injection molding machine 12 movable-side mounting plate (12a; movable side mold plate) 13 fixed side mounting plate (13a; fixed die plate ) 14 cavity 15 vents 16 nozzle 17 runner 18 grooves (O-ring) 19 gap

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl. 7識別記号 FI テーマコート゛(参考) // B29L 11:00 G02B 1/10 A Fターム(参考) 2H042 BA04 BA12 BA13 BA15 BA20 2K009 AA10 BB11 BB14 BB24 DD15 4F202 AA13 AA29 AA44 AH75 CA11 CB01 CD23 CK11 CK83 CK86 CP01 CP06 4J011 AC04 QA03 QA06 QA09 QA12 QA13 QA26 QA38 QA40 QB12 QB14 QB16 QB19 SA02 SA12 SA22 SA32 SA33 SA34 SA64 SA83 SA86 SA87 UA04 VA04 WA07 ────────────────────────────────────────────────── ─── of the front page continued (51) Int.Cl. 7 identification mark FI theme Court Bu (reference) // B29L 11:00 G02B 1/10 a F-term (reference) 2H042 BA04 BA12 BA13 BA15 BA20 2K009 AA10 BB11 BB14 BB24 DD15 4F202 AA13 AA29 AA44 AH75 CA11 CB01 CD23 CK11 CK83 CK86 CP01 CP06 4J011 AC04 QA03 QA06 QA09 QA12 QA13 QA26 QA38 QA40 QB12 QB14 QB16 QB19 SA02 SA12 SA22 SA32 SA33 SA34 SA64 SA83 SA86 SA87 UA04 VA04 WA07

Claims (11)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 透明性成形品の少なくとも片面に、透明性素材で形成され、光の波長以下のピッチの無数の微細凹凸からなり、厚み方向に光の屈折率が変化する反射防止構造を有することを特徴とする反射防止性成形品。 On at least one surface of 1. A transparent molded article, formed of a transparent material, made innumerable fine irregularities of the following pitch wave of light, having an antireflection structure in which the refractive index changes in the optical thickness direction antireflective molded article, characterized in that.
  2. 【請求項2】 透明性成形品の片面に、透明性素材で形成され、光の波長以下のピッチの無数の微細凹凸からなり、厚み方向に光の屈折率が変化する反射防止構造を有することを特徴とする反射防止性成形品。 On one side of 2. A transparent molded article, formed of a transparent material, made innumerable fine irregularities smaller than the wavelength of the pitch of the light, it has a reflection preventing structure in which the refractive index of the light is changed in the thickness direction antireflective molded article characterized by.
  3. 【請求項3】 透明性成形品の両面に、透明性素材で形成され、光の波長以下のピッチの無数の微細凹凸からなり、厚み方向に光の屈折率が変化する反射防止構造を有することを特徴とする反射防止性成形品。 On both sides of 3. A transparent molded article, formed of a transparent material, made innumerable fine irregularities smaller than the wavelength of the pitch of the light, it has a reflection preventing structure in which the refractive index of the light is changed in the thickness direction antireflective molded article characterized by.
  4. 【請求項4】 透明性を有する基板層と前記反射防止構造を有する表面層とが積層されており、各々が一つの射出成形機に接続された異なる樹脂射出装置または複数の樹脂材料を射出する一つの樹脂射出装置から射出された素材からなることを特徴とする請求項1〜請求項3いずれか記載の反射防止性成形品。 4. A surface layer having the anti-reflection structure and the substrate layer having transparency are laminated, each of which emits different resin injection device or a plurality of resin material connected to one of the injection molding machine It claims 1 to 3 antireflective molded article according to any one which is characterized in that it consists of material emitted from one of resin injection device.
  5. 【請求項5】 表面層の一部、表面層の全部、もしくは表面層および基板層を含む全体が電離放射線硬化性樹脂組成物の硬化物からなることを特徴とする請求項1〜請求項4いずれか記載の反射防止性成形品。 5. A part of the surface layer, the entire surface layer, or claims 1 to 4, the entire surface layer and comprising a substrate layer is characterized by comprising a cured product of an ionizing radiation curable resin composition antireflective molded article according to any one.
  6. 【請求項6】 内面の少なくとも片面に、光の波長以下のピッチの無数の微細凹凸が形成された金型を準備する準備工程、前記金型の内部に透明性を有する成形用樹脂を射出して充填する充填工程、冷却工程、および金型を開いて成形品を取り出す脱型工程とを逐次行なうことからなる反射防止性成形品の製造方法。 On at least one surface of 6. inner surface preparation step of preparing a mold having innumerable fine unevenness of the wavelength or less of the pitch of the light is formed, a molding resin having transparency to the inside of the mold by injection filling process, the cooling process, and the manufacturing method of the anti-reflective molded article comprising to perform a demolding step sequential to the mold by opening removing the molded article to be filled Te.
  7. 【請求項7】 内面の片面に、光の波長以下のピッチの無数の微細凹凸が形成された金型を準備する準備工程、 7. On one surface of the inner surface, a preparation step of preparing a mold innumerable fine unevenness of the wavelength or less of the pitch of the light is formed,
    前記金型の内部に透明性を有する成形用樹脂を射出して充填する充填工程、冷却工程、および金型を開いて成形品を取り出す脱型工程とを逐次行なうことからなる反射防止性成形品の製造方法。 Filling step of filling by injection molding resin having transparency to the inside of the mold, the cooling step, and mold open consists in performing the demolding step for taking out the molded article sequentially antireflective molded article the method of production.
  8. 【請求項8】 内面の相対する二面に、光の波長以下のピッチの無数の微細凹凸が形成された金型を準備する準備工程、前記金型の内部に透明性を有する成形用樹脂を射出して充填する充填工程、冷却工程、および金型を開いて成形品を取り出す脱型工程とを逐次行なうことからなる反射防止性成形品の製造方法。 The two opposite sides of 8. inner surface preparation step of preparing a mold having innumerable fine unevenness of the wavelength or less of the pitch of the light is formed, a molding resin having transparency in the interior of the mold filling process, the cooling process, and the manufacturing method of the anti-reflective molded article comprising to perform a demolding step sequential to the mold by opening removing the molded article to fill the injection to.
  9. 【請求項9】 前記充填工程を、一つの射出成形機に接続された二以上の樹脂射出装置または複数の樹脂材料を射出する一つの樹脂射出装置を用いて行なうことを特徴とする請求項6〜請求項8いずれか記載の反射防止性成形品の製造方法。 9. claims, characterized in that performing the filling step, using one of the resin injection device for injecting connected to one of the injection molding machine more of a resin injection device or a plurality of resin material 6 ~ 8. the manufacturing method of the antireflective molded article according to any one.
  10. 【請求項10】 前記充填工程に先立って、金型の内部を排気して真空状態とする排気工程を行なうことを特徴とする請求項5〜請求項9いずれか記載の反射防止性成形品の製造方法。 10. Prior to the filling process, the inside was of claims 5 to 9 antireflective molded article according to any one, characterized in that performing the exhaust process of the vacuum state evacuation of the mold Production method.
  11. 【請求項11】 前記充填工程中も排気工程を続けることを特徴とする請求項10記載の反射防止性成形品の製造方法。 11. The method for producing anti-reflective molded article according to claim 10, wherein also during the filling process continued evacuation process.
JP2001064668A 2001-03-08 2001-03-08 Reflection preventive molded part and method for manufacturing the same Pending JP2002267815A (en)