JP2002219143A - Wound covering material - Google Patents

Wound covering material

Info

Publication number
JP2002219143A
JP2002219143A JP2001017061A JP2001017061A JP2002219143A JP 2002219143 A JP2002219143 A JP 2002219143A JP 2001017061 A JP2001017061 A JP 2001017061A JP 2001017061 A JP2001017061 A JP 2001017061A JP 2002219143 A JP2002219143 A JP 2002219143A
Authority
JP
Japan
Prior art keywords
chitin
chitosan
cotton
material
wound
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2001017061A
Other languages
Japanese (ja)
Inventor
Yusuke Matsuda
Katsuhiko Takayanagi
Nobuyuki Tanimoto
裕介 松田
信行 谷本
勝彦 高柳
Original Assignee
Unitika Ltd
ユニチカ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Unitika Ltd, ユニチカ株式会社 filed Critical Unitika Ltd
Priority to JP2001017061A priority Critical patent/JP2002219143A/en
Publication of JP2002219143A publication Critical patent/JP2002219143A/en
Application status is Pending legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a wound covering material which imparts adequately strong force to a cotton-like material made from chitin or chitosan, prevents a kink, a displacement and fall-off relative to a wound surface, enhances production efficiency, and avoids the influence of a residual monomer such as a synthetic fiber material.
SOLUTION: In the wound covering material, the cotton-like material made from chitin or chitosan and a nonwoven fabric composed of natural fibers are laminated. The cotton-like material is composed of a cotton-like aggregate obtained by opening a fiber made from chitin or chitosan, or a fibril. The wound covering material is characterized in that the basis weight ratio of the cotton- like material to the nonwoven fabric is taken as 1:2-10:1.
COPYRIGHT: (C)2002,JPO

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、嵩高なキチン又はキトサン綿状物と、支持体として天然繊維からなる不織布とを積層一体化した不織布支持体付キチン綿状物であり、医療分野における外傷、熱傷等の創傷被覆材に関するものである。 The present invention relates includes a bulky chitin or chitosan cotton-like material, a nonwoven support with chitin cotton-like materials having a nonwoven fabric made of natural fibers integrally laminated as a support, trauma in the medical field relates wound dressing burns like.

【0002】 [0002]

【従来の技術】従来、キチン又はキトサンは抗菌作用、 Conventionally, chitin or chitosan antibacterial action,
止血作用、治癒促進作用、吸着作用、植物の生育促進作用などさまざまな性質が解明され、幅広い分野で使用されている。 Hemostatic effect, healing promoting action, adsorption effect, been elucidated a variety of nature, such as growth-promoting effect of the plant, has been used in a wide range of fields. 使用される形態も粉末、繊維、フィルム、 Form used also powders, fibers, films,
膜、綿状、ウェブ状などさまざまであり、それぞれの用途によって使い分けられているが、特にキチン又はキトサン綿状物は上記の性質を利用した応用が数多く考えられる。 Film, like cotton, are varied, such as web-like, but are used for different respective applications, particularly chitin or chitosan cotton-like materials applications utilizing the above properties can be considered a number.

【0003】例えば特許第3046099号公報には、キチン又はキトサン綿状物を傷の保護材として使用することが提案され、その優れた浸出液排除効果や、治癒促進効果から良い結果を得られると記載されている。 [0003] For example, Japanese Patent No. 3046099 publication, it is proposed to use the chitin or chitosan flocculent as a protective material for wound, wherein the superior exudate elimination effect or, to be obtained good results from the healing-promoting effects It is.

【0004】更に特開平7-102458号公報において使いやすさ等においてかなり改善されたキチンウェブ状混合物が提案されている。 [0004] Further chitin web-like mixture which is considerably improved in usability or the like in JP-A 7-102458 JP has been proposed. また、天然繊維以外の不織布支持体としてナイロン不織布とキチン綿状物を積層し使いやすさ等が改良された創傷被覆材を使用した報告がある(新薬と臨床、 44 〔7〕(1995)(株)医薬情報研究所P. Further, there is a report that by laminating a nylon nonwoven fabric and chitin flocculent usability such as non-woven support other than natural fibers were used wound dressings improved (new drugs and clinical, 44 (7) (1995) ( Ltd.) pharmaceutical information Institute P.
1255)。 1255).

【0005】 [0005]

【発明が解決しようとする課題】しかしながら、特許第 The object of the invention is to, however, No.
3046099号公報に記載のキチン又はキトサン綿状物のみからなる傷の保護材においては、キチン又はキトサン綿状物を屈曲部や外部からの強い力がかかる部位に使用した場合もしくはそれ以外の部位に使用した場合においても体動等によりキチン又はキトサン綿状物が創面からズレたり、ヨレたり、脱落する場合もあった。 In protective material wound comprising only chitin or chitosan cotton-like materials described in 3,046,099 discloses the chitin or chitosan flocculent strong force is the case or other use in such sites sites from the bent portion and the outside or displaced chitin or chitosan cotton-like materials from the wound by body movement or the like even when used, or twisted, there sometimes fall off. また創面に貼付し縫合固定を行った場合においてもキチン又はキトサン綿状物の強力が低いため縫合部が裂けたり、ちぎれる場合もあり、また創面に貼付したキチン又はキトサン綿状物の上に二次ドレッシングとしてガーゼを使用するが、ガーゼ交換の際にキチン又はキトサン綿状物とガーゼが固着して破れたり脱落したりする場合もある等使用には限界があった。 The tearing suture unit for powerful low chitin or chitosan flocculent even when performed affixed to the wound suture fixation, sometimes torn, also two on a chitin or chitosan flocculent was affixed to the wound using the gauze as the next dressing, but also equal use with the case where chitin or chitosan flocculent and gauze in gauze replacement or falling torn by fixing is limited.

【0006】更に製造工程においてキチン又はキトサン綿状物は強力が低くロール様巻取りができなかった。 [0006] chitin or chitosan cotton-like material in the further manufacturing process was not a strong roll-like winding low. このため出来上がったシートは折りたたんだ状態での保管となり、キチン又はキトサン綿状物に折り目がつき収率低下や、使用上支障となる等の問題があった。 Thus resulting sheet becomes storage in a folded state, the yield decreases and sticks crease chitin or chitosan cotton-like material, there are problems such a usage hindrance.

【0007】また、特開平7-102458号公報に記載されたキチンウェブ状混合物の場合には、混合されているキチン以外の合成繊維が創面に付着し組織に取込まれ残存するという問題があった。 [0007] In the case of chitin web-like mixtures described in JP-A-7-102458, the synthetic fibers other than chitin being mixed is taken to adhere to the wound surface tissue there is a problem that remains It was. さらに、不織布支持体として天然繊維以外の例えばナイロン等の合成繊維材料を使用すると、撥水性の素材のために浸出液の吸収が悪く浸出液の多い創や深い創へは適用できなく、また残留モノマー等の溶出、医療廃棄物として処理するときの環境への負荷が大きい等安全および環境面に問題があった。 Furthermore, the nonwoven fabric when the support using the synthetic fiber materials of natural fibers other than such as nylon or the like as, not be applied with exudate poor absorption of exudate for the water-repellent material often wounds and deep into the wound, also residual monomers elution, there is a problem at equal safety and environmental load is large on the environment when handling as medical waste.

【0008】本発明は、キチン又はキトサン綿状物に充分な強力を付与し、創面に対するヨレ、ズレ、脱落を防ぎ、生産効率を向上させ、更に合成繊維材料のような残留モノマーの影響も回避した創傷被覆材を提供することを目的とするものである。 [0008] The present invention is to provide sufficient strong to chitin or chitosan cotton-like material, twisted against wound surface, preventing deviation, a falling off, improve production efficiency, even further the influence of such residual monomer as a synthetic fiber material around it is an object to provide a the wound dressing.

【0009】 [0009]

【課題を解決するための手段】本発明者らは、上記の目的を達成するために鋭意研究をかさねた結果、キチン又はキトサン綿状物と天然繊維からなる不織布とを積層した不織布支持体付キチン又はキトサン綿状物がかかる課題を解決できることを見出し、本発明に到達した。 The present inventors have SUMMARY In order to achieve the above, intensive result of extensive research, with a nonwoven fabric support by laminating a nonwoven fabric made of chitin or chitosan flocculent and natural fibers in order to achieve the above object can solve the above problem chitin or chitosan cotton-like material, we have reached the present invention.

【0010】すなわち、本発明は、キチン又はキトサンの繊維又はフィブリルを開繊して得られる綿状集合体からなるキチン又はキトサン綿状物と、天然繊維からなる不織布とが積層された創傷被覆材であって、キチン又はキトサン綿状物と天然繊維からなる不織布との目付量比率(キチン又はキトサン綿状物:天然繊維不織布)が1:2〜10:1であることを特徴とする創傷被覆材を要旨とするものである。 [0010] Namely, the present invention provides a wound dressing and chitin or chitosan cotton-like material made of flocculent aggregates obtained by spreading the fibers or fibrils of chitin or chitosan, and a nonwoven fabric made of natural fibers are stacked a is, the basis weight ratio (chitin or chitosan flocculent: natural fiber nonwoven fabric) and nonwoven fabric made of chitin or chitosan flocculent and natural fibers 1: 2 to 10: a wound dressing which is a 1 it is to the wood and gist.

【0011】 [0011]

【実施の態様】以下、本発明を詳細に説明する。 [Aspect of implementation The present invention will now be described in detail. 本発明におけるキチン又はキトサンとは、甲殻類、昆虫類等の外骨格を塩酸処理並びに苛性ソーダ処理して灰分および蛋白質を除去して得られるもの及びその誘導体をいい、 The chitin or chitosan of the present invention, refers to crustaceans, and those derivatives obtained Exoskeleton to remove hydrochloric acid treatment and sodium hydroxide treatment to ash and proteins such as insects,
通常のキチン(ポリ-N-アセチル-D-グルコサミン)及びその脱アセチル化物(これらのうち脱アセチル化度が高く酸に溶解するものをキトサンと呼んでいる)、さらにはグルコサミン残基の-OH基または-CH 2 OH基がエステル化、エーテル化、カルボキシメチル化あるいはO-エチル化等に修飾されたキチン誘導体も含まれる。 -OH of the normal chitin (is calling what degree of deacetylation of these are dissolved in a high acid and chitosan) (poly -N- acetyl -D- glucosamine) and its de-acetylated product, more glucosamine residues group or -CH 2 OH group is esterified, etherified, also includes chitin derivatives that are modified carboxymethylated or O- ethyl and the like.

【0012】本発明で脱アセチル化キチンを使用する場合、キチンの脱アセチル化はキチンをアルカリ処理という周知の方法により行うことができる。 [0012] When using a deacetylated chitin in the present invention, deacetylation of chitin can be carried out by methods well known that alkaline treatment of chitin. この際、使用するアルカリ濃度、処理温度、処理時間等を適宜変えることにより、脱アセチル化度を容易に調整することができる。 At this time, alkali concentration used, processing temperature, by varying the treatment time or the like as appropriate, can be easily adjusted deacetylation degree.

【0013】本発明で用いられるキチン又はキトサン綿状物とは、キチン又はキトサンの繊維又はフィブリルを開繊して得られる綿状集合体である。 [0013] The chitin or chitosan cotton-like materials used in the present invention, a flocculent aggregates obtained by spreading the fibers or fibrils of chitin or chitosan. キチン又はキトサン綿状物の目付量は特に限定されず、使用時に必用とする創傷の状態、深さによって適宜決定すればよく、通常 Basis weight of the chitin or chitosan cotton-like materials is not particularly limited, the wound to be required when using state, may be suitably determined by the depth, usually
10〜400g/cm 2の範囲であり、好ましくは30〜250g/cm 2 In the range of 10 to 400 g / cm 2, preferably 30 to 250 g / cm 2,
更に好ましくは60〜150 g/cm 2の範囲であれば最適である。 More preferably is optimal if in the range of 60~150 g / cm 2.

【0014】本発明の創傷被覆材で使用される天然繊維からなる支持体不織布は、精製されたコットン、木綿、 [0014] The support nonwoven fabric made of natural fibers used in the wound dressing of the present invention, purified cotton, cotton,
麻、シルク、ウール等をウォータージェット機もしくはニードルパンチ機にて交絡させる等の公知の方法で製造されたものが好ましい。 Hemp, silk, those produced by a known method such as that of entangled wool in a water jet or needle punch machine is preferred. この不織布の目付量は、特に限定されないが、使用時に必用とする強さによって適宜決定すればよいが、目付量と強さ、強さと厚み及び硬さは比例するので、創傷部位に密着し浸出液の適度な吸排液により適正な湿潤環境を創出することによって治癒効果を最大限に発揮する目付量としては通常10〜300 g/cm 2 Basis weight of the nonwoven fabric is not particularly limited, may be suitably determined depending on the intensity of the necessity at the time of use, the basis weight and strength, because the strength and thickness and hardness in proportion to, and in close contact with the wound site exudate the weight per unit area to maximize the healing effect by creating a proper moist environment by moderate intake fluid usually 10 to 300 g / cm 2
であり、好ましくは15〜200 g/cm 2 、更に好ましくは25 , And the preferably 15 to 200 g / cm 2, more preferably 25
〜100 g/cm 2の範囲が最適である。 Range to 100 g / cm 2 is optimal.

【0015】本発明の創傷被覆材においては、キチン又はキトサン綿状物と天然繊維からなる支持体不織布の目付量比率(キチン又はキトサン綿状物:支持体不織布) [0015] In the wound dressing of the present invention, chitin or chitosan cotton-like material and support non-woven fabric made of natural fiber basis weight ratio (chitin or chitosan flocculent: support nonwoven)
が、1:2〜10:1の範囲であることが必要であり、好ましくは1:1〜5:1更に好ましくは2:1〜4:1の範囲である。 But 1: 2 to 10: should be in the 1, preferably in the range of from 1: 1 to 5: 1 and more preferably 2: 1 to 4: 1. キチン又はキトサン綿状物と天然繊維からなる支持体不織布の目付量比率が前記範囲内であれば、創傷治癒効果を有し、且つ強力に優れる創傷被覆材を得ることができる。 Within the basis weight ratio is the range of the support non-woven fabric made of chitin or chitosan flocculent and natural fibers can have a wound healing effect, obtain and strong excellent wound dressing. キチン又はキトサン綿状物と天然繊維からなる支持体不織布の目付量比率が前記範囲外であると、必要とする強力が得られなかったり、硬すぎて充分な治癒効果が期待できない場合がある。 If the basis weight ratio of the support non-woven fabric made of chitin or chitosan flocculent and natural fibers is outside the above range, or not strong is obtained require, a sufficient curing effect too hard may not be expected. 得られた創傷被覆材全体の目付量は、目的に応じて決定すればよく、特に限定されるものではないが、目付量が20g/m 2以上が好ましく、 Basis weight of the overall resulting wound dressing may be determined according to the purpose, but are not particularly limited, but 20 g / m 2 or more is preferable basis weight,
更に40g/m 2以上のものがより好ましく、70g/m 2以上が最適である。 Further more preferably a 40 g / m 2 or more, and optimally 70 g / m 2 or more.

【0016】本発明の創傷被覆材は、上記のようにキチン又はキトサン綿状物と天然繊維の不織布とが積層されてなるものであるが、キチン又はキトサン綿状物が天然繊維不織布の片面のみに積層されていても、また両面に積層されていてもよい。 The wound dressing of the present invention is chitin or chitosan cotton-like material as described above and the natural fiber of the nonwoven fabric is made by laminating, chitin or chitosan cotton-like materials is only one side of the natural fiber non-woven fabric it is laminated to, or may be laminated on both sides. さらに多層構造のものでもよい。 In addition it may be of multi-layer structure.

【0017】本発明の創傷被覆材の作製方法は、特に限定されるものではないが、例えば以下のようにして作製することができる。 [0017] The method for manufacturing a wound dressing of the present invention is not particularly limited, can be produced, for example, as follows. まず、キチン又はキトサン繊維の短繊維をカード機等の開繊機で開繊、交絡してキチン又はキトサン綿状物を作成する。 First, opening the short fibers of chitin or chitosan fiber opener carding machine or the like, entangled to create a chitin or chitosan cotton-like material.

【0018】ここで用いられるキチン又はキトサンの繊維とは、長手方向に長い形状のものであればよい。 [0018] The chitin or chitosan fiber, as used herein, as long as a long shape in the longitudinal direction. 天然から得られたキチン又はキトサンが繊維状のものであればそのまま使用することができる。 Chitin or chitosan obtained from natural, can be used as long as fibrous. また、キチン又はキトサンを溶剤に溶かした後、凝固液にて凝固してフィブリル状、繊維状にし作製したものを使用してもよい。 Furthermore, was dissolved chitin or chitosan in a solvent, solidification to fibrillar at the coagulating solution may be used after prepared to fibrous.

【0019】溶剤としてはキチン、キトサン、及びその誘導体の種類によって適切なものを使用することができる。 [0019] The solvent can be used chitin, chitosan, and an appropriate one depending on the type of its derivatives. 例えば、天然物を精製したままのキチン及び脱アセチル化度の比較的低いキチンについては、ハロゲン化炭化水素とトリクロル酢酸の混合物、N-メチルピロリドン又はN,N-ジメチルアセトアミドと塩化リチウムとの混合物が好ましく使用され、脱アセチル化されたキチン及びキトサンに対しては、酢酸等の酸溶液が好ましく用いられる。 For example, for the relatively low chitin chitin and deacetylation degree remains purified natural products, mixtures of halogenated hydrocarbons and trichloroacetic acid, a mixture of N- methylpyrrolidone or N, N- dimethylacetamide and lithium chloride is preferably used, for deacetylated chitin and chitosan, the acid solution such as acetic acid is preferably used.

【0020】キチン又はキトサンを溶剤に溶かしてから繊維にする方法としては、通常の湿式紡糸法又は湿式成型法を採用することができる。 [0020] The chitin or chitosan as a method for the fiber and dissolved in a solvent may be employed conventional wet spinning method or a wet molding method. 例えば、キチンを上記溶剤にとかしドープを作製し、ステンレスネット等のフィルターで濾過して不溶解部分や異物を除去した後、ギヤポンプ等で計量輸送し、細孔であるノズルから水、アルコール類、ケトン類又はアルカリ液等の凝固液中に押し出して凝固する。 For example, chitin to produce a dope dissolved in the solvent, after removal of the insoluble portion and foreign matter was filtered through a filter of stainless steel net etc., weighed transported with a gear pump or the like, water from the nozzle is pores, alcohols, ketones or extruding into a coagulation liquid of the alkaline solution or the like to solidify. 凝固物は回転ローラー等にて一定速度で引き取ることにより、繊維を得ることができる。 Coagulum by taking up at a constant speed by rotating roller or the like, it is possible to obtain fibers.

【0021】キチン又はキトサン繊維の太さは、通常の太さのものを使うことができるが、好ましくは0.27〜9. [0021] The thickness of the chitin or chitosan fibers, which can be used those of normal weight, preferably from 0.27 to 9.
0dtex、さらに好ましくは0.45〜4.5dtexであり、0.6〜 0Dtex, more preferably from 0.45~4.5dtex, 0.6~
2.7dtexが最適である。 2.7dtex is optimal. キチン又はキトサン繊維の長さは、0.1〜30.0cm、好ましくは0.5〜15.0cmさらに好ましくは2.0〜8.0cmが最適である。 The length of the chitin or chitosan fiber, 0.1~30.0cm, preferably more preferably 0.5~15.0cm 2.0~8.0cm optimum.

【0022】上記のようにして得られたキチン又はキトサンの繊維又はフィブリルを開繊機により開繊して綿状集合体からなる綿状物を得る。 [0022] obtain a cotton-like material made of flocculent aggregates by spreading the fibers or fibrils of the obtained chitin or chitosan as the opening machine. 得られたキチン又はキトサン綿状物を、次いで支持体である不織布に積層し一体化する。 The resulting chitin or chitosan flocculent was then laminated to the nonwoven fabric as a support to integrate. 積層するためにはニードルパンチ機もしくはウォータージェット機にて交絡させる等の公知の方法が使用できる。 Known method such as for lamination to entangling by needle punching machine or a water jet machine can be used. このようにして本発明の創傷被覆材を作製することができる。 In this manner, it is possible to produce a wound dressing of the present invention.

【0023】本発明の創傷被覆材は、キチン又はキトサン綿状物に支持体として天然繊維からなる不織布が一体化し、創傷被覆材の少なくとも一面がキチン又はキトサン綿状物面となっており、使用に際しては、創傷部にキチン又はキトサン綿状物面を直接貼与すればよい。 The wound dressing of the present invention, a nonwoven fabric made of natural fiber is integrated as a support to the chitin or chitosan cotton-like material, at least one surface of the wound dressing has a chitin or chitosan cotton-like material surface, using in may be given adhered chitin or chitosan flocculent surface directly to the wound portion.

【0024】 [0024]

【実施例】以下、本発明を実施例によって具体的に説明する。 EXAMPLES Hereinafter, the present invention will be described examples specifically. 実施例1 キチンの粉末を100メッシュに粉砕し、1M-塩酸にて4℃ The powder of Example 1 chitin was ground to 100 mesh, 4 ° C. at 1M- hydrochloride
で1時間処理した後、3%苛性ソーダ中90℃で3時間加熱処理し、再度キチンの粉末中に含まれるカルシウム分およびタンパク質を除去し、水洗を繰り返し乾燥した。 In After 1 hour, heat-treated for 3 hours at 90 ° C. in a 3% sodium hydroxide to remove the calcium content and protein contained in the powder of chitin again and repeated drying washed with water. 塩化リチウムを8重量%含むジメチルアセトアミド溶液に得られたキチンを0.2重量%の濃度になるように溶解し、30℃における溶液の粘度を測定したところ265mPa・ Dissolving chitin obtained dimethylacetamide solution containing lithium chloride 8 wt% to a concentration of 0.2 wt%, 265 MPa · Measurement of the viscosity of the solution at 30 ° C.
sであった。 It was s. 次に得られたキチンを8重量%の塩化リチウムを含んだジメチルアセトアミド溶液に7重量%となるように溶解し、ドープを得た。 Next, the resulting chitin is dissolved in and adjusted to 7% by weight dimethylacetamide solution containing 8 wt% lithium chloride to obtain a dope. 得られたドープは、1480 The resulting dope, 1480
メッシュの金網で濾過し放置脱泡後、タンクに入れ加圧下でギヤポンプにて輸送し、口径0.05mmのノズルから80 After standing defoaming was filtered through a wire mesh of, transported by a gear pump in placed under pressure in the tank 80 to the nozzle of diameter 0.05mm
℃の熱水中に押出し凝固した後、10m/minの速度で引取り再度熱水洗浄脱水後、白色ワセリンを主成分とする、 After extrusion coagulated in hot water at ° C., 10 m / min speed take-up again after hot water washing dried in, a main component of white petrolatum,
柔軟剤を付与し十分に乾燥させて0.81dtexのキチン繊維を得ることができた。 Grant softening agent sufficiently dried it was possible to obtain a chitin fiber 0.81Dtex. 上記のごとく得られたフィラメントを5cmの長さにカットした。 Cut filaments obtained as described above to the length of 5 cm.

【0025】上記キチン繊維をローラーカード機(大和機工株式会社製、SC-360)でキチン繊維の綿状物を作成しニードルパンチ(大和機工株式会社製、NL-380)により交絡、固定しコットン不織布(ユニチカ社製、コットエースR )と積層化した後巻き取った。 [0025] The chitin fiber a roller card machine (Daiwa Kiko Co., Ltd., SC-360) to create a cotton-like material of chitin fibers with a needle punch (Daiwa Kiko Co., Ltd., NL-380) by confounding, fixed cotton nonwoven (manufactured by Unitika Ltd., cot Ace R) wound up after the lamination. このときのキチン綿状物の目付けは90g/m 2 、コットン不織布の目付けは Basis weight 90 g / m 2 of chitin cotton-like materials of this time, the weight of the cotton nonwoven fabric
30g/m 2であった。 It was 30g / m 2. 得られた不織布支持体付キチン綿の性能を下記の表1に示す。 The resulting performance of chitin cotton with non-woven fabric support are shown in Table 1 below. 強力はJIS L 1912(医療用不織布試験方法)に従い測定した。 Strong was measured in accordance with JIS L 1912 (medical nonwoven test method).

【0026】 [0026]

【表1】 [Table 1]

【0027】比較例1 一方、キチン繊維をローラーカード機にかけ、ニードルパンチにより固定してキチン繊維のみからなるキチン綿状物を得た。 [0027] Comparative Example 1 On the other hand, over the chitin fiber to the roller carding machine to obtain a chitin cotton-like material consisting only of chitin fibers were fixed by needle punching. このときのキチン綿状物の目付量は90g/cm Weight per unit area of ​​chitin cotton-like material at this time is 90g / cm
2であった。 It was 2. 得られたキチン綿の性能を表1に示す。 The resulting performance of the chitin cotton are shown in Table 1.

【0028】試験例1 皮膚移植における採皮創10例に対し実施例1および比較例1の創傷被覆材を用い患者に了解の上ハーフサイドテストを施行し比較検討行った。 [0028] Been examined in Test Example 1 underwent a half side test on the understanding to the patient using the wound dressings of Examples 1 and Comparative Example 1 to Tokawa wounds 10 patients in skin transplantation comparison. すなわち創傷面である採皮創の半分を実施例1の創傷被覆材で覆い、残り半分を比較例1の創傷被覆材を貼付しそれらの上から2次ドレッシングとしてガーゼをあて包帯にて固定した。 That half of Tokawa wound a wound surface covered with the wound dressing of Example 1, and fixed with the other half is stuck to the wound dressing of Comparative Example 1 and applying a gauze as a secondary dressing over their bandages . 2次ドレッシングは毎日交換した。 Secondary dressing was changed every day. 簡便性、止血効果、鎮痛効果、表皮形成、乾燥度、密着度に関しての結果を表2に示す。 Simplicity, hemostatic effect, analgesic effect, skin formation, indicating dryness, the results regarding the degree of adhesion in Table 2.

【0029】 [0029]

【表2】 [Table 2]

【0030】採皮創における創傷治癒の程度には、実施例1と比較例1の創傷被覆材に関して明確な差は認められなかったが、実施例1の創傷被覆材は創面に対して密着性が良く、創の治癒迄の保護能が高かった。 [0030] The extent of wound healing in TokawaSo, but a clear difference with respect to the wound dressing of Comparative Example 1 and Example 1 was not observed, the wound dressing of Example 1 adhesion to the wound well, it was higher protection capacity of up healing of wounds. また、実施例1の創傷被覆材はコットン不織布支持体によりガーゼ等の2次ドレッシングとの固着が少なく包帯交換が容易であった。 Further, the wound dressing of Example 1 sticking less dressing changes the secondary dressing gauze was facilitated by cotton nonwoven support.

【0031】試験例2 臀部の分層採皮創に対し実施例1の創傷被覆材を用い、 [0031] The wound dressing of Example 1 using relative Test Example 2 buttocks min layer Tokawa wounds,
それぞれズレ、ヨレ、脱落を防止するために縫合固定を行った。 Each shift was performed twist, a suture secured to prevent falling off. それらの上から2次ドレッシングとしてガーゼをあて、包帯にて固定した。 It addressed gauze over them as a secondary dressing, and fixed with bandage. 2次ドレッシグは毎日交換した。 Secondary Doresshigu was changed every day. 同様な分創採皮創に対して比較例1の創傷被覆材を貼付し縫合固定を行った。 It was affixed to the suture fixing the wound dressing of Comparative Example 1 for a similar partial wound Tokawa wounds. 比較例1の創傷被覆材は縫合固定の際にちぎれることがあったが、実施例1の創傷被覆材では縫合固定はそのようなことはなく皮膚への固定化が容易であった。 Wound dressing of Comparative Example 1 but was sometimes torn during suture fixation, the wound dressing of Example 1 was easy suture fixation immobilization to the skin rather than that. 密着性、疼痛軽減作用などは何れも殆ど同等であり、ともに浸出液の吸収がよかった。 Adhesion, such as pain-relieving effect is almost equivalent to both, was good both absorption of exudate. 貼付後5日目頃から比較例1の創傷被覆材はその一部がガーゼに固着するようになり創面から剥がれたり、ちぎれたりした。 Wound dressing of Comparative Example 1 from about 5 days after application is peeled off from the wound surface become partially stick to the gauze and torn. これにより、患者が苦痛を訴えることがあった。 As a result, there has been that the patient is complaining of pain. 一方、実施例1の創傷被覆剤の縫合固定部は術後14 Meanwhile, the suture fixation of the wound dressing of Example 1 after surgery 14
日後もしっかりした強度を保っており、ズレ、ヨレ、脱落等もなく患者の苦痛は抑えられていた。 The day after and even maintains a firm strength, shift, twist, pain of patients without falling off, etc. was suppressed.

【0032】 [0032]

【発明の効果】本発明のよれば、キチン又はキトサン綿状物の長所である弾力性、密着性、浸出液の吸収除去能、肉芽生成能、表皮形成能などの性質を失うことなく、物理的強度が飛躍的に向上し、創面貼付時の縫合固定も容易にできる。 According the present invention, advantages and is resilient chitin or chitosan cotton-like material, adhesion, absorption capability of removing exudate, granulation formation potential, without losing the properties such as skin formation ability, physical strength is dramatically improved, even suture fixation at the wound surface patch can be easily. また、ズレ、ヨレ、脱落による疼痛の軽減や治癒の遅延がなくなり更にガーゼ交換時の固着も抑えられ患者の苦痛も軽減される。 In addition, shift, twist, pain of the patient is also suppressed secured at the time of delay is no further gauze exchange of alleviation and healing of pain due to fall off is also reduced. さらに支持体は天然繊維不織布であるので、医療廃棄物として処理するとき環境への負荷も少なく、また合成繊維不織布のような残留モノマー等の溶出の心配も解消される。 Furthermore, since the support is a natural fiber nonwoven fabric, less impact on the environment when processing as medical waste, also concerns the elution of residual monomers and the like are also eliminated, such as synthetic fiber nonwoven fabric. また、製造工程においても強度向上によりロール様巻取りが可能となり生産効率が向上し良質な創傷被覆材を得ることができる。 Further, improved production efficiency becomes possible roll-like winding it by the strength improvement in the manufacturing process can be obtained a high-quality wound dressing.

Claims (1)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 キチン又はキトサンの繊維又はフィブリルを開繊して得られる綿状集合体からなるキチン又はキトサン綿状物と、天然繊維からなる不織布とが積層された創傷被覆材であって、キチン又はキトサン綿状物と天然繊維からなる不織布との目付量比率(キチン又はキトサン綿状物:天然繊維不織布)が1:2〜10:1であることを特徴とする創傷被覆材。 1. A chitin or chitosan flocculent comprising fibers or fibrils of chitin or chitosan from flocculent aggregates obtained by spreading, a wound dressing and a nonwoven fabric made of natural fibers are stacked, basis weight ratio (chitin or chitosan flocculent: natural fiber nonwoven fabric) and nonwoven fabric made of chitin or chitosan flocculent and natural fibers 1: 2 to 10: a wound dressing which is a 1.
JP2001017061A 2001-01-25 2001-01-25 Wound covering material Pending JP2002219143A (en)