JP2002105874A - Polyolefin floor material - Google Patents

Polyolefin floor material

Info

Publication number
JP2002105874A
JP2002105874A JP2000303238A JP2000303238A JP2002105874A JP 2002105874 A JP2002105874 A JP 2002105874A JP 2000303238 A JP2000303238 A JP 2000303238A JP 2000303238 A JP2000303238 A JP 2000303238A JP 2002105874 A JP2002105874 A JP 2002105874A
Authority
JP
Japan
Prior art keywords
layer
olefin
surface
olefinic
flooring
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2000303238A
Other languages
Japanese (ja)
Inventor
Takashi Ikeda
Shigemiki Kato
Takanori Matsuzawa
Hiromasa Togasaki
茂幹 加藤
浩昌 戸賀崎
孝教 松沢
尚 池田
Original Assignee
Toppan Printing Co Ltd
凸版印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toppan Printing Co Ltd, 凸版印刷株式会社 filed Critical Toppan Printing Co Ltd
Priority to JP2000303238A priority Critical patent/JP2002105874A/en
Publication of JP2002105874A publication Critical patent/JP2002105874A/en
Application status is Pending legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a polyolefin floor material which is used with the same manner conventional wood floor materials and has good durability against dry cracks, discoloration, warpage, gap forming and the like, and can massively be produced at a low cost keeping qualities on design and physical properties. SOLUTION: This olefinic floor material characterized by laminating a surface-decorating sheet 2 comprising an olefinic raw material and having a thickness of 50 to 500 μm to a substrate 1 comprising an olefinic raw material and having a thickness of 1 to 50 mm. The olefinic floor material, wherein the substrate 1 preferably comprises two or more layers, and the lowest layer among the layers is a foamed layer 11 having a foaming magnification of 1.5 to 20 times. The olefinic floor material, wherein at least one inorganic filler- charged layer 12 containing 10 to 50 wt.% of inorganic particles having an average particle diameter of 3 to 10 μm is disposed in the layer excluding the lowest layer 11. The olefinic floor material, wherein a protecting layer comprising an ionizing radiation-curable resin and having a thickness of 3 to 10 μm is desirably disposed on the surface of the surface-decorating sheet 2.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、オレフィン系素材からなる床材に関する。 The present invention relates to relates to flooring consisting of an olefin-based material. さらに詳しくは、マンション等の集合住宅または戸建て住宅等において、居室や寝室、 More particularly, in the apartment or single-family housing such as condominiums, a living room or bedroom,
廊下、厨房、浴室脱衣場や手洗所等の床面に使用される住宅用フロア全般に好適な、従来の木質系フローリング材の代替品としてのオレフィン系床材に関するものである。 Hallway, kitchen, suitable for residential floors in general used in the floor, such as a bathroom dressing room and restroom, it relates to olefin flooring as an alternative to conventional wood flooring.

【0002】 [0002]

【従来の技術】従来より住宅用に使用されている床材としては様々なものがあるが、特に現在、住宅用のフロア材として主に使用されている床材としては、木質系床材、クッションフロア、タイルカーペットなどが、その中心的なものである。 2. Description of the Related Art As flooring material used for conventionally houses there are various, but particularly now, as the flooring that has been mainly used as a floor material for residential, wood flooring, vinyl flooring, such as carpet tiles is what the central.

【0003】木質系床材は、現在では最も多く使用されているものであり、天然木の無垢材や、合板の表面に突板を貼り合わせたものなどである。 [0003] The wood-based flooring, are those which are most often used in the current, and of natural wood solid wood, and the like formed by bonding the veneer on the surface of the plywood. これらは、天然の木の質感を活かした高級感には優れたものがあるが、その反面、天然木を使用したものであるがゆえに、長く使用していると干割れが発生したり、紫外線等の作用による変色や褪色が発生したり、乾燥又は湿潤により寸法が変化し反りや目透きが発生するなど、耐久性に問題がある。 They are, but there is one excellent in the feeling of luxury that take advantage of the texture of natural wood, on the other hand, therefore it is obtained by using the natural wood, Hiware has occurred or to be used long, ultraviolet rays discoloration or fading or generated by the action of an equal, by dry or wet, such as size changes and the warp and eyes Translucent occurs, there is a problem in durability. また、意匠面でも、これまで殆どオーク材が使用されてきたが、消費者の嗜好の多様化により、床材に求められる木目意匠のバリエーションが拡がってきているために、例えば樺材や楢材などといった、安定供給が困難な材料の使用量が多くなりつつあり、これに伴って、色違いやムラなどの品質問題が増加しつつある。 Further, even in the design surface, it has been mostly oak used heretofore, the diversification of consumer preferences, to variations in grain design required for the flooring has been spread, for example, birch or oak wood such as, is becoming much amount of stable supply is difficult material, along with this, quality problems such as color differences or irregularities are increasing.

【0004】クッションフロアは、ポリ塩化ビニル系素材を絵柄と同調するように発泡させたもので、その優れたクッション性と共にデザイン性の高い床材である。 [0004] cushion floor, which was foamed allowed to tune the picture a polyvinyl chloride material, a high flooring-designed with its excellent cushioning property. しかし、床材の表面を発泡させているために、実際に床材として使用する場合に、箪笥や机、ベッド等の脚部において高荷重がかかった際に、凹凸の後残りが発生してしまうという問題がある。 However, since the foamed surface of the flooring, actually when used as flooring, chest or desk, when the applied high load in the leg portion such as bed rest after the unevenness is generated there is a problem that put away. また近年では、燃焼時に塩化水素ガスやダイオキシン類等の有害物質を発生することが問題となっており、ポリ塩化ビニル系素材自体が敬遠される傾向にある。 In recent years, it has become that the problem of generating harmful substances such as hydrogen chloride gas or dioxin when burned, tend to polyvinyl chloride materials themselves is avoided.

【0005】タイルカーペットは、基布にポリエステル繊維等のパイル糸を植毛したタフテッドカーペット等のカーペット地を合成樹脂等で裏打ちし、50cm角程度の寸法に裁断した置敷式の床材であり、施工が容易で柔軟性や防音性にも優れることからOAフロア等を中心に使用されるケースが増えている。 [0005] tile carpet, lined the carpeting of tufted carpet or the like planting a pile yarns such as polyester fiber to the base fabric of a synthetic resin or the like, is a 置敷 flooring of which was cut to the size of about 50cm square, construction is an increasing number of cases to be used mainly in OA floor or the like because it is excellent in ease and flexibility and sound insulation. しかし一般住宅用としては、繊維系素材であることからコーヒーやカレー等の家庭汚染物質による汚れが拭き取りづらいという問題などがある。 But as for general housing, there is such a problem that the dirt is hard to wipe off by household pollutants such as coffee and curry from it is a fiber-based material.

【0006】このほか、店舗や事務所用としては、厚さ2〜5mm程度の硬質ポリ塩化ビニル樹脂板からなる塩ビ床タイルなどもあるが、これは専ら土足用であり、素足で生活する一般家庭用の床材としては、その硬く冷たい感触が嫌われ、殆ど使用実績がない。 [0006] Generally In addition, as for shops and offices, there is also such as PVC floor tile having a thickness of 2~5mm about hard polyvinyl chloride resin plate, which is exclusively for shoes, to live in bare feet the flooring for the home, the hard cold feel hated, there is almost no actual use. この様な事情により、従来の木質系床材と同一感覚で使用可能であり、 By such circumstances, it may be used in a conventional wood-based flooring and the same sense,
しかも木質系床材の持つ問題点が解決された、木質系床材に代わる新規な床材の開発が待望されている。 Moreover problems of wood flooring has been resolved, it has been desired the development of new flooring alternative to wood flooring.

【0007】 [0007]

【発明が解決しようとする課題】本発明は、従来の技術における上記の様な問題点を解決するためになされたものであり、その課題とするところは、従来の木質系床材と同一の感覚で使用可能でありながら、干割れや変褪色、反り、目透き等に強く耐久性に優れ、しかも、意匠的にも物性的にも一定した品質のものを安価に大量供給可能な床材を提供することにある。 [SUMMARY OF THE INVENTION The present invention has been made in order to solve the above such problems in the prior art points, and has as its object, the same as the conventional wooden flooring yet available in the sense, Hiware and discoloration, warping, excellent strong durability in the eyes show-like, moreover, a design specific to enabling low-cost large supply those of constant quality both in the physical properties of floor coverings It is to provide a.

【0008】 [0008]

【課題を解決するための手段】本発明は、厚さ1〜50 Means for Solving the Problems The present invention is 1 to 50 thickness
mmのオレフィン系素材からなる基材上に、厚さ50〜 On a substrate made of mm olefinic material, 50 to a thickness of
500μmのオレフィン系素材からなる表面装飾用シートを積層してなることを特徴とするオレフィン系床材である。 That formed by laminating a surface decorative sheet consisting of 500μm olefinic material is an olefin-based flooring material, characterized in.

【0009】また本発明は、前記基材は2層以上からなり、その最下層は、発泡したオレフィン系素材からなる発泡層であることを特徴とするオレフィン系床材である。 [0009] The present invention, the base material is composed of two or more layers, the bottom layer is an olefinic flooring which is a foamed layer made of foamed olefinic material.

【0010】また本発明は、前記発泡層の発泡倍率が1.5〜20倍であることを特徴とするオレフィン系床材である。 [0010] The present invention is an olefinic flooring, wherein the expansion ratio of the foam layer is 1.5 to 20 times.

【0011】また本発明は、前記基材は2層以上からなり、その最下層を除く層に、無機物粒子を含有するオレフィン系素材からなる無機物充填層を、少なくとも1層含むことを特徴とするオレフィン系床材である。 [0011] The present invention, the base material is composed of two or more layers, the layers except the lowermost layer, the inorganic filler layer made of olefin-based materials containing inorganic particles, characterized in that it comprises at least one layer olefin-based flooring material.

【0012】また本発明は、前記無機物充填層に含有される無機物粒子の平均粒径が3〜10μmであることを特徴とするオレフィン系床材である。 [0012] The present invention has an average particle diameter of the inorganic particles contained in the inorganic filler layer is an olefin-based flooring material, which is a 3 to 10 [mu] m.

【0013】また本発明は、前記無機物充填層中の前記無機物粒子の含有量が10〜50重量%であることを特徴とするオレフィン系床材である。 [0013] The present invention is an olefinic flooring, wherein the content of the inorganic particles of the inorganic filler layer is 10 to 50 wt%.

【0014】また本発明は、前記表面装飾用シートは、 [0014] Further, the present invention, the surface decorative sheet,
表面に電離放射線硬化型樹脂からなる表面保護層を有することを特徴とするオレフィン系床材である。 Olefin-based flooring material, characterized in that it comprises a surface protective layer made of an ionizing radiation curable resin on the surface.

【0015】また本発明は、前記電離放射線硬化型樹脂層の厚さが3〜10μmであることを特徴とするオレフィン系床材である。 [0015] The present invention is an olefinic flooring, wherein the thickness of the ionizing radiation-curable resin layer is 3 to 10 [mu] m.

【0016】 [0016]

【発明の実施の形態】本発明のオレフィン系床材は、図1に示す様に、オレフィン系素材からなる基材1の上に、オレフィン系素材からなる表面装飾用シート2が積層されて構成される。 Olefin flooring DETAILED DESCRIPTION OF THE INVENTION The present invention is, as shown in FIG. 1, on a substrate 1 consisting of an olefin based material, the surface decorative sheet 2 made of an olefin-based material is stackup It is. 基材1の厚さは1〜50mm、より好ましくは3〜20mm、表面装飾用シート2の厚さは50〜500μm、より好ましくは100〜200μ The thickness of the substrate 1 is 1 to 50 mm, more preferably 3 to 20 mm, the thickness of the surface decorative sheet 2 is 50 to 500 [mu] m, more preferably 100~200μ
mとするのが適当である。 It is appropriate to m. 基材1と表面装飾用シート2 The substrate 1 and the surface of the decorative sheet 2
とは、接着剤層を介することなく直接積層されていても良いし、必要に応じて図2に示す様に、接着剤層3を介して積層した構成とすることもできる。 And it may be be laminated directly without interposing an adhesive layer, as shown in FIG. 2 as necessary, may be formed by the lamination through an adhesive layer 3.

【0017】本発明のオレフィン系床材の基材1や表面装飾用シート2に使用されるオレフィン系樹脂は、ポリエチレン、ポリプロピレン、ポリブテン、ポリ−4−メチルペンテン、ポリイソプレン、エチレン−プロピレン共重合体、エチレン−α−オレフィン共重合体、プロピレン−α−オレフィン共重合体、エチレン−酢酸ビニル共重合体、エチレン−エチルアクリレート共重合体及びその酸変性物、エチレン−不飽和カルボン酸共重合体金属中和物(アイオノマー樹脂)等の各種のオレフィン系樹脂の中から適宜選択が可能であり、単一種の樹脂であっても複数種の樹脂の混合物であっても良い。 The olefin olefin resin used in the substrate 1 or the surface decorative sheet 2 of the floor material of the present invention include polyethylene, polypropylene, polybutene, poly-4-methylpentene, polyisoprene, ethylene - propylene copolymerization coalescence, ethylene -α- olefin copolymer, propylene -α- olefin copolymer, ethylene - vinyl acetate copolymer, ethylene - ethyl acrylate copolymer and its acid modified products, ethylene - unsaturated carboxylic acid copolymer metal-neutralized product is capable of appropriately selected from various olefin resins (ionomer resin) or the like, may be a mixture of single type of a plurality of types of resin be a resin. また必要に応じて、例えば着色剤、充填材、紫外線吸収剤、光安定剤、熱安定剤、可塑剤、酸化防止剤、帯電防止剤、滑剤、造核剤、難燃剤、抗菌剤、防黴剤、艶調整剤等の添加剤の1種以上を添加することもできる。 If necessary, such as colorants, fillers, UV absorbers, light stabilizers, heat stabilizers, plasticizers, antioxidants, antistatic agents, lubricants, nucleating agents, flame retardants, antibacterial agents, antifungal agents, may be added one or more additives, such as gloss control agents.

【0018】但し、床材として要求される耐荷重性や耐歩行性、耐摩耗性、耐傷付性、耐衝撃性、耐熱性(直射日光、暖房器具、熱湯、煙草火等)、寸法安定性(反り・目透き防止)等を考慮すると、各種のオレフィン系樹脂の中でも、ポリプロピレン又はプロピレン−α−オレフィン共重合体等のポリプロピレン系樹脂を使用することが最も望ましい。 [0018] However, load bearing and 耐歩 line resistance required as flooring, abrasion resistance, scratch resistance, impact resistance, heat resistance (direct sunlight, heaters, hot water, cigarette fire, etc.), dimensional stability considering the (warping-eye Translucent prevention), etc., among various olefin resins, it is most desirable to use a polypropylene-based resin such as polypropylene or propylene -α- olefin copolymer. 該ポリプロピレン系樹脂として具体的には、ホモポリプロピレン、ランダム共重合ポリプロピレン、ブロック共重合ポリプロピレンや、プロピレン以外のα−オレフィン、具体的には例えばブテン−1、 Specific examples the polypropylene resin, homopolypropylene, random copolymerization polypropylene, and block copolymers of polypropylene, other than propylene α- olefin, specifically, for example butene-1,
ペンテン−1、ヘキセン−1、オクテン−1等、を10 Pentene-1, hexene-1, octene-1, etc., 10
〜60モル%程度共重合させてなるプロピレン−α−オレフィン共重合体等を挙げることができ、これらを単独又は2種以上の混合系で使用することができる。 60 mol% of copolymerized allowed can be exemplified propylene -α- olefin copolymer comprising, and these can be used alone or as a mixture of two or more systems. また、 Also,
必要に応じて、例えば低密度ポリエチレン、アタクチックポリプロピレン、エチレン−プロピレン共重合ゴム、 If necessary, for example, low density polyethylene, atactic polypropylene, ethylene - propylene copolymer rubber,
エチレン−ジエンモノマー共重合ゴム、スチレン−ブタジエン共重合ゴム又はその水素添加物等から選ばれる軟質オレフィン系樹脂やエラストマー等を5〜30重量% Ethylene - diene monomer copolymer rubber, styrene - butadiene copolymer rubber or soft olefin resin or elastomer such as selected from a hydrogenated product thereof, etc. 5 to 30 wt%
程度配合することによって、上記したポリプロピレン系樹脂に適度の柔軟性や耐衝撃性を付与した樹脂組成物等を使用することもできる。 By degree blended, it is also possible to use the resin composition or the like impart moderate flexibility and impact resistance to polypropylene resin described above.

【0019】基材1は単一層から構成されていても良いが、同一又は相異なるオレフィン系素材からなる2層以上が積層されて構成されていても良い。 The substrate 1 may be composed of a single layer, but two or more layers may be formed by stacking of the same or different olefinic material. 例えば、図1に示す様に、基材1を2層から構成し、その最下層を発泡層11とすることにより、コンクリートスラブ等の床下地面の不陸を吸収して床面を平坦に仕上げることを可能とすると共に、防音性や断熱性を付与したり、歩行感や耐衝撃性の向上のためのクッション性を付与したりすることもできる。 For example, as shown in FIG. 1, and constituting the substrate 1 from the second layer, by the lowermost and the foamed layer 11, finish flat on the floor to absorb the uneven surface of the floor ground such as concrete slabs together makes it possible, to attach the sound insulation and thermal insulation properties, it is also possible to grant or cushioning for improving walking sensation and impact resistance.

【0020】上記発泡層11は、オレフィン系樹脂に例えばアゾジカルボンアミド等の発泡剤を添加して熱により発泡させて形成することができ、発泡倍率としては低すぎると上記した発泡層としての機能が十分に発現されず、高すぎると強度に劣るので、1.5〜20倍程度の範囲内とすることが望ましい。 [0020] The foam layer 11, with the addition of foaming agent such as an olefin resin, for example, azodicarbonamide is foamed by heat can be formed, functions as a too low foam layer described above as a foaming ratio it is not sufficiently expressed, since poor too high strength, it is preferably in the range of about 1.5 to 20 times. また、発泡層11に用いるオレフィン系樹脂としては、耐熱性や耐荷重性等の点で、ポリプロピレン系樹脂を使用することが最も望ましい。 As the olefin resin used in the foam layer 11, in terms such as heat resistance and load resistance, it is most desirable to use a polypropylene resin. ポリプロピレン系樹脂は高発泡させても荷重によるへたりが少なく、上記した発泡層としての機能を高荷重下でも長期間に亘り維持できると共に、耐熱性にも優れ、クリープ変形が発生しにくいので、経時的に位置ずれにより目透きを発生することもないからである。 Polypropylene resin has less sag due to the load also be high foaming, the function of the foam layer described above with can be maintained even over a long period of time under a high load, excellent heat resistance, because creep deformation hardly occurs, This is because not generated eye Translucent by over time position shift. ポリプロピレン系樹脂を発泡時に破泡させることなく安定的に高発泡体を得るためには、高溶融張力のポリプロピレン系樹脂を使用することが望ましい。 To obtain a stable high foam without foam breaking the polypropylene resin at the time of foaming, it is preferable to use a polypropylene resin having a high melt tension.

【0021】上記高溶融張力のポリプロピレン系樹脂として具体的には、フローテスター法にて230℃で測定した溶融張力が3〜30cN程度の範囲内であるポリプロピレン系樹脂が適しており、更に望ましくは、上記溶融張力MTと135℃テトラリン中での固有粘度ηとの関係が下式 log(MT)>4.24×log(η)−0.962 で表され、及び/又は、上記溶融張力MTと230℃におけるメルトフローレートMFRとの関係が下式 log(MT)>−1.16×log(η)+0.92 で表されるポリプロピレン系樹脂を採用することが最も望ましい。 [0021] Examples of the polypropylene-based resin of the high melt tension, melt tension measured at 230 ° C. at a flow tester method is suitable polypropylene resin is in the range of about 3~30CN, and more preferably , the relationship between the intrinsic viscosity eta of the above melt tension MT and 135 ° C. in tetralin is represented by the following formula log (MT)> 4.24 × log (η) -0.962, and / or, the melt tension MT When the melt flow rate MFR underlying relationship between the expression log at 230 ℃ (MT)> - 1.16 × log (η) it is most desirable to employ a polypropylene resin represented by Tasu0.92.

【0022】発泡層11の上側には、床材としての機械的強度や表面物性等を担保するための、非発泡のオレフィン系素材からなる層が設けられるのであるが、この非発泡の層は、無機物粒子を含有するオレフィン系素材からなる無機物充填層12を、少なくとも1層含んでいることが望ましい。 [0022] upper side of the foam layer 11, for guaranteeing the mechanical strength and surface properties as a floor material or the like, but the layer consisting of a non-foamed olefinic material is the provided, the layer of the non-foaming the inorganic filler layer 12 made of olefin-based materials containing inorganic particles, it is desirable to contain at least one layer. 無機物粒子を含有させることによって、表面硬度や剛性、寸法安定性、耐熱性等が更に向上し、重量物の載置後の跡残りや、経時による反り・目透き等を更に効果的に防止することができるからである。 By containing inorganic particles, surface hardness and rigidity, dimensional stability, improved heat resistance and the like are further and marks remaining after loading of heavy, more effectively prevent warpage-eye Translucent due time it is because it is.
また、オレフィン系樹脂より材料単価の易い無機物粒子を配合することで、樹脂の使用量を減じ、安価に製造できる利点もある。 In addition, by blending the easy inorganic particles from an olefin resin of the material unit price, reducing the amount of resin used, there is an advantage that can be inexpensively manufactured.

【0023】上記無機物粒子としては、従来よりオレフィン系樹脂等の熱可塑性樹脂への添加用の充填材として使用されているものなどが使用可能であり、具体的には、例えばシリカ、アルミナ、炭化珪素、炭酸カルシウム、硫酸バリウム、水酸化アルミニウム、水酸化マグネシウム、酸化チタン、酸化亜鉛、クレー、タルク、カオリン、ゼオライト、珪藻土等の従来公知の各種の無機物粒子の中から1種若しくは2種以上を適宜選択して使用すれば良い。 [0023] As the inorganic particles, such as those used as conventionally filler for addition to thermoplastic resins such as olefin resins can be used, specifically, for example, silica, alumina, carbide silicon, calcium carbonate, barium sulfate, aluminum hydroxide, magnesium hydroxide, titanium oxide, zinc oxide, clay, talc, kaolin, zeolite, one or more from among various known inorganic particles diatomaceous earth appropriately selected and may be used. 特にタルク等の様に鱗片状の無機物粒子を選択すると、成形時に無機物粒子が面内方向に配向し、 In particular, when selecting the scaly inorganic particles as such as talc, inorganic particles are oriented in the plane direction at the time of molding,
面内方向の機械的強度や寸法安定性の向上に寄与すると共に、表面側から裏面側への水分等の浸透に対し遮蔽層として機能することから、耐水性や耐湿性も向上する利点がある。 Together contributes to the improvement of mechanical strength and dimensional stability in the in-plane direction, since the function as a shielding layer against penetration of moisture or the like on the back side from the front side, the advantage of improved water resistance and moisture resistance .

【0024】上記無機物粒子の粒径は、小さ過ぎると諸物性の向上の効果に乏しく、逆に大き過ぎると樹脂組成物の成形性を悪化させたり表面粗れや表面粉落ちの原因となったりするので、平均粒径が3〜10μm程度のものを使用することが望ましい。 The particle size of the inorganic particles have poor effects of too small various physical properties improve, or become too large in the opposite cause surface hail or surface-falling or worsen the moldability of the resin composition since, the average particle size may be desirable to use of about 3 to 10 [mu] m. また、無機物粒子の配合量は、少な過ぎると上記した効果がなく、逆に多過ぎても脆くなって機械的強度や耐久性が低下するので、概ね10〜50重量%の範囲内とすることが望ましい。 The amount of inorganic particles, no too small and the effect, the mechanical strength and durability becomes brittle even multi only contrary decreases generally be in the range of 10 to 50 wt% It is desirable

【0025】本発明のオレフィン系床材における基材1 The substrate 1 in the olefin flooring material of the present invention
は、発泡層11及び無機物充填層12との2層のみからなるものに限定されるものではなく、発泡層11と無機物充填層12との間、及び/又は、無機物充填層12の上側に、発泡もせず無機物も充填されていないオレフィン系素材からなる層が設けられていても構わない。 Is not intended to be limited to those consisting of only two layers of the foam layer 11 and the inorganic filler layer 12, between the foam layer 11 and the inorganic filler layer 12, and / or the upper side of the inorganic filler layer 12, foam may be also a layer inorganic also comprising an olefin-based material that is not filled without is provided. 但し、基材1の総厚に対して発泡層11や無機物充填層1 However, the foam layer to the total thickness of the substrate 1 11 and inorganic filler layer 1
2が薄過ぎると、上記した種々の効果が十分に発揮されないので、目的の床材に要求される特性に合わせて各層の厚みを適宜設計する必要がある。 When 2 is too thin, the various effects described above are not sufficiently exhibited, it is necessary to appropriately design the thickness of each layer in accordance with the characteristics required for flooring purposes. 一般的には、発泡層11の厚さは0.5〜5mm程度であって基材1の総厚の50%以下とするのが良く、無機物充填層12の厚さは基材1の総厚の20〜90%程度、更に好ましくは4 In general, the thickness of the foam layer 11 may not more than 50% was in the total thickness of the substrate 1 is about 0.5 to 5 mm, the thickness of the inorganic filler layer 12 is the total of the base 1 20% to 90% approximately of the thickness, more preferably 4
0〜80%程度とするのが良い。 Good to be about 0-80%.

【0026】基材1の成形方法は特に問わず、例えば押出成形法、カレンダー成形法、圧縮成形法、射出成形法、型内重合法等、従来公知の任意の樹脂成形方法を適宜適用することができる。 The molding method of the substrate 1 is not particularly limited, for example, extrusion molding, calender molding, compression molding, injection molding, in-mold polymerization method, appropriately applied to any conventionally known resin molding methods can. 基材1を例えば発泡層11と無機物充填層12という様に複数層の積層体から構成する場合には、各層を個別に成形した後に積層する方法(例えば熱ラミネート法、ドライラミネート法、サンドラミネート法等)によっても良いし、既に成形された層の上に他の層を成形すると同時に積層する方法(例えば押出ラミネート法等)や、各層を成形すると同時に積層する方法(例えば共押出法等)によっても良い。 When constituting the substrate 1, for example a stack of foam layer 11 and a plurality of layers as that inorganic filler layer 12, a method (e.g., heat lamination method of laminating each layer after forming separately, a dry lamination method, sand lamination also may by law, etc.), already a method of laminating at the same time as forming the other layers on top of the formed layer (for example, extrusion lamination method), a method of laminating at the same time as forming each layer (e.g., co-extrusion method) it may be by. 基材1 Substrate 1
が3層以上の積層体から構成される場合には、これらから選ばれる複数の手法を組み合わせて積層することも可能である。 There When composed of three or more layers of the laminate, it is possible to laminate a combination of multiple techniques selected from these.

【0027】基材1の側面部には、施工時の便宜のために図3に示す様に、実部13や溝部14等の嵌合のための実加工が施されていてもよい。 [0027] The side surface portions of the substrate 1, as shown in FIG. 3 for convenience during construction, the actual machining may be subjected to the fitting of such real part 13 and the groove 14. 係る実加工は、基材1 Actual machining, the base material 1 according
の成形後に切削加工等により施されても良いが、予め内周が実部13や溝部14の形状に加工された金型から溶融樹脂を押出して成形する異形押出成形法によると、基材1の成形と同時に実加工を施すことができる利点がある。 Of it may be applied by cutting or the like after molding but, according to the profile extrusion molding method for molding the molten resin extruded from the mold inner circumferential previously is processed into the shape of the real part 13 and the groove 14, the substrate 1 it can be advantageously applied molding the actual machining time of.

【0028】基材1上に積層される表面装飾用シート2 [0028] surface decorative sheet 2 is laminated on the base material 1
は、オレフィン系素材からなる厚さ50〜500μm程度のシート状体であれば良く、その詳細構成は問わず、 May be any sheet-like member having a thickness of about 50~500μm consisting olefinic material, its detailed structure is not limited,
例えば従来より化粧板等の表面装飾用として用いられているものなどを使用することができる。 For example it can be used such as those used for the surface decoration of the decorative plate or the like conventionally. 具体的には、オレフィン系素材からなる透明シート21と裏打シート2 Specifically, the transparent sheet 21 and backing sheet 2 made of an olefin-based material
3との間に印刷等による木目等の絵柄層22を挟持した構成のもの(図4)や、裏打シート23を用いずに透明シート21とその裏面に形成された絵柄層22とから構成されるもの(図5)などが代表的なものである。 3 and having a structure which sandwiches a pattern layer 22 of wood grain due printing between (Fig. 4) and is composed of a transparent sheet 21 and is formed on the rear surface a pattern layer 22. without the backing sheet 23 shall (Fig. 5) is what typical like. 必要に応じて、透明シート21の表面に諸物性の向上のための表面保護層24を設けたり、絵柄層22又は裏打シート23の裏面に基材1との熱接着のためのホットメルト樹脂層25を設けたりすることも、任意に行うことができる。 If necessary, or providing a surface protective layer 24 for improving the physical properties on the surface of the transparent sheet 21, a hot-melt resin layer for thermal adhesion to the substrate 1 on the back of the picture layer 22 or backing sheet 23 also may be provided 25, it can be arbitrarily performed.

【0029】透明シート21や裏打シート23に使用されるオレフィン系樹脂の種類に関しては既に述べた通りであるが、特に絵柄層22の表面側に配置される透明シート21としては、床材の表面材として十分な表面硬度、耐傷付き性、耐磨耗性等を具備させるために、アイソタクチックインデックス(沸騰デカン抽出残率)が9 [0029] While with respect to the type of olefin resin used in the transparent sheet 21 and backing sheet 23 is as already mentioned, as a transparent sheet 21 which is particularly arranged on the surface side of the pattern layer 22, the surface of flooring sufficient surface hardness as wood, scratch resistance, in order to include a wear resistance, etc., isotactic index (boiling decane extraction residue ratio) 9
0%以上、より好ましくは95%以上である高結晶性ポリプロピレン樹脂を主成分とするオレフィン系樹脂組成物を使用することが望ましい。 0% or higher, more preferably it is desirable to use an olefin resin composition composed mainly of a high crystalline polypropylene resin is 95% or more. なお、当該オレフィン系樹脂組成物に耐衝撃性の向上や押出成形性の改善等の目的で低密度ポリエチレンや熱可塑性エラストマー等の軟質成分を配合する場合には、上記高結晶性ポリプロピレン樹脂の特性を大幅に減殺することのない様に、前記軟質性分の配合量は15重量%以下、更に望ましくは10 Incidentally, in the case of blending a soft component low density such as polyethylene and thermoplastic elastomer for the purpose of improvement of improvement and extrusion of the impact on the olefin resin composition, the characteristics of the high-crystalline polypropylene resin as not to diminish significantly, the amount of the softness content is 15 wt% or less, more desirably 10
重量%以下とするのがよい。 Preferably set to% by weight or less.

【0030】絵柄層22の絵柄の種類は特に制限されるものではなく、例えば木目柄、石目柄、布目柄、抽象柄等から任意に選択可能である。 The type of the pattern of the pattern layer 22 is not particularly limited, for example grain pattern, pebble pattern, weft pattern can be arbitrarily selected from an abstract pattern or the like. また、基材1に対する隠蔽性が必要とされる場合には、その裏面側に隠蔽ベタ印刷層を併設しても良い。 Also, if the masking property to the substrate 1 is required, it may be features a concealed solid print layer on the back surface side. 絵柄層22は通常、染料又は顔料等の着色剤を合成樹脂等のバインダー中に混合分散してなる印刷インキ又は塗料等を使用して、適宜の印刷方法により印刷形成される。 Picture layer 22 is typically a colorant such as a dye or pigment using synthetic resin or the like of the printing ink or paint binder comprising mixture dispersed like, is printed and formed by an appropriate printing method.

【0031】上記着色剤としては、例えば縮合アゾ系、 [0031] As the coloring agent, for example, condensed azo,
不溶性アゾ系、キナクリドン系、イソインドリノン系、 Insoluble azo, quinacridone, isoindolinone,
アンスラキノン系、イミダゾロン系、フタロシアニン系等の有機顔料や、カーボンブラック、コバルトブルー、 Anthraquinone, imidazolone, and organic phthalocyanine pigments such as carbon black, cobalt blue,
酸化チタン、酸化鉄等の無機顔料、酸化チタン被覆雲母等のパール顔料等がよく用いられる。 Titanium oxide, inorganic pigments such as iron oxide, pearl pigments such as titanium oxide-coated mica is often used. また、上記バインダーとしては、例えば硝化綿等のセルロース誘導体、塩化ビニル−酢酸ビニル共重合体、ポリビニルブチラール等のビニル系樹脂、ポリウレタン系樹脂、アクリル系樹脂、ポリエステル系樹脂等の単独もしくは各変性物の中から適宜選定すればよい。 As the above binder, for example, cellulose derivatives such as nitrocellulose, vinyl chloride - vinyl acetate copolymer, vinyl resins such as polyvinyl butyral, polyurethane resins, acrylic resins, alone or each modified products such as polyester resin it may be suitably selected from among. これらは水性、溶剤系、エマルジョン系のいずれでも問題なく、また1液型でも硬化剤を使用した2液型でも任意に選定可能である。 These aqueous, solvent-based, without either problems of emulsion systems, also be arbitrarily selected in two-using a curing agent in one-. さらに紫外線や電子線等の照射により硬化させる電離放射線硬化型印刷インキを使用することも可能である。 It is also possible to use an ionizing radiation-curable printing inks to further cured by irradiation of ultraviolet rays or electron beams. オレフィン系素材用の印刷インキとして最も一般的なものは、イソシアネート化合物からなる硬化剤で硬化させる2液硬化型ウレタン樹脂系の印刷インキであり、オレフィン系素材に対する接着性に優れている利点がある。 The most common ones as printing ink for olefinic material is a two component curing type urethane resin printing ink curing by the curing agent consisting of an isocyanate compound, there is an advantage to have excellent adhesion to olefinic materials .

【0032】絵柄層22の印刷方法としては例えばグラビア印刷法、オフセット印刷法、グラビアオフセット印刷法、ドライオフセット印刷法、スクリーン印刷法、フレキソ印刷法、凸版印刷法、インクジェット印刷法、静電印刷法、転写印刷法等の従来公知の適宜の印刷方法を用いることができる。 [0032] For example gravure printing method as a printing method of the picture layer 22, an offset printing method, gravure offset printing method, a dry offset printing method, a screen printing method, flexo printing method, relief printing method, inkjet printing, electrostatic printing method , it may be a conventionally known appropriate printing methods such as transfer printing. また隠蔽ベタ印刷層等のようなベタ層を併用する場合には、例えばグラビアコート法、マイクログラビアコート法、ロールコート法、ナイフコート法、エアーナイフコート法、キスコート法、ロッドコート法、ダイコート法、リップコート法、コンマコート法、フローコート法、ディップコート法等の塗工方法を用いることもできる。 Also in case of using a solid layer such as concealing solid print layer, for example a gravure coating method, micro gravure coating method, roll coating method, knife coating method, an air knife coating method, kiss coating method, a rod coating method, a die coating method can lip coating method, comma coating method, flow coating method, it may be used coating methods such as dip coating. 絵柄層22の印刷形成前に必要に応じて、その被印刷面に例えばコロナ放電処理、プラズマ処理、オゾン処理、火炎処理、酸処理、アルカリ処理、プライマー又はアンカー処理等の表面処理を施して、印刷インキとの接着性を向上させることもできる。 If necessary before printing the formation of the pattern layer 22, the printing surface, for example, corona discharge treatment, plasma treatment, ozone treatment, flame treatment, acid treatment, alkali treatment, subjected to a surface treatment such as a primer or anchor treatment, it is also possible to improve the adhesion to the printing ink.

【0033】絵柄層22を透明シート21と裏打シート23との層間に設ける場合には、絵柄層22は透明シート21の裏面に印刷形成しても裏打シート23の表面に印刷形成してもよい。 [0033] When the pattern layer 22 is provided between the layers of the transparent sheet 21 and backing sheet 23, the pattern layer 22 may be formed by printing on the surface of the backing sheet 23 be formed by printing on the back surface of the transparent sheet 21 . 透明シート21と裏打シート23 Transparent sheet 21 and the backing sheet 23
との積層方法も特に限定されるものではなく、例えば接着剤を介したドライラミネート法又はウェットラミネート法、接着剤を介した又は介さない熱ラミネート法、サンドラミネート法、押出ラミネート法等、従来公知の任意の積層方法から透明シート21や裏打シート23の材質に合わせた方法を適宜選択すれば良い。 Heat lamination method lamination method is also not particularly limited, for example, a dry lamination method or a wet laminating method through the adhesive, no or intervention through the adhesive and, sand lamination method, extrusion lamination method, conventionally known method tailored to the material of any transparent from lamination method sheet 21 and backing sheet 23 may be appropriately selected.

【0034】表面保護層24は、床材の表面として歩行や重量物の運搬等に耐える硬質で強靱な材質から構成することが望ましく、一般的には硬化型樹脂を主成分とする組成物が採用される。 The surface protective layer 24 is desirably constructed from a tough material hard to withstand transportation like walking and heavy as the surface of the flooring, compositions based on curable resins are generally It is adopted. 例えばウレタン系樹脂、アルキド系樹脂、メラミン系樹脂、エポキシ系樹脂、不飽和ポリエステル系樹脂、フェノール系樹脂、ユリア系樹脂等の熱硬化型樹脂や、不飽和ポリエステル系樹脂、アクリレート系樹脂又はメタクリレート系樹脂等の電子線又は紫外線等の電離放射線の照射により硬化する電離放射線硬化型樹脂等である。 For example, urethane resins, alkyd resins, melamine resins, epoxy resins, unsaturated polyester resins, and phenolic resins, thermosetting resins such as urea resin, unsaturated polyester resin, acrylate resin or methacrylate a ionizing radiation curable resin that is cured by irradiation of ionizing radiation such as electron beam or ultraviolet rays such as a resin. 特に後者の電離放射線硬化型樹脂は表面硬度や耐磨耗性、耐傷付き性等の各種表面物性に優れており、本発明の目的には最も適したものである。 Especially the latter ionizing radiation curable resin surface hardness and wear resistance, is excellent in various surface properties of scratch resistance and the like, for the purposes of the present invention is the most suitable.

【0035】表面保護層24には必要に応じて、例えばシリカ、アルミナ、炭化珪素等の高硬度の耐磨耗性粒子を含有させることによって、表面の耐傷付き性を更に向上させることもできる。 [0035] If necessary, the surface protective layer 24, for example, silica, alumina, by the inclusion of high hardness wear resistance particles such as silicon carbide, it is also possible to further improve the scratch resistance of the surface. その他、例えば紫外線吸収剤、 Others, such as UV absorbers,
光安定剤、熱安定剤、酸化防止剤、艶調整剤、滑剤、帯電防止剤、結露防止剤、抗菌剤、防黴剤、着色剤、充填剤等の各種の添加剤を適宜添加することも任意である。 Light stabilizers, heat stabilizers, antioxidants, gloss modifiers, lubricants, antistatic agents, condensation preventing agents, antibacterial agents, antifungal, coloring agent, may be added suitably various additives such as fillers it is optional.
表面保護層24の厚さは、薄過ぎると表面保護の効果がなく、逆に厚過ぎても可撓性の低下や硬化時の残留応力等によって亀裂や剥離等が発生し易くなるので、一般的には1〜50μm程度の範囲であり、中でも3〜10μ The thickness of the surface protective layer 24 has no effect of the surface protective too thin, a crack or peeling is likely to occur due to residual stress at the time of reduction and curing of flexibility it is too thick conversely, etc., generally thereof include a range of about 1 to 50 [mu] m, inter alia 3~10μ
m程度とすることが最も望ましい。 It is most desirable to about m.

【0036】ホットメルト樹脂層25は、基材1と表面装飾用シート2とを熱ラミネート法等により加熱下で積層する場合に、予め表面装飾用シート2の裏面に設けておくことが推奨されるものである。 The hot-melt resin layer 25, when the substrate 1 and the surface decorative sheet 2 is laminated under heating by a heat lamination method, is recommended to keep provided on the back surface of the pre-surface decorative sheet 2 is shall. これに使用されるホットメルト樹脂としては、例えば変性又は未変性ポリオレフィン系樹脂、塩素化ポリオレフィン系樹脂、エチレン−酢酸ビニル共重合体系樹脂、塩化ビニル−酢酸ビニル共重合体系樹脂、アクリル系樹脂、ポリウレタン系樹脂、ポリアミド系樹脂、ポリエステル系樹脂等の80〜 The hot-melt resin to be used for such products, for example modified or unmodified polyolefin resin, chlorinated polyolefin resins, ethylene - vinyl acetate copolymer resin, vinyl chloride - vinyl acetate copolymer resin, acrylic resin, polyurethane system resin, polyamide resin, 80, such as polyester resin
150℃程度で溶融する熱可塑性樹脂を使用することができる。 It can be used a thermoplastic resin which melts at about 0.99 ° C.. 中でも、例えばカルボキシル基、アミノ基、グリシジル基又はエステル基等の極性官能基を側鎖又は末端に有する、変性ポリオレフィン系樹脂やエチレン−酢酸ビニル共重合体系樹脂、アクリル系樹脂などからなるホットメルト樹脂が、オレフィン系素材からなる基材1 Among them, for example a carboxyl group, an amino group, having a polar functional group such as a glycidyl group or an ester group in the side chain or terminal, modified polyolefin resins, ethylene - vinyl acetate copolymer resin, a hot melt resin comprising an acrylic resin but the substrate 1 made of olefin-based materials
との熱接着性の面で優れている。 It is excellent in thermal adhesion surfaces of the.

【0037】その他、特に図示しないが、表面装飾用シート2の表面には、エンボスによる凹凸模様を施したり、該凹凸模様の凹部をワイピング法又はバレープリント法等により着色したり、透明シート21又は表面保護層24の表面とは艶状態の異なる印刷インキの1種又は2種以上を使用して艶変化のある模様を形成するなどの、従来公知の任意の表面装飾加工の1種以上を施すこともできる。 [0037] Other, although not specifically shown, the surface of the surface decorative sheet 2, or subjected to a rugged pattern by embossing, or colored by wiping method or valley printing method or the like recess of the concave convex pattern, the transparent sheet 21 or the surface of the surface protective layer 24 by using one or more kinds of different printing inks gloss conditions such as to form a pattern shiny change, applying one or more conventionally known any surface decoration processing it is also possible.

【0038】本発明のオレフィン系床材において、基材1と表面装飾用シート2との積層方法は特に制限されるものではなく、例えば、接着剤層3を介したドライラミネート法又はウェットラミネート法、接着剤層3を介するか又は介さない熱ラミネート法、基材1用の樹脂組成物を加熱溶融して押出すと同時に溶融状態ないし高温軟化状態の基材1の表面にその熱接着力を利用して表面装飾用シート2を積層する押出成形同時ラミネート法、予め内面に表面装飾用シート2を設置した射出成形用金型に加熱溶融した基材1用の樹脂組成物を射出して基材1 [0038] In olefin flooring of the present invention, a method of laminating the substrate 1 and the surface decorative sheet 2 is not particularly limited, for example, a dry lamination method or a wet laminating method through the adhesive layer 3 , heat lamination method or without intervention via the adhesive layer 3, the heat adhesion of the resin composition heated and melted by extruding the same time molten state to hot substrate 1 of the surface of the softened state of the base material 1 extrusion simultaneous lamination method for laminating the surface decorative sheet 2 by utilizing and injecting a heated resin composition of the molten base material 1 in the injection mold was installed surface decorative sheet 2 beforehand the inner surface based on wood 1
を成形すると同時に表面装飾用シート2を積層する射出成形同時ラミネート法、加熱軟化した表面装飾用シート2を真空成形法により基材1の表面に沿って成形しつつ積層する真空成形ラミネート法等、従来公知の任意の積層方法から任意に選択して実施することができる。 Simultaneous injection molding lamination method of laminating the surface decorative sheet 2 and at the same time forming a vacuum forming lamination method of the heat softened surface decorative sheet 2 is laminated with molded along the surface of the substrate 1 by a vacuum molding method, may be carried out arbitrarily selected from any conventionally known lamination method.

【0039】 [0039]

【実施例】以下に本発明の具体的な実施例を示し本発明をより詳細に説明する。 EXAMPLES shows a specific embodiment of the present invention will be described the present invention in more detail.

【0040】実施例1 図3に示す断面形状の2層構成から成り総厚6mmのオレフィン系素材からなる床材用の基材を押出成形法により作製した。 [0040] was prepared by extrusion molding a substrate for flooring consisting of olefin-based material having a total thickness of 6mm a two-layer structure of a cross-sectional shape shown in Embodiment 1 FIG. その際の材料としては、上層である無機物充填層については、ホモポリプロピレン樹脂に平均粒径3〜5μの鱗片状タルクを30重量%添加したものを使用し、下層である発泡層については、溶融張力20cN As the material of the case, for inorganic filler layer is the upper layer, using that scale-like talc having an average particle diameter 3~5μ the homopolypropylene resin was added 30 wt%, the foamed layer is the lower layer, the molten tension 20cN
の高溶融張力ポリプロピレン樹脂にアゾジカルボンアミド系熱分解型化学発泡剤を3重量%添加したものを使用し、両者を加熱溶融共押出成形すると同時に後者を発泡させ、発泡層の発泡倍率は10倍、発泡後の厚みは2m High melt tension polypropylene resin azodicarbonamide thermal decomposition type chemical foaming agent using a 3 have been added wt%, upon heating melt coextrusion both by foaming the latter simultaneously, the expansion ratio of the foamed layer is 10 times , the thickness of the post-foaming 2m
m、無機物充填層の厚みは4mmとした。 m, the thickness of the inorganic filler layer was 4 mm.

【0041】一方、厚さ70μmの隠蔽性白色ポリプロピレン系樹脂シート上に、2液硬化型ウレタン樹脂系印刷インキを使用してグラビア印刷法により、淡いベージュ色のメープル柄からなる絵柄を印刷し、該印刷面に2 On the other hand, the thickness 70μm of hiding white polypropylene resin sheet by a gravure printing method using a two-component curable urethane resin printing ink, and printing a pattern consisting of light-beige Maple Pattern, 2 to the printing surface
液硬化型ウレタン系接着剤を介して、前記白色ポリプロピレン系樹脂シートと同系のポリプロピレン系樹脂からなる厚さ70μmのクリアーシートを貼り合わせ、更に該クリアーシートの表面にコロナ放電処理を施した後、 Via the liquid curable urethane adhesive, the bonding a clear sheet of white polypropylene-based resin sheet and the thickness of 70μm consisting of syngeneic polypropylene resin, it was subjected to corona discharge treatment further surface of said clear sheet,
平均粒径5μmのアルミナ粒子を10重量%添加した(メタ)アクリレート系紫外線硬化型樹脂を、硬化後の厚みが10μmになるように塗工したのちに紫外線照射により硬化させて表面保護層を形成して、図4に示す構成のオレフィン系素材からなる表面装飾用シートを作製した。 Forming a surface protective layer by curing the addition of alumina particles having an average particle diameter of 5 [mu] m 10 wt% of (meth) acrylate ultraviolet curable resin by ultraviolet irradiation after the thickness after curing was applied so as to 10μm There was fabricated a surface decorative sheet consisting of an olefin-based material having the configuration shown in FIG.

【0042】上記の基材の表面にコロナ放電処理を施した後、溶剤型ウレタン系接着剤を用いて上記の表面装飾用シートを貼り合わせて、本発明のオレフィン系床材を作製した。 [0042] was subjected to corona discharge treatment to the surface of the base material, by bonding sheet for surface decoration of the using a solvent type urethane adhesive, to prepare an olefinic flooring material of the present invention.

【0043】実施例2 厚さ120μmの透明ポリプロピレン系樹脂シートの裏面に、前記実施例1におけると同一の要領にて絵柄を印刷し、該印刷面にアクリル系ホットメルト樹脂を厚さ5 [0043] back surface of the transparent polypropylene resin sheet of Example 2 thickness of 120 [mu] m, and printing a pattern in the same manner as in Example 1, an acrylic-based hot melt resin thickness 5 to the printing surface
μmに塗工し、しかる後、前記実施例1におけると同一の要領にて表面保護層を形成して、図5に示す構成のオレフィン系素材からなる表面装飾用シートを作製した。 It was applied to the [mu] m, and thereafter, to form a surface protective layer in the same manner as in Example 1 to prepare the surface decorative sheet consisting of an olefin-based material having a structure shown in FIG.

【0044】前記実施例1におけると同一の要領にて基材を共押出成形すると同時に、その溶融熱を利用して、 [0044] At the same time coextruding a substrate in the same manner as in Example 1, by utilizing the heat of fusion,
基材の表面に上記表面装飾用シートのホットメルト樹脂層面を接着させて、本発明のオレフィン系床材を作製した。 On the surface of the base material to adhere the hot-melt resin layer side of the surface decorative sheet was produced olefinic flooring material of the present invention.

【0045】 [0045]

【発明の効果】本発明のオレフィン系床材は、従来の木質系床材で問題であった、長期間の使用や様々な使用環境によって発生する、無垢材や突板の干割れや退色については、素材をオレフィン系とすることにより解消され、物性や耐久性の水準についても、オレフィン系樹脂の種類の選択や、オレフィン系樹脂に添加する添加剤の選択により、用途による要求品質に応じた自由な材料設計が可能となった。 [Effect of the Invention Olefinic flooring material of the present invention, been a problem with conventional wood-based flooring, caused by long-term use and various use environments, the Hiware and discoloration of solid wood or veneer is , it is eliminated by the material and olefin, for the level of physical properties and durability, the type of selection or olefin resin, by selecting the additives to be added to the olefin resins, free in accordance with the required quality by the application material design, such has become possible.

【0046】また、従来のタイルカーペットで問題であった表面の汚れやすさについても、本発明のオレフィン系床材は表面が樹脂層(オレフィン系樹脂層若しくは硬化型樹脂からなる表面保護層など)であるから、タイルカーペットのような汚れやすさはない。 [0046] As for the stain ease of conventional carpet tile problem occurring surface, olefinic flooring material of the present invention the surface of the resin layer (olefin resin layer or the surface protective layer comprising a cured resin, etc.) since it is not a dirty ease as carpet tiles.

【0047】従来のクッションフロアで問題であった、 [0047] was a problem in the conventional cushion floor,
家具やベッド等の高荷重がかかった際の凹凸の跡残りについても、請求項2で規定する様に、発泡層を最下層とし、上層は非発泡の層とすることで回避できる。 For even uneven marks remaining when the high load is applied, such as furniture or bed, as defined in claim 2, the foam layer and the bottom layer, the top layer can be avoided by a layer of non-foamed. さらに、請求項4で規定する様に、無機物充填層を設けることで、基材の表面硬度を高くかつ寸法安定性にも優れた設計にすることで、クッションフロアのような凹凸の跡残りはほぼ完全に解消できる。 Further, as defined in claim 4, by providing the inorganic filler layer, by the excellent design high and dimensional stability of the surface hardness of the base material, uneven marks remaining like cushion floor almost can be completely eliminated.

【0048】また、請求項2で規定する様に、基材を2 [0048] Further, as defined in claim 2, the substrate 2
層以上から構成し、最下層をオレフィン系樹脂の発泡層とすることで、本発明のオレフィン系床材をコンクリート打設面やコンクリートスラブ板、捨て板等の施工面に敷き詰める際の表面の多少の凹凸は発泡層で吸収できるので、従来の床材の場合のような施工前の下地ならしの手間を大幅に省くことができる。 Constitute the above layers, the lowermost layer by a foam layer of an olefin resin, an olefin-based flooring material of the present invention concrete 設面 or concrete slab plate, the surface when laying the construction surface discard plate like some the unevenness can be absorbed by the foam layer, it is possible to save labor under earthmoving prior construction as in the case of the conventional flooring for significantly. さらに、施工後の経時変化により床材の反りや施工面からの浮きなどが多少発生することがあっても、床材の裏面が発泡層であるので音鳴りも発生しにくい。 Furthermore, even if the like floating from warping or construction surface flooring due to aging after construction is somewhat generated, sounding hardly occurs because the back surface of the floor material is foamed layer.

【0049】係る如く、本発明のオレフィン系床材は、 [0049] As according olefinic flooring material of the present invention,
例えば木質系床材、クッションフロア、タイルカーペット等の、従来の床材が有していた種々の問題を一挙に解決し、施工性、物性、耐久性ともに優れ、一定の品質で安価に大量生産可能であり、しかも全体がオレフィン系素材からなるので廃棄性(焼却処分性、リサイクル性) For example wooden flooring, vinyl flooring, such as carpet tiles, various problems conventional flooring had resolved at once, excellent workability, physical properties, durability both inexpensively mass produced in constant quality possible and, moreover disposal of the whole is made of olefin-based material (incineration disposal of, recyclability)
にも優れるなどの多くの実用上の利点を有するものである。 Also excellent and has a lot of practical advantages, such as.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】本発明のオレフィン系床材の実施の形態を示す模式断面図である。 1 is a schematic sectional view showing an embodiment of an olefin-based flooring material of the present invention.

【図2】本発明のオレフィン系床材の他の実施の形態を示す模式断面図である。 2 is a schematic sectional view showing another embodiment of the olefin flooring material of the present invention.

【図3】本発明のオレフィン系床材の実施の形態に用いられる基材の構造を示す模式断面図である。 3 is a schematic sectional view showing a structure of a substrate used in the embodiment of the olefinic flooring material of the present invention.

【図4】本発明のオレフィン系床材の実施の形態に用いられる表面装飾用シートの構造を示す模式断面図である。 4 is a schematic sectional view showing the surface structure of the decorative sheet used in the embodiment of the olefinic flooring material of the present invention.

【図5】本発明のオレフィン系床材の他の実施の形態に用いられる表面装飾用シートの構造を示す模式断面図である。 5 is a schematic sectional view showing the surface structure of the decorative sheet used in another embodiment of the olefin flooring material of the present invention.

【符号の説明】 DESCRIPTION OF SYMBOLS

1‥‥‥基材 11‥‥発泡層 12‥‥無機物充填層 13‥‥実部 14‥‥溝部 2‥‥‥表面装飾用シート 21‥‥透明シート 22‥‥絵柄層 23‥‥裏打シート 24‥‥表面保護層 25‥‥ホットメルト樹脂層 3‥‥‥接着剤層 1 ‥‥‥ substrate 11 ‥‥ foam layer 12 ‥‥ inorganic filler layer 13 ‥‥ real part 14 ‥‥ groove 2 ‥‥‥ surface decorative sheet 21 ‥‥ transparent sheet 22 ‥‥ pattern layer 23 ‥‥ backing sheet 24 ‥‥ surface protective layer 25 ‥‥ hot-melt resin layer 3 ‥‥‥ adhesive layer

───────────────────────────────────────────────────── フロントページの続き (72)発明者 加藤 茂幹 東京都台東区台東1丁目5番1号 凸版印 刷株式会社内 Fターム(参考) 4F055 AA12 BA19 CA05 DA12 FA05 FA40 GA02 GA18 GA32 HA15 4F100 AK01D AK03A AK03B AK03C BA02 BA03 BA04 BA05 BA07 BA10A BA10B BA10D CA01 CA23A CA23C DJ01B EH20 GB09 HB01 JB14D JL00 JL04 YY00A YY00B YY00C YY00D ────────────────────────────────────────────────── ─── front page of the continuation (72) inventor Kato ShigeruMiki Taito-ku, Tokyo, Taito-1-chome fifth No. 1 Toppan printing Co., Ltd. in the F-term (reference) 4F055 AA12 BA19 CA05 DA12 FA05 FA40 GA02 GA18 GA32 HA15 4F100 AK01D AK03A AK03B AK03C BA02 BA03 BA04 BA05 BA07 BA10A BA10B BA10D CA01 CA23A CA23C DJ01B EH20 GB09 HB01 JB14D JL00 JL04 YY00A YY00B YY00C YY00D

Claims (8)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】厚さ1〜50mmのオレフィン系素材からなる基材上に、厚さ50〜500μmのオレフィン系素材からなる表面装飾用シートを積層してなることを特徴とするオレフィン系床材。 1. A thickness of an olefin based material onto become substrates of 1 to 50 mm, olefinic flooring, characterized in that formed by laminating a surface decorative sheet consisting of an olefin-based material having a thickness of 50~500μm .
  2. 【請求項2】前記基材は2層以上からなり、その最下層は、発泡したオレフィン系素材からなる発泡層であることを特徴とする請求項1に記載のオレフィン系床材。 Wherein said substrate is composed of two or more layers, the bottom layer, olefin based flooring material according to claim 1, characterized in that a foamed layer made of foamed olefinic material.
  3. 【請求項3】前記発泡層の発泡倍率が1.5〜20倍であることを特徴とする請求項2に記載のオレフィン系床材。 3. The olefin flooring material according to claim 2, expansion ratio of the foam layer is characterized in that 1.5 to 20 times.
  4. 【請求項4】前記基材は2層以上からなり、その最下層を除く層に、無機物粒子を含有するオレフィン系素材からなる無機物充填層を、少なくとも1層含むことを特徴とする請求項1〜3のいずれかに記載のオレフィン系床材。 Wherein said substrate is composed of two or more layers, according to claim 1 that the layers except the lowermost layer, the inorganic filler layer made of olefin-based materials containing inorganic particles, characterized in that it comprises at least one layer olefin flooring according to any one of to 3.
  5. 【請求項5】前記無機物充填層に含有される無機物粒子の平均粒径が3〜10μmであることを特徴とする請求項4に記載のオレフィン系床材。 5. The olefin flooring material according to claim 4, the average particle diameter of the inorganic particles contained in the inorganic filler layer is characterized in that it is a 3 to 10 [mu] m.
  6. 【請求項6】前記無機物充填層中の前記無機物粒子の含有量が10〜50重量%であることを特徴とする請求項4又は5に記載のオレフィン系床材。 6. The olefin-based flooring material according to claim 4 or 5 content of the inorganic particles of the inorganic filler layer is characterized in that it is a 10 to 50% by weight.
  7. 【請求項7】前記表面装飾用シートは、表面に電離放射線硬化型樹脂からなる表面保護層を有することを特徴とする請求項1〜6のいずれかに記載のオレフィン系床材。 7. The sheet wherein the surface decoration, olefinic flooring material according to any one of claims 1 to 6, wherein a surface protective layer made of an ionizing radiation curable resin on the surface.
  8. 【請求項8】前記表面保護層の厚さが3〜10μmであることを特徴とする請求項7に記載のオレフィン系床材。 8. olefin flooring material according to claim 7 in which the thickness of the surface protective layer is characterized by a 3 to 10 [mu] m.
JP2000303238A 2000-10-03 2000-10-03 Polyolefin floor material Pending JP2002105874A (en)