JP2002097392A - Anti-counterfeit ink and anti-counterfeit sheet produced by using the ink - Google Patents

Anti-counterfeit ink and anti-counterfeit sheet produced by using the ink

Info

Publication number
JP2002097392A
JP2002097392A JP2000289189A JP2000289189A JP2002097392A JP 2002097392 A JP2002097392 A JP 2002097392A JP 2000289189 A JP2000289189 A JP 2000289189A JP 2000289189 A JP2000289189 A JP 2000289189A JP 2002097392 A JP2002097392 A JP 2002097392A
Authority
JP
Japan
Prior art keywords
anti
counterfeit
ink
liquid crystal
sheet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2000289189A
Other languages
Japanese (ja)
Inventor
Akira Hirasawa
Shingo Naoi
朗 平澤
信吾 直井
Original Assignee
Toppan Forms Co Ltd
トッパン・フォームズ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toppan Forms Co Ltd, トッパン・フォームズ株式会社 filed Critical Toppan Forms Co Ltd
Priority to JP2000289189A priority Critical patent/JP2002097392A/en
Publication of JP2002097392A publication Critical patent/JP2002097392A/en
Application status is Pending legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a new anti-counterfeit sheet having high anti-counterfeit effect on paper money, cash voucher, ticket and coupon ticket having a film or paper as the substrate and difficult to falsify and provide an anti-counterfeit ink for the sheet.
SOLUTION: The anti-counterfeit ink contains a cholesteric liquid crystal compound. The above problem can be solved by the use of an anti-counterfeit sheet having a thin film of cholesteric liquid crystal formed on a substrate by using the anti-counterfeit ink.
COPYRIGHT: (C)2002,JPO

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、偽造防止用インキおよびそれを用いた偽造防止用シートに関するものである。 The present invention relates to relates to anti-counterfeit sheet used for preventing the ink and it counterfeit.

【0002】 [0002]

【従来の技術】従来、フィルムや用紙などを基材とした有価証券など(偽造防止用シート)として、シート基材にホログラムラベルや光輝ラベルなどの偽造が困難なラベルを貼付したものがある。 Conventionally, as such securities such as film or sheet of a base material (anti-counterfeit sheet), the sheet substrate are those forged such as a hologram labels and photoluminescent labels were affixed difficult label. これらは容易に偽造されず、特別な真贋判定装置を必要としない点で優れているが、反面、ホログラムラベルは製造方法が複雑で、高価であり、光輝ラベルも高価であり、したがって製造コストがアップする問題があった。 These are not easily counterfeited, is superior in that it does not require special authenticity determination device, the other hand, the hologram label a complicated manufacturing process, are expensive, bright label is also expensive, therefore the manufacturing cost there has been a problem to be up. 一方、特殊な蛍光インキでマークなどを印刷する方法があり、この方法によれば製造コストのアップや製造工程の煩雑さを伴わず、通常状態ではマークが隠蔽されるために、使用者に意識させないという点で優れているが、この種の特殊な蛍光インキは色調が淡く、判別がし難い場合が起こる可能性があり、加えて、真贋判定にブラックライト照射装置が必要である。 On the other hand, there is a method of printing such as marking a special fluorescent inks, without the complexity of the manufacturing cost of the up and manufacturing processes According to this method, in order to mark is hidden in the normal state, conscious user is superior in that it does not let special fluorescent inks of this kind pale color tone, there is a possibility that if it is difficult to be discriminated occurs, in addition, it is necessary to black light irradiation device authentication judgment. これらの真贋判定の技術は、技術的に確立されてから年月日が経過し、一般に認知され、公知化されるようになると逆に偽造され易くなる可能性が高くなるという問題がある。 These authenticity determination technique is technically elapsed since the established date, generally recognized, there is a problem that can become easy to be forged on the contrary will be known reduction increases.

【0003】 [0003]

【発明が解決しようとする課題】カラーコピー機やパソコン、スキャナ、カラープリンタなどの普及により、金券やチケット、クーポン券などが偽造される機会は増加する一方である。 THE INVENTION Problems to be Solved] color copy machine or a personal computer, a scanner, with the spread, such as a color printer, opportunity to cash vouchers and tickets, such as the coupon is counterfeit, which is one to increase. そこで、本発明の第1の目的は、従来の問題を解決し、フィルムや用紙を基材とする有価証券や金券、チケット、クーポン券などの偽造防止効果が高く、容易に偽造されることがない新規な偽造防止用シートを提供できる偽造防止用インキを提供することであり、本発明の第2の目的は、この偽造防止用インキを用いた新規な偽造防止用シートを提供することである。 Accordingly, a first object of the present invention is to solve the conventional problems, securities and cash vouchers to the film or sheet as a substrate, ticket, high forgery prevention effect such as coupons, to be easily counterfeited it is to provide anti-counterfeit ink can provide no new anti-counterfeit sheet, a second object of the present invention is to provide a novel anti-counterfeit sheet using the anti-counterfeit ink .

【0004】 [0004]

【課題を解決するための手段】本発明者等は前記課題を解決すべく鋭意研究を重ねた結果、コレステリック液晶性化合物を含む偽造防止用インキを用いることにより、 The present inventors have Means for Solving the Problems] As a result of extensive studies to solve the above problem, by using the anti-counterfeit ink comprising a cholesteric liquid crystal compound,
解決できることを見出し、本発明を完成するに至った。 It can be solved, which resulted in the completion of the present invention.

【0005】すなわち、本発明の請求項1記載の偽造防止用インキは、コレステリック液晶性化合物を含むことを特徴とする。 Namely, anti-counterfeit ink according to claim 1 of the present invention is characterized by comprising a cholesteric liquid crystal compound.

【0006】本発明の請求項2記載の偽造防止用シートは、基材に請求項1記載の偽造防止用インキを用いて形成されたコレステリック液晶薄膜を有してなることを特徴とする。 [0006] anti-counterfeit sheet according to claim 2 of the present invention is characterized by comprising a cholesteric liquid crystal film formed by using the anti-counterfeit ink according to claim 1, wherein the substrate.

【0007】 [0007]

【発明の実施の形態】図1は、本発明の偽造防止用シートの一実施形態を説明する説明図である。 Figure 1 DETAILED DESCRIPTION OF THE INVENTION is an explanatory diagram for explaining an embodiment of the anti-counterfeit sheet of the present invention. 図1において、本発明の偽造防止用シート1は、基材の用紙2に透明なポリエステル2軸延伸フィルム3が貼付・積層されており、コレステリック液晶薄膜4(例えば、厚さ約1 In Figure 1, the anti-counterfeit sheet 1 of the present invention is paper 2 to a transparent polyester biaxially oriented film 3 of the substrate is stuck-layered cholesteric liquid crystal film 4 (e.g., thickness of about 1
00μm〜1,000μm程度)が両者にサンドイッチされて積層されて構成されている。 About 00Myuemu~1,000myuemu) is formed by laminating is sandwiched therebetween. すなわち、ポリエステル2軸延伸フィルム3の用紙2に対向する箇所に偽造防止用インキを用いて印刷されて形成されたコレステリック液晶薄膜4が用紙2およびポリエステル2軸延伸フィルム3に接着されて形成されている。 That, is formed a cholesteric liquid crystal film 4 formed by being printed by using the ink for preventing forgery in locations opposing the paper 2 of the polyester biaxially oriented film 3 is bonded to the sheet 2 and a polyester biaxially oriented film 3 there. 7は用紙2に印刷された印刷部である。 7 is a printing unit which is printed on the paper 2. コレステリック液晶薄膜4は、 Cholesteric liquid crystal thin film 4,
見る角度により変化する美しい色の輝きを示し偽造困難なものである。 Is the angle it difficult forge shows beautiful color brilliance of which changes by the viewer.

【0008】図2は、従来の偽造防止用シートの説明図である。 [0008] Figure 2 is an explanatory view of a conventional anti-counterfeit sheet. 図1〜図2において同じ構成部分には同一参照符号を付すことにより、重複した説明を省略する。 Denoted by the same reference numerals to the same components in FIGS. 1-2, and a redundant description is omitted. 従来の偽造防止用シート5は、コレステリック液晶薄膜4の替わりに光輝インキを用いて印刷されて形成された光輝インキ薄膜6が用紙2およびポリエステル2軸延伸フィルム3に接着されて形成されている以外は、図1に示す本発明の偽造防止用シート1と同様になっている。 Conventional anti-counterfeit sheet 5, except that the glitter ink film 6 which is formed by printing using a glitter ink instead of the cholesteric liquid crystal film 4 is formed is bonded to the sheet 2 and a polyester biaxially oriented film 3 It has become the same manner as anti-counterfeit sheet 1 of the present invention shown in FIG. 光輝インキ薄膜6は、見る角度により美しい輝きを示すが、 Glitter ink thin film 6, shows a beautiful glow depending on the angle of viewing,
見る角度により変色することがないため、偽造防止効果は不十分である。 Since no discolor depending on the angle of viewing, anti-counterfeit effect is insufficient.

【0009】本発明で用いるコレステリック液晶性化合物は、コレステリック構造を有するか、温度条件などの条件によりコレステリック構造をとる化合物、あるいはこれらの中から選択される2種以上の混合物である。 [0009] Cholesteric liquid crystal compounds used in the present invention, either having a cholesteric structure, the compound takes a cholesteric structure by conditions such as temperature conditions, or a mixture of two or more selected from these.

【0010】コレステリック相における分子の配列は、 [0010] The arrangement of the molecules in the cholesteric phase,
一つの面内で分子はネマチック液晶のように一定方向に配向しているが、隣接する面内での分子配向軸がねじれを起こしているため、配向方向が面の垂直軸のまわりにらせん構造をとっている。 Although molecules in one plane are oriented in a constant direction as a nematic liquid crystal, the molecular orientation axis of the adjacent plane has caused twisting, spiral around a vertical axis of alignment directions foliation It is taking. この構造をコレステリック構造という。 The structure of the cholesteric structure. コレステリック液晶の薄膜は白色光のもとで選択反射による美しい干渉色を示す。 Thin film of a cholesteric liquid crystal exhibits a beautiful interference color by selective reflection under white light. 反射光の波長は、 Wavelength of the reflected light,
コレステリック液晶性化合物の種類、温度、反射角、入射角により変化する。 Type of cholesteric liquid crystal compound, the temperature, the angle of reflection varies with the angle of incidence.

【0011】代表的なコレステリック液晶性化合物としては、安息香酸コレステリル、塩化コレステリル、オクタン酸コレステリル、ノナン酸コレステリルクロルギ酸コレステリル、炭酸オレイルコレステリル、酢酸コレステリル、エレオステアリン酸コレステリルなどの他、液晶オリゴマー、液晶ポリマーなどを例示することができる。 [0011] Exemplary cholesteric liquid crystal compound, cholesteryl benzoate, cholesteryl chloride, cholesteryl octanoic acid, nonanoic acid cholesteryl chloro formic acid cholesteryl, carbonic oleyl cholesteryl, cholesteryl acetate, other such eleostearic acid cholesteryl, liquid crystal oligomers, it can be exemplified such as a liquid crystal polymer.

【0012】本発明の偽造防止用インキはコレステリック液晶性化合物以外に、ビヒクル、溶剤、水、硬化剤、 [0012] anti-counterfeit inks of the present invention other than the cholesteric liquid crystal compounds, vehicle, solvent, water, a curing agent,
硬化促進剤などを配合して調製されるが、顔料、染料、 Is prepared by blending and curing accelerators, pigments, dyes,
分散剤、安定剤、増粘剤、粘着剤、接着剤その他通常のインキに配合される添加剤を基材への接着・積層を妨げたり、特に偽造防止効果を妨げない範囲で配合することができる。 Dispersants, stabilizers, thickeners, adhesives, or interfere with adhesion-lamination of the adhesive additive formulated into other normal ink to the substrate, be added in amounts in particular does not interfere with the anti-counterfeit effect it can.

【0013】本発明のコレステリック液晶性化合物を含む偽造防止用インキを用いてフィルムや用紙などの基材にコレステック液晶薄膜を形成することにより、ホログラムラベルや光輝ラベルとは全く異なる色彩を得ることができ、この液晶特有の色彩は、コピー機やスキャナでの偽造は不可能であり、高い偽造防止効果を発現することができる。 [0013] By forming the same stick crystal thin film on a substrate such as a film or paper by using the anti-counterfeit ink comprising a cholesteric liquid crystal compound of the present invention, to obtain a completely different color from the hologram labels and photoluminescent labels can be, the liquid crystal of the specific color is forged in copiers and scanners is impossible, it is possible to express a high forgery prevention effect.

【0014】本発明で用いる基材としては、上質紙、アート紙、コート紙、ミラーコート紙、コンデンサー紙、 [0014] As the base material used in the present invention, high-quality paper, art paper, coated paper, mirror coated paper, condenser paper,
パラフィン紙、その他の紙の他に、合成紙、あるいはポリエチレン、透明性を有するポリエチレンテレフタレート、ポリプロピレン、塩化ビニルなどの合成フィルムやシート、銅、アルミニウムなどの金属あるいはこれらを組み合わせた複合体を用いることができる。 Wax paper, in addition to the other paper, synthetic paper, or polyethylene, polyethylene terephthalate having transparency, polypropylene, using synthetic films or sheets such as vinyl chloride, copper, a metal or a complex combination of these such as aluminum can. これらの合成フィルムやシートを用いる場合には基材の表面をマット処理、コロナ処理などの表面処理を施してもよい。 Matted surface of the substrate in the case of using these synthetic film or sheet may be subjected to a surface treatment such as corona treatment.

【0015】本発明の偽造防止用インキは、凸版印刷、 [0015] The anti-counterfeit ink of the present invention, letterpress printing,
グラビア印刷法などの凹版印刷、オフセット方式などの平板印刷、スクリーン印刷およびインクジェット方式その他の通常用いられる印刷方法で基材の面の所定部に塗工してコレステリック液晶薄膜を形成したり、あるいは他の透明性を有する基材に塗工してコレステリック液晶薄膜を形成したものを紙などの基材に積層したりするなどして本発明の偽造防止用シートを作成することができる。 Intaglio printing such as gravure printing, or to form a cholesteric liquid crystal film by applying a lithographic printing such as offset method, a predetermined portion of the surface of the substrate by screen printing and ink-jet method other conventional printing methods used or other, it can be applied to a substrate having transparency to create an anti-counterfeit sheet to the present invention such or stacked one formed a cholesteric liquid crystal film on a substrate such as paper.

【0016】なお、本発明は上記実施形態に限定されるものではないので、特許請求の範囲に記載の趣旨から逸脱しない範囲で各種の変形実施が可能である。 [0016] The present invention is therefore intended in no limited to the above embodiments but may be various modifications within a range without departing from the spirit described in the claims.

【0017】 [0017]

【実施例】以下実施例および比較例により本発明を更に詳しく説明するが、本発明はこれら実施例に何ら制約されるものではない。 By the following examples and comparative examples illustrate the present invention in more detail, but the present invention should not be construed as being in any way constrained to these examples. (実施例1)イオン交換水40質量部にヒドロキシプロピルセルロース(HPC)〈銘柄:ヒドロキシプロピルセルロースSL(日本曹達社製)〉(コレステリック液晶性化合物)60質量部を加え溶解する。 (Example 1) hydroxypropyl cellulose in ion-exchange water 40 parts by mass (HPC) <brand: hydroxypropylcellulose SL (Nippon Soda Co., Ltd.)> is added and dissolved (cholesteric liquid crystal compound) 60 parts by weight. これに、アクリルモノマ〈商品名:ライトアクリレート9EG−A To this, acrylic monomer <product name: Light Acrylate 9EG-A
(共栄社化学社製)〉9.5質量部に光重合開始剤〈商品名:VICURE55(アクゾノーベル社製)〉0. (Kyoeisha Chemical Co., Ltd.)> 9.5 parts by weight of the photo-polymerization initiator <Product name: VICURE55 (Akzo Nobel)> 0.
5質量部を混合した液を加え、混合して本発明のコレステリック液晶性化合物を含む偽造防止用インキを調製した。 5 parts by weight mixed solution was added and mixed to the anti-counterfeit ink comprising a cholesteric liquid crystal compound of the present invention was prepared. このインキを用いて図1に示す本発明の偽造防止用シート1を次のようにして作成する。 The anti-counterfeit sheet 1 of the present invention shown in FIG. 1 with the ink is prepared as follows. すなわち、このインキを厚さ12μmの透明なポリエステル二軸延伸フィルム〈商品名:エンブレットPTM12(ユニチカ社製)〉3に厚み150μmになるように塗工し、この塗工面が用紙2側になるように用紙2と張り合わせた後、 That is, the transparent polyester biaxially oriented film of this ink thickness 12 [mu] m: was coated so that the thickness 150μm to <tradename Emblet PTM12 (manufactured by Unitika Ltd.)> 3, the coated surface is 2 side sheet after bonding with the paper 2 as,
紫外線を照射し硬化・接着・貼付して図1に示す本発明の偽造防止用シート(チケット)1を作成した。 Ultraviolet irradiation and cured, adhesion, sticking a created the anti-counterfeit sheet (ticket) 1 of the present invention shown in FIG. 作成した本発明の偽造防止用シート(チケット)1のコレステリック液晶薄膜4は、見る角度により美しい赤色から緑色に変化するものであり、偽造は困難であった。 Cholesteric liquid crystal film 4 of anti-counterfeit sheet (ticket) 1 of the present invention prepared are those changes to green from the beautiful red depending on the angle of viewing, counterfeiting is difficult.

【0018】(実施例2)実施例1で使用したアクリルモノマを19質量部に、光重合開始剤を1.0質量部に変更した以外は実施例1と同様の操作を行って本発明のコレステリック液晶性化合物を含む偽造防止用インキを調製し、このインキを用いて本発明の偽造防止用シート(チケット)1を作成した。 [0018] 19 parts by weight of acrylic monomers used in (Example 2) Example 1, except for changing the photopolymerization initiator 1.0 part by weight by performing the same operations as in Example 1 of the present invention to prepare anti-counterfeit ink comprising a cholesteric liquid crystal compound, to prepare a anti-counterfeit sheet (ticket) 1 of the present invention using the ink. 作成した本発明の偽造防止用シート(チケット)1のコレステリック液晶薄膜4 Anti-counterfeit sheet of the present invention prepared (ticket) 1 cholesteric liquid crystal film 4
は、見る角度により美しい赤色から緑色に変化するものであり、偽造は困難であった。 Is to turn green from the beautiful red depending on the angle of viewing, counterfeiting is difficult.

【0019】(実施例3)イオン交換水40質量部にヒドロキシプロピルセルロース(HPC)〈銘柄:ヒドロキシプロピルセルロースSL(日本曹達社製)〉(コレステリック液晶性化合物)60質量部を加え溶解させる。 [0019] (Example 3) hydroxypropylcellulose ion-exchanged water 40 parts by mass (HPC) <brand: hydroxypropylcellulose SL (Nippon Soda Co., Ltd.)> is added and dissolved (cholesteric liquid crystal compound) 60 parts by weight. これに水系エポキシ樹脂〈商品名:アデカレジンE This water-based epoxy resin <Product name: Adecaresin E
M−0487(旭電化社製)〉10質量部を混合して本発明のコレステリック液晶性化合物を含む偽造防止用インキを調製した。 M-0487 (manufactured by Asahi Denka Co.)> 10 parts by mass were mixed with the anti-counterfeit ink comprising a cholesteric liquid crystal compound of the present invention was prepared. このインキを用いて図1に示す本発明の偽造防止用シート1を次のようにして作成する。 The anti-counterfeit sheet 1 of the present invention shown in FIG. 1 with the ink is prepared as follows. このインキを厚さ12μmの透明なポリエステル二軸延伸フィルム〈商品名:エンブレットPTM12(ユニチカ社製)〉3に厚み180μmに成るように塗工し、この塗工面が用紙2側になるように用紙2と張り合わせ、接着・貼付して図1に示す本発明の偽造防止用シート(チケット)1を作成した。 Transparent polyester biaxially oriented film of this ink thickness 12 [mu] m <trade name: (manufactured by Unitika) Emblet PTM12> 3 was applied in such a manner that the thickness 180μm, as the coated surface becomes 2 side sheet laminating a sheet 2, creating the anti-counterfeit sheet (ticket) first adhesive-attached to the present invention shown in FIG. 作成した本発明の偽造防止用シート(チケット)1のコレステリック液晶薄膜4は、見る角度により美しい赤色から緑色に変化するものであり、 Cholesteric liquid crystal film 4 of anti-counterfeit sheet (ticket) 1 of the present invention prepared are those changes to green from the beautiful red depending on the angle of viewing,
偽造は困難であった。 Counterfeiting has been difficult.

【0020】(比較例1)UVベースインキ〈商品名: [0020] (Comparative Example 1) UV-based ink <Product name:
シルバーワニス(T&K TOKA社製)〉80質量部に対して、パール顔料〈製品名:Iriondin21 Silver varnish (T & K TOKA Co., Ltd.)> with respect to 80 parts by weight, pearl pigment <Product Name: Iriondin21
1(メルク社製)〉を20質量部添加し、粘度調整剤としてTPGDA(トリプロピレングリコールジアクリレート)を適量加えて、シルク印刷可能な光輝インキを得た。 1 (Merck)> were added 20 parts by weight, added an appropriate amount TPGDA the (tripropylene glycol diacrylate) as a viscosity modifier, to obtain a silk printable brilliant ink. 得られた光輝インキを使用して実施例1と同様にして図2に示すデザインの比較のための偽造防止用シート(チケット)5を作成した。 Obtained using the bright ink in the same manner as in Example 1 was prepared the anti-counterfeit sheet (ticket) 5 for comparison the design shown in FIG. 得られた比較のための偽造防止用シート(チケット)5の光輝インキ薄膜6は見る角度により強く赤色に輝いて見えた。 Glittering ink film 6 of anti-counterfeit sheet (ticket) 5 for comparison obtained are shines red strongly depending on the angle of viewing. しかしながら赤色以外には変色はなく、偽造防止効果としては不十分であった。 However no discoloration in addition red, was insufficient as a forgery prevention effect.

【0021】(比較例2)比較例1のパール顔料を製品名Iriondin299(メルク社製)に変えた以外は、比較例1と同様の操作によって図2に示すデザインの比較のための偽造防止用シート(チケット)5を作成した。 [0021] (Comparative Example 2) except for changing the pearl pigment of Comparative Example 1 product name Iriondin299 (Merck), for preventing forgery for the comparison of the design shown in FIG. 2 by the same procedure as Comparative Example 1 We have created a 5 seat (ticket). 得られた比較のための偽造防止用シート(チケット)5の光輝インキ薄膜6は見る角度により強く緑色に輝いて見えた。 Glittering ink film 6 of anti-counterfeit sheet (ticket) 5 for comparison obtained are shines green strongly depending on the angle of viewing. しかしながら緑色以外には変色はなく、 However no discoloration in addition green,
偽造防止効果としては不十分であった。 It was insufficient as a forgery prevention effect.

【0022】 [0022]

【発明の効果】本発明の請求項1記載の偽造防止用インキは、コレステリック液晶性化合物を含むインキであるので、従来の諸問題を解決することができ、フィルムや用紙を基材とする有価証券や金券、チケット、クーポン券などの偽造防止効果が高く、容易に偽造されることがない新規な偽造防止用シートを経済的にかつ容易に提供できるという顕著な効果を奏する。 Anti-counterfeit ink according to the first aspect of the present invention exhibits, because it is an ink containing cholesteric liquid crystal compound, it is possible to solve the conventional problems, valuable for the film or sheet as the base material securities and cash vouchers, tickets, high forgery prevention effect such as coupons, easily achieves the remarkable effect that forged is that the novel anti-counterfeit sheet is not economically and easily can be provided.

【0023】本発明の請求項2記載の偽造防止用シートは、本発明の偽造防止用インキを用いて形成されたコレステリック液晶薄膜を有してなるので、安価である上、 The anti-counterfeit sheet according to claim 2 of the present invention, since a cholesteric liquid crystal film formed by using the anti-counterfeit ink of the present invention, besides being inexpensive,
偽造防止効果が高く、容易に偽造されることがないという顕著な効果を奏する。 Forgery preventing effect is high, readily achieves the remarkable effect that is it is not counterfeit.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】本発明の偽造防止用シートの一実施形態を説明する説明図である。 1 is an explanatory diagram for explaining an embodiment of the anti-counterfeit sheet of the present invention.

【図2】従来の偽造防止用シートの説明図である。 FIG. 2 is an explanatory view of a conventional anti-counterfeit sheet.

【符号の説明】 DESCRIPTION OF SYMBOLS

1 本発明の偽造防止用シート 2 基材の用紙 3 ポリエステル2軸延伸フィルム 4 コレステリック液晶薄膜 5 従来の偽造防止用シート 6 光輝インキ薄膜 7 印刷部 One sheet 3 polyester biaxially oriented film 4 cholesteric liquid crystal film 5 conventional anti-counterfeit sheet 6 glittering ink film 7 Printing unit of anti-counterfeit sheet 2 substrate of the invention

───────────────────────────────────────────────────── フロントページの続き Fターム(参考) 2C005 HA01 HB10 HB13 JB09 JB11 JB40 KA03 KA40 2H113 AA03 BA01 BA03 BA05 BA10 BB08 BC05 BC09 CA37 CA39 DA43 DA53 DA57 4J039 BE01 FA01 FA02 GA01 GA02 GA03 GA10 GA24 ────────────────────────────────────────────────── ─── front page of continued F-term (reference) 2C005 HA01 HB10 HB13 JB09 JB11 JB40 KA03 KA40 2H113 AA03 BA01 BA03 BA05 BA10 BB08 BC05 BC09 CA37 CA39 DA43 DA53 DA57 4J039 BE01 FA01 FA02 GA01 GA02 GA03 GA10 GA24

Claims (2)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 コレステリック液晶性化合物を含むことを特徴とする偽造防止用インキ。 1. A forgery preventing ink which comprises a cholesteric liquid crystal compound.
  2. 【請求項2】 基材に請求項1記載の偽造防止用インキを用いて形成されたコレステリック液晶薄膜を有してなる偽造防止用シート。 Wherein the anti-counterfeit sheet comprising a cholesteric liquid crystal film formed by using the anti-counterfeit ink according to claim 1, wherein the substrate.
JP2000289189A 2000-09-22 2000-09-22 Anti-counterfeit ink and anti-counterfeit sheet produced by using the ink Pending JP2002097392A (en)