JP2002079563A - Stretch-resistant wire for extrusion molding and manufacturing method therefor - Google Patents

Stretch-resistant wire for extrusion molding and manufacturing method therefor

Info

Publication number
JP2002079563A
JP2002079563A JP2000267490A JP2000267490A JP2002079563A JP 2002079563 A JP2002079563 A JP 2002079563A JP 2000267490 A JP2000267490 A JP 2000267490A JP 2000267490 A JP2000267490 A JP 2000267490A JP 2002079563 A JP2002079563 A JP 2002079563A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
wire
metal plating
extrusion
plating layer
steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2000267490A
Other languages
Japanese (ja)
Inventor
Seinosuke Mizuno
精之助 水野
Original Assignee
Nippon Purai Kk
日本プライ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To provide a stretch-resistant wire for an extrusion molding which has such advantages that a degreasing treatment before molding is not required and the binding strength is high without the application of an adhesive and further, the high adhesion can be retained in the molding for a long time as well as a manufacturing method therefor. SOLUTION: This wire W for preventing the extrusion molding M from stretching is embedded in one piece with the molding M as a core. The entirety of the wire 11 made of steel is covered with a metal plated layer 12 and an irregular part 15 is nicked on both surface side 10A and back side 10B of the wire 11.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】この発明は押出成形品のための伸縮防止用平線及びその製法に関する。 BACKGROUND OF THE INVENTION for this invention stretch preventing spur lines and their preparation for extrusion.

【0002】 [0002]

【従来の技術】例えば図6に示すような自動車の車体に取り付けられる紐状のモール材Mは合成樹脂やゴム等の高分子材料の押出成形によって製造される。 String-shaped molding material M to be attached to a vehicle body of an automobile as shown in FIG. 6 for example is manufactured by extrusion of a polymeric material such as synthetic resin or rubber. これらの押出成形品よりなる長尺のモール材にあっては温度変化によって製品の長さ方向の伸縮が生ずることがあるので、 Since In the mall material long made from these extrusions may stretch in the length direction of the product caused by the temperature change,
その伸縮を防止するために、従来から芯材として鋼材製平線Wを該成形品の内部に一体に埋設することが行われている。 In order to prevent the stretching, a steel-made flat wire W into the interior of the molded article to be buried together being carried out as a core material conventionally.

【0003】このような鋼材製平線を芯材としてモール材に一体に埋設するには、押出工程ラインの押出成形機内で該芯材をモール材の溶融材料内にインサートしこれらを一体に押出成形するのであるが、溶融材料との結合強度を高めるために、芯材となる鋼材製平線に接着剤を塗着して一体押出をしている。 [0003] Thus buried integrally in a molding material steel steel flat wire as the core material, extruded integrally insert to them into the extruder in the molten material of the core material the molding material extrusion process line although to mold, in order to enhance the bond strength of the molten material, and the integrally extruded by Nurigi adhesive to steel-made flat wire serving as a core. しかるに、この種鋼材製平線は防蝕のために油処理が施されており、この油類は接着剤の塗布や密着性を阻害するので、接着剤塗布に先立ってまずその脱脂処理を行い、その後接着剤を塗布し、さらにこの接着剤を加熱等により焼き付けした後に一体成形を行っている。 However, this type steel-made flat wire oil treatment has been applied for corrosion protection, since the oils inhibit coating and adhesion of adhesives, performs first its degreasing treatment prior to the adhesive application, Thereafter the adhesive is applied, it is carried out integral molding after baked by further heating or the like adhesive.

【0004】このように、伸縮防止用の鋼材製平線Wをモール材Mに一体に埋設するには、押出成形工程のライン内で、成形前に線材の脱脂処理をし、その後接着剤を塗布し、さらにこの接着剤の焼き付けを行うなど特別な工程を経なければならず、煩雑な工程管理が必要であった。 [0004] Thus, the buried integrally in a steel-made flat wire W for stretching preventing molding material M, in the line of the extrusion process, the degreasing process wire prior to molding, followed adhesive coated, must go through a special process such as further performing baking of the adhesive, it was required complicated process control.

【0005】 [0005]

【発明が解決しようとする課題】そこで、この発明は、 The present invention To solve the above problems, the present invention,
このような状況に鑑み、成形前の脱脂処理が不要で、かつ接着剤を塗着しなくても高い結合強度を備え、しかも成形品内において高い密着性を長期に亘って保持することができる押出成形品のための伸縮防止用平線を提案するものである。 In view of this situation, degreasing treatment prior to molding is not required, and an adhesive having high bonding strength without Nurigi, yet can be held for a long time with high adhesion in the molded article It proposes a telescopic prevention spur lines for extrusion. また、この発明は、該伸縮防止用平線を効率良く簡単かつ確実に製造する方法を提案するものである。 Further, the present invention is to propose a method for producing the stretch preventing spur line efficiently easily and reliably.

【0006】 [0006]

【課題を解決するための手段】すなわち、請求項1の発明は、押出成形品の芯材として一体に埋設され該押出成形品の伸縮を防止する平線であって、鋼材製平線の全体が金属メッキ層によって覆われているとともに、表面側および裏面側の両面に凹凸部が刻設されていることを特徴とする押出成形品のための伸縮防止用平線に係る。 Means for Solving the Problems That is, the invention of claim 1, a flat wire to prevent the expansion and contraction of the buried the extrusion molded article integrally as a core material for extrusion, the entire steel-made flat wire There together are covered with metal plating layer, uneven portions on both sides of the front and back surface side according to the expansion and contraction prevention spur lines for extrusion, characterized in that it is engraved.

【0007】また、請求項2の発明は、請求項1において、前記凹凸部が四角錘形状の凹陥部を均一に配置したものよりなり、該凹陥部の対角線の長さが0.5mm、 Further, the invention of claim 2, in claim 1, consists that the uneven portion is uniformly arranging recess of square pyramid-shaped, the length of the diagonal of the recessed portion is 0.5 mm,
窪み深さが0.11mm、各凹陥部の間隔が0.25m Recess depth 0.11 mm, interval between the concave portions is 0.25m
mである押出成形品のための伸縮防止用平線に係る。 According to expansion and contraction prevention spur lines for extrusion is m.

【0008】請求項3の発明は、前記伸縮防止用平線を製造する方法に関し、断面円形の鋼材製丸線に金属メッキを施して全体が金属メッキ層によって覆われた鋼材製丸線を得る工程と、前記丸線を圧延ロール間に挿通圧延して全体に金属メッキ層を有する平線を得る工程と、次いで前記平線を凹凸部を有するロール間に挿通して全体に金属メッキ層を有しかつその表面側および裏面側の両面に凹凸部が刻設された所定厚みおよび幅の平線を得る工程とからなることを特徴とする。 [0008] The invention of claim 3 relates to a method of producing the stretch preventing spur line, the whole is subjected to metal plating on a circular section of the steel material made of round wire to obtain a steel material made of round wire covered by a metal plating layer a step, a step of obtaining a flat wire having a metal plating layer on the entire inserted through rolling the round wire to rolling rolls and then a metal plating layer on the entire inserted through between the rolls having an uneven portion of the flat wire a and wherein the uneven portion on both sides of the surface side and the back side and a step of obtaining a flat line engraved and predetermined thickness and width.

【0009】さらに、請求項4の発明も、同様に、前記伸縮防止用平線を製造する方法に関し、断面円形の鋼材製丸線に金属メッキを施して全体が金属メッキ層によって覆われた鋼材製丸線を得る工程と、前記丸線を凹凸部を有する圧延ロール間に挿通圧延して全体に金属メッキ層を有しかつその表面側および裏面側の両面に凹凸部が刻設された所定厚みおよび幅の平線を得る工程とからなることを特徴とする。 Furthermore, also the invention of claim 4, likewise relates to a method of producing the stretch preventing spur line, the whole is subjected to metal plating on a circular section of the steel material made of round wire is covered with a metal plating layer steel obtaining a manufacturing round wire, given the uneven portions on both sides of the insertion rolled whole has a metal plating layer and the surface side and the back side is engraved on rolling rolls having an uneven portion of the round wire characterized in that comprising the step of obtaining a flat wire thickness and width.

【0010】 [0010]

【発明の実施の形態】以下添付の図面に従って、この発明の実施例について説明する。 According DETAILED DESCRIPTION OF THE INVENTION accompanying drawings, a description will be given of an embodiment of the present invention. 図1はこの発明に係る伸縮防止用平線の一実施例を示す部分斜視図、図2は図1 Figure 1 is a partial perspective view showing an embodiment of a stretchable anti-flat wire according to the present invention, Figure 2 is Figure 1
の部分拡大平面図、図3は図2の3−3線で切断した断面図、図4は請求項3の発明の伸縮防止用平線を製造する方法の一実施例を表す概略工程図、図5は請求項4の発明の伸縮防止用平線を製造する方法の実施例を表す概略工程図である。 Partially enlarged plan view of FIG. 3 is a sectional view taken along line 3-3 in FIG. 2, FIG. 4 is a schematic process chart showing an embodiment of a method for producing a stretch-preventing flat wire of the invention of claim 3, Figure 5 is a schematic process diagram showing an embodiment of a method for producing a stretch-preventing flat wire of the invention of claim 4.

【0011】図1に示した伸縮防止用平線10は、前記したモール材Mのような押出成形品の芯材として一体に埋設され該押出成形品の伸縮を防止する平線である。 [0011] stretching prevention flat wire 10 shown in FIG. 1 is a flat wire to prevent the expansion and contraction of the molded product out pressing embedded together as a core material of the extrusion molded articles such as the above-mentioned molding material M. そして、この平線10は、鋼材製平線11の全体が金属メッキ層12によって覆われているとともに、表面側10 Then, the flat wire 10, together with the whole of the steel-made flat wire 11 is covered with the metal plating layer 12, the surface side 10
Aおよび裏面側10Bの両面に凹凸部15が刻設されている。 Uneven portion 15 is engraved on both sides of A and the back side 10B.

【0012】鋼材製平線11はこの種芯材として一般に使用されている例えばスチール材よりなる。 [0012] consisting of steel-made flat wire 11 such as steel materials are commonly used as this type core. 金属メッキ層12は、前記鋼材製平線11の腐食を防ぐためのもので、該鋼材製平線11に対してメッキ加工が可能なものであれば何でもよいが、柔軟性及び経済性の点から、亜鉛メッキ、黄銅メッキ等が好ましく用いられる。 Metal plating layer 12, the used to prevent corrosion of the steel-made flat wire 11, but may be any ones capable of plating against steel material made flat wire 11, the point of flexibility and economy from galvanized, brass plating and the like are preferably used.

【0013】そして、この発明の平線10には、その表面側10Aおよび裏面側10Bの両面に、凹凸部15が刻設されている。 [0013] Then, the flat wire 10 of the present invention, on both sides of the surface side 10A and the back side 10B, uneven portions 15 are engraved. この凹凸部15は、例えば、請求項2 The uneven portion 15 is, for example, claim 2
の発明として規定し図2及び図3に図示したように、逆四角錘形状(逆ピラミッド型)の凹陥部16を均一に配置したものよりなる。 Invention, as illustrated in and FIGS. 2 and 3 defined as the consists that uniformly arranging the recess 16 of the opposite square pyramid shape (inverted pyramid). この凹陥部16は、対角線の長さaが0.5mm、窪み深さbが0.11mm、各凹陥部の間隔cが0.25mmである。 The recess 16 has a diagonal length a is 0.5 mm, the depression depth b is 0.11 mm, the interval c of the recess is 0.25 mm. なお、この例における平線10の厚みは0.55mmで、幅は2.00mmである。 The thickness of the flat wire 10 in this example is 0.55 mm, a width of 2.00 mm. このような凹陥部16よりなる凹凸部15は、後述するロールによるいわゆるインデント加工によって形成することができる。 Such recess 16 irregular portion 15 made of, can be formed by a so-called indentation processed by the roll, which will be described later.

【0014】凹凸部15は、平線10が押出成形品内に芯材として一体に埋設されたときに、該成形品と結合してアンカー効果を生じ、該押出成形品の伸縮を防止するものである。 [0014] uneven portion 15, which Tairasen 10 when implanted together as a core material in the extrusion, resulting an anchoring effect in combination with the molded article, to prevent the expansion and contraction of the extrusion molded article it is. 従って、このようなアンカー結合効果を生ずる凹凸部であればどのような形状でもよい。 Therefore, it may be any shape as long as uneven portion caused such anchoring effect. なお、前記したモール材のような成形品にあっては、凹凸部の窪み深さが0.11mm以上であれば、所期のアンカー結合効果を有する。 Incidentally, in the molded article, such as the above-mentioned molding material, the depression depth of the uneven portion is not less than 0.11 mm, having a desired anchoring effect.

【0015】次に、この伸縮防止用平線10を製造する方法についてさらに説明する。 Next, further description will be given of a method of manufacturing the stretchable prevention flat wire 10. 請求項3の発明として規定した製法は、図4に図示したように、鋼材製丸線20 Production method was defined as the invention of claim 3, as shown in FIG. 4, the steel-made round wire 20
に金属メッキを施す工程と、前記金属メッキ層21に覆われた鋼材製丸線22を圧延ロール30間に挿通圧延して全体に金属メッキ層12を有する平線11を得る工程と、前記平線11を凹凸部41を有するロール40間に挿通する工程ととからなる。 A step of obtaining a step of applying a metal plating, a flat wire 11 having a metal plating layer 12 on the entire inserted through rolling between the rolling a metal plating layer 21 steel steel round wire 22 covered with the roll 30 in the flat comprising the step Toto inserting the line 11 between the roll 40 having the uneven portion 41.

【0016】図4に図示のように、断面円形の鋼材製丸線20に対して、公知の手法により金属メッキを施して、全体が金属メッキ層21によって覆われた鋼材製丸線22を得る。 [0016] As shown in FIG. 4, with respect to a circular cross section of the steel material made of round wire 20, is subjected to metal plating by a known method, the whole to obtain a steel material made of round wire 22 covered by the metal plating layer 21 . 実施例では、鋼材製丸線20としてJI In an embodiment, JI as steel manufactured round wire 20
S G 3505(軟鋼線材)のSWRM6K材を用いて、これを冷間伸線し、これに亜鉛メッキを施して、全体が亜鉛メッキ層21によって覆われた鋼材製丸線22 Using SWRM6K material S G 3505 (mild steel wire rod), which was cold drawing, to which is subjected to galvanizing, the entire steel material made of round wire covered by a zinc plating layer 21 22
を得た。 It was obtained.

【0017】次に、前記金属メッキ層21に覆われた鋼材製丸線22を、図のように、上下の圧延ロール30, Next, the steel-made round wire 22 covered with the metal plating layer 21, as shown, the upper and lower rolling rolls 30,
30間に挿通して圧延し、全体が金属メッキ層12を有する鋼材製平線11を得る。 It is inserted between the 30 rolling to obtain a steel-made flat wire 11 entirely with a metal plating layer 12.

【0018】次いで、前記鋼材製平線11を、図のように、凹凸部41を有する上下のロール40,40間に挿通する。 [0018] Then, the steel-made flat wire 11, as shown, is inserted between the upper and lower rolls 40, 40 having an uneven portion 41. この工程によって、前記したような鋼材製平線11の全体が金属メッキ層12で覆われ、かつその表面側10Aおよび裏面側10Bの両面に凹凸部15が刻設された所定厚みおよび幅の伸縮防止用平線10を得ることができる。 This process, entirely covered with a metal plating layer 12, and the expansion and contraction of a predetermined thickness and width uneven portion 15 is engraved on both sides of the surface side 10A and the back side 10B of the steel-made flat wire 11 as described above it can be obtained for preventing flat wire 10.

【0019】さらに、この発明の伸縮防止用平線10を製造する方法として、請求項4として規定した製法が提案される。 Furthermore, as a method for producing a stretch-preventing flat wire 10 of the present invention, production method was defined as claim 4 is proposed. すなわち、請求項4の発明は、図5に図示したように、鋼材製丸線20に金属メッキを施す工程と、 That is, the invention of claim 4, as shown in FIG. 5, the steps of applying a metal plating to the steel material made of round wire 20,
前記金属メッキ層21に覆われた鋼材製丸線22を凹凸部41を有する圧延ロール50間に挿通圧延する工程とからなる。 And a step of inserting rolling between the rolling roll 50 having a concave-convex portion 41 a steel material made of round wire 22 covered with the metal plating layer 21.

【0020】この製法では、前記したと同様に、鋼材製丸線20に金属メッキを施される。 [0020] In this method, in the same manner as above, it is subjected to metal plating on the steel material made of round wire 20. なお、この工程は先の実施例と同一であるため同一符号を付し、その説明を省略する。 Note that this step will be denoted by the same reference numerals are the same as the previous embodiment, description thereof is omitted. そして、金属メッキ層21に覆われた鋼材製丸線22を、図のように、凹凸部41を有する上下の圧延ロール50,50間に挿通して圧延する。 Then, the steel-made round wire 22 covered with the metal plating layer 21, as shown, be rolled is inserted between the upper and lower rolling rolls 50, 50 having an uneven portion 41. この工程によって、鋼材製平線11の全体が金属メッキ層12で覆われ、かつその表面側10Aおよび裏面側10Bの両面に凹凸部15が刻設された所定厚みおよび幅の伸縮防止用平線10を一時に得ることができる。 In this step, the entire steel-made flat wire 11 is covered with a metal plating layer 12, and stretch-preventing flat wire having a predetermined thickness and width uneven portion 15 is engraved on both sides of the surface side 10A and the back side 10B 10 can be obtained at a time.

【0021】これらの製法において、伸縮防止用平線1 [0021] In these processes, expansion and contraction prevention for flat line 1
0の厚み及び凹凸部15の形態等は各ロール30,4 0 Each the form such thickness and uneven portion 15 rolls of 30,4
0,50によって適宜定められ、所望のものを得ることができる。 0,50 appropriately determined, it is possible to obtain a desired one. 上記の実施例では、図2及び図3に示したものを製造した。 In the embodiment described above, were prepared as shown in FIGS.

【0022】 [0022]

【発明の効果】以上図示し説明したように、この発明による押出成形品のための伸縮防止用平線にあっては、鋼材製平線の全体が金属メッキ層によって覆われているとともに、表面側および裏面側の両面に凹凸部が刻設されていることより次のような効果を有する。 [Effect of the Invention] shown above as described, in the stretch preventing spur lines for extrusion according to this invention, the entire steel-made flat wire are covered with metal plating layer, the surface has the following effects from the uneven portion is engraved on both sides of the side and the back side. まず、第一に、鋼材製平線の全体が金属メッキ層によって覆われていることより、鋼材製平線の腐食が防止できるので、従来のような防蝕のための油処理が不要となる。 In the first place, from the whole of the steel-made flat wire are covered with metal plating layer, it is possible to prevent corrosion of the steel-made flat wire, oil processing for corrosion protection as in the prior art becomes unnecessary. 油処理がなされていなければ、押出成形品との一体成形時における脱脂処理も必要がなくなる。 If the oil treatment is not done, the need is eliminated degreasing process when integrally molded with the extrusion.

【0023】第二に、表面側および裏面側の両面に凹凸部が刻設されていることより、押出成形品と結合してアンカー効果を生じ、接着剤を塗着しなくても高い結合強度を備え、該押出成形品の伸縮を防止することができる。 [0023] Secondly, from the uneven portion is engraved on both sides of the front and back side, produce anchor effect combined with extrusion, higher even without Nurigi adhesive bond strength the provided, it is possible to prevent the expansion and contraction of the extrusion molded article. 特に、請求項2の発明として規定した伸縮防止用平線にあっては、従来の接着剤塗着のものと同等以上の結合強度を有し、その伸縮防止効果を有する。 In particular, in the stretch preventing spur line was defined as the invention of claim 2 has a binding strength of at least equivalent to those of conventional adhesives the coating has its stretch preventing effect. また、接着剤を使用する必要がないので、あらゆる樹脂材料に対応することができる。 Since it is not necessary to use an adhesive, it is possible to address all the resin material.

【0024】第三に、芯材として成形品内に一体に埋設された後にあっては、伸縮防止用平線の全体が金属メッキ層によって覆われているので、鋼材製平線の経時的な腐食や劣化が防止され、凹凸部のアンカー結合による密着効果の低減を防止でき、芯材としての伸縮防止用平線の高い密着性を長期に亘って保持することができる。 [0024] Third, in the after being embedded integrally in the molded article as the core material, since the entire stretch preventing flat wire are covered with metal plating layer, a time of the steel material made of flat wire corrosion and deterioration can be prevented, it is possible to prevent reduction of the adhesion effect anchoring of the concave-convex portion, a high adhesion stretch preventing flat wire as the core material can be maintained over a long term.

【0025】第四に、この発明の伸縮防止用平線を使用すれば、前記した従来の鋼材製平線を使用して押出成形品を成形する場合に比し、脱脂処理工程、接着剤塗布工程及び接着剤焼き付け工程の全てを省略することが可能となり、工程管理及びコスト面において大きな有利性を有する。 [0025] Fourth, the use of stretch-preventing flat wire of the invention, compared with the case of forming the extrusion using conventional steel-made flat wire described above, degreasing step, the adhesive application It can be omitted all the steps and adhesive baking step and becomes, has a large advantage in the process control and cost.

【0026】また、この発明に係る製法にあっては、前記した伸縮防止用平線を効率良く簡単かつ確実に製造することができる。 Further, in the method according to the present invention, it is possible to manufacture the above-mentioned stretch preventing spur line efficiently easily and reliably.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】この発明に係る伸縮防止用平線の一実施例を示す部分斜視図である。 1 is a partial perspective view showing one embodiment of a stretch-preventing flat wire according to the present invention.

【図2】図1の部分拡大平面図である。 2 is a partially enlarged plan view of FIG.

【図3】図2の3−3線で切断した断面図である。 3 is a cross-sectional view taken along line 3-3 in FIG.

【図4】請求項3の発明の伸縮防止用平線を製造する方法の一実施例を表す概略工程図である。 4 is a schematic process diagram showing an embodiment of a method for producing a stretch-preventing flat wire of the invention of claim 3.

【図5】請求項4の発明の伸縮防止用平線を製造する方法の実施例を表す概略工程図である。 5 is a schematic flow diagram illustrating an embodiment of a method for producing a stretch-preventing flat wire of the invention of claim 4.

【図6】自動車用モール材の一例を断面とともに表した部分斜視図である。 6 is a partial perspective view illustrating with section an example of an automotive molding material.

【符号の説明】 DESCRIPTION OF SYMBOLS

10 伸縮防止用平線 10A 表面側 10B 裏面側 11 鋼材製平線 12 金属メッキ層 15 凹凸部 16 凹陥部(四角錘形状) 20 鋼材製丸線 21 金属メッキ層 22 金属メッキ覆鋼材製丸線 30 圧延ロール 40 ロール 41 凹凸部 50 凹凸部を有する圧延ロール 10 stretch preventing spur line 10A surface 10B back side 11 steel-made flat wire 12 metal plating layer 15 uneven portion 16 recess (square pyramid shape) 20 steel steel round wire 21 metal plating layer 22 metal plating covering the steel-made round wire 30 rolling roll having a rolling roll 40 roll 41 irregular portion 50 irregular portion

Claims (4)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 押出成形品の芯材として一体に埋設され該押出成形品の伸縮を防止する平線であって、鋼材製平線の全体が金属メッキ層によって覆われているとともに、表面側および裏面側の両面に凹凸部が刻設されていることを特徴とする押出成形品のための伸縮防止用平線。 1. A flat wire to prevent the expansion and contraction of the buried the extrusion molded article integrally as a core material for extrusion, together with the whole of the steel-made flat wire are covered with metal plating layer, the surface side and stretch preventing spur lines for extrusion of uneven portions on both sides of the back surface side, characterized in that it is engraved.
  2. 【請求項2】 請求項1において、前記凹凸部が四角錘形状の凹陥部を均一に配置したものよりなり、該凹陥部の対角線の長さが0.5mm、窪み深さが0.11m 2. A method according to claim 1, wherein the irregular portion is than placed uniformly recess of square pyramid shape, the recessed portion of the diagonal of 0.5mm length, the depression depth is 0.11m
    m、各凹陥部の間隔が0.25mmである押出成形品のための伸縮防止用平線。 m, stretch-preventing flat wire for extrusion intervals of the concave portions is 0.25 mm.
  3. 【請求項3】 断面円形の鋼材製丸線に金属メッキを施して全体が金属メッキ層によって覆われた鋼材製丸線を得る工程と、前記丸線を圧延ロール間に挿通圧延して全体に金属メッキ層を有する平線を得る工程と、次いで前記平線を凹凸部を有するロール間に挿通して全体に金属メッキ層を有しかつその表面側および裏面側の両面に凹凸部が刻設された所定厚みおよび幅の平線を得る工程とからなることを特徴とする押出成形品のための伸縮防止用平線の製法。 3. A process whole is subjected to metal plating on a circular section of the steel material made of round wire to obtain a steel material made of round wire covered by a metal plating layer on the whole by inserting rolling the round wire to rolling rolls step and then the flat line has a metal plating layer on the entire inserted through between the rolls having an uneven portion and the concave-convex portion is engraved on both sides of the surface side and back surface side to obtain a flat wire having a metal plating layer have been preparation of the telescopic prevention spur lines for extrusion, characterized in that it consists of a step of obtaining a flat wire having a predetermined thickness and width.
  4. 【請求項4】 断面円形の鋼材製丸線に金属メッキを施して全体が金属メッキ層によって覆われた鋼材製丸線を得る工程と、前記丸線を凹凸部を有する圧延ロール間に挿通圧延して全体に金属メッキ層を有しかつその表面側および裏面側の両面に凹凸部が刻設された所定厚みおよび幅の平線を得る工程とからなることを特徴とする押出成形品のための伸縮防止用平線の製法。 4. A process for the whole is subjected to metal plating on a circular section of the steel material made of round wire to obtain a steel material made of round wire covered by a metal plating layer, through rolling the rolling rolls having an uneven portion of the round wire for having a metal plating layer and extrusion, characterized in that uneven portions on both sides of the surface side and the back side and a step of obtaining a flat line engraved and predetermined thickness and width throughout and process of expansion and contraction prevention for the flat line.
JP2000267490A 2000-09-04 2000-09-04 Stretch-resistant wire for extrusion molding and manufacturing method therefor Pending JP2002079563A (en)