JP2002030707A - Water section fitting and its manufacturing method - Google Patents

Water section fitting and its manufacturing method

Info

Publication number
JP2002030707A
JP2002030707A JP2000218147A JP2000218147A JP2002030707A JP 2002030707 A JP2002030707 A JP 2002030707A JP 2000218147 A JP2000218147 A JP 2000218147A JP 2000218147 A JP2000218147 A JP 2000218147A JP 2002030707 A JP2002030707 A JP 2002030707A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
layer
water
primer
corrosion
faucet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2000218147A
Other languages
Japanese (ja)
Inventor
Makoto Ahara
Takeshi Ito
Ryohei Matsui
Takeshi Nishikawa
毅 伊藤
良平 松井
武 西川
真 阿原
Original Assignee
Inax Corp
株式会社イナックス
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To provide a faucet capable of easily removing adhering dirt. SOLUTION: An antifouling layer composed of a primer layer 4 and a topcoat layer 5 having water repellency and oil repellency is formed on the surface side of a base material 1 made of a metal through a corrosion-resistant layer consisting of a nickel plated layer 2 and a chromium plated layer 3.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明が属する技術分野】本発明は、水栓等のように水と接触する場所で用いられる水廻り金具及びその製造方法に関する。 The present invention relates] relates plumbing fittings and a manufacturing method thereof, for use in places where contact with water, such as such as faucets.

【0002】 [0002]

【従来の技術】水廻り金具として代表的な水栓は主として金属製母材により構成されている。 A typical faucet 2. Description of the Prior Art As water around the bracket is composed mainly by the metal base material. この金属製母材としては、複雑な形状のものを製造可能であるという理由等から、BC6等の鋳物用の銅合金が多用されている。 The metal-made base material, because such that it can produce the intended complex shape, a copper alloy for casting such BC6 is frequently used.
また、その母材の表面の耐摩耗性及び耐蝕性を向上させるとともに平滑な表面を得るため、その母材にはニッケルめっきが施され得る。 Further, the order to obtain a smooth surface improves the wear resistance and corrosion resistance of the surface of the base, and its base material may subjected to nickel plating. さらに、審美的にも優れた金属光沢を有する鏡面仕上げ面を得るため、ニッケルめっきを施した母材にさらにクロムめっきが施される。 Furthermore, in order to obtain a mirror-finished surface having aesthetic excellent metallic luster, more chromium plated base metal plated with nickel is subjected.

【0003】 [0003]

【発明が解決しようとする課題】しかし、水廻り金具は、水と接触する機会が多いことから、汚れが付着しやすく、かつ拭い落とすことが困難であるという欠点を有することが明らかとなった。 [SUMMARY OF THE INVENTION] However, plumbing fitting, since it is many opportunities to contact with water, were found to have the disadvantage that dirt is difficult to drop easily, and wipe attachment . この点、発明者らの試験結果によれば、金属製母材にニッケルめっき及びクロムめっきを施した水栓においてはこれが顕著である。 In this regard, according to the inventors of the test result, which is significant in faucet plated with nickel and chrome plating the metal base material.

【0004】本発明者らは、従来の水廻り金具についてのこのような欠点を克服すべく、金属製母材にニッケルめっき及びクロムめっきを施した水栓を例として、その汚れの付着メカニズムについて鋭意研究した結果、以下のことを考察した。 [0004] The present inventors have found that in order to overcome such drawbacks of conventional water around fittings, as an example faucet plated with nickel and chrome plating the metal base material, for attachment mechanism of dirt extensive research and as a result, was considered to be the following.

【0005】すなわち、水栓に付着する汚れは無機系のものと有機系のものとの二種類のものが存在する。 Namely, dirt adhering to the faucet is present those two types of those ones of inorganic and organic. 無機系の汚れは、主成分がケイ酸であり、水中の溶性シリカが網目構造をなすケイ酸としてめっき皮膜の表面上に析出することにより生じたものである。 Dirt inorganic system, the main component is silicic acids arose by water-soluble silica is deposited on the surface of the plating film as a silicate which forms a network structure. また、ケイ酸の他、水の中に含まれるカルシウム分が炭酸イオンと結びついて生成した炭酸カルシウムも析出し得る。 Another silicate, calcium carbonate calcium content generated in conjunction with carbonate ions contained in the water may also be precipitated. 他方、有機系の汚れは、石鹸カス、皮脂、ぬめり乾燥物等からなる。 On the other hand, contamination of the organic system, consisting of soap scum, oil, slime drying and the like.

【0006】上記無機系の汚れは親水性であるため、同じく親水性であるめっき皮膜上に強固に付着し、拭い落とすことが困難となる。 [0006] contamination of the inorganic is hydrophilic, also firmly attached to the plated film is hydrophilic, it is difficult to drop wipe. また、めっきの代替としてアクリル樹脂等の塗装を施した場合、ある程度の撥水性は得られるが、ケイ酸や炭酸カルシウム等の無機系の汚れが塗膜に食い込み、容易に拭い落とすことはできない。 Also, when painted, such as an acrylic resin as a substitute for plating, although some water repellency obtained, dirt inorganic such as silica or calcium carbonate bites into the coating film can not be dropped easily wiped.

【0007】有機系の汚れの場合、それは単独では固着までには至っておらず、洗浄剤を使用すればそれを落とすことは可能であるが、水拭き、乾拭き程度ではそれが塗り広がるだけであり、落としにくい。 [0007] When soil organic, it alone does not reached the stage anchoring is to drop it Using detergent can be wiped with water, about wipe is only it spreads coating , hard to drop. また、有機系の汚れが無機系の汚れとともに複合化した場合、それは容易に落とし得ない。 Also, if the contamination of the organic system is complexed with dirt inorganic, it can not easily drop.

【0008】この点、他の水廻り金具も同様であるが、 [0008] In this regard, although other water around fittings are also the same,
特に水栓は常時水と接触しているため、上記不具合が顕著である。 Especially faucet because in contact with always water, the problem is remarkable.

【0009】本発明は、上記従来の実情に鑑みてなされたものであり、付着した汚れを容易に除去することが可能である水廻り金具を提供することを解決すべき課題とする。 [0009] The present invention has been made in view of the above conventional circumstances, and an object to be achieved by providing a plumbing fitting can be easily remove adhering dirt.

【0010】 [0010]

【課題を解決するための手段】本発明の水廻り金具は、 Means for Solving the Problems] water around fitting of the present invention,
水廻りに使用され、金属製母材の表面側に撥水性及び撥油性を有する防汚層が形成されていることを特徴とする。 It is used in the water around, wherein the antifouling layer having water repellency and oil repellency is formed on the surface side of the metal base material.

【0011】すなわち、この水廻り金具の表面側には撥水性を有する防汚層が形成されているため、ケイ酸や炭酸カルシウム等を含む水を弾き易く、汚れとして付着しにくい。 [0011] That is, this order on the surface side of the plumbing fitting is formed antifouling layer having water repellency, easy to play water containing silicic acid and calcium carbonate and the like, hardly deposited as dirt. 仮にケイ酸や炭酸カルシウム等が析出したとしても、それらが表面に強固に付着しにくい。 Even if silicic acid or calcium carbonate is precipitated, hardly they firmly adhered to the surface.

【0012】また、防汚層は撥油性も有するため、皮脂を弾き易く、汚れとして付着しにくい。 [0012] The antifouling layer to have also oil repellency, easily play the sebum, hardly deposited as dirt. 仮に石鹸カス、 If soap scum,
ぬめり乾燥物等の有機系の汚れが付着しても、それらが表面に強固に付着しにくい。 Be deposited dirt organic slime drying, etc., firmly hardly adhere thereto the surface.

【0013】このため、水廻り金具の表面に付着した汚れについては、無機系及び有機系の区別にかかわらず、 [0013] Therefore, for the dirt adhering to the surface of the water around fittings, regardless of the distinction between inorganic and organic,
容易に拭い落とすことが可能となる。 It is possible to drop easily wiped.

【0014】母材が水栓を構成している場合に特に効果が大きい。 [0014] The effect is particularly large in the case where the base material constitutes a faucet. 水栓は、浴室、洗面所等において、常時水と接触しているからである。 Faucet is full, the toilet or the like, because in contact at all times with water.

【0015】防汚層はフッ素樹脂により形成することができる。 [0015] The antifouling layer can be formed by fluorocarbon resin. フッ素樹脂は優れた撥水性、撥油性及び非粘着性を有するため、上記作用効果を奏することができる。 Since fluororesin having excellent water repellency, oil repellency and non-tackiness, it is possible to obtain the above advantageous effects.
また、フッ素樹脂製の防汚層は、水廻りで多用されるスポンジや雑巾による摩耗に対して、優れた耐久性を奏する。 Further, fluororesin antifouling layer, to abrasion by sponge or rag frequently used in plumbing, exhibits an excellent durability.

【0016】フッ素樹脂の種類については特に限定はないが、例えばポリテトラフルオロエチレン(PTF [0016] There is no particular limitation on the type of fluororesin, such as polytetrafluoroethylene (PTF
E)、PTFEと無機化合物との混合体(例えばダイキン工業株式会社製「ポリフロンTFEエナメル(登録商標)」等)、テトラフルオロエチレン−ヘキサフルオロプロピレン共重合体(例えばダイキン工業株式会社製「ネオフロンFEP(登録商標)」等のFEP)、テトラフルオロエチレン−エチレン共重合体(例えばダイキン工業株式会社製「ネオフロンETFE(登録商標)」 E) mixture of PTFE and the inorganic compound (e.g., manufactured by Daikin Industries, Ltd., "Polyflon TFE Enamel (registered trademark)", etc.), tetrafluoroethylene - hexafluoropropylene copolymer (for example, Daikin Industries, Ltd., "Neoflon FEP (R) FEP of ", etc.), tetrafluoroethylene - ethylene copolymer (e.g. manufactured by Daikin Industries, Ltd.," Neoflon ETFE (registered trademark) "
等のETFE)、ポリビニリデンフルオライド(例えばダイキン工業株式会社製「ネオフロンVDF(登録商標)」等のPVDF)、ポリフッ化ビニル(PVF)、 ETFE) etc., polyvinylidene fluoride (e.g. Daikin Industries Ltd., "Neoflon VDF (registered trademark)" PVDF etc.), polyvinyl fluoride (PVF),
ポリクロロトリフルオロエチレン(例えばダイキン工業株式会社製「ネオフロンCTFE(登録商標)」等のP Polychlorotrifluoroethylene (e.g. Daikin Industries Ltd., "Neoflon CTFE (registered trademark)" P such as
CTFE)、テトラフルオロエチレン−パーフルオロアルキルビニルエーテル共重合体(例えばダイキン工業株式会社製「ネオフロンPFA(登録商標)」等のPF CTFE), tetrafluoroethylene - perfluoroalkyl vinyl ether copolymer (e.g. Daikin Industries Ltd., "Neoflon PFA (registered trademark)" PF etc.
A)等を用いることができる。 It can be used A) or the like.

【0017】防汚層は母材の表面側にプライマ層を有することが好ましい。 The antifouling layer preferably has a primer layer on the surface side of the base material. プライマ層を除く防汚層(トップコート層)の密着性が向上するからである。 Adhesion of the antifouling layer excluding the primer layer (topcoat layer) is improved.

【0018】かかるプライマ層にはフッ素樹脂粒子が混合されていることが好ましい。 [0018] In such a primer layer is preferably the fluorine resin particles are mixed. こうであれば、トップコート層としてフッ素樹脂を採用した場合、そのトップコート層とプライマ層中のフッ素樹脂粒子とが熱融着し、 If this, in the case of adopting the fluororesin as a top coat layer, and the fluorine resin particles of the topcoat layer and the primer layer heat-sealed,
防汚層の密着性が向上する。 Adhesion of the antifouling layer is improved.

【0019】また、かかるプライマ層には金属粉末が混合されていることも好ましい。 [0019] It is also preferred that the metal powder is mixed in such a primer layer. こうであれば、表面からプライマ層中の金属粉末が透ける場合、防汚層の外見をメタリック風にすることが可能となり、審美性に富む水廻り金具とすることができる。 If this, if the metal powder primer layer from the surface seen through, it is possible to the appearance of the antifouling layer to metallic wind can be water around metal-rich aesthetics. トップコート層に金属粉末を混合すると、表面の平滑性に欠けるとともに、金属粉末の酸化による審美性の低下という不具合を生じる。 When mixing the metal powder in the top coat layer, with lacks smoothness of the surface, resulting in inconvenience of decreased aesthetics due to oxidation of the metal powder.
このような金属粉末としては、アルミニウム粉末、ステンレス粉末、真鍮粉末、青銅粉末、銅粉末、白金粉末、 Examples of such a metal powder, aluminum powder, stainless steel powder, brass powder, bronze powder, copper powder, platinum powder,
金箔粉末等を採用することができる。 It can be employed gold foil powder.

【0020】本発明の水廻り金具は、母材の表面と防汚層との間に耐蝕層が形成されていることが好ましい。 The water around fitting of the present invention, it is preferable that the corrosion-resistant layer is formed between the surface and the antifouling layer of the base material. こうであれば、例え防汚層に傷がついたとしても、金属製母材が剥き出しとなることはなく、耐蝕層によって金属製母材の腐蝕を防止できるからである。 If this, even scratched even antifouling layer, never metal base material is exposed, is because it prevents corrosion of the metal base material by a corrosion-resistant layer.

【0021】この場合において、耐蝕層はニッケルめっき及びクロムめっきを含むことができる。 [0021] In this case, corrosion-resistant layer may comprise a nickel plating and chrome plating. ニッケルめっきは優れた耐蝕性を示すのみならず、レベリング作用によって金属製母材の表面の凹凸を平滑化する。 Nickel plating not only exhibit excellent corrosion resistance, to smooth the unevenness of the surface of the metal base material by a leveling action. また、この上に形成されるクロムめっきは表面の硬度を上げる。 Also, chromium plating formed on the increase the hardness of the surface.
耐蝕層としてニッケルめっきのみを採用することもできる。 It is also possible to employ only the nickel plating as corrosion-resistant layer. これにより優れた耐蝕性と平滑化の効果が得られ、 The effect of this by excellent corrosion resistance and smoothed is obtained,
水廻り金具としての使用に耐え得る。 It can withstand the use of as water around the bracket.

【0022】本発明の水廻り金具の製造方法は、金属製母材の表面にニッケルめっき及びクロムめっきからなる耐蝕層を形成する第1工程と、該耐蝕層上にプライマとフッ素樹脂とからなる防汚層を形成する第2工程とからなることを特徴とする。 The method of producing a water-around fitting of the present invention comprises a first step of forming a corrosion-resistant layer of nickel plating and chrome plating on the surface of the metal base material, a primer and fluorine resin on the corrosion-resistant layer characterized in that and a second step of forming an antifouling layer.

【0023】第1工程では、金属製母材より硬くて腐蝕にも強いニッケルめっき及びクロムめっきからなる耐蝕層を金属製母材の表面に形成する。 [0023] In the first step, to form a corrosion-resistant layer made of a strong nickel plating even and chrome plated corrosion and harder than the metal base material to the surface of the metal base material. かかる第1工程は公知のめっき法により行い得る。 Such first step can be carried out by known plating method.

【0024】第2工程では、まず耐蝕層上にプライマからなるプライマ層を形成する。 [0024] In the second step, first forming a primer layer comprising a primer on the corrosion-resistant layer. これは、フッ素樹脂のみのトップコート層だけでは、耐蝕層への密着性が悪く、 This is because only the top coat layer of a fluorine resin alone has poor adhesion to the corrosion-resistant layer,
実用に耐え得ないためである。 This is because the practical use not withstand. プライマとしては、フッ素樹脂粒子とバインダとを混合したものを採用することができる。 The primer may be employed a mixture of fluorine resin particles and a binder. このようにすれば、耐蝕層との密着性を確保しつつ、防汚層において、トップコート層とプライマ層のフッ素樹脂粒子とを熱融着させることにより、防汚層の密着性をさらに向上させることができる。 Thus, while ensuring the adhesion between the corrosion-resistant layer, in an antifouling layer, by heat fusion and fluorine resin particles of the topcoat layer and the primer layer, further improving the adhesion of the antifouling layer it can be. プライマとして、金属粉末とバインダとを混合したものを採用することもできる。 As primers, it can be employed a mixture of a metal powder and a binder. このようにすれば、表面からプライマ層中の金属粉末が透ける場合、防汚層の外見をメタリック風にすることが可能となり、審美性に富む水廻り金具とすることができる。 Thus, if the metal powder primer layer from the surface seen through, it is possible to the appearance of the antifouling layer to metallic wind can be water around metal-rich aesthetics. プライマ層を形成する工程は、スプレー法等によりプライマを耐蝕層上に形成した後、加熱を行うことにより行い得る。 Forming a primer layer is formed by forming a primer on the corrosion-resistant layer by spraying or the like may be carried out by heating.

【0025】そして、第2工程として、プライマ層上にフッ素樹脂からなるトップコート層を形成する。 [0025] Then, as a second step, to form a topcoat layer made of a fluorine resin on a primer layer. こうして、プライマ層とトップコート層とからなる防汚層が耐蝕層上に形成される。 Thus, antifouling layer composed of a primer layer and the topcoat layer is formed on the corrosion-resistant layer. トップコート層を形成する工程としては、特に限定はないが、例えばフッ素樹脂粒子を静電塗装した後、加熱することを採用することができる。 The step of forming the top coat layer is not particularly limited, for example, fluorine resin particles after electrostatic coating, can be employed to heat.

【0026】 [0026]

【発明の実施の形態】以下、本発明を具体化した実施形態1、2を比較形態とともに図面を参照しつつ説明する。 BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, will be described with comparative form the first and second embodiments embodying the present invention with reference to the drawings.

【0027】(実施形態1)実施形態1では、水廻り金具として水栓を採用している。 [0027] In (Embodiment 1) Embodiment 1, adopts the faucet as water around the bracket. この水栓は、図1に示すように、青銅鋳物合金の一種であるBC6を鋳造してなる母材1を有している。 The faucet, as shown in FIG. 1, has a base material 1 formed by casting of the BC6 is a kind of bronze casting alloy.

【0028】「第1工程」この母材1の表面を研磨紙及びバフを用いて研磨を行う。 [0028] performing polishing using a "first step" abrasive paper and buff the surface of the base material 1. その後、図2に示すように、この母材1にニッケルめっき層2を約10μmの膜厚となるよう施す。 Thereafter, as shown in FIG. 2, it applied to a thickness of about 10μm nickel plating layer 2 in the preform 1. さらに、図3に示すように、ニッケルめっき層2上にクロムめっき層3を約0.5μmの膜厚となるよう施す。 Furthermore, as shown in FIG. 3, it applied to a thickness of about 0.5μm chrome plating layer 3 on the nickel plated layer 2. これらニッケルめっき層2及びクロムめっき層3が耐蝕層である。 These nickel plating layer 2 and the chromium plating layer 3 is corrosion-resistant layer.

【0029】「第2工程」図4に示すように、第1工程終了後、耐蝕層上にフッ素樹脂粒子4aとアルミニウム粉末4bとバインダとが混合されている一液型フッ素系塗料(例えば、ダイキン工業株式会社製「ポリフロンT As shown in the "second step" 4, after completion of the first step, the fluorine resin particles 4a and aluminum powder 4b binder and one part is mixed fluorine-based paint on the corrosion-resistant layer (e.g., manufactured by Daikin Industries, Ltd. "Polyflon T
FEタフコートエナメル(登録商標)」)をスプレー塗装する。 FE tough coat enamel (registered trademark) ") to spray painting. この後、これを90°Cで15分間加熱し、プライマ層4を得る。 Thereafter, it was heated for 15 minutes at 90 ° C, to obtain a primer layer 4.

【0030】次いで、図5に示すように、プライマ層4 [0030] Then, as shown in FIG. 5, the primer layer 4
上にテトラフルオロエチレン−パーフルオロアルキルビニルエーテル共重合体製のトップコート(ダイキン工業株式会社製「ネオフロンPFA(登録商標)」)を静電塗装する。 Tetrafluoroethylene above - perfluoroalkyl vinyl ether copolymer manufactured by the topcoat (manufactured by Daikin Industries, Ltd., "Neoflon PFA (registered trademark)") electrostatically painting. この後、380°Cで20分間加熱し、トップコート層5を得る。 Thereafter, heating at 380 ° C 20 minutes, to obtain a topcoat layer 5. これらプライマ層4及びトップコート層5が防汚層である。 These primer layer 4 and the top coat layer 5 is an antifouling layer. こうして、水栓を得る。 Thus, to obtain a faucet.

【0031】(比較形態)市販の水栓を比較形態として用意する。 [0031] is prepared as a comparative embodiment (Comparative Embodiment) A commercially available faucet. この水栓は、母材がやはりBC6であり、その母材の表面を研磨紙及びバフを用いて研磨した後、ニッケルめっきを約10μmの膜厚となるよう施し、さらにニッケルめっき層上にクロムめっき層を約0.5μm The water faucet is the base material is again BC6, was polished with abrasive paper and buff the surface of the base material is subjected to a thickness of about 10μm to nickel plating, further chromium on the nickel plated layer about 0.5μm a plating layer
の膜厚となるよう施したものである。 It is that has been subjected so as to be of thickness. プライマ層及びトップコート層は施されていない。 Primer layer and the top coat layer has not been applied. すなわち、実施形態1 That is, embodiments 1
における第1工程のみの処理で終了し、第2工程を行わない水栓である。 It finished in the processing of only the first step in a faucet is not performed second step.

【0032】(評価1)実施形態1の水栓と比較形態の水栓とについて、「見ばえ」、「防汚性能」及び「耐久性」について評価した。 [0032] (Evaluation 1) For the faucet of comparative form the faucet embodiment 1, "fruit fly", were evaluated for "antifouling performance" and "durability".

【0033】ここで、「見ばえ」は目視による「外観」 [0033] In here, "fruit flies", "appearance" is by visual inspection
と「初期撥水性」との評価である。 And the evaluation of the "initial water repellency". 初期撥水性は、製造後、未使用の段階における表面張力(dyn/cm)により評価し、32dyn/cm未満を「○」とし、32 The initial water repellency, after production, and evaluated by the surface tension at the stage of the unused (dyn / cm), of less than 32dyn / cm as "○", 32
dyn/cm以上を「×」とした(JISK6768 More than dyn / cm was evaluated as "×" (JISK6768
(ポリエチレン及びポリプロピレンフィルムの濡れ試験方法)参照)。 (Wetting test method polyethylene and polypropylene films) reference).

【0034】また、「防汚性能」は「付きにくさ」と「落としやすさ」との両方の評価である。 [0034] In addition, "antifouling performance" is an evaluation of both the "drop ease" and "marked with difficulty". 「付きにくさ」は「無機系汚れ」及び「有機汚れ」について評価した。 "Attached difficulty" was evaluated for "inorganic dirt" and "organic dirt". 「無機系汚れ」については、乾湿繰り返しを200 For "inorganic dirt" is, the wet and dry repetition 200
0回行った後の表面を目視により評価した。 0 times the surface of the after was visually evaluated. 「有機系汚れ」については、一定条件下で汚れた水を貯留した浴槽へ24時間浸漬した後の表面を目視により評価した。 For "organic dirt" was evaluated by visually surfaces after immersion for 24 hours into bath which stores the dirty water under certain conditions.
「無機系汚れ」及び「有機系汚れ」ともに、汚れがつきにくかった場合を「○」とし、汚れがつきやすかった場合を「×」とした。 Both "inorganic dirt" and "organic dirt", a case where the dirt was hard luck as "○", was a case where the dirt is likely regard as "×".

【0035】さらに、「落としやすさ」は「無機系汚れ」、「有機汚れ」及び「油性インク」について評価した。 [0035] In addition, the "drop ease" was evaluated for "inorganic dirt", "organic dirt" and "oil-based ink". 「無機系汚れ」については、上記乾湿繰り返しを2 For "inorganic dirt" is 2 the above-mentioned wet and dry repetition
000回行った後の表面のふき取り試験により評価した。 It was evaluated by wiping test of the surface after carrying out 000 times. 「有機系汚れ」については、オレイン酸及びたんぱく質の混合物を付着した後、乾燥させ、ふき取り試験により評価した。 For "organic dirt", after depositing a mixture of oleic acid and protein, dried and evaluated by wiping test. 「油性インク」については、市販の油性インクを付着した後、24時間経過させ、この後のふき取り試験により評価した。 For "oil-based ink", after attaching a commercially available oil-based inks, aged 24 hours was evaluated by wiping the test after this. 「無機系汚れ」、「有機系汚れ」及び「油性インク」ともに、洗剤や溶剤を使用しなくても汚れが落としやすかった場合を「○」とし、汚れが落としにくかった場合を「×」とし、その中間を「△」とした。 "Inorganic dirt", "organic dirt" and "oil-based ink" together, a case where contamination is likely off without using detergents or solvents as "○", the case where dirt was difficult down as "×" , was the middle as "△".

【0036】また、「耐久性」については、「表面硬度」及び「耐摩耗性」について評価を行った。 Further, the "durability" was evaluated for "surface hardness" and "abrasion resistance". 「表面硬度」は、鉛筆による引っ掻き傷つき性の評価により、1 "Surface hardness" is, by scratching damage of the evaluation by the pencil, 1
2Hでも傷が認められない場合を「◎」、6H以上で傷が認められない場合を「○」、1H以上で傷が認められない場合を「△」、それ未満の硬度で傷が認められる場合を「×」として評価した。 The case where 2H not observed scratches even "◎", "○" and if the flaw is not observed in the above 6H, "△" a case where flaws are not observed at least 1H, observed scratches in less hardness It was evaluated as "×" the case.

【0037】さらに、「耐摩耗性」は「スポンジ摩耗」 [0037] In addition, "abrasion resistance" is "sponge wear"
と「雑巾摩耗」とについて行った。 Was performed on a "rag wear," he said. 「スポンジ摩耗」 "Sponge wear"
は、含水させたスポンジを100g/cm 2の負荷で3 Is 3 sponges were hydrated at a load of 100 g / cm 2
万回往復させ、この後の表面接触角(°)の測定を行った。 Million times back and forth, was measured surface contact angle after the (°). 「雑巾摩耗」は、含水させた雑巾を100g/cm "Rag wear" is, was allowed to moisture cloth 100g / cm
2の負荷で3万回往復させ、この後の表面接触角(°) Back and forth 30,000 times at two loads, the surface contact angle after the (°)
の測定を行った。 It was of measurement. 「スポンジ摩耗」及び「雑巾摩耗」ともに、接触角が100°以上であった場合を「○」、接触角が90°未満であった場合を「×」とした。 Both "sponge wear" and "rag wear", where the contact angle was 100 ° or more "○", and the contact angle is less than 90 ° as "×". 以上の評価試験の結果を表1に示す。 Table 1 shows the results of the evaluation tests of the above.

【0038】 [0038]

【表1】 [Table 1]

【0039】表1からわかるように、「見ばえ」についての「外観」では、比較形態の水栓の表面が既存の鏡面の金属光沢であり、実施形態1の水栓の表面は新規性のあるシルバーメタリックであり、ともに「○」の評価が得られる。 [0039] As can be seen from Table 1, the "appearance" of the "fruit fly", the surface of the water faucet of Comparative Embodiment is an existing mirror surface of the metal gloss, surface novelty of faucet Embodiment 1 is a silver metallic, both the evaluation of the "○" is obtained. しかし、実施形態1の水栓は既存品にない審美性を有している。 However, water faucet of the first embodiment has the aesthetics is not in existing products. これは、実施形態1の水栓では、プライマ層4にアルミニウム粉末4bが含まれ、トップコート層5が表面からプライマ層4中のアルミニウム粉末4bを透けさせるためである。 This is because the water faucet embodiment 1, aluminum powder 4b is included in the primer layer 4, the top coat layer 5 is for causing sheer aluminum powder 4b primer layer 4 from the surface.

【0040】また、「初期撥水性」については、比較形態の水栓は「△」であるのに対し、実施形態1の水栓では「○」となった。 [0040] In addition, the "initial water repellency" is, while the faucet of comparison form is "△", becomes "○" in the water faucet according to the first embodiment. これは、実施形態1の水栓の表面側には撥水性を有するトップコート層5が形成されているため、ケイ酸や炭酸カルシウム等を含む水を弾き易く、 This is on the surface side of the faucet embodiment 1 because the top coat layer 5 having water repellency is formed, apt to play water containing silicic acid and calcium carbonate,
汚れとして付着しにくいことを意味する。 Means that the difficult adhesion as dirt.

【0041】さらに、「防汚性能」における「付きにくさ」については、「無機系汚れ」及び「有機系汚れ」のいずれについても、100回程度の初期においては差が見られるものの、それを超える長期試験においては差がなくなり、比較形態の水栓及び実施形態1の水栓で「×」であり、汚れがつきやすいという結果となった。 [0041] In addition, the "per difficulty" in "antifouling performance", for any "inorganic dirt" and "organic dirt" also, although the difference is observed in the order of 100 times the initial, it in long-term studies in excess is eliminated the difference is "×" in the faucet and the water faucet according to the first embodiment of the comparative embodiment was the result that dirt is likely month.
これは以下の「落としやすさ」により解消可能であれば問題とならない。 This is not a problem, if possible eliminated by "drop ease" below.

【0042】このため、「防汚性能」における「落としやすさ」について検討すると、比較形態の水栓では「無機系汚れ」及び「油性インク」が「×」であり、「有機系汚れ」は「△」であったのに対し、実施形態1の水栓では全て「○」の評価であった。 [0042] Therefore, it is when considering the "drop ease" in "antifouling", in the water faucet of comparative form "inorganic dirt" and "oil-based ink" is "×", "organic fouling" is while there was a "△", it was the evaluation of all the water faucet according to the first embodiment "○". このため、実施形態1 Therefore, Embodiment 1
の水栓では、ケイ酸や炭酸カルシウム等が析出したとしても、それらが表面に強固に付着しにくいことがわかる。 Of the faucet, as silicate and calcium carbonate precipitated, they seen to be less firmly attached to the surface. また、実施形態1の水栓では、トップコート層5が撥油性も有するため、石鹸カス、ぬめり乾燥物等の有機系の汚れが付着しても、それらが表面に強固に付着しにくいこともわかる。 Further, in the faucet embodiment 1, since the top coat layer 5 also has oil repellency, soap scum, also attached dirt organic such as slime dried product, also they can be difficult to firmly adhere to the surface Understand.

【0043】また、「耐久性」については、「表面硬度」において、比較形態の水栓では「◎」の評価であったのに対し、実施形態1の水栓では「△」の評価となった。 [0043] In addition, for the "durability", in "surface hardness", in the faucet of the comparative form while was the evaluation of the "◎", a rating of "△" in the water faucet according to the first embodiment It was. しかしながら、実施形態1の水栓は「スポンジ摩耗」及び「雑巾摩耗」ともに「○]の評価であり、実用上問題はない。 However, faucet embodiment 1 is an evaluation of the "sponge wear" and "rag wear" both "○], practically no problem.

【0044】また、発明者らの試験結果によれば、実施形態1の水栓では、トップコート層5を形成する加熱処理により、プライマ層4中のフッ素樹脂粒子4aとトップコート層5のテトラフルオロエチレン−パーフルオロアルキルビニルエーテル共重合体(PFA)とが融着し、密着性に優れた防汚層5となっていた。 Further, according to the inventors of the test results, the faucet embodiment 1, the heat treatment for forming the top coat layer 5, the primer layer 4 of a fluorine resin particles 4a and the top coat layer 5 tetra fluoroethylene - fused perfluoroalkyl vinyl ether copolymer (PFA) transgressions, had become excellent antifouling layer 5 adhesion.

【0045】さらに、実施形態1の水栓では、ニッケルめっき層2が母材1の表面に多少の凹凸を平滑化し、クロムめっき層3が耐蝕層の硬度を上げていた。 [0045] Furthermore, in the faucet embodiment 1, the nickel plating layer 2 is smooth some unevenness on the surface of the base 1, the chromium plating layer 3 had raised the hardness of the corrosion-resistant layer. そして、 And,
耐蝕層は、例えトップコート層5及びプライマ層4に傷が付いたとしても、BC6製の母材1が剥き出しとなることはなく、腐蝕を防止できることが想定される。 Corrosion-resistant layer, even with a flaw in the top coat layer 5 and the primer layer 4 example, never preform 1 made of BC6 is exposed, it is contemplated that prevents corrosion.

【0046】(評価2)プライマにフッ素樹脂粒子4a [0046] (Evaluation 2) fluorine resin particles 4a to the primary
が含まれている上記実施形態1の水栓と、プライマにフッ素樹脂粒子4aが含まれていない実施形態2の水栓とについて、碁盤目試験により、密着性の差を評価した。 And faucet Embodiment 1 that contains, for the faucet embodiment 2 does not contain the fluorine resin particles 4a to the primary, the cross-cut adhesion test was evaluated differences in adhesion.
ここで、実施形態2の水栓は、プライマにフッ素樹脂粒子4aが含まれていない点を除き、上記実施形態1と同一の製造方法で製造したものであり、同一の構成を有する。 Here, the faucet embodiment 2, except that does not contain fluorine resin particles 4a to the primary, which was manufactured in the first embodiment and the same manufacturing process, have the same configuration.

【0047】この結果、実施形態1の水栓は、実施形態2の水栓と比較して、トップコート層5が高い密着性を示した。 [0047] As a result, the faucet embodiment 1, as compared to the faucet embodiment 2, showing a top coat layer 5 is high adhesion. この理由は、図6に示すように、フッ素樹脂粒子4aとトップコート層5のPFAとが第2工程における加熱処理によって融着しているからであると考えられる。 This is because, as shown in FIG. 6, is considered that the PFA of the fluorine resin particles 4a and the top coat layer 5 is because being fused by the heat treatment in the second step.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】実施形態1の水栓に係り、製造中の部分断面図である。 [1] relates to the faucet embodiment 1 is a partial cross-sectional view of manufacturing.

【図2】実施形態1の水栓に係り、製造中の部分断面図である。 [2] relates to a faucet embodiment 1 is a partial cross-sectional view of manufacturing.

【図3】実施形態1の水栓に係り、製造中の部分断面図である。 [3] relates to a faucet embodiment 1 is a partial cross-sectional view of manufacturing.

【図4】実施形態1の水栓に係り、製造中の部分断面図である。 [4] relates to faucets embodiment 1 is a partial cross-sectional view of manufacturing.

【図5】実施形態1の水栓に係り、部分断面図である。 [5] relates to the faucet embodiment 1 is a partial cross-sectional view.

【図6】実施形態1の水栓に係り、拡大断面図である。 [6] relates to the faucet embodiment 1 is an enlarged cross-sectional view.

【符号の説明】 DESCRIPTION OF SYMBOLS

1…金属製母材(BC6) 4、5…防汚層(4…プライマ層、5…トップコート層) 4a…フッ素樹脂粒子 4b…金属粉末(アルミニウム粉末) 2、3…耐蝕層(2…ニッケルめっき層、3…クロムめっき層) 1 ... Metal base material (BC6) 4, 5 ... antifouling layer (4 ... primer layer, 5 ... topcoat layer) 4a ... fluororesin particles 4b ... metal powders (aluminum powder) 2,3 ... corrosion-resistant layer (2 ... nickel plating layer, 3 ... chromium plating layer)

───────────────────────────────────────────────────── フロントページの続き (72)発明者 阿原 真 愛知県常滑市鯉江本町5丁目1番地 株式 会社イナックス内 (72)発明者 松井 良平 奈良県大和郡山市今国府町6番2号 東邦 化成株式会社内 Fターム(参考) 2D060 AC01 BD01 ────────────────────────────────────────────────── ─── of the front page continued (72) inventor Awara true, Aichi Prefecture Tokoname Koiehon-cho 5-chome address 1 stock company in Inakkusu (72) inventor Ryohei Matsui Nara Prefecture Yamatokoriyama Imago-cho, No. 6 No. 2 Toho Chemical Industry Co., Ltd. in the F-term (reference) 2D060 AC01 BD01

Claims (10)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】水廻りに使用され、金属製母材の表面側に撥水性及び撥油性を有する防汚層が形成されていることを特徴とする水廻り金具。 1. A used in plumbing, metal matrix plumbing fitting, characterized in that the antifouling layer is formed having water repellency and oil repellency to the surface side of the.
  2. 【請求項2】母材は水栓を構成していることを特徴とする請求項1記載の水廻り金具。 2. A preform water around fitting according to claim 1, characterized in that it constitutes a faucet.
  3. 【請求項3】防汚層はフッ素樹脂により形成されていることを特徴とする請求項1又は2記載の水廻り金具。 3. The antifouling layer around water fitting according to claim 1 or 2, characterized in that it is formed by fluorine resin.
  4. 【請求項4】防汚層は母材の表面側にプライマ層を有し、該プライマ層にはフッ素樹脂粒子が混合されていることを特徴とする請求項3記載の水廻り金具。 4. antifouling layer has a primer layer on the surface side of the base material, the water around fitting according to claim 3, wherein the said primer layer, characterized in that the fluorine resin particles are mixed.
  5. 【請求項5】防汚層は母材の表面側にプライマ層を有し、該プライマ層には金属粉末が混合されていることを特徴とする請求項1、2、3又は4記載の水廻り金具。 5. antifouling layer has a primer layer on the surface side of the base material, the water of claim 1, 2, 3 or 4, wherein the said primer layer, wherein a metal powder is mixed around the bracket.
  6. 【請求項6】母材の表面と防汚層との間には耐蝕層が形成されていることを特徴とする請求項1、2、3、4又は5記載の水廻り金具。 6. The water around fitting according to claim 1, 2, 3, 4 or 5, wherein the corrosion-resistant layer is formed between the surface and the antifouling layer of the base material.
  7. 【請求項7】耐蝕層はニッケルめっき及びクロムめっきを含むことを特徴とする請求項6記載の水廻り金具。 7. A corrosion-resistant layer is water around fitting according to claim 6, characterized in that it comprises a nickel plating and chrome plating.
  8. 【請求項8】金属製母材の表面にニッケルめっき及びクロムめっきからなる耐蝕層を形成する第1工程と、 該耐蝕層上にプライマとフッ素樹脂とからなる防汚層を形成する第2工程とからなることを特徴とする水廻り金具の製造方法。 8. A second step of forming a first step of forming a corrosion-resistant layer of nickel plating and chrome plating on the surface of the metal base material, an antifouling layer composed of a primer and a fluororesin on the corrosion-resistant layer method of manufacturing plumbing fitting, characterized by comprising a.
  9. 【請求項9】プライマはフッ素樹脂粒子を含むことを特徴とする請求項8記載の水廻り金具の製造方法。 9. primer method of producing a water-around fitting according to claim 8, characterized by containing a fluorine resin particles.
  10. 【請求項10】プライマは金属粉末を含むことを特徴とする請求項8又は9記載の水廻り金具の製造方法。 10. A primer method of producing a water-around fitting according to claim 8 or 9, wherein the containing metal powder.
JP2000218147A 2000-07-19 2000-07-19 Water section fitting and its manufacturing method Pending JP2002030707A (en)