JP2001355131A - Polyester conjugated fiber - Google Patents

Polyester conjugated fiber

Info

Publication number
JP2001355131A
JP2001355131A JP2000178064A JP2000178064A JP2001355131A JP 2001355131 A JP2001355131 A JP 2001355131A JP 2000178064 A JP2000178064 A JP 2000178064A JP 2000178064 A JP2000178064 A JP 2000178064A JP 2001355131 A JP2001355131 A JP 2001355131A
Authority
JP
Japan
Prior art keywords
polyester
fiber
feeling
composite fiber
irregular
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2000178064A
Other languages
Japanese (ja)
Inventor
Yasuki Kobayashi
靖希 小林
Masahide Matsumura
正英 松村
Koichi Sato
晃一 佐藤
Original Assignee
Toray Ind Inc
東レ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toray Ind Inc, 東レ株式会社 filed Critical Toray Ind Inc
Priority to JP2000178064A priority Critical patent/JP2001355131A/en
Publication of JP2001355131A publication Critical patent/JP2001355131A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide a modified bimetal polyester composite fiber consisting of a polyester, being a side by side type conjugated fiber consisting of one component of a polypropyle terephthalate and another one of a polyethylene terephthalate, and having functionalities such as a dry feeling, light weighted feeling and water-absorbing property in addition to stretching property, soft feeling and an appearance having specific crimps by having a modified cross section. SOLUTION: This polyester conjugated fiber is characterized by consisting of a polyester, being a side by side type composite fiber consisting of one component of a polypropylene terephthalate and another one of a polyethylene terephthalate, and having that the cross sectional shape of the above composite fiber is the modified cross section.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION
【0001】[0001]
【発明の属する技術分野】本発明は、ポリエステルから
なる、一方がポリプロピレンテレフタレートであり、他
方がポリエチレンテレフタレートであるサイドバイサイ
ド型異形断面ポリエステル複合繊維に関し、さらに詳し
くは、高異形断面の毛細管現象を利用した吸水性にソフ
ト感のあるバイメタルによる捲縮発現が加わることで、
繊維間空隙がさらに多くなり、毛細管現象が格段に起こ
りやすくなり、吸水性が向上し、高異形断面による粗硬
感のないストレッチ性、ソフト感、ドライ感、軽量感、
吸水性等の機能性を有するポリエステル複合繊維に関す
る。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a side-by-side type irregularly shaped polyester composite fiber made of polyester, one of which is polypropylene terephthalate and the other is polyethylene terephthalate. More specifically, the invention utilizes a capillary phenomenon of a highly irregular cross section. By adding crimp expression by bimetal with soft feeling to water absorption,
The inter-fiber voids are further increased, the capillary phenomenon is much more likely to occur, the water absorption is improved, the stretchability without rough and hard feeling due to the high profile cross section, soft feeling, dry feeling, light weight feeling,
The present invention relates to a polyester composite fiber having functionality such as water absorption.
【0002】[0002]
【従来の技術】従来からポリエステル繊維を様々な天然
繊維のもつ風合いに近づけるための検討が数多く行わ
れ、特に付加価値の高い絹様の風合いに近づけるための
検討が多く、サイドバイサイド型複合による羊毛様繊維
を異形断面にすることで絹様の風合いが得られるため、
これによりサイドバイサイド型複合によるストレッチ性
付与に加え、他の機能を付与するための検討が行われて
いる。
2. Description of the Related Art Conventionally, many studies have been made to make polyester fibers approach the texture of various natural fibers, and many studies have been made to approach the texture of high value-added silk. Since silk-like texture can be obtained by making the fiber an irregular cross section,
Accordingly, studies have been made to provide other functions in addition to the stretchability provided by the side-by-side composite.
【0003】例えば、特開昭63−219628号公報
には、サイドバイサイド型複合繊維の繊維断面をW型と
し、特開平2−68311号公報には、サイドバイサイ
ド型複合繊維の繊維断面をL型とし、深みのある色と絹
様な風合いを有する繊維を得る方法が、また、特開平4
−214433号公報には、偏平サイドバイサイド型複
合繊維同士を混繊し、ふくらみと張りのある絹様織編物
を得る方法が開示されている。これらの提案によるサイ
ドバイサイド型複合繊維は確かに絹様な風合いをもつ織
編物をそれぞれ得ることができるが、高い吸水性を同時
に得られる織編物を得ることはできない。
For example, Japanese Patent Application Laid-Open No. 63-219628 discloses a W-shaped cross section of a side-by-side composite fiber, and Japanese Patent Application Laid-Open No. 2-68311 discloses an L-shaped cross section of a side-by-side composite fiber. A method for obtaining a fiber having a deep color and a silky texture is disclosed in
JP-A-214433 discloses a method of blending flat side-by-side type composite fibers to obtain a silk-like woven knitted fabric having swelling and tension. The side-by-side type composite fibers according to these proposals can certainly obtain woven or knitted fabrics having a silky texture, but cannot obtain woven or knitted fabrics capable of simultaneously obtaining high water absorption.
【0004】一方、ポリプロピレンテレフタレート繊維
は、伸長弾性回復率が優れ、ヤング率が低く、染色性が
良好で、化学的にも安定しており、特開昭52−532
0号公報や特開昭52−8124号公報などにみられる
ように単成分では古くから知られているが、複合および
異形断面化による捲縮特性、ドライ感、軽量感および吸
水性をもつ優れた織編物はなかった。
On the other hand, polypropylene terephthalate fiber has an excellent elongation elastic recovery rate, a low Young's modulus, good dyeability, and is chemically stable.
No. 0, JP-A-52-8124, etc., which have been known for a long time as a single component, but have excellent crimping properties, dryness, lightness and water absorption due to composite and irregular cross-sections. There were no woven or knitted fabrics.
【0005】[0005]
【発明が解決しようとする課題】本発明の目的は、上記
従来技術では達成できなかったストレッチ性、ソフト
感、捲縮性をもつ絹様な風合いに加え、ドライ感、軽量
感、吸水性等の機能性を有する異形バイメタルポリエス
テル複合繊維を提供することにある。
SUMMARY OF THE INVENTION The object of the present invention is to provide, in addition to the silky texture having stretchability, softness and crimpability, which could not be achieved by the above prior art, dryness, lightness, water absorption and the like. An object of the present invention is to provide a modified bimetallic polyester composite fiber having the above-mentioned functionality.
【0006】[0006]
【課題を解決するための手段】上記の目的を達成するた
め、本発明は以下の構成を採用する。すなわち、 (1)ポリエステルからなる、一方がポリプロピレンテ
レフタレートであり、他方がポリエチレンテレフタレー
トであるサイドバイサイド型複合繊維であって、該複合
繊維の断面形状が異形断面であることを特徴とするポリ
エステル複合繊維。 (2)前記異形断面の異形度が1.7〜6.0であるこ
とを特徴とする前記(1)記載のポリエステル複合繊
維。 (3)前記異形断面が3個以上の凹部を有する多葉断面
形状であることを特徴とする前記(1)または(2)に
記載のポリエステル複合繊維。 (4)複合繊維を構成するポリエステルのうち少なくと
も一方のポリエステルが共重合ポリエステルであり、そ
の共重合量が5〜15モル%であることを特徴とする前
記(1)〜(3)のいずれかに記載のポリエステル複合
繊維。
In order to achieve the above object, the present invention employs the following constitution. That is, (1) a polyester conjugate fiber which is a side-by-side conjugate fiber composed of polyester, one of which is polypropylene terephthalate and the other is polyethylene terephthalate, wherein the cross-sectional shape of the conjugate fiber is irregular. (2) The polyester composite fiber according to (1), wherein the degree of irregularity of the irregular cross section is 1.7 to 6.0. (3) The polyester composite fiber according to (1) or (2), wherein the irregular cross section has a multi-lobed cross-sectional shape having three or more concave portions. (4) Any one of the above (1) to (3), wherein at least one of the polyesters constituting the conjugate fiber is a copolymerized polyester, and the copolymerization amount is 5 to 15 mol%. Polyester conjugate fiber according to 1.
【0007】[0007]
【発明の実施の形態】以下、本発明をさらに詳細に説明
する。
BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in more detail.
【0008】本発明の異形バイメタルポリエステル複合
繊維は、ストレッチ性、ソフト感、捲縮性を得るため
に、ポリエステルからなり、一方がポリプロピレンテレ
フタレートであり、他方がポリエチレンテレフタレート
であるサイドバイサイド型複合繊維で構成されているも
のである。なお、十分な捲縮特性を発現させるために
は、上記一方のポリエステルと他方のポリエステルとの
複合比率は60:40〜40:60が好ましい。
The modified bimetallic polyester composite fiber of the present invention is composed of a polyester, one of which is polypropylene terephthalate and the other is polyethylene terephthalate, in order to obtain stretchability, softness and crimpability. Is what is being done. In order to exhibit sufficient crimp characteristics, the composite ratio of the one polyester and the other polyester is preferably from 60:40 to 40:60.
【0009】本発明で用いられるポリプロピレンテレフ
タレートとは、テレフタル酸を主たる酸成分とし、1,
3プロパンジオールを主たるグリコール成分として得ら
れるポリエステルである。
The polypropylene terephthalate used in the present invention refers to terephthalic acid as a main acid component,
Polyester obtained by using 3-propanediol as a main glycol component.
【0010】また、上記ポリプロピレンテレフタレート
の固有粘度は0.7以上1.6以下であることが好まし
い。0.7以上として捲縮発現を十分にして、ストレッ
チ性のある物を得るものである。また、固有粘度を1.
6以下として、ソフト感がより発揮されるものである。
より好ましくはポリプロピレンテレフタレートの固有粘
度は0.8以上1.4以下である。
The intrinsic viscosity of the polypropylene terephthalate is preferably 0.7 or more and 1.6 or less. When the ratio is 0.7 or more, the crimp expression is sufficiently obtained to obtain a stretchable material. In addition, the intrinsic viscosity is 1.
When it is 6 or less, a soft feeling is more exhibited.
More preferably, the intrinsic viscosity of polypropylene terephthalate is 0.8 or more and 1.4 or less.
【0011】一方、本発明で用いられるポリエチレンテ
レフタレートとは、テレフタル酸を主たる酸成分とし、
エチレングリコールを主たるグリコール成分として得ら
れるポリエステルであり、その固有粘度は0.45以上
0.7以下であることが好ましい。0.45以上とする
ことで、十分に捲縮発現が得られ、ストレッチ性のある
ものが得られる。また、固有粘度0.7以下とすること
で、ポリプロピレンテレフタレートとの粘度差が十分あ
り、期待した捲縮発現が得られ、ストレッチ性をはじめ
とする目的の機能を得ることができる。
On the other hand, the polyethylene terephthalate used in the present invention is terephthalic acid as a main acid component,
It is a polyester obtained by using ethylene glycol as a main glycol component, and its intrinsic viscosity is preferably 0.45 or more and 0.7 or less. When the content is 0.45 or more, sufficient crimping can be obtained, and a stretchable material can be obtained. When the intrinsic viscosity is 0.7 or less, there is a sufficient difference in viscosity from polypropylene terephthalate, the expected crimping can be obtained, and the intended functions such as stretchability can be obtained.
【0012】また、本発明の異形バイメタルポリエステ
ル複合繊維は、より捲縮特性を発現させるために、複合
繊維を構成するポリエステルのうち少なくとも一方のポ
リマに共重合ポリエステルを含有してもよい。なお、耐
熱性の点から、共重合量は5モル%以上15モル%以下
であることが好ましい。捲縮発現と製糸性をよりよくす
るには共重合量が7〜13モル%であることがより好ま
しい。また、必要に応じて艶消し剤、消臭剤、難燃剤、
糸摩擦低減剤、抗酸化剤、着色顔料等として無機微粒子
や有機化合物を必要に応じて添加することができる。
Further, the modified bimetallic polyester conjugate fiber of the present invention may contain a copolymerized polyester in at least one of the polyesters constituting the conjugate fiber in order to develop more crimping properties. From the viewpoint of heat resistance, the copolymerization amount is preferably 5 mol% or more and 15 mol% or less. The copolymerization amount is more preferably from 7 to 13 mol% in order to improve the crimping and the spinning property. In addition, matting agents, deodorants, flame retardants,
If necessary, inorganic fine particles and organic compounds can be added as a yarn friction reducing agent, an antioxidant, a coloring pigment, and the like.
【0013】共重合成分としては、芳香族ジカルボン酸
類、スルホン酸基を有する芳香族ジカルボン酸成分およ
びその誘導体、リン酸基を有する芳香族ジカルボン酸成
分およびその誘導体、脂肪族ジカルボン酸類、脂肪族ジ
オール類、脂環式ジオール類、芳香族ジオール類あるい
は、それにエチレンオキサイド等を添加した高分子ジオ
ール類などを用いることができ、具体的には、イソフタ
ル酸、アジピン酸、ナフタリン−2,6−ジカルボン
酸、セバシン酸、5−ナトリウムスルホイソフタル酸、
5−ナトリウムスルホテレフタル酸、5−カリウムスル
ホイソフタル酸、5−カリウムスルホテレフタル酸、5
−リチウムスルホイソフタル酸、3,5−ジ(カルボ−
β−ヒドロキシエトキシ)ベンゼンスルホン酸ナトリウ
ム、3,5−ジ(カルボ−β−ヒドロキシエトキシ)ベ
ンゼンスルホン酸カリウム、3,5−ジ(カルボ−β−
ヒドロキシエトキシ)ベンゼンスルホン酸リチウム、5
−ナトリウムスルホイソフタル酸ジメチル、5−カリウ
ムスルホイソフタル酸ジメチル、5−リチウムスルホイ
ソフタル酸ジメチル、1,4−ブタンジオール、ジエチ
レングリコール、トリメチレングリコール、シクロヘキ
サンジオール、ビスフェノールA、ビスフェノールスル
ホン、ビスフェノールAのEO付加物、ビスフェノール
スルホンのEO付加物等を好ましく用いることができ
る。また、ポリエチレングリコール等を併用しても差し
支えない。より好ましくは、ポリエステルを高収縮化す
るため、イソフタル酸とビスフェノールAのEO付加物
を併用することが好ましい。
The copolymerization components include aromatic dicarboxylic acids, aromatic dicarboxylic acid components having sulfonic acid groups and derivatives thereof, aromatic dicarboxylic acid components having phosphoric acid groups and derivatives thereof, aliphatic dicarboxylic acids, and aliphatic diols. , Alicyclic diols, aromatic diols, or high molecular diols to which ethylene oxide or the like is added, and specific examples thereof include isophthalic acid, adipic acid, and naphthalene-2,6-dicarboxylic acid. Acid, sebacic acid, 5-sodium sulfoisophthalic acid,
5-sodium sulfoterephthalic acid, 5-potassium sulfoisophthalic acid, 5-potassium sulfoterephthalic acid, 5
-Lithium sulfoisophthalic acid, 3,5-di (carbo-
sodium β-hydroxyethoxy) benzenesulfonate, potassium 3,5-di (carbo-β-hydroxyethoxy) benzenesulfonate, 3,5-di (carbo-β-
(Hydroxyethoxy) lithium benzenesulfonate, 5
-EO addition of dimethyl sodium sulfoisophthalate, dimethyl 5-potassium sulfoisophthalate, dimethyl 5-lithium sulfoisophthalate, 1,4-butanediol, diethylene glycol, trimethylene glycol, cyclohexanediol, bisphenol A, bisphenol sulfone, bisphenol A EO adducts of bisphenolsulfone and the like can be preferably used. Further, polyethylene glycol or the like may be used in combination. More preferably, an EO adduct of isophthalic acid and bisphenol A is preferably used in order to increase the shrinkage of the polyester.
【0014】さらにまた、本発明の効果を発現するため
に、本発明においては、異形バイメタルポリエステル複
合繊維を構成する複合繊維が異形断面であることを特徴
とするものである。さらに、本発明の複合繊維におい
て、十分な効果を発現するには上記異形断面の異形度が
1.7〜6.0であることが好ましい。異形度を1.7
以上にすることによって、繊維単糸間の空隙が増し、吸
水性が高くなる。また、空隙が多くなることで、軽量感
を付与することもできるのである。ただし、あまり異形
度を大きくすると繊維が割れたり、フィブリル化が起こ
り、製織性不良や製品品位の低下を招くため、異形度は
6.0以下とすることが好ましい。吸水性、軽量感の効
果をさらに発現し、かつ製織性を維持するためには、異
形度は2.0〜4.0の範囲がより好ましい。なお、本
発明でいう異形度は以下の方法によって求めたものであ
る。
Furthermore, in order to exhibit the effects of the present invention, the present invention is characterized in that the conjugate fibers constituting the bimetallic polyester composite fibers have an irregular cross section. Furthermore, in the conjugate fiber of the present invention, the irregularity of the irregular cross section is preferably 1.7 to 6.0 in order to exhibit a sufficient effect. 1.7 degree of irregularity
By doing so, the voids between the single fiber fibers increase, and the water absorption increases. Further, by increasing the number of voids, it is possible to impart a lightweight feeling. However, if the degree of irregularity is too large, the fibers may be broken or fibrillated, resulting in poor weaving or deterioration in product quality. Therefore, the degree of irregularity is preferably 6.0 or less. In order to further exhibit the effects of water absorption and lightness and to maintain the weaving property, the degree of irregularity is more preferably in the range of 2.0 to 4.0. The degree of irregularity referred to in the present invention is determined by the following method.
【0015】(異形度)=L1/L2 ただし、L1:繊維横断面の外接円の直径 L2:繊維横断面の内接円の直径 さらに、本発明の異形バイメタルポリエステル複合繊維
において、ドライ感、軽量感および吸水性を付与するた
めに、繊維の断面形状が多葉断面形状をした異形断面で
あることが好ましい。十分なドライ感、軽量感および吸
水性を付与するには3〜6個の凹部をもつ多葉断面形状
とすることがより好ましい。断面形状の凹部が3〜6個
の場合、繊維単糸間に形成される空隙が十分にあり、毛
細管現象による吸水性および繊維単糸間の空隙による軽
量感や多葉断面化によるドライ感を十分発現させること
ができる。
(Deformation degree) = L1 / L2 where L1: diameter of circumscribed circle of fiber cross section L2: diameter of inscribed circle of fiber cross section Further, in the modified bimetallic polyester composite fiber of the present invention, dry feeling and light weight are obtained. In order to give a feeling and water absorption, it is preferable that the cross-sectional shape of the fiber is an irregular cross-section having a multi-lobed cross-sectional shape. In order to impart sufficient dry feeling, light weight feeling and water absorption, it is more preferable to have a multi-leaf cross-sectional shape having 3 to 6 concave portions. When there are three to six concave portions in the cross-sectional shape, there are sufficient voids formed between the fiber single yarns, and the water absorption due to the capillary phenomenon and the lightness due to the voids between the fiber single yarns and the dry feeling due to the multi-leaf cross section are provided. It can be sufficiently expressed.
【0016】本発明の効果をより発現するために、上記
断面形状に加え、凹部の深さが図1に示すように隣接す
る凸部間の接線A、凹部の最深部と接線Aの垂線Bと
し、その比率A/Bが2.0以上であることが好まし
い。より好ましくは3.5以上である。
In order to further exhibit the effects of the present invention, in addition to the above-described cross-sectional shape, the depth of the concave portion is, as shown in FIG. 1, a tangent A between adjacent convex portions, and a perpendicular line B between the deepest portion of the concave portion and the tangential line A. And the ratio A / B is preferably 2.0 or more. More preferably, it is 3.5 or more.
【0017】本発明の異形バイメタルポリエステル複合
繊維の製造方法としては、ポリプロピレンテレフタレー
トとポリエチレンテレフタレートを同一紡糸温度にし、
融解しサイドバイサイド型に貼り合わせ、複合繊維を得
る方法で製造可能である。異形断面形状を得る紡糸方法
としては、口金吐出孔を任意の形状とし、任意の紡糸速
度にて巻き取ることで製造可能である。巻取った原糸は
任意の倍率で延伸することによって、本発明の効果を発
現する複合繊維を得ることができるが、本発明の製造方
法はこれに限った物ではない。
In the method for producing the modified bimetallic polyester composite fiber of the present invention, polypropylene terephthalate and polyethylene terephthalate are brought to the same spinning temperature,
It can be manufactured by a method of melting and bonding to a side-by-side type to obtain a composite fiber. As a spinning method for obtaining an irregular cross-sectional shape, the spinneret can be manufactured by forming a die discharge hole into an arbitrary shape and winding it at an arbitrary spinning speed. By stretching the wound yarn at an arbitrary magnification, a conjugate fiber exhibiting the effects of the present invention can be obtained, but the production method of the present invention is not limited to this.
【0018】本発明の異形バイメタルポリエステル複合
繊維は、他の繊維と混繊することによって、別の特性も
付与できる。例えば、染色性の異なる繊維と混繊するこ
とで杢調が得られたり、収縮特性の異なる繊維と混繊す
ることでふくらみ感が得られる。なお、混繊方法として
は、1つの口金から同時に製糸する紡糸混繊法、延伸工
程で合糸して巻き取る後混繊法が挙げられる。
The modified bimetallic polyester composite fiber of the present invention can be imparted with other properties by blending with another fiber. For example, a heather tone can be obtained by mixing with fibers having different dyeing properties, or a swelling feeling can be obtained by mixing with fibers having different shrinkage characteristics. Examples of the fiber mixing method include a spinning fiber mixing method in which yarns are simultaneously formed from a single die, and a fiber mixing method after combining and winding in a stretching step.
【0019】[0019]
【実施例】以下、実施例により、本発明をより詳細に説
明する。なお、実施例中の各特性値は次の方法で求めた
ものである。 A.固有粘度 オルトクロロフェノール中(25℃)で測定した値であ
る。 B.吸水性 バイレック法で長さ12cm×幅1cmの短冊状サンプ
ルの下端を20±2℃の蒸留水中に浸漬し、10分後の
吸水高さ(cm)を測定した。 C.捲縮数 100℃の沸騰水中で15分間処理し、単糸1cm間の
山の数を測定した。 D.風合い特性(ドライ感、軽量感、ストレッチ性、ソ
フト感) 各項目とも、試料を基準試料との一対比較による官能試
験を実施し、「極めて優れている」は○○、「優れてい
る」は○、「普通」は△、「劣っている」は×の4段階
評価で示した。なお、基準試料にはポリエチレンテレフ
タレートからなる56dtex−12filの丸断面糸
の延伸糸を用いて、上記試料と同様に製織、加工を施し
たものを用い、これを「劣っている:×」とした。 E.操業性 各水準(各200本)を糸加工した際の糸切れやタルミ
の発生状況から評価した。
The present invention will be described in more detail with reference to the following examples. Each characteristic value in the examples was obtained by the following method. A. Intrinsic viscosity It is a value measured in orthochlorophenol (25 ° C). B. Water Absorbency The lower end of a strip sample having a length of 12 cm and a width of 1 cm was immersed in distilled water at 20 ± 2 ° C. by a birec method, and the water absorption height (cm) after 10 minutes was measured. C. The number of crimps was treated in boiling water at 100 ° C. for 15 minutes, and the number of peaks between 1 cm of single yarns was measured. D. Feeling characteristics (dry feeling, light feeling, stretchability, soft feeling) For each item, a sensory test was performed by comparing the sample with the reference sample, and "very good" was XX, and "excellent" was 、, “normal” was indicated by Δ, and “inferior” was indicated by four-point evaluation of ×. In addition, what was woven and processed in the same manner as the above-mentioned sample using a drawn yarn having a round cross section of 56 dtex-12fil made of polyethylene terephthalate was used as a reference sample, and this was evaluated as “poor: ×”. . E. FIG. Operability Evaluated based on the occurrence of yarn breakage and tarmi when each level (200 yarns) was processed.
【0020】 糸切れ、タルミ発生率5%未満 ○ 糸切れ、タルミ発生率5%以上10%未満 △ 糸切れ、タルミ発生率10%以上 × 実施例1〜3および比較例1 固有粘度が1.41のイソフタル酸を10モル%共重合
した共重合ポリプロピレンテレフタレートと固有粘度が
0.56のポリエチレンテレフタレートを複合比率5
0:50でサイドバイサイド型に複合し、図1に示す繊
維断面となるような異形吐出孔の口金から紡糸速度18
00m/分で引き取った後、延伸して巻き取った。得ら
れた延伸糸特性を表1に示す。
Thread breakage, Talmi generation rate less than 5% ○ Thread breakage, Talmi generation rate of 5% or more and less than 10% △ Thread breakage, Talmi generation rate of 10% or more × Examples 1-3 and Comparative Example 1 Intrinsic viscosity is 1. A copolymerized polypropylene terephthalate obtained by copolymerizing 10% by mole of isophthalic acid of 41 with polyethylene terephthalate having an intrinsic viscosity of 0.56;
At a ratio of 0:50, the composite was formed into a side-by-side type, and the spinning speed of 18 from the die of the irregularly shaped discharge hole having the fiber cross section shown in FIG.
After drawing at 00 m / min, it was stretched and wound up. Table 1 shows the obtained drawn yarn characteristics.
【0021】次いで、得られた延伸糸を用いて平織物を
織った。得られた織物の特性を表1に示す。
Next, a plain fabric was woven using the obtained drawn yarn. Table 1 shows the properties of the obtained woven fabric.
【0022】実施例1は、十分な捲縮を有しており、極
めて優れたストレッチ性、かつ断面を高異形化すること
により、ドライ感、軽量感および吸水性に優れたソフト
感のある織物が得られた。
In Example 1, a fabric having a sufficient crimp, an extremely excellent stretch property and a highly deformed cross-section to provide a soft feeling with excellent dry feeling, light weight feeling and water absorption. was gotten.
【0023】実施例2は、十分な捲縮を有することによ
り、優れたストレッチ性、かつ断面を高異形化すること
により、ドライ感、軽量感および吸水性の極めて優れた
ソフト感のある織物が得られたが、異形度がやや高く、
若干フィブリル化が見られた。
In Example 2, a fabric having a sufficient crimp, excellent stretchability, and a highly deformed cross-section provides a soft feeling of dryness, lightness and water absorbency. It was obtained, but the irregularity was slightly higher,
Some fibrillation was observed.
【0024】実施例3は、本発明の効果を発現するには
非常に適した捲縮を有し、かつ繊維断面であり、極めて
優れたストレッチ性、ドライ感、軽量感および吸水性が
あり、ソフト感のあるものであった。さらに、操業性に
も問題はなかった。
Example 3 has a crimp and a fiber cross section which are very suitable for exhibiting the effects of the present invention, and has extremely excellent stretchability, dry feeling, light weight feeling and water absorption. It had a soft feeling. Furthermore, there was no problem in operability.
【0025】比較例1は、捲縮を有することにより、優
れたストレッチ性があり、ソフト感を有するが、断面形
状が丸であるため、ドライ感、軽量感および吸水性がな
いものであった。
Comparative Example 1 had excellent stretchability and softness due to crimping, but lacked dryness, lightness, and water absorption because the cross-sectional shape was round. .
【0026】比較例2は、高異形断面であり、ドライ
感、軽量感および、吸水性を有するが、サイドバイサイ
ド型バイメンタル糸でないために捲縮が発現せず、スト
レイッチ性がなく、PETであるためソフト感がないも
のであった。
Comparative Example 2 has a highly irregular cross section and has a dry feeling, a light weight feeling, and water absorbency, but does not exhibit crimp, is not stretchy, and is a PET because it is not a side-by-side type vital yarn. Therefore, there was no soft feeling.
【0027】実施例4〜7 イソフタル酸とビスフェノールAのEO付加物を併用し
た共重合量を表2に示す通り変更した共重合ポリプロピ
レンテレフタレートと固有粘度が0.50のポリエチレ
ンテレフタレートを複合比率50:50でサイドバイサ
イド型に複合し、異形吐出孔の口金から紡糸速度180
0m/分で引き取った後、延伸して巻き取った。得られ
た延伸糸特性を表2に示した。次いで得られた延伸糸を
用いて織物を織り、得られた織物の特性を表2に示す。
Examples 4 to 7 Copolymerized polypropylene terephthalate in which the copolymerization amount of isophthalic acid and bisphenol A EO adduct was used in combination as shown in Table 2 was mixed with polyethylene terephthalate having an intrinsic viscosity of 0.50 in a composite ratio of 50: The spinning speed is combined with the side-by-side type at 50, and the spinning speed is 180
After drawing at 0 m / min, the film was stretched and wound up. Table 2 shows the obtained drawn yarn characteristics. Next, a woven fabric is woven using the obtained drawn yarn, and the properties of the obtained woven fabric are shown in Table 2.
【0028】実施例4は、優れたストレッチ性、ソフト
感があり、繊維断面を高異形化することで、極めて優れ
たドライ感、軽量感および吸水性を有するが、共重合量
が若干少なく、捲縮がやや低いものとなった。
Example 4 has excellent stretchability and softness, and has extremely excellent dryness, lightness and water absorbability by highly deforming the fiber cross section. The crimp was slightly lower.
【0029】実施例5は、十分な捲縮を有することによ
り、極めて優れたストレッチ性、ソフト感、繊維断面を
高異形化することにより、優れたドライ感、軽量感およ
び吸水性のあるものとなった。
In Example 5, a material having an extremely excellent stretchability, a soft feeling and a highly deformed fiber cross section by having a sufficient crimp, thereby having an excellent dry feeling, light weight feeling and water absorbability. became.
【0030】実施例6は、本発明の効果をより発現する
のに適した捲縮を有し、繊維断面を高異形化することに
より、極めて優れたストレッチ性、ソフト感、ドライ
感、軽量感および吸水性のあるものであった。更に、操
業性に問題はなかった。
Example 6 has a crimp suitable for further exhibiting the effects of the present invention, and has an extremely excellent stretchability, softness, dryness, and lightness by deforming the fiber cross section to a high degree. And water-absorbent. Furthermore, there was no problem in operability.
【0031】実施例7は、十分な捲縮を有し、繊維断面
形状を高異形化することにより、極めて優れたストレッ
チ性、ソフト感、ドライ感、軽量感および吸水性のある
ものとなったが、共重合量がやや多いため、操業性がや
や低いものとなった。
Example 7 had sufficient crimp and highly deformed fiber cross-sectional shape, resulting in extremely excellent stretchability, softness, dryness, lightness and water absorption. However, the operability was somewhat low because the copolymerization amount was rather large.
【0032】[0032]
【表1】 [Table 1]
【0033】[0033]
【表2】 [Table 2]
【0034】[0034]
【発明の効果】本発明によれば、従来のサイドバイサイ
ド型の複合繊維を織編物とした際の捲縮の特異な外観に
加え、ストレッチ性、ソフト感、吸水性および軽量感を
持つ異形バイメタルポリエステル繊維の織編物を得るこ
とができる。また、この織編物は衣料用途をはじめ、様
々な用途に好適であり、優れた品位を持つ織編物を提供
するばかりでなく、ドライタッチおよび軽量感といった
機能性のある原糸を提供することが可能である。
According to the present invention, in addition to the specific appearance of crimping when a conventional side-by-side type conjugate fiber is formed into a woven or knitted fabric, the modified bimetallic polyester has stretchability, softness, water absorption and light weight. A woven or knitted fabric of fibers can be obtained. In addition, this woven or knitted fabric is suitable for various uses, including apparel applications, and not only provides a woven or knitted fabric having excellent quality, but also provides a functional yarn such as dry touch and lightweight feeling. It is possible.
【図面の簡単な説明】[Brief description of the drawings]
【図1】ポリエステル(a)、(b)からなる、本発明
の異型断面繊維の一例を示す横断面図である。
FIG. 1 is a cross-sectional view showing an example of an irregular cross-section fiber of the present invention composed of polyesters (a) and (b).
───────────────────────────────────────────────────── フロントページの続き Fターム(参考) 4L041 AA08 BA02 BA05 BA09 BA38 BA60 BC02 BD14 CA06 CA08 CA14 DD01 DD04 DD10 DD15 ──────────────────────────────────────────────────続 き Continued on the front page F term (reference) 4L041 AA08 BA02 BA05 BA09 BA38 BA60 BC02 BD14 CA06 CA08 CA14 DD01 DD04 DD10 DD15

Claims (4)

    【特許請求の範囲】[Claims]
  1. 【請求項1】ポリエステルからなる、一方がポリプロピ
    レンテレフタレートであり、他方がポリエチレンテレフ
    タレートであるサイドバイサイド型複合繊維であって、
    該複合繊維の断面形状が異形断面であることを特徴とす
    るポリエステル複合繊維。
    1. A side-by-side composite fiber comprising polyester, one of which is polypropylene terephthalate and the other is polyethylene terephthalate,
    A polyester conjugate fiber, wherein the cross-sectional shape of the conjugate fiber is irregular.
  2. 【請求項2】前記異形断面の異形度が1.7〜6.0で
    あることを特徴とする請求項1記載のポリエステル複合
    繊維。
    2. The polyester composite fiber according to claim 1, wherein the degree of irregularity of the irregular cross section is 1.7 to 6.0.
  3. 【請求項3】前記異形断面が3個以上の凹部を有する多
    葉断面形状であることを特徴とする請求項1または2に
    記載のポリエステル複合繊維。
    3. The polyester composite fiber according to claim 1, wherein the irregular cross section has a multi-lobed cross section having three or more concave portions.
  4. 【請求項4】複合繊維を構成するポリエステルのうち少
    なくとも一方のポリエステルが共重合ポリエステルであ
    り、その共重合量が5〜15モル%であることを特徴と
    する請求項1〜3のいずれか1項に記載のポリエステル
    複合繊維。
    4. The polyester according to claim 1, wherein at least one of the polyesters constituting the conjugate fiber is a copolymerized polyester, and the copolymerization amount is 5 to 15 mol%. Item 12. The polyester composite fiber according to item 1.
JP2000178064A 2000-06-14 2000-06-14 Polyester conjugated fiber Pending JP2001355131A (en)