JP2001207077A - Pearl gloss pigment - Google Patents

Pearl gloss pigment

Info

Publication number
JP2001207077A
JP2001207077A JP2000017547A JP2000017547A JP2001207077A JP 2001207077 A JP2001207077 A JP 2001207077A JP 2000017547 A JP2000017547 A JP 2000017547A JP 2000017547 A JP2000017547 A JP 2000017547A JP 2001207077 A JP2001207077 A JP 2001207077A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
pearl
gloss
pigment
metal
high
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2000017547A
Other languages
Japanese (ja)
Inventor
Akiyoshi Inubushi
Tomohiro Tanaka
昭嘉 犬伏
智博 田中
Original Assignee
Otsuka Chem Co Ltd
大塚化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To obtain a pearl gloss pigment, using a specific boehmite as a base material in place of a mica flake, thin and uniform, having a large average aspect ratio, as colorless and transparent as possible as it is, having a high temperature resistance and characteristics of high mechanical strength, and the like, and having a low precipitation property. SOLUTION: This pearl gloss pigment is a flake boehmite containing an alkali metal or an alkaline earth metal covered with a metal oxide.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は真珠光沢顔料に関する。 The present invention relates to relates to a pearlescent pigment. 詳しくは、アルカリ金属又はアルカリ土類金属含有板状ベーマイトに金属酸化物が被覆されたことを特徴とする真珠光沢顔料に関する。 More particularly, to pearlescent pigments, characterized in that the metal oxide is coated on an alkali metal or alkaline earth metal-containing plate-like boehmite.

【0002】 [0002]

【従来の技術】従来より、真珠光沢顔料としては、薄片状の基材、例えば雲母片等に屈折率の大きな金属酸化物、例えば酸化チタン等を被覆した顔料が知られている(特開平4−249584号公報、特公平5−3646 Conventionally, as a pearlescent pigment, flake-form substrates, for example large metal oxide having a refractive index in the mica flakes or the like, for example, pigments coated with titanium oxide and the like are known (JP-A-4 -249584, JP fair 5-3646
3号公報等)。 3 JP, etc.).

【0003】 [0003]

【発明が解決しようとする課題】しかし、これらのように基材に雲母フレークを使用した真珠光沢顔料は、基材が天然物であるため品質が安定せず、また不純物として鉄を含有するため白色度に限界があり、更には表面平滑性に劣るため真珠光沢の光輝感及び発色も不十分であるという問題があった。 [0006] However, pearlescent pigments using these mica flakes to the substrate as, without quality stable because the substrate is a natural product, also because they contain iron as an impurity There is a limit to the degree of whiteness, there is a problem that more glitter and coloring pearlescent have poor surface smoothness is insufficient.

【0004】そこで、雲母フレークに代わる基材として、厚みが薄く且つ均一で、平均アスペクト比が大きく、それ自体は極力無色透明で、高温耐熱性を有しており、且つ機械的強度が高い等の特性を有するものが望まれている。 [0004] Therefore, as a substrate in place of mica flakes, the thickness is a thin and uniform, large average aspect ratio, it itself is minimized colorless and transparent, has a high-temperature heat resistance, and mechanical strength such as high having a characteristic is desired. かかる要求に対して、基材として酸化チタンを含有する薄片状酸化アルミニウムが提案されている(特開平9−77512号公報)。 For such requirements, flaky aluminum oxide containing titanium oxide has been proposed as a substrate (JP-A-9-77512). このものは、前記の諸特性を満足するものであるが、顔料用途に使用する場合には沈降してしまい取扱に不便であるという問題を有している。 This thing is those satisfying the properties described above, has a problem that when used in pigment applications is inconvenient in handling will be settled.

【0005】本発明の課題は、上記のような問題点に鑑み、雲母フレークに代わる基材として特定のベーマイトを用いることにより、厚みが薄く且つ均一で、平均アスペクト比が大きく、それ自体は極力無色透明で、高温耐熱性を有しており、且つ機械的強度が高い等の特性を有すると共に、沈降性の少ない真珠光沢顔料を提供することにある。 An object of the present invention has been made in view of the above problems, by using a specific boehmite as a substrate in place of mica flakes, the thickness is a thin and uniform, large average aspect ratio itself as much as possible colorless and transparent, it has a high-temperature resistant, and the mechanical strength has characteristics of high such as to provide a less pearlescent pigment of precipitated.

【0006】 [0006]

【課題を解決するための手段】本発明は、アルカリ金属又はアルカリ土類金属含有板状ベーマイトに金属酸化物が被覆されたことを特徴とする真珠光沢顔料に係る。 SUMMARY OF THE INVENTION The present invention relates to a pearlescent pigment, wherein the metal oxide is coated on an alkali metal or alkaline earth metal-containing plate-like boehmite. 本発明の真珠光沢顔料は、従来の真珠光沢顔料と比較して、厚みが薄く且つ均一で、平均アスペクト比が大きく、沈降性が少ないという優れた特徴を有するものである。 Pearlescent pigments of the present invention, as compared with the conventional pearlescent pigment, thickness a thin and uniform, large average aspect ratio, and has an excellent feature that less sedimentation. 本発明の真珠光沢顔料の粒子形状は、通常、平均長径1〜30μm、平均厚み0.1〜1μm、平均アスペクト比20以上であり、好ましくは平均長径5〜25μ Particle shape of the pearlescent pigments of the present invention is generally an average diameter 1 to 30 [mu] m, an average thickness of 0.1 to 1 [mu] m, and an average aspect ratio of 20 or more, preferably having an average major axis 5~25μ
m、平均厚み0.1〜0.3μm、平均アスペクト比30 m, the average thickness of 0.1 to 0.3 [mu] m, an average aspect ratio of 30
以上がよい。 More than is good. 尚、平均アスペクト比の上限は通常300 The upper limit of the average aspect ratio is typically 300
程度である。 It is the degree.

【0007】 [0007]

【発明の実施の形態】本発明の真珠光沢顔料に使用する基材は、アルカリ金属又はアルカリ土類金属を含有する板状ベーマイトである。 The substrate used for the pearlescent pigments of the present invention DETAILED DESCRIPTION OF THE INVENTION is a plate-like boehmite containing an alkali metal or alkaline earth metal. かかる板状ベーマイトとしては、板状ベーマイトの層間にアルカリ金属又はアルカリ土類金属がイオンの状態で挿入されているものが知られている。 Such tabular boehmite, alkali metal or alkaline earth metal are known which are inserted in a state of ions between layers of plate boehmite. 例えば、アルカリ金属を含む化合物(アルカリ金属化合物)又はアルカリ土類金属を含む化合物(アルカリ土類金属化合物)と、水酸化アルミニウム、及び水とを含む原料を加圧し、且つ150〜300℃の温度で加熱することにより得られる反応生成物から、反応生成物に残留する余剰のアルカリ金属化合物やアルカリ土類金属化合物を除去することによりアルカリ金属又はアルカリ土類金属を含有する板状ベーマイトが得られる(特願平10−261425号参照)。 For example, compounds containing alkali metals and (alkali metal compound) or an alkaline earth compound containing a metal (alkaline earth metal compound), aluminum hydroxide, and pressurizes the material comprising water, and a temperature of 150 to 300 ° C. from in the reaction product obtained by heating, plate boehmite containing an alkali metal or alkaline earth metal is obtained by removing the excess alkali metal compound or an alkaline earth metal compound remaining in the reaction product (refer to Japanese Patent Application No. 10-261425).

【0008】本発明の真珠光沢顔料の基材として用いるアルカリ金属又はアルカリ土類金属を含有する板状ベーマイトは、通常のベーマイトに比較して均一微細な形状を有すると共に、金属酸化物の被覆性が良好で、真珠光沢顔料とした際の発色性に優れるという優れた効果を奏するものである。 [0008] plate boehmite containing an alkali metal or alkaline earth metal is used as the base material of the pearlescent pigments of the present invention, with compared to the conventional boehmite having a uniform fine shape, coverage of the metal oxide a good, in which an excellent effect of being excellent in coloring property as a pearlescent pigment.

【0009】アルカリ金属の具体例としては、リチウム、ナトリウム、カリウム、ルビジウム、セシウム、フランシウム等が挙げられるが、好ましくはナトリウム、 [0009] Specific examples of the alkali metals, lithium, sodium, potassium, rubidium, cesium, and francium, and the like, preferably sodium,
カリウムがよい。 Potassium is good. また、アルカリ金属化合物としては、 As the alkali metal compound,
水酸化ナトリウム、水酸化カリウム等の水酸化物、酸化ナトリウム、酸化カリウム、酸化リチウム等の酸化物、 Sodium hydroxide, hydroxides such as potassium hydroxide, sodium oxide, potassium oxide, oxides such as lithium oxide,
塩化ナトリウム、塩化カリウム等の塩化物、炭酸ナトリウム、炭酸カリウム等の炭酸化合物、硝酸カリウム、硝酸ナトリウム等の硝酸塩、リン酸ナトリウム、リン酸カリウム等のリン酸塩および酢酸塩や蟻酸塩を含む有機酸塩等あるいはそれらの水和物が挙げられる。 Sodium, chlorides such as potassium chloride, sodium carbonate, carbonate compounds such as potassium carbonate, potassium nitrate, nitrates such as sodium nitrate, sodium phosphate, an organic acid containing a phosphate and acetate or formate salts such as potassium phosphate salts or include their hydrates.

【0010】アルカリ土類金属の具体例としては、ベリリウム、マグネシウム、カルシウム、ストロンチウム、 [0010] Specific examples of the alkali earth metals are beryllium, magnesium, calcium, strontium,
バリウム、ラジウム等が挙げられるが、好ましくは、カルシウム、ストロンチウム、バリウムがよい。 Barium, but radium, etc., preferably, calcium, strontium, good barium. また、アルカリ土類金属含有化合物の具体例としては、水酸化カルシウム、水酸化ストロンチウム、水酸化バリウム等のアルカリ土類金属の水酸化物、酸化カルシウム、酸化ストロンチウム、酸化バリウム等の酸化物、塩化カルシウム、塩化ストロンチウム、塩化バリウム等の塩化物、炭酸カルシウム、炭酸ストロンチウム、炭酸バリウム等の炭酸化合物、硝酸カルシウム、硝酸ストロンチウム、硝酸バリウム等の硝酸塩、リン酸カルシウム等のリン酸塩および酢酸塩や蟻酸塩を含む有機酸塩等あるいはそれらの水和物が挙げられる。 Specific examples of the alkaline earth metal-containing compounds, calcium hydroxide, strontium hydroxide, alkaline earth metal hydroxides such as barium hydroxide, calcium oxide, strontium oxide, oxides such as barium oxide, chloride calcium, strontium chloride, and barium chloride, calcium carbonate, strontium carbonate, carbonate compounds such as barium carbonate, calcium nitrate, strontium nitrate, nitrates such as barium nitrate, phosphate and acetate and formate salts of calcium phosphate organic acid salts or their hydrates, including and the like.

【0011】本発明でアルカリ金属又はアルカリ土類金属を含有する板状ベーマイトの被覆に用いる金属酸化物としては、屈折率の大きな金属酸化物又はその含水物を好ましく用いることができ、酸化チタン、酸化ジルコニウム、酸化錫、チタン酸コバルト、リチウムコバルトチタネート、ニッケルチタネート、チタン酸鉄、酸化鉄及びこれらの含水物を例示できる。 [0011] As the metal oxide used for the covering of plate boehmite containing an alkali metal or alkaline earth metal in the present invention, it can be preferably used a large metal oxide or its hydrate of the refractive index, titanium oxide, zirconium oxide, tin oxide, cobalt titanate, lithium cobalt titanate, nickel titanate, iron titanate, iron oxide and these hydrate can be exemplified. これらは二種以上を併用してもよい。 These may be used in combination of two or more thereof. 中でも、酸化チタン、酸化ジルコニウム又はこれらの含水物を特に好ましく用いることができる。 Of these, particularly preferably used titanium oxide, zirconium oxide, or these hydrate.

【0012】アルカリ金属又はアルカリ土類金属含有板状ベーマイトを金属酸化物で被覆する方法としては、特に制限はなく従来公知の各種の方法によることができ、 [0012] As a method for the alkali metal or alkaline earth metal-containing plate-like boehmite coated with metal oxides, can especially by various known methods without restriction,
例えば水中乃至アルカリ熱水中に懸濁させたベーマイトに加水分解により金属水酸化物を生成する化合物(テトラアルコキシチタン、テトラ−n−ブトキシジルコニウム等の金属アルコキシド、金属アシレート等)を滴下し加水分解による金属水酸化物被膜をベーマイト表面に形成させた後、焼成する方法、ベーマイトを水中懸濁液としておき、四塩化チタン、塩化錫等の金属塩化物とアルカリを該懸濁液中に同時に滴下してベーマイト表面に金属水酸化物からなる被膜を形成した後焼成する中和加水分解法等を例示できる。 For example dropwise compound that produces a metal hydroxide by hydrolysis in water or boehmite suspended in alkaline hot water (tetraalkoxy titanium, a metal alkoxide such as tetra -n- butoxy zirconium, metal acylate, etc.) Hydrolysis after the metal hydroxide film is formed on the boehmite surface by a method of baking, leave the boehmite suspension in water, at the same time titanium tetrachloride, metal chlorides and alkali such as tin chloride in the suspension dropwise the neutralized hydrolysis method or the like can be exemplified firing after forming a coating film made of a metal hydroxide of the boehmite surface is.

【0013】また、これらの方法は一又は二以上の方法を繰り返して行うこともでき、それにより光沢や発色の改善等のための金属酸化物の多層被覆を施すことができる。 Further, these methods can also be carried out repeatedly one or more methods, thereby performing multi-coated metal oxide for improvement of gloss and color. これらの方法における焼成工程は、窒素、アルゴン、水素、アンモニア等の不活性雰囲気又は還元雰囲気で行うことにより、低次酸化チタンや低次酸化鉄等、酸素欠損を有する金属酸化物被膜とすることもでき、黒色を帯びた真珠光沢顔料を得ることができる。 Firing step in these methods, nitrogen, argon, hydrogen, by performing in an inert or reducing atmosphere such as ammonia, be a metal oxide film having low-order titanium oxide or low-order iron oxide, oxygen deficiency it can also be, to obtain a pearlescent pigment tinged black.

【0014】本発明の真珠光沢顔料は、セラミックス原料としても有用であり、更に塗料用、ブラスチックスへの練り込み用、インク用、化粧料用、釉薬用等の顔料としても極めて優れているものである。 Nacreous pigments [0014] The present invention is useful as a ceramic raw material, which is excellent as a further coating material, for kneading to brass Chicks, ink, cosmetic, pigment such as a glaze it is. 本発明の真珠光沢顔料には、その用途に応じて、耐水性、耐候性、耐薬品性、耐変色性、高分散性等を付与する処理を適宜施すことができる。 Pearlescent pigments of the present invention, depending on the application, water resistance, weather resistance, chemical resistance, can be applied properly discoloration resistance, a treatment for imparting high dispersibility and the like.

【0015】 [0015]

【実施例】以下に実施例を挙げ、本発明をより詳細に説明するが、本発明はこれらにより限定されるものではない。 EXAMPLES the following examples, the present invention will be described in more detail, the present invention is not intended to be limited to these.

【0016】製造例1 カルシウム含有板状ベーマイトの合成 オートクレーブ中に、脱イオン水5Lを入れ、酢酸カルシウム168g、水酸化アルミニウム1000gを加えて攪拌混合し、原料スラリーを得た。 [0016] Synthesis autoclave Production Example 1 Calcium-containing plate-like boehmite, Deionized water 5L, calcium acetate 168 g, and stirred mixed with aluminum hydroxide 1000 g, to obtain a raw material slurry. 該スラリーを攪拌しながら、昇温速度200℃/時間で170℃まで加熱し、加温・加圧された状態で12時間保持して水熱反応を行った。 While stirring the slurry, it was heated to 170 ° C. at a heating rate of 200 ° C. / time, and held 12 hours for hydrothermal reaction in a pressurized state temperature and pressure. 反応後、スラリーを自然冷却により放冷し、 After the reaction, the slurry was allowed to cool by natural cooling,
攪拌を止めて、スラリーを取り出してろ過・水洗・乾燥し、平均長径5.3μm、平均厚み0.2μm、平均アスペクト比27のカルシウム含有板状ベーマイトを得た。 It stopped stirring, the slurry was filtered, washed with water and dried removed to yield an average diameter 5.3 .mu.m, the average thickness of 0.2 [mu] m, a calcium-containing plate-like boehmite having an average aspect ratio of 27.

【0017】製造例2 バリウム含有板状ベーマイトの合成 水酸化バリウム8水和物を使用する他は製造例1と同様にして、平均長径6.2μm、平均厚み0.2μm、平均アスペクト比31のバリウム含有板状ベーマイトを得た。 [0017] Another use of synthetic barium hydroxide octahydrate in Production Example 2 Barium-containing plate-like boehmite in the same manner as in Preparation Example 1, the average major axis 6.2 .mu.m, the average thickness of 0.2 [mu] m, average aspect ratio 31 to obtain a barium-containing plate-like boehmite.

【0018】製造例3 ストロンチウム含有板状ベーマイトの合成 水酸化ストロンチウム8水和物を使用する他は製造例1 [0018] Another use of synthetic strontium hydroxide octahydrate in Production Example 3 containing strontium-shaped boehmite Production Example 1
と同様にして、平均長径7.0μm、平均厚み0.18μ In the same manner as, the average long diameter 7.0 .mu.m, the average thickness of 0.18μ
m、平均アスペクト比40のストロンチウム含有板状ベーマイトを得た。 m, to obtain a strontium-containing plate-like boehmite having an average aspect ratio of 40.

【0019】製造例4 カリウム含有板状ベーマイトの合成 水酸化カリウムを使用する他は製造例1と同様にして、 [0019] Another use of synthetic potassium hydroxide Production Example 4 Potassium containing plate-like boehmite in the same manner as in Preparation Example 1,
平均長径5.5μm、平均厚み0.15μm、平均アスペクト比36のカリウム含有ベーマイトを得た。 Average major axis 5.5 [mu] m, an average thickness of 0.15 [mu] m, to obtain a potassium-containing boehmite having an average aspect ratio of 36.

【0020】実施例1 製造例1で得られたカルシウム含有板状ベーマイト10 [0020] Calcium obtained in Production Example 1 containing plate-like boehmite 10
0gを脱イオン水1Lに分散させたスラリーを80℃に加熱した。 The slurry was dispersed in deionized water 1L and 0g was heated to 80 ° C.. 該スラリーに四塩化チタン溶液(濃度150 The slurry of titanium tetrachloride solution (concentration 150
g/L)を0.5ml/分の速度で滴下し、それと同時にpHが2に保たれるように水酸化ナトリウム溶液(1 g / L) was added dropwise at 0.5 ml / min, the same sodium hydroxide solution as simultaneous pH is maintained at 2 (1
0重量%溶液)を滴下した。 0 wt% solution) was added dropwise. スラリー中に銀色光沢が得られた時点で滴下を中止し、スラリーをろ過、水洗、乾燥した後、480℃にて焼成し、白色で高光沢の真珠光沢顔料を得た。 It stops dropping when the silver luster was obtained in the slurry, the slurry is filtered, washed with water, dried and then calcined at 480 ° C., to obtain a pearlescent pigment high gloss white.

【0021】実施例2 製造例2で得られたバリウム含有板状ベーマイトを使用する他は実施例1と同様にして、白色で高光沢の真珠光沢顔料を得た。 [0021] Another of using barium-containing plate-like boehmite obtained in Example 2 Production Example 2 in the same manner as in Example 1 to obtain a high gloss of the pearlescent pigment in white.

【0022】実施例3 製造例3で得られたストロンチウム含有板状ベーマイトを使用する他は実施例1と同様にして、白色で高光沢の真珠光沢顔料を得た。 [0022] Another of using strontium-containing plate-like boehmite obtained in Example 3 Production Example 3 in the same manner as in Example 1 to obtain a high gloss of the pearlescent pigment in white.

【0023】実施例4 製造例1で得られたカルシウム含有板状ベーマイト10 [0023] Example 4 Calcium obtained in Production Example 1 containing plate-like boehmite 10
0gを脱イオン水1Lに分散させたスラリーを80℃に加熱した。 The slurry was dispersed in deionized water 1L and 0g was heated to 80 ° C.. スラリーのpHが9になるように水酸化ナトリウム溶液(10重量%溶液)を添加し、20分間撹拌した後、四塩化錫溶液(濃度40g/L)100mlを0.5ml/分の速度で滴下し、それと同時にpHが2 Adding sodium hydroxide solution as the pH of the slurry is 9 (10 wt% solution), After stirring for 20 min, added dropwise tin tetrachloride solution (concentration 40 g / L) 100 ml at 0.5 ml / min and, at the same time the pH is 2
に保たれるように水酸化ナトリウム溶液(10重量%溶液)を滴下した。 It was added dropwise sodium hydroxide solution (10 wt% solution) so as to keep the. スラリー中に銀色光沢が得られた時点で滴下を中止し、スラリーをろ過、水洗、乾燥した後、 Stops dropping when the silver luster was obtained in the slurry, the slurry is filtered, washed with water, dried,
480℃にて焼成し、白色で高光沢の真珠光沢顔料を得た。 And baked at 480 ° C., to obtain a pearlescent pigment high gloss white.

【0024】実施例5 製造例4で得られたカリウム含有ベーマイトを使用する他は実施例1と同様にして白色で高光沢の真珠光沢顔料を得た。 The yield Example 5 except that using potassium-containing boehmite obtained in Production Example 4 in the same manner as in Example 1 of the high gloss white nacreous pigments.

【0025】比較例1 平均長径11.5μm、平均厚み0.2μm、平均アスペクト比57の板状アルミナ100gを使用する他は実施例1と同様にして白色で高光沢の真珠光沢顔料を得た。 [0025] Comparative Example 1 The average major diameter 11.5 .mu.m, an average thickness of 0.2 [mu] m, in addition to using the plate-like alumina 100g and an average aspect ratio of 57 was obtained pearlescent pigments high gloss white in the same manner as in Example 1 .

【0026】沈降性の評価 実施例及び比較例にて得られた真珠光沢顔料サンプル5 The pearlescent obtained in Evaluation Examples and Comparative Examples of precipitated pigment sample 5
gを脱イオン水及びトルエンの各50ml中に添加して10分撹拌後、1時間静置して懸濁層と上澄み層の厚みを測定し、懸濁層の厚みの割合により沈降性を評価した。 10 minutes after stirring was added to g in each 50ml of deionized water and toluene, and allowed to stand for 1 hour to measure the thickness of the suspension layer and a supernatant layer, evaluate precipitated by the ratio of the thickness of the suspension layer did.

【0027】 [0027]

【表1】懸濁層の厚み比 TABLE 1 thickness ratio of the suspension layer (懸濁層の厚み比:%)=(懸濁層の厚み)/(懸濁層の厚み+上澄み層の厚み)×100 (Suspending layer thickness ratio of:%) = (suspension layer thickness) / (the thickness of the thick + supernatant layer of the suspension layer) × 100

【0028】 [0028]

【発明の効果】本発明によれば、厚みが薄く且つ均一で、平均アスペクト比が大きく、それ自体は極力無色透明で、高温耐熱性を有しており、且つ機械的強度が高い等の特性を有すると共に、沈降性の少ない真珠光沢顔料を得ることができる。 According to the present invention, a thickness of a thin and uniform, large average aspect ratio, it itself is minimized colorless and transparent, the characteristics of which have a high-temperature heat resistance, and mechanical strength such as high it can be obtained with less pearlescent pigments with, the precipitated having.

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl. 7識別記号 FI テーマコート゛(参考) C09D 5/36 C09D 5/36 201/00 201/00 Fターム(参考) 4G004 BA00 4G076 AA18 AA24 AB04 AB06 AB07 AB09 AB12 BA12 BA43 BC07 BC08 BD01 BD02 BF05 CA02 CA08 CA26 DA15 FA08 4J037 AA24 CA09 CB05 DD05 DD10 DD27 EE03 EE14 EE43 FF09 4J038 EA011 HA216 KA08 KA15 NA01 NA03 NA04 NA16 NA19 NA26 ────────────────────────────────────────────────── ─── of the front page continued (51) Int.Cl. 7 identification mark FI theme Court Bu (reference) C09D 5/36 C09D 5/36 201/00 201/00 F-term (reference) 4G004 BA00 4G076 AA18 AA24 AB04 AB06 AB07 AB09 AB12 BA12 BA43 BC07 BC08 BD01 BD02 BF05 CA02 CA08 CA26 DA15 FA08 4J037 AA24 CA09 CB05 DD05 DD10 DD27 EE03 EE14 EE43 FF09 4J038 EA011 HA216 KA08 KA15 NA01 NA03 NA04 NA16 NA19 NA26

Claims (3)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 アルカリ金属又はアルカリ土類金属含有板状ベーマイトに金属酸化物が被覆されたことを特徴とする真珠光沢顔料。 1. A pearlescent pigments metal oxide to an alkali metal or alkaline earth metal-containing plate-like boehmite and wherein the coated.
  2. 【請求項2】 アルカリ金属がナトリウム又はカリウム、アルカリ土類金属がカルシウム、ストロンチウム又はバリウムである請求項1の真珠光沢顔料。 Wherein sodium or potassium alkali metal, alkaline earth metal calcium, pearlescent pigments according to claim 1 is a strontium or barium.
  3. 【請求項3】 金属酸化物が酸化チタン、酸化ジルコニウム、酸化スズ又はこれらの含水物である請求項1又は2の真珠光沢顔料。 Wherein the metal oxide is titanium oxide, zirconium oxide, tin oxide or claim 1 or 2 of pearlescent pigments is their hydrate.
JP2000017547A 2000-01-26 2000-01-26 Pearl gloss pigment Pending JP2001207077A (en)