JP2001166113A - Light-condensing film, surface light source device and liquid crystal display device - Google Patents

Light-condensing film, surface light source device and liquid crystal display device

Info

Publication number
JP2001166113A
JP2001166113A JP34892599A JP34892599A JP2001166113A JP 2001166113 A JP2001166113 A JP 2001166113A JP 34892599 A JP34892599 A JP 34892599A JP 34892599 A JP34892599 A JP 34892599A JP 2001166113 A JP2001166113 A JP 2001166113A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
light
film
light source
condensing
condensing film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP34892599A
Other languages
Japanese (ja)
Inventor
Tadahiro Mazaki
忠宏 真崎
Original Assignee
Dainippon Printing Co Ltd
大日本印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To provide a light-condensing film having a light-condensing effect and a diffusing effect and to provide an efficient surface light source device and liquid crystal display device with a small number of films. SOLUTION: The light-condensing film 10 consists of a base film 11 and unit prisms 12 irregularly arranged on the film 11 to form a light-diffusing and condensing layer. The obtained light-condensing film 10 is disposed in the light-exiting side of a surface light source device and used as a back light of a liquid crystal display device.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、集光フィルムに関し、特に、集光性を保ちつつ拡散性を同時に備えた集光フィルムと、それを用いた面光源装置及び液晶表示装置に関するものである。 BACKGROUND OF THE INVENTION The present invention relates to a condensing film, in particular, those with condensing film having a diffusion resistance simultaneously while maintaining the light collecting relates to a surface light source device and a liquid crystal display device using the same .

【0002】 [0002]

【従来の技術】従来、この種の集光フィルムは、例えば、面光源装置の出光面側に設けられ、光源からの照明光を必要な範囲のみに集光するために使用されていた。 Conventionally, condensing film of this kind, for example, provided on the light outgoing surface side of the surface light source device, it has been used for condensing only to the extent required illumination light from the light source.
図6は、従来の集光フィルムの一例を示す図である。 Figure 6 is a diagram showing an example of a conventional condensing film. 従来の集光フィルム110は、単位プリズム112が基材フィルム111上に等ピッチで規則的に並べて配置されており、これらの集合体でひとつの集光フィルム110 Conventional condensing film 110 is arranged unit prism 112 is arranged at an equal pitch regularly on the base film 111, one of the condensing film 110 at these assemblies
を構成している。 Constitute a.

【0003】図7は、従来の集光フィルム110を用いた面光源装置の一例として、エッジ型平面光源である面光源装置120を設けた液晶表示装置135を示す断面図である。 [0003] Figure 7 shows, as an example of the surface light source device using the conventional condensing film 110 is a sectional view showing a liquid crystal display device 135 provided with a surface light source device 120 is an edge-type planar light source. 面光源装置120は、光源121、導光板1 The surface light source device 120 includes a light source 121, a light guide plate 1
22、反射フィルム124、拡散板125、集光フィルム110A,110B等からなっている。 22, the reflective film 124, diffusion plate 125, which is condensing film 110A, the 110B, and the like. ここで、集光フィルム110A,110Bは、同じ諸元を有する集光フィルムである。 Here, the condensing films 110A, 110B is a condensing film having the same specifications. 導光板122は、側面に光源121を備え、光源121からの光を拡散させて出光方向に向けるためのドットパターン123を出光面122aと対向する面に設けている。 The light guide plate 122 is provided with a light source 121 to the side surface, it is provided in Idemitsumen 122a which faces the dot pattern 123 for the diffuse light directed in the light exit direction from the light source 121. 反射フイルム124は、導光板1 Reflection film 124, the light guide plate 1
22を囲むように設けられ、不要な方向へ出光する光線を遮ると共に、所定の方向に光線を反射して戻す役割を果たしている。 Provided so as to surround the 22, with shielding the light rays exiting the undesired direction, and plays a role of reflecting back rays in a predetermined direction.

【0004】導光板122の出光面122a側には、光を拡散することにより、ドットパターン123を隠蔽するための拡散板125を挟んで、集光フィルム110 [0004] exit surface 122a side of the light guide plate 122, by diffusing the light, across the diffuser plate 125 for concealing the dot pattern 123, condensing film 110
A,110Bが、それらの頂線方向が互いに直交するように組み合わされ、プリズム面を出光面117として配置されている。 A, 110B are combined so that their apex line direction are perpendicular to each other, it is arranged a prism surface as Idemitsumen 117. 面光源装置120の出光側には、下基板132と上基板131に挟まれた液晶層130からなる透過型の液晶表示素子133が設けられており、面光源装置120は、液晶表示素子133を裏面から照明する。 The light outgoing side of the surface light source device 120 has a transmission type liquid crystal display device 133 comprising a liquid crystal layer 130 sandwiched between the lower substrate 132 and the upper substrate 131 is provided, the surface light source device 120, a liquid crystal display device 133 illuminating from the back surface.

【0005】 [0005]

【発明が解決しようとする課題】しかし、前述した従来の装置は、2枚以上の集光フィルム110A,110B [SUMMARY OF THE INVENTION] However, the conventional apparatus described above, two or more condensing film 110A, 110B
を、その頂線の方向を直交させて配置する必要があり、 And it must be located by orthogonal to the direction of the top line,
組み立て作業が繁雑であるという問題があった。 Assembly work there has been a problem in that it is complicated. また、 Also,
ドットパターン123を隠すためだけに、拡散板125 Just to hide the dot pattern 123, the diffusion plate 125
も別途必要であった。 It was also required separately. 拡散板125は、光の損失が大きいので、拡散板125を設けることにより、本来必要な性能である照明光の効率が悪くなり、照明光が暗くなるという弊害があった。 Diffuser 125, since loss of light is large, by providing the diffusion plate 125, the efficiency of the illumination light which is originally required performance deteriorates, there is a drawback that the illumination light becomes dark. この効率の低下を補うためには、 To compensate for this reduction in efficiency,
光源121の光量を上げる必要があり、携帯型の機器等に使用する場合には、図示しないバッテリによる駆動可能時間の短縮を招き、また、光源21及びバッテリのサイズも大型化するという問題があった。 It is necessary to increase the amount of light of the light source 121, when used in portable devices such as, lead to shortened drivable time by a battery, not shown, also, the size of the light source 21 and the battery also disadvantageously large It was. 更に、これらの光学部品が多数枚必要であるため、面光源装置120の薄型化をすることができないという問題があった。 Furthermore, because these optical parts are required large number, there is a problem that can not be thinner surface light source device 120. 更にまた、部品管理上も類似した部品を扱う必要があり、管理が複雑になったり、部品点数が多いため、価格が高くなるという問題もあった。 Furthermore, also on the part management there is a need to deal with similar parts, management or become complicated, because there are a lot of parts, there is also a problem that the price is high.

【0006】本発明の課題は、集光効果及び拡散効果を有する集光フィルム及び、少ない枚数のフィルムで効率がよい面光源装置及び液晶表示装置を提供することである。 An object of the present invention is to provide a condensing films and less number of films in efficient surface light source device and a liquid crystal display device having a light collecting effect and diffusion effect.

【0007】 [0007]

【課題を解決するための手段】本発明は、以下のような解決手段により、前記課題を解決する。 The present invention SUMMARY OF] is the following such a solution solves the problems. なお、理解を容易にするために、本発明の実施形態に対応する符号を付して説明するが、これに限定されるものではない。 In order to facilitate understanding, it will be explained by reference numeral corresponding to the embodiment of the present invention, but is not limited thereto. すなわち、請求項1の発明は、基材フィルム(11)と、前記基材フィルム上に設けられ、集光性を有する少なくとも1種類の単位光学要素(12)を不規則に配置した拡散集光層とを備える集光フィルム(10)である。 That is, the invention of claim 1 includes a base film (11), wherein provided on the base film, collecting at least one unit diffuse focus light irregularly arranged optical elements (12) having a light- a condensing film and a layer (10).

【0008】請求項2の発明は、請求項1に記載の集光フィルム(10)において、前記拡散集光層は、前記単位光学要素(12)が同一方向となる範囲内で不規則に配置されていることを特徴とする集光フィルム(10) [0008] The second aspect of the present invention is, in the light converging film according to claim 1 (10), the diffuse focus layer is irregularly arranged within a range in which the unit optical elements (12) are the same direction condensing film, characterized by being (10)
である。 It is.

【0009】請求項3の発明は、請求項1又は請求項2 [0009] The invention of claim 3, claim 1 or claim 2
に記載の集光フィルムにおいて、前記単位光学要素(1 In condensing film according to the unit optical elements (1
2,12A,12B)は、複数種類あることを特徴とする集光フィルムである。 2, 12a, 12B) is a condensing film, wherein a plurality kinds of.

【0010】請求項4の発明は、請求項1から請求項3 [0010] The invention of claim 4, claims 1 to 3
までのいずれか1項に記載の集光フィルムにおいて、前記単位光学要素は、プリズム(12)であることを特徴とする集光フィルム(10)である。 In condensing film according to any one of up, the unit optical element is a light-collecting film, characterized in that the prism (12) (10).

【0011】請求項5の発明は、請求項1から請求項4 [0011] The invention of claim 5, claims 1 to 4
までのいずれか1項に記載の集光フィルムにおいて、前記単位光学要素(12)は、底部幅5μm以上200μ In condensing film according to any one of up, the unit optical elements (12), the bottom width 5μm or 200μ
m以下、頂線長5μm以上200μm以下の三角柱状であることを特徴とする集光フィルム(10)である。 m or less, a light collecting film, which is a top line length 5μm or 200μm or less of the triangular-shaped (10).

【0012】請求項6の発明は、光源(21)と、前記光源の光を投光面から所定の方向に面投光する面投光手段(22,23,24)と、前記投光面側に配置された請求項1から請求項5までのいずれか1項に記載の集光フィルム(10)とを備える面光源装置(20)である。 [0012] The invention of claim 6 includes a light source (21), Mento light means Mento light in a predetermined direction the light from the light projecting surface of the light source and (22, 23, 24), wherein the light projecting surface a condensing film according to any one of claims 1 disposed on the side to claim 5 (10) and the surface light source device comprising a (20).

【0013】請求項7の発明は、光源(21)と、前記光源の光を投光面から所定の方向に面投光する面投光手段(22,23,24)と、前記投光面側に配置された請求項1から請求項5までのいずれか1項に記載の集光フィルム(10)と、前記集光フィルムの出光面側に配置された、透過型の液晶表示素子(33)とを備える液晶表示装置(35)である。 [0013] The invention of claim 7 includes a light source (21), Mento light means Mento light in a predetermined direction the light from the light projecting surface of the light source and (22, 23, 24), wherein the light projecting surface a condensing film according to any one of claims 1 disposed on the side to claim 5 (10), disposed on the light exit surface side of the condenser film, the transmission type liquid crystal display device (33 ) and a liquid crystal display device comprising a (35).

【0014】 [0014]

【発明の実施の形態】以下、図面等を参照して、本発明の実施の形態について、さらに詳しく説明する。 BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, with reference to the drawings, embodiments of the present invention will be described in more detail. 図1 Figure 1
は、本発明による集光フィルムの実施形態を示す斜視図である。 Is a perspective view showing an embodiment of a condensing film according to the present invention. なお、前述した従来例と同様の機能を果たす部分には、末尾に同一の符号を付して、重複する説明を適宜省略する。 Incidentally, portions having the same functions as those of the conventional example described above, omitted trailing are denoted by the same reference numerals, and redundant description as appropriate. 集光フィルム10は、基材フィルム11上に単位プリズム12が不規則に並べられ、この集合体により拡散集光層をなしている。 Condensing film 10, the unit prisms 12 on the base film 11 are aligned irregularly, and has a diffuse focus layer by the assembly.

【0015】基材フィルム11は、透明なフィルムであり、セルローストリアセテート、ポリエステル、ポリアミド、ポリイミド、ポリプロピレン、ポリメチルペンテン、ポリ塩化ビニル、ポリビニルアセタール、ポリメタアクリル酸メチル、ポリカーボネート、ポリウレタン等の熱可塑性樹脂の延伸又は未延伸フィルムを使用することができる。 The base film 11 is a transparent film, a cellulose triacetate, polyesters, polyamides, polyimides, polypropylene, polymethylpentene, polyvinyl chloride, polyvinyl acetal, polymethyl methacrylate, polycarbonate, thermoplastic and polyurethane stretched or unstretched films of resins may be used. 基材フィルム11の厚みは、フイルムがもつ剛性にもよるが、50〜200μmのものが、加工性等の取扱い面からいって好ましい。 The thickness of the substrate film 11, depending on the rigidity possessed by the film, those of 50~200μm is preferable say from handling surface such as processability. また、単位プリズム12を設ける面は、コロナ放電処理等の易接着処理を施すことが、積層する単位プリズム12との接着を強固に安定化するために好ましい。 The surface providing the unit prisms 12, be subjected to easy adhesion treatment such as corona discharge treatment, preferably in order to firmly stabilize the adhesion between the unit prism 12 to be stacked.

【0016】単位プリズム12は、各々がプリズムの作用をする単位光学要素である。 The unit prisms 12 is a unit optical elements, each of the operation of the prism. 各々の単位プリズム12 Each of the unit prisms 12
は、三角柱であって、頂角α=90度,頂線長L=50 Is a triangular prism, the apex angle alpha = 90 °, the top line length L = 50
〜150μmであり、高さHは、H=20〜40μm Is a ~150μm, height H, H = 20~40μm
(従って、底部幅B=40〜80μm)の範囲で各々異なる。 (Thus, the bottom width B = 40 to 80 [mu] m) each different range. 各単位プリズムの頂線は、同一方向となるように配置され、それらの位置は、不規則に並んでいる。 Top line of each unit prism is arranged to have the same direction, their positions are at irregularly arranged. ここで、頂線長Lは、5〜200μmの範囲がよく、底部幅Bは、5〜200μmの範囲がよい。 Here, the top line length L may have a range of 5 to 200 [mu] m, the bottom width B, it is the range of 5 to 200 [mu] m. 頂線長L及び底部幅Bが小さすぎると、波長分散が生じて不要な色を呈したり、拡散しすぎて輝度の低下を招く。 When the top line length L and the bottom width B is too small, or exhibit unwanted color wavelength dispersion occurs, too diffuse lowering the luminance. 逆に頂線長L及び底部幅Bが大きすぎると、後述する導光板22のドットパターン23が見えてしまう。 If conversely top line length L and the bottom width B is too large, the dot pattern 23 of the light guide plate 22 described later is seen. 上記頂線長L及び底部幅Bは、これらの点を考慮して導き出された範囲である。 The top line length L and the bottom width B is in the range derived in consideration of these points.

【0017】単位プリズム12は、多価アルコール等の多官能化合物の(メタ)アクリレート(以下、本明細書では、アクリレートとメタアクリレートとを(メタ)アクリレートと記載する。)等のオリゴマー又はプレポリマー及び反応性の希釈剤を比較的多量に含むものから構成する。 The unit prisms 12, multivalent polyfunctional compound such as an alcohol (meth) acrylate (hereinafter, in this specification, describes acrylate and methacrylate and (meth) acrylate.) Oligomers or prepolymers, such as and constituting a reactive diluent from the relatively large amounts include those. 上記希釈剤としては、エチル(メタ)アクリレート、エチルヘキシル(メタ)アクリレート、スチレン、ビニルトルエン、N−ビニルピロリドン等の単官能モノマー、並びに多官能モノマー、例えばトリメチロールプロパントリ(メタ)アクリレート、ヘキサンジオール(メタ)アクリレート、トリプロピレングリコールジ(メタ)アクリレート、ジエチレングリコールジ(メタ)アクリレート、ペンタエリスリトールトリ(メタ) As the diluent, ethyl (meth) acrylate, ethylhexyl (meth) acrylate, styrene, vinyl toluene, monofunctional monomers such as N- vinylpyrrolidone, and polyfunctional monomers, such as trimethylolpropane tri (meth) acrylate, hexanediol (meth) acrylate, tripropylene glycol di (meth) acrylate, diethylene glycol di (meth) acrylate, pentaerythritol tri (meth)
アクリレート、ジペンタエリスリトールヘキサ(メタ) Acrylate, dipentaerythritol hexa (meth)
アクリレート、1,6ヘキサンジオールジ(メタ)アクリレート、ネオペンチルグリコールジ(メタ)アクリレート等がある。 Acrylate, 1,6-hexanediol di (meth) acrylate, neopentyl glycol di (meth) acrylate.

【0018】更に、上記の電離放射線硬化型樹脂を紫外線硬化型樹脂として使用するときは、これらの中に光重合開始剤として、アセトフェノン類、ベンゾフェノン類、ミヒラーベンゾイルベンゾエート、αーアミロキシムエステル、チオキサントン類や、光増感剤としてn− Furthermore, when using the ionizing radiation curing resin as an ultraviolet curable resin, photopolymerization initiator in these, acetophenones, benzophenones, Michler's benzoyl benzoate, alpha over amyloxime ester, thioxanthones and, as photosensitizer n-
ブチルアミン、トリエチルアミン、トリn−ブチルホスフィン等を混合して使用する。 Butylamine, triethylamine, a mixture of tri-n- butylphosphine used.

【0019】上記の電離放射線硬化型樹脂には、次の反応性有機ケイ素化合物を含ませることもできる。 [0019] The above ionizing radiation-curable resin, may also be included the following reactive organosilicon compound. m R m S
i(0R′) nで表せる化合物であり、ここでR、R′ i (0R ') is a compound represented by n, wherein R, R'
は、炭素数1〜10のアルキル基を表し、m+n=4であり、そしてm及びnは、それぞれ整数である。 Represents an alkyl group having 1 to 10 carbon atoms, m + n = 4; and m and n are integers, respectively. 更に具体的には、テトラメトキシシラン、テトラエトキシシラン、テトラ−iso−プロポキシシラン、テトラ−n− More specifically, tetramethoxysilane, tetraethoxysilane, tetra -iso- propoxysilane, tetra -n-
プロポキシシラン、テトラ−n−ブトキシシラン、テトラ−sec−ブトキシシラン、テトラ−tert−ブトキシシラン、テトラペンタエトキシシラン、テトラペンタ−iso−プロポキシシラン、テトラペンタ−n−プロポキシシラン、テトラペンタ−n−ブトキシシラン、 Propoxysilane, tetra -n- butoxysilane, tetra -sec- butoxysilane, tetra -tert- butoxysilane, tetra-penta-ethoxy silane, Tetorapenta -iso- propoxysilane, Tetorapenta -n- propoxysilane, Tetorapenta -n- butoxysilane,
テトラペンタ−sec−ブトキシシラン、テトラペンタ−tert−ブトキシシラン、メチルトリメトキシシラン、メチルトリエトキシシラン、メチルトリプロポキシシラン、メチルトリブトキシシラン、ジメチルジメトキシシラン、ジメチルジエトキシシラン、ジメチルエトキシシラン、ジメチルメトキシシラン、ジメチルプロポキシシラン、ジメチルブトキシシラン、メチルジメトキシシラン、メチルジエトキシシラン、ヘキシルトリメトキシシラン等があげられる。 Tetorapenta -sec- butoxysilane, Tetorapenta -tert- butoxysilane, methyltrimethoxysilane, methyltriethoxysilane, methyl tripropoxysilane, methyl tributoxysilane silane, dimethyldimethoxysilane, dimethyldiethoxysilane, dimethylethoxysilane, dimethyl silane , dimethyl propoxysilane, dimethyl-butoxy silane, methyl dimethoxy silane, methyl diethoxy silane, hexyl trimethoxy silane, and the like.

【0020】単位プリズム12は、上記の反応硬化型樹脂ばかりでなく、熱可塑性樹脂を用いて形成することもできる。 The unit prisms 12 is not only curable resins described above, can also be formed by using a thermoplastic resin. 例えば、メチルメタアクリレート、エチルメタアクリレート等のアクリル樹脂、、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート等のポリエステル、ポリカーボネートや、 For example, methyl methacrylate, ethyl methacrylate acrylic resins such as ,, polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate and the like, and polycarbonate,
ポリスチレン、ポリプロピレン、ポリメチルペンテン等のポリハイドロカーボン、6,6ナイロン、6ナイロン等のポリアミド、エチレン・酢酸ビニル共重合体ケン化物、ポリイミド、ポリスルホン、ポリ塩化ビニル、アセチルセルロース等の熱可塑性樹脂から選択できる。 Polystyrene, polypropylene, poly hydrocarbon such as polymethyl pentene, 6,6 nylon, polyamides such 6 nylon, ethylene-vinyl acetate copolymer saponification product, polyimides, polysulfones, polyvinyl chloride, thermoplastic resins such as acetyl cellulose It can be selected.

【0021】本実施形態では、基材フィルム11、単位プリズム12について、上記素材の中から、以下のものを選択して使用した。 [0021] In this embodiment, the base film 11, the unit prisms 12, from among the materials were selected and used below. 基材フィルム11は、PETフィルム:A4300(東洋紡績社製)の125μm厚を使用した。 The base film 11, PET film: A 4300 using 125μm thick (manufactured by Toyobo Co., Ltd.). 単位プリズム12は、紫外線硬化型樹脂:Z9 Unit prism 12, an ultraviolet curing resin: Z9
009(JSR製)を使用した。 009 (manufactured by JSR) was used.

【0022】集光フィルム10は、基材フィルム11上に、単位プリズム12を形成することにより製造した。 The light-condensing film 10 on the base film 11 was prepared by forming a unit prism 12.
図2は、単位プリズム12を形成する工程の概略を説明する図である。 Figure 2 is a schematic diagram for explaining the process of forming the unit prism 12. 最初に、単位プリズム12の集合である不規則に配置された凹形状を形成してある版胴88に、 First, the plate cylinder 88 which is formed irregularly arranged concave shape which is a set of unit prisms 12,
ポンプ87で電離放射線硬化型樹脂82をダイヘッド8 Die head ionizing radiation curable resin 82 by a pump 87 8
6に送り、版胴88に電離放射線硬化型樹脂82を均一に押し込む。 Sent to 6, evenly push the ionizing radiation curable resin 82 on plate cylinder 88. そして、基材フイルム11の面と版胴88 Then, the surface of the substrate film 11 and plate cylinder 88
とを入口ニップ83で密着したものに、電離放射線照射装置85〔Dバルブ紫外線ランプ(フュージョン社製)〕により電離線を照射し、硬化した電離放射線硬化型樹脂81とするとともに基材フィルム11との接着を行う。 Preparative to those in close contact with the inlet nip 83, the base film 11 with the ionizing radiation irradiation device 85 [D bulb UV lamp (manufactured by Fusion Co.)] was irradiated with ionizing radiation, and ionizing radiation-curable resin 81 cured carry out the adhesive. そして、出口ニップ84で版胴88から基材フイルム11に形成した単位プリズム12を剥離し、集光フイルム10を形成した。 Then, peeling off the unit prisms 12 formed on the substrate film 11 from the plate cylinder 88 at the exit nip 84 to form a light collecting film 10.

【0023】版胴88は、電解加工、放電加工、超音波加工等の方法により作製することができるが、本実施形態では、放電加工により、版胴88を作製した。 The plate cylinder 88 is electrochemical machining, electrical discharge machining, can be produced by the method of ultrasonic processing, etc., in the present embodiment, the electric discharge machining to prepare a plate cylinder 88. 図3 Figure 3
は、放電加工に使用した電極15を示す図である。 Is a diagram showing an electrode 15 used in the electric discharge machining. 版胴88の素材であるCr(クロム)製のシリンダに対して、電極15を深さ方向に所望の大きさが得られるまで不規則に進入させた。 Against Cr (chromium) steel cylinder which is a material of the plate cylinder 88, a desired size of the electrodes 15 in the depth direction was irregularly enters to obtain. このとき、電極15の角度は、変化させずに、NC制御により電極位置を不規則に移動させて、シリンダ表面に不規則に配置された単位プリズムの型を多数形成させ、版胴88を作製した。 At this time, the angle of the electrode 15, without changing, irregularly moving the electrode position by the NC control, to form a large number of randomly type arranged unit prisms on the cylinder surface, making the plate cylinder 88 did.

【0024】図4は、本実施形態の集光フィルム10を用いた面光源装置20を設けた液晶表示装置35を示す断面図である。 FIG. 4 is a sectional view showing a liquid crystal display device 35 provided with a surface light source device 20 using the light-condensing film 10 of the present embodiment. 面光源装置20は、光源21、導光板2 The surface light source device 20 includes a light source 21, the light guide plate 2
2、反射フィルム24、集光フィルム10A,10B等からなっている。 2, the reflective film 24, formed of a condensing film 10A, 10B or the like. ここで、集光フィルム10A,10B Here, the condensing films 10A, 10B
は、共に同じ諸元の集光フィルム10であり、単位プリズム12の頂線方向を互いに直交するように配置されている。 Is both a condensing film 10 having the same specifications are arranged a top line direction of the unit prisms 12 so as to be perpendicular to each other. 導光板22は、側面に蛍光ランプの光源21を備え、光源21からの光を拡散させて出光方向に向けるためのドットパターン23を出光面22aと対向する面に設けている。 The light guide plate 22 includes a light source 21 of the fluorescent lamp on the side surface, are provided on a surface of the dot pattern 23 faces the Idemitsumen 22a for the diffuse light directed to the light output direction from the light source 21. 面光源装置20の出光側には、下基板32 The light outgoing side of the surface light source device 20, the lower substrate 32
と上基板31に挟まれた液晶層30からなる透過型の液晶表示素子33が設けられており、面光源装置20は、 The liquid crystal display device 33 of the transmission type comprising a liquid crystal layer 30 sandwiched between the upper substrate 31 is provided with a surface light source device 20,
液晶表示素子33を裏面から照明する。 It illuminates the liquid crystal display element 33 from the back.

【0025】(評価試験)以上のようにして作製した集光フィルム10及びこれを用いた面光源装置20の評価を、正面輝度,外観について、2つの比較例との対比により行った。 [0025] The evaluation of (Evaluation Test) The thus to the condensing film 10 and the surface light source device 20 using the same manufacturing, front luminance, the appearance was performed by comparison with two comparative examples. 比較例1は、従来技術の説明に使用した図7と同様の形態であり、拡散板として光拡散フィルムD Comparative Example 1 has the same configuration as FIG. 7 used for the description of the prior art, the light diffusing film D as a diffusion plate
121(ツジデン社製)を1枚使用し、図6に示した集光フィルム110と同様の形態をしたレンズフィルムB 121 (Tsujiden Inc.) using one of the lens film B was the same form as the condensing film 110 shown in FIG. 6
EFII(住友3M社製)を、プリズムの頂線が直交するように2枚配置した。 EFII (manufactured by Sumitomo 3M Co.) was placed two sheets as the top line of the prism is perpendicular. 比較例2は、比較例1から、光拡散フィルムを除去したものである。 Comparative Example 2, Comparative Example 1 is obtained by removing the light diffusing film. 以上3種類の面光源装置を用いて評価を行った。 It was evaluated using three kinds of surface light source device or more. 正面輝度は、光源21を点灯させた状態で、輝度計BM−7を用いて、各面光源装置の正面法線方向から、面光源装置の表面の輝度を測定した。 The front luminance, a state where the light source 21 is lit using a luminance meter BM-7, from the front direction normal of each surface light source device was measured the brightness of the surface of the surface light source device. 外観は、光源21を点灯させて、導光板22の裏面のドットパターン23に注目して目視により観察した。 Appearance, the light source 21 is lit, was visually observed to focus on the back surface of the dot pattern 23 of the light guide plate 22.

【0026】以上の結果をまとめて、表1に示す。 [0026] The above results are summarized, shown in Table 1. この表より、本実施形態は、比較例2に比べると正面輝度は、低いが、ドット見えは、無い。 From this table, the present embodiment, front luminance as compared to Comparative Example 2 are lower, dot visible, no. また、比較例1と比較すると、光拡散フィルムを使用していないため、正面輝度が向上している。 In comparison with Comparative Example 1, because it does not use a light diffusing film, it has improved front brightness. 従って、拡散板が無くても外観がよく、正面輝度も充分に確保できていると、評価することができる。 Therefore, the diffusion plate may be without even appearance and is made also sufficiently secured front luminance can be evaluated.

【0027】 [0027]

【表1】 [Table 1]

【0028】本実施形態によれば、単位レンズ12を不規則に配置して集光フィルム10を作製するので、面光源装置は、拡散板を使用しなくても導光板22の裏面にあるドットパターン23を隠蔽することができ、光の損失が少なくて済み、効率よく照明をすることができる。 In accordance with the present embodiment, since the unit lenses 12 are irregularly arranged to produce a light trapping film 10, the surface light source device, on the back side of the light guide plate 22 without using the diffusion plate dots it can be hidden patterns 23, fewer loss of light can be efficiently illuminated.
従って、照明光の明るさも向上することができる。 Therefore, it is possible to improve also the brightness of the illumination light. また、部品点数も少なくて済み、より薄くすることができ、更に、価格も低価格にすることができる。 In addition, the number of parts is fewer, can be thinner, can be further, price is also at a low price.

【0029】(変形形態)以上説明した実施形態に限定されることなく、種々の変形や変更が可能であって、それらも本発明の均等の範囲内である。 [0029] (variant) or Without being limited to the embodiments described, there may be variously modified and variations are also within the scope of equivalents of this invention.

【0030】(1)本実施形態では、単位光学要素として、三角柱形状の単位プリズム12を設けた例を示したが、単位光学要素は、この形態に限るものではない。 [0030] (1) In the present embodiment, as the unit optical element, an example in which a unit prism 12 of the triangular shape, the unit optical elements is not limited to this form. 図5は、単位光学要素の変形形態を示す図である。 Figure 5 is a diagram illustrating a modified form of the unit optical element. 図5 Figure 5
(a)は、本実施形態で示した形態の単位光学要素である。 (A) is a unit optical element of the embodiment shown in this embodiment. 図5(b)は、特定の長手方向を有する単位光学要素の変形形態を示す図である。 5 (b) is a view showing a modified form of the unit optical element having a specific longitudinal direction. 単位光学要素は、単位光学要素12Aのように半円柱形状や、断面形状が台形形状をした多角柱形状である単位光学要素12B等を1種類で多数不規則に配置して、単位プリズム12とは、異なる光学特性を与えてもよいし、図5(b)に示すように、それらを組合せて、全体として所望の光学特性を与えるようにしてもよい。 Unit optical element, and a semi-cylindrical shape as unit optical elements 12A, the unit optical elements 12B, etc. is a polygonal shape in which the cross-sectional shape was trapezoidal and irregularly arranged a number of one type, the unit prisms 12 is different may be given optical characteristic, as shown in FIG. 5 (b), they combination may be given the desired optical properties as a whole. 図5(b)に示すように、複数種類の単位光学要素を組合せた場合、その単位光学要素の割合を変更することにより、集光フィルム全体の光学特性を変更することができる。 As shown in FIG. 5 (b), when a combination of plural kinds of unit optical elements, by changing the ratio of the unit optical elements, it is possible to change the optical characteristics of the entire condensing film. 図5(c)は、特定の長手方向を持たない単位光学要素の例を示す図である。 5 (c) is a diagram showing an example of unit optical elements without a specific longitudinal direction. 単位光学要素は、特定の長手方向を有する柱状をしている必要はなく、例えば、四角錐12C,半球12D,角錐台12E等を1種類で多数不規則に配置してもよいし、 Unit optical elements need not be columnar having a specific longitudinal direction, for example, quadrangular pyramid 12C, hemisphere 12D, to the truncated pyramid 12E or the like may be irregularly arranged in large numbers at one,
図5(c)に示したように、複数種類を多数不規則に配置してもよい。 As shown in FIG. 5 (c), it may be arranged a plurality of types many irregularly. このように、より小型の単位光学要素を多数配置すると、配置の自由度も大きくなり、また、拡散性を更に大きくすることができる。 Thus, more when arranging a large number of small unit optical elements, also increases the degree of freedom of arrangement, also, it is possible to further increase the diffusion resistance.

【0031】(2)本実施形態では、面光源装置20 [0031] (2) In the present embodiment, the surface light source device 20
は、光拡散フィルム10を2枚必要とした例を示したが、これに限らず、例えば、1枚でもよいし、3枚以上であってもよい。 Showed an example in which the light diffusing film 10 requires two is not limited thereto, for example, may be a one, may be three or more.

【0032】 [0032]

【発明の効果】以上詳しく説明したように、請求項1の発明によれば、基材フィルム上に少なくとも1種類の単位光学要素を単一光学要素の頂線方向は、一定方向でありながら、各要素を不規則に配置したので、集光フィルムは、集光性と拡散性を有することができる。 As described above in detail, according to the present invention, According to the present invention, the top line direction of a single optical element at least one unit optical elements on the substrate film, while a constant direction, since the irregularly arranged the elements, condensing film may have a diffusion property and light harvesting.

【0033】請求項2の発明によれば、単位光学要素が同一方向となる範囲内で不規則に配置されているので、 According to the invention of claim 2, since the unit optical elements are arranged irregularly within a range having the same direction,
集光フィルムを成形するための版,金型等の製造が簡単になる。 Edition for shaping the condensing film, the production of molds or the like is simplified.

【0034】請求項3の発明によれば、単位光学要素は、複数種類あるので、複数の光学的作用を一枚のフィルムに収めることができ、その比率を変更することにより、簡単に光学特性を変更することができる。 According to the invention of claim 3, the unit optical elements, since a plurality kinds of a plurality of optical effects can be accommodated in one film, by changing the ratio, easy optical properties it is possible to change the.

【0035】請求項4の発明によれば、単位光学要素は、プリズムであるので、構造が簡単になり、製造が簡単になるので、集光フィルムをより低価格にすることができる。 [0035] According to the invention of claim 4, the unit optical elements, since the prism, the structure is simplified, since manufacturing is simplified, it is possible to lower cost condensing film.

【0036】請求項5の発明によれば、単位光学要素は、底部幅5μm以上200μm以下、頂線長5μm以上200μm以下の三角柱状であるので、波長分散による不要な着色や、輝度低下をすることなく、導光板のドットパターンを隠すことができる。 According to the invention of claim 5, the unit optical elements, the following bottom width 5μm or 200 [mu] m, since a top line length 5μm or 200 [mu] m or less triangular shape, or unwanted coloring due to wavelength dispersion, a brightness decrease You can hide the dot pattern without a light guide plate that.

【0037】請求項6の発明によれば、光源の光を投光面から所定の方向に面投光する面投光手段と、投光面側に配置された請求項1から請求項5までのいずれか1項に記載の集光フィルムとを備える面光源装置であるので、光学フィルムの枚数を減らすことができ、拡散板も省略することができるので面光源装置を、より薄型で低価格にすることができ、照明光の輝度も高くすることができる。 [0037] According to the invention of claim 6, the light source and Mento light means for Mento light in a predetermined direction from the light projecting surface, claims 1 to 5 disposed on the light projection surface because it is a surface light source device and a condensing film according to any one of, can reduce the number of optical films, the surface light source device can be omitted the diffusion plate, low cost thinner can be, the luminance of the illumination light can also be increased.

【0038】請求項7の発明によれば、光源の光を投光面から所定の方向に面投光する面投光手段と、投光面側に配置された請求項1から請求項5までのいずれか1項に記載の集光フィルムと、集光フィルムの出光面側に配置された、透過型の液晶表示素子とを備えるので、液晶表示装置を薄型で低価格にすることがでる。 [0038] According to the invention of claim 7, the light source and Mento light means for Mento light in a predetermined direction from the light projecting surface, claims 1 to 5 disposed on the light projection surface a condensing film according to any one of, disposed on the light exit side of the condensing film, so and a transmission type liquid crystal display device of, it is out of the low-cost liquid crystal display device thin. また、照明が明るくなるので、より鮮明に表示をすることができる。 Further, since the illumination is bright, it is possible to more clearly displayed.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】本発明による集光フィルムの実施形態を示す斜視図である。 Is a perspective view showing an embodiment of a condensing film according to the invention; FIG.

【図2】単位プリズム12を形成する工程の概略を説明する図である。 Figure 2 is a schematic diagram for explaining the process of forming the unit prism 12.

【図3】放電加工に使用した電極15を示す図である。 3 is a diagram showing an electrode 15 used in the electric discharge machining.

【図4】本実施形態の集光フィルム10を用いた面光源装置20を設けた液晶表示装置35を示す断面図である。 It is a sectional view showing a liquid crystal display device 35 provided with a [4] The surface light source device 20 that the condensing film 10 of the present embodiment is used.

【図5】単位光学要素の変形形態を示す図である。 5 is a diagram showing a variation of unit optical elements.

【図6】従来の集光フィルムを示す図である。 6 is a diagram showing a conventional condensing film.

【図7】従来の面光源装置120を設けた液晶表示装置135を示す断面図である。 7 is a sectional view showing a liquid crystal display device 135 of the conventional surface light source device 120 is provided.

【符号の説明】 10,10A,10B 集光フィルム 11 基材フィルム 12 単位プリズム 15 電極 20 面光源装置 21 光源 22 導光板 23 ドットパターン 24 反射フィルム 30 液晶層 31 上基板 32 下基板 35 液晶表示装置 [Description of Reference Numerals] 10, 10A, 10B light-condensing film 11 substrate film 12 unit prisms 15 electrode 20 surface light source device 21 light source 22 light guide plate 23 dot pattern 24 reflection film 30 liquid crystal layer 31 on the substrate 32 under the substrate 35 liquid crystal display device

───────────────────────────────────────────────────── フロントページの続き Fターム(参考) 2H042 BA04 CA12 2H091 FA21Z FA23Z FA26Z FA31Z LA11 5G435 AA00 AA03 AA17 BB12 BB15 DD09 DD13 EE27 EE33 FF03 FF06 FF07 FF08 GG03 GG24 HH02 KK07 ────────────────────────────────────────────────── ─── front page of continued F-term (reference) 2H042 BA04 CA12 2H091 FA21Z FA23Z FA26Z FA31Z LA11 5G435 AA00 AA03 AA17 BB12 BB15 DD09 DD13 EE27 EE33 FF03 FF06 FF07 FF08 GG03 GG24 HH02 KK07

Claims (7)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 基材フィルムと、 前記基材フィルム上に設けられ、集光性を有する少なくとも1種類の単位光学要素を不規則に配置した拡散集光層と、 を備える集光フィルム。 1. A a substrate film, provided on the base film, condensing film comprising a diffuse focus layers were irregularly arranged at least one unit optical element having a light harvesting, a.
  2. 【請求項2】 請求項1に記載の集光フィルムにおいて、 前記拡散集光層は、前記単位光学要素が同一方向となる範囲内で不規則に配置されていること、 を特徴とする集光フィルム。 2. A condensing film according to claim 1, wherein the diffuse focus layer includes a condenser, characterized in that, said unit optical elements are arranged irregularly within a range having the same direction the film.
  3. 【請求項3】 請求項1又は請求項2に記載の集光フィルムにおいて、 前記単位光学要素は、複数種類あること、 を特徴とする集光フィルム。 3. The condensing film according to claim 1 or claim 2, wherein the unit optical element, condensing film, wherein a plurality kinds of.
  4. 【請求項4】 請求項1から請求項3までのいずれか1 Wherein any of claims 1 to 3 1
    項に記載の集光フィルムにおいて、 前記単位光学要素は、プリズムであること、 を特徴とする集光フィルム。 In condensing film according to claim, wherein the unit optical element includes a condenser film characterized, that a prism.
  5. 【請求項5】 請求項1から請求項4までのいずれか1 5. The one of claims 1 to 4 1
    項に記載の集光フィルムにおいて、 前記単位光学要素は、底部幅5μm以上200μm以下、頂線長5μm以上200μm以下の三角柱状であること、 を特徴とする集光フィルム。 In condensing film according to claim, wherein the unit optical element, condensing film, wherein the following bottom width 5μm or 200 [mu] m, it is the top line length 5μm or 200 [mu] m or less triangular shape, a.
  6. 【請求項6】 光源と、 前記光源の光を投光面から所定の方向に面投光する面投光手段と、 前記投光面側に配置された請求項1から請求項5までのいずれか1項に記載の集光フィルムと、 を備える面光源装置。 6. A light source, a Mento light means Mento light in a predetermined direction from the light projecting surface light of the light source, any of claims 1 disposed on the light emitting surface side to claim 5 or a surface light source device and a condensing film according to item 1.
  7. 【請求項7】 光源と、 前記光源の光を投光面から所定の方向に面投光する面投光手段と、 前記投光面側に配置された請求項1から請求項5までのいずれか1項に記載の集光フィルムと、 前記集光フィルムの出光面側に配置された、透過型の液晶表示素子と、 を備える液晶表示装置。 7. A light source, a Mento light means Mento light in a predetermined direction from the light projecting surface light of the light source, any of claims 1 disposed on the light emitting surface side to claim 5 the liquid crystal display device comprising either a condensing film according to item 1, arranged on the light exit surface side of the condenser film, a transmission type liquid crystal display element, a.
JP34892599A 1999-12-08 1999-12-08 Light-condensing film, surface light source device and liquid crystal display device Pending JP2001166113A (en)