JP2001138470A - Decorative material with hardwearing properties - Google Patents

Decorative material with hardwearing properties

Info

Publication number
JP2001138470A
JP2001138470A JP32659499A JP32659499A JP2001138470A JP 2001138470 A JP2001138470 A JP 2001138470A JP 32659499 A JP32659499 A JP 32659499A JP 32659499 A JP32659499 A JP 32659499A JP 2001138470 A JP2001138470 A JP 2001138470A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
layer
curable resin
ionizing radiation
recoatability
pattern
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP32659499A
Other languages
Japanese (ja)
Inventor
Kazuyasu Kono
Shigeki Sugita
茂樹 杉田
和保 河野
Original Assignee
Dainippon Printing Co Ltd
大日本印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To enhance hardwearing properties without giving rise to a feel of surface roughness and make a surface massive touch representable with sophisticated design.
SOLUTION: This decorative material D is composed of an inner pictorial pattern layer 2, a matted recoatable ionizing radiation-curable resin layer 3A containing a filler F, a partially formed lustrous pictorial pattern layer 4A and a top coat layer 5 consisting of a curable resin, all of these layers being laminated in that order on a base 1. Alternatively, the two layers above the inner pictorial pattern layer 2 are substituted with a lustrous recoatable ionizing radiation-curable resin layer 3B containing the filler F and a partially formed matted pictorial pattern layer 4B respectively. For the curable resin of the top coat layer 5, an ionizing radiation-curable resin or a heat-curable resin are preferable.
COPYRIGHT: (C)2001,JPO

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、住宅内装や家具等の表面装飾用の化粧紙等として用いられる化粧材に関する。 The present invention relates to relates to a decorative material which is used as a decorative paper or the like for surface decoration such as residential interior and furniture. 特に、家具の水平面等に使用できる耐久物性(耐摩耗性、耐汚染性)を有する化粧材に関する。 In particular, endurance properties (wear resistance, stain resistance) that can be used on a horizontal surface such as furniture relates to a cosmetic material having a.

【0002】 [0002]

【従来の技術】従来、例えば建築物内装、建具等の用途に使用する化粧材のうち、トップコート層とする最表面のトップコート層には、ウレタン樹脂等からなる熱硬化性の2液硬化型樹脂や、或いは紫外線や電子線等の電離放射線で硬化する電離放射線硬化性樹脂等の硬化性樹脂が、耐摩耗性、耐汚染性表面の耐久物性の点から使用されている。 Conventionally, for example, a building interior, of the decorative material to be used in applications such as fittings, the top coat layer of the outermost surface of the top coat layer, two-component curing thermosetting made of urethane resin or the like type resin, or ultraviolet light or curable resin such as an ionizing radiation-curable resin curable with ionizing radiation such as electron beams is, abrasion resistance, have been used from the viewpoint of durability properties of stain resistant surface. そして、特にそれら耐摩耗性や表面硬度をより向上させる為には、該トップコート層中にフィラーを添加する事が多い。 Then, in order to particularly improve further their abrasion resistance and surface hardness, often adding filler in the top coat layer. 例えば、特許第2740943号公報(特開平8−183147号公報)では、基体上に絵柄層を形成した後、その上の最表面層として架橋性樹脂にフィラーを含有させた耐摩耗性樹脂層を設けた構成の化粧材を開示している。 For example, in Japanese Patent No. 2740943 (JP-A-8-183147), after forming a pattern layer on the substrate, abrasion resistant resin layer containing a filler crosslinkable resin as the outermost surface layer thereon to It discloses a decorative material provided configuration. また、特開平10−11922 In addition, JP-A-10-11922
6号公報では、基体上に絵柄層を形成し、該絵柄層上に、中間層用熱乾燥型電離放射線硬化性樹脂層を形成した上で、最表面層としてトップコート層用電離放射線硬化性樹脂層を形成するが、フィラーは前記の中間層用熱乾燥型電離放射線硬化性樹脂層に含有させた構成の化粧材を開示している。 The 6 discloses, a pattern layer formed on the substrate, the 該絵 pattern layer, after forming the intermediate layer heat drying type ionizing radiation-curable resin layer, an ionizing radiation-curable topcoat layer as the outermost layer forming the resin layer, but the filler discloses a decorative material having the structure is contained in the intermediate layer for thermal drying type ionizing radiation-curable resin layer of the.

【0003】 [0003]

【発明が解決しようとする課題】しかしながら、前記特許第2740943号公報の様に、最表面層となる層にフィラーを含有させた場合、水平面に使用できる十分な耐摩耗性等の物性は付与できるが、その反面、フィラーによって表面の艶が低下すると共に、表面にフィラーが頭出しし、表面ざらつき感が生じ、実際にこれを内装用途(水平面)に使用すると、接触したものを損傷させたり、摩耗させたりする問題があった。 [SUMMARY OF THE INVENTION However, as in the Patent No. 2740943 publication, when obtained by a filler in the layer to be the outermost layer, properties such as sufficient wear resistance which can be used in a horizontal plane can be imparted but or the other hand, the gloss of the surface is reduced by the filler, the surface filler cued in, cause graininess surface, when actually using this interior applications (horizontal plane), to damage the material coming in contact, there has been a problem that or to wear. 一方、前記特開平10−119226号公報の様に、フィラーを最表面層には含有させずに、内部の層(中間層用熱乾燥型電離放射線硬化性樹脂層)に含有させて、その上にトップコート層を設けた場合では、表面が平滑であり、意匠感・表面質感に乏しいものしか得られなかった。 On the other hand, as the JP-A-10-119226, JP-filler without containing the outermost layer, by incorporating into the interior of the layer (intermediate layer for thermal drying type ionizing radiation-curable resin layer) thereon in the case of providing a top coat layer, the surface is smooth, not only obtained poor to design sense and surface texture.

【0004】そこで、本発明の課題は、耐摩耗性を有する上、優れた意匠感や表面質感も表現できる化粧材を提供することである。 [0004] Therefore, an object of the present invention, on having abrasion resistance, to provide a decorative material may also represent excellent design sense and surface texture.

【0005】 [0005]

【課題を解決するための手段】上記課題を解決するために、本発明の耐摩耗性を有する化粧材の第1の形態では、基体上に内部絵柄層を有し、該内部絵柄層上にフィラーを含有し艶消しのリコート性電離放射線硬化性樹脂層を有し、該リコート性電離放射線硬化性樹脂層上に部分的に形成された艶有り絵柄層を有し、該艶有り絵柄層(及びリコート性電離放射線硬化性樹脂層)上に硬化性樹脂からなるトップコート層を有する構成とした。 Means for Solving the Problems] To solve the above problem, in the first embodiment of the decorative material having a wear resistance of the present invention, having an internal design layer on the substrate, on the internal pattern layer a filler having a recoatability ionizing radiation-curable resin layer of the matte has a glossy pattern layer partially formed on the recoating property ionizing radiation curable resin layer, 該艶 there pattern layer ( and recoatability ionizing radiation-curable resin layer) was configured to have a top coat layer comprising a cured resin on.

【0006】また、本発明の本発明の耐摩耗性を有する化粧材の第2の形態では、基体上に内部絵柄層を有し、 [0006] In the second embodiment of the decorative material having a wear resistance of the present invention of the present invention, having an internal design layer on a substrate,
該内部絵柄層上にフィラーを含有し艶有りのリコート性電離放射線硬化性樹脂層を有し、該リコート性電離放射線硬化性樹脂層上に部分的に形成された艶消し絵柄層を有し、該艶消し絵柄層(及びリコート性電離放射線硬化性樹脂層)上に硬化性樹脂からなるトップコート層を有する構成とした。 A filler on to the internal pattern layer has recoatability ionizing radiation curable resin layer there gloss, has a matte pattern layer partially formed on the recoating property ionizing radiation curable resin layer, matte pattern layer (and recoatability ionizing radiation-curable resin layer) was configured to have a top coat layer comprising a cured resin on.

【0007】この様に、第1及び第2の形態では共に、 [0007] Thus, both the first and second embodiment,
フィラーは内部の層の電離放射線硬化性樹脂層に含有させ、且つ該樹脂層はリコート性であるので、該樹脂層を未硬化状態のままで該樹脂層上にトップコート層等を形成した後に該樹脂層を硬化させる様な面倒な事をせずに、該樹脂層を硬化させて完成させた後に、該樹脂層上にトップコート層等を密着の問題なく容易に形成でき、 Fillers are contained in the ionizing radiation-curable resin layer of the inner layer, and since the resin layer is recoatability, after forming the top coat layer or the like to the resin layer while the resin layer in an uncured state the resin layer without such troublesome thing is cured, after completing curing the resin layer can be easily formed without problems of adhesion of the top coat layer or the like to the resin layer,
自由度の高い構成が可能となり、優れた耐摩耗性が得られることになる。 It enables highly flexible structure, so that excellent wear resistance can be obtained. しかも、フィラーは最表面のトップコート層にでは無く、内部の層である電離放射線硬化性樹脂層に含有させてあるので、フィラーによって表面の艶が低下したり、表面にフィラーが頭出しして表面ざらつき感が生じたり、内装用途(水平面)で表面に接触したものを損傷、摩耗させたりする問題を起こさずに、優れた耐摩耗性が得られる。 Moreover, the filler rather than the top coat layer on the outermost surface, so are not contained in the ionizing radiation-curable resin layer is an internal layer, or reduced gloss of the surface by the filler, the filler on the surface is cued or cause graininess surface damage that contact with the surface in interior applications (horizontal plane), without causing a problem or to wear, resulting excellent wear resistance.

【0008】そして、第1の形態の化粧材では、内部絵柄層と、その上の艶消しとしたリコート性電離放射線硬化性樹脂層と、該リコート性電離放射線硬化性樹脂層の上に部分的に形成された艶有り絵柄層との組み合わせによって、艶有り絵柄層の絵柄に同調した艶模様によって優れた表面質感及び意匠感も得られる。 [0008] In the decorative material of the first embodiment, and the internal pattern layer, and recoatability ionizing radiation-curable resin layer was matte thereon, partly on the said recoatability ionizing radiation curable resin layer the combination of the formed glossy picture layer, good surface texture and decorative feeling by gloss pattern tuned to the pattern of the glossy picture layer is also obtained. しかも、内部絵柄層はリコート性電離放射線硬化性樹脂層の下に設けてあるのでリコート性電離放射線硬化性樹脂(及びトップコート層)で保護され、また、艶有り絵柄層でもトップコート層の下に設けてあるのでトップコート層によって保護される結果、これら内部絵柄層、艶有り絵柄層の耐摩耗性は良好なものとなる。 Moreover, under internal pattern layer is protected by the so is provided below the recoatability ionizing radiation-curable resin layer recoatability ionizing radiation-curable resin (and top coat layer) The top coat layer in glossy pattern layer since is provided a result that is protected by a top coat layer, these internal pattern layer, the wear resistance of the glossy picture layer becomes good.

【0009】一方、第2の形態の化粧材では、内部絵柄層と、その上の艶有りとしたリコート性電離放射線硬化性樹脂層と、該リコート性電離放射線硬化性樹脂層の上に部分的に形成された艶消し絵柄層との組み合わせによって、艶消し絵柄層の絵柄に同調した艶模様によって優れた表面質感及び意匠感も得られる。 On the other hand, in the decorative material of the second embodiment, and the internal pattern layer, and recoatability ionizing radiation curable resin layer that there gloss thereon, partly on the said recoatability ionizing radiation curable resin layer the combination of matte pattern layer formed on the superior surface texture and decorative feeling by gloss pattern tuned to the pattern of matte pattern layer can be obtained. しかも、内部絵柄層はリコート性電離放射線硬化性樹脂層の下に設けてあるのでリコート性電離放射線硬化性樹脂(及びトップコート層)で保護され、また、艶消し絵柄層でもトップコート層の下に設けてあるのでトップコート層によって保護される結果、これら内部絵柄層、艶消し絵柄層の耐摩耗性は良好なものとなる。 Moreover, under internal pattern layer is protected by the so is provided below the recoatability ionizing radiation-curable resin layer recoatability ionizing radiation-curable resin (and top coat layer) The top coat layer in matte pattern layer since is provided a result that is protected by a top coat layer, these internal pattern layer, the wear resistance of the matte pattern layer becomes excellent.

【0010】また、本発明の本発明の耐摩耗性を有する化粧材の第3の形態では、上記いずれかの形態に於いて、トップコート層の硬化性樹脂が、電離放射線硬化性樹脂又は熱硬化性樹脂である構成とした。 [0010] In the third embodiment of the decorative material having a wear resistance of the present invention of the present invention, the In one embodiment, the curable resin of the topcoat layer is an ionizing radiation curable resin or heat configured as a curable resin.

【0011】この様に、最表面となるトップコート層に熱硬化性樹脂を使用すれば、安価且つ平易に優れた耐摩耗性が得られ、また、トップコート層に電離放射線硬化性樹脂を使用すれば極めて優れた耐摩耗性が得られる。 [0011] Thus, the use of thermosetting resins in the top coat layer serving as the outermost surface, low cost and easy excellent wear resistance can be obtained and, using an ionizing radiation-curable resin in the top coat layer very good wear resistance can be obtained by.

【0012】 [0012]

【発明の実施の形態】以下、図面を参照しながら、本発明の耐摩耗性を有する化粧材について、実施の形態を説明する。 BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, with reference to the drawings, the decorative material having a wear resistance of the present invention, exemplary embodiments will be described.

【0013】先ず、図1(A)は、本発明の耐摩耗性を有する化粧材Dの一形態として、基体1上に、全ベタ層2A及び柄パターン層2Bとからなる内部絵柄層2が形成された上に、フィラーFを含有してリコート性を有し且つ艶消しのリコート性電離放射線硬化性樹脂層3A、 [0013] First, FIG. 1 (A), as a form of decorative material D having a wear resistance of the present invention, on the substrate 1, an internal pattern layer 2 composed of a total solid layer 2A and the pattern pattern layer 2B is on which it is formed, and matte recoatability ionizing radiation-curable resin layer 3A has recoatability contain a filler F,
部分的に形成された艶有り絵柄層4A、硬化性樹脂からなるトップコート層5がこの順に形成された構成の化粧材である。 Partially formed glossy pattern layer 4A, a top coat layer 5 of the curable resin is a decorative material formed in this order. トップコート層5は、熱可塑性樹脂でも良いが、好ましくは電離放射線硬化性樹脂又は熱硬化性樹脂で形成する。 Top coat layer 5 may be a thermoplastic resin, but is preferably formed of an ionizing radiation-curable resin or a thermosetting resin. 一方、図1(B)は、図1(A)の構成に於いて、艶消しのリコート性電離放射線硬化性樹脂層3 Meanwhile, FIG. 1 (B), FIG. 1 at the structure of (A), recoatability ionizing radiation-curable resin layer of the matte 3
Aを、艶有りのリコート性電離放射線硬化性樹脂層3B The A, gloss of recoatability ionizing radiation-curable resin layer 3B
として、その上の艶有り絵柄層4Aを、艶消し絵柄層4 As the glossy picture layer 4A thereon, matte pattern layer 4
Bに置き換えた構成の別の形態の化粧材である。 A decorative material of another form of structure that was replaced by the B.

【0014】以下、更に各層について詳述する。 [0014] The following will be described in more detail for each layer.

【0015】〔基体〕基体1としては、形状、材質、その他特性等は特に制限は無い。 [0015] As the [base] base 1, shape, material, and other characteristics is not particularly limited. 例えば形状は、シートの他、板、立体物などでも良い。 For example shape, other sheets, plates, or the like three-dimensional object. また、材質は、紙系、木質系、金属系、無機非金属系(セラミック系、非セラミックス窯業系等)、樹脂系等である。 The material may be paper-based, woody, metallic, inorganic non-metallic (ceramic, non ceramic ceramic-based, etc.), a resin or the like. また、インキ浸透性のあるもの(紙、不織布等)、インキ浸透性の無いもの(樹脂シート等)、いずれでも良い。 Also, some of the ink permeability (paper, nonwoven fabric, etc.), having no ink permeability (resin sheet), may be either. 中でも紙や樹脂シート(フィルム)は代表的であり、これらを基体として用いれば、本発明の化粧材は化粧シートとなり得る。 Among them, paper or a resin sheet (film) is a typical, the use of these as the substrate, the decorative material of the present invention can be a decorative sheet.

【0016】また、紙系以外の繊維質基体としては、ポリエステル樹脂、アクリル樹脂、ナイロン、ビニロン、 [0016] As the fibrous substrate other than paper-based, polyester resins, acrylic resins, nylon, vinylon,
硝子等の繊維からなる不織布等も用いられる。 Nonwoven fabrics made of fibers such as glass may also be used. 不織布は前記紙系の場合と同様に、アクリル樹脂、スチレンブタジエンゴム、メラミン樹脂、ウレタン樹脂等の樹脂を添加(抄造後樹脂含浸、又は抄造時に内填)させたものでも良い。 Nonwoven fabric as in the case of the paper-based, acrylic resin, styrene-butadiene rubber, a melamine resin, adding a resin and urethane resin (papermaking after the resin impregnation, or inner Hama during papermaking) may be those is allowed.

【0017】樹脂系では、例えば、ポリエチレン、ポリプロピレン、オレフィン系熱可塑性エラストマー等のポリオレフィン系樹脂、塩化ビニル樹脂、塩化ビニリデン樹脂、ポリビニルアルコール、エチレン−ビニルアルコール共重合体等のビニル系樹脂、ポリエチレンテレフタレート、ポリブチレンテレフタレート等のポリエステル樹脂、ポリメタクリル酸メチル、ポリアクリル酸メチル、ポリメタクリル酸エチル等のアクリル樹脂、ポリスチレン、アクリロニトリル−ブタジエン−スチレン共重合体(ABS樹脂)、三酢酸セルロース、セロハン、ポリカーボネート等の樹脂等の樹脂材料がある。 [0017] In the resin system, for example, polyethylene, polypropylene, polyolefin resins such as olefin-based thermoplastic elastomer, vinyl chloride resin, vinylidene chloride resin, polyvinyl alcohol, ethylene - vinyl alcohol copolymer vinyl resins, polyethylene terephthalate , polybutylene terephthalate polyester resin, polymethyl methacrylate, polymethyl acrylate, an acrylic resin polyethylmethacrylate methacrylate, polystyrene, acrylonitrile - butadiene - styrene copolymer (ABS resin), cellulose triacetate, cellophane, polycarbonate there is a resin material such as resin and the like. これら樹脂は、シート、板、立体物として使用される。 These resins, sheets, plates, is used as a three-dimensional object. また、樹脂系では、フェノール樹脂、尿素樹脂、不飽和ポリエステル樹脂、ウレタン樹脂、エポキシ樹脂、メラミン樹脂等の熱硬化性樹脂からなる熱硬化性樹脂板、フェノール樹脂、尿素樹脂、不飽和ポリエステル樹脂、ウレタン樹脂、エポキシ樹脂、メラミン樹脂、ジアリルフタレート樹脂等の樹脂を、硝子繊維不織布、布帛、紙、その他各種繊維質基体に含浸硬化させて複合化した所謂FRP Further, in the resin, phenol resin, urea resin, unsaturated polyester resins, urethane resins, epoxy resins, thermosetting resin plate made of a thermosetting resin such as melamine resins, phenol resins, urea resins, unsaturated polyester resins, urethane resins, epoxy resins, melamine resins, and resins such as diallyl phthalate resin, glass fiber nonwoven fabric, fabric, paper, a so-called FRP complexed impregnated cured in other various fibrous substrate
(繊維強化プラスチック)板、等の樹脂板も有る。 (Fiber-reinforced plastic) plate, also there is a resin plate and the like.

【0018】また、木質系では、例えば、杉、檜、樫、 [0018] In addition, in the wood-based, for example, cedar, cypress, oak,
ラワン、チーク等からなる単板、合板、パーティクルボード、繊維板、集成材等の木質材料がある。 Lauan, veneer made of teak, etc., plywood, particle board, fiber board, there is a woody material, such as laminated wood. 木質系はシート、板、立体物として使用される。 Wood is used sheets, plates, as three-dimensional object. また、金属系では、例えば、鉄、アルミニウム、ステンレス鋼、銅等の金属材料がある。 Further, the metal-based, for example, iron, aluminum, stainless steel, metal material such as copper. 金属系はシート(箔)、板、立体物として使用される。 Metallic sheet (foil), a plate, is used as a three-dimensional object. また、無機非金属系では、例えば、押し出しセメント、スラグセメント、ALC(軽量気泡コンクリート)、GRC(硝子繊維強化コンクリート)、 In addition, the inorganic non-metallic, for example, extrusion cement, slag cement, ALC (lightweight concrete), GRC (glass fiber reinforced concrete),
パルプセメント、木片セメント、石綿セメント、ケイ酸カルシウム、石膏、石膏スラグ等の非セラミックス窯業系材料、土器、陶器、磁器、セッ器、硝子、琺瑯等のセラミックス系材料等がある。 Pulp cement, cemented chip, asbestos cement, calcium silicate, gypsum, non ceramic ceramic-based materials such as gypsum slag, pottery, earthenware, porcelain, stoneware, glass, there is a ceramic material such as enamel. 無機非金属系は主として板や立体物として使用される。 Inorganic nonmetal is used primarily as a plate or a three-dimensional object.

【0019】或いは、上記各種材料の2種以上を接着剤、熱融着等の公知の手段により積層して複合化した基体等も挙げられる。 [0019] Alternatively, the adhesive of two or more of the various materials, substrates, etc. complexed laminated by known means heat sealing or the like may be mentioned. 例えば、樹脂含浸紙やFRP等はその一例でもある。 For example, resin-impregnated paper and FRP and the like is also an example.

【0020】また、その他特性は、例えばイキン浸透性の有無等である。 Further, other characteristics, for example Ikin permeability presence or absence. 例えば、インキ浸透性の無い基体は、 For example, there is no base of ink permeability,
塩化ビニル樹脂、ポリエチレンテレフタレート(PE Vinyl chloride resin, polyethylene terephthalate (PE
T)、ポリオレフィン系樹脂等による樹脂シート等であり、インキ浸透性の有る基体は、例えば印刷用純白紙、 T), a resin sheet according to polyolefin resins, the substrate having the ink permeability, for example, printing pure white paper,
紙間強化紙、硬化性樹脂を含浸させた含浸紙等の紙類、 Paper impregnated paper or the like which is impregnated sheet between reinforced paper, a curable resin,
織布、不織布等のその他の繊維質基体である。 Woven fabrics, and other fibrous substrates such as a nonwoven fabric.

【0021】基体の厚みは、形状、材質、用途等にもよるが、例えば紙系の様な繊維質基体を使用する場合は、 [0021] The thickness of the substrate, shape, material, if depending on the application or the like, using, for example, fibrous substrate, such as paper system,
坪量で50〜150g/m 2程度で、厚みが50〜30 In 50 to 150 g / m 2 approximately at a basis weight, thickness 50-30
0μm程度が望ましい。 About 0μm is desirable.

【0022】〔内部絵柄層〕内部絵柄層2は、目的とする意匠表現や要求物性等に応じて、化粧材に於ける従来公知の形成方法・材料で形成すれば良く、特に限定は無い。 [0022] [interior design layer] internal pattern layer 2, depending on the design expression and required physical properties such as for the purpose, may be formed by in the decorative material known forming methods and materials, it is not particularly limited.

【0023】なお、内部絵柄層2は、部分形成と全面形成とで区分けすれば、図1で例示の如く、任意のパターン形状を表現する為に部分的に形成される柄パターン層2Bと、全面に形成される全ベタ層2Aとに分類することができる。 [0023] The internal pattern layer 2, if divided by the partial formation and formed over the entire surface, as illustrated in FIG. 1, and the handle pattern layer 2B partially formed to represent arbitrary pattern, it can be classified into a total solid layer 2A formed on the entire surface. 全ベタ層2Aと柄パターン層2Bとは各々単独で使用される事もあるが、通常は、下地としての全ベタ層2Aとその上に形成して絵柄パターンを表現する為の柄パターン層2Bとを組み合わせて使用する事が多い。 Some things are each used alone and total solid layer 2A and the handle pattern layer 2B, but typically, the handle pattern layer 2B for expressing the picture pattern formed thereon and full solid layer 2A as a base it is often used in combination bets.

【0024】そして、内部絵柄層2は、グラビア印刷、 [0024] Then, the internal pattern layer 2, gravure printing,
シルクスクリーン印刷、オフセット印刷、電子写真複写、手描(例えば筆描等)等の従来公知の印刷等による形成方法及び材料で形成すれば良い。 Silk screen printing, offset printing, electrophotographic copying may be formed by forming methods and materials by conventional printing such as Te描 (e.g. brush 描等). 内部絵柄層は通常、顔料添加で着色した層とする。 Internal pattern layer is usually a layer colored with pigments added. 内部絵柄層が表す絵柄は任意であり、用途に合わせて、例えば木目模様、石目模様、布目模様、タイル調模様、煉瓦調模様、皮絞模様、文字、幾何学模様等である。 A pattern is any representative of the internal picture layer, according to the application, for example wood grain, pebble pattern, weft pattern, tile tone pattern, brick pattern, Kawashibo patterns, characters, geometric patterns and the like. なお、内部絵柄層のうち全面ベタとなる全ベタ層は、グラビアコート、ロールコート等の公知の塗工法によって塗料で形成する事もできる。 Note that the entire solid layer as a whole-area solid of the internal pattern layer may also be formed gravure coating, by a known coating method such as roll coating with paint.

【0025】内部絵柄層2を形成する為のインキ(又は塗料)は、一般的なインキ(又は塗料)同様に、バインダー等からなるビヒクル、顔料や染料等の着色剤、これに適宜加える各種添加剤からなる。 [0025] Ink for forming an inner pattern layer 2 (or paint), as well common ink (or paint), a vehicle composed of a binder or the like, colorants such as pigments and dyes, various additives optionally added thereto consisting of agents. バインダーの樹脂には、例えば、塩素化ポリオレフィン樹脂、ポリエステル樹脂、アクリル樹脂、セルロース系樹脂、塩化ビニル− The resin binder, for example, chlorinated polyolefin resins, polyester resins, acrylic resins, cellulose resins, vinyl chloride -
酢酸ビニル共重合体、ポリウレタン樹脂等といった汎用の樹脂を選択出来、単体又はこれらを含む混合物として使用する。 Vinyl acetate copolymer, can choose the purpose resins such polyurethane resins, used alone or as a mixture containing them. 但し、リコート性電離放射線硬化性樹脂層との密着性の点で、バインダーの樹脂としては、ニトロセルロース系やアクリル樹脂系は望ましい樹脂である。 However, in view of adhesion to the recoatability ionizing radiation curable resin layer, the resin binder, nitrocellulose-based and acrylic resin are preferable resin.

【0026】また、着色剤としては、例えば、チタン白、亜鉛華、弁柄、朱、群青、コバルトブルー、チタン黄、黄鉛、カーボンブラック等の無機顔料、イソインドリノン、ハンザイエローA、キナクリドン、パーマネントレッド4R、フタロシアニンブルー、インダスレンブルーRS、アニリンブラック等の有機顔料(或いは染料も含む)、アルミニウム、真鍮、等の金属顔料、二酸化チタン被覆雲母、塩基性炭酸鉛等の箔粉からなる真珠光沢(パール)顔料等を使用すれば良い。 [0026] In addition, as the coloring agent, for example, titanium white, zinc white, red iron, Zhu, ultramarine blue, cobalt blue, titanium yellow, chrome yellow, inorganic pigments such as carbon black, isoindolinone, Hansa yellow A, quinacridone , permanent red 4R, phthalocyanine blue, (including or dye) indanthrene blue RS, organic pigments such as aniline black, aluminum, brass, metal pigments etc., titanium dioxide-coated mica, foil powders such basic lead carbonate pearlescent (pearl) may be used pigments, and the like.

【0027】なお、内部絵柄層2は金属薄膜層等でも良い。 [0027] The internal pattern layer 2 may be a metal thin film layer or the like. 金属薄膜層の形成は、アルミニウム、クロム、金、 Formation of the metal thin film layer, aluminum, chromium, gold,
銀、銅等の金属を用い、真空蒸着、スパッタリング等の方法で製膜する。 Silver, a metal such as copper, forming a film by vacuum deposition method such as sputtering. 或いはこれらの組み合わせでも良い。 Or it may be a combination of these.
該金属薄膜層は、全面に設けても(全ベタ層2Aとなる)、或いは、部分的にパターン状に設けても(柄パターン層2Bとなる)良い。 The metal thin film layer may be provided on the entire surface (the entire solid layer 2A), or be provided partially pattern (a pattern pattern layer 2B) good.

【0028】〔リコート性電離放射線硬化性樹脂層〕リコート性電離放射線硬化性樹脂層3A又は3Bは、層中にフィラーを含有し、且つリコート性(後塗装適性)を有する電離放射線硬化性樹脂からなる層である。 [0028] [recoatability ionizing radiation curing resin layer] recoatability ionizing radiation-curable resin layer 3A or 3B contains the filler in the layer, and the ionizing radiation-curable resin having recoating property (rear coatability) it is composed of layers. そして、リコート性電離放射線硬化性樹脂層3Aは艶有りの層であり、リコート性電離放射線硬化性樹脂層3Bは艶消しの層である。 The recoatability ionizing radiation curable resin layer 3A is a layer there gloss, recoatability ionizing radiation curable resin layer 3B is a layer of matte. また、本発明ではこのリコート性電離放射線硬化性樹脂層3A又は3Bは、該層上に他の層を形成する前に完全硬化させた後でも密着良く積層できる。 Also, the recoatability ionizing radiation-curable resin layer 3A or 3B in the present invention can be laminated may contact even after being completely cured before forming another layer on said layer. したがって、リコート性電離放射線硬化性樹脂層を未硬化又は半硬化等の完全硬化前の状態を維持して、該層上にトップコート層、及び艶消し絵柄層或いは艶有り絵柄層等の上層を、塗工・印刷等で形成しなくても密着良く積層できる。 Therefore, to maintain the state before complete curing of such uncured or semi-cured recoatability ionizing radiation curable resin layer, a topcoat layer on said layer, and matting pattern layer or the upper layer of the glossy picture layer, etc. , can be laminated may contact even without forming by coating or printing. これに対して、トップコート層等の上記上層を、リコート性電離放射線硬化性樹脂3A又は3 In contrast, the upper layer such as a top coat layer, recoatability ionizing radiation curable resin 3A or 3
Bを完全硬化前の状態としてその上に形成し、この後で、リコート性電離放射線硬化性樹脂層を完全硬化させる場合には、トップコート層等の上層を形成時には、リコート性電離放射線硬化性樹脂層は非粘着状態としなければ、印刷機や塗工機でトップコート層等の上層を形成する事ができない。 B was formed thereon as the state before complete curing, after this, in the case of completely curing the recoating property ionizing radiation-curable resin layer, during formation of the upper layer of such a topcoat layer, recoatability ionizing radiation curable unless the resin layer is a non-tacky state, it is impossible to form the upper layer of the top coat layer or the like in the printing machine or coating machine. ところが、リコート性電離放射線硬化性樹脂層3A又は3Bが完全硬化後でもその上にトップコート層等の前記上層を密着良く形成できる場合には、リコート性電離放射線硬化性樹脂層は完全硬化前の状態では粘着状態でも液状状態でも良く、要求物性等に応じて電離放射線硬化性樹脂をその分自由に選択できる利点がある。 However, if the recoatability ionizing radiation-curable resin layer 3A or 3B can be formed well in close contact with the upper layer of the top coat layer or the like thereon even after full cure, the recoatability ionizing radiation curable resin layer before complete curing in the state may be in a liquid state in a tacky state, it is advantageous in that the ionizing radiation curable resin can be selected correspondingly freely according to the required physical properties and the like.

【0029】なお、本発明で言う「リコート性」とは、 [0029] It should be noted that, in the present invention, the term "recoating soluble",
この(リコート性)電離放射線硬化性樹脂層3A又は3 The (recoatability) ionizing radiation curable resin layer 3A or 3
B上に、塗膜として、ウレタン系樹脂、電離放射線硬化性樹脂、メラミンアルキド樹脂、その他樹脂等からなるトップコート層、及び艶消し絵柄層や艶有り絵柄層等の上層を、塗液やインキによって積層した際に、実使用上十分な密着性が保持されることを意味する。 On the B, as a coating, urethane resins, ionizing radiation curable resins, melamine alkyd resins, and other topcoat layer composed of a resin or the like, and an upper layer, such as a matte pattern layer and glossy picture layer, coating liquid or ink when laminated by, practically sufficient adhesion is meant to be retained. 具体的には例えば、JIS K5400 で規定する付着性試験(リコート後の塗膜表面のシリコーンや汚れを消しゴムで除去した後、カッターナイフで少なくともリコート性電離放射線硬化性樹脂層にまで達する切り込みを入れ、 Specifically, for example, after the silicone and dirt adhesion test (the coating film surface after recoating specified in JIS K5400 was removed with an eraser, an incision reaching the least recoatability ionizing radiation-curable resin layer with a cutter knife ,
表面に貼り付けたセロハン粘着テープを剥がして塗膜の剥離状況で評価する方法等)で、リコート性電離放射線硬化性樹脂層と、その上に形成されたトップコート層等の前記上層との層間で、これら層同士が剥離しない密着強度を有する事である。 Peel off the pasted cellophane adhesive tape to the surface by a method, etc.) to evaluate in the state of peeling of the coating film layers of the recoatability ionizing radiation curable resin layer, and the upper layer of the top coat layer or the like formed thereon in that it has a adhesive strength of the layers to each other without being stripped. なお、トップコート層は、通常は塗工法で形成するが、塗工法のみならず、印刷法で全面に形成することも可能である。 Incidentally, the top coat layer is normally will form in the coating method, not coating method only, it is also possible to form on the entire surface by a printing method. また、部分形成する、 In addition, a portion formation,
艶消し絵柄層及び艶有り絵柄層は通常は印刷で形成する。 Matte pattern layer and glossy pattern layer is usually formed by printing. そこで、「リコート」、すなわち、再塗工(或いは再塗装)は、塗工法のみならず印刷等の他の手法による積層に対する意味も包含する。 Therefore, "recoating", i.e., re-coating (or repainting) also means for lamination by other methods such as printing not coating method only encompasses.

【0030】この様なリコート性電離放射線硬化性樹脂層3A又は3Bに用いる電離放射線硬化性樹脂としては、分子中にアクリロイル基等のラジカル重合性不飽和結合、又はエポキシ基等のカチオン重合性官能基を有する、プレポリマー(所謂オリゴマーも包含する)及び/ Examples of the ionizing radiation-curable resin used in such recoatability ionizing radiation-curable resin layer 3A or 3B, a radical polymerizable unsaturated bond acryloyl group in the molecule, or cationically polymerizable functional, such as an epoxy group having a group, (also includes so-called oligomer) prepolymer and /
又はモノマーからなる組成物で、紫外線や電子線等の電離放射線により硬化可能なものが用いられる。 Or with a composition comprising a monomer, capable curing is used by ionizing radiation such as ultraviolet rays or electron beams. また、プレポリマー、モノマーは単体又は複数種を混合して用いる。 Further, prepolymers, monomers used in combination alone or in combination. なお、ここで電離放射線とは、分子を重合或いは架橋させ得るエネルギーを有する電磁波又は荷電粒子を意味し、通常、紫外線(UV)又は電子線(EB)が用いられる。 Here, the ionizing radiation is meant electromagnetic wave or charged particles having an energy capable of polymerizing or to crosslink the molecules, usually ultraviolet (UV) or electron beam (EB) is used.

【0031】通常、プレポリマーには、不飽和ポリエステル類、ポリアクリレート類、カチオン重合型エポキシ類等が使用され、モノマーには、スチレン系、アクリル酸エステル系、不飽和カルボン酸アミド等が使用される。 [0031] Normally, the prepolymer, unsaturated polyesters, polyacrylates, are used cationically polymerizable epoxy compounds or the like, the monomer is styrene, acrylic ester, etc., unsaturated carboxylic acid amides are used that.

【0032】例えば、分子中にラジカル重合性不飽和基を有するプレポリマーの例としては、ポリエステル(メタ)アクリレート、ウレタン(メタ)アクリレート、エポキシ(メタ)アクリレート、メラミン(メタ)アクリレート、トリアジン(メタ)アクリレート、シリコーン(メタ)アクリレート等が使用できる。 [0032] For example, as examples of the prepolymer having a radically polymerizable unsaturated groups in the molecule, a polyester (meth) acrylate, urethane (meth) acrylate, epoxy (meth) acrylate, melamine (meth) acrylates, triazine (meth ) acrylate, silicone (meth) acrylate. なお、(メタ) In addition, (meth)
アクリレートとはメタクリレート又はアクリレートの意味である。 The acrylate means a methacrylate or acrylate. また、分子中にカチオン重合性官能基を有するプレポリマーの例としては、ビスフェノール型エポキシ樹脂、ノボラック型エポキシ化合物等のエポキシ系樹脂、脂肪酸系ビニルエーテル、芳香族系ビニルエーテル等のビニルエーテル系樹脂のプレポリマーがある。 In addition, examples of the prepolymer having a cation polymerizable functional group in the molecule, bisphenol type epoxy resin, epoxy resins such as novolak type epoxy compounds, fatty acid ether, a prepolymer vinyl ether based resin such as aromatic ether there is.

【0033】また、分子中にラジカル重合性不飽和基を有するモノマーの例としては、単官能モノマーでは、メチル(メタ)アクリレート、2−エチルヘキシル(メタ)アクリレート、フェノキシエチル(メタ)アクリレート等がある。 Further, examples of the monomer having a radical polymerizable unsaturated group in the molecule, the monofunctional monomer, methyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, phenoxyethyl (meth) acrylate . また、多官能モノマーでは、ジエチレングリコールジ(メタ)アクリレート、プロピレングリコールジ(メタ)アクリレート、トリメチールプロパントリ(メタ)アクリレート、トリメチロールプロパンエチレンオキサイドトリ(メタ)アクリレート、ジペンタエリスリトールペンタ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート等もある。 Further, the polyfunctional monomer, diethylene glycol di (meth) acrylate, propylene glycol di (meth) acrylate, trimethylopropane steel tri (meth) acrylate, trimethylolpropane ethylene oxide tri (meth) acrylate, dipentaerythritol penta (meth) acrylate , there is also a dipentaerythritol hexa (meth) acrylate.

【0034】なお、リコート性を電離放射線硬化性樹脂からなる層に付与してリコート性電離放射線硬化性樹脂層3A又は3Bとする為には、電離放射線硬化性樹脂硬化物の平均架橋間分子量が200〜1000程度になる様に設計する事が好ましい。 [0034] Incidentally, in order to recoatability ionizing radiation-curable resin layer 3A or 3B by applying a layer composed of an ionizing radiation curable resin recoatability an average molecular weight between crosslinks of ionizing radiation-curable resin cured product it is preferable to design so as to be about 200 to 1000. 平均架橋間分子量を制御する手段として、平均架橋間分子量を上げる場合は、添加モノマー濃度を減らす、プレポリマーやアクリレートモノマーの官能基数を減らすといった手段がある。 As a means of controlling the average molecular weight between crosslinks, when increasing the average molecular weight between crosslinks reduces the added monomer concentration, there is a means such as reducing the functionality of the prepolymer and an acrylate monomer. 一方、 on the other hand
平均架橋間分子量を下げる場合は、逆にモノマー濃度を増やしたり、3官能以上のアクリレートモノマーを添加してやれば良い。 If lowering the average molecular weight between crosslinks is increased or the monomer concentration in the reverse may do it by adding 3 or more functional acrylate monomers. なお、平均架橋間分子量とは、平均架橋間分子量=全体の分子量/架橋点の数であり、全体の分子量はΣ(各成分の配合モル数×各成分の分子量)であり、架橋点の数はΣ〔{(各成分の官能基数−1)× Incidentally, the average molecular weight between crosslinks, the number of average molecular weight between crosslinks = overall molecular weight / crosslinking points, the overall molecular weight is sigma (molecular weight of the formulation moles × each component of each component), the number of crosslinking points the Σ [{(number of functional groups -1 of each component) ×
2}×各成分のモル数〕である。 2} × the molar number] of each component.

【0035】なお、紫外線又は可視光線にて硬化させる場合には、上記電離放射線硬化性樹脂に、さらに光重合開始剤を添加する。 It should be noted, in the case of curing by ultraviolet or visible radiation, in the ionizing radiation-curable resin, further adding a photopolymerization initiator. ラジカル重合性不飽和基を有する樹脂系の場合は、光重合開始剤として、アセトフェノン類、ベンゾフェノン類、チオキサントン類、ベンゾイン、ベンゾインメチルエーテル類を単独又は混合して用いることができる。 For resin system having a radical polymerizable unsaturated group, as the photopolymerization initiator, acetophenones, benzophenones, thioxanthones, benzoins, benzoin methyl ethers can be used singly or as a mixture. また、カチオン重合性官能基を有する樹脂系の場合は、光重合開始剤として、芳香族ジアゾニウム塩、芳香族スルホニウム塩、芳香族ヨードニウム塩、メタロセン化合物、ベンゾインスルホン酸エステル等を単独又は混合物として用いることができる。 In the case of a resin system having a cation polymerizable functional group, it is used as a photopolymerization initiator, an aromatic diazonium salts, aromatic sulfonium salts, aromatic iodonium salts, metallocene compounds, benzoin sulfonic esters and the like alone or as a mixture be able to. なお、 It should be noted that,
これらの光重合開始剤の添加量としては、電離放射線硬化性樹脂100質量部に対して、0.1〜10質量部程度である。 The addition amount of the photopolymerization initiator, relative to 100 parts by mass of the ionizing radiation curable resin is about 0.1 to 10 parts by weight.

【0036】なお、電離放射線の線源としては、紫外線源としては、超高圧水銀灯、高圧水銀灯、低圧水銀灯、 [0036] As the source of ionizing radiation, the ultraviolet light source, ultra-high pressure mercury lamp, high pressure mercury lamp, low pressure mercury lamp,
カーボンアーク灯、ブラックライト型蛍光灯、メタルハライドランプ等の光源が使用される。 Carbon arc lamp, black light fluorescent lamp, a light source such as a metal halide lamp is used. 紫外線の波長としては通常190〜380nmの波長域が主として用いられる。 The wavelength of the ultraviolet wavelength range of normal 190~380nm is mainly used. また、電子線源としては、コッククロフトワルトン型、バンデグラフト型、共振変圧器型、絶縁コア変圧器型、或いは、直線型、ダイナミトロン型、高周波型等の各種電子線加速器を用い、100〜1000keV、 As the electron beam source, Cockcroft Walton type, Van de Graft type, resonance transformer type, insulated core transformer type, or using linear, dynamitron type, various electron beam accelerators of the high frequency type, etc., 100~1000KeV ,
好ましくは、100〜300keVのエネルギーをもつ電子を照射するものが使用される。 Preferably, it irradiates an electron having an energy of 100~300keV is used. 電子線の照射量は、 The irradiation amount of the electron beam,
通常2〜15Mrad程度である。 It is usually about 2~15Mrad.

【0037】リコート性電離放射線硬化性樹脂層3A又は3B中にフィラーFを含有させる事によって、耐摩耗性が向上する。 [0037] During recoatability ionizing radiation-curable resin layer 3A or 3B by the inclusion of filler F, the wear resistance is improved. この様なフィラーとしては、例えば、α Examples of such fillers include, for example, alpha
−アルミナ、シリカ、炭化ケイ素等の無機粒子、架橋アクリル樹脂ビーズ等の有機粒子等を上記した電離放射線硬化性樹脂からなる組成物に添加して使用する。 - alumina, silica, inorganic particles such as silicon carbide, is used by adding to a composition comprising an ionizing radiation-curable resin and organic particles such as described above, such as cross-linked acrylic resin beads. フィラーの粒子形状、粒径は任意であるが、リコート性電離放射線硬化性樹脂層3A又は3Bを形成する為の塗液の塗工装置の摩耗の問題から球状が望ましい。 Particle shape of the filler, although the particle size is arbitrary, spherical is preferable from abrasion problem of the coating apparatus of the coating solution for forming the recoatability ionizing radiation curable resin layer 3A or 3B. またフィラーの粒径は平均粒径で通常はリコート性電離放射線硬化性樹脂層3A又は3Bの厚みの0.3〜2倍程度とするのが良い。 The particle size of the filler is usually an average particle size of amount may be 0.3 to 2 times the thickness of the recoatability ionizing radiation-curable resin layer 3A or 3B. 0.3未満では十分な耐摩耗性を得にくく、2 Difficult to obtain sufficient wear resistance is less than 0.3, 2
を超えるとリコート性電離放射線硬化性樹脂層3A又は3Bの表面にフィラーがはみ出して脱落する恐れが出る。 The filler protrudes fear leaves fall off the surface of the recoatability ionizing radiation-curable resin layer 3A or 3B exceeds. くわえて、表面凹凸の為にトップコート層の印刷適性・塗工適性が悪くなる。 In addition, printability, coating suitability of the top coat layer is made worse because of surface irregularities. なお、フィラーの含有量は、 The content of the filler,
リコート性電離放射線硬化性樹脂層3A又は3Bを透して下の内部絵柄層が見える程度以上の透明性が損なわれない範囲内で、要求物性等により適宜量とすれば良い。 To the extent that more transparency looking degree internal pattern layer beneath it through recoatability ionizing radiation curable resin layer 3A or 3B is not impaired by the required physical properties such as may be the appropriate amount.

【0038】また、リコート性電離放射線硬化性樹脂層を艶消しのリコート性電離放射線硬化性樹脂層3Aとするには、更に、上記の様な電離放射線硬化性樹脂の組成物に更に艶消し剤を添加する。 Further, recoatability ionizing radiation curable resin layer to the recoatability ionizing radiation-curable resin layer 3A matte further further matting agent in the compositions of the ionizing radiation curable resin, such as the It is added. 艶消し剤としては公知の物で良い。 The matting agent may in a known thing. 例えば、艶消し剤としては、シリカ、硫酸バリウム、炭酸カルシウム等の粉末を使用する。 For example, the matting agent, use silica, barium sulfate, a powder such as calcium carbonate.

【0039】一方、この様な艶消し剤を添加しなければ、リコート性電離放射線硬化性樹脂層は艶有りのリコート性電離放射線硬化性樹脂層3Bとすることができる。 On the other hand, if the addition of such matting agents, recoatability ionizing radiation-curable resin layer may be a recoatability ionizing radiation-curable resin layer 3B of there gloss. なお、艶消し剤を添加しなくても、含有されるフィラーによって艶が低下して差し支える場合には、艶有りのリコート性電離放射線硬化性樹脂層上に、少なくともその表面凹凸を平坦化する程度の厚さに、フィラー未含有又はフィラー含有量を落とした電離放射線硬化性樹脂層を高艶シーラー層として、形成しても良い。 Even without the addition of matting agents, when interfere reduced gloss by filler contained is in recoatability ionizing radiation-curable resin layer on there gloss, to flatten at least the surface roughness a thickness on the order, an ionizing radiation-curable resin layer has been dropped filler non-containing or filler content as Kotsuya sealer layer may be formed. 艶消し絵柄層4Bは高艶シーラー層の上に形成する。 Matte pattern layer 4B is formed on the Kotsuya sealer layer.

【0040】そして、上記の様な組成物からる電離放射線硬化性樹脂は、通常は常温(室温乃至は適宜加熱した塗工温度において)にて液状の塗液として、ロールコート、フローコート等の従来公知の塗工法で塗工する。 [0040] Then, the above-described such compositions Calalou ionizing radiation curing resin is usually a coating solution liquid at normal temperature (at room temperature or the coating temperature appropriately heated), roll coating, such as flow coating to coated by a known coating method. なお、リコート性電離放射線硬化性樹脂層の厚さは、要求される耐摩耗性の程度等の要求物性に応じて適宜厚さとすれば良く特に制限は無いが、例えば10〜50μm程度とする。 The thickness of the recoatability ionizing radiation-curable resin layer is not particularly limited well if appropriate thickness depending on the required physical properties such as the degree of the required wear resistance, for example, 10~50μm about.

【0041】〔艶有り絵柄層〕艶有り絵柄層4Aは、該層表面が艶有りで、艶消しのリコート性電離放射線硬化性樹脂層3A上に部分的に形成され、艶有り絵柄層部分が艶有りの絵柄パターンを表現する為の層である。 [0041] [glossy picture layer] glossy pattern layer 4A is a there gloss said layer surface, partially formed on recoatability ionizing radiation curable resin layer 3A matte and glossy picture layer portion it is a layer for expressing the gloss of a picture pattern. この艶有り絵柄層4Aは、前述した内部絵柄層2でその形成に用いるインキ(又は)塗料を使用して印刷等の公知の形成方法で形成すれば良い。 The glossy pattern layer 4A may be formed by a known forming method such as printing, using an ink (or) coating used in its formation inside the pattern layer 2 described above.

【0042】そして、艶有り絵柄層4Aの未形成部からは艶消しのリコート性電離放射線硬化性樹脂層3Aが露出し、この艶有り絵柄層4Aと艶消しのリコート性電離放射線硬化性樹脂層3Aとによる艶の高低差によって、 [0042] Then, gloss from unformed portions of the pattern layer 4A is exposed recoatability ionizing radiation-curable resin layer 3A matte, recoatability ionizing radiation-curable resin layer of the pattern layer 4A and matte there this gloss by a difference in gloss due to the 3A,
艶有り絵柄層4Aが形成されたパターン形状に同調した艶の大小による模様を現出させることができる。 Thereby revealing the pattern due to glossy magnitude of glossy pattern layer 4A is tuned to the formed pattern. また、 Also,
その艶の大小による模様は、艶有り絵柄層4Aと内部絵柄層2との色の差による模様と同調させる事もできる。 Its magnitude by design of gloss can also be tuned with a pattern due to the difference in the color of the pattern layer 4A and the inner pattern layer 2 there luster.
なお、本発明ではこの艶有り絵柄層の上に、更にトップコート層が形成されるが、このトップコート層は、この艶の高低差(大小)を完全に消失させてしまわない程度の厚さに形成し、この艶の高低差を化粧材表面の意匠表現とするのである。 Incidentally, on this glossy pattern layer in the present invention, further has a top coat layer is formed, the top coat layer has a thickness enough not Shimawa completely abolished height difference of the gloss (magnitude) formed in, it is to the height difference of the gloss and design representation of the decorative material surface. この様な、艶有り絵柄層4A、艶消しのリコート性電離放射線硬化性樹脂層3A、及び内部絵柄層2等による意匠表現は任意であるが、例えば内部絵柄層の絵柄は木目柄として、艶有り絵柄層4Aで木目導管溝柄を表現する等ある。 Such, glossy picture layer 4A, recoatability ionizing radiation curable resin layer 3A matte, and the design represented by the internal pattern layer 2 and the like is optional, as grain pattern design, for example the internal pattern layer, gloss There picture layer 4A is like representing the grain conduit groove pattern in. もちろん、意匠表現は、この他、石目柄、砂目柄、抽象柄等、用途に応じたもので良い。 Of course, design representation, the other, pebble patterns, grain patterns, abstract patterns, etc., may be one depending on the application.

【0043】〔艶消し絵柄層〕艶消し絵柄層4Bは、該層表面が艶消しで、艶有りのリコート性電離放射線硬化性樹脂層3B上に部分的に形成され、前述した艶有り絵柄層の場合とは逆に、艶消しの絵柄パターンを表現する為の層である。 [0043] [matte pattern layer] matte pattern layer 4B is a matte is the layer surface, partially formed on recoatability ionizing radiation-curable resin layer 3B of there glossy, glossy picture layer described above the case of the opposite, a layer for expressing a pattern pattern matte. この艶消し絵柄層4Bは、上記艶有り絵柄層に用いるインキ(又は塗液)、すなわち、前述した内部絵柄層2でその形成に用いるインキ(又は)塗料に対して、更に艶消し剤を添加したものを使用して、印刷等の公知の形成方法で形成すれば良い。 The matte pattern layer 4B is an ink (or coating solution) used for the picture layer there above luster, i.e., added to the ink (or) coating used in its formation inside the pattern layer 2 described above, a further matting agent using the ones, it may be formed by a known forming method such as printing. なお、艶消し剤としては公知のもので良く、例えば、艶消し剤としては、シリカ、硫酸バリウム、炭酸カルシウム等の粉末を使用すれば良い。 Incidentally, it may be of known as matting agents, for example, as a matting agent, silica, barium sulfate, may be used a powder such as calcium carbonate. なお、トップコート層は、上記艶有り絵柄層の場合と同様に、艶消し絵柄層と艶有りのリコート性電離放射線硬化性樹脂層とによる艶の高低差(大小)を完全に消失させてしまわない程度の厚さとするのはもちろんである。 Incidentally, the top coat layer, as in the case of the gloss pattern layer, Shimawa by the height difference between the gloss by the recoatability ionizing radiation curable resin layer there matte pattern layer and the luster of (large and small) completely abolished it is, of course, to the thickness of the extent not. またこの様な、艶消し絵柄層4B、 In addition such, matte pattern layer 4B,
艶有りのリコート性電離放射線硬化性樹脂層3B、及び内部絵柄層2等による意匠表現も任意であるが、例えば、内部絵柄層の絵柄は木目柄として、艶消し絵柄層4 Gloss of recoatability ionizing radiation-curable resin layer 3B, and it is also optional that the design represented by the internal pattern layer 2 and the like, for example, the grain pattern design of the internal pattern layer, matte pattern layer 4
Bで木目導管溝柄を表現する等ある。 Some like to express the grain conduit groove pattern in B. もちろん、意匠表現は、この他、石目柄、砂目柄、抽象柄等、用途に応じたもので良い。 Of course, design representation, the other, pebble patterns, grain patterns, abstract patterns, etc., may be one depending on the application.

【0044】〔トップコート層〕トップコート層5は、 [0044] [top coat layer] top coat layer 5,
化粧材の最表面層として位置して、化粧材表面性状を決める層である。 Located as the outermost surface layer of the decorative material is a layer that determines the decorative material surface properties. 最表面層としてのトップコート層の存在によって、リコート性電離放射線硬化性樹脂層が該層中のフィラーの存在によって、たとえその表面が粗面化しても、化粧材表面としては表面ざらつき感を無くす事が可能となる。 The presence of the top coat layer as the outermost layer, by the presence of filler in the layer is recoatability ionizing radiation-curable resin layer, even though its surface is roughened, eliminate graininess surface as a cosmetic material surface thing is possible. また、耐摩耗性向上目的で含有させるフィラーは下層のリコート性電離放射線硬化性樹脂層に含有させ、このトップコート層には含有させる必要が無いので、最表面層にフィラーを含有させた場合に起き得る表面ざらつき感、またそれによって起きる、化粧面が水平面用途で使用したときの接触物の損傷・摩耗、等の問題を防げる。 Further, the filler to be contained in the wear resistance improved object is contained in the lower layer of recoatability ionizing radiation curable resin layer, there is no need to be contained in the top coat layer, when it is contained a filler in the outermost surface layer graininess surface may occur, also thereby happens, the decorative surface damage and wear of the contact product when used in a horizontal plane applications, prevent the problems such. 更に、このトップコート層によって、リコート性電離放射線硬化性樹脂層上に形成する艶消し絵柄層又は艶有り絵柄層が、簡単に損傷、消失したりしない様な耐摩耗性も付与できる。 Moreover, this top coat layer, matte picture layer or glossy pattern layer formed on recoatability ionizing radiation-curable resin layer is easily damaged, lost or not such abrasion resistance can be imparted.

【0045】なお、本発明ではこのトップコート層の下に、艶消しのリコート性電離放射線硬化性樹脂層や艶消し絵柄層等を有するので、艶消しのリコート性電離放射線硬化性樹脂層と艶有り絵柄層、或いは艶有りのリコート性電離放射線硬化性樹脂層と艶消し絵柄層とによる艶の高低差(大小)を、完全に消失させてしまわない程度の厚さにトップコート層を形成することは、言うまでもない。 [0045] Incidentally, under this top coat layer in the present invention, because it has a recoatability ionizing radiation-curable resin layer of matte or matte pattern layer or the like, recoatability ionizing radiation-curable resin layer of matte and glossy There pattern layer, or the height difference between the gloss by the recoatability ionizing radiation curable resin layer and the matte pattern layer of gloss (the magnitude) to form a top coat layer to a thickness as not Shimawa completely abolished it is, needless to say. そこで、トップコート層の厚さは、艶消し面の表面凹凸度合いにもよるが、例えば1〜5μm程度の厚さとする。 Therefore, the thickness of the top coat layer, although it depends on the surface roughness degree of matte surface, for example, of about 1~5μm thickness. なお、薄すぎても、トップコート層としての表面保護(例えば耐擦傷性)効果が薄れる。 Even if too thin, the surface protection as a top coat layer (e.g., scratch resistance) effect fades.

【0046】この様なトップコート層5としては、汎用のオーバーコート剤が使用可能である。 [0046] As the top coat layer 5 such this way, the general purpose of the overcoat agent is available. 特に耐摩耗性の点で表面性能を向上する為には、オーバーコート剤は硬化性樹脂を用いたものが好ましい。 Especially in order to improve the surface properties in terms of wear resistance, overcoating agent is preferably one using a curable resin. 該硬化性樹脂としては、熱硬化性樹脂、電離放射線硬化性樹脂等で良い。 The curable resin, thermosetting resin, or ionizing radiation-curable resin or the like. トップコート層の形成は、ロールコート等の公知の塗工法、或いはグラビア印刷等の公知の印刷法で形成すれば良い。 Formation of the top coat layer may be formed known coating method such as roll coating, or by a known printing method gravure printing.

【0047】上記熱硬化性樹脂としては、2液硬化型樹脂が使用できる。 [0047] Examples of the thermosetting resin, two-part curable resins. 例えば、2液硬化型ウレタン樹脂等である。 For example, a two component curing type urethane resin. 2液硬化型ウレタン樹脂としては、主剤にアクリルポリオール、ポリエステルポリオール、ポリエーテルポリオール等のポリオールを用い、架橋剤(硬化剤)に2,4−トリレンジイソシアネート、1,6−ヘキサメチレンジイソシアネート、イソホロンジイソシアネート等のポリイソシアネートを用いた公知のウレタン樹脂から適宜選択すれば良い。 The two-component curable urethane resin, acrylic polyol base resin, a polyester polyol, with a polyol such as polyether polyol, the crosslinking agent (hardener) 2,4-tolylene diisocyanate, 1,6-hexamethylene diisocyanate, isophorone it may be appropriately selected from known urethane resin using polyisocyanate diisocyanate. また、上記電離放射線硬化性樹脂としては、前述したリコート性電離放射線硬化性樹脂層で述べた如き電離放射線硬化性樹脂を使用できる。 Moreover, as the ionizing radiation-curable resin, it can be used with such ionizing radiation curable resin mentioned recoatability ionizing radiation-curable resin layer described above. 但し、トップコート層ではリコート性は不要な為、リコート性を配慮したフィラー添加及び樹脂選定は必要無い。 However, since recoatability is not required in the top coat layer, filler loading and resin selected with consideration of the recoatability is not necessary.

【0048】なお、トップコート層中には、耐摩耗性向上目的のフィラーは必須では無いが、表面ざらつき感が出ない程度であれば、フィラーを含有させても良い。 [0048] Note that in the topcoat layer, but there is no filler improve wear resistance purposes essential, as long as not out graininess surface may contain a filler. 含有させるフィラーは前述リコート性電離放射線硬化性樹脂層で述べた如きフィラーである。 Filler to be contained is such fillers mentioned above recoatability ionizing radiation-curable resin layer.

【0049】また、トップコート層中には、その表面性状を所望のものとする為に、例えば表面全体の艶調整の為に、フィラーを含有させても良い。 [0049] Also, the topcoat layer, to the surface properties and the desired ones, for example, for the luster control of the entire surface may contain a filler. 例えば、シリカ、 For example, silica,
炭酸カルシウム、硫酸バリウム等の公知の艶消し剤を使用すれば良い。 Calcium carbonate, may be used a known matting agents such as barium sulfate. 表面全体の艶調整によって、艶消し(又は艶有り)のリコート性電離放射線硬化性樹脂層と艶有り絵柄層(又は艶消し絵柄層)との組み合わせによる艶の高低模様のその艶を全体として調整する事もできる。 By the overall luster control surface, it adjusts the overall the gloss of glossy high and low pattern in combination with recoatability ionizing radiation-curable resin layer and the glossy picture layer (or matte pattern layer) of matt (or gloss) It can also be.

【0050】 [0050]

【実施例】以下、本発明の耐摩耗性を有する化粧材を実施例により更に説明する。 EXAMPLES The following further illustrate the decorative material having a wear resistance of the present invention through examples. なお、以下において、「部」 In the following, "parts"
とあるのは全て質量基準である。 All phrase are by weight.

【0051】〔実施例1〕図1(A)の如き層構成の化粧材Dを次の様にして作製した。 [0051] The decorative material D-described layer structure of Example 1 FIG. 1 (A) was prepared in the following manner. シート状の基体1とする化粧原紙として、アクリル樹脂ラテックスを含浸した樹脂含浸紙の片面に、内部絵柄層2として、グラビア印刷法で厚み2μmの全ベタ層(着色ベタ層)2Aと、木目柄の柄パターン層2Bとをこの順に形成した。 As a cosmetic base paper a sheet-like substrate 1, on one surface of the resin-impregnated paper impregnated with an acrylic resin latex, as the internal pattern layer 2, the total solid layer having a thickness of 2μm by a gravure printing method (colored solid layer) 2A and, grain pattern a pattern pattern layer 2B of formed in this order. なお、 It should be noted that,
全ベタ層には、バインダーの樹脂がアクリル樹脂とニトロセルロース系樹脂との混合物で着色剤が添加されたインキを使用した。 All of the solid layer, the resin binder is used an ink in which the colorant is added with a mixture of acrylic resin and nitrocellulose resin. また、柄パターン層には、バインダーの樹脂がニトロセルロース系樹脂とアルキド樹脂との混合物で着色剤が添加されたインキを使用した。 In addition, the handle pattern layer, the resin binder is used an ink in which the colorant is added with a mixture of nitrocellulose-based resin and an alkyd resin. 次いで、 Then,
下記の(電子線硬化型の)艶消しリコート性電離放射線硬化性樹脂塗料を用いて厚み25μmの塗膜を塗工形成した後、電子線照射装置を用いて電子線照射を行い塗膜を架橋硬化させて、アルミナをフィラーFとして含有しシリカを艶消し剤として含有する、艶消しのリコート性電離放射線硬化性樹脂層3Aを形成した。 After using (electron beam curing) matte recoatability ionizing radiation curing resin coating following the coating film thickness 25μm was coated form, crosslinking the coating film subjected to electron beam irradiation using an electron beam irradiation device is cured, the alumina containing silica containing as a filler F as matting agent, to form a recoatability ionizing radiation curable resin layer 3A matte.

【0052】 艶消しリコート性電離放射線硬化性樹脂塗 [0052] matte recoatability ionizing radiation curing resin coating
ウレタンアクリレート 30部 2官能アクリレート系オリゴマー 20部 3官能アクリレート系オリゴマー 10部 シリコーンアクリレート 3部 不定形シリカ(平均粒径1.8μm) 15部 微粉末シリカ(平均粒径0.1μm) 2部 球状α−アルミナ(平均粒径25μm) 20部 Fee urethane acrylate 30 parts 2-functional acrylate oligomer 20 parts trifunctional acrylate oligomer 10 parts silicone acrylate 3 parts amorphous silica (average particle size 1.8 .mu.m) 15 parts of finely divided silica (average particle size 0.1 [mu] m) 2 parts Spherical α- alumina (average particle size 25 [mu] m) 20 parts

【0053】次いで、上記艶消しのリコート性電離放射線硬化性樹脂層3A上に、艶有り絵柄層4Aとして、ポリオールとイソシアネートとかなる2液硬化型アクリルウレタン樹脂系インキをグラビア印刷して、前記内部絵柄層2に同調させた木目導管柄を形成した。 [0053] Then, on recoatability ionizing radiation-curable resin layer 3A of the matte, as a glossy pattern layer 4A, a two-component curable acrylic urethane resin ink comprising Toka polyol and isocyanate with gravure printing, the internal to form a wood grain conduit pattern tuned to the pattern layer 2.

【0054】次いで、下記の電離放射線型のトップコート剤をグラビア塗工法により全面に塗工して厚み3μm [0054] Then, the thickness 3μm by coating the top coating agent of ionizing radiation type below the whole surface by a gravure coating method
の透明樹脂層5を形成して、化粧シートとなる図1 To form a transparent resin layer 5, the decorative sheet 1
(A)の如き化粧材Dを得た。 It was obtained, such as decorative material D of (A).

【0055】 電離放射線硬化型トップコート剤アクリレートオリゴマー 50部 1,6−ヘキサンジオールアクリレート 40部 不定形シリカ(平均粒径1.8μm) 8部 微粉末シリカ(平均粒径0.1μm) 1部 両末端メタクリレート変成シリコーン 1部 [0055] Ionizing radiation curable top coating agents acrylate oligomer 50 parts of 1,6-hexanediol acrylate 40 parts amorphous silica (average particle size 1.8 .mu.m) 8 parts finely divided silica (average particle size 0.1 [mu] m) 1 part both terminal methacrylate modified silicone 1 part

【0056】〔実施例2〕実施例1に於いて、艶消しのリコート性電離放射線硬化性樹脂層3Aに代えて、下記組成の艶有りリコート性電離放射線硬化性樹脂塗料を用いて、艶有りリコート性電離放射線硬化性樹脂層3Bを形成し、且つ、艶有り絵柄層4Aに代えて、艶消し剤としてシリカを添加したインキを用いて、木目導管柄の艶消し絵柄層4Bを形成した他は、実施例1と同様にして、化粧シートとなる図1(B)の如き化粧材Dを得た。 [0056] In Example 2 Example 1, in place of the recoatability ionizing radiation-curable resin layer 3A of the matte, with recoatability ionizing radiation curing resin coating there gloss having the following composition, glossy forming a recoatability ionizing radiation curable resin layer 3B, and, instead of the glossy picture layer 4A, by using an ink prepared by adding silica as matting agent, to form a matte pattern layer 4B wood grain conduit pattern other , the same procedure as in example 1 to obtain such decorative material D of Figure 1 as a decorative sheet (B).

【0057】 艶有りリコート性電離放射線硬化性樹脂塗 [0057] glossy recoating of ionizing radiation-curable resin coating
ウレタンアクリレート 30部 2官能アクリレート系オリゴマー 20部 3官能アクリレート系オリゴマー 10部 シリコーンアクリレート 3部 球状α−アルミナ(平均粒径25μm) 20部 Fee urethane acrylate 30 parts 2-functional acrylate oligomer 20 parts trifunctional acrylate oligomer 10 parts silicone acrylate 3 parts spherical α- alumina (average particle size 25 [mu] m) 20 parts

【0058】〔実施例3〕実施例2に於いて、トップコート層の形成に用いたトップコート剤を下記組成のトップコート剤に変更し、該トップコート剤を塗布後、60 [0058] Example 3 In Example 2, by changing the top coating agent used for forming the top coat layer to the top coat agent having the following composition, after applying the top coating agents, 60
℃で3日間加熱乾燥してトップコート層を完全硬化させた他は、実施例2と同様にして、図1(B)の如き化粧材Dを得た。 Other drying by heating for 3 days to completely cure the topcoat layer at ℃, the procedure of Example 2, was obtained such decorative material D of FIG. 1 (B).

【0059】 2液硬化型ウレタン系トップコート剤アルキド変性アクリルポリオール 100部 変性ポリイソシアネート 15部 スリップ剤(シリコーンオイル) 5部 希釈溶剤(酢酸エチル+トルエン) 適当量 [0059] 2-part curing type urethane-based top coating agents alkyd modified acrylic polyol 100 parts modified polyisocyanate and 15 parts slip agent (silicone oil) 5 parts diluent (ethyl acetate and toluene) appropriate amount

【0060】〔比較例1〕実施例1に於いて、艶消しのリコート性電離放射線硬化性樹脂層3Aと艶有り絵柄層4Aの形成を省略した他は、実施例1と同様にして化粧材を作製した。 [0060] Comparative Example 1 In Example 1, except that was omitted form the pattern layer 4A there recoatability ionizing radiation-curable resin layer 3A and the gloss matt, decorative material in the same manner as in Example 1 It was produced.

【0061】〔比較例2〕実施例1に於いて、基体1に内部絵柄層2を形成した後、艶消しのリコート性電離放射線硬化性樹脂層3Aとトップコート層5を形成する代わりに、内部絵柄層2の上に直接、艶有り絵柄層4Aを形成した後、フィラー含有の下記の如き電離放射線硬化性樹脂塗料を用いて、最外層として厚み25μmの電離放射線硬化性樹脂層を形成した構成の化粧材を作製した。 [0061] In Comparative Example 2 Example 1, after forming the inner pattern layer 2 on the substrate 1, instead of forming the recoatability ionizing radiation curable resin layer 3A and the top coat layer 5 of the matte, directly on the inner pattern layer 2, after forming a glossy picture layer 4A, using such ionizing radiation curing resin coating of the following filler content, to form an ionizing radiation-curable resin layer having a thickness of 25μm as an outermost layer the decorative material of the structure was fabricated.

【0062】 電離放射線硬化性樹脂塗料ビスフェノールAエチレンオキサイド変性ジアクリレート 50部 トリメチロールプロパンエチレンオキサイド変性トリアクリレート 20部 球状α−アルミナ(平均粒径25μm) 20部 不定形シリカ(平均粒径1.8μm) 8部 微粉末シリカ(平均粒径0.1μm) 1部 両末端メタクリレート変性シリコーン 1部 [0062] Ionizing radiation curable resin paint of bisphenol A ethylene oxide modified diacrylate 50 parts of trimethylolpropane ethylene oxide-modified triacrylate 20 parts spherical α- alumina (average particle size 25 [mu] m) 20 parts amorphous silica (average particle size 1.8μm ) 8 parts finely divided silica (average particle size 0.1 [mu] m) 1 part both ends methacrylate-modified silicone 1 part

【0063】〔比較例3〕実施例1に於いて、トップコート層5の形成を省略した他は、実施例1と同様にして化粧材を作製した。 [0063] In Comparative Example 3 Example 1, except that was omitted form the top coat layer 5, to prepare a decorative material in the same manner as in Example 1.

【0064】〔性能評価〕耐摩耗性と、表面ザラツキ感として表面滑り性を、下記の様にして評価して、表1及び表2の如き結果を得た。 [0064] and (Performance Evaluation) abrasion resistance, the surface slip characteristics as the surface roughness, and evaluated in the manner described below, to obtain a such results in Table 1 and Table 2.

【0065】耐摩耗性:JIS K6902(熱硬化性樹脂化粧板試験方法)に準じた方法で試験評価した。 [0065] Abrasion resistance: tested evaluated by JIS K6902 method according to (thermosetting resin decorative plate test method). 表面滑り性:30kPaの荷重で綿布を押し当てた状態で、10cmの距離を10往復擦り付け、綿布の傷み具合を目視評価した。 Surface smoothness: in a state of pressing a cotton cloth under a load of 30kPa, a distance of 10cm rubbed back and forth 10 times, was visually evaluated the damage condition of cotton cloth.

【0066】 [0066]

【表1】 [Table 1]

【0067】 [0067]

【表2】 [Table 2]

【0068】表1の如く、各実施例(実施例1、2及び3)は、比較例(比較例2及び比較例3)に比べて、耐摩耗性が向上し、しかも、表面が削られた際にも、導管(艶有り絵柄層4A又は艶消し絵柄層4B)が簡単に消失せず意匠感が保持される事が確認された。 [0068] As Table 1, each example (Examples 1, 2 and 3) are compared with the comparative example (Comparative Example 2 and Comparative Example 3), improved abrasion resistance, moreover, the surface is shaved It was time to be a conduit that (glossy picture layer 4A or matte pattern layer 4B) is a design feeling not easily disappear is held has been confirmed. しかも、各実施例は実用上問題の無い耐摩耗性を有しながら、表2 Moreover, each embodiment while having no wear resistant practical problem, Table 2
の如く、表面滑り性も良好で、滑らかな表面を持つ事が確認された。 As of, the surface sliding property is good, and it was confirmed to have a smooth surface. なお、比較例2は実施例同様に耐摩耗性は良好だが、表面滑り性が不良である。 In Comparative Example 2, the wear resistance in the same manner as in Examples but excellent surface slipperiness is poor. 更に、各実施例は、木目導管柄部分とその他の部分とで表面艶状態が異なり意匠感に優れていた。 Further, each example had excellent design sense different surface luster state with grain conduit handle portion and other portions. しかし、比較例1では木目導管柄が無い上、艶模様も無く、表面質感及び意匠感に乏しかった。 However, on the absence of the grain conduit pattern Comparative Example 1, gloss pattern without any, it was poor in surface texture and design sense.

【0069】 [0069]

【発明の効果】本発明の耐摩耗性を有する化粧材によれば、耐摩耗性を向上させる為のフィラーは内部の層の電離放射線硬化性樹脂層に含有させ、且つ該樹脂層はリコート性であるので、該樹脂層を未硬化状態のままで該樹脂層上にトップコート層等を形成した後に該樹脂層を硬化させる様な面倒な事をせずに、該樹脂層を硬化させて完成させた後に、該樹脂層上にトップコート層等を密着の問題なく容易に形成でき、自由度の高い構成が可能となり、優れた耐摩耗性が得られることになる。 According to the decorative material having a wear resistance of the present invention, a filler for improving the wear resistance is contained in ionizing radiation-curable resin layer of the inner layer, and the resin layer is recoatability since it is, without such troublesome thing to cure the resin layer after the formation of the top coat layer and the like remain in the resin layer on the unhardened the resin layer, curing the resin layer after completing, the resin layer on the top coat layer or the like adhesion without problems can be easily formed, it is possible to highly flexible structure, so that excellent wear resistance can be obtained. しかも、フィラーは最表面のトップコート層にでは無く、内部の層である電離放射線硬化性樹脂層に含有させてあるので、フィラーによって表面の艶が低下したり、表面にフィラーが頭出しして表面ざらつき感が生じたり、内装用途(水平面)で表面に接触したものを損傷、摩耗させたりする問題を起こさずに、優れた耐摩耗性が得られる。 Moreover, the filler rather than the top coat layer on the outermost surface, so are not contained in the ionizing radiation-curable resin layer is an internal layer, or reduced gloss of the surface by the filler, the filler on the surface is cued or cause graininess surface damage that contact with the surface in interior applications (horizontal plane), without causing a problem or to wear, resulting excellent wear resistance.

【0070】そして、内部絵柄層と、その上の艶消しとしたリコート性電離放射線硬化性樹脂層と、該リコート性電離放射線硬化性樹脂層の上に部分的に形成された艶有り絵柄層とを組み合わせる第1の形態の化粧材では、艶有り絵柄層の絵柄に同調した艶模様によって優れた表面質感及び意匠感も得られる。 [0070] Then, an internal pattern layer, and recoatability ionizing radiation-curable resin layer was matte thereon, and the picture layer there partially formed gloss over the recoatability ionizing radiation curable resin layer the decorative material of the first embodiment combining excellent surface texture and decorative feeling by gloss pattern tuned to the pattern of the glossy picture layer is also obtained. しかも、内部絵柄層はリコート性電離放射線硬化性樹脂層の下に設けてあるのでリコート性電離放射線硬化性樹脂で保護され、また、艶有り絵柄層でもトップコート層の下に設けてあるのでトップコート層によって保護される結果、これら内部絵柄層、艶有り絵柄層の耐摩耗性は良好なものとなる。 Moreover, the internal pattern layer is protected by the recoatability ionizing radiation-curable resin so is provided below the recoatability ionizing radiation curable resin layer, and since even glossy pattern layer is provided under a top coat layer Top results that are protected by the coating layer, these internal pattern layer, the wear resistance of the glossy picture layer becomes good.

【0071】一方、内部絵柄層と、その上の艶有りとしたリコート性電離放射線硬化性樹脂層と、該リコート性電離放射線硬化性樹脂層の上に部分的に形成された艶消し絵柄層とを組み合わる第2の形態の化粧材では、艶消し絵柄層の絵柄に同調した艶模様によって優れた表面質感及び意匠感も得られる。 [0071] On the other hand, an internal pattern layer, and recoatability ionizing radiation curable resin layer that there gloss thereon, a partially formed matt pattern layer on top of the recoatability ionizing radiation curable resin layer that combine the decorative material of the second embodiment, the surface texture and decorative feeling excellent by gloss pattern tuned to the pattern of matte pattern layer can be obtained. しかも、内部絵柄層はリコート性電離放射線硬化性樹脂層の下に設けてあるのでリコート性電離放射線硬化性樹脂で保護され、また、艶消し絵柄層でもトップコート層の下に設けてあるのでトップコート層によって保護される結果、これら内部絵柄層、艶消し絵柄層の耐摩耗性は良好なものとなる。 Moreover, the internal pattern layer is protected by the recoatability ionizing radiation-curable resin so is provided below the recoatability ionizing radiation curable resin layer, and since even matte pattern layer is provided under a top coat layer Top results that are protected by the coating layer, these internal pattern layer, the wear resistance of the matte pattern layer becomes excellent.

【0072】更に、トップコート層の硬化性樹脂が、 [0072] In addition, the curable resin of the top coat layer,
電離放射線硬化性樹脂又は熱硬化性樹脂である構成とすれば、熱硬化性樹脂の場合では安価且つ平易に優れた耐摩耗性が得られ、電離放射線硬化性樹脂の場合では極めて優れた耐摩耗性が得られる。 By configuring as the ionizing radiation-curable resin or thermosetting resin, low cost and easy to excellent wear resistance can not be obtained in the case of a thermosetting resin, excellent abrasion in the case of the ionizing radiation curing resin gender can be obtained.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】本発明の耐摩耗性を有する化粧材の2形態を例示する断面図。 Cross-sectional view illustrating the two forms of decorative material having a wear resistance of the present invention; FIG.

【符号の説明】 DESCRIPTION OF SYMBOLS

1 基体 2 内部絵柄層 2A 全ベタ層 2B 柄パターン層 3A 艶消しのリコート性電離放射線硬化性樹脂層 3B 艶有りのリコート性電離放射線硬化性樹脂層 4A 艶有り絵柄層 4B 艶消し絵柄層 5 トップコート層 D 化粧材 F フィラー 1 base 2 internal pattern layer 2A whole solid layer 2B design pattern layer 3A gloss recoatability ionizing radiation-curable resin layer 4A glossy picture layer 4B matte pattern layer 5 top recoatability ionizing radiation-curable resin layer 3B gloss of erasure coat layer D decorative material F filler

フロントページの続き Fターム(参考) 4F100 AA19H AA20H AJ06H AK01C AK01E AK25 AK25H AK41H AL09 AS00E AT00A BA05 BA10A BA10E CA13 CA23C CC00 DG10 EJ821 GB08 GB81 HB00B HB00D HB01 HB31 JB12E JB13E JB14C JB14E JK09 JL06 JN21C JN26C JN26D Front page of the continued F-term (reference) 4F100 AA19H AA20H AJ06H AK01C AK01E AK25 AK25H AK41H AL09 AS00E AT00A BA05 BA10A BA10E CA13 CA23C CC00 DG10 EJ821 GB08 GB81 HB00B HB00D HB01 HB31 JB12E JB13E JB14C JB14E JK09 JL06 JN21C JN26C JN26D

Claims (3)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 基体上に内部絵柄層を有し、該内部絵柄層上にフィラーを含有し艶消しのリコート性電離放射線硬化性樹脂層を有し、該リコート性電離放射線硬化性樹脂層上に部分的に形成された艶有り絵柄層を有し、該艶有り絵柄層上に硬化性樹脂からなるトップコート層を有する、耐摩耗性を有する化粧材。 1. A has internal pattern layer on a substrate, a filler on to the internal pattern layer has recoatability ionizing radiation-curable resin layer of matte, the recoatability ionizing radiation curable resin layer It has a partially formed glossy picture layer, having a top coat layer comprising a cured resin in 該艶 there picture layer, the decorative material having wear resistance.
  2. 【請求項2】 基体上に内部絵柄層を有し、該内部絵柄層上にフィラーを含有し艶有りのリコート性電離放射線硬化性樹脂層を有し、該リコート性電離放射線硬化性樹脂層上に部分的に形成された艶消し絵柄層を有し、該艶消し絵柄層上に硬化性樹脂からなるトップコート層を有する、耐摩耗性を有する化粧材。 2. A has internal pattern layer on a substrate, a filler on to the internal pattern layer has recoatability ionizing radiation curable resin layer there luster, the recoatability ionizing radiation curable resin layer partially formed has a matte pattern layer, having a top coat layer comprising a cured resin in matte pattern layer, the decorative material having wear resistance.
  3. 【請求項3】 トップコート層の硬化性樹脂が、電離放射線硬化性樹脂又は熱硬化性樹脂である、請求項1又は2記載の耐摩耗性を有する化粧材。 Curable resin wherein the top coat layer is a ionizing radiation-curable resin or thermosetting resin, decorative material having wear resistance according to claim 1 or 2, wherein.
JP32659499A 1999-11-17 1999-11-17 Decorative material with hardwearing properties Pending JP2001138470A (en)