JP2001080299A - Container for coating forming composition - Google Patents

Container for coating forming composition

Info

Publication number
JP2001080299A
JP2001080299A JP25954899A JP25954899A JP2001080299A JP 2001080299 A JP2001080299 A JP 2001080299A JP 25954899 A JP25954899 A JP 25954899A JP 25954899 A JP25954899 A JP 25954899A JP 2001080299 A JP2001080299 A JP 2001080299A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
cap
container
forming composition
film
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP25954899A
Other languages
Japanese (ja)
Inventor
Sadahiro Okai
Kenji Yoshii
賢二 吉井
禎浩 岡井
Original Assignee
Pentel Corp
ぺんてる株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To provide a painting material container in which the adhesion between a cap and a container main body is not generated even after the container is used for a long period. SOLUTION: A container for a coating forming composition is composed of a container main body 2 and a cap which is spirally engaged freely attachably/detachably with the main body 2. The cap is formed from a mixture of a polyolefin resin and a graft copolymer in which polydimethylsiloxane is grafted on polyethylene.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、水彩絵の具、ポスターカラー、糊など、乾燥時に皮膜を形成する性質を有する組成物を保管する容器に関する。 The present invention relates to the paint watercolor, Posters Color, etc. glue, a container storing a composition having the property of forming a film when dry.

【0002】 [0002]

【従来の技術】従来、絵の具、ポスターカラー、糊などの皮膜形成性組成物は、乾燥防止を目的としてネジ式キャップを有する容器に保管されることが多い。 Conventionally, paint, poster color, film-forming composition, such as glue, is often stored in a container having a screw cap for the purpose of preventing drying. このような容器にあっては、皮膜形成性組成物をネジ部に付着したままキャップを閉めた場合、乾燥して形成した皮膜が接着剤となりキャップと容器が固着し、キャップを開けるのが大変困難となる問題が発生する。 In such a container, when capped remain attached to the film-forming composition to the threaded portion, dried formed was coating fixed cap and the container becomes adhesive, hard to open the cap difficult to become a problem occurs. 特に、皮膜形成性組成物の収容部を有する容器本体が、ガラスや金属など堅く変形しない材質のものほど開けるのが困難となる。 In particular, the container body having an accommodating portion of the film-forming composition becomes difficult to open as those made of a material not rigid deformation such as glass and metal. このような問題の発生を防止するため、容器本体やキャップのネジ部にシリコーンオイル、シリコーングリース、流動パラフィン等を塗布し固着を防止する方法が採用されていた。 To prevent such a problem, the silicone oil to the threads of the container body and the cap, silicone grease, a method for preventing the applied anchoring the liquid paraffin or the like has been adopted.

【0003】 [0003]

【発明が解決しようとする課題】しかしながら、上記シリコーンオイル、シリコーングリース、流動パラフィン等をネジ部に塗布する方法は、シリコーンオイル、シリコーングリース、流動パラフィン等が容器本体内に収容した皮膜形成性組成物と混ざり、皮膜形成性組成物を変質させたり、繰り返し使用しているうちに皮膜形成性組成物と共に脱落したりして長期的に効果が得られないという問題が発生した。 [SUMMARY OF THE INVENTION However, the silicone oil, silicone grease, a method of applying the liquid paraffin to a screw portion, silicone oil, silicone grease, film-forming composition liquid paraffin or the like is accommodated in the container body mixed with objects, or to alter the film-forming composition, a problem that long-term effects can not be obtained by or falling off with film-forming composition during repeated use has occurred. 本発明は、長期間使用しても、キャップと容器本体との固着が発生しない皮膜形成性組成物用容器を提供することを課題とする。 The present invention may be used for a long period, and to provide a film-forming composition for containers sticking does not occur between the cap and the container body.

【0004】 [0004]

【課題を解決するための手段】本発明は、容器本体と、 Means for Solving the Problems The present invention comprises a container body,
この容器本体に螺合により着脱自在に取り付けられるキャップとよりなる皮膜形成性組成物用容器において、前記キャップはオレフィン系樹脂と、ポリエチレンにポリジメチルシロキサンをグラフト重合したグラフト共重合体との混合物により形成されたものであることを特徴とする皮膜形成性組成物用容器を要旨とするものである。 In a more becomes a film-forming composition container and a cap removably attached by threaded engagement to the container body, said cap and an olefin-based resin, a mixture of a graft copolymer obtained by graft polymerization of polydimethylsiloxane polyethylene it is an gist film-forming composition container which characterized in that formed.

【0005】図1は、本発明の一実施例である。 [0005] Figure 1 is an embodiment of the present invention. 1はキャップである。 1 is a cap. 2は容器本体であり、内部は皮膜形成性組成物の収容部となっている。 2 is a vessel body, the interior has a housing portion of the film-forming composition.

【0006】キャップ1は、内側の側壁に雌ねじ部1a [0006] The cap 1, the internal thread portion 1a on the inner side of the side wall
が形成されており、この雌ねじ部1aは、容器本体2開口部側外壁に形成された雄ねじ部2aと螺合可能となっている。 There is formed, the female screw portion 1a has become a male screw portion 2a formed in the container body 2 opening side wall and can be screwed. 本発明において、キャップ1は、オレフィン系樹脂と、ポリエチレンにポリジメチルシロキサンをグラフト重合したグラフト共重合体との混合物により形成されたものであることが必要である。 In the present invention, the cap 1, an olefin resin, it is necessary that one formed by a mixture of the graft copolymer obtained by graft polymerization of polydimethylsiloxane polyethylene.

【0007】オレフィン系樹脂としては、ポリエチレン、ポリプロピレンといったものを用いることができる。 [0007] As the olefin resin, there can be used polyethylene, such as polypropylene ones. ポリエチレンにポリジメチルシロキサンをグラフト重合したグラフト共重合体は、ポリジメチルシロキサンを40から60重量%含有し、グラフト率は60から9 Graft copolymers of polyethylene polydimethylsiloxane graft-polymerized is a polydimethylsiloxane containing 60% by weight 40, the graft rate is from 60 9
0%のものであって、市販品としては、グリーンベルS It is of 0%, as commercially available products, green bell S
P−300(ポリジメチルシロキサン40重量%含有、 P-300 (polydimethylsiloxane 40 weight% content,
グラフト率60から80%)、同SP−310(ポリメチルシロキサン60重量%含有、グラフト率80から9 80% graft of 60), the SP-310 (polymethyl siloxane 60 wt% containing, graft ratio of 80 9
0%)、同SP−350(ポリメチルシロキサン50重量%含有、グラフト率85から90%)(以上、カネボウ化成(株)製)といったものが例示できる。 0%), the SP-350 (polymethyl siloxane 50 wt% containing, graft rate of 85 to 90%) (or, Kanebo Kasei Co., Ltd.) such materials can be exemplified. キャップを形成するにあたって、オレフィン系樹脂に対するグラフト共重合体の割合は、1.0から10.0重量が%好ましい。 In the formation of the cap, the proportion of the graft copolymer to olefin-based resin is% preferably 10.0 weight from 1.0.

【0008】キャップを形成するには、オレフィン樹脂とポリエチレンにポリジメチルシロキサンをグラフト重合したグラフト共重合体をドライブレンドし、射出成形機にて成形しネジ部を有するキャップを得る。 [0008] To form the cap, a graft copolymer obtained by graft polymerization of polydimethylsiloxane olefin resin and a polyethylene were dry-blended to obtain a cap having a shaped screw portion with an injection molding machine.

【0009】容器本体2は、皮膜形成性組成物を収容するもので、ガラス、セラミック、金属やポリスチレン、 [0009] the container body 2 is intended to accommodate the film-forming composition, glass, ceramics, metals, polystyrene,
AS樹脂、PET、PBT等の樹脂製のものを用いることができる。 AS resin, PET, can be used as the resin such as PBT. その形状は開口部にネジ部があれば、他には特に限定されことはない。 Its shape if any threaded portion in the opening, is not particularly limited to the other. 尚、容器は、透明なものを用いると内容物が見えるので、残量確認や入っているものの色の確認が容易なので好ましい。 Incidentally, the container, the contents thereof are visible when used as a transparent, since it is easy confirmation of the color of those remaining check entered preferable.

【0010】容器本体2に収容される皮膜形成性組成物は、水彩絵の具、ポスターカラーといった水性絵の具類、印刷・塗装などに用いられる水性塗料などの液状描画材や、糊が挙げられる。 [0010] film-forming composition contained in the container body 2, paints watercolor, aqueous paints such like Posters Color, and liquid drawing material, such as an aqueous paint used such as printing, painting, and glue. 上記液状描画材は、顔料、樹脂、水、その他添加剤よりなる。 The liquid drawing material, pigment, resin, water, consisting of other additives. また、糊は、ポリビニルアルコール、水、その他添加剤よりなる。 Also, glue, polyvinyl alcohol, water, consisting of other additives.

【0011】顔料は、着色剤として使用するものであって従来公知の酸化チタン、酸化亜鉛、カーボンブラック、鉄黒、ハンザイエロー、ベンジジンイエロー、ベンジジンオレンジ、ワッチャンレッド、弁柄、フタロシアニンブルー、フタロシアニングリーン、群青、アルミニウム粉、ブロンズ粉、蛍光顔料など、無機顔料、有機顔料を問わず使用可能であって、単独または2種以上混合しても良い。 [0011] pigments, conventionally known titanium oxide was intended to be used as a coloring agent, zinc oxide, carbon black, iron black, Hansa yellow, benzidine yellow, benzidine orange, Watcha down red, red iron oxide, phthalocyanine blue, phthalocyanine Green, ultramarine, aluminum powder, bronze powder, fluorescent pigments, inorganic pigments, there can be used regardless of organic pigments, may be alone or in combination. その使用量は顔料の種類によっても大きく異なるが、発色並びに印刷・塗装を考慮すると液状描画材全量に対して3から50重量%が好ましい。 The amount used varies greatly depending on the kind of pigment, 3 is preferably 50% by weight with respect to the consideration of the liquid drawing material total amount of color development and printing and painting.

【0012】樹脂は、定着剤、展色剤及び被膜剤として使用し固着の原因となるものであって、膠、アラビアゴム、デキストリン、カゼイン、カルボキシメチルセルロース、ヒドロキシエチルセルロース等の天然樹脂、ポリビニルアルコール、ポリ酢酸ビニル、アクリルエマルジョン、ポリビニルピロリドン等の合成樹脂を単独または2種以上混合して使用でき、その使用量は全量に対して2から30重量%が好ましい。 [0012] resins, there is cause sticking was used as a fixing agent, coatability agents and coatings, glues, gum arabic, dextrin, casein, carboxymethyl cellulose, natural resins such as hydroxyethyl cellulose, polyvinyl alcohol, polyvinyl acetate, acrylic emulsion, synthetic resin such as polyvinyl pyrrolidone alone or in combination may be using, the amount used 2 from preferably 30% by weight based on the total amount.

【0013】その他添加剤は、アルコール類、グリセリン、エチレングリコール、プロピレングリコール、ジプロピレングリコール、ソルビトール等、必要に応じて炭酸カルシウム、シリカ等の体質顔料、界面活性剤、防腐剤、防黴剤、防錆剤、脱泡剤などを適宜用いることができる。 [0013] Other additives, alcohols, glycerin, ethylene glycol, propylene glycol, dipropylene glycol, sorbitol, calcium carbonate optionally an extender pigment such as silica, surfactants, preservatives, fungicide, rust inhibitors, can be used as appropriate, such as defoamers.

【0014】 [0014]

【作用】本発明の描画材容器のキャップは、オレフィン樹脂とポリエチレンにポリジメチルシロキサンをグラフト重合したグラフト共重合体との混合物により形成されている。 Cap drawing material container of the effects of the present invention is formed by a mixture of the graft copolymer obtained by graft polymerization of polydimethylsiloxane olefin resin and polyethylene. グラフト共重合体において、グラフト重合は、 In the graft copolymer, the graft polymerization,
反応性のポリジメチルシロキサンによって進みシロキサンの部分がポリエチレンと反応し、メチル基の部分がポリエチレン表面に露出する。 Parts of the siloxane proceeds by reaction of the polydimethylsiloxane is reacted with polyethylene, part of the methyl group is exposed to the polyethylene surface. この為、表面がより一層疎水になり撥水性が向上する。 For this reason, the surface is improved water repellency becomes more and more hydrophobic. このようなグラフト共重合体をオレフィン樹脂に添加し射出成形すると、ポリエチレンの部分がオレフィン樹脂と相溶性が良好な為、メチル基の部分を樹脂表面に向ける様に成型物を形成する。 When such a graft copolymer is added to an olefin resin injection molding, parts of polyethylene olefin resin compatible for a good, to form a molded product as direct part of the methyl groups on the resin surface.
従って、液状描画材がキャップのネジ部に付着しても、 Therefore, even the liquid drawing member is attached to the threaded portion of the cap,
キャップ自身の有する強い撥水性により皮膜形成性組成物の乾燥時の固着力を低下することができる。 It is possible to decrease the fixing strength of the dry film-forming composition by the strong water repellency possessed by the cap itself.

【0015】 [0015]

【実施例】 実施例1 ポリプロピレン(PM900M、日本ポリオレフィン(株)) 99重量部 グリーンベルSP300 1重量部 上記成分を、ミキサーでドライブレンドし射出成型機で射出成形し、図1に示すキャップを得た。 EXAMPLE 1 Polypropylene (PM900M, Nippon Polyolefin Co.) 99 parts by weight of green bell SP300 1 part by weight The above components were injection molded at a dry blend to an injection molding machine with a mixer, to obtain a cap shown in FIG. 1 It was.

【0016】 実施例2 ポリプロピレン(PM900M、日本ポリオレフィン(株)) 97重量部 グリーンベルSP300 3重量部 上記成分を、実施例1と同様になし図1に示すキャップを得た。 [0016] Example 2 polypropylene (PM900M, Nippon Polyolefin Co.) 97 parts by weight of green bell SP300 3 parts by weight The above components, to give the cap shown in none Figure 1 in the same manner as in Example 1.

【0017】 実施例3 ポリプロピレン(PM900M、日本ポリオレフィン(株)) 95重量部 グリーンベルSP300 5重量部 上記成分を、実施例1と同様になし図1に示すキャップを得た。 [0017] Example 3 Polypropylene (PM900M, Nippon Polyolefin Co.) 95 parts by weight of green bell SP300 5 parts by weight The above components, to give the cap shown in none Figure 1 in the same manner as in Example 1.

【0018】 実施例4 ポリプロピレン(PM900M、日本ポリオレフィン(株)) 93重量部 グリーンベルSP300 7重量部 上記成分を、実施例1と同様になし図1に示すキャップを得た。 [0018] Example 4 Polypropylene (PM900M, Nippon Polyolefin Co.) 93 parts by weight of green bell SP300 7 parts by weight The above components, to give the cap shown in none Figure 1 in the same manner as in Example 1.

【0019】 実施例5 ポリプロピレン(PM600A、日本ポリオレフィン(株)) 99重量部 グリーンベルSP350 1重量部 上記成分を、実施例1と同様になし図1に示すキャップを得た。 [0019] Example 5 Polypropylene (PM600A, Nippon Polyolefin Co.) 99 parts by weight of green bell SP350 1 part by weight The above components, to give the cap shown in none Figure 1 in the same manner as in Example 1.

【0020】 実施例6 ポリプロピレン(PM600A、日本ポリオレフィン(株)) 95重量部 グリーンベルSP350 5重量部 上記成分を、実施例1と同様になし図1に示すキャップを得た。 [0020] Example 6 Polypropylene (PM600A, Nippon Polyolefin Co.) 95 parts by weight of green bell SP350 5 parts by weight The above components, to give the cap shown in none Figure 1 in the same manner as in Example 1.

【0021】比較例1 ポリプロピレン(PM900M、日本ポリオレフィン(株))のみで、射出成型機で射出成形し、図1に示すキャップを得た。 [0021] Comparative Example 1 Polypropylene (PM900M, Nippon Polyolefin Co.) alone was injection molded at an injection molding machine to obtain a cap shown in FIG.

【0022】比較例2 ポリプロピレン(PM600A、日本ポリオレフィン(株))のみで、射出成型機で射出成形し、図1に示すキャップを得た。 [0022] Comparative Example 2 Polypropylene (PM600A, Nippon Polyolefin Co.) alone was injection molded at an injection molding machine to obtain a cap shown in FIG.

【0023】比較例3 比較例1で得たキャップのネジ部にシリコーンオイル(KF96、信越化学工業(株)製)を塗布しキャップを得た。 [0023] to give a silicone oil to the threads of the cap obtained in Comparative Example 3 Comparative Example 1 was applied to (KF96, manufactured by Shin-Etsu Chemical Co., Ltd.) cap.

【0024】比較例4比較例1で得たキャップのネジ部に流動パラフィン(ダフニーオイルKP−1 5、出光興産(株)製)を塗布しキャップを得た。 The yield of liquid paraffin to a screw portion of the cap obtained in Comparative Example 4 Comparative Example 1 was applied to (Daphne Oil KP-1 5, Idemitsu Kosan Co., Ltd.) cap.

【0025】上記実施例1〜6、比較例1〜4で得たキャップを用いて、キャップの固着試験を行った結果を表1に示す。 The above Examples 1-6, by using the cap obtained in Comparative Example 1-4, Table 1 shows the results of the fixation test of the cap. なお、上記キャップは、ポスターカラー(ぺんてる(株)製)のキャップと同じ寸法のものとなし、 In addition, the cap is, without those of the same dimensions as the cap of the poster color (Pentel Co., Ltd.),
容器本体もポスターカラー(ぺんてる(株)製)の容器本体と同じ寸法のガラス製のものを用いた。 The container body is also used as the glass of the same dimensions as the container body of the poster color (Pentel Co., Ltd.).

【0026】 [0026]

【表1】 [Table 1]

【0027】キャップ固着試験:容器本体にポスターカラー蛍光ピンク(ぺんてる(株)製)を充填し、上記ポスターカラー蛍光ピンク2gを容器本体雄ねじ部2aにまんべんなく塗り、キャップを締めトルク15(kgf [0027] Cap fixation test: filling the container body poster color fluorescent pink (Pentel Co., Ltd.), thoroughly coating the poster color fluorescent pink 2g to the container body externally threaded portion 2a, tighten the cap torque 15 (kgf
・cm)で閉める。 · Cm) close by. 50℃で24時間放置し、その後、 It was allowed to stand at 50 ° C. 24 h, then
室温で冷却する。 It cooled at room temperature. このようにねじ部の絵の具を乾燥した後、キャップの開けトルクをトルクメーター(Mode Thus after drying the paint of the threaded portion, the opening torque of the cap torque meter (Mode
l2−OT、Tohnichi(株)製)で測定し、初期開けトルクとする。 l2-OT, as measured by Tohnichi (Ltd.)), as an initial open torque. 以上の試験を5回繰り返した後、 After repeating five times or more of the test,
トルクメーターで再度開けトルクを測定し、使用後の開けトルクとする。 Again measured for open torque with a torque meter, and open torque of after use.

【0028】 [0028]

【発明の効果】以上詳細に説明した様に、本発明に係わる、描画材容器は、絵の具などによるキャップの固着力を低下させ、また繰り返し使用によってもその効果が低下しない優れたものである。 As described above in detail, according to the present invention, according to the present invention, drawing material container, paint reduces the fixing strength of the cap due, also in which the effect is superior not decrease even by repeated use.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】 正断面図 FIG. 1 is a front cross-sectional view

【符号の説明】 DESCRIPTION OF SYMBOLS

1 キャップ 1a 雌ネジ部 2 容器本体 2a 雄ネジ部 1 cap 1a female screw portion 2 container body 2a male threaded portion

Claims (1)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 容器本体と、この容器本体に螺合により着脱自在に取り付けられるキャップとよりなる皮膜形成性組成物用容器において、前記キャップはオレフィン系樹脂と、ポリエチレンにポリジメチルシロキサンをグラフト重合したグラフト共重合体との混合物により形成されたものであることを特徴とする皮膜形成性組成物用容器。 1. A container body, the more becomes a film-forming composition container and a cap removably attached by threaded engagement to the container body, said cap graft-polymerized with an olefin-based resin, a polyethylene polydimethylsiloxane It was for film-forming composition, wherein the container to be mixed and is formed by composition of the graft copolymer.
JP25954899A 1999-09-13 1999-09-13 Container for coating forming composition Pending JP2001080299A (en)