JP2001054597A - Golf club head - Google Patents

Golf club head

Info

Publication number
JP2001054597A
JP2001054597A JP11231302A JP23130299A JP2001054597A JP 2001054597 A JP2001054597 A JP 2001054597A JP 11231302 A JP11231302 A JP 11231302A JP 23130299 A JP23130299 A JP 23130299A JP 2001054597 A JP2001054597 A JP 2001054597A
Authority
JP
Japan
Prior art keywords
head
stainless steel
club head
thickness
golf club
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP11231302A
Other languages
Japanese (ja)
Inventor
Yu Hasebe
Yasunori Imamoto
泰範 今本
祐 長谷部
Original Assignee
Bridgestone Sports Co Ltd
ブリヂストンスポーツ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bridgestone Sports Co Ltd, ブリヂストンスポーツ株式会社 filed Critical Bridgestone Sports Co Ltd
Priority to JP11231302A priority Critical patent/JP2001054597A/en
Publication of JP2001054597A publication Critical patent/JP2001054597A/en
Application status is Pending legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a stainless steel club head which may be made smaller in the thickness of an outer shell than the conventional stainless steel hollow golf club head and consequently, may be made larger in size than the conventional stainless steel head.
SOLUTION: The outer shell is formed of the stainless steel having tensile strength of ≥1800 MPa and the elongation of ≥10%. Also, the thickness of a face part is specified to a range of 1.5 to 2.5 mm, the center width a of the face part to 44 to 52 mm and the thickness of a crown part to 0.4 to 0.7 mm. As a result, the head volume may be made to ≥250 cc.
COPYRIGHT: (C)2001,JPO

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、ステンレス鋼製の中空ゴルフクラブヘッドに関し、さらに詳述すると、外殻が薄肉に形成され、大型化を図ることが可能なゴルフクラブヘッドに関する。 BACKGROUND OF THE INVENTION The present invention relates to a hollow golf club head made of stainless steel, To be more specific, the outer shell is formed to be thin, a golf club head capable of achieving size.

【0002】 [0002]

【従来の技術】従来、ステンレス鋼製のゴルフクラブヘッドでは、一般に、ステンレス鋼としてSUS630が使用されている。 In a conventional, golf club head made of stainless steel, in general, SUS630 as stainless steel is used. SUS630は、Crが15.00〜 SUS630 is, Cr is 15.00~
17.50%、Niが3.00〜5.00%、Cuが3.00〜5.00%、Nbが0.15〜0.45%、 17.50% Ni is 3.00 to 5.00% Cu is 3.00 to 5.00% Nb is 0.15 to 0.45%,
Cが0.07%以下、Siが1.00%以下、Mnが1.00%以下、Pが0.040%以下、Sが0.03 C is 0.07% or less, Si is 1.00% or less, Mn is 1.00% or less, P is 0.040% or less, S is 0.03
0%以下の組成を有する析出硬化系ステンレス鋼である。 0% precipitation hardening stainless steel having the following composition. このSUS630で形成されたウッド型の中空ゴルフクラブヘッドの体積は、最大のものでも235cc程度である。 The volume of the hollow golf club head of wood type formed in this SUS630 is 235cc about also the largest ones.

【0003】 [0003]

【発明が解決しようとする課題】近年、金属製のウッド型中空ゴルフクラブヘッドの大型化が進み、チタニウム合金製のヘッドでは体積250cc以上の大型ヘッドが実現している。 [0005] In recent years, upsizing of the metal wood type hollow golf club head, in titanium alloy of the head is realized volume 250cc or larger head. これに対し、前述のようにステンレス鋼製のクラブヘッドの体積が最大でも235cc程度であるのは、SUS630の強度及び比重を考慮すると、それが限度だからである。 In contrast, the volume of the stainless steel club head as described above is 235cc about at most, considering the strength and specific gravity of SUS630, it is because the limit. すなわち、ヘッドを大きくするためには、外殻の薄肉化を図る必要があるが、SUS6 That is, in order to increase the head, it is necessary to reduce the thinning of the outer shell, SUS6
30のヘッドで外殻を薄くして体積235ccを超えるヘッドを作製した場合には、ヘッドの強度が不十分になるものであった。 When produced a head by thinning the outer shell exceeds the volume 235cc and the 30 head was achieved, the strength of the head becomes insufficient. この場合、フェース部の厚さを部分的に2.0mm程度に薄くすることができても、フェース部の内面にリブを設けて補強したりするような緻密な設計が必要であった。 In this case, even if it is possible to reduce the thickness of the face portion in order partially 2.0 mm, dense design as or reinforce ribs on the inner surface of the face portion is required. また、SUS630でヘッド強度を保持したまま体積240ccのヘッドを作製した場合、 Also, in the case of manufacturing a head remains volume 240cc holding the head strength SUS630,
ヘッド重量が195g以上となってしまい、これに60 Head weight becomes equal to or greater than 195g, this 60
g台の軽量シャフトを付けたとしても、重量の点でクラブ長さが44インチ以上のゴルフクラブを作ることは難しかった。 Even with the g table of lightweight shaft, club length in terms of weight it was difficult to make the golf club of more than 44 inches.

【0004】一方、前述したように、最近では比重の小さいチタニウム合金による大型ヘッドが製造されているが、チタニウム合金は酸化しやすいため、製造時のヘッド研磨にステンレス鋼製ヘッドの2倍程度の時間をかけて酸化しないようにする必要があり、また、溶接にもアルゴンガスを用いるなどして酸化防止に細心の注意を払う必要があった。 On the other hand, as described above, but a large head by small titanium alloy specific gravity recently been manufactured, since the titanium alloy is easily oxidized, about twice the stainless steel head head polishing during manufacture should not oxidize over time, also, it is necessary to pay close attention to the antioxidant, such as using the argon gas to the welding. そのため、チタニウム合金製のクラブヘッドは、材料が高価であることに加え、加工に時間がかかることにより、製造コストが高くなるという問題があった。 Therefore, titanium alloy club head, in addition to that the material is expensive, by take time to process, there is a problem that manufacturing cost becomes high. さらに、一般にチタニウム合金はステンレス鋼に比べて弾性係数が低いので、チタニウム合金製ヘッドは打撃時の球離れが遅く、ヘッドスピードの速いゴルファーにとっては打球感が物足りないという欠点があった。 Further, generally titanium alloy has a lower modulus of elasticity as compared to stainless steel, titanium alloy head slow ball away at the time of hitting, for the fast head speed golf player has a disadvantage that it is unsatisfactory feel at impact.

【0005】本発明は、前述した事情に鑑みてなされたもので、ヘッド強度を低下させることなく、外殻の肉厚を従来のステンレス鋼製ヘッドに比べて薄くすることができ、したがって従来のステンレス鋼製ヘッドよりも大型にすることが可能なステンレス鋼製中空ゴルフクラブヘッドを提供することを目的とする。 [0005] The present invention has been made in view of the above, without reducing the head strength can be thinner than the thickness of the outer shell in conventional stainless steel heads, therefore conventional It is large than stainless steel head and an object thereof is to provide a stainless steel hollow golf club head capable.

【0006】 [0006]

【課題を解決するための手段】本発明は、前記目的を達成するため、ヘッドの外殻がステンレス鋼により形成された中空ゴルフクラブヘッドにおいて、前記ステンレス鋼の引張強度が1800MPa以上、伸びが10%以上であり、かつ、フェース部の肉厚が1.5mm〜2.5 The present invention SUMMARY OF] In order to achieve the above object, in a hollow golf club head formed outer shell of the head of stainless steel, the tensile strength of the stainless steel is more than 1800 MPa, elongation 10 % or more, and the and the thickness of the face portion is 1.5mm~2.5
mm、フェース部のセンター幅aが44〜52mm、クラウン部の肉厚が0.4mm〜0.7mmの範囲にあることを特徴とするゴルフクラブヘッドを提供する。 mm, center width a of the face portion is 44~52Mm, the thickness of the crown portion to provide a golf club head, characterized in that the range of 0.4Mm~0.7Mm.

【0007】従来のステンレス鋼製のウッド型ヘッドは、SUS630の引張強度が1300MPa程度、伸びが10%程度であるため、ヘッド強度を保持するためにフェース部の肉厚を2.7mm程度、フェース部のセンター最大幅を43mm程度、クラウン部の肉厚を0. [0007] Conventional stainless steel wood head, about the tensile strength of SUS630 is 1300 MPa, since the elongation is about 10%, 2.7 mm about the thickness of the face portion to hold the head strength, the face 43mm about the center maximum width of the part, the thickness of the crown portion 0.
8mm程度にしており、その結果、最大でも体積235 It has been to about 8mm, as a result, volume at most 235
cc程度のヘッドしか作ることができなかった。 It was only able to make cc about the head.

【0008】これに対し、本発明では、ヘッド材料にS [0008] On the other hand, in the present invention, S to head material
US630より強度が高いステンレス鋼を用いるので、 Since US630 from strength having a high stainless steel,
ヘッド強度を保持しつつフェース部の肉厚を1.5mm 1.5mm the thickness of the face portion while maintaining the head strength
〜2.5mm、フェース部のセンター幅aを44〜52 ~2.5mm, the center width a of the face portion 44 to 52
mm、クラウン部の肉厚を0.4mm〜0.7mmの範囲にすることができ、その結果、体積250cc以上の大型ヘッドを作製することが可能となる。 mm, the thickness of the crown portion can be in the range of 0.4Mm~0.7Mm, as a result, it is possible to produce a volume 250cc or larger head.

【0009】この場合、従来のSUS630では、フェース部の肉厚を2.5mmにしても、フェース部の最大幅は43.5mm程度にしかできなかったが、本発明では強度がより高いステンレス鋼を用いるので、フェースセンター幅aを従来のSUS630製ヘッドより広い4 [0009] In this case, the conventional SUS630, even if the thickness of the face portion to 2.5 mm, the maximum width of the face portion could not be only about 43.5 mm, a higher strength in the present invention of stainless steel since use of the face center width a wider than conventional SUS630 steel head 4
4〜52mmとしても、十分なヘッド強度を得ることができる。 Even 4~52Mm, it is possible to obtain a sufficient head strength.

【0010】また、本発明においてヘッドをステンレス鋼で作製するのは、錆びにくい材料であるためである。 Further, for making the head of stainless steel in the present invention is for a rust resistant material.
具体的には下記理由及びからである。 And specifically by the following reasons and color. ウッド型ヘッドは表面をウレタン塗料などで塗装するのが通常であるが、本発明で用いるステンレス鋼と強度的に比較的近いマルエイジング鋼は錆びやすいため、ウッド型ヘッドをマルエイジング鋼で作製した場合には、 Although wood head is usually to paint the surface such as a urethane coating, stainless steel and strength relatively close maraging steel used in the present invention and is easily rusty to prepare a wood head with maraging steel in case of,
塗装に傷が付いたときにそこからヘッドが錆びる可能性がある。 From there you head there is a possibility that the rust when scratched in the paint. したがって、ウッド型ヘッドの材料としては、 Therefore, as the material of the wood head,
マルエイジング鋼はあまり好ましくなく、ステンレス鋼が適当である。 Maraging steel less preferred, are suitable stainless steel.

【0011】ウッド型ヘッドを錆びやすい材料で作製した場合、フェース面をウレタン塗料などで塗装する必要があるが、フェース面を塗装したヘッドは、雨天時にボールと塗膜との間に水の層ができ、バックスピン量が減少したり、しなかったりして、インパクト後の弾道が不安定となることがある。 [0011] When prepared in wood-type head an easy-rust material, it is necessary to paint the face, such as a urethane paint, head painted the face surface, a layer of water between the ball and the coating film at the time of rainy weather It can be, or back spin rate is reduced, then or not, ballistic after the impact may become unstable. したがって、ウッド型ヘッドのフェース面には塗装を施さない方が好ましく、そのためにはヘッドの材料としてステンレス鋼を用いることが適当である。 Accordingly, preferred is better not subjected to coating on the face of the wood head, for which is suitable to use a stainless steel as the material of the head.

【0012】 [0012]

【発明の実施の形態】以下、本発明につきさらに詳しく説明する。 DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, will be explained in more detail per the present invention. 本発明で用いるステンレス鋼は、引張強度が1800MPa以上、より好ましくは2000〜300 Stainless steel for use in the present invention has a tensile strength of more than 1800 MPa, more preferably from 2000 to 300
0MPaで、伸びが10%以上、より好ましくは12〜 In 0 MPa, elongation of 10% or more, more preferably 12 to
16%のものである。 It is of 16%. このようなステンレス鋼としては、限定されるものではないが、Feを主成分とし、C Such stainless steel, but are not limited to, the main component Fe, C
rが14〜16%、Niが5〜7%、Cuが1.25〜 r is 14~16%, Ni is 5~7%, Cu is 1.25
1.75%、Moが0.5〜1.0%、Pが0.01〜 1.75%, Mo is 0.5~1.0%, P is 0.01
0.05%、Cが0〜0.05%、Mnが0〜1.0 0.05%, C is 0 to 0.05%, Mn is 0 to 1.0
%、Sが0〜0.03%、Siが0〜1.0%の組成を有するステンレス鋼を挙げることができる。 %, S is 0 to 0.03%, Si can be mentioned stainless steel having a composition 0 to 1.0%.

【0013】本発明のゴルフクラブヘッドは、図1及び図2を参照すると、上述したステンレス鋼を用い、フェース部の肉厚を1.5mm〜2.5mm、より好ましくは1.8〜2.3mm、フェース部のセンター幅aを4 [0013] The golf club head of the present invention, referring to FIGS. 1 and 2, using the above-described stainless steel, 1.5 mm to 2.5 mm the thickness of the face portion, and more preferably 1.8 to 2. 3mm, the center width a of the face portion 4
4〜52mm、より好ましくは45〜50mm、クラウン部の肉厚を0.4mm〜0.7mm、より好ましくは0.5〜0.6mmの範囲に形成するものである。 4~52Mm, more preferably 45~50mm, 0.4mm~0.7mm the thickness of the crown portion, and more preferably those that form a range of 0.5-0.6 mm. フェース部のセンター幅aは、より詳細に述べると、グランドラインに対してクラブを所定のライ角に設定した場合におけるフェースセンター幅である。 Center width a of the face portion, More particularly, a face center width in case of setting the club to a predetermined lie angle with respect to the ground line.

【0014】フェース面には、通常、スコアラインと呼ばれる深さ0.5mm程度の溝を形成するので、フェース部の肉厚を1.5mmより薄くすると、フェース部の強度が低下し、打撃時にフェース部が変形するおそれが生じる。 [0014] face is usually because a groove depth of approximately 0.5mm called score line, if the thickness of the face portion thinner than 1.5 mm, the strength of the face portion is reduced, when hit possibility that the face portion is deformed arises. 一方、フェース部の肉厚を2.5mmより厚くすると、ヘッドの大型化を図ることが難しくなる。 On the other hand, if the thickness of the face portion is thicker than 2.5 mm, it becomes difficult to reduce the size of the head. また、フェース部のセンター幅aを44mmより狭くすると、ヘッドの大型化を図ることが難しくなり、52mm Further, when the center width a of the face portion is narrower than 44 mm, it becomes difficult to reduce the size of the head, 52 mm
より広くすると、ヘッド強度が低下したり、ヘッドが重くなりすぎて一般ゴルファーが扱いにくくなったりする可能性が生じる。 And more broadly, or head strength is lowered, the possibility that the head may become general golfer unwieldy too heavy occurs. さらに、クラウン部の肉厚を0.4m In addition, 0.4m the wall thickness of the crown portion
mより薄くするとヘッド強度が低下し、0.7mmより厚くするとヘッドの大型化を図ることが難しくなる。 Head strength decreases when thinner than m, possible to head size of difficult when thicker than 0.7 mm.

【0015】なお、本発明のヘッドは、フェース部の肉厚を2.0mm以上とすれば、フェース部の内面に補強用のリブを付けなくても確実に十分な強度を保つことができるが、フェース部の肉厚を1.5〜1.8mm程度とし、フェース部の強度低下が懸念されるような場合でも、幅1.5mm程度、高さ1mm程度の2〜6本位の細長いリブをフェース部の内面に設けることにより、十分に強度を保つことができる。 [0015] The head of the present invention, if the thickness of the face portion and above 2.0 mm, can be kept reliably sufficient strength even without attaching the reinforcing ribs on the inner surface of the face portion the thickness of the face portion is about 1.5~1.8Mm, even when the strength reduction of the face portion is concerned, a width of about 1.5 mm, the elongated ribs of 2-6-oriented height of about 1mm by providing the inner surface of the face portion, it is possible to maintain a sufficiently strength.

【0016】本発明では、前述のようにフェース部及びクラウン部を薄肉に形成することによって、体積250 In the present invention, by forming the face portion and the crown portion thin as described above, volume 250
cc以上の大型のステンレス鋼製ヘッドを得ることができる。 It can be obtained a large stainless steel head over cc. このようにヘッド体積をチタニウム合金製ヘッドと同等の250cc以上とすることにより、ヘッドの大きさや、ヘッドの重心周りの慣性モーメントなどの機能の点で、ゴルファーが十分に満足できるゴルフクラブとすることができる。 Thus by making the head volume and titanium alloy head equivalent 250cc or more, the size of the head and, in terms of functions, such as moment of inertia around the center of gravity of the head, to a golf club golfer fully satisfactory can. ただし、ヘッド体積が320ccを超えると、ヘッド強度が低下したり、ヘッドが重くなりすぎて一般ゴルファーが扱いにくくなったりする可能性がある。 However, when the head volume is more than 320 cc, there is a possibility that the head strength may become or generally golfer unwieldy head too heavy reduction. したがって、本発明のゴルフクラブヘッドの体積は、250cc〜320ccとすることが好ましい。 Accordingly, the volume of the golf club head of the present invention, it is preferable that the 250Cc~320cc.

【0017】 [0017]

【実施例】下記表1に示す材料A〜Dを用いて実施例1 EXAMPLES using materials A~D shown in Table 1 in Example 1
〜3及び比較例1〜5のウッド型中空ゴルフクラブヘッドを作製した。 To 3 and were prepared wood type hollow golf club head of Comparative Example 1-5. 材料A〜Dの比重、引張強度、伸びを表1に、本発明のステンレス鋼の組成を表2に、作製したクラブヘッドの性状を表3に示す。 The specific gravity of the material to D, tensile strength, elongation in Table 1, the composition of the stainless steel of the present invention in Table 2 shows the properties of the club head was manufactured in Table 3. なお、本発明のステンレス鋼とは、引張強度1800MPa以上、伸び10 Note that the stainless steel of the present invention has a tensile strength 1800MPa or more, elongation 10
%以上の本発明で用いるステンレス鋼のことである。 % Or more is that the stainless steel used in the present invention.

【0018】 [0018]

【表1】 [Table 1]

【0019】 [0019]

【表2】 [Table 2]

【0020】 [0020]

【表3】 [Table 3]

【0021】実施例1〜3及び比較例1〜5のクラブヘッドを用いてゴルフクラブを作製し、各クラブヘッドの強度試験を行った。 [0021] to produce a golf club with a club head of Examples 1-3 and Comparative Examples 1-5 was subjected to a strength test of the club head. 強度試験は、図3に示すように、クラブを垂直にした状態でグリップをグリップ固定用具に固定し、ボール打撃試験機を用いてヘッドのフェース面の中心部に真正面から1000発のゴルフボールを当てた後、フェース部の変形を調べた。 Strength test, as shown in FIG. 3, the grip in the upright club fixed to the grip retainer, 1000 shots of the golf ball squarely in the center of the face surface of the head with the ball striking tester after the hit, it examined the deformation of the face portion. 上記ボール打撃試験機は、圧縮空気を利用してゴルフボールを所定速度で発射するものである。 The ball striking tester utilizes the compressed air is to launch a golf ball at a predetermined speed. また、ボール速度は、一般ゴルファーやシニア層レベルの40m/s、上級ゴルファーレベルの45m/s、トッププロレベルの50m/sとした。 In addition, ball speed was generally golfers and senior layer level 40m / s, senior golfer level of 45m / s, and 50m / s of the top professional level.

【0022】 [0022]

【表4】 [Table 4]

【0023】表4より、本発明のクラブヘッドは、ステンレス鋼による大型ヘッドでありながら、十分な強度を有することが分かる。 [0023] From Table 4, the club head of the present invention is to provide a large head by stainless steel, it is found to have sufficient strength.

【0024】 [0024]

【発明の効果】本発明のクラブヘッドは、強度が高くかつ割れにくいステンレス鋼で外殻を形成したので、ヘッド強度を低下させることなく、外殻の肉厚を従来のステンレス鋼製ヘッドに比べて薄くすることができ、したがって従来のステンレス鋼製ヘッドよりも大型にすることが可能である。 Club head of the present invention according to the present invention, since the formation of the outer shell with high strength and hard to break stainless steel, without reducing the head strength, than the wall thickness of the outer shell in conventional stainless steel heads Te thinner it can, therefore it is possible to a large than conventional stainless steel heads. また、ステンレス鋼ヘッドであるため、 Furthermore, since a stainless steel head,
チタニウム合金製ヘッドに比べて材料コスト、製造時の作業性などの点で有利であるとともに、打球感が良いという利点を有する。 Material cost than a titanium alloy head, with the advantage of workability during production, with the advantage that the shot feel is good.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】本発明のゴルフクラブヘッドの一例を示す正面図である。 1 is a front view showing an example of a golf club head of the present invention.

【図2】図1のゴルフクラブヘッドの左側面図である。 FIG. 2 is a left side view of the golf club head of FIG. 1.

【図3】クラブヘッドの強度試験のための装置を示す説明図である。 3 is an explanatory diagram showing an apparatus for strength testing of the club head.

【符号の説明】 DESCRIPTION OF SYMBOLS

a フェース部のセンター幅 a face portion of the center width

Claims (2)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 ヘッドの外殻がステンレス鋼により形成された中空ゴルフクラブヘッドにおいて、前記ステンレス鋼の引張強度が1800MPa以上、伸びが10%以上であり、かつ、フェース部の肉厚が1.5mm〜2. 1. A shell of the head in the hollow golf club head formed of stainless steel, the tensile strength of the stainless steel or 1800 MPa, and an elongation of 10% or more and thickness of the face portion 1. 5mm~2.
    5mm、フェース部のセンター幅aが44〜52mm、 5mm, center width a of the face portion is 44~52mm,
    クラウン部の肉厚が0.4mm〜0.7mmの範囲にあることを特徴とするゴルフクラブヘッド。 Golf club head the wall thickness of the crown portion is characterized in that it is in the range of 0.4mm~0.7mm.
  2. 【請求項2】 ヘッド体積が250cc〜320ccの範囲にある請求項1に記載のゴルフクラブヘッド。 2. A golf club head according to claim 1 head volume is in the range of 250Cc~320cc.
JP11231302A 1999-08-18 1999-08-18 Golf club head Pending JP2001054597A (en)