JP2000313843A - Coating material composition - Google Patents

Coating material composition

Info

Publication number
JP2000313843A
JP2000313843A JP2000208321A JP2000208321A JP2000313843A JP 2000313843 A JP2000313843 A JP 2000313843A JP 2000208321 A JP2000208321 A JP 2000208321A JP 2000208321 A JP2000208321 A JP 2000208321A JP 2000313843 A JP2000313843 A JP 2000313843A
Authority
JP
Japan
Prior art keywords
coating composition
coating
building
composition according
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
JP2000208321A
Other languages
Japanese (ja)
Other versions
JP2000313843A5 (en
Inventor
Rikuo Himeno
陸男 姫野
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to JP2000208321A priority Critical patent/JP2000313843A/en
Publication of JP2000313843A publication Critical patent/JP2000313843A/en
Publication of JP2000313843A5 publication Critical patent/JP2000313843A5/ja
Withdrawn legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To obtain an coating material containing slaked lime as the major component and excellent in opacifying properties with reduced coating amounts, and coated materials coated therewith. SOLUTION: This coating material composition comprises slaked lime, an acrylic resin, an inorganic pigment, and water, and as the compounding ratio, (a) the slaked lime is less than 30 wt.% (in terms of solids); (b) the acrylic resin which is a homopolymer or copolymer containing at least one member, as the monomer component, selected from the group consisting of (meth)acrylic acid, a (meth)acrylic ester, (meth)acrylamide and (meth)acrylonitrile is 1-85 wt.% (in terms of solids); and (c) the inorganic pigment is 0.1-90 wt.% (in terms of solids). Coated materials can be prepared by using the coating material composition.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【発明の属する技術分野】本発明は、各種建築物の内・
外壁、屋根及び天井などの内装若しくは外装の化粧塗装
に適した水性塗料に関する。より詳細には、本発明は、
水性塗料として要求される各種の塗料性能並びに塗膜物
性を充足するとともに、漆喰特有の落ち着いた艶消しの
質感を有する塗膜を形成する建築用塗料組成物に関す
る。さらに本発明は該塗料組成物を塗布してなる塗装
物、特に建材に関する。
TECHNICAL FIELD The present invention relates to various types of buildings.
The present invention relates to a water-based paint suitable for interior or exterior decoration such as an outer wall, a roof and a ceiling. More specifically, the present invention provides
The present invention relates to an architectural coating composition which satisfies various coating properties and coating film properties required as a water-based coating, and forms a coating film having a calm matte texture unique to plaster. Furthermore, the present invention relates to a coated product obtained by applying the coating composition, particularly a building material.

【0002】[0002]

【従来の技術】漆喰は、落ち着きのある重厚な仕上がり
感に加えて、調湿性(吸湿性及び放湿性)、結露防止性
及び防カビ性といった機能に優れているため、日本建築
の屋内外の塗り壁材として古くから使用されている建築
材料である。
2. Description of the Related Art In addition to the calm and profound finish, plaster has excellent functions such as humidity control (moisture absorption and moisture release), anti-condensation and anti-mold properties. It is a building material that has long been used as a painted wall material.

【0003】しかし、漆喰の施工には熟練を要する左官
作業が必要であり、作業者の技術によって仕上がりにバ
ラツキが生じ易く、また複数回の繰り返し施工(塗りと
コテこすり)の必要性から施工能率が悪く、施工期間が
長くかかったり施工コストも高くつくという欠点があ
る。
However, plastering requires plastering work that requires skill, and the finish is likely to vary due to the skill of the worker. In addition, the necessity of multiple repetitions (painting and rubbing) makes the construction efficient. However, there is a disadvantage that the construction period is long and the construction cost is high.

【0004】このため、近年の住宅建築における室内壁
面の仕上げには、塩ビクロス貼りや合成樹脂エマルジョ
ン塗装などの仕上げ方法が多く採用されているが、最近
になって化学物質過敏症やシックハウス症候群などとい
った化学物質の悪害が問題視されるようになり、かかる
悪害のない上記漆喰等の天然素材が再び見直されてきて
いる。
For this reason, in order to finish the interior wall of a recent residential building, many finishing methods such as PVC cloth application and synthetic resin emulsion painting have been adopted, but recently, chemical sensitivity, sick house syndrome, etc. The harm of such chemical substances has been regarded as a problem, and natural materials such as the above plaster without such harm have been reviewed again.

【0005】[0005]

【発明が解決しようとする課題】本発明は、漆喰壁材の
成分である消石灰を配合した水性の塗料組成物を提供す
ることを目的とする。より具体的には、本発明は水性塗
料としての性能を有するとともに、形成される塗膜が漆
喰壁特有の質感を有し且つ耐アルカリ性や耐洗浄性を始
めとする塗膜物性並びに防カビ性及び耐火性等といった
塗膜機能に優れることにより建築用塗料として好適に使
用できる塗料組成物を提供することを目的とするもので
ある。
SUMMARY OF THE INVENTION An object of the present invention is to provide an aqueous paint composition containing slaked lime, which is a component of a plaster wall material. More specifically, the present invention has the performance as a water-based paint, and the coating film formed has a texture unique to a stucco wall, and the coating film properties such as alkali resistance and washing resistance, and mold resistance. It is an object of the present invention to provide a coating composition which can be suitably used as an architectural coating because of its excellent coating function such as fire resistance and the like.

【0006】さらに本発明は上記塗料組成物から形成さ
れる塗膜を有する塗装物、具体的には内・外壁材や天井
材として用いられる内装及び外装用の各種建材(ボー
ド、パネル、クロス等)を提供することを目的とするも
のである。
Further, the present invention relates to a painted product having a coating film formed from the above-mentioned coating composition, specifically, various building materials (board, panel, cloth, etc.) for interior and exterior used as inner / outer wall materials and ceiling materials. ).

【0007】[0007]

【課題を解決するための手段】本発明者は、漆喰の優れ
た美粧性及び機能に着目し、漆喰特有の質感(外観)や
機能を備えながらも慣用のエマルションペイントと同様
の品質及び使用感を有する水性塗料を開発することを目
的として、鋭意検討を重ねたところ、漆喰の主成分であ
る消石灰に特定の樹脂及び水を配合することにより、漆
喰の質感や機能を備えた状態で貯蔵安定性及び塗装作業
性に優れた水性塗料組成物が調製できることを見出し
た。また、かかる塗料組成物から形成される塗膜は、従
来漆喰壁材に必須であったすさ等の繊維素材を必ずしも
含有しなくても十分な付着性及び靱性を発揮し成膜性に
優れること、また逆に繊維素材を含まないことによっ
て、レベリング性が向上してより少ない塗布量で薄塗膜
化が可能となり、刷毛、ローラー、スプレー、フローコ
ーター等の慣用の塗装作業によって塗膜を簡単にかつ美
しく仕上げることができることを見出した。
SUMMARY OF THE INVENTION The present inventor has paid attention to the excellent cosmetic properties and functions of stucco, and has the same quality and usability as conventional emulsion paints while having the texture (appearance) and functions peculiar to stucco. After a thorough study with the aim of developing a water-based paint having a stucco, storage stability with the texture and function of the stucco was achieved by blending the specific resin and water with slaked lime, which is the main component of the stucco. It has been found that an aqueous coating composition having excellent properties and coating workability can be prepared. In addition, a coating film formed from such a coating composition exhibits sufficient adhesion and toughness even if it does not necessarily contain fiber material such as susa, which has conventionally been essential for a plaster wall material, and has excellent film-forming properties. Conversely, the absence of fibrous materials improves the leveling properties and enables thinner coatings with less application amount.Since coatings can be easily applied by brush, roller, spray, flow coater, etc. I found that it can be finished smoothly and beautifully.

【0008】さらに本発明者は、かかる知見に基づいて
更なる検討を進めたところ、上記塗料組成物に更に顔料
として酸化チタンを始めとする無機の白色顔料を配合す
ることにより、漆喰特有の質感を有しながら極めて少量
の塗布量で施工面を隠蔽でき、かつ成膜性に優れるこ
と、さらにこの効果は体質顔料を配合することによって
さらに強化できることを見出し、これらのことから、本
発明の塗料組成物によれば、低コストでかつ少ない労力
で、漆喰特有の落ち着きのある重厚な質感を有する塗膜
が形成できることを確認した。
Further, the present inventor has conducted further studies based on the above findings. As a result, by further adding an inorganic white pigment such as titanium oxide as a pigment to the coating composition, the texture unique to stucco was obtained. It has been found that the construction surface can be concealed with an extremely small amount of coating while having an excellent coating property, and that this effect can be further enhanced by blending the extender pigment. According to the composition, it was confirmed that a low-cost and low-laboratory coating film having a calm and heavy texture unique to plaster can be formed.

【0009】本発明は、かかる知見に基づいて開発され
たものである。
The present invention has been developed based on such knowledge.

【0010】すなわち本発明は、下記1.〜12.に掲
げる塗料組成物である: 1.消石灰、アクリル系樹脂、無機顔料及び水を含有す
る塗料組成物であって、(a)消石灰の配合割合が30
重量%未満(固形換算)、(b)アクリル系樹脂が(メ
タ)アクリル酸、(メタ)アクリル酸エステル、(メ
タ)アクリルアミド類及び(メタ)アクリロニトリルよ
りなる群から選択されるいずれか少なくとも1種をモノ
マー成分として含有するホモポリマーまたはコポリマー
であって、該樹脂の配合割合が1〜85重量%(固形換
算)、並びに(c)無機顔料の配合割合が0.1〜90
重量%(固形換算)である建築用塗料組成物。 2.アクリル系樹脂が、(メタ)アクリル酸若しくはそ
のエステルから形成されるホモポリマーまたはコポリマ
ーである1記載の建築用塗料組成物。 3.無機顔料が酸化チタン,亜鉛華,リトポン,硫化亜
鉛及びアンチモン白よりなる群から選択される少なくと
も1種の白色顔料、好ましくは酸化チタンである1また
は2に記載の建築用塗料組成物。 4.消石灰の配合割合が14〜30重量%未満(固形換
算)である1乃至3のいずれかに記載の建築用塗料組成
物。 5.アクリル系樹脂の配合割合が1〜17重量部(固形
換算)である、1乃至4のいずれかに記載の建築用塗料
組成物。 6.無機顔料の配合割合が1〜5重量部(固形換算)で
ある1乃至5のいずれかに記載の建築用塗料組成物。 7.さらに体質顔料を含有することを特徴とする1乃至
6のいずれかに記載の建築用塗料組成物。 8.体質顔料がタルク、炭酸カルシウム、カオリンクレ
ー、水酸化アルミニウム、ベントナイト、硫酸バリウ
ム、ホワイトカーボン及びシリカよりなる群から選択さ
れる少なくとも1種である7に記載の建築用塗料組成
物。 9.繊維素材を含まないことを特徴とする1乃至8のい
ずれかに記載の建築用塗料組成物。 10.乾燥塗膜の隠蔽力が500μm以下である1乃至
9のいずれかに記載の建築用塗料組成物。 11.粘度が常温で300〜8000センチポイズであ
る1乃至10のいずれかに記載の建築用塗料組成物。 12.塗液またはその乾燥塗膜の (1)容器の中での状
態、(2)塗装作業性、(3)低温安定性、(4)塗膜の外観、
(5)耐アルカリ性、(6)耐洗浄性、(7)隠蔽率が、JISK 56
63-1995に規定される少なくとも2種ペイントの性質を
満たすものである、1乃至11のいずれかに記載の建築
用塗料組成物。
That is, the present invention provides the following 1. ~ 12. The coating compositions are as follows: A paint composition containing slaked lime, an acrylic resin, an inorganic pigment and water, wherein (a) the blending ratio of slaked lime is 30
(B) at least one selected from the group consisting of (meth) acrylic acid, (meth) acrylic acid esters, (meth) acrylamides and (meth) acrylonitrile Is a homopolymer or a copolymer containing as a monomer component, the compounding ratio of the resin is 1 to 85% by weight (solid basis), and the compounding ratio of (c) the inorganic pigment is 0.1 to 90%.
An architectural coating composition in% by weight (solid basis). 2. 2. The architectural coating composition according to 1, wherein the acrylic resin is a homopolymer or a copolymer formed from (meth) acrylic acid or an ester thereof. 3. 3. The architectural coating composition according to 1 or 2, wherein the inorganic pigment is at least one white pigment selected from the group consisting of titanium oxide, zinc white, lithopone, zinc sulfide and antimony white, preferably titanium oxide. 4. 4. The architectural coating composition according to any one of 1 to 3, wherein the blended ratio of slaked lime is 14 to less than 30% by weight (solid basis). 5. 5. The architectural coating composition according to any one of 1 to 4, wherein the blending ratio of the acrylic resin is 1 to 17 parts by weight (solid basis). 6. 6. The architectural coating composition according to any one of 1 to 5, wherein the blending ratio of the inorganic pigment is 1 to 5 parts by weight (solid basis). 7. The architectural coating composition according to any one of claims 1 to 6, further comprising an extender pigment. 8. 8. The architectural coating composition according to 7, wherein the extender is at least one selected from the group consisting of talc, calcium carbonate, kaolin clay, aluminum hydroxide, bentonite, barium sulfate, white carbon, and silica. 9. 9. The architectural coating composition according to any one of 1 to 8, which does not contain a fiber material. 10. 10. The architectural coating composition according to any one of 1 to 9, wherein the hiding power of the dried coating film is 500 µm or less. 11. 11. The architectural coating composition according to any one of 1 to 10, which has a viscosity of 300 to 8000 centipoise at room temperature. 12. (1) state of the coating liquid or its dried coating film in a container, (2) coating workability, (3) low-temperature stability, (4) appearance of coating film,
(5) Alkali resistance, (6) Wash resistance, (7) Concealment ratio is JISK 56
12. The architectural coating composition according to any one of 1 to 11, which satisfies at least two kinds of paint properties specified in 63-1995.

【0011】また本発明は、上記に掲げる建築用塗料組
成物から形成される塗膜を有する塗装物、具体的には内
・外壁材、屋根材や天井材などに用いられる内装及び外
装用の建材に関する。さらに、本発明は上記建築用塗料
組成物の塗装方法及び上記建材を用いた建築物内外装の
施工方法に関する。また本発明は上記塗料組成物を用い
た建築物内外装面の修復方法に関する。
[0011] The present invention also relates to a painted product having a coating film formed from the above-mentioned architectural coating composition, and specifically to interior and exterior materials used for interior and exterior wall materials, roofing materials and ceiling materials, and the like. Concerning building materials. Furthermore, the present invention relates to a method for applying the above-mentioned architectural coating composition and a method for constructing the interior and exterior of a building using the above-mentioned building material. The present invention also relates to a method for restoring the interior and exterior surfaces of a building using the coating composition.

【0012】[0012]

【発明の実施の形態】(1)塗料組成物 本発明の塗料組成物は、消石灰、アクリル系樹脂、無機
顔料及び水を主成分として含有する水性の塗料組成物で
ある。
DESCRIPTION OF THE PREFERRED EMBODIMENTS (1) Paint Composition The paint composition of the present invention is an aqueous paint composition containing slaked lime, an acrylic resin, an inorganic pigment and water as main components.

【0013】本発明で用いられる消石灰としては、通常
漆喰壁材の成分として用いられるものであればよく特に
制限されない。例えば、工業用消石灰(例えば、JIS A6
902)をはじめ、水硬性及び気硬性の別なく各種の水酸
化カルシウムを用いることができる。また着色等の処理
を施した消石灰を使用することもできる。なお、その粒
子径も特に制限されず、工業用消石灰として通常用いら
れる粒子径のほか、該粒子径より小さいものも任意に使
用することができる。尚、消石灰の主成分である水酸化
カルシウムは空気中の二酸化炭素の影響を受けて炭酸カ
ルシウムになる性質を有することから、上記消石灰の一
部若しくは全部に代えて炭酸カルシウムを用いることも
本件発明の範囲に含まれる。
The slaked lime used in the present invention is not particularly limited as long as it is generally used as a component of a plaster wall material. For example, industrial slaked lime (for example, JIS A6
902), various types of calcium hydroxide can be used regardless of hydraulic or air-hardness. Slaked lime that has been subjected to a treatment such as coloring can also be used. The particle size is not particularly limited, and a particle size smaller than the particle size can be arbitrarily used in addition to a particle size usually used as industrial slaked lime. Since calcium hydroxide, which is a main component of slaked lime, has the property of becoming calcium carbonate under the influence of carbon dioxide in the air, it is also possible to use calcium carbonate in place of part or all of the slaked lime. Included in the range.

【0014】塗料組成物中の消石灰の配合割合は、本発
明の塗料組成物が貯蔵安定性や塗装作業性並びに成膜性
等において所望の性能を充足するような範囲であれば特
に制限されず、塗料組成物の固形分100重量%あたり
30重量%未満の範囲から適宜選択することができる。
かかる範囲として、制限はされないが、より詳細には、
例えば2〜30重量%未満、5〜30重量%未満、10
〜30重量%未満または14〜30重量%未満の範囲を
挙げることができる。
The mixing ratio of slaked lime in the coating composition is not particularly limited as long as the coating composition of the present invention satisfies the desired performance in storage stability, coating workability, film formability and the like. , Can be appropriately selected from the range of less than 30% by weight per 100% by weight of the solid content of the coating composition.
Such ranges are not limited, but more specifically,
For example, less than 2-30% by weight, less than 5-30% by weight, 10
The range may be up to less than 30% by weight or 14 to less than 30% by weight.

【0015】また本発明でいうアクリル系樹脂とは、
(メタ)アクリル酸、(メタ)アクリル酸エステル、
(メタ)アクリルアミド類、及び(メタ)アクリロニト
リルを主原料(モノマー成分)とし単独ないし相互間ま
たは他樹脂(モノマー成分)との共重合によって調製さ
れる樹脂を意味するものである。かかるモノマー成分と
して具体的には、上記各範疇に含まれるものであって商
業的に入手可能なものであればよく、特に制限されな
い。
The acrylic resin referred to in the present invention is:
(Meth) acrylic acid, (meth) acrylic acid ester,
It means a resin prepared by using (meth) acrylamides and (meth) acrylonitrile as main raw materials (monomer components) alone or by copolymerization with each other or with another resin (monomer components). Specific examples of such monomer components are not particularly limited as long as they are included in each of the above categories and are commercially available.

【0016】好ましくは、 (i)アクリル酸、メタアクリル酸: (ii)アクリル酸エステルまたはメタクリル酸エステル:
例えばアクリル酸メチル、アクリル酸エチル、アクリル
酸n−プロピル、アクリル酸イソプロピル、アクリル酸
n-ブチル、アクリル酸イソブチル、アクリル酸t-ブチ
ル、アクリル酸ヘキシル、アクリル酸n-オクチル、ア
クリル酸-2-エチルヘキシル、アクリル酸ラウリル、ア
クリル酸ステアリル、アクリル酸パルミチルまたはアク
リル酸シクロヘキシル等のアルキル基の炭素数が1〜18
のアクリル酸アルキルエステル;メタアクリル酸メチ
ル、メタアクリル酸エチル、メタアクリル酸n−プロピ
ル、メタアクリル酸イソプロピル、メタアクリル酸n−
ブチル、メタアクリル酸イソブチル、メタアクリル酸t
−ブチル、メタアクリル酸ヘキシル、メタアクリル酸n
−オクチル、メタアクリル酸−2−エチルヘキシル、メ
タアクリル酸ラウリル、メタアクリル酸ステアリル、メ
タアクリル酸パルミチル及びメタアクリル酸シクロヘキ
シル等のアルキル基の炭素数が1〜18程度のメタアクリ
ル酸アルキルエステル;アクリル酸ヒドロキシエチル、
メタクリル酸ヒドロキシエチル、アクリル酸ヒドロキシ
プロピル、メタクリル酸ヒドロキシプロピル、アクリル
酸ヒドロキシブチル、メタクリル酸ヒドロキシブチル等
のように(メタ)アクリル酸の側鎖に水酸基を有するア
ルキルエステル;アクリル酸メトキシブチル、メタクリ
ル酸メトキシブチル、アクリル酸メトキシエチル、メタ
クリル酸メトキシエチル、アクリル酸エトキシブチル、
メタクリル酸エトキシブチル等のように(メタ)アクリ
ル酸の側鎖にアルコキシル基を有するアルキルエステ
ル;アクリル酸アリルやメタクリル酸アリル等の(メ
タ)アクリル酸のアルケニルエステル;アリルオキシエ
チルアクリレートやアリルオキシエチルメタクリレート
等の(メタ)アクリル酸のアルケニルオキシアルキルエ
ステル;アクリル酸グリシジル、メタアクリル酸グリシ
ジル、並びにアクリル酸メチルグリシジルやメタアクリ
ル酸メチルグリシジル等のようにアクリル酸の側鎖にエ
ポキシ基を有するアルキルエステル;アクリル酸ジエチ
ルアミノエチル、メタクリル酸ジエチルアミノエチル、
アクリル酸メチルアミノエチル、メタクリル酸メチルア
ミノエチル等の(メタ)アクリル酸のモノ−又はジ−ア
ルキルアミノアルキルエステル;側鎖としてシリル基、
アルコキシシリル基または加水分解性アルコキシシリル
基などを有するシリコーン変性(メタ)アクリル酸エス
テル; (iii)アクリルアミド類またはメタクリルアミド類:例
えばアクリルアミド;メタクリルアミド;N−メチロー
ルアクリルアミド及びN−メチロールメタクリルアミド
等のようにメチロール基を有する(メタ)アクリルアミ
ド;N−アルコキシメチロールアクリルアミド(例え
ば、N−イソブトキシメチロールアクリルアミド等)、
及びN−アルコキシメチロールメタクリルアミド(例え
ば、N−イソブトキシメチロールメタクリルアミド等)
等のようにアルコキシメチロール基を有する(メタ)ア
クリルアミド;N−ブトキシメチルアクリルアミドやN
−ブトキシメチルメタクリルアミドなどのアルコキシア
ルキル基を有する(メタ)アクリルアミドなど、 (iv)アクリロニトリル、メタクリロニトリル等の各種の
アクリル系単量体を挙げることができる。
Preferably, (i) acrylic acid or methacrylic acid: (ii) acrylate or methacrylate:
For example, methyl acrylate, ethyl acrylate, n-propyl acrylate, isopropyl acrylate, n-butyl acrylate, isobutyl acrylate, t-butyl acrylate, hexyl acrylate, n-octyl acrylate, 2-acrylic acid The alkyl group such as ethylhexyl, lauryl acrylate, stearyl acrylate, palmityl acrylate or cyclohexyl acrylate has 1 to 18 carbon atoms.
Alkyl acrylate; methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, isopropyl methacrylate, n-methacrylate
Butyl, isobutyl methacrylate, t-methacrylate
-Butyl, hexyl methacrylate, n-methacrylate
-Octyl, 2-ethylhexyl methacrylate, lauryl methacrylate, stearyl methacrylate, palmityl methacrylate, cyclohexyl methacrylate and the like, wherein the alkyl group has about 1 to 18 carbon atoms; Hydroxyethyl acid,
Alkyl esters having a hydroxyl group in the side chain of (meth) acrylic acid, such as hydroxyethyl methacrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, hydroxybutyl acrylate, hydroxybutyl methacrylate; methoxybutyl acrylate, methacrylic acid Methoxybutyl, methoxyethyl acrylate, methoxyethyl methacrylate, ethoxybutyl acrylate,
Alkyl esters having an alkoxyl group in the side chain of (meth) acrylic acid such as ethoxybutyl methacrylate; alkenyl esters of (meth) acrylic acid such as allyl acrylate and allyl methacrylate; allyloxyethyl acrylate and allyloxyethyl Alkenyloxyalkyl esters of (meth) acrylic acid such as methacrylate; glycidyl acrylate, glycidyl methacrylate, and alkyl esters having an epoxy group in the side chain of acrylic acid such as methyl glycidyl acrylate and methyl glycidyl methacrylate Diethylaminoethyl acrylate, diethylaminoethyl methacrylate,
Mono- or di-alkylaminoalkyl esters of (meth) acrylic acid such as methylaminoethyl acrylate and methylaminoethyl methacrylate; a silyl group as a side chain;
(Iii) Acrylamides or methacrylamides: for example, acrylamides or methacrylamides; N-methylol acrylamide, N-methylol methacrylamide and the like, having an alkoxysilyl group or a hydrolyzable alkoxysilyl group. (Meth) acrylamide having a methylol group as described above; N-alkoxymethylolacrylamide (for example, N-isobutoxymethylolacrylamide and the like);
And N-alkoxymethylol methacrylamide (for example, N-isobutoxymethylol methacrylamide and the like)
(Meth) acrylamide having an alkoxymethylol group, such as N-butoxymethylacrylamide and N
(Iv) Various acrylic monomers such as (meth) acrylamide having an alkoxyalkyl group such as butoxymethyl methacrylamide, and (iv) acrylonitrile and methacrylonitrile.

【0017】これらのアクリル系単量体は単独で、また
は二種以上を任意に混合して使用することができる。す
なわち、本発明で用いられるアクリル系樹脂は、例えば
上記に例示する各種のモノマー成分の1種単独から構成
されるホモポリマーであっても、上記に例示する各種モ
ノマー成分を2種以上任意に組み合わせてなるコポリマ
ーであってもよい。さらに上記アクリル系単量体は他の
モノマー成分と任意に組み合わせてコポリマー(共重合
体)を形成することもでき、本発明のアクリル系樹脂に
は当該共重合体も包含される。アクリル系単量体と組み
合わせて用いられるモノマー成分としては、アクリル系
単量体と共重合体を形成するものであれば特に制限され
ず、例えば酢酸ビニル、塩化ビニル、塩化ビニリデン、
乳酸ビニル、酪酸ビニル、ピバル酸ビニル、V酸(vers
atic acid)ビニル及び安息香酸ビニルなどのビニル系
単量体、ブタジエン、スチレン等を挙げることができ
る。このような共重合体として、具体的には、スチレン
−アクリルエステル,スチレン−アクリロニトリル及び
スチレン−アクリルアミド−アクリル酸エチルなどのス
チレン/アクリル共重合体、酢酸ビニル−アクリル酸エ
ステルや酢酸ビニル−メタクリル酸エステル等の酢酸ビ
ニル/アクリル共重合体、ブタジエン−アクリロニトリ
ル等のブタジエン/アクリル共重合体、塩化ビニル/ア
クリル共重合体、塩化ビニリデン/アクリル共重合体、
ベオバ/アクリル共重合体などを例示することができ
る。本発明のアクリル系樹脂には、そのほかアクリル変
性・アルキド樹脂、アクリル変性・酢酸ビニル/塩化ビ
ニル共重合体樹脂、フッ素変性アクリル樹脂等が包含さ
れる。
These acrylic monomers can be used alone or in any combination of two or more. That is, the acrylic resin used in the present invention may be, for example, a homopolymer composed of one of the various monomer components exemplified above alone, or any combination of two or more of the various monomer components exemplified above. May be used. Further, the acrylic monomer can be arbitrarily combined with other monomer components to form a copolymer (copolymer), and the acrylic resin of the present invention includes the copolymer. The monomer component used in combination with the acrylic monomer is not particularly limited as long as it forms a copolymer with the acrylic monomer, for example, vinyl acetate, vinyl chloride, vinylidene chloride,
Vinyl lactate, vinyl butyrate, vinyl pivalate, V acid (vers
atic acid) vinyl monomers such as vinyl and vinyl benzoate, butadiene, styrene and the like. Specific examples of such a copolymer include styrene / acrylic copolymers such as styrene-acrylic ester, styrene-acrylonitrile and styrene-acrylamide-ethyl acrylate, vinyl acetate-acrylic ester and vinyl acetate-methacrylic acid. Vinyl acetate / acrylic copolymers such as esters, butadiene / acrylic copolymers such as butadiene-acrylonitrile, vinyl chloride / acrylic copolymers, vinylidene chloride / acrylic copolymers,
A veoba / acrylic copolymer can be exemplified. The acrylic resin of the present invention further includes an acrylic-modified alkyd resin, an acrylic-modified vinyl acetate / vinyl chloride copolymer resin, a fluorine-modified acrylic resin, and the like.

【0018】本発明で用いられるアクリル系樹脂とし
て、好ましくは上記アクリル系単量体を単独で、または
二種以上を任意に混合して調製されるホモポリマーまた
はコポリマー、及びシリコーン変性アクリル樹脂(アク
リルシリコン樹脂)である。より好ましくは(メタ)ア
クリル酸またはそのエステルのホモポリマーまたはコポ
リマー、及びシリコーン変性アクリル樹脂(アクリルシ
リコン樹脂)である。なお、シリコーン変性アクリル樹
脂(アクリルシリコン樹脂)には、側鎖としてシリル
基、アルコキシシリル基または加水分解性アルコキシシ
リル基などを有するシリコーン変性(メタ)アクリル酸
エステルをモノマー成分として調製されるもののほか、
シリコンとアクリレートを複合化したもの、両者をブロ
ック共重合体したもの、シリコンを部分的にアクリル修
飾したもの、並びにシリコンとアクリレートを他の架橋
剤で架橋させたもの等が含まれる。
The acrylic resin used in the present invention is preferably a homopolymer or a copolymer prepared by mixing the above acrylic monomers alone or arbitrarily mixing two or more of them, and a silicone-modified acrylic resin (acrylic resin). Silicone resin). More preferred are a homopolymer or copolymer of (meth) acrylic acid or an ester thereof, and a silicone-modified acrylic resin (acrylic silicone resin). The silicone-modified acrylic resin (acrylic silicone resin) includes a silicone-modified (meth) acrylic ester having a silyl group, an alkoxysilyl group, a hydrolyzable alkoxysilyl group, or the like as a side chain, as well as those prepared as a monomer component. ,
Examples include those in which silicon and acrylate are combined, those in which both are block copolymerized, those in which silicon is partially modified with acryl, those in which silicon and acrylate are crosslinked with another crosslinking agent, and the like.

【0019】前述するアクリル系単量体及び該アクリル
系単量体と組み合わせて用いられる各種モノマー成分の
種類、使用量及び重合度等は、得られる本発明の塗料組
成物の使用温度(硬化温度)や消石灰などの塗料組成物
の他成分との相溶性等を考慮しながら、例えば得られる
樹脂のガラス転移点(Tg)等を目安として適宜選択さ
れる。例えば、塗料組成物を常温乾燥型塗料として調製
する場合に用いられるアクリル系樹脂としては、特に制
限はされないが、ガラス転移点が−100〜+30℃程
度にあるものを選択することができる。また塗料組成物
を強制乾燥型塗料(例えば乾燥温度:50〜200℃)
として調製する場合に用いられるアクリル系樹脂として
は、特に制限されないが、ガラス転移点が+30〜15
0℃の範囲にあるものを選択することができる。
The type, amount and degree of polymerization of the above-mentioned acrylic monomer and various monomer components used in combination with the acrylic monomer are determined by the operating temperature (curing temperature) of the obtained coating composition of the present invention. ) And slaked lime, taking into consideration the compatibility with other components of the coating composition and the like, and are appropriately selected, for example, using the glass transition point (Tg) of the obtained resin as a guide. For example, there is no particular limitation on the acrylic resin used when preparing the coating composition as a room-temperature-drying coating, but a resin having a glass transition point of about -100 to + 30 ° C can be selected. In addition, the coating composition is subjected to forced drying type coating (for example, drying temperature: 50 to 200 ° C).
The acrylic resin used in the case where it is prepared as is not particularly limited, but has a glass transition point of +30 to 15
Those in the range of 0 ° C. can be selected.

【0020】本発明の塗料組成物を現場での塗装施工に
簡便に用いる態様で調製する場合には、当該塗料組成物
は室温〜常温で硬化し得る常温乾燥型塗料であることが
好ましく、この場合に用いられるアクリル系樹脂も常温
乾燥型樹脂であることが好ましい。
When the coating composition of the present invention is prepared in a mode that is easily used for on-site coating, the coating composition is preferably a room temperature-drying type coating material that can be cured at room temperature to room temperature. The acrylic resin used in this case is also preferably a room temperature drying type resin.

【0021】また用いられるアクリル系樹脂の形態は特
に制限されず、エマルジョンや水性ポリマーディスパー
ジョン等の水性乳濁もしくは分散形態、再乳化形粉末樹
脂などの粉末形態、液状ポリマーなどの液状等のいずれ
の態様であってもよい。好ましくはエマルジョンの態様
である。エマルジョンとして配合する場合、エマルジョ
ンは重合性不飽和二重結合を有するモノマーをエマルジ
ョン重合して得られるもの、または、予め合成した樹脂
を水系分散媒に分散剤を使用して分散したものの何れで
もよく、さらに粉末型のポリマーを水等に分散して調製
したものを挙げることができる。
The form of the acrylic resin used is not particularly limited, and may be any of an aqueous emulsion or dispersion form such as an emulsion or an aqueous polymer dispersion, a powder form such as a re-emulsified powder resin, and a liquid form such as a liquid polymer. May be adopted. Preferably, it is in the form of an emulsion. When blended as an emulsion, the emulsion may be obtained by emulsion polymerization of a monomer having a polymerizable unsaturated double bond, or may be obtained by dispersing a previously synthesized resin in an aqueous dispersion medium using a dispersant. And those prepared by dispersing a powder type polymer in water or the like.

【0022】本発明で用いるアクリル系樹脂は塗料組成
物中の消石灰同士の接着強度、消石灰と後述する添加剤
との接着強度、並びに塗料組成物と被塗布物との付着強
度を高め、その結果として、被塗布物表面に形成された
塗膜層(被覆層)のひび割れを防止し、建材の靱性を向
上させる働きを有している。
The acrylic resin used in the present invention increases the adhesive strength between slaked limes in the coating composition, the adhesive strength between slaked lime and the additives described below, and the adhesive strength between the coating composition and the object to be coated. It has the function of preventing cracks in the coating layer (coating layer) formed on the surface of the object to be coated and improving the toughness of the building material.

【0023】アクリル系樹脂の配合割合は、貯蔵安定性
や塗装作業性並びに成膜性等といった水性塗料として要
求される性能、好ましくは後述するJIS K 5663-1995に
規定される少なくとも2種ペイントの性質を充足する範
囲であれば特に制限されず、使用するアクリル系樹脂の
種類に応じて適宜定めることができる。具体的には、塗
料組成物100重量%(固形換算)中のアクリル系樹脂
の配合割合として、通常1〜85重量%(固形換算)の
範囲から選択調整することができる。好ましくは1〜5
0重量%、より好ましくは1〜30重量%、更に好まし
くは1〜17重量%である。また、当該アクリル系樹脂
は消石灰100重量部に対して3〜1000重量部(固
形換算)の範囲で配合することが好ましい。当該配合割
合としてより具体的には10〜500重量部、好ましく
は10〜300重量部、より好ましくは10〜130重
量部の範囲を例示することができる。
The mixing ratio of the acrylic resin is determined by the performance required as an aqueous paint such as storage stability, coating workability and film formability, preferably at least two paints specified in JIS K 5663-1995 described later. There is no particular limitation as long as the range satisfies the properties, and it can be appropriately determined according to the type of acrylic resin used. Specifically, the blending ratio of the acrylic resin in 100% by weight (solid basis) of the coating composition can be selected and adjusted usually from the range of 1 to 85% by weight (solid basis). Preferably 1 to 5
0% by weight, more preferably 1 to 30% by weight, still more preferably 1 to 17% by weight. Further, the acrylic resin is preferably blended in a range of 3 to 1000 parts by weight (solid basis) based on 100 parts by weight of slaked lime. More specifically, the mixing ratio may be in the range of 10 to 500 parts by weight, preferably 10 to 300 parts by weight, more preferably 10 to 130 parts by weight.

【0024】本発明においては、上記消石灰及びアクリ
ル系樹脂に加えて、更に顔料(白色顔料、有色顔料)並
びに各種の添加剤を配合することができる。かかる添加
剤としては、例えば顔料分散剤、湿潤剤、消泡剤、増粘
剤、凍結融解安定剤、皮膜形成助剤及びレオロジー調整
剤等の塗膜形成助剤の他、無機材料(細骨材などの無機
充填剤)、界面活性剤、可塑剤、減水剤、流動化剤、防
腐剤、防水剤、抗菌剤等を挙げることができる。
In the present invention, in addition to the slaked lime and the acrylic resin, a pigment (white pigment, colored pigment) and various additives can be further blended. Such additives include, for example, pigment dispersants, wetting agents, defoamers, thickeners, freeze-thaw stabilizers, film-forming aids such as film-forming aids and rheology modifiers, as well as inorganic materials (fine bones). Inorganic fillers such as materials), surfactants, plasticizers, water reducing agents, fluidizing agents, preservatives, waterproofing agents, antibacterial agents and the like.

【0025】顔料としては、水性塗料に用いられるもの
であれば特に制限されず、いずれの顔料をも採用するこ
ともできるが、好ましくは無機顔料である。かかる無機
顔料としては、酸化チタン,亜鉛華,リトポン,硫化亜
鉛,アンチモン白、鉛白、ジルコニア等の白色顔料;カ
ーボンブラックや酸化鉄等の黒色顔料:カドミウムレッ
ド,べんがら(酸化鉄),モリブデンレッド、鉛丹等の
赤色顔料:黄鉛(クロムイエロー),チタンイエロー,
カドミウムイエロー,黄色酸化鉄,タン,アンチモンイ
エロー,バナジウムスズイエロー,バナジウムジルコニ
ウムイエローの黄色顔料:酸化クロム,ビリジアン,チ
タンコバルトグリーン,コバルトグリーン,コバルトク
ロムグリーン,ビクトリアグリーン等の緑色顔料:群
青,紺青,コバルトブルー,セルリアンブルー,コバル
トシリカブルー,コバルト亜鉛シリカブルーなどの青色
顔料といった各種の有色顔料を例示することができる。
本発明の塗料組成物中に配合する顔料の割合は特に制限
されず、所望の隠蔽力並びに色彩(明度、色度、彩度)
に応じて適宜選択調整することができる。
The pigment is not particularly limited as long as it is used for an aqueous paint, and any pigment can be employed, but an inorganic pigment is preferred. Examples of such inorganic pigments include white pigments such as titanium oxide, zinc white, lithopone, zinc sulfide, antimony white, lead white, and zirconia; black pigments such as carbon black and iron oxide: cadmium red, red iron oxide, and molybdenum red. And red pigments such as lead red: yellow (chrome yellow), titanium yellow,
Yellow pigments of cadmium yellow, yellow iron oxide, tan, antimony yellow, vanadium tin yellow, vanadium zirconium yellow: green pigments such as chromium oxide, viridian, titanium cobalt green, cobalt green, cobalt chrome green, and Victoria green: ultramarine, navy blue, Various colored pigments such as a blue pigment such as cobalt blue, cerulean blue, cobalt silica blue, and cobalt zinc silica blue can be exemplified.
The proportion of the pigment to be blended in the coating composition of the present invention is not particularly limited, and the desired hiding power and color (brightness, chromaticity, saturation) are desired.
Can be selected and adjusted as appropriate.

【0026】無機顔料のうち好ましいものとして酸化チ
タン,亜鉛華,リトポン,硫化亜鉛またはアンチモン白
等の白色顔料を挙げることができる。隠蔽力や着色力の
観点から好ましくは酸化チタンである。但し、特にこれ
に拘泥されることなく、酸化チタンと同等もしくは類似
の隠蔽力または着色力を有する白色顔料が、酸化チタン
に代えて若しくは酸化チタンと組み合わせて、任意に使
用できることは当業者であれば容易に想到できることで
ある。かかる白色顔料として、制限されないがリトポ
ン,硫化亜鉛,亜鉛華が例示できる。
Preferred among the inorganic pigments are white pigments such as titanium oxide, zinc white, lithopone, zinc sulfide and antimony white. Titanium oxide is preferable from the viewpoint of hiding power and coloring power. However, it should be understood by those skilled in the art that a white pigment having a hiding power or coloring power equivalent or similar to titanium oxide can be optionally used in place of titanium oxide or in combination with titanium oxide without being particularly limited thereto. It is easy to imagine. Examples of such white pigments include, but are not limited to, lithopone, zinc sulfide, and zinc white.

【0027】また、酸化チタンは一般にルチル形のほう
がアナタース形よりも耐光性や隠蔽力が優れているもの
の、本発明においてはそれらの別を特に問うものでな
く、ルチル形、アナタース形並びにブルッカイト形のい
ずれをも使用することができる。また粒径及び形状も特
に制限されず、市販品の中から目的に応じて適宜選択す
ることができる。一般に酸化チタンとして、粒径0.1
〜0.5μmの略球状形のものや0.01〜0.05μ
mの超微粒子のもの、並びに紫外線吸収用板状酸化チタ
ン等が知られている。隠蔽力の観点からは、制限されな
いがルチル形の酸化チタンを用いることが好ましく、ま
た0.1〜0.3μmの粒径を有する酸化チタンが好適に
使用できる。
In general, the rutile type titanium oxide is more excellent in light resistance and hiding power than the anatase type. However, in the present invention, it does not matter whether the titanium oxide is rutile type, anatase type or brookite type. Any of these can be used. The particle size and shape are not particularly limited, and can be appropriately selected from commercially available products according to the purpose. Generally, titanium oxide has a particle size of 0.1
Approximately 0.5 μm or approximately 0.01 to 0.05 μm
m ultrafine particles, plate-like titanium oxide for ultraviolet absorption, and the like are known. From the viewpoint of hiding power, although not limited, it is preferable to use rutile titanium oxide, and titanium oxide having a particle size of 0.1 to 0.3 μm can be suitably used.

【0028】酸化チタンなどの無機顔料の塗料組成物1
00重量%(固形換算)中の配合割合は特に制限され
ず、0.1〜90重量%の範囲から適宜選択することが
できる。好ましくは0.5〜50重量%、より好ましく
は0.5〜30重量%、更に好ましくは1〜5重量%で
ある。また、当該無機顔料は消石灰100重量部に対し
て3〜1000重量部(固形換算)の範囲で配合するこ
とが好ましい。当該配合割合としてより具体的には3〜
500重量部、好ましくは3〜200重量部、より好ま
しくは3〜35重量部の範囲を例示することができる。
Coating composition 1 of inorganic pigment such as titanium oxide
The blending ratio in 00% by weight (solid basis) is not particularly limited, and can be appropriately selected from the range of 0.1 to 90% by weight. Preferably it is 0.5 to 50% by weight, more preferably 0.5 to 30% by weight, further preferably 1 to 5% by weight. Further, it is preferable that the inorganic pigment is blended in a range of 3 to 1000 parts by weight (solid basis) with respect to 100 parts by weight of slaked lime. More specifically, the mixing ratio is 3 to
500 parts by weight, preferably 3 to 200 parts by weight, more preferably 3 to 35 parts by weight.

【0029】消石灰に酸化チタンを始めとする無機顔
料、特に白色顔料を上記割合で配合することにより調製
される本発明の塗料組成物は、より少ない塗布量で被塗
布面を隠蔽することができ、しかもかかる少量の塗料で
形成された塗膜は、薄塗膜ながら所望の外観や物性を有
しており、また消石灰の配合割合に応じて調湿性やそれ
に伴う結露防止性等の機能を発揮させることも可能であ
る。
The coating composition of the present invention prepared by blending slaked lime with an inorganic pigment such as titanium oxide, particularly a white pigment, in the above-mentioned ratio can cover the surface to be coated with a smaller amount of coating. In addition, the coating film formed with such a small amount of paint has the desired appearance and physical properties in spite of being a thin coating film, and exhibits functions such as humidity control and accompanying dew condensation prevention depending on the mixing ratio of slaked lime. It is also possible to make it.

【0030】また隠蔽力を向上させるためには、更に体
質顔料を組み合わせて使用することもできる。かかる体
質顔料としては、特に制限されないが、タルク,カオリ
ンクレー,水酸化アルミニウム,炭酸カルシウム(重質
炭酸カルシウム、沈降炭酸カルシウム),ベントナイ
ト、硫酸バリウム(沈降性硫酸バリウム、バライト
粉)、ホワイトカーボン及びシリカなどを挙げることが
できる。なお、これらの体質顔料は1種単独で使用して
も、2種以上を組み合わせて使用することもできる。中
でも好ましい体質顔料はタルク、炭酸カルシウムまたは
ホワイトカーボンである。
In order to improve the hiding power, an extender may be used in combination. Such extenders are not particularly limited, but include talc, kaolin clay, aluminum hydroxide, calcium carbonate (heavy calcium carbonate, precipitated calcium carbonate), bentonite, barium sulfate (precipitable barium sulfate, barite powder), white carbon and Silica and the like can be mentioned. In addition, these extenders can be used alone or in combination of two or more. Among them, preferred extenders are talc, calcium carbonate and white carbon.

【0031】体質顔料を配合する場合のその配合割合と
しては、制限されないが、塗料組成物100重量%(固
形換算)中、通常0.1〜90重量%の範囲を挙げるこ
とができる。好ましくは1〜70重量%、より好ましく
は1〜50重量%、さらに好ましくは1〜30重量%で
ある。また、当該体質顔料は消石灰100重量部に対し
て0.3〜4500重量部(固形換算)の範囲で配合す
ることができる。当該配合割合としてより具体的には3
〜3500重量部、好ましくは3〜2500重量部、よ
り好ましくは3〜1500重量部の範囲を例示すること
ができる。
When the extender is blended, the blending ratio thereof is not limited, but is usually in the range of 0.1 to 90% by weight based on 100% by weight (solid basis) of the coating composition. It is preferably from 1 to 70% by weight, more preferably from 1 to 50% by weight, still more preferably from 1 to 30% by weight. In addition, the extender can be added in a range of 0.3 to 4500 parts by weight (solid basis) based on 100 parts by weight of slaked lime. More specifically, the mixing ratio is 3
A range of from 3 to 3,500 parts by weight, preferably from 3 to 2500 parts by weight, more preferably from 3 to 1500 parts by weight can be exemplified.

【0032】上記の薄塗膜ながら所望の外観や物性を有
するような塗膜は、本発明の塗料組成物を1m2あたり
固形重量換算で少なくとも100g、好ましくは300
g程度使用することによって形成することができる。調
湿性等の塗膜機能は塗料組成物の塗布量を増すに従って
向上するため、かかる機能に鑑みれば、本発明は塗料組
成物の塗布量の上限を制限するものではない。しかしな
がら、塗料の成膜性、コスト並びに塗装作業性等を考慮
すれば、本発明の塗料組成物は1m2あたり固形重量換
算で100g〜1000gの範囲で用いることが好まし
く、所望に仕上げ感(意匠)に合わせて例えば100〜
800g、100〜500g、150〜400g、20
0〜300gなどの範囲を種々選択できる。
The above-mentioned thin coating film having desired appearance and physical properties can be obtained by coating the coating composition of the present invention with at least 100 g, preferably 300 g, in terms of solid weight per 1 m 2.
It can be formed by using about g. The coating function such as humidity control improves as the coating amount of the coating composition is increased. Therefore, in view of such a function, the present invention does not limit the upper limit of the coating amount of the coating composition. However, in consideration of the coating film formability, cost, coating workability, and the like, the coating composition of the present invention is preferably used in a range of 100 g to 1000 g in terms of solid weight per 1 m 2 , and a desired finish (design) 100)
800g, 100-500g, 150-400g, 20
Various ranges such as 0 to 300 g can be selected.

【0033】本発明の塗料組成物は、消石灰を主成分と
する従来の塗材に比して高い塗膜隠蔽力を有することを
特徴とすることができる。例えば本発明の塗料組成物を
黒白板上に塗布したとき、形成される塗膜を通して肉眼
で観察した場合に下地の黒白の判別が不可能となる塗膜
の厚さは、1mm以下、好ましくは500μm以下、よ
り好ましくは300μm以下、さらに好ましくは200
μm以下、また更に好ましくは100μm以下であるこ
とが望ましい。本発明において塗膜隠蔽力とは、塗料組
成物を素地に塗布した場合にその素地の色を認識し得な
くなる塗膜の最小膜厚のことであり、具体的には黒白板
上に塗装した塗膜を通して肉眼で観察した場合に下地の
黒白の判別が不可能となる塗膜の最小膜厚を意味する。
The coating composition of the present invention can be characterized by having a higher coating film hiding power than a conventional coating material containing slaked lime as a main component. For example, when the coating composition of the present invention is applied on a black-and-white plate, the thickness of the coating film from which it is impossible to determine the black and white of the base when observed with the naked eye through the formed coating film is 1 mm or less, preferably 500 μm or less, more preferably 300 μm or less, even more preferably 200 μm or less.
μm or less, and more preferably 100 μm or less. In the present invention, the coating film hiding power is the minimum film thickness of a coating film that cannot recognize the color of the base material when the coating composition is applied to the base material, and specifically, is applied on a black and white plate. It means the minimum thickness of the coating film that makes it impossible to determine the black and white of the base when observed with the naked eye through the coating film.

【0034】本発明で用いられる無機質充填剤として
は、例えば珪砂、寒水砂、パーライト,バーミキュライ
ト,シラス球及び汚泥焼成骨材などの再生骨材等の無機
質骨材(細骨材)の他、カオリン、ハロイサイト、モン
モリロナイト、ベントナイト、ギブサイト、マイカ、セ
ラミックサンド、ガラスビーズ、パーライト、酸性白
土、陶石、ロウ石、長石、石灰石、石膏、ドロマイト、
マグネサイト、滑石などの天然無機質材料;水酸化バリ
ウム、水酸化マグネシウム、天然カルシウム等の水不溶
性金属水酸化物;トベルモナイトやゾノトライト等のケ
イ酸カルシウム系水和物;カルシウムアルミネート水和
物、カルシウムスルホアルミネート水和物等の各種酸化
物の水和物;アルミナ、シリカ、含水ケイ酸、マグネシ
ア、酸化亜鉛、スピネル、合成炭酸カルシウム、リン酸
カルシウム、炭酸マグネシウム、硫酸バリウム、チタン
酸カリウムなどの合成無機質などの粉末状、繊維状もし
くは粒状の無機質材料を挙げることができる。
The inorganic filler used in the present invention includes, for example, inorganic aggregates (fine aggregates) such as regenerated aggregates such as silica sand, cold water sand, perlite, vermiculite, shirasu spheres and sludge fired aggregates, and kaolin. , Halloysite, montmorillonite, bentonite, gibbsite, mica, ceramic sand, glass beads, perlite, acid clay, pottery stone, feldspar, feldspar, limestone, gypsum, dolomite,
Natural inorganic materials such as magnesite and talc; water-insoluble metal hydroxides such as barium hydroxide, magnesium hydroxide and natural calcium; calcium silicate hydrates such as tobermonite and zonotlite; calcium aluminate hydrate, calcium Hydrates of various oxides such as sulfoaluminate hydrate; synthetic minerals such as alumina, silica, hydrous silicic acid, magnesia, zinc oxide, spinel, synthetic calcium carbonate, calcium phosphate, magnesium carbonate, barium sulfate, potassium titanate And powdery, fibrous, or granular inorganic materials.

【0035】これら無機質材料の粒度は特に制限されな
いが、60〜130メッシュ、または80〜100メッ
シュの範囲を例示することができる。また無機細骨材
等、無機質充填剤を本発明の塗料組成物に配合する場合
のその割合は、適宜設定することができる。制限されな
いが、消石灰100重量部に対して5〜1000重量
部、好ましくは10〜500重量部、より好ましくは2
0〜300重量部の範囲を例示することができる。
The particle size of these inorganic materials is not particularly limited, but may be in the range of 60 to 130 mesh or 80 to 100 mesh. In addition, when an inorganic filler such as an inorganic fine aggregate is blended in the coating composition of the present invention, the ratio thereof can be appropriately set. Although not limited, 5-1000 parts by weight, preferably 10-500 parts by weight, more preferably 2 to 100 parts by weight per 100 parts by weight of slaked lime.
A range of 0 to 300 parts by weight can be exemplified.

【0036】(顔料)分散剤及び湿潤剤としては、いず
れも通常塗料に配合して用いられるものが広く採用で
き、例えばアルキルナフタレンスルホン酸ソーダのホル
マリン縮合物、低分子ポリアクリル酸アンモン、低分子
量スチレン−マレイン酸アンモン共重合体、ポリオキシ
エチレンの脂肪酸エステルやアルキルフェノールエーテ
ル、スルホコハク酸誘導体、ポリエチレンオキサイドと
ポリプロピレンオキサイドとのブロックポリマーなどを
例示することができる。
As the (pigment) dispersant and wetting agent, those commonly used in the art can be widely used by blending them in paints. For example, formalin condensate of sodium alkylnaphthalenesulfonate, low molecular weight ammonium polyacrylate, low molecular weight Examples thereof include a styrene-ammonium maleate copolymer, a fatty acid ester of polyoxyethylene, an alkylphenol ether, a sulfosuccinic acid derivative, and a block polymer of polyethylene oxide and polypropylene oxide.

【0037】消泡剤としては、通常塗料や建築用吹き付
け材に配合して用いられるものであれば特に制限され
ず、いずれをも採用することもできる。例えば、オクチ
ルアルコール、グリコール誘導体、シクロヘキサン、シ
リコン、プルロニック系界面活性剤、ポリオキシエチレ
ンアルキルフェニルエーテル等の各種の抑泡剤及び破泡
剤を挙げることができる。
The defoaming agent is not particularly limited as long as it is usually used by being blended into a paint or a building spray material, and any of them can be employed. For example, various foam inhibitors and foam breakers such as octyl alcohol, glycol derivatives, cyclohexane, silicon, pluronic surfactants, and polyoxyethylene alkyl phenyl ether can be mentioned.

【0038】増粘剤としてはメチルセルロース、ヒドロ
キシエチルセルロース、ヒドロキシプロピルメチルセル
ロース等のセルロース系;サッカロース、グルコースな
どの多糖類;アクリル系;その他、アルミニウムステア
レート、ジンクステアレート、有機ベントナイト、シリ
カゲル、ポリビニルアルコール、アルギン酸ソーダ、ケ
イ酸系、ベントナイト、カゼイン酸ソーダ等を例示する
ことができる。
Examples of the thickener include cellulosics such as methylcellulose, hydroxyethylcellulose and hydroxypropylmethylcellulose; polysaccharides such as saccharose and glucose; acrylics; and other materials such as aluminum stearate, zinc stearate, organic bentonite, silica gel, polyvinyl alcohol, Examples thereof include sodium alginate, silicic acid, bentonite, and sodium caseinate.

【0039】また本発明の塗料組成物には更に珪藻土ま
たはゼオライト(合成ゼオライトを含む)を配合するこ
ともできる。珪藻土等は漆喰と同様に有害物質を含まな
い自然素材として注目されている素材であり、珪藻土や
ゼオライトを配合することによって塗膜の調湿性や結露
防止性を向上改善したり、断熱性や脱臭効果等の諸機能
性を付与することができる。
The coating composition of the present invention may further contain diatomaceous earth or zeolite (including synthetic zeolite). Diatomaceous earth is attracting attention as a natural material that does not contain harmful substances like stucco.By blending diatomaceous earth and zeolite, the moisture control and dew condensation prevention of the coating film are improved and improved, and heat insulation and deodorization are achieved. Various functions such as effects can be provided.

【0040】防水剤としては、特に制限されないが、シ
リコーンオイル、シリコーン樹脂、オルガノアルコキシ
シラン等を例示することができる。これらの成分によれ
ば、一般に塗膜の防水性、耐薬品性及び耐候性等を向上
させることができるが、本発明においては塗膜に求めら
れる所望の調湿性を妨げない範囲で用いることが好まし
い。
The waterproofing agent is not particularly restricted but includes silicone oil, silicone resin, organoalkoxysilane and the like. According to these components, generally, the waterproofness, chemical resistance, weather resistance, and the like of the coating film can be improved.However, in the present invention, it is possible to use the coating film within a range that does not hinder the desired humidity control property required for the coating film. preferable.

【0041】前述する各種成分は、本発明の塗料組成物
の固形分含有量が塗料組成物100重量%(全量)あた
り40〜80重量%、好ましくは50〜70重量%とな
るように配合調整されることが望ましい。
The above-mentioned various components are mixed and adjusted so that the solid content of the coating composition of the present invention is 40 to 80% by weight, preferably 50 to 70% by weight per 100% by weight (total amount) of the coating composition. It is desirable to be done.

【0042】本発明の塗料組成物は、従来漆喰壁材にひ
び割れ防止を目的に配合されていた、麻、和紙、しゅ
ろ、木材パルプ、合成繊維及びガラス繊維といった各種
の繊維素材を配合しなくても、ひび割れすることなく付
着性、靱性及び成膜性に優れた塗膜が形成できることを
1つの特徴とするものである。
The coating composition of the present invention does not use various fiber materials such as hemp, Japanese paper, shiroko, wood pulp, synthetic fiber and glass fiber which have been conventionally compounded in plaster wall materials for the purpose of preventing cracking. However, one of the features is that a coating film having excellent adhesion, toughness, and film-forming properties can be formed without cracking.

【0043】一般に塗料中の繊維素材の存在は、塗装に
際してスプレーやガンの吐出口が閉塞するという問題や
塗着工程後にコテ押さえを必要とするといった施工性
(塗装作業性)の悪さ、塗装後に塗膜表面が毛羽立った
り塗布面が不均一となる外観上並びに成膜性の問題、及
び塗膜が可燃性(易燃性)となるといった機能の低下を
伴う傾向がある。よって、低塗布量で美観並びに成膜性
に優れた薄塗膜を形成するためには、繊維素材を含まな
い塗料組成物であることが好ましい。しかしながら、塗
装作業性、成膜性並びに塗膜の外観等に影響を与えない
範囲であれば、本発明はその塗料組成物中に繊維素材を
含むことをなんら制限するものではない。
In general, the presence of the fiber material in the paint is caused by the problem that the discharge port of the spray or the gun is blocked at the time of painting, the poor workability (painting workability) such as the necessity of holding down the iron after the painting process, and the There is a tendency that the coating film surface becomes fluffy or the coating surface becomes non-uniform, and there is a problem of film forming property, and the coating film becomes flammable (flammable). Therefore, in order to form a thin coating film having excellent appearance and film-forming properties with a low coating amount, a coating composition containing no fiber material is preferable. However, the present invention does not restrict inclusion of a fiber material in the coating composition as long as it does not affect the coating workability, the film forming property, the appearance of the coating film, and the like.

【0044】本発明の塗料組成物は、上記各成分と水を
混合して塗料の常套方法、例えば塗料調合用機器(ミキ
サー、シェーカー、ミル、ニーダーなど)を用いて混合
することにより、消石灰、アクリル系樹脂及び顔料等を
水中に安定に分散させて、スプレー液、スラリー、また
はパテ等の各種形態の塗料として調製することができ
る。混合は通常20〜95℃で行うことができる。
The paint composition of the present invention is prepared by mixing the above-mentioned components with water and mixing with a paint in a conventional manner, for example, using a paint blending device (mixer, shaker, mill, kneader, etc.) to obtain slaked lime, An acrylic resin, a pigment, and the like can be stably dispersed in water to prepare a paint in various forms such as a spray liquid, a slurry, and a putty. Mixing can be usually performed at 20 to 95 ° C.

【0045】この際、塗料組成物は、例えばスプレー塗
り(エアスプレー、エアレススプレーなど)、刷毛塗
り、ローラー塗り、パテ塗り、コート塗り(カーテンフ
ローコーター、ロールコーター)などの各種塗装方法に
応じて所望の粘度を有するように調製することが好まし
く、塗装作業性、レベリング、塗膜外観等を考慮して好
ましい粘度範囲を適宜選択調製することができる。通
常、常温(25℃±5)で100〜60000センチポ
イズの範囲となるように調製される。例えば、液状の塗
料組成物の粘度としては、刷毛塗り、ローラー塗り、コ
ート塗りまたはスプレー塗りに適するように常温で30
0〜8000センチポイス、好ましくは500〜500
0センチポイズ、より好ましくは1000〜4500セ
ンチポイズの範囲を挙げることができる。またパテ状の
塗料組成物の粘度としては、制限されないが、常温(2
5℃±5)で8000〜30000センチポイズ、好ま
しくは8000〜20000センチポイズの範囲を挙げ
ることができる。
At this time, the coating composition is applied according to various coating methods such as spray coating (air spray, airless spray, etc.), brush coating, roller coating, putty coating, and coat coating (curtain flow coater, roll coater). The viscosity is preferably adjusted so as to have a desired viscosity, and a preferable viscosity range can be appropriately selected and adjusted in consideration of coating workability, leveling, appearance of a coating film, and the like. Usually, it is prepared to have a range of 100 to 60,000 centipoise at normal temperature (25 ° C. ± 5). For example, the viscosity of the liquid coating composition is 30 at room temperature so as to be suitable for brush coating, roller coating, coat coating or spray coating.
0-8000 centipoise, preferably 500-500
0 centipoise, more preferably in the range of 1000 to 4500 centipoise. The viscosity of the putty-like coating composition is not limited, but may be room temperature (2.
(5 ° C. ± 5) 8,000 to 30,000 centipoise, preferably 8,000 to 20,000 centipoise.

【0046】本発明の塗料組成物は、各種建築物の天井
面や壁(内・外壁)面等の内装面及び外装面の塗装、並
びに建築物の天井、屋根や壁(内・外壁)の下地材や化
粧材として用いられる各種の建材(クロス、パネル、ボ
ード)の塗装に使用することができる。また、本発明の
塗料組成物は常法に従って塗装した後に、凹凸模様付け
ローラーで模様付けを行ったり、塗膜表面を処理するこ
とによってさらに意匠仕上げを施すこともできる。
The coating composition of the present invention can be used for coating interior and exterior surfaces such as ceilings and walls (inner and outer walls) of various buildings, and for building ceilings, roofs and walls (inner and outer walls). It can be used for painting various building materials (cloths, panels, boards) used as base materials and decorative materials. Further, after the coating composition of the present invention is applied according to a conventional method, it is possible to further apply a design finish by performing patterning with an uneven patterning roller or treating the coating film surface.

【0047】本発明の塗料組成物は、好適には、塗液の
性状並びにその乾燥塗膜の外観及び物性が日本工業規格
JIS K 5663-1995に規定の少なくとも2種ペイントに関
する(1) 容器の中での状態、(2) 塗装作業性、(3) 低温
安定性、(4) 塗膜の外観、(5) 耐アルカリ性、(6) 耐洗
浄性及び (7) 隠蔽率の要件を満たすものである。
The coating composition of the present invention preferably has the properties of a coating liquid and the appearance and physical properties of a dried coating film of Japanese Industrial Standards.
Regarding at least two types of paint specified in JIS K 5663-1995 (1) State in a container, (2) Painting workability, (3) Low temperature stability, (4) Appearance of coating film, (5) Alkali resistance Satisfies the requirements of (6) wash resistance and (7) concealment ratio.

【0048】具体的には、本発明の塗料組成物は、JIS
K 5663-1995の規定に従ってJIS K 5400の方法に準じて
測定した場合に少なくとも下記の品質(JIS K 5663-199
5)を有する建築用塗料組成物である: (1) 容器の中での状態:かき混ぜた場合に塊がなく中身
全体が一様になる: (2) 塗装作業性:2回塗りで塗装作業に支障がない: (3) 低温安定性:−5℃に冷やしたとき変質しない: (4) 塗膜の外観:塗膜の外観が正常である: (5) 耐アルカリ性:水酸化カルシウム飽和溶液(20±1
℃)に18時間浸したときに異常がない: (6) 耐洗浄性:100回の洗浄に耐える: (7) 隠蔽率:0.95以上 さらに本発明の塗料組成物は、耐水性(JIS K 5400の8.
19)に関して、脱イオン水に96時間浸しても異常がな
く(JIS K 5663-1995の5.9)、促進耐候性(JIS K 5400
の9.8.1)に関して、白亜化度が8点以上で、膨れ・は
がれ・割れがなく、色の変化の程度が見本品に比べて大
きくない(JIS K 5663-1995の5.12)ことが好ましく、
また隠蔽率が0.93以上(JIS K 5663-1995の5.8)をみた
し、さらに耐候性(JIS K 5400の9.9)に関して、12ヶ
月の試験期間後に膨れ・はがれ・割れがなく色の変化の
程度と白亜化度が見本品に比べて大きくない(JIS K 56
63-1995の5.13)という要件を満たしていることが好ま
しい。
More specifically, the coating composition of the present invention
When measured according to the method of JIS K 5400 according to the provisions of K 5663-1995, at least the following quality (JIS K 5663-199
It is an architectural coating composition having 5): (1) State in a container: When stirred, there is no lump and the whole contents become uniform: (2) Painting workability: Painting work with two coats (3) Low temperature stability: No deterioration when cooled to -5 ° C: (4) Appearance of coating: Appearance of coating is normal: (5) Alkali resistance: Calcium hydroxide saturated solution (20 ± 1
(6) Washing resistance: withstands 100 washes: (7) Hiding ratio: 0.95 or more Furthermore, the coating composition of the present invention has a water resistance (JIS K 5400). 8.
Regarding item 19), there is no abnormality when immersed in deionized water for 96 hours (5.9 of JIS K 5663-1995), and accelerated weather resistance (JIS K 5400
Regarding 9.8.1), it is preferable that the degree of chalk is 8 or more, there is no blistering, peeling or cracking, and the degree of color change is not greater than that of the sample (5.12 of JIS K 5663-1995). ,
In addition, the concealment ratio was 0.93 or more (5.8 in JIS K 5663-1995), and the weather resistance (9.9 in JIS K 5400) showed no swelling, peeling or cracking after a 12-month test period. The degree of chalk is not large compared to the sample (JIS K 56
It is preferable to meet the requirement of 5.13) of 63-1995.

【0049】本発明の塗料組成物は、その乾燥時間によ
って特に限定されるものではないが、JIS K 5663-1995
の5.6に従って、JIS K 5400の6.5の試験方法に準じて実
施した場合に20℃で2時間以内に半硬化状態になるよ
うに、また5℃で4時間以内に半硬化状態になるように
調製されることが好ましい。これは塗料組成物に配合す
る固形含量や水分含量並びに粘度を適宜調製することに
よって行うことができる。
[0049] The coating composition of the present invention is not particularly limited by its drying time.
In accordance with 5.6 of JIS K 5400, when prepared according to the test method of 6.5, prepare a semi-cured state at 20 ° C within 2 hours and a semi-cured state at 5 ° C within 4 hours. Is preferably performed. This can be performed by appropriately adjusting the solid content, the water content, and the viscosity to be added to the coating composition.

【0050】(2)塗装物 また、本発明は上記塗料組成物を塗布してなる塗装物を
提供する。
(2) Painted Article The present invention also provides a coated article obtained by applying the above coating composition.

【0051】本発明の塗料組成物を塗布する基材(被塗
装物)としては、特に制限されることはないが、好適に
は建築物の天井、屋根や壁(内・外壁)の下地材や化粧
材として用いられる各種の建材、例えばクロス、ボード
及びパネル等を挙げることができる。なお、かかる基材
(建材)は表面がシーラー処理等の各種処理がなされて
いてもよい。
The substrate (object to be coated) to which the coating composition of the present invention is applied is not particularly limited, but is preferably a base material for ceilings, roofs and walls (inner / outer walls) of buildings. And various building materials used as decorative materials, such as cloths, boards and panels. The surface of such a base material (building material) may be subjected to various treatments such as a sealer treatment.

【0052】クロスとしては、例えば建築用の内装(室
内の壁や天井等)に用いられるクロス材料を広く挙げる
ことができる。クロス材料としては紙や各種繊維からな
る不織布または織布等の繊維質シートを挙げることがで
きる。具体的には、紙としては和紙、洋紙(上質紙、中
質紙)、クラフト紙、薄葉紙、裏打紙、樹脂含浸紙等、
ボール紙、厚紙等のをいずれであってもよく、例えば難
燃処理を施した紙であって壁紙の施工に適したもの、例
えば難燃性裏打紙や不燃紙等も包含される。繊維質シー
トとしては、例えば天然繊維;ガラス繊維;またはポリ
プロピレン、アクリル、ナイロン、ポリエステル、ポリ
アミド、ビニロン等の合成繊維などを構成素材として得
られる多孔性の織布や不織布、編み物等を挙げることが
できる。なお、上記素材は、1種単独で用いられても、
また2種以上を任意で組み合わせて用いることもでき
る。
Examples of the cloth include a wide variety of cloth materials used for building interiors (such as indoor walls and ceilings). Examples of the cloth material include a fibrous sheet such as a nonwoven fabric or a woven fabric made of paper or various fibers. Specifically, as paper, Japanese paper, Western paper (high quality paper, medium quality paper), kraft paper, tissue paper, backing paper, resin impregnated paper, etc.
Any of cardboard, cardboard, and the like may be used, and examples include paper that has been subjected to a flame-retardant treatment and is suitable for application of wallpaper, such as flame-retardant backing paper and non-combustible paper. Examples of the fibrous sheet include a porous woven fabric, a nonwoven fabric, and a knitted fabric obtained by using natural fibers; glass fibers; or synthetic fibers such as polypropylene, acrylic, nylon, polyester, polyamide, and vinylon as constituent materials. it can. In addition, even if the above-mentioned material is used alone,
Also, two or more kinds can be arbitrarily used in combination.

【0053】ボード及びパネルとしては、例えば建築用
の内装(室内の壁や天井等)や外装に用いられるボード
材料及びパネル材料を広く挙げることができる。具体的
には、木質板、合板、中密度繊維板、プラスチック板、
セメントモルタル、コンクリート板、PCパネル、AL
Cパネル、石綿スレート、石膏ボード、パーティクルボ
ード、発泡セメントボード、木片セメント板、ケイ酸カ
ルシウムボード、サイディングボードなどを例示するこ
とができる。好ましくは、石膏ボード、石膏パーティク
ルボード、木質板、中密度繊維板、プラスチック板、サ
イディングボード(金属系、窯業系を含む)等である。
As the board and the panel, for example, a board material and a panel material used for building interiors (indoor walls and ceilings) and exteriors can be widely used. Specifically, wood board, plywood, medium density fiber board, plastic board,
Cement mortar, concrete board, PC panel, AL
Examples include C panel, asbestos slate, gypsum board, particle board, foam cement board, wood chip cement board, calcium silicate board, siding board, and the like. Preferably, it is a gypsum board, a gypsum particle board, a wood board, a medium density fiber board, a plastic board, a siding board (including a metal-based and a ceramic-based).

【0054】これらの基材(建材)への塗料組成物の塗
布方法は、特に制限されず、ロールコーターやフローコ
ーター、ハケやローラー等を用いる塗付け方法及びスプ
レーや各種ガンを用いた吹きつけ方法を挙げることがで
きる。一例として圧縮空気を用いたスプレー塗装によれ
ば、例えば、まず適当な粘度に調製されてなる塗料組成
物のスプレー液若しくはスラリーを基材の一面に吹き付
ける。この吹き付けによって、塗料組成物は基材の表面
に塗膜を形成し基材と一体化する。この際、塗料組成物
に含まれるアクリル系樹脂成分が消石灰などの成分を強
固に結合させるとともに、塗料組成物を基材表面に抱合
させて、塗膜層と基材を一体化する。これにより層間剥
離が防止できる。次いで、基材に塗布された塗料組成物
を乾燥、硬化させる。かかる方法は、基材に塗料組成物
を塗布後、自然乾燥、通風乾燥または強制乾燥に供する
ことにより簡便に行うことができる。なお、本発明の塗
装物は必要に応じてさらに形成された塗膜層の表面を凹
凸模様付きローラー等で意匠を施したりヤスリや各種研
磨機で研磨ずりして仕上げることもできる。
The method of applying the coating composition to these base materials (building materials) is not particularly limited, and a coating method using a roll coater, a flow coater, a brush or a roller, and a spraying method using a spray or various guns. Methods can be mentioned. According to spray coating using compressed air as an example, for example, a spray liquid or slurry of a coating composition prepared to have an appropriate viscosity is first sprayed onto one surface of a substrate. By this spraying, the coating composition forms a coating film on the surface of the substrate and is integrated with the substrate. At this time, the acrylic resin component contained in the coating composition firmly binds components such as slaked lime, and the coating composition is conjugated to the surface of the base material to integrate the coating layer with the base material. Thereby, delamination can be prevented. Next, the coating composition applied to the substrate is dried and cured. Such a method can be easily performed by applying the coating composition to the substrate and then subjecting the coating composition to natural drying, ventilation drying, or forced drying. The coated product of the present invention can be finished by applying a design to the surface of the further formed coating layer with a roller having a concavo-convex pattern or polishing and polishing with a file or various types of polishing machines, if necessary.

【0055】本発明の塗料組成物から形成される塗膜の
厚さは、基材の塗布面が十分に隠蔽被覆される厚さであ
れば特に制限されない。本発明の塗料組成物は、塗膜隠
蔽力が前述するように1mm以下、好ましくは500μ
m以下、より好ましくは300μm以下、さらに好まし
くは200μm以下、またさらに好ましくは100μm
以下となるように調製できることを特徴とするものであ
る。よって、塗膜の厚さとして少なくとも1mm、好ま
しくは500μm、より好ましくは少なくとも300μ
m、さらに好ましくは少なくとも200μm、また更に
好ましくは少なくとも100μmの厚さを挙げることが
できるが、コスト、塗装作業性及び成膜性、並びに調湿
性等といった塗膜の物性や機能等に鑑みれば、通常0.
1〜5mm、好ましくは0.1〜3mm、より好ましく
は0.2〜2mm、さらに好ましくは0.3〜1.5m
m、またさらに好ましくは0.5〜1mmの範囲を例示
することができる。但し、調湿性機能の観点からは塗膜
の厚さは厚い方が好ましく、本発明は本発明の塗料組成
物を使用してさらに厚い塗膜を形成することを制限する
ものではない。
The thickness of the coating film formed from the coating composition of the present invention is not particularly limited as long as the coating surface of the substrate is sufficiently covered and covered. The coating composition of the present invention has a coating film hiding power of 1 mm or less as described above, preferably 500 μm.
m or less, more preferably 300 μm or less, still more preferably 200 μm or less, and still more preferably 100 μm or less.
It is characterized in that it can be prepared as follows. Therefore, the thickness of the coating film is at least 1 mm, preferably 500 μm, more preferably at least 300 μm.
m, more preferably at least 200 μm, and still more preferably at least 100 μm, but in view of the physical properties and functions of the coating film such as cost, coating workability and film formability, and humidity control, Usually 0.
1 to 5 mm, preferably 0.1 to 3 mm, more preferably 0.2 to 2 mm, still more preferably 0.3 to 1.5 m
m, and more preferably in the range of 0.5 to 1 mm. However, the thickness of the coating film is preferably thicker from the viewpoint of the humidity control function, and the present invention does not limit the formation of a thicker coating film using the coating composition of the present invention.

【0056】本発明の塗料組成物から形成される塗膜を
有する塗装物は、調湿性(吸湿性及び放湿性)に優れ、
高い結露防止効果を発揮するとともに、漆喰特有の質感
(色、つや、きめ細かさ等の外観やテクスチャー)を呈
する。またかくして製造される塗装物は、直射日光、斜
光、照明、陰影等の建材が配置される場所の種々の光に
対しても吹きむら、色むら及び艶むら等の不都合を生じ
ず、常に一定の色、艶及びきめを有した外観を呈してい
る。塗装物のかかる性質は、内・外壁材、天井材等の各
種建材に有用である。
A coated article having a coating film formed from the coating composition of the present invention has excellent humidity control properties (moisture absorption and moisture release properties),
While exhibiting a high dew condensation preventing effect, it exhibits a plaster-specific texture (appearance and texture such as color, gloss, and fineness). In addition, the painted product thus produced does not cause inconvenience such as unevenness in color, unevenness in gloss and unevenness in blown light, unevenness in color, and unevenness in various places where building materials are arranged, such as direct sunlight, oblique light, lighting, and shading. With a color, luster and texture. Such properties of the painted object are useful for various building materials such as inner / outer wall materials and ceiling materials.

【0057】一般にボード(パネル)やクロスなどの建
材の場合、施工後の建材間の継目や接合部の処理が問題
となりやすい。例えば繊維素材を含まない本発明の塗料
組成物を塗布して調製された塗装物(建材)によれば、
壁などに施工後、建材の継目や接合部の塗膜表面を研磨
ずりすることにより周囲の塗膜層と殆ど区別できないほ
どに連続的かつ均一に仕上げることができる。また繊維
素材を含まない本発明の塗料組成物を塗布して調製され
た塗装物(建材)によれば、壁などに施工された後の修
繕が簡便にできるという利点もある。すなわち、施工後
に建材に傷や汚れが生じた場合、本発明の塗料組成物を
使用してその損傷部だけを部分的に修繕することが可能
である。かかる修繕は、具体的にはまず損傷部を削り、
該部分に周辺塗膜層と同じ組成であって含水率を低減し
て粘度を高くした本発明の塗料組成物を充填し、養生硬
化後、必要に応じて表面を研磨ずりすることによって行
うことができる。研磨ずりすることによって損傷部が他
周辺領域と区別できないほどに修復修繕することが可能
となる。
In general, in the case of building materials such as boards (panels) and cloths, the processing of joints and joints between building materials after construction tends to be a problem. For example, according to a painted product (building material) prepared by applying the coating composition of the present invention containing no fiber material,
After construction on a wall or the like, the coating surface of the joint or the joint of the building material can be polished and polished to achieve a continuous and uniform finish almost indistinguishable from the surrounding coating layer. Further, according to a painted product (building material) prepared by applying the coating composition of the present invention containing no fiber material, there is also an advantage that repair after being applied to a wall or the like can be easily performed. That is, when the building material is damaged or stained after the construction, it is possible to partially repair only the damaged portion using the coating composition of the present invention. In such repairs, first of all, the damaged part is first cut,
This portion is filled with the coating composition of the present invention having the same composition as that of the peripheral coating layer but having a reduced water content to increase the viscosity, and after curing and curing, the surface is polished and ground as necessary. Can be. By polishing, it becomes possible to repair and repair the damaged portion so that the damaged portion cannot be distinguished from other peripheral regions.

【0058】また、これは建材の施工(内外装の施工)
においても有用である。すなわち、本発明の塗装物(建
材)とくに内外装パネルを壁下地材に釘やビス打ち施工
する場合、釘(ビス)打ちによって形成された建材表面
の釘頭凹部に、上記のように比較的粘度の高い塗料組成
物(パテ)を充填し、また必要であればその上からさら
に塗料組成物(スプレー液、スラリー)を塗布して、養
生硬化し、更に必要に応じて該塗膜表面を研磨ずりする
ことによって、釘打ち部がほとんどわからぬように施工
することが可能となる(図1参照)。これによって、接
着剤による建材の貼着が回避できる。
This is the construction material construction (interior and exterior construction)
It is also useful in That is, when the painted object (building material) of the present invention, in particular, the interior and exterior panels are nailed or screwed on the wall base material, the nail head recesses on the surface of the building material formed by nailing (screw) as described above are relatively small. A high-viscosity coating composition (putty) is filled, and if necessary, a coating composition (spray liquid, slurry) is further applied thereon to cure and cure. By grinding and polishing, the nailing portion can be constructed so that the nailing portion is hardly recognized (see FIG. 1). Thereby, the sticking of the building material with the adhesive can be avoided.

【0059】(3)建築内外装の施工方法 更に本発明は、上記塗料組成物または塗装物(建材)を
用いた建築物内装・外装の施工方法に関する。本発明の
施工方法としては、下記の実施態様を挙げることができ
る。 A.建築下地材の表面に、上記本発明の塗料組成物を塗
布し、乾燥後、必要に応じて塗膜面を研磨ずりすること
を特徴とする塗装方法。 B. (i)建築下地材に本発明の建材を複数連設する工
程、(ii)各建材の接合部に、本発明の塗料組成物を充填
若しくは塗布して乾燥する工程、及び(iv)必要に応じ
て、塗膜面を研磨ずりする工程を含む、建築物内外装の
施工方法。 C.(i)建築下地材に本発明の建材を複数連設する工
程、(ii)必要に応じて、各建材の接合部に本発明の塗料
組成物を充填若しくは塗布する工程、(iii)該接合部を
補強部材で覆う工程、(iv)該補強部材上に本発明の塗料
組成物を塗布して乾燥する工程、及び(v)必要に応じ
て、塗膜面を研磨ずりする工程を含む、建築物内外装の
施工方法。
(3) Construction Method for Interior and Exterior of Building Further, the present invention relates to a method for constructing interior and exterior of a building using the coating composition or the painted product (building material). Examples of the construction method of the present invention include the following embodiments. A. A coating method, which comprises applying the coating composition of the present invention to the surface of a building base material, drying the coating composition, and optionally polishing the coating film surface, if necessary. B. (i) a step of connecting a plurality of the building materials of the present invention to the building base material, (ii) a step of filling or applying the coating composition of the present invention to the joint of each building material and drying, and (iv) A method for constructing interior and exterior of buildings, including a step of polishing and polishing the coating film surface as necessary. C. (i) a step of arranging a plurality of building materials of the present invention in a building base material, (ii) a step of filling or applying the coating composition of the present invention to a joint of each building material, if necessary, (iii) the joining. Covering the part with a reinforcing member, (iv) a step of applying the coating composition of the present invention on the reinforcing member and drying, and (v) if necessary, a step of polishing and polishing the coating film surface, Construction method of building interior and exterior.

【0060】本発明の建築内外装の施工方法には、建
築物の内・外壁、屋根や天井の下地材(内外壁下地材)に
直接、上記本発明の塗料組成物を塗布積層する方法、並
びに内外壁下地材に本発明の建材(クロス、パネル、
ボード)を貼着または配設する方法が含まれる。
The construction method of the interior and exterior of a building according to the present invention includes a method of applying and laminating the coating composition of the present invention directly on a base material (a base material of an inner / outer wall) of an inner / outer wall, a roof or a ceiling of a building. And the building materials of the present invention (cloths, panels,
Board) is attached or arranged.

【0061】の施工方法は、具体的には、建築物の内
外壁、屋根や天井の下地材(素地材)の表面に、直接ま
たはシーラー若しくはプライマー処理した後、前記本発
明の塗料組成物、好適には常温(25±5℃)での粘度
が300〜8000センチポイズ、好ましくは500〜
5000センチポイズ、より好ましくは1000〜45
00センチポイズの塗料組成物を塗布して、固化するま
で常温乾燥若しくは通風乾燥し、次いで必要に応じて内
外壁下地材上に積層された塗膜層の表面を研磨ずりする
ことによって、行うことができる。
Specifically, the coating method according to the present invention is carried out by directly or after applying a sealer or a primer treatment to the surface of a base material (base material) for the inner and outer walls of a building, a roof or a ceiling. The viscosity at room temperature (25 ± 5 ° C.) is suitably 300 to 8000 centipoise, and preferably 500 to
5000 centipoise, more preferably 1000 to 45
By applying a coating composition of 00 centipoise, drying at room temperature or ventilation until solidified, and then, if necessary, polishing and polishing the surface of the coating layer laminated on the inner and outer wall base material. it can.

【0062】本発明の塗料組成物が塗布できる建築物の
下地材(素地材)としては、その素材を特に制限され
ず、例えばコンクリート、セメントモルタル、石膏プラ
スター、ドロマイトプラスター、石綿スレート、石膏ボ
ード、漆喰壁、パルプセメント板、石綿セメント珪酸カ
ルシウム板、木毛・木片セメント板、GRCガラス繊維
強化コンクリートパネル及び石綿セメント中空押出成形
板などのセメント系及び石膏系塗素地;ベニア板、積層
材、合板、木質繊維板及びパーティクルボード等の木質
系素地;塩化ビニル樹脂や酢酸ビニル等のビニル系樹脂
などを素材とするプラスチック系素地;その他、各種金
属系素地を挙げることができる。また、本発明が対象と
する建築下地材には、クロスが貼着されたり各種塗料が
塗布されてなるものであってもよい。すなわち、本発明
の塗料組成物によれば、当該クロスや塗面に塗布施工す
ることによって建築物の内外壁、屋根や天井をリフォー
ムすることが可能である。
The base material (base material) of a building to which the coating composition of the present invention can be applied is not particularly limited, and examples thereof include concrete, cement mortar, gypsum plaster, dolomite plaster, asbestos slate, gypsum board, and the like. Cement and gypsum coatings such as plaster walls, pulp cement boards, asbestos cement calcium silicate boards, wood wool / wood chip cement boards, GRC glass fiber reinforced concrete panels and asbestos cement hollow extruded boards; veneer boards, laminates, plywood Wood base such as wood fiber board and particle board; plastic base made of vinyl resin such as vinyl chloride resin and vinyl acetate; and other various metal bases. Further, the building base material targeted by the present invention may be one in which a cloth is stuck or various paints are applied. That is, according to the coating composition of the present invention, it is possible to renovate the inner and outer walls, the roof, and the ceiling of a building by applying and applying the cloth and the painted surface.

【0063】また、の施工方法は、建築物の内外壁や
天井の下地材(素地材)もしくは下地材(素地材)に設
けられた内外壁枠や下桟等に前記本発明の塗装物(クロ
ス、パネル、ボードなどの建材)を、各側端面同士を当
接して配置する工程、各建材の接合部の表面領域に本発
明の塗料組成物、好適には常温での粘度が300〜80
00センチポイズ、好ましくは500〜5000センチ
ポイズ、より好ましくは1000〜4500センチポイ
ズの塗料組成物を塗布して固化するまで乾燥し、次いで
必要に応じて当該塗膜層領域の表面を研磨ずりすること
によって行うことができる。
The construction method of the present invention is preferably applied to a base material (base material) for an inner or outer wall or ceiling of a building or an inner / outer wall frame or a lower crossbar provided on the base material (base material). (A building material such as a cloth, a panel, a board, etc.) is disposed in such a manner that the side end faces are in contact with each other, and the coating composition of the present invention, preferably a viscosity at room temperature of 300 to 80 is applied to the surface area of the joint of each building material.
The coating is performed by applying a coating composition of 00 centipoise, preferably 500 to 5,000 centipoise, more preferably 1,000 to 4,500 centipoise, drying until solidified, and then, if necessary, polishing the surface of the coating layer region. be able to.

【0064】建材として内外装パネルを用いる場合、各
パネルの連設態様は特に制限されないが、一例として図
2に示す連設方法を挙げることができる。具体的には、
垂直な側面を有するパネルの該側面同士を当接して連設
することにより平坦なパネル面を形成する突付け張り法
(図2(a))、少なくとも表面側に面取り斜面を有す
る内外装パネルを各々その側面同士を当接して連設し
て、該連設部においてV字状の溝を有するパネル面を形
成する突付けV形みぞ張り法(図2(b))、辺部がお
互いに相じゃくり、又は相じゃくりざね又は本ざね等の
仕口を形成してなる内外装パネルを各々その側面同士を
当接して連設して、該連設部において角溝を有するパネ
ル面を形成する突付け張りもしくは目透かし張り法(図
2(c))を例示できる。
When the interior and exterior panels are used as a building material, there is no particular limitation on the manner in which the panels are connected, but an example is the connection method shown in FIG. In particular,
A bumping method (FIG. 2 (a)) for forming a flat panel surface by abutting the side surfaces of a panel having vertical side surfaces to form a continuous panel surface (FIG. 2 (a)). A butt V-groove method (FIG. 2B) in which the side surfaces are abutted and connected to form a panel surface having a V-shaped groove in the connected portion (FIG. 2B), The interior and exterior panels each forming a connection such as phase-locking or phase-locking or main-linking are connected to each other with their side surfaces in contact with each other, and a panel surface having a square groove in the connecting portion is formed. An example of a butt or eye-opening method (FIG. 2 (c)) is shown.

【0065】図2(b)及び(c)のようにパネルの接
合部分に溝が形成される場合は、上記塗料組成物の塗布
に先立って接合部の該溝部に塗布した塗料組成物と同じ
組成の粘度の高い(低含水率)塗料組成物、好適には常
温で8000〜20000センチポイズ、好ましくは8
000〜10000センチポイズの粘度を有する塗料組
成物をシール材として充填し、次いでその上から常温で
300〜8000センチポイズの粘度を有する塗料組成
物を塗布することが好ましい。また、塗料組成物の充填
若しくは塗布に先立って、パネル間の接合部を補強部材
で被覆することもできる(図3、図4)。
When a groove is formed in the joint portion of the panel as shown in FIGS. 2 (b) and 2 (c), the same as the coating composition applied to the groove portion of the joining portion prior to the application of the coating composition. High viscosity (low water content) coating composition, suitably 8000-20,000 centipoise at room temperature, preferably 8
It is preferable to fill a coating composition having a viscosity of 000 to 10,000 centipoise as a sealing material, and then apply a coating composition having a viscosity of 300 to 8000 centipoise at room temperature. Prior to filling or application of the coating composition, the joint between the panels can be covered with a reinforcing member (FIGS. 3 and 4).

【0066】補強部材としては、織布、不織布、セラミ
ックペーパー、合成紙、メッシュ、寒冷紗などのテープ
状部材を例示することができ、これらはそのまま、ある
いはこれに目止め塗料、樹脂などを塗布して、あるいは
フィルムをラミネートして使用することができる(図
3)。また、補強部材として、断面略T字型若しくは略
エ字型のプラスチック製もしくは金属製のジョイナーを
用いることもできる(図4)。
Examples of the reinforcing member include woven fabric, non-woven fabric, ceramic paper, synthetic paper, mesh, and tape-shaped members such as cold gauze. These may be used as they are or by applying a filling paint, a resin or the like thereto. Or laminated film (FIG. 3). Further, a plastic or metal joiner having a substantially T-shaped or substantially E-shaped cross section can be used as the reinforcing member (FIG. 4).

【0067】本発明の施工方法によれば、特に仕上げ工
程における塗装または研磨ずりによって、クロスやパネ
ル等の建材の接合部において、その継目が目立つことな
く、建材表面を実質上均一乃至連続した綺麗な状態にす
ることができ、美観の良好な内外装を施すことが可能と
なる。
According to the construction method of the present invention, especially at the joint of building materials such as cloths and panels, the joints are not conspicuous, and the surface of the building materials is substantially uniform or continuous due to coating or polishing shearing in the finishing step. It is possible to provide interior and exterior with good appearance.

【0068】(4)建築内外装の修復方法 また本発明は、上記建材または塗料組成物を用いた建築
物内装・外装の施工面の修復方法に関する。かかる修復
・修繕方法の実施態様としては下記のものを挙げること
ができる。
(4) Method of Restoring Building Interior / Exterior The present invention also relates to a method of restoring a construction surface of a building interior / exterior using the above-mentioned building material or coating composition. Embodiments of such a repair / repair method include the following.

【0069】消石灰、アクリル系樹脂、無機顔料及び水
を含有する本発明の塗料組成物を塗布して形成される塗
膜層を表面に有する壁面の損傷部を修復する方法であっ
て、(i) 必要であれば該損傷部の塗膜層を削りとる工
程、(ii) 壁面損傷部に本発明の塗料組成物を充填若し
くは塗布して乾燥する工程、及び(iii)必要に応じて、
当該塗膜面を研磨ずりする工程を含む、建築物内外装壁
面の修復方法。
A method for repairing a damaged portion of a wall surface having a coating layer formed by applying a coating composition of the present invention containing slaked lime, an acrylic resin, an inorganic pigment and water, comprising: ) If necessary, a step of shaving off the coating layer of the damaged portion, (ii) a step of filling or applying the coating composition of the present invention to the damaged wall portion and drying, and (iii) if necessary,
A method for repairing a building interior / exterior wall surface, including a step of polishing and polishing the coating film surface.

【0070】[0070]

【発明の効果】本発明の塗料組成物は、消石灰を成分と
して含有することによって、形成される塗膜が漆喰特有
の落ち着きのある質感を備えることができる。すなわ
ち、本発明の塗料組成物によれば、建築物の天井、屋根
や内壁、及び外壁に、従来施工に時間がかかり又コスト
が高い漆喰壁と同様な質感を備えた塗面(化粧面)を施
工形成することができる。
According to the coating composition of the present invention, by containing slaked lime as a component, the formed coating film can have a calm texture peculiar to stucco. That is, according to the coating composition of the present invention, a painted surface (decorative surface) having a texture similar to that of a plaster wall, which is time-consuming and costly to construct conventionally, is applied to the ceiling, roof, inner wall, and outer wall of a building. Can be formed.

【0071】またの塗料組成物は、消石灰の配合割合に
応じて調湿性及び結露防止性といった機能を発揮するこ
とができる。このため、建築物、特にマンション等の湿
気が問題となる壁、天井及び押入内壁等の内装用塗料若
しくは建材用塗料として極めて有用である。また、特に
酸化チタンを顔料として含む本発明の塗料組成物は、調
湿性を損なうことなく、低塗布量で優れた隠蔽力を有
し、しかも付着性及び成膜性(歩留まり、耐ひび割れ
性、可撓性、外観性)に優れているため、低コストで調
湿性等の有用な機能を有する薄塗膜を形成することがで
きる。また、本発明の塗料組成物は、従来消石灰を主成
分とする漆喰には必須であったスサなどの繊維素材を配
合しなくても、付着性及び成膜性(歩留まり、耐ひび割
れ性、可撓性、靱性)に優れており、これによってさら
に塗装作業の簡便化を図ることができるものである。
Further, the coating composition can exhibit functions such as humidity control and dew condensation prevention in accordance with the proportion of slaked lime. For this reason, it is extremely useful as a paint for interiors or a building material such as walls, ceilings, and pushed-in inner walls of buildings, especially condominiums, etc. where moisture is a problem. In addition, the coating composition of the present invention, particularly containing titanium oxide as a pigment, has excellent hiding power at a low coating amount without impairing humidity control properties, and has adhesion and film forming properties (yield, crack resistance, (Flexibility, appearance), it is possible to form a thin coating film having useful functions such as humidity control at low cost. In addition, the coating composition of the present invention can provide adhesiveness and film forming properties (yield, crack resistance, (Flexibility, toughness), thereby further simplifying the painting operation.

【0072】本発明の塗料組成物は、消石灰を成分とし
て含有する一液型塗料であって、しかもJIS 5663-1995
に規定される合成樹脂エマルションペイントの少なくと
も2種(屋内用ペイント)、または1種(屋外用ペイン
ト)の品質を備えることを特徴とするものである。従っ
て、事前に工場などで1液に調合したものを容器に充填
した状態で提供できるため、現場での調合の手間を省く
ことができ、また塗装後残ったものは再び容器に戻して
貯蔵できる利点を有するものである。また本発明の塗料
組成物は主に消石灰という自然素材から調製されるもの
であるため、「化学物質過敏症」や「シックハウス症候
群」等が問題となっている今日において、当該塗料並び
に該塗料を用いて調製される建材(クロス、ボード、パ
ネル等)は人に優しい屋内又は屋外塗料(内・外装用塗
料)並びに内・外装用建材(壁材、屋根材、天井材)と
して有用である。
The coating composition of the present invention is a one-pack type coating containing slaked lime as a component, and it is JIS 5663-1995.
Characterized in that it has at least two types (indoor paint) or one type (outdoor paint) of the synthetic resin emulsion paint defined in (1). Therefore, since it can be provided in a state filled in a container with one liquid prepared in advance in a factory or the like, the labor of preparation at the site can be omitted, and the remaining material after painting can be returned to the container and stored again. It has advantages. In addition, since the coating composition of the present invention is prepared mainly from a natural material called slaked lime, today, when `` chemical sensitivity '' or `` sick house syndrome '' is a problem, the coating composition and the coating composition are used. The building materials (cloths, boards, panels, etc.) prepared by using them are useful as human-friendly indoor or outdoor paints (paints for interior / exterior) and interior / exterior construction materials (wall materials, roof materials, ceiling materials).

【0073】本発明の塗料組成物は、低コスト性、施工
の簡便性、美観性、機能性等の点からきわめて商品価値
の高い塗料組成物である。また本発明の塗料組成物は、
クロス間またはパネル間の継目の隠蔽処理にも好適に使
用でき、また薄塗膜化が可能であることから内外装壁面
や天井面の修復・修繕にも有用であり、この点からも新
規施工並びにリフォーム施工にも幅広く使用できる商品
価値の高い塗料組成物である。
The coating composition of the present invention is a coating composition having a very high commercial value in terms of low cost, easiness of construction, aesthetics, and functionality. Further, the coating composition of the present invention,
It can be suitably used for concealing seams between cloths or panels, and because it can be made into a thin film, it is also useful for repairing and repairing interior and exterior walls and ceiling surfaces. Moreover, it is a paint composition with high commercial value that can be widely used for renovation work.

【0074】[0074]

【実施例】以下、本発明の内容を以下の実施例を用いて
具体的に説明する。ただし、これらの実施例は本発明の
一態様にすぎず、本発明はこれらの例に何ら限定される
ものではない。実施例1 消石灰 18.0 (29.0%) アクリル樹脂エマルジョン(旭化成) 47.0 (32.0%) 酸化チタン(EP-498、大日精化) 6.0 ( 9.7%) 体質顔料 17.0 (27.4%) 増粘剤(SP-600、ダイセル化学) 0.03 消泡剤(KM-70、信越化学) 0.67 分散剤 0.3 水 残 部 全 量 100.0 重量部 上記成分を塗料調合用ミキサーに入れて撹拌することに
より固形分及び樹脂成分を水に安定に分散させて、本発
明の一液型水性塗料組成物(固形分含有率約62%)を調
製した。尚、上記アクリル系樹脂エマルジョン(ポリア
クリル酸エステル)は固形分を42重量%の割合で含む
ものを使用した。上記処方において、かっこ内の数値は
塗料組成物の固形分100重量%あたりの配合割合(固
形換算)を示すものである(以下の実施例においても同
じ)。
DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be specifically described below with reference to the following embodiments. However, these examples are only one embodiment of the present invention, and the present invention is not limited to these examples. Example 1 Slaked lime 18.0 (29.0%) Acrylic resin emulsion (Asahi Kasei) 47.0 (32.0%) Titanium oxide (EP-498, Dainichi Seika) 6.0 (9.7%) Extender pigment 17.0 (27.4% ) Thickener (SP-600, Daicel Chemical) 0.03 Defoamer (KM-70, Shin-Etsu Chemical) 0.67 Dispersant 0.3 Water Residual amount 100.0 parts by weight The solid content and the resin component were stably dispersed in water by stirring in a mixer to prepare a one-pack type aqueous coating composition of the present invention (solid content: about 62%). The acrylic resin emulsion (polyacrylic ester) used had a solid content of 42% by weight. In the above formulation, the numerical values in parentheses indicate the mixing ratio (solid basis) per 100% by weight of the solid content of the coating composition (the same applies to the following Examples).

【0075】 実施例2 消石灰 10.0 (16 %) アクリル樹脂エマルジョン(旭化成) 23.0 (16 %) 酸化チタン(EP-498、大日精化) 10.0 (16 %) 体質顔料 31.0 (50 %) 消泡剤(KM-70、信越化学) 0.67 分散剤 0.3 レベリング剤 0.03 水 残 部 全 量 100.0重量部 上記成分を塗料調合用ミキサーに入れて撹拌することに
より固形分及び樹脂成分を水に安定に分散させて、本発
明の一液型水性塗料組成物(固形分含有率約62%)を調
製した。尚、上記アクリル系樹脂エマルジョン(ポリア
クリル酸エステル)は固形分を43.5重量%の割合で
含むものを使用した。
Example 2 Slaked lime 10.0 (16%) Acrylic resin emulsion (Asahi Kasei) 23.0 (16%) Titanium oxide (EP-498, Dainichi Seika) 10.0 (16%) extender pigment 31.0 (50%) Antifoaming agent (KM-70, Shin-Etsu Chemical) 0.67 Dispersant 0.3 Leveling agent 0.03 Water Residual amount 100.0 parts by weight Put the above ingredients into a paint mixing mixer and stir As a result, the solid content and the resin component were stably dispersed in water to prepare a one-part aqueous coating composition of the present invention (solid content: about 62%). The acrylic resin emulsion (polyacrylic ester) used had a solid content of 43.5% by weight.

【0076】 実施例3 消石灰 5.0 ( 8.6%) アクリル系樹脂エマルジョン(旭化成) 47.0 (34.5%) 酸化チタン(EP-498、大日精化) 7.0 (12.1%) 体質顔料 25.0 (43.0%) 増粘剤(SP-600、ダイセル化学) 0.03 消泡剤(KM-70、信越化学) 0.67 分散剤 0.3 水 残 部 全 量 100.0重量部 上記成分を塗料調合用ミキサーに入れて撹拌することに
より固形分及び樹脂成分を水に安定に分散させて、本発
明の一液型水性塗料組成物(固形分含有率約58%)を調
製した。尚、上記アクリル系樹脂エマルジョン(ポリア
クリル酸エステル)は固形分を42.6重量%の割合で
含むものを使用した。
Example 3 Slaked lime 5.0 (8.6%) Acrylic resin emulsion (Asahi Kasei) 47.0 (34.5%) Titanium oxide (EP-498, Dainichi Seika) 7.0 (12.1%) extender pigment 25. 0 (43.0%) Thickener (SP-600, Daicel Chemical) 0.03 Defoamer (KM-70, Shin-Etsu Chemical) 0.67 Dispersant 0.3 Water Residual amount 100.0 parts by weight Was put into a paint mixing mixer and stirred to stably disperse the solid content and the resin component in water to prepare a one-pack type aqueous coating composition of the present invention (solid content: about 58%). The acrylic resin emulsion (polyacrylic ester) used had a solid content of 42.6% by weight.

【0077】 実施例4 消石灰 16.0 (27.6%) アクリル系樹脂エマルジョン(旭化成) 15.0 (12.1%) 酸化チタン(EP-498、大日精化) 2.0 ( 3.4%) 体質顔料 32.0 (55.0%) 増粘剤(SP-600、ダイセル化学) 0.03 消泡剤(KM-70、信越化学) 0.67 分散剤 0.3 水 残 部 全 量 100.0重量部 上記成分を塗料調合用ミキサーに入れて撹拌することに
より固形分及び樹脂成分を水に安定に分散させて、本発
明の一液型水性塗料組成物(固形分含有率約58%)を調
製した。尚、上記アクリル系樹脂エマルジョン(シリコ
ン変性アクリル樹脂)は固形分を46.7重量%の割合
で含むものを使用した。
Example 4 Slaked lime 16.0 (27.6%) Acrylic resin emulsion (Asahi Kasei) 15.0 (12.1%) Titanium oxide (EP-498, Dainichi Seika) 2.0 (3.4%) extender pigment 32. 0 (55.0%) Thickener (SP-600, Daicel Chemical) 0.03 Antifoamer (KM-70, Shin-Etsu Chemical) 0.67 Dispersant 0.3 Water Residual Total 100.0 parts by weight Was put into a paint mixing mixer and stirred to stably disperse the solid content and the resin component in water to prepare a one-pack type aqueous coating composition of the present invention (solid content: about 58%). The acrylic resin emulsion (silicon-modified acrylic resin) used had a solid content of 46.7% by weight.

【0078】実施例5 実施例1で調製した塗料組成物をエアレススプレーに入
れて、石膏ボード(タテ20cm×ヨコ20cm×厚さ
1cm、吉野石膏製)の一面に満遍なく吹き付け、通風
乾燥によって塗膜(合計塗布量(塗料総量)500g/m2
乾燥塗膜0.35mm)を形成した。石膏パネルは、直射日
光、斜光、照明等の様々の光に対して、いずれも吹きム
ラ、色ムラ及び艶ムラが見られず、均一な外観を有して
いた。該パネルは、吸湿性及び放湿性に優れており湿度
80%の環境下においても結露の発生を有意に防止する
ことができた。さらに、該パネルの塗膜層の表面に直火
を近づけても発火せず、また煙も発生せず、耐燃性に優
れていることが確認された。
Example 5 The coating composition prepared in Example 1 was put into an airless spray, sprayed evenly on one side of a gypsum board (vertical 20 cm × width 20 cm × thickness 1 cm, manufactured by Yoshino Gypsum), and dried by ventilation drying. (Total application amount (total paint amount) 500g / m 2 ,
A dried coating film (0.35 mm) was formed. The plaster panel had a uniform appearance without any blowing unevenness, color unevenness, and gloss unevenness against various lights such as direct sunlight, oblique light, and illumination. The panel was excellent in hygroscopicity and moisture release, and was able to significantly prevent the occurrence of dew condensation even in an environment with a humidity of 80%. Further, it was confirmed that even when an open flame was brought close to the surface of the coating layer of the panel, it did not ignite, did not generate smoke, and had excellent flame resistance.

【0079】次いで得られた石膏パネルを、室内の内装
壁材として、壁下地材に塗膜層を表にして釘で打付施工
した。釘頭が被覆層の内部に陥没するまで打ち付け、そ
れによって形成された釘頭凹部に、消石灰、アクリル系
樹脂エマルジョン(ポリアクリル酸エステル)及び増粘
材からなる組成物に水を入れてやや固めに混練りしたパ
テ状塗材(粘度8000センチポイズ)を挿入・充填
し、固化後、釘打ち部及びその周辺部に再度実施例1の
塗料組成物を塗布して仕上げた。壁材として施工された
内装材は、釘打部(補修部)表面が周辺部と区別できな
いほど一体化してきれいに仕上がった。また、該内装パ
ネルに塗布形成された塗膜は、室内の壁に施工後も、ひ
び割れすることなく十分な靱性並びに可撓性を備えてい
た。
Next, the obtained gypsum panel was nailed with the coating layer facing up on a wall base material as an interior wall material in a room. The nail head is nailed until it sinks into the inside of the coating layer, and the nail head recess formed thereby is slightly hardened by pouring water into a composition comprising slaked lime, an acrylic resin emulsion (polyacrylate) and a thickener. And a kneaded putty-like coating material (viscosity: 8,000 centipoise) was inserted and filled, and after solidification, the coating composition of Example 1 was applied again to the nailed portion and its peripheral portion to finish. The interior material constructed as a wall material was finished in such a way that the surface of the nailed part (repair part) could not be distinguished from the surrounding part and was beautifully integrated. Moreover, the coating film formed on the interior panel had sufficient toughness and flexibility without cracking even after being applied to the indoor wall.

【0080】実験例1 実施例1で調製した塗料組成物を用いて付着強度並びに
乾燥塗膜の強度を測定した。 (1)付着強度 実施例1で調製した塗料組成物をエアレススプレーに入
れて、歩道板(プライマー処理ありとプライマー処理な
しの2種類)及びベニア板(プライマー処理なし)(30
0×150×5mm)の一面に満遍なく吹き付け、通風乾燥に
よって固化させて塗膜厚0.5mmのパネル(試験板)
を作成した。かかるパネルをそれぞれ3検体ずつ用いて
JIS K5400-1990 8.8に規定される試験(引張強さ)に従
って試験を行い、塗膜の付着性を評価した。なお、引張
り試験機としてADHESION TESTERELCOMETERを使用した。
具体的には、接着面破断または内部面破断を生じた時点
の荷重(kgf)を測定して、引張強さを算出した(JIS K
5400-1990 8.8)。結果として、各試験板において行っ
た3検体の平均を表1に示す。
Experimental Example 1 Using the coating composition prepared in Example 1, the adhesive strength and the strength of the dried coating film were measured. (1) Adhesive strength The paint composition prepared in Example 1 was put into an airless spray, and a sidewalk board (with and without primer treatment) and a veneer board (without primer treatment) (30)
(0 x 150 x 5 mm) Sprayed evenly on one side, solidified by ventilation drying, and 0.5mm thick panel (test plate)
It was created. Using three such panels each
A test was performed in accordance with the test (tensile strength) specified in JIS K5400-1990 8.8, and the adhesion of the coating film was evaluated. In addition, ADHESION TESTERELCOMETER was used as a tensile tester.
Specifically, the tensile strength was calculated by measuring the load (kgf) at the time when the adhesive surface fracture or the internal surface fracture occurred.
5400-1990 8.8). As a result, Table 1 shows the average of three samples performed on each test plate.

【0081】[0081]

【表1】 [Table 1]

【0082】(2) 乾燥塗膜強度 上記で調製した試験板についてJIS K5400-1990 8.4に規
定される鉛筆引っかき値測定法(手かき法)に従って試
験を行い、塗膜の強度を評価した。具体的には、上記で
調製した試験板(歩道板)に形成された塗膜表面に鉛筆
で引っかいて、5回の試験で塗膜のすり傷が2回以上に
なる鉛筆の芯濃度(H)から、本発明の塗料組成物から
形成される塗膜の強度をHBとして評価した。
(2) Dry Film Strength The test plate prepared above was subjected to a test in accordance with the pencil scratch value measurement method (hand scratch method) specified in JIS K5400-1990 8.4 to evaluate the film strength. Specifically, the surface of the coating film formed on the test board (sidewalk board) prepared above was scratched with a pencil, and the core density (H) of the pencil was such that the coating film was scratched twice or more in five tests. ), The strength of the coating film formed from the coating composition of the present invention was evaluated as HB.

【0083】実験例2 実施例1で調製した塗料組成物をエアレススプレーに入
れて、石膏ボード(タテ40cm×ヨコ25cm×厚さ
5mm)の一面に満遍なく吹き付け、通風乾燥によって
固化させて、塗膜厚0.6mmのパネルを作成した。
Experimental Example 2 The coating composition prepared in Example 1 was put into an airless spray, sprayed evenly on one side of a gypsum board (length 40 cm × width 25 cm × thickness 5 mm), and solidified by ventilation drying to form a coating film. A panel having a thickness of 0.6 mm was prepared.

【0084】かかるパネルを6検体用いて調湿試験を行
った。なお、塗膜層の調湿性を正当に評価するためにパ
ネルの側面及び裏面(塗料非塗布面)には防湿性シール
を施して水蒸気が透過しないようにした。具体的には、
本発明の建材パネルを相対湿度65%温度20℃の環境
下に放置して、水分吸収量がほぼ平衡に達する48時間
後に秤量し、次いで被検体を相対湿度98%温度20℃
の環境下に移して、再び水分吸収率がほぼ平衡に達する
48時間後に秤量して単位表面積(1m2)あたりのパ
ネルの水分吸収量を求めた。次に吸湿試験後の検体を同
様に相対湿度65%温度20℃の環境下に移して、24
時間放置した後に秤量して単位表面積(1m2)あたり
のパネルの水分吸収量を求めた。そして、これらの実験
における水分吸収量の差をそれぞれ吸湿量及び放湿量と
して評価した。
A humidity control test was performed using six samples of such panels. In order to properly evaluate the humidity control of the coating film layer, a moisture-proof seal was applied to the side and back surfaces of the panel (the surface on which no paint was applied) to prevent the passage of water vapor. In particular,
The building material panel of the present invention was left in an environment at a relative humidity of 65% and a temperature of 20 ° C., weighed 48 hours after the amount of water absorbed almost reached equilibrium, and then the subject was weighed at a relative humidity of 98% and a temperature of 20 ° C.
Was weighed 48 hours after the water absorption rate reached substantially equilibrium again, to determine the water absorption of the panel per unit surface area (1 m 2 ). Next, the sample after the moisture absorption test was similarly transferred to an environment of a relative humidity of 65% and a temperature of 20 ° C.
After standing for a period of time, the weight was measured to determine the amount of water absorbed by the panel per unit surface area (1 m 2 ). Then, the difference between the water absorption amounts in these experiments was evaluated as the moisture absorption amount and the moisture release amount, respectively.

【0085】結果を比較品として用いた塩化ビニル製の
壁紙(タテ40cm×ヨコ25cm)の調湿効果と併せ
て、表2に示す。
The results are shown in Table 2 together with the humidity control effect of a vinyl chloride wallpaper (length 40 cm × width 25 cm) used as a comparative product.

【0086】[0086]

【表2】 [Table 2]

【0087】なお、表中の表示は下記のことを意味す
る。 20℃65%重量(g/m2)*1:20℃65%RH 48時間放置後の1m2
あたりの重量 20℃65%重量(g/m2)*2:20℃65%RH 24時間放置後の1m2
あたりの重量 20℃98%重量(g/m2) :20℃98%RH 48時間放置後の1m2
たりの重量 吸湿性 (g/m2) :20℃98%重量 − 20℃65%重量*1 放湿性 (g/m2) :20℃98%重量 − 20℃65%重量*2 このことから、本発明の塗料組成物を塗布して形成され
る塗膜には優れた調湿機能(吸湿性、放出性)があるこ
とが確認された。
The indications in the table mean the following. 20 ° C 65% weight (g / m 2 ) * 1 : 1m 2 after standing at 20 ° C 65% RH for 48 hours
Weight per unit 20 ° C 65% weight (g / m 2 ) * 2 : 1m 2 after standing at 20 ° C 65% RH for 24 hours
Weight 20 ° C. 98% by weight per (g / m 2): 20 ℃ 98% RH 48 hours 1 m 2 per weight hygroscopic after standing (g / m 2): 20 ℃ 98% by weight - 20 ° C. 65% by weight * 1 Moisture release (g / m 2 ): 98% by weight at 20 ° C-65% by weight at 20 ° C * 2 This indicates that the coating formed by applying the coating composition of the present invention has an excellent humidity control function. (Hygroscopicity and release) were confirmed.

【0088】実験例3 実施例1及び2で調製した塗料組成物(塗料1及び2)
について、日本工業規格JIS K 5400に規定されている方
法に基づいて、(1)容器の中での状態(JIS K 5400の4.1
(2))、(2)塗装作業性(JIS K 5400の6.1)、(3)低温安
定性(JIS K 5400の5.1)について調べ、さらに形成さ
れた塗膜について、(4)乾燥時間(JIS K5400の6.5)、
(5)塗膜の外観(JIS K 5400の7.1)、(6)隠蔽率(JIS K
5400の7.2)、(7)耐アルカリ性(JIS K 5400の8.2
1)、(8)耐洗浄性(JIS K 5400の8.11)、(9)耐水性(J
IS K 5400の8.19)及び(10)促進耐候性(JIS K 5400の
9.8.1)の各項目について調べた。なお各項目の試験方
法並びに評価は、全てJIS K5663-1995に規定されている
方法に準拠した。
Experimental Example 3 The coating compositions prepared in Examples 1 and 2 (Coatings 1 and 2)
Based on the method specified in Japanese Industrial Standards JIS K 5400, (1) state in the container (JIS K 5400 4.1
(2)), (2) Paint workability (6.1 of JIS K 5400), (3) Low temperature stability (5.1 of JIS K 5400), and check the formed coating film for (4) Drying time (JIS 6.5 of K5400),
(5) Appearance of coating film (JIS K 5400 7.1), (6) Hiding ratio (JIS K 5400
7.2 of 5400), (7) Alkali resistance (8.2 of JIS K 5400
1), (8) Washing resistance (8.11 of JIS K 5400), (9) Water resistance (J
8.19 of IS K 5400) and (10) Accelerated weather resistance (JIS K 5400
9.8.1). The test method and evaluation of each item were all based on the method specified in JIS K5663-1995.

【0089】(1) 容器の中での状態(JIS K5663-1995の
5.3) 塗料を容器(金属製内面コート缶)に充填し、室温で2
4時間以上静置した後、容器の蓋を開け棒で中身をかき
混ぜて塗料の状態を調べた。かき混ぜたときに、堅い塊
がなくて中身全体が一様になる場合を「良好」、塊はな
いが一様になりにくい場合を「普通」、塊を認める場合
を「不良」とした。
(1) State in a container (JIS K5663-1995)
5.3) Fill the container (metal inner coated can) with paint,
After leaving still for 4 hours or more, the lid of the container was opened and the contents were stirred with a stick to check the state of the paint. When the mixture was stirred, there was no hard lump and the whole contents were uniform. "Good", when there was no lump but it was difficult to make it uniform, "normal", and when the lump was recognized was "poor".

【0090】(2) 塗装作業性(JIS K5663-1995の5.4) 試験板(フレキシブル板、500×200×3mm)の平滑な面
に塗料をそれぞれ刷毛で一様に塗り(1回目、塗布量:1
0〜13mml/1枚)、6時間おいてから2回目の刷毛塗り
(塗布量:9〜11mml/1枚)を行い、2回目を塗る際の
刷毛運びの困難性の有無から塗装作業性を評価した。2
回目を塗る際の刷毛運びが困難でない場合を「2回塗り
で塗装作業に支障がない」として評価を「良好」とし、
刷毛運びの困難性に応じて順次「普通」、「不良」とし
た。
(2) Painting workability (JIS K5663-1995, 5.4) Paint was uniformly applied to the smooth surface of a test plate (flexible plate, 500 × 200 × 3 mm) with a brush (first time, amount of application: 1
0 to 13 mml / sheet), and after 6 hours, a second brush coating (coating amount: 9 to 11 mml / sheet) is performed, and the coating workability is determined based on the difficulty of carrying the brush when applying the second time. evaluated. 2
When it is not difficult to carry the brush when applying the second time, the evaluation is "good" as "two coats do not hinder the painting work",
“Normal” and “Poor” were sequentially determined according to the difficulty of brush transfer.

【0091】(3) 低温安定性(JIS K5663-1995の5.5) 塗料を容器(金属製内面コート缶)にほぼ一杯に満たし
て密閉し、温度−5±2℃の低温恒温器中に18時間収
納した後、取り出して室温下に6時間放置する操作を3
回繰り返した。次いで、容器の蓋を開けて中の塗料を棒
でかき混ぜて一様になるかどうかを調べた。また、前述
する(2)の方法に準じて塗装作業性を調べた。具体的
には、低温恒温器に入れる前の塗料で1回塗りし、低温
安定性を調べた処理塗料を用いて2回塗りを行い、2回
目の刷毛運びの困難性を評価した。さらに、上記塗装作
業性試験の終わった試験板を24時間乾燥して、形成され
た塗膜の外観を評価した。塗料が容易に一様となり、塗
装作業性と塗膜の外観に異常がないとき「−5℃に冷や
したときに変質しない」として評価を「良好」とし、順
次不良の程度に応じて「普通」及び「不良」とした。
(3) Low-temperature stability (5.5 of JIS K5663-1995) A container (metal inner surface coated can) is almost completely filled with the paint and hermetically sealed, and kept in a low-temperature incubator at a temperature of -5 ± 2 ° C. for 18 hours. After storing, remove and leave at room temperature for 6 hours.
Repeated times. Next, the lid of the container was opened, and the paint in the container was stirred with a stick to check whether the paint became uniform. Further, the coating workability was examined according to the method (2) described above. Specifically, it was applied once with a paint before being put into a low-temperature constant temperature oven, applied twice using a treated paint whose low-temperature stability was checked, and evaluated for difficulty in carrying a second brush. Furthermore, the test plate after the above-mentioned coating workability test was dried for 24 hours, and the appearance of the formed coating film was evaluated. When the paint was easily uniform and there was no abnormality in the coating workability and appearance of the coating film, the evaluation was "good" as "no deterioration when cooled to -5 ° C". And "Poor".

【0092】(4) 乾燥時間(JIS K5663-1995の5.6) 塗料をガラス板(200×100×2mm)の片面に隙間100μ
mのB形フィルムアプリケータを用いて塗布し、これを
20±1℃、湿度65±5%の恒温恒湿室に入れて、塗
膜が半硬化状態(塗面の中央を指先で静かに軽くこすっ
て塗面に擦り傷がつかない状態)まで乾燥する時間を測
定した。
(4) Drying time (5.6 of JIS K5663-1995) Paint was applied to one side of a glass plate (200 × 100 × 2 mm) with a clearance of 100 μm.
m using a B-type film applicator, put it in a thermo-hygrostat at 20 ± 1 ° C, 65 ± 5% humidity, and the coating film is in a semi-cured state. The drying time was measured until the coated surface was rubbed gently so as not to scratch the coated surface.

【0093】(5) 塗膜の外観(JIS K5663-1995の5.7) 上記(2)塗装作業性の試験で塗料を塗布した試験板を24
時間乾燥させて、拡散昼光の下で塗面を肉眼でみて、刷
毛目の程度の大きさ、穴や弛みの有無、塗膜表面の一様
性(むらなし)を評価した。刷毛目の程度が大きくな
く、穴や弛みがなく、塗膜表面が一様(むらなし)であ
るとき、「塗膜の外観が正常である」として評価を「良
好」とし、順次不良の程度に応じて「普通」及び「不
良」とした。
(5) Appearance of the coating film (5.7 of JIS K5663-1995)
After drying for an hour, the coated surface was visually observed under diffused daylight to evaluate the size of the brush, the presence or absence of holes and slackness, and the uniformity of the coating surface (unevenness). When the degree of brush eyes is not large, there are no holes or slacks, and the coating film surface is uniform (no unevenness), the evaluation is evaluated as "good" as "the appearance of the coating film is normal", and the degree of failure is sequentially "Normal" and "Poor" according to

【0094】(6) 隠蔽率(JIS K5663-1995の5.8) 隠蔽率試験紙をガラス板の上に固定し、その上に塗料を
隙間150μmのB形フィルムアプリケーターを用いて塗
り、24時間放置して乾燥させた。試験紙の白地と黒地の
上に形成された塗膜の視感反射率を反射率測定装置を用
いて、試験片の3カ所について測定した。得られた視感
反射率から下記の式から隠蔽率を求めた。
(6) Hiding Ratio (5.8 of JIS K5663-1995) A hiding ratio test paper was fixed on a glass plate, and a paint was applied thereon using a B-type film applicator having a gap of 150 μm, and allowed to stand for 24 hours. And dried. The luminous reflectance of the coating film formed on the white background and the black background of the test paper was measured at three places of the test piece using a reflectance measuring device. From the obtained luminous reflectance, the hiding ratio was determined from the following equation.

【0095】[0095]

【数1】 (Equation 1)

【0096】(7) 耐アルカリ性(JIS K5663-1995の5.1
0) 試験片:予め周辺及び裏面を同種の塗料で2〜3回
塗り包んでおいたフレキシブル板(150×70×3mm)の表
面に塗料を刷毛で1±0.1ml/100cm2 の割合で一様に
塗り、6時間後、同様に更に1回塗って5日間乾燥し、
次いで試験板の周辺及び裏面をパラフィンで被覆して、
試験片とした(3枚準備、うち1枚は原状試験片)。 上記試験片を水酸化カルシウム飽和溶液(20±1
℃)中に18〜48時間浸漬し、2枚の試験片について
溶液から取り出した直後と2時間後の観察で、塗膜の状
態を原状試験片との比較で評価した(膨れ、割れ、剥が
れ、穴、軟化、色、艶)。 評価:48時間または18時間の浸漬処理で、試験片2
枚の塗膜に膨れ、割れ、剥がれ、穴、軟化を認めず、更
に浸漬溶液の着色や濁りがなく、原状試験片と比べて艶
の変化や変色の程度が大きくない時を、それぞれ「48時
間浸したとき異常がない」として評価を「良好」、また
は「18時間浸したとき異常がない」として評価を「良」
とした。
(7) Alkali resistance (5.1 of JIS K5663-1995)
0) Test piece: A paint was applied to the surface of a flexible plate (150 × 70 × 3 mm) whose peripheral and back surfaces were previously coated with the same type of paint two or three times with a brush at a rate of 1 ± 0.1 ml / 100 cm 2. After 6 hours, apply once more in the same manner and dry for 5 days.
Next, the periphery and back surface of the test plate were covered with paraffin,
Test pieces were prepared (three pieces were prepared, one of which was an original test piece). The test piece was placed in a calcium hydroxide saturated solution (20 ± 1).
C.) for 18 to 48 hours, and the state of the coating film was evaluated by comparing it with the original test piece immediately after taking out the two test pieces from the solution and two hours later (swelling, cracking, and peeling). , Holes, softening, color, luster). Evaluation: Test piece 2 after immersion treatment for 48 hours or 18 hours
When no swelling, cracking, peeling, pitting, or softening was observed on the coating films, there was no coloring or turbidity of the immersion solution, and the degree of gloss change or discoloration was not greater than that of the original test specimen, `` 48 Evaluation is "good" as "No abnormality when soaked for 18 hours", or "Good" as "No abnormality when soaked for 18 hours"
And

【0097】(8) 耐洗浄性(JIS K5663-1995の5.11) 試験片:フレキシブル板(430×170×5mm)の中央部
の長辺の長さ約400mmに隙間150μmのB形フィルムアプ
リケーターで塗料を塗り、塗面を上向きにして7日間乾
燥したものを試験片とした(2枚準備)。 ウォッシャビリティーマシンを用いて、0.5%の石鹸
水で濡らした試験片(2枚)の塗膜面をブラシで往復
(100回〜500回)して擦り、その後試験片を試験機から
外して水で洗い、ブラシで擦った跡の中央にあたる長さ
100mmの部分の塗膜を拡散昼光の下で、塗膜の破れや摩
滅の有無を目視で調べた。 評価:500回以上のブラシ往復で、試験片2枚とも中
央部分の塗膜が破れまたは摩滅によって試験片の素地の
露出が認められない場合を「500回の洗浄に耐える」と
して評価を「良好」とし、また100回以上の往復で試験
片の素地の露出が認められない場合を「100回の洗浄に
耐える」として評価を「良」とした。
(8) Washing resistance (5.11 of JIS K5663-1995) Specimen: Painted with a B-type film applicator with a gap of 150 μm on the long side of about 400 mm at the center of a flexible plate (430 × 170 × 5 mm). And dried for 7 days with the coated surface facing upward as test pieces (two pieces prepared). Using a washer machine, rub the coating surface of the test piece (2 pieces) wetted with 0.5% soap water by reciprocating (100 to 500 times) with a brush, and then remove the test piece from the testing machine. Wash with water and brush the length of the center of the mark
The coating film of the 100 mm portion was visually inspected under diffused daylight for the presence or absence of breakage or wear of the coating film. Evaluation: When 500 or more brush reciprocations, the coating film in the center part of both test pieces was not broken or worn and no exposure of the base material of the test piece was recognized, and the evaluation was "good" as "withstanding 500 washes". In addition, when no exposure of the substrate of the test specimen was observed after 100 or more reciprocations, the evaluation was "good" as "withstanding 100 washes".

【0098】(9) 耐水性(JIS K5663-1995の5.9) 上記(7)耐アルカリ性試験で使用した試験片と同じもの
を使用して(2枚)、これを脱イオン水(20±1℃)に
96時間浸漬して、試験片2枚について溶液から取り出
した直後と2時間後の観察で、塗面の状態を評価した
(シワ、膨れ、割れ、剥がれ、色、艶)。
(9) Water resistance (5.9 of JIS K5663-1995) Using the same test specimen (2 sheets) used in the above (7) Alkali resistance test, this was deionized water (20 ± 1 ° C.) ) For 96 hours, and the state of the coated surface was evaluated (wrinkles, blisters, cracks, peeling, color, gloss) immediately after the two test pieces were taken out of the solution and two hours later.

【0099】(10) 促進耐候性(JIS K5663-1995の5.1
2)(サンシャインカーボンアーク灯式:JIS K 5400 9.
8.1) 試験片:予めJPIA-23の合成樹脂エマルジョンシーラ
ーで処理したフレキシブル板(150×70×3mm)に塗料
を2回一様に刷毛塗りし(一回につき塗布量:1.0±0.1
ml/cm2)、5日間乾燥して試験片とした(2枚、うち
1枚原状試験片)。尚、1回塗りと2回塗りとの間が6
時間とした。 サンシャインカーボンアーク灯式耐光性試験器(ブ
ラックパネル温度:63℃、降雨サイクル:120分間隔で
18分間)を用いて200時間照射して、原状試験片と
耐候試験片の塗膜を肉眼観察して、色むらと色つやの変
化の程度、白亜化・か膨れ・剥がれ・割れの有無を調べ
た。 白亜化度が8点以上で、膨れ、はがれ、割れがな
く、色の変化の程度が原状試験片に比べて大きくないと
きは、評価を「良好」とし、順次不良の程度に応じて
「普通」及び「不良」とした。
(10) Accelerated weathering resistance (5.1 of JIS K5663-1995)
2) (Sunshine carbon arc lamp type: JIS K 5400 9.)
8.1) Specimen: A flexible plate (150 x 70 x 3 mm) previously treated with a synthetic resin emulsion sealer of JPIA-23 was evenly brushed twice with paint (amount applied per time: 1.0 ± 0.1).
ml / cm 2 ) and dried for 5 days to obtain test pieces (two pieces, one of which was an original test piece). In addition, the interval between the first coating and the second coating is 6
Time. Irradiation was performed for 200 hours using a sunshine carbon arc lamp type light resistance tester (black panel temperature: 63 ° C, rain cycle: 120 minutes, 18 minutes), and the coating films of the original test piece and the weather resistance test piece were visually observed. Then, the degree of color unevenness and color gloss change, and the presence or absence of chalking, blistering, peeling, and cracking were examined. If the degree of chalk is 8 or more, no swelling, peeling or cracking, and the degree of color change is not greater than that of the original test specimen, the evaluation is evaluated as “good”, and the evaluation is evaluated as “normal” in accordance with the degree of failure. And "Poor".

【0100】結果を表3に示す。Table 3 shows the results.

【0101】[0101]

【表3】 [Table 3]

【0102】これらの結果から、本発明の塗料組成物
は、合成樹脂エマルジョンペイントの少なくとも2種、
特に1種の規格(JIS K5663-1995)を満たす塗料である
ことが確認された。
From these results, it was found that the coating composition of the present invention contains at least two kinds of synthetic resin emulsion paints,
In particular, it was confirmed that the paint satisfied one type of standard (JIS K5663-1995).

【図面の簡単な説明】[Brief description of the drawings]

【図1】本発明の建材の下地材(素地)へ配設方法を示
す断面図である。
FIG. 1 is a cross-sectional view showing a method of arranging a building material on a base material (base) according to the present invention.

【図2】本発明の建材(パネル)の連設態様を示す断面
図である。(a)は突付け張り、(b)は突付けV形み
ぞ張り、及び(c)相じゃくりの仕口による目透かし張
りをそれぞれ示す。
FIG. 2 is a cross-sectional view showing a continuous construction mode of building materials (panels) of the present invention. (A) shows an abutment, (b) shows an abutment V-shaped groove, and (c) shows an eye-opening by a phased joint.

【図3】パネルの施工方法によって処理された(補強部
材として寒冷紗等のテープ材を使用)、パネル接合部を
示す断面図である。
FIG. 3 is a cross-sectional view showing a panel joint, which has been processed by a panel construction method (using a tape material such as cold gauze as a reinforcing member).

【図4】パネルの施工方法によって処理された(補強部
材として略T字形ジョイナーを使用)、パネル接合部を
示す断面図である。
FIG. 4 is a cross-sectional view showing a panel joint processed by a panel construction method (using a substantially T-shaped joiner as a reinforcing member).

【符号の説明】[Explanation of symbols]

1.パネル基材 2.塗膜層 3.釘 4.塗料組成物(パテ)充填部 5.壁下地材 6.接合部 7.テープ材(補強部材) 8.ジョイナー(補強部材) 1. Panel substrate 2. Coating layer 3. Nail 4. 4. Paint composition (putty) filling section Wall base material 6. Joint 7. 7. Tape material (reinforcing member) Joiner (reinforcing member)

Claims (18)

【特許請求の範囲】[Claims] 【請求項1】消石灰、アクリル系樹脂、無機顔料及び水
を含有する塗料組成物であって、(a)消石灰の配合割
合が30重量%未満(固形換算)、(b)アクリル系樹
脂が(メタ)アクリル酸、(メタ)アクリル酸エステ
ル、(メタ)アクリルアミド類及び(メタ)アクリロニ
トリルよりなる群から選択されるいずれか少なくとも1
種をモノマー成分として含有するホモポリマーまたはコ
ポリマーであって、該樹脂の配合割合が1〜85重量%
(固形換算)、並びに(c)無機顔料の配合割合が0.
1〜90重量%(固形換算)である建築用塗料組成物。
1. A coating composition containing slaked lime, an acrylic resin, an inorganic pigment and water, wherein (a) the blending ratio of slaked lime is less than 30% by weight (solid basis), and (b) the acrylic resin is (A) At least one selected from the group consisting of (meth) acrylic acid, (meth) acrylic acid ester, (meth) acrylamides and (meth) acrylonitrile
A homopolymer or a copolymer containing a seed as a monomer component, wherein the compounding ratio of the resin is 1 to 85% by weight.
(In terms of solids), and (c) the mixing ratio of the inorganic pigment is 0.5%.
1 to 90% by weight (solid basis) of an architectural coating composition.
【請求項2】アクリル系樹脂が、(メタ)アクリル酸若
しくはそのエステルから形成されるホモポリマーまたは
コポリマーである請求項1記載の建築用塗料組成物。
2. The architectural coating composition according to claim 1, wherein the acrylic resin is a homopolymer or a copolymer formed from (meth) acrylic acid or an ester thereof.
【請求項3】無機顔料が酸化チタン,亜鉛華,リトポ
ン,硫化亜鉛及びアンチモン白よりなる群から選択され
る少なくとも1種の白色顔料、好ましくは酸化チタンで
ある請求項1または2に記載の建築用塗料組成物。
3. The building according to claim 1, wherein the inorganic pigment is at least one white pigment selected from the group consisting of titanium oxide, zinc white, lithopone, zinc sulfide and antimony white, preferably titanium oxide. Paint composition.
【請求項4】消石灰の配合割合が14〜30重量%未満
(固形換算)である請求項1乃至3のいずれかに記載の
建築用塗料組成物。
4. The architectural coating composition according to claim 1, wherein the proportion of slaked lime is 14 to less than 30% by weight (solid basis).
【請求項5】アクリル系樹脂の配合割合が1〜17重量
部(固形換算)である、請求項1乃至4のいずれかに記
載の建築用塗料組成物。
5. The architectural coating composition according to claim 1, wherein the blending ratio of the acrylic resin is 1 to 17 parts by weight (solid basis).
【請求項6】無機顔料の配合割合が1〜5重量部(固形
換算)である請求項1乃至5のいずれかに記載の建築用
塗料組成物。
6. The architectural coating composition according to claim 1, wherein the blending ratio of the inorganic pigment is 1 to 5 parts by weight (solid basis).
【請求項7】さらに体質顔料を含有することを特徴とす
る、請求項1乃至6のいずれかに記載の建築用塗料組成
物。
7. The architectural coating composition according to claim 1, further comprising an extender pigment.
【請求項8】体質顔料がタルク、炭酸カルシウム、カオ
リンクレー、水酸化アルミニウム、ベントナイト、硫酸
バリウム、ホワイトカーボン及びシリカよりなる群から
選択される少なくとも1種である請求項7に記載の建築
用塗料組成物。
8. The paint according to claim 7, wherein the extender is at least one selected from the group consisting of talc, calcium carbonate, kaolin clay, aluminum hydroxide, bentonite, barium sulfate, white carbon and silica. Composition.
【請求項9】繊維素材を含まないことを特徴とする請求
項1乃至8のいずれかに記載の建築用塗料組成物。
9. The architectural coating composition according to claim 1, which does not contain a fiber material.
【請求項10】乾燥塗膜の隠蔽力が500μm以下であ
る請求項1乃至9のいずれかに記載の建築用塗料組成
物。
10. The architectural coating composition according to claim 1, wherein the hiding power of the dried coating film is 500 μm or less.
【請求項11】粘度が常温で300〜8000センチポ
イズである請求項1乃至10のいずれかに記載の建築用
塗料組成物。
11. The architectural coating composition according to claim 1, which has a viscosity of 300 to 8000 centipoise at room temperature.
【請求項12】塗液またはその乾燥塗膜の (1)容器の中
での状態、(2)塗装作業性、(3)低温安定性、(4)塗膜の
外観、(5)耐アルカリ性、(6)耐洗浄性、(7)隠蔽率が、J
IS K 5663-1995に規定される少なくとも2種ペイントの
性質を満たすものである、請求項1乃至11のいずれか
に記載の建築用塗料組成物。
12. The coating liquid or its dried coating film (1) state in a container, (2) coating workability, (3) low temperature stability, (4) appearance of coating film, (5) alkali resistance , (6) Washing resistance, (7) Concealment ratio is J
The architectural coating composition according to any one of claims 1 to 11, which satisfies the properties of at least two paints specified in IS K 5663-1995.
【請求項13】請求項1乃至12のいずれかに記載の塗
料組成物から形成される塗膜を有することを特徴とする
塗装物。
13. A coated article having a coating film formed from the coating composition according to claim 1. Description:
【請求項14】建材である請求項13記載の塗装物。14. The coated article according to claim 13, which is a building material. 【請求項15】建築下地材又は素地材の表面に、請求項
1乃至12のいずれかに記載の塗料組成物を塗布し、乾
燥後、必要に応じて塗膜面を研磨ずりすることを特徴と
する塗装方法。
15. A coating composition according to any one of claims 1 to 12, which is applied to the surface of a building base material or a base material, dried, and then, if necessary, polished on the surface of the coating film. And painting method.
【請求項16】 (i) 建築下地材または素地材に請求項
14記載の建材を複数連設する工程、(ii) 各建材の接
合部に、請求項1乃至12のいずれかに記載の塗料組成
物を充填若しくは塗布して乾燥する工程、及び(iii) 必
要に応じて、塗膜面を研磨ずりする工程を含む、建築物
内外装の施工方法。
16. The coating according to claim 1, wherein (i) a step of arranging a plurality of the building materials according to claim 14 on a building base material or a base material, and (ii) a joint between the building materials. A method for applying the composition to the interior and exterior of a building, comprising a step of filling or applying the composition and drying, and (iii) a step of polishing and polishing the coating film surface as necessary.
【請求項17】(i) 建築下地材または素地材に請求項1
4記載の建材を複数連設する工程、(ii) 必要に応じ
て、各建材の接合部に請求項1乃至12のいずれかに記
載の塗料組成物を充填若しくは塗布する工程、(iii) 該
接合部を補強部材で覆う工程、(iv) 該補強部材上に請
求項1乃至12のいずれかに記載の塗料組成物を塗布し
て乾燥する工程、及び(v) 必要に応じて、塗膜面を研磨
ずりする工程を含む、建築物内外装の施工方法。
17. The method according to claim 1, wherein (i) the base material of the building or the base material is used.
(4) a step of filling or applying the coating composition according to any one of claims 1 to 12 to a joint of each building material, if necessary, A step of covering the joint with a reinforcing member, (iv) a step of applying the coating composition according to any one of claims 1 to 12 on the reinforcing member and drying, and (v) a coating film, if necessary. A construction method for interior and exterior of buildings, including a process of polishing and polishing surfaces.
【請求項18】請求項1乃至12のいずれかに記載の塗
料組成物を塗布して形成される塗膜層を表面に有する建
築物内・外装面の損傷部を修復する方法であって、(i)
必要であれば該損傷部の塗膜層を削りとる工程、(ii)
壁面損傷部に請求項1乃至12のいずれかに記載の塗料
組成物を充填若しくは塗布して乾燥する工程、及び(ii
i)必要に応じて、当該塗膜面を研磨ずりする工程を含
む、建築物内・外装面の修復方法。
18. A method for repairing a damaged portion of an interior / exterior surface of a building having a coating layer formed on the surface thereof by applying the coating composition according to any one of claims 1 to 12, (i)
Removing the coating layer of the damaged part if necessary, (ii)
A step of filling or applying the coating composition according to any one of claims 1 to 12 to a damaged wall surface and drying; and (ii)
i) A method for repairing the interior and exterior surfaces of a building, including a step of polishing and polishing the coating film surface as necessary.
JP2000208321A 1999-10-22 2000-07-10 Coating material composition Withdrawn JP2000313843A (en)