JP2000234862A - Method and system for drying ceramic molding - Google Patents

Method and system for drying ceramic molding

Info

Publication number
JP2000234862A
JP2000234862A JP3309799A JP3309799A JP2000234862A JP 2000234862 A JP2000234862 A JP 2000234862A JP 3309799 A JP3309799 A JP 3309799A JP 3309799 A JP3309799 A JP 3309799A JP 2000234862 A JP2000234862 A JP 2000234862A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
temperature
hot air
furnace
drying
air
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP3309799A
Other languages
Japanese (ja)
Other versions
JP3455813B2 (en )
Inventor
Shinji Sugiura
伸二 杉浦
Original Assignee
Takahama Kogyo Kk
高浜工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To ensure optimal control of drying a ceramic molding by determining a target temperature of hot air being fed into a drying furnace based on the set wet- bulb temperature in the drying furnace, the outer air temperature and the relative humidity of outer air and heating the outer air and then controlling the quantity of hot air being supplied into the furnace based on the difference between the set temperature and the measured temperature in the furnace. SOLUTION: When a drying furnace 10 is controlled, an operating means 24 determines a target drying temperature (hereinafter referred to target temperature) of hot air optimal for drying operation and a heating control means 26 controls a hot air generation source 14 based on the target temperature before hot air produced by heating the outer air is blown into the drying furnace 10. Temperature of hot air measured by a hot air temperature sensor 34 is transmitted to the heating control means 26 where the measured hot air temperature is compared with the target temperature and the hot air generation source 14 is controlled based on the comparison results. On the other hand, a fan controller 30 compares the temperature in the furnace measured by a temperature sensor 28 in the furnace with a preset temperature in the furnace and controls a fan 16 according to the difference tus controlling hot air supply correctly.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【産業上の利用分野】この発明は、瓦、タイル、煉瓦などの窯業成形物の乾燥方法およびその装置に関するものである。 BACKGROUND OF THE INVENTION This invention tiles, tiles, on Drying method and apparatus for ceramic moldings, such as bricks.

【0002】 [0002]

【従来の技術】一般的に瓦、タイル、煉瓦などの窯業製品は水分を含んだ粘土を主体とする原料から製造されるが、成形された直後の窯業成形物の水分率は約20%であるから、窯業成形物を乾燥させる必要のあることは知られるとおりである。 BACKGROUND ART Generally, tiles, tiles, although ceramic products such as bricks are made from raw materials mainly composed of clay containing water, moisture content of the ceramic molded product immediately after being molded is about 20% because there are as to be known that that need to dry the ceramic molded product. 窯業成形物の乾燥の際、乾燥に伴う収縮が窯業成形物に発生することは避けられない。 During the drying of the ceramic molded product, it is inevitable that shrinkage due to drying will occur in ceramic molding.

【0003】とくに、当業界で広く採用されている熱風を利用したいわゆる強制乾燥の場合では、この乾燥に伴う収縮の差が著しく生じるおそれがあり、乾燥に伴う著しい収縮の差が窯業成形物の変形や亀裂の原因となっていた。 [0003] Particularly, in the case of so-called forced drying using hot air is widely used in the art, the difference in shrinkage caused by the drying may significantly occur fear, significant difference in shrinkage due to drying of the ceramic molded product It has been a cause of deformation and cracks. したがって、窯業成形物に変形や亀裂を生じさせないようにするためには、窯業成形物の乾燥を適切に制御することが重要であり、そのための乾燥方法やその装置の選択や工夫は適切な乾燥を実現する大きな要素であった。 Therefore, in order not to cause deformation or cracks in the ceramic molding, it is important to appropriately control the drying of ceramic moldings, selection and devising methods of drying and apparatus therefor suitable drying It was a major element to achieve.

【0004】窯業成形物の乾燥は、予熱期間、恒率乾燥期間、減率乾燥期間の3つの期間に区分することができる。 [0004] Drying of the ceramic moldings can be divided into three periods of the preheating period, constant rate drying period, falling-rate drying period.

【0005】予熱期間は、窯業成形物の温度が上昇し、 [0005] preheating period, the temperature of the ceramic molding is increased,
一定の温度に保たれるまでの期間をいう。 It refers to a period of up to be kept at a constant temperature. 予熱期間は、 Preheating period,
乾燥炉内に供給される熱風により窯業成形物の温度が上昇する期間であり、熱風の熱のほとんどは窯業成形物の温度上昇に費やされ、窯業成形物の乾燥には費やされない。 The hot air to be supplied to the drying oven is a period in which the temperature of the ceramic molding is increased, most of the hot air heat spent the temperature rise of the ceramic molded product, not spent to dry the ceramic molded product.

【0006】ただし、窯業成形物の内部の温度が上昇する前に、窯業成形物の表面から乾燥が行われると、窯業成形物の内部の水分は十分に移動できないから、乾燥に伴う著しい収縮の差を生じ、この著しい収縮の差により窯業成形物に変形や亀裂を生じる。 [0006] However, before the internal temperature of the ceramic molding is increased, the drying from the surface of the ceramic molding is performed, the inside of the ceramic molding because moisture can not be sufficiently moved, significant shrinkage due to drying resulting differences, resulting in deformation or cracks in the ceramic molded product by the difference of the significant shrinkage.

【0007】そこで、窯業成形物の表面からの乾燥を抑制する一方、乾燥時間を短縮するために窯業成形物の温度をできるだけ上昇させることが求められる。 [0007] Therefore, while suppressing the drying of the surface of the ceramic molded product, to increase as much as possible the temperature of the ceramic molded product obtained in order to shorten the drying time.

【0008】恒率乾燥期間は、窯業成形物の温度がほぼ一定に保たれた状態から窯業成形物の水分率が限界水分率に達するまでの期間をいう。 [0008] constant rate drying period refers to the period from the state where the temperature of the ceramic molded product was kept almost constant until the moisture content of the ceramic molded product reaches a limit moisture content. 恒率乾燥期間では、窯業成形物の温度がほぼ一定の温度を保つが、窯業成形物の表面から水分が蒸発し、表面からの水分の蒸発に追従するように窯業成形物の内部の水分は表面に向けて移動する状態にある。 The constant rate drying period, the temperature of the ceramic molded product maintains a substantially constant temperature, water evaporates from the surface of the ceramic molded product, the moisture therein ceramic molded product so as to follow the evaporation of water from the surface It is in a state to move toward the surface. したがって、恒率乾燥期間では窯業成形物の水分率が限界水分率に達するまでほぼ一定の乾燥速度で窯業成形物が乾燥される。 Thus, ceramics molded product is dried at a substantially constant rate of drying to the moisture content of the ceramic molded product at constant rate drying period reaches the limit water content.

【0009】一般的に、窯業成形物の温度が高いほど窯業成形物の内部から表面へ移動する水分が多くなる。 [0009] In general, water increases to move from the interior of the higher temperature of the ceramic molded product has high ceramic molding to the surface. しかし、単に乾燥炉内の温度を上昇させ、窯業成形物の温度を高めると、その表面から蒸発する水分が増加する一方、内部から表面に向けて移動する水分が表面から蒸発する水分に対応して追従することができなくなる。 However, merely increasing the temperature in the drying furnace, increasing the temperature of the ceramic molded product, while the water evaporates from the surface increases, in response to the moisture moisture moves toward the surface from the inside is evaporated from the surface it is not possible to follow Te.

【0010】したがって、窯業成形物の表面と内部において乾燥状態に差が生じる。 Accordingly, a difference in a dry state occurs at the surface and inside of the ceramic molding. その結果、窯業成形物に乾燥に伴う著しい収縮の差が生じ、窯業成形物に変形や亀裂が発生する。 As a result, a difference occurs in significant shrinkage due to drying ceramic shaped articles, deformation or cracking occurs in the ceramic molding. そこで、恒率乾燥期間では窯業成形物に対して乾燥に伴う収縮の差を極力生じさせないようにすることが重要となる。 Therefore, be adapted not to minimize occurs a difference in shrinkage due to drying with respect to ceramic molded product becomes important at the constant rate drying period.

【0011】減率乾燥期間は、窯業成形物の水分率が限界水分率から平衡水分率に達するまでの乾燥期間をいう。 [0011] falling rate drying period refers to the drying period until the moisture content of the ceramic molded product reaches an equilibrium moisture content of the limit water content. 減率乾燥期間では、窯業成形物の表面から蒸発する水分が内部から表面に移動する水分よりも多くなり、窯業成形物に残存する水分の低下に伴って乾燥速度は低下する。 The falling rate drying period, moisture evaporates from the surface of the ceramic molded product becomes more than moisture to move from the inside to the surface, with a decrease in the moisture remaining in the ceramic molding drying rate decreases. 減率乾燥期間では窯業成形物の温度は上昇し、窯業成形物の水分率が平衡水分率に達すると窯業成形物の乾燥が終了する。 The falling rate drying period the temperature of the ceramic molded product increases, the drying of the ceramic molding is completed when the moisture content of the ceramic molded product reaches equilibrium moisture content. 減率乾燥期間では、窯業成形物に対する乾燥の収縮がほとんど発生しないので、乾燥による変形や亀裂などの窯業成形物への影響は小さいものである。 The falling rate drying period, the drying shrinkage for ceramics molding hardly occurs, the influence of the ceramic molded product, such as deformation and cracks due to drying is smaller.

【0012】次に、従来のこの種の乾燥装置を乾燥方法と併せて説明する。 [0012] Next, the this type of conventional drying apparatus in conjunction with the drying process. 図6に示された乾燥装置は、湿式成形された窯業成形物を収容する乾燥炉aにバ−ナ−iを介設した熱風供給路が接続され、乾燥炉aに設けられた炉内温度センサkにより炉内温度の検出値と炉内温度の設定値に基づいてバ−ナ−iの燃焼量を制御して乾燥炉内の温度調整を行うようにしたものである。 Drying apparatus shown in Figure 6, bar the drying oven a housing the ceramic molded product is wet-molded - hot air supply passage which is interposed a na -i is connected, furnace temperature provided the drying oven a sensor k based on the set value of the detected value of the temperature in the furnace and the furnace temperature by bar - is obtained as by controlling the amount of combustion na -i adjusting the temperature in the drying furnace.

【0013】そして、熱風供給路に介設されて熱風中に蒸気を混入する加湿器jと、供給される熱風の相対湿度を検出する熱風湿度センサrと、供給される熱風の温度を検出する熱風温度センサpと、炉内相対湿度の設定値と、前記炉内温度センサkによる炉内温度の検出値または炉内温度の設定値とから絶対湿度を演算し、さらに、 [0013] Then, to detect the humidifier j to incorporate steam in the hot air is interposed in the hot air supply path, a hot air humidity sensor r for detecting the relative humidity of the hot air supplied, the temperature of hot air supplied a hot air temperature sensor p, calculates a set value of the furnace relative humidity, absolute humidity and a detected value or furnace temperature settings for the furnace temperature by the furnace temperature sensor k, furthermore,
その絶対湿度に対する前記熱風温度センサpで得られた熱風の温度における相対湿度を演算し、その演算値を相対湿度の補正値として出力する演算手段tとを備えたものである。 Calculates the relative humidity at the temperature of the hot air obtained by the hot air temperature sensor p for the absolute humidity is obtained by an arithmetic means t for outputting the calculated value as a correction value of the relative humidity.

【0014】さらに、前記熱風湿度センサrの検出値と前記演算手段で得られた前記補正設定値の差に基づいて、前記加湿器jの蒸気混入量を制御する制御手段sを備えている。 Furthermore, based on the difference of the correction set value obtained by the detection value and the calculation means of the heated air humidity sensor r, and a control unit s for controlling the vapor mixing amount of the humidifier j.

【0015】この装置によれば、乾燥炉aの相対湿度を制御するに際して、演算手段tにより予め設定された炉内相対温度の設定値と、炉内温度センサkによる炉内温度の検出値または予め定められた炉内温度の設定値とから絶対湿度が演算され、さらにその絶対湿度に対する熱風温度センサpで得られた熱風の温度における相対湿度が演算され、その演算値が相対湿度の補正値として出力される。 According to this device, when controlling the relative humidity of the drying oven a, a preset value in the relative temperature furnace by calculation means t, the detection value of the in-furnace temperature by furnace temperature sensor k or absolute humidity is calculated from the set value of a defined furnace temperature in advance, further the relative humidity at a temperature of the hot air obtained by the hot air temperature sensor p with respect to the absolute humidity is calculated, the correction value for the operation value is relative humidity It is output as.

【0016】つづいて、制御手段sにおいて、熱風湿度センサrで得られた熱風の相対湿度の検出値が、上記の演算手段tから出力された補正設定値と比較されて、その差に基づいて加湿器jから熱風中に混入される蒸気量が制御され、熱風の相対湿度が補正設定値に制御される。 [0016] Subsequently, the control unit s, the detection value of the relative humidity of the hot air obtained by the hot-air humidity sensor r is compared with the corrected setting value output from said operation means t, on the basis of the difference steam amount to be mixed into the hot air from the humidifier j is controlled, the relative humidity of the hot air is controlled to the corrected set value.

【0017】この場合、炉内温度が変化し、炉内相対湿度が変化するのを見越してそれを補完するように熱風へ混入する蒸気量が制御され、炉内温度が変化するにもかかわらず炉内相対湿度が設定値に正確に調整される。 [0017] In this case, the temperature changes in the furnace, the amount of steam to be mixed to the hot air as in anticipation of a change in the furnace relative humidity to complement it is controlled, despite the furnace temperature is varied furnace relative humidity is adjusted accurately to the set value.

【0018】したがって、炉内相対湿度の制御がより正確で繊細に行われるので、複雑な形状の窯業成形物でも切れや変形を防止して乾燥歩留まりの向上を図ることができ、また、乾燥時間のより短縮化を図ることなどの利点を有するとされている。 [0018] Thus, since the control of the furnace relative humidity is more accurate and delicate carried out, it can be prevented even cutting or deformation at ceramics molded product having a complicated shape and improve the dry yield, also, the drying time It is to have advantages such as be shortened from the.

【0019】しかし、前記した従来例の技術では、乾燥炉内の温度を測定し、測定された炉内温度と炉内温度の設定値の差に基づいて乾燥炉内の温度を制御する一方、 [0019] However, the aforementioned conventional art, while the temperature in the drying furnace is measured, controls the measured furnace temperature and furnace temperature setting difference between the temperature in the drying furnace based on the,
設定された乾燥炉内の相対湿度を維持するために、熱風の相対湿度を加湿器を用いて制御するというものである。 To maintain the relative humidity of the set drying oven, is that controlled using a humidifier relative humidity of the hot air. つまり、乾燥炉内の温度制御は熱風の加熱制御により行い、乾燥炉内の相対湿度の制御を熱風の蒸気混入量の制御により行うものである。 In other words, the temperature control in the drying furnace is carried out by heating control of the hot air, the control of the relative humidity in the drying furnace is performed by controlling the vapor mixing amount of hot air.

【0020】ところが、乾燥炉内の温度制御のために熱風の温度を制御すると熱風の相対湿度が追従して変化し、乾燥炉内の相対湿度が変化する。 [0020] However, the hot air of relative humidity by controlling the temperature of hot air for temperature control in the drying furnace is changed to follow, the relative humidity in the drying furnace is changed. そこで、相対湿度の変化に対応させて蒸気を混入し、設定された相対湿度に維持させるが、適切な蒸気量の制御のために以下の手順が必要となる。 Therefore, in correspondence with changes in the relative humidity mixed with steam, but is maintained at the set relative humidity, the following steps are required to control the proper amount of steam. 炉内の相対湿度の設定値と炉内温度の測定値により絶対湿度を求める。 The absolute humidity by setting and measurement of furnace temperature relative humidity in the furnace. 熱風の温度を測定し、熱風の温度の測定値と算出された炉内の絶対湿度とにより補正設定値としての相対湿度を求める。 The temperature of hot air was measured to determine the relative humidity as a correction set value by the absolute humidity in the furnace and the calculated measurement value of the temperature of the hot air. 熱風湿度センサにより測定された熱風の湿度の測定値と、補正設定値を比較する。 The measured value of the humidity of the hot air measured by the hot air humidity sensor, comparing the correction set value. 比較結果により混入する蒸気量を制御する。 Controlling the amount of steam to be mixed with the comparison result.

【0021】このように、熱風の温度を制御することによる乾燥炉内の温度の制御は、温度と相対湿度との密接かつ複雑な関係にあることから、温度の変化に対応するように相対湿度の変化を考慮しなければならず、乾燥炉内の相対湿度の制御を複雑化する結果となるほか、窯業成形物の最適な乾燥を実現するための条件を見いだすことが極めて困難であった。 [0021] Thus, control of the temperature of the drying furnace by controlling the temperature of the hot air, since it is in close and complex relationship between temperature and relative humidity, the relative humidity so as to correspond to a change in temperature It must consider the change, in addition to resulting in complicating the control of the relative humidity in the drying furnace, it has been extremely difficult to find conditions for optimal drying of the ceramics molded product.

【0022】したがって、最適な乾燥を実現するための乾燥の制御は、乾燥装置の設計者など乾燥技術に精通した者に限られ、窯業成形物の製造に従事するオペレ−タが、窯業成形物の変更などに応じてこれらの制御を自由に変更することは不可能であった。 [0022] Thus, control of drying for optimum drying is limited to those familiar with such drying techniques designers of the drying device, engaged in the production of ceramic moldings operator - data are ceramic moldings depending on the change was not possible to change these control freely.

【0023】 [0023]

【発明が解決しようとする課題】この発明が解決しようとする課題は、従来の乾燥技術が熱風の温度を制御して乾燥炉内の温度を制御する一方、熱風に蒸気を混入して乾燥炉内の相対湿度を制御するため、乾燥炉内の相対湿度の制御を複雑化する点や温度と相対湿度との密接かつ複雑な関係により、温度の変化に対応するように相対湿度の変化を考慮しなければならず、温度と相対湿度の制御を個別にすることができない点にあるほか、窯業成形物の最適な乾燥を実現するための条件を見いだすことが困難である点であり、乾燥炉内の相対湿度や温度の制御は乾燥の専門的な知識を有する者に限られる点である。 THE INVENTION Problems to be Solved] Problem to be Solved by the invention, while the conventional drying technique to control the temperature in the drying furnace by controlling the temperature of hot air, drying oven and mixed with steam in a hot-air to control the relative humidity of the inner, the close and complex relationship between the complex points and temperature and relative humidity control of the relative humidity in the drying furnace, taking into account the changes in relative humidity so as to correspond to a change in temperature must, in addition in the inability to individually control the temperature and relative humidity, and in that it is difficult to find conditions for optimal drying of ceramics molding, drying furnace control of relative humidity and temperature of the inner is a point to be limited to a person having specialized knowledge of drying.

【0024】この発明の目的は、窯業成形物の最適な乾燥を実現することのほか、熱風の温度の制御と供給量の制御を個別に行い、窯業成形物の最適な乾燥の制御をより容易なものとし、乾燥の制御に特別な知識や経験のない乾燥炉のオペレ−タなどが手軽に乾燥条件の制御を行うことができる窯業成形物の乾燥方法とその装置を提供することにある。 The object of the present invention, in addition to realizing an optimum drying of the ceramic molded product, and controls the control and supply amount of the temperature of the hot air separately, easier control of the optimum drying of ceramic moldings and things, operating the drying oven without special knowledge and experience in the control of drying - data etc. is to provide a drying method and apparatus of ceramic moldings can be controlled easily drying conditions.

【0025】 [0025]

【課題を解決するための手段および作用効果】上記の目的を達成するため、請求項1記載の窯業成形物の乾燥方法は、湿式成形された窯業成形物を乾燥炉に収容し、外気を加熱して熱風を得るとともに熱風を乾燥炉内へ供給し、供給された熱風により窯業成形物を乾燥させる窯業成形物の乾燥方法において、乾燥炉内の設定湿球温度と炉内設定温度を予め設定し、外気の温度と相対湿度を測定して外気温度と外気相対湿度を求め、乾燥炉内の設定湿球温度、外気温度および外気相対湿度に基づいて乾燥炉内に供給する熱風の目標温度を求め、求められた熱風の目標温度となるように外気を加熱し、外気を加熱して得られた熱風を乾燥炉へ供給し、他方、乾燥炉内の温度を測定して炉内温度を求め、炉内設定温度と測定された炉内温度の差に基 To achieve Means and effects to an aspect of the above object, the drying method of claim 1 ceramic molding description, the ceramic molded product is wet-molded housing in a drying oven heated outside air previously set in the drying method of the ceramic molded product by supplying the hot air into the drying furnace to dry the ceramic molded product by the supplied hot air with obtaining hot air, a setting wet-bulb temperature and the furnace set temperature in the drying furnace and and obtains the outside air temperature and the ambient relative humidity by measuring the ambient air temperature and relative humidity, setting wet bulb temperature in the drying furnace, the target temperature of hot air supplied to the drying oven on the basis of the outside air temperature and the outdoor air relative humidity determined by heating the outside air so that the target temperature of the obtained hot air, hot air obtained by heating the outside air is supplied into the drying furnace, while seeking furnace temperature by measuring the temperature in the drying furnace , furnace set temperature and the measured furnace temperature difference based on the いて乾燥炉内へ供給する熱風の供給量を制御することを特徴とするものである。 It is characterized in that to control the supply amount of hot air supplied into the drying furnace are.

【0026】したがって、請求項1記載の窯業成形物の乾燥方法は、乾燥炉内の設定湿球温度、外気温度および外気相対湿度に基づいて乾燥炉内に供給する熱風の目標温度が求められ、求められた熱風の目標温度となるように外気を加熱し、外気を加熱して得られた熱風が乾燥炉内へ供給される。 [0026] Thus, the drying method of claim 1 ceramic molding according to a setting wet bulb temperature in the drying furnace, the target temperature of hot air supplied to the drying oven is obtained based on the outside air temperature and the outdoor air relative humidity, the obtained heated outside air so that the target temperature of the hot air, hot air obtained by heating the outside air is supplied into the drying furnace.

【0027】そして、乾燥炉内へ供給された熱風により窯業成形物の乾燥が行われるが、乾燥炉内に供給された熱風の湿球温度は乾燥炉内の設定湿球温度と同じである。 [0027] Then, the drying of the ceramic molding is performed by being supplied into the drying furnace hot air, wet-bulb temperature of supplied into the drying furnace hot air is the same as setting the wet-bulb temperature in the drying furnace. また、乾燥により熱風が断熱冷却されると熱風の相対湿度は上昇するが、熱風の湿球温度は変化しない。 Also, hot air drying is but when the adiabatic cooling relative humidity of the hot air rises, not wet-bulb temperature of the hot air is changed.

【0028】したがって、窯業成形物の温度と乾燥炉内の湿球温度に差が生じないので、乾燥が安定して進行し、乾燥に伴う著しい収縮の差による変形や亀裂の発生を抑制して窯業成形物の乾燥が行われる。 [0028] Thus, the difference in the wet-bulb temperature and a drying oven of ceramic molding does not occur, dried stable in progress by suppressing deformation and crack occurrence due to significant difference in shrinkage caused by drying drying of the ceramic molding is performed.

【0029】他方、乾燥炉内に供給される熱風は乾燥炉内の設定湿球温度、外気温度および外気相対湿度に基づく目標温度が設定されているため、熱風の温度を乾燥炉内の温度変化に追従させることができない。 [0029] On the other hand, hot air to be supplied to the drying furnace set wet-bulb temperature in the drying furnace, since the target temperature based on the outside air temperature and the outdoor air relative humidity is set, the temperature change of the temperature of the hot air drying oven It can not be made to follow on.

【0030】そこで、乾燥炉内の温度を測定して炉内温度を求め、炉内温度と炉内設定温度との差を求め、この差に基づいて熱風の供給量を制御することにより、乾燥炉内の温度は炉内設定温度に保たれる。 [0030] Therefore, the temperature in the drying oven to measure sought furnace temperature, obtains the difference between the furnace temperature and furnace set temperature, by controlling the supply amount of hot air on the basis of this difference, dried temperature in the furnace is maintained in the furnace within the set temperature. なお、炉内設定温度を経時的に上昇させるように設定すれば乾燥時間を短縮化することが可能となる。 Incidentally, it is possible to shorten the drying time by setting the furnace temperature setting so that over time increases.

【0031】請求項1記載の窯業成形物の乾燥方法は、 The drying method according to claim 1 ceramic molding description,
上記のように構成されているので以下の利点を有する。 It has the following advantages because it is constructed as described above.
外気の加熱により得られた熱風は、乾燥炉内の設定湿球温度に対応する目標温度にあるので、熱風の湿球温度と窯業成形物の温度が一致し、熱風の湿球温度と窯業成形物の温度との差により生じがちな著しい収縮を抑制することができ、変形や亀裂を抑制して窯業成形物を乾燥することができる。 Hot air obtained by heating the outside air, since the target temperature corresponding to the set wet-bulb temperature in the drying furnace, consistent temperature of wet bulb and ceramic molding of hot air, wet-bulb and ceramic molding hot-air it is possible to suppress liable to occur significant shrinkage due to the difference between the temperature of the object, it is possible to dry the ceramic molded product by suppressing deformation and cracking.

【0032】また、乾燥炉内の温度制御は熱風の温度を変化させることなく、熱風の供給量の制御により行うので、熱風の温度制御により乾燥炉内の温度制御を図る場合と比較して、熱風の温度の変化に追従して熱風の相対湿度が変化するという複雑な関係を考慮する必要がない。 Further, the temperature control in the drying furnace without changing the temperature of the hot air, is performed by controlling the supply amount of hot air, as compared with the case where the temperature control of the hot air achieving a temperature control in the drying furnace, there is no need to consider the complex relationships that following the change in the temperature of the hot air relative humidity of the hot air is changed.

【0033】このように、目標温度の熱風による乾燥炉内の湿球温度の制御と、熱風の供給量の制御による乾燥炉内の温度制御により、窯業成形物の理想的な乾燥を実現し、窯業成形物の乾燥歩留まりを向上させることができる。 [0033] Thus, the control of the wet-bulb temperature of the drying furnace by hot air target temperature, the temperature control in the drying furnace by controlling the supply amount of hot air, to achieve an ideal drying of ceramics molded product, it is possible to improve the dry yield of ceramic moldings.

【0034】また、熱風の温度制御が乾燥炉内の湿球温度の制御を目的としており、温度変化に伴う相対湿度の変化を考慮する必要がなく、熱風の供給量の制御が乾燥炉内の温度制御を目的としているので、熱風の温度と供給量を個別に制御することが可能であり、乾燥条件の変動が発生しても乾燥炉のオペレ−タなどが手軽に制御の変更を行うことができる。 Further, the temperature control of the hot air has the purpose of controlling the wet-bulb temperature in the drying furnace, it is not necessary to consider the change in relative humidity with a change in temperature, control of the supply amount of the hot air in the drying furnace since the purpose of temperature control, it is possible to control the temperature and supply amount of hot air separately, operator variation of the drying oven occurs drying conditions - such data is possible to easily control the change can.

【0035】請求項2記載の窯業成形物の乾燥方法は、 The drying method of the ceramic molded article according to the second aspect,
湿式成形された窯業成形物を乾燥炉に収容し、外気を加熱して熱風を得るとともに熱風を乾燥炉内へ供給し、供給された熱風により窯業成形物を乾燥させる窯業成形物の乾燥方法において、乾燥炉内の設定湿球温度と炉内設定温度を予め設定し、乾燥炉内へ供給される熱風の温度と相対湿度を測定して熱風温度と熱風相対湿度を求め、 The wet molded ceramic molded was taken up in a drying oven, supplying hot air into the drying furnace with obtaining hot air to heat the outside air to the drying process of ceramic molded product for drying ceramic molded product by the supplied hot air , the setting wet-bulb temperature and the furnace set temperature in the drying furnace set in advance, the temperature and relative humidity of the hot air to be supplied into the drying furnace to measure seeking hot air temperature of hot air relative humidity,
乾燥炉内の設定湿球温度、熱風温度および熱風相対湿度に基づいて乾燥炉内へ供給する熱風の目標温度を求め、 Setting wet bulb temperature in the drying furnace, it obtains a target temperature of the hot air supplied into the drying furnace based on the hot air temperature and hot air relative humidity,
求められた熱風の目標温度となるように外気を加熱し、 Outside air is heated so that the the obtained hot air target temperature,
外気を加熱して得られた熱風を乾燥炉内へ供給し、他方、乾燥炉内の温度を測定して炉内温度を求め、炉内設定温度と測定された炉内温度の差に基づいて乾燥炉内へ供給する熱風の供給量を制御することを特徴とするものである。 Supplying hot air obtained by heating the outside air into the drying furnace, while the temperature in the drying oven to measure sought furnace temperature, based on the difference in the furnace was measured to the furnace set temperature Temperature it is characterized in that to control the supply amount of hot air supplied to the drying oven.

【0036】したがって、請求項2記載の窯業成形物の乾燥方法は、請求項1記載の窯業成形物の乾燥方法の場合と同様な作用を奏するが、熱風の目標温度は乾燥炉内の設定湿球温度、熱風温度および熱風相対湿度に基づいているため、外気を加熱した熱風の目標温度がより正確に維持される。 [0036] Thus, the drying method of the ceramic molded article according to claim 2, which provides the same effect as in the drying method of claim 1 ceramic molding according, the target temperature of the hot air is set in the drying furnace humidity bulb temperature, because it is based on hot air temperature and hot air relative humidity, the target temperature of the hot air heated outside air can be maintained more accurately.

【0037】したがって、請求項2記載の窯業成形物の乾燥方法は、請求項1記載の窯業成形物の乾燥方法が奏する効果のほか、外気を加熱した熱風の目標温度をより正確に維持することができるので、乾燥炉内の設定湿球温度に対する熱風の湿球温度をより安定して保つことができ、より正確な乾燥の制御を行うことができる。 [0037] Thus, the drying method of the ceramic molded article according to claim 2, wherein, in addition to the effect of drying method of claim 1 ceramic molded product described exhibit, to maintain the target temperature of hot air to heat the outdoor air more accurately since it is, the wet-bulb temperature of the hot to the configuration wet-bulb temperature in the drying furnace can be maintained more stably, and can be performed more accurately controlled drying.

【0038】請求項3記載の窯業成形物の乾燥装置は、 The drying apparatus of claim 3 ceramic moldings description,
湿式成形された窯業成形物を収容する乾燥炉が備えられ、乾燥炉に接続された熱風供給ダクトに熱風発生源が設けられ、熱風発生源に外気吸引ダクトが接続され、乾燥炉に排気ダクトが接続された窯業成形物の乾燥装置において、外気の温度を測定する外気温度センサと外気の相対湿度を測定する外気湿度センサが外気吸引ダクトに設けられ、外気温度センサにより測定された外気温度と外気温度センサに測定された外気相対湿度とにより、予め設定された乾燥炉内の設定湿球温度に対応する熱風の目標温度を求める演算手段が設けられ、乾燥炉内へ供給される熱風の温度が目標温度となるように熱風発生源を制御する加熱制御手段が設けられ、他方、乾燥炉に該乾燥炉内の温度を測定する炉内温度センサが設けられ、炉内温度センサにより Drying furnace is provided for accommodating the wet molded ceramic moldings, hot air source is provided to the connected hot air supply duct to the drying oven, the outside air suction duct is connected to a hot air source, the exhaust duct to the drying furnace the drying apparatus of a connected ceramic moldings, outdoor air humidity sensor for measuring the outside air temperature sensor and the ambient relative humidity to measure the outside air temperature is provided in the outside air suction duct, the outside air temperature measured by the outside air temperature sensor and the outside air by the outside air relative humidity measured in the temperature sensor, calculating means are provided to determine the target temperature of the hot air corresponding to the set wet-bulb temperature of the preset drying oven, the temperature of the hot air to be supplied into the drying furnace heating control means is provided for controlling the hot air source so that the target temperature, on the other hand, furnace temperature sensor for measuring the temperature of the drying oven is provided in the drying furnace, the furnace temperature sensor 定された炉内温度と予め設定された炉内設定温度の差に基づいて熱風の供給量を制御する風量制御手段が設けられたことを特徴とするものである。 It is characterized in that the air volume control means based on the difference between the preset furnace set temperature and the constant has been furnace temperature to control the supply amount of hot air is provided.

【0039】したがって、請求項3記載の窯業成形物の乾燥装置によれば、外気吸引ダクトに外気が吸引され、 [0039] Thus, according to the drying apparatus according to claim 3 ceramic moldings according, outside air is sucked to the air suction duct,
外気温度センサにより外気温度が測定されるとともに外気湿度センサにより外気相対湿度が測定される。 Outdoor air relative humidity is measured by the outdoor air humidity sensor with the outside air temperature is measured by the outside air temperature sensor. 予め設定された乾燥炉内の設定湿球温度、測定された外気温度および外気相対湿度に基づいて乾燥炉内へ供給する熱風の目標温度が演算手段により求められる。 Setting wet bulb preset drying oven, the target temperature of the hot air supplied into the drying furnace is determined by calculation means based on the measured ambient temperature and the outdoor air relative humidity.

【0040】求められた熱風の目標温度となるように加熱制御手段が熱風発生源を制御し、熱風発生源により外気が加熱され、目標温度の熱風は熱風供給ダクトを通じて乾燥炉内へ供給される。 The heating control means so that the target temperature of the obtained hot air is controlled hot air source, the outside air is heated by hot air source, hot air target temperature is supplied into the drying furnace through the hot air supply duct .

【0041】そして、乾燥炉内に供給された熱風により窯業成形物の乾燥が行われるが、乾燥炉内に供給された熱風の湿球温度は乾燥炉内の設定湿球温度と同じである。 [0041] Then, the drying of the ceramic molding is performed by being supplied to the drying furnace hot air, wet-bulb temperature of supplied into the drying furnace hot air is the same as setting the wet-bulb temperature in the drying furnace. また、乾燥により熱風が断熱冷却されると熱風の相対湿度は上昇するが、熱風の湿球温度は変化しない。 Also, hot air drying is but when the adiabatic cooling relative humidity of the hot air rises, not wet-bulb temperature of the hot air is changed. したがって、窯業成形物の温度と乾燥炉内の湿球温度に差が生じないので、乾燥が安定して進行し、乾燥に伴う著しい収縮の差による窯業成形物の変形や亀裂の発生を抑制される。 Therefore, the difference in the wet-bulb temperature and a drying oven of ceramic molding does not occur, drying is suppressed stably proceeds, the occurrence of deformation and cracking of the ceramic moldings by significant difference in shrinkage caused by drying that.

【0042】他方、乾燥炉内に供給される熱風は乾燥炉内の設定湿球温度、外気温度および外気相対湿度に基づく目標温度が設定されているため、熱風の温度を乾燥炉内の温度変化に追従させることができない。 [0042] On the other hand, hot air to be supplied to the drying furnace set wet-bulb temperature in the drying furnace, since the target temperature based on the outside air temperature and the outdoor air relative humidity is set, the temperature change of the temperature of the hot air drying oven It can not be made to follow on. そこで、乾燥炉内の温度を炉内温度センサにより測定して炉内温度を求め、炉内温度と炉内設定温度との差を求め、この差に基づいて風量制御手段を制御して熱風の供給量を制御することにより、乾燥炉内の温度は炉内設定温度に保たれる。 Therefore, the temperature in the drying furnace is measured by a furnace temperature sensor determine the furnace temperature, obtains the difference between the furnace temperature and furnace set temperature, the hot air by controlling the air volume control means on the basis of this difference by controlling the supply amount, the temperature in the drying furnace is maintained in the furnace set temperature.

【0043】請求項3記載の窯業成形物の乾燥装置は、 The drying apparatus of claim 3 ceramic moldings description,
上記のように構成されているので、以下の利点を有する。 Which is configured as described above has the following advantages. 乾燥炉内の設定湿球温度に対応する目標温度の熱風を供給することができ、熱風の湿球温度と窯業成形物の温度が一致した状態で窯業成形物を乾燥することができるので、熱風の湿球温度と窯業成形物の温度の差により生じがちな乾燥に伴う著しい収縮の差による窯業成形物の変形や亀裂が抑制され、理想的な窯業成形物の乾燥を行うことができる。 Drying oven settings can supply the hot air of the corresponding target temperature wet bulb, it is possible to dry the ceramic molded product in the state where temperature is matched to the wet-bulb temperature and ceramic molding of hot air, hot air deformation and cracking of the wet-bulb and ceramic moldings by significant differences in shrinkage caused by the liable to occur dried by differences in the temperature of the ceramic molded product is suppressed, it is possible to perform the drying of the ideal ceramic moldings.

【0044】熱風の温度制御による乾燥炉内の湿球温度の制御と、熱風の供給量の制御による乾燥炉内の温度制御により、窯業成形物の理想的な乾燥を実現し、窯業成形物の乾燥歩留まりを向上させることができる。 The control of the wet-bulb temperature of the drying furnace with temperature control of the hot air, the temperature control in the drying furnace by controlling the supply amount of hot air, to achieve an ideal drying of ceramics molding, Ceramic moldings thereby improving the drying yield.

【0045】また、熱風の温度制御は乾燥炉内の湿球温度の制御を目的とし、熱風の供給量の制御は乾燥炉内の温度制御を目的としているので、従来のような温度と相対湿度を制御するために熱風の温度と蒸気混入量を制御する場合と比較して、熱風の温度と供給量を独立させて制御することが可能であり、乾燥炉内の雰囲気を最適な状態にすることが極めて容易となり、乾燥に対する特別な知識を持たない乾燥炉のオペレ−タなどが手軽に乾燥の制御を変更することができる。 Further, the temperature control of the hot air is intended to control the wet-bulb temperature in the drying furnace, the control of the supply amount of the hot air is intended to control the temperature of the drying furnace, as in the prior art temperature and relative humidity as compared with the case of controlling the temperature and vapor mixing amount of the hot air to control, it is possible to control by independent temperature and supply amount of hot air, an optimum condition the atmosphere in the drying furnace it becomes extremely easy, operating the drying furnace no special knowledge of drying - can such data to change the control of easily drying.

【0046】請求項4記載の窯業成形物の乾燥装置は、 The drying apparatus of claim 4 ceramic molded product described,
湿式成形された窯業成形物を収容する乾燥炉が備えられ、乾燥炉に接続された熱風供給ダクトに熱風発生源が設けられ、熱風発生源に外気吸引ダクトが接続され、乾燥炉に排気ダクトが接続された窯業成形物の乾燥装置において、熱風の温度を測定する熱風温度センサと熱風の相対湿度を測定する熱風湿度センサが熱風供給ダクトに設けられ、熱風温度センサにより測定された熱風温度と熱風湿度センサにより測定された熱風相対湿度とにより、予め設定された乾燥炉内の設定湿球温度に対応する熱風の目標温度を求める演算手段と、乾燥炉内へ供給される熱風の温度が目標温度となるように熱風発生源を制御する加熱制御手段が設けられ、他方、乾燥炉に該乾燥炉内の温度を測定する炉内温度センサが設けられ、炉内温度センサにより測定 Drying furnace is provided for accommodating the wet molded ceramic moldings, hot air source is provided to the connected hot air supply duct to the drying oven, the outside air suction duct is connected to a hot air source, the exhaust duct to the drying furnace the drying apparatus of a connected ceramic moldings, hot air humidity sensor for measuring the hot air temperature sensor and the relative humidity of the hot air to measure the temperature of hot air is provided in the hot air supply duct, a hot air temperature of the hot air measured by the hot air temperature sensor by the measured hot air relative humidity by a humidity sensor, a preset arithmetic means for obtaining a target temperature of the hot air corresponding to the set wet-bulb temperature of the drying oven, the temperature is the target temperature of the hot air to be supplied into the drying furnace provided heating control means for controlling the hot air source such that, on the other hand, furnace temperature sensor for measuring the temperature of the drying oven is provided in the drying furnace, measured by a furnace temperature sensor れた炉内温度と予め設定された炉内設定温度の差に基づいて熱風の供給量を制御する風量制御手段が設けられたことを特徴とするものである。 Air volume control means for controlling the supply amount of hot air was based on the difference between the furnace temperature and a preset furnace set temperature is characterized in that is provided.

【0047】請求項4記載の窯業成形物の乾燥装置によれば、外気吸引ダクトに外気が吸引され、外気は熱風発生源により加熱され熱風供給ダクトに送入される。 [0047] According to the drying apparatus according to claim 4 ceramic molded product according, outside air is sucked to the air suction duct, the external air is fed into a hot air supply duct is heated by hot air source. 熱風温度センサにより熱風温度が測定されるとともに熱風湿度センサにより熱風相対湿度が測定される。 Hot air relative humidity is measured by the hot air humidity sensor by hot air temperature is measured by the hot air temperature sensor.

【0048】予め設定された炉内の設定湿球温度、測定された熱風温度および熱風相対湿度に基づいて乾燥炉内に供給する熱風の目標温度が演算手段により求められる。 [0048] Setting wet-bulb temperature of the preset furnace, the target temperature of hot air supplied to the drying furnace based on the measured temperature of hot air and hot air relative humidity is determined by the calculating means. 求められた熱風の目標温度となるように加熱制御手段が熱風発生源を制御し、熱風発生源により外気が加熱され、目標温度の熱風は熱風供給ダクトを通じて乾燥炉内へ供給される。 Heating control means so that the target temperature of the obtained hot air is controlled hot air source, the outside air is heated by hot air source, hot air target temperature is supplied into the drying furnace through the hot air supply duct.

【0049】そして、供給された熱風により窯業成形物の乾燥が行われるが、乾燥炉内に供給された熱風の湿球温度は乾燥炉内の設定湿球温度と同じである。 [0049] Then, the drying of the ceramic molding is carried out by the supplied hot air, wet-bulb temperature of supplied into the drying furnace hot air is the same as setting the wet-bulb temperature in the drying furnace. また、乾燥により熱風が断熱冷却されると熱風の相対湿度は上昇するが熱風の湿球温度は変化しない。 Although the hot air is adiabatic cooling relative humidity of the hot air rises not wet-bulb temperature of the hot air is changed by drying. したがって、窯業成形物の温度と乾燥炉内の湿球温度に差が生じないので、乾燥が安定して進行し、乾燥に伴う著しい収縮の差による窯業成形物の変形や亀裂の発生が抑制される。 Therefore, the difference in the wet-bulb temperature and a drying oven of ceramic molding does not occur, dried stable proceeds, deformation and cracking of the ceramic moldings by significant difference in shrinkage caused by drying can be suppressed that.

【0050】他方、乾燥炉内に供給される熱風は乾燥炉内の設定湿球温度、熱風温度および熱風相対湿度に基づく目標温度が設定されているため、熱風の温度を乾燥炉内の温度変化に追従させることができない。 [0050] On the other hand, hot air to be supplied to the drying furnace set wet-bulb temperature in the drying furnace, since the target temperature based on the temperature of hot air and hot air relative humidity is set, the temperature change of the temperature of the hot air drying oven It can not be made to follow on. そこで、乾燥炉内の温度を炉内温度センサにより測定して炉内温度を求め、炉内温度と炉内設定温度との差を求め、この差に基づいて風量制御手段を制御して熱風の供給量を制御することにより、乾燥炉内の温度が炉内設定温度に保たれる。 Therefore, the temperature in the drying furnace is measured by a furnace temperature sensor determine the furnace temperature, obtains the difference between the furnace temperature and furnace set temperature, the hot air by controlling the air volume control means on the basis of this difference by controlling the supply amount, the temperature in the drying furnace is maintained in the furnace set temperature.

【0051】請求項4記載の窯業成形物の乾燥装置は、 The drying apparatus of claim 4 ceramic molded product described,
上記のように構成されているので、請求項3記載の窯業成形物の乾燥装置の効果を奏するほか以下の利点を有する。 Which is configured as described above, with the addition following advantages to achieve the effect of a drying apparatus according to claim 3 ceramic moldings according. 熱風温度センサと熱風湿度センサが熱風供給ダクトに設けられているので、乾燥炉内へ供給される熱風の目標温度をより安定して維持できる。 Since the hot air temperature sensor and the hot air humidity sensor is provided in the hot air supply duct can maintain a target temperature of the hot air to be supplied into the drying furnace more stably. なお、これらのセンサを熱風供給ダクトの乾燥炉寄りに設ければ、熱風の目標温度の正確性を一層図ることができる。 Incidentally, by providing these sensors in the drying oven side of the hot air supply duct, it is possible to further improve the accuracy of the target temperature of hot air.

【0052】請求項5記載の窯業成形物の乾燥装置は、 [0052] Drying apparatus according to claim 5 ceramic molded product described,
請求項3または4記載の窯業成形物の乾燥装置において、風量制御手段が、外気吸引ダクトに設けられた送風ファンと、炉内温度センサにより測定される炉内温度と炉内設定温度との差に基づいて送風ファンを制御する送風用制御器とからなることを特徴とするものである。 Difference in the drying apparatus according to claim 3 or 4 ceramic moldings according, air volume control means comprises a blower fan provided in the outdoor air suction duct, the furnace temperature and furnace setting temperature measured by the furnace temperature sensor and it is characterized in that comprising a blower control unit for controlling the blower fan based on.

【0053】請求項5記載の窯業成形物の乾燥装置によれば、炉内温度センサにより測定された炉内温度と炉内設定温度との差に基づいて送風用制御器が送風ファンを制御するので、乾燥炉の設定温度に対応する熱風の供給量が正確に制御される。 [0053] According to the drying apparatus according to claim 5 Ceramic moldings according blower control unit controls the blowing fan based on the difference between the furnace temperature measured by the furnace temperature sensor and a furnace set temperature since the supply amount of hot air corresponding to the set temperature of the drying oven is accurately controlled.

【0054】また、請求項5記載の窯業成形物の乾燥装置は、上記の構成であるから、請求項3または4記載の窯業成形物の乾燥装置が奏する効果のほか、送風ファンにより外気を吸引して熱風を乾燥炉内に供給するので、 [0054] Further, the drying apparatus according to claim 5 Ceramic moldings according, since the configuration of the above, in addition to the effect of drying apparatus according to claim 3 or 4 ceramic molded product described exhibit, sucking the outside air by the blowing fan since supplying hot air into the drying furnace and,
外気吸引ダクトや熱風供給ダクトにダンパを設ける必要がなく、装置の構造が簡単になるほか、風量制御手段が送風ファンと送風用制御器からなることから、送風用制御器により送風ファンは制御されるので、炉内設定温度に対応する熱風を正確に供給することができ、乾燥炉の温度制御を容易にかつ正確に行うことができる。 There is no need to provide a damper to the outside air suction duct and the hot air supply duct, in addition to the structure of the apparatus is simplified, since the air volume control means comprises a blower fan and the blower control unit, the blower fan is controlled by blowing controller Runode, it is possible to accurately supply the hot air corresponding to the furnace set temperature, the temperature control of the drying oven can be easily and accurately performed.

【0055】請求項6記載の窯業成形物の乾燥装置は、 [0055] Drying apparatus according to claim 6 ceramic molded product described,
請求項3または4記載の窯業成形物の乾燥装置において、外気吸引ダクトに送風ファンが設けられ、風量制御手段が、熱風供給ダクトに設けられた熱風用ダンパと、 The drying apparatus according to claim 3 or 4 ceramic moldings according blower fan to the air suction duct is provided, air volume control means comprises a hot air damper provided in the hot air supply duct,
炉内温度センサにより測定される炉内温度と炉内設定温度との差に基づいて熱風用ダンパを開閉する開閉用制御器とからなり、熱風用ダンパにより分岐された熱風の一部を外気吸引ダクトへ循環させる循環ダクトが設けられるとともに外気吸引ダクトに送風ファンが設けられたことを特徴とするものである。 It consists of a closing control device for opening and closing the hot air damper on the basis of the difference between the furnace temperature and furnace setting temperature measured by the furnace temperature sensor, the outside air suction part of the hot air which is branched by the hot air damper it is characterized in that the circulation duct for circulating the duct blower fan to the air suction duct with provided is provided.

【0056】請求項6記載の窯業成形物の乾燥装置によれば、送風ファンにより外気を吸引くするとともに熱風を乾燥炉内へ供給する。 [0056] supplying According to the drying apparatus according to claim 6 Ceramic moldings according, hot air with suction Kusuru outside air by the blowing fan into the drying furnace. 熱風が供給される熱風供給ダクトに熱風用ダンパが設けられており、炉内温度センサにより測定された炉内温度と炉内設定温度との差に基づいて開閉用制御器が熱風用ダンパの開閉による送風を制御するので、乾燥炉の設定温度に対応する熱風の供給量が正確に制御される。 Hot air has hot air damper is provided in the hot air supply duct supplied, the opening and closing opening and closing controller of the hot air damper on the basis of the difference between the measured furnace temperature and furnace set temperature by furnace temperature sensor and it controls the air blowing by the feed rate of the hot air corresponding to the set temperature of the drying oven is accurately controlled. また、熱風用ダンパにより分岐された熱風の一部は、循環ダクトを通じて外気吸引ダクトへ循環される。 Part of the hot air which is branched by a hot air damper, is circulated to the outside air suction duct through the circulation duct.

【0057】請求項6記載の窯業成形物の乾燥装置は、 [0057] Drying apparatus according to claim 6 ceramic molded product described,
上記の構成であるから、請求項3または4記載の窯業成形物の乾燥装置の効果のほか、外気を吸引するとともに熱風を乾燥炉内へ供給する送風ファンが設けられているものの、熱風用ダンパの開閉により、乾燥炉内への熱風の供給量を制御するとともに、熱風用ダンパにより分岐された熱風の一部は、循環ダクトを通じて外気吸引ダクトへ循環されるので、熱風の再利用を図ることができ、 Since the configuration of the above, in addition to the effect of the drying apparatus according to claim 3 or 4 ceramic moldings according While blowing fan for supplying hot air into the drying furnace sucks outside air is provided, the hot air damper the opening and closing controls the supply amount of hot air into the drying furnace, a portion of the branched hot with hot air damper, because it is circulated to the outside air suction duct through the circulation duct, possible to reuse the heated air It can be,
熱風発生源による外気への加熱量を低減して乾燥装置の省エネルギ−化を図ることができる。 Energy saving of reduced drying apparatus the heating amount of the outside air by a hot air source - reduction can be achieved.

【0058】また、風量制御手段が熱風用ダンパと開閉用制御器とからなることから、開閉用制御器により熱風用ダンパの開閉は制御されるので、炉内設定温度に対応する熱風を正確に供給することができ、乾燥炉内の温度制御を容易にかつ正確に行うことができるほか、送風ファンを一定の回転数を保って運転することができる。 [0058] Further, since the air volume control means comprises a hot air damper opening and closing control unit, the opening and closing of the hot air damper is controlled by the opening and closing control unit, exactly a hot air corresponding to the furnace set temperature can be supplied, in addition to the temperature control in the drying furnace can be easily and accurately performed, it is possible to operate the blower fan while maintaining a constant rotational speed.

【0059】 [0059]

【発明の実施の形態】この発明の実施の形態を図面を参照して以下に説明する。 DETAILED DESCRIPTION OF THE INVENTION be described below with reference to the drawings an embodiment of the present invention. 図1はこの実施の形態その1に係る窯業成形物の乾燥装置の概略図、図2は実施の形態その2に係る窯業成形物の乾燥装置の概略図、図3は実施の形態その3に係る窯業成形物の乾燥装置の概略図、 Figure 1 is a schematic view of a drying apparatus ceramic molded product according to the Part 1 of this embodiment, a schematic view of a drying apparatus ceramic molded product 2 according to the Part 2 of the embodiment, in FIG. 3 embodiment the 3 schematic view of a drying apparatus ceramic moldings according,
図4は湿球温度と温度制御との関係を示す説明図、図5 Figure 4 is an explanatory view showing the relationship between the wet-bulb temperature control, 5
は実施の形態その1に係る窯業成形物の乾燥装置による乾燥特性を示すグラフ、図6は従来例の窯業成形物の乾燥装置の概略図である。 Is a graph showing the drying properties by the drying apparatus of ceramic moldings according to the its first embodiment, FIG. 6 is a schematic view of a drying apparatus ceramic molding in the prior art.

【0060】この発明の実施の形態その1に係る窯業成形物の乾燥装置について説明する。 [0060] described drying device of Embodiment Ceramic moldings according to Part 1 of the present invention. (全体構成)図1に示されるように、窯業成形物を収容するバッチ式の乾燥炉10が設けられており、図示しないが乾燥炉10の内部には乾燥炉10内の空気を撹拌して乾燥炉10内の雰囲気をより均一にするための撹拌用ファンが設けられている。 As shown in (Overall Configuration) FIG. 1 is provided with a batch type drying furnace 10 for accommodating the ceramic moldings, the interior of the not shown drying furnace 10 by stirring the air in the drying oven 10 agitation fan for the atmosphere in the drying furnace 10 in more uniform is provided.

【0061】この乾燥炉10に熱風供給ダクト12の一端が接続され、熱風供給ダクト12の他端に熱風発生源14が接続され、熱風発生源14に外気吸引ダクト18 [0061] One end of the hot air supply duct 12 to the drying furnace 10 is connected, a hot air source 14 is connected to the other end of the hot air supply duct 12, outside air suction duct 18 to the hot air source 14
の一端が接続され、外気吸引ダクト18の他端は開放されている。 The one end is connected, the other end of the outdoor air suction duct 18 is open.

【0062】熱風供給ダクト12は、熱風(熱風発生源14により加熱された外気)を乾燥炉10内へ供給するものである。 [0062] hot air supply duct 12 is for supplying hot air (outside air which is heated by hot air source 14) into the drying furnace 10. 外気吸引ダクト18は外気を熱風発生源1 Outside air suction duct 18 is a hot air source 1 outside air
4へ送るためのものであり、熱風発生源14は外気を加熱するためのもので、具体的手段としてバ−ナが採用されている。 Is intended for delivery to 4, the hot air source 14 is used to heat the outside air, Ba as a specific means - Na is employed.

【0063】外気吸引ダクト18には送風ファン16が設けられており、送風ファン16は外気を外気吸引ダクト18に吸引するとともに、外気吸引ダクト18内に吸引された外気を熱風発生源14へ送るほか、熱風を乾燥炉10内へ供給する機能を備えており、送風ファン16 [0063] The outside air suction duct 18 and blower fan 16 is provided, and sends the blower fan 16 outside air sucks in the outside air suction duct 18, the outside air sucked into the outdoor air suction duct 18 to the hot air source 14 in addition, provided with a function to supply hot air into the drying furnace 10, the blower fan 16
は後述する熱風の供給量を制御する風量制御手段32の一部を構成している。 Constitutes a part of the air volume control means 32 for controlling the supply of hot air to be described later.

【0064】送風ファン16が設けられた外気吸引ダクト18の上流側には、外気の乾球温度(以下、単に外気温度という)を測定するための外気温度センサ20と外気の相対湿度(以下、単に外気相対湿度という)を測定するための外気湿度センサ22が設けられている。 [0064] the upstream side of the outdoor air suction duct 18 to the blower fan 16 is provided, outside air dry bulb temperature (hereinafter, simply referred to as the outside air temperature) outside air temperature sensor 20 and the ambient air relative humidity to measure (hereinafter, simply outdoor air humidity sensor 22 for measuring) of outside air relative humidity is provided.

【0065】外気温度センサ20と外気相対湿度センサ22は、測定された外気温度と外気相対湿度を別に設けられた演算手段24に伝達できるように、演算手段24 [0065] the outside air temperature sensor 20 and the ambient air relative humidity sensor 22, the measured outside air temperature and outdoor air relative humidity so that it can be transmitted to the calculator 24 which is provided separately, the arithmetic means 24
に接続されている。 It is connected to the. なお、外気吸引ダクト18に設けられた両センサ20、22のさらに上流側に外気用ダンパを設ければ、外気用ダンパの開閉により外気の吸引量を制御することができる。 Incidentally, by providing the outside air damper further upstream side of the both sensors 20 and 22 provided in the outside air suction duct 18, it is possible to control the outside air suction amount by opening and closing of the outside air damper.

【0066】(演算手段)演算手段24は、乾燥に最適な熱風の目標の乾球温度(以下、単に目標温度という) [0066] (arithmetic means) calculating unit 24, the optimum hot goal of dry-bulb temperature in the drying (hereinafter, simply referred to as the target temperature)
を求めるほか、目標温度に基づいて後述する加熱制御手段26を制御する機能を有するものである。 Besides seeking, it has a function of controlling the heating control means 26 which will be described later, based on the target temperature. そして、演算手段24には、乾燥炉10内の湿球温度を予め設定した設定湿球温度のデータが格納されているほか、乾燥炉10内の設定湿球温度、測定された外気温度と外気相対湿度により熱風の目標温度を求めるためのプログラムが格納されている。 Then, the arithmetic unit 24, in addition to setting the wet-bulb temperature of the data set the wet-bulb temperature in advance of the drying furnace 10 is stored, set the wet-bulb temperature of the drying oven 10, the measured outside air temperature and the outside air program for calculating the target temperature of the hot air is stored by the relative humidity.

【0067】熱風の目標温度を演算手段24により求めるプログラムは、図4に示される湿度図表に基づいて以下の要素を求める手順から構成されている。 [0067] Programs for determining by calculation means 24 the target temperature of the hot air, and a procedure for obtaining the following elements based on the psychrometric chart shown in FIG. 乾燥炉10内の設定湿球温度に対応する相対湿度10 Relative humidity 10 corresponding to the set wet-bulb temperature of the drying oven 10
0%における断熱冷却線。 Adiabatic cooling line at 0%. 測定された外気温度および外気相対湿度における絶対湿度(kg/kg)。 The measured ambient temperature and the absolute humidity in the ambient air relative humidity (kg / kg). 乾燥炉10内の設定湿球温度と相対湿度100%における断熱冷却線と、測定された外気温度および外気相対湿度における絶対湿度(kg/kg)との交点における温度(目標温度)。 Setting the drying furnace 10 wet bulb temperature and the adiabatic cooling line in the relative humidity of 100% and a temperature at the intersection of the absolute humidity in the measured outside air temperature and outdoor air relative humidity (kg / kg) (target temperature).

【0068】この湿度図表に基づいて、乾燥炉10内の設定湿球温度、測定された外気温度および外気相対湿度とにより目標温度を求める意図は、とくに恒率乾燥期間における窯業成形物の変形や亀裂の抑制を図るため、熱風の温度制御により乾燥炉10内の湿球温度の制御を図るためである。 [0068] Based on the psychrometric chart, setting wet bulb temperature of the drying oven 10, intended to determine the target temperature by the measured outside air temperature and the outdoor air relative humidity, Ya especially deformation of ceramic moldings in the constant rate drying period order to suppress crack, is order to control the wet-bulb temperature in the drying furnace 10 by controlling the temperature of hot air.

【0069】(加熱制御手段)加熱制御手段26は、先に述べた演算手段24に接続されるとともに、熱風発生源14と接続されており、演算手段24により求められた熱風の目標温度に基づいて熱風発生源14の外気に対する加熱を制御するためのものである。 [0069] (heating control means) heating control means 26 is connected to the calculating means 24 as described above, is connected to a hot air source 14, based on the target temperature of the hot air obtained by the calculating means 24 Te is for controlling the heating of the outside air hot air source 14.

【0070】したがって、熱風発生源14は加熱制御手段26の制御を受けつつ外気を加熱するが、外気を加熱して得られた熱風の温度が目標温度となるまで外気を加熱する。 [0070] Thus, although the hot air source 14 to heat the outside air while under the control of the heating control means 26, the temperature of the hot air obtained by heating the outside air to heat the outside air until the target temperature. この実施の形態では、熱風発生源14による外気の加熱温度の正確性をより高めるために、熱風の温度を測定する熱風温度センサ34が、熱風供給ダクト12 In this embodiment, in order to improve the accuracy of the outside air heating temperature by the hot air source 14, a hot air temperature sensor 34 for measuring the temperature of the hot air, hot air supply duct 12
に設けられ、熱風温度センサ34は加熱制御手段26に接続されている。 Provided, hot-air temperature sensor 34 is connected to the heating control means 26.

【0071】したがって、熱風温度センサ34により測定された熱風の温度(以下、単に熱風温度という)は加熱制御手段26へ伝達され、測定された熱風温度と熱風の目標温度が比較され、その結果により熱風発生源14 [0071] Thus, the hot air temperature sensor 34 by the measured hot air temperature (hereinafter, simply referred to as hot air temperature) is transmitted to the heating control means 26, the target temperature of the measured temperature of hot air and hot air are compared, the result hot air source 14
に対する制御を行うので、熱風の温度制御が極めて正確に行われる。 Since the control for the temperature control of the hot air is very precisely performed.

【0072】(風量制御手段)一方、乾燥炉10内の温度を測定するための炉内温度センサ28が乾燥炉10に設けられている。 [0072] (air volume control means) Meanwhile, furnace temperature sensor 28 for measuring the temperature of the drying oven 10 is provided in the drying oven 10. そして、炉内温度センサ28は測定された炉内の温度(以下、単に炉内温度という)を別に設けられた送風用制御器30に伝達できるよう送風用制御器30に接続されている。 The furnace temperature sensor 28 is the measured temperature in the furnace (hereinafter simply referred to as the furnace temperature) is connected to the blower control unit 30 so that the can be transmitted to blower controller 30 which is provided separately. 送風用制御器30は、外気吸引ダクト18に設けられた送風ファン16の運転を制御するためのものであり、送風用制御器30と送風ファン16により風量制御手段32が構成される。 Blowing controller 30 is for controlling the operation of the blower fan 16 provided in the outside air suction duct 18, air volume control means 32 is constituted by the blast controller 30 and the blower fan 16.

【0073】送風用制御器30を詳しく述べると、炉内温度センサ28により測定された炉内温度と予め設定された乾燥炉10内の設定温度(以下、単に炉内設定温度という)との比較が送風用制御器30により行われ、炉内温度が炉内設定温度よりも高い場合は、送風ファン1 [0073] Comparison of the details the blast controller 30, set temperature of the preset drying oven 10 and measured by furnace temperature sensor 28 furnace temperature (hereinafter, simply referred furnace set temperature) and There is performed by blowing controller 30, when the furnace temperature is higher than the furnace set temperature, the blower fan 1
6による乾燥炉10への熱風の供給量を減少させ、一方、炉内温度が炉内設定温度よりも低い場合は、送風ファン16による熱風の供給量を増大させるように送風用制御器30により送風ファン16の運転を制御し、乾燥炉10内の温度を炉内設定温度に保つように図られている。 6 reduces the supply amount of hot air into the drying furnace 10 by, on the other hand, if the furnace temperature is lower than the furnace set temperature, the blowing controller 30 to increase the supply amount of hot air by the blower fan 16 It controls the operation of the blower fan 16, has been attempted to keep the temperature of the drying oven 10 into the furnace set temperature.

【0074】送風ファン16と送風用制御器30からなる風量制御手段32の目的は、とくに恒率乾燥期間における窯業成形物の変形や亀裂を抑制しつつ、熱風の供給量の制御により乾燥炉内の温度の制御を図ることにある。 [0074] The purpose of the air volume control means 32 for the blower fan 16 to consist of blowing controller 30, particularly while suppressing deformation and cracking of the ceramic molded product at constant rate drying period, drying oven by controlling the supply amount of hot air in possible to control the temperature of the.

【0075】なお、この実施の形態において予め設定される炉内設定温度は、窯業成形物の乾燥時間をより短縮化するために、恒率乾燥期間においては経時的に上昇するように設定されており、炉内設定温度のデータは送風用制御器30に格納される。 [0075] Incidentally, the furnace set temperature set in advance in this embodiment, in order to shorten the drying time of the ceramic moldings, in the constant rate drying period is set to over time increase cage, the data of the in-furnace set temperature is stored in the blower controller 30.

【0076】また、炉内設定温度を経時的に上昇するように設定することにより、温度上昇に伴って窯業成形物に含まれる水分が低下して窯業成形物の強度が増加することから、乾燥に伴う著しい収縮の差による変形や亀裂の抑制を図ることができる。 [0076] Further, by setting the furnace temperature setting to increased over time, since the strength of the ceramic molded product increases with increasing temperature and reduced moisture contained in the ceramic molded product, dried it is possible to deformation and cracking of the suppression due to the difference in significant shrinkage due to.

【0077】(排気ダクト)乾燥炉10内の空気を排出するために乾燥炉10に排気ダクト36が設けられ、排気量を調節する排気ダンパ38が排気ダクト36に設けられている。 [0077] (exhaust duct) the exhaust duct 36 to the drying furnace 10 in order to discharge the air in the drying oven 10 is provided, an exhaust damper 38 to adjust the exhaust volume is provided in the exhaust duct 36. 一方、乾燥炉10内に炉内圧力センサ40 On the other hand, inner pressure sensor 40 into a drying oven 10
が設けられ、炉内圧力センサ40により測定された乾燥炉10内の圧力に応じて排気ダンパ38の開閉を制御し、排気を図るように構成されている。 It is provided to control the opening and closing of the exhaust damper 38 in accordance with the pressure of the drying furnace 10 which is determined by the furnace pressure sensor 40 is configured to achieve an exhaust.

【0078】排気ダンパ38の開閉制御により乾燥炉1 [0078] drying furnace 1 by the opening and closing control of the exhaust damper 38
0内の圧力を調整する目的は、乾燥炉10内の圧力が高くなると、熱風の乾燥炉10への供給が阻害されるほか、乾燥炉10の内壁が物理的損傷を受けるおそれのあることに鑑み、乾燥炉10内への熱風の供給を安定して行うことと併せて乾燥炉10の内壁の物理的損傷を防止することにある。 The purpose of adjusting the pressure in the 0, the pressure in the drying furnace 10 is increased, in addition to supply to the drying furnace 10 of the hot air is inhibited, that the inner wall of the drying oven 10 is at risk of undergoing physical damage in view, it is to prevent physical damage to the inner wall of the stable drying furnace 10 together with that carried out the supply of hot air into the drying furnace 10.

【0079】次に、実施の形態その1に係る窯業成形物の乾燥装置の制御の説明と併せてその乾燥方法の制御について説明する。 Next, together with the description of the control of the drying apparatus of the ceramic molded product according to the part 1 of the embodiment will be described control of the drying process. この実施の形態の乾燥炉10内の湿球温度の制御については、外気温度センサ20により測定された外気温度と、外気湿度センサ22により測定された外気相対湿度と、予め設定された乾燥炉10内の設定湿球温度とから演算手段24により熱風の目標温度が求められ、目標温度に基づいて加熱制御手段26を制御させ、熱風発生源14による外気の加熱が制御される。 Control of wet-bulb temperature of the drying oven 10 of the present embodiment, the outside air temperature measured by the outside air temperature sensor 20, and the outside air relative humidity measured by the outdoor air humidity sensor 22, a drying furnace 10 which is set in advance the target temperature of the hot air by the arithmetic unit 24 from the setting wet-bulb temperature and the internal is obtained, to control the heating control means 26 based on the target temperature, outside air heating by hot air source 14 is controlled.

【0080】この熱風の温度制御による乾燥炉10内の湿球温度の制御は、窯業成形物の乾燥時における変形および亀裂を防止するために有効である。 [0080] Control of wet-bulb temperature of the drying furnace 10 with temperature control of the hot air is effective to prevent the deformation and cracking during the drying of the ceramic molded product. 未乾燥の窯業成形物は水分を含んだ湿潤なものであるから、窯業成形物の温度は、窯業成形物の周囲の雰囲気の湿球温度(温度計に湿ったガ−ゼを付けて測定した温度)とほぼ等しく扱うことができる。 Since undried ceramic molded product are those wetting containing water, the temperature of the ceramic moldings, wet bulb temperature of the ambient atmosphere of the ceramic molding (thermometer wet gas - was measured with a zero temperature) and can be handled substantially equal.

【0081】そこで、加熱期間を経過して恒率乾燥期間における窯業成形物の温度と、恒率乾燥期間における乾燥炉10内の湿球温度を等しく保つことができると、熱風の熱は水分の蒸発にのみ使用され、適切な乾燥速度で窯業成形物を乾燥させることができる。 [0081] Therefore, the temperature of the ceramic molding in the constant rate drying period elapsed heating period, when it is possible to maintain equal wet-bulb temperature of the drying oven 10 at constant rate drying period, the hot air heat water is used only for evaporation, it is possible to dry the ceramic molded product at a suitable drying rate. したがって、窯業成形物の一部に急激な乾燥や窯業成形物の表面への結露が発生することなく、恒率乾燥期間における窯業成形物の変形や亀裂を抑制できる。 Therefore, without condensation on the surface of the rapid drying and ceramics molded to a portion of ceramic molded product occurs, it is possible to suppress the deformation and cracking of the ceramic molding at the constant rate drying period.

【0082】ほぼ密閉された乾燥炉10内において、熱風が窯業成形物の乾燥に使用されても近似的に断熱冷却され、熱風が断熱冷却される場合、断熱冷却の過程において熱風の湿球温度が変化しない。 [0082] In substantially sealed drying oven 10, hot air is also used for drying the ceramic molded product is approximately adiabatic cooling, if hot air is adiabatically cooled, wet-bulb temperature of hot air in the process of adiabatic cooling There does not change.

【0083】そして、乾燥炉10内の湿球温度が設定湿球温度に維持されるためには、乾燥炉10内の設定湿球温度に対応する断熱冷却線上に位置するように熱風の目標温度を求め、求められた目標温度となるように外気を加熱すればよい。 [0083] Then, in order to wet-bulb temperature of the drying oven 10 is maintained at the set wet-bulb temperature, the target temperature of hot air so as to be positioned adiabatic cooling line corresponding to the set wet-bulb temperature of the drying oven 10 look, may be heated outside air so that the determined target temperature.

【0084】したがって、目標温度の加熱を乾燥炉10 [0084] Thus, drying furnace 10 to heat the target temperature
内に供給し、乾燥炉10内において熱風が乾燥に使用されても、乾燥炉10内の湿球温度は設定湿球温度と同じに維持され、また、乾燥炉10内の湿球温度と窯業成形物の温度が一致するので、恒率乾燥期間において窯業成形物の乾燥は安定して進行する。 Supplied within, even hot air in the drying oven 10 is used in dry, wet-bulb temperature of the drying oven 10 is maintained the same as setting the wet-bulb temperature, also a wet bulb temperature of the drying oven 10 Ceramic since the temperature of the molding is matched, drying of the ceramic molding at the constant rate drying period proceeds stably.

【0085】一方、乾燥炉10内の温度制御は、熱風の供給量を制御することにより行われる。 [0085] On the other hand, the temperature control of the drying oven 10 is performed by controlling the supply amount of hot air. つまり、乾燥炉10内の温度が熱風の温度より低い場合、一定の温度の熱風であっても、供給される熱風の供給量を増大させると、供給量に応じて乾燥炉10内の温度は上昇する現象を利用するものである。 That is, when the temperature of the drying furnace 10 is lower than the temperature of the hot air, even in hot air at a constant temperature, increasing the supply amount of hot air supplied, the temperature of the drying furnace 10 in accordance with the supply amount advantage of the phenomenon to rise.

【0086】この実施の形態における窯業成形物の乾燥の制御の具体例は、以下のようなプログラムに基づいて行った。 [0086] Specific examples of the control of the drying of the ceramic molded product in this embodiment was performed based on the following program. 加熱期間を約2時間とし、この期間で窯業成形物の温度が35℃から45℃まで上昇するように乾燥炉10内の湿球温度を35℃から45℃に上昇させる設定とした。 The heating period of about 2 hours, was set to increase the wet-bulb temperature of the drying furnace 10 so that the temperature of the ceramic molded product at this time rises to 45 ° C. from 35 ° C. to 45 ° C. from 35 ° C..

【0087】次に、恒率乾燥期間を約8時間とし、この期間の設定湿球温度を45℃とし、炉内温度を47℃から68℃まで段階的に上昇するように設定した。 [0087] Next, the constant rate drying period of about 8 hours, the setting wet-bulb temperature of this period and 45 ° C., was set to stepwise increase the furnace temperature to 68 ° C. from 47 ° C.. 減率乾燥期間を約4時間とし、この期間の設定湿球温度についても45℃とする一方、炉内温度を68℃から80℃に上昇させ、温度80℃で約2時間の保持時間設定した(図5を参照)。 The falling rate drying period of about 4 hours, this while the 45 ° C. also set wet bulb periods, increasing the furnace temperature from 68 ° C. to 80 ° C., were set retention time of about 2 hours at a temperature 80 ° C. (see Figure 5).

【0088】この乾燥における外気温度は35℃、外気の相対湿度は60%であったことから、乾燥炉10内の設定湿球温度が45℃であることを併せ、演算手段24 [0088] the outside air temperature is 35 ° C. in the drying is ambient air relative humidity was 60%, together the setting wet-bulb temperature of the drying oven 10 is 45 ° C., computing means 24
により熱風の目標温度は145℃であった(図4を参照)。 The target temperature of hot air was 145 ° C. (refer to FIG. 4).

【0089】以上の設定および条件に基づいて窯業成形物の乾燥を行ったところ、乾燥された窯業成形物において乾燥による変形や亀裂はほとんど発生しなかった。 [0089] Based on the above settings and conditions were subjected to dry the ceramic molded product, deformation or cracking due to drying in the dried ceramic moldings hardly occur. すなわち、乾燥炉10内の設定湿球温度、測定された外気温度と外気相対湿度とにより、乾燥炉10内の設定湿球温度に対応する熱風の目標温度が求められ、外気を目標温度まで加熱し、外気の加熱により得られた熱風が乾燥炉10内に供給され、乾燥炉10内に供給された目標温度の熱風は乾燥に使用されても湿球温度は変化することなく、設定湿球温度に保たれることにより、窯業成形物の温度と乾燥炉10内の湿球温度が一致する状態を維持し、窯業成形物の一部に急激な乾燥や表面への結露が生じないためである。 In other words, setting the wet bulb temperature of the drying oven 10, by a measured outside air temperature and the ambient relative humidity, the drying oven target temperature of the corresponding hot air set wet-bulb temperature of 10 is obtained, the outside air to the target temperature heating and, hot air obtained by the outside air heating is supplied to the drying furnace 10, hot air is supplied to the drying furnace 10 the target temperature wet bulb be used for drying unchanged, set wet bulb by being kept at a temperature to maintain the state in which the temperature and the wet-bulb temperature of the drying oven 10 of the ceramic molded product match, because the condensation of the rapid drying and surface portion of the ceramic molded product does not occur is there.

【0090】恒率乾燥期間における乾燥炉10内の設定湿球温度と窯業成形物の温度を常に一致させる制御であるから、窯業成形物の種類に応じて設定湿球温度を自由に変更しても窯業成形物の温度が設定湿球温度と一致するように熱風の目標温度が求められ、従来のように温度と相対湿度の関係を考慮する必要もないので、乾燥炉1 [0090] Since it is always controlled to match the set temperature wet bulb and ceramic moldings in a drying oven 10 in the constant rate drying period, and freely change the settings wet-bulb temperature according to the type of ceramic molded product since also the target temperature of the hot air is determined so that the temperature of the ceramic molded product matches the set wet-bulb temperature, require no consider the conventional relationship between the temperature and the relative humidity as a drying oven 1
0のオペレ−タによる乾燥の制御の変更が容易となった。 0 of operator - has become easy to change the control of the drying by motor.

【0091】併せて、乾燥炉10の湿度制御を熱風の供給量の制御により行うので、乾燥炉10内の温度を変動させても湿球温度が設定湿球温度に維持されていれば、 [0091] In addition, it is performed by controlling the supply amount of hot air and humidity control of the drying furnace 10, if it be wet-bulb temperature be varied the temperature of the drying oven 10 is maintained at the set wet-bulb temperature,
一定の範囲内において乾燥時間の変更の自由にでき、この実施の形態では乾燥時間が14時間に短縮することができた。 In a certain range can be freely changed in the drying time, the drying time in this embodiment could be shortened to 14 hours.

【0092】また、乾燥途中において外気温度や外気相対湿度の変動が生じても、演算手段24により、これらの変動に対応するように熱風の目標温度が求められ、目標温度に基づいて加熱制御手段26が制御されるので、 [0092] Further, even if variations in ambient temperature and ambient air relative humidity occur in the middle drying, the calculating means 24, the target temperature of the hot air is determined so as to correspond to these variations, the heating control means on the basis of the target temperature since 26 is controlled,
熱風発生源14による熱風の適切な加熱を行うことができる。 It is possible to perform an appropriate heating of hot air by the hot air source 14.

【0093】次に、実施の形態その2に係る窯業成形物の乾燥装置について説明する。 Next, a description will be given drying apparatus ceramic molded product according to the Part 2 of the embodiment. この実施の形態の乾燥装置においては、熱風温度センサ42と熱風湿度センサ4 The drying apparatus of this embodiment, the hot air temperature sensor 42 and the hot air humidity sensor 4
4が熱風供給ダクト12に設けられ、熱風温度センサ4 4 is provided in the hot air supply duct 12, the hot air temperature sensor 4
2により測定された熱風の温度(以下、単に熱風温度という)と熱風湿度センサ44により測定された熱風の相対湿度(以下、単に熱風相対湿度という)が演算手段4 Determined by 2 the hot air temperature (hereinafter, simply referred to as hot air temperature) measured hot air relative humidity by hot air humidity sensor 44 (hereinafter, simply referred to as hot air relative humidity) is operation means 4
6に伝達されるように設けられている点が、先の実施の形態と比較して異なる。 That is provided so as to be transmitted to 6 is different compared to the previous embodiments.

【0094】したがって、熱風温度は熱風温度センサ4 [0094] Thus, the hot air temperature is hot air temperature sensor 4
2により測定され、また、熱風相対湿度は熱風湿度センサ44により測定される。 Measured by 2, also hot air relative humidity is measured by a hot air humidity sensor 44. 測定された熱風温度と熱風相対湿度は演算手段46へ伝達され、演算手段46において熱風温度、熱風相対湿度および乾燥炉10内の設定湿球温度により熱風の目標温度が求められる。 The measured temperature of hot air and hot air relative humidity is transmitted to the computing unit 46, the hot air temperature in the operation unit 46, the target temperature of the hot air is determined by the setting the wet-bulb temperature of the hot relative humidity and drying oven 10. 求められた目標温度に基づいて加熱制御手段26が熱風発生源14 Heating control means 26 based on the determined target temperature hot air source 14
による外気の加熱を制御する。 To control the outside air heated by.

【0095】この実施の形態においては、熱風供給ダクト12の乾燥炉10寄りに熱風温度センサ42が設けられており、熱風が乾燥炉10へ供給される直前で熱風温度を監視することになり、加熱制御手段26による熱風発生源14の加熱制御は、熱風の目標温度に対するより繊細な制御とすることができるので、乾燥炉10内へ供給される熱風の温度制御をより正確に行うことができる。 [0095] In this embodiment is a hot air temperature sensor 42 is provided in the drying furnace 10 side of the hot air supply duct 12, it will be to monitor the temperature of hot air just before the hot air is supplied into the drying furnace 10, heating control of the hot air source 14 by the heating control means 26 can be the delicate control over the target temperature of hot air, it is possible to control the temperature of the hot air to be supplied into the drying furnace 10 more accurately .

【0096】次に、実施の形態その3に係る窯業成形物の乾燥装置について説明する。 Next, a description will be given drying apparatus ceramic molded product according to the their third embodiment. この実施の形態の乾燥装置は、熱風供給ダクト12に熱風用ダンパ50が設けられ、実施の形態その1における送風用制御器30に代えて開閉用制御器52が設けられている。 Drying device of this embodiment, the hot air damper 50 provided in the hot air supply duct 12, the opening and closing controller 52 is provided instead of the blower controller 30 in accordance with the first embodiment. 開閉用制御器5 Opening and closing controller 5
2は、炉内温度センサ54により測定された炉内温度を開閉用制御器52に伝達できるように炉内温度センサ5 2, furnace temperature sensor 5 so as to be able to transmit the furnace temperature measured by the furnace temperature sensor 54 to the opening and closing controller 52
4と接続されているほか、熱風用ダンパ50の開閉を制御するために熱風用ダンパ50とも接続されている。 4 with other connected is also connected to the hot air damper 50 to control the opening and closing of the hot air damper 50.

【0097】また、熱風用ダンパ50により分岐される熱風の一部を外気吸引ダクト18に循環させる循環ダクト56が設けられており、循環ダクト56は熱風用ダンパ50から外気温度センサ20および外気湿度センサ2 [0097] Further, the circulation duct 56 for circulating a portion of the hot air is branched into the outside air suction duct 18 is provided with hot air damper 50, the circulation duct 56 is outside air temperature sensor 20 and the ambient humidity from the hot air damper 50 sensor 2
2の上流側の外気吸引ダクト18に向けて接続されている。 Connected toward the second upstream side of the outdoor air suction duct 18.

【0098】開閉用制御器52は、炉内温度センサ54 [0098] opening and closing controller 52, furnace temperature sensor 54
により測定された炉内温度の伝達を受け、炉内温度に応じて熱風用ダンパ50の開閉を制御して熱風の供給量を制御することができる。 Receiving a transmission of the measured furnace temperature, it is possible to control the supply amount of hot air by controlling the opening and closing of the hot air damper 50 in response to furnace temperature. したがって、この実施の形態における風量制御手段48は開閉用制御器52と熱風用ダンパ50から構成される。 Therefore, air volume control means 48 in this embodiment is composed of the opening and closing controller 52 and the hot air damper 50. この実施の形態において、外気吸引ダクト18に設けられた送風ファン58は一定の回転数を保って運転されるものであり、熱風の供給量を炉内温度に基づいて制御する風量制御手段48を構成するものではない。 In this embodiment, the blower fan 58 provided in the outside air suction duct 18 is intended to be operated while maintaining a constant rotational speed, the air volume control means 48 for controlling based on the supply amount of hot air into the furnace temperature It does not constitute.

【0099】この実施の形態によれば、送風ファン58 [0099] According to this embodiment, the blower fan 58
により外気吸引ダクト18に吸引された外気は、熱風発生源14により加熱される。 Outside air sucked to the air suction duct 18 is heated by hot air source 14 by. このときの熱風発生源14 Hot air source 14 at this time
による加熱制御は、実施の形態その1と同様に、演算手段24により乾燥炉10内の設定湿球温度、測定された外気温度、外気相対湿度とから熱風の目標温度が求められ、求められた熱風の目標温度になるように熱風発生源14により外気が加熱されるが、熱風発生源14は加熱制御手段26により制御されるものである。 Heating control by, as in the embodiment No. 1 of the embodiment, setting the wet bulb temperature in the drying furnace 10 by calculating means 24, the measured outside air temperature, the target temperature of the hot air from the outside air relative humidity is required, the obtained Although outside air is heated by hot air source 14 so that the target temperature of the hot air, a hot air source 14 and is controlled by the heating control means 26.

【0100】一方、乾燥炉10内の温度制御は風量制御手段48による熱風の供給量の制御により行われるが、 [0100] On the other hand, the temperature control of the drying oven 10 is performed by control of the hot air supply amount of the air volume control means 48,
風量制御手段48は熱風用ダンパ50と開閉用制御器5 Air volume control means 48 controls opening and closing the hot air damper 50 5
2から構成されているので、炉内温度センサ54により測定された炉内温度は開閉用制御器52へ伝達され、開閉用制御器52は炉内温度に応じて熱風用ダンパ50の開閉を制御して、乾燥炉10内へ供給する熱風の供給量を制御する。 Because it is composed of 2, the furnace temperature measured by furnace temperature sensor 54 is transmitted to the opening and closing controller 52, opening and closing controller 52 controls the opening and closing of the hot air damper 50 in response to furnace temperature and controls the supply amount of hot air supplied into the drying furnace 10.

【0101】そして、熱風用ダンパ50により分岐された熱風の一部は、乾燥炉10内へ供給する必要がないので、循環ダクト56を通じて外気吸引ダクト18へ回収される。 [0102] Then, part of the hot air which is branched by a hot air damper 50, since it is not necessary to supply into the drying furnace 10, is recovered to the outside air suction duct 18 through the circulation duct 56. 外気吸引ダクト18へ回収された熱風は外気と混合されて熱風発生源14へ送られ、再び加熱されて熱風として再利用されるので、熱風発生源14による外気への加熱量が低減され、乾燥装置の省エネルギ−化を図ることができる。 By hot air recovered to the outside air suction duct 18 is fed is mixed with outside air to the hot air source 14, is because it is reused, the amount of heat to the outside air by a hot air source 14 is reduced as the hot air is heated again, dried it can be achieved reduction - energy conservation of the apparatus.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】実施の形態その1に係る窯業成形物の乾燥装置の概略図である。 1 is a schematic view of a drying apparatus embodiment Ceramic moldings according to Part 1.

【図2】実施の形態その2に係る窯業成形物の乾燥装置の概略図である。 Figure 2 is a schematic view of a drying apparatus embodiment Ceramic moldings according to Part 2.

【図3】実施の形態その3に係る窯業成形物の乾燥装置の概略図である。 Figure 3 is a schematic view of a drying apparatus embodiment Ceramic moldings according to Part 3.

【図4】湿球温度と温度制御との関係を示す説明図である。 4 is an explanatory diagram showing the relationship between the wet-bulb temperature control.

【図5】実施の形態その1に係る窯業成形物の乾燥装置による乾燥特性を示すグラフ、である。 Figure 5 is a graph showing drying characteristics due to drying apparatus embodiment Ceramic moldings according to the 1, a.

【図6】従来例の窯業成形物の乾燥装置の概略図である。 6 is a schematic view of a drying apparatus in the prior art ceramic molded product.

【符号の説明】 DESCRIPTION OF SYMBOLS

10 乾燥炉 12 熱風供給ダクト 14 熱風発生源 16 送風ファン 18 外気吸引ダクト 20 外気温度センサ 22 外気湿度センサ 24 演算手段 26 加熱制御手段 28 炉内温度センサ 30 送風用制御器 32 風量制御手段 34 熱風温度センサ 36 排気ダクト 38 排気ダンパ 40 炉内圧力センサ 42 熱風温度センサ 44 熱風湿度センサ 46 演算手段 48 風量制御手段 50 熱風用ダンパ 52 開閉用制御器 54 炉内温度センサ 56 循環ダクト 58 送風ファン 10 drying oven 12 hot air supply duct 14 the hot air source 16 blower fan 18 outside air suction duct 20 outside air temperature sensor 22 outside air humidity sensor 24 calculation means 26 heating control means 28 furnace temperature sensor 30 blower controller 32 air volume control means 34 hot air temperature sensor 36 exhaust duct 38 exhaust damper 40 furnace pressure sensor 42 hot air temperature sensor 44 hot-air humidity sensor 46 calculation means 48 air volume control means 50 hot air damper 52 for opening and closing controller 54 furnace temperature sensor 56 circulation duct 58 the blower fan

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl. 7識別記号 FI テーマコート゛(参考) F27D 7/06 F27D 7/06 C ────────────────────────────────────────────────── ─── of the front page continued (51) Int.Cl. 7 identification mark FI theme Court Bu (reference) F27D 7/06 F27D 7/06 C

Claims (6)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 湿式成形された窯業成形物を乾燥炉に収容し、外気を加熱して熱風を得るとともに熱風を乾燥炉内へ供給し、供給された熱風により窯業成形物を乾燥させる窯業成形物の乾燥方法において、 乾燥炉内の設定湿球温度と炉内設定温度を予め設定し、 外気の温度と相対湿度を測定して外気温度と外気相対湿度を求め、 乾燥炉内の設定湿球温度、外気温度および外気相対湿度に基づいて乾燥炉内に供給する熱風の目標温度を求め、 求められた熱風の目標温度となるように外気を加熱し、 外気を加熱して得られた熱風を乾燥炉へ供給し、 他方、乾燥炉内の温度を測定して炉内温度を求め、炉内設定温度と測定された炉内温度の差に基づいて乾燥炉内へ供給する熱風の供給量を制御することを特徴とする窯業成形物の乾燥方法。 The method according to claim 1] Ceramic moldings which is wet-molded housing in a drying furnace, ceramic supplies hot air to the drying oven with obtaining hot air to heat the ambient air to dry the ceramic molded product by the supplied hot air molding in the drying method of an object, the set wet-bulb temperature and the furnace set temperature in the drying furnace set in advance, it obtains the outside air temperature and the ambient relative humidity by measuring the ambient air temperature and relative humidity, set in the drying furnace wet bulb temperature, obtains a target temperature of hot air supplied to the drying oven on the basis of the outside air temperature and the outdoor air relative humidity, to heat the outside air so that the target temperature of the obtained hot air, hot air obtained by heating the outside air supplied to the drying furnace, while seeking furnace temperature by measuring the temperature in the drying furnace, the supply amount of hot air supplied into the drying furnace based on the difference between the measured and the furnace set temperature furnace temperature drying methods ceramic molded article and controlling.
  2. 【請求項2】 湿式成形された窯業成形物を乾燥炉に収容し、外気を加熱して熱風を得るとともに熱風を乾燥炉内へ供給し、供給された熱風により窯業成形物を乾燥させる窯業成形物の乾燥方法において、 乾燥炉内の設定湿球温度と炉内設定温度を予め設定し、 乾燥炉へ供給される熱風の温度と相対湿度を測定して熱風温度と熱風相対湿度を求め、 乾燥炉内の設定湿球温度、熱風温度および熱風相対湿度に基づいて乾燥炉内に供給する熱風の目標温度を求め、 求められた熱風の目標温度となるように外気を加熱し、 外気を加熱して得られた熱風を乾燥炉内へ供給し、 他方、乾燥炉内の温度を測定して炉内温度を求め、炉内設定温度と測定された炉内温度の差に基づいて乾燥炉内へ供給する熱風の供給量を制御することを特徴とする窯業成形 2. A housing the wet molded ceramic molded product drying furnace, ceramic supplies hot air to the drying oven with obtaining hot air to heat the ambient air to dry the ceramic molded product by the supplied hot air molding in the drying method of an object, the set wet-bulb temperature and the furnace set temperature in the drying furnace set in advance, it obtains a hot air temperature and hot air relative humidity by measuring the temperature and relative humidity of the hot air supplied to the drying oven, drying setting wet-bulb temperature in the furnace to obtain the target temperature of hot air supplied to the drying oven on the basis of hot air temperature and hot air relative humidity, to heat the outside air so that the target temperature of the obtained hot air, heated outside air the hot air obtained Te supplied into the drying furnace, while the temperature in the drying oven to measure sought furnace temperature, based on the difference in the furnace was measured furnace temperature setting temperature into the drying furnace ceramic molding and controlling the supply amount of hot air supplied 物の乾燥方法。 Drying method of things.
  3. 【請求項3】 湿式成形された窯業成形物を収容する乾燥炉が備えられ、乾燥炉に接続された熱風供給ダクトに熱風発生源が設けられ、熱風発生源に外気吸引ダクトが接続され、乾燥炉に排気ダクトが接続された窯業成形物の乾燥装置において、 外気の温度を測定する外気温度センサと外気の相対湿度を測定する外気湿度センサが外気吸引ダクトに設けられ、 外気温度センサにより測定された外気温度と外気温度センサにより測定された外気相対湿度により、予め設定された乾燥炉内の設定湿球温度に対応する熱風の目標温度を求める演算手段が設けられ、 乾燥炉内へ供給される熱風の温度が目標温度となるように熱風発生源を制御する加熱制御手段が設けられ、 他方、乾燥炉に該乾燥炉内の温度を測定する炉内温度センサが設けられ、 炉 3. A drying furnace for accommodating the wet molded ceramic moldings is provided, the hot air source is provided to the connected hot air supply duct to the drying oven, the outside air suction duct is connected to a hot air source, dried the drying apparatus of ceramic moldings exhaust duct is connected to the furnace, outside air humidity sensor for measuring the outside air temperature sensor and the ambient relative humidity to measure the outside air temperature is provided in the outside air suction duct is measured by the outside air temperature sensor by the outdoor air relative humidity measured by the outdoor air temperature and the outside air temperature sensor, calculating means are provided to determine the target temperature of the hot air corresponding to the set wet-bulb temperature of the preset drying oven, it is fed into the drying furnace heating control means is provided that the temperature of the hot air to control the hot air source so that the target temperature, on the other hand, furnace temperature sensor for measuring the temperature of the drying oven is provided in the drying furnace, the furnace 温度センサにより測定された炉内温度と予め設定された炉内設定温度の差に基づいて乾燥炉内へ供給する熱風の供給量を制御する風量制御手段が設けられたことを特徴とする窯業成形物の乾燥装置。 Ceramic molding, characterized in that the air volume control means for controlling the supply amount of hot air supplied into the drying furnace based on the difference between the measured furnace temperature and a preset furnace set temperature by the temperature sensor is provided drying apparatus of thing.
  4. 【請求項4】 湿式成形された窯業成形物を収容する乾燥炉が備えられ、乾燥炉に接続された熱風供給ダクトに熱風発生源が設けられ、熱風発生源に外気吸引ダクトが接続され、乾燥炉に排気ダクトが接続された窯業成形物の乾燥装置において、 熱風の温度を測定する熱風温度センサと熱風の相対湿度を測定する熱風湿度センサが熱風供給ダクトに設けられ、 熱風温度センサにより測定された熱風温度と熱風湿度センサにより測定された熱風相対湿度とにより、予め設定された乾燥炉内の設定湿球温度に対応する熱風の目標温度を求める演算手段と、 乾燥炉内へ供給される熱風の温度が目標温度となるように熱風発生源を制御する加熱制御手段が設けられ、 他方、乾燥炉に該乾燥炉内の温度を測定する炉内温度センサが設けられ、 炉内温度 4. A drying furnace for accommodating the wet molded ceramic moldings is provided, the hot air source is provided to the connected hot air supply duct to the drying oven, the outside air suction duct is connected to a hot air source, dried the drying apparatus of ceramic moldings exhaust duct to the furnace is connected, a hot air humidity sensor for measuring the hot air temperature sensor and the relative humidity of the hot air to measure the temperature of hot air is provided in the hot air supply duct is measured by the hot air temperature sensor the hot air temperature and hot air humidity sensor by the measured hot air relative humidity, and calculating means for calculating a target temperature of the hot air corresponding to the set wet-bulb temperature of the preset drying oven, hot air is supplied into the drying furnace heating control means is provided that the temperature of the controls hot air source so that the target temperature, on the other hand, furnace temperature sensor for measuring the temperature of the drying oven is provided in the drying furnace, the furnace temperature ンサにより測定された炉内温度と予め設定された炉内設定温度の差に基づいて熱風の供給量を制御する風量制御手段が設けられたことを特徴とする窯業成形物の乾燥装置。 Drying device of ceramic molded product, wherein a flow rate control means for controlling the supply amount of hot air is provided on the basis of the difference between the measured furnace temperature and a preset furnace set temperature by capacitors.
  5. 【請求項5】 風量制御手段が、外気吸引ダクトに設けられた送風ファンと、炉内温度センサにより測定される炉内温度と炉内設定温度の差に基づいて送風ファンを制御する送風用制御器とからなることを特徴とする請求項3または4記載の窯業成形物の乾燥装置。 5. The air volume control means comprises a blower fan provided in the outdoor air suction duct, blowing control for controlling the blower fan based on the difference between the furnace temperature and furnace setting temperature measured by the furnace temperature sensor drying apparatus according to claim 3 or 4 ceramic molded article according to characterized in that it consists of a vessel.
  6. 【請求項6】 風量制御手段が、熱風供給ダクトに設けられ熱風用ダンパと、炉内温度センサにより測定される炉内温度と炉内設定温度との差に基づいて熱風用ダンパを開閉する開閉用制御器とからなり、 熱風用ダンパにより分岐された熱風の一部を外気吸引ダクトへ循環させる循環ダクトが設けられるとともに外気吸引ダクトに送風ファンが設けられたことを特徴とする請求項3または4記載の窯業成形物の乾燥装置。 6. The air volume control means, opening and closing of opening and closing the hot air damper provided in the hot air supply duct, a hot air damper on the basis of the difference between the furnace temperature and furnace setting temperature measured by the furnace temperature sensor consists of a use controller, according to claim 3 or, characterized in that the blower fan to the outside air suction duct is provided with circulation duct for circulating a portion of the hot air is branched into the outside air suction duct with hot air damper is provided 4 drying apparatus ceramic moldings according.
JP3309799A 1999-02-10 1999-02-10 Drying method and apparatus for ceramic moldings Active JP3455813B2 (en)