JP2000178540A - Antistatic agent for inorganic substance - Google Patents

Antistatic agent for inorganic substance

Info

Publication number
JP2000178540A
JP2000178540A JP36016898A JP36016898A JP2000178540A JP 2000178540 A JP2000178540 A JP 2000178540A JP 36016898 A JP36016898 A JP 36016898A JP 36016898 A JP36016898 A JP 36016898A JP 2000178540 A JP2000178540 A JP 2000178540A
Authority
JP
Japan
Prior art keywords
antistatic
inorganic substance
silane compound
treated
filler
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP36016898A
Other languages
Japanese (ja)
Inventor
Kanji Hayashi
寛治 林
Original Assignee
Altech Co Ltd
アルテック株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Altech Co Ltd, アルテック株式会社 filed Critical Altech Co Ltd
Priority to JP36016898A priority Critical patent/JP2000178540A/en
Publication of JP2000178540A publication Critical patent/JP2000178540A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To obtain a bleed-free antistatic agent by using as the constituent a silane compound containing a molecular chain of a specified structure having a terminal quaternary ammonium salt group. SOLUTION: This antistatic agent contains a silane compound represented by the formula: R-SiX3, wherein R is a molecular chain of a structure represented by the formula, having a terminal quaternary ammonium salt group. 100 wt.% inorganic substance such as silica or alumina is treated with the silane compound in an amount of 0.1-5 wt.% to form an antistatic functional layer on the surface, thus giving a modified inorganic substance excellent in compatibility with a solvent-soluble resin binder. The silane compound can be synthesized by the urethane reaction of γ-isocyanatopropyltriethoxysilane with a quaternary salt of 2-hydroxyethyl-N-dimethyl,N-ethylaminoeto sulfate. In the formula, R1 to R4 are each a 1-2C alkyl; and X is -OCH3 or -OC2H5.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【発明の属する技術分野】本発明は、無機物質に帯電防
止性を付与するための帯電防止処理剤に関するものであ
る。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an antistatic agent for imparting an antistatic property to an inorganic substance.

【0002】[0002]

【従来の技術】印刷インキ、塗料或いはプラスチック成
形材料への帯電防止性の付与は、一般には、帯電防止剤
の添加・練り込みなどである。このような方法で印刷イ
ンキ或いは塗料の樹脂バインダーに添加された帯電防止
剤は、その表面ブリード性によって、帯電防止性を発現
させるものであるが、このようにブリードにより帯電防
止性を付与すると、ブリードした帯電防止剤が印刷イン
キや塗料などの被着体に対する密着性阻害の要因となっ
ている場合が多く、品質を悪化させることから、印刷イ
ンキ、塗料等を用いる製品については、帯電防止対策が
十分にとられていないのが現状である。
2. Description of the Related Art In general, an antistatic property is imparted to a printing ink, a paint or a plastic molding material by adding or kneading an antistatic agent. The antistatic agent added to the resin binder of the printing ink or paint by such a method is one that expresses antistatic properties due to its surface bleeding property. Bleeded antistatic agents are often a factor in inhibiting adhesion to adherends such as printing inks and paints, which degrade the quality. At present, it is not enough.

【0003】[0003]

【発明が解決しようとする課題】本発明の課題は、シラ
ン化合物のシランカップリング性による無機物質表面と
の水素結合或いは、シロキサン結合などの化学反応で、
無機物質表面を改質させ、本発明に係るシラン化合物の
他端の4級アンモニウム塩基で無機物質表面に帯電防止
性を付与させようとするものであり、かつ、無機物質と
の化学結合によって、非ブリード性を有する帯電防止処
理剤を提供することである。
SUMMARY OF THE INVENTION An object of the present invention is to provide a chemical reaction such as a hydrogen bond or a siloxane bond with the surface of an inorganic substance due to the silane coupling property of a silane compound.
The surface of the inorganic substance is modified, the quaternary ammonium base at the other end of the silane compound according to the present invention is intended to impart antistatic properties to the surface of the inorganic substance, and by chemical bonding with the inorganic substance, An object of the present invention is to provide an antistatic treatment agent having non-bleeding properties.

【0004】[0004]

【課題を解決するための手段】上記課題を達成するため
の手段として、請求項1に記載の発明においては、無機
物質用帯電防止処理剤において、一般式R−SiX3
表すシラン化合物で、式2中Rは末端に4級アンモニウ
ム塩基を持つことを特徴とするものである。
Means for Solving the Problems As means for achieving the above object, in the invention according to claim 1, an antistatic treatment agent for inorganic substances is a silane compound represented by the general formula R-SiX 3 , In Formula 2, R has a quaternary ammonium base at the terminal.

【式2】 1,R2,R3,R4は、炭素数がC1〜C2のアルキル基
である。Xは−OCH3或いは−OC25である。
(Equation 2) R 1 , R 2 , R 3 , and R 4 are alkyl groups having 1 to 2 carbon atoms. X is -OCH 3 or -OC 2 H 5.

【0005】更に、請求項2に記載の発明においては、
帯電防止性無機物質において、請求項1記載のシラン化
合物により表面処理されたことを特徴とするものであ
る。
[0005] Further, in the invention according to claim 2,
An antistatic inorganic substance, which has been surface-treated with the silane compound according to claim 1.

【0006】更に、請求項3に記載の発明においては、
帯電防止性無機物質において、請求項2記載の無機物質
が酸化チタン又はシリカ又はアルミナ等を一例とする無
機充填物であることを特徴とするものである。
Further, in the invention according to claim 3,
In the antistatic inorganic substance, the inorganic substance according to claim 2 is an inorganic filler exemplified by titanium oxide, silica, alumina, or the like.

【0007】更に、請求項4に記載の発明においては、
帯電防止性印刷インキにおいて、請求項2又は3記載の
表面処理された帯電防止性無機物質を充填剤として作ら
れたことを特徴とするものである。
Further, in the invention according to claim 4,
An antistatic printing ink, characterized in that the surface treated antistatic inorganic substance according to claim 2 or 3 is used as a filler.

【0008】更に、請求項5に記載の発明においては、
帯電防止性塗料において、請求項2又は3記載の表面処
理された帯電防止性無機物質を充填剤として作られたこ
とを特徴とするものである。
Further, in the invention according to claim 5,
An antistatic paint, characterized in that the surface-treated antistatic inorganic substance according to claim 2 or 3 is used as a filler.

【0009】更に、請求項6に記載の発明においては、
帯電防止性プラスチック成形材料において、請求項2又
は3記載の帯電防止性無機物質を充填剤として作られた
ことを特徴とするものである。
Further, in the invention according to claim 6,
An antistatic plastic molding material, characterized in that the antistatic inorganic substance according to claim 2 or 3 is used as a filler.

【0010】[0010]

【発明の実施の形態】請求項1に記載の式1の末端に4
級アンモニウム塩基をもつ特殊なシラン化合物は、γ−
イソシアネートプロピルトリエトキシシラン(γ−isoc
yanatepropyl-triethoxysilan)と2−ハイドロキシエ
チル−Nジメチル、Nエチルアミノエトサルフェート4
級化塩(2-Hydroxyethyl-N-dimethyl, N-ethylamino-et
hosulfate quaternarysalt)とのウレタン反応で、比較
的容易に合成することができる。
BEST MODE FOR CARRYING OUT THE INVENTION
A special silane compound having a quaternary ammonium base is γ-
Isocyanatopropyltriethoxysilane (γ-isoc
yanatepropyl-triethoxysilan) and 2-hydroxyethyl-N-dimethyl, N-ethylaminoethosulfate 4
Graded salts (2-Hydroxyethyl-N-dimethyl, N-ethylamino-et
It can be synthesized relatively easily by urethane reaction with hosulfate quaternary salt.

【0011】また、本発明に係るシラン化合物は、ほと
んど無色透明な粘性液体で、水に不溶で、エステル系溶
剤、ケトン系溶剤、アルコール系溶剤に可溶である。一
方、水/IPAの混合溶剤には可溶である。
The silane compound according to the present invention is a viscous liquid which is almost colorless and transparent, insoluble in water, and soluble in ester solvents, ketone solvents and alcohol solvents. On the other hand, it is soluble in a mixed solvent of water / IPA.

【0012】従って、印刷インキや塗科などに使用され
る溶剤との親和性に優れることから、無機物質、例えば
酸化チタン、シリカ、アルミナなどの表面を本発明に係
るシラン化合物で改質処理することによって、上記溶剤
に可溶の樹脂バインダーとの親和性に極めて優れた無機
充填剤として改質することができる。
Accordingly, the surface of an inorganic substance such as titanium oxide, silica, alumina or the like is modified with the silane compound according to the present invention because of its excellent affinity with solvents used for printing inks and coatings. This makes it possible to modify the inorganic filler as an inorganic filler having an extremely good affinity for a resin binder soluble in the solvent.

【0013】また、他端に有する4級アンモニウム塩基
により、改質された無機充填物の表面には帯電防止性を
もつ機能層が形成される。改質無機充填物添加によって
作られる印刷インキ或いは塗料の塗布面は、表面へのブ
リードもなく、優れた帯電防止性をもつ印刷物或いは塗
装面とすることができる。
Further, a functional layer having antistatic properties is formed on the surface of the modified inorganic filler by the quaternary ammonium base at the other end. The coated surface of the printing ink or paint prepared by adding the modified inorganic filler can be a printed or coated surface having excellent antistatic properties without bleeding on the surface.

【0014】印刷インキ(白色)に使用される白色顔料
の酸化チタンは、予めシリカやアルミナ処理されたもの
を使用する。この白色顔科に対して、重量%で2%の本
シリカ化合物をIPA/水の混合比1/1の10%溶液
に調整したものを酸化チタンに添加し、充分攪拌したの
ち、約100℃、5〜10分間加熱乾燥することによ
り、酸化チタンの表面処理を行う。その後、酸化チタン
を微粉化して、印刷インキメジウムに添加可能な充填剤
に調整する。本発明で処理済酸化チタンと未処埋酸化チ
タンを個別に水中に投入すると、水中での沈殿分離の経
時変化は24時間後において、処理済酸化チタンには沈
殿分離は認められないが、未処理酸化チタンでは沈殿分
離することが認められた。このことは溶剤型印刷インキ
ばかりでなく、水性印刷インキの充填剤にも有用性をも
つものであることを示す。
As the white pigment titanium oxide used in the printing ink (white), one that has been previously treated with silica or alumina is used. To this white face, a 2% by weight silica compound prepared in a 10% solution having a mixing ratio of IPA / water of 1/1 was added to titanium oxide, and the mixture was sufficiently stirred. The surface treatment of titanium oxide is performed by heating and drying for 5 to 10 minutes. Thereafter, the titanium oxide is pulverized to prepare a filler that can be added to the printing ink medium. When the treated titanium oxide and the untreated titanium oxide are separately put into water according to the present invention, the sedimentation and separation in water with the lapse of time after 24 hours show no precipitation and separation in the treated titanium oxide. Precipitation separation was observed in the treated titanium oxide. This indicates that it has utility not only for solvent-based printing inks but also for fillers for aqueous printing inks.

【0015】本発明に係る特殊シラン化合物の無機顔料
に対する処理添加量は、実験の結果、無機顔料100重
量%に対して、0.1〜5.0重量%であるが、好まし
い添加量は0.1〜3.0重量%である。すなわち、印
刷インキ本来の性能を阻害することなく、帯電防止性能
を付与できる添加量の範囲である。
As a result of experiments, the amount of the special silane compound of the present invention added to the inorganic pigment is 0.1 to 5.0% by weight based on 100% by weight of the inorganic pigment. 0.1 to 3.0% by weight. That is, the addition amount is a range in which the antistatic performance can be imparted without impairing the original performance of the printing ink.

【0016】[0016]

【実施例】 1.表刷り用酸化チタン(アルミナ処理)を本発明に係る シラン化合物に2.0重量%添加して処理した処理済 酸化チタン粉末 35.0g 2.印刷インキメジウム(OS−M=PSフィルム用イン キメジウム−固形分 30% 大日精化工業株式会社製) 32.0g 3.溶剤=イソピルアルコール 33.0g 上記混合比で白色印刷インキを調合。PSフィルム(6
0ミクロン)に該印刷インキを乾燥厚約3ミクロンに全
面塗布した。 (印刷PSフィルムの評価結果) 使用測定器:ハイレスター高抵抗値測定器 スタチック
ボルトメータ SV−511 測定環境 :温度=22℃,湿度32%RH 3.テープ剥離 印刷剥離 ナシ 4.揉みテスト 脱落 ナシ 5.引掻きテスト 脱落 ナシ
[Examples] 1. 1. 35.0 g of treated titanium oxide powder obtained by adding 2.0% by weight of titanium oxide for surface printing (alumina treatment) to the silane compound according to the present invention. 2. Printing ink medium (OS-M = ink medium for PS film-solid content 30%, manufactured by Dainichi Seika Kogyo Co., Ltd.) 32.0 g Solvent = 33.0 g of isopropyl alcohol A white printing ink was prepared at the above mixing ratio. PS film (6
0 micron), the printing ink was applied over the entire surface to a dry thickness of about 3 microns. (Evaluation result of printed PS film) Measuring device used: High Leicester high resistance value measuring device Static voltmeter SV-511 Measurement environment: Temperature = 22 ° C, Humidity 32% RH 3. 3. Tape peeling Print peeling None Massage test dropout pear 5. Scratch test drop off pear

【0017】[0017]

【比較例】表刷り用酸化チタン顔料に未処理酸化チタン
顔料を使用した以外は、全て実施例と同一である。 3.テープ剥離 印刷剥離 ナシ 4.揉みテスト 脱落 ナシ 5.引掻きテスト 脱落 ナシ
[Comparative Examples] All of the examples were the same as the examples except that an untreated titanium oxide pigment was used as the titanium oxide pigment for surface printing. 3. 3. Tape peeling Print peeling None Massage test dropout pear 5. Scratch test drop off pear

【0018】[0018]

【発明の効果】本発明に係る帯電防止処理剤は、酸化チ
タン、シリカ、アルミナ等の無機物質の表面を改質させ
ることにより、この無機物質の表面に帯電性を付与する
ことができる。この結果、この無機物質を印刷インキ、
塗料、或いはプラスチック成形材料に配合して用いるこ
とにより、これらの物質にその特性を阻害することなく
帯電性を付与できる効果がある。
The antistatic treatment agent according to the present invention can impart a charging property to the surface of an inorganic substance such as titanium oxide, silica and alumina by modifying the surface of the inorganic substance. As a result, this inorganic substance is used for printing ink,
When used in a paint or a plastic molding material, there is an effect that these substances can be given a chargeability without inhibiting their properties.

【手続補正書】[Procedure amendment]

【提出日】平成11年6月21日(1999.6.2
1)
[Submission date] June 21, 1999 (1999.6.2
1)

【手続補正1】[Procedure amendment 1]

【補正対象書類名】明細書[Document name to be amended] Statement

【補正対象項目名】0018[Correction target item name] 0018

【補正方法】変更[Correction method] Change

【補正内容】[Correction contents]

【0018】[0018]

【発明の効果】本発明に係る帯電防止処理剤は、酸化チ
タン、シリカ、アルミナ等の無機物質の表面を改質させ
ることにより、この無機物質の表面に帯電防止性を付与
することができる。この結果、この無機物質を印刷イン
キ、塗料、或いはプラスチック成形材料に配合して用い
ることにより、これらの物質にその特性を阻害すること
なく帯電防止性を付与できる効果がある。
Antistatic treatment agent according to the present invention include titanium oxide, silica, by reforming the surface of an inorganic material such as alumina, it is possible to impart antistatic property to the surface of the inorganic material. As a result, the printing ink of this inorganic material, paint, or by using blended in plastic molding material, the effect of the antistatic property can be imparted without impairing its characteristics to these materials.

Claims (6)

【特許請求の範囲】[Claims] 【請求項1】 一般式R−SiX3で表すシラン化合物
で、式1中Rは末端に4級アンモニウム塩基を持つ無機
物質用帯電防止処理剤。 【式1】 1,R2,R3,R4は、炭素数がC1〜C2のアルキル基
である。Xは−OCH3或いは−OC25である。
1. An antistatic treatment agent for inorganic substances having a quaternary ammonium base at the terminal, wherein R is a silane compound represented by the general formula R—SiX 3 . (Equation 1) R 1 , R 2 , R 3 , and R 4 are alkyl groups having 1 to 2 carbon atoms. X is -OCH 3 or -OC 2 H 5.
【請求項2】 請求項1記載のシラン化合物により表面
処理された帯電防止性無機物質。
2. An antistatic inorganic substance surface-treated with the silane compound according to claim 1.
【請求項3】 請求項2記載の無機物質が酸化チタン又
はシリカ又はアルミナであるところの帯電防止性無機物
質。
3. An antistatic inorganic substance according to claim 2, wherein the inorganic substance is titanium oxide, silica or alumina.
【請求項4】 請求項2又は3記載の表面処理された帯
電防止性無機物質を充填剤として作られた帯電防止性印
刷インキ。
4. An antistatic printing ink prepared using the surface-treated antistatic inorganic substance according to claim 2 or 3 as a filler.
【請求項5】 請求項2又は3記載の表面処理された帯
電防止性無機物質を充填剤として作られた帯電防止性塗
料。
5. An antistatic paint made by using the surface-treated antistatic inorganic substance according to claim 2 as a filler.
【請求項6】 請求項2又は3記載の帯電防止性無機物
質を充填剤として作られた帯電防止性プラスチック成形
材料。
6. An antistatic plastic molding material prepared by using the antistatic inorganic substance according to claim 2 as a filler.
JP36016898A 1998-12-18 1998-12-18 Antistatic agent for inorganic substance Pending JP2000178540A (en)