JP2000172182A - Electromagnetic shieldable and light transparent window material and electromagnetic shieldable and heat ray cuttable light transparent window material - Google Patents

Electromagnetic shieldable and light transparent window material and electromagnetic shieldable and heat ray cuttable light transparent window material

Info

Publication number
JP2000172182A
JP2000172182A JP34723298A JP34723298A JP2000172182A JP 2000172182 A JP2000172182 A JP 2000172182A JP 34723298 A JP34723298 A JP 34723298A JP 34723298 A JP34723298 A JP 34723298A JP 2000172182 A JP2000172182 A JP 2000172182A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
electromagnetic
transparent
film
light transmitting
transparent substrate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP34723298A
Other languages
Japanese (ja)
Inventor
Hideshi Kotsubo
Yasuhiro Morimura
Masahito Yoshikawa
雅人 吉川
秀史 小坪
泰大 森村
Original Assignee
Bridgestone Corp
株式会社ブリヂストン
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To provide an electromagnetic shieldable and light transparent window material which is an electromagnetic shieldable and light transparent window material formed by disposing a transparent conductive film between two transparent substrates and is easy in assembly of window materials and building into casings and is capable of attaining conduction of uniform and low resistance to the casings and to enhance the mechanical strength and chemical durability of the transparent substrates. SOLUTION: Crosslinking type conductive tacky adhesive tape A are stuck to the electromagnetic shieldable and light transparent window material 1 formed by interposing the transparent conductive film between the two transparent substrates 2A and 2B so as to arrive at the edge on the front surface of the transparent substrate 2B from the edge of the transparent conductive film 3 through the end faces of the transparent substrate 2B. At least one of the transparent substrates 2A and 2B consists of tempered glass.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明はPDP(プラズマディスプレーパネル)の前面フィルタ等として有用な電磁波シールド性光透過窓材に係り、特に、OA機器等の筐体に容易に組み込むことができ、しかも、筐体に対して良好な導通を図ることができる電磁波シールド性光透過窓材、及び良好な電磁波シールド性と熱線カットとを兼備する電磁波シールド熱線カット性光透過窓材に関する。 The present invention relates to relates to useful electromagnetic-wave shielding and light transmitting plate as front filter such as the PDP (plasma display panel), in particular, it can be easily integrated into the housing of such OA equipment, moreover , electromagnetic-wave shielding and light transmitting plate capable of achieving a good continuity with respect to the housing, and a good electromagnetic shielding properties and the heat ray electromagnetic shielding heat-ray shielding and light transmitting member having both a cut.

【0002】 [0002]

【従来の技術】近年、OA機器や通信機器等の普及にともない、これらの機器から発生する電磁波が問題視されるようになっている。 In recent years, with the spread of OA equipment and communication equipment, electromagnetic waves generated from these devices are adapted to be problematic. 即ち、電磁波の人体への影響が懸念され、また、電磁波による精密機器の誤作動等が問題となっている。 That is about an impact on the human body of electromagnetic waves, also malfunction or the like of the precision apparatus by electromagnetic waves has become a problem.

【0003】そこで、従来、OA機器のPDPの前面フィルタとして、電磁波シールド性を有し、かつ光透過性の窓材が開発され、実用に供されている。 [0003] Therefore, conventionally, as a PDP front filter of the OA equipment, has electromagnetic shielding property, and optical transparency of the window material have been developed and put to practical use. このような窓材はまた、携帯電話等の電磁波から精密機器を保護するために、病院や研究室等の精密機器設置場所の窓材としても利用されている。 Such a window material also, in order to protect the precision equipment from electromagnetic waves such as mobile phones, have also been used as a window material of precision equipment installation location such as a hospital or laboratory.

【0004】また、OA機器本体からの熱で画面が過熱するという問題もあることから、OA機器のPDPの前面フィルタとして、電磁波シールド性と熱線カット性を有し、かつ光透過性の窓材が必要となる。 Further, since the screen by the heat from the OA apparatus body is also a problem that overheats, as PDP front filter of the OA equipment, has an electromagnetic wave shielding property and heat-ray shielding property, and optical transparency of the window material Is required.

【0005】従来の電磁波シールド性光透過窓材は、主に、金網のような導電性メッシュ材又は透明導電性フィルムをアクリル板等の透明基板の間に介在させて一体化した構成とされている。 [0005] Conventional electromagnetic-wave shielding and light transmitting plate, mainly, the conductive mesh material or a transparent conductive film such as wire mesh is configured to have integrally be interposed between the transparent substrates such as an acrylic plate there.

【0006】また、電磁波シールド性と熱線カット性とを兼備する窓材としては、ITO(インジウムスズ酸化物)や銀などの透明導電膜を形成したガラス板又は透明フィルムを張り合わせたものが提案されている。 Further, as the window material having both an electromagnetic wave shielding property and heat-ray shielding property, ITO that laminated glass plate or a transparent film to form a transparent conductive film such as indium tin oxide () and silver have been proposed ing.

【0007】また、モアレ現像を防止すると共に、光透過性、電磁波シールド性、熱線(近赤外線)カット性が良好な電磁波シールド性光透過窓材とするために、2種以上の透明導電性膜フィルムを2枚の透明基板間に介在させて積層する場合もある。 Further, it is possible to prevent the moire development, light transmissive electromagnetic wave shielding properties, heat rays to (near infrared) cut resistance and good electromagnetic-wave shielding and light transmitting plate, two or more transparent conductive films sometimes laminating a film is interposed between two transparent substrates. このような電磁波シールド性光透過窓材は、例えば、一方の板面に透明導電性フィルムを接着した透明基板を、2枚用意し、これらを接着用樹脂フィルムを介して、透明導電性フィルム同士が対面するように積層して接着一体化することにより製造される。 Such electromagnetic-wave shielding and light transmitting plate, for example, a transparent substrate having adhered to one plate surface on the transparent conductive film, prepared two and, these via the adhesive resin film, a transparent conductive film to each other There is produced by bonding integrally laminated to face.

【0008】このような電磁波シールド性光透過窓材をPDP等に組み込んで良好な電磁波シールド性を得るためには、電磁波シールド性光透過窓材とこれを組み込む筐体との間、即ち、電磁波シールド性光透過窓材の導電性メッシュと筐体の導電面との間に均一な導通を図る必要がある。 [0008] During the such electromagnetic-wave shielding and light transmitting plate incorporating a PDP or the like in order to obtain good electromagnetic shielding properties, an electromagnetic-wave shielding and light transmitting plate and the housing incorporating this, i.e., electromagnetic waves it is necessary to achieve uniform conduction between the conductive mesh and the conductive surface of the casing of the shielding and light transmitting plate.

【0009】従来、簡易な構造で電磁波シールド性光透過窓材と筐体との導通を図るものとして、2枚の透明基板間に介在させた導電性メッシュの周縁部を透明基板周縁部からはみ出させ、このはみ出し部分を一方の透明基板の表面側に折り曲げ、この折り曲げた導電性メッシュの周縁部を筐体との導通部とし、筐体側に圧接するようにしたものが提案されている(特開平9−147752 Conventionally, as to achieve conduction between the electromagnetic-wave shielding and light transmitting plate and the housing with a simple structure, protruding the periphery of the conductive mesh is interposed between two transparent substrates from the transparent substrate peripheral portion is, bending the protruding portion on the surface side of the one transparent substrate, the periphery of the bent conductive mesh in a conductive portion of the housing, that as pressed against the housing side has been proposed (Japanese Patent No. 9-147752
号公報)。 JP).

【0010】ところで、従来、金属箔の一方の面に導電性粒子を分散させた接着剤層を設けた導電性接着テープが、各種電気機器の組み立てに当り、導通部ないし電極取り出し部の形成等に用いられている。 By the way, conventionally, one surface to the conductive particles electrically conductive adhesive tape having a adhesive layer having dispersed therein a metal foil, hit the assembly of the various electric appliances, conductive portion or electrode lead-out portion of the formation such as It has been used to. 従来の導電性接着テープの接着剤層は、一般にエポキシ系又はフェノール系樹脂と硬化剤を主成分とする接着剤に導電性粒子を分散させたもので構成され、特に、利便性等の点から接着剤としては1液型の熱硬化型のものが主流になってきているが、エポキシ系又はフェノール系樹脂を接着剤とする導電性接着テープでは、 粘着性が殆どなく、仮り止め等を行い難い。 Conventional conductive adhesive tape of the adhesive layer, typically composed of one obtained by dispersing conductive particles in adhesives based curing agent and epoxy or phenolic resin, in particular, from the viewpoint of convenience such as as the adhesive agent as the heat curable one-pack type has become the mainstream, with the conductive adhesive tape to be an epoxy or phenolic resin and adhesive, adhesive is little performs temporary stop, etc. hard. また、 Also,
貼り直しがきかない。 Reattachment does not work. このため、修整作業が殆ど不可能である。 For this reason, retouching work is almost impossible. 特に、フェノール樹脂では、耐湿・耐熱性が悪く、 In particular, the phenolic resin, has poor moisture-heat resistance,
長期耐久性に劣る。 Inferior to the long-term durability. 特に、エポキシ系樹脂では、硬化のための加熱温度が150℃以上と高く、接着が容易ではない。 In particular, the epoxy resin, the heating temperature for curing is as high as 0.99 ° C. or higher, the adhesion is not easy. 接着強度が十分でない。 The adhesive strength is not sufficient. といった欠点があった。 There has been a drawback.

【0011】このような導電性接着テープの代わりに導電性粘着テープを用いることも考えられるが、従来の導電性粘着テープは粘着層の厚みが大きく、また付着力が弱く剥れ易いという欠点がある。 [0011] Although it is considered to use a conductive adhesive tape instead of such a conductive adhesive tape, a conventional conductive adhesive tape has a large thickness of the adhesive layer, also the drawback of easily peeling weak adhesive force is there.

【0012】 [0012]

【発明が解決しようとする課題】2枚の透明基板間に導電性メッシュを介在させたものであれば、上述の如く、 As long as it is interposed a conductive mesh between THE INVENTION Problems to be Solved by the two transparent substrates, as described above,
導電性メッシュの周縁部を透明基板周縁部からはみ出させ、このはみ出し部分を折り曲げ、この折り曲げた部分から筐体との導通を図ることができるが、2枚の透明基板間に透明導電性フィルムを介在させた窓材にあっては、透明導電性フィルムの周縁部を透明基板周縁部からはみ出させて折り曲げると、この折り目部分でフィルムが裂けてしまい、筐体との導通をとることができない。 Thereby protrude the periphery of the conductive mesh from the transparent substrate peripheral portion, bending the protruding portion, but from the bent portion can be reduced conduction between housing, a transparent conductive film between two transparent substrates in the window material is interposed, when bent by protrude from the transparent substrate peripheral portion a peripheral portion of the transparent conductive film, would tear film at this folded portion, it is impossible to obtain conductivity with the housing.

【0013】また、透明導電性フィルムの代りに、一方の透明基板の接着面に透明導電性膜を直接成膜して電磁波シールド性光透過窓材を構成することも考えられるが、この場合には、透明導電性膜が他方の透明基板で覆われてしまい、透明導電性膜から筐体への導通を図ることができない。 Further, instead of the transparent conductive film, it is conceivable to configure the electromagnetic-wave shielding and light transmitting plate by directly forming a transparent conductive film on the adhesive surface of the one transparent substrate, in this case is cause transparent conductive film is covered with the other transparent substrate, it is impossible to ensure electrical connections from the transparent conductive film to the housing.

【0014】従って、このような場合には、他方の透明基板を一方の透明基板よりも小面積とし、透明導電性膜の表出部を形成したり、透明基板に貫通孔を形成して透明導電性膜との導通路を設けたりするなどの設計変更が必要となり、電磁波シールド性光透過窓材の組み立てや筐体への組み込み作業が複雑となる。 [0014] Therefore, in such a case, a smaller area than the one transparent substrate and the other transparent substrate, or forming a exposed portion of the transparent conductive film, transparent to form a through hole in the transparent substrate design changes, such as may be provided a conductive path between the conductive film is required, incorporation work on assembly and the housing of the electromagnetic-wave shielding and light transmitting plate is complicated.

【0015】特に、モアレ現像を防止すると共に、光透過性、電磁波シールド性、熱線(近赤外線)カット性がいずれも良好な電磁波シールド性光透過窓材とするために、2種以上の透明導電性膜フィルムを2枚の透明基板間に介在させて積層した電磁波シールド性光透過窓材にあっては、透明導電性膜と筐体との導通を図ることが非常に困難である。 [0015] In particular, as to prevent moire development, light transmissive electromagnetic wave shielding properties, heat rays (near infrared) to the cutting property both good electromagnetic-wave shielding and light transmitting plate, two or more transparent conductive is a sex film film electromagnetic-wave shielding and light transmitting plate formed by laminating be interposed between two transparent substrates, it is very difficult to achieve conduction between the transparent conductive film and the housing. この電磁波シールド性光透過窓材であっても、例えば、透明基板に貫通孔を形成して透明導電性膜との導通路を設けるなどの設計変更が必要となり、 Even in this electromagnetic-wave shielding and light transmitting plate, for example, it requires a design change, such as by forming a through hole in the transparent substrate provided with conductive paths between the transparent conductive film,
電磁波シールド性光透過窓材の組み立てや筐体への組み込み作業が複雑となる。 Incorporation work on assembly and the housing of the electromagnetic-wave shielding and light transmitting plate is complicated.

【0016】また、従来の電磁波シールド性光透過窓材では、PDP用フィルタとしての透明性、電磁波シールド性及び熱線カット性等の要求特性のすべてを十分に満たすことはできなかった。 Further, in the conventional electromagnetic-wave shielding and light transmitting plate, the transparency as a PDP filter, it was not possible to meet all the sufficient electromagnetic shielding property and heat rays required properties of the cut and the like.

【0017】また、電磁波シールド性光透過窓材の透明基板としては、剛性に優れ、PDPからの伝熱による変形がなく、耐食性等にも優れることから、ガラス基板を用いるのが好ましいが、通常のガラス基板の場合、強い荷重をかけると割れるという機械的強度に大きな欠点を持っている。 Further, as the transparent substrate of the electromagnetic-wave shielding and light transmitting plate, excellent rigidity, no deformation due to heat transfer from the PDP, since the excellent corrosion resistance and the like, although it is preferable to use a glass substrate, usually for glass substrates, it has a major drawback in mechanical strength that cracks and applying a strong force. また、化学的安定性が十分であるとは言えず、耐候性が不足し、高温高湿環境下に長期間晒されると表面にヤケが発生するなどの欠点があった。 Moreover, it can not be said chemical stability is sufficient, insufficient weather resistance, is burnt in a long period of time exposed to the surface in high-temperature, high-humidity environment has a disadvantage such as generation.

【0018】本発明は上記従来の問題点を解決し、2枚の透明基板間に透明導電性膜を設けた電磁波シールド性光透過窓材であって、透明基板としてのガラス基板の機械的強度と化学的耐久性が著しく良好で、窓材の組み立て、筐体への組み込みが容易で、筐体に対して、均一かつ低抵抗の導通を図ることができる電磁波シールド性光透過窓材を提供することを目的とする。 [0018] The present invention solves the above conventional problems, an electromagnetic-wave shielding and light transmitting plate having a transparent conductive film between two transparent substrates, the mechanical strength of the glass substrate as a transparent substrate chemical durability significantly better and, the assembly of the window material, easy integration into the housing, provided for housing an electromagnetic-wave shielding and light transmitting plate capable of achieving continuity of uniform and low resistivity an object of the present invention is to.

【0019】本発明はまた、モアレ現像を防止すると共に、光透過性、電磁波シールド性、熱線(近赤外線)カット性がいずれも極めて良好な電磁波シールド性光透過窓材とするために、2種以上の透明導電性膜フィルムを2枚の透明基板間に介在させて積層した電磁波シールド性光透過窓材であって、透明基板としてのガラス基板の化学的耐久性が著しく良好で、窓材の組み立て、筐体への組み込みが容易で、筐体に対して、均一かつ低抵抗の導通を図ることができる電磁波シールド性光透過窓材を提供することを目的とする。 [0019] The present invention also serves to prevent moire development, light transmissive electromagnetic wave shielding properties, both heat ray (near infrared) cut resistance to a very good electromagnetic-wave shielding and light transmitting plate, two a wave shielding and light transmitting material layered by interposing between the above two transparent conductive films film transparent substrate, is markedly better chemical durability of the glass substrate as a transparent substrate, a window material assembling, easy integration into the housing, relative to the housing, and an object thereof is to provide an electromagnetic wave shielding and light transmitting plate capable of achieving continuity of uniform and low resistance.

【0020】本発明はまた、透明基板としてのガラス基板の機械的強度と化学的耐久性が著しく良好で、しかも、高透明性で、電磁波シールド性及び熱線カット性が著しく良好な電磁波シールド熱線カット性光透過窓材を提供することを目的とする。 [0020] The present invention also is markedly better mechanical strength of the glass substrate and the chemical durability of the transparent substrate, moreover, a high transparency, electromagnetic wave shielding property and heat-ray shielding properties significantly better electromagnetic shielding heat-ray shielding and to provide sexual light transmitting plate.

【0021】 [0021]

【課題を解決するための手段】請求項1の電磁波シールド性光透過窓材は、第1及び第2の透明基板間に透明導電性膜を介在させてなる電磁波シールド性光透過窓材において、該第1及び第2の透明基板のうちの少なくとも一方は強化ガラスよりなる電磁波シールド性光透過窓材であって、該透明導電性膜の縁部から該第1の透明基板の端面を経て該第1の透明基板の表面の縁部にまで達するように導電性粘着テープAが貼り付けられていることを特徴とする。 [Summary of the electromagnetic wave shielding and light transmitting plate according to claim 1, in electromagnetic-wave shielding and light transmitting plate comprising by interposing a transparent conductive film between the first and second transparent substrates, at least one of the first and second transparent substrates is an electromagnetic-wave shielding and light transmitting plate consisting of reinforced glass, the from the edge of the transparent conductive film through an end face of the first transparent substrate characterized in that a conductive adhesive tape a is attached so as to reach the edge of the surface of the first transparent substrate.

【0022】本発明によれば、透明導電性膜の縁部に導電性粘着テープを貼り、透明基板の端面を回り込ませることにより、透明基板の大きさを変えたり、貫通孔を設けたりする設計変更を行うことなく、容易に導通部を引き出すことができる。 According to the invention, bonding the conductive adhesive tape to the edge of the transparent conductive film, by Wrapping end face of the transparent substrate, or changing the size of the transparent substrate, or a through-hole design without changing, it can be drawn easily conducting portion. このため、電磁波シールド性光透過窓材を容易に組み立てることができ、また、筐体に容易に組み込むことができるようになり、導電性粘着テープを介して電磁波シールド性光透過窓材の透明導電性膜と筐体との間に良好な導通を得ることができる。 Therefore, the electromagnetic-wave shielding and light transmitting plate can be easily assembled, also be able to be easily incorporated into a housing, a transparent conductive electromagnetic shielding and light transmitting plate through a conductive adhesive tape it is possible to obtain good conduction between the sexual membrane and the housing.

【0023】また、この電磁波シールド性光透過窓材は、2枚の透明基板のうちの少なくとも一方が強化ガラス、好ましくは化学強化ガラスであることから、透明基板の機械的強度と化学的安定性が向上し、良好な耐候、 Further, the electromagnetic-wave shielding and light transmitting plate, at least one is reinforced glass of the two transparent substrates, since it is preferably chemically strengthened glass, the mechanical strength and chemical stability of the transparent substrate but improved, good weather,
耐久性が得られる。 Durability can be obtained.

【0024】請求項2では、導電性粘着テープAとは別に、更に、第1及び第2の透明基板の端面から、第1の透明基板の表面の縁部と第2の透明基板の表面の縁部とに回り込んで導電性粘着テープBを貼り付けるのが好ましく、これにより、より一層筐体への組み込みが容易になると共に、均一かつ安定な導通を図ることができるようになる。 [0024] According to claim 2, apart from the electroconductive pressure-sensitive adhesive tape A, further from the end surfaces of the first and second transparent substrates, the edge and the surface of the second transparent substrate of the surface of the first transparent substrate preferably pasting a conductive adhesive tape B wraps around to the edge, thereby, together with further integration into the casing is facilitated, it is possible to achieve uniform and stable conduction.

【0025】請求項3の電磁波シールド性光透過窓材は、一方の板面に第1の透明導電性膜を有する第1の透明基板と、一方の板面に第2の透明導電性膜を有する第2の透明基板とを、該透明導電性膜同士を対面させて接合一体化してなる電磁波シールド性光透過窓材において、該第1及び第2の透明基板のうちの少なくとも一方は強化ガラスよりなる電磁波シールド性光透過窓材であって、該第1の透明導電性膜の縁部から該第1の透明基板の端面を経て該第1の透明基板の他方の板面の縁部にまで達するように第1の導電性粘着テープが貼り付けられており、該第2の透明導電性膜の縁部から該第2の透明基板の端面を経て該第2の透明基板の他方の板面の縁部にまで達するように第2の導電性粘着テープが貼り付けられていることを特 The electromagnetic-wave shielding and light transmitting plate according to claim 3, a first transparent substrate having a first transparent conductive film on one of the plate surface, a second transparent conductive film on one of the plate surfaces second and a transparent substrate, in electromagnetic-wave shielding and light transmitting plate formed by joining integrally so as to face the transparent conductive film to each other, at least one of reinforced glass of the first and second transparent substrates having a more becomes electromagnetic-wave shielding and light transmitting plate, the edge of the other plate surface from the edge of the transparent substrate of the first through the end face of the first transparent substrate of the first transparent conductive film up and pasted the first conductive adhesive tape so as to reach, the second transparent conductive film other plate from the edge of the second through the end face of the second transparent substrate of the transparent substrate Patent that the second conductive adhesive tape is attached so as to reach the edge of the surface とする。 To.

【0026】請求項3によれば、各透明導電性膜の縁部に導電性粘着テープを貼り、各々の透明基板の端面を回り込ませることにより、窓材の設計変更を行うことなく、容易に導通部を引き出すことができる。 According to claim 3, bonding the conductive adhesive tape to the edge of the transparent conductive film, by Wrapping end face of each of the transparent substrate, without changing the design of the window material, easily conducting portion can be drawn. このため、 For this reason,
電磁波シールド性光透過窓材を容易に組み立てることができ、また、筐体に容易に組み込むことができるようになり、導電性粘着テープを介して電磁波シールド性光透過窓材の透明導電性膜と筐体との間に良好な導通を得ることができる。 The electromagnetic-wave shielding and light transmitting plate can be easily assembled, also be able to be easily incorporated into the housing, and the transparent conductive layer of the electromagnetic-wave shielding and light transmitting plate through a conductive adhesive tape it is possible to obtain good conduction between the casing.

【0027】また、この電磁波シールド性光透過窓材は、2枚の透明基板のうちの少なくとも一方が強化ガラス、好ましくは化学強化ガラスであることから、透明基板の機械的強度と化学的安定性が向上し、良好な耐候、 Further, the electromagnetic-wave shielding and light transmitting plate, at least one is reinforced glass of the two transparent substrates, since it is preferably chemically strengthened glass, the mechanical strength and chemical stability of the transparent substrate but improved, good weather,
耐久性が得られる。 Durability can be obtained.

【0028】請求項3では、第1及び第2の導電性粘着テープとは別に、更に、第1及び第2の透明基板の端面から、第1の透明基板の表面の縁部と第2の透明基板の表面の縁部とに回り込んで第3の架橋型導電性粘着テープを貼り付けるのが好ましく、これにより、電磁波シールド性光透過窓材の接合強度が向上して、取り扱い性が良くなり、より一層筐体への組み込みが容易になると共に、均一かつ安定な導通を図ることができるようになる。 [0028] According to claim 3, separately from the first and second conductive adhesive tape, and further, from the end face of the first and second transparent substrates, the surface of the first transparent substrate edge and the second third is preferred paste crosslinked electroconductive pressure-sensitive adhesive tape wraps around to the edge of the surface of the transparent substrate, thereby, improved bonding strength of the electromagnetic-wave shielding and light transmitting plate is, good handling properties becomes, the more incorporation into the housing is facilitated, it is possible to achieve uniform and stable conduction.

【0029】ところで、従来の導電性接着テープでは、 By the way, in the conventional conductive adhesive tape,
前述の如く、仮り止め、貼り直しができないために作業性が悪く、接着部の耐久性や接着強度が十分でないといった不具合が生じる。 As previously described, stop temporarily, poor workability because it can not re-paste, a problem occurs, such as durability and adhesive strength of the adhesive portion is not sufficient.

【0030】そこで、請求項1,3の電磁波シールド性光透過窓材において、導電性粘着テープとしては特に架橋型導電性粘着テープを用いるのが好ましい。 [0030] Therefore, in the electromagnetic-wave shielding and light transmitting plate according to claim 1 and 3, preferably is particularly using a crosslinking type conductive adhesive tape as the conductive adhesive tape.

【0031】この架橋型導電性粘着テープ、特に、エチレン−酢酸ビニル系共重合体とその架橋剤を含む後架橋型接着層よりなる粘着層を有する架橋型導電性粘着テープであれば、次のような特長を有し、効率的な組み立てを行える。 [0031] The crosslinking type electroconductive pressure-sensitive adhesive tape, in particular, ethylene - if crosslinked electroconductive pressure-sensitive adhesive tape having an adhesive layer made of cross-linked adhesive layer after including vinyl acetate copolymer and its cross-linking agent, the following It has features like, enabling an efficient assembling.

【0032】(i) 優れた粘着性を有し、被貼着対象に容易に、かつ適度な粘着力で仮り止めすることができる。 [0032] (i) have excellent adhesion, can be temporarily fixed with ease, and moderate adhesion to the destination object stuck object. (ii) 架橋前の粘着力は仮り止めには十分であるが、さほど強くないため、貼り直しが可能であり、修整作業を容易に行える。 But (ii) prior to crosslinking pressure-sensitive adhesive force is sufficient to temporarily stop, because not very strong, but may be re-paste, easily gets work. (iii) 架橋硬化させた後の接着力は極めて強固であるため、高い接着強度を得ることができる。 (Iii) adhesion after cured by crosslinking is because it is very strong, it is possible to obtain a high adhesive strength. (iv) 耐湿・耐熱性が高く、長期耐久性に優れる。 (Iv) a high moisture and heat resistance, excellent long-term durability. (v) 熱架橋の場合でも、一般に、130℃以下の温度で架橋硬化可能であり、また、光架橋性とすることもでき、比較的低温で架橋硬化できるため、接着作業が容易である。 Even in the case of (v) thermal crosslinking, generally a crosslinkable cure at 130 ° C. or less of the temperature and can also be a photocrosslinkable, since it crosslinking curing at relatively low temperatures, it is easy bonding operation.

【0033】請求項7の電磁波シールド熱線カット性光透過窓材は、2枚の透明基板間に中間膜を介在させて、 The electromagnetic wave shielding heat-ray shielding and light transmitting material according to claim 7, an intermediate film is interposed between two transparent substrates,
接着樹脂で接合一体化してなる電磁波シールド熱線カット性光透過窓材において、該2枚の透明基板のうちの少なくとも一方は強化ガラスよりなる電磁波シールド性光透過窓材であって、該中間膜は、酸化物透明導電膜と金属薄膜とを交互に積層してなる多層膜を備えることを特徴とする。 In the electromagnetic shielding heat-ray shielding and light transmitting material formed integrally joined with an adhesive resin, at least one of said two transparent substrates is a electromagnetic-wave shielding and light transmitting plate consisting of reinforced glass, the intermediate film , characterized in that it comprises a multilayer film formed by laminating a transparent conductive oxide film and the metal thin film alternately.

【0034】酸化物透明導電膜と金属薄膜とを交互に積層してなる多層膜であれば、透明性を損なうことなく、 [0034] If the multilayer film and a transparent conductive oxide film and the metal thin film formed by laminating alternately, without impairing the transparency,
著しく良好な電磁波シールド性と熱線(近赤外線)カット性を得ることができる。 It is possible to obtain significantly better electromagnetic shielding properties and heat ray (near infrared) cut resistant.

【0035】また、この電磁波シールド熱線カット性光透過窓材は、2枚の透明基板のうちの少なくとも一方が強化ガラス、好ましくは化学強化ガラスであることから、透明基板の機械的強度と化学的安定性が向上し、良好な耐候、耐久性が得られる。 Further, the electromagnetic wave shielding heat-ray shielding and light transmitting material, at least one of reinforced glass of the two transparent substrates, preferably from it is chemically tempered glass, mechanical strength and chemical transparent substrate improved stability, good weatherability, durability can be obtained.

【0036】この多層膜は、これをベースフィルム上に形成して、2枚の透明基板間に独立した中間膜として介在させても良く、また、透明基板上に直接形成したものとしても良い。 [0036] The multilayer film which was formed on a base film may be interposed as a separate intermediate layer between two transparent substrates, also may be obtained by directly formed on a transparent substrate.

【0037】 [0037]

【発明の実施の形態】以下に図面を参照して本発明の電磁波シールド性光透過窓材及び電磁波シールド熱線カット性光透過窓材の実施の形態を詳細に説明する。 BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter will be described with reference to the drawings in detail an embodiment of an electromagnetic wave shielding and light transmitting plate and the electromagnetic wave shielding heat-ray shielding and light transmitting material of the present invention to.

【0038】まず、図1を参照して請求項1の電磁波シールド性光透過窓材の実施の形態を説明する。 [0038] First, referring to FIG. 1 illustrating an embodiment of an electromagnetic wave shielding and light transmitting plate according to claim 1.

【0039】図1(a)は本発明の電磁波シールド性光透過窓材の実施の形態を示す模式的な断面図であり、図1(b)は導電性粘着テープを貼り付けた透明導電性フィルムを示す平面図である。 [0039] FIG. 1 (a) is a schematic sectional view showing an embodiment of the electromagnetic-wave shielding and light transmitting plate of the present invention, FIG. 1 (b) a transparent conductive pasted conductive adhesive tape film is a plan view showing a.

【0040】この電磁波シールド性光透過窓材1は、2 [0040] The electromagnetic-wave shielding and light transmitting plate 1, 2
枚の透明基板2A,2Bの間に透明導電性フィルム3を挟んで接着用樹脂フィルム4A,4Bにより接合一体化したものであり、透明導電性フィルム3の4側辺の縁部から透明基板2Bの端面を経て透明基板2Bの表面の縁部にまで達するように、それぞれ導電性粘着テープAを貼り付けてある。 Sheets of transparent substrates 2A, adhesive resin film 4A sandwich the transparent conductive film 3 during 2B, is obtained by joining together by 4B, the transparent substrate 2B from the edge of the four sides of the transparent conductive film 3 as reach the edge of the surface of the transparent substrate 2B through the end faces, are respectively affixed conductive adhesive tape a.

【0041】本実施例において、透明基板2A,2Bと透明導電性フィルム3の積層体の全周において、端面の全体に付着すると共に、この積層体の表裏の角縁を回り込み、一方の透明基板2Aの表面の端縁部と他方の透明基板2Bの表面の端縁部の双方に付着するように、更に導電性粘着テープBが設けられている。 [0041] In this embodiment, the transparent substrate 2A, the entire periphery of 2B and a transparent conductive film 3 of the laminate, while adhering to the entire end face, wraparound front and back corner edge of the stack, one of the transparent substrate to adhere to both the edge portions of the edge and the surface of the other transparent substrate 2B of 2A surface, it is provided with further conductive adhesive tape B.

【0042】導電性粘着テープA,Bは、例えば、金属箔aの一方の面に導電性の粘着層bを形成してなるものである。 The electroconductive pressure-sensitive adhesive tape A, B are, for example, those obtained by forming an adhesive layer b one surface to the conductive metal foil a. 導電性粘着テープA,Bの金属箔aとしては、 Conductive adhesive tape A, as the metal foil a of B is
厚さ1〜100μm程度の銅、銀、ニッケル、アルミニウム、ステンレス等の箔を用いることができる。 The thickness 1~100μm about copper, silver, can be used nickel, aluminum, foil such as stainless steel.

【0043】また、導電性の粘着層bは、導電性粒子を分散させた接着剤をこのような金属箔aの一方の面に塗工して形成される。 [0043] Further, the adhesive layer b of conductivity is formed by applying an adhesive by dispersing conductive particles on one surface of the metal foil a.

【0044】この接着剤としては、エポキシ系又はフェノール系樹脂に硬化剤を配合したもの、或いは、アクリル系粘着剤、ゴム系粘着剤、シリコン系粘着剤などを用いることができるが、本発明においては、導電性粘着テープ7として、前述の理由から、特に、架橋型導電性粘着テープを用いるのが好ましく、この場合、この粘着層7の接着剤としては後述のエチレン−酢酸ビニル系共重合体を主成分とするポリマーとその架橋剤とを含む後架橋型接着剤を用いるのが好ましい。 [0044] As the adhesive, those obtained by blending a curing agent to the epoxy or phenolic resin, or acrylic adhesive, rubber-based adhesives, and the like can be used silicone-based adhesive, in the present invention as conductive adhesive tape 7, for the reasons described above, particularly preferably to use a crosslinked electroconductive pressure-sensitive adhesive tape, in this case, ethylene later as an adhesive of the adhesive layer 7 - vinyl acetate copolymer preferably used crosslinking adhesive after comprising a polymer as a main component and its crosslinking agent.

【0045】接着剤に分散させる導電性粒子としては、 [0045] As the conductive particles dispersed in the adhesive,
電気的に良好な導体であれば良く、種々のものを使用することができる。 May be any electrically good conductor, it can be used various ones. 例えば、銅、銀、ニッケル等の金属粉体、酸化錫、インジウム錫酸化物、酸化亜鉛等の金属酸化物粉体、このような金属又は金属酸化物で被覆された樹脂又はセラミック粉体等を使用することができる。 For example, copper, silver, metal powders such as nickel, tin oxide, indium tin oxide, metal oxide powder such as zinc oxide, such metal or metal oxide coated with a resin or ceramic powder or the like it can be used. また、その形状についても特に制限はなく、りん片状、樹枝状、粒状、ペレット状、球状、星状、こんぺい糖状(多数の突起を有する粒状)等の任意の形状をとることができる。 There is not any special restriction on the shape, may take the form of flakes, dendritic, granular, pellet, spherical, star-shaped, any shape such as Imataira sugar-like (particulate having a large number of projections) .

【0046】この導電性粒子の配合量は、接着剤に対し0.1〜15容量%であることが好ましく、また、その平均粒径は0.1〜100μmであることが好ましい。 [0046] The amount of the conductive particles is preferably 0.1 to 15% by volume based on the adhesive, and it is preferable that the average particle diameter of 0.1 to 100 [mu] m.
このように、配合量及び粒径を規定することにより、導電性粒子の凝集を防止して、良好な導電性を得ることができるようになる。 Thus, by defining the amount and particle size, to prevent aggregation of the conductive particles, it is possible to obtain good conductivity.

【0047】次に、本発明に好適な架橋型導電性粘着テープの構成について説明する。 Next, description will be given of a configuration of a preferred crosslinked electroconductive pressure-sensitive adhesive tape of the present invention.

【0048】本発明で用いる架橋型導電性粘着テープは、上述した金属箔aの一方の面に、導電性粒子を分散させた粘着層bを設けたものであって、この粘着層bの接着剤として、好ましくはエチレン−酢酸ビニル系共重合体を主成分とするポリマーとその架橋剤とを含む後架橋型接着剤を用いたものである。 The cross-linked conductive adhesive tape used in the present invention, on one surface of the metal foil a described above, the conductive particles be those in which a pressure-sensitive adhesive layer b dispersed, adhesion of the adhesive layer b agents as, preferably an ethylene - is obtained using a crosslinking type adhesive after comprising a polymer mainly composed of vinyl acetate copolymer and its cross-linking agent.

【0049】この場合、粘着層bを構成するポリマーは、下記(A)〜(C)から選ばれる、エチレン−酢酸ビニル系共重合体を主成分とし、メルトインデックス(MFR)が1〜3000、特に1〜1000、とりわけ1〜800であるものが好ましい。 [0049] In this case, the polymer constituting the adhesive layer b is selected from the following (A) ~ (C), ethylene - the main component vinyl acetate copolymer, melt index (MFR) is 1 to 3000, in particular 1-1000, especially it is preferred at 1 to 800.

【0050】このようにMFRが1〜3000で、かつ酢酸ビニル含有率が2〜80重量%の下記(A)〜 [0050] In MFR in this way 1 to 3000, and the following vinyl acetate content of 2 to 80 wt% (A) ~
(C)の共重合体を使用することにより、架橋前の粘着性が上がり、作業性が向上すると共に、架橋後の硬化物は3次元架橋密度が高くなり、強固な接着力を発現し、 By using a copolymer of (C), up sticky before crosslinking, thereby improving workability, the cured product after crosslinking is high 3D crosslink density, expressed strong adhesive force,
耐湿・耐熱性も向上する。 Moisture and heat resistance is also improved.

【0051】(A)酢酸ビニル含有率が20〜80重量%であるエチレン−酢酸ビニル共重合体 (B)酢酸ビニル含有率が20〜80重量%であり、アクリレート系及び/又はメタクリレート系モノマーの含有率が0.01〜10重量%であるエチレンと酢酸ビニルとアクリレート系及び/又はメタクリレート系モノマーとの共重合体 (C)酢酸ビニル含有率が20〜80重量%であり、マレイン酸及び/又は無水マレイン酸の含有率が0.01 [0051] (A) an ethylene vinyl acetate content of 20 to 80 wt% - vinyl acetate copolymer (B) vinyl acetate content of from 20 to 80 wt%, of acrylate and / or methacrylate monomer ethylene and vinyl acetate and acrylate and / or copolymer of a methacrylate monomer (C) content of vinyl acetate content of from 0.01 to 10% by weight is 20 to 80 wt%, maleic acid and / or the content of maleic anhydride is 0.01
〜10重量%であるエチレンと酢酸ビニルとマレイン酸及び/又は無水マレイン酸との共重合体 上記(A)〜(C)のエチレン−酢酸ビニル系共重合体において、エチレン−酢酸ビニル共重合体の酢酸ビニル含有率は20〜80重量%であり、好ましくは20〜6 In vinyl acetate copolymer, ethylene - - Ethylene Copolymer above of ethylene and vinyl acetate and maleic acid and / or maleic anhydride is 10 wt% (A) ~ (C) vinyl acetate copolymer the vinyl acetate content of 20 to 80 wt%, preferably 20-6
0重量%である。 0, which is the percent by weight. 酢酸ビニル含有率が20重量%より低いと高温時に架橋硬化させる場合に十分な架橋度が得られず、一方、80重量%を超えると、(A),(B)のエチレン−酢酸ビニル系共重合体では樹脂の軟化温度が低くなり、貯蔵が困難となり、実用上問題であり、 Can not be obtained sufficient crosslinking degree when vinyl acetate content of crosslinking curing at high temperatures is lower than 20 wt%, whereas, if it exceeds 80 wt%, (A), ethylene (B) - vinyl acetate copolymer the softening temperature of the resin is lowered in the polymer, storage becomes difficult, a practical problem,
(C)のエチレン−酢酸ビニル系共重合体では接着層強度や耐久性が著しく低下してしまう傾向がある。 Ethylene (C) - it tends to deteriorate markedly the adhesion layer strength and durability in the vinyl acetate copolymer.

【0052】また、(B)のエチレンと酢酸ビニルとアクリレート系及び/又はメタクリレート系モノマーとの共重合体において、アクリレート系及び/又はメタクリレート系モノマーの含有率は0.01〜10重量%であり、好ましくは0.05〜5重量%である。 [0052] Further, an ethylene and in copolymer of vinyl acetate and acrylate and / or methacrylate monomer, from 0.01 to 10% by weight content of acrylate and / or methacrylate monomer (B) , preferably 0.05 to 5 wt%. このモノマーの含有率が0.01重量%より低いと接着力の改善効果が低下し、一方、10重量%を超えると加工性が低下してしまう場合がある。 The content of this monomer reduces the effect of improving the adhesion is lower than 0.01 wt%, whereas, in some cases exceeds 10 wt% the workability is lowered. なお、アクリレート系及び/又はメタクリレート系モノマーとしては、アクリル酸エステル又はメタクリル酸エステル系モノマーの中から選ばれるモノマーが挙げられ、アクリル酸又はメタクリル酸と炭素数1〜20、特に〜18の非置換又はエポキシ基等の置換基を有する置換脂肪族アルコールとのエステルが好ましく、例えばアクリル酸メチル、メタクリル酸メチル、アクリル酸エチル、メタクリル酸エチル、メタクリル酸グリシジル等が挙げられる。 As the acrylate and / or methacrylate monomers, include monomers selected from among acrylic acid ester or methacrylic acid ester monomer, unsubstituted acrylic acid or methacrylic acid with 1 to 20 carbon atoms, in particular to 18 or esters of substituted aliphatic alcohols having a substituent such as an epoxy group is preferred, for example methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, and glycidyl methacrylate.

【0053】また、(C)のエチレンと酢酸ビニルとマレイン酸及び/又は無水マレイン酸との共重合体において、マレイン酸及び/又は無水マレイン酸の含有率は0.01〜10重量%であり、好ましくは0.05〜5 [0053] Further, in the copolymer of ethylene and vinyl acetate and maleic acid and / or maleic anhydride (C), the content of maleic acid and / or maleic anhydride is 0.01 to 10 wt% , preferably from 0.05 to 5
重量%である。 In weight percent. この含有率が0.01重量%より低いと接着力の改善効果が低下し、一方、10重量%を超えると加工性が低下してしまう場合がある。 This content reduces the effect of improving the adhesion is lower than 0.01 wt%, whereas, in some cases exceeds 10 wt% the workability is lowered.

【0054】本発明に係るポリマーは、上記(A)〜 [0054] Polymers according to the present invention, the (A) ~
(C)のエチレン−酢酸ビニル系共重合体を40重量% Ethylene (C) - vinyl acetate copolymer 40 wt%
以上、特に60重量%以上含むこと、とりわけ上記(A)〜(C)のエチレン−酢酸ビニル系共重合体のみから構成されることが好ましい。 Above, it includes in particular 60 wt% or more, especially the (A) ~ ethylene (C) - can be composed of only vinyl acetate copolymer preferably. ポリマーがエチレン− Polymer is an ethylene -
酢酸ビニル系共重合体以外のポリマーを含む場合、エチレン−酢酸ビニル系共重合体以外のポリマーとしては、 If it contains polymers other than vinyl acetate copolymer, ethylene - As the vinyl acetate copolymer polymers other than the polymer,
主鎖中に20モル%以上のエチレン及び/又はプロピレンを含有するオレフィン系ポリマー、ポリ塩化ビニル、 Olefin polymers containing ethylene and / or propylene least 20 mol% in the main chain, polyvinyl chloride,
アセタール樹脂等が挙げられる。 Acetal resins.

【0055】このポリマーの架橋剤としては、熱硬化型接着層を形成するためには熱架橋剤としての有機過酸化物が、また、光硬化型接着層を形成するためには光架橋剤としての光増感剤を用いることができる。 [0055] As the crosslinking agent for the polymer, an organic peroxide as a thermal crosslinking agent to form a thermosetting adhesive layer, also as a photo crosslinking agent to form a photocurable adhesive layer it can be used of the photosensitizer.

【0056】ここで、有機過酸化物としては、70℃以上の温度で分解してラジカルを発生するものであればいずれも使用可能であるが、半減期10時間の分解温度が50℃以上のものが好ましく、粘着剤の塗工温度、調製条件、貯蔵安定性、硬化(接着)温度、被貼着対象の耐熱性等を考慮して選択される。 [0056] Here, organic as the peroxides, but both can be used as long as it generates a radical by decomposition at 70 ° C. or higher, the decomposition half-life temperature of 10 hours is not less than 50 ° C. those are preferred, the coating temperature of the adhesive, the preparation conditions, storage stability, curing (bonding) temperature is selected in view of the heat resistance of the bonded wear subject.

【0057】使用可能な有機過酸化物としては、例えば2,5−ジメチルヘキサン−2,5−ジハイドロパーオキサイド、2,5−ジメチル−2,5−ジ(t−ブチルパーオキシ)ヘキシン−3、ジ−t−ブチルパーオキサイド、t−ブチルクミルパーオキサイド、2,5−ジメチル−2,5−ジ(t−ブチルパーオキシ)ヘキサン、 [0057] As the usable organic peroxides, such as 2,5-dimethyl-2,5-hydroperoxide, 2,5-dimethyl-2,5-di (t-butylperoxy) hexyne - 3, di -t- butyl peroxide, t- butyl cumyl peroxide, 2,5-dimethyl-2,5-di (t-butylperoxy) hexane,
ジクミルパーオキサイド、α,α'−ビス(t−ブチルパーオキシイソプロピル)ベンゼン、n−ブチル−4, Dicumyl peroxide, alpha,. Alpha .'- bis (t-butylperoxy isopropyl) benzene, n- butyl-4,
4'−ビス(t−ブチルパーオキシ)バレレート、1, 4'-bis (t-butylperoxy) valerate, 1,
1−ビス(t−ブチルパーオキシ)シクロヘキサン、 1,1-bis (t-butylperoxy) cyclohexane,
1,1−ビス(t−ブチルパーオキシ)−3,3,5− 1,1-bis (t-butylperoxy) -3,3,5
トリメチルシクロヘキサン、t−ブチルパーオキシベンゾエート、ベンゾイルパーオキサイド、t−ブチルパーオキシアセテート、メチルエチルケトンパーオキサイド、2,5−ジメチルヘキシル−2,5−ビスパーオキシベンゾエート、ブチルハイドロパーオキサイド、p− Trimethylcyclohexane, t- butyl peroxybenzoate, benzoyl peroxide, t- butyl peroxy acetate, methyl ethyl ketone peroxide, 2,5-dimethyl-hexyl-2,5-bis peroxybenzoate, butyl hydroperoxide, p-
メンタンハイドロパーオキサイド、p−クロロベンゾイルパーオキサイド、ヒドロキシヘプチルパーオキサイド、クロロヘキサノンパーオキサイド、オクタノイルパーオキサイド、デカノイルパーオキサイド、ラウロイルパーオキサイド、クミルパーオキシオクトエート、サクシニックアシッドパーオキサイド、アセチルパーオキサイド、t−ブチルバーオキシ(2−エチルヘキサノエート)、m−トルオイルパーオキサイド、t−ブチルパーオキシイソブチレート、2,4−ジクロロベンゾイルパーオキサイド等が挙げられる。 Menthane hydroperoxide, p- chlorobenzoyl peroxide, hydroxyheptyl peroxide, chloro hexanone peroxide, octanoyl peroxide, decanoyl peroxide, lauroyl peroxide, cumylperoxy octoate, succinate Nick acid peroxide, acetyl peroxide oxide, t- butyl bar oxy (2-ethylhexanoate), m-toluoyl peroxide, t- butyl peroxy isobutyrate, 2,4-dichlorobenzoyl peroxide, and the like. 有機過酸化物としては、 The organic peroxide,
これらのうちの少なくとも1種が単独で又は混合して用いられ、通常前記ポリマーに対し0.1〜10重量%が添加される。 At least one of these is used alone or as a mixture thereof, 0.1 to 10 wt% with respect to normal the polymer is added.

【0058】一方、光増感剤(光重合開始剤)としては、ラジカル光重合開始剤が好適に用いられる。 [0058] On the other hand, the photosensitizer (photopolymerization initiator), a radical photopolymerization initiator is preferably used. ラジカル光重合開始剤のうち、水素引き抜き型開始剤としてはベンゾフェノン、o−ベンゾイル安息香酸メチル、4− Among radical photopolymerization initiator, a hydrogen abstraction type initiators benzophenone, o- benzoyl benzoate, 4-
ベンゾイル−4'−メチルジフェニルサルファイド、イソプロピルチオキサントン、ジエチルチオキサントン、 Benzoyl-4'-methyl diphenyl sulfide, isopropylthioxanthone, diethylthioxanthone,
4−(ジエチルアミノ)安息香酸エチル等が使用可能である。 4- (diethylamino) ethyl benzoate and the like can be used. また、ラジカル光重合開始剤のうち、分子内開裂型開始剤として、ベンゾインエーテル、ベンゾイルプロピルエーテル、ベンジルジメチルケタール、α−ヒドロキシアルキルフェノン型として、2−ヒドロキシ−2− Further, of the radical photopolymerization initiator, as intramolecular cleavage type initiators, benzoin ether, benzoyl propyl ether, benzyl dimethyl ketal, as α- hydroxyalkylphenone type, 2-hydroxy-2-
メチル−1−フェニルプロパン−1−オン、1−ヒドロキシシクロヘキシルフェニルケトン、アルキルフェニルグリオキシレート、ジエトキシアセトフェノンが、また、α−アミノアルキルフェノン型として、2−メチル−1− [4−(メチルチオ)フェニル)−2−モルフォリノプロパノン−1、2−ベンジル−2−ジメチルアミノ−1−(4−モルフォリノフェニル)ブタノン−1 Methyl-1-phenylpropane-1-one, 1-hydroxycyclohexyl phenyl ketone, alkyl phenyl glyoxylate, diethoxy acetophenone, also as α- aminoalkylphenone type, 2-methyl-1- [4- (methylthio ) phenyl) -2-morpholinopropanone-1,2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) butanone -1
が、またアシルフォスフィンオキサイド等が用いられる。 But also acylphosphine oxide and the like are used. 光増感剤としては、これらのうちの少なくとも1種が単独で又は混合して用いられ、通常前記ポリマーに対し0.1〜10重量%が添加される。 The photosensitizer, at least one of these is used alone or as a mixture, from 0.1 to 10 wt% with respect to normal the polymer is added.

【0059】本発明に係る粘着層は、接着促進剤としてシランカップリング剤を含むことが好ましい。 [0059] The present invention in accordance adhesive layer preferably contains a silane coupling agent as an adhesion promoter. シランカップリング剤としては、ビニルトリエトキシシラン、ビニルトリス(β−メトキシエトキシ)シラン、γ−メタクリロキシプロピルトリメトキシシラン、ビニルトリアセトキシシラン、γ−グリシドキシプロピルトリメトキシシラン、γ−グリシドキシプロピルトリエトキシシラン、β−(3,4−エポキシシクロヘキシル)エチルトリメトキシシラン、ビニルトリクロロシラン、γ−メルカプトプロピルトリメトキシシラン、γ−アミノプロピルトリエトキシシラン、N−β−(アミノエチル)−γ The silane coupling agents, vinyltriethoxysilane, vinyltris (beta-methoxyethoxy) silane, .gamma.-methacryloxypropyl trimethoxysilane, vinyl triacetoxy silane, .gamma.-glycidoxypropyltrimethoxysilane, .gamma.-glycidoxy aminopropyltriethoxysilane, beta-(3,4-epoxycyclohexyl) ethyltrimethoxysilane, vinyltrichlorosilane, .gamma.-mercaptopropyltrimethoxysilane, .gamma.-aminopropyltriethoxysilane, N-beta-(aminoethyl)-gamma
−アミノプロピルトリメトキシシラン等の1種又は2種以上の混合物が用いられる。 - one or more mixtures of such aminopropyltrimethoxysilane are used. これらのシランカップリング剤は、前記ポリマーに対し、通常0.01〜5重量% These silane coupling agents, relative to the polymer, usually 0.01 to 5 wt%
程度用いられる。 The extent used.

【0060】更に接着促進剤としてはエポキシ基含有化合物を配合しても良く、この場合、エポキシ基含有化合物としては、トリグリシジルトリス(2−ヒドロキシエチル)イソシアヌレート、ネオペンチルグリコールジグリシジルエーテル、1,6−ヘキサンジオールジグリシジルエーテル、アリルグリシジルエーテル、2−エチルヘキシルグリシジルエーテル、フェニルグリシジルエーテル、フェノール(EO) 5グリシジルエーテル、p− [0060] Still adhesion promoter may be blended with the epoxy group-containing compound, in this case, as the epoxy group-containing compound, triglycidyl tris (2-hydroxyethyl) isocyanurate, neopentyl glycol diglycidyl ether, 1 , 6-hexanediol diglycidyl ether, allyl glycidyl ether, 2-ethylhexyl glycidyl ether, phenyl glycidyl ether, phenol (EO) 5 glycidyl ether, p-
t−ブチルフェニルグリシジルエーテル、アジピン酸ジグリシジルエステル、フタル酸ジグリシジルエステル、 t- butylphenyl glycidyl ether, diglycidyl adipate, diglycidyl phthalate,
グリシジルメタクリレート、ブチルグリシジルエーテル等が挙げられる。 Glycidyl methacrylate, butyl glycidyl ether, and the like. また、エポキシ基を含有するポリマーをアロイ化することによっても同様の効果を得ることができる。 Further, a polymer containing an epoxy group can be obtained similar effects by alloying. これらのエポキシ基含有化合物は、1種又は2 These epoxy group-containing compound, one or
種以上の混合物として、前記ポリマーに対し、通常0. As a mixture of more species, relative to the polymer, usually 0.
1〜20重量%程度用いられる。 About 1 to 20% by weight is used.

【0061】粘着層ないし接着層の物性(機械的強度、 [0061] Physical properties of the adhesive layer or adhesive layer (mechanical strength,
接着性、光学的特性、耐熱性、耐湿性、耐候性、架橋速度等)の改良や調節のために、粘着層には、アクリロキシ基、メタクリロキシ基又はアリル基を有する化合物を配合することもできる。 Adhesion, optical properties, heat resistance, moisture resistance, weather resistance, due to the improvements and adjustment of crosslinking rate, etc.), the adhesive layer may be compounded compound having an acryloxy group, methacryloxy group or allyl group .

【0062】この目的で用いられる化合物としては、アクリル酸又はメタクリル酸誘導体、例えばそのエステル及びアミドが最も一般的であり、エステル残基としてはメチル、エチル、ドデシル、ステアリル、ラウリルのようなアルキル基のほかに、シクロヘキシル基、テトラヒドロフルフリル基、アミノエチル基、2−ヒドロキシエチル基、3−ヒドロキシプロピル基、3−クロロ−2− [0062] Compounds used for this purpose, acrylic acid or methacrylic acid derivatives, such as its an ester and amides are most common, as the ester residues methyl, ethyl, dodecyl, stearyl, alkyl groups such as lauryl Besides, a cyclohexyl group, tetrahydrofurfuryl group, aminoethyl group, 2-hydroxyethyl group, 3-hydroxypropyl group, 3-chloro-2
ヒドロキシプロピル基等が挙げられる。 Hydroxypropyl group and the like. また、エチレングリコール、トリエチレングリコール、ポリプロピレングリコール、ポリエチレングリコール、トリメチロールプロパン、ペンタエリスリトール等の多官能アルコールとのエステルも同様に用いられる。 The ethylene glycol, triethylene glycol, polypropylene glycol, polyethylene glycol, trimethylol propane, esters of polyfunctional alcohols such as pentaerythritol is used as well. アミドとしては、ダイアセトンアクリルアミドが代表的である。 Examples of the amide, diacetone acrylamide is typical. 多官能架橋助剤としては、トリメチロールプロパン、ペンタエリスリトール、グリセリン等のアクリル酸又はメタクリル酸エステル、アリル基を有する化合物としては、トリアリルシアヌレート、トリアリルイソシアヌレート、フタル酸ジアリル、イソフタル酸ジアリル、マレイン酸ジアリル等が挙げられる。 The polyfunctional coagent, trimethylolpropane, pentaerythritol, acrylic acid or methacrylic acid esters such as glycerin, as a compound having an allyl group, triallyl cyanurate, triallyl isocyanurate, diallyl phthalate, diallyl isophthalate , and diallyl maleate and the like. これらの化合物は1種又は2種以上の混合物として、前記ポリマーに対し、通常0.1〜5 These compounds as one or more mixtures, relative to the polymer, 0.1 to 5
0重量%、好ましくは0.5〜30重量%添加使用される。 0 wt%, preferably 0.5 to 30% by weight additives used. この添加量が50重量%を超えると粘着剤の調製時の作業性や塗工性を低下させることがある。 The addition amount is may reduce the workability and coating properties at the time of preparation of the adhesive exceeds 50% by weight.

【0063】更に、加工性や貼り合わせ等の向上の目的で炭化水素樹脂を粘着層中に添加することができる。 [0063] Furthermore, it is possible to add a hydrocarbon resin in the adhesive layer in workability and bonding improvement such purposes. この場合、添加される炭化水素樹脂は天然樹脂系、合成樹脂系のいずれでもよい。 In this case, the hydrocarbon resin added natural resin may be either of synthetic resin. 天然樹脂系としてはロジン、ロジン誘導体、テルペン系樹脂が好適に用いられる。 As the natural resin rosin, rosin derivatives, terpene resin is preferably used. ロジンではガム系樹脂、トール油系樹脂、ウッド系樹脂を用いることができる。 The rosin can be used gum resin, tall oil resin, wood resin. ロジン誘導体としてはロジンをそれぞれ水素化、不均一化、重合、エステル化、金属塩化したものを用いることができる。 Each hydrogenated rosin as rosin derivatives, disproportionation, polymerization, esterification, can be used those metal chlorides. テルペン系樹脂としてはα−ピネン、β−ピネン等のテルペン系樹脂の他、テルペンフェノール樹脂を用いることができる。 As the terpene resin other α- pinene, terpene resins β- pinene, it can be used terpene phenol resin. また、その他の天然樹脂としてダンマル、コーバル、シェラックを用いてもよい。 Furthermore, dammar as other natural resins, copal may be used shellac. 一方、合成樹脂系では石油系樹脂、フェノール系樹脂、キシレン系樹脂が好適に用いられる。 On the other hand, petroleum resins with a synthetic resin, phenol resin, xylene resin is preferably used. 石油系樹脂では脂肪族系石油樹脂、芳香族系石油樹脂、脂環族系石油樹脂、共重合系石油樹脂、水素化石油樹脂、 Petroleum resin aliphatic petroleum resins, aromatic petroleum resins, alicyclic petroleum resins, copolymer petroleum resins, hydrogenated petroleum resins,
純モノマー系石油樹脂、クマロンインデン樹脂を用いることができる。 Pure monomer petroleum resin, coumarone-indene resin. フェノール系樹脂ではアルキルフェノール樹脂、変性フェノール樹脂を用いることができる。 The phenolic resin can be used alkylphenol resin, a modified phenol resin. キシレン系樹脂ではキシレン樹脂、変性キシレン樹脂を用いることができる。 The xylene-based resins can be used xylene resin, a modified xylene resin. これら炭化水素樹脂の添加量は適宜選択されるが、ポリマーに対して1〜200重量%が好ましく、更に好ましくは5〜150重量%である。 The addition amount of these hydrocarbon resins may be suitably selected, preferably 1 to 200% by weight with respect to the polymer, more preferably from 5 to 150% by weight.

【0064】以上の添加剤のほか、本発明においては、 [0064] In addition to the above additives, in the present invention,
老化防止剤、紫外線吸収剤、染料、加工助剤等を本発明の目的に支承をきたさない範囲で粘着層中に配合してもよい。 Antioxidants, UV absorbers, dyes, processing aids such as within a range that does not cause the bearing to the object of the present invention may be formulated into the adhesive layer.

【0065】粘着層bは、前述の金属箔aに、前記エチレン−酢酸ビニル系共重合体、架橋剤及び必要に応じてその他の添加剤と導電性粒子とを所定の割合で均一に混合したものをロールコーター、ダイコーター、ナイフコーター、マイカバーコーター、フローコーター、スプレーコーター等により塗工することにより容易に形成することができる。 [0065] the adhesive layer b is the aforementioned metal foil a, the ethylene - vinyl acetate copolymer, and homogeneously mixing the crosslinking agent and the other as necessary additives and conductive particles at a predetermined ratio things a roll coater, die coater, knife coater, can be easily formed by coating the My cover coater, flow coater, spray coater or the like.

【0066】このような粘着層bの厚さは通常の場合5 [0066] The thickness of the adhesive layer b is usually 5
〜100μm程度とされる。 It is about ~100μm.

【0067】請求項1の電磁波シールド性光透過窓材において、透明基板2A,2Bの構成材料としては、ガラス、ポリエステル、ポリエチレンテレフタレート(PE [0067] In the electromagnetic shielding and light transmitting plate according to claim 1, the transparent substrate 2A, as the material of 2B, glass, polyester, polyethylene terephthalate (PE
T)、ポリブチレンテレフタレート、ポリメチルメタアクリレート(PMMA)、アクリル板、ポリカーボネート(PC)、ポリスチレン、トリアセテートフィルム、 T), polybutylene terephthalate, polymethyl methacrylate (PMMA), acrylic board, polycarbonate (PC), polystyrene, triacetate film,
ポリビニルアルコール、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリエチレン、エチレン−酢酸ビニル共重合体、ポリビニルブチラール、金属イオン架橋エチレン− Polyvinyl alcohol, polyvinyl chloride, polyvinylidene chloride, polyethylene, ethylene - vinyl acetate copolymer, polyvinyl butyral, metal ion crosslinked ethylene -
メタアクリル酸共重合体、ポリウレタン、セロファン等、好ましくは、ガラス、PET、PC、PMMAが挙げられるが、本発明においては、透明基板2A、2Bのうち、少なくとも一方は強化ガラスよりなるものを用いる。 Methacrylic acid copolymers, polyurethane, cellophane, etc., preferably, glass, PET, PC, although PMMA and the like, in the present invention, the transparent substrate 2A, among 2B, at least one of used ones made of reinforced glass .

【0068】本発明において、この透明基板2A及び/ [0068] In the present invention, the transparent substrate 2A and /
又は2Bを構成するガラスとしては、好ましくは化学強化ガラスを用いる。 Or as the glass constituting the 2B, preferably using a chemically strengthened glass.

【0069】この化学強化ガラスとしては、例えば、次のようなものを用いることができる。 [0069] As the chemically strengthened glass, for example, it can be used as follows.

【0070】 アルカリ成分としてナトリウムイオンを含有するガラスを、カリウムイオンを含有する溶融塩に接触させてナトリウムイオンとカリウムイオンとのイオン交換により、ガラス表面に圧縮層を形成し、その後ガラス表面をリチウム塩水溶液に接触させて、表面にリチウムイオンを固定したガラス。 [0070] lithium glass containing sodium ions as the alkali component, by ion exchange of sodium ions to potassium ions is brought into contact with the molten salt containing potassium ions, to form a compressed layer in the glass surface, then the glass surface It is brought into contact with an aqueous salt solution, the glass fixing the lithium ion to the surface. アルカリ成分としてナトリウムイオンを含有するガラスを、硝酸亜鉛と硝酸カリウムからなる混合溶融塩に漬け、ガラス表面に亜鉛イオンを含むアルカリ溶出防止層を形成したガラス。 The glass containing sodium ions as the alkali component, dipped in a molten salt mixture consisting of zinc nitrate and potassium nitrate, to form an alkali elution preventing layer containing zinc ions to the glass surface glass. アルカリ成分としてナトリウムイオンを含有するガラスを、硝酸カルシウムと硝酸カリウムからなる混合溶融塩に漬け、ガラス表面にガラス内部よりも少ないアルカリ成分を含むアルカリ溶出防止層を形成したガラス。 The glass containing sodium ions as the alkali component, dipped in a molten salt mixture consisting of calcium nitrate and potassium nitrate, to form an alkali elution preventing layer containing less alkaline component than the glass inside the glass surface glass. アルカリ成分としてナトリウムイオンを含有するガラスを、硝酸リチウムと硝酸カリウムからなる混合溶融塩に漬け、ガラス表面にリチウムイオンを含有するアルカリ溶出防止層を形成したガラス。 The glass containing sodium ions as the alkali component, dipped in a molten salt mixture consisting of lithium nitrate and potassium nitrate, to form an alkali elution preventing layer containing lithium ions into the glass surface glass.

【0071】の強化ガラスでは、カリウムイオンを含む溶融塩中でガラス表面近傍のナトリウムイオンをカリウムイオンに置換した後、リチウム塩水溶液中で溶融塩を溶解し、さらに、別のリチウム塩水溶液中に浸漬することにより、ガラスの化学的耐久性が大幅に向上する。 [0071] In the reinforced glass, after replacing the sodium ions in the vicinity of the glass surface to potassium ions in a molten salt containing potassium ions, to dissolve the molten salt in the lithium salt solution, further, in a separate lithium salt solution by immersion, chemical durability of the glass is greatly improved.
用いるリチウム塩としては、硝酸リチウム、硫酸リチウムが好んで用いられ、なかでも硝酸リチウムが好ましい。 Examples of the lithium salt used, lithium nitrate, used prefer lithium sulfate, among them lithium nitrate are preferred. 硝酸リチウム水溶液の硝酸リチウム濃度は、10 -4 Lithium nitrate concentration of lithium nitrate aqueous solution, 10 -4
モル/リットル以上とするのが好ましく、1モル/リットル以上の濃度としても化学的耐久性は濃度に応じて増大しないことから、特に10 -4 〜1モル/リットルの濃度範囲、とりわけ10 -2 〜1モル/リットルの範囲とするのが好ましい。 It is preferable to be mole / l or more, 1 mol / chemical durability as concentrations above liter since no increase depending on the concentration, in particular 10 -4 to 1 mol / liter concentration range, especially 10-2 preferably in the range of ~ 1 mole / liter.

【0072】このように溶融塩を用いたイオン交換反応により化学強化されたガラス表面は、非常に高活性であり、水溶液に触れるとアルカリ金属イオンと水素イオンとのイオン交換反応が行われ、一定量の水和層がガラス表面に形成され表面が安定化する。 [0072] chemically strengthened glass surface by an ion exchange reaction using such molten salt is very high activity, ion exchange reaction between alkali metal ions and hydrogen ions on contact with an aqueous solution is performed, a constant surface hydration layer amount is formed on the glass surface is stabilized. この安定化がリチウムイオンが存在する水溶液中で行われると、リチウムイオンがガラス表面に固定され、ガラス表面に耐候性の強い層を形成する。 When the stabilization is carried out in aqueous solution the presence of lithium ions, lithium ions are fixed to the glass surface to form a strong layer on the glass surface weatherproof. これにより、ガラスの機械的強度を向上させると共にガラス表面の高温高湿雰囲気下の化学的耐久性が向上し、ガラス表面にヤケの発生が抑制される。 Accordingly, improves the mechanical strength of the glass and improving chemical durability of high temperature and high humidity atmosphere of a glass surface, the occurrence of scorching on the glass surface is suppressed.

【0073】の強化ガラスは、硝酸亜鉛をモル濃度で0.01〜0.5%含有する硝酸亜鉛と硝酸カリウムからなる混合溶融塩、或いは、硝酸亜鉛をモル濃度で20 [0073] The tempered glass, molten salt mixture consisting of zinc nitrate and potassium nitrate, containing 0.01-0.5% zinc nitrate at a molar concentration, or zinc nitrate at a molar concentration of 20
〜50%含有する硝酸亜鉛と硝酸カリウムからなる混合溶融塩を用いて製造される。 It is prepared by using a mixed molten salt consisting of zinc nitrate and potassium nitrate, containing 50%. 硝酸亜鉛は単独で存在する場合はその分解温度は350℃であるが、硝酸カリウム中に上限値として0.5モル%までの量で含まれるときは、その分解温度以上であっても安定して存在するため、330℃〜450℃の混合溶融塩にガラスを漬けることで溶融塩の安定性確保と処理時間の短縮化を図ることができる。 Although when zinc nitrate is present alone its decomposition temperature is 350 ° C., when included in an amount of up to 0.5 mol% as the upper limit in the potassium nitrate are stable even its decomposition temperature or higher for present, it is possible to shorten the stability ensured and the processing time of the molten salt by immersing glass mixed molten salt of 330 ° C. to 450 ° C..

【0074】また、硝酸亜鉛をモル濃度で20〜50% [0074] In addition, 20% to 50% zinc nitrate at a molar concentration
含有する硝酸亜鉛と硝酸カリウムからなる混合溶融塩を用いると硝酸リチウムと硝酸亜鉛の系が有する共融点近傍の低い温度で処理することができ、混合溶融塩の共融点以上350℃以下の比較的低温度域で強化処理を行うことができる。 When a mixed molten salt consisting of zinc nitrate and potassium nitrate containing can be treated at a low temperature of eutectic vicinity included in the system of lithium nitrate and zinc nitrate, following a relatively low 350 ° C. or higher eutectic point of the mixed molten salt strengthening treatment in the temperature range can be carried out.

【0075】この方法では、溶融した硝酸カリウムと硝酸亜鉛との混合塩中にアルカリ成分としてナトリウムイオンを含むガラスを漬けると、ガラス中のナトリウムイオンと溶融塩中の亜鉛イオンがイオン交換により置換し、表面近傍に亜鉛を含む層が形成され、この層により機械的強度が向上すると共に高耐湿性が付与される。 [0075] In this way, when immersing glass containing sodium ions as the alkali component in the mixed salts with molten potassium nitrate and zinc nitrate, zinc ions of sodium ions and the molten salt in the glass is replaced by ion exchange, layer containing zinc is formed in the vicinity of the surface, high moisture resistance is imparted with mechanical strength is improved by this layer. 特に、硝酸亜鉛を20〜50モル%含む混合塩では、その共融点近傍の低い温度で、表面近傍に亜鉛を含む層を形成することができ、この層により機械的強度が向上すると共に高耐湿性が付与される。 In particular, high humidity with a mixed salt comprising zinc nitrate 20 to 50 mol%, at a low temperature of the eutectic point near, it is possible to form a layer containing zinc in the vicinity of the surface, the mechanical strength is improved by this layer sex is given.

【0076】の強化ガラスは、アルカリ成分としてナトリウムイオンを含有するガラスを、硝酸カルシウムをモル濃度で10〜40%含有する硝酸カルシウムと硝酸カリウムからなる混合溶融塩に漬け、ガラス表面近傍にアルカリ溶出防止層を形成することにより製造される。 Glass of [0076] the glass, dipped in a mixed molten salt consisting of calcium nitrate and potassium nitrate, containing 10-40% calcium nitrate in molar concentrations, the alkaline elution preventive near the glass surface containing sodium ions as the alkali component It is produced by forming a layer.
ここで混合溶融塩の温度は350〜470℃とするのが好ましい。 Wherein the temperature of the mixed molten salt is preferably a three hundred fifty to four hundred and seventy ° C..

【0077】この方法では、ガラス表面近傍にアルカリがガラス内部よりも減少した層が形成され、この層により機械的強度が向上すると共に高耐湿性が付与される。 [0077] In this method, a layer of alkali in the vicinity of the glass surface is reduced than the glass is formed, high moisture resistance is imparted with mechanical strength is improved by this layer.

【0078】の強化ガラスは、アルカリ成分としてナトリウムイオンを含有するガラスを、硝酸リチウムをモル濃度で1〜30%含有する硝酸リチウムと硝酸カリウムからなるなる混合溶融塩に漬け、ガラス表面近傍にリチウムイオンを含有するアルカリ溶出防止層を形成することにより製造される。 Glass of [0078] is a glass containing sodium ions as the alkali component, immersed in the molten salt mixture composed consisting lithium nitrate and potassium nitrate, containing 1% to 30% lithium nitrate at a molar concentration of lithium ions in the vicinity of the glass surface It is prepared by forming an alkali elution preventing layer containing. ここで、混合溶融塩の温度は3 Here, the temperature of the mixed molten salt 3
30〜450℃とするのが好ましい。 Preferably in the 30~450 ℃.

【0079】この方法では、ガラス中のナトリウムイオンと溶融塩中のリチウムイオンがイオン交換により置換し、表面近傍にリチウムを含む層が形成され、この層により機械的強度が向上すると共に高耐湿性が付与される。 [0079] In this method, a lithium ion sodium ions in the molten salt in the glass is replaced by ion exchange, a layer containing lithium in the vicinity of the surface is formed, the high moisture resistance together with mechanical strength is improved by this layer There are granted.

【0080】なお、前記混合溶融塩にガラスを漬けるに先立ち、硝酸カリウムのみからなる溶融塩に漬けてその溶融塩中のカリウムイオンとガラス中のナトリウムイオンとをイオン交換することが好ましい。 [0080] Prior to the immersing glass to the molten salt mixture, it is preferred that the sodium ions immersed in a molten salt consisting only of potassium nitrate potassium ions in the glass in the molten salt ion-exchange.

【0081】透明基板2A,2Bの厚さは得られる窓材の用途による要求特性(例えば、強度、軽量性)等によって適宜決定されるが、通常の場合、0.1〜10mm [0081] transparent substrate 2A, request by use of the window material thickness of 2B obtained characteristics (e.g., strength, light weight) is appropriately determined by such, usually, 0.1 to 10 mm
の範囲とされる。 It is in the range.

【0082】透明基板2A,2Bは、必ずしも同材質である必要はなく、例えば、PDP前面フィルタのように、表面側のみに耐傷付性や耐久性等が要求される場合には、この表面側となる透明基板2Aを厚さ0.1〜1 [0082] transparent substrate 2A, 2B is not necessarily the same material, for example, as a PDP front filter, when the surface side only scratch resistance and durability, etc. is required, this surface the transparent substrate 2A as thickness of 0.1 to 1
0mm程度の強化ガラス板とし、裏面側(電磁波発生源側)の透明基板2Bを厚さ1μm〜10mm程度のPE And 0mm about tempered glass sheet, the back side having a thickness of about 1μm~10mm the transparent substrate 2B of (electromagnetic wave generating source side) PE
Tフィルム又はPET板、アクリルフィルム又はアクリル板、ポリカーボネートフィルム又はポリカーボネート板等とすることもできる。 T films or PET plate, may be an acrylic film or an acrylic plate, a polycarbonate film or polycarbonate plate or the like.

【0083】本実施例の電磁波シールド性光透過窓材1 [0083] electromagnetic-wave shielding and light transmitting plate 1 of this embodiment
では、裏面側となる透明基板2Bの周縁部にアクリル樹脂をベースとする黒枠塗装6が設けられている。 So black frame paint 6 based on acrylic resin is provided on the periphery of the transparent substrate 2B which is a rear surface side.

【0084】また、本実施例の電磁波シールド性光透過窓材1では、表面側となる透明基板2Aの表面に反射防止膜5が形成されている。 [0084] In the electromagnetic-wave shielding and light transmitting plate 1 of this embodiment, the anti-reflection film 5 on the surface of the transparent substrate 2A to be the surface side is formed. この透明基板2Aの表面側に形成される反射防止膜5としては、下記(1)の単層膜や、高屈折率透明膜と低屈折率透明膜との積層膜、例えば、下記(2)〜(5)のような積層構造の積層膜が挙げられる。 The antireflection film 5 formed on the surface side of the transparent substrate 2A, a single-layer film or a high refractive index transparent films and low-refractive-index transparent film and the laminated film of the following (1), for example, the following (2) a laminated film of multilayer structure, such as a - (5) below.

【0085】(1) 透明基板よりも屈折率の低い透明膜を一層積層したもの (2) 高屈折率透明膜と低屈折率透明膜を1層ずつ合計2層に積層したもの (3) 高屈折率透明膜と低屈折率透明膜を2層ずつ交互に合計4層積層したもの (4) 中屈折率透明膜/高屈折率透明膜/低屈折率透明膜の順で1層ずつ、合計3層に積層したもの (5) 高屈折率透明膜/低屈折率透明膜の順で各層を交互に3層ずつ、合計6層に積層したもの 高屈折率透明膜としては、ITO(スズインジウム酸化物)又はZnO、AlをドープしたZnO、TiO 2 [0085] (1) clear that to further laminated lower refractive index transparent film than the substrate (2) a laminate of a total of two layers, one layer of high-refractive-index transparent films and low-refractive-index transparent film (3) High layer-by-layer in the order of refractive index transparent films and low-refractive-index transparent films alternately on the sum 4-layer laminated by two layers (4) in the refractive-index transparent film / high refractive index transparent film / low refractive index transparent films, the total 3 formed by laminating a layer (5) by three layers each layer alternately in this order of the high-refractive-index transparent film / low refractive index transparent film, as the high-refractive-index transparent film formed by laminating a total of six layers, ITO (indium tin oxide) or ZnO, ZnO doped with Al, TiO 2,
SnO 2 、ZrO等の屈折率1.8以上の薄膜、好ましくは透明導電性の薄膜を形成することができる。 Refractive index of 1.8 or more of a thin film of SnO 2, ZrO, etc., preferably are capable of forming a transparent conductive thin film. また、 Also,
低屈折率透明膜としてはSiO 2 、MgF 2 、Al 23等の屈折率が1.6以下の低屈折率材料よりなる薄膜を形成することができる。 The low refractive index transparent film can form a thin film having a refractive index such as SiO 2, MgF 2, Al 2 O 3 is formed of 1.6 or lower refractive index material. これらの膜厚は光の干渉で可視光領域での反射率を下げるため、膜構成、膜種、中心波長により異なってくるが4層構造の場合、透明基板側の第1層(高屈折率透明膜)が5〜50nm、第2層(低屈折率透明膜)が5〜50nm、第3層(高屈折率透明膜)が50〜100nm、第4層(低屈折率透明膜)が50〜150nm程度の膜厚で形成される。 Since these film thickness to reduce the reflectance in the visible light region in the interference of light, the film structure, film type, if different come although four-layer structure by a center wavelength, the transparent substrate-side first layer (high refractive index transparent film) is 5 to 50 nm, a second layer (low-refractive-index transparent film) is 5 to 50 nm, the third layer (high-refractive-index transparent film) is 50 to 100 nm, the fourth layer (low-refractive-index transparent film) 50 It is formed to a thickness of about ~150Nm.

【0086】従来の電磁波シールド性光透過窓材では、 [0086] In a conventional electromagnetic-wave shielding and light transmitting plate,
画面における光の反射で画像が見難く、視野角が小さく、横からの入射光に対して画面内容を十分に視認できないという欠点があったが、このように電磁波発生源側と反対側に位置する透明基板2Aの表面に、高屈折率透明膜と低屈折率透明膜との積層膜等よりなる反射防止膜5を形成することにより、この反射防止膜の光の干渉作用で光の反射を防止して高視野角とすることができる。 Images difficult to see in reflection of light on the screen, a small viewing angle, but the screen contents to the incident light from the side has a drawback that can not be fully visible, positioned on the opposite side of the electromagnetic wave generating source side such on the surface of the transparent substrate 2A to, by forming the anti-reflection film 5 comprising a laminated film of the high refractive index transparent films and low-refractive-index transparent films, the reflection of light at the interference of light in the anti-reflection film preventing and can be a high viewing angle.

【0087】また、このような反射防止膜5の上に更に汚染防止膜を形成して、表面の耐汚染性を高めるようにしても良い。 [0087] Moreover, such a further form an antifouling film on the antireflection film 5, may be enhanced stain resistance of the surface. この場合、汚染防止膜としては、フッ素系薄膜、シリコン系薄膜等よりなる膜厚1〜1000nm In this case, the contamination prevention film, the film thickness made of fluorine-based thin film, silicon-based thin film and the like 1~1000nm
程度の薄膜が好ましい。 The extent of the thin film is preferable.

【0088】本発明の電磁波シールド性光透過窓材では、表面側となる透明基板2Aには、更に、シリコン系材料等によるハードコート処理、或いはハードコート層内に光散乱材料を練り込んだアンチグレア加工等を施しても良い。 [0088] In the electromagnetic wave shielding and light transmitting plate of the present invention, the transparent substrate 2A as a surface side, further, kneaded light scattering material to a hard coat treatment or a hard coat layer of silicon based material antiglare processing, or the like may be subjected to. また、透明基板2Aに前述の反射防止フィルム、ハードコートフィルム、アンチグレアフィルム等を透明粘着剤や透明接着剤で貼り付けることもできる。 Further, antireflection film described above on a transparent substrate 2A, a hard coat film, also paste with a transparent adhesive or a transparent adhesive anti-glare film or the like.

【0089】一方、裏面側となる、即ち、電磁波発生源側に位置する透明基板2Bには、金属薄膜又は透明導電性膜等の熱線反射コート等を施して機能性を高めることができる。 [0089] On the other hand, the rear surface side, i.e., the transparent substrate 2B located electromagnetic wave generating source side, it is possible to enhance the functionality subjected to heat-reflecting coating or the like, such as a metal thin film or a transparent conductive film.

【0090】この場合、透明基板2Bに形成される熱線反射性の透明導電膜としては、ITO(スズインジウム酸化物)、ATO(スズアンチモン酸化物)、ZnO、 [0090] In this case, as the heat ray reflective transparent conductive film formed on a transparent substrate 2B, ITO (indium tin oxide), ATO (antimony tin oxide), ZnO,
AlをドープしたZnO、SnO 2等の薄膜を形成することができる。 ZnO doped with Al, it is possible to form a thin film of SnO 2 or the like. また、金、銀、銅、プラチナ等の金属薄膜又はこれらの元素を含む合金薄膜を薄くコーティングすることでも可視光透過性を有し、赤外光を反射させるような熱線反射膜も用いることができる。 Further, gold, silver, copper, and by thinly coating an alloy thin film comprising a metal thin film or these elements, such as platinum has a visible light transparency, also be used heat-reflecting layer such as to reflect infrared light it can. その膜厚は、 The film thickness,
要求される電磁波シールド性、光透過性、断熱性によっても異なるが、通常の場合、金属酸化物薄膜の場合5Å Required electromagnetic shielding property, light transmittance, varies depending thermal insulation, usually, when the metal oxide thin film 5Å
〜5μm程度、金属薄膜の場合2Å〜3000Å程度であることが好ましい。 About 5 .mu.m, it is preferable if the metal thin film is about 2A~3000A.

【0091】これらの酸化物透明導電膜及び金属薄膜は積層化することで導電性、熱線カット性を高めることができる。 [0091] These transparent conductive oxide film and the metal thin film can be enhanced conductivity by laminating a heat-ray shielding property. 層数が多すぎると可視光領域の透明性が損なわれる。 When the number of layers is too large transparency in the visible light region is impaired. 好ましい積層数は各々1〜20層、合計で2〜4 Preferred number of stacked layers each 20 layers 2-4 in total
1層である。 It is a single layer.

【0092】これらの酸化物透明導電膜及び金属薄膜はスパッタ法や真空蒸着法、イオンプレーティング法、C [0092] These transparent conductive oxide film and the metal thin film is a sputtering method, a vacuum evaporation method, ion plating method, C
VD法等、好ましくは膜厚制御が容易なスパッタ法によりベースとなる透明基板上に形成することができる。 VD method can preferably be formed on the underlying transparent substrate by film thickness control easy sputtering.

【0093】従来の電磁波シールド性光透過窓材では、 [0093] In a conventional electromagnetic-wave shielding and light transmitting plate,
ディスプレイからの熱で画面が加熱するという問題があったが、電磁波発生源側に位置する透明基板2Bの表面に、熱線反射性の透明導電膜を形成することにより、ディスプレイからの熱を反射して、良好な断熱効果を得ることができる。 Although the screen by heat from the display there is a problem that the heat on the surface of the transparent substrate 2B located electromagnetic wave generating source side, by forming a heat ray reflective transparent conductive film, and reflects heat from the display Te, it is possible to obtain a good thermal insulation effect. また、特にPDPの場合、発光時に可視光以外に近赤外線が放射されるため、PDP自体のリモコン操作ができなくなる場合もある。 Further, particularly in the case of PDP, since the near infrared is emitted in addition to visible light during light emission, there is a case where remote control of the PDP itself can not. また、周囲の家電製品の誤動作を引き起こす可能性もあるため、この近赤外線領域の光を充分にカットする必要がある。 Moreover, since there is a possibility of causing a malfunction of peripheral appliances, it is necessary to cut the light in the near infrared region sufficiently.

【0094】このような透明導電性膜は表面側の透明基板2Aに形成することもできる。 [0094] It is also possible that such a transparent conductive film is formed on the transparent substrate 2A on the surface side.

【0095】透明基板2A,2Bに介在させる透明導電性フィルム3としては、導電性粒子を分散させた樹脂フィルムを用いることができ、この導電性粒子としては、 [0095] As the transparent substrate 2A, a transparent conductive film 3 to be interposed 2B, the conductive particles can be used a resin film obtained by dispersing, as the conductive particles,
導電性を有するものであれば良く特に制限はないが、例えば、次のようなものが挙げられる。 It is not particularly limited well as long as it has conductivity, for example, as follows.

【0096】(i) カーボン粒子ないし粉末 (ii) ニッケル、インジウム、クロム、金、バナジウム、すず、カドミウム、銀、プラチナ、アルミ、銅、チタン、コバルト、鉛等の金属又は合金或いはこれらの導電性酸化物の粒子ないし粉末 (iii) ポリスチレン、ポリエチレン等のプラスチック粒子の表面に上記(i),(ii)の導電性材料のコーティング層を形成したもの これらの導電性粒子の粒径は、過度に大きいと光透過性や透明導電性フィルム3の厚さに影響を及ぼすことから、0.5mm以下であることが好ましい。 [0096] (i) carbon particles or powder (ii) nickel, indium, chromium, gold, vanadium, tin, cadmium, silver, platinum, aluminum, copper, titanium, cobalt, or alloys or these conductive and lead particles or powder (iii) polystyrene oxide, above the surface of the plastic particles such as polyethylene (i), the particle size of these conductive particles obtained by forming a coating layer of a conductive material (ii) is excessively big from affecting the thickness of the light transmission property and the transparent conductive film 3 is preferably 0.5mm or less. 好ましい導電性粒子の粒径は0.01〜0.5mmである。 The particle size of the preferred conductive particles is 0.01 to 0.5 mm.

【0097】また、透明導電性フィルム3中の導電性粒子の混合割合は、過度に多いと光透過性が損なわれ、過度に少ないと電磁波シールド性が不足するため、透明導電性フィルム3の樹脂に対する重量割合で0.1〜50 [0097] The mixing ratio of the conductive particles in the transparent conductive film 3 is excessively large, the optical transparency is impaired, too small and for electromagnetic shielding properties is insufficient, the transparent conductive film 3 of the resin in a weight ratio of 0.1 to 50
重量%、特に0.1〜20重量%、とりわけ0.5〜2 Wt%, in particular 0.1 to 20% by weight, especially 0.5 to 2
0重量%程度とするのが好ましい。 Preferably about 0 wt%.

【0098】導電性粒子の色、光沢は、目的に応じ適宜選択されるが、ディスプレーフィルタの場合は、黒、茶等の暗色で無光沢のものが好ましい。 [0098] The color of the conductive particles, the gloss is appropriately selected depending on the intended purpose, in the case of display filters, black, those dark dull tea or the like. この場合は、導電性粒子がフィルタの光線透過率を適度に調整することで、画面が見やすくなるという効果もある。 In this case, the conductive particles are appropriately adjusted light transmittance of the filter, there is also an effect that the screen is easier to see.

【0099】なお、透明導電性フィルムのマトリックス樹脂としては、ポリエステル、ポリエチレンテレフタレート(PET)、ポリブチレンテレフタレート、ポリメチルメタクリレート(PMMA)、アクリル板、ポリカーボネート(PC)、ポリスチレン、トリアセテートフィルム、ポリビニルアルコール、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリエチレン、エチレン−酢酸ビニル共重合体、ポリビニルブチラール、金属イオン架橋エチレン−メタクリル酸共重合体、ポリウレタン、セロファン等、好ましくは、PET、PC、PMMAが挙げられる。 [0099] As the matrix resin of the transparent conductive film, polyester, polyethylene terephthalate (PET), polybutylene terephthalate, polymethyl methacrylate (PMMA), acrylic board, polycarbonate (PC), polystyrene, triacetate film, polyvinyl alcohol, polyvinyl chloride, polyvinylidene chloride, polyethylene, ethylene - vinyl acetate copolymer, polyvinyl butyral, metal ion crosslinked ethylene - methacrylic acid copolymer, polyurethane, cellophane, etc., preferably, PET, PC, PMMA and the like.

【0100】このような透明導電性フィルム3の厚さは、電磁波シールド性光透過窓材の用途等によっても異なるが、通常の場合1μm〜5mm程度とされる。 [0100] The thickness of the transparent conductive film 3 is different depending application of the electromagnetic-wave shielding and light transmitting plate, are usually about 1Myuemu~5mm. この透明導電性フィルム3の導電性層の厚さが0.01μm The thickness of the transparent conductive film 3 of the electrically conductive layer is 0.01μm
未満では、電磁波シールドのための導電性層の厚さが薄過ぎ、十分な電磁波シールド性を得ることができず、5 Below, the only the thickness of the conductive layer for electromagnetic shielding is thin, it is impossible to obtain a sufficient electromagnetic shielding property, 5
μmを超えると光透過性が損なわれる恐れがある。 There is a possibility that optical transparency is impaired when it exceeds [mu] m.

【0101】請求項1において、透明基板2A,2Bを透明導電性フィルム3を介して接着する接着用樹脂フィルム4A,4Bの接着樹脂としては、エチレン−酢酸ビニル共重合体、エチレン−アクリル酸メチル共重合体、 [0102] In claim 1, the transparent substrate 2A, adhesive resin film 4A of 2B to be bonded via the transparent conductive film 3, 4B adhesive resins, ethylene - vinyl acetate copolymer, ethylene - methyl acrylate copolymer,
エチレン−(メタ)アクリル酸共重合体、エチレン− Ethylene - (meth) acrylic acid copolymer, ethylene -
(メタ)アクリル酸エチル共重合体、エチレン−(メタ)アクリル酸メチル共重合体、金属イオン架橋エチレン−(メタ)アクリル酸共重合体、部分鹸化エチレン− (Meth) ethyl acrylate copolymer, ethylene - (meth) methyl acrylate copolymer, metal ion crosslinked ethylene - (meth) acrylic acid copolymer, partially saponified ethylene -
酢酸ビニル共重合体、カルボキシルエチレン−酢酸ビニル共重合体、エチレン−(メタ)アクリル−無水マレイン酸共重合体、エチレン−酢酸ビニル−(メタ)アクリレート共重合体等のエチレン系共重合体が挙げられる(なお、「(メタ)アクリル」は「アクリル又はメタクリル」を示す。)。 Include (meth) acrylate copolymer, and ethylene copolymer of - vinyl acetate copolymer, carboxyl ethylene - vinyl acetate copolymer, ethylene - (meth) acrylic - maleic anhydride copolymer, ethylene - vinyl acetate is (Note that "(meth) acryl" means "acryl or methacryl".). その他、ポリビニルブチラール(P Other, polyvinyl butyral (P
VB)樹脂、エポキシ樹脂、アクリル樹脂、フェノール樹脂、シリコン樹脂、ポリエステル樹脂、ウレタン樹脂等も用いることができるが、性能面で最もバランスがとれ、使い易いのはエチレン−酢酸ビニル共重合体(EV VB) resins, epoxy resins, acrylic resins, phenol resins, silicone resins, polyester resins, may also be used urethane resins, take the most balanced in performance, easy-to-use of ethylene - vinyl acetate copolymer (EV
A)である。 It is A). また、耐衝撃性、耐貫通性、接着性、透明性等の点から自動車用合せガラスで用いられているPV Moreover, impact resistance, penetration resistance, have been used in adhesive, automotive laminated glass in terms of transparency and the like PV
B樹脂も好適である。 B resin is also suitable.

【0102】PVB樹脂は、ポリビニルアセタール単位が70〜95重量%、ポリ酢酸ビニル単位が1〜15重量%で、平均重合度が200〜3000、好ましくは3 [0102] PVB resin, polyvinyl acetal units 70 to 95 wt%, polyvinyl acetate units in 15 wt%, average polymerization degree of 200 to 3,000, preferably 3
00〜2500であるものが好ましく、PVB樹脂は可塑剤を含む樹脂組成物として使用される。 Preferably has a 00-2500, PVB resin is used as resin composition containing plasticizer.

【0103】PVB樹脂組成物の可塑剤としては、一塩基酸エステル、多塩基酸エステル等の有機系可塑剤や燐酸系可塑剤が挙げられる。 [0103] As a plasticizer of the PVB resin composition, monobasic acid ester, organic plasticizer and phosphoric acid plasticizers such as polybasic acid esters.

【0104】一塩基酸エステルとしては、酪酸、イソ酪酸、カプロン酸、2−エチル酪酸、ヘプタン酸、n−オクチル酸、2−エチルヘキシル酸、ペラルゴン酸(n− [0104] The monobasic acid ester, butyric acid, isobutyric acid, caproic acid, 2-ethyl butyric acid, heptanoic acid, n- octyl acid, 2-ethylhexyl acid, pelargonic acid (n-
ノニル酸)、デシル酸等の有機酸とトリエチレングリコールとの反応によって得られるエステルが好ましく、より好ましくは、トリエチレン−ジ−2−エチルブチレート、トリエチレングリコール−ジ−2−エチルヘキソエート、トリエチレングリコール−ジ−カプロネート、トリエチレングリコール−ジ−n−オクトエート等である。 Nonyl acid), esters obtained by the reaction of an organic acid with triethylene glycol such as decyl acid, more preferably, triethylene - di-2-ethyl butyrate, triethylene glycol - di-2-Echiruhekiso benzoate, triethylene glycol - di - Kapuroneto, triethylene glycol - di -n- octoate and the like. なお、上記有機酸とテトラエチレングリコール又はトリプロピレングリコールとのエステルも使用可能である。 Incidentally, esters of the organic acid with tetraethylene glycol or tripropylene glycol can also be used.

【0105】多塩基酸エステル系可塑剤としては、例えば、アジピン酸、セバチン酸、アゼライン酸等の有機酸と炭素数4〜8の直鎖状又は分岐状アルコールとのエステルが好ましく、より好ましくは、ジブチルセバケート、ジオクチルアゼレート、ジブチルカルビトールアジペート等が挙げられる。 [0105] As polybasic acid ester plasticizers, such as adipic acid, sebacic acid, esters of linear or branched alcohols of the organic acid and 4 to 8 carbon atoms such as azelaic acid, and more preferably , dibutyl sebacate, dioctyl azelate, dibutyl carbitol adipate and the like.

【0106】燐酸系可塑剤としては、トリブトキシエチルフォスフェート、イソデシルフェニルフォスフェート、トリイソプロピルフォスフェート等が挙げられる。 [0106] As the phosphoric acid type plasticizer, tributoxyethyl phosphate, isodecyl phenyl phosphate, and triisopropyl phosphate and the like.

【0107】PVB樹脂組成物において、可塑剤の量が少ないと製膜性が低下し、多いと耐熱時の耐久性等が損なわれるため、ポリビニルブチラール樹脂100重量部に対して可塑剤を5〜50重量部、好ましくは10〜4 [0107] In PVB resin composition, reduces the film forming property and a small amount of plasticizer, often because the durability at the time of heat is impaired, the plasticizer with respect to 100 parts by weight of the polyvinyl butyral resin 5 50 parts by weight, preferably from 10 to 4
0重量部とする。 And 0 parts by weight.

【0108】PVB樹脂組成物には、更に劣化防止のために、安定剤、酸化防止剤、紫外線吸収剤等の添加剤が添加されていても良い。 [0108] The PVB resin composition may further prevent deterioration, stabilizers, antioxidants, additives such as ultraviolet absorber may be added.

【0109】以下に、樹脂としてEVAを用いた場合を例示して本発明に係る接着層についてより詳細に説明する。 [0109] In the following, a more detailed description adhesive layer illustrated in accordance with the present invention the case of using EVA as a resin.

【0110】EVAとしては酢酸ビニル含有量が5〜5 [0110] vinyl acetate content as EVA is 5 to 5
0重量%、好ましくは15〜40重量%のものが使用される。 0 wt%, preferably those 15 to 40 wt% used. 酢酸ビニル含有量が5重量%より少ないと耐候性及び透明性に問題があり、また40重量%を超すと機械的性質が著しく低下する上に、成膜が困難となり、フィルム相互のブロッキングが生ずる。 There is a problem with the vinyl acetate content is less than 5 wt% in weather resistance and transparency, also on the mechanical properties when more than 40% by weight significantly decreased, the film formation becomes difficult, resulting films mutual blocking .

【0111】架橋剤としては加熱架橋する場合は、有機過酸化物が適当であり、シート加工温度、架橋温度、貯蔵安定性等を考慮して選ばれる。 [0111] In the case of thermal crosslinking is as a cross-linking agent is suitably an organic peroxide, a sheet processing temperature, the crosslinking temperature is selected in consideration of the storage stability and the like. 使用可能な過酸化物としては、例えば2,5−ジメチルヘキサン−2,5−ジハイドロパーオキサイド;2,5−ジメチル−2,5− Usable peroxides, such as 2,5-dimethyl-2,5-hydroperoxide; 2,5-dimethyl-2,5
ジ(t−ブチルパーオキシ)ヘキサン−3;ジーt−ブチルパーオキサイド;t−ブチルクミルパーオキサイド;2,5−ジメチル−2,5−ジ(t−ブチルパーオキシ)ヘキサン;ジクミルパーオキサイド;α,α'− Di (t-butylperoxy) hexane -3; di t-butyl peroxide; t-butyl cumyl peroxide; 2,5-dimethyl-2,5-di (t-butylperoxy) hexane; dicumyl peroxide ; α, α'-
ビス(t−ブチルパーオキシイソプロピル)ベンゼン; Bis (t-butylperoxy isopropyl) benzene;
n−ブチル−4,4−ビス(t−ブチルパーオキシ)バレレート;2,2−ビス(t−ブチルパーオキシ)ブタン;1,1−ビス(t−ブチルパーオキシ)シクロヘキサン;1,1−ビス(t−ブチルパーオキシ)−3, n- butyl-4,4-bis (t-butylperoxy) valerate; 2,2-bis (t-butylperoxy) butane; 1,1-bis (t-butylperoxy) cyclohexane; 1,1 bis (t-butylperoxy) -3,
3,5−トリメチルシクロヘキサン;t−ブチルパーオキシベンゾエート;ベンゾイルパーオキサイド;第3ブチルパーオキシアセテート;2,5−ジメチル−2,5 3,5-trimethylcyclohexane; t-butyl peroxybenzoate; benzoyl peroxide; tertiary butyl peroxy acetate; 2,5-dimethyl-2,5
−ビス(第3ブチルパーオキシ)ヘキシン−3;1,1 - bis (t-butylperoxy) hexyne-3; 1,1
−ビス(第3ブチルパーオキシ)−3,3,5−トリメチルシクロヘキサン;1,1−ビス(第3ブチルパーオキシ)シクロヘキサン;メチルエチルケトンパーオキサイド;2,5−ジメチルヘキシル−2,5−ビスパーオキシベンゾエート;第3ブチルハイドロパーオキサイド;p−メンタンハイドロパーオキサイド;p−クロルベンゾイルパーオキサイド;第3ブチルパーオキシイソブチレート;ヒドロキシヘプチルパーオキサイド;クロルヘキサノンパーオキサイドなどが挙げられる。 - bis (tert-butylperoxy) -3,3,5-trimethylcyclohexane; 1,1-bis (t-butylperoxy) cyclohexane; methyl ethyl ketone peroxide; 2,5-dimethyl-hexyl-2,5-Bisupa oxybenzoate; tertiary butyl hydroperoxide; p-menthane hydroperoxide; p-chlorobenzoyl peroxide; tertiary butyl peroxy isobutyrate; hydroxyheptyl peroxide; and chlorobenzene hexanone peroxide. これらの過酸化物は1種を単独で又は2種以上を混合して、通常EVA100重量部に対して、10重量部以下、好ましくは0.1〜10重量部の割合で使用される。 These peroxides are mixed alone, or two or more one, the normal EVA100 parts, 10 parts by weight or less, is used in a proportion of preferably 0.1 to 10 parts by weight.

【0112】有機過酸化物は通常EVAに対し押出機、 [0112] Organic peroxide extruder to normal EVA,
ロールミル等で混練されるが、有機溶媒、可塑剤、ビニルモノマー等に溶解し、EVAのフィルムに含浸法により添加しても良い。 While being kneaded in a roll mill or the like, an organic solvent, a plasticizer, dissolved in vinyl monomers, it may be added by impregnation method to a film of EVA.

【0113】なお、EVAの物性(機械的強度、光学的特性、接着性、耐候性、耐白化性、架橋速度など)改良のために、各種アクリロキシ基又はメタクリロキシ基及びアリル基含有化合物を添加することができる。 [0113] The physical properties of EVA (mechanical strength, optical properties, adhesion, weather resistance, whitening resistance, rate of crosslinking, etc.) for improved, to add various acryloxy group or methacryloxy group and allyl group-containing compound be able to. この目的で用いられる化合物としてはアクリル酸又はメタクリル酸誘導体、例えばそのエステル及びアミドが最も一般的であり、エステル残基としてはメチル、エチル、ドデシル、ステアリル、ラウリル等のアルキル基の他、シクロヘキシル基、テトラヒドロフルフリル基、アミノエチル基、2−ヒドロキシエチル基、3−ヒドロキシプロピル基、3−クロロ−2−ヒドロキシプロピル基などが挙げられる。 Acrylic acid or methacrylic acid derivatives as compounds used for this purpose, such as its an ester and amides are most common, other methyl, ethyl, dodecyl, stearyl, alkyl groups lauryl such as an ester residue, a cyclohexyl group , tetrahydrofurfuryl group, aminoethyl group, 2-hydroxyethyl group, 3-hydroxypropyl group, 3-chloro-2-hydroxypropyl group. また、エチレングリコール、トリエチレングリコール、ポリエチレングリコール、トリメチロールプロパン、ペンタエリスリトール等の多官能アルコールとのエステルを用いることもできる。 Further, ethylene glycol, triethylene glycol, polyethylene glycol, trimethylol propane, also possible to use an ester of a polyfunctional alcohol such as pentaerythritol. アミドとしてはダイアセトンアクリルアミドが代表的である。 Examples of the amide diacetone acrylamide is typical.

【0114】より具体的には、トリメチロールプロパン、ペンタエリスリトール、グリセリン等のアクリル又はメタクリル酸エステル等の多官能エステルや、トリアリルシアヌレート、トリアリルイソシアヌレート、フタル酸ジアリル、イソフタル酸ジアリル、マレイン酸ジアリル等のアリル基含有化合物が挙げられ、これらは1種を単独で、或いは2種以上を混合して、通常EVA10 [0114] More specifically, trimethylol propane, pentaerythritol, and polyfunctional esters of acrylic or methacrylic acid esters such as glycerin, triallyl cyanurate, triallyl isocyanurate, diallyl phthalate, diallyl isophthalate, maleic include allyl group-containing compounds such as diallyl, they are mixed alone, or two or more, usually EVA10
0重量部に対して0.1〜2重量部、好ましくは0.5 0.1 to 2 parts by weight to 0 parts by weight, preferably 0.5
〜5重量部用いられる。 5 parts by weight is used.

【0115】EVAを光により架橋する場合、上記過酸化物の代りに光増感剤が通常EVA100重量部に対して10重量部以下、好ましくは0.1〜10重量部使用される。 [0115] If the crosslinking by light and EVA, photosensitizer in place of the peroxide 10 parts by weight or less relative to the normal EVA100 parts by weight is used preferably 0.1 to 10 parts by weight.

【0116】この場合、使用可能な光増感剤としては、 [0116] In this case, as a usable light sensitizer,
例えばベンゾイン、ベンゾフェノン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインイソプロピルエーテル、ベンゾインイソブチルエーテル、ジベンジル、5−ニトロアセナフテン、ヘキサクロロシクロペンタジエン、p−ニトロジフェニル、p−ニトロアニリン、2,4,6−トリニトロアニリン、1,2−ベンズアントラキノン、3−メチル−1,3−ジアザ− Such as benzoin, benzophenone, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, benzoin isobutyl ether, dibenzyl, 5-nitroacenaphthene, hexachloro cyclopentadiene, p- nitro diphenyl, p- nitroaniline, 2,4,6 nitroaniline, 1,2-anthraquinone, 3-methyl-1,3-diaza -
1,9−ベンズアンスロンなどが挙げられ、これらは1 1,9 etc. benzanthrone and the like, which 1
種を単独で或いは2種以上を混合して用いることができる。 It can be used a seed alone or in admixture of two or more.

【0117】また、この場合、促進剤としてシランカップリング剤が併用される。 [0117] In this case, the silane coupling agent is used together as an accelerator. このシランカップリング剤としては、ビニルトリエトキシシラン、ビニルトリス(β As the silane coupling agent, vinyltriethoxysilane, vinyltris (beta
−メトキシエトキシ)シラン、γ−メタクリロキシプロピルトリメトキシシラン、ビニルトリアセトキシシラン、γ−グリシドキシプロピルトリメトキシシラン、γ - methoxyethoxy) silane, .gamma.-methacryloxypropyl trimethoxysilane, vinyl triacetoxy silane, .gamma.-glycidoxypropyltrimethoxysilane, gamma
−グリシドキシプロピルトリエトキシシラン、β− - glycidoxypropyl triethoxysilane, beta-
(3,4−エポキシシクロヘキシル)エチルトリメトキシシラン、γ−クロロプロピルメトキシシラン、ビニルトリクロロシラン、γ−メルカプトプロピルトリメトキシシラン、γ−アミノプロピルトリエトキシシラン、N (3,4-epoxycyclohexyl) ethyltrimethoxysilane, .gamma.-chloropropyl trimethoxysilane, vinyl trichlorosilane, .gamma.-mercaptopropyltrimethoxysilane, .gamma.-aminopropyltriethoxysilane, N
−β(アミノエチル)−γ−アミノプロピルトリメトキシシランなどが挙げられる。 -β etc. (aminoethyl)-.gamma.-aminopropyltrimethoxysilane.

【0118】これらのシランカップリング剤は通常EV [0118] These silane coupling agent is usually EV
A100重量部に対して0.001〜10重量部、好ましくは0.001〜5重量部の割合で1種又は2種以上が混合使用される。 0.001 parts by weight to A100 parts by weight, preferably at least one or at a ratio of 0.001 to 5 parts by weight are mixed use.

【0119】なお、本発明に係る接着用樹脂フィルムには、その他、紫外線吸収剤、赤外線吸収剤、老化防止剤、塗料加工助剤を少量含んでいてもよく、また、フィルター自体の色合いを調整するために染料、顔料などの着色剤、カーボンブラック、疎水性シリカ、炭酸カルシウム等の充填剤を適量配合してもよい。 [0119] Incidentally, the adhesive resin film according to the present invention, other UV absorbers, infrared absorbers, anti-aging agent may contain a small amount of paint processing aid, also adjust the hue of the filter itself colorants dyes and pigments in order to, carbon black, hydrophobic silica, a filler such as calcium carbonate may be appropriate amount.

【0120】特に、接着用樹脂フィルムとして、上述のような無色透明樹脂に顔料を添加して着色した有色透明樹脂よりなるフィルムを用いることにより、青色輝度を補強するなどして自然な表示を得ることができ、或いはカラーフィルター等を用いることなく、色純度を向上させ優れた色再現性を得ることができる。 [0120] In particular, as the adhesive resin film, by using a colorless and transparent resin made of a colored transparent resin colored by adding a pigment to the film as described above, to obtain a natural display and the like to reinforce the blue luminance it can be, or without using a color filter or the like, it is possible to obtain an excellent color reproducibility improves color purity.

【0121】即ち、PDPにはRGB各色に対応する蛍光体が各セルに塗布されているが、その発光効率は必ずしも同じではないため、各色を合成した発光色例えば白色を表示させた場合、選択されている蛍光体の種類等の影響により違った色度、色温度となる。 [0121] That is, when the phosphor in a PDP corresponding to each of the RGB colors have been applied to each cell, the luminous efficiency was necessarily because it is not the same, to display the synthesized luminescent color such as white and colors, select chromaticity different due to the influence of such kinds of phosphors are, the color temperature. これを所定の設計値に合わせるためには複雑な処理が必要となる。 Complicated processing is required to match it to the predetermined design value.

【0122】一般に、PDPの場合、青色発光が弱いため、青色輝度を補強する必要がある。 [0122] In general, in the case of PDP, since blue emission is weak, it is necessary to reinforce the blue luminance. また、色純度を向上させ、優れた色再現性を得るには、別途カラーフィルターが必要となる。 Further, to improve color purity, in order to obtain excellent color reproducibility, it is necessary to separate the color filters.

【0123】しかしながら、無色透明の接着樹脂を用いて接合一体化した電磁波シールド性光透過窓材では、色調を変える作用は得られない。 [0123] However, in the electromagnetic-wave shielding and light transmitting plate which is integrally joined with an adhesive resin colorless transparent, not obtained effect of changing the color tone.

【0124】これに対して、接着樹脂として有色透明のものを用いることにより、光透過性を損なうことなく、 [0124] In contrast, by using a colored transparent as the adhesive resin, without impairing the optical transparency,
青色輝度の補強又は色純度の向上を図ることができ、鮮明な画像を得ることができる。 It is possible to reinforce or improve the color purity of the blue luminance, it is possible to obtain a clear image.

【0125】この場合、使用される顔料としては、特に制限はなく、一般的なプラスチック用着色剤などを用いることができるが、例えば、黄色酸化鉄、黄鉛、カドミウムイエロー、ファストイエロー、ジスアゾイエロー、 [0125] In this case, as the pigment used is not particularly limited and may be used as the common plastic colorants, for example, yellow iron oxide, chrome yellow, cadmium yellow, fast yellow, disazo yellow ,
モリブデートオレンジ、ピラゾロンオレンジ、ベンガラ、カドミウムレッド、レーキレッドC、ブリリアントカーミン6B、キナクリドンレッド、マンガンバイオレット、メチルバイオレットレーキ、ジオキサジンバイオレット、群青、紺青、コバルトブルー、ビクトリアブルーレーキ、フタロシアニンブルー、クロムグリーン、酸化クロム、フタロシアニングリーン等の1種を単独で或いは2種以上を混合して用いることができる。 Molybdate orange, pyrazolone orange, red iron oxide, cadmium red, lake red C, brilliant carmine 6B, quinacridone red, manganese violet, methyl violet lake, dioxazine violet, ultramarine blue, Prussian blue, cobalt blue, Victoria blue lake, phthalocyanine blue, chrome green , it can be used chromium oxide, one such phthalocyanine green alone or in admixture of two or more.

【0126】前述の如く、PDPの発光パネルでは青色発光が弱く、青色輝度を補強することが望まれる点、及び色純度向上のため、本発明では、 群青、紺青、コバルトブルー、ビクトリアブルーレーキ、フタロシアニンブルーなどの青色顔料の1種又は2種以上、或いはマンガンバイオレット、メチルバイオレットレーキ、ジオキサジンバイオレット等の紫色顔料との組み合わせ等により青色に着色させる。 [0126] As described above, weak blue emission at PDP emitting panel, the point where it is desired to reinforce the blue luminance and for the color purity enhancing, in the present invention, ultramarine, Prussian blue, cobalt blue, Victoria Blue Lake, phthalocyanine blue one or more blue pigments, such as, or manganese violet, is colored blue by the combination of methyl violet lake, and violet pigments such as dioxazine violet. 或いは RGB各種の色純度を向上するような顔料、クロムグリーン、酸化クロム、フタロシアニングリーン等の緑色顔料と紫色又は青色顔料とを混合して配合する。 Or a pigment such as to improve the RGB various color purity, chrome green, chromium oxide, formulated by mixing a green pigment and a violet or blue pigments such as phthalocyanine green. などの方法を採用するのが好ましい。 It is preferable to adopt a method such as.

【0127】顔料の配合量は、透明性を損なうことなく、コントラスト等の特性を向上させるために、EVA [0127] The amount of the pigment without impairing the transparency, in order to improve the characteristics such as contrast, EVA
等のマトリックス樹脂100重量部に対して0.001 Against the matrix resin 100 parts by weight of an equal 0.001
〜10重量部とするのが好ましい。 Preferably set to 10 parts by weight.

【0128】なお、このような有色透明樹脂フィルムを用いる場合、電磁波シールド性光透過窓材に用いるすべての接着用樹脂フィルムが有色透明樹脂フィルムであっても良く、また、接着用樹脂フィルム4A,4Bのうちの一方のみが有色透明樹脂フィルムであって、他方は無色透明樹脂フィルムであっても良い。 [0128] In the case of using such a colored transparent resin film, all of the adhesive resin film used in the electromagnetic wave shielding and light transmitting plate is may be a colored transparent resin film, also, adhesive resin film 4A, only one of 4B is a colored transparent resin film and the other may be a colorless transparent resin film.

【0129】また、本発明で用いる接着用樹脂フィルムは接着性改良の手段として、シート化された接着用中間膜面へのコロナ放電処理、低温プラズマ処理、電子線照射、紫外光照射などの手段を施したものであっても良い。 [0129] Further, as the adhesive resin film means the adhesion improving used in the present invention, a corona discharge treatment to sheeted adhesive intermediate film surface, low-temperature plasma treatment, electron beam irradiation, means such as irradiation with ultraviolet light or it may be subjected to.

【0130】本発明に係る接着用樹脂フィルムは、接着樹脂と上述の添加剤とを混合し、押出機、ロール等で混練した後カレンダー、ロール、Tダイ押出、インフレーション等の成膜法により所定の形状にシート成形することにより製造される。 [0130] adhesive resin film according to the present invention, the predetermined and the adhesive resin was mixed with the above-mentioned additives, extruder, calender were kneaded by a roll or the like, roll, T-die extrusion, the film formation method of inflation such It is produced by sheet molding into shape. 成膜に際してはブロッキング防止、透明基板との圧着時の脱気を容易にするためエンボスが付与される。 Antiblocking. Before film formation, embossing for facilitating deaeration during crimping of the transparent substrate is applied.

【0131】図1に示す電磁波シールド性光透過窓材1 [0131] electromagnetic-wave shielding and light transmitting plate 1 shown in FIG. 1
は、反射防止膜5を形成した透明基板2Aと、黒枠塗装6を設けた透明基板2Bと透明導電性フィルム3、接着用樹脂フィルム4A,4B及び導電性粘着テープ、好ましくは架橋型導電性粘着テープA,Bを準備し、まず、 Includes a transparent substrate 2A forming the antireflection film 5, the black frame paint 6 is provided with a transparent substrate 2B and a transparent conductive film 3, adhesive resin film 4A, 4B and the conductive adhesive tape, preferably crosslinked electroconductive pressure-sensitive adhesive prepare the tape a, B, first,
透明導電性フィルム3を接着用樹脂フィルム4Bを介して透明基板2Bと積層し、この積層体に導電性粘着テープAを貼り付け、その後、透明基板2A及び接着用樹脂フィルム4Aを積層し、接着用樹脂フィルムの硬化条件で加圧下、加熱又は光照射して一体化した後、更に、透明基板2Aの表面の縁部から透明基板2Bの表面の縁部に到るように導電性粘着テープBを貼り付けることにより容易に製造することができる。 The transparent conductive film 3 is laminated with the transparent substrate 2B via the adhesive resin film 4B, paste the conductive adhesive tape A in the laminate, then laminating the transparent substrate 2A and adhesive resin film 4A, the adhesive under pressure curing conditions use a resin film, was integrated heated or irradiated with light, further, the surface of the conductive so reach the edge of the surface of the transparent substrate 2B from the edge of the transparent substrate 2A adhesive tape B it can be easily produced by pasting.

【0132】なお、導電性粘着テープAの透明導電性フィルム3の縁部における貼り付け幅(図1(b)のW) [0132] The conductive adhesive tape applying width at the edge of the transparent conductive film 3 of A (W in FIG. 1 (b))
は、電磁波シールド性光透過窓材の面積によっても異なるが、通常の場合、3〜20mm程度とされる。 Varies depending area of ​​the electromagnetic wave shielding and light transmitting plate, usually, is about 3 to 20 mm.

【0133】導電性粘着テープA,Bとして、架橋型導電性粘着テープを用いる場合には、まず、透明導電性フィルム3の周辺に架橋型導電性粘着テープAを貼り付け、ヒートシーラー等で加熱加圧して架橋しながらフィルムと金属箔間に導通を持たせる。 [0133] conductive adhesive tape A, as B, and the case of using a crosslinked electroconductive pressure-sensitive adhesive tape is first adhered to crosslinked electroconductive pressure-sensitive adhesive tape A in the periphery of the transparent conductive film 3, heated in a heat sealer or the like pressurized to have continuity between crosslinking while the film and the metal foil. 次に接着性樹脂フィルム4Bを介して透明基板2Bと積層し、その後、透明基板2A及び接着用樹脂フィルム4Aを積層し、接着用樹脂フィルムの硬化条件で加圧下、加熱又は光照射して一体化した後、更に、透明基板2Aの表面の縁部から透明基板2Bの表面の縁部に到るように架橋型導電性粘着テープBを貼り付ける。 Then laminating the transparent substrate 2B via an adhesive resin film 4B, then laminating the transparent substrate 2A and adhesive resin film 4A, under pressure curing conditions of the adhesive resin film, heating or irradiation with light integrated after ized, further paste edges reaching as crosslinked electroconductive pressure-sensitive adhesive tape B of the surface of the transparent substrate 2B from the edge of the surface of the transparent substrate 2A.

【0134】架橋型導電性粘着テープA,Bの貼り付けに際しては、その粘着層bの粘着性を利用して積層体に貼り付け(この仮り止めは、必要に応じて、貼り直しが可能である。)、その後、必要に応じて圧力をかけながら加熱又は紫外線照射する。 [0134] crosslinked electroconductive pressure-sensitive adhesive tape A, upon paste B, the paste (the temporarily fixed to the laminate using the adhesion of the adhesive layer b is optionally possible reapplication some.), then heated or irradiated with ultraviolet light while applying pressure as necessary. この紫外線照射時には併せて加熱を行っても良い。 It may be heated together at the time of the ultraviolet irradiation. なお、この加熱又は光照射を局部的に行うことで、架橋型導電性粘着テープの一部分のみを接着させるようにすることもできる。 Note that by locally performing the heating or light irradiation, can be so as to adhere only a portion of the cross-linked conductive adhesive tape.

【0135】加熱接着は、一般的なヒートシーラーで容易に行うことができ、また、加圧加熱方法としては、架橋型導電性粘着テープを貼り付けた積層体を真空袋中に入れ脱気後加熱する方法でも良く、接着はきわめて容易に行える。 [0135] heating bonding can be easily performed by a general heat sealer, also, as the pressure heating method, after degassing put laminate pasted crosslinked electroconductive pressure-sensitive adhesive tape in a vacuum bag may be a method of heating, the adhesive can be performed very easily.

【0136】この接着条件としては、熱架橋の場合は、 [0136] As the bonding conditions, in the case of thermal cross-linking,
用いる架橋剤(有機過酸化物)の種類に依存するが、通常70〜150℃、好ましくは70〜130℃で、通常10秒〜120分、好ましくは20秒〜60分である。 It depends on the kind of the crosslinking agent (organic peroxide) to be used, usually 70 to 150 ° C., preferably at 70 to 130 ° C., 10 sec to 120 minutes usually, and preferably from 20 seconds to 60 minutes.

【0137】また、光架橋の場合、光源としては紫外〜 [0137] In addition, in the case of the light cross-linking, as the light source ultraviolet to
可視領域に発光する多くのものが採用でき、例えば超高圧、高圧、低圧水銀灯、ケミカルランプ、キセノンランプ、ハロゲンランプ、マーキュリーハロゲンランプ、カーボンアーク灯、白熱灯、レーザー光等が挙げられる。 Many things can be adopted which emits in the visible region, for example ultra-high pressure, high pressure, low pressure mercury lamp, chemical lamp, xenon lamp, halogen lamp, mercury halogen lamp, carbon arc lamp, an incandescent lamp, laser light, and the like.
照射時間は、ランプの種類、光源の強さによって一概には決められないが、通常数十秒〜数十分程度である。 The irradiation time, the type of lamp, but not be determined in unanimously by the strength of the light source, which is usually several tens seconds to several tens minutes. 架橋促進のために、予め40〜120℃に加熱した後、これに紫外線を照射してもよい。 For crosslinking promoter, was preheated to 40 to 120 ° C., it may be irradiated with ultraviolet rays thereto.

【0138】また、接着時の加圧力についても適宜選定され、通常0〜50kg/cm 2 、特に0〜30kg/ [0138] In addition, the suitably selected also pressure applied during bonding is usually 0~50kg / cm 2, particularly 0~30Kg /
cm 2の加圧力とすることが好ましい。 It is preferable that the pressure of cm 2.

【0139】このようにして導電性粘着テープ、好ましくは架橋型導電性粘着テープA,Bを取り付けた電磁波シールド性光透過窓材1は、筐体に単にはめ込むのみで極めて簡便かつ容易に筐体に組み込むことができ、同時に、架橋型導電性粘着テープA,Bを介して透明導電性フィルム3と筐体との良好な導通をその4側縁部において均一にとることができる。 [0139] In this way the conductive adhesive tape, preferably crosslinked electroconductive pressure-sensitive adhesive tape A, electromagnetic-wave shielding and light transmitting plate 1 fitted with B is very simple and easy housing only by simply fitting the housing can be incorporated into, the same time, it is possible to take the crosslinked electroconductive pressure-sensitive adhesive tape a, good conduction between the transparent conductive film 3 and the housing through the B uniform in its 4 side edges. このため、良好な電磁波シールド効果が得られる。 Therefore, good electromagnetic wave shielding effect is obtained.

【0140】なお、図1に示す電磁波シールド性光透過窓材は請求項1の電磁波シールド性光透過窓材の一例であって、請求項1は図示のものに限定されるものではない。 [0140] Incidentally, the electromagnetic wave shielding and light transmitting plate shown in FIG. 1 is an example of an electromagnetic wave shielding and light transmitting plate according to claim 1, claim 1 is not intended to be limited to the illustrated. 例えば、導電性粘着テープA,Bは透明導電性フィルム3の4側縁部に取り付ける他、対向する2側縁部においてのみ取り付けるようにしても良い。 For example, conductive adhesive tape A, B addition be attached to the 4-side edge portion of the transparent conductive film 3 may be attached only at the 2-side opposite edges. ただし、均一導通性の面からは、図示の如く、4側縁部に取り付けるのが好ましい。 However, from the viewpoint of uniformity conductivity, as shown, preferably mounted in four side edges.

【0141】また、請求項1の電磁波シールド性光透過窓材は、図1に示す如く、2枚の透明基板間に透明導電性フィルムを介在させるものに限らず、少なくとも一方の透明基板に直接透明導電性膜を形成し、接着用樹脂フィルムで他方の透明基板と一体化したものであっても良い。 [0141] Further, the electromagnetic wave shielding and light transmitting plate according to claim 1, as shown in FIG. 1 is not limited to the interposition of a transparent conductive film between two transparent substrates, directly on at least one transparent substrate forming a transparent conductive film, an adhesive resin film may be formed by integrating with the other transparent substrate. このような電磁波シールド性光透過窓材としては、 Such electromagnetic-wave shielding and light transmitting plate,
一方の透明基板に次のような透明導電性膜を形成したものが挙げられる。 That forms the one transparent substrate on the transparent conductive film such as the following may be mentioned.

【0142】 透明基板の板面に、フォトレジストのコーティング、パターン露光及びエッチングの工程により所定パターンにエッチングして形成した格子状又はパンチングメタル状の金属膜。 [0142] The plate surface of the transparent substrate, a coating of photoresist, lattice or punching metal-like metal film is formed by etching a predetermined pattern by a process of pattern exposure and etching. 透明基板の板面に導電性インキをパターン印刷して形成した格子状又はパンチングメタル状の印刷膜。 Lattice or punching metal-like printed film was formed by pattern printing conductive ink on the plate surface of the transparent substrate.

【0143】また、請求項1の電磁波シールド性光透過窓材は、図1に示す電磁波シールド性光透過窓材において、透明導電性フィルムの代りに、パターンエッチングにより格子状又はパンチングメタル状とした金属箔を2 [0143] Further, the electromagnetic wave shielding and light transmitting plate according to claim 1, in electromagnetic-wave shielding and light transmitting plate shown in FIG. 1, in place of the transparent conductive film, and a lattice or punching metal form by pattern etching the metal foil 2
枚の透明基板間に介在させたものであっても良く、この場合においても、折り返しにより切断し易い金属箔について、これを折り返すことなく、容易に導通を図ることができる。 It may be one that is interposed between sheets of transparent substrates, in this case, the easy metal foil is cut by the folding, without folding it, it is possible to easily conduct.

【0144】次に図2を参照して請求項3の電磁波シールド性光透過窓材の実施の形態を詳細に説明する。 [0144] Next, embodiments of the electromagnetic-wave shielding and light transmitting plate according to claim 3 with reference to FIG. 2 will be described in detail.

【0145】図2(a)は請求項3の電磁波シールド性光透過窓材の実施の形態を示す模式的な断面図であり、 [0145] FIG. 2 (a) is a schematic sectional view showing an embodiment of the electromagnetic-wave shielding and light transmitting plate according to claim 3,
図2(b)は導電性粘着テープを貼り付けた透明導電性フィルムを示す平面図である。 Figure 2 (b) is a plan view showing a transparent conductive film was attached a conductive adhesive tape.

【0146】この電磁波シールド性光透過窓材11は、 [0146] The electromagnetic-wave shielding and light transmitting plate 11,
一方の板面に透明導電性フィルム14Aを接着用樹脂フィルム13Aで接着した透明基板12Aと、一方の板面に透明導電性フィルム14Bを接着用樹脂フィルム13 Transparent and substrate 12A adhered in one plate transparent electrically conductive surface film 14A the adhesive resin film 13A, one for adhering the transparent conductive film 14B in the plate surface resin film 13
Bで接着した透明基板12Bとを、透明導電性フィルム14A,14Bが対面するように接着用樹脂フィルム1 And a transparent substrate 12B adhered with B, the adhesive resin film as a transparent conductive film 14A, 14B are face to face 1
3Cで接着一体化したものであり、各透明基板12A, 3C in is obtained by bonding and integrating, the transparent substrate 12A,
12Bの透明導電性フィルム14A,14Bの4側辺の縁部から当該透明基板12A,12Bの端面を経てその表面の縁部にまで達するように、それぞれ第1,第2の導電性粘着テープ17A,17Bを貼り付けてある。 The transparent conductive film 14A of the 12B, so as to reach from the edge of the four sides of 14B to the edge of the transparent substrate 12A, the surface via the end surface of the 12B, first, second conductive adhesive tape 17A respectively , it is pasted 17B.

【0147】本実施例において、透明基板12A,12 [0147] In this embodiment, the transparent substrate 12A, 12
Bの積層体の全周において、端面の全体に付着すると共に、この積層体の表裏の角縁を回り込み、一方の透明基板12Aの表面の端縁部と他方の透明基板12Bの表面の端縁部の双方に付着するように、更に第3の導電性粘着テープ17Cが設けられている。 In the entire circumference of the laminate of B, as well as adhere to the whole of the end face, the edges of the front and rear corner edges of the stack wraparound to the surface of the edge portion and the other of the transparent substrate 12B on the surface of one transparent substrate 12A to adhere to both parts is provided with yet a third conductive adhesive tape 17C.

【0148】請求項3で用いる導電性粘着テープ17 [0148] conductive used in claim 3 adhesive tape 17
A,17B,17Cとしては、図示の如く、金属箔17 A, 17B, as 17C is as shown, the metal foil 17
aの一方の面に、導電性粒子を分散させた粘着層17b On one surface of a, the adhesive layer 17b obtained by dispersing conductive particles
を設けたものであって、前述の請求項1の電磁波シールド性光透過窓材で用い得る導電性粘着テープとして例示したもの、好ましくは、粘着層がエチレン−酢酸ビニル系共重合体を主成分とするポリマーと架橋剤とを含む後架橋型接着層であるものを用いることができる。 Mainly of vinyl acetate copolymer - be those were provided, those exemplified as the conductive adhesive tape which can be used in electromagnetic-wave shielding and light transmitting plate according to claim 1 described above, preferably, the adhesive layer is ethylene it can be used a crosslinked adhesive layer after including the form of a polymer and a crosslinking agent.

【0149】また、透明基板12A,12B、透明導電性フィルム14A,14B、接着用樹脂フィルム13 [0149] The transparent substrate 12A, 12B, the transparent conductive film 14A, 14B, adhesive resin film 13
A,13B,13Cの構成材料や厚み等についても、前述の請求項1の電磁波シールド性光透過窓材で用い得る透明基板2A,2B、透明導電性フィルム3、接着用樹脂フィルム4A,4Bとして記述したものと同様のものを採用することができる。 A, 13B, for even such constituent materials and thicknesses of 13C, the above-described first aspect of electromagnetic-wave shielding and light transmitting plate can be used in the transparent substrate 2A, 2B, the transparent conductive film 3, adhesive resin film 4A, as 4B it can be adopted similar to those described.

【0150】本実施例の電磁波シールド性光透過窓材1 [0150] electromagnetic-wave shielding and light transmitting plate 1 of this embodiment
1においても、裏面側となる透明基板12Bの周縁部にアクリル樹脂をベースとする黒枠塗装16が設けられており、また、表面側となる透明基板12Aの表面に反射防止膜15が形成されている。 Also in 1, black border paint 16 based on acrylic resin on the periphery of the transparent substrate 12B serving as a rear surface side is provided, also, the antireflection film 15 on the surface of the transparent substrate 12A serving as the surface side is formed there. この反射防止膜15としても、前述の請求項1の電磁波シールド性光透過窓材の説明で記述したものと同様の構成とすることができる。 Even the anti-reflection film 15 can be the same structure as that described in the description of the electromagnetic-wave shielding and light transmitting plate according to claim 1 described above.

【0151】更に、このような反射防止膜5の上に形成し得る汚染防止膜やハードコート処理、アンチグレア加工、透明導電性膜の熱線反射コート等においても前述の通りである。 [0151] Furthermore, such a contamination prevention film or a hard coat treatment can be formed on the antireflection film 5, anti-glare processing is as described above also in the heat-reflecting coating or the like of the transparent conductive film.

【0152】図2に示す電磁波シールド性光透過窓材1 [0152] electromagnetic-wave shielding and light transmitting plate 1 shown in FIG. 2
1は、反射防止膜15を形成した透明基板12Aと、黒枠塗装16を設けた透明基板12Bと透明導電性フィルム14A,14B、接着用樹脂フィルム13A,13 1 includes a transparent substrate 12A forming the antireflection film 15, a black frame paint 16 transparent substrate 12B and the transparent conductive film 14A is provided, 14B, adhesive resin film 13A, 13
B,13C及び導電性粘着テープ、好ましくは架橋型導電性粘着テープ17A,17B,17Cを準備し、架橋型導電性粘着テープを用いる場合には、まず、透明導電性フィルム14A,14Bの周辺に架橋型導電性粘着テープ17A、17Bを貼り付け、ヒートシーラー等で加熱加圧して架橋しながらフィルムと金属箔間に導通を持たせる。 B, @ 13 C and the conductive adhesive tape, preferably crosslinked electroconductive pressure-sensitive adhesive tape 17A, 17B, to prepare the 17C, in the case of using a cross-linked conductive adhesive tape, first, a transparent conductive film 14A, the periphery of the 14B crosslinked electroconductive pressure-sensitive adhesive tape 17A, paste 17B, to have continuity between the film and the metal foil with crosslinking heated and pressed by a heat sealer or the like. 次に各々接着性樹脂フィルム13A、13Bを介して透明基板12A、12Bと積層し、その後、積層体同士を接着用樹脂フィルム13Cを介して積層し、接着用樹脂フィルムの硬化条件で加圧下、加熱又は光照射して一体化した後、更に、透明基板12Aの表面の縁部から透明基板12Bの表面の縁部に到るように架橋型導電性粘着テープ17Cを貼り付けることにより容易に製造することができる。 Then each adhesive resin film 13A, 13B and the transparent laminated substrate 12A, 12B and through, then a laminate with each other are laminated through an adhesive resin film 13C, under pressure curing conditions of the adhesive resin film, after integrating heated or irradiated with light, further, readily prepared by attaching a crosslinkable conductive adhesive tape 17C as reach the edge of the surface of the transparent substrate 12B from the edge of the surface of the transparent substrate 12A can do.

【0153】架橋型導電性粘着テープ17A〜17Cの貼り付け、接着は、前述の請求項1の電磁波シールド性光透過窓材における貼り付け、接着方法と同様に実施することができる。 [0153] Paste crosslinking type conductive adhesive tape 17A-17C, the adhesive is adhered in the electromagnetic-wave shielding and light transmitting plate according to claim 1 described above, can be carried out similarly to the bonding method.

【0154】なお、架橋型導電性粘着テープ17A,1 [0154] Incidentally, crosslinked electroconductive pressure-sensitive adhesive tape 17A, 1
7Bの透明導電性フィルム14A,14Bの縁部における貼り付け幅(図2(b)のW)は、電磁波シールド性光透過窓材の面積によっても異なるが、通常の場合、3 The transparent conductive film 14A of 7B, pasting width at the edge of 14B (W in FIG. 2 (b)) varies depending on the area of ​​the electromagnetic-wave shielding and light transmitting plate, usually, 3
〜20mm程度とされる。 It is about ~20mm.

【0155】このようにして架橋型導電性粘着テープ1 [0155] In this manner, the cross-linked conductive adhesive tape 1
7A〜17Cを取り付けた電磁波シールド性光透過窓材1は、筐体に単にはめ込むのみで極めて簡便かつ容易に筐体に組み込むことができ、同時に、架橋型導電性粘着テープ17A〜17Cを介して透明導電性フィルム14 Electromagnetic-wave shielding and light transmitting plate 1 fitted with 7A~17C can be incorporated extremely conveniently and easily housing only by simply fitting the housing, at the same time, through a cross-linked conductive adhesive tape 17A~17C transparent conductive film 14
A,14Bと筐体との良好な導通をその4側縁部において均一にとることができる。 A, good conduction between 14B and the housing can take the uniform in the 4-side edge. このため、良好な電磁波シールド効果が得られる。 Therefore, good electromagnetic wave shielding effect is obtained.

【0156】なお、図2に示す電磁波シールド性光透過窓材は請求項3の電磁波シールド性光透過窓材の一例であって、請求項3は図示のものに限定されるものではない。 [0156] Incidentally, the electromagnetic wave shielding and light transmitting plate shown in FIG. 2 is an example of an electromagnetic wave shielding and light transmitting plate according to claim 3, claim 3 is not intended to be limited to the illustrated. 例えば、架橋型導電性粘着テープ17A,17Bは透明導電性フィルム14A,14Bの4側縁部に取り付ける他、対向する2側縁部においてのみ取り付けるようにしても良い。 For example, cross-linked conductive adhesive tape 17A, 17B transparent conductive film 14A, in addition be attached to the 4-side edge of the 14B, it may be attached only at the 2-side opposite edges. ただし、均一導通性の面からは、図示の如く、4側縁部に取り付けるのが好ましい。 However, from the viewpoint of uniformity conductivity, as shown, preferably mounted in four side edges.

【0157】また、請求項3の電磁波シールド性光透過窓材は、図2に示す如く、透明基板に接着用樹脂フィルムにより透明導電性フィルムを接着したものに限らず、 [0157] Further, the electromagnetic wave shielding and light transmitting plate according to claim 3, as shown in FIG. 2 is not limited to bonding the transparent conductive film by an adhesive resin film on a transparent substrate,
各々の透明基板に前述の請求項1の電磁波シールド性光透過窓材の説明で記述したような透明導電性膜を直接形成し、接着用樹脂フィルムで互いに接合一体化したものであっても良い。 A transparent conductive film such as described in the description of each of the transparent substrate foregoing electromagnetic-wave shielding and light transmitting plate according to claim 1 formed directly, or may be joined integrally to each other by an adhesive resin film .

【0158】また、請求項3の電磁波シールド性光透過窓材は、図2に示す電磁波シールド性光透過窓材において、透明導電性フィルムの代りに、パターンエッチングにより格子状又はパンチングメタル状とした金属箔を透明基板に接着したものであっても良く、この場合においても、折り返しにより切断し易い金属箔について、これを折り返すことなく、容易に導通を図ることができる。 [0158] Further, the electromagnetic wave shielding and light transmitting plate according to claim 3, in electromagnetic-wave shielding and light transmitting plate shown in FIG. 2, instead of the transparent conductive film, and a lattice or punching metal form by pattern etching may be obtained by bonding a metal foil to the transparent substrate, in this case, the easy metal foil is cut by the folding, without folding it, it is possible to easily conduct.

【0159】次に図3,4を参照して請求項7の電磁波シールド熱線カット性光透過窓材の実施の形態を説明する。 [0159] Referring now to FIGS explaining an embodiment of an electromagnetic wave shielding heat-ray shielding and light transmitting material according to claim 7.

【0160】図3は請求項7の電磁波シールド熱線カット性光透過窓材の実施の形態を示す模式的な断面図、図4は中間膜の拡大断面図である。 [0160] Figure 3 is a schematic sectional view showing an embodiment of an electromagnetic wave shielding heat-ray shielding and light transmitting material according to claim 7, FIG. 4 is an enlarged sectional view of the intermediate layer.

【0161】まず、中間膜について詳細に説明する。 [0161] First, the intermediate layer will be described in detail.

【0162】図4に示す如く、本実施例の中間膜23 [0162] As shown in FIG. 4, the intermediate layer 23 of this embodiment
は、ベースフィルム31上に、酸化物透明導電膜32と金属薄膜33とを交互に積層してなる多層膜を設けたものである。 The base film 31 on, is provided with a multilayer film formed by laminating a transparent conductive oxide film 32 and a metal thin film 33 alternately.

【0163】このベースフィルム31としては、後述の透明基板の構成材料と同様の樹脂フィルム、好ましくは、PET、PC、PMMA等よりなるフィルムを用いることができる。 [0163] As the base film 31, the same resin film and the material of the transparent substrate to be described later, can be preferably used a PET, PC, made of PMMA such as a film. このフィルムは、得られる窓材の厚さを過度に厚くすることなく、取り扱い性、耐久性を確保する上で1μm〜5mm程度とするのが好ましい。 The film, without unduly increasing the thickness of the resulting window material, handling properties, preferably with 1μm~5mm about in order to ensure durability.

【0164】このベースフィルム31上に形成される酸化物透明導電膜32としては、ITO、ZnO、AlをドープしたZnO、SnO 2等の薄膜を形成することができ、その膜厚は、通常の場合、5〜5000Å程度である。 [0164] As the transparent conductive oxide film 32 formed on the base film 31, ITO, ZnO, it is possible to form ZnO doped with Al, a thin film of SnO 2 or the like, the film thickness is usually the If, it is about 5~5000Å.

【0165】また、金属薄膜33としては、銀、銅、アルミニウム、ニッケル、金、白金、クロム等の単独膜、 [0165] The metal thin film 33, silver, copper, aluminum, nickel, gold, platinum, single film such as chromium,
真鍮、ステンレス等の合金膜等の膜を光透過性を損なわない薄さで形成することができ、その膜厚は、通常の場合、2〜2000Å程度である。 Brass, can be a film such as an alloy film such as stainless steel formed with a thin which does not impair the optical transparency and has a thickness, usually, it is about 2~2000A.

【0166】これらの酸化物透明導電膜32及び金属薄膜33の積層数が少ないと十分な電磁波シールド性及び熱線カット性が得られず、多過ぎると透明性が損なわれる。 [0166] not laminated fewer sufficient electromagnetic shielding property and heat-ray shielding properties of the oxide transparent conductive film 32 and the metal thin film 33 is obtained, the transparency when too much is lost. 好ましい積層数は各々1〜20層、合計で2〜40 Preferred number of stacked layers each 20 layers, from 2 to 40 in total
層である。 It is a layer.

【0167】これらの酸化物透明導電膜32及び金属薄膜33は、スパッタ法や真空蒸着法、イオンプレーティング法、CVD法等、好ましくは膜厚制御が容易なスパッタ法により、ベースフィルム31上に容易に形成することができる。 [0167] These transparent conductive oxide film 32 and the metal thin film 33, a sputtering method, a vacuum evaporation method, ion plating method, CVD method, or the like, preferably by a thickness control easy sputtering, on the base film 31 it can be easily formed.

【0168】図3に示す電磁波シールド熱線カット性光透過窓材21は、このような中間膜23を2枚の透明基板22A,22Bの間に介在させて接着用樹脂フィルムに24A,24Bで接合一体化してなるものである。 [0168] electromagnetic wave shielding heat-ray shielding and light transmitting member 21 shown in FIG. 3, the bonding of such intermediate layer 23 two transparent substrates 22A, 24A to the adhesive resin film is interposed between 22B, at 24B it is intended to be integrated.

【0169】請求項7において、透明基板22A,22 [0169] In claim 7, the transparent substrate 22A, 22
B、接着用樹脂フィルム24A,24Bの構成材料や厚み等については、前述の請求項1の電磁波シールド性光透過窓材で用い得る透明基板2A,2B、接着用樹脂フィルム4A,4Bとして記述したものと同様のものを採用することができる。 B, adhesive resin film 24A, for such construction materials and thickness of 24B, described above in claim 1 of the electromagnetic wave shielding and light transmitting plate can be used in the transparent substrate 2A, 2B, adhesive resin film 4A, as 4B it can be adopted similar to the ones.

【0170】本実施例の電磁波シールド熱線カット性光透過窓材21においても、裏面側となる透明基板22B [0170] In the electromagnetic shielding heat-ray shielding and light transmitting member 21 of the present embodiment, the transparent substrate 22B serving as a rear surface side
の周縁部にアクリル樹脂をベースとする黒枠塗装26が設けられており、また、裏面側となる透明基板22Aの表面に反射防止膜25が形成されている。 Periphery of which the black frame paint 26 is provided based on acrylic resin, anti-reflection film 25 on the surface of the transparent substrate 22A serving as a rear surface side is formed. この反射防止膜25としても、前述の請求項1の電磁波シールド性光透過窓材の説明で記述したものと同様の構成とすることができる。 Even the anti-reflection film 25 can be the same structure as that described in the description of the electromagnetic-wave shielding and light transmitting plate according to claim 1 described above.

【0171】更に、このような反射防止膜25の上に形成し得る汚染防止膜やハードコート処理、アンチグレア加工、透明導電性膜の熱線反射コートにおいても、前述の通りである。 [0171] Additionally, contamination prevention film or a hard coat treatment may be formed on the antireflection film 25, anti-glare processing, even in the heat-reflecting coating of the transparent conductive film, as described above.

【0172】透明基板22A,22Bと中間膜23の積層体は、前述の接着用樹脂フィルム24A,24Bを用い、この接着用樹脂フィルム24A,24Bの間に中間膜23を挟んだものを透明基板22A,22B間に介在させ、減圧、加温下に脱気して予備圧着した後、加熱又は光照射により接着層を硬化させて一体化することにより容易に製造することができる。 [0172] transparent substrate 22A, 22B and laminate the intermediate layer 23, adhesive resin film 24A described above, using 24B, transparent substrate which sandwich the intermediate layer 23 in this adhesive resin film 24A, 24B between the 22A, is interposed between 22B, vacuum, after pre-compression bonding was degassed under heating, it can be easily produced by integrating by curing the adhesive layer by heating or light irradiation.

【0173】なお、接着用樹脂フィルム24A,24B [0173] The adhesive resin film 24A, 24B
の厚さは、通常の場合、1μm〜1mm程度である。 The thickness of the case of normal, is about 1μm~1mm.

【0174】図示の電磁波シールド熱線カット性光透過窓材は請求項7の一例であって、請求項7は何ら図示のものに限定されるものではない。 [0174] The electromagnetic wave shielding heat-ray shielding and light transmitting material shown an example of Claim 7, Claim 7 shall by no means be limited to the illustrated.

【0175】例えば、中間膜は、透明基板とは別体のフィルムとして2枚の透明基板間に介在させる他、一方又は双方の透明基板の接着面側に、直接、前記酸化物透明導電膜と金属薄膜との多層膜を形成したものであっても良い。 [0175] For example, the intermediate layer, in addition to be interposed between two transparent substrates as a film separately from the transparent substrate, on the adhesive surface side of the transparent substrate of one or both, directly, with the transparent conductive oxide film be one obtained by forming a multilayer film with a metal thin film may be.

【0176】このような本発明の電磁波シールド性光透過窓材は、PDPの前面フィルタとして、或いは、病院や研究室等の精密機器設置場所の窓材等として有効に利用可能である。 [0176] electromagnetic-wave shielding and light transmitting plate of the present invention as described above, as a front filter of PDP, or, it is effective to be used as a window material or the like of the precision equipment location, such as a hospital or laboratory.

【0177】 [0177]

【実施例】以下に請求項7の電磁波シールド熱線カット性光透過窓材に係る実施例及び比較例を挙げる。 EXAMPLES Hereinafter according to the electromagnetic wave shielding heat-ray shielding and light transmitting material according to claim 7 Examples and Comparative Examples.

【0178】なお、実施例及び比較例で用いた接着用樹脂フィルム、中間膜及び強化ガラス板は、次のようにして製造した。 [0178] The adhesive resin film used in Examples and Comparative Examples, the intermediate layer and tempered glass plate was prepared as follows.

【0179】[接着用樹脂フィルム]エチレン−酢酸ビニル共重合体(東洋曹逹社製ウルトラセン634:酢酸ビニル含量26%、メルトインデックス4)100重量部に、1,1−ビス(t−ブチルパーオキシ)−3, [0179] [adhesive resin film] ethylene - vinyl acetate copolymer (Toyo 曹逹 Co. Ultrathene 634: vinyl acetate content 26%, melt index 4) to 100 parts by weight, 1,1-bis (t-butylperoxy ) -3,
3,5−トリメチルシクロヘキサン(日本油脂社製パーヘキサ3M)1重量部、γ−メタクリロキシプロピルトリメトキシシラン0.1重量部、ジアリルフタレート2 3,5-trimethylcyclohexane (manufactured by NOF Corporation Perhexa 3M) 1 part by weight, .gamma.-methacryloxypropyl 0.1 parts trimethoxysilane, diallyl phthalate 2
重量部、及び紫外線吸収剤としてスミソルブ130(住友化学工業社製)0.5重量部とを混合し、40mm押出機にて500μm厚さの両面エンボスの接着用樹脂フィルム4A,4Bを作製した。 Parts, and Sumisorubu 130 (manufactured by Sumitomo Chemical Co., Ltd.) as an ultraviolet absorber were mixed with 0.5 parts by weight, to prepare adhesive resin film 4A-sided embossing of 500μm thickness at 40mm extruder, a 4B.

【0180】[中間膜]厚さ100μmのPETフィルム上にマグネトロンスパッタリング法により厚さ400 [0180] Intermediate layer] thick by magnetron sputtering onto a PET film having a thickness of 100μm is 400
ÅのITO膜と厚さ100ÅのAg膜とを表1に示す積層数で交互に積層して多層膜を形成して中間膜3とした。 A Ag film of ITO film and the thickness of 100Å of Å was intermediate film 3 to form a multilayer film by alternately laminating a laminate number shown in Table 1.

【0181】[強化ガラス板]硝酸亜鉛濃度が0.5% [0181] [tempered glass] zinc nitrate concentration of 0.5%
となるように硝酸亜鉛6水和物Zn(NO 3 )2・6H 2 Become as zinc nitrate hexahydrate Zn (NO 3) 2 · 6H 2
Oと硝酸カリウムKNO 3をステンレス容器に入れ、3 O or potassium nitrate KNO 3 placed in a stainless steel vessel, 3
60℃に加熱して溶融塩とした。 Was molten salt heated to 60 ° C.. 縦1000mm、横6 Vertical 1000mm, horizontal 6
00mm、厚み3mm又は1mmのソーダライムシリカ組成のフロートガラスをこの溶融塩に1時間漬けてその後除冷して化学強化ガラス板とした。 300 mm, was cooled then dividing immersed 1 hour float glass soda-lime-silica composition having a thickness of 3mm or 1mm in the molten salt and chemically tempered glass.

【0182】実施例1,2 表面側透明基板2Aとして厚さ3.0mmの強化ガラス板を用い、この透明基板2Aの表面に、SiO 2 /IT [0182] Using the tempered glass plate having a thickness of 3.0mm as in Examples 1 and 2 the surface side transparent substrate 2A, the surface of the transparent substrate 2A, SiO 2 / IT
O/SiO 2 /ITOよりなる反射防止膜(総膜厚約2 O / SiO 2 / ITO made of the anti-reflection film (total thickness of about 2
500Å)5を形成し、裏面側透明基板2Bとして厚さ0.1mmのPETシートを用い、これらの間に2枚の接着用樹脂フィルム4A,4Bに表1に示す中間膜3を挟んだものを介在させ、これをゴム袋に入れて真空脱気し、90℃の温度で10分加熱して予備圧着した。 500 Å) 5 is formed, using a PET sheet having a thickness of 0.1mm as the back-side transparent substrate 2B, adhesive resin film 4A two between them, which sandwich the intermediate layer 3 shown in Table 1 to 4B the interposed, which was deaerated under vacuum and put in a rubber bag, and pre-bonding by heating 10 minutes at a temperature of 90 ° C.. その後、この予備圧着体をオーブン中に入れ、150℃の条件下で15分間加熱処理し、架橋硬化させて一体化した。 Then, the preliminary compression member placed in an oven and heated for 15 minutes under the conditions of 0.99 ° C., and integrated by crosslinking curing.

【0183】得られた窓材について下記方法により、3 [0183] For the obtained window material by the following method, 3
0MHz〜300MHzにおける電磁波シールド性、光透過率、熱線カット性を調べ、結果を表1に示した。 Electromagnetic shielding property in 0MHz~300MHz, light transmittance, examine the heat-ray shielding property, and the results are shown in Table 1.

【0184】[電磁波シールド性]KEC法(関西電子工業振興センター)に準拠したアンリツ社製EMIシールド測定装置(MA8602B)を用いて電界の減衰測定を行った。 [0184] went [electromagnetic shielding property] KEC method the attenuation measurement of the electric field by using the (Kansai Electronic Industry Development Center) manufactured by Anritsu Corporation EMI shield measuring device that conforms to the (MA8602B). サンプルの大きさは90mm×110mm The size of the sample is 90mm × 110mm
であった。 Met.

【0185】[光透過率(%)]日立製可視紫外光分光測定装置(U−4000)を用い、380nm〜780 [0185] Using the light transmittance (%)] Hitachi visible UV light spectrometer (U-4000), 380nm~780
nm間の平均可視光透過率を求めた。 To obtain an average visible light transmittance between nm.

【0186】[熱線カット性]上記日立製可視紫外光分光測定装置(U−4000)を用い、850〜1100 [0186] Using the heat-ray shielding property] the Hitachi visible UV light spectrometer (U-4000), 850~1100
nm間の平均近赤外光透過率を求めた。 To obtain an average infrared light transmission between nm.

【0187】比較例1,2 比較のため、中間膜として、ベースフィルム上に厚さ1 [0187] For Comparative Examples 1 and 2 compared, as an intermediate layer, the thickness on a base film of 1
600ÅのITO膜のみを形成したもの(比較例1)又はベースフィルム上に厚さ300ÅのAg膜のみを形成したもの(比較例2)を用いたこと以外は実施例1と同様にして窓材を製造し、同様にその評価を行って、結果を表1に示した。 Those formed only an ITO film of 600 Å (Comparative Example 1) or a base film obtained by forming only Ag film having a thickness of 300Å on, except for using (Comparative Example 2) In the same manner as in Example 1 window material manufactured similarly performing the evaluation, the results are shown in Table 1.

【0188】 [0188]

【表1】 [Table 1]

【0189】表1より、請求項7の電磁波シールド熱線カット性光透過窓材は、透明性、電磁波シールド性、熱線カット性のすべてにおいて良好な特性を示すことがわかる。 [0189] From Table 1, the electromagnetic wave shielding heat-ray shielding and light transmitting material according to claim 7, transparency, electromagnetic wave shielding property, it can be seen that good characteristics in all of the heat ray shielding properties.

【0190】実施例3、比較例3 通常のフロートガラスと、上記の化学強化ガラスを用いて機械的強度試験を行った。 [0190] Example 3, and Comparative Example 3 conventional float glass was the mechanical strength test using the above chemically strengthened glass. 図1の構造において透明基板2Aを厚さ2mmのフロートガラス板、透明基板2B Float glass plate having a thickness of 2mm the transparent substrate 2A in the structure of FIG. 1, the transparent substrate 2B
を厚さ1mmのフロートガラス板又は化学強化ガラス板として、インストロン社製圧縮試験機を用いて3点曲げ試験を行った。 As float glass or chemically reinforced glass plate having a thickness of 1 mm, it was subjected to three-point bending test using the Instron compression tester. サンプル形状、試験条件を下記に示す。 Sample shape, the test conditions are shown below.
また、試験結果を表2に示す。 Also, the test results in Table 2. サンプル形状 :50mm×150mm 3点曲げスパン :80mm クロスヘッド速度:2mm/min サンプル数 :n=5の平均値 Sample shape: 50 mm × 150 mm 3-point bending span: 80 mm Cross head speed: 2 mm / min sample size: n = 5 the average value

【0191】 [0191]

【表2】 [Table 2]

【0192】表2より、化学強化ガラスを用いることで破壊応力を向上させることができることがわかる。 [0192] From Table 2, it can be seen that it is possible to improve the fracture strength by using a chemically strengthened glass.

【0193】 [0193]

【発明の効果】以上詳述した通り、本発明の電磁波シールド性光透過窓材は、組み立てが容易で、また、設置対象の筐体に対して容易に組み込むことができ、しかも筐体に対して均一かつ低抵抗な導通を確実に得ることができるため、高い電磁波シールド性能を得ることができる。 As described above in detail, the electromagnetic wave shielding and light transmitting plate of the present invention, the assembly is easy, also it can be incorporated easily with respect to the housing of the installation target, yet housing to it is possible to reliably obtain a uniform and low resistance conductive Te, it is possible to obtain a high electromagnetic shielding performance.

【0194】また、本発明の電磁波シールド熱線カット性光透過窓材は、高透明性で、電磁波シールド性及び熱線カット性が著しく良好であるため、PDP用フィルター等として工業的に極めて有用である。 [0194] Further, the electromagnetic wave shielding heat-ray shielding and light transmitting material of the present invention is a high transparency, for electromagnetic shielding and heat-ray shielding properties are significantly better, it is industrially extremely useful as a PDP filter, etc. .

【0195】しかも、本発明の電磁波シールド性光透過窓材及び電磁波シールド熱線カット性光透過窓材は、透明基板の機械的強度が高く、また化学的安定性に富むため、高強度で良好な耐候、耐久性が得られる。 [0195] Moreover, the electromagnetic wave shielding and light transmitting plate and the electromagnetic wave shielding heat-ray shielding and light transmitting material of the present invention has high mechanical strength of the transparent substrate, and because rich in chemical stability, good high strength weather, durability can be obtained.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】図1(a)は請求項1の電磁波シールド性光透過窓材の実施の形態を示す模式的な断面図であり、図1 [1] Figure 1 (a) is a schematic sectional view showing an embodiment of the electromagnetic-wave shielding and light transmitting plate according to claim 1, FIG. 1
(b)は導電性粘着テープを貼り付けた透明導電性フィルムを示す平面図である。 (B) is a plan view showing a transparent conductive film was attached a conductive adhesive tape.

【図2】図2(a)は請求項3の電磁波シールド性光透過窓材の実施の形態を示す模式的な断面図であり、図2 [2] 2 (a) is a schematic sectional view showing an embodiment of the electromagnetic-wave shielding and light transmitting plate according to claim 3, Figure 2
(b)は導電性粘着テープを貼り付けた透明導電性フィルムを示す平面図である。 (B) is a plan view showing a transparent conductive film was attached a conductive adhesive tape.

【図3】図3は請求項7の電磁波シールド熱線カット性光透過窓材の実施の形態を示す模式的な断面図である。 Figure 3 is a schematic sectional view showing an embodiment of an electromagnetic wave shielding heat-ray shielding and light transmitting material according to claim 7.

【図4】請求項7に係る中間膜の実施の形態を示す模式的な断面図である。 4 is a schematic sectional view showing an embodiment of an intermediate film according to claim 7.

【符号の説明】 DESCRIPTION OF SYMBOLS

1,11 電磁波シールド性光透過窓材 2A,2B,12A,12B,22A,22B 透明基板 3,14A,14B 透明導電性フィルム 4A,4B,13A,13B,13C,24A,24B 1,11 electromagnetic-wave shielding and light transmitting plate 2A, 2B, 12A, 12B, 22A, 22B transparent substrate 3,14A, 14B transparent conductive film 4A, 4B, 13A, 13B, 13C, 24A, 24B
接着用樹脂フィルム 5,15,25 反射防止膜 A,B,17A,17B,17C 導電性粘着テープ(架橋型導電性粘着テープ) a,17a 金属箔 b,17b 粘着層 21 電磁波シールド熱線カット性光透過窓材 23 中間膜 31 ベースフィルム 32 酸化物透明導電膜 33 金属薄膜 Adhesive resin film 5, 15, 25 an anti-reflection film A, B, 17A, 17B, 17C electrically conductive adhesive tape (crosslinked electroconductive pressure-sensitive adhesive tape) a, 17a metallic foil b, 17b adhesive layer 21 electromagnetic shielding heat-ray shielding properties of light transmitting plate 23 intermediate film 31 base film 32 transparent conductive oxide film 33 a metal thin film

───────────────────────────────────────────────────── フロントページの続き (72)発明者 森村 泰大 東京都小平市小川東町3−1−1 株式会 社ブリヂストン技術センター内 Fターム(参考) 5C032 AA07 EE02 EE03 EF02 5C040 MA08 5E321 AA04 BB23 BB25 CC16 GG05 GH01 5G435 AA00 AA14 AA16 AA17 BB06 GG00 GG33 HH02 HH03 HH12 KK07 ────────────────────────────────────────────────── ─── front page of the continuation (72) inventor Morimura Tie Dye Tokyo Kodaira Kogawahigashi-cho 3-1-1 stock companies Bridgestone technical Center in the F-term (reference) 5C032 AA07 EE02 EE03 EF02 5C040 MA08 5E321 AA04 BB23 BB25 CC16 GG05 GH01 5G435 AA00 AA14 AA16 AA17 BB06 GG00 GG33 HH02 HH03 HH12 KK07

Claims (9)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 第1及び第2の透明基板間に透明導電性膜を介在させてなる電磁波シールド性光透過窓材において、 該第1及び第2の透明基板のうちの少なくとも一方は強化ガラスよりなる電磁波シールド性光透過窓材であって、 該透明導電性膜の縁部から該第1の透明基板の端面を経て該第1の透明基板の表面の縁部にまで達するように導電性粘着テープAが貼り付けられていることを特徴とする電磁波シールド性光透過窓材。 1. A first and electromagnetic-wave shielding and light transmitting plate comprising by interposing a transparent conductive film between the second transparent substrate, at least one of the tempered glass of the first and second transparent substrates a more becomes electromagnetic-wave shielding and light transmitting plate, a conductive to reach from the edge of the transparent conductive film to the edge of the surface of the first transparent substrate via an end face of the first transparent substrate electromagnetic-wave shielding and light transmitting plate, wherein the pressure-sensitive adhesive tape a is attached.
  2. 【請求項2】 請求項1において、前記第1及び第2の透明基板の端面から第1の透明基板の表面の縁部と第2 2. A claim in 1, the edge portion and the second surface of the first transparent substrate from the end face of the first and second transparent substrates
    の透明基板の表面の縁部とに回り込んで導電性粘着テープBが貼り付けられていることを特徴とする電磁波シールド性光透過窓材。 Electromagnetic-wave shielding and light transmitting plate, wherein the affixed conductive adhesive tape B wraps around the on the edge of the surface of the transparent substrate.
  3. 【請求項3】 一方の板面に第1の透明導電性膜を有する第1の透明基板と、一方の板面に第2の透明導電性膜を有する第2の透明基板とを、該透明導電性膜同士を対面させて接合一体化してなる電磁波シールド性光透過窓材において、 該第1及び第2の透明基板のうちの少なくとも一方は強化ガラスよりなる電磁波シールド性光透過窓材であって、 該第1の透明導電性膜の縁部から該第1の透明基板の端面を経て該第1の透明基板の他方の板面の縁部にまで達するように第1の導電性粘着テープが貼り付けられており、 該第2の透明導電性膜の縁部から該第2の透明基板の端面を経て該第2の透明基板の他方の板面の縁部にまで達するように第2の導電性粘着テープが貼り付けられていることを特徴とする電磁波シールド性光透過窓材。 A first transparent substrate having a wherein one of the first transparent conductive film on the plate surface, and a second transparent substrate having a second transparent conductive film on one of the plate surface, transparent in electromagnetic-wave shielding and light transmitting plate formed by integrally bonding a conductive film to each other so as to face, at least one of the first and second transparent substrates was in electromagnetic-wave shielding and light transmitting plate consisting of reinforced glass Te, the first conductive adhesive tape to reach from the edge of the first transparent conductive film to the edge of the other plate surface of the first transparent substrate via an end face of the first transparent substrate and it is pasted, the second to reach from the edge of the second transparent conductive film to the edge of the other plate surface of the transparent substrate of the second through the end face of the second transparent substrate electromagnetic-wave shielding and light transmitting plate, wherein the affixed is conductive adhesive tape.
  4. 【請求項4】 請求項3において、前記第1及び第2の透明基板の端面から第1の透明基板の他方の板面の縁部と第2の透明基板の他方の板面の縁部とに回り込んで第3の導電性粘着テープが貼り付けられていることを特徴とする電磁波シールド性光透過窓材。 4. The method of claim 3, and the edge of the other plate surface of the edge portion and the second transparent substrate of the other plate surface of the first transparent substrate from the end face of the first and second transparent substrates It wraps around in electromagnetic-wave shielding and light transmitting plate, wherein the third and the conductive adhesive tape is adhered to.
  5. 【請求項5】 請求項1ないし4のいずれか1項において、該導電性粘着テープが架橋型導電性粘着テープであることを特徴とする電磁波シールド性光透過窓材。 5. A any one of claims 1 to 4, electromagnetic-wave shielding and light transmitting plate of conductive adhesive tape is characterized in that it is a crosslinked electroconductive pressure-sensitive adhesive tape.
  6. 【請求項6】 請求項5において、該架橋型導電性粘着テープは、金属箔の一方の面に、導電性粒子を分散させた粘着層を設けてなり、 該粘着層は、エチレン−酢酸ビニル系共重合体を主成分とするポリマーとその架橋剤とを含む後架橋型接着層であることを特徴とする電磁波シールド性光透過窓材。 6. The method of claim 5, the crosslinking type conductive adhesive tape on one surface of the metal foil, it is provided an adhesive layer in which conductive particles are dispersed, the adhesive layer is an ethylene - vinyl acetate electromagnetic-wave shielding and light transmitting plate, which is a crosslinked adhesive layer after including the polymer as a main component system copolymers and their cross-linking agent.
  7. 【請求項7】 2枚の透明基板間に中間膜を介在させて、接着樹脂で接合一体化してなる電磁波シールド熱線カット性光透過窓材において、 該2枚の透明基板のうちの少なくとも一方は強化ガラスよりなる電磁波シールド性光透過窓材であって、 該中間膜は、酸化物透明導電膜と金属薄膜とを交互に積層してなる多層膜を備えることを特徴とする電磁波シールド熱線カット性光透過窓材。 And 7. is interposed an intermediate layer between two transparent substrates, in the electromagnetic shielding heat-ray shielding and light transmitting material formed integrally joined with an adhesive resin, at least one of said two transparent substrates a electromagnetic-wave shielding and light transmitting plate consisting of reinforced glass, the intermediate film, electromagnetic shielding heat-ray shielding properties, characterized in that it comprises a multilayer film formed by laminating a transparent conductive oxide film and the metal thin film are alternately the light transmission window material.
  8. 【請求項8】 請求項7において、該中間膜は透明基板上に形成されていることを特徴とする電磁波シールド熱線カット性光透過窓材。 8. The method of Claim 7, the electromagnetic wave shielding heat-ray shielding and light transmitting material, characterized in that the intermediate film is formed on a transparent substrate.
  9. 【請求項9】 請求項1ないし8のいずれか1項において、該強化ガラスは化学強化ガラスであることを特徴とする光透過窓材。 9. A any one of claims 1 to 8, the light transmission window material, wherein the reinforcing glass is chemically strengthened glass.
JP34723298A 1998-12-07 1998-12-07 Electromagnetic shieldable and light transparent window material and electromagnetic shieldable and heat ray cuttable light transparent window material Pending JP2000172182A (en)