JP2000149937A - Negative electrode material for nonaqueous electrolyte secondary battery, and its manufacture - Google Patents

Negative electrode material for nonaqueous electrolyte secondary battery, and its manufacture

Info

Publication number
JP2000149937A
JP2000149937A JP11249017A JP24901799A JP2000149937A JP 2000149937 A JP2000149937 A JP 2000149937A JP 11249017 A JP11249017 A JP 11249017A JP 24901799 A JP24901799 A JP 24901799A JP 2000149937 A JP2000149937 A JP 2000149937A
Authority
JP
Japan
Prior art keywords
si
negative electrode
secondary battery
material
method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP11249017A
Other languages
Japanese (ja)
Other versions
JP3562398B2 (en
Inventor
Masaru Abe
Hideya Kaminaka
Noriyuki Negi
Yoshiaki Nitta
Kazuhiro Okamura
Harunari Shimamura
秀哉 上仲
一広 岡村
治成 島村
芳明 新田
教之 禰宜
賢 阿部
Original Assignee
Matsushita Electric Ind Co Ltd
Sumitomo Metal Ind Ltd
住友金属工業株式会社
松下電器産業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to JP10-253981 priority Critical
Priority to JP25398198 priority
Application filed by Matsushita Electric Ind Co Ltd, Sumitomo Metal Ind Ltd, 住友金属工業株式会社, 松下電器産業株式会社 filed Critical Matsushita Electric Ind Co Ltd
Priority to JP24901799A priority patent/JP3562398B2/en
Publication of JP2000149937A publication Critical patent/JP2000149937A/en
Application granted granted Critical
Publication of JP3562398B2 publication Critical patent/JP3562398B2/en
Anticipated expiration legal-status Critical
Application status is Expired - Lifetime legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a negative electrode and a negative electrode material for a nonaqueous electrolyte secondary battery, having high discharge capacity and an excellent cycle life. SOLUTION: A negative electrode is manufactured using a material which comprises alloy particles having 0.1-50 μm of average particle size and containing an Si phase particle 40, and a solid solution or an intermetallic compound phase (for example, NiSi2 phase 41), for surrounding the particle 40, of Si and other element selected from the group comprising 2A group elements, transition elements, 3B group elements and 4B group elements in the periodic table, and in which a content of the Si phase particles 40 is 5-99 wt.%. The alloy particle is prepared by quenching-solidifying (for example, atomizing, roll-quenching) a fusion containing Si and other element, or by conducting heat-treatment after other element is deposited on Si powder by electrodeless plating or mechanical alloying. A negative electrode material excellent in discharge capacity and a cycle life is provided in the case of the quenching-solidification without heat-treatment.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、Li等のアルカリ金属を多量に、かつ可逆的に吸蔵・放出することができる非水電解質二次電池用の粉末状の負極材料と、この負極材料の製造方法に関する。 The present invention relates is a large amount of alkali metal such as Li, and a powdered negative electrode material for a non-aqueous electrolyte secondary battery capable of reversibly occluding and releasing of the negative electrode material It relates to a method for manufacturing. 本発明はまた、この負極材料を備えた負極の製造方法、ならびにこの負極材料を利用した、充電・放電容量とサイクル寿命が共に改善された非水電解質二次電池にも関する。 The present invention also relates a method of manufacturing a negative electrode having the negative electrode material, and using the anode material, in a non-aqueous electrolyte secondary battery charge and discharge capacity and cycle life were improved both.

【0002】なお、本発明でいう非水電解質二次電池は、支持電解質を有機溶媒に溶解した非水電解質を用いた電池と、高分子電解質やゲル電解質等の非水電解質を用いた電池とを包含する。 [0002] Incidentally, a non-aqueous electrolyte secondary battery in the present invention includes a battery supporting electrolyte using nonaqueous electrolyte dissolved in an organic solvent, a battery using a non-aqueous electrolyte, such as a polymer electrolyte or a gel electrolyte encompasses.

【0003】 [0003]

【従来の技術】携帯可能な小型の電気・電子機器の普及と性能向上に伴い、リチウムイオン二次電池で代表される非水電解質二次電池の生産量は大きく伸びており、その容量やサイクル寿命の向上が引き続き求められている。 BACKGROUND ART With the widespread use and performance improvement of electric and electronic equipment small-sized portable, production of nonaqueous electrolyte secondary batteries represented by lithium ion secondary batteries is growing larger, the capacity and cycle improvement of life is a continuing need.

【0004】現在の一般的な非水電解質二次電池では、 [0004] In the current general non-aqueous electrolyte secondary batteries,
負極材料として主に炭素材が使用されている。 Mainly carbon material is used as a negative electrode material. しかし、 But,
炭素材からなる負極では、LiC 6の組成までしかLiを吸蔵できないため、容量の理論的最大値は372 mAh/g と、金属リチウムの場合の約1/10に過ぎず、容量の向上に限界がある。 In the negative electrode made of carbon material, it can not occlude Li only to the composition of LiC 6, the theoretical maximum value of the capacity and 372 mAh / g, only about 1/10 of the case of metallic lithium, a limit to the improvement of capacity there is.

【0005】負極材料として当初使用された金属リチウムは、高容量を得ることができるものの、電池の充電・ [0005] Metal lithium was initially used as a negative electrode material, although it is possible to obtain a high capacity, charge and battery
放電を繰り返すとデンドライトが析出して短絡が発生するため、充電・放電のサイクル寿命が短く、実用的ではなかった。 Since short-circuiting repeated discharge the dendrite deposition occurs, the cycle life of charge-discharge is short, not practical.

【0006】高容量化を図るため、金属間化合物の形成によりLiを可逆的に吸蔵・放出することができる、Alといった元素を負極材料に用いる提案もあったが、吸蔵・ [0006] To increase the capacity, it is possible to reversibly absorbing and desorbing Li by the formation of intermetallic compounds, it was also proposed to use an element such as Al as a negative electrode material, absorbing and
放出に伴う体積変化により割れが生じ、微粉化する。 Cracking due to volume change associated with the release occurs, micronized. そのため、この負極材料を用いた二次電池は、充電・放電のサイクルが進むと急激に容量が低下し、サイクル寿命が短いものになる。 Therefore, a secondary battery using the anode material, rapidly capacity decreases when the cycle of charging and discharging proceeds, be something short cycle life.

【0007】この体積変化による負極材料の微粉化を防止するための対策として、負極材料のAlにLi、Si、B等を添加してAl材の格子定数を予め大きくすることが提案されている (特開平3−280363号公報) 。 [0007] As a countermeasure for preventing the pulverization of the negative electrode material according to this volume change, Li to Al of the anode material, Si, be pre large lattice constant of Al material was added to such B has been proposed (JP-A-3-280363). しかし、効果が不十分で、サイクル寿命を十分に向上させることができない。 However, the effect is insufficient, it is impossible to sufficiently improve the cycle life.

【0008】また、珪化物や他の金属間化合物の格子間にLiを吸蔵・放出させる提案もなされているが (特開平7−240201号、同9−63651 号各公報等) 、何れも大きな効果があるものではなかった。 Further, although, it is also suggested to occlusion and release of Li between lattices of silicide or other intermetallic compounds (JP-A-7-240201, the 9-63651 Patent JP-like), large none It was not there is an effect.

【0009】更に、各種の非水電解質二次電池用負極材料やその材料を備えた負極電極の提案はあっても、その材料の性能を最もよく発揮させるための組織を持つ負極材料やその製造方法の提案はなかった。 Furthermore, even if the proposal of negative electrodes having various non-aqueous electrolyte secondary battery negative electrode material and the material, negative electrode material and its production with a tissue for best demonstrate the performance of the material proposal of the method was not.

【0010】 [0010]

【発明が解決しようとする課題】本発明は、Liを吸蔵・ The object of the invention is to solve the present invention is, absorbing and the Li
放出する量が大きく、従って非水電解質二次電池の負極材料として用いた場合の充電・放電容量が大きく、しかも充電・放電を繰り返すことによる容量低下が少なく、 The amount of releasing large, thus a non-aqueous charge and discharge capacity is large when used as the negative electrode material for electrolyte secondary batteries, moreover less capacity degradation due to repeated charging and discharging,
サイクル寿命に優れている、非水電解質二次電池の負極材料を提供することを目的とする。 It has excellent cycle life, and to provide a negative electrode material of a nonaqueous electrolyte secondary battery.

【0011】本発明の別の目的は、この負極材料からなる負極を備えた非水電解質二次電池がその性能を最もよく発揮するような組織を持つ負極材料および負極の製造方法を提供することである。 Another object of the present invention, the negative electrode non-aqueous electrolyte secondary battery comprising a comprising the negative electrode material to provide a negative electrode material and the negative electrode manufacturing method having a tissue, such as to best exert its performance it is.

【0012】 [0012]

【課題を解決するための手段】シリコン(Si)は、Liとの金属間化合物 (Li 22 Si 5等) の生成を通して、Liを可逆的に吸蔵・放出することができる。 Means for Solving the Problems] Silicon (Si), through the generation of an intermetallic compound of Li (Li 22 Si 5, etc.), can be reversibly absorbing and desorbing Li. Siを非水電解質二次電池の負極材料に用いた場合のSiの充電・放電容量は、 Charge and discharge capacity of Si in the case of using Si as a negative electrode material for non-aqueous electrolyte secondary battery,
理論的には約4020 mAh/g (9800 mAh/cc : 比重2.33) と大きい。 In theory, about 4020 mAh / g: as large as (9800 mAh / cc specific gravity 2.33). この理論的最大容量は、現在実用化されている炭素材の理論的最大容量の372 mAh/g (844 mAh/cc : 比重2.27として) より遙かに大きく、金属リチウムの理論的最大容量3900 mAh/g (2100 mAh/cc : 比重0.53) と比較しても、電池の小型化という観点から重要な単位体積あたりの電極の容量は遙かに大きい。 The theoretical maximum capacity, 372 mAh / g theoretical maximum capacity of the carbon material that have already been put into practical use: much larger than (844 mAh / cc specific gravity 2.27), the theoretical maximum capacity 3900 mAh lithium metal / g: as compared with the (2100 mAh / cc specific gravity 0.53), the capacitance of the electrode per key unit volume from the viewpoint of miniaturization of the batteries much larger. 従って、Siは高容量の負極材料となりうる。 Therefore, Si can be a negative electrode material having a high capacity.

【0013】しかし、Siからなる負極材料は、Alの場合と同様に、Liの吸蔵・放出に伴う体積変化による割れで微粉化し易いため、充電・放電サイクルに伴う容量の低下が甚だしく、サイクル寿命が短いので、Siを負極材料にする試みはこれまでほとんどなされたことがない。 [0013] However, the anode material consisting of Si, as in the case of Al, for easily triturated with cracks due to volume change associated with occlusion and release of Li, severely decrease in the capacity accompanying the charging-discharging cycle, cycle life is short, never attempt has been made most far for the Si negative electrode material.

【0014】本発明者らは、Siからなる負極材料の持つ高い理論容量という特性に着目し、そのサイクル寿命の向上を目的として検討した結果、Si相粒の表面を、Siを含む固溶体又は金属間化合物の相で包囲すると、Liの吸蔵・放出に伴う体積変化が拘束されるため、Siの割れおよび微粉化が防止され、サイクル寿命が向上することを見出した。 [0014] The present inventors focused on the characteristics of high theoretical capacitance of the negative electrode material composed of Si, the results of investigation for the purpose of improving the cycle life, the surface of the Si phase grains, solid solution or a metal including Si When surrounded by a phase between compounds, the volume change associated with occlusion and release of Li is bound, it is prevented cracking and pulverization of Si, found that improved cycle life. この効果を十分に得るには、包囲に用いた固溶体や金属間化合物相の拘束が効くように、Si相を小さな粒径にした方が好ましく、そのような小さな粒径のSi To obtain this effect sufficiently, so effective against restraint of solid solution and intermetallic phases used in the siege, preferably better to the Si phase to a small particle size, Si of such small particle size
相は、急冷凝固法により効率よく形成することができる。 Phase can be efficiently formed by a rapid solidification method.

【0015】本発明により、1または2以上のSi相粒と、このSi相粒を少なくとも部分的に包囲するSi含有固溶体又は金属間化合物の相とを含んでいる合金粒子からなる非水電解質二次電池用負極材料であって、該合金粒子の平均粒径が0.1 μm以上、50μm以下であり、負極材料の5wt%以上、99wt%以下をSi相粒が占める、非水電解質二次電池用負極材料、が提供される。 [0015] The present invention, one or a more of Si phase grains, the non-aqueous electrolyte secondary comprising the Si phase grains from alloy particles and a phase of at least partially Si-containing solid solution or intermetallic compound surrounding a next cell negative electrode material, alloy particles having an average particle diameter of 0.1 [mu] m or more and 50μm or less, or more 5 wt% of the anode material, the following 99 wt% occupied Si phase grains, the non-aqueous electrolyte secondary battery anode material, is provided.

【0016】この合金粒子においてSi相粒を包囲する「Si含有固溶体又は金属間化合物」は、Siと、長周期型周期表の2A族元素、遷移元素、3B族元素、並びにSi [0016] "Si-containing solid solution or intermetallic compound" surrounding the Si phase grains in the alloy particles, Si and, 2A group elements of the long form periodic table, transition elements, 3B group elements, as well as Si
を除く4B族元素よりなる群から選ばれた少なくとも1 At least one selected from the group consisting of Group 4B elements other than
種の元素とから構成することができる。 It can be constructed from the seed of the element.

【0017】上記の非水電解質二次電池用負極材料は、 The negative electrode material for a nonaqueous electrolyte secondary battery described above,
下記の方法により製造することができる。 It can be prepared by the following method.

【0018】一つの方法は、合金粒子を構成する原料 [0018] One method, raw materials that make up the alloy particles
(Si元素+Siと固溶体又は金属間化合物を形成する少なくとも1種の元素) の溶融物を凝固速度が100 ℃/秒以上となるように冷却して凝固させて、Si相粒とこれを少なくとも部分的に包囲するSi含有固溶体又は金属間化合物の相とを含む合金を形成する工程を含む。 A melt of (at least one element forming a Si element + Si solid solution or an intermetallic compound) and cooled to solidifying as the solidification speed is 100 ° C. / sec or more, Si phase grains of at least part of this comprising the step of forming an alloy comprising a phase of Si-containing solid solution or intermetallic compound to surround. この方法は、凝固工程で得られた合金を該固溶体又は金属間化合物の固相線温度より10℃以上低い温度で熱処理する工程をさらに含んでいてもよい。 This method is an alloy obtained by solidification process may further comprise the step of heat treatment at solidus temperature than 10 ° C. or more lower temperature of the solid solution or an intermetallic compound. この熱処理は、急冷凝固により合金内に生じた歪みを除去することが目的であり、 This heat treatment is it is a purpose of removing the distortion caused in the alloy by rapid solidification,
歪みの程度が大きい場合には実施してもよい。 May be carried out in case the degree of distortion is large. 凝固速度が100 ℃/秒以上となる溶融物の冷却は、アトマイズ法、ロール急冷法及び回転電極法よりなる群から選ばれた方法で行うことができる。 Cooling of the melt solidification rate is 100 ° C. / sec or more can be performed by an atomization method, selected from the group consisting of a roll quenching method and a rotating electrode method method.

【0019】別の製造方法は、Si金属又はSi相を含む合金の粉末の表面に、Siと固溶体又は金属間化合物を構成する元素を含む材料の付着層を形成する工程、および付着層を形成した粉末を、該固溶体又は金属間化合物の固相線温度より10℃以上低い温度で熱処理して、付着層の材料をSi含有固溶体又は金属間化合物に変化させる工程を含む。 [0019] Another manufacturing method is formed on the surface of the alloy powder containing Si metal or Si phase, the step of forming a deposit of a material containing an element constituting the Si solid solution or intermetallic compound, and an adhesion layer powder was, was heat-treated at solidus temperature than 10 ° C. or more lower temperature of the solid solution or intermetallic compound, comprising the step of changing the material of the adhesion layer to the Si-containing solid solution or intermetallic compound. 付着層の形成は、メッキ法又はメカニカルアロイング法により行うことができる。 Formation of adhesive layer can be performed by a plating method or a mechanical alloying method.

【0020】上記の何れの製造方法においても、生成した合金粒子は、平均して5wt%以上、99wt%以下のSi相粒を含み、合金粒子の平均粒径が0.1 μm以上、50μm [0020] In any of the manufacturing methods described above, the resulting alloy particles have an average of 5 wt% or more, include 99 wt% or less of Si phase grains, the average grain size of the alloy particles is 0.1 [mu] m or more, 50 [mu] m
以下であることが好ましい。 That it is preferably less.

【0021】本発明によれば、非水電解質二次電池用負極の製造方法も提供される。 According to the present invention, a method of manufacturing a non-aqueous electrolyte secondary battery negative electrode it is also provided. この方法は、Si金属又はSi This method, Si metal or Si
相を含む合金の粉末を負極基板上に付着させて該基板上に粉末層を形成した後、この粉末層に、Siと固溶体又は金属間化合物を構成する元素を含む材料をメッキし、次いで前記固溶体又は金属間化合物の固相線温度より10℃ After forming the powder layer a powder of an alloy containing phases deposited on the negative electrode substrate on the substrate, to the powder layer, plated with a material containing an element constituting the Si solid solution or intermetallic compound, and then the 10 ° C. than the solidus temperature of the solid solution or intermetallic compound
以上低い温度で熱処理を施して、該メッキをSi含有固溶体又は金属間化合物に変化させることを特徴とする。 Subjected to heat treatment at a temperature lower than, and wherein the changing the plating Si-containing solid solution or intermetallic compound.

【0022】本発明はまた、非水電解質と、リチウムを可逆的に吸蔵および放出することができる正極と負極を備えた非水電解質二次電池において、該負極が上記の負極材料を含有する負極であるか、または上記の負極材料の製造方法で製造された負極材料を含有する負極であるか、または上記の負極の製造方法で製造された負極であることを特徴とする非水電解質二次電池にも関する。 [0022] The present invention also includes a non-aqueous electrolyte, in reversibly absorbing and non-aqueous electrolyte secondary battery comprising a positive electrode and a negative electrode capable of releasing lithium, a negative electrode the negative electrode contains a negative electrode material of the in it, or a non-aqueous electrolyte secondary, characterized in that either a negative electrode containing a negative electrode material manufactured by the manufacturing method of the negative electrode material or a negative electrode a negative electrode produced by the production method of the above also it relates to a battery.

【0023】この負極は、上記負極材料に対して5wt% [0023] The negative electrode, 5 wt% with respect to the negative electrode material
以上、80wt%以下の炭素材料を含有するものでよい。 Above, it may be those containing 80 wt% or less of the carbon material. 正極はリチウム含有遷移金属化合物を活物質とするものが好ましく、非水電解質はリチウム塩を炭酸エステルを含む有機溶媒に溶かした溶液が好ましい。 The positive electrode is preferably one that the lithium-containing transition metal compound as an active material, a non-aqueous electrolyte solution of lithium salt in an organic solvent containing a carbonic ester is preferable.

【0024】 [0024]

【発明の実施の形態】以下に、本発明に係る負極材料とその製造方法、およびこの負極材料からなる負極の製造方法、さらにこの負極材料を利用した非水電解質二次電池について詳述する。 DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS, anode material and manufacturing method thereof according to the present invention, and the negative electrode manufacturing method comprising the negative electrode material, will be described in more detail this nonaqueous electrolyte secondary battery using a negative electrode material. なお、以下の説明において、材料組成に関する%は、特に指定のない限り、重量%である。 In the following description,% regarding material composition, unless otherwise specified, are percent by weight.

【0025】 負極材料本発明に係る負極材料は、コアの1または2以上のSi相粒と、このSi相粒を少なくとも部分的に包囲するSi含有固溶体又は金属間化合物の相 (以下、包囲材ともいう) The negative electrode material according to the negative electrode material the invention, and one or more Si phase grains of the core, a phase of Si-containing solid solution or intermetallic compound at least partially surrounding the Si phase particles (hereinafter, enclosure member also called)
とを含む合金粒子からなる。 Consisting of alloy particles containing the door. 包囲材は、Si含有固溶体と金属間化合物との混合物であってもよく、さらに他の相を含有していてもよい。 Surrounding material may be a mixture of a Si-containing solid solution and intermetallic compound, it may further contain other phases.

【0026】コアのSi相粒は、負極活物質であって、金属間化合物 (例、Li 22 Si 5 )を形成することにより、リチウムと可逆的に化合・解離することができる。 The core of the Si phase grains is a negative electrode active material, the intermetallic compound (e.g., Li 22 Si 5) by forming a can with lithium reversibly compound and dissociation. 即ち、充電時にはLiと化合することでLiを吸蔵し、放電時にはLi That occludes Li by compounds with Li during charging, during discharging Li
を解離することでLiを放出する。 Releasing Li in dissociating. Si相粒は、Si相がマトリックスであれば、その中に他相が分散していてもよい。 Si phase grains, if Si phase matrix, other phases may be dispersed therein.

【0027】包囲材であるSi含有固溶体又は金属間化合物の相は、Liの吸蔵・放出に伴うSi相の体積変化を拘束して、その割れと微粉化を抑制し、サイクル寿命を向上させる。 The phases of Si-containing solid solution or intermetallic compound is surrounded material, to restrain the change in the volume of Si phase associated with occlusion and release of Li, suppressing the cracking and pulverization, thereby improving the cycle life. 負極活物質であるSi相粒が包囲材で完全に包囲されていても、Liイオンはイオン半径が非常に小さいため、包囲材の格子間を容易に通り抜けて、コアのSi相に到達し、これと化合することができる。 Even negative electrode active substances Si phase grains are completely surrounded by the surrounding material, since Li ions are ion radius is very small, readily pass through the interstices of the surrounding material, to reach the Si phase of the core, it can be combined with this. Si相から解離したLiイオンも同様に包囲材を通過して電解液中に放出される。 Li ions dissociated from the Si phase is also released into the electrolyte solution through the surrounding material as well. 即ち、包囲材は、Liイオンの通過を実質的に妨げずに、Si相粒を体積変化に対して拘束することができる。 That is, enclosure member is not substantially interfere with the passage of Li ions, it is possible to restrain the Si phase grains to volume change.

【0028】包囲の目的は、負極活物質であるSi相粒の体積変化を拘束することであるので、原理的には、包囲材はSiを含まない材料でもよい。 The purpose of the siege, so is to constrain the change in volume of the Si phase grains as a negative electrode active material, in principle, surrounding material may be a material that does not contain Si. しかし、包囲が剥離すると、この目的を達成することができない。 However, when the surrounding is peeled off, it is impossible to achieve this goal. この剥離を防止するために、包囲材は、Si相との同時凝固や包囲されたSi元素からのSiの拡散で形成できる、Siを含有する固溶体または金属化合物の相とする。 To prevent this peeling, enclosing member may be formed of Si diffusion from the simultaneous coagulation and enclosed Si element of the Si phase and a phase of solid solution or metal compound containing Si.

【0029】包囲材は、コアのSi相粒を完全に包囲したものでも、部分的に包囲したものでもよい。 The surrounding material is not intended to completely surround the Si phase grains of the core, it may be obtained by partially surrounding. 部分的に包囲した場合でも、上記拘束の目的を実質的に達成することができる。 Even when partially surrounding, it can be substantially achieving the above object constraint. 特に工業的生産では、すべてのSi相粒について厳密な意味で完全に包囲することは難しいし、又その確認も難しい。 In particular, in the industrial production, to it it is difficult to completely surround the strict sense for all of the Si phase grains, also difficult also the confirmation.

【0030】この粉末状の負極材料を構成する個々の合金粒子は、単一のSi相粒を含んでいても、複数のSi相粒を含んでいてもよい。 The individual alloy particles constituting the powdery negative electrode material may contain a single Si phase grains may comprise a plurality of Si phase grains. 単一のSi相粒を含む場合、合金粒子は、この単一のSi相粒の周囲が包囲材で少なくとも部分的に包囲された粒子からなる。 When containing a single Si phase grains, the alloy particles, the periphery of the single Si phase grains is at least partially enclosed particles enclosure member. 複数のSi相粒を含む合金粒子では、Si相粒が包囲材のマトリックス中に散在した形態 (Si相粒が比較的微細で、包囲材の割合が比較的多い) が一般的であるが、上記の単一のSi相粒を含む合金粒子が複数個結合したような、包囲材の割合が比較的少ないものも可能である。 The alloy particles containing a plurality of Si phase grains, form Si phase grains are dispersed in a matrix of surrounding material (Si phase grains are relatively fine, the rate of the envelope material is relatively large), but is generally, such as alloy particles containing a single Si phase grains described above was plurality bonds, the ratio of the envelope material is a relatively less available ones. 一つの負極材料の中で、この単一のSi相粒を含む合金粒子と、複数のSi相粒を含む合金粒子が混在していてもよい。 Within a single negative electrode material, the alloy particles comprising the single Si phase grains, the alloy particles comprising a plurality of Si phase grains may be mixed.

【0031】合金粒子中のSi相粒の平均粒径は、0.01μ The average particle diameter of the Si phase grains in the alloy particles, 0.01 micron
m以上、40μm以下であることが好ましく、より好ましくは1μm以上、35μm以下である。 m or more, preferably 40μm or less, more preferably 1μm or more and 35μm or less. コアのSi相粒の平均粒径が40μmを超えると、上記の拘束が効きにくくなることがある上、合金粒子の平均粒径が50μmを越えることがあり、Siの微粉化とサイクル寿命の悪化を防止することが困難となる。 When the average particle diameter of the core of the Si phase grains exceeds 40 [mu] m, on the above constraints may not be effective, may mean particle diameter of the alloy particles exceeds 50 [mu] m, deterioration of the micronized and cycle life of the Si it is difficult to prevent. Si相粒の平均粒径が0.01μm未満であると、合金粒子の製造時に表面酸化等が発生し易く、取扱いがむずかしくなる。 When the average particle diameter of the Si phase grains is less than 0.01 [mu] m, easily surface oxidation or the like occurs during production of the alloy particles, the handling becomes difficult. なお、合金粒子中が複数のSi相粒を含む場合には、Si相粒の平均粒径は好ましくは20μm以下である。 In the case where the alloy particles include a plurality of Si phase grains, the average grain size of Si phase grains is preferably 20μm or less.

【0032】合金粒子の平均粒径は0.1 μm以上、50μ The mean particle size of the alloy particles 0.1 [mu] m or more, 50.mu.
m以下である。 m is less than or equal to. 合金粒子の平均粒径が50μmを超えると、電極中の負極材料の充填密度が小さくなり、その容量が低下する。 When the average particle diameter of the alloy particles exceeds 50 [mu] m, the packing density of the negative electrode material in the electrode is reduced, the capacity is reduced. また、Si相粒の平均粒径は上記のように The average particle diameter of the Si phase grains, as described above
40μm以下が好ましいので、平均粒径が50μmを超えると包囲材の厚さが大きくなりすぎ、Si相の占める割合が減って、結果として負極材料としての容量が小さくなる。 Since less preferred 40 [mu] m, average particle size becomes too large thickness of the surrounding material more than 50 [mu] m, decreases the ratio of Si phase, the capacity of the negative electrode material is reduced as a result. 合金粒子の平均粒径が0.1 μmより小さいと、包囲材が薄すぎて前記の拘束が効きにくくなる。 Mean particle and diameter 0.1 [mu] m smaller than the alloy particles, wherein the restraint function may not be effective too a thin enclosure member. 合金粒子の好ましい平均粒径は1μm以上、40μm以下、より好ましくは5μm以上、35μm以下である。 The preferred average particle diameter of the alloy particles 1μm or more, 40 [mu] m or less, more preferably 5μm or more and 35μm or less.

【0033】Si相粒および合金粒子のいずれについても、粒子形状が、例えばフレーク (薄片) のように不規則 (非球形) である場合には、合金粒子の粒径は短径と長径の平均値をとる。 [0033] For any of Si phase grains and alloy particles, particle shape, for example in the case of flake irregular (non-spherical) as (flakes), the particle diameter of the alloy particles have an average minor diameter and the major diameter It takes a value. こうして求めた合金粒子の粒径の粒子体積に対する平均値を平均粒径とする。 The average value for the particle volume of the particle diameter of the alloy particles thus obtained and the average particle size.

【0034】Si相粒の粒径は、例えば走査型電子顕微鏡(SEM) により測定することができる。 The Si phase grains of particle size may be measured, for example, by a scanning electron microscope (SEM). 合金粒子の粒径については各種の測定法が可能である。 The particle diameter of the alloy particles can various measurement methods. 例えば、レーザー回折型粒度測定装置により測定した体積粒度分布のメジアン径を平均粒径とすることができ、実施例ではこの方法を採用した。 For example, the median diameter of volume particle size distribution measured by a laser diffraction type particle size measuring device can be an average particle size, in the embodiment employing this method.

【0035】負極材料の5〜99wt%をSi相粒が占める。 [0035] Si phase grains account for 5~99wt% of the negative electrode material.
残りは本質的にSi含有固溶体又は金属間化合物の相が占める (即ち、本質的にこの相とSi相粒とから合金粒子が構成される) ことが好ましいが、負極性能に著しい悪影響がなければ、Siを含有しない第3の相が合金粒子中に共存していもよい。 The remainder occupied by phase essentially Si-containing solid solution or intermetallic compound is (i.e., essentially the alloy particles from this phase and the Si phase grains is constructed) it is preferable, if there is no significant adverse effect on the negative electrode performance , a third phase containing no Si may coexist in the alloy particles. Si相の比率が99wt%を越えると、包囲材の厚さが小さくなり過ぎ、上記拘束が効きにくくなる。 When the ratio of the Si phase is more than 99 wt%, the thickness becomes too small enclosure member, the restraint function may not be effective. Si相の比率が5wt%未満では、負極材料として容量が小さくなりすぎる。 In less than 5 wt% ratio of the Si phase, the capacity is too small as a negative electrode material. Si相の比率は、好ましくは8wt% The ratio of the Si phase is preferably 8 wt%
以上、95wt%以下、より好ましくは10wt%以上、50wt% Above, 95 wt% or less, more preferably 10 wt% or more, 50 wt%
以下である。 Less.

【0036】前述したように、包囲材の材料は、コアの [0036] As described above, the material of the envelope material, the core
Si相粒との剥離を防止するために、Siを含有する固溶体又は金属間化合物から構成する。 To prevent separation of the Si phase grains, constituting a solid solution or intermetallic compound containing Si. Siと固溶体又は金属間化合物を形成する元素は、好ましくは長周期型周期表の2A族元素 (アルカリ土類金属) 、遷移元素、3B族 Forming elements Si and solid solutions or intermetallic compound, preferably a Group 2A element of the long form periodic table (alkaline earth metals), transition elements, 3B group
(ホウ素族) 元素、並びにSi以外の4B族 (炭素族) 元素よりなる群から選ばれた1種もしくは2種以上の金属元素である。 (Group boron) element, and Group 4B other than Si is one or more metal elements selected from the group consisting of (carbon group) elements.

【0037】上記元素の好ましい例を挙げると、2A族元素ではMg、Ca、Ba;遷移元素ではNd、Pr、Ce等の希土類元素と、Ti、Cr、W、Mn、Fe、Co、Ni、Cu;3B族元素ではAl、Ga、In、Tl;4B族元素ではGe、Sn、Pbである。 [0037] and preferred examples of the above elements, Mg in Group 2A element, Ca, Ba; and rare earth elements Nd, Pr, and Ce, etc. is transition element, Ti, Cr, W, Mn, Fe, Co, Ni, Cu; the group 3B element Al, Ga, in, Tl; the group 4B element is Ge, Sn, Pb. これらのうち、より好ましい元素はMg、Ca、W、F Among these, more preferable elements are Mg, Ca, W, F
e、Co、Niである。 e, Co, is Ni.

【0038】 負極材料の製造方法 1または2以上のSi相粒がSi含有固溶体又は金属間化合物からなる包囲材で少なくとも部分的に包囲された合金粒子からなる、本発明に係る非水電解質二次電池用負極材料は、次に説明する2つの製造方法のいずれかにより製造することができる。 [0038] Production Method 1 or 2 or more of the Si phase grains of the anode material consists at least partly enclosed alloy particles enclosure member consisting of Si-containing solid solution or intermetallic compound, a non-aqueous electrolyte secondary according to the present invention anode material for batteries, can then be prepared by one of two manufacturing methods described.

【0039】(製造方法1)合金粒子を構成する原料 (即ち、Siと、Siと固溶体又は金属間化合物相を形成できる1種もしくは2種以上の元素、との混合物) を溶融して得た溶融物を、凝固速度が100 ℃/秒以上となるように冷却して凝固させ、Si相粒がSi含有固溶体又は金属間化合物で少なくとも部分的に包囲された合金を生成させる。 The material constituting the (production method 1) alloy particles (i.e., the Si, 1 kind or two or more elements capable of forming Si and solid solutions or intermetallic phases, a mixture of) obtained by melting the melt solidification rate allowed to cool and solidify such that the 100 ° C. / sec or more, Si phase grains to produce an at least partially enclosed alloys Si-containing solid solution or intermetallic compound. 必要であれば、凝固物を、包囲材を構成するSi含有固溶体又は金属間化合物の固相線温度より10℃以上低い温度を用いて熱処理を行い、および/または粉砕を行う。 If necessary, performs coagulum was heat-treated using a solidus temperature lower 10 ° C. or higher than the temperature of the Si-containing solid solution or intermetallic compound constituting the surrounding material, and / or grinding. 熱処理する場合には、粉砕は熱処理の前と後のいずれで行ってもよい。 If the heat treatment, the milling may be performed either before and after heat treatment.

【0040】この第1の方法では、前記溶融物の凝固により、Si相粒がSi含有固溶体又は金属間化合物で少なくとも部分的に包囲された合金が生成する。 [0040] In this first method, the by solidification of the melt, alloy Si phase grains are at least partially surrounded by Si-containing solid solution or intermetallic compound is produced. 凝固速度が10 Solidification rate is 10
0 ℃/秒以上となる急冷により凝固させると、多くの析出核が生成するため、多相系合金の場合には、最初に析出する初晶の相と、引き続き析出する相のどちらも微細となる。 0 ℃ when solidifying by rapid cooling to be / sec or more, because many precipitation nuclei to generate, in the case of a multi-phase alloy has a phase of the primary crystal that initially precipitated, both phase to continue precipitated fine Become. 即ち、上記合金の場合には、Si相粒とSi含有固溶体又は金属間化合物の相のどちらも微細な結晶粒となる。 That is, in the case of the alloy, both phases of the Si phase grains and the Si-containing solid solution or intermetallic compound becomes a fine grain.

【0041】凝固中の合金の析出形態は一定ではない。 [0041] precipitated the form of an alloy during solidification is not constant.
共晶系の合金原料の場合、Si相とSi含有固溶体又は金属間化合物の相とが同時に析出し、Si相とSi含有固溶体又は金属間化合物の相が微細に混ざり合った組織の合金が得られる。 For alloy materials of eutectic system, phases and precipitates simultaneously Si phase and Si-containing solid solution or intermetallic compound, an alloy of tissue phases of the Si phase and Si-containing solid solution or intermetallic compound is mixed in the fine is obtained It is. Si相が初晶である場合、最初に析出した微細なSi相粒が、後から析出したSi含有固溶体又は金属間化合物の微細な相 (この相がSi相との共晶となることもある) で少なくとも部分的に包囲され、またはその中に閉じ込められた組織を持つ合金が得られる。 If Si phase is the primary phase, it is initially deposited fine Si phase grains, fine phase Si-containing solid solution or intermetallic compound precipitated later (also this phase is the eutectic of Si phase ) in at least partially surrounded or alloy is obtained with a tissue trapped therein. Si含有固溶体又は金属間化合物の相が初晶である場合、この相からなる多くの微細な結晶粒が最初に析出し、その粒界に後から微細なSi相 (これも共晶となりうる)が析出する。 If the phase of the Si-containing solid solution or intermetallic compound is primary crystal, many fine grains comprising the phase initially precipitated, fine Si phase after its grain boundaries (which may also be a eutectic) There is precipitated. その結果、微細なSi相粒がSi含有固溶体又は金属間化合物の相の中に点在した組織の合金が得られる。 As a result, the alloy fine Si phase grains are interspersed with the phase of Si-containing solid solution or intermetallic compound structure is obtained. いずれ合金組織も、微細なSi相粒がSi含有固溶体又は金属間化合物の相で少なくとも部分的に包囲された合金ということができる。 Any alloy structure may also be referred to as fine Si phase grains are at least partially surrounded by a phase of Si-containing solid solution or intermetallic alloy.

【0042】溶融原料は、包囲材となるSi含有固溶体又は金属間化合物相に対してSiリッチとする。 The molten raw material, a Si-rich relative to Si-containing solid solution or intermetallic compound phase becomes enclosure member. 原料中のSi Si in the raw material
と他の元素との割合により、凝固中に生成するSi相粒が負極材料中で占める比率が決まる。 And the ratio of the other elements, determines the ratio of Si phase grains formed during solidification occupies the negative electrode material. 第1の方法で製造される合金粒子は、単一のSi相粒を含む場合もあるが、通常は複数のSi相粒を含むことが多い。 Alloy particles produced by the first method, but also include a single Si phase grains, usually often include a plurality of Si phase grains. この方法は、製造工程が比較的単純である。 The method, the manufacturing process is relatively simple.

【0043】凝固速度が100 ℃/秒未満であると、析出したSi相粒が成長して粗大となり、その平均粒径が40μ [0043] If the solidification rate is less than 100 ° C. / sec, it becomes coarse precipitated Si phase particle grows, the average particle diameter of 40μ
mを越えることがある。 It may exceed m. 好ましい凝固速度は1000℃/秒以上である。 Preferred solidification rate is 1000 ° C. / sec or more. 凝固速度の上限は制限されないが、工業的には10 6 ℃/秒台以下とすることが好ましい。 The upper limit of the cooling rate is not limited, but industrially it is preferable to 10 6 ° C. / sec table below.

【0044】凝固速度が100 ℃/秒以上になるような冷却方法 (以下、急冷凝固法という)としては、製造技術の完成度、量産性、コスト等を考慮すれば、アトマイズ法、急冷ロール法、および回転電極法が好ましい。 The cooling method as the solidification rate becomes more than 100 ° C. / sec (hereinafter, referred to as rapid solidification) as the maturity of the manufacturing technology, mass production, considering the cost, an atomizing method, chill roll method , and rotary electrode method are preferable. これらの方法のうち、アトマイズ法と回転電極法では粉末状の合金が得られる。 Among these methods, the powdered alloy is obtained by the atomization process rotary electrode method. それぞれの凝固方法について、添付図面を参照して次に詳述する。 For each of the coagulation method, it is explained in detail below with reference to the accompanying drawings.

【0045】アトマイズ法は、ガスアトマイズ法と液体アトマイズ法のいずれも可能であるが、球形に近い粒子が得られるガスアトマイズ法の方が好ましい。 The atomizing method is susceptible neither the gas atomizing method and a liquid atomizing method, towards gas atomizing method nearly spherical particles are obtained preferably. なお、いずれの場合も、粒子の酸化を防ぐために、非酸化性の雰囲気または環境を保持することが好ましい。 Incidentally, in either case, to prevent oxidation of the particles, it is preferable to hold the non-oxidizing atmosphere or environment.

【0046】図1(a) はガスアトマイズ法の装置を模式的に示した説明図であり、図1(b)はそのノズル部の拡大断面図である。 [0046] FIG. 1 (a) is an explanatory view of the apparatus of the gas atomizing method shown schematically, FIG. 1 (b) is an enlarged sectional view of the nozzle portion. 所定割合で配合された原料は、通常、 Raw material formulated in a predetermined ratio, typically,
真空または不活性雰囲気で高周波誘導溶解炉で溶解する。 Dissolved in a high-frequency induction melting furnace in a vacuum or in an inert atmosphere. 溶解した溶融物 (溶湯) は、直接給湯管12に注湯されることもあるが、通常はタンディッシュや保熱炉等の貯湯装置に一旦貯められて、給湯管12を介してアトマイズタンク11内に滴下される。 Dissolved melt (molten metal) is also be poured directly into hot water supply pipe 12, normally are accumulated temporarily in the hot water storage device, such as a tundish or a heat retaining furnace, atomizing tank 11 via the hot water supply pipe 12 It is added dropwise within. タンク11内は通常不活性ガス雰囲気に保たれており、生成したアトマイズ粉末の酸化を防ぐようにしている。 The tank 11 typically is kept in an inert gas atmosphere, and to prevent oxidation of the resulting atomized powder.

【0047】図1(b) に示すように、タンク11内では、 [0047] As shown in FIG. 1 (b), in the tank 11,
前記給湯管12の近傍にガスアトマイズノズル13を配置する。 Placing the gas atomizing nozzles 13 in the vicinity of the hot water supply pipe 12. アトマイズガス13b を、ガス供給系15よりガス供給管14を介してノズル13に供給し、17として示すように、 The atomizing gas 13b, and supplied to the nozzle 13 through the gas supply pipe 14 from a gas supply system 15, as shown as 17,
ノズル13に設けられた孔またはスリット13aから、滴下中の溶湯に向けて噴出させる。 From holes or slits 13a provided in the nozzle 13, it is ejected toward the molten metal in the dropping. 溶湯は噴出ガス17のエネルギーにより四散し、凝固し、粉末化する。 Molten metal was Shisan by the energy of the jet gas 17, solidified, pulverized. 生成した粉末は、アトマイズタンク11の下部より粉末収納装置 (図示せず) へ導かれ、収納される。 The resulting powder is led from the bottom of the atomizing tank 11 powder storage device (not shown) are housed.

【0048】ガスアトマイズ法で生成した粉末の粒径は、滴下中の溶湯に与える噴出ガスのエネルギーが大きくなるほど通常は小さくなる。 [0048] The powder produced by gas atomization a particle size is usually small enough energy of the jet gas to give the molten metal in the dropping is increased. 噴出ガスのエネルギーは、例えばガスの圧力や、ノズルの孔またはスリット大きさや配置により調節できる。 Energy of the jet gas, for example gas pressure or can be adjusted by the hole or slit size and arrangement of the nozzles. また、噴出ガスのエネルギーが同一であれば、単位時間当たりの溶湯の滴下量が少ないほど粉末の粒径は小さくなるのが普通である。 Further, if the energy of the jet gas is the same, the particle size of the powder as dropping amount of the molten metal per unit time is small is usually smaller. 溶湯の滴下量は、給湯管の内径や給湯管内の溶湯に加える圧力により調節できる。 Dropping amount of the molten metal can be adjusted by the pressure applied to the molten metal of an inner diameter and hot water pipe of the hot water supply pipe.

【0049】図2は、単ロール急冷法の装置の例を模式的に示した説明図である。 [0049] Figure 2 is an explanatory diagram an example of an apparatus of a single roll quenching method shown schematically. 図1の場合と同様に原料を溶解して得た原料溶融物 (溶湯) を溶湯タンディッシュ22 Raw material melt obtained by dissolving the raw material as in the case of FIG. 1 (melt) the melt tundish 22
に注湯する。 It is poured into. 溶湯タンディッシュ22には、溶湯を急冷ロール21の外周部へ注ぐために、底部にタンディッシュノズル23が配置されている。 The melt tundish 22, to pour the molten metal into the outer peripheral portion of the chill roll 21, tundish nozzle 23 is disposed at the bottom. タンディッシュノズル23の孔の形状は、単独の孔でもよいし、孔を1列または2列以上に並べたものでもよく、またスリット状のものでもよい。 The shape of the hole of the tundish nozzle 23 may be a single hole, it may be those obtained by arranging holes in one or more or two columns, or may be of a slit shape. 溶湯タンディッシュ22の形状も、箱状、円筒状等周囲の装置部品の配置等を考慮して設計すればよい。 The shape of the molten metal tundish 22, box-shaped, the arrangement of the parts of the device surrounding the cylindrical or the like may be designed in consideration. 内部に、耐火物や溶湯のスラグ等の混入を防止するために堰を設けることもよく行われている。 Therein, it has been made also often construct a dam to prevent the mixing of slag such as refractory and the molten metal.

【0050】急冷ロール21は、外周部には銅等の熱伝導性の良い材料を用い、その内側の芯金部には通常鋼材を用いていることが多い。 The chill roll 21, with a good heat conductivity material such as copper on the outer peripheral portion, it is often using conventional steel core metal portion of the inside. これらの急冷ロールの材料は、 The material of these quenching roll,
これに限ることなく、使用目的に沿ったものであれば特に限定されない。 The present invention is not limited to this, but are not particularly limited as long as in line with the intended use. ロールの寿命を延長するためにロール内部に冷却水を通すことも周知の方法である。 It is also well known methods through the cooling water inside the roll in order to extend the life of the roll. また同様の目的でロール21の外周部にNi、W、Cr等の金属や炭化物等の化合物等のメッキや溶射を施すこともある。 There also Ni to the outer peripheral portion of the roll 21 for the same purpose, W, also be subjected to plating or spraying compounds such as metal or carbides Cr.

【0051】急冷ロール21は矢印25の方向に回転させておく。 The chill roll 21 is allowed to rotate in the direction of arrow 25. ロール回転時のロール外周の周速度の値は種々の値が用いられているが、通常1×10 -2 〜6×10 2 m/秒の範囲内であることが多い。 Peripheral velocity of the values of the roll outer during the roll rotation is various values have been used, often in the range of usually 1 × 10 -2 ~6 × 10 2 m / sec. 急冷ロールの直径も特に限定されるものではないが、直径100〜600 mmのものが比較的よく用いられている。 But are not limited to the diameter of the chill roll in particular, it has been used relatively frequently having a diameter 100 to 600 mm. 実用的見地からは、ロール直径 From a practical point of view, roll diameter
400〜600mm 、ロール周速6×10 -2 〜1.3 ×10 2 m/秒が好ましい。 400 to 600 mm, preferably a roll peripheral speed 6 × 10 -2 ~1.3 × 10 2 m / sec.

【0052】溶湯タンディッシュ22に貯められた溶湯をタンディッシュノズル23を介して急冷ロール21の外周部に注ぐと、溶湯はロールによって抜熱されて急速に冷却され、凝固する。 [0052] Once the molten metal has been accumulated in the melt tundish 22 through the tundish nozzle 23 is poured into the outer periphery of the chill roll 21, the molten metal is rapidly cooled is heat extraction by rolls, solidifies. 凝固した合金の形状は、箔帯状または/あるいは片状 (以後、急冷片と言う) をなしていることが多い。 The shape of the solidified alloy often forms a foil web or / or flake (hereinafter referred to as quenching piece). 得られた急冷片は、急冷片回収フード24を介して、矢印で示すように落下させて、急冷片収納装置 Resulting quench piece, via a quenching piece collection hood 24, is dropped as indicated by the arrow, quench piece storage device
(図示せず) に収納すればよい。 It may be housed (not shown).

【0053】急冷片の凝固速度を制御する方法は、例えば、急冷ロール21の回転速度や溶湯タンディッシュ23から急冷ロール21へ注ぐ単位時間当たりの溶湯の量を調整する方法がある。 [0053] The method of controlling the solidification rate of the quenching piece, for example, a method of adjusting the amount of molten metal per unit time to pour into the chill roll 21 from the rotational speed and molten metal tundish 23 of the chill roll 21. すなわち、回転速度を大きくしたり、 That, or increasing the rotational speed,
急冷ロール21へ注ぐ単位時間当たりの溶湯の量を減らすと、前記急冷片の厚みが薄くなり凝固速度は大きくなる。 Reducing the amount of molten metal per unit time pouring into chill roll 21, the thickness becomes thinner solidification rate of the quench piece increases.

【0054】得られた急冷片は一般に厚みが非常に薄いので、機械的な粉砕手段 (例、ボールミル、ジェットミル等) により容易に粉末にすることができる。 Since [0054] the resulting quench pieces are generally very thin thickness can be easily powdered by mechanical pulverization means (e.g., ball mill, jet mill, etc.). この粉砕も含めて、ロール急冷法も不活性ガス雰囲気中で行うことが好ましい。 The ground included, roll quenching method is also preferably carried out in an inert gas atmosphere.

【0055】図3(a) には、回転電極法の例として、プラズマ回転電極法による冷却装置の模式図を示す。 [0055] FIG. 3 (a), as an example of the rotary electrode method, shows a schematic view of a cooling device according to the plasma rotating electrode process. この冷却装置30は、密閉チャンバー31で覆われ、チャンバー内は通常排気装置39により10 -2 〜10 -1 torr程度に減圧されている。 The cooling device 30 is covered with a sealed chamber 31, it is depressurized in the chamber by a normal vacuum apparatus 39 of about 10 -2 ~10 -1 torr. 対極32と消耗電極33を対向して配置し、それぞれ駆動軸35、36を介して矢印方向に設けた駆動装置 The counter electrode 32 and the consumable electrode 33 is disposed to face the driving device provided in an arrow direction respectively through the drive shaft 35, 36
(図示せず) に連結し、回転できるようにする。 Connected to (not shown), to rotate.

【0056】対極32の構造の例は、図3(b) に示すように、銅製のノズル321 とタングステン製の電極部322 で構成される。 [0056] Examples of the structure of the counter electrode 32, as shown in FIG. 3 (b), it consists of copper nozzle 321 and the tungsten electrode 322. それぞれを冷却水324 で冷却できるようにして、プラズマ発生時の高温の環境に耐えられるようにしておく。 So as to each be cooled by cooling water 324 in advance so as to withstand the high temperature environment during plasma generation. プラズマアーク用の不活性ガス323 をタングステン製の電極部322 に図に示すように供給し、両電極間に作用させた電圧30Vの電場で高温のプラズマアーク The inert gas 323 for plasma arc fed as shown in Figure in a tungsten electrode 322, a high temperature in an electric field voltage 30V which is applied to between the electrodes plasma arc
34が発生し、消耗電極33を構成する材料を溶解させる。 34 occurs, dissolving the material constituting the consumable electrode 33.

【0057】この間、両電極32, 33をそれぞれの駆動軸 [0057] During this time, each of the drive shafts of both electrodes 32, 33
35、36およびそれに連結された適宜駆動装置 (図示せず) により互いに反対方向に回転させる。 Rotate in opposite directions to each other by 35, 36 and appropriately driving device coupled thereto (not shown). 該回転の回転数は種々の値をとることができ、通常は1000〜5000 rpm Rotational speed of the rotation can take various values, usually of 1000-5000 rpm
程度であるが、20,000 rpmのものもある。 Is a degree, there is also a thing of 20,000 rpm.

【0058】消耗電極33は、粉末化しようとする材料 [0058] consumable electrode 33, tries to powdered material
(即ち、Si+他の元素) で構成する。 (I.e., Si + other elements) composed of. 原料を上記のように溶解し、この溶融物を所望の形状に鋳込み、電極とする。 Material was dissolved as described above, casting the melt into a desired shape to the electrode. 円筒状の形状にすることが多い。 Often in a cylindrical shape. 円筒の直径も種々の値をとることができ、直径30〜50 mm のものを用いることが多いが、直径120 mm程度のものもある。 Cylinder diameter also can take various values, it is often used a diameter of 30 to 50 mm, there is also a diameter of about 120 mm.

【0059】電極33は、上記のように発生したプラズマアーク34により先端から順次溶解され、その回転に伴って四散して、急冷凝固し、粉末となる。 [0059] electrode 33, the plasma arc 34 generated as described above are dissolved successively from the tip, and Shisan along with its rotation, and rapid solidification, and powder. 四散した粉末はチャンバー31の下部より矢印方向に取り出され、粉末収納装置 (図示せず) に導かれ収納される。 Shisan powder was taken out in an arrow direction from the lower part of the chamber 31, it is guided to the powder storage device (not shown) housed.

【0060】粉末の粒径は、主として電極33の回転数およびビレット径で決まる。 [0060] The powder particle size is determined by the rotational speed and the billet diameter of mainly electrode 33. 例えば、粉末の粒径をより小さくしようとする場合は、陰極33の回転数を大きくすればよいし、ビレット径を小さくすればよい。 For example, when trying to further reduce the particle size of the powder, may be increasing the rotational speed of the cathode 33 may be reduced billet diameter. また、プラズマアーク用ガスは、ArまたはHeを用いることが多い。 The plasma arc gas is often used Ar or He.

【0061】第1の方法に従って急冷凝固法により形成された合金は、Ni−Si合金を例にとると、Si相粒と、金属間化合物 NiSi 2相およびNiSi相とが共存した状態になる。 [0061] alloy formed by rapid solidification in accordance with the first method, taking the NiSi alloy as an example, a state in which the Si phase grains, and the intermetallic compound NiSi 2 phase and NiSi phase coexist. この例では、3相の中で最も凝固温度が高いSi相が凝固中に析出して初晶を形成し、引き続き初晶Si相の周囲に、液相とSi相との反応でNiSi 2が晶出する。 In this example, the most solidification temperature is higher Si phase among the three phases is precipitated during solidification to form a primary crystal, continuing around the primary crystal Si phase, the NiSi 2 in the reaction between the liquid phase and the Si phase It crystallizes. その後、残った液相はNiSiとNiSi 2との共晶を晶出して凝固する。 After that, the remaining liquid phase is solidified out of the eutectic of the NiSi and NiSi 2 crystals. ガスアトマイズ法または回転電極法により凝固させた球形合金粒子は、図4に示すように、NiSi 2相42で包囲されたSi相粒40が(NiSi 2 +NiSi) 相41からなるマトリックス中に散在した凝固組織を持つ。 Spherical alloy particles was solidified by gas atomization or rotary electrode method, as shown in FIG. 4, solidification Si phase grains 40 surrounded by NiSi 2 phase 42 is dispersed in the matrix of (NiSi 2 + NiSi) phase 41 with the organization. この合金粒子は1個の粒子中に複数個のSi相粒を有する組織を持つことが多い。 The alloy particles often have tissue having a plurality of Si phase grains in one particle.

【0062】急冷凝固では、析出したどの相も微細であるので、生成した合金中のSi相粒は、平均粒径が通常25 [0062] In rapid solidification, since any phase precipitated also fine, Si phase grains in the resulting alloy has an average particle diameter of usually 25
μm以下となり、特に凝固速度の大きいアトマイズ法や急冷ロール法では平均粒径が10μm以下となることが多い。 Become μm or less, an average particle size often becomes 10μm or less, especially greater atomizing method or a quenching roll method of solidification rate. Si相と共に析出する、Siを含有する金属間化合物は、1種類の場合もあるし、2種類以上になることもある。 Precipitated with Si phase, intermetallic compound containing Si may or may one type may also be a two or more. また、Si以外の元素の種類によっては、金属間化合物の代わりに、および/または金属間化合物と一緒に、 In addition, depending on the type of element other than Si, instead of the intermetallic compound, and / or with intermetallic compounds,
Siを含有する固溶体が生成することもある。 Sometimes solid solution containing Si is produced. いずれの場合も、通常は最も凝固温度の低い相が、微細な結晶粒から構成されるマトリックス相となり、その中にSi相粒が存在する。 In any case, usually low phases of most solidification temperature, it is composed of a matrix phase of fine crystal grains, Si phase grains are present therein.

【0063】急冷凝固により生成した合金を必要に応じて粉砕して、平均粒径が0.1 μm以上、50μm以下の合金粒子を得る。 [0063] In optionally milled alloys produced by rapid solidification, the average particle diameter of 0.1 [mu] m or more, to obtain the following alloy particles 50 [mu] m. 合金が粉末状で得られるアトマイズ法や回転電極法でも、必要または所望により、得られた合金粉末を粉砕してもよい。 Alloy in atomizing method or rotating electrode method obtained in powder form, if necessary or desired, an alloy powder obtained may be crushed. 粉砕はボールミル等の慣用手段により実施できる。 Milling can be carried out by conventional means such as a ball mill.

【0064】急冷凝固法を利用して製造した合金粒子は、急冷による歪みが残る場合がある。 [0064] alloy particles produced utilizing rapid solidification may distortion due quenching remains. 歪みがある材料は使用中に微粉化し、サイクル寿命が短くなる傾向がある。 Material is distorted finely divided during use, tends to cycle life is shortened. 従って、急冷歪みを取り除くために熱処理を行ってもよい。 Therefore, heat treatment may be performed to remove quenching distortion. 粉砕を行う場合には、熱処理は粉砕前と粉砕後のいずれの時点で行ってもよい。 When performing grinding, heat treatment may be performed at the time of or after milling and before grinding. 熱処理雰囲気は、熱処理中の負極材料の酸化を防止するため、真空または不活性ガス雰囲気といった非酸化性雰囲気中で行うことが好ましい。 The heat treatment atmosphere in order to prevent oxidation of the negative electrode material during the heat treatment is preferably performed in a non-oxidizing atmosphere such as vacuum or inert gas atmosphere.

【0065】熱処理温度は、包囲材を構成するSi含有金属間化合物または固溶体の固相線温度より10℃以上低い温度で行う。 [0065] The heat treatment temperature is carried out in solidus temperature than 10 ° C. or more lower temperature of the Si-containing intermetallic compounds or solid solutions constituting the surrounding material. なお、この包囲材を構成する相が、図4に示すように2以上ある場合には、量が多い主要なSi含有金属間化合物又は固溶体の相(主要な相は、組成や状態図から判定できる;図4の場合はNiSi 2相) の固相線温度より10℃以上低温とする。 Incidentally, the phase constituting the enclosing material, in some cases two or more as shown in FIG. 4, the amount is often key Si-containing intermetallic compound or solid solution phase (main phase, determined from the composition and state diagram it; in the case of FIG. 4, a low temperature 10 ° C. or higher than the solidus temperature of the NiSi 2 phase). 好ましい熱処理温度は、該固相線温度より20℃以上低温である。 A preferred thermal processing temperature is low 20 ° C. or higher than the solid phase line temperature.

【0066】この熱処理は、急冷歪みの解消に加えて、 [0066] This heat treatment, in addition to the elimination of quenching distortion,
拡散効果を生ずる。 It produces a diffusion effect. 本発明者らの観察では、図4に示した合金に熱処理を施した場合の各相の変化の状況は次の通りであった。 In the inventors' observations, the status of each phase change when subjected to heat treatment to an alloy shown in FIG. 4 were as follows.

【0067】熱処理の初期の段階では、(NiSi 2 +NiSi) [0067] In the early stages of the heat treatment, (NiSi 2 + NiSi)
相からなるマトリックス41中のNiSiが、粒状Si相40の周囲のNiSi 2相42からSiの供給を受けて、NiSi 2へ転換する。 NiSi in the matrix 41 made of phase, supplied with Si from NiSi 2 phase 42 surrounding the granular Si phase 40 is converted into NiSi 2. 一方、NiSi 2相42は、この供給により不足するSi On the other hand, NiSi 2 phase 42 lack this supply Si
を、隣接するSi相40から取り込む。 The captures of Si phase 40 adjacent. その結果、Si相40は収縮して平均粒径が小さくなる。 As a result, Si phase 40 the average particle diameter decreases to contract. (NiSi 2 +NiSi) 相41中のNiSiが全てNiSi 2に転換した後は、合金粒子はマトリックスのNiSi 2相と散在する粒状Si相40の2相からなる合金となる。 NiSi in (NiSi 2 + NiSi) phase 41 After the conversion of all the NiSi 2, the alloy particles are an alloy composed of two phases of granular Si phase 40 interspersed with NiSi 2 phase matrix. さらに熱処理を続けると、比較的粒径の大きなSi相は肥大し、比較的粒径の小さなSi相は消滅するオストワルド成長により、Si相の平均粒径は大きくなる。 Continuing to heat treatment, relatively having a large grain size Si phase is enlarged, by Ostwald growth disappears relatively particle size of small Si phase, the average particle diameter of the Si phase increases. 合金粒子の平均粒径には実質的な変化はない。 There is no substantial change in the average particle diameter of the alloy particles.

【0068】熱処理は、熱処理後のSi相粒40の平均粒径が40μmを超えないように設定した条件で行うことが好ましい。 [0068] heat treatment is preferably carried out under a condition with an average particle size of Si phase grains 40 after the heat treatment are set so as not exceed 40 [mu] m. 熱処理温度が前記固相線温度より10℃低い温度よりも高くなると、コアのSi相粒の粒径が大きくなりすぎることや、使用する熱処理炉の温度制御の精度によっては固相線を越えてしまって、粉末の焼結が起こり、後で粉砕が必要となるため、適当ではない。 If the heat treatment temperature is higher than the solidus temperature than 10 ° C. lower temperature, the particle size of the core of the Si phase grains becomes too large and, depending on the accuracy of the temperature control of the heat treatment furnace to be used beyond the solidus gone by, it occurs sintering of the powder, because it requires later pulverization, not suitable. 熱処理温度の下限は、急冷歪みがとれれば制限されないが、300 ℃以上が望ましく、500 ℃以上がさらに好ましい。 The lower limit of heat treatment temperature, rapid cooling distortion is not limited as Torere, desirably 300 ° C. or higher, more preferably at least 500 ° C.. 熱処理の時間は、合金粒子を構成する各元素の拡散速度を考慮すれば2時間以上、特に4時間以上とすることが望ましい。 Time of heat treatment is 2 hours or more in consideration of the diffusion rate of each element constituting the alloy particles, it is desirable that the particular 4 hours or more.

【0069】熱処理により、Si相粒の平均粒径が大きくなる一方で、合金中のSi相粒の重量比率が通常は低下する。 [0069] By heat treatment, while the average particle diameter of the Si phase grains is increased, the weight ratio of the Si phase grains in the alloy is usually reduced. これは前述したNiSiからNiSi 2への転換にSi相のSi This Si of the Si phase conversion of NiSi described above to NiSi 2
が消費されたためである。 There is because it was consumed. 負極活物質であるSi相の重量比率が小さくなるため、熱処理すると、充電・放電容量は低下する傾向がある。 Since the weight ratio of the Si phase which is the negative electrode active material is reduced, the heat treatment, the charge-discharge capacity tends to decrease.

【0070】急冷凝固法により本発明の負極材料を製造した場合、アトマイズ法や急冷ロール法といった凝固速度が高い方法では、急冷によりSiが微細に分散した組織になるので、多少の歪みが残存していても、熱処理なしでサイクル寿命が良好な負極材料が得られることが判明した。 [0070] When the negative electrode material of the present invention were prepared by rapid solidification, the atomizing method or a quenching roll method such solidification rate is high way, since Si by rapid cooling is finely dispersed tissue, it remains a little distortion even if the negative electrode material cycle life is good without the heat treatment could be obtained was found. 従って、時間のかかる熱処理工程を省略した生産性の高い方法により、容量が著しく高く、サイクル寿命も良好な負極材料を製造することができる。 Thus, the method highly productive omitting time-consuming heat treatment process, the capacity is significantly higher, the cycle life can be produced satisfactory anode materials.

【0071】(製造方法2)Si金属又はSi相を含む合金からなる粉末 (以下、Si相粉末という) の表面に、Siと固溶体又は金属間化合物を構成する元素を含む材料の付着層を形成し、次いで、前記固溶体又は金属間化合物の固相線温度より10℃以上低い温度で熱処理を行う。 [0071] (Manufacturing method 2) consisting of Si metal or an alloy containing Si phase powder (hereinafter, referred to as Si phase powder) on the surface of the deposition layer of a material containing an element constituting the Si solid solution or intermetallic compounds formed and, then, subjected to heat treatment in the solid solution or solidus temperature than 10 ° C. or more lower temperature of the intermetallic compound. 即ち、 In other words,
予めコアのSi相粒を作製し、その周囲に包囲材を付着と熱拡散を利用し、後から形成する方法である。 Previously prepared cores Si phase grains, utilizing the adhesion and thermal diffusion of surrounding material around a process for forming later.

【0072】この第2の方法では、熱処理により、Si相粉末中のSiが付着層に拡散して、付着層の材料がSi含有固溶体又は金属間化合物に変化し、コアのSi相粒がSi含有固溶体又は金属間化合物で少なくとも部分的に包囲された合金粒子が生成する。 [0072] In the second method, by heat treatment, to diffuse into the Si adhesion layer of the Si phase in the powder, the material of the adhesion layer changes the Si-containing solid solution or intermetallic compound, the core of the Si phase grains Si containing solid solution, or at least partially enclosed alloy particles intermetallic compound is produced. このような粒子も、本発明ん「合金」粒子に含まれる。 Such particles also, N the present invention are also included in the "alloy" particles. 粉末がSi金属からなる場合には、各合金粒子は通常は単一のSi相粒を含むことが多い。 If the powder consists of Si metal, each alloy particles are usually often include a single Si phase grains.

【0073】Si相粉末は、Si金属の粉末でもよいが、Si [0073] Si phase powder may be a powder of Si metal but, Si
相が析出していればSi合金の粉末であってもよい。 Phases may be a powder of a Si alloy if precipitated. このような合金の例としては、これに限られないが、Ni−Si Examples of such alloys include, but are not limited to, Ni-Si
合金が例示される。 Alloys are exemplified.

【0074】Si相粉末の形状は、鋭い角がない形状が好ましく、さらに長軸径/短軸径の比が3以下の球形状であることが好ましい。 [0074] The shape of the Si phase powder shape without sharp corners are preferred, preferably further a ratio of the major axis diameter / minor axis is 3 or less spherical. 鋭い角があると、前記付着層が均一になりにくい。 If there is a sharp corner, the adhesion layer is not easily made uniform. 球形状であると、微粉化しにくいし、 If it is spherical, to hardly pulverized,
付着層の厚さが均一になりやすい点でも有利である。 In terms prone to thickness of the deposited layer is uniform also advantageous. Si Si
相粉末は、機械的粉砕法で製造してもよいが、ロール急冷法、アトマイズ法又は回転電極法で製造することが有利である。 Phase powder may be produced by mechanical grinding method, but a roll quenching method, it is advantageous to manufacture by atomizing method or rotating electrode method. 中でも、ほぼ球形の粉末が得られるガスアトマイズ法又は回転電極法が好ましい。 Of these, approximately gas atomizing method or rotating electrode method spherical powder is obtained is preferred.

【0075】Si相粉末は、何れの方法で製造した場合でも、平均粒径が40μm以下であることが好ましい。 [0075] Si phase powder, even if produced by any method, it is preferable that the average particle diameter of 40μm or less. 平均粒径が40μmを超えると、コアのSi相粒が大きくなり、 When the average particle diameter exceeds 40 [mu] m, Si phase grains of the core is increased,
周囲に形成する金属間化合物の拘束が効きにくくなり、 Constraint of the intermetallic compound formed around is less likely effectiveness,
Liを吸蔵・放出する際に発生する微粉化を防止することができにくくなる。 Hardly it is possible to prevent the pulverized for generating Li when it absorbs and releases.

【0076】Si相粉末は、単一粒子からなる必要はなく、複数の粒子が例えば焼結により結合したような複合粒子であってもよい。 [0076] Si phase powder need not consist of a single particle, or may be composite particles, such as binding a plurality of particles, for example by sintering. 粉末の粒径が10μm以下であるような微粉末の場合、そのまま表面に前記付着層を形成すると、粉末の量に対して付着層の元素の占める割合が多くなり好ましくない。 When the particle size of the powder is fine powder such that 10μm or less, as it is to form the adhesive layer on the surface, the rate is often undesirably occupied by the elements of the deposition layer with respect to the amount of powder. そのような場合、微粉末を部分的に焼結して複合粒子化することで付着層の元素の付着粉末の割合を低くすることができる。 In such a case, it is possible to lower the percentage of adhering powder elements of the deposited layer by composite particles of partially sintering the fine powder. 複合粒子の場合は、 In the case of composite particles,
複合粒子の平均粒径が40μm以下であることが好ましい。 It is preferable that the average particle diameter of the composite particles is 40μm or less.

【0077】Si相粉末の表面に、Siと金属間化合物又は固溶体を形成することができる1種または2種以上の元素 (以下、第2の元素という) を含む材料の相を付着させる。 [0077] the surface of the Si phase powder, one or more elements capable of forming a Si intermetallic compound or solid solution (hereinafter referred to as a second element) depositing a phase materials including. この付着層は、第2の元素以外にSiを含有していてもよく、またSiと金属間化合物又は固溶体を形成しない他の元素も少量であれば含有しうる。 The adhesion layer may contain, if may also contain Si in addition to the second element, also other elements that do not form Si intermetallic compound or solid solution is also small. 第2の元素の付着の方法は、メッキといった化学的方法、並びにメカニカルアロイング法 (MA法) といった物理的方法の何れも可能である。 The method of attachment of the second element, chemical methods such as plating, as well as all are possible physical methods such as mechanical alloying method (MA method).

【0078】第2の元素からなる付着層の厚さは0.05〜 [0078] The thickness of the deposited layer of a second element 0.05
10μm程度が望ましい。 About 10μm is desirable. 0.05μm未満の場合は、付着層から形成される包囲材 (Si含有金属間化合物又は固溶体) の厚みが小さくなり、Liを吸蔵・放出する際の体積変化に対する拘束が効きにくくなり、電極のサイクル寿命が低下する。 When it is less than 0.05 .mu.m, the thickness of the envelope material formed from deposited layer (Si-containing intermetallic compound or solid solution) is reduced, it becomes difficult effectiveness restraint of Li to volume change at the time of occlusion and release, of the electrode cycle life is reduced. 付着層の厚みが10μmを越えると、負極活物質であるSi相粒の量が相対的に少なくなり、電極の容量が小さくなる。 When the thickness of the deposited layer exceeds 10 [mu] m, the amount of Si phase grains as the negative electrode active material is relatively reduced, the capacity of the electrode is reduced.

【0079】付着層の形成法のうち、メッキ法では、電解メッキ法を用いることも可能であるが、粉末全体に通電することは煩雑な手順を用するので、無電解メッキ法が適している。 [0079] Of the method for forming the adhesion layer, the plating method, it is possible to use an electrolytic plating method, so energizing the entire powder to use a complicated procedure, the electroless plating method is suitable . 無電解メッキ法を用いることができる第2の元素としては、Ni、Co、Pd、Cu、Ag、Au、Pt、Pb、 The second element may be used electroless plating, Ni, Co, Pd, Cu, Ag, Au, Pt, Pb,
Rh、およびRuが挙げられる。 Rh, and Ru, and the like. Si相粉末の表面が酸化膜等で覆われメッキしにくい場合は、適宜酸洗等により酸化膜を除去した後、無電解メッキを施せばよい。 If the surface of the Si phase powder is not easily plated covered with an oxide film or the like, after removing the oxide film by appropriate pickling or the like, may be subjected to electroless plating. また、P In addition, P
d、Sn等のメッキ助剤を用いることも無電解メッキの付着性を向上させるので有効である。 d, since it improves the adhesion of electroless plating using a plating aid such as Sn it is effective.

【0080】付着層を構成する第2の元素がメッキしにくい元素である場合は、MA法によって第2の元素をSi相粉末に付着させることができる。 [0080] When the second element that constitutes the adhesion layer is a plated hard elements can be deposited second element Si phase powder by MA method. MA法は、Si相粉末と第2の元素の粉末 (Si相粉末と同様の方法で作製できる) MA method (can be made of Si phase powder and similar methods) Si phase powder and a second element of the powder
を遊星ボールミルや攪拌型ミル等の高エネルギーミルに一緒に投入して混合する方法で、Si相粉末の表面部に第2の元素の粉末が付着して得られる。 With method of mixing was put together in a high energy mill such as a planetary ball mill or a stirred mill, the powder of the second element is obtained by adhering to the surface portion of the Si phase powder.

【0081】MA法に用いる第2の元素の粉末の平均粒径は、Si相粉末の平均粒径より小さく、かつ10μm以下であることが望ましい。 [0081] The average particle size of the powder of the second element used in the MA process is smaller than the average particle diameter of the Si phase powder, and is desirably 10μm or less. 10μmを越えると、Si相粉末の表面に付着した第2の元素の層の厚さが10μmを越える可能性があり、Si層の量に対する第2の元素の量の割合が増加して好ましくない。 Exceeds 10 [mu] m, the thickness of the second element of the layer adhering to the surface of the Si phase powder may exceed 10 [mu] m, unfavorable ratio of the amount of the second element relative to the amount of Si layer is increased . 第2の元素の粉末の平均粒径の下限は特に限定されないが、粉末の酸化等の汚染を考慮すると、平均粒径が1μm以上であることが好ましい。 The lower limit of the average particle size of the powder of the second element is not particularly limited, considering the contamination such as oxidation of the powder preferably has an average particle diameter of 1μm or more.
Si相粉末の量に対して第2の元素の粉末の付着量は10〜 Relative to the amount of the Si phase powder deposition amount of the powder of the second element 10
30%程度が好ましい。 About 30% is preferred.

【0082】MA法により付着層を形成する場合、第2の元素の粉末に、少量 (例、第2の元素の粉末の 0.1〜5 [0082] When forming the adhesion layer by MA method, the powder of the second element, a small amount (e.g., 0.1 to 5 of the powder of the second element
重量%、好ましくは 0.5〜2重量%) のセラミック粉末を混合してもよい。 Wt%, preferably it may be mixed ceramic powder 0.5-2% by weight). セラミック粉末は、例えば、SiC 、 Ceramic powder, for example, SiC,
Si 3 N 4 、TiC 、TiB 2 、Al 2 O 3等の1種もしくは2種以上のセラミックの粉末を使用することができる。 Si 3 N 4, TiC, may be used one or two or more ceramic powders such as TiB 2, Al 2 O 3. セラミック粉末は、平均粒径が第2の元素の粉末より小さいものが好ましい。 Ceramic powder, an average particle diameter smaller than the powder of the second element is preferred. こうしてセラミックが微細に分散した包囲材を形成すると、包囲材の拘束効果が強まり、サイクル寿命が一層向上することがある。 Thus the ceramic to form a surrounding material dispersed finely, intensified restraining effect of surrounding material, cycle life may be further improved.

【0083】付着層の形成方法としては、他に、第2の元素の粉末を、後工程の熱処理で除去できるバインダー、例えば有機バインダー等で塗料化し、Si相粉末に塗布する方法、第2の元素の溶融物をSi相粉末に溶射する方法なども採用できる。 [0083] As a method for forming the adhesion layer, the other, the powder of the second element, the binder can be removed by heat treatment in a later step, and paint, for example, an organic binder or the like, a method of coating the Si phase powder, the second the melt of the elements can be adopted a method of spraying the Si phase powder.

【0084】上述したような適当な方法でSi相粉末の表面に第2の元素の付着層を形成した後、熱処理を施す。 [0084] After forming the adhesion layer of the second element on the surface of the Si phase powder with a suitable method as described above, subjected to a heat treatment.
この熱処理で生ずる拡散現象により、付着層にSi相粉末中のSiが拡散して、Siが付着層の元素と化合するか、付着層中に固溶する。 The diffusion phenomenon occurring during the heat treatment, Si of the Si phase powder adhesion layer is diffused, or Si is combined with elements of the deposited layer, a solid solution to adhere layer. その結果、付着層は、Si含有固溶体又は金属間化合物の層に変化するので、Si相粒の表面が As a result, adhesion layer, since changes in the layer of Si-containing solid solution or intermetallic compounds, the surface of the Si phase grains
Si含有固溶体又は金属間化合物の層で包囲された、本発明の合金粒子が得られる。 Si surrounded by a layer containing a solid solution or intermetallic compound, alloy particles of the present invention is obtained.

【0085】例えば、Si相粉末の表面にNiの無電解メッキを施してNi付着層を形成し、次いで熱処理を施すと、 [0085] For example, by performing electroless plating of Ni to form a Ni deposited layer on the surface of the Si phase powder, and then the heat treatment,
Ni付着層にSiが拡散し、Niと化合してNiSi 2の金属間化合物に変化する。 Si is diffused in the Ni deposition layer, combine with Ni changes to intermetallic compounds NiSi 2. その結果、Si相粒の周囲が包囲材となるNiSi 2相で包囲された合金粒子になる。 As a result, the alloy particles surrounding Si phase grains were surrounded by NiSi 2 phase as the surrounding material.

【0086】この拡散のための熱処理の温度は、拡散により生成する主要な固溶体又は金属間化合物の固相線温度より低ければよいが、熱処理による粉末同士の焼結を防ぐという観点からは、固相線温度より10℃以上低い温度が好ましい。 [0086] The temperature of the heat treatment for the diffusion, if it is lower than the solidus temperature of the primary solid solution or intermetallic compound is produced by diffusion, from the viewpoint of preventing the sintering of the powder particles by the heat treatment, the solid phase line temperature from 10 ° C. or higher lower temperatures are preferred. 熱処理温度の下限は、Si元素と付着層の元素の拡散を早めるということに配慮して500 ℃以上であることが好ましい。 The lower limit of the heat treatment temperature is preferably in consideration of the fact that hasten the diffusion of elements of the deposited layer and the Si element is 500 ° C. or higher. 熱処理時間は、拡散が十分に起こればよく、通常は2時間以上、好ましくは4時間以上である。 The heat treatment time, diffusion may be happen enough, usually 2 hours or more, preferably 4 hours or more. 熱処理雰囲気は、真空や不活性ガス雰囲気のような非酸化性雰囲気が好ましい。 The heat treatment atmosphere is non-oxidizing atmosphere such as vacuum or inert gas atmosphere is preferable.

【0087】Si相粉末を前記急冷凝固をさせて製造した場合に生ずる急冷歪みや、付着層の元素をSi相粉末に付着させる方法としてMA法を用いた場合に生ずる歪みは、 [0087] quenching distortion occurring or in the case of the Si phase powder produced by the rapid solidification, the strain caused when the elements of the adhesive layer using the MA method as a method of attaching to Si phase powder,
この熱処理によって除去されるので、別に歪み取り用の熱処理を施す必要はない。 Since it is removed by the heat treatment, it is not necessary to heat treatment for a separate strain relief.

【0088】 負極の製造 (製造方法A)本発明に係るSi相粒をSi含有固溶体又は金属間化合物の相で包囲した合金粒子からなる負極材料から、当業者には周知の電極の製造方法に従って、非水電解質二次電池用負極を製造することができる。 [0088] from the negative electrode material consisting of a negative electrode of the production (manufacturing method A) alloy particles of Si phase grains according to the present invention is surrounded by a phase of Si-containing solid solution or intermetallic compounds, according to the manufacturing method of the known electrode to those skilled in the art , it is possible to manufacture a negative electrode for a nonaqueous electrolyte secondary battery.

【0089】例えば、上記の第1または第2の方法に従って製造した本発明の負極材料の粉末に、適当な結着剤を混合し、必要に応じて導電性向上のために適当な導電粉を混合する。 [0089] For example, the powder of the negative electrode material of the present invention prepared in accordance with the first or second method described above, mixing a suitable binder, a suitable electrically conductive powder in order to improve conductivity as required mixed. この混合物に、結着剤を溶解する溶媒を加え、必要であればホモジナイザー、ガラスビーズを用いて充分に攪拌してスラリー状にする。 To this mixture, a solvent is added for dissolving the binder, sufficient to form a slurry and stirred with a homogenizer, glass beads if necessary. このスラリーを圧延銅箔、銅電析銅箔などの電極基板 (集電体) に、ドクターブレード等を用いて塗布し、乾燥した後、ロール圧延等で圧密化させることで非水電解質二次電池用負極を製造することができる。 Rolled copper foil The slurry, on the electrode substrate such as a copper conductive 析銅 foil (collector), was applied using a doctor blade or the like, dried, non-aqueous electrolyte secondary by causing compacted rolling etc. it is possible to manufacture a negative electrode for a battery.

【0090】結着剤としては、PVDF(ポリフッ化ビニリデン)、PMMA(ポリメチルメタクリレート)、PTFE(ポリテトラフルオロエチレン)、スチレン−ブタジエン系ゴム等の非水溶性の樹脂 (但し、電池の非水電解質に使用する溶媒に不溶性のもの)、並びにCMC(カルボキシメチルセルロース) 、PVA(ポリビニルアルコール) 等の水溶性樹脂が例示される。 [0090] As the binder, PVDF (polyvinylidene fluoride), PMMA (polymethyl methacrylate), PTFE (polytetrafluoroethylene), styrene - water-insoluble resin such as butadiene rubber (provided that the non-aqueous battery those insoluble) in the solvent used in the electrolyte, as well as CMC (carboxymethylcellulose), water-soluble resin such as PVA (polyvinyl alcohol) are exemplified. 溶媒としては、結着剤に応じて、NMP (N−メチルピロリドン) 、DMF(ジメチルホルムアミド) 等の有機溶媒、または水を使用する。 As the solvent, depending on the binder, NMP (N-methylpyrrolidone), using an organic solvent or water, such as DMF (dimethylformamide).

【0091】導電粉としては、炭素材料 (例、カーボンブラック、黒鉛) および金属(例、Ni)のいずれも使用できるが、好ましいのは炭素材料である。 [0091] As the conductive powder, carbon materials (e.g., carbon black, graphite) and metal (e.g., Ni) is either can be used in, preferred is a carbon material. 炭素材料は、 The carbon material,
その層間にLiイオンを吸蔵することができるので、導電性に加えて、負極の容量にも寄与することができ、また保液性にも富んでいる。 It is possible to occlude Li ion between the layers, is added to the conductive, it can also contribute to the capacity of the negative electrode, also rich in liquid retention. 好ましい炭素材料はアセチレンブラックである。 Preferred carbon material is acetylene black.

【0092】負極に炭素材料を配合する場合、本発明に係る合金粒子からなる負極材料に対して5wt%以上、80 [0092] When blending a carbon material for the negative electrode, 5 wt% or more with respect to the negative electrode material consisting of alloy particles according to the present invention, 80
wt%以下の量で炭素材料を使用することが好ましい。 It is preferable to use a carbon material in an amount of less wt%. この量が5wt%未満では十分な導電性を付与することができず、80wt%を超えると負極の容量が低下する。 This amount can not be imparted sufficient conductivity is less than 5 wt%, the capacity of the negative electrode decreases when exceeding 80 wt%. より好ましい配合量は20wt%以上、50wt%以下である。 More preferably the amount is 20 wt% or more, or less 50 wt%.

【0093】なお、この方法の変形として、上記の製造方法2に従ってSi相粉末に付着層を形成した後、熱処理を行う前の粉末を用いて、上記のようにスラリー化し、 [0093] As a modification of this method, after forming the adhesive layer on the Si phase powder according to the above manufacturing method 2, using a powder prior to the heat treatment, was slurried as described above,
電極基板に塗布してもよい。 It may be applied to the electrode substrate. その場合には、乾燥工程に代えて、或いは最後のロール圧延後に、熱処理を行って、付着層にSiを拡散させ、Si含有固溶体又は金属間化合物の相からなる包囲材を形成する。 In that case, instead of the drying step, or after the final rolling, heat treatment is performed, adhesion layer is diffused Si, to form a surrounding material of phase of Si-containing solid solution or intermetallic compound. 即ち、製造方法2 In other words, the production method 2
における熱処理工程は切り離して、負極製造時に行うこともできる。 Heat treatment step in isolation in can also be performed at the time of manufacturing the negative electrode.

【0094】(製造方法B)本発明に係る非水電解質二次電池用負極の別の製造方法では、Si相粉末を、付着層の形成や熱処理を施さないまま、上記のように電極の製造工程に付し、その後で第2の元素 (Siと金属間化合物又は固溶体を形成することができる1種または2種以上の元素) による付着層の形成と熱処理を行う。 [0094] In (Preparation Method B) Another method for producing a non-aqueous electrolyte secondary battery negative electrode according to the present invention, the Si phase powder, without subjected to formation and heat treatment of the deposited layer, the production of electrodes as described above subjected to step, the subsequent heat treatment and formation of the adhesive layer by the second element (at least one element capable of forming a Si intermetallic compound or solid solution).

【0095】即ち、この方法では、Si相粉末を、上記と同様に、結着剤や必要により導電粉(例、炭素材料) と混合し、スラリー化して電極基板に塗布し、乾燥し、必要に応じてロール圧延等で圧密化して、電極基板の表面にSi相粉末の層を形成する。 [0095] That is, in this method, the Si phase powder, in the same manner as described above, the conductive powder if necessary and binder (e.g., carbon material) is mixed with, coated on the electrode substrate was slurried, dried, requires and compacted rolling or the like according to, to form a layer of the Si phase powder to the surface of the electrode substrate. その後、Si相粉末層に第2 Then, the second to the Si phase powder layer
の元素を含む材料の層を付着させる。 Depositing a layer of material comprising the elements. この場合、付着層の形成は、MA法が適用できないので、メッキ法が適している。 In this case, the formation of the adhesion layer, since MA method can not be applied, a plating method is suitable. メッキ法は、無電解メッキ法は勿論のこと、Si相粉末同士が既に導通しているので電解メッキ法も可能である。 Plating method, electroless plating method, of course, also possible electrolytic plating because Si phase powder particles already conducting. メッキされた第2の元素は、Si相粉末層の表面だけでなくSi相粉末の隙間に入り込み、Si相粉末の表面を部分的に包囲する。 Second element is plated, it enters the gap between the Si phase powder not only on the surface of the Si phase powder layer, partially surrounding the surface of the Si phase powder.

【0096】メッキ後に熱処理を行うと、メッキにより形成された付着層にSi相粉末中のSiが拡散して、付着層はSi含有固溶体又は金属間化合物の相に変化し、Si相粒がSi含有固溶体又は金属間化合物の相で部分的に包囲された合金粒子からなる、本発明に係る負極材料を備えた負極が得られる。 [0096] When performing the heat treatment after plating, and Si in the Si phase powder deposition layer formed by plating are diffused, adhesion layer changes the phase of the Si-containing solid solution or intermetallic compound, Si phase grains Si consists partially enclosed alloy particles in phase containing a solid solution or intermetallic compound, a negative electrode is obtained with the anode material according to the present invention. 熱処理条件は、負極材料の製造方法2 The heat treatment conditions, the production of negative electrode material Method 2
(第2の元素の付着層を形成する方法) で説明した条件と同様でよい。 It may be the same as the conditions described in (a method of forming a deposition layer of the second element).

【0097】Si相粉末層の厚さは40μm以下が好ましい。 [0097] The thickness of the Si phase powder layer is preferably 40μm or less. 40μmを越えると、Liを吸蔵・放出する際のSi相粒の体積変化による微粉化を防止できなくなることがある。 Exceeds 40 [mu] m, it may be impossible to prevent the pulverization due to volume change in the Si phase grains at the time of occlusion and release of Li. 付着層の厚さは0.05μm以上、10μm以下が好ましい。 The thickness of the deposited layer is 0.05μm or more, preferably not more than 10 [mu] m. 0.1 μm未満ではSi相粒を拘束する効果が小さく、 Small the effect of restraining the Si phase grains is less than 0.1 [mu] m,
また10μmを越えると、Si相の量が相対的に少なくなってLiを吸蔵・放出する容量が少なくなる。 Also if it exceeds 10 [mu] m, capacity of absorbing and releasing Li is the amount of the Si phase is relatively small decreases. Si相粉末層が1層のみでは、電極の厚さが少なく、負極の容量が不足する場合は、Si相粉末層及び付着層の元素をそれぞれ交互に塗布及びメッキした後で、熱処理を施して、多層構造をとるようにすることも可能である。 Si phase powder layer is only one layer, less the thickness of the electrode, if the capacity of the negative electrode is insufficient, the elements of Si phase powder layer and adhesion layer after coating and plating alternately respectively, by heat treatment it is also possible to adopt a multi-layer structure.

【0098】電極基板上にSi相粉末を塗布してから付着層を形成し、熱処理を施す、製造方法Bに従って負極を製造すると、付着層の元素の量が少なくて済み、また通常の電極製造ラインで付着処理を行うことが可能になり、コスト低減、設備投資の抑制、生産性の向上に効果がある。 [0098] by applying Si phase powder to form a deposited layer from the electrode substrate is subjected to a heat treatment, when a negative electrode according to the production method B, submitted requires less amount of the element deposited layer, also conventional electrode manufacturing it is possible to perform the deposition process in line, cost reduction, suppression of capital investment, it is effective in improving the productivity.

【0099】 非水電解質二次電池上記のようにして製造された負極を用いて、非水電解質二次電池を作製する。 [0099] Nonaqueous using a negative electrode prepared electrolyte secondary battery as described above, to produce a non-aqueous electrolyte secondary battery. 非水電解質二次電池の代表例はリチウムイオン二次電池であり、本発明に係る負極材料および負極は、リチウムイオン二次電池の負極材料および負極として好適である。 Representative examples of non-aqueous electrolyte secondary battery is a lithium ion secondary battery, the negative electrode material and the negative electrode according to the present invention is suitable as a negative electrode material and the negative electrode of the lithium ion secondary battery. 但し、理論的には、他の非水電解質二次電池にも適用できる。 However, in theory, be applied to other non-aqueous electrolyte secondary battery.

【0100】非水電解質二次電池は、基本構造として、 [0100] non-aqueous electrolyte secondary battery, as a basic structure,
負極、正極、セパレーター、非水系の電解質を含んでいる。 Anode comprises a positive electrode, a separator, an electrolyte of the non-aqueous. 負極は上記のように本発明に従って製造したものを使用するが、他の正極、セパレーター、電解質は、従来より公知のもの、或いは今後開発される材料を適当に使用すればよい。 Anode is used which has been prepared in accordance with the present invention as described above, other positive electrode, the separator, the electrolyte, those conventionally known, or can be suitably employed the materials to be developed in the future.

【0101】リチウムイオン二次電池の正極は、Li含有遷移金属化合物を活物質とするものが好ましい。 [0102] The positive electrode of the lithium ion secondary battery, which the Li-containing transition metal compound as an active material is preferable. Li含有遷移金属化合物の例は、LiM 1-X M' X O 2または LiM 2y M' y Examples of the Li-containing transition metal compound, LiM 1-X M 'X O 2 or LiM 2y M' y
O 4 (式中、0≦X, Y≦1、M とM'はそれぞれBa、Co、N O 4 (where, 0 ≦ X, Y ≦ 1 , M and M 'respectively Ba, Co, N
i、Mn、Cr、Ti、V、Fe、Zn、Al、In、Sn、Sc、Yの少なくとも1種) で示される化合物である。 i, is a compound represented Mn, Cr, Ti, V, Fe, Zn, Al, In, Sn, Sc, at least one) of Y. 但し、遷移金属カルコゲン化物;バナジウム酸化物およびそのLi化合物;ニオブ酸化物およびそのLi化合物;有機導電性物質を用いた共役系ポリマー;シェブレル相化合物;活性炭、活性炭素繊維等といった他の正極材料を用いることもできる。 However, the transition metal chalcogenide; vanadium oxide and its Li compound; niobium oxides and their Li compound; Chevrel phase compounds; conjugated polymer using an organic conductive material activated carbon, the other positive electrode materials such as activated carbon fiber It can also be used.

【0102】正極も、上述した負極材料の製造方法Aと同様に、粉末状の正極材料を結着剤や必要に応じて導電剤と一緒にスラリー化し、電極基板に塗布し、圧密化するという方法で製造できる。 [0102] The positive electrode, like the production method A of negative electrode materials described above, was slurried with conductive agent in accordance with powdered cathode material required and a binder, it is applied to the electrode substrate, that compaction It can be produced by the method. 正極材料の平均粒径は1〜 The average particle diameter of the positive electrode material 1
30μmの範囲内が好ましい。 Preferably in the range of 30μm. 正極用の結着剤としてはPV As the binder for the positive electrode PV
DFおよびPTFEが好ましく、導電剤は炭素材料が好ましい。 DF and PTFE are preferred, the conductive agent is preferably carbon material.

【0103】リチウムイオン二次電池の電解質は、一般に支持電解質となるリチウム塩を有機溶媒に溶解させた非水系電解質である。 [0103] The electrolyte of a lithium ion secondary battery is a nonaqueous electrolyte generally lithium salt as a supporting electrolyte dissolved in an organic solvent. リチウム塩としては、例えば、Li Examples of the lithium salt, for example, Li
ClO 4 , LiBF 4 , LiAlCl 4 , LiPF 6 , LiAsF 6 , LiSbF 6 , LiB(C ClO 4, LiBF 4, LiAlCl 4 , LiPF 6, LiAsF 6, LiSbF 6, LiB (C
6 H 5 ), LiCF 3 SO 3 , LiCH 3 SO 3 ,Li(CF 3 SO 2 ) 2 N, LiC 4 F 9 SO 3 , 6 H 5), LiCF 3 SO 3, LiCH 3 SO 3, Li (CF 3 SO 2) 2 N, LiC 4 F 9 SO 3,
Li(CF 2 SO 2 ) 2 , LiCl, LiBr, LiI, LiSCN, 低級脂肪族カルボン酸リチウム、クロロボランリチウム、四フェニルホウ酸リチウム等が例示され、1種もしくは2種以上を使用することができる。 Li (CF 2 SO 2) 2 , LiCl, LiBr, LiI, LiSCN, lithium lower aliphatic carboxylic acids, chloroborane lithium, four lithium phenylboronic acid and the like are exemplified, can be used singly or in combination.

【0104】有機溶媒としては、エチレンカーボネート、プロピレンカーボネート、ビニレンカーボネート等の環状炭酸エステル類とエチルメチルカーボネート、ジメチルカーボネート、ジエチルカーボネートなどの鎖状炭酸エステル類とを包含する炭酸エステル類;ギ酸メチル、酢酸エチル、プロピオン酸メチルなどの脂肪族カルボン酸エステル類;γ−ブチロラクトン等のγ−ラクトン類;1,2-ジメトキシエタン等の鎖状エーテル類;テトラヒドロフラン等の環状エーテル類;その他ジメチルスルホキシド、ジオキソラン類、アミド類、ニトリル類、 [0104] As the organic solvent, ethylene carbonate, propylene carbonate, cyclic carbonates such as vinylene carbonate and ethyl methyl carbonate, dimethyl carbonate, chain carbonate esters and carbonic acid esters include, such as diethyl carbonate; methyl formate, γ- lactones such as γ- butyrolactone; ethyl acetate, aliphatic carboxylic acid esters such as methyl propionate 1,2 chain ethers dimethoxyethane and the like; cyclic ethers such as tetrahydrofuran; other dimethyl sulfoxide, dioxolane kind, amides, nitriles,
スルホラン類等の各種の非プロトン性溶媒の1種もしくは2種以上を使用できる。 One or two or more kinds of various aprotic solvents sulfolane and the like can be used. 好ましい溶媒は炭酸エステルとの混合系、およびこれにさらに脂肪族カルボン酸エステルを混合した系である。 The preferred solvent is a mixed system, and further a system obtained by mixing an aliphatic carboxylic acid ester to the carbonic ester. 中でもエチレンカーボネートとエチルメチルカーボネートとの混合溶媒が好ましい。 Among these mixed solvent of ethylene carbonate and ethyl methyl carbonate are preferable.

【0105】溶媒中の支持電解質の濃度は特に制限されないが、通常は 0.2〜2Mの範囲、特に 0.5〜1.5 Mの範囲が好ましい。 [0105] The concentration of the supporting electrolyte in the solvent is not particularly limited, but usually in the range of 0.2~2M, in the range of particularly 0.5 to 1.5 M preferred.

【0106】非水電解質は、液体 (溶液) ではなく、固体であってもよい。 [0106] The non-aqueous electrolyte, rather than liquid (solution) may be a solid. 非水電解質二次電池用の固体電解質は、無機固体電解質と有機固体電解質とに大別される。 The solid electrolyte for a non-aqueous electrolyte secondary batteries are roughly divided into inorganic solid electrolytes and organic solid electrolytes.
無機固体電解質には、Liの窒化物、ハロゲン化物、酸素酸塩などが知られている。 The inorganic solid electrolyte, nitrides of Li, halides, oxygen acid salts are known. 中でも、Li 4 SiO 4 , Li 4 SiO 4 -L Among them, Li 4 SiO 4, Li 4 SiO 4 -L
iI-LiOH, xLi 3 PO 4 - (1-x) Li 4 SiO 4, Li 2 SiS 3 , Li 3 PO 4 -Li 2 iI-LiOH, xLi 3 PO 4 - (1-x) Li 4 SiO 4, Li 2 SiS 3, Li 3 PO 4 -Li 2
S-SiS 2 , 硫化リン化合物等が有効である。 S-SiS 2, it is effective and the like phosphorus sulfide compound. 有機固体電解質としては、例えば、ポリエチレンオキサイド、ポリプロピレンオキサイド、ポリホスファゼン、ポリアジリジン、ポリエチレンスルフィド、ポリビニルアルコール、 As the organic solid electrolyte, for example, polyethylene oxide, polypropylene oxide, polyphosphazene, polyaziridine, polyethylene sulfide, polyvinyl alcohol,
ポリフッ化ビニリデン、ポリヘキサフルオロプロピレン等や、これらの誘導体、混合物、複合体等のポリマー材料が有効である。 Polyvinylidene fluoride, or poly hexafluoropropylene, derivatives thereof, mixtures are effective polymeric materials such as composites.

【0107】非水電解質には、充放電特性を改善する目的で、他の化合物を添加することができる。 [0107] The non-aqueous electrolyte, for the purpose of improving the charge-discharge characteristics, it is possible to add other compounds. かかる化合物として、トリエチルホスファイト、トリエタノールアミン、環状エーテル、エチレンジアミン、n-グライム、 As such compounds, triethyl phosphite, triethanolamine, cyclic ether, ethylenediamine, n- glyme,
ピリジン、ヘキサリン酸トリアミド、ニトロベンゼン誘導体、クラウンエーテル類、第四級アンモニウム塩、エチレングリコールジアルキルエーテル等が例示される。 Pyridine, triamide hexaphosphate, nitrobenzene derivatives, crown ethers, quaternary ammonium salts, ethylene glycol dialkyl ether, and the like.

【0108】セパレータは、正極と負極とを電気的に絶縁する絶縁膜としての役割を果たす他、非水電解質の保持にも寄与する。 [0108] The separator serves other positive and negative electrodes as electrically insulating dielectric film, also contributes to retention of the nonaqueous electrolyte. セパレータとしては、大きなイオン透過度と適度の機械的強度を持ち、絶縁性の微多孔質薄膜が用いられる。 The separator having high ion permeability and moderate mechanical strength, microporous films of insulating is used. 電池の安全性を高めるため、一定温度以上になると細孔が閉塞して、抵抗を増大させる機能を持つものが好ましい。 To increase the safety of the battery, and the pores are closed becomes more than a certain temperature, it is preferable to have the function of increasing the resistance.

【0109】耐有機溶剤性と疎水性を考慮して、セパレータにはポリオレフィン系ポリマーまたはガラス繊維から作られた微多孔質シート、不織布、織布等を用いることが多い。 [0109] In view of organic solvent resistance and hydrophobicity, microporous sheet separator made of polyolefin polymers or glass fibers, nonwoven fabric, are often used fabric or the like. セパレータの細孔径は、電極から離脱した材料が透過しないように0.01〜1μm程度が好ましい。 Pore ​​size of the separator is about 0.01~1μm as detached material is not transmitted from the electrode is preferred. セパレータの厚みは一般には10〜300 μm程度である。 The thickness of the separator is generally of the order of 10 to 300 [mu] m. その空孔率は通常は30〜80%の範囲が好ましい。 Its porosity is usually preferably in the range of 30% to 80%.

【0110】リチウム二次電池の1種として、非水電解質溶液を吸収・保持させたポリマー材料を正極と負極に含ませ、セパレータのポリマーにも同様の非水電解質溶液を吸収・保持させて、電池を構成したものがある。 [0110] As one of a lithium secondary battery, the polymer material is absorbed and hold the nonaqueous electrolyte solution included in the positive electrode and the negative electrode, and absorbed and is retained the same non-aqueous electrolyte solution to the polymer of the separator, there are things you have configured the battery. この場合の有機電解液を吸収・保持させるポリマー材料としては、特にフッ化ビニリデンとヘキサフルオロプロピレンとの共重合体が好ましい。 The polymeric material for absorbing and holding the organic electrolyte solution in this case, in particular a copolymer of vinylidene fluoride and hexafluoropropylene is preferable.

【0111】非水電解質二次電池の形状は特に制限されず、円筒型、角形、コイン型、ボタン型、シート型、積層型、偏平型、電気自動車用の大型等の何れでもよい。 [0111] The shape of the nonaqueous electrolyte secondary battery is not particularly limited, cylindrical, prismatic, coin, button, sheet, laminated, flat type, may be any of a large etc. for electric vehicles.
本発明の非水電解質二次電池は、これらに限られないが、携帯情報端末、携帯電子機器、家庭用小型電力貯蔵装置、自動二輪車、電気自動車、ハイブリッド電気自動車等に用いることができる。 The non-aqueous electrolyte secondary battery of the present invention include, but are not limited to, portable information terminals, portable electronic devices, domestic small power storage device, motorcycles, electric cars, can be used in hybrid electric vehicles.

【0112】本発明に係る負極材料または本発明に係る方法で製造した負極材料もしくは負極を使用した非水電解質二次電池は、負極活物質 (Li吸蔵物質) が理論的容量の高いSi相であるため、高容量である。 [0112] Negative electrode material or a non-aqueous electrolyte secondary battery using the negative electrode material or negative electrode prepared by the process according to the present invention according to the present invention, the negative electrode active material (Li occluding substance) is a high Si phase of the theoretical capacity there is therefore a high capacity. また、Si相粒の周囲をSi含有固溶体又は金属間化合物の相で包囲して、Si相粒を体積変化に対して拘束することにより、Si Further, the periphery of the Si phase grains are surrounded by a phase of Si-containing solid solution or intermetallic compound, by constraining the Si phase grains to volume changes, Si
相を負極活物質とする場合の充電・放電時の体積変化が効果的に防止されるので、微粉化によるサイクル寿命の低下が起こりにくく、サイクル寿命にも優れている。 Since charging and volume change at the time of discharging in the case of the phase with the negative electrode active material can be prevented effectively, hardly occurs reduction in cycle life due to pulverization, it is excellent in cycle life.

【0113】 [0113]

【実施例】非水電解質二次電池用負極材料と負極の評価に用いた負極試験について説明する。 Anodes test is described used for the evaluation of EXAMPLES nonaqueous negative electrode material and a negative electrode electrolyte for a secondary battery.

【0114】<負極試験>供試する負極材料を、分級して、平均粒径30μmの粉末に調整した。 [0114] The negative electrode material that try <anode test> test and classified and adjusted to powder having an average particle diameter of 30 [mu] m. この負極材料の粉末に、結着剤としてポリフッ化ビニリデンを粉末重量の10wt%添加し、さらに溶媒のN−メチルピロリドンを同様に10wt%添加してポリフッ化ビニリデンを溶解した。 The powder of the negative electrode material, a polyvinylidene fluoride was added 10 wt% of the powder weight, obtained by dissolving polyvinylidene fluoride was further added similarly 10 wt% of N- methylpyrrolidone solvent as a binder. この混合物に、導電粉として炭素材料 (アセチレンブラック) の粉末を、この混合物の10wt%の量で加え、 To this mixture, a powder of carbon material (acetylene black) as a conductive powder was added in an amount of 10 wt% of the mixture,
混練し均一なスラリーを作成した。 Kneaded to form a homogeneous slurry.

【0115】このスラリーを30μm厚の電解銅箔に塗布し、乾燥させ、ロール圧延して圧密化させた後、直径13 [0115] After the slurry is applied to the electrolytic copper foil of 30μm thick, dried, compacted by rolling, diameter 13
mm の大きさのポンチを用いて打ち抜きし、非水溶媒二次電池の負極とした。 Punching with punches of mm size, and a negative electrode of a non-aqueous solvent secondary battery. 銅箔上の負極材料層の厚みは約10 The thickness of the negative electrode material layer on the copper foil of about 10
0 μmであった。 Was 0 μm.

【0116】上記負極の単極での性能を、対極、参照極にLi金属を用いた、いわゆる3極式セルを用いて評価した。 [0116] The performance of a single pole of the negative electrode, counter electrode, using a Li metal reference electrode was evaluated by using a so-called three-electrode cell. 電解液としては、エチレンカーボネートとジメトシキエタンの1:1混合溶媒中に、支持電解質のLiPF 6を1M濃度で溶解させた溶液を使用した。 As an electrolytic solution, ethylene carbonate and Jimetoshikietan 1: 1 mixed solvent, the LiPF 6 of the supporting electrolyte was used a solution prepared by dissolving in 1M concentration. 測定は25℃で行い、グローブボックスのように、不活性雰囲気を維持できる装置を用いて、雰囲気の露点が−70℃程度である条件で測定した。 Measurements were performed at 25 ° C., as a glove box, using a device capable of maintaining an inert atmosphere, was measured at the dew point of the atmosphere is about -70 ° C..

【0117】まず、1/10充電 (10時間で満充電になるような条件) で参照極の電位に対して負極の電位が 0Vになるまで充電を行い、同じ電流値で参照極の電位が負極の電位に対して 2Vになるまで放電を行って、この時の1サイクル目の放電容量をその負極材料を用いた負極の放電容量とした。 [0117] First, 1/10 the potential of the negative electrode relative to the potential of the reference electrode in the charge (conditions as fully charged at 10 hours) is performed to charge until to 0V, and the potential of the reference electrode at the same current value performing discharged to 2V with respect to the negative electrode potential, the discharge capacity at the first cycle at this time was the discharge capacity of the negative electrode using the negative electrode material. この充電・放電のサイクルを繰り返し、300 サイクル目の放電容量を測定して、次式からサイクル寿命を計算した。 Repeated cycles of charging and discharging, and measure the discharge capacity of the 300th cycle was calculated cycle life from the following equation. サイクル寿命が80%以上である場合を合格とした。 Where the cycle life is 80% or more was regarded as passed.

【0118】サイクル寿命(%) =(300サイクル目の放電容量/1サイクル目の放電容量) ×100 但し1サイクル目の放電容量とは、第1回目の充電を行い、次いで放電したときの放電容量を言う。 [0118] Cycle life (%) = A (discharge capacity / 1st cycle discharge capacity of 300th cycle) × 100 where first cycle discharge capacity, performs the first charge, then discharge when discharged It refers to the capacity. また、300 In addition, 300
サイクル目の放電容量とは、300 回目の充電を行い、放電したときの放電容量を言う。 The discharge capacity of the cycle, performs a 300 th of charging, say the discharge capacity at the time of discharge.

【0119】なお、上記の製造方法Bに従って製造された負極の評価も、上記の3極式セルにより同様に実施した。 [0119] The evaluation of the negative electrode produced according to the above manufacturing method B were also carried out in the same manner by the above three-electrode cell. 各実施例において、放電容量はmAh/ccの単位 (ccは負極板の容積、負極板の面積と負極材料層の厚みで算出) で示す。 In each example, the discharge capacity is shown in units of mAh / cc (cc is the volume of the negative electrode plate, calculated by the thickness of the area and the negative electrode material layer of the negative electrode plate).

【0120】 [0120]

【実施例1】本実施例は、上記の製造方法1 (急冷凝固法) に従って本発明の負極材料を製造する場合を例示する。 EXAMPLE 1 This example illustrates the case of producing a negative electrode material of the present invention according to the above production method 1 (rapid solidification). 冷却方法としては、それぞれ図1ないし図3に示す装置を用いたガスアトマイズ法、単ロール急冷法、および回転電極法を実施した。 As the cooling method was gas atomizing method using the apparatus shown in FIGS. 1 to 3, respectively, single-roll quenching method, and rotating electrode method was carried out.

【0121】先ず、各方法の凝固速度 (凝固時の冷却速度) をAl−4wt%Cu合金を用いて測定した。 [0121] First, the solidification rate of the process (cooling rate during solidification) was measured using the Al-4wt% Cu alloy.

【0122】 凝固速度の測定 (単ロール急冷法)直径20 mm の芯金部を炭素鋼で、10 m [0122] The metal core portion of the measurement of the coagulation rate (single-roll quenching method) 20 mm in diameter in carbon steel, 10 m
m 厚さの外周部をCuで、それぞれ構成した単ロールを20 m thickness of the outer peripheral portion in Cu, the single roll configured respectively 20
00 rpmの回転速度で回転させ、その外周部にAl−4wt% 00 is rotated at a rpm rotational speed of, Al-4wt% peripherally thereof
Cu合金の溶融原料を滴下して凝固させた。 It was solidified by dropping a molten material of a Cu alloy. 凝固物を光学顕微鏡で観察し、デンドライトの二次アーム間の距離を測定して、凝固速度を求めた。 The coagulum was observed with an optical microscope, to measure the distance between the dendrite secondary arm, to determine the rate of solidification.

【0123】(ガスアトマイズ法)40 kg/cm 2の圧力のAr [0123] (gas atomization) 40 kg / pressure cm 2 of Ar
ガスをガス噴出ノズルを介して噴出させ、Al−4wt%Cu Gas is ejected through the gas ejection nozzle, Al-4wt% Cu
合金の溶融原料を150 g/分の速度で噴出ガス中に滴下して、凝固させた。 The molten material alloy was dropped into the gas injected at 0.99 g / min, and allowed to solidify. 生成した凝固粒子の顕微鏡観察により、単ロール急冷法の場合と同様に凝固速度を測定した。 By microscopic observation of the resulting solidified particles were measured in the same manner solidification rate as in the single roll quenching method.

【0124】(回転電極法)Al−4wt%Cu合金の溶融原料の鋳込みにより直径20 mm の電極を作製し、これをアノード側に装着して500 rpm の回転速度で回転させて、凝固粒子を得た。 [0124] The casting of the molten raw material (rotary electrode method) Al-4wt% Cu alloy to prepare an electrode with a diameter of 20 mm, which is rotated at a rotational speed of the mounting to 500 rpm on the anode side, the coagulated particles Obtained. 凝固速度は上記と同様の方法で求めた。 Solidification rate was determined in the same manner as described above.

【0125】比較のために、インゴット法で原料溶湯を鋳込んで凝固させたものも、上記と同様の方法で凝固速度を求めた。 [0125] For comparison, others solidified by casting a raw material melt in the ingot method, was determined solidification rate in the same manner as described above. 表1に結果を示す。 The results are shown in Table 1.

【0126】 [0126]

【表1】 [Table 1]

【0127】表1からわかるように、単ロール急冷法、 [0127] As can be seen from Table 1, a single roll quenching method,
ガスアトマイズ法、回転電極法は、いずれも凝固速度が Gas atomization, rotating electrode method are both solidification rate
100 ℃/秒以上と急冷凝固である。 A rapid solidification and 100 ° C. / sec or more. 中でも、単ロール法およびガスアトマイズ法が凝固速度が1000℃/秒以上と大きくなった。 Above all, the single roll method and gas atomizing method is the solidification rate becomes large as 1000 ° C. / sec or more. 一方、インゴット法の凝固速度は30℃/ On the other hand, the solidification rate of the ingot method 30 ° C. /
秒であり、100 ℃/秒より小さくなった。 In seconds, it was smaller than 100 ℃ / sec.

【0128】 負極材料の製造 Ni−52wt%Si合金を用いて、非水電解質二次電池負極材料としてのLiの充電・放電特性に対する凝固速度 (冷却方法) の影響を調査した。 [0128] Using the manufacturing Ni-52 wt% Si alloy of the negative electrode material were investigated the effects of the solidification rate for the charge and discharge characteristics of Li as a non-aqueous electrolyte secondary battery negative electrode material (cooling method).

【0129】Ni:48wt%、Si:52wt%の組成割合になるように、単体元素と母合金を適宜配合し、高周波誘導溶解炉で溶解して、均一溶融物とし、各冷却法による供試材として使用した。 [0129] Ni: 48wt%, Si: so that the composition ratio of 52 wt%, suitably blended single element and mother alloy was melted in a high frequency induction melting furnace, a homogeneous melt, the test according to the cooling method It was used as a wood. なお、回転電極法には、この合金溶湯を直径20mmの丸棒に鋳込んで得た電極を供試材として用いた。 Incidentally, the rotating electrode method using an electrode obtained by casting the molten alloy into a round bar having a diameter of 20mm as a test material. いずれの冷却方法も、冷却雰囲気はアルゴン雰囲気であった。 Any method of cooling also, cooling the atmosphere was an argon atmosphere.

【0130】各冷却方法で得られた凝固物の一部について、アルゴン雰囲気中で900 ℃×4時間の熱処理を行った。 [0130] For some of the solidified product obtained in the cooling process, a heat treatment was carried out 900 ° C. × 4 hours in an argon atmosphere. Ni−52wt%Si合金の凝固中に析出して包囲材を構成する可能性があるNi−Si金属間化合物の主要なものはNi Ni-52 wt% Si main thing Ni-Si intermetallic compound precipitated during solidification may constitute the surrounding material of the alloy Ni
Si 2であり、このNiSi 2の固相線温度は993 ℃である。 A Si 2, the solidus temperature of the NiSi 2 is 993 ° C..
熱処理後に、単ロール法とインゴット法の凝固物は粉砕した。 After heat treatment, the solidification of the single roll method and the ingot method was crushed.

【0131】各方法で得られた合金粒子の熱処理した供試材 (熱処理材) 及び熱処理しなかった供試材 (凝固まま材) を用いて、上記の負極試験を行い、放電容量およびサイクル寿命を評価した。 [0131] Using a test piece obtained by heat treatment of the obtained alloy particles by the method (heat treatment material), and heat treatment that did not test materials (solidification Mom material), the negative electrode test described above, the discharge capacity and cycle life It was evaluated. また、各冷却方法で得られた凝固物 (粉砕した場合は粉砕前) の断面をSEMで調べたところ、いずれの場合も、図4に示すように、マトリックスがNiSi 2相であり、その中にNiSi相で包囲され、または包囲されていないSi相粒が存在する組織を有していた。 It also examined the cross-section of the solidified product obtained in the cooling process (before when pulverized pulverization) in SEM, in any case, as shown in FIG. 4, a matrix NiSi 2 phase, therein to be surrounded by NiSi phase, or enclosed non Si phase grains had a tissue present. このコアのSi相粒の平均粒径と全体での重量割合 (重量%) をSEM写真 (平均粒径はランダムに選択した100 個の平均値) により調べた結果を、負極試験結果と一緒に表2に示す。 The average particle diameter and the weight ratio (wt%) of the SEM photograph of the entire Si phase grains of the core (average particle diameter 100 average values ​​selected randomly) the results of examining by, together with the negative electrode test results It is shown in Table 2.

【0132】 [0132]

【表2】 [Table 2]

【0133】本発明に従って、凝固速度 100℃/秒以上で急冷凝固させて製造した合金粒子では、どの冷却方法でもSi相粒の平均粒径が25μm以下となったのに対し、 [0133] In accordance with the present invention, whereas the alloy particles prepared by rapid solidification at a solidification rate 100 ° C. / sec or more, an average particle diameter of the Si phase grains in any cooling method becomes 25μm or less,
比較例の製造方法で作製した供試材はSi相粒の平均粒径は50μmを越えた。 Test materials were fabricated by the manufacturing method of the comparative example average particle diameter of the Si phase grains was over 50 [mu] m. 負極試験に用いた供試材、即ち合金粒子の平均粒径は30μmである。 The average particle diameter of the test material, i.e. alloy particles used in the negative electrode test is 30 [mu] m. 従って、本発明例では、Si相粒の平均粒径が合金粒子の平均粒径より小さいため、Si相粒は少なくとも部分的に包囲材を有していた。 Accordingly, in the present invention embodiment, since the average particle diameter of the Si phase grains is smaller than the average particle diameter of the alloy particles, Si phase grains had at least partially surrounding material. 一方、比較例では、Si相粒の平均粒径の方が合金粒子の平均粒径よりずっと大きいので、包囲材で全く包囲されていないSi相粒が多数存在した。 On the other hand, in the comparative example, since the direction of the average particle diameter of the Si phase grains is much larger than the average particle diameter of the alloy particles, Si phase grains of at surrounding material is not completely surrounded there were many.

【0134】負極試験の結果を見ると、負極の放電容量は比較例のインゴット法でも本発明とさほど遜色のない値となった。 [0134] Looking at the results of the negative electrode test, the discharge capacity of the negative electrode became much no comparable value as the invention in an ingot method of the comparative example. しかし、注目すべきはサイクル寿命であって、Si相粒の平均粒径が40μmより小さい本発明例では何れもサイクル寿命が80%以上と高いのに対し、比較例のそれは48%または68%と不合格の値になった。 However, a cycle life Notably, while higher and 80% or more cycle life both in the average particle size is 40μm smaller the invention examples of Si phase grains, 48% while that of Comparative Example or 68% and it became a failure of value. なお、 It should be noted that,
本発明例の中でもSi相粒の平均粒径が小さいロール急冷法とアトマイズ法でサイクル寿命が88%と高くなった。 Cycle life was as high as 88% by a roll quenching method and an atomizing method the average particle diameter of the Si phase grains is small in the present invention embodiment.

【0135】熱処理材と凝固まま材とを比較すると、熱処理によりSi相の平均粒径は大きくなったが、Si相粒の重量比率は減少した。 [0135] Comparing the heat treated material solidified Mom material, the average particle diameter of the Si phase is increased by heat treatment, the weight ratio of the Si phase grains decreased. Si相の平均粒径が小さく、その重量比率の大きい凝固まま材の方が、放電容量がかなり高くなった。 The average particle diameter of the Si phase is small, towards greater coagulation Mom material of its weight ratio, the discharge capacity is much higher. サイクル寿命は、凝固まま材では、Si相粒の微細分散効果により熱処理材と同等または僅かに劣るという程度であった。 Cycle life, in the coagulation Mom material was much inferior to the equivalent heat treatment material or slightly by finely dispersing effect of the Si phase grains.

【0136】 [0136]

【実施例2】Ni−52wt%Si合金を用いて実施例1に記載したガスアトマイズ法と同様にして、熱処理温度だけを変更して負極材料を作製した。 In the same manner as the gas atomization method described in EXAMPLE 2 Example 1 using Ni-52 wt% Si alloy, to prepare a negative electrode material by changing only the heat treatment temperature. 得られた負極材料のSi相粒の平均粒径および負極試験結果を、熱処理温度と一緒に表3に示す。 The average particle size and a negative test result for Si phase grains of the resulting negative electrode material are shown in Table 3 together with the heat treatment temperature.

【0137】 [0137]

【表3】 [Table 3]

【0138】表3に示すように、熱処理温度が、Ni−52 [0138] As shown in Table 3, heat treatment temperature, Ni-52
wt%Si合金の凝固中に生成する主要な金属間化合物であるNiSi 2の固相線温度の993 ℃より10℃以上低い本発明例では、Si相粒の平均粒径は40μm以下にとどまり、サイクル寿命が何れも90%以上となった。 The wt% Si main solidus 993 lower the present invention example 10 ° C. or higher than ° C. of the temperature of NiSi 2 is an intermetallic compound produced during the solidification of the alloy, the average particle diameter of the Si phase grains remained at 40μm or less, any cycle life becomes 90% or more. これに対し、この固相線温度より8℃低い温度で熱処理した比較例では、熱処理によるSi相粒の成長でSi相粒の平均粒径が40 In contrast, in the comparative example in which heat treatment at 8 ° C. lower temperature than the solidus temperature, the average particle diameter of the Si phase grains in the Si phase grains grow due to the heat treatment is 40
μmを超えたため、体積変化を防止する拘束がききにくくなり、サイクル寿命は80%に達しなかった。 Due to exceeded [mu] m, restraint is not easily heard to prevent volume change, the cycle life was not reached 80%.

【0139】 [0139]

【実施例3】実施例1に記載したガスアトマイズ法と同様にして、原料のNi−Si合金の組成(Siのwt%で示す) EXAMPLE 3 In the same manner as the gas atomization method described in Example 1, the composition of the Ni-Si alloy material (indicated by wt% of Si)
だけを変更して (900 ℃×4時間の熱処理を実施、及び熱処理なし) 負極材料を作製した。 Only by changing (heat treatment is performed for 900 ° C. × 4 hours, and no heat treatment) to prepare a negative electrode material. 得られた負極材料の The resulting negative electrode material
Si相粒の平均粒径および負極試験結果を表4に示す。 The average particle size and the negative test results Si phase grains shown in Table 4.

【0140】 [0140]

【表4】 [Table 4]

【0141】表4に示すように、熱処理実施の有無にかかわらずSi相粒の占める重量比が大きくなるに従って放電容量は大きくなるが、体積変化に対して拘束する包囲材の割合が少なくなるため、サイクル寿命は少しづつ低減する傾向がある。 [0141] As shown in Table 4, although the discharge capacity increases as the weight ratio occupied by the Si phase grains or without heat treatment performed is increased, the ratio of the enclosing member for constraining the volume change is reduced cycle life tends to decrease little by little. また、同じSi量であれば、熱処理を実施した方が、放電容量は低くなるが、サイクル寿命は多少高くなる。 Further, if the same Si content, is better to conduct the heat treatment, although the discharge capacity is low, the cycle lifetime is slightly higher. しかし、現行の炭素電極と比較すると放電容量、サイクル寿命とも同等以上である。 However, it is to be compared with the current of the carbon electrode discharge capacity, both the cycle life equal to or higher.

【0142】 [0142]

【実施例4】実施例1に記載したガスアトマイズ法と同様にして、Ni−52wt%Si合金のNiの一部を他の元素で置換した置換型固溶体合金を作製した。 EXAMPLE 4 In the same manner as the gas atomization method described in Example 1 to prepare a substitutional solid solution alloy obtained by substituting a part of Ni of Ni-52 wt% Si alloy with other elements. 得られた合金の一部にアルゴン雰囲気中で 850℃×8時間の熱処理を施した。 Some of the obtained alloy was heat-treated at 850 ° C. × 8 hours in an argon atmosphere. 凝固まま材と熱処理材の合金を用いて負極試験を行った。 Using coagulation Mom material and alloy heat treatment material subjected to negative test. 合金組成と負極試験結果を表5に示す。 Alloy composition and the negative test results are shown in Table 5.

【0143】 [0143]

【表5】 [Table 5]

【0144】表5において、例えば、 Ni-5Fe-52Siは43 [0144] In Table 5, for example, Ni-5Fe-52Si 43
wt%Ni-5wt%Fe-52wt%Si合金であることを示し、Feは、金属間化合物のNiSi 2およびNiSi中のNiの一部を置換して固溶している。 It indicates that the wt% Ni-5wt% Fe- 52wt% Si alloy, Fe is solid solution by substituting a part of Ni in NiSi 2 and NiSi intermetallic compound. Co、Mn、Cr、Cuも、Feと同様に挙動する。 Co, Mn, Cr, Cu also behave similarly to Fe.

【0145】表5に示すように、包囲材が固溶体であってもSi相の重量比に見合った放電容量を示し、サイクル寿命も良好な値となっている。 [0145] As shown in Table 5, enclosure member represents the discharge capacity commensurate with the weight ratio of the Si phase even solid solution, also has a favorable value cycle life. また、実施例1と同様に、Si相が微細で、その重量比率の高い凝固まま材の方が、熱処理材より放電容量が高くなった。 Further, in the same manner as in Example 1, Si phase is fine, towards the high solidification Mom material having the weight ratio, a discharge capacity than heat treatment material was higher. サイクル寿命はいずれの場合も良好であった。 Cycle life was good in both cases.

【0146】 [0146]

【実施例5】実施例1に記載したガスアトマイズ法と同様にして、Siと合金化する第2の元素の種類と量および熱処理温度を変更して、凝固まま材と熱処理材の負極材料を作製した。 EXAMPLE 5 In the same manner as the gas atomization method described in Example 1, by changing the type and amount and heat treatment temperature of the second element to Si alloyed, prepare a negative electrode material of the solidified Mom material and heat treatment material did. 使用した原料合金の組成、その二元合金系の凝固中に生成する主要な金属間化合物とその固相線温度、および熱処理温度を、得られた負極材料のSi相粒の平均粒径および負極試験結果と共に表6に示す。 The average particle diameter and the negative electrode of the Si phase grains of the negative electrode material composition of the raw material alloy used includes a major intermetallic compounds formed during solidification of the binary alloy system the solidus temperature, and the heat treatment temperature was obtained It is shown in Table 6 together with the test results.

【0147】 [0147]

【表6】 [Table 6]

【0148】表6に示す通り、Siと金属間化合物又は固溶体を形成する元素の種類を変更して負極材料を作製すると、放電容量は種々の値をとるものの、サイクル寿命はいずれも良好であった。 [0148] As shown in Table 6, when to change the type of element which forms a Si intermetallic compound or solid solution to produce a negative electrode material, the discharge capacity although take various values, either the cycle life was good It was. 放電容量は凝固まま材の方が高くなった。 Discharge capacity became higher in the coagulation Mom material.

【0149】 [0149]

【実施例6】本実施例は、上記の製造方法2 (付着層形成法) に従って、本発明の負極材料を形成する場合を例示する。 EXAMPLE 6 This example, according to the above production method 2 (adhesion layer formation process) illustrates a case of forming a negative electrode material of the present invention. 下記に述べるようにして合金粒子のサンプル1 As described below the sample 1 of the alloy particles
〜7を調製した。 To 7 were prepared.

【0150】(1) アルゴンガスアトマイズ法により得られた平均粒径約30μmのSiの球状粉末に、市販のアルカリ性無電解ニッケルメッキ液を用いて約1μmの厚さの [0150] (1) spherical powder of Si having an average particle size of about 30μm obtained by argon gas atomizing method, a thickness of about 1μm using a commercially available alkaline electroless nickel plating solution
Niメッキを施した。 It was plated with Ni. 次いで、アルゴンガス雰囲気中で70 Then, 70 in an argon gas atmosphere
0 ℃×4時間の熱処理を行って、平均粒径32μmの合金粒子を得た。 0 performed heat treatment ° C. × 4 hours to obtain alloy particles having an average particle size of 32 [mu] m. 熱処理後の粉末の断面を光学顕微鏡で観察したところ、Si粉末が約1μmの厚さのNiSi 2層 (組成はEPMAで決定) で包囲されていた。 Observation of the powder of the cross-section after the heat treatment under an optical microscope, NiSi 2 layer thickness of the Si powder is about 1 [mu] m (composition determined by EPMA) was surrounded by. この負極材料をサンプル1とする。 To the anode material as Sample 1. なお、包囲材であるNiSi 2の固相線温度は、実施例1および表5に示したように983 ℃であるので、熱処理温度は、この固相線温度より10℃以上低かった。 Note that the solidus temperature of NiSi 2 is surrounding material, since it is so 983 ° C. As shown in Example 1 and Table 5, the heat treatment temperature was lower 10 ° C. or higher than the solidus temperature.

【0151】(2) サンプル1と同様にガスアトマイズ法で作製したSi粉末の表面に、遊星ボールミル (フリッチェ社製、p-5)によるMA法で10時間処理することにより、 [0151] (2) Sample 1 in the same manner as the surface of the Si powder produced by a gas atomizing method, a planetary ball mill (Fritsch Co., p-5) by 10 hours at MA method based on,
平均粒径1μmのNi粉末を付着させ、サンプル1と同様の熱処理を行って、平均粒径32μmの合金粒子を得た。 Depositing a Ni powder having an average particle diameter of 1 [mu] m, the sample 1 by performing the same heat treatment as to obtain alloy particles having an average particle size of 32 [mu] m.
Si粉末の表面を包囲する厚さ約1μmのNiSi 2層が形成されていた。 NiSi 2 layer having a thickness of about 1μm surrounding the surface of the Si powder was formed. この負極材料をサンプル2とする。 To the anode material and sample 2.

【0152】(3) サンプル1と同様にガスアトマイズ法で作製した、化学組成が重量比でNi:Si=20:80の合金の平均粒径約30μmの粉末の表面に、サンプル1と同様に無電解ニッケルメッキにより厚さ約1μmのNiメッキと熱処理を施した。 [0152] (3) Sample 1 was prepared in the same as a gas atomizing method, Ni in chemical composition by weight: Si = 20: 80 average particle size of about 30μm of the powder surface of the alloy, Sample 1 and likewise no It was subjected to Ni plating and heat treatment of the thickness of about 1μm by electrolytic nickel plating. 平均粒径が32μmで、Si相のマトリックス中にNiSi 2相が析出した組織を有するSi相粉末を包囲する約1μm厚さのNiSi 2層が形成されていた。 An average particle diameter of 32 [mu] m, approximately 1μm thick NiSi 2 layer surrounding the Si phase powder having a tissue NiSi 2 phase precipitated was formed in a matrix of Si phase. この負極材料をサンプル3とする。 To the anode material as Sample 3.

【0153】(4) サンプル1と同様にガスアトマイズ法で作製した平均粒径約30μmのSi粉末を、遊星ボールミル (フリッチェ社製P-5)により、平均粒径1μmのNi粉末に和光純薬製の平均粒径0.6 μmのTiC 粉末を1wt% [0153] (4) Sample 1 and the Si powder having an average particle diameter of about 30μm was produced by similarly gas atomization, by a planetary ball mill (Fritsch Co. P-5), the Ni powder having an average particle diameter of 1μm by Wako Pure Chemical Industries, Ltd. the average particle size 0.6 [mu] m of TiC powder 1 wt%
混合した混合粉末を用いて、10時間のMA法処理を行い、 By using a mixed powder mixed performs MA method for 10 hours,
Si粉末の表面に上記混合粉末を付着させた。 On the surface of the Si powder was deposited the mixed powder. その後、Ar Then, Ar
ガス雰囲気中で700 ℃×4時間の熱処理を行って、合金粒子を得た。 Subjected to heat treatment of 700 ° C. × 4 hours in a gas atmosphere to give alloy particles. この負極材料をサンプル4とする。 To the anode material as Sample 4.

【0154】熱処理後のサンプル4の粉末の断面を光学顕微鏡で観察したところ、Si粉末の表面に約1μm厚の [0154] When a powder of a cross section of Sample 4 after heat treatment was observed with an optical microscope, of about 1μm thick on the surface of the Si powder
NiSi 2相からなる包囲層が形成されていることが判明した。 It has been found that enclosing layer composed of NiSi 2 phase is formed. またNiSi 2相中には0.1 μm以下の微細なTiC 析出が観察できた。 Also during NiSi 2 phase 0.1 [mu] m or less fine TiC precipitates could be observed. (NiSi 2相はEPMA分析のNi、Siの量比から決定、微細析出物はEPMAの分析ビーム径より小さいサイズであるが、必ずTiとCが検出できることからTiC と推定した。) TiC 相の析出粒度は使用した粉末粒度より小さくなっているが、これはMA時の機械的エネルギーにより、使用粉末 (1次粒子が凝集して0.6 μmになっているもの) が解砕されて1次粒子(0.1μm以下) になったためと考えられる。 (NiSi 2 phase Ni of EPMA analysis, determined from the ratio of Si, although fine precipitates is smaller than the analysis beam diameter of EPMA, was estimated to TiC because it can detect always Ti and C.) Of TiC phase Although precipitation particle size is smaller than the powder particle size used, which is by mechanical energy during MA, use powder (those primary particles is in the aggregate to 0.6 [mu] m) collapsed granulated has been primary particles presumably because it became (0.1 [mu] m or less).

【0155】(5) サンプル4と同様にして、TiC の代わりに、和光純薬製試薬の平均粒径0.27μmのSiC を重量割合で1%混合してMA処理し、同条件の熱処理を施して得た負極材料をサンプル5とする。 [0155] (5) Sample 4 was prepared in analogy to, instead of TiC, and MA treated by mixing 1% SiC having an average particle diameter of 0.27μm of Wako Junyaku Co. reagent in a weight ratio, subjected to heat treatment under the same conditions the negative electrode material was obtained with sample 5.

【0156】(6) 比較のために、Ni−80wt%Si合金をインゴット法で作製し、Arガス雰囲気中で700 ℃×8時間の熱処理を施した。 [0156] (6) For comparison, the Ni-80wt% Si alloy was prepared by ingot method, was subjected to heat treatment at 700 ° C. × 8 hours in an Ar gas atmosphere. 得られた合金は、Si相のマトリックス中にNiSi 2相が析出している組織を持つものであるが、NiSi 2相は粗大であった。 The resulting alloys are those with a tissue NiSi 2 phase is precipitated in the matrix of the Si phase, the NiSi 2 phase was coarse. このインゴットを不活性雰囲気中で粉砕し、平均粒径が約32μmになるように分級して粉末を得た。 The ingot was ground in an inert atmosphere, to obtain a classified to a powder to an average particle size of about 32 [mu] m. NiSi相が粗大であるため、粉末の組織は、Si相のみのもの、Si相とNiSi 2相が共に存在するものおよびNiSi 2相のみのものとがそれぞれ存在していた。 Since NiSi phase is coarse, powder tissues are those of the Si phase only, and were present each one of those and NiSi 2 phase only Si phase and NiSi 2 phase are both present. このNi−Si合金粉末をサンプル6とする。 To this Ni-Si alloy powder and Sample 6.

【0157】(7) サンプル6と同様に作製した、平均粒径30μmのNi−80wt%Si合金のインゴット粉末に、サンプル1と同様の無電解ニッケルメッキによりNiメッキを施し、サンプル1と同様の熱処理を施して、合金粒子を作製した。 [0157] (7) was prepared in the same manner as Sample 6, the ingot powder Ni-80 wt% Si alloy having an average particle diameter of 30 [mu] m, plated with Ni in the same electroless nickel plating as in Sample 1, Sample 1 with the same subjected to a heat treatment, we were prepared alloy particles. この粉末のコア組織はサンプル6と同様であり、その粉末の表面にNiSi 2またはNiSi相を含む包囲材が形成されていた。 This powder core tissue is similar to Sample 6, enclosure member including a NiSi 2 or NiSi phase was formed on the surface of the powder. コアのSi相粒のNiSi 2相は、サンプル6と同様に粗大であった。 NiSi 2 phase core of the Si phase grains were similar coarse as Sample 6. この合金粒子の粉末 (平均粒径32μm) をサンプル7とする。 To the powder of the alloy particles (average particle size 32 [mu] m) and the sample 7.

【0158】サンプル1ないし7の合金粒子は何れも平均粒径は約32μmで、化学組成は、サンプル1、2、4 [0158] In samples 1 to any alloy particles of 7 average particle size of about 32 [mu] m, the chemical composition, the sample 1,2,4
〜6はNi:Si=20:80、サンプル3、7はNi:Si=36: 6 is Ni: Si = 20: 80, the sample 3 and 7 Ni: Si = 36:
64となっていることを確認した。 It was confirmed that a 64. これらの負極材料のサンプルを用いて負極試験を行った結果を表7に示す。 The results of the negative electrode tested with samples of these negative electrode materials shown in Table 7.

【0159】 [0159]

【表7】 [Table 7]

【0160】表7に示すように、放電容量の大きさは概ねSiのwt%により決まり、Si含有量の多いサンプル1、 [0160] Table as shown in 7, the size of the discharge capacity is approximately determined by wt% of Si, more sample 1 having Si content,
2、4〜6の放電容量が高くなった。 Discharge capacity of 2,4~6 was higher. しかし、包囲材を持たない比較例のサンプル6は、サイクル寿命が極めて短く、不合格となった。 However, Sample 6 of Comparative Example having no surrounding material has a very short cycle life, it had failed. 一方、本発明に従ってSi相粒の周囲に包囲材を形成した場合には、サイクル寿命が80% On the other hand, in the case of forming the surrounding material around the Si phase grains in accordance with the present invention, the cycle life is 80%
以上と良好であった。 It was good and more. 特に、包囲材中にTiC 、SiC を微細分散させたサンプル4、5は最も良好なサイクル寿命を示した。 In particular, samples 4 and 5 TiC, the SiC was finely dispersed in the surrounding material showed the most excellent cycle life.

【0161】 [0161]

【実施例7】実施例6のサンプル1と同様にして、Si粉末に無電解ニッケルメッキを施した後、熱処理を行うことにより、Si相粒がNiSi 2相で包囲された合金粒子からなる負極材料を作製した。 EXAMPLE 7 In the same manner as Sample 1 of Example 6, was subjected to electroless nickel plating to Si powder, heat treatment is performed, the negative electrode Si phase grains composed of alloy particles surrounded by NiSi 2 phase the material was produced. 但し、無電解ニッケルメッキ液の濃度を変化させて、メッキ厚さを種々変えた。 However, by changing the concentration of the electroless nickel plating solution was variously changed the plating thickness. この負極材料の負極試験を行った結果を、Si相粒の重量比の結果と共に表8に示す。 The results of the negative electrode test of the negative electrode material are shown in Table 8 together with the results of the Si phase grains in a weight ratio. なお、Si相粒の重量比は、顕微鏡観察によりSi相粒の占める面積比を測定し、各相の比重をそれぞれの相の面積比に掛け合わせて計算で求めた。 The weight ratio of the Si phase grains, measuring the area ratio occupied by the Si phase grains by microscopic observation was determined by calculation by multiplying each phase specific gravity to the area ratio of each phase.

【0162】 [0162]

【表8】 [Table 8]

【0163】表8に示すように、製造方法2を用いると、Si相粒の重量比が98wt%と高くなっても良好なサイクル寿命を示す。 [0163] As shown in Table 8, when using the production method 2, the weight ratio of the Si phase grains exhibit good cycle life as high as 98 wt%. Si相粒の割合が多いほど放電容量が高くなるので、製造方法2では2000 mAh/cc を超える非常に高い放電容量を実現することができる。 Since the discharge capacity as the ratio of the Si phase grains is large becomes high, it is possible to achieve a very high discharge capacity exceeding production method 2, 2000 mAh / cc.

【0164】従って、保有する製造設備や製造コストを勘案して、製造方法1と2とを適宜用いることにより、 [0164] Therefore, in consideration of the manufacturing equipment and manufacturing cost of holding, by using the manufacturing method 1 and 2 as appropriate,
Si相粒の重量比が5wt%以上、99wt%までの負極材料を作製することができる。 The weight ratio of the Si phase grains 5 wt% or more, it is possible to prepare a negative electrode material of up to 99 wt%.

【0165】 [0165]

【実施例8】熱処理温度を変更した以外は、実施例6のサンプル1と同様にしてSi相粒がNiSi 2相で包囲された合金粒子からなる負極材料を作製し、負極試験を行った結果を、熱処理温度およびSi相粒の平均粒径と一緒に表9に示す。 Example 8 except for changing the heat treatment temperature, as a result of the Si phase grains in the same manner as Sample 1 of Example 6 to prepare a negative electrode material consisting of alloy particles surrounded by NiSi 2 phase, were negative test They are shown in Table 9 together with the average particle diameter of the heat treatment temperature and Si phase grains. この場合のSi相粒の重量比は、何れの例でも約50wt%であった。 The weight ratio of the Si phase grains in this case was about 50 wt% in any of the examples.

【0166】 [0166]

【表9】 [Table 9]

【0167】比較例の熱処理温度は、固相線温度993 ℃ [0167] heat treatment temperature of the comparative example, solidus temperature 993 ° C.
より8℃だけ低い温度であったため、粉末が焼結し、供試材として使用できなかった。 Because it was only a low temperature more 8 ° C., the powder is sintered, could not be used as a test material. 本発明に従って熱処理したものは、放電容量が高い上に、サイクル寿命も良好であった。 Which was heat treated in accordance with the present invention, on the discharge capacity is high, were also good cycle life.

【0168】 [0168]

【実施例9】実施例7と同様にして、アトマイズ法による平均粒径30μmのSi粉末に、種々の金属を無電解メッキした後、表10に示す温度で熱処理 (時間は何れも4時間)を行って、Si相粒が表示の金属間化合物又は固溶体で包囲された合金粒子からなる負極材料を作製した。 Example 9 In the same manner as in Example 7, the Si powder having an average particle diameter of 30μm by atomizing method, after electroless plating various metals, (4 hours both times) Heat treatment at a temperature shown in Table 10 the go, Si phase grains to prepare a negative electrode material consisting enclosed alloy particles intermetallic compound or solid solution of the display. なお、Si相粒の重量比がすべて50wt%となるように、各元素のメッキ厚さをその比重に応じて調整した。 The weight ratio of the Si phase grains are all such that 50 wt%, to prepare a plating thickness of each element according to its specific gravity. この負極材料の負極試験の結果も表10に一緒に示す。 Results of the negative electrode test of the negative electrode material is also shown together in Table 10. 比較のために、現在の一般的な負極材料である炭素材についての負極試験の結果も併せて示す。 For comparison, also shown the results of negative electrode test for carbon material which is a current general negative electrode material.

【0169】 [0169]

【表10】 [Table 10]

【0170】表10に示すように、メッキにより形成した付着層の元素を変更しても、炭素材の場合より放電容量の高い負極材料を得ることができた。 [0170] As shown in Table 10, changes to elements of the attachment layer formed by plating, it was possible to obtain a negative electrode material having high discharge capacity than that of the carbon material. また、いずれの場合も、サイクル寿命は80%以上と良好であった。 In either case, it was good and the cycle life is more than 80%. なお包囲材がAl、Pbの固溶体であるものは、Al、Pb自身がLiを吸蔵および放出するため放電容量は比較的大きな値となった。 Note that enclosure member is Al, a solid solution of Pb is, Al, discharge capacity since the Pb itself absorbing and releasing Li was a relatively large value.

【0171】 [0171]

【実施例10】本実施例は、製造方法Bによる負極の製造例を例示する。 EXAMPLE 10 This example illustrates the production example of the negative electrode due to the production method B. アルゴンガスアトマイズ法により粒径 The particle size by argon gas atomizing
25μm以下、平均粒径15μmのSi粉末を作製し、負極試験に説明したのと同様にして、付着層を有しないSi粉末のスラリーを作製した。 25μm or less, to prepare a Si powder having an average particle size of 15 [mu] m, in the same manner as described in the anode study to create a slurry of Si powder having no adhesion layer. このスラリーを電解銅箔に約25 About this slurry to the electrolytic copper foil 25
μmの厚さに塗布し、乾燥して、銅箔上にSi粉末層を形成した。 It was coated to a thickness of [mu] m, and dried to form a Si powder layer on the copper foil.

【0172】このSi粉末層に、無電解メッキ法または電解メッキ法により表11に示す元素をメッキして付着層を形成し、次いで表11に示す温度でアルゴン雰囲気中にて熱処理 (処理時間は4時間) を施して、非水電解質二次電池用の負極を作製した。 [0172] This Si powder layer by electroless plating or electrolytic plating to form an adhesion layer by plating the element shown in Table 11, followed by heat treatment in an argon atmosphere at a temperature shown in Table 11 (treating time 4 hours) is subjected to, to produce a negative electrode for a non-aqueous electrolyte secondary battery. なお、メッキ付着層の厚みはいずれの3μmとした。 The thickness of the plating adhesion layer was either 3 [mu] m. Si相粒の重量比は、メッキと熱処理により形成された包囲材の比重により多少は変動するが、何れも50wt%前後であった。 The weight ratio of the Si phase grains will vary somewhat with the specific gravity of the surrounding material formed by plating and heat treatment, they were both 50 wt% and forth.

【0173】こうして作製された負極の性能を、前述した負極試験に説明したのと同様にして3極式セルで測定した。 [0173] Thus the performance of the fabricated negative electrode, was measured at three electrode cell in the same manner as described negative electrode test described above. この測定結果も表11に示す。 The measurement results are also shown in Table 11.

【0174】 [0174]

【表11】 [Table 11]

【0175】表11に示すように、製造方法Bに従って、 [0175] As shown in Table 11, according to the production method B, submitted
最初にSi粉末層を形成してから、Si粉末層に第2の元素を付着させ、熱処理して包囲材を形成しても、放電容量とサイクル寿命の良好な負極を製造することができた。 From the beginning to form a Si powder layer, the second element is attached to the Si powder layer, be formed surrounding material by heat treatment, it was possible to produce a good negative electrode of the discharge capacity and cycle life .

【0176】 [0176]

【実施例11】実施例9と同様にして、Si粉末に、Ni、 EXAMPLE 11 Analogously to Example 9, the Si powder, Ni,
Mg、Ca、Co、FeまたはWからなる付着層を無電解メッキにより形成し、熱処理することにより得た合金粒子からなる負極材料を用いて、リチウムイオン二次電池を作製し、以下に示す要領で電池試験を行った。 Mg, Ca, Co, an adhesive layer composed of Fe or W is formed by electroless plating, by using a negative electrode material consisting of alloy particles obtained by heat treatment, to prepare a lithium ion secondary battery, a manner shown below in went a battery test. なお、比較のために、現在、使用されている炭素材を負極に用いた電池も同様の要領で作製し、同様の試験を行った。 For comparison, now also batteries using carbon material used in the negative electrode was prepared in the same manner, a similar test was carried out. 結果を表12に示す。 The results are shown in Table 12.

【0177】図5に、本実施例で用いた円筒形非水電解液二次電池の縦断面図を示す。 [0177] FIG. 5 shows a longitudinal sectional view of a cylindrical non-aqueous electrolyte secondary battery used in this example. 図5において1は耐有機電解液性のステンレス鋼板を加工した電池ケース、2は安全弁を設けた封口板、3は絶縁パッキンを示す。 The battery case 1 is obtained by processing a stainless steel plate resistant to organic electrolyte solution of 5, 2 sealing plate provided with a safety valve, 3 denotes an insulating packing. 4は極板群であり、正極板5および負極板6がセパレータ7 4 is a electrode plate group, the positive electrode plate 5 and the negative electrode plate 6 is a separator 7
を介して複数回渦巻状に巻回されてケース内に収納されている。 Through it is accommodated by winding a plurality of times spirally in the case. そして上記正極板5からは正極アルミリード5a And the positive electrode aluminum lead 5a from the positive electrode plate 5
が引き出されて封口板2に接続され、負極板6からは負極ニッケルリード6aが引き出されて電池ケース1の底部に接続されている。 Is connected to the sealing plate 2 is pulled out, from the negative electrode plate 6 is connected to the bottom of the battery case 1 is drawn anode nickel lead 6a is. 8は絶縁リングで、極板群4の上下部にそれぞれ設けられている。 8 are provided at the upper and lower portions of an insulating ring, the electrode plate group 4.

【0178】正極板5は、次のようにして作製した。 [0178] The positive electrode plate 5, was prepared as follows. まず炭酸リチウムと炭酸コバルトを所定の割合で混合し、 Lithium carbonate and cobalt carbonate were mixed at a predetermined ratio is first,
この混合物を空気雰囲気下において、900 ℃で一定時間焼成して正極活物質であるLiCoO 2を得た。 The mixture in an air atmosphere to obtain a LiCoO 2 is a positive electrode active material by firing a certain time at 900 ° C.. このLiCoO 2の粉末100 重量部に、導電助剤のアセチレンブラック3重量部、フッ素樹脂系結着剤5重量部を混合し、N−メチルピロリドン溶液に懸濁させてペースト状にした後、このペーストを厚さ0.020 mmのアルミ箔の両面に塗着し、 To 100 parts by weight of powder of this LiCoO 2, 3 parts by weight of acetylene black of the conductive auxiliary agent, fluorine resin-based binder 5 parts by weight were mixed, the mixture was a paste was suspended in N- methylpyrrolidone solution, this It was coated on both sides of an aluminum foil having a thickness of 0.020 mm the paste,
乾燥後厚み0.130 mm、幅35mm、長さ270 mmの正極板5を作製した。 Thickness after drying 0.130 mm, to prepare a positive electrode plate 5 having a width 35 mm, length 270 mm. また正極リードとしてアルミニウム片を取り付けた。 The aluminum was attached to pieces as a positive electrode lead.

【0179】負極板6の作製法は次の通りである。 [0179] The negative electrode plate production method of 6 is as follows. 実施例9に準じて作製した合金粒子からなる負極材料100 重量部に、スチレン−ブタジエンゴム系結着剤10重量部と導電助剤のアセチレンブラック3重量部とを混合し、カルボキシメチルセルロース水溶液に懸濁させてペースト状にした。 The negative electrode material 100 parts by weight of the alloy particles prepared as in Example 9, styrene - and 3 parts by weight of acetylene black of the butadiene rubber-based binder 10 parts by weight and the conductive auxiliary agent were mixed, suspended in an aqueous solution of carboxymethyl cellulose to was a paste to Nigosa. このペーストを、厚さ0.015 mmの銅箔の表面の塗着し、乾燥後厚さ0.2 mm、幅37mm、長さ300 mmの負極板を作製した。 The paste was coated wearing surfaces of a copper foil having a thickness of 0.015 mm, dried thickness 0.2 mm, to produce a negative electrode plate of width 37 mm, length 300 mm.

【0180】上記のようにして作製した正極板と負極板を、セパレータを介して渦巻状に巻回し、直径13.8mm、 [0180] The positive electrode plate and negative electrode plate prepared as described above, spirally wound through a separator, diameter 13.8 mm,
高さ50mmの電池ケース内に収納した。 It was housed in height 50mm in the battery case. 電解液には炭酸エチレンと炭酸エチルメチルの等容積混合溶媒に、LiPF 6 In equal volume mixed solvent of the electrolytic solution of ethylene carbonate and ethyl methyl carbonate, LiPF 6
を1M濃度で溶解した溶液を使用し、極板群4に注入した後、電池を封口し、試験電池A〜F (メッキ元素はそれぞれNi、Mg、Ca、Fe、Co、W) を作製した。 The use of a solution prepared by dissolving in 1M concentrations, was injected into the electrode plate group 4, and sealing the battery, test battery to F (plating elements Ni, Mg, Ca, Fe, Co, W, respectively) was prepared . 負極材料が炭素材である試験電池Gも同様に作製した。 Negative electrode material was also prepared in the same manner test battery G is a carbon material.

【0181】これらの電池を、充放電電流100 mAで充電終止電圧4.2 V、放電終止電圧25Vで充放電サイクル試験を行い、1サイクル目の充放電容量を測定するとともに、500 サイクル後の放電容量を測定し、1サイクル目の放電容量に対する500 サイクル目の放電容量の割合 [0181] These batteries, charging and discharging current charge voltage at 100 mA 4.2 V, subjected to the charge-discharge cycle test at a discharge end voltage 25V, as well as measuring the charge and discharge capacity in the first cycle, the discharge capacity after 500 cycles the measured proportion of the discharge capacity of the 500th cycle to the discharge capacity at the first cycle
(%) をサイクル寿命として求めた。 (%) Was determined as the cycle life.

【0182】これらの電池の1サイクル目の充電、放電容量および500 サイクル後の放電容量とサイクル寿命を表12に示した。 [0182] charge the first cycle of these batteries, the discharge capacity and cycle life after discharge capacity and 500 cycles are shown in Table 12.

【0183】 [0183]

【表12】 [Table 12]

【0184】本発明の非水電解質二次電池は、Si粉末に付着させた元素が何れであっても、負極材料が炭素材である比較電池より極めて高い容量を示し、またサイクル寿命も高く、良好な結果であった。 [0184] non-aqueous electrolyte secondary battery of the present invention, be either an element which is attached to the Si powder, the anode material exhibits a very high capacity than the comparative battery is a carbon material, also the cycle life is high, It was a good result.

【0185】 [0185]

【発明の効果】本発明により、従来の炭素材からなる負極材料に比べて放電容量が非常に高く、サイクル寿命も According to the present invention, the discharge capacity as compared with the negative electrode material comprising a conventional carbon material is very high, the cycle life
80%以上と良好な非水電解質二次電池用負極材料を得ることができる。 80% good nonaqueous electrolyte secondary battery negative electrode material can be obtained. 従って、本発明はリチウムイオン二次電池を始めとする非水電解質二次電池の性能向上に寄与するものと期待される。 Accordingly, the invention is expected to improve the performance of the nonaqueous electrolyte secondary battery including a lithium ion secondary battery.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】図1(a) はガスアトマイズ法の装置を模式的に示す説明図、図1(b) はそのノズル部の拡大断面図である。 [FIG. 1 (a) is an explanatory view schematically showing an apparatus for gas atomizing method, 1 (b) is an enlarged sectional view of the nozzle portion.

【図2】単ロール急冷法の装置の1例を模式的に示す説明図である。 FIG. 2 is an explanatory view schematically showing one example of an apparatus of a single-roll quenching method.

【図3】図3(a) は、プラズマ回転電極法の装置の1例を模式的に示す説明図であり、図3(b) はその陽極の構造を示す説明図である。 [3] FIG. 3 (a), an example of a device of the plasma rotating electrode process is an explanatory view schematically showing, FIG. 3 (b) is an explanatory diagram showing the structure of the anode.

【図4】本発明に係る合金粒子の組織の1例を示す説明図である。 Is an explanatory diagram showing an example of structure of the alloy particles according to the present invention; FIG.

【図5】実施例で試験電池として作製した非水電解質二次電池の構造を示す断面図である。 5 is a cross-sectional view showing the structure of the manufactured nonaqueous electrolyte secondary battery as a test cell in Example.

【符号の説明】 DESCRIPTION OF SYMBOLS

11:アトマイズタンク、12:給湯管、13:ガスアトマイズノズル、15:ガス供給系、21:急冷ロール、22:溶湯タンディッシュ、23:タンディッシュノズル23、30:冷却装置、31:密閉チャンバー、32:陽極、33:陰極、 3 11: atomizing tank, 12: hot water supply pipe, 13: gas atomizing nozzle, 15: Gas supply system, 21: chill roll, 22: molten metal tundish, 23: tundish nozzles 23, 30: Cooling device, 31: sealed chamber, 32 : anode, 33: cathode, 3
21:ノズル、 322:電極部、 323:不活性ガス、 324: 21: nozzle, 322: electrode unit, 323: inert gas, 324:
冷却水、40:Si相粒、41:(NiSi 2 +NiSi)マトリックス相、42:NiSi 2相、1:電池ケース、2:封口板、3: Cooling water, 40: Si phase grains, 41: (NiSi 2 + NiSi ) matrix phase, 42: NiSi 2 phase, 1: battery case, 2: sealing plate, 3:
絶縁パッキン、4:極板群、5:正極板、6:負極板、 Insulating packing, 4: the electrode plate group, 5: the positive electrode plate, 6: negative electrode plate,
7:セパレータ、8:絶縁リング。 7: separator, 8: insulating ring.

───────────────────────────────────────────────────── フロントページの続き (72)発明者 島村 治成 大阪府門真市大字門真1006番地 松下電器 産業株式会社内 (72)発明者 岡村 一広 大阪府門真市大字門真1006番地 松下電器 産業株式会社内 (72)発明者 上仲 秀哉 尼崎市扶桑町1番8号 住友金属工業株式 会社エレクトロニクス技術研究所内 (72)発明者 阿部 賢 尼崎市扶桑町1番8号 住友金属工業株式 会社エレクトロニクス技術研究所内 (72)発明者 禰宜 教之 尼崎市扶桑町1番8号 住友金属工業株式 会社エレクトロニクス技術研究所内 ────────────────────────────────────────────────── ─── of the front page continued (72) inventor OsamuNaru Shimamura Osaka Prefecture Kadoma Oaza Kadoma 1006 address Matsushita Electric industrial Co., Ltd. in the (72) inventor Kazuhiro Okamura Osaka Prefecture Kadoma Oaza Kadoma 1006 address Matsushita Electric industrial Co., Ltd. the inner (72) inventor Uenaka Hideya Amagasaki Fuso-cho, No. 1 No. 8 Sumitomo Metal Industries, Ltd. Electronics technology in the Laboratory (72) inventor Ken Abe Amagasaki Fuso-cho, No. 1 No. 8 Sumitomo Metal Industries, Ltd. electronics technology within the Institute (72) inventor green onions Noriyuki Sumitomo Metal Industries, Amagasaki Fuso-cho, No. 1 No. 8 stock company electronics technology within the Institute

Claims (15)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 1または2以上のSi相粒と、このSi相粒を少なくとも部分的に包囲するSi含有固溶体又は金属間化合物の相とを含む合金粒子からなる非水電解質二次電池用負極材料であって、該合金粒子の平均粒径が0.1 μ 1. A one or more Si phase grains and, Si-containing solid solution or a non-aqueous electrolyte secondary battery negative electrode comprising an alloy particle containing a phase of an intermetallic compound at least partially surrounding the Si phase grains a material, an average grain size of the alloy particles 0.1 mu
    m以上、50μm以下であり、負極材料の5wt%以上、99 m or more and 50μm or less, or more 5 wt% of the negative electrode material, 99
    wt%以下をSi相粒が占める、非水電解質二次電池用負極材料。 The following wt% occupied Si phase grains, the negative electrode material for non-aqueous electrolyte secondary battery.
  2. 【請求項2】 Siを含む固溶体又は金属間化合物が、Si 2. A solid solution or an intermetallic compound containing Si has, Si
    と、長周期型周期表の2A族元素、遷移元素、3B族元素、並びにSiを除く4B族元素よりなる群から選ばれた少なくとも1種の元素とから構成される、請求項1記載の非水電解質二次電池用負極材料。 If, 2A group elements of the long form periodic table, transition elements, 3B group elements, and composed of at least one element selected from the group consisting of Group 4B elements other than Si, according to claim 1, the non-described anode material for aqueous electrolyte secondary battery.
  3. 【請求項3】 1または2以上のSi相粒と、このSi相粒を少なくとも部分的に包囲するSi含有固溶体又は金属間化合物の相とを含んでいる合金粒子からなる非水電解質二次電池用負極材料の製造方法であって、 合金粒子を構成する原料の溶融物を凝固速度が100 ℃/ Wherein one or more of Si phase grains and a non-aqueous electrolyte secondary battery comprising the Si phase grains from alloy particles and a phase of at least partially Si-containing solid solution or intermetallic compound surrounding a method of manufacturing a use negative electrode material, the solidification rate is 100 ° C. the melt of the raw materials constituting the alloy particles /
    秒以上となるように冷却して凝固させて、Si相粒とこれを少なくとも部分的に包囲するSi含有固溶体又は金属間化合物の相とを含む合金を形成する工程、を含むことを特徴とする、非水電解質二次電池用負極材料の製造方法。 Cooling and solidifying so that the second or higher, characterized in that it comprises a step, to form an alloy comprising a phase of Si phase particles and this Si-containing solid solution or intermetallic compound that at least partially surrounds the method of the negative electrode material for non-aqueous electrolyte secondary battery.
  4. 【請求項4】 該合金を該Si含有固溶体又は金属間化合物の固相線温度より10℃以上低い温度で熱処理する工程、 をさらに含む請求項3記載の非水電解質二次電池用負極材料の製造方法。 The 4. alloy of the Si-containing solid solution or intermetallic compound solidus step of heat treatment at a temperature lower 10 ° C. or higher than the temperature, the negative electrode material for a nonaqueous electrolyte secondary battery according to claim 3, further comprising a Production method.
  5. 【請求項5】 100 ℃/秒以上の速度での冷却が、アトマイズ法、ロール急冷法及び回転電極法よりなる群から選ばれた方法で行われる、請求項3または4記載の非水電解質二次電池用負極材料の製造方法。 5. A cooling at 100 ° C. / sec or faster is, atomizing method, performed by a method selected from the group consisting of a roll quenching method and a rotating electrode method, according to claim 3 or 4 non-aqueous electrolyte according two method of preparing a negative electrode material for the next cell.
  6. 【請求項6】 1または2以上のSi相粒と、このSi相粒を少なくとも部分的に包囲するSi含有固溶体又は金属間化合物の相とを含んでいる合金粒子からなる非水電解質二次電池用負極材料の製造方法であって、 Si金属又はSi相を含む合金の粉末の表面に、Siと固溶体又は金属間化合物を形成する元素を含む材料の付着層を形成する工程、および付着層を形成した粉末を、該固溶体又は金属間化合物の固相線温度より10℃以上低い温度で熱処理して、付着層の材料をSi含有固溶体又は金属間化合物に変化させる工程、を含むことを特徴とする、非水電解質二次電池用負極材料の製造方法。 6. one or more Si phase grains and a non-aqueous electrolyte secondary battery comprising the Si phase grains from alloy particles and a phase of at least partially Si-containing solid solution or intermetallic compound surrounding a method of manufacturing a use negative electrode material, the surface of the alloy powder containing Si metal or Si phase, the step of forming a deposit of a material containing an element which forms a Si solid solution or intermetallic compounds, and deposition layer the formed powder, and characterized in that it comprises heat-treated at solidus temperature than 10 ° C. or more lower temperature of the solid solution or intermetallic compound, process of changing the material of the adhesion layer to the Si-containing solid solution or intermetallic compound, a to, method of preparing a negative electrode material for non-aqueous electrolyte secondary battery.
  7. 【請求項7】 付着層の形成が、メッキ法又はメカニカルアロイング法により行われる、請求項6記載の非水電解質二次電池用負極材料の製造方法。 Formation of 7. deposited layer is performed by a plating method or a mechanical alloying method, a manufacturing method of the negative electrode material for a nonaqueous electrolyte secondary battery according to claim 6, wherein.
  8. 【請求項8】 製造された負極材料が5wt%以上、99wt 8. The negative electrode material produced is 5 wt% or more, 99 wt
    %以下のSi相粒を含み、合金粒子の平均粒径が0.1 μm % Include the following Si phase grains, the average grain size of the alloy particles is 0.1 [mu] m
    以上、50μm以下である、請求項3ないし7の何れかに記載の非水電解質二次電池用負極材料の製造方法。 Or more and 50μm or less, the production method of the negative electrode material for a nonaqueous electrolyte secondary battery according to any one of claims 3 to 7.
  9. 【請求項9】 Siを含む固溶体又は金属間化合物が、Si 9. solid solution or an intermetallic compound containing Si has, Si
    と、長周期型周期表の2A族元素、遷移元素、3B族元素、並びにSiを除く4B族元素よりなる群から選ばれた少なくとも1種の元素とから構成される、請求項3ないし8の何れかに記載の非水電解質二次電池用負極材料の製造方法。 If, 2A group elements of the long form periodic table, transition elements, 3B group elements, and composed of at least one element selected from the group consisting of Group 4B elements other than Si, of claims 3 to 8 method for producing a non-aqueous electrolyte secondary battery negative electrode material according to any one.
  10. 【請求項10】 Si金属又はSi相を含む合金の粉末を負極基板上に付着させて該基板上に粉末層を形成した後、 10. After formation of the powder layer to the powder of alloy containing Si metal or Si phase is deposited on the negative electrode substrate base plate,
    この粉末層に、Siと固溶体又は金属間化合物を構成する元素を含む材料をメッキした後、前記固溶体又は金属間化合物の固相線温度より10℃以上低い温度で熱処理を施して、該メッキを、Siを含む固溶体又は金属間化合物に変化させることを特徴とする、非水電解質二次電池用負極の製造方法。 This powder layer, after plating a material containing an element constituting the Si solid solution or intermetallic compound is subjected to a heat treatment at said solid solution or solidus temperature than 10 ° C. or more lower temperature of the intermetallic compound, the plating , and wherein the changing to a solid solution or an intermetallic compound containing Si, aqueous method for producing a negative electrode for a electrolyte secondary battery.
  11. 【請求項11】 Siを含む固溶体又は金属間化合物が、 11. solid solution or an intermetallic compound containing Si has
    Siと、長周期型周期表の2A族元素、遷移元素、3B族元素、並びにSiを除く4B族元素よりなる群から選ばれた少なくとも1種の元素とから構成される、請求項10記載の非水電解質二次電池用負極の製造方法。 And Si, 2A group elements of the long form periodic table, transition elements, 3B group elements, and composed of at least one element selected from the group consisting of Group 4B elements other than Si, according to claim 10, wherein method for producing a negative electrode for a nonaqueous electrolyte secondary battery.
  12. 【請求項12】 非水電解質と、リチウムを可逆的に吸蔵および放出することができる正極と負極を備えた非水電解質二次電池において、 該負極が請求項1または2記載の負極材料を含有することを特徴とする非水電解質二次電池。 Containing 12. A non-aqueous electrolyte, the nonaqueous electrolyte secondary battery comprising a positive electrode and a negative electrode capable of reversibly occluding and releasing lithium, a negative electrode material of the negative electrode according to claim 1 or 2, wherein non-aqueous electrolyte secondary battery characterized by.
  13. 【請求項13】 非水電解質と、リチウムを可逆的に吸蔵および放出することができる正極と負極を備えた非水電解質二次電池において、 該負極が請求項3ないし9の何れかに記載の方法により製造された負極材料を含有する負極であるか、又は請求項10若しくは11記載の方法により製造された負極であることを特徴とする非水電解質二次電池。 13. A non-aqueous electrolyte, in reversibly absorbing and non-aqueous electrolyte secondary battery comprising a positive electrode and a negative electrode capable of releasing lithium, negative electrode according to any one of claims 3 to 9 negative or where a non-aqueous electrolyte secondary battery which is a negative electrode produced by the method of claim 10 or 11, wherein containing the negative-electrode material produced by the method.
  14. 【請求項14】 該負極が、該負極材料に対して5wt% 14. negative electrode, 5 wt% with respect to the negative electrode material
    以上、80wt%以下の炭素材料を含有する、請求項12又は Above, containing 80 wt% or less of the carbon material, according to claim 12 or
    13に記載の非水電解質二次電池。 The non-aqueous electrolyte secondary battery according to 13.
  15. 【請求項15】 該正極がリチウム含有遷移金属化合物を活物質とするものであり、該非水電解質がリチウム塩を炭酸エステルを含む有機溶媒に溶かした溶液である、 15. the positive electrode is one that the lithium-containing transition metal compound as an active material, a solution non-aqueous electrolyte by dissolving lithium salt in an organic solvent containing a carbonic ester,
    請求項12ないし14の何れかに記載の非水電解質二次電池。 The non-aqueous electrolyte secondary battery according to any one of claims 12 to 14.
JP24901799A 1998-09-08 1999-09-02 Method for producing negative electrode material for non-aqueous electrolyte secondary battery and secondary battery Expired - Lifetime JP3562398B2 (en)