GB2536642A

GB2536642A - Epilatory compositions

Info

Publication number: GB2536642A
Application number: GB1504855.6A
Authority: GB
Inventors: Pope Alice; Cass Terry; Morris-Curtis Victoria
Original assignee: Reckitt Benckiser Brands Ltd
Current assignee: Reckitt Benckiser Brands Ltd
Priority date: 2015-03-23
Filing date: 2015-03-23
Publication date: 2016-09-28
Anticipated expiration: 2035-03-23
Also published as: MX2017012071A; RU2017134772A3; RU2704806C2; RU2017134772A; WO2016151314A1; EP3273931B1; ES2826873T3; US20210069090A1; AU2016238582B2; GB201504855D0; PH12017501724A1; AU2016238582A1; GB2536642B; EP3273931A1; US11439580B2; US20180064626A1

Abstract

An epilatory composition comprising an admixture of a hydrocarbon resin material and a mineral oil in weight ratio of 1.3:1 to 2.8:1, a particulate silica, and a polyethylene in the form of a homopolymer. The hydrocsrbon resin is preferably selected from poly(methylsytrene-co-indene), hydrogenated polycyclopentadiene resin, C5 C9 partially or fully hydrogenated hydrocarbon resin and hydrogenated styrene/methylstyrene/indene copolymer. The hydrocarbon is preferably hydrogenated styrene/methylstyrene/indene copolymer. The epilatory composition preferably comprises 55-70% wt/wt hydrocarbon resin. The polyethylene preferably has a molecular weight from 100 to 1000 mass units, and is preferably present in 0.1-5% wt/wt of the composition. The silica and the polyethylene are preferably present in a ratio between 16:1 and 2:3. The particulate silica is preferably present in 2% by weight of the composition. A preferred composition comprises 60-68.5 wt% of a hydrocarbon resin; 30-38.5 wt% of a mineral oil; 1-2 wt% of particulate silica; and 0.5-1 wt% of a polyethylene linear homopolymer. The composition has improved grip of a users hair, thereby leading to more efficient hair removal and increased ease of use.

Description

EPILATORY COMPOSITIONS

The present invention relates to an epilatory composition and its use.

Epilatory compositions formed of viscoelastic materials are well known. The viscoelastic materials may in certain embodiments be rosin-based. In other embodiments they may be sugar-based. A tackifier, such as colophony, may be M included to make them sticky.

In some products the epilatory compositions may be supplied in the form of strips, retained between cellophane or woven sheets. The cellophane sheets may have coatings of polyvinyl chloride, which acts as a barrier preventing the composition, or components of it, from migrating through the sheets; and also having the correct adhesive properties for use. In use, the user peels away one of the cellophane sheets, presses the 20 epilatory strip firmly onto the area to be plucked, then pulls one end of the remaining sheet sharply away from the area. The hairs trapped in the composition are removed from the treated area along with, optimally, all of the composition, still attached to the remaining backing 25 strip.

In an alternative approach a composition may be warmed, and then applied to the skin by means of a spatula or other applicator. Strips of fabric are then applied so that they adhere to the epilatory composition. The strips are then pulled sharply to remove the epilatory material, and hair, from the skin.

In both approaches the viscoelastic properties of the compositions are important. However this is particularly so in the case of the compositions supplied as strips, since these are applied to the skin at ambient temperature. At ambient temperature the compositions should be soft and pliable, such that they mould closely to the body shape. On the other hand they must not be so soft that they flow prior to use. When they are in place on the body and the user pulls the remaining backing M strip, applying a high frequency strain rate to the compositions, their elastic properties should predominate over their viscous properties.

There is a need for an epilatory composition having an 15 improved 'grip' of the user's hair thus leading to more efficient hair removal. In current compositions the grip' of the wax is sub-optimal and as a result care must be taken when removing the wax to ensure maximum efficacy.

In accordance with the present invention there is provided an epilatory composition comprising an admixture of a hydrocarbon resin material and a mineral oil in weight ratio of 1.3:1 to 2.8:1, particulate silica, and a polyethylene in the form of a homopolymer.

Preferably the ratio of hydrocarbon resin to mineral oil is 1.5:1 to 2.3:1. More preferably the ratio is 1.9:1 to 2.2:1. Most preferably the ratio is 1.9:1 to 1.95:1.

Preferably, however, the hydrocarbon resin is selected from poly(methylstyrene-co-indene), hydrogenated polycyclopentadiene resin, C5 -C9 partially or fully hydrogenated hydrocarbon resin, hydrogenated styrene/methyl styrene/indene copolymer. A more preferred resin is hydrogenated styrene/methyl styrene/indene copolymer.

Preferably the epilatory composition comprises from 55 -70% wt/wt of hydrocarbon resin material, preferably from 63 -68% wt/wt, more preferably 64 -66% wt/wt.

The mineral oil can be selected from the group consisting M of mineral oils, argan oils and castor oils. A preferred mineral oil is paraffin oil.

Typically, the composition comprises 25 -40% wt/wt of the mineral oil. More typically the amount is 30 -35 % 15 wt/wt. More typically, the amount is 32 -34% wt/wt.

The addition of a polyethylene in the form of a homopolymer to an epilatory composition with a resin mix and silica substantially improves the hair removal efficacy of the composition when compared to other polymers known in the art, for example polyisobutane or C1_4 polyalkylene. The efficacy is especially improved when the epilatory formulation is in a cold wax strip format. It has also been observed to improve the stability of the wax on strips, and the resistance to flow under warm conditions.

Preferably the polyethylene has a molecular weight from 100 to 1000, preferably from 250 to 800 more preferably from 300 to 600 unified mass units. This gives the advantage of ease of incorporation of the polyethylene into the hydrophobic particles of the invention by melting and blending. Polyethylene suitable for use in compositions of the invention is a substantially linear or non-branched polymer with the structure CH3CH2(CH2CH2)nCH2 CH3, where n is a mean number from 5 to 35, preferably from 8 to 15. Preferably at least 90% by weight of the polyethylene is linear or non-branched. A particularly preferred polyethylene is that sold under the registered trade name Performalene. Other suitable polymers include polybutene grades, ethylene and vinyl acetate, goovean fibre viscose, however performalene is preferred.

The polyethylene is typically present in an amount in the range 0.1% to 5% by weight of the composition. Preferably, 0.5% to 4.0%, more preferably 0.5% to 3.0% by weight of the composition. However, a particularly preferred amount is in the range 0.75% to 1.5%, such as around 1.0% by weight of the composition.

It is desirable that the ratio of the silica to polyethylene is in the range 16:1 to 2:3. Preferably the 20 ratio of silica to polymer or co-polymer is in the range 6:1 to 6:5. A particularly preferred ratio is in the range 2:1.

The matrix material is suitably a gel-like material with 25 adhesive properties.

The epilatory composition can be used in any suitable form such as a hot wax, a cold wax or as part of a cold wax strip. Preferably the epilatory composition is a so-called "cold" epilatory composition (that is, one which can be applied at ambient temperature without reheating).

Typically, the particulate silica is fumed silica. Preferably the particulate fumed silica is a colloidal material. Preferably it has particles of mean diameter 1200 nm, more preferably 5-100 nm, and most preferably 10-50 nm.

Preferably the particles are present in the matrix material in an amount of at least 0.5% wt/wt, more preferably at least 1.0% wt/wt, and most preferably at M least 1.5% wt/wt. Suitably they are present in an amount up to 10% wt/wt, preferably up to 8.0% wt/wt, and most preferably up to 6.0% wt/wt. It is particularly preferred that the particulate silica is present in an amount substantially about 2.0 by weight of the formulation.

Fumed silica is currently manufactured in a process that involves flame hydrolysis of silicon tetrachloride, in an oxy-hydrogen flame. It is a colloidal form of silica having silanol groups, able to participate in hydrogen bonding. Fumed silica typically comprises colloidal particles of mean diameter 1-200 nm. Preferably the fumed silica is of mean diameter 5-100 nm, more preferably 10-50 nm. The external surface area is typically in the range 15-360 m2/g. Fumed silicas are typically non-porous and thus have no internal surface area. They may be hydrophobic and of use in the present invention but preferred fumed silicas for use in the present invention are hydrophilic.

The epilatory composition may suitably comprise up to 40%, preferably up to 20%, of other components, which may include one or more of a natural wax, a fragrance, a polymer, an essential oil, a silicone oil, a colorant or an anti-oxidant.

In an embodiment there is provided an epilatory 5 composition comprising: a. 60 -68.5 wt% of a hydrocarbon resin; b. 30 -38.5 wt% of a mineral oil; c. 1 -2 wt% of a particulate silica; and d. 0.5 -1 wt8 of a polyethylene in the form of a linear homopolymer.

In an alternative embodiment the composition comprises: a. 64 -66 wt4 of a hydrocarbon resin; b. 31 -33 wtf of a mineral oil; c. 1 -2 wt4 of a particulate silica; and d. 0.8 -1.2 wtf of a polyethylene in the form of a linear homopolymer.

The composition can comprise: a. a hydrogenated styrene/methyl styrene/indene copolymer; b. a mineral oil; c. particulate silica; and d. a polyethylene in the form of a linear homopolymer wherein the ratio of the resin to paraffin oil is 1.9:1 to 1.95:1.

In an alternative embodiment the composition consists essentially of a. 60 -68.5 wt8 of a hydrogenated styrene/methyl styrene/indene copolymer; b. 30 -38.5 wt% of a mineral oil; c. 1 -2 wt8 of a particulate silica; and d. 0.5 -1.5 wt% of a polyethylene in the form of a linear homopolymer.

In an alternative preferred embodiment the composition 5 consists essentially of a. 64 -66 wt% of a hydrogenated styrene/methyl styrene/indene copolymer; b. 31 -33 wt% of a mineral oil; c. 1 -2 wt% of particulate silica; and d. 0.8 -1.2 wt% of a polyethylene in the form of a linear homopolymer.

In a more preferred embodiment the composition consists of a. 60 -68.5% of a hydrogenated styrene/methyl styrene/indene copolymer; b. 30 -38.59, of a paraffin oil; c. 1 -2' of particulate silica; d. 0.5 -1.5 wtc._, of a polyethylene in the form of a linear homopolymer; e. 0.1% of shea butter; and f. 0.6 -0.65% of a fragrance.

In an alternative more preferred embodiment the composition consists of a. 64 - 66-1 of a hydrogenated styrene/methyl styrene/indene copolymer; b. 31 -33% of a paraffin oil; c. 1 -2% of particulate silica; d. 0.5 -1.5 wt9, of a polyethylene in the form of a linear homopolymer; e. 0.1% of shea butter; and f. 0.6 -0.65% of a fragrance.

S

Suitably an epilatory composition comprising a hydrocarbon resin material, when formed into sheets and not under applied stress, is shape-stable for a period of 6 months at all temperatures in the range 20-50°C.

Suitably an epilatory composition comprising a hydrocarbon resin material, when formed into sheets and not under applied stress, is shape-stable for a period of 6 months at all temperatures in the range 20-50°C; whereas the M corresponding matrix material not containing any said particles, when formed into flat sheets and not under applied stress, flows under its own weight at least some temperatures in the range 20-50°C during a period of 6 months.

Suitably the epilatory composition is such that its elastic modulus exceeds its viscous modulus at all frequencies up to 0.1 rad/s at 50°C.

Preferably the elastic modulus of the epilatory composition exceeds its viscous modulus at all frequencies up to 1 rad/s at 50°C, more preferably at all frequencies up to 2 rad/s at 50°C.

Preferably at certain higher frequencies (representative of the rapid removal of the epilatory composition from the user's skin), the elastic modulus also exceeds the viscous modulus, at temperatures within the temperature range 2050°C.

Preferably the elastic modulus exceeds the viscous modulus (when measured at 35°C) at a frequency of at least 10,000 rad/s, more preferably at a frequency at least 5,000 rad/s.

Thus, preferably the epilatory composition is such that, 5 at ambient temperatures, at low frequencies of applied stress the elastic modulus exceeds the viscous modulus; at high frequencies of applied stress the elastic modulus exceeds the viscous modulus; and at moderate frequencies, in between, the viscous modulus exceeds the elastic M modulus. The epilatory composition in transit and storage corresponds to the low frequency condition, ard the non-viscous nature of the composition aids shape stability in storage and transit; the application of the epilatory composition to the skin corresponds to the moderate frequency condition, and the viscous nature of the composition aids application and good contact with hair and skin; and pulling the epilatory composition sharply from the skin corresponds to the high frequency condition, the non-viscous, glassy nature of the composition aiding effective hair removal. The transition between the low frequency condition and the moderate frequency condition is known as the gel point. The transition between the moderate frequency condition and the high strain rate condition is known as the glass transition.

The elastic modulus G' (sometimes known as the storage modulus) corresponds to the energy which can be stored and released by a bulk material. The viscous modulus G" (sometimes known as the loss modulus) corresponds to the 30 energy dissipated by a bulk material due to friction between its macromolecules when it is deformed.

G' = a. cos 5 G" = co sin 5 wherein do is the stress amplitude, yo is the strain amplitude and 5 is the out-of-phase coefficient.

The measurements quoted later are based on studies carried out into the rheology of the viscoelastic compositions in M order to obtain a better understanding of their adhesive behaviour and their suitability as epilatory materials. These studies involved subjecting the materials to dynamic investigations in which a sinusoidal strain at defined frequencies was applied to the materials and the resulting output force was measured. In these studies a stress control rheometer was used, the SR rheometer commercially available from the company Rheometrics, using parallel plate geometry of 25 ram in diameter. The output force was found to include an in-phase elastic component G'and an out-of-phase viscous component G". The output force can be expressed as follows.

o -go sin (to + -go cos5 sin to + co cos5 costo where co is the test frequency and t is the time.

Within the linear stress-strain domain of the material G' is desirably lower than G" at moderate frequency 30 oscillation in order to prevent the material cracking and to ensure that the material has strong adhesion at the material/hair interface. The values of G' and G" at moderate frequency oscillation are a measure of how readily the material wets the hairs. Moderate frequency oscillation is a long time process and corresponds to the time when the material is being applied to the skin. The lower values of G' and G" at this moderate frequency, the better the material wets the hairs. Thus the hairs become well embedded in the material in a very short time (ie the time needed for spreading the material on the skin). However G' should be higher than G" at high frequency oscillation (which mimics the action of the user in M rapidly pulling the strip from the body) in order to remove hairs efficiently. Also, at low frequency oscillation, or no oscillation, G' is preferably higher than G", in accordance widi this invention, in order to obtain the benefit of enhanced stability, even when warm.

The definitions given herein refer to stresses applied to the material within its linear stress-strain domain, which may typically be up to a few thousand Pa.

By ensuring that the epilatory composition satisfies the above parameters, it can be readily applied to the skin at body temperature, yet it is very efficient at removing hairs from the skin and, surprisingly, the user experiences less pain.

References in this specification to a material not under applied stress are to a material in the form of a flat sheet, resting on a horizontal surface.

Whilst we are not bound by any theory, we believe that the composition of the present invention has increased efficacy as a result of an improvement in the coating of the individual's hair.

If wished the epilatory composition of the present invention may be provided in a container, from which the user removes it using, for example, a spatula or an 5 applicator fitted to the container, and applies it to the skin. A fabric can then be used to pull the applied material in one piece from the skin. Alternatively, and preferably, the epilatory composition is supplied in the form of strips, sandwiched between sheets, for example of M cellophane, or paper or another non-woven material. In use, one sheet is removed from a strip of epilatory composition and that strip is then applied to the skin with the remaining sheet uppermost. The end of that sheet is grasped and pulled sharply, to remove the strip of 15 epilatory composition from the skin, along with hairs with which it is in contact.

In accordance with a further aspect there is provided an epilatory product, comprising epilatory strips formed of an epilatory composition as defined herein, the epilatory strips being sandwiched between sheets which are peelable from the strips.

In accordance with a further aspect there is provided a 25 method of epilation, using a composition or product of the invention.

The invention will now be further described, by way of example with reference to the accompanying Figure which 30 illustrates fibre removal speeds of compositions of the present application.

Example 1 L3

Standard Name Function Percentage Petroleum Hydrocarbon Resin Epilatory Agent 64.5116 White Mineral Oil Solvent 31.7744 Fumed Silica Rheology Modifier 2.0000 Polyethylene Rheology Modifier 1.0000 Shea Butter Cosmetic Active 0.1000 Fragrance Fragrance 0.6140 Total 100.00 The formulation can be made in the following way: The mineral oil is heated to about 100°C at which point the resin is added slowly with stirring to form a uniform mixture. Polyethylene is then added with stirring until a homogeneous mixture is formed. Silica is added and stirred until homogenous. Shea butter and premix are then added and the resulting mixture is left to cool for 24 hours. At that time the wax is heated until free flowing and subsequently homogenized.

Figure 1 illustrates a graph that plots the fibre removal 15 speed of an example composition of the present invention (R1100) and an example composition of the prior art (benchmark).

As can be seen the required removal speed for the example of the present application is significantly slower than that of the prior art. From this it can be concluded that the compositions of the present application have improved grip over the prior art.

An advantage of the present invention is that there is provided an epilatory composition having improved grip of a user's hair such that the composition having a more efficacious mode of action.

A further advantage of the compositions of the present invention is that as a result of their improved grip/adherence the compositions can be used more quickly than those compositions which have poorer grip/adherence thus requiring a longer period of time to become effective.

Further modifications and improvements can be made without departing from the scope of the invention described herein.

Claims

CLAIMS: 1. An epilatory composition comprising an admixture of a hydrocarbon resin material and a mineral oil in weight ratio of 1.3:1 to 2.8:1, particulate silica, and a polyethylene in the form of a homopolymer.
2. An epilatory composition as claimed in claim 1 wherein ratio of hydrocarbon resin to mineral oil is 1.5:1 to 2.3:1.
3. An epilatory composition as claimed in claim 2 wherein the ratio is 1.9:1 to 2.2:1.
An epilatory composition as claimed in claim I or claim 2 wherein the ratio is 1.9:1 to 1.95:1.
5. An epilatory composition as claimed in any of the previous claims wherein the hydrocarbon resin is selected from poly(methylstyrene-co-indene), hydrogenated polycyclopentadiene resin, 05 09 partially or fully hydrogenated hydrocarbon resin, hydrogenated styrene/methyl styrene/indene copolymer.
An epilatory composition as claimed in claim 5 wherein the resin is hydrogenated styrene/methyl styrene/indene copolymer.
7. An epilatory composition as claimed in any of the preceding claims wherein the epilatory composition comprises from 55 -70% wt/wt of hydrocarbon resin material.
8. An epilatory composition as claimed in claim 7 wherein the epilatory composition comprises from 63 68% wt/wt of hydrocarbon resin material.
9. An epilatory composition as claimed in claim 8 wherein the epilatory composition comprises from 64 66% wt/wt of hydrocarbon resin material.
10. An epilatory composition as claimed in any of the preceding claims wherein the polyethylene has a molecular weight from 100 to 1000 unified mass units.
11. An epilatory composition as claimed in claim 10 wherein the polyethylene has a molecular weight of 250 to 800 unified mass units.
12. An epilatory composition as claimed in claim 11 wherein the polyethylene has a molecular weight of from 300 to 600 unified mass units.
13. An epilatory composition as claimed in any of the preceding claims wherein the polyethylene is present in an amount in the range 0.1% to 5%.
14. An epilatory composition as claimed in claim 13 wherein the polyethylene is present in an amount in the range 0.5% to 3.0% by weight of the composition.
15. An epilatory composition as claimed in claim 13 or claim 14 wherein the polyethylene is present in an amount in the range 0.75% to 1.5% by weight of the composition.
16. An epilatory composition as claimed in any of claims wherein the ratio of the silica to polyethylene is in the range 16:1 to 2:3.
17. An epilatory composition as claimed in claim 16 wherein the ratio of silica to polyethylene is in the range 6:1 to 6:5.
18. An epilatory composition as claimed in either claims 16 or claim 17 wherein the ratio of silica to polyethylene is 2:1.
19. An epilatory composition as claimed in any of the preceding claims wherein the particulate silica is present in an amount substantially about 2.0% by weight of the composition.
20. An epilatory composition as claimed in any of the preceding claims comprising: a. 60 -68.5 wt% of a hydrocarbon resin; b. 30 -38.5 wt% of a mineral oil; c. 1 -2 wt7 of a particulate silica; and d. 0.5 -1 wt% of a polyethylene in the form of a linear homopolymer. 25
21. An epilatory composition as claimed in claim 20 wherein the the composition comprises: a. 64 -66 wt'8 of a hydrocarbon resin; b. 31 -33 wt% of a mineral oil; c. 1 -2 wtc of a particulate silica; and d. 0.8 -1.2 wt'8 of a polyethylene in the form of a linear homopolymer.
22. An epilatory composition as claimed in any of claims 1 -19 wherein said composition comprises: a. a hydrogenated styrene/methyl styrene/indene copolymer; b. a mineral oil; c. particulate silica; and d. a polyethylene in the form of a linear homopolymer wherein the ratio of the resin to paraffin oil is 1.9:1 to 1.95:1.
23. An epilatory compositon as claimed in any of claims 1 -19 wherein the the composition consists essentially of a. 60 -68.5 wt% of a hydrogenated styrene/methyl styrene/indene copolymer; b. 30 -38.5 wt% of a mineral oil; c. 1 -2 wt% of a particulate silica; and d. 0.5 -1.5 wt% of a polyethylene in the form of a linear homopolymer.
24. An epilatory compositon as claimed in claim 23 wherein the composition consists essentially of a. 64 -66 wt% of a hydrogenated styrene/methyl styrene/indene copolymer; b. 31 -33 wt% of a mineral oil; c. 1 -2 wt% of particulate silica; and d. 0.8 -1.2 wt% of a polyethylene in the form of a linear homopolymer.
25. An epilatory composition as claimed in claim 24 wherein the composition consists of a. 60 -68.5% of a hydrogenated styrene/methyl styrene/indene copolymer; b. 30 -38.53 of a paraffin oil; c. 1 -2% of particulate silica; d. 0.5 -1.5 wt:, of a polyethylene in the form of a linear homopolymer; e. 0.1?_ of shea butter; and f. 0.6 -0.65 of a fragrance.M
26. An epilatory composition as claimed in claim 25 wherein the composition consists of a. 64 -661 of a hydrogenated styrene/methyl styrene/indene copolymer; b. 31 - of a paraffin oil; c. 1 -2?, of particulate silica; d. 0.5 -1.5 wt% of a polyethylene in the form of a linear homopolymer; e. 0.1% of shea butter; and f. 0.6 -0.65; of a fragrance.