FR2526222A1 - Method for manufacturing bundles of glass fibers, resulting in beam and a multichannel plate comprising application, including photomultipliers - Google Patents

Method for manufacturing bundles of glass fibers, resulting in beam and a multichannel plate comprising application, including photomultipliers Download PDF

Info

Publication number
FR2526222A1
FR2526222A1 FR8307335A FR8307335A FR2526222A1 FR 2526222 A1 FR2526222 A1 FR 2526222A1 FR 8307335 A FR8307335 A FR 8307335A FR 8307335 A FR8307335 A FR 8307335A FR 2526222 A1 FR2526222 A1 FR 2526222A1
Authority
FR
France
Prior art keywords
tubes
kind
characterized
polygon
smaller number
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
FR8307335A
Other languages
French (fr)
Other versions
FR2526222B1 (en
Inventor
John Treagus Balkwill
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Varian Medical Systems Inc
Original Assignee
Varian Medical Systems Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to US37453582A priority Critical
Application filed by Varian Medical Systems Inc filed Critical Varian Medical Systems Inc
Publication of FR2526222A1 publication Critical patent/FR2526222A1/en
Application granted granted Critical
Publication of FR2526222B1 publication Critical patent/FR2526222B1/en
Application status is Expired legal-status Critical

Abstract

<P>CHACUN DES FAISCEAUX QUI SONT ASSEMBLES EN PARALLELE ET COMPRIMES LES UNS CONTRE LES AUTRES POUR FORMER UN BARREAU AU COURS DU PROCESSUS DE FABRICATION DE PLAQUES A MICROCANAUX EST DE SECTION HEXAGONALE, ET DES FIBRES INDIVIDUELLES A PAROI DE CANAL PLUS EPAISSE SONT PLACEES AUX SOMMETS DE L'HEXAGONE AFIN D'EVITER L'ENDOMMAGEMENT DES FIBRES DES SOMMETS, QUI SONT EXPOSEES AUX FORCES EXTERIEURES LES PLUS GRANDES, AU COURS DE L'OPERATION D'ASSEMBLAGE.</P> <P> ALL BEAMS THAT ARE JOINED IN PARALLEL AND TABLETS EACH AGAINST OTHER TO FORM A BAR IN THE PROCESS OF MAKING PLATES MICRO IS SECTION ALLEN, AND INDIVIDUAL FIBER WALL CANAL PLUS THICK ARE PLACED TO SUMMITS OF THE hEXAGON TO pREVENT DAMAGE TO FIBER HEIGHTS, WHICH ARE eXPOSED TO EXTERNAL FORCES HIGHEST DURING THE ASSEMBLY OPERATION. </ P>

Description

La présente invention est relative aux plaques à microcanaux, et plus The present invention relates to microchannel plates, and more

particulièrement à un nouveau produit dans lequel des fibres de verre tubulaires sont assemblées de façon à former un faiseau d'un grand nombre de fibres constituant le barreau à partir duquel sont réalisées des plaques à microcanaux. particularly to a new product wherein the tubular glass fibers are assembled to form a faiseau a large number of fibers constituting the bar from which are formed microchannel plates. La fabrication des plaques à microcanaux comporte généralement l'opération d'assemblage d'un grand nombre de tubes de verre en parallèle et d'étiraoe longitudinal de oet assemblage afin d'en réduire l'épaisseur globale uh faisceau ainsi formé contient des milliers de fibres tubulaires élémentaires à dimensions de section sensiblement identiques, The manufacture of microchannel plates generally includes the assembly operation of a large number of glass tubes in parallel and longitudinal oet étiraoe assembly in order to reduce the overall thickness uh beam thus formed contains thousands elementary hollow fiber substantially identical cross-sectional dimensions,

et on réalise un barreau en assemblant de nouveau en paral- and sends a rod assembling again paral-

lèle d'une façon similaire une grande quantité de faisceaux et en les pressant les uns contre les autres Le barreau a lel in a similar way a large quantity of bundles and pressing them against each other The bar has

la forme d'une colonne, et on obtient des plaques à micro- the form of a column, and obtaining plates micro-

canaux en débitant transversalement un barreau en tranches minces. channels by debiting a rod transversely into thin slices. En vue d'améliorer la qualité d'image obtenue avec In order to improve the image quality obtained with

les plaques à microcanaux, il est souhaitable que les fibres élénen- the microchannel plates, it is desirable that the fibers élénen-

taires soient assemblées de manière aussi compacte et uni- tary are assembled as compactly and uni-

forme que possible, et ceci nécessite non seulement que les fibres élémentaires de chaque faisceau de fibres soienc form as possible, and this requires not only that the elementary fibers of each fiber bundle soienc

disposées uniformément, mais aussi que les faisceaux mutuel- evenly arranged, but also the beams mutually

lement adjacents s'adaptent exactement les uns aux autres de façon à remplir sans solution de continuité la totalité de la section transversale du barreau Pour cette raison, il est habituel de donner aux faisceaux de fibres la forme d'un prisme à base hexagonale de façon qu'ils puissent s'adapter les uns aux autres en formant une configuration LEMENT adjacent exactly fit to each other so as to perform seamless the entire cross section of the bar For this reason, it is customary to provide the fiber bundles in the form of a hexagonal prism so as to they can adapt to each other by forming a configuration

en nid d'abeilles A cet effet, il est naturellement es- honeycomb To this end, it is naturally es-

sentiel que chaque faisceau soit dimensionné avec précision, sensate that each beam is dimensioned precisely,

et en particulier que les angles de chaque sommet de l'hexa- and particularly that the angles of each peak of hexa-

gone soient définis avec exactitude afin qu'aucun vide ne subsiste aux endroits o des faisceaux adjacents sont pressés gone be defined accurately so that no void is left in places where adjacent beams are pressed

les uns contre les autres. against each other.

Les forces s'exerçant sur des arêtes vives sont cependant nécessairement plus grandes que celles s'exerçant sur des surfaces planes ou que les forces internes Au cours du processus de fabrication d'un barreau, par exemple, lors- que les faisceaux sont assemblés et pressés les uns contre les autres, les fibres individuelles situées aux arêtes ou à leur proximité se trouvent déformées en donnant un très faible écartement entre canaux Ainsi, de petits vides The forces acting on sharp edges are, however, necessarily greater than those exerted on flat surfaces or the internal forces In the manufacturing process of a bar, for example, lors- that the bundles are assembled and pressed against each other, the individual fibers located at the edges or their vicinity are distorted giving a very low channel spacing Thus, small voids

triangulaires risquent de se former aux endroits o les arê- Triangular may form in places where the are-

tes de trois faisceaux mutuellement adjacents devraient théo- your three mutually adjacent beams should theo-

riquement se confondre en un même point Dans une situation classique, de tels vides sont comblés par le verre de gainage des fibres et l'écartement entre les fibres des arêtes et les fibres adjacentes tend à être fortement réduit En fait, on trouve fréquemyentcinq ou six fibres à parois très minces en une même arête, et il est très courant d'assister à la disparition ou à la rupture de parois ically be confused at the same point In a typical situation, such voids are filled by the fiber cladding glass and the distance between the fiber edges and adjacent fibers tends to be greatly reduced In fact, there are six or fréquemyentcinq fibers with very thin walls in the same edge, and it is very common to attend the disappearance or breaking walls

de canaux après le processus d'attaque chimique pour la fabri- channels after the etching process for the manufacture

cation des plaques à microcanzux De wtels défauts aux arêtes donnent lieu à la création de points sombres et à d'autres cation plates microcanzux From wtels defects to the edges result in the creation of dark spots and other

défauts de la qualité de l'image. defects in image quality.

L'un des buts de la présente invention est de fournir des faisceaux de fibres d'uns configuration nouvelle One of the aims of the present invention is to provide fiber bundles of each new configuration

à partir desquels peuvent être fabriquées des plaques à ni- from which can be made of plates ni-

crocanaux à qualité d'image améliorée. crocanaux to improved image quality.

Un autre but de la présente invention est de fournir un procédé permettant d'éviter les ruptures ou manques de parois de canaux dans les plaques à microcanaux Another object of the present invention is to provide a method for avoiding breaks or gaps in the channel walls Microchannel plates

et des plaques à microcanaux fabriquées par ce procédé. and microchannel plates made by this method.

Les caractéristiques et avantages de l'invention The features and advantages of the invention

ressortiront plus amplement de la description détaillée qui emerge more fully from the detailed description

est donnée ci-après à titre d'exemple non limitatif en référence aux dessins annexés, sur lesquels: is given below by way of non limiting example with reference to the accompanying drawings, in which:

La Fig 1 est une vue en coupe d'une région d'arê- Figure 1 is a sectional view of a region of are-

te d'un faisceau de fibres de configuration conforme à la présente invention; you a configuration fiber bundle according to the present invention; et and

la Fig 2 est une vue en coupe d'une région d'arê- Figure 2 is a sectional view of a region of are-

te d'un autre faisceau présentant une configuration diffé- you another beam having a configuration differ-

rente conforme à la présente invention. rent according to the present invention.

Décrites sous une forme très rudimentaire, les plaques à microcanaux selon la présente invention sont obtenues en découpant transversalement un barreau en tranches Described in a very rudimentary form, the microchannel plates according to the present invention are obtained by cutting transversely a sliced ​​rod

minces, ce barreau étant essentiellement formé par un assem- thin, this bar being essentially formed by an assembled

blage en parallèle de faisceaux de fibres dont chacun con- wiring in parallel fiber bundles each of which con-

tient deux types de fibres individuelles disposées selon une holds two types of individual fibers arranged in a

configuration prédéterminée. predetermined configuration.

Ces deux types de fibres individuelles ont le même diamètre extérieur, et un grand nombre d'entre elles sont assemblées de façon compacte parallèlement les unes aux autres de telle façon que l'on obtienne le plus grand nombre Both types of individual fibers have the same outside diameter, and a large number of them are assembled compactly in parallel with each other so as to obtain the largest number

de celle-ci par unité de surface de la section du faisceau. thereof per unit area of ​​the beam's section.

Vu que toutes les fibres individuelles ont le même diamètre extérieur, ceci signifie que leurs centres de section forment Since all the individual fibers have the same outside diameter, this means that their centers form section

un réseau uniforme de triangles équilatéraux au sein de cha- a uniform network of equilateral triangles in Cha-

que faisceau On donne de préférence aux faisceaux un profil de that beam is given preferably to a beam profile

section en hexagone régulier, de sorte qu'ils puissent s'adap- section regular hexagon, so that they can adapt

ter les uns aux autres sans laisser de vide entre eux lors- ter to each other without leaving a gap between them lors-

qu'ils sont assemblés, chaque groupe de trois faisceaux mutuel- they are assembled, each group of three beams mutually

lement adjacents se réunissant théoriquement en un même point (dénommé arête multiple) de sorte que d'une part on obtienne une structure de faisceaux en nid d'abeilles sur toute la section du barreau, mais que d'autres part les fibres LEMENT adjacent theoretically bringing together at the same point (referred to as multiple edge) so that one hand is obtained a structure beams honeycomb over the entire section of the bar, but on the other hand the fibers

individuelles appartenant à des faisceaux différents se pré- individual belonging to different beams pre-

sentent aussi en couches continues et uniformes le long des limites définissant les faisceaux Des groupes de faisceaux présentant d'autres profils de section, tels que des profils en triangle équilatéral et en losange, peuvent donner le also feel continuous layers and uniform along the boundaries defining the beam bundles groups having other sectional profiles such as profiles equilateral triangle and diamond can give the

même résultat, mais le profil de section hexagonal est pré- same result, but the hexagonal section profile is pre-

férable en raison du fait que les fibres individuelles situées aux arêtes vives et à proximité de celles-ci sont facilement endommagées lorsque les faisceaux sont assemblés et pressés les uns contre les autres pour former un barreau. preferable due to the fact that the individual fibers located at sharp edges and near these are easily damaged when the beams are joined and pressed against each other to form a bar. Il n'y a pas de limitation stricte quant au nombre de fibres individuelles qui sont assemblées pour former un faisceau Si sa section est un hexagone régulier dont chaque côté contient N fibres individuelles, le nombre total de fibres individuelles contenues dans un tel faisceau sera N = 3 N 2 3 N + 1 Si N est trop grand ou trop petit, le There is no strict limitation on the number of individual fibers which are assembled to form a bundle If its cross section is a regular hexagon in which each side contains N individual fibers, the total number of individual fibers in such a beam will be N = 3 N 2 3 N + 1 If N is too large or too small, the

rendement de fabrication et/ou la qualité d'image sont sus- manufacturing yield and / or image quality are sus-

ceptibles d'en souffrir, et la difficulté d'obtenir des cou- ceptibles to suffer, and the difficulty of obtaining LYING

ches continues est susceptible de devenir grande Des valeurs de N de l'ordre de plusieurs milliers ou davantage ongoing tasks is likely to become greater Des N in the range of values ​​of several thousand or more

sont généralement préférables. are generally preferable.

Dans une forme de réalisation de la présente in- In one embodiment of the present in-

vention comportant au total 2437 fibres individuelles (c'est- vention having a total of 2437 individual fibers (that is

à-dire avec N = 29) pour chaque faisceau, six de ces 2437 i.e. with N = 29) for each beam, six of these 2437

fibres individuelles ont un diamètre de canal considérable- Individual fibers have a diameter considerably channel

ment plus petit Par conséquent, comme toutes les fibres in- ment smaller Therefore, as every fiber in-

dividuelles ont le même diamètre extérieur,-ces six fibres individuelles ont des parois de canal plus épaisses et elles sont donc moins sujettes à casser ou à être endommagés d'une autre manière Ces fibres sont placées à raison d'une par arête de l'hexagone, o les forces extérieures agissant sur le faisceau dividuelles have the same outside diameter, -these six individual fibers have thicker channel walls and are therefore less prone to break or be damaged otherwise These fibers are placed one for each edge of the hexagon, where the external forces acting on the beam

sont à considérer comme étant les plus grandes. be considered as being the biggest.

La Fig 1 est une vue en coupe d'une région d'arête d'un faisceau 10 réalisé conformément à ce mode de réalisation de la présente invention Une fibre spécialeil et des fibres Figure 1 is a sectional view of an edge region for a beam 10 made in accordance with this embodiment of the present invention A spécialeil fiber and fiber

ordinaires 12 qui ont le même diamètre extérieur sont assem- ordinary 12 have the same outer diameter are assembled

blées parallèlement les unes aux autres de façon compacte blies parallel to each other in a compact manner

afin que le faisceau 10 contienne le plus grand nombre pos- so that the beam 10 contains the greatest number pos-

sible de fibres il et 12 par unité de surface de sa section. sible fibers it and 12 per unit area of ​​its section.

Les fibres spéciales et ordinaires sont visibles sur la Fig 1 en raison du fait que les fibres ordinaires 12 ont un plus The special and ordinary fibers are visible in Figure 1 due to the fact that ordinary fibers 12 have a

grand diamètre de canal (ou une paroi de canal plus mince). large channel diameter (or a thinner channel wall).

Conformément à ce mode de réalisation, une fibre spéciale 11 occupe chaque arête hexagonale du faisceau, toutes les fibres restantes étant des fibres normales 12 En d'autres termes, il est fait appel à 2431 fibres individuelles de In accordance with this embodiment, a special hexagonal fiber 11 occupies each edge of the beam, all of the remaining fibers being natural fibers 12 In other words, it is resorted to 2431 individual fibers of

type ordinaire et à 6 fibres spéciales pour former un fais- ordinary type, 6 special fibers to form a fais-

ceau. CWater. Les fibres spéciales 11 et les fibres ordinaires The special fibers and ordinary fibers 11

12 peuvent être obtenues à partir de tubes en verre iden- 12 can be obtained from glass tubes identical

tiques Des tubes en verre d'environ 34,3 mm de diamètre extérieur et d'environ 3,8 mm d'épaisseur de paroi, par exemple, sont amenés par étirage à environ 0,76 mm de diamètre extérieur, une tige de verre d'âme d'environ 22,9 mm de diamètre étant utilisée pour obtenir une fibre normale et une tige de verre d'âme plus mince d'environ ticks glass tubes of approximately 34.3 mm outside diameter and about 3.8 mm wall thickness, for example, are caused by stretching at approximately 0.76 mm in outer diameter, a glass rod core of approximately 22.9 mm in diameter is used to obtain a natural fiber and a core glass rod thinner about

19 mm de diamètre pour obtenir une fibre spéciale. 19 mm diameter to obtain a special fiber.

Des faisceaux dont chacun présente la configura- Beams each having the configurations

tion représentée par la Fig 1 sont ensuite tassées étroi- tion shown in Fig 1 are then packed narrowness

tement les unes parallèlement aux autres pour former un barreau de façon à ne laisser théoriquement subsister aucun espace vide sur toutes les limites (non représentées) définissant le barreau Ceci fait venir en contact mutuel les arêtes de trois faisceaux mutuellement adjacents si les faisceaux sont précisément conformes en concordance exacte avec la configuration décrite Après assemblage d'une grande quantité de faisceaux de façon compacte pour former un barreau, celui-ci est débité transversalement en tranches minces par n'importe quel procédé classique Les plaques ment each parallel to the other to form a rod so as to leave theoretically exist no empty space on all boundaries (not shown) defining the bar This brought in mutual contact edges of three mutually adjacent beams if the beams are precisely conform in exact concordance with the configuration described After assembly of a large amount of compact beams to form a rod, the latter is charged transversely into thin slices by any conventional method plates

à microcanaux ainsi obtenues sont évasées et attaquées chi- microchannel thus obtained are flared and attacked chi-

miquement afin d'en accroître la surface ouverte relative, cally in order to increase the relative open area,

puis laquées et revêtues de minces couches d'autres maté- then lacquered and coated with thin layers of other mate-

riaux, tels que Mg O, Si O et Si O 2, afin d'éviter le refou- rials, such as Mg O, SiO and SiO 2, in order to avoid refou-

lement de particules chargées lorsque la plaque à micro- LEMENT of charged particles when the plate microwave

canaux est, par exemple, utilisée dans un tube photomul- channels is, for example, used in a tube photomul-

tiplicateur Ainsi, une plaque à microcanaux selon la présente invention comporte une surface sensiblement plate composée de régions hexagonales qui s'adaptent étroitement tiplicateur Thus, a microchannel plate according to the present invention comprises a substantially flat surface composed of hexagonal regions which fit closely

les unes aux autres en constituant uniformément une con- to each other by uniformly forming a con-

figuration en nid d'abeilles, chaque hexagone représentant la section d'un faisceau de fibres comportant des fibres spéciales à paroi de canal plus épaisse à ses arêtes et des fibres normales étroitement assemblées partout ailleurs honeycomb figuration, each hexagon representing the section of a fiber bundle having special fiber thicker channel wall at its edges and natural fibers closely assembled elsewhere

en couches uniformes. in uniform layers.

Les fibres spéciales Il à paroi plus épaisse sont plus résistantes vis-àvis des forces extérieures et ont pour effet d'augmenter l'écartement entre canaux Ainsi, non seulement les parois des canaux peuvent être empêchées de se briser lorsque ces fibres sont tassées et pressées en un barreau, mais Les fibres des arêtes peuvent aussi résister plus facilement à l'opération d'évasement et à The special fibers to thicker wall are more resistant vis-à-vis the external forces and the effect of increasing the channel spacing Thus, the channel walls not only can be prevented from breaking when the fibers are packed and pressed a bar, but the fibers of the edges can also resist more easily the flaring operation and

l'attaque chimique. chemical attack.

La Fig 2 est une vue en coupe montrant un autre mode de réalisation de la présente invention, qui ne diffère de celui qui a été décrit précédemment qu'en ceci qu'il est placé trois fibres spéciales il' au lieu d'une Figure 2 is a sectional view showing another embodiment of the present invention which differs from that which has been described previously in this it is placed three special fibers it 'instead of a

en chacune des six arêtes du faisceau de fibres à struc- in each of the six edges of the fiber bundle to struc-

ture hexagonale Ainsi, chaque faisceau contient 2419 fibres ordinaires 12 ' et 18 fibres spéciales il', si N = 29 hexagonal ture Thus, each bundle contains 2419 ordinary fibers 12 'and 18 special fibers it', if N = 29

comme précédemment Lorsque de tels faisceaux sont assem- as previously When such beams are assembled

blés et pressés en un barreau, on trouve généralement neuf fibres spéciales groupées à chaque arête multiple Ce mode de réalisation a pour avantage de conférer une plus grande résistance mécanique aux arêtes, o les parois des canaux sont le plus susceptibles de se rompre Par contre, des groupes d'un nombre plus grand de fibres spéciales à diamètre de canal plus petit tendent à affecter de façon néfaste les paramètres de visualisation de la plaque à wheat and pressed into a bar, typically found nine special fibers grouped at each multiple ridge This embodiment has the advantage to confer a greater strength to the edges, where the channel walls are most likely to rupture By against, groups of a greater number of special fibers smallest channel diameter tend to adversely affect the plaque visualization settings

canaux multiples. multiple channels.

En résumé, on vient de décrire la présente In summary, just described this

invention en n'en considérant que quelques modes de réali- invention not considering that some modes réali-

sation La description est cependant à considérer comme tion Description is however to be considered

illustrative et non pas comme limitative Par exemple, le nombre N défini plus haut peut être choisi dans un large domaine de valeurs Les faisceaux n'ont pas nécessairement besoin d'être de section hexagonale, cette solution étant illustrative and not as limiting, for example, the number N defined above may be selected from a wide range of values ​​beams do not necessarily need to be hexagonal, this solution being

cependant préférée D'autres profils polygonaux sont à con- however preferred Other polygonal profiles are con-

sidérer comme compris dans le cadre de la présente inven- sider as included within the scope of the present invention

tion Les dimensions de section des fibres individuelles peuvent aussi être modifiées librement en fonction des effets désirés En outre, bien que les deux types de fibres tion sectional dimensions of the individual fibers can be freely changed depending upon the desired effects In addition, although the two types of fibers

individuelles décrits plus haut aient été rendu discerna- individual described above were made discerna-

bles par leur diamètre intérieur, leur canal n'a pas néces- ble by their inner diameter, their channel has not neces-

sairement besoin d'être de section circulaire La seule obligation est que les fibres spéciales aient des parois de canal plus épaisses, et qu'elles soient de ce fait plus ily need to be circular section The only requirement is that the special fibers have thicker channel walls, and are therefore more

robustes que les fibres ordinaires. robust than conventional fibers.

Claims (10)

REVENDICATIONS
1 Faisceau de fibres, caractérisé en ce qu'il comprend un grand nombre de tubes cylindriques ( 12) d'un premier genre et un nombre plus petit de tubes cylindrique ( 11) d'un second genre, lesdits tubes du premier et du second genre étant d'un même diamètre extérieur et étant groupés de façon compacte en parallèle de façon à former sensiblement un prisme à profil de section en polygone convexe lesdits tubes du premier genre ( 12) ayant des parois de canal plus minces que lesdits du second genre ( 11), et au moins l'un desdits tubes du second genre ( 11) étant présent en chaque One fiber bundle, characterized in that it comprises a large number of cylindrical tubes (12) of a first kind and a smaller number of cylindrical tubes (11) of a second kind, said tubes of the first and second type being of the same outer diameter and being grouped compactly in parallel so as to form substantially a sectional profile prism convex polygon said tubes of the first kind (12) having thinner walls than said channel of the second kind (11), and at least one of said tubes of the second kind (11) being present in each
sommet dudit polygone. top of said polygon.
2 Faisceau selon la revendication 1, caractérisé 2 Beam according to claim 1, characterized
en ce que lesdits tubes ( 11,12 > sont en verre. in that said tubes (11,12> are glass.
3 Faisceau selon la revendication 2, caractérisé 3 Beam according to Claim 2, characterized
en ce que ledit polygone est un hexagone régulier. in that said polygon is a regular hexagon.
4 Faisceau selon la revendication 3, caractérisé 4 Beam according to Claim 3, characterized
en ce que ledit nombre plus petit est de six. in that said smaller number is six.
Faisceau selon la revendication 3, caractérisé en ce que ledit nombre plus petit est de dix-huit, et en ce que trois desdits tubes du second genre ( 11) sont présents Beam according to claim 3, characterized in that said smaller number is eighteen, and in that three of said tubes of the second kind (11) are present
en chaque sommet dudit hexagone. at each apex of said hexagon.
6 Plaque à microcanaux présentant une surface frontale sensiblement plate, ladite plaque étant caractérisée en ce qu'elle comprend une multiplicité de segments assemblés 6 microchannel plate having a substantially flat end face, said plate being characterized in that it comprises a plurality of assembled segments
de façon compacte les uns aux autres, chaque segment présen- compactly to each other, each segment présen-
tant une surface polygonale, qui fait partie de ladite sur- as a polygonal surface which is part of said over-
face frontale, chaque segment comprenant un grand nombre de tubes ( 12) en verre cylindriques d'un premier genre et un nombre plus petit de tubes ( 11) en verre cylindriques d'un second genre qui présentent des parois de canal plus épaisses que lesdits tubes du premier genre, lesdits tubes du premier et du second genre ayant un même diamètre extérieur et étant groupés ensemble de façon compacte en parallèle dans la direction perpendiculaire à ladite surface polygonale, et l'un au moins desdits tubes du second genre étant présent front face, each segment comprising a plurality of tubes (12) in cylindrical glass of a first kind and a smaller number of tubes (11) cylindrical glass of a second kind which have thicker walls than said channel the first type tubes, said tubes of the first and the second kind having a same outer diameter and being grouped together compactly in parallel in the direction perpendicular to said polygonal surface, and at least one of said tubes of the second kind being present
en chaque sommet dudit polygone. at each vertex of said polygon.
7 Plaque à microcanaux selon la revendication 6, caractérisée en ce que ledit polygone est un hexagone. 7 microchannel plate according to claim 6, characterized in that said polygon is a hexagon. 8 Plaque à microcanaux selon la revendication 7, 8 microchannel plate according to claim 7,
caractérisée en ce que ledit nombre plus petit est de six. characterized in that said smaller number is six.
9 Plaque à microcanaux selon la revendication 7, 9 microchannel plate according to claim 7,
caractérisée en ce que ledit nombre plus petit est de dix- characterized in that said smaller number is ten-
huit et en ce que trois desdits tubes du second genre sont eight and in that three of said tubes of the second kind are
présents en chaque sommet dudit hexagone. present in each apex of said hexagon.
Procédé pour la fabrication d'un faisceau de fibres caractérisé en ce qu'il comprend l'opération consistant à assembler de façon compacte en parallèle un grand nombre de tubes en verre ( 12) cylindriques d'un premier genre et un nombre plus petits de tubes en verre ( 11) cylindriques d'un second genre, lesdits tubes du second genre présentant le même diamètre extérieur et des parois de canal plus ".naisses que lesdits tubes du premier genre, A method for producing a fiber bundle characterized in that it comprises the operation of assembling compactly in parallel a large number of glass tubes (12) cylindrical of a first kind and a smaller number of glass tubes (11) cylindrical of a second kind, said tubes of the second kind having the same outer diameter and channel walls more ".naisses that said tubes of the first kind,
lesdits, tube S du premier et du second genres étant as- said, S tube of the first and second kinds being as-
semblés de telle façon sous forme de prisme à profil de section en polygone convexe que l'un au moins desdits tubes ( 11) du second genre soit présent en chaque-sommet dudit polygone. seem such as a sectional profile prism convex polygon that at least one of said tubes (11) of the second type is present in each-vertex of said polygon. 11 Procédé selon la revendication 6, caractérisé en ce que ledit polygone est un hexagone régulier et en ce 11 A method according to claim 6, characterized in that said polygon is a regular hexagon and in that
que ledit nombre plus petit est de dix-huit. said smaller number is eighteen.
12 Procédé pour la fabrication de plaques à microcanaux comprenant les opérations de fabrication de faisceau x de fibres à profil de section en polygones convexe et de formation d'un barreau par assemblage compact en parallèle et compression desdits faisceaux les uns contre les autres caractérisé en oe que ladite opération de fabrication de faisceaux cnpre l'opération consistant à assembler de façon compacte en parallèle un grand nombre de tubes ( 12) en verre cylindriques d'un premier genre et un nombre plus petit de tubes ( 11) en verre cylindriques d'un second genre, lesdits tubes du second genre présentant le même diamètre extérieur et des parois de canal plus petites que lesdits tubes du premier genre, lesdits tubes du premier et du second genre étant assemblés de telle façon que l'un au moins desdits tubes du 12 A method for the manufacture of microchannel plates against comprising the operations of manufacturing sectional profile beam x fiber convex polygons and of forming a rod with compact assembly and compression of said beams parallel to each other characterized in oe said harness making operation CNPRE the operation of assembling compactly in parallel a large number of tubes (12) in cylindrical glass of a first kind and a smaller number of tubes (11) in cylindrical glass of a second kind, said tubes of the second kind having the same outer diameter and smaller channel walls that said tubes of the first kind, the said tubes of the first and second kind being assembled such that at least one of said tubes
second genre soit présent en chaque sommet dudit polygone. second type is present in each corner of said polygon.
13 Procédé selon la revendication 12, caractérisé en ce qu'il comprend en outre l'opération de découpage dudit 13 A method according to claim 12, characterized in that it further comprises the operation of said cutting
barreau en tranches. Bar slices.
14 Procédé selon la revendication 12, caractérisé en ce que ledit polygone est un hexagone régulier et en ce 14 A method according to claim 12, characterized in that said polygon is a regular hexagon and in that
que ledit nombre plus petit est de dix-huit. said smaller number is eighteen.
FR8307335A 1982-05-03 1983-05-03 Method for manufacturing bundles of glass fibers, resulting in beam and a multichannel plate comprising application, including photomultipliers Expired FR2526222B1 (en)