DE7914233U1 - FIRE-RESISTANT PANEL ELEMENT - Google Patents

FIRE-RESISTANT PANEL ELEMENT

Info

Publication number
DE7914233U1
DE7914233U1 DE19797914233U DE7914233U DE7914233U1 DE 7914233 U1 DE7914233 U1 DE 7914233U1 DE 19797914233 U DE19797914233 U DE 19797914233U DE 7914233 U DE7914233 U DE 7914233U DE 7914233 U1 DE7914233 U1 DE 7914233U1
Authority
DE
Germany
Prior art keywords
magnesium oxychloride
layer
plate element
foam
fire
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE19797914233U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
VKI Rheinhold and Mahla AG
Original Assignee
VKI Rheinhold and Mahla AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by VKI Rheinhold and Mahla AG filed Critical VKI Rheinhold and Mahla AG
Priority to DE19797914233U priority Critical patent/DE7914233U1/en
Publication of DE7914233U1 publication Critical patent/DE7914233U1/en
Expired legal-status Critical Current

Description

VKI Reinhold & Mahla AG, MannheimVKI Reinhold & Mahla AG, Mannheim

15. Mai 1979May 15, 1979

Je/SchoJe / Scho

Eeuerbeständiges PlattenelementTax-resistant plate element

Die Neuerung betrifft ein feuerhemmendes bzw. feuerbeständiges Plattenelement, z. B. ein Wand- bzw. Deckenelement für Gebäude, insbesondere für Wohnhäuser und Fabrikhallen.The innovation concerns a fire-retardant or fire-resistant one Plate element, e.g. B. a wall or ceiling element for buildings, especially for residential buildings and Factory halls.

Feuerbeständige Vielschichtplatten, dia zum Brandschutz eingesetzt werden, sind bekannt. Diese oft aus mehreren Schichten bestehenden Platten sind zwar unbrennbar, bringen jedoch in vielen Fällen nicht die gewünschten Feuerwiderstandszeiten. Auch ist die mechanische Festigkeit dieser feuerbeständigen Platten oft so niedrig, daß Blechplatten als Deckschichten verwendet werden müssen. Das Verankern dieser Schichten stellt ein weiteres Problem bei diesem Konstruktionsprinzip dar, da im Brandfall die stark unterschiedlichen Ausdehnungskoeffizienten der verschiedenen Materialien zu Ablösungen führen. Da die Verbindung der Blechdeckschichten mit den feuerbeständigen Schichten nicht allein über Klebstoffe bewerkstelligt werden kann, wurden komplizierte Anker bzw. Verklammerungen erforderlich. Fire-resistant multilayer panels, which are used for fire protection, are known. These panels, which often consist of several layers, are non-flammable, but in many cases do not provide the desired fire resistance times. The mechanical strength of these fire-resistant plates is also often so low that sheet metal plates have to be used as cover layers. The anchoring of these layers poses a further problem with this construction principle, since in the event of a fire the widely differing expansion coefficients of the various materials lead to detachment. Since the connection of the sheet metal cover layers to the fire-resistant layers cannot be achieved using adhesives alone , complicated anchors or brackets were required.

RM 424RM 424

Aufgabe der vorliegenden Neuerung war es daher, eine leichte und unbrennbare Platte zu schaffen, die in ihrer Feuerwiderstandszeit einstellbar ist und eine solche mechanische Festigkeit besitzt, daß ihr Einsatz im verbeugenden konstruktiven Brandschutz ermöglicht wird.The task of the present innovation was therefore to create a light and incombustible panel that can be used in their fire resistance time is adjustable and one has such mechanical strength that it can be used in preventive structural fire protection.

Diese Aufgabe wird nach der Neuerung durch ein Plattenelement, bei dem mindestens eine Schicht des mehrschichtigen Elementes aus einer Magnesiumoxichloridschaumschicht besteht, gelöst.According to the innovation, this task is achieved by a plate element in which at least one layer of the multilayer element made of a magnesium oxychloride foam layer exists, solved.

Das mehrschichtige Plattenelement besteht aus zwei, drei oder gegebenenfalls noch weiteren Schichten. Bei der zweischichtigen Ausführungsform ist die Magnesiumoxichloridschaumschicht die Außenschicht, die der zu erwartenden Brandseite zugekehrt ist. Bei der dreiteiligen Ausgestaltung des Plattenelementes ist es möglich, die Magnesiumoxichloridschaumschicht als Innenschicht oder auch als beide Außenschichten anzuordnen, je nach Einsatzzweck. Die Magnesiumoxichloridschicht wird mit einer oder mehreren anorganischen Stützschichten mit oder ohne Faser-Verstärkung unlösbar verbunden. Als anorganische Stützschicht können z.B. glasfaserverstärkter Beton, glasfaserverstärkter Magnesiumoxichlorid-Beton oder ein mit Magnesiumoxichlorid-Beton gebundenes Faser/Glimmer-Gemisch sowie die üblichen Materialien, wie Fertigbeton, Stahlbeton o.a.The multilayer plate element consists from two, three or possibly further layers. In the two-layer embodiment, the magnesium oxychloride foam layer is the outer layer facing the expected fire side. With the three-part Design of the plate element, it is possible to use the magnesium oxychloride foam layer as an inner layer or can also be arranged as both outer layers, depending on the intended use. The magnesium oxychloride layer is covered with an or several inorganic support layers with or without fiber reinforcement inextricably linked. As an inorganic support layer can e.g. glass fiber reinforced concrete, glass fiber reinforced magnesium oxychloride concrete or one with magnesium oxychloride concrete Bound fiber / mica mixture as well as the usual materials such as precast concrete, reinforced concrete, etc.

eingesetzt werden. Auch mit Wasserglas gebundene Materialien sind als anorganische Stützschichten einsetzbar. Vorzugsweise werden jedoch Glasfasermatten oder Gewebe, die mit Magnesiumoxichlorid-Beton imprägniert sind als Stützschicht eingesetzt. Da die Deckschicht und das isolierende Dämm-Material bei dieser Ausführungsform z.Teilcan be used. Materials bound with water glass can also be used as inorganic support layers. Preferably However, fiberglass mats or fabrics that are impregnated with magnesium oxychloride concrete are used as a support layer used. Since the cover layer and the insulating insulating material in this embodiment z.Teil

RM 424RM 424

aus dem gleichen Material bestehen, ist es möglich,
auf die noch nicht ausreagierte Magnesiumoxichlorid-Glasfaser-Stützschicht den Magnesiumoxichloridschaum aufzutragen. Durch diese Maßnahme wird ein sehr guter | Deckschicht-Kernverbund erreicht. fjconsist of the same material, it is possible
to apply the magnesium oxychloride foam to the not yet fully reacted magnesium oxychloride glass fiber support layer. This measure results in a very good | Top layer core composite achieved. fj

Bex anderen anorganischen Stützschichten wird der IWith other inorganic support layers, the I

noch nicht anreagierte Magnesiumoxichloridschaum ψ Magnesium oxychloride foam that has not yet reacted ψ

auf die Stützschicht aufgebracht, eine zusätzliche
Verklebung ist auch hier nicht erforderlich.applied to the support layer, an additional one
Gluing is not necessary here either.

Die anorganischen Stützschichten sind so dimensioniert,
daß sie nach dem Verbund mit der Magnesiumoxichloridschicht die gewünschte Festigkeit bewirken. Die ;: gewünschte Feuerwiderstandsdauer wird durch die Dicke
der Magnesiumoxichloridschicht erreicht. Die so aufge- ,The inorganic support layers are dimensioned so that
that after bonding with the magnesium oxychloride layer they produce the desired strength. The ; : desired fire resistance period is determined by the thickness
reached the magnesium oxychloride layer. Who are so excited

bauten Elemente sind unbrennbar. Ibuilt elements are incombustible. I.

Nach diesem Verfahren lassen sich jedoch nicht nur |However, this method does not only allow |

Platten, sondern auch plattenförmige Formteile in fPlates, but also plate-shaped molded parts in f

dem vorstehend beschriebenen Aufbau herstellen, da f produce the structure described above, since f

es für den Brandschutz unerheblich ist, welche Kontur | die Konstruktionsteile aufweisen. Die Dicke der einge- § setzten Magnesiumoxichloridschaumschicht muß jedoch <it is irrelevant for fire protection which contour | which have structural parts. However, the thickness of the magnesium oxychloride foam layer used must be <

ausreichend dimensioniert sein, um im Brandfalle ge- : nügend Feuerwiderstandszeit zu besitzen. Es ist auch
möglich, die Dicke dieser MagnesiumoxichloridschichtBe sufficiently dimensioned to have sufficient fire resistance time in the event of a fire. It is also
possible the thickness of this magnesium oxychloride layer

je nach den Erfordernissen innerhalb eines plattenförmigen Formteiles zu variieren.to vary depending on the requirements within a plate-shaped molded part.

In besonders vorteilhafter Weise kann das Plattenelement,
entsprechend ästhetisch ausgestattet, z.B. als
Brüstungs- und/oder Verkleidungselement, also nicht
nur als tragendes Konstruktionselement, eingesetztIn a particularly advantageous manner, the plate element,
appropriately aesthetically equipped, e.g. as
Parapet and / or cladding element, so not
only used as a load-bearing construction element

RM 424RM 424

werden. Durch Zusatz von unbrennbaren Pigmenten, welche die Schaumstruktur nicht nachteilig beeinflussen, kann dem Plattenelement eine ansprechende Färbung gegeben werden.will. By adding non-flammable pigments, which do not adversely affect the foam structure the plate element can be given an appealing color.

Der Magnesiumoxichloridschaum wird in bekannter Weise durch Vermischen von Magnesiumchlorid, Magnesiumoxid bzw. gebranntem Magnesit, Wasser, Netzmitteln und gegebenenfalls versteifenden Zusatzmitteln hergestellt und dieses Gemisch durch Verschäumer, z.B. Wasserstoffperoxid und gegebenenfalls Katalysatoren verschäumt.The magnesium oxychloride foam is made in a known manner by mixing magnesium chloride and magnesium oxide or burnt magnesite, water, wetting agents and optionally stiffening additives this mixture is foamed by foaming agents, e.g. hydrogen peroxide and possibly catalysts.

Vorzugsweise enthält die Magnesiumoxichloridschaumschicht noch feinteilige Glasfaser, die auf den Schaum noch stärker verfestigend wirkt und im Brandfall eine Rissebildung verhindert.Preferably the magnesium oxychloride foam layer contains still finely divided glass fiber, which has an even stronger solidifying effect on the foam and, in the event of a fire, a Prevents cracking.

Die Herstellung der neuerungsgemäßen plattenförmigen EIemante ist sehr einfach, da die Beschichtung mit Magnesiumoxichloridschaum z.B. sowohl auf feuchten als auch trockenen Beton aufgebracht werden kann und mit diesem ohne zusätzliche Befestigungsmittel, wie Schrauben, BolzenThe production of the plate-shaped egg shell according to the innovation is very easy, because the coating with magnesium oxychloride foam, for example, on both damp and dry concrete can be applied and with this without additional fasteners, such as screws, bolts

u. ä. eine feste Verbindung eingeht. In solchen Fällen erhalten die Betonteile nur die statisch erforderliche Dimensionierung,während die aufgebrachte Magnesiumoxichloridschicht bzw. die aufgebrachten Magnesiumoxichloridschichten den notwendigen Brandschutz bewerksteiligen. Die Magnesiumoxichloridschaumschicht bzw. Schichten werden im allgmeinen also wesentlich dünner und leichter ausgeführt werden können als dieand the like enters into a permanent connection. In such cases, the concrete parts only receive what is statically necessary Dimensioning while the applied layer of magnesium oxychloride or the applied layers of magnesium oxychloride provide the necessary fire protection. The magnesium oxychloride foam layer or layers are therefore generally essential can be made thinner and lighter than that

RM 424RM 424

jeweils notwendige anorganische Stützschicht. Schon im festen Bauverbund bestehende Hohlplatten können in einfacher Weise durch Einführen des Magnesiumoxichloridschaums als Kern zu Brandschutzelementen umgerüstet werden.inorganic support layer required in each case. Hollow slabs that are already in the solid building network can converted into fire protection elements in a simple manner by introducing the magnesium oxychloride foam as the core will.

Durch Armierungen und gegebenenfalls Befestigungsanker in der Ummantelung des Plattenelementes lassen sich in vorteilhafter Weise besonders stabile plattenförmige Elemente schaffen, die sicher festlegbar bzw. zu befestigen sind.Reinforcements and, if necessary, fastening anchors in the sheathing of the plate element can be used in advantageously create particularly stable plate-shaped elements that can be securely fixed or fastened are.

Die Neueruncr soll anhand der folgenden Beispiele und Figuren noch näher erläutert werden:The new company should be based on the following examples and Figures are explained in more detail:

RM 424RM 424

Beispiel 1:Example 1:

In eine fertig geformte und ausgehärtete glasfaserverstärkte Betonschale (1) wird Magnesiumoxichloridschaum (2) in noch nicht ausreagiertem Zustand eingetragen. Die Dicke dieser Schaumschicht ist unterschiedlich.Magnesium oxychloride foam is placed in a molded and hardened glass fiber reinforced concrete shell (1) (2) entered in a not yet fully reacted state. The thickness of this foam layer is different.

Beispiel 2:Example 2:

Die glasfaserverstärkte Magnesiumoxichloridschaumschicht (l) wird in das Werkzeugnegativ (2) laminiert. Gleichzeitig wird die anorganische Stützschicht (3) in gleicher Weise auf das Werkzeugpositiv (4) laminiert. Die Magnesiumoxichloridschaumschicht (5) wird auf die noch nicht anreagierte Deckschicht (l) aufgetragen. Nach dem Schließen der Werkzeaghälften (2) und (4) und Aushärten der Deckschichten (l) und (3) läßt sich das feuerbeständige Element entformen.The glass fiber reinforced magnesium oxychloride foam layer (l) is laminated into the tool negative (2). At the same time, the inorganic support layer (3) laminated in the same way on the positive tool (4). The magnesium oxychloride foam layer (5) is on the Top layer (l) that has not yet reacted is applied. After closing the tool halves (2) and (4) and curing of the cover layers (1) and (3), the fire-resistant element can be removed from the mold.

RM 424RM 424

Claims (7)

Schutzansprüche:Protection claims: 1) Mehrschichtiges feuerbeständiges Plattenelement, dadurch gekennzeichnet, daß mindestens eine Schicht aus Magnesiumoxichloridschaum besteht.1) Multi-layer fire-resistant plate element, characterized in that at least one layer consists of magnesium oxychloride foam. Z) Plattenelement nach Anspruch 1, dadurch gekennzeichnet, daß eine oder beide Außenschichten aus Magnesiumoxichloridschaum bestehen. Z) plate element according to claim 1, characterized in that one or both outer layers consist of magnesium oxychloride foam. 3) Plattenelement nach Anspruch 1, dadurch gekennzeichnet, daß die Innenschicht aus Magnesiumoxichloridschaum besteht.3) plate element according to claim 1, characterized in that the inner layer made of magnesium oxychloride foam consists. 4) Plattenelement nach einem oder mehreren4) Plate element according to one or more der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß die anorganische tragende Stützschicht unlösbar mit der bzw. den Magnesiumoxichloridschaumschichten verbunden ist.of claims 1 to 3, characterized in that the inorganic load-bearing support layer is inextricably linked which is connected to the magnesium oxychloride foam layer (s). 5) Plattenelement nach einem oder mehreren der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß es unbrennbare Pigmente in der Magnesiumoxichloridschaumschicht enthält.5) Plate element according to one or more of the claims 1 to 4, characterized in that it contains incombustible pigments in the magnesium oxychloride foam layer. 6) Plattenelement nach einem oder mehreren der Ansprüche 1 bis 5, dadurch gekennzeichnet, daß die Magnesiumoxichloridschaumschicht feinteilige Glasfaser enthält.6) plate element according to one or more of claims 1 to 5, characterized in that the Magnesium oxychloride foam layer contains finely divided glass fibers. 7) Plattenelement nach einem oder mehreren der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß Armierungen bzw. Befestigungsanker in dem Plattenelement integriert sind.7) plate element according to one or more of claims 1 to 6, characterized in that Reinforcements or fastening anchors in the plate element are integrated. RM 424RM 424
DE19797914233U 1979-05-17 1979-05-17 FIRE-RESISTANT PANEL ELEMENT Expired DE7914233U1 (en)