DE4241042C1 - Composite brick or slab prodn. with ready-made decorative cover plate of silicate - by moulding on cement and/or lime compsn., pre-hardening and steam cure in autoclave. - Google Patents

Composite brick or slab prodn. with ready-made decorative cover plate of silicate - by moulding on cement and/or lime compsn., pre-hardening and steam cure in autoclave.

Info

Publication number
DE4241042C1
DE4241042C1 DE19924241042 DE4241042A DE4241042C1 DE 4241042 C1 DE4241042 C1 DE 4241042C1 DE 19924241042 DE19924241042 DE 19924241042 DE 4241042 A DE4241042 A DE 4241042A DE 4241042 C1 DE4241042 C1 DE 4241042C1
Authority
DE
Grant status
Grant
Patent type
Prior art keywords
characterized
method according
cover plate
concrete
lime
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE19924241042
Other languages
German (de)
Inventor
Emmo Dr Frey
Sigfried Peuker
Uwe Kraeft
Karl Dr Kroboth
Michael Dr Schmidt
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HeidelbergCement AG
Hebel AG
Original Assignee
HeidelbergCement AG
Hebel AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Grant date

Abstract

Prodn. of composite bricks or slabs (I), consisting of a support (II) made from a compsn. (III) contg. cement and/or lime and a ready-made decorative cover plate (IV) or silicate, involves moulding (III) in the plastic state in a mould contg. (IV). The novelty is that when (I) have reached the green stage strength of a cement concrete compsn. or a lime-sandstone compsn. has been pressed, they are hardened with steam under pressure in an autoclave at 150-230 deg. C. Pref. (III) consists of a normal, porous, glass fibre-reinforced or lightweight cement concrete mix or lime-sandstone mix. (IV) consists of natural stone contg. silicate, pref. granite, a ceramic tile or a glass plate. (V) is milk of lime or cement size, pref. applied to a layer of fibre or fabric.

Description

Die Erfindung betrifft ein Verfahren zur Herstellung von Verbundsteinen oder -platten, bestehend aus einem tragen den Element aus einer zement- und/oder kalkhaltigen Masse und einer vorgefertigten, dekorativen Deckplatte aus sili katischem Material, bei dem die zement- und/oder kalkhal tige Masse in plastischem Zustand an die Innenseite einer in einer Form angeordneten Deckplatte angeformt wird. The invention relates to a method for making composite stones or slabs, comprising a carrying the element from a cement and / or lime-containing mass and a prefabricated decorative cover plate sili katischem material, wherein the cement and / or kalkhal term mass is molded in a plastic state to the inside, arranged in the form of a cover plate.

Bei einem derartigen bekannten Verfahren zur Herstellung von Verbundsteinen oder -platten (FR 1 524 275) werden zunächst an der Innenseite der Deckplatte, die aus Natur stein, Steinzeug, Glas, Terrakotta bestehen kann, zwei Metallklammern befestigt. In such known processes for producing composite stone or plates (FR 1524275) are initially may be made on the inner side of the cover plate, the natural stone, stoneware, glass, terracotta, fastened two metal brackets. Die so vorbereitete Deckplatte wird dann in eine Form gestellt, die mit einer Porenbeton- Rohmischung gefüllt wird. The thus prepared cover plate is then placed in a mold which is filled with an aerated concrete crude mixture. Die Porenbeton-Rohmischung wird hierbei unmittelbar an die Innenseite der Deckplatte ange gossen, wobei der von der Innenseite vorstehende Teil der Metallklammern von der Porenbeton-Rohmischung umhüllt wird. The aerated concrete raw mix is ​​poured in this case directly on the inside of the cover plate being, which protruding from the inside portion of the metal brackets is encased in the aerated concrete crude mixture. Durch die Metallklammern soll eine sichere Verbindung zwischen dem aus Porenbeton bestehenden tragenden Element und der Deckplatte geschaffen werden. is to create a secure connection between the existing cellular concrete bearing member and the top plate through the metal clips. Die Haftzugfestig keit zwischen dem Porenbeton, der bei Umgebungstemperatur erhärtet, und der Innenseite der Deckplatte ist nämlich verhältnismäßig gering, so daß die Gefahr besteht, daß sich die Deckplatte von dem Porenbeton löst. The Haftzugfestig ness between the cellular concrete hardens at ambient temperature, and the inside of the cover plate is in fact relatively low, so that the danger exists that the cover plate of the aerated concrete dissolves. Diese Gefahr ist besonders bei Frosteinwirkung gegeben. This risk is particularly evident in frost. Durch die Me tallklammern, die aus rostfreiem Stahl bestehen müssen und daher teuer in der Herstellung sind, werden jedoch die Herstellungskosten des gesamten Verbundsteines oder der Verbundplatte wesentlich erhöht. By Me tallklammern that need to be made of stainless steel and are therefore expensive to manufacture, however, the production cost of the entire composite stone or the composite plate to be substantially increased. Es müssen nämlich an der Innenseite der Deckplatte Ausnehmungen vorgesehen wer den, in welche die Metallklammern eingreifen können. It must provided on the inside of the cover plate recesses who can, in which engage the metal brackets namely.

Außerdem ist es erforderlich, die Metallklammern in diese Ausnehmungen einzusetzen. Moreover, it is necessary to use the metal brackets in these recesses. Da die so vorbereiteten Deck platten anschließend in eine Form gebracht werden müssen, besteht außerdem die Gefahr, daß hierbei die Metallklam mern irgendwo anstoßen und sich hierdurch ungewollt wie der von der Deckplatte lösen oder zumindest verbogen wer den. Since the so prepared cover plates must then be placed in a mold, there is a danger that in this case the numbers Metallklam bump it and thereby inadvertently as the resolve of the cover plate or at least bent who the.

Der Erfindung liegt daher die Aufgabe zugrunde, ein Ver fahren zur Herstellung von Verbundsteinen oder -platten der eingangs erwähnten Art aufzuzeigen, durch welches eine Verbesserung der Verbindung, insbesondere der Haft zugfestigkeit, zwischen Deckplatte und tragendem Element erreicht wird, so daß Metallklammern oder dgl. entfallen können und damit die Herstellung vereinfacht wird. The invention is therefore based on the object, a Ver drive for producing composite stone or plates of the type initially mentioned to show by which an improvement of the connection, in particular the adhesive is tensile strength achieved between the cover plate and carrying member so that metal clips or the like. can be omitted and thus the manufacturing is simplified.

Dies wird nach der Erfindung dadurch erreicht, daß die Verbundsteine oder -platten nach dem Erreichen der Grün standsfestigkeit einer Betonmasse oder nach dem Anpres sen einer Kalksandsteinmasse einer Dampfdruckhärtung in einem Autoklaven bei Temperaturen von 150 bis 230° un terzogen werden. This is achieved according to the invention that the composite stones or plates after reaching the green strength of a mass of concrete or sand-lime brick according to the Anpres sen a mass of a Dampfdruckhärtung in an autoclave at temperatures of 150 to 230 ° be subjected un.

Überraschenderweise wird durch die Dampfdruckhärtung eine wesentlich höhere Haftzugfestigkeit zwischen dem tragenden Element und der Deckplatte erreicht, als dies bei einem Aushärten der zement- und/oder kalkhaltigen Masse bei Um gehungstemperatur der Fall ist. Surprisingly, a much higher tensile bond strength between the supporting member and the cover plate is achieved by the Dampfdruckhärtung than is in a hardening of the cement and / or lime-containing mass in order gehungstemperatur the case. Besonders bei Porenbeton wurde bei Anwendung der Dampfdruckhärtung eine wesentliche und unerwartete Erhöhung der Haftzugfestigkeit zwischen dem Porenbetonstein und der Deckplatte festgestellt. Particularly with aerated concrete a substantial and unexpected increase in the tensile bond strength between the cinder block and the cover plate was found when using the Dampfdruckhärtung. Auch wurde durch entsprechende Frost-Tau-Wechselversuche eine unerwartet hohe Frostbeständigkeit der Verbindung zwischen Porenbeton und Deckplatte beobachtet. Also, an unexpectedly high frost resistance of the connection between aerated concrete and cover plate was observed by appropriate freeze thaw resistance tests. Es wird vermutet, daß die hohe Haftzugfestigkeit dadurch erreicht wird, daß sich durch das Autoklavieren Calciumsilikathydrate bilden, die einen verbesserten Kontakt zu den aus silikatischem Mate rial bestehenden Deckplatten vermitteln. It is believed that the high tensile bond strength is achieved in that form by autoclaving calcium silicate hydrates, which provide an improved contact to the existing of silicate mate rial cover plates. Da mit dem erfin dungsgemäßen Verfahren eine hohe Haftzugfestigkeit erzielt wird, kann man auf Metallklammern zwischen Deckplatte und tragendem Element völlig verzichten. Since a high tensile bond strength is achieved with the method according OF INVENTION dung, can completely dispense with metal clips between the cover plate and carrying member. Hierdurch wird die Herstellung der Verbundsteine oder -platten wesentlich vereinfacht, und damit werden auch die Herstellungskosten gesenkt. In this way the production of the composite stones or slabs is considerably simplified and thus the manufacturing cost can be reduced.

Die DE 41 34 296 C1 (nachveröffentlicht) offenbart eine Verbundsteinplatte aus wenigstens zwei in verlegtem Zu stand übereinander angeordneten, im wesentlichen ganz flächig miteinander verbundenen Schichten, wobei die obere Schicht von einem Naturstein und die untere Schicht von einer Betonschicht gebildet ist. The DE 41 34 296 C1 (post-published) discloses a composite slab consisting of at least two when installed to stand superposed, substantially the entire surface interconnected layers, the top layer of a natural stone and the lower layer is formed by a concrete layer. Die groben Zuschlag stoffe der Betonschicht sind durch kantig geformten Splitt aus dem gleichen Natursteinmaterial wie die obere Schicht gebildet, die eine Granitplatte sein kann. The coarse aggregate of the concrete layer are formed by edged shaped chips of the same natural stone material as the upper layer, which may be a granite slab. Die obere und die untere Schicht können über eine die Erhö hung der Haftfähigkeit vermittelnde Zwischenschicht mit einander verbunden sein, wobei die Zwischenschicht von einem aus Zement, Quarzsand und Kunststoffmaterial be stehenden Bindemittel gebildet sein kann. The upper and the lower layer, the raised stabili hung the adhesion-promoting intermediate layer with each other to be connected, wherein the intermediate layer may be formed of one of cement, quartz sand and plastic material be stationary with a binder.

Aus der DE 39 21 779 A1 ist eine vorgefertigte, transpor tierbare und selbsttragende Platte, Wand oder Formteil bekannt, die einen Plattenkern aus Beton und auf der Vorder- und Rückseite aufgebrachte Fliesen oder Keramik platten aus Steingut oder Steinzeug aufweist. From DE 39 21 779 A1 a pre-fabricated, transported tierbare and self-supporting panel, wall or molding is known, the slabs a panel core made of concrete and on the front and back coated tiles or ceramic earthenware or stoneware having. Um eine wesentliche Verringerung der Stärke und des Gewichtes zu erreichen und ferner auch eine dauerhafte Befestigung von belasteten Gegenständen zu ermöglichen, ohne die gute Stabilität und die guten selbst tragenden Eigenschaften zu verschlechtern, sind auf beiden Seiten des mit geringer Stärke ausgebildeten Plattenkerns aus Beton zwischen Plat tenkern und Fliesen bzw. Keramikplatten dünne Haftvermitt lungsschichten mit darin eingebetteten Glasfasermatten oder Glasfasergittern vorgesehen. In order to achieve a substantial reduction in thickness and weight and also to permit a permanent attachment of loaded articles without deteriorating the good stability and the good self-supporting properties, are on both sides of the formed low-strength panel core made of concrete between Plat tenkern and tile or thin ceramic plates Haftvermitt lung layers provided with embedded glass fiber mats or glass fiber gratings. Zur Herstellung der Platte, Wand oder des Formteiles wird auf eine ebene, ein geschalte Fläche zunächst eine Schicht Fliesen oder dgl. mit der Glasur nach unten aufgelegt. To prepare the plate, wall, or a layer of the molding tiles or the like is on a level, a peeled surface initially. Launched with the glaze down. Danach wird auf die Rückseite der Fliesen die relativ flüssig angesetzte Haft vermittlungsschicht dünn aufgetragen. Then switching layer thinly applied to the back of the tiles the relatively liquid scheduled detention. Auf diese Haftver mittlungsschicht wird dann die Glasfasermatte aufgelegt und in die Haftvermittlungsschicht eingedrückt. the glass fiber mat is mediation layer to this adhesion promoter then placed and pressed into the adhesive layer. Auf die noch feuchte Haftvermittlungsschicht wird der Frischbeton für den Plattenkern dünn aufgetragen und darüber dann die übrigen Schichten in umgekehrter Reihenfolge. the fresh concrete for the core plate is thinly applied onto the still wet adhesive layer and then about the other layers in the reverse order. Nach dem Anklopfen oder Anrütteln der oberen Fliesenschicht erfolgt das Aushärten bei Umgebungstemperatur. After the call waiting or Anrütteln the top layer of tiles, curing takes place at ambient temperature.

Die DE 35 17 669 A1 beschreibt einen Baukörper, wie Mauer, Wand, Wand-, Fassaden-, Verbundplatte oder dgl., der wenig stens aus einem platten- oder wandartigen Porenbetonteil und einer Wärme-, Kälte- und Schall-Isolationsschicht ge bildet ist, welche beiden Teile durch eine Klebschicht auf Zementbasis miteinander flächig verbunden sind, wobei in der Klebschicht ein zähelastisches, metallfreies, korrosionsfestes Gewebe, z. The DE 35 17 669 A1 describes a building structure, such as masonry, wall, wall, facade, composite plate or the like., Which forms little least ge of a plate-like or wall-like aerated concrete part and a heating, cooling and sound-insulation layer is which two parts are connected by an adhesive layer on each other cement-based surface, wherein the adhesive layer in a viscoplastic, metal-free, corrosion-resistant fabric, z. B. aus Glasfasern, Keramikfa sern oder Kohlefasern, eingebettet ist. Is embedded as glass fibers, Keramikfa fibers or carbon fibers.

Aus der DE 32 02 817 A1 ist ein quaderförmiger, organischer Verbundstein, bestehend aus einem Calciumsilikathydratstein im Verbund mit einem anorganischen Dämmstoff geringer Roh dichte bekannt. From DE 32 02 817 A1, a cuboid, organic composite stone consisting of a lower Calciumsilikathydratstein in combination with an inorganic insulating material raw density is known. Der Dämmstoff bildet eine Schicht oder einen Kanal oder mehrere zueinander parallele Schichten oder Kanäle, die den Calciumsilikathydratstein durchziehen. The insulation material forms a layer or a channel or a plurality of mutually parallel layers or channels, run through the the Calciumsilikathydratstein. Der Verbundstein läßt sich z. The composite stone can be such. B. dadurch herstellen, daß man in den Hohlraum eines Kalksandstein-Rohlings eine expandier fähige anorganische Dämmstoff-Vorstufe einfüllt, die man expandieren läßt. B. be prepared by one fills an expander capable of inorganic insulating material precursor in the cavity of a sand-lime brick blank, which is allowed to expand. Anschließend werden der Kalksandstein und der Dämmstoff mit überhitztem Wasserdampf ausgehär tet. Then the sand-lime brick and insulation material with superheated steam are tet ausgehär.

Die DE-AS 23 30 796 beschreibt ein Verfahren zur Herstel lung von Fertigbauteilen aus Kunststeinen, insbesondere von Wandelementen. The DE-AS 23 30 796 describes a process for the manufacture of prefabricated components lung of plastic blocks, in particular of wall elements. Die vorzugsweise aus Calciumsilikat material bestehenden Kunststeinrohlinge, z. The preferably made of calcium silicate material artificial stone blanks, z. B. Kalksand steinrohlinge, werden dabei in eine Form nach einem vor gegebenen Muster eingelegt, wobei die sich berührenden Flächen mit einem Kleber oder Bindemittel, z. B. lime sand stone blanks, are thereby inserted into a mold for a given pattern before, wherein the contacting surfaces with an adhesive or binder, eg. B. mit Kalk milch, bestrichen werden. B. milk of lime, are coated. Anschließend wird der Baustein verband in der Form nachverdichtet und mit oder ohne Form einer Dampfdruckhärtung unterzogen. The block is then combined in the form of post-compressed and subjected, with or without the form of a Dampfdruckhärtung.

Schließlich ist aus der DE-AS 15 71 330 ein Verfahren zur Herstellung dampfgehärteter, kalksilikathydrat- bzw. kalk silikataluminathydratgebundener, gegebenenfalls poröser Granalien aus hydrothermalhärtbaren Granalien, bekannt, bei dem ein härtbares Gemisch in einem Autoklaven gleich zeitig granuliert und unter Dampfdruck vollständig ausge härtet wird. Finally, a method of preparation is known from DE-AS 15 71 330 steam hardened, kalksilikathydrat- or lime silikataluminathydratgebundener, optionally porous granules of hydrothermalhärtbaren granules known in which a curable composition equal granulated time in an autoclave, and completely under steam pressure is cured , Man erhält mit diesem Verfahren ausgehärtete, gegebenenfalls poröse Granalien, die als Bau- oder Zuschlag stoffe geeignet sind, in einem einzigen Arbeitsgang. with this process gives cured, optionally porous granules which are suitable as building materials or additives, in a single operation.

Die vorgenannten Druckschriften konnten jedoch die vorlie gende Erfindung nicht nahelegen, da jeweils nur Teilaspekte des erfindungsgemäßen Verfahrens betrachtet werden und sich hieraus auch kein Anhaltspunkt für eine Zusammenschau einzel ner Druckschriften ergibt. However, the above-mentioned documents could not suggest of the products contained restrictive invention, since only partial aspects of the inventive method are considered and from this also no indication of a synopsis indi vidual documents obtained.

Zur Durchführung des erfindungsgemäßen Verfahrens wird als plastische Masse, die später das tragende Element bildet, zum Beispiel eine Porenbeton-Rohmischung verwendet. To carry out the inventive process, the plastic mass which later forms the supporting element, for example, using a cellular concrete crude mixture. Diese kann Portlandzement und/oder andere Zemente mit üblicher Erhärtungsgeschwindigkeit und/oder rasch erhärtenden Schnellzement enthalten. This may contain Portland cement and / or other cements with conventional hardening speed and / or rapid setting quick-setting cement. Nachdem die Deckplatte in eine Form gebracht wurde, wird die Rohmischung in die Form gegossen und gewartet, bis der Porenbeton eine ausreichende Grünfe stigkeit erreicht hat, damit er aus der Form genommen werden kann. After the top plate was placed in a mold, the crude mixture is poured into the mold and wait until the aerated concrete has reached sufficient Grünfe stigkeit so that it can be removed from the mold. Das kann bei Verwendung von Schnellzement relativ rasch erfolgen. This can be done relatively quickly when using quick-setting cement. Es erfolgt dann die Dampfdruckhärtung in einem Autoklaven unter den beim Autoklavieren von Porenbeton übli chen Bedingungen. There is then the Dampfdruckhärtung in an autoclave under the übli when autoclaving porous concrete surfaces conditions. Nach der Dampfdruckhärtung liegt ein Ver bundstein oder eine Verbundplatte vor, bei der das dekorative Aussehen und die Wetterbeständigkeit der Verbundplatte mit den guten wärmedämmenden Eigenschaften von Porenbeton kombi niert sind. After a Dampfdruckhärtung Ver bund is stone or before a composite panel in which the decorative appearance and weather resistance of the composite panel with good thermal insulation properties of aerated concrete are combinatorial ned.

Unter Porenbeton wird hier vor allem sogenannter Gasbeton verstanden, bei dem die Poren durch Zugabe von Aluminium pulver gebildet sind. Under aerated concrete, especially of so-called gas concrete is meant in which the pores are formed by adding aluminum powder here. Anstelle von Gasbeton kann jedoch auch Schaumbeton verwendet werden. However, foam concrete can be used instead of gas concrete.

Das erfindungsgemäße Verfahren läßt sich auch für Normalbe ton, Glasfaserbeton oder Leichtbeton anwenden. The inventive method can also be applied for Normalbe ton, fiber concrete or lightweight concrete. Auch bei die ser Art von Beton muß die Grünstandsfestigkeit des Betons abgewartet werden, bevor die Form abgenommen und mit der Dampfdruckhärtung begonnen werden kann. Even with the ser type of concrete, the green strength of the concrete must be awaited before the mold removed and can be started with the Dampfdruckhärtung. Dieses kann bei Ver wendung von Schnellzement relativ rasch erfolgen. This can be done relatively quickly with Ver application of quick-setting cement. Wenn bei der Durchführung des Verfahrens als plastische Masse eine Kalksandstein-Rohmischung verwendet wird, dann hat diese nach dem Anpressen an die Innenseite der Deck platte eine ausreichende Standfestigkeit, so daß die Ver bundsteine oder -platten sofort nach dem Anpressen in den Autoklaven zur Dampfdruckhärtung gebracht werden können. If a sand-lime brick the raw mix is ​​used in carrying out the process as a plastic mass, this has after the pressing against the inside of the cover plate, a sufficient stability, so that the Ver composite stones or slabs immediately after pressing in the autoclave brought to Dampfdruckhärtung can be.

Zur Durchführung des Verfahrens werden zweckmäßig silikat haltige Naturwerksteinplatten verwendet. For performing the method containing natural stone slabs are advantageously used silicate. Hier hat sich be sonders Granit als geeignet erwiesen. Here be Sonder granite has been found suitable. Als silikathaltige Naturwerksteine kommen jedoch auch Diorit, Syenit, Gabbros, Vulkanite, Sandsteine, Gneise und Schiefer in Frage. As a siliceous stone material but also diorite, syenite, gabbros, volcanic rocks, sandstones, gneisses and slates come into question.

Als Deckplatte kann auch eine silikatische Keramikplatte oder eine Glasplatte verwendet werden. As a cover plate, a silicate ceramic plate or a glass plate can be used.

Gegebenenfalls kann es zweckmäßig sein, vor dem Angießen oder Anpressen der plastischen Masse auf die Innenseite der Deckplatte einen Haftvermittler aufzubringen, um die Haft zugfestigkeit noch zu verbessern. It may be appropriate to apply a bonding agent to the inside of the cover plate before the casting or pressing of the plastic mass to tensile strength further improve the adhesion. Besonders geeignet als Haftvermittler sind z. Particularly suitable as an adhesion promoter z. B. Kalkhydratmilch oder Zementleim. B. Kalkhydratmilch or cement.

Ferner kann es zweckmäßig sein, die Verbindung von Deck platte und tragendem Element dadurch zu verbessern, daß auf die Haftvermittlerschicht eine Faserschicht oder ein Gewebe angeordnet wird. Further it may be expedient, to improve the connection of cover plate and carrying member characterized in that a fibrous layer or a fabric is placed on the adhesive layer. Als Fasern für diese Faser- oder Gewebeschicht eignen sich vor allem Glasfasern, Metallfa sern oder gegebenenfalls auch Kokosfasern, oder andere Fasern. The fibers of this fiber or fabric layer mainly glass fibers, metal fibers or possibly coconut fibers, or other fibers are suitable. Weitere vorteilhafte Maßnahmen bei der Durchführung des Ver fahrens zur Herstellung von Verbundbausteinen und -platten sind in folgendem, anhand der bei liegenden Zeichnung erläu tert. Further advantageous measures for the implementation of the proceedings for manufacturing composite blocks and plates are in the following, with reference to the tert erläu lying in the drawing. Die Deckplatten können hierbei entweder gemäß Fig. 1 horizontal liegend oder gemäß Fig. 2 vertikal stehend in einer nicht dargestellten Form angeordnet sein. The cover plates can in this case in accordance with either Fig. 1 or lying horizontally as shown in FIG. 2 may be standing vertically arranged in a not-shown mold. Beide Möglichkeiten werden im Zusammenhang mit der Verwendung von Porenbeton beschrieben. Both possibilities are described in connection with the use of porous concrete.

Gemäß Fig. 1 werden mehrere Deckplatten 1 in horizontaler Stellung mit nach oben gerichteten Innenseiten 1 a auf den Boden einer nicht dargestellten Form gelegt. According to Fig. 1 a plurality of top plates 1 are placed on the bottom of a mold, not shown in the horizontal position with upwardly directed inner sides 1 a. Die Deckplat ten 1 werden dabei mit ihren Schmalseiten dicht an dicht angeordnet. The Deckplat th 1 are arranged with their narrow sides close together. In die Form wird dann die Porenbeton-Rohmischung, insbesondere eine Gasbeton-Rohmischung, die Aluminiumpulver als Treibmittel enthält, eingefüllt. is in the shape then the crude mixture aerated concrete, in particular a gas-concrete raw mixture containing aluminum powder as a propellant was charged. Die Porenbeton-Roh mischung kommt in innigen Kontakt mit den Innenseiten 1 a der Deckplatten 1 . The aerated concrete raw mixture comes into intimate contact with the inner surfaces 1a of the deck boards 1. Nachdem die Porenbeton-Rohmischung die erforderliche Grünstandsfestigkeit erreicht hat, können die Seitenwände der Form abgenommen werden. Once the aerated concrete raw mixture has reached the required green strength, the side walls of the mold can be removed. Mittels mehre rer vertikal geführter Schneiddrähte 2 und 3 kann der an gesteifte Porenbetonblock in eine der Anzahl und den Ab messungen der Deckplatten 1 entsprechende Anzahl von Ver bundsteinen oder -platten geschnitten werden. By means of several rer vertically guided cutting wires 2 and 3, the porous concrete block in a stiffened to the number and Ab of the cover plates measurements composite stones 1 corresponding number of Ver or cut sheet format. Die Schneid drähte 2 , 3 werden dabei so weit nach unten bewegt, bis sie die nach oben gerichteten Innenseiten 1 a der Deck platten erreicht haben. The cutting wires 2, 3 are moved so far down until they have reached the upwardly directed inner sides 1 a of the cover plates. Die Schnitte werden jeweils in denjenigen Bereichen geführt, die vertikal über den Rän dern der aneinandergrenzenden Deckplatten liegen. The sections are each guided in those regions which countries vertically above the knurled of the adjacent cover plates lie.

Damit die bei der Porenbetonherstellung üblichen Gießfor men verwendet und voll ausgenützt werden können, wird in die Formen zweckmäßig mehr Rohmischung eingefüllt, als zur Herstellung der Verbundsteine oder -platten er forderlich wäre. Thus the usual when the AAC production Gießfor can be used men and fully utilized in the forms appropriate more raw mix is ​​filled, as for the production of paving stones or slabs he was conducive. Es kann dann durch einen weiteren Schneiddraht 4 , der in horizontaler Richtung bewegbar ist, eine obere Schicht von Porenbetonsteinen oder -platten abgetrennt werden. It can then by a further cutting wire 4, which is movable in the horizontal direction, an upper layer of aerated concrete blocks or panels are separated. Diese in der oberen Schicht enthaltenen Porenbetonsteine oder -platten 5 weisen dann keine Deck platten auf und können nach dem Autoklavieren wie übliche Porenbetonsteine oder -platten verwendet werden. This porous concrete blocks or panels 5 included in the top layer then do not have to cover plates and can after autoclaving as conventional porous concrete blocks or plates are used.

Nachdem der Porenbeton auf diese Weise mittels der Schneid drähte 2 , 3 , 4 in einzelne Porenbetonsteine 5 und Verbund steine 6 aufgeteilt wurde, wird er auf dem Formboden ruhend in einen Autoklaven gebracht und dort bei Temperaturen zwi schen 150 und 230°C einer Dampfdruckhärtung unterworfen. Once the aerated concrete in this way wires by the cutting 2, 3, 4 in single porous concrete blocks 5 and composite stone was partitioned 6, it is brought resting in an autoclave on the mold bottom and there Zvi rule 150 and 230 ° C a Dampfdruckhärtung at temperatures subjected , Bei Gasbeton der Festigkeitsklasse GP2 mit einer Rohdichte von 0,5 kg/dm 3 wurde nach dem Autoklavieren zwischen der aus Granit bestehenden Deckplatte und dem Gasbeton eine Haftzugfestigkeit von 0,17 N/mm 2 festgestellt. In gas concrete of strength class GP2 having an apparent density of 0.5 kg / dm 3 an adhesive strength of 0.17 N / mm 2 was observed after autoclaving between the group consisting of granite cover plate and the gas concrete. Nach fünf undzwanzig Frost-Tau-Wechseln war die Haftzugfestigkeit überraschenderweise noch höher und lag bei 0,22 N/mm 2 . After five twenty-freeze thaw cycles, the tensile bond strength was surprisingly even higher and amounted to 0.22 N / mm 2. Man könnte gemäß Fig. 2 auch so verfahren, daß mehrere Deckplatten 1 in vertikaler Stellung in eine nicht darge stellte Form gebracht und dort durch entsprechende Halte mittel fixiert werden. Of FIG. 2 could be also possible to proceed so that a plurality of cover plates placed 1 in a vertical position in a non-turned Darge shape and be fixed there by means of appropriate holding medium. Es können jeweils zwei Deckplatten mit ihren Außenseiten aneinanderliegend in die Form ge stellt werden. Any two cover plates with their outer sides against one another ge into the mold are up. Zwischen den einander zugekehrten Innen seiten zweier benachbarter Deckplatten wird jedoch ein Zwischenraum belassen, dessen Breite B doppelt so groß ist wie die Breite der Porenbetonschicht des fertigen Verbundsteines bzw. der fertigen Verbundplatte. However, a gap is left between the mutually facing inner sides of two adjacent cover plates, whose width B is twice as large as the width of the porous concrete layer of the final composite stone or of the final composite sheet. In die Zwischenräume zwischen den einander zugekehrten Innen seiten der Deckplatten 1 wird anschließend die Porenbe ton-Rohmischung eingegossen. In the spaces between the mutually facing inner sides of the cover plates 1 the Porenbe ton crude mixture is then poured. Nach dem Erreichen der Grün standsfestigkeit werden dann mittels der vertikal ange ordneten Schneiddrähte 7 Schnitte ausgeführt, die jeweils in der Mitte jedes Zwischenraumes verlaufen. After achieving stability of the Green 7 cuts are then carried out by means of the vertically arranged cutting wires each extending in the middle of each gap. Man kann in der Form auch mehrere Deckplatten in Längsrichtung der Form hintereinander anordnen. It can be in the form of several cover plates arranged in the longitudinal direction of the mold in succession. Hierbei ist es jedoch zweckmäßig, zwischen den vertikalen Schmalseiten benach barter Deckplatten jeweils einen kleinen Spalt zu belas sen, der etwa der Dicke des Schneiddrahtes entspricht. However, in this case it is expedient Benach between the vertical narrow sides barter cover plates each sen to belas a small gap that corresponds approximately to the thickness of the cutting wire.

Dieser Spalt wird zwar durch die Porenbeton-Rohmischung ebenfalls ausgefüllt, jedoch kann ein durch den Spalt geführter Schneiddraht den noch weichen Porenbeton leicht schneiden und aus dem Spalt entfernen. This gap is likewise filled by the cellular concrete raw mix, but a guided through the gap cutting wire can easily cut the still soft porous concrete and remove from the gap. Nach dem Aufteilen des Porenbetons mittels der Schneiddrähte werden dann die Verbundsteine wiederum in einen Autoklaven zur Dampfhär tung gebracht. After dividing the expanded concrete by means of the cutting wires, the composite stones are then in turn placed in an autoclave for Dampfhär processing.

Bei Normalbeton, Glasfaserbeton und Leichtbeton erfolgt das Aufteilen in einzelne Verbundsteine oder -platten nach dem Autoklavieren durch Sägen. When normal concrete, glass fiber reinforced concrete and lightweight concrete splitting takes place into individual composite stones or slabs after autoclaving by sawing. Auch Porenbeton konnte gegebenenfalls nach dem Autoklavieren gesägt werden. Aerated concrete could if necessary be cut after autoclaving. Hier bei und auch bei Verwendung von Porenbeton ist es möglich, Deckplatten, die ursprünglich die doppelte Dicke aufwiesen, der Länge nach durchzusägen. Here at, and even with the use of porous concrete it is possible to cover plates, which originally had twice the thickness, saw through lengthwise.

Um die Verbindung zwischen Deckplatte und tragendem Ele ment noch zu verbessern, könnte die dem tragenden Element zugekehrte Innenseite der Deckplatte aufgerauht oder gege benenfalls auch profiliert sein. To establish the connection between the cover plate and carrying Ele ment still improving, which faces the supporting element inside of the cover plate may be roughened or gege be appropriate, also profiled.

Claims (21)

  1. 1. Verfahren zur Herstellung von Verbundsteinen oder -platten, bestehend aus einem tragenden Element aus einer zement- und/oder kalkhaltigen Masse und einer vorgefertigten, dekorativen Deckplatte aus silikati schem Material, bei dem die zement- und/oder kalkhal tige Masse in plastischem Zustand an die Innenseite einer in einer Form angeordneten Deckplatte angeformt wird, dadurch gekennzeichnet, daß die Verbundsteine oder -platten nach dem Erreichen der Grünstandsfestig keit einer Betonmasse oder nach dem Anpressen einer Kalksandsteinmasse, einer Dampfdruckhärtung in einem Autoklaven bei Temperaturen von 150 bis 230°C unter zogen werden. 1. A process for the production of composite stones or slabs, consisting of a supporting element from a cement and / or lime-containing mass and a prefabricated decorative cover plate silikati-magnetic material, wherein the cement and / or kalkhal term mass in a plastic state is formed on the inside, arranged in a mold cover plate, characterized in that the composite blocks or sheets after reaching the Grünstandsfestig ness a mass of concrete or after pressing a sand-lime brick mass, a Dampfdruckhärtung in an autoclave at temperatures of 150 to 230 ° C be attracted.
  2. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß als plastische Masse eine Porenbeton-Rohmischung ver wendet wird. 2. The method of claim 1, characterized in that the plastic mass a cellular concrete crude mixture turns is ver.
  3. 3. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß als plastische Masse eine Normalbeton-Rohmischung ver wendet wird. 3. A method according to claim 1, characterized in that the plastic mass a normal concrete crude mixture turns is ver.
  4. 4. Verfahren nach Anspruch 3, dadurch gekennzeichnet, daß als plastische Masse eine Glasfaserbeton-Rohmischung verwendet wird. 4. The method according to claim 3, characterized in that a glass fiber-concrete raw mix is ​​used as a plastic mass.
  5. 5. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß als plastische Masse eine Leichtbeton-Rohmischung ver wendet wird. 5. The method according to claim 1, characterized in that a lightweight concrete crude mixture turns ver as a plastic mass.
  6. 6. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß als plastische Masse eine Kalksandstein-Rohmischung verwendet wird. 6. The method according to claim 1, characterized in that a sand-lime brick the raw mix is ​​used as a plastic mass.
  7. 7. Verfahren nach einem der Ansprüche 1-6, dadurch gekennzeichnet, daß als Deckplatte eine silikathaltige Naturwerksteinplatte verwendet wird. 7. The method according to any one of claims 1-6, characterized in that a silicate-containing natural stone plate is used as a cover plate.
  8. 8. Verfahren nach Anspruch 7, dadurch gekennzeichnet, daß als Deckplatte eine Granitplatte verwendet wird. 8. A method according to claim 7, characterized in that a slab of granite is used as the cover plate.
  9. 9. Verfahren nach einem der Ansprüche 1-6, dadurch gekennzeichnet, daß als Deckplatte eine silikatische Keramikplatte verwendet wird. 9. The method according to any one of claims 1-6, characterized in that a silicate ceramic plate is used as a cover plate.
  10. 10. Verfahren nach einem der Ansprüche 1-6, dadurch gekennzeichnet, daß als Deckplatte eine Glasplatte verwendet wird. 10. The method according to any one of claims 1-6, characterized in that a glass plate is used as a cover plate.
  11. 11. Verfahren nach einem der Ansprüche 1-10, dadurch gekennzeichnet, daß vor dem Angießen oder Anpressen der plastischen Masse auf die Innenseite der Deck platte ein Haftvermittler aufgebracht wird. 11. The method according to any one of claims 1-10, characterized in that before casting or pressing the plastic composition on the inside of the cover plate, a bonding agent is applied.
  12. 12. Verfahren nach Anspruch 11, dadurch gekennzeichnet, daß als Haftvermittler Kalkhydratmilch verwendet wird. 12. The method according to claim 11, characterized in that Kalkhydratmilch is used as an adhesion promoter.
  13. 13. Verfahren nach Anspruch 11, dadurch gekennzeichnet, daß als Haftvermittler Zementleim verwendet wird. 13. The method according to claim 11, characterized in that is used as an adhesion promoter cement paste.
  14. 14. Verfahren nach einem der Ansprüche 11-13, dadurch gekennzeichnet, daß auf der Haftvermittlerschicht eine Faserschicht oder ein Gewebe angeordnet wird. 14. A method according to any one of claims 11-13, characterized in that a fibrous layer or a fabric is placed on the adhesive layer.
  15. 15. Verfahren nach einem der Ansprüche 1-14, dadurch gekennzeichnet, daß mindestens eine Deckplatte in horizontaler Stellung mit nach oben gerichteter Innen seite auf den Boden einer Form gelegt und die plasti sche Masse darüber aufgegossen oder aufgepreßt wird. 15. The method according to any one of claims 1-14, characterized in that at least one cover plate placed in horizontal position with an upwardly directed inner side of the bottom of a mold and the plasticized specific mass is poured over or pressed.
  16. 16. Verfahren nach Anspruch 15, dadurch gekennzeichnet, daß eine Porenbeton-Rohmischung nach dem Erreichen der Grünstandsfestigkeit mittels Schneiddrähten in eine der Anzahl und den Abmessungen der Deckplatten ent sprechende Anzahl von Verbundsteinen oder -platten geschnitten und anschließend der Dampfdruckhärtung unterzogen wird. 16. The method according to claim 15, characterized in that an aerated concrete crude mixture after reaching the green strength of the number and the dimensions of the cover plates plates cut by means of cutting wires in take out a suitable number of composite stone or and then the Dampfdruckhärtung is subjected.
  17. 17. Verfahren nach Anspruch 16, dadurch gekennzeichnet, daß mittels eines Schneiddrahtes eine obere Schicht von Porenbetonsteinen oder -platten abgetrennt wird, die keine Deckplatten aufweist. 17. The method according to claim 16, characterized in that an upper layer of aerated concrete blocks or plates is separated by means of a cutting wire, which has no cover plates.
  18. 18. Verfahren nach einem der Ansprüche 1-5, dadurch gekennzeichnet, daß mehrere Deckplatten in vertikaler Stellung unter Belassung von Zwischenräumen zwischen ihren einander zugekehrten Innenseiten in einer Form angeordnet, dann die Zwischenräume mit der plasti schen Masse ausgefüllt und diese durch vertikale, im Bereich der Zwischenräume geführte Schnitte in einzel ne Verbundsteine oder -platten aufgeteilt wird. 18. The method according to any one of claims 1-5, characterized in that a plurality of cover plates disposed in a vertical position while leaving spaces between their mutually facing inner sides in a mold, then filling in the gaps with said plasti's mass and this by vertical, in the range the gaps guided cuts in individual ne interlocking pavers or slabs is divided.
  19. 19. Verfahren nach Anspruch 18, dadurch gekennzeichnet, daß die Deckplatten mit ihren Außenseiten aneinander liegend in die Form gestellt werden. 19. The method according to claim 18, characterized in that the cover plates are placed with their outer sides adjacent to one another in the mold.
  20. 20. Verfahren nach Anspruch 18 oder 19, dadurch gekenn zeichnet, daß das Aufteilen durch vertikale Schnitte bei Porenbeton nach Erreichen der Grünstandsfestig keit vor der Dampfdruckhärtung erfolgt. 20. The method of claim 18 or 19, characterized in that the dividing by vertical cuts with aerated concrete after reaching the Grünstandsfestig ness takes place before the Dampfdruckhärtung.
  21. 21. Verfahren nach Anspruch 18 oder 19, dadurch gekenn zeichnet, daß das Aufteilen bei Normal- und Leicht beton nach der Dampfdruckhärtung durch Sägen erfolgt. 21. The method of claim 18 or 19, characterized in that the splitting in normal and lightweight concrete according to the Dampfdruckhärtung by sawing takes place.
DE19924241042 1992-12-05 1992-12-05 Composite brick or slab prodn. with ready-made decorative cover plate of silicate - by moulding on cement and/or lime compsn., pre-hardening and steam cure in autoclave. Expired - Fee Related DE4241042C1 (en)