DE4101032A1 - Moulding compsn. used as finish and casting material - contains bulk material comprising particles of calcined clay and liq. polymer binder - Google Patents

Moulding compsn. used as finish and casting material - contains bulk material comprising particles of calcined clay and liq. polymer binder

Info

Publication number
DE4101032A1
DE4101032A1 DE19914101032 DE4101032A DE4101032A1 DE 4101032 A1 DE4101032 A1 DE 4101032A1 DE 19914101032 DE19914101032 DE 19914101032 DE 4101032 A DE4101032 A DE 4101032A DE 4101032 A1 DE4101032 A1 DE 4101032A1
Authority
DE
Germany
Prior art keywords
bulk
molding composition
particles
clay
binder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19914101032
Other languages
German (de)
Inventor
Anton Mack
Original Assignee
Anton Mack
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anton Mack filed Critical Anton Mack
Priority to DE19914101032 priority Critical patent/DE4101032A1/en
Publication of DE4101032A1 publication Critical patent/DE4101032A1/en
Withdrawn legal-status Critical Current

Abstract

A moulding compsn. (I) comprises bulk material of defined grain size, to which is added a cured binder. The bulk material contains particles of calcined clay and the binder is a liquid polymer cured by incorporating air. Mixing ratio of bulk material to binder is adjusted so that punctiform bonds between particles occurs. Finely ground calcined lime is pref. mixed with the clay, pref. the clay contains up to 35% lime. Esp. fibrous materials, such as glass, plastic, steel, carbon or the like, are added. The particles have spherical shape. The bulk material has spheres of the same or different diameters, and is pref. a mixt. of spheres of approx 0.3mm, approx. 1 mm and approx. 3mm. The liq. polymer is a highly unsatd. polybutadiene. USE/ADVANTAGE - Used as a finish for floor heating, as casting material to mfr. mouldings, e.g. paving stones, plates, dripstone, decorating stones, plant pots or the like (all claimed). (I) has a relative low specific densit

Description

Die Erfindung betrifft eine Formmasse, bestehend aus Schüttgut vorbestimmter Körnung, dem ein aushärtendes Binde­ mittel zugesetzt ist.The invention relates to a molding compound consisting of Bulk material of predetermined grain size, to which a hardening bandage medium is added.

Es sind Formmassen bekannt, die aus mineralischem Schütt­ gut, z. B. Quarzkörnern, wie Sand oder Kieseln bestehen. In ei­ ner schüttfähigen Masse liegen die Körner dicht aneinander und können durch Zusatz eines aushärtenden Bindemittels, z. B. hy­ draulisch abbindendem Zement, aneinander gebunden werden. Be­ vor das Bindemittel aushärtet, kann eine zubereitete Formmasse entsprechend verarbeitet werden, um daraus z. B. Formteile her­ zustellen.Molding compositions are known which consist of mineral bulk well, e.g. B. quartz grains such as sand or pebbles. In egg In a pourable mass, the grains lie close together and can by adding a hardening binder, e.g. B. hy draulic setting cement to be bound together. Be A prepared molding compound can be used before the binder hardens are processed accordingly, z. B. molded parts deliver.

Aufgrund des hohen spezifischen Gewichtes aus Quarz beste­ hender Schüttgüter hat die Formmasse und haben somit auch die daraus hergestellten Formteile hohes Gewicht, was bei bestimm­ ten Anwendungsfällen von Nachteil sein kann.Best due to the high specific weight of quartz bulk goods have the molding compound and thus also have the Molded parts made from it are very heavy, which at certain ten applications can be disadvantageous.

Der Erfindung liegt die Aufgabe zugrunde, eine Formmasse mit aushärtendem Bindemittel bereitzustellen, die bekannte Ei­ genschaften mineralischer Formmassen hat, jedoch ein vorteil­ haft geringes Gewicht aufweist.The invention has for its object a molding compound provide with hardening binder, the well-known egg properties of mineral molding compounds, but has an advantage has low weight.

Diese Aufgabe ist erfindungsgemäß dadurch gelöst, daß das Schüttgut Körperteilchen aus gebranntem Ton enthält und daß das Bindemittel ein durch Aufnahme von Luftsauerstoff aushär­ tendes flüssiges Polymer ist, wobei das Mischungsverhältnis zwischen Körperteilchen des Schüttgutes und dem Bindemittel so eingestellt ist, daß sich im wesentlichen punktförmige Bindun­ gen zwischen den Körperteilchen ergeben.This object is achieved in that the Bulk contains body particles from fired clay and that  the binder cures by absorbing atmospheric oxygen is liquid polymer, the mixing ratio between body particles of the bulk material and the binder so is set that essentially punctiform Bindun between the body particles.

Gebrannter Ton ist ein mineralischer Werkstoff, der auf­ grund seiner Porigkeit ein relativ geringes spezifisches Ge­ wicht hat. Die unter Verwendung von Körperteilchen aus gebranntem Ton angemischte Formmasse sowie daraus hergestellte Formteile weisen ein vorteilhaft geringes Gewicht auf. Nach dem Aushärten des Bindemittels sind die Körperteilchen punkt­ förmig miteinander verklebt, so daß auch innerhalb der ausge­ härteten Formmasse das Gewicht noch weiter reduzierende Hohl­ räume erhalten bleiben. Aufgrund ihres relativ geringen Ge­ wichts und der sowohl in den Körperteilchen als auch in den Hohlräumen zwischen den Körperteilchen eingeschlossenen Luft, läßt sich die erfindungsgemäße Formmasse optimal für Wärmeiso­ lierungen verwenden. Da das Bindemittel ein durch Aufnahme von Luftsauerstoff aushärtendes flüssiges Polymer ist, kann die Formmasse vorbereitet und mit Bindemittel versetzt in luft­ dichten Portionspackungen, beispielsweise aufreißbaren Kunst­ stoffbeuteln, am Verwendungsort angeliefert werden. Diese Ge­ bindeform hat den Vorteil, daß die Formmasse nach Öffnen des Gebindes die Konsistenz eines Gießmaterials aufweist und pro­ blemlos in auszufüllende Hohlräume gegossen werden kann, um dort nach dem Aushärten zu verbleiben oder, z. B. aus einer Form wieder herausgenommen und einer weiteren Verwendung als Formteil zugeführt zu werden. Burnt clay is a mineral material that is based on due to its porosity a relatively low specific Ge important. That made using body particles fired clay mixed molding compound and produced therefrom Molded parts are advantageously light in weight. To the body particles are the point of hardening of the binder glued together in shape, so that also within the out hardened molding compound further reducing the weight of the hollow rooms are preserved. Because of their relatively low Ge weight and that in both the body particles and in the Cavities between air trapped in the body particles, the molding composition according to the invention can be optimal for heat iso Use lashings. Since the binder is a by absorbing Airborne oxygen-curing liquid polymer can Molding compound prepared and mixed with binder in air dense portion packs, such as tearable art fabric bags are delivered to the place of use. This Ge Bindeform has the advantage that the molding compound after opening the Container has the consistency of a casting material and per can be easily poured into cavities to be filled to remain there after curing or, for. B. from a Removed form and another use as Molding to be fed.  

Durch den Einsatz eines durch Aufnahme von Luftsauerstoff aus­ härtenden flüssigen Polymers als Bindemittel, bedarf es in vor­ teilhafter Weise keiner weiteren Anmischung der Formmassen. Nach dem Öffnen eines Gebindes ist die Formmasse verarbeitungs­ fertig.By using a by absorbing atmospheric oxygen curing liquid polymer as a binder, is required in advance geous no further mixing of the molding compositions. After opening a container, the molding compound is processed finished.

Dem Ton für die Körperteilchen kann vor dem Ausformen der Körperteilchen feingemahlener, gebrannter Kalk bis zu etwa 35% zugesetzt sein. Durch die Beimischung von gebranntem Kalk wird die Formmasse noch leichter bei in vorteilhafter Weise zuneh­ mender Fertigkeit. Kalk kann auch durch Schüttgut beigemischt werden. Durch eine Beimischung von Fasermaterial zur Formmasse erhalten daraus hergestellte Formteile eine höhere Biege- und Zugfestigkeit. Zweckmäßigerweise wird Fasermaterial mit dem Bindemittel vermischt.The clay for the body particles can be molded before molding Particles of finely ground, quicklime up to about 35% be clogged. By adding burnt lime the molding compound increases even more easily in an advantageous manner skill. Lime can also be mixed in with bulk material will. By adding fiber material to the molding compound molded parts obtained therefrom have a higher bending and Tensile strenght. Advantageously, fiber material with the Binder mixed.

Die Körperteilchen aus gebranntem Ton, aus denen das Schüttgut der Formmasse besteht, können Linsenform aufweisen oder auch Bruchstücke aus insbesondere blasigem, während des Brennvorganges aufgeblähtem Ton sein. Vorzugsweise weisen die Körperteilchen Kugelform auf. Die Kugeln können einen Durch­ messer von 0,3-5 mm oder auch darüber aufweisen. Tonkugeln mit einem Durchmesser von 0,3 mm lassen sich im industriellen Maßstab noch herstellen. Die Herstellung größerer Tonkugeln ist problemlos. Tonkugeln können durch Aussieben in gleiche Größen sortiert werden. Es ist möglich, das Schüttgut aus Ku­ geln gleichen Durchmessers bereitzustellen. Die Formmasse ist dann eine sogenannte Einkornmasse. Solche Einkornmassen sind besonders durchlässig und leicht. Soll die Formmasse im ausge­ härteten Zustand etwas größere Festigkeit ausweisen, wird das Schüttgut aus Kugeln unterschiedlicher Durchmesser gemischt. Eine bevorzugte Mischung weist drei Körnungen der Tonkugeln von etwa 0,3 mm, etwa 1 mm und etwa 3 mm auf. Tonkugeln mit diesen Durchmessern legen sich dicht aneinander, so daß be­ reits eine geringe Menge des Bindemittels ausreicht, um deren punktförmige, gegenseitige Verklebung zu erreichen. Dabei reicht es aus, daß die Formmasse das Bindemittel in einer Men­ ge von etwa 2-3% enthält.The body particles made of fired clay that make up the Bulk material of the molding compound may have a lens shape or fragments of particularly blistered, during the Blown clay. Preferably, the Body particles spherical. The balls can go through have a diameter of 0.3-5 mm or more. Clay balls with a diameter of 0.3 mm can be used in industrial Still make scale. The production of larger clay balls is easy. Clay balls can be sieved into the same Sizes are sorted. It is possible to get the bulk goods from Ku to provide the same diameter. The molding compound is then a so-called one-grain mass. Such single grain masses are particularly permeable and light. Should the molding compound in the  will show somewhat greater strength when hardened, that will Bulk mixed from balls of different diameters. A preferred mixture has three grain sizes of the clay balls of about 0.3 mm, about 1 mm and about 3 mm. Clay balls with these diameters lie close together so that be a small amount of the binder is sufficient to make them to achieve punctiform, mutual bonding. Here it is sufficient that the molding compound contains the binder in a menu contains about 2-3%.

Das als Bindemittel verwendete, durch Aufnahme von Luftsau­ erstoff aushärtende flüssige Polymer kann z. B. aus einem hoch ungesättigten Polybutadien bestehen. Dies ist für die Bindung mineralischer bzw. keramischer Körperteilchen innerhalb einer Formmasse besonders geeignet.The used as a binder by absorbing air sows Erstoff-hardening liquid polymer z. B. from a high unsaturated polybutadiene exist. This is for the bond mineral or ceramic body particles within one Molding compound particularly suitable.

Die erfindungsgemäße Formmasse ist aufgrund ihrer mechani­ schen Festigkeit, des geringen Gewichts und der darin enthalte­ nen Hohlräume auch besonders vorteilhaft als Estrich für Fußbo­ denheizungen verwendbar. Aufgrund der geringen Masse pro Volu­ meneinheit ist die Wärmespeicherkapazität der erfindungsgemä­ ßen Formmasse relativ gering, so daß sich eine Fußbodenheizung in vorteilhafter Weise relativ schnell nachregeln läßt.The molding composition according to the invention is due to its mechani strength, light weight and what it contains Nen cavities also particularly advantageous as screed for Fußbo the heaters can be used. Due to the low mass per volume Unit unit is the heat storage capacity of the invention ß molding compound relatively low, so that there is underfloor heating can be readjusted relatively quickly in an advantageous manner.

Die erfindungsgemäße Formmasse kann auch mit besonderem Vorteil aufgrund ihrer Eigenschaften als Gießmaterial zur Her­ stellung von Formkörpern, wie z. B. Pflastersteine, Pflaster­ platten, z. B. für die Begrünung von Dachgärten, Filtermaterial oder daraus hergestellten Filterkörpern, Dekorsteinen, Pflan­ zenschalen und dergleichen verwendet werden. Aufgrund der Durchlässigkeit bietet sich besonders eine Verwendung als Fil­ ter und für die Ausformung von Pflanzschalen an. In Pflanzscha­ len kann keine Staunässe entstehen, da sich ansammelndes über­ schüssiges Gießwasser aus der Pflanzschale durch die durchläs­ sigen Wandungen absickern kann. Aufgrund der Filterwirkung der Formmasse, aus der die Pflanzschale hergestellt ist, wird die Pflanzerde jedoch in der Pflanzschale zurückgehalten.The molding composition according to the invention can also be used with particular Advantage due to their properties as a casting material provision of moldings, such as. B. paving stones, pavement plates, e.g. B. for the greening of roof gardens, filter material or filter bodies, decorative stones, plants produced therefrom  zenschalen and the like can be used. Due to the Permeability is particularly useful as a fil ter and for the formation of plant trays. In the nursery len there can be no waterlogging, because accumulated over shot water from the plant bowl through the drains seeping walls. Due to the filter effect of the The molding compound from which the planting bowl is made is the However, potting soil is retained in the planting bowl.

Claims (13)

1. Formmasse bestehend aus Schüttgut vorbestimmter Kör­ nung, dem ein aushärtendes Bindemittel zugesetzt ist, dadurch gekennzeichnet, daß das Schüttgut Körperteilchen aus gebranntem Ton enthält und daß das Bindemittel ein durch Aufnahme von Luftsauerstoff aushärtendes flüssiges Polymer ist, wobei das Mischungsverhält­ nis zwischen Körperteilchen des Schüttgutes und dem Bindemit­ tel so eingestellt ist, daß sich im wesentlichen punktförmige Bindungen zwischen den Körperteilchen ergeben.1. Molding composition consisting of bulk material predetermined Körung, to which a hardening binder is added, characterized in that the bulk material contains body particles from fired clay and that the binder is a liquid polymer which is hardened by absorption of atmospheric oxygen, the mixing ratio between body particles of the bulk material and the Bindemit tel is set so that there are essentially point-like bonds between the body particles. 2. Formmasse nach Anspruch 1, dadurch gekennzeichnet, daß dem Ton für die Körperteilchen feingemahlener gebrannter Kalk beigemischt ist.2. Molding composition according to claim 1, characterized in that the clay for the body particles finely ground lime is added. 3. Formmasse nach Anspruch 2, dadurch gekennzeichnet, daß der Ton bis zu 35% Kalk enthält.3. Molding composition according to claim 2, characterized in that the clay contains up to 35% lime. 4. Formmasse nach Anspruch 1 oder 2, dadurch gekennzeich­ net, daß dem aus Körperteilchen aus gebranntem Ton bestehenden Schüttgut körniger gebrannter Kalk beigemischt ist.4. Molding composition according to claim 1 or 2, characterized net that that consisting of body particles from fired clay Bulky granular burnt lime is added to the bulk. 5. Formmasse nach einem der Ansprüche 1 bis 3, gekennzeich­ net durch eine Beimischung von Fasermaterial aus Glas, Kunst­ stoff, Stahl, Kohlenstoff und dergleichen Werkstoffen.5. Molding composition according to one of claims 1 to 3, characterized net by adding fiber material made of glass, art fabric, steel, carbon and the like materials. 6. Formmasse nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß die Körperteilchen Kugelform aufweisen. 6. Molding composition according to one of claims 1 to 4, characterized characterized in that the body particles have a spherical shape.   7. Formmasse nach Anspruch 6, dadurch gekennzeichnet, daß die Kugeln einen Durchmesser von 0,3-5 mm aufweisen.7. Molding composition according to claim 6, characterized in that the balls have a diameter of 0.3-5 mm. 8. Formmasse nach den Ansprüchen 6 und 7, dadurch gekenn­ zeichnet, daß das Schüttgut aus Kugeln gleichen Durchmessers besteht.8. Molding composition according to claims 6 and 7, characterized records that the bulk material from balls of the same diameter consists. 9. Formmasse nach den Ansprüchen 6 und 7, dadurch gekenn­ zeichnet, daß das Schüttgut aus Kugeln unterschiedlicher Durch­ messer besteht.9. Molding composition according to claims 6 and 7, characterized records that the bulk material from balls of different diameters knife exists. 10. Formmasse nach Anspruch 9, dadurch gekennzeichnet, daß das Schüttgut eine Mischung aus Kugeln von etwa 0,3 mm, etwa 1 mm und etwa 3 mm ist.10. Molding composition according to claim 9, characterized in that the bulk material is a mixture of balls of approximately 0.3 mm, approximately 1 mm and about 3 mm. 11. Formmasse nach einem der vorhergehenden Ansprüche, da­ durch gekennzeichnet, daß das flüssige Polymer aus einem hoch ungesättigten Polybutadien besteht.11. Molding composition according to one of the preceding claims, since characterized in that the liquid polymer from a high unsaturated polybutadiene. 12. Verwendung der Formmasse nach einem der vorhergehenden Ansprüche als Estrich für Fußbodenheizungen.12. Use of the molding composition according to one of the preceding Requirements as screed for underfloor heating. 13. Verwendung der Formmasse nach einem der Ansprüche 1 bis 11 als Gießmaterial zur Herstellung von Formkörpern, wie z. B. Pflastersteinen, Pflasterplatten, Filtersteinen, Dekor­ steinen, Pflanzschalen und dergleichen.13. Use of the molding composition according to one of claims 1 to 11 as a casting material for the production of moldings, such as e.g. B. paving stones, paving slabs, filter stones, decor stones, plant pots and the like.
DE19914101032 1991-01-16 1991-01-16 Moulding compsn. used as finish and casting material - contains bulk material comprising particles of calcined clay and liq. polymer binder Withdrawn DE4101032A1 (en)