DE4024877C2 - Sintered molded body, method for its preparation and its use - Google Patents

Sintered molded body, method for its preparation and its use

Info

Publication number
DE4024877C2
DE4024877C2 DE19904024877 DE4024877A DE4024877C2 DE 4024877 C2 DE4024877 C2 DE 4024877C2 DE 19904024877 DE19904024877 DE 19904024877 DE 4024877 A DE4024877 A DE 4024877A DE 4024877 C2 DE4024877 C2 DE 4024877C2
Authority
DE
Grant status
Grant
Patent type
Prior art keywords
molded body
zirconia
sintered
wt
matrix
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE19904024877
Other languages
German (de)
Other versions
DE4024877A1 (en )
Inventor
Wolfgang Dipl Chem Dr Burger
Michael Dipl Ing Dr Fripan
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Cerasiv GmbH Innovatives Keramik-Engineering
Original Assignee
Cerasiv GmbH Innovatives Keramik-Engineering
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Grant date

Description

Die vorliegende Erfindung betrifft einen Sinterformkörper, mit einer Aluminiumoxidmatrix, darin gelöstem Chromoxid und eingelagertem Zirkoniumdioxid und/oder Hafniumdioxid. The present invention relates to a sintered shaped body, with an alumina matrix, is dissolved chromium oxide, and zirconium dioxide and / or hafnium dioxide. Die Erfindung betrifft auch ein Verfahren zur Herstellung des Sinterformkörpers und die Verwendung des Sinterformkörpers. The invention also relates to a method for producing the sintered molded article and the use of the sintered molding.

In der DE 36 08 854 ist die Verwendung eines Oxidkeramik-Werkstoffes für Preßwerkzeuge zum Ausformen von Bauteilen aus Glas oder glashaltiger Keramik angegeben. In DE 36 08 854 using an oxide ceramic material for press tools is provided for molding of components made from glass or glass-containing ceramic. Als Matrixwerkstoffe werden neben kubischem und tetragonalem Zirkoniumdioxid auch Aluminiumoxid, Chromoxid, Spinell und ein Al-Cr-Mischoxid (AlCr 2 O 3 ) angegeben. As matrix materials in addition to cubic and tetragonal zirconia and alumina, chromia, spinel, and a AlCr mixed oxide (AlCr 2 O 3) can be given. Die einzelnen Vorschläge für die Matrixkomponenten stehen dabei gleichberechtigt nebeneinander, so daß zur Auswahl einer besonderen Matrixkomponente wie auch zum Anteil der in die Matrix einzulagernden Menge an z. The individual proposals for the matrix components are thereby equal footing so that the selection of a particular matrix component as well as on the proportion of the matrix to be held in amount of z. B. Zirkoniumdioxid keine Lehre Vermittelt wird. B. zirconia is Conveys no teaching. Neben den vorstehend genannten Komponenten können noch stabilisierende Oxide wie z. In addition to the aforementioned components stabilizing oxides such still can. B. Yttriumoxid (Y 2 O 3 ) in einer Menge von 3,5 bis 12, vorzugsweise 8 bis 10 oder Magnesiumoxid (MgO) in einer Menge von 6,0 bis 16, vorzugsweise 8 bis 14 Mol.%, bezogen auf den Oxidkeramik-Werkstoff, vorliegen. B. yttrium oxide (Y 2 O 3) in an amount of 3.5 to 12, preferably 8 to 10, or magnesium oxide (MgO) in an amount of 6.0 to 16, preferably 8 to 14 mol.%, Based on the oxide ceramic -Material are present. Als Partikelgröße für die in eine polykristalline Matrix eingelagerten Teilchen wird eine Größe zwischen 5 und 5000 nm entsprechend 0,005 bis 5 µm genannt. As particle size for the incorporated in a polycrystalline matrix particles have a size between 5 and 5000 nm corresponding to 0.005 is called to 5 microns.

Ein weiterer Vorschlag zu einer sogenannten "umwandlungsverstärkten" Keramikzusammensetzung, bei der eine feinverteilte feste Lösung aus ZrO 2 -HfO 2 in einer festen Lösung aus entweder Chromoxid enthaltendem Aluminiumoxid oder Chromoxid enthaltendem Mullit angegeben ist, findet sich in der WO 85/01936 und wird dort für Hochtemperaturanwendungsbereiche, wie z. Another proposal for a so-called "conversion reinforced" ceramic composition in which a finely divided solid solution of ZrO 2 -HfO 2 in a solid solution of chromium oxide containing aluminum oxide or chromium oxide containing mullite is specified either, can be found in WO 85/01936, where it is for high temperature applications such. B. für Dieselmotoren und Gasturbinen vorgeschlagen. As for diesel engines and gas turbines proposed. Der in Erwägung gezogene Chromoxidanteil zwischen 3 und 30 Mol.%, insbesondere ein Anteil von 20 Mol.% Chromoxid im Zusammenwirken mit einem Anteil von 10 bis 20 Mol.% Hafniumdioxid, soll zur Verbesserung der Härte und zur Einstellung einer niedrigen Wärmeleitfähigkeit dienen. The contemplated chromium oxide between 3 and 30 mol.%, In particular, a proportion of 20 mol.% Of chromium oxide in conjunction with a proportion of 10 to 20 mol.% Of hafnium dioxide is intended to serve to improve the hardness and to adjust a low thermal conductivity. Steigende Anteile an Chrom- und Hafniumdioxid führen zu einer Abnahme der Wärmeleitfähigkeit. Increasing proportions of chromium and hafnium dioxide result in a decrease in thermal conductivity. Zu der Korngröße der eingelagerten ZrO 2 -HfO 2 -Phase wird in den Beispielen dieser Schrift eine Größenordnung von 5 µm angegeben, und der Nichterhalt der tetragonalen Modifikation darauf zurückgeführt, daß es nicht gelungen ist, die dispergierte ZrO 2 -HfO 2 -feste Lösung in ausreichender Feinheit zu erhalten. To the grain size of the incorporated ZrO 2 -HfO 2 phase is given an order of magnitude of 5 microns in the examples of this document, and the non-receipt of the tetragonal modification attributed to the fact that it has not succeeded in the dispersed ZrO 2 -HfO 2 solid solution to obtain a sufficient fineness.

Die EP-A-199 459 betrifft keramische Zusammensetzungen hoher Zähigkeit und sieht ein Zusammenwirken von Zirkoniumdioxid, teilstabilisiertem Zirkoniumdioxid, festen Lösungen von Zirkoniumdioxid/Hafniumdioxid, festen Lösungen von teilstabilisiertem Zirkoniumdioxid/Hafniumdioxid, teilstabilisiertem Hafniumdioxid und Hafniumdioxid mit Mischungen von Metalloxiden, insbesondere von Yttriumnioboxid (YNbO 4 ) oder Yttriumtantaloxid (YTaO 4 ) vor. EP-A-199 459 relates to ceramic compositions of high toughness and provides an interaction of zirconia, partially stabilized zirconia, solid solutions of zirconia / hafnia solid solutions of partially stabilized zirconia / hafnia partially stabilized hafnium dioxide and hafnium dioxide with mixtures of metal oxides, especially of Yttriumnioboxid ( YNbO 4) or Yttriumtantaloxid (YTaO 4) in front. Gemäß einer weiteren Variante dieser Schrift kann die beschriebene keramische Legierung, also z. According to another variant of this document, the ceramic alloy described, that is z. B. ZrO 2 unter Zusatz von YNbO 4 in einer Menge von wenigstens 5 Vol.% mit z. B. ZrO 2 with the addition of YNbO 4 in an amount of at least 5 vol.% With z. B. α-Aluminiumoxid oder auch Al 2 O 3 -Cr 2 O 3 , Mullit oder B. α-alumina or Al 2 O 3 -Cr 2 O 3, mullite, or Titaniumcarbid, abgemischt werden. Titanium carbide, are mixed. Der Nachteil dieser bekannten Zusammensetzung ist darin zu sehen, daß in Folge der Nb oder Ta enthaltenden Mischoxide bei den hergestellten Keramikprodukten eine weitere Korngrenzenphase entsteht und sich ein für viele Anwendungsbereiche noch nicht ausreichend hoher Erweichungspunkt einstellt. The disadvantage of this known composition is the fact that as a result of containing Nb or Ta mixed oxides in the produced ceramic products produced another grain boundary phase and a not yet high enough for many applications softening adjusts.

In der EP-A-131 895 wird ein aus Keramik hergestelltes Magnetplattensubstrat beschrieben, wobei die Keramik im wesentlichen aus Aluminiumoxid und/oder Zirkonoxid besteht und durch Heißpressen oder isostatisches Pressen hergestellt ist. In EP-A-131 895 a made of ceramic magnetic disk substrate is described, wherein the ceramic consists essentially of aluminum oxide and / or zirconium oxide and is manufactured by hot pressing or isostatic pressing. Als Sinterhilfsstoffe können in einer Aluminiumoxidkeramik bis zu 5 Gew.-% MgO, ZrO 2 , Y 2 O 3 , Cr 2 O 3 , MnO 2 , SiO 2 , NiO und TiO 2 enthalten sein, während für eine Keramik auf Basis Zirkonoxid/Yttriumoxid 4 bis 30 Gew.-%, vorzugsweise 10 bis 25 Gew.-% Yttriumoxid, vorgeschlagen werden. As sintering aids up to 5 may in an alumina ceramic wt .-% MgO, ZrO 2, Y 2 O 3, Cr 2 O 3, MnO 2, SiO 2, NiO, and TiO 2 be contained as a ceramic based on zirconium oxide / yttrium oxide 4 to 30 wt .-%, preferably 10 to 25 wt .-% of yttrium oxide, are proposed. Für eine aus den Oxiden des Aluminiums/Zirkoniums und Yttriums gebildete Keramik wird eine bis zu 95 Gew.-% Aluminiumoxid enthaltende Zusammensetzung vorgeschlagen, wobei das Zirkoniumoxid 4 bis 30 Gew.-%, vorzugsweise 10 bis 25 Gew.-% Yttriumoxid, enthält. For a formed from the oxides of aluminum / zirconium and yttrium ceramic composition is up to 95 wt .-% aluminum oxide containing is proposed, wherein the zirconium oxide 4 to 30 wt .-%, preferably 10 to 25 wt .-% of yttria. Der Einsatz eines Yttriumoxid-dotierten Zirkoniumdioxids in eine aus Aluminiumoxid und Chromoxid gebildete Matrix wird in dieser Schrift nicht erwähnt. The use of an yttria-doped zirconia in a formed of aluminum oxide and chromium oxide matrix is ​​not mentioned in this document.

Die US-PS 47 70 673 betrifft ein keramisches Schneidwerkzeug, das zu 20 bis 45% aus einer 1 bis 4 Mol.% eines gemischten Metalloxids enthaltenden Zirkoniumdioxid-Legierung und 55 bis 80 Gew.-% einer Hartkeramik-Zusammensetzung besteht, wobei die gemischten Metalloxide aus der Gruppe YNbO 4 , YTaO 4 , MNbO 4 , MTaO 4 und deren Mischungen bestehen, und M aus einem Kation besteht, das zur Substitution des Yttriumkations vorgesehen ist und aus Mg +2 , Ca +2 , Sc +3 und Seltenerdmetallionen ausgewählt ist, bestehend aus der Gruppe La +3 , Ce +4 , Ce +3 , Pr +3 , Nd +3 , Sm +3 , Eu +3 , Gd +3 , Tb +3 , Dy +3 , HO +3 , Er +3 , Tm +3 , Yb +3 und Lu +3 und deren Mischungen besteht. The US-PS 47 70 673 relates to a ceramic cutting tool, the zirconia alloy to 20 to 45% of a 1 to 4 mol.% Of a mixed metal oxide containing between 55 and 80 consists wt .-% of a hard ceramic composition, wherein the mixed metal oxides from the group YNbO 4, YTaO 4, MNbO 4, MTaO 4 and consist mixtures thereof, and M consists of a cation which is provided for substitution of the Yttriumkations and selected from Mg +2, Ca +2, +3 Sc and rare earth metal is selected from the group consisting La +3, Ce +4, Ce +3, Pr +3, Nd +3, Sm +3, Eu +3, Gd +3, Tb +3, Dy +3, +3 HO, he +3, +3 Tm, Yb and Lu +3 +3, and mixtures thereof. Als Hartkeramik kommt neben Aluminiumoxid und z. As hard ceramic comes in addition to aluminum and z. B. Sialon, SiC, Si 3 N 4 auch Al 2 O 3 -Cr 2 O 3 in Betracht, wobei ein Cr 2 O 3 -Anteil bis zu ungefähr 5 Mol.% vorgesehen ist. B. sialon, SiC, Si 3 N 4 and Al 2 O 3 -Cr 2 O 3 into consideration, wherein a Cr 2 O 3 content up to about 5 mol.% Is provided. Auch hier besteht wiederum der Nachteil, daß sich durch die dem ZrO 2 zugefügten Legierungsbestandteile in Form der Niob bzw. Tantal enthaltenden Mischoxide in der Keramik ein zu niedriger Erweichungsbereich ergibt. Here again there is the drawback that containing the mixed oxides in the ceramic obtained by the ZrO 2 added alloy constituents in the form of niobium or tantalum, too low a softening range.

Ein älterer Vorschlag der Anmelderin betrifft gemäß der DE 29 23 213 eine Schneidplattenzusammensetzung aus 70 bis 90 Gew.-% Aluminiumoxid, 10 bis 30 Gew.-% Zirkoniumdioxid und 0,1 bis 0,5 Gew.-% Magnesiumoxid unter Einstellung einer bestimmten Porosität, mittleren Korngröße und Bruchzähigkeit. An older proposal of the Applicant relates, according to DE 29 23 213, a cutting insert composition of 70 to 90 wt .-% aluminum oxide, 10 to 30 wt .-% zirconia and 0.1 to 0.5 wt .-% magnesium oxide by setting a certain porosity , average grain size and fracture toughness.

Demgegenüber betrifft die US-PS 43 16 964 eine auch zur Herstellung von Schneidplatten in Erwägung gezogene Zusammensetzung aus Aluminiumoxid und Zirkoniumdioxid unter Zusatz von Yttriumoxid. In contrast, US-PS 43 16 964 relates to a solid for the production of cutting inserts into consideration the composition of alumina and zirconia with the addition of yttria.

Die vorstehend diskutierten Vorschläge haben sich in der Praxis zum Teil gut bewährt, es besteht aber nach wie vor die Aufgabe, die bekannten Werkstoffe zu verbessern und Sinterformkörper zur Verfügung zu stellen, die auch unter erhöhter Temperaturbeanspruchung ihr hohes Festigkeitsniveau beibehalten, insbesondere will die Erfindung einen für die Verwendung als Schneidplatte geeigneten Sinterformkörper zur Verfügung stellen, bei dem eine weiter verbesserte Stabilisierung der in die Matrix eingelagerten tetragonalen Zirkonium- und/oder Hafniumdioxid-Phase und gleichzeitig eine höhere Härte und damit eine höhere Verschleißfestigkeit des Sinterformkörpers eingestellt ist. The above-discussed proposals are well proven in practice to some extent, but there is still the task of improving the known materials and to provide sintered molding available that maintain their high level of strength even under high temperature stress, in particular wants the invention provides a filters for use as a cutting insert suitable sintering shaped bodies available, in which a further improved stability of the incorporated into the matrix tetragonal zirconium and / or hafnium dioxide phase, and at the same time a higher hardness and a higher wear resistance of the sintered molded body is set. Eine weitere Aufgabe sieht die Erfindung darin, ein Verfahren zur Verfügung zu stellen, bei dem unter Rückgriff auf die an sich bekannten Herstellungsmethoden des keramischen Betriebes eine problemlose Fertigung des Sinterformkörpers ermöglicht wird. A further object, the present invention is to provide a method available in which a trouble-free production of the sintered molded body is made possible by resorting to the known methods of preparation of the ceramic operation.

Zur Lösung dieser Aufgabe sieht die Erfindung bei einem Sinterformkörper, mit einer Aluminiumoxidmatrix, darin gelöstem Chromoxid und eingelagertem Zirkoniumdioxid und/oder Hafniumdioxid, die Kombination der nachfolgenden Merkmale vor: To achieve this object, the invention provides for a sintered shaped body, with an alumina matrix, is in front of dissolved chromium oxide, and zirconium dioxide and / or hafnium dioxide, the combination of the following features:
Der Matrixanteil des Sinterformkörpers beträgt mindestens 70 Vol.%, The matrix portion of the sintered compact body is.% Of at least 70 volume,
der in der Matrix vorliegende Chromoxidanteil beträgt 0,01 bis 1,41 Gew.-%, bezogen auf den gesamten Sinterformkörper, bzw. 0,01 bis 2,32 Gew.-%, bezogen auf Aluminiumoxid, the present in the matrix chromium oxide is from 0.01 to 1.41 wt .-%, based on the total of the sintered molded body, or from 0.01 to 2.32 wt .-%, based on aluminum oxide,
in die Matrix eingelagert sind 2 bis 30 Vol.%, entsprechend 3 bis 39,1 Gew.-% von überwiegend in der tetragonalen Modifikation vorliegendem Zirkoniumdioxid und/oder Hafniumdioxid mit einer durchschnittlichen Korngröße von nicht mehr als 2 µm, das mit 0,5 bis 5,4 Gew.-% Yttriumdioxid, bezogen auf Zirkoniumdioxid bzw. Hafniumdioxid. incorporated in the matrix. 2 to 30% by volume, corresponding to 39.1 wt .-% bis 3 of predominantly present in the tetragonal modification zirconia and / or hafnia having an average grain size of not more than 2 microns, with 0.5 up to 5.4 wt .-% yttria based on the zirconia or hafnia.

Es hat sich gezeigt, daß die erfindungsgemäße Kombination aus mit Yttriumoxid anstabilisiertem tetragonalem Zirkoniumdioxid und/oder Hafniumdioxid und der in an sich nur geringe Mengen Chromoxid in einer festen Lösung enthaltenden Aluminiumoxidmatrix ein Sinterformkörper entsteht, der auch bei Temperatureinwirkung eine ausgezeichnete mechanische Festigkeit, insbesondere eine ausgeprägte Bruchzähigkeit aufweist. It has been found that the combination of the invention is formed of yttria anstabilisiertem tetragonal zirconia and / or hafnia and in a manner only small amounts of chromium oxide contained in a solid solution alumina matrix is ​​a sintered shaped body, which is also the effect of temperature, excellent mechanical strength, particularly a pronounced having fracture toughness. Diese Wirkung erklärt sich durch das Gefüge des Sinterformkörpers, bei dem außer der aus Al 2 O 3 und Cr 2 O 3 gebildeten festen Lösung und dem in die Matrix eingelagerten, Yttriumoxid enthaltenden und überwiegend in der tetragonalen Modifikation vorliegendem Zirkoniumdioxid und/oder Hafniumdioxid keine weitere Phase vorliegt. This effect is explained by the structure of the sintered molding, in which, besides the group formed by Al 2 O 3 and Cr 2 O 3 solid solution and embedded in the matrix, yttrium oxide-containing and predominantly present in the tetragonal modification zirconia and / or hafnia no further phase.

Demgegenüber ist bei den aus dem Stand der Technik bekannten Zusätzen von Stoffen, wie YNbO 4 oder YTaO 4 ein Nachteil darin zu sehen, daß sie im Sinterformkörper neben Aluminiumoxid und Zirkoniumoxid eine weitere kristalline Phase mit nicht ausreichend hohem Schmelzpunkt bilden. In contrast, you can see a disadvantage in that they form in the sintered shaped body adjacent alumina and zirconia with a further crystalline phase is not sufficiently high melting point, in the known from the prior art, additions of substances, such as YNbO 4 or YTaO. 4

Gemäß einer weiteren bevorzugten Ausführungsform liegt der Anteil des in tetragonaler Modifikation vorliegenden Zirkoniumdioxids und/oder Hafniumdioxids bei mehr als 95 Vol.%; According to another preferred embodiment, the proportion of water present in the tetragonal modification zirconia and / or Hafniumdioxids is more than 95 vol.%; ganz besonders bevorzugt ist die Einhaltung einer durchschnittlichen Korngröße des eingelagerten Zirkoniumdioxids und/oder Hafniumdioxids im Bereich von 0,2 bis 1 µm, insbesondere sogar die Einstellung einer durchschnittlichen Korngröße von weniger als 0,6 µm. most preferably compliance with an average grain size of the deposited zirconium dioxide and / or Hafniumdioxids in the range of 0.2 to 1 .mu.m, in particular even the setting of an average grain size of less than 0.6 .mu.m. Demgegenüber hat sich eine durchschnittliche Korngröße der Matrix im Bereich von 0,8 bis 1,5 µm als besonders geeignet erwiesen. In contrast, an average grain size of the matrix in the range of 0.8 to 1.5 microns has been found to be particularly suitable.

Zur Herstellung des erfindungsgemäßen Sinterformkörpers kommt ein Verfahren zur Anwendung, bei dem zur Vermeidung von unerwünschten und die Festigkeitseigenschaften beeinträchtigenden Phasen, insbesondere Korngrenzenphasen, einer Mischung aus Aluminiumoxid und Zirkoniumdioxid und/oder Hafniumdioxid YCr 2 O 3 zugesetzt wird. For the production of the sintered molded body according to the invention a process for the application where the 3 is added to prevent unwanted and strength properties affecting phases, in particular grain boundary phases, a mixture of alumina and zirconia and / or hafnia YCR 2 O comes. Beim Sintern zersetzt sich das Yttriumchromat unter Bildung von Yttriumoxid, das sich wiederum im ZrO 2 /HfO 2 -Gitter löst und dessen tetragonale Modifikation stabilisiert, während andererseits eine vollständige Auflösung des entstehenden Cr 2 O 3 im Aluminiumoxidgitter erfolgt. During sintering, the Yttriumchromat form of yttrium oxide, which in turn dissolves in the ZrO 2 / HfO 2 grid and stabilizes the tetragonal modification, while on the other hand, there is a complete resolution of the resulting Cr 2 O 3 in the alumina lattice decomposed. Bei der Durchführung des erfindungsgemäßen Verfahrens und zur Erzielung einer von weiteren unerwünschten Phasen freien Gefügestruktur werden vorzugsweise hochreine Rohstoffe eingesetzt, dh Aluminiumoxid, Zirkoniumdioxid und Hafniumdioxid mit einer Reinheit von mehr als 99%. In carrying out the process of the invention and to achieve free of other undesirable phases microstructure preferably highly pure raw materials are used, that is, alumina, zirconia and hafnia having a purity of more than 99%. Vorzugsweise ist der Grad der Verunreinigungen noch wesentlich geringer und liegt in bevorzugter Weise bei weniger als 0,2%, insbesondere sind SiO 2 -Anteile mit mehr als 0,2%, bezogen auf den fertigen Sinterformkörper, unerwünscht. Preferably, the degree of contamination is still substantially less and is preferably less than 0.2%, in particular SiO 2 contents are more than 0.2%, based on the finished sintered molding, undesirable.

Die Sinterformkörper entsprechend der vorliegenden Erfindung sind für Einsatzgebiete geeignet, bei denen eine hohe mechanische Festigkeit auch bei hoher Temperatur erforderlich ist und die infolge des Matrixanteils aus Al 2 O 3 /Cr 2 O 3 noch ein relativ gutes Wärmeleitvermögen aufweisen. The sintered molded body according to the present invention are suitable for applications where high mechanical strength is required even at high temperatures and still have a relatively good thermal conductivity as a result of the matrix portion of Al 2 O 3 / Cr 2 O 3. Die geringen Anteile von Chromoxid tragen dabei nicht zur Verschlechterung der Wärmeleitfähigkeit bei. The low levels of chromium oxide not wear it to the deterioration of the thermal conductivity. Die erfindungsgemäßen Sinterformkörper werden daher besonders bevorzugt als Schneidplatten bei der spanabhebenden Bearbeitung, insbesondere bei der Bearbeitung von Eisenwerkstoffen wie Gußeisen eingesetzt. The sintered moldings of the invention are therefore particularly preferably used as inserts in the machining, especially when machining ferrous materials such as cast iron.

Claims (6)

  1. 1. Sinterformkörper, mit einer Aluminiumoxidmatrix, darin Gelöstem Chromoxid und eingelagertem Zirkoniumdioxid und/oder Hafniumdioxid, dadurch gekennzeichnet , daß 1. sintered shaped body, with an alumina matrix, dissolved therein, chromium oxide and zirconium dioxide and / or hafnium, characterized in that
    der Matrixanteil des Sinterformkörpers mindestens 70 Vol.% beträgt, .% Of the matrix portion of the sintered molded body is at least 70 volume amounts,
    der in der Matrix vorliegende Chromoxidanteil 0,01 bis 1,41 Gew.-%, bezogen auf Sinterformkörper, entsprechend 0,01 bis 2,32 Gew.-%, bezogen auf Aluminiumoxid, beträgt, the present in the matrix chromium oxide 0.01 to 1.41 wt .-%, based on the sintered molded body, corresponding to 0.01 to 2.32 wt .-%, based on aluminum oxide is,
    das Zirkoniumdioxid und/oder Hafniumdioxid in einer Menge von 2 bis 30 Vol.% entsprechend einer Menge von 3 bis 39,1 Gew.-% in einer 2 µm nicht überschreitenden durchschnittlichen Korngröße überwiegend in der tetragonalen Modifikation vorliegt und the zirconia and / or hafnia in an amount of 2 to 30 vol.% predominantly present in the tetragonal modification in accordance with an amount of 3 to 39.1 wt .-% in a 2 micrometers not exceeding average grain size and
    das Zirkoniumdioxid und/oder Hafniumdioxid 0,5 bis 5,4 Gew.-% Yttriumoxid, bezogen auf Zirkoniumdioxid und/oder Hafniumdioxid, enthält. the zirconium dioxide and / or hafnium dioxide from 0.5 to 5.4 wt .-% of yttrium oxide based on the zirconia and / or hafnia contains.
  2. 2. Sinterformkörper nach Anspruch 1, dadurch gekennzeichnet, daß das Zirkoniumdioxid und/oder Hafniumdioxid zu mindestens 95 Vol.% die tetragonale Modifikation aufweist. 2. sintered molded body according to claim 1, characterized in that the zirconia and / or hafnia having at least 95 vol.% Tetragonal modification.
  3. 3. Sinterformkörper nach einem der Ansprüche 1 und 2, dadurch gekennzeichnet, daß die durchschnittliche Korngröße der Matrix bei 0,8 bis 1,5 µm liegt. 3. sintered molded body according to one of claims 1 and 2, characterized in that the average grain size of the matrix is ​​from 0.8 to 1.5 microns.
  4. 4. Sinterformkörper nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß die durchschnittliche Korngröße des Zirkoniumdioxids und/oder Hafniumdioxids bei 0,2 bis 1 µm liegt. 4. sintered molded body according to one of claims 1 to 3, characterized in that the average grain size of zirconia and / or Hafniumdioxids is from 0.2 to 1 micron.
  5. 5. Verfahren zur Herstellung eines Sinterformkörpers nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß zu einer Aluminiumoxid und Zirkoniumdioxid und/oder Hafniumdioxid enthaltenden Ausgangsmischung Yttriumchromat (YCr 2 O 3 ) zugefügt und nach Fertigstellung der Mischung ein Körper geformt und gesintert wird. 5. A process for the manufacture of a sintered molded body according to any one of claims 1 to 4, characterized in that an alumina and zirconia and / or hafnia-containing starting mixture Yttriumchromat (YCR 2 O 3) was added and formed a body after completion of the mixture, and sintered.
  6. 6. Verwendung eines Sinterformkörpers nach einem der Ansprüche 1 bis 4 als Schneidplatte für die spanabhebende Bearbeitung. 6. The use of a sintered molding according to one of claims 1 to 4 as cutting plate for the machining.
DE19904024877 1990-08-06 1990-08-06 Sintered molded body, method for its preparation and its use Expired - Lifetime DE4024877C2 (en)