DE3638532A1 - Electrically conducting material for producing dental prostheses - Google Patents

Electrically conducting material for producing dental prostheses

Info

Publication number
DE3638532A1
DE3638532A1 DE19863638532 DE3638532A DE3638532A1 DE 3638532 A1 DE3638532 A1 DE 3638532A1 DE 19863638532 DE19863638532 DE 19863638532 DE 3638532 A DE3638532 A DE 3638532A DE 3638532 A1 DE3638532 A1 DE 3638532A1
Authority
DE
Grant status
Application
Patent type
Prior art keywords
metal
dental
produce
use
mould
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19863638532
Other languages
German (de)
Inventor
Christian Frank
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
C Hafner GmbH and Co KG
Original Assignee
C Hafner GmbH and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

To produce dental prostheses there is a need for an inert metal cap whose interior is to form an accurate image of the tooth stump. In order to be able to produce a cap of this type by electroplating, a positive mould is required and has hitherto been produced from low-melting metal. In order to avoid the use of a low-melting metal, which is difficult to handle and requires very elaborate apparatus, and to achieve great accuracy of reproduction, the invention proposes the use of a mixture of dental plaster with metal powder to produce the positive mould.

Description

Die Erfindung betrifft ein elektrisch leitendes Material, das bei der Herstellung von Zahnersatzteilen zum Bilden der Positivform benötigt wird, die die Grundlage für ein auf galvanischem Wege zu formendes Metallnegativ bildet. The invention relates to an electrically conductive material, which is required in the production of dental replacement parts for forming the positive mold, which forms the basis for a galvanic means to be molded metal negative.

Beim Herstellen von Zahnersatzteilen wird vom Zahntech niker eine Positivform des Zahnstumpfes, die mit der vom Zahnarzt erstellten Urform übereinstimmt, hergestellt. In the manufacture of dental prostheses, is made of Zahntech technician a positive mold of the tooth stump, which agrees with the created master mold by the dentist. Diese Positivform bildet die Grundlage für die Herstel lung des Zahnersatzteils, das exakt dem Zahnstumpf ange paßt sein muß. This male mold forms the basis for the development herstel of the dental prosthesis which fits exactly is the tooth stub has to be. Das Zahnersatzteil besteht hierbei im allgemeinen aus einem, die Negativform des Zahnstumpfes bildenden Käppchen, das dann oberseitig noch durch Kunst stoff, Keramik oder Porzellan etc. verblendet beziehungs weise anatomisch geformt wird. The dental prosthesis is in this case generally made of a, forming the negative mold of the tooth stump cap which then material on the upper side or by synthetic, ceramic or porcelain etc. blinded relationship as is anatomically shaped.

Bei dem bisher üblichen Verfahren wird dieses Zahnersatz teil aus Edelmetall, einer Edelmetallegierung oder einer sonstigen Dentallegierung gegossen. In the usual method of this prosthesis is part of precious metal, cast a noble metal alloy or other dental alloy. Hierzu muß von der Originalform eine Gießform hergestellt werden, was nicht nur recht aufwendig ist, sondern was, durch die verschie denen zum Gießen notwendigen Verfahrensschritte, auch regelmäßig dazu führt, daß das Zahnersatzteil nicht exakt dem Zahnstumpf entspricht, also mühsam nachgearbeitet werden muß. For this purpose, a mold of the original form must be produced which is not only very complicated, but what, through the various necessary where the casting process steps also leads regularly that the dental prosthesis does not exactly match the tooth stump, that must be reworked tedious.

Eine Verbesserung dieses altbekannten Verfahrens wird nach einem zum Stande der Technik nach der DE-OS 32 18 300 beschriebenen Verfahren dadurch erreicht, daß die Herstellung des Zahnersatzteils auf galvanischem Wege erfolgt. An improvement to this well-known method is achieved according to a method described with the prior art according to DE-OS 32 18 300 method is that the manufacture of the dental prosthesis is effected by galvanic means. Hierzu wird von der Originalform wiederum eine Gießform hergestellt, die jedoch mit niedrigschmel zendem Metall ausgegossen wird. For this purpose, in turn is prepared from the master mold, a mold, which is, however, filled with niedrigschmel zendem metal. Diese so hergestellte positive Form wird nunmehr in einem galvanischen Bad mit einem Edelmetallüberzug gewünschter Stärke versehen. This thus prepared positive mold is now provided in a galvanic bath with a noble metal coating of desired thickness. Nach Beendigung dieses galvanischen Prozesses wird das niedrig schmelzende Metall ausgeschmolzen, weitgehend ohne daß das hochschmelzende Edelmetall beziehungsweise die hoch schmelzende Dentallegierung angegriffen wird. After completion of this galvanic process the low melting point metal is melted, largely without the high melting precious metals or the high-melting dental alloy is attacked. Hierdurch wird ein dem Zahnstumpf entsprechendes Negativ-Käppchen hergestellt, auf dem sodann das eigentliche Zahnersatz teil aufgebaut werden kann. In this way, a corresponding said tooth stump negative cap is made, then on the the actual dental prosthesis can be constructed.

Obwohl das in der der DE-OS 32 18 300 beschriebene Ver fahren schon eine deutliche Verbesserung bei der Herstel lung derartiger Zahnersatzteile gebracht hat, ist es doch noch, insbesondere wegen des notwendigen Gießvorganges der niedrigschmelzenden Metallegierung, recht aufwendig. Although the United has described in DE-OS 32 18 300 have been going a significant improvement in the development of such herstel dental prostheses made, it is still, in particular because of the necessary casting of low-melting metal alloy, quite complex. Die Herstellung der Positivform beim Gießen dieser nied rigschmelzenden Metallegierung erfordert nicht nur sehr sorgsames Arbeiten von hierzu entsprechend ausgebildeten Fachkräften, sondern auch einen großen apparativen Auf wand. The production of the male mold during casting this nied rigschmelzenden metal alloy not only requires very caring work of this trained staff, but also overcame a great equipment on. Trotzdem verbleiben selbstverständlich die bekann ten Fehlerquellen, die mit dem Gießvorgang verbunden sind, bestehen, wie die Schrumpfung des Metalls, die Bildung von Lunker und auch die Porenbildung. Nevertheless, of course, remain the most th error sources that are connected to the casting process, there are, as the shrinkage of the metal, the formation of voids and pore formation. Außerdem sind diese niedrigschmelzenden Legierungen nicht unbedenk lich zu handhaben, insbesondere wenn sie, was die Regel ist, Blei und Cadmium enthalten. In addition, these low-melting alloys are not without thinking Lich to handle, especially if they know what the rule is, contain lead and cadmium.

Die Erfindung gibt eine Möglichkeit an, auf dieses um ständliche schwierige und gesundheitlich nicht unbedenk liche Herstellen der Positivform zum Formen des Zahner satzteils auf galvanischem Wege zu verzichten. The invention provides a way for this to pass up comprehensible difficult and not without health thinking Liche making the positive mold for molding the Zahner set partly by electroplating. Möglich ist dies durch die Verwendung einer Mischung aus Dental gips und Metallpulver, wobei diese Mischung auf übliche Weise wie normaler Dentalgips angerührt und in eine ent sprechende Negativform eingefüllt wird. this is possible through the use of a mixture of dental stone and metal powder, said mixture is stirred in the usual manner as a normal dental plaster and filled into take out a suitable negative mold. Die sich hieraus ergebende, exakt die Form des Zahnstumpfes wiedergebende Positivform kann nunmehr unmittelbar auf galvanischem Wege mit der gewünschten Edelmetallschicht versehen werden, da diese Positivform durch das dem Dentalgips beigefügte Metallpulver für den elektrischen Strom lei tend gemacht ist. The resultant exactly the shape of the tooth stump reproducing positive mold can be provided now directly galvanically with the desired noble metal layer because these positive mold is made tend by the annexed to the dental plaster metal powder for the electric current lei. Das umständliche, schwierige und nicht unbedenkliche Vergießen der niedrigschmelzenden Legierung entfällt damit vollkommen. The cumbersome, difficult and not safe casting of low-melting alloy is thus eliminated completely. Es wird ersetzt durch das An rühren und Eingießen des mit dem Metallpulver vermischten Dentalgipses, das nicht nur jedem Zahntechniker vertraut ist, sondern auch auf jeden Fall eine exakte Reproduktion der Form ergibt. It is replaced by the on stirring and pouring the resulting mixed with the metal powder dental plaster, which is not only familiar to each dental technician, but also definitely an exact reproduction of the form. Auch nach dem Herstellen des galvanisch geformten Negativs von dieser Positivform ergibt sich wiederum eine vereinfachte Handhabung dadurch, daß an stelle des Herausschmelzens der niedrigschmelzenden Legie rung das Metallpulver durch Säure herausgelöst wird, wo durch sich die Positivform auflöst und das gewünschte Edelmetall-Käppchen, das in seiner Hohlform nunmehr exakt dem Zahnstumpf entspricht, verbleibt. Also, after forming the electroformed negative of the positive shape to a simplified handling in turn results in that in place of taking out the melting of the low melting alloy coins tion the metal powder is dissolved out by acid, which by itself dissolves the positive mold and the desired noble metal cap which in now corresponds exactly to its hollow mold to the tooth stump remains.

Wird, wie vorzugsweise nach der Erfindung vorgeschlagen wird, als Metallpulver Kupferpulver eingesetzt, so kann das Herauslösen auf einfachste Weise durch Einlegen der Form in Salpetersäure erfolgen. If, as is proposed according to the invention is preferably used as the metal powder of copper powder, the leaching can be done in the simplest manner by inserting the mold into nitric acid.

Zweckmäßigerweise wird die Mischung von Dentalgips und Metallpulver im Vehrhältnis 50/50 hergestellt, wodurch, wie Versuche belegt haben, die Abbindezeit des Dental gipses nur unwesentlich verzögert wird, ebenso wie auch nur eine in der Praxis vernachlässigbare Verringerung der Endhärte festzustellen ist. Conveniently, the mixture of dental plaster and metal powders in Vehrhältnis 50/50 is prepared, which have as experiments demonstrated the setting time of the dental gypsum is delayed only slightly, as well as only a negligible in practice reduce the final hardness is observed.

Zusammenfassend kann festgestellt werden, daß der Vorteil der Erfindung in der hohen Reproduktionsgenauigkeit des Zahnersatzteils liegt, sowie auch in der, gegenüber dem bekannten Verfahren, erheblichen Zeit-, Kosten- und Materialersparnis. In summary it can be stated that the advantage of the invention lies in the high reproduction accuracy of the dental prosthesis, as well as in, compared with the known methods, considerable time, cost and material savings.

Am Beispiel der Herstellung eines Käppchens zum Aufsetzen eines Zahnstumpfes soll die Verwendungsweise der Mischung nach der Erfindung aus Dentalgips und Metallpulver er läutert werden. The example of the manufacture of a cap for mounting of a tooth stump, the manner of use of the mixture according to the invention consists of dental plaster and metal powder should it be explained.

Von der vom Zahntechniker hergestellten Positivform des Zahnstumpfes wird auf an sich bekannte Art und Weise über ein Arbeitsmodell eine Gießform, vorzugsweise aus Silikon kautschuk, hergestellt. From the compound prepared by the dental technician positive mold of the tooth stump is made on rubber-se known manner via a working model of a mold, preferably made of silicone. Diese so gewonnene Gießform stellt das genaue Abbild der Originalform dar, ist also die Negativform des Zahnstumpfes. This mold thus obtained is the exact image of the original form, so the negative mold of the tooth stump. Zur Herstellung der Positivform wird Dentalgips mit Kupferpulver etwa im Ver hältnis 50/50 vermischt und sodann, auf bekannte Art und Weise, unter Vakuum mit Wasser angerührt. To prepare the positive mold dental plaster is mixed with copper powder in about Ver ratio 50/50, and then, stirred in a known manner under vacuum with water. Die Verarbei tungszeit dieser Mischung liegt in der gewohnten Verarbei tungszeit des Dentalgipses bei etwa zehn Minuten. The process ing time this mixture is the usual process ing time of the dental gypsum at about ten minutes. Diese angerührte Mischung wird nunmehr in die Negativform ein gegossen und kann dieser Form nach etwa eineinhalb bis zwei Stunden entnommen werden. This is stirred mixture is poured now in the negative form, and this form can be removed in about one and a half to two hours. Da die gesamte Positivform durch das beigefügte Metallpulver elektrisch leitend ist, kann die Positivform unmittelbar galvanisiert werden. Since the entire positive mold is electrically conductive by the attached metal powder, the positive mold may be directly electroplated. Zweckmäßigerweise wird zuerst eine dünne Kupferschicht aufgalvanisiert, auf die sodann die eigentliche Edel metallschicht folgt. Appropriately, a thin layer of copper is first electroplated, then metal layer followed by the actual precious. Die Dicke der Edelmetallschicht kann hierbei verhältnismäßig gering gehalten werden, da Nach arbeiten zum Anpassen des Zahnersatzteils nicht notwendig sind. The thickness of the precious metal layer can be kept relatively low in this case, since after working to adjust the dental prosthesis are not necessary.

Ist die gewünschte Dicke der galvanischen Schicht er reicht, wird die galvanisierte Positivform dem Bad ent nommen und in Salpetersäure gelegt. When the desired thickness of the electroplated layer it extends, the galvanized positive mold is taken ent placed in the bath and nitric acid. Dadurch wird das Kupfer der Positivform chemisch umgewandelt, so daß die Positivform zerfällt und lediglich das galvanisch ge formte Käppchen, das zum Bilden des Zahnersatzteils not wendig ist, verbleibt. Thereby, the copper of the positive mold is chemically transformed, so that the positive mold decomposes and only the galvanically shaped cap which is not manoeuvrable for forming the dental prosthesis part, remains. Die Ränder dieses Käppchens können nunmehr noch bis zur Präparationsgrenze beschliffen, also den anatomischen Verhältnissen angepaßt werden. The edges of this small cap can now still ground down to the margin line, are so adapted to the anatomical conditions.

Claims (4)

  1. 1. Elektrisch leitendes Material, das bei der Herstel lung von Zahnersatzteilen zum Bilden der Positivform be nötigt wird, die die Grundlage für ein auf galvanischem Wege zu formendes Metallnegativ bildet, gekennzeichnet durch eine Mischung aus Dentalgips mit Metallpulver. 1. An electrically conductive material that is forces in herstel development of dental prostheses for forming the positive mold be, which forms the basis for a galvanic means to be molded metal negative, characterized by a mixture of dental plaster with metal powder.
  2. 2. Material nach Anspruch 1, gekennzeichnet durch eine Korngröße des Metallpulvers um 60 my. 2. Material according to claim 1, characterized by a grain size of the metal powder to 60 microns.
  3. 3. Material nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß das Metallpulver Kupferpulver ist. 3. Material according to claim 1 or 2, characterized in that the metal powder is copper powder.
  4. 4. Material nach Anspruch 1, dadurch gekennzeichnet, daß das Mischungsverhältnis von Dentalgips zu Metall pulver bei etwa 50/50 liegt. 4. Material according to claim 1, characterized in that the mixing ratio of gypsum to the dental metal powder is about 50/50.
DE19863638532 1986-11-11 1986-11-11 Electrically conducting material for producing dental prostheses Withdrawn DE3638532A1 (en)